RU2301218C1 - Tiling glaze - Google Patents

Abstract

FIELD: manufacture of building materials.

SUBSTANCE: tiling glaze for deposition on ceramic tiles is composed of, wt parts: clay 40-50, quartz sand 5-10, chalk 2-3, litharge 20-30, pyrolusite 6-10, blast furnace slag 30-60, and, additionally, calcium borate 3-5.

EFFECT: reduced cost price of glaze composition.

2 cl, 1 tbl

Description

Изобретение относится к промышленности строительных материалов и касается составов глазурей для нанесения на керамическую черепицу.The invention relates to the building materials industry and relates to glaze compositions for application to ceramic tiles.

Известна глазурь, содержащая глину, металлургический (медеплавильный) шлак, фритту, корунд [1].Known glaze containing clay, metallurgical (copper) slag, frit, corundum [1].

Известна матово-черная черепичная глазурь, содержащая, вес.ч.: глину 45; кварцевый песок 6,7; мел 2,5; свинцовый глет 40; окись железа 9,7; пиролюзит 7,5 [2].Known matte black tiled glaze containing, parts by weight: clay 45; silica sand 6.7; chalk 2.5; lead litharge 40; iron oxide 9.7; pyrolusite 7.5 [2].

Задача изобретения состоит в удешевлении состава глазури.The objective of the invention is to reduce the cost of the composition of the glaze.

Технический результат решения поставленной задачи достигается тем, что черепичная глазурь, включающая глину, кварцевый песок, мел, свинцовый глет, окись железа, пиролюзит, дополнительно содержит доменный шлак при следующем соотношении компонентов, вес.ч.: глина 40-50; кварцевый песок 5-10; мел 2-3; свинцовый глет 20-30; пиролюзит 6-10; доменный шлак 30-60. Черепичная глазурь дополнительно содержит 3-5 вес.ч. бората кальция.The technical result of the solution of this problem is achieved by the fact that tiled glaze, including clay, quartz sand, chalk, lead litharge, iron oxide, pyrolusite, additionally contains blast furnace slag in the following ratio of components, parts by weight: clay 40-50; silica sand 5-10; chalk 2-3; lead litharge 20-30; pyrolusite 6-10; blast furnace slag 30-60. Tiled glaze additionally contains 3-5 parts by weight. calcium borate.

Глазурь получают следующим образом.Glaze is prepared as follows.

Подготавливают и дозируют компоненты, например, согласно любому выбранному составу (см.табл.1).The components are prepared and dosed, for example, according to any selected composition (see table 1).

Берут, например, 50 кг глины (используемой в производстве черепицы, подлежащей глазурованию), 5 кг кварцевого песка (промытого и высушенного), 3 кг мела, 30 кг свинцового глета, 8 кг пиролюзита, 30 кг доменного шлака, 3 кг бората кальция. Компоненты подвергают помолу по полного прохождения через сетку 008. Подготавливают глазурную суспензию с влажностью 45-47%. Суспензию наносят в виде тонкого слоя на поверхность отформованной и высушенной черепицы, вторично сушат изделия с нанесенным слоем и обжигают. Температура обжига выбирается в зависимости от технологии производства черепицы и свойств используемой в составе глазури глины.Take, for example, 50 kg of clay (used in the manufacture of tiles to be glazed), 5 kg of quartz sand (washed and dried), 3 kg of chalk, 30 kg of lead lead, 8 kg of pyrolusite, 30 kg of blast furnace slag, 3 kg of calcium borate. The components are milled after passing through mesh 008. Prepare the glaze suspension with a moisture content of 45-47%. The suspension is applied in the form of a thin layer on the surface of the molded and dried tiles, the products with the applied layer are dried again and fired. The firing temperature is selected depending on the technology of tile production and the properties of the clay used in the glaze.

Таблица 1Table 1 Составы черепичной глазуриTiled Glaze Compositions КомпонентыComponents Содержание в составах, мас.%:The content in the compositions, wt.%:   №1No. 1 №2Number 2 №3Number 3 №4Number 4 ГлинаClay 4040 50fifty 4040 50fifty Кварцевый песокQuartz sand 1010 55 1010 55 Мелa piece of chalk 22 33 22 22 Свинцовый глетLitharge 20twenty 30thirty 20twenty 30thirty ПиролюзитPyrolusitis 66 88 1010 1010 ДоменныйDomain         шлакslag 6060 30thirty 50fifty 30thirty Борат кальцияCalcium borate -- 33 55 --

При обжиге глазурь может не расплавляться в стекловидную жидкость, а только образовывать спекшийся слой, прочно удерживающийся на поверхности черепицы. В результате на черепице получают защитно-декоративное стекловидное покрытие, имеющее матово-черный цвет.During firing, the glaze may not melt into a glassy liquid, but only form a sintered layer that is firmly held on the surface of the tile. As a result, a protective and decorative glassy coating having a matte black color is obtained on the tile.

Состав черепичной глазури отличается невысокой стоимостью, включает большое количество металлургических отходов (доменного шлака). Возможно применение предложенной глазури в производстве керамического кирпича.The composition of the tiled glaze is not very expensive, it includes a large amount of metallurgical waste (blast furnace slag). Perhaps the use of the proposed glaze in the production of ceramic bricks.

Источники информацииInformation sources

1. Патент №255748 ПНР, С 03 С, 1986.1. Patent No. 255748 NDP, C 03 C, 1986.

2. Гехт Г. Керамика / Пер. с нем. - Л. - М.: Главная редакция химической литературы, 1938. - С.177.2. Hecht G. Ceramics / Per. with him. - L. - M .: The main edition of the chemical literature, 1938. - P.177.

Claims (2)

1. Черепичная глазурь, включающая глину, кварцевый песок, мел, свинцовый глет, окись железа, пиролюзит, отличающаяся тем, что дополнительно содержит доменный шлак при следующем соотношении компонентов, вес.ч.:1. Tiled glaze, including clay, quartz sand, chalk, lead litharge, iron oxide, pyrolusite, characterized in that it further comprises blast furnace slag in the following ratio of components, parts by weight: глинаclay 40-5040-50 кварцевый песокquartz sand 5-105-10 мелa piece of chalk 2-32-3 свинцовый глетlitharge 20-3020-30 пиролюзитpyrolusitis 6-106-10 доменный шлакblast furnace slag 30-6030-60 2. Черепичная глазурь по п.1, отличающаяся тем, что дополнительно содержит 3-5 вес.ч. бората кальция.2. Tiled glaze according to claim 1, characterized in that it further comprises 3-5 parts by weight calcium borate.