RU2020123958A - Отверждаемая эпоксидная система - Google Patents
Отверждаемая эпоксидная система Download PDFInfo
- Publication number
- RU2020123958A RU2020123958A RU2020123958A RU2020123958A RU2020123958A RU 2020123958 A RU2020123958 A RU 2020123958A RU 2020123958 A RU2020123958 A RU 2020123958A RU 2020123958 A RU2020123958 A RU 2020123958A RU 2020123958 A RU2020123958 A RU 2020123958A
- Authority
- RU
- Russia
- Prior art keywords
- epoxy system
- fiber
- curable epoxy
- reinforced
- curable
- Prior art date
Links
- 239000004593 Epoxy Substances 0.000 title claims 23
- 238000000034 method Methods 0.000 claims 10
- 239000002131 composite material Substances 0.000 claims 4
- 239000003733 fiber-reinforced composite Substances 0.000 claims 4
- 238000010438 heat treatment Methods 0.000 claims 4
- 239000003795 chemical substances by application Substances 0.000 claims 3
- CIZUMWWHWPJAAK-UHFFFAOYSA-N 4-[9-(4-amino-3-chlorophenyl)fluoren-9-yl]-2-chloroaniline Chemical compound C1=C(Cl)C(N)=CC=C1C1(C=2C=C(Cl)C(N)=CC=2)C2=CC=CC=C2C2=CC=CC=C21 CIZUMWWHWPJAAK-UHFFFAOYSA-N 0.000 claims 2
- MQJKPEGWNLWLTK-UHFFFAOYSA-N Dapsone Chemical compound C1=CC(N)=CC=C1S(=O)(=O)C1=CC=C(N)C=C1 MQJKPEGWNLWLTK-UHFFFAOYSA-N 0.000 claims 2
- 239000002657 fibrous material Substances 0.000 claims 2
- OWEYKIWAZBBXJK-UHFFFAOYSA-N 1,1-Dichloro-2,2-bis(4-hydroxyphenyl)ethylene Chemical compound C1=CC(O)=CC=C1C(=C(Cl)Cl)C1=CC=C(O)C=C1 OWEYKIWAZBBXJK-UHFFFAOYSA-N 0.000 claims 1
- WZCQRUWWHSTZEM-UHFFFAOYSA-N 1,3-phenylenediamine Chemical compound NC1=CC=CC(N)=C1 WZCQRUWWHSTZEM-UHFFFAOYSA-N 0.000 claims 1
- CBCKQZAAMUWICA-UHFFFAOYSA-N 1,4-phenylenediamine Chemical compound NC1=CC=C(N)C=C1 CBCKQZAAMUWICA-UHFFFAOYSA-N 0.000 claims 1
- RNFJDJUURJAICM-UHFFFAOYSA-N 2,2,4,4,6,6-hexaphenoxy-1,3,5-triaza-2$l^{5},4$l^{5},6$l^{5}-triphosphacyclohexa-1,3,5-triene Chemical compound N=1P(OC=2C=CC=CC=2)(OC=2C=CC=CC=2)=NP(OC=2C=CC=CC=2)(OC=2C=CC=CC=2)=NP=1(OC=1C=CC=CC=1)OC1=CC=CC=C1 RNFJDJUURJAICM-UHFFFAOYSA-N 0.000 claims 1
- LJGHYPLBDBRCRZ-UHFFFAOYSA-N 3-(3-aminophenyl)sulfonylaniline Chemical compound NC1=CC=CC(S(=O)(=O)C=2C=C(N)C=CC=2)=C1 LJGHYPLBDBRCRZ-UHFFFAOYSA-N 0.000 claims 1
- YBRVSVVVWCFQMG-UHFFFAOYSA-N 4,4'-diaminodiphenylmethane Chemical compound C1=CC(N)=CC=C1CC1=CC=C(N)C=C1 YBRVSVVVWCFQMG-UHFFFAOYSA-N 0.000 claims 1
- VIOMIGLBMQVNLY-UHFFFAOYSA-N 4-[(4-amino-2-chloro-3,5-diethylphenyl)methyl]-3-chloro-2,6-diethylaniline Chemical compound CCC1=C(N)C(CC)=CC(CC=2C(=C(CC)C(N)=C(CC)C=2)Cl)=C1Cl VIOMIGLBMQVNLY-UHFFFAOYSA-N 0.000 claims 1
- NWIVYGKSHSJHEF-UHFFFAOYSA-N 4-[(4-amino-3,5-diethylphenyl)methyl]-2,6-diethylaniline Chemical compound CCC1=C(N)C(CC)=CC(CC=2C=C(CC)C(N)=C(CC)C=2)=C1 NWIVYGKSHSJHEF-UHFFFAOYSA-N 0.000 claims 1
- 239000006096 absorbing agent Substances 0.000 claims 1
- 239000000654 additive Substances 0.000 claims 1
- 230000000996 additive effect Effects 0.000 claims 1
- 150000001412 amines Chemical class 0.000 claims 1
- 150000008064 anhydrides Chemical class 0.000 claims 1
- 150000004982 aromatic amines Chemical group 0.000 claims 1
- -1 bisphenol C diglycidyl ether derivatives Chemical class 0.000 claims 1
- GYZLOYUZLJXAJU-UHFFFAOYSA-N diglycidyl ether Chemical compound C1OC1COCC1CO1 GYZLOYUZLJXAJU-UHFFFAOYSA-N 0.000 claims 1
- 239000000835 fiber Substances 0.000 claims 1
- 239000003063 flame retardant Substances 0.000 claims 1
- 230000009477 glass transition Effects 0.000 claims 1
- 238000004519 manufacturing process Methods 0.000 claims 1
- 239000002245 particle Substances 0.000 claims 1
- 239000000049 pigment Substances 0.000 claims 1
- 239000004014 plasticizer Substances 0.000 claims 1
- 229920005862 polyol Polymers 0.000 claims 1
- 150000003077 polyols Chemical class 0.000 claims 1
- 239000011347 resin Substances 0.000 claims 1
- 229920005989 resin Polymers 0.000 claims 1
- 229920001169 thermoplastic Polymers 0.000 claims 1
- 239000004416 thermosoftening plastic Substances 0.000 claims 1
- 239000004034 viscosity adjusting agent Substances 0.000 claims 1
- 239000000080 wetting agent Substances 0.000 claims 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G59/00—Polycondensates containing more than one epoxy group per molecule; Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups
- C08G59/18—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing
- C08G59/40—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing characterised by the curing agents used
- C08G59/50—Amines
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G59/00—Polycondensates containing more than one epoxy group per molecule; Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups
- C08G59/18—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing
- C08G59/20—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing characterised by the epoxy compounds used
- C08G59/22—Di-epoxy compounds
- C08G59/30—Di-epoxy compounds containing atoms other than carbon, hydrogen, oxygen and nitrogen
- C08G59/308—Di-epoxy compounds containing atoms other than carbon, hydrogen, oxygen and nitrogen containing halogen atoms
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G59/00—Polycondensates containing more than one epoxy group per molecule; Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups
- C08G59/18—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing
- C08G59/20—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing characterised by the epoxy compounds used
- C08G59/22—Di-epoxy compounds
- C08G59/30—Di-epoxy compounds containing atoms other than carbon, hydrogen, oxygen and nitrogen
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G59/00—Polycondensates containing more than one epoxy group per molecule; Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups
- C08G59/18—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing
- C08G59/20—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing characterised by the epoxy compounds used
- C08G59/22—Di-epoxy compounds
- C08G59/24—Di-epoxy compounds carbocyclic
- C08G59/245—Di-epoxy compounds carbocyclic aromatic
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
- C08J5/04—Reinforcing macromolecular compounds with loose or coherent fibrous material
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
- C08J5/24—Impregnating materials with prepolymers which can be polymerised in situ, e.g. manufacture of prepregs
- C08J5/241—Impregnating materials with prepolymers which can be polymerised in situ, e.g. manufacture of prepregs using inorganic fibres
- C08J5/243—Impregnating materials with prepolymers which can be polymerised in situ, e.g. manufacture of prepregs using inorganic fibres using carbon fibres
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
- C08J5/24—Impregnating materials with prepolymers which can be polymerised in situ, e.g. manufacture of prepregs
- C08J5/249—Impregnating materials with prepolymers which can be polymerised in situ, e.g. manufacture of prepregs characterised by the additives used in the prepolymer mixture
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K7/00—Use of ingredients characterised by shape
- C08K7/02—Fibres or whiskers
- C08K7/04—Fibres or whiskers inorganic
- C08K7/06—Elements
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J2363/00—Characterised by the use of epoxy resins; Derivatives of epoxy resins
- C08J2363/02—Polyglycidyl ethers of bis-phenols
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Manufacturing & Machinery (AREA)
- Inorganic Chemistry (AREA)
- Epoxy Resins (AREA)
- Reinforced Plastic Materials (AREA)
- Preparation Of Compounds By Using Micro-Organisms (AREA)
- Compositions Of Macromolecular Compounds (AREA)
Claims (18)
1. Отверждаемая эпоксидная система, содержащая эпоксидный компонент, выбранный из простого диглицидилового эфира бисфенола C, одного или нескольких производных простого диглицидилового эфира бисфенола C, и их сочетания; и 9,9-бис(4-амино-3-хлорфенил)флуорен.
2. Отверждаемая эпоксидная система по п.1, дополнительно содержащая, по меньшей мере, один компонент смолы и отверждающий агент, выбранный из амина, ангидрида, полиола и их сочетания.
3. Отверждаемая эпоксидная система по п.2, где отверждающий агент представляет собой ароматический амин, выбранный из 1,3-диаминобензола, 1,4-диаминобензола, 4,4’диамино-дифенилметана, 4,4’-диаминодифенилсульфона, 4-аминофенилсульфона, 3,3’-диаминодифенилсульфона, 4,4’-метиленбис(3-хлор-2,6-диэтиланилина), 4,4’-метиленбис(2,6-диэтиланилина) и их сочетания.
4. Отверждаемая эпоксидная система по п.1, дополнительно содержащая, по меньшей мере, одну добавку, выбранную из термопластичных частиц, флексибилайзера, добавки, повышающей ударную прочность, ускорителя, каучука сердцевина-оболочка, смачивающего агента, замедлителя горения, пигмента или красителя, пластификатора, УФ-поглотителей, модификатора вязкости и их сочетания.
5. Отверждаемая эпоксидная система по п.1, где объединенное количество эпоксидного компонента и 9,9-бис(4-амино-3-хлорфенил)флуорена больше 40% масс по отношению к массе отверждаемой эпоксидной системы.
6. Отверждаемая эпоксидная система по любому из пп.1-5, где отверждаемая эпоксидная система имеет энтальпию отверждения меньше 300 Дж/г и температуру стеклования больше 190°C.
7. Способ изготовления композита, включающий нагрев отверждаемой эпоксидной системы по любому из пп.1-5 при установленной температуре отверждения в пределах от 100°C до 220°C в течение времени достаточного для получения, по меньшей мере, частично отверждаемого композита.
8. Способ по п.7, где установленная температура отверждения достигается посредством нагрева отверждаемой эпоксидной системы при скорости повышения температуры при отверждении в пределах от 0,5°C в минуту до 25°C в минуту от температуры окружающей среды.
9. Способ по п.7, где разность между установленной температурой отверждения и максимальной температурой, достигаемой в центре отверждаемой эпоксидной системы, меньше 20°C.
10. Композит, получаемый способом по любому из пп.7-9.
11. Препрег, содержащий волокнистый материал в контакте с отверждаемой эпоксидной системой по п.1.
12. Способ получения армированной волокнами композитной структуры, включающий приведение в контакт волокнистого материала с отверждаемой эпоксидной системой по любому из пп.1-5 для формирования армированной волокнами отверждаемой эпоксидной системы; и отверждение армированной волокнами эпоксидной системы для формирования армированной волокнами композитной структуры.
13. Способ по п.12, где стадия отверждения армированной волокнами эпоксидной системы включает нагрев армированной волокнами эпоксидной системы при установленной температуре отверждения в пределах от 100°C до 220°C в течение времени достаточного для получения, по меньшей мере, частично армированной волокнами отверждаемой композитной структуры.
14. Способ по п.13, где установленная температура отверждения достигается посредством нагрева отверждаемой эпоксидной системы при скорости повышения температуры при отверждении в пределах от 0,5°C в минуту до 25°C в минуту от температуры окружающей среды.
15. Способ по п.13, где разность между установленной температурой отверждения и максимальной температурой, достигаемой в центре армированной волокнами отверждаемой эпоксидной системы, меньше 20°C.
16. Способ по п.12, где армированная волокнами эпоксидная система имеет толщину самое большее 60 мм.
17. Армированная волокнами композитная структура, полученная с помощью способа по п.12.
18. Аэрокосмический компонент, содержащий армированную волокнами композитную структуру по п.17.