RU2018126064A - Тонкое окрашенное химически упрочненное стекло - Google Patents

Тонкое окрашенное химически упрочненное стекло Download PDF

Info

Publication number
RU2018126064A
RU2018126064A RU2018126064A RU2018126064A RU2018126064A RU 2018126064 A RU2018126064 A RU 2018126064A RU 2018126064 A RU2018126064 A RU 2018126064A RU 2018126064 A RU2018126064 A RU 2018126064A RU 2018126064 A RU2018126064 A RU 2018126064A
Authority
RU
Russia
Prior art keywords
glass
sheet
sio
content
ratio
Prior art date
Application number
RU2018126064A
Other languages
English (en)
Other versions
RU2018126064A3 (ru
RU2736837C2 (ru
Inventor
Коринн КЛЕРО
Кароль ФРЕДИ
Октавио СИНТОРА-ГОНСАЛЕС
Original Assignee
Сэн-Гобэн Гласс Франс
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Сэн-Гобэн Гласс Франс filed Critical Сэн-Гобэн Гласс Франс
Publication of RU2018126064A publication Critical patent/RU2018126064A/ru
Publication of RU2018126064A3 publication Critical patent/RU2018126064A3/ru
Application granted granted Critical
Publication of RU2736837C2 publication Critical patent/RU2736837C2/ru

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C21/00—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface
    • C03C21/001—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface in liquid phase, e.g. molten salts, solutions
    • C03C21/002—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface in liquid phase, e.g. molten salts, solutions to perform ion-exchange between alkali ions
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/10009—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets
    • B32B17/10036—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets comprising two outer glass sheets
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/10009—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets
    • B32B17/10082—Properties of the bulk of a glass sheet
    • B32B17/1011—Properties of the bulk of a glass sheet having predetermined tint or excitation purity
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/10009—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets
    • B32B17/10082—Properties of the bulk of a glass sheet
    • B32B17/10119—Properties of the bulk of a glass sheet having a composition deviating from the basic composition of soda-lime glass, e.g. borosilicate
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/10009—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets
    • B32B17/10128—Treatment of at least one glass sheet
    • B32B17/10137—Chemical strengthening
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/10743—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer containing acrylate (co)polymers or salts thereof
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/10761—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer containing vinyl acetal
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/10788—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer containing ethylene vinylacetate
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B60—VEHICLES IN GENERAL
    • B60J—WINDOWS, WINDSCREENS, NON-FIXED ROOFS, DOORS, OR SIMILAR DEVICES FOR VEHICLES; REMOVABLE EXTERNAL PROTECTIVE COVERINGS SPECIALLY ADAPTED FOR VEHICLES
    • B60J3/00—Antiglare equipment associated with windows or windscreens; Sun visors for vehicles
    • B60J3/007—Sunglare reduction by coatings, interposed foils in laminar windows, or permanent screens
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B23/00—Re-forming shaped glass
    • C03B23/02—Re-forming glass sheets
    • C03B23/023—Re-forming glass sheets by bending
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C21/00—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C3/00—Glass compositions
    • C03C3/04—Glass compositions containing silica
    • C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
    • C03C3/083—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound
    • C03C3/085—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound containing an oxide of a divalent metal
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C3/00—Glass compositions
    • C03C3/04—Glass compositions containing silica
    • C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
    • C03C3/083—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound
    • C03C3/085—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound containing an oxide of a divalent metal
    • C03C3/087—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound containing an oxide of a divalent metal containing calcium oxide, e.g. common sheet or container glass
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C3/00—Glass compositions
    • C03C3/04—Glass compositions containing silica
    • C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
    • C03C3/089—Glass compositions containing silica with 40% to 90% silica, by weight containing boron
    • C03C3/091—Glass compositions containing silica with 40% to 90% silica, by weight containing boron containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C4/00—Compositions for glass with special properties
    • C03C4/02—Compositions for glass with special properties for coloured glass
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C4/00—Compositions for glass with special properties
    • C03C4/18—Compositions for glass with special properties for ion-sensitive glass
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C8/00—Enamels; Glazes; Fusion seal compositions being frit compositions having non-frit additions
    • C03C8/02—Frit compositions, i.e. in a powdered or comminuted form
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/40—Properties of the layers or laminate having particular optical properties
    • B32B2307/402—Coloured
    • B32B2307/4026—Coloured within the layer by addition of a colorant, e.g. pigments, dyes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2605/00—Vehicles
    • B32B2605/006—Transparent parts other than made from inorganic glass, e.g. polycarbonate glazings
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2204/00—Glasses, glazes or enamels with special properties
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2207/00—Compositions specially applicable for the manufacture of vitreous enamels
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P40/00—Technologies relating to the processing of minerals
    • Y02P40/50—Glass production, e.g. reusing waste heat during processing or shaping
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P40/00—Technologies relating to the processing of minerals
    • Y02P40/50—Glass production, e.g. reusing waste heat during processing or shaping
    • Y02P40/57—Improving the yield, e-g- reduction of reject rates

Landscapes

  • Chemical & Material Sciences (AREA)
  • General Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Geochemistry & Mineralogy (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Mechanical Engineering (AREA)
  • Glass Compositions (AREA)
  • Joining Of Glass To Other Materials (AREA)
  • Surface Treatment Of Glass (AREA)
  • Laminated Bodies (AREA)

Claims (78)

1. Лист окрашенного стекла из алюмосиликатной композиции, химически упрочненный посредством ионного обмена, отличающийся тем, что он содержит следующие оксиды с содержанием по весу, лежащим в диапазонах:
SiO2 от 59,20 до 68,00%
Al2O3 от 2,00 до 8,00%
MgO от 6,00 до 9,00%, если содержание Al2O3 составляет от 5,00 до 8,00%, и если отношение SiO2/Al2O3 больше или равно 7,8 или
от 8,00 до 10,00%, если содержание Al2O3 составляет от 2,00 до 5,00%, и если отношение SiO2/Al2O3 больше или равно 24,
Na2O от 9,00 до 16,00%
K2O от 5,00 до 11,00%
B2O3 от 0 до 3,00%
CaO от 0 до 1,00%
и следующие красители с содержанием по весу, лежащим в диапазонах:
Fe2O3 всего от 0,05 до 6,00%
CoO от 0 до 2,00%
NiO от 0 до 1,00%
Se от 0 до 0,10%,
при этом, стекло характеризуется окислительно-восстановительным коэффициентом от 0,10 до 0,65.
2. Лист окрашенного стекла из алюмосиликатной композиции, химически упрочненный посредством ионного обмена, отличающийся тем, что он содержит следующие оксиды с содержанием по весу, лежащим в диапазонах:
SiO2 от 59,20 до 68,00%
Al2O3 от 3,00 до 8,00%
MgO от 6,00 до 9,00%, если содержание Al2O3 составляет от 5,00 до 8,00%, и если отношение SiO2/Al2O3 больше или равно 7,8 или
от 8,00 до 10,00%, если содержание Al2O3 составляет от 3,00 до 5,00%, и если отношение SiO2/Al2O3 больше или равно 24,
Na2O от 9,00 до 16,00%
K2O от 5,00 до 11,00%
B2O3 от 0 до 3,00%
CaO от 0 до 1,00%
и следующие красители с содержанием по весу, лежащим в диапазонах:
Fe2O3 всего от 0,05 до 6,00%
CoO от 0 до 2,00%
NiO от 0 до 1,00%
Se от 0 до 0,10%,
при этом, стекло характеризуется окислительно-восстановительным коэффициентом от 0,10 до 0,65.
3. Лист стекла по одному из предшествующих пунктов, отличающийся тем, что он содержит другие красители, выбранные из оксидов ванадия, хрома, марганца, меди, олова, лантаноидов, серебра, титана и/или сульфидов, в весовом процентном содержании менее 1,00%.
4. Лист стекла по одному из предшествующих пунктов, отличающийся тем, что он упрочнен посредством химической закалки с глубиной ионного обмена, по меньшей мере, 30 мкм, предпочтительно, по меньшей мере, 35 мкм.
5. Ламинированное остекление, отличающееся тем, что включает, по меньшей мере, первый лист известково-натриевого стекла, промежуточный полимерный слой и второй лист стекла, содержащий следующие оксиды с содержанием по весу, лежащим в диапазонах:
SiO2 от 59,20 до 68,00%
Al2O3 от 2,00 до 8,00%
MgO от 6,00 до 9,00%, если содержание Al2O3 составляет от 5,00 до 8,00%, и если отношение SiO2/Al2O3 больше или равно 7,8 или
от 8,00 до 10,00%, если содержание Al2O3 составляет от 2,00 до 5,00%, и если отношение SiO2/Al2O3 больше или равно 24,
Na2O от 9,00 до 16,00%
K2O от 5,00 до 11,00%
B2O3 от 0 до 3,00%
CaO от 0 до 1,00%
и следующие красители с содержанием по весу, лежащим в диапазонах:
Fe2O3 всего от 0,05 до 6,00%
CoO от 0 до 2,00%
NiO от 0 до 1,00%
Se от 0 до 0,10%,
при этом, стекло характеризуется окислительно-восстановительным коэффициентом от 0,10 до 0,65.
6. Ламинированное остекление по предшествующему пункту, отличающееся тем, что включает, по меньшей мере, первый лист известково-натриевого стекла, промежуточный полимерный слой и второй лист стекла, содержащий следующие оксиды с содержанием по весу, лежащим в диапазонах:
SiO2 от 59,20 до 68,00%
Al2O3 от 3,00 до 8,00%
MgO от 6,00 до 9,00%, если содержание Al2O3 составляет от 5,00 до 8,00%, и если отношение SiO2/Al2O3 больше или равно 7,8 или
от 8,00 до 10,00%, если содержание Al2O3 составляет от 3,00 до 5,00%, и если отношение SiO2/Al2O3 больше или равно 24,
Na2O от 9,00 до 16,00%
K2O от 5,00 до 11,00%
B2O3 от 0 до 3,00%
CaO от 0 до 1,00%
и следующие красители с содержанием по весу, лежащим в диапазонах:
Fe2O3 всего от 0,05 до 6,00%
CoO от 0 до 2,00%
NiO от 0 до 1,00%
Se от 0 до 0,10%,
при этом, стекло характеризуется окислительно-восстановительным коэффициентом от 0,10 до 0,65.
7. Остекление по одному из пп. 5 или 6, отличающееся тем, что первый лист стекла относится к типу известково-натриевых стекол и содержит следующие оксиды с содержанием по весу, лежащим в диапазонах:
SiO2 от 65,00 до 75,00%
Na2O от 10,00 до 20,00%
CaO от 2,00 до 15,00%
Al2O3 от 0 до 5,00%
MgO от 0 до 5,00%
K2O от 0 до 5,00%.
8. Остекление по одному из пп. 5-7, отличающееся тем, что разность температур Т(log η=10,3), при которых вязкость каждого из листов стекла составляет 1010,3 Пуаз, по абсолютной величине меньше 30°С, предпочтительно, по абсолютной величине меньше 23°С.
9. Остекление по одному из пп. 5-8, отличающееся тем, что первый лист стекла имеет толщину, самое большее, 2,1 мм, предпочтительно, самое большее, 1,6 мм.
10. Остекление по одному из пп. 5-9, отличающееся тем, что второй лист стекла, более тонкий, чем первый, имеет толщину, самое большее, 1,5 мм, предпочтительно, самое большее, 1,1 мм и даже менее 1 мм.
11. Остекление по одному из пп. 5-10, отличающееся тем, что промежуточный полимерный слой, помещаемый между двумя листами стекла, образован одним или несколькими слоями термопластичного материала, а именно, из полиуретана, поликарбоната, поливинилбутираля (PVB), метилполиметакрилата (PMMA), этиленвинилацетата (EVA) или иономерной смолы.
12. Остекление по п. 11, отличающееся тем, что толщина промежуточного полимерного слоя составляет от 50 мкм до 4 мм.
13. Способ производства ламинированного остекления по любому из пп. 5-12, отличающийся тем, что включает, по меньшей мере, стадию, на которой одновременно придают выпуклость первому и второму листам стекла; стадию, на которой проводят ионный обмен во втором листе стекла; и стадию, на которой собирают два листа стекла с промежуточным полимерным слоем.
14. Способ по п. 13, отличающийся тем, что стадию ионного обмена проводят при температуре менее 490°С в течение времени менее 24 часов, предпочтительно, времени, меньшего или равного 4 часам, даже меньшего или равного 2 часам.
15. Способ по одному из пп. 13 или 14, отличающийся тем, что на стадии придания выпуклости второй лист стекла, более тонкий, чем первый лист, помещают поверх первого листа стекла.
16. Остекление для автомобиля, получаемое способом по одному из пп. 13-15, отличающееся тем, что второй лист стекла обращен в сторону салона автомобиля.
RU2018126064A 2015-12-17 2016-12-16 Тонкое окрашенное химически упрочненное стекло RU2736837C2 (ru)