RU2000104834A - Низколегированная, практически не содержащая бора сталь - Google Patents
Низколегированная, практически не содержащая бора стальInfo
- Publication number
- RU2000104834A RU2000104834A RU2000104834/02A RU2000104834A RU2000104834A RU 2000104834 A RU2000104834 A RU 2000104834A RU 2000104834/02 A RU2000104834/02 A RU 2000104834/02A RU 2000104834 A RU2000104834 A RU 2000104834A RU 2000104834 A RU2000104834 A RU 2000104834A
- Authority
- RU
- Russia
- Prior art keywords
- steel according
- steel
- niobium
- vanadium
- approximately
- Prior art date
Links
- 229910000831 Steel Inorganic materials 0.000 title claims 17
- 239000010959 steel Substances 0.000 title claims 17
- 239000010955 niobium Substances 0.000 claims 6
- 229910052758 niobium Inorganic materials 0.000 claims 5
- GUCVJGMIXFAOAE-UHFFFAOYSA-N niobium Chemical compound [Nb] GUCVJGMIXFAOAE-UHFFFAOYSA-N 0.000 claims 4
- 229910052720 vanadium Inorganic materials 0.000 claims 4
- 239000010936 titanium Substances 0.000 claims 3
- LEONUFNNVUYDNQ-UHFFFAOYSA-N vanadium(0) Chemical compound [V] LEONUFNNVUYDNQ-UHFFFAOYSA-N 0.000 claims 3
- 239000000654 additive Substances 0.000 claims 2
- 229910001563 bainite Inorganic materials 0.000 claims 2
- 229910052799 carbon Inorganic materials 0.000 claims 2
- XEEYBQQBJWHFJM-UHFFFAOYSA-N iron Chemical compound [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 claims 2
- 239000011572 manganese Substances 0.000 claims 2
- ZOKXTWBITQBERF-UHFFFAOYSA-N molybdenum Chemical compound [Mo] ZOKXTWBITQBERF-UHFFFAOYSA-N 0.000 claims 2
- 229910052750 molybdenum Inorganic materials 0.000 claims 2
- 239000011733 molybdenum Substances 0.000 claims 2
- 229910052759 nickel Inorganic materials 0.000 claims 2
- 229910052761 rare earth metal Inorganic materials 0.000 claims 2
- 150000002910 rare earth metals Chemical class 0.000 claims 2
- 229910052719 titanium Inorganic materials 0.000 claims 2
- 230000000996 additive Effects 0.000 claims 1
- 229910045601 alloy Inorganic materials 0.000 claims 1
- 239000000956 alloy Substances 0.000 claims 1
- 229910001566 austenite Inorganic materials 0.000 claims 1
- OKTJSMMVPCPJKN-UHFFFAOYSA-N carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 claims 1
- 229910001567 cementite Inorganic materials 0.000 claims 1
- 229910052804 chromium Inorganic materials 0.000 claims 1
- 229910052802 copper Inorganic materials 0.000 claims 1
- 229910052742 iron Inorganic materials 0.000 claims 1
- PWHULOQIROXLJO-UHFFFAOYSA-N manganese Chemical compound [Mn] PWHULOQIROXLJO-UHFFFAOYSA-N 0.000 claims 1
- 229910052748 manganese Inorganic materials 0.000 claims 1
- 229910000734 martensite Inorganic materials 0.000 claims 1
- 150000001247 metal acetylides Chemical class 0.000 claims 1
- 239000000203 mixture Substances 0.000 claims 1
- 239000002244 precipitate Substances 0.000 claims 1
- 238000001556 precipitation Methods 0.000 claims 1
- RTAQQCXQSZGOHL-UHFFFAOYSA-N titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 claims 1
- DIMMBYOINZRKMD-UHFFFAOYSA-N vanadium(5+) Chemical compound [V+5] DIMMBYOINZRKMD-UHFFFAOYSA-N 0.000 claims 1
Claims (14)
1. Низколегированная, практически не содержащая бора сталь, которая имеет прочность на растяжение по меньшей мере приблизительно 900 МПа, ударную вязкость, измеренную в испытании образцов с V-надрезом по Шарпи при -40oС, по меньшей мере приблизительно 120 Дж и практически неотпущенную микроструктуру, содержащую преимущественно мелкозернистый низший бейнит, мелкозернистый сетчатый мартенсит, или их смеси, преобразованную из практически нерекристаллизованных зерен аустенита, причем эта сталь содержит железо и следующие добавки в указанных ниже мас.%:
Приблизительно от 0,03 до 0,10% углерода (С)
Приблизительно от 1,6 до 2,1% марганца (Мn)
Приблизительно от 0,01 до 0,10% ниобия (Nb)
Приблизительно от 0,01 до 0,10% ванадия (V)
Приблизительно от 0,3 до 0,6% молибдена (Мо)
Приблизительно от 0,005 до 0,03% титана (Ti),
причем показатели Сэ и Рсм находятся в интервале: 0,5≤Сэ≤0,7 и Рсм≤0,35.
Приблизительно от 0,03 до 0,10% углерода (С)
Приблизительно от 1,6 до 2,1% марганца (Мn)
Приблизительно от 0,01 до 0,10% ниобия (Nb)
Приблизительно от 0,01 до 0,10% ванадия (V)
Приблизительно от 0,3 до 0,6% молибдена (Мо)
Приблизительно от 0,005 до 0,03% титана (Ti),
причем показатели Сэ и Рсм находятся в интервале: 0,5≤Сэ≤0,7 и Рсм≤0,35.
2. Сталь по п.1, которая дополнительно содержит по меньшей мере одну добавку, выбранную из группы, состоящей из (i) от 0 до приблизительно 0,6 мас. % Si, (ii) от 0 до приблизительно 1,0 мас.% Сu, (iii) от 0 до приблизительно 1,0 мас. % Ni, (iv) от 0 до приблизительно 1,0 мас.% Сr, (v) от 0 до приблизительно 0,006 мас.% Са, (vi) от 0 до приблизительно 0,06 мас.% Al, (vii) от 0 до приблизительно 0,02 мас.% редкоземельных металлов (РЗМ) и (viii) от 0 до приблизительно 0,006 мас.% Мg.
3. Сталь по п.1, которая дополнительно содержит мелкий осадок цементита.
4. Сталь по п. 1, которая дополнительно содержит осадки карбидов или карбонитридов ванадия, ниобия и молибдена.
5. Сталь по п.4, в которой общая концентрация ванадия и ниобия составляет больше, чем приблизительно 0,06 мас.%.
6. Сталь по п.4, в которой индивидуальная концентрация ванадия и ниобия составляет больше, чем приблизительно 0,03 мас.%.
7. Сталь по п.1, в которой указанная микроструктура стали представляет собой преимущественно мелкозернистый низший бейнит.
8. Сталь по п.1 в виде листа, имеющего толщину по меньшей мере приблизительно 10 мм.
9. Сталь по п.1, которая содержит приблизительно от 0,05 до 0,09 мас.% С.
10. Сталь по п.1, которая содержит приблизительно от 0,2 до 1,0 мас.% Ni.
11. Сталь по п.1, которая содержит приблизительно от 0,03 до 0,06 мас.% Nb.
12. Сталь по п.1, которая содержит приблизительно от 0,03 до 0,08 мас.% V.
13. Сталь по п.1, которая содержит приблизительно от 0,015 до 0,02 мас.% Ti.
14. Сталь по п.1, которая содержит приблизительно от 0,001 до 0,06 мас.% Аl.