NO321152B1 - Oppsvulmende laminater med hoy varmegjennomtrengningsmotstand og anvendelse derav - Google Patents
Oppsvulmende laminater med hoy varmegjennomtrengningsmotstand og anvendelse derav Download PDFInfo
- Publication number
- NO321152B1 NO321152B1 NO19994293A NO994293A NO321152B1 NO 321152 B1 NO321152 B1 NO 321152B1 NO 19994293 A NO19994293 A NO 19994293A NO 994293 A NO994293 A NO 994293A NO 321152 B1 NO321152 B1 NO 321152B1
- Authority
- NO
- Norway
- Prior art keywords
- component
- intumescent
- weight
- melamine
- laminate according
- Prior art date
Description
Anvendelsen av oppsvulmende materialer foregår ved bygningsbrannbeskyttelsen i form av malinger, lakker, belegninger, pastaer, kitter, mørtler, tetninger, plater, snitt, striper, oppskummede plaster, bånd, folier, profiler og andre halvfabrikata. Oppsvulmende materialer er slike som under varmepåvirkning skummer opp og danner en isolerende og brannbestandig skum, som beskytter den der underliggende flate og substans fra brannpåvirkningen. Den klassiske trippelblandingen består av karbongivere, dehydratiseirngsmidler og drivmidler.
Porøse bærematerialer som er belagt med oppsvulmningsmasser er f.eks. kjent fra De 27 03 022, DE 28 17 268, DE 28 27 828, US 4.375.516 eller DE 30 42 788.
De siterte patentsøknader omhandler gjennomgående materialer på formen av sjikthalvfabrikater, som plater, folier, baner, som gjennom deres lukkede overflater til å begynne med ikke er egnet til bestemte områder, som f.eks. lydbeskyttelse eller brannavskjermning av åpne kanaler.
Videre viste det seg at på tross av et flertall av i handelen tilgjengelige oppsvulmning-materialer er en tilfredsstillende impregnering av mikroporøse bærematerialer i dag ikke gjennomførlig. Da dannelse av kondensvann ikke kan utlukkes ved flere potensielle anvendelsesområder, kommer til å begynne med kun impregneirngsmidlet i betraktning som danner vann i oppløselige eller i det minste tungt oppløselige forbindelser. Dermed innskrenker utvalget seg på enkelte brannbeskyttelses-malinger og lakker som etter tørking danner vannfaste filmer.
Impregneirngsforsøk med mineralfiberplater eller mikroporøse melaminharpiksskum med vannfaste brannbeskyttelsesmalinger førte imidlertid ikke til noen teknisk anvendelige resultater. De pulverformede brannbeskyttelseskomponentene ble konsentrert på overflaten av bærematerialene, mens kun bindemidlet diffunderte inn i det indre av bæreplatene. Etter tørkingen dryssede de nå løst vedheftede brannbeskyttelseskomponentene av.
Også gjennom den nærliggende anvendelsen av ikke-pigmenterte brannbeskyttelses-lakker kunne der ikke oppnås en betydelig forbedring. Med disse høyviskøse formuleringene lar mikroporøse bærematerialer seg ikke gjennomfukte. Først etter passende fortynning kom det til en gjennomtrengning av bærematerialene. Men etter tørkingen var andelen av de anbrakte brannbeskyttelseskomponentene for lav til ved de etterfølgende branntester å føre til positive resultater.
I DE 297 10 462 U beskrives videre brannsbeskyttelsesmaterialer som består av et fleksibelt bæremateriale som er belagt med en oppsvulmende substans. Som oppsvulmende substans anvendes fortrinnsvis ekspanderbar grafitt. Alternativt kan det som oppsvulmende substans også anvendes fosfat, spesielt ammoniumpolyfosfat eller etylendiaminfosfat, eller en kombinasjon av ammoniumpolyfosfatmelamin og pentaerytol eller vermikulitt eller vannglass. Egenskaper som varmegjennomtrengningsmotstand og ekspansjonsfaktor er ikke beskrevet.
Oppgave for den foreliggende oppfinnelsen var det å tilveiebringe fleksible laminater med høy ekspansjonsgrad og varme gjennomtrengningsmotstand, som ikke utviser de ovenfornevnte ulempene.
På uventet vis kunne oppgaven løses gjennom et laminat av et glassbæremateriale og et spesielt trekomponentbelegg.
Gjenstand for oppfinnelsen er derfor et oppsvulmende laminat med høy varmegjennomtrengningsmotstand, kjennetegnet ved at den består av en glassfiberflis eller -vevnad, belagt med en oppsvulmende trekomponentmasse omfattende
a) et reaksjonsprodukt av fosforsyre, etylenglykol, og pentaerytritol,
b) en melaminforbindelse
og
c) en uorganisk strukturdannende forbindelse.
Laminatet ifølge oppfinnelsen har en belegning av tre komponenter. Som komponent A
anvendes en polyolfosforsyredelester. Med polyolfosforsyredelester forstås forbindelser som eksempelvis oppnås gjennom forestring av polyoler med fosforsyre eller polyfosforsyrer. Disse er ifølge oppfinnelsen reaksjonsprodukter av fosforsyre, etylenglykol og pentaerytritol.
Komponent b) er en melaminforbindelse fra gruppen melamin, heksametoksymetylmelamin (HMMM), dimelaminpyrofosfat, melaminpolyfosfat, melaminfosfat. Fortrinnsvis anvendes HMMM eller melamin.
Den tredje komponenten c) er en uorganisk, strukturdannende forbindelse fra gruppen titandioksid, aluminiumsilikat, leire, zinkborat, kalsiumborat, natriumfosfat eller - silikat, zeolitt, wollastonitt, borfosfat, serpentin, kaolin, talkum, sepiolitt, jordalkali og plagioklase, som albitt og anoptitt.
Fortrinnsvis anvendes titandioksid eller aluminiumsilikat.
Komponent a) blir herved anvendt i en mengde fra 5 til 50 vekt-%, fortrinnsvis fra 10 til 30 vekt-%.
Anvendelen av komponent b) ligger tilsvarende ved 5 til 50 vekt-%, fortrinnsvis 5 til 30 vekt-%.
Komponent c) blir anvendt i en mengde fra 5 til 30 vekt-%, fortrinnsvis 5 til 20 vekt-%.
Der gjelder betingelsen at summen av komponentene a) til c) i alle tilfeller gir 100 vekt-%<.>
Det kan herved i ethvert tilfelle kun anvendes en forbindelse pr. komponent, det kan dog også for en eller flere av komponentene anvendes to eller flere av de anførte forbindelsene.
Trekomponentmassen kan eventuelt inneholde vanlige hjelpemidler som fuktemidler, skumdemperer, fortykningsmidler, fargestoffer, fungizider, myknere, bindemidler, flammehemmere eller diverse fyllstoffer.
Andelen av de enkelte tilsetningsstoffer ligger i ethvert tilfelle mellom 0 og 10 vekt-%, fortrinnsvis mellom 0,1 og 6 vekt-%. Det må herved igjen bemerkes at summen av alle andelene ikke overstiger 100 vekt-%.
Som hjelpemidler egner seg f.eks. blant annet gjengse fuktemidler på basis av polyakrylater og/eller polyfosfater, alginatfortykkelsesmidler, silikonskumdempere, bindemidler som f.eks. polyvinyl-acetat, -alkohol, -butyren- og -klorid, styrenakrylat, vinyltoluenacetat osv., myknere som klorholdige vokser, fyllstoffer som vermikulitt, uorganiske fibrer, kvartssand, mikroglasskuler, glimmer, silisiumdioksid, mineralull osv., flammehemmerer som f.eks. fosforsyreestrer, hostaflam TPOP 920 (Clariant), Amgard V 490 (Albright + Wilson), trisetylfosfat, trisklorpropylfosfat, osv.
Belegningen blir påført bæreren som oppløsning hhv. pasta, slik at komponent-blandingen eventuelt blir tilsatt vann i en mengde fra 10 til 50 vekt-%, fortrinnsvis 15 til 45 vekt-%, igjen med den betingelsen at summen av alle bestanddelene ikke overstiger 100 vekt-%.
Som bæremateriale til laminaten ifølge oppfinnelsen blir det anvendt en glassfiberflis eller et glassfibervevnad. Fortrinnsvis oppviser bærematerialet en arealvekt mellom 50 og 500 g/m<2.>
Belegningen foregår på en horisontal male- og belegnings-(hhv. tørkings)anordning.
Temperaturen under belegningsfremgangsmåten ligger ved omkring 10 til 30°C, tørkingstemperaturen ligger ved omkring 70 til 170°C.
Ifølge oppfinnelsen foretrekkes laminater med en på 0,5-15 mm. Den samlede tykkelsen av laminaten ligger fortrinnsvis på 1 til 5 mm.
Laminatene ifølge oppfinnelsen er kjennetegnet ved en høy varmegjennomtrengningsmotstand. Ved 800°C utgjør denne verdi mer enn 0,3 KnvVW. Videre er laminatene kjennetegnet av en høy ekspansjonsfaktor. Således ligger denne faktor ved 300°C minst over 20. Laminatene ifølge oppfinnelsen egner seg derfor f.eks. som varm gasstetning ved brannbeskyttelsesdører, som brannbeskyttelsesforheng ved muråpninger, som dørfylling som omviklingsmateriale til enkeltkabler eller kabelskinner osv.
Følgelig angår foreliggende oppfinnelse også anvendelse av et oppsvulmende laminat ifølge oppfinnelsen som varmgasstetning ved brannbeskyttelsesdører som brannbeskyttelsesforheng ved muråpninger, som dørfylling eller som omvikling til enkeltkabler og kabelskinner.
Eksempel:
På en Molteni-blander med planetomrøring ble de enkelte komponentene til de tilsvarende oppskummende masser blandet homogent. De ferdige pastaer ble etterfølgende påført på en horisontal male- og tørkningsanordning og tørket. Tørkingstemperaturen lå mellom 70 og 120°C.
Sammensetningen av blandingen kan finnes i den etterfølgende tabellen.
K30: Omsatt produkt av etylenglykol, pentaeryritol og fosforsyre
Resultatene av testene av de ferdige laminatene sees i den etterfølgende tabellen:
Eksp. H Ekspansjonshøyde, ubelastet, 450°C, 15 min.
Eksp. F Ekspansjonsfaktor = Eksp. H/sjikttykkelse
Fuktighetsopptak: direkte vannkontakt. 20 timer.
Flis: Microlith PM 10/2 (Fabrikant Schuller)
Claims (5)
1.
Oppsvulmende laminat med høy varmegjermomtrengningsmotstand, karakterisert ved at det består av en glassfiberflis eller-vevnad, belagt med en oppsvulmende trekomponentmasse omfattende a) et reaksjonsprodukt av fosforsyre, etylenglykol, og pentaerytritol, b) en melaminforbindelse
og c) en uorganisk strukturdannende forbindelse.
2.
Oppsvulmende laminat ifølge krav 1, karakterisert ved at komponent a) anvendes i en mengde på 5 til 50 vekt-%, komponent b) i en mengde fra 5 til 50 vekt-%, og komponent c) i en mengde fira 5 til 30 vekt-%, med den betingelse at summen av komponentene gir 100 vekt-%.
3.
Oppsvulmende laminat ifølge krav 1, karakterisert ved at komponent b) er en melaminforbindelse valgt fra gruppen melamin, heksametoksymetylmelamin, dimelaminpyrofosfat, melaminpolyfosfat og melaminfosfat.
4.
Oppsvulmende laminat ifølge krav 1, karakterisert v e d at komponent c) er en uorganisk, strukturdannende forbindelse, valgt fra gruppen titandioksid, aluminiumsilikat, leire, zinkborat, kalsiumborat, natriumfosfat eller -silikat, zeolitt, wollastonit, borfosfat, serpentin, kaolin, talkum, sepiolitt, jordalkali og plagioklase, som albitt og anoptitt.
5.
Anvendelse av oppsvulmende laminat ifølge krav 1 som varmgasstetning ved brannbeskyttelsesdører som brannbeskyttelsesforheng ved muråpninger, som dørfylling eller som omvikling til enkeltkabler og kabelskinner.