NO313594B1 - Flammebestandige tekstiler omfattende melaminharpiksfibre - Google Patents

Flammebestandige tekstiler omfattende melaminharpiksfibre Download PDF

Info

Publication number
NO313594B1
NO313594B1 NO19985060A NO985060A NO313594B1 NO 313594 B1 NO313594 B1 NO 313594B1 NO 19985060 A NO19985060 A NO 19985060A NO 985060 A NO985060 A NO 985060A NO 313594 B1 NO313594 B1 NO 313594B1
Authority
NO
Norway
Prior art keywords
fibers
weight
resistant
flame
textiles
Prior art date
Application number
NO19985060A
Other languages
English (en)
Other versions
NO985060L (no
NO985060D0 (no
Inventor
Heinz Berbner
Aegidius Eckel
Hans-Dieter Eichhorn
Karl Ott
Original Assignee
Basf Ag
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Basf Ag filed Critical Basf Ag
Publication of NO985060D0 publication Critical patent/NO985060D0/no
Publication of NO985060L publication Critical patent/NO985060L/no
Publication of NO313594B1 publication Critical patent/NO313594B1/no

Description

Foreliggende oppfinnelse omhandler flammebestandige tekstiler basert på melaminharpiksfibre, og anvendelse av flammebestandige tekstiler, fortrinnsvis ikke-vevede tekstiler.
Konvensjonelle brannsikre tepper, eller bare "branntepper", anvendes vanligvis til å bekjempe mindre branner ved å slukke flammene ved kvelning.
Kjente brannsikre tepper og brannsikre klær består ofte av glassfiber-tekstiler. Disse brannsikre teppene har den ulempen at de er svært sprø og at de har lett for å smelte. I særdeleshet er det følgelig en fare for at det vil brenne igjennom brannsikre tepper fremstilt av dette tekstilet dersom det oppstår en brann. Videre er brannsikre tepper basert på aramidfibre kjent, men slike tepper er fremdeles svært kostbare. Dessuten er den brannhemmende effekten i aramidbaserte tekstiler fremdeles utilfredsstillende. I tillegg har brannsikre klær fremstilt i disse tekstilene bare en moderat brukskomfort.
Det er imidlertid også et behov for brannsikre tepper, som ikke primært anvendes som brannslukningstepper, men som bør være anvendelige i særdeleshet til å beskytte personer eller gjenstander mot brann, varme, forbrenningsprodukter, som for eksempel sot, eller slukkemidler.
Slike beskyttelsestepper ville være særlig anvendelige for eksempel i kirker og museer, som ofte rommer et mangfold av uerstattelige kunstgjenstander som er heller dårlig beskyttet mot brann og, dersom en brann skulle oppstå, mot de direkte konsekvenser av en brann, som for eksempel varme og sot, og også mot konsekvensene forbundet med slokningstiltak.
Brannsikre tepper fra tidligere fagområde er uegnet til dette særskilte formål, ettersom de enten er for tunge, for stive eller for gjennomtrengelige for mikro-partikler eller væsker.
Det er et formål med foreliggende oppfinnelse å tilveiebringe et flammebestandig tekstil til brannsikre tepper eller klær, som gir effektiv beskyttelse mot ild, slukkemidler og/eller forbrenningsprodukter, dvs. som er varme-, vann-, jord-og/eller olje-bestandig.
Vi har funnet at dette formålet er dekket ved tilveiebringelsen av et flammebestandig tekstil som omfatter, basert på tekstilets totalvekt,
a) fra 4,9 til 95 vektprosent melaminharpiksfibre,
b) fra 0 til 90,1 vektprosent flammebestandige fibre valgt fra gruppen bestående av aramidfibre, karbonfibre, glassfibre, flammebestandig
ull og flammebestandig viskose,
og
c) fra 0 til 20 vektprosent fyllstoff,
og videre omfatter
d) eventuelt fra 4,9 til 95 vektprosent normalt brennbare fibre hvor fra 0,1 til 20 vektprosent av minst én varme-, olje-, jord- og/eller fuktighetsbestandig appretur, omfattende minst ett en- eller tosidig metallbelegg, hvor tekstiler veves fra garn fremstilt på en sedvanlig måte. Oppfinnelsen tilveiebringer videre en anvendelse av flammebestandige tekstiler, fortrinnsvis ikke-vevede tekstiler, basert på dets totale vekt omfattende (a) fra 4,9 til 95 vektprosent melaminharpiksfibre, (b) fra 0 til 90,1 vektprosent flammebestandige fibre valgt fra gruppen bestående av aramidfibre, karbonfibre, glassfibre, flammebestandig ull og flammebestandig viskose,
og
(c) fra 0 til 20 vektprosent fyllstoff,
og videre omfatter
(d) eventuelt fra 4,9 til 95 vektprosent normalt brennbare fibre og (e) fra 0,1 til 20 vektprosent av minst én varme-, olje-, jord- og/eller fuktighetsbestandig appretur, omfattende minst et én- eller tosidig metallbelegg, hvor tekstiler veves fra garn fremstilt på en sedvanlig måte, for fremstilling av brannsikre tepper eller klær.
Flammehemmende tekstiler som omfatter de ovenfor nevnte bestanddeler
a), b), c) og d) kan veves på konvensjonelt vis med garn eller fremstilles i form av ikke-vevde tekstiler av fibrene eller fiberblandingene (se Ullmann's Enzyklopådie
der Technischen Chemie, 4. utgave, Volum 23, "Textiltechnik"). Deretter påføres komponent e). Det er også mulig å appretere fibrene a), b) og d), eller garn spun-net av disse, med komponent e), og deretter bearbeide fibrene eller garnet videre til tekstilene ifølge foreliggende oppfinnelse.
I tillegg kan imidlertid tekstilene ifølge foreliggende oppfinnelse videre omfatte fra omtrent 4,9 til 95 vektprosent, fortrinnsvis fra omtrent 5 til 50 vektprosent, i særdeleshet fra omtrent 10 til 45 vektprosent, normalt brennbare tekstiler, for eksempel ull, bomull, polyamidfibre, polyesterfibre og viskose. Men mengden som anvendes av disse fibrene må ikke ha en ugunstig innvirkning på tekstilets flammehemmende evne.
Tilsetningen av normalt brennbare fibre tilveiebringer flere fordeler. Dersom for eksempel bomull eller andre sammenlignbare fibre anvendes som en ytterligere komponent, vil dette gjøre det mulig å fremstille tekstiler med en øket kapa-sitet med hensyn til vannabsorpsjon, hvilket gjør det mulig å tilveiebringe en for-bedret beskyttelse mot fuktighet, for eksempel mot vann som anvendes ved slokking av brannen. Videre kan tilsetningen av normalt brennbare fibre forbedre tekstilenes brukskomfort. Dette er spesielt fordelaktig når beskyttelsesklær skal fremstilles av tekstilene. Tilsetningen av normalt brennbare fibre fører også til en betydelig reduksjon i kostnadene til de flammebestandige tekstilene basert på melaminharpiksfibre.
I stedet for de normalt brennbare fibrene eller i kombinasjon med disse, kan tekstilene i foreliggende oppfinnelse omfatte fra 0,1 til 20 vektprosent, fortrinnsvis fra omtrent 0,5 til 10 vektprosent, av en varme-, olje, jord- og/eller fuktighetsbestandig appretur. Tekstilet kan impregneres eller belegges med appreturen.
Eksempler på appretur som er egnet for anvendelse sammen med foreliggende oppfinnelse er én- eller to-sidig påførte belegg av metall, for eksempel aluminium. Slike metallbelegg, som vanligvis påføres i en tykkelse på for eksempel 5 - 200 |j.m, fortrinnsvis 10-100^m, slik at det ikke gir en ugunstig innvirkning på tekstilets fleksibilitet, beskytter mot brann, påvirkning av varme, spesielt strålevarme, sot og slukkemidler, for eksempel vann og skum eller pulvere. I tråd med den Europeiske provisoriske standard pr. EN 1486, er metalliserte tekstiler egnet for fremstilling av beskyttelsesdrakter som beskyttelse ved ekstra kraftig brann og varme. Tekstilet metalliseres vanligvis ved dampavsetning under vaku-um (se Ullmann's Enzyklopådie der Technischen Chemie, 3. utgave, Volum 15, side 276 og henvisninger anført deri). Det er også mulig å klebe tynne metallfolier til tekstilet. Generelt består slike metallfolier av en polymer støttefilm belagt med en tynn metallfilm. De omfatter fortrinnsvis en polymer bærer basert på polyester. Metallfoliene kan påføres én eller fortrinnsvis begge sidene på tekstilet i foreligg ende oppfinnelse ifølge TL 8415-0203 (TL = teknisk forsyningsspesifikasjon for de tyske forsvarsstyrker), for eksempel ved anvendelse av et klebemiddel eller ved anvendelse av klebemiddel eller ved anvendelse av varmkalandrering. Slike folier anvendes til belegging av tekstiler av forskjellige produsenter (for eksempel Gentex Corp., Carbondale PA, USA: CF. Ploucquet GmbH & Co, D-89522 Heidenheim; Darmstådter GmbH, D-46485 Wesel).
Det er også mulig å fremstille tekstilene i foreliggende oppfinnelse av metal-lisert garn eller fibre. Garnet belegges fortrinnsvis med aluminium i sjikttykkelser innenfor grensene fra 0,01 til 1 |am. Slike garn eller fibre lar seg fremstille for eksempel i tråd med prosessene som beskrives i DE-B 27 43 768, DE-A 38 10 597 eller EP-A 528 192.
Ytterligere eksempler på appreturer som er egnet for anvendelse i forbindelse med foreliggende oppfinnelse er vannavstøtende hydrofobe sjikt påført på den ene eller begge sidene av tekstilet. Slike sjikt består fortrinnsvis av polyuretan-omfattende tekstiler og/eller polytetrafluoreten-omfattende tekstiler. Slike belegg er allerede kjent for å forbedre tekstilers evne til værbeskyttelse (se Ullmann's Enzyklopådie der Technischen Chemie, 5. utgave, Volum A26, side 306-312, og Lexikon fur Textilveredelung, 1955, side 211 etseq.). Disse beleg-gene kan fremstilles på en slik måte at vanndamp kan diffundere gjennom sjiktet, mens flytende vann eller lignende brannslukkemidler og forbrenningsprodukter ikke kan trenge igjennom i noen betydelig grad, hvis i det hele tatt. Disse beleg-gene adheres eller kalandreres vanligvis til tekstilet i form av polymerfilmer.
Ytterligere tiltak for å forbedre den beskyttelsen som brannsikre tepper gir er å appretere fibrene eller tekstilet med vann-, olje- og/eller jord-avstøtende forbindelser (hydrofobe eller oleofobe appreturer). Ved anvendelse er slike forbindelser kjent som tekstil-forbedringsmidler (assistants) (jevnfør Ullmann's Encyclo-pedia of Industrial Chemistry 5. utgave, Volum A26, side 306-312). Eksempler på vannavstøtende forbindelser er metallsåper, silikoner, organofluor-forbindelser, for eksempel salter av perfluorerte karboksylsyrer, polyakrylater av perfluorerte alko-holer (se EP-B-366 338 og henvisninger anført deri) eller tetrafluoretenpolymere. Spesielt de to siste polymerene anvendes også som oleofobe, olje-avstøtende appreturer.
Melaminharpiksfibrene som anvendes i forbindelse med foreliggende oppfinnelse kan fremstilles for eksempel ved anvendelse av fremgangsmåtene som beskrives i EP-A-93 965, DE-A-23 64 091, EP-A-221 330 eller EP-A-408 947. Særskilt foretrukne melaminharpiksfibre omfatter som monomer byggeblokk (A) fra 90 til 100 mol% av en blanding i det vesentlige bestående av fra 30 til 100, fortrinnsvis fra 50 til 99, særlig foretrukket fra 85 til 95, i særdeleshet fra 88 til 93 mol% melamin, og fra 0 til 70, fortrinnsvis fra 1 til 50, særlig foretrukket fra 5 til 15, i særdleshet fra 7 til 12 mol% av et substituert melamin I eller blandinger av substituerte melaminer I.
Vedrørende kjent teknikk vises det også til WO-A1 95/14126 som omfatter fremstilling av flammebestandige tekstiler inneholdende melaminharpiksfibre.
Som en ytterligere monomer byggeblokk (B), omfatter de særlig foretrukne melaminharpiksfibrene fra 0 til 10, fortrinnsvis fra 0,1 til 9,5, i særdeleshet fra 1 til 5 mol%, basert på det totale molantallet av monomer-byggeblokkene (A) og (B), av en fenol eller en blanding av fenoler.
De særlig foretrukne melaminharpiksfibrene tilveiebringes sedvanligvis ved å reagere komponentene (A) og (B) med formaldehyd eller formaldehyd-tilførende forbindelser i et molart forhold av melaminer til formaldehyd innenfor grensene fra 1 : 1,15 til 1 : 4,5, fortrinnsvis fra 1 : 1,8 til 1 : 3,0, og påfølgende spinning. Egnede substituerte melaminer etter den generelle formel I
er de hvorX1,X<2>og X<3>hver er valgt fra gruppen bestående av -NH2, -NHR<1>og -NR1R<2>, selv omX1, X<2>og X<3>ikke alle må være -NH2, og R<1>og R2 er hver valgt fra gruppen bestående av hydroksy-C2-Cio-alkyl, hydroksy-C2-C4-alkyl-(oksa-C2-C4-alkyl)n, hvor n er fra 1 til 5, og amino-C2-Ci2-alkyl.
Hydroksy-C2-Ci0-alkyl er fortrinnsvis hydroksy-C2-C6-alkyl så som 2-hydroksyetyl, 3-hydroksy-n-propyl, 2-hydroksyisopropyl, 4-hydroksy-n-butyl, 5-hydroksy-n-pentyl, 6-hydroksy-n-heksyl, 3-hydroksy-2,2-dimetylpropyl, fortrinnsvis hydroksy-C2-C4-alkyl så som 2-hydroksyetyl, 3-hydroksy-n-propyl, 2-hydroksy isopropyl og 4-hydroksy-n-butyl, spesielt fortrinnsvis 2-hydroksyetyl eller 2-hydroksyisopropyl.
Hydroksy-C2-C4-alkyl-(oksa-C2-C4-alkyl)nhar fortrinnsvis n fra 1 til 4, spesielt fortrinnsvis n = 1 eller 2, så som 5-hydroksy-3-oksapentyl, 5-hydroksy-3-oksa-2,5-dimetylpentyl, 5-hydroksy-3-oksa-1,4-dimetylpentyl, 5-hydroksy-3-oksa-1,2,4,5- tetrametylpentyl, 8-hydroksy-3,6-dioksaoktyl.
Amino-C2-Ci2-alkyl er fortrinnsvis amino-C2-C8-alkyl så som 2-aminoetyl, 3-aminopropyl, 4-aminobutyl, 5-aminopentyl, 6-aminoheksyl, 7-aminoheptyl og også 8-aminooktyl, spesielt fortrinnsvis 2-aminoetyl og 6-aminoheksyl, meget spesielt fortrinnsvis 6-aminoheksyl.
Substituerte melaminer spesielt egnet for oppfinnelsen omfatter de følgende forbindelser: 2-hydroksyetylamino-substituerte melaminer så som 2-(2-hydroksyetylamino)-4,6-diamino-1,3,5-triazin, 2,4-di-(2-hydroksyetylamino)-6-amino-1,3,5-triazin, 2,4,6-tris(2-hydroksyetylamino)-1,3,5-triazin, 2-hydroksyisopropylamino-substituerte melaminer så som 2-(2-hydroksyisopropylamino)-4,6-diamino-1,3,5-triazin, 2,4-di-(2-hydroksyisopropylamino)-6-amino-1,3,5-triazin, 2,4,6-tris(2-hydroksyisopropylamino)-1,3,5-triazin, 5-hydroksy-3-oksapentylamino-substituerte melaminer så som 2-(5-hydroksy-3-oksapentylamino)-4,6-diamino-1,3,5-triazin, 2,4,6-tris-(5-hydroksy-3-oksapentylamino)-1,3,5-triazin, 2,4-di(5-hydroksy-3-oksapentylamino)-6-amino;1,3,5-triazin og også 6-aminoheksylamino-substituerte melaminer så som 2-(6-aminoheksylamino)-4,6-diamino-1,3,5-triazin, 2,4-di(6-amino-heksylamino)-6-amino-1,3,5-triazin, 2,4,6-tris(6-aminoheksylamino)-1,3,5-triazin eller blandinger av disse forbindelser, for eksempel en blanding av 10 mol% av 2-(5-hydroksy-3-oksapentylamino)-4,6-diamino-1,3,5-triazin, 50 mol% of 2,4-di(5-hydroksy-3-oksapentylamino)-6-amino-1,3,5- triazin og 40 mol% av 2,4,6-tris(5-hydroksy-3-oksapentylamino)-1,3,5-triazin.
Egnede fenoler (B) erfenoler inneholdende én eller to hydroksylgrupper, så som usubstituerte fenoler, fenoler substituert med rester valgt fra gruppen bestående av d-Cg-alkyl og hydroksyl og også CrC4-alkaner substituert med to eller tre fenolgrupper, di(hydroksyfenyl) sulfoner eller blandinger derav.
Foretrukne fenoler omfatter fenol, 4-metylfenol, 4-tert-butylfenol, 4-n-oktylfenol, 4-n-nonylfenol, pyrocatechol, resorcinol, hydrokinon, 2,2-bis(4- hydroksyfenyl)propan, Bis(4-hydroksyfenyl) sulfon, spesielt fortrinnsvis fenol, resorcinol og 2,2-bis(4-hydroksyfenyl)propan.
Formaldehyd anvendes generelt i form av en vandig oppløsning som har en konsentrasjon på, for eksempel, fra 40 til 50 vektprosent eller i form av forbindelser som tilfører formaldehyd i løpet av reaksjonen med (A) og (B), for eksempel i form av en oligomer eller polymer formaldehyd i fast form, som for eksempel para-formaldehyd, 1,3,5-trioksan eller 1,3,5,7-tetroksan.
De spesielt foretrukne melaminharpiksfibrene fremstilles ved å polykonden-sere sedvanlig melamin, eventuelt substituert melamin og eventuelt fenol, sammen med formaldehyd eller formaldehyd-tilførende forbindelser. Alle komponentene kan være tilstede i utgangspunktet, eller de kan reageres litt om gangen og gradvis, mens de resulterende pre-kondensatene etterpå blandes sammen med ytterligere melamin, substituert melamin eller fenol.
Polykondensasjonen utføres generelt på konvensjonelt vis (se EP-A-355 760, Houben-Weyl, Volum 14/2, side 357 ff).
De anvendte reaksjonstemperaturene vil generelt ligge innenfor grensene fra 20 til 150°C, fortrinnsvis fra 40 til 140°C.
Reaksjonstrykket er generelt sett ukritisk. Generelt utføres reaksjonen innenfor grensene fra 100 til 500 kPa, fortrinnsvis ved atmosfærisk trykk.
Reaksjonen kan utføres med eller uten et oppløsningsmiddel. Dersom en vandig formaldehydoppløsning anvendes, tilsettes det typisk ikke noe oppløs-ningsmiddel. Dersom det anvendes formaldehyd bundet i fast form, anvendes sedvanligvis vann som oppløsningsmiddel. Mengden som anvendes ligger generelt innenfor grensene fra 5 til 40, fortrinnsvis fra 15 til 20 vektprosent, basert på den totale mengde anvendt monomer.
Videre utføres generelt sett polykondensasjonen innenfor et pH-spekter på over 7. Et pH-spekter fra 7,5 til 10 foretrekkes, og spesielt foretrekkes fra 8 til 9.
I tillegg kan reaksjonsblandingen omfatte små mengder av sedvanlige addi-tiver, som for eksempel alkalimetallsulfitter, for eksempel natriummetabisulfitt og natriumsulfitt, alkalimetallformater, foreksempel natriumformat, alkalimetall-citrater, for eksempel natriumcitrat, fosafter, polyfosfater, urea, dicyandiamid eller cyanamid. De kan tilsettes som rene individuelle forbindelser, eller som blandinger med hverandre, enten uten et oppløsningsmiddel eller som vandige oppløsninger, før, i løpet av eller etter kondensasjonsreaksjonen.
Andre modifiseringsmidler er aminer og aminoalkoholer, som for eksempel dietylamin, etanolamin, dietanolamin eller 2-dietylaminoetanol.
Eksempler på egnede fyllmidler omfatter fibrøse eller pulveriserte, uorga-niske forsterkningsmidler eller fyllstoff så som glassfibre, metallpulvere, metall-salter eller silikater, for eksempel kaolin, talk, barytt, kvarts eller kritt, også pigmenter og fargestoffer. Anvendte emulgeringsmidler er generelt sett de sedvanlige ikke-ioniske, anioniske eller kationiske, organiske forbindelsene med lang-kjedete alkylradikaler.
Polykondensasjonen kan utføres porsjonsvis eller kontinuerlig, for eksempel i en ekstruder (se EP-A-355 760), på konvensjonelt vis.
Fibrene fremstilles generelt ved å spinne melaminharpiks ifølge foreliggende oppfinnelse på en konvensjonell måte, for eksempel etter tilsetning av et herdemiddel, vanligvis syrer som for eksempel maursyre, svovelsyre eller am-moniumklorid, ved romtemperatur i en rotorspinnende apparatur og deretter full-føre herdingen av de uforedlede fibrene i en oppvarmet atmosfære, eller å spinne i en oppvarmet atmosfære samtidig som vannet, som ble anvendt som oppløs-ningsmiddel, fordampes og så herde kondensatet. En slik prosess beskrives i detalj i DE-A-23 64 091.
Fibrene kan etter ønske få tilsatt opp til 25, fortrinnsvis opp til 10 vektprosent av sedvanlige fyllmidler, i særdeleshet de som er basert på silikater, så som glimmer, fargestoffer, pigmenter, metallpulvere og avglansningsmidler (delusterants), og deretter bli bearbeidet til de tilsvarende brannsikre teppene og ikke-vevde tekstiler.
Brannsikre tepper fremstilles vanligvis ved å konvertere fibrene til garn på en sedvanlig måte, for eksempel ved ullspinning (Ullmann's Enzyklopådie der Technischen Chemie, 4. utgave, Volum 23, "Textiltechnik"). Garnet har fortrinnsvis en lineær tetthet innenfor grensene fra 100 til 200, særlig foretrukket fra 140 til 160, tex. Garnet blir deretter vanligvis vevd på ven konvensjonell måte til vevinger (wovens) med en basisvekt innenfor grensene fra 70 til 900, fortrinnsvis fra 120 til 500, g/m<2>.
De brannsikre teppene i foreliggende oppfinnelse kan også fremstilles fra ikke-vevde fiberflettverk (fiber web). Generelt tilveiebringes ikke-vevde tekstiler ved å bearbeide fibrene i tverrlag på formduker (webbers). De har fortrinnsvis en basisvekt som varierer fra 30 til 600 g/m<2>, foretrukket fra 50 til 450 g/m<2>.
Ifølge oppfinnelsen er det også mulig å fremstille brannsikre tepper fra fiberblandinger som omfatter i det vesentlige fra 4,9 til 95 vektprosent, fortrinnsvis fra 25 til 90 vektprosent, særlig foretrukket fra 40 til 75 vektprosent, melaminharpiksfibre og fra 0 til 90,1 vektprosent, fortrinnsvis fra 5 til 70 vektprosent, særlig foretrukket fra 15 til 50 vektprosent, flammebestandige fibre. Som allerede nevnt, kan disse fiberblandingene i tillegg omfatte fra 4,9 til 95 vektprosent, fortrinnsvis fra 5 til 50 vektprosent, i særdleshet fra 5 til 45 vektprosent, av normalt brennbare fibre valgt fra gruppen bestående av ull, bomull, polyamidfibre, polyesterfibre og viskose.
De flammebestandige fibrene er fortrinnsvis glassfibre, karbonfibre, flammebestandig ull, flammebestandig viskose og i særdeleshet aramidfibre. Aramidfibre fremstilles fortrinnsvis ved å spinne oppløsninger av polykondensa-sjonsprodukter av iso- eller tereftalinsyre (ephthalic acid) eller derivater av disse, som for eksempel sure klorider, med para- eller meta-fenylendiamin (phenylene-diamine) i oppløsningsmidler som for eksempel N-metylpyrrolidon, heksametyl-fosforsyre-triamid, konsentrert svovelsyre eller vanlige blandinger av disse. De resulterende sammenhengende filamentfibrene blir deretter vanligvis kuttet til stapelfibre, med en tykkelse som generelt ligger innenfor spekteret fra 5 til 25 (am. Foretrukne amamidfibre er de som er basert på en isomer poly-p-fenylentereftal-amid.
Fiberblandingene bearbeides på en konvensjonell måte, for eksempel med anvendelse av sedvanlig fiberblandingsapparatur ifølge beskrivelse i Vliesstoffe, Georg Thieme Verlag. I en foretrukket utførelsesform, er det vanlig å begynne med utgangspunkt i stapelfibre som har en vanlig lengde fra 1 til 20 cm. Disse tilføres vanligvis via en transportør til en karde med stasjonær-topp (stationary-top card) og forblandes i denne. Generelt blir blandingen deretter fullført i en karde med valse-topp (roller-top card) for å tilveiebringe et vatt-lignende flettverk (web). Det vatt-lignende flettverket videreforedles deretter til garn eller ikke-vevde tekstiler.
De vevde eller ikke-vevde tekstilene skjæres deretter til de ønskede teppe-dimensjoner, som basert på erfaring pr. i dag kun avhenger av beregnet anvendelse. Til slutt føyes kantene på teppene sammen, vanligvis med anvendelse av søm.
Brannsikre tepper som omfatter et metallbelegg, enten direkte påført fiberet eller påført det ferdige tekstilet, erkarakterisert vedat varmen som passerer gjennom teppet hemmes, og at teppet således gir bedre varmebeskyttelse til gjenstandene som skal beskyttes.
I en ytterligere utførelsesform blir fibrene tilsatt salter, i særdeleshet silikater, men særlig foretrukket magnesiumaluminium-silikater, eller skum-utviklende stoffer ved impregnering, penselbestrykning eller lignende fremgangsmåter.
Ifølge oppfinnelsen anvendes de brannsikre teppene til slokking av branner, brennende gjenstander og personer.
Tekstilene ifølge foreliggende oppfinnelse anvendes videre til fremstilling av brannsikre tepper for å beskytte personer og gjenstander mot brann, slukkemidler og/eller forbrenningsprodukter ved å dekke til personene og gjenstandene, som skal beskyttes, med de brannsikre teppene ifølge oppfinnelsen. I tillegg er de brannsikre teppene ifølge oppfinnelsen egnet til å beskytte kunstgjenstander og/eller antikviteter. De er også anvendelige til beskyttelse av hus og containere på lastebiler, tog eller skip som inneholder lettantennelige stoffer, og likeledes tankbiler og gassbeholdere, elektrisk eller elektronisk utstyr, som for eksempel datamaskiner, terminaler, kontrollpaneler.
Tekstilene ifølge foreliggende oppfinnelse er også egnet for anvendelse som flammehemmende trekk til polstrede seter i biler, fly, jernbanevogner, osv.
Én fordel med de brannsikre teppene og de ikke-vevde artiklene fremstilt ifølge oppfinnelsen er at de brannsikre teppene og de ikke-vevde artiklene fremstilt ifølge oppfinnelsen ikke smelter ved oppvarming eller ved direkte kontakt med en brann eller flamme, og derfor ikke drypper, og at teppene og de ikke-vevde artiklene derfor også forblir form-stabile under varmepåvirkning. En videre fordel med de brannsikre teppene ifølge foreliggende oppfinnelse er at de gir effektiv beskyttelse mot vann og andre slukkemidler og mot forbrenningsprodukter, som for eksempel sot.
Eksempler
Eksempel 1:
Et tekstil bestående av 60 vektprosent melaminharpiksfibre og 40 vektprosent p-aramidfibre, og med en basisvekt på 220 g/m<2>, ble behandlet med en kommersielt tilgjengelig appretur av fluorkarboksylsyre ved å gjennombløte tekstilet med en væske omfattende 30 g/l Persistol"®" O (kommersielt tilgjengelig produkt fra BASF) og dessuten 3 g/l aluminiumsulfat og 1 g/l eddiksyre av 60% styrke. Væskeopptaket var 70 vektprosent. Tekstilet ble deretter tørket ved 130°C til et restfuktighets-innhold på fra 6 til 8 vektprosent og deretter varmet opp ved 150°C i 4 minutter.
Tekstilet ble testet med hensyn til hydrofobe egenskaper med anvendelse av sprøytetesten AATCC 22 og oppnådde en gradering (rating) på 70. Med hensyn til oljebestandighet, ble det oppnådd en AATCC 118 testgradering på 6.
Testing av de flammehemmende egenskapene:
Beskyttelsen som tilveiebringes av tekstilet ble testet på grunnlag av ret-ningslinjene "the Assessment of the Ignibility of Upholstered Seating by Smould-ering and Flaming Ignition Sources, British Standards BS 582:1990, Section 3, Crib 5 or Crib 7".
Til dette formål ble tekstilet strukket over en blokk av kommersielt tilgjengelig fleksibelt polyuretanskum uten flammehemmende midler (omtrent 95 vektdeler polyol, 50 vektdeler methylendiisocyanforbindelse, 5 vektdeler vann og kata-lysator) og utsatt for en krybbe (crib) 5 tenningskilde. Skummet ble ikke antent så lenge tenningskilden brant og til den slukket (omtrent 8 til 10 min.), og det oppsto heller ingen ulming eller glødeeffekter. Den samme testen ble gjentatt uten tekstilet ifølge foreliggende oppfinnelse. Polyuretanskummet antente spontant og ble fullstendig fortært av flammene.
I en ytterligere test ble tenningskilden slukket med vann etter 30 sekunder. En påfølgende undersøkelse av polyuretanskummet viste ingen spor etter vann.
Eksempel 2:
Det anvendte testtekstilet var et materiale bestående av et garn som om-fattet 60 vektprosent melaminharpiksfibre og 40 vektprosent p-aramidfibre. Tekstilet var i tillegg belagt på begge sider med en polyesterfilm aluminisert ved høyvakuum. Det således tilveiebragte materialet hadde en basisvekt på 725 g/m<2>.
Test av brannhemmingseffekten:
Tekstilet ifølge foreliggende oppfinnelse ble strukket over en blokk av fleksibelt polyuretanskum, som beskrevet i Eksempel 1, og deretter utsatt for en krybbe 7 tenningskilde. Skummet ble ikke antent selv etter å ha blitt utsatt for tenningskilden over lengere tid; det oppsto heller ingen ulming eller glødeeffekter. Testen ble gjentatt, bortsett fra at tenningskilden ble slukket med skum fra et kommersielt tilgjengelig brannslukningsapparat etter 60 sekunder. Brann-slukningsskummet trengte ikke igjennom materialet; polyuretanskummet ble ikke funnet å inneholde noen spor etter påvirkning av brann og heller ikke etter det påfølgende slokningstiltaket.
Eksempel 3:
En skumblokk av polyuretan ble dekket med en m-aramid nålefilt med en basisvekt på 200 g/m<2>, som beskrevet i Eksempel 1, og deretter utsatt for en krybbe 7 tenningskilde. Etter 30 sekunder ble tenningskilden slukket med vann. Nålefilten var gjennomvåt, og likeledes viste skummet spor etter vannet.

Claims (8)

1. Flammebestandige tekstiler, fortrinnsvis ikke-vevede tekstiler, basert på dets totalvekt omfattende (a) fra 4,9 til 95 vektprosent melaminharpiksfibre, (b) fra 0 til 90,1 vektprosent flammebestandige fibre valgt fra gruppen bestående av aramidfibre, karbonfibre, glassfibre, flammebestandig ull og flammebestandig viskose, og (c) fra 0 til 20 vektprosent fyllstoff, og videre omfatter (d) eventuelt fra 4,9 til 95 vektprosent normalt brennbare fibre; karakterisert vedat (e) fra 0,1 til 20 vektprosent av minst én varme-, olje-, jord- og/eller fuktighetsbestandig appretur, omfattende minst et én- eller tosidig metallbelegg, hvor tekstiler veves fra garn fremstilt på en sedvanlig måte.
2. Tekstiler ifølge krav 1, hvor de normalt brennbare fibrene i materialet velges fra gruppen bestående av ull, bomull, polyamidfibre, polyesterfibre og viskose.
3. Tekstiler ifølge kravene 1 eller 2, hvor materialets metallbelegg omfatter aluminium som hovedbestanddel.
4. Tekstiler ifølge ethvert av de foregående kravene, hvor det omfatter et vannavstøtende middel som appretur.
5. Tekstiler ifølge ethvert av de foregående kravene, hvor det omfatter et oljeavstøtende middel som appretur.
6. Tekstiler ifølge ethvert av de foregående kravene, hvor melaminharpiksfibrene i materialet kan tilveiebringes ved kondensasjon av en blanding som omfatter som vesentlige komponenter (A) fra 90 til 100 mol% av en blanding bestående i det vesentlige av (a) fra 30 til 100 mol% melamin og (b) fra 0 til 70 mol% av en substituert melamin etter den generelle formel I
hvorX<1>,X2 og X<3>hver er valgt fra gruppen bestående av -NH2, NHR<1>og NR1 R2, ogX<1>,X<2>og X<3>ikke alle må være -NH2, ogR<1>og R2 er valgt fra gruppen bestående av hydroksy-C2-C20-alkyl, hydroksy-C2-C4-alkyl-(oksa-C2-C4-alkyl)n, hvor n er fra 1 til 5, og amino-C2-Ci2-alkyl, eller blandinger av melamin I, og (B) fra 0 til 10 mol%, basert på (A) og (B), av fenoler som er usubstituerte eller substituerte med radikaler valgt fra gruppen bestående av Ci-C9-alkyl og hydroksyl, CrC4-alkaner substituert med to eller tre fenolgrupper, di(hydroksyfenyl) sulfoner, eller blandinger av disse fenolene, med formaldehyd eller formaldehyd-tilførende forbindelser i et molart forhold av melaminer til formaldehyd innenfor grensene fra 1 : 1,15 til 1 : 4,5.
7. Tekstiler ifølge ethvert av de foregående kravene, karakterisert vedat det omfatter som bestanddel b) aramidfibre som tilveiebringes ved polykondensasjon av iso- eller tereftalinsyre (ephthalic acid) med en meta- eller para-fenylendiamin.
8. Anvendelse av flammebestandige tekstiler, fortrinnsvis ikke-vevede tekstiler, basert på dets totalvekt omfattende (a) fra 4,9 til 95 vektprosent melaminharpiksfibre, (b) fra 0 til 90,1 vektprosent flammebestandige fibre valgt fra gruppen bestående av aramidfibre, karbonfibre, glassfibre, flammebestandig ull og flammebestandig viskose, og (c) fra 0 til 20 vektprosent fyllstoff, og videre omfatter (d) eventuelt fra 4,9 til 95 vektprosent normalt brennbare fibre og (e) fra 0,1 til 20 vektprosent av minst én varme-, olje-, jord- og/eller fuktighetsbestandig appretur, omfattende minst et én- eller tosidig metallbelegg, hvor tekstiler veves fra garn fremstilt på en sedvanlig måte, for fremstilling av brannsikre tepper eller klær.
NO19985060A 1996-05-02 1998-10-30 Flammebestandige tekstiler omfattende melaminharpiksfibre NO313594B1 (no)