MX2017001526A - Lamina de acero de alta resistencia y metodo para fabricar la misma. - Google Patents
Lamina de acero de alta resistencia y metodo para fabricar la misma.Info
- Publication number
- MX2017001526A MX2017001526A MX2017001526A MX2017001526A MX2017001526A MX 2017001526 A MX2017001526 A MX 2017001526A MX 2017001526 A MX2017001526 A MX 2017001526A MX 2017001526 A MX2017001526 A MX 2017001526A MX 2017001526 A MX2017001526 A MX 2017001526A
- Authority
- MX
- Mexico
- Prior art keywords
- steel sheet
- hot
- temperature
- rolled steel
- strength steel
- Prior art date
Abstract
Se describe un método que comprende: preparar una plancha de acero con una composición química predeterminada; someter la plancha de acero a laminación en caliente al calentarla a una temperatura de 1100-1300°C, al laminarla en caliente con una temperatura de suministro de terminador de 800-1000°C para formar una lámina de acero laminada en caliente, y al bobinar la lámina de acero en una temperatura de bobinado media de 200-500°C; al someter la lámina de acero al tratamiento de decapado; someter la lámina de acero a recocido al retener la lámina de acero en una temperatura de 740-840°C durante 10-900 s, después enfriar la lámina de acero a una velocidad de enfriamiento media de 5-50°C/s a una temperatura de detención de enfriamiento de mayor que 350°C y 550°C o menor, y retener la lámina de acero en un intervalo de temperatura de mayor que 350°C a 550°C durante 10 s o más.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2014161676 | 2014-08-07 | ||
PCT/JP2015/003946 WO2016021195A1 (ja) | 2014-08-07 | 2015-08-05 | 高強度鋼板およびその製造方法 |
Publications (1)
Publication Number | Publication Date |
---|---|
MX2017001526A true MX2017001526A (es) | 2017-05-11 |
Family
ID=55263486
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2017001526A MX2017001526A (es) | 2014-08-07 | 2015-08-05 | Lamina de acero de alta resistencia y metodo para fabricar la misma. |
Country Status (6)
Country | Link |
---|---|
US (1) | US20170218475A1 (es) |
EP (1) | EP3187601B1 (es) |
JP (1) | JP5967320B2 (es) |
CN (1) | CN106574318B (es) |
MX (1) | MX2017001526A (es) |
WO (1) | WO2016021195A1 (es) |
Families Citing this family (18)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2016046582A1 (en) * | 2014-09-22 | 2016-03-31 | Arcelormittal | Bumper-reinforcing system for motor vehicle |
MX2018010791A (es) * | 2016-03-07 | 2019-02-07 | Jfe Steel Corp | Lamina de acero de alta resistencia y metodo para fabricar la misma. |
EP3412787B1 (en) * | 2016-03-11 | 2021-01-06 | JFE Steel Corporation | High-strength thin steel sheet and method for manufacturing same |
KR102128838B1 (ko) * | 2016-04-19 | 2020-07-02 | 제이에프이 스틸 가부시키가이샤 | 강판, 도금 강판 및, 그들의 제조 방법 |
MX2018012658A (es) * | 2016-04-19 | 2019-02-28 | Jfe Steel Corp | Lamina de acero, lamina de acero recubierta, y metodos para la fabricacion de las mismas. |
JP6524977B2 (ja) * | 2016-07-05 | 2019-06-05 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
WO2019020169A1 (de) * | 2017-07-25 | 2019-01-31 | Thyssenkrupp Steel Europe Ag | Blechbauteil, hergestellt durch warmumformen eines stahlflachprodukts und verfahren zu dessen herstellung |
WO2019106894A1 (ja) | 2017-11-29 | 2019-06-06 | Jfeスチール株式会社 | 高強度亜鉛めっき鋼板およびその製造方法 |
KR102020435B1 (ko) * | 2017-12-22 | 2019-09-10 | 주식회사 포스코 | 굽힘성 및 저온인성이 우수한 고강도 열연강판 및 이의 제조방법 |
JP6569745B2 (ja) | 2018-01-29 | 2019-09-04 | Jfeスチール株式会社 | コイルドチュービング用熱延鋼板およびその製造方法 |
US11473165B2 (en) | 2018-03-30 | 2022-10-18 | Jfe Steel Corporation | High-strength galvanized steel sheet, high strength member, and method for manufacturing the same |
US11560614B2 (en) | 2018-03-30 | 2023-01-24 | Jfe Steel Corporation | High-strength galvanized steel sheet, high strength member, and method for manufacturing the same |
JP6631760B1 (ja) | 2018-03-30 | 2020-01-15 | Jfeスチール株式会社 | 高強度亜鉛めっき鋼板および高強度部材 |
CN112867807B (zh) * | 2018-10-18 | 2023-04-21 | 杰富意钢铁株式会社 | 高延展性高强度电镀锌系钢板及其制造方法 |
EP3910087B1 (en) * | 2019-01-09 | 2023-04-05 | JFE Steel Corporation | High-strength cold-rolled steel sheet and production method for same |
CN115038807B (zh) * | 2020-06-08 | 2023-08-11 | 日本制铁株式会社 | 钢板及其制造方法 |
KR20230006895A (ko) * | 2020-06-08 | 2023-01-11 | 닛폰세이테츠 가부시키가이샤 | 강판 및 그 제조 방법 |
MX2023003464A (es) | 2020-09-30 | 2023-04-19 | Nippon Steel Corp | Lamina de acero. |
Family Cites Families (13)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH01272720A (ja) * | 1988-04-22 | 1989-10-31 | Kobe Steel Ltd | 高延性高強度複合組織鋼板の製造法 |
JP3475788B2 (ja) * | 1998-05-29 | 2003-12-08 | Jfeスチール株式会社 | 加工性の優れた高張力熱延鋼板の製造方法 |
JP5438302B2 (ja) * | 2008-10-30 | 2014-03-12 | 株式会社神戸製鋼所 | 加工性に優れた高降伏比高強度の溶融亜鉛めっき鋼板または合金化溶融亜鉛めっき鋼板とその製造方法 |
JP5786316B2 (ja) * | 2010-01-22 | 2015-09-30 | Jfeスチール株式会社 | 加工性および耐衝撃特性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
JP5488129B2 (ja) * | 2010-03-31 | 2014-05-14 | 新日鐵住金株式会社 | 冷延鋼板およびその製造方法 |
JP5018934B2 (ja) * | 2010-06-29 | 2012-09-05 | Jfeスチール株式会社 | 加工性に優れた高強度鋼板およびその製造方法 |
JP5408382B2 (ja) * | 2011-03-28 | 2014-02-05 | 新日鐵住金株式会社 | 熱延鋼板及びその製造方法 |
JP5825119B2 (ja) * | 2011-04-25 | 2015-12-02 | Jfeスチール株式会社 | 加工性と材質安定性に優れた高強度鋼板およびその製造方法 |
MX363038B (es) * | 2011-07-06 | 2019-03-01 | Nippon Steel & Sumitomo Metal Corp | Metodo para producir hoja de acero laminada en frio. |
JP5365673B2 (ja) * | 2011-09-29 | 2013-12-11 | Jfeスチール株式会社 | 材質均一性に優れた熱延鋼板およびその製造方法 |
KR101618477B1 (ko) * | 2011-10-04 | 2016-05-04 | 제이에프이 스틸 가부시키가이샤 | 고강도 강판 및 그 제조 방법 |
KR101359281B1 (ko) * | 2011-12-20 | 2014-02-06 | 주식회사 포스코 | 점용접성, 강도 및 연신율이 우수한 자동차용 강판 및 그 제조방법 |
JP5632947B2 (ja) * | 2012-12-12 | 2014-11-26 | 株式会社神戸製鋼所 | 加工性と低温靭性に優れた高強度鋼板およびその製造方法 |
-
2015
- 2015-08-05 WO PCT/JP2015/003946 patent/WO2016021195A1/ja active Application Filing
- 2015-08-05 JP JP2015558684A patent/JP5967320B2/ja active Active
- 2015-08-05 EP EP15829318.3A patent/EP3187601B1/en active Active
- 2015-08-05 US US15/500,446 patent/US20170218475A1/en not_active Abandoned
- 2015-08-05 MX MX2017001526A patent/MX2017001526A/es unknown
- 2015-08-05 CN CN201580041527.1A patent/CN106574318B/zh active Active
Also Published As
Publication number | Publication date |
---|---|
WO2016021195A1 (ja) | 2016-02-11 |
EP3187601A1 (en) | 2017-07-05 |
EP3187601B1 (en) | 2019-01-09 |
CN106574318B (zh) | 2019-01-08 |
EP3187601A4 (en) | 2017-07-05 |
JPWO2016021195A1 (ja) | 2017-04-27 |
US20170218475A1 (en) | 2017-08-03 |
JP5967320B2 (ja) | 2016-08-10 |
CN106574318A (zh) | 2017-04-19 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
MX2017001526A (es) | Lamina de acero de alta resistencia y metodo para fabricar la misma. | |
MX2017001527A (es) | Lamina de acero de alta resistencia y metodo para fabricar la misma. | |
JP2016529392A5 (es) | ||
HRP20210247T1 (hr) | Postupak proizvodnje lima od silicijskog čelika neorijentiranog zrna koji sadrži kositar | |
IN2015DN00613A (es) | ||
JP2015516503A5 (es) | ||
IN2015DN00610A (es) | ||
RU2014132737A (ru) | Способ изготовления горячекатаной кремнистой стали | |
MX363038B (es) | Metodo para producir hoja de acero laminada en frio. | |
IN2012DN00945A (es) | ||
IN2015DN00612A (es) | ||
ZA202002478B (en) | Cold rolled and heat treated steel sheet, method of production thereof and use of such steel to produce vehicle parts | |
ZA202103425B (en) | Cold rolled and annealed steel sheet, method of production thereof and use of such steel to produce vehicle parts | |
WO2016035345A8 (ja) | 方向性電磁鋼板の製造方法および窒化処理設備 | |
MY174492A (en) | Steel sheet for crown cap, method for manufacturing same, and crown cap | |
PT3754034T (pt) | Tratamento térmico de tira de aço laminada a frio | |
MX368535B (es) | Tren de laminacion de bandas de laminacion en caliente de aluminio y procedimiento para laminar en caliente una banda de laminacion en caliente de aluminio. | |
ZA201903188B (en) | Cold rolled and heat treated steel sheet, method of production thereof and use of such steel to produce vehicle parts | |
FI20195052A1 (fi) | Menetelmä ruostumattomien teräsnauhojen valmistamiseksi | |
IN2015KN00599A (es) | ||
WO2016001888A3 (en) | Multipurpose processing line for heat treating and hot dip coating a steel strip | |
PT3754035T (pt) | Método de tratamento térmico de uma tira de aço laminada a frio | |
PT3754037T (pt) | Método de tratamento térmico de uma tira de aço laminada a frio de alta resistência | |
EP3231523A4 (en) | Heat treatment method for ahss hot rolled coils, and cold rolling method using same and heat treatment apparatus | |
MX2016012711A (es) | Instalacion y procedimiento para el decapado y recubrimiento metalico de una banda metalica. |