MA44134B1 - Procédé de production d'une tôle d'acier présentant une résistance, une ductilité et une aptitude au formage améliorées - Google Patents

Procédé de production d'une tôle d'acier présentant une résistance, une ductilité et une aptitude au formage améliorées

Info

Publication number
MA44134B1
MA44134B1 MA44134A MA44134A MA44134B1 MA 44134 B1 MA44134 B1 MA 44134B1 MA 44134 A MA44134 A MA 44134A MA 44134 A MA44134 A MA 44134A MA 44134 B1 MA44134 B1 MA 44134B1
Authority
MA
Morocco
Prior art keywords
sheet
steel sheet
temperature
producing
segregation
Prior art date
Application number
MA44134A
Other languages
English (en)
Inventor
Hyun Jo Jun
Pavan Venkatasurya
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of MA44134B1 publication Critical patent/MA44134B1/fr

Abstract

Cette invention concerne un procédé de production d'une tôle d'acier possédant une microstructure constituée, en fraction de surface, de 20 à 50 % de ferrite intercritique, 10 à 20 % d'austénite résiduelle, 25 à 45 % de martensite revenue, 10 à 20 % de martensite fraîche, et de bainite, la somme de la martensite revenue et de la bainite étant comprise entre 30 et 60 %, le procédé comprenant les étapes successives suivantes : - la fourniture d'une tôle d'acier laminée à froid, la composition chimique de l'acier contenant, en % en poids : 0,18 % = c = 0,25 %, 0,9 % = si = 1,8 %, 0,02 % = al = 1,0 %, où 1,00 % = si + al = 2,35 %, 1,5 % = mn = 2,5 %, 0,010 % = nb = 0,035 %, 0,10 % = cr = 0,40 %, le reste étant du fe et les inévitables impuretés, - le recuit de la tôle d'acier à une température de recuit ta et pendant une durée de recuit ta, de manière à obtenir une structure comprenant de 50 à 80 % d'austénite et de 20 à 50 % de ferrite, - la trempe de la tôle à une vitesse de refroidissement comprise entre 20 et 50 °c/s jusqu'à une température de trempe qt comprise entre ms-50 °c et ms-5 °c, - le réchauffement la tôle jusqu'à une température de ségrégation pt comprise entre 375 et 450 °c et le maintien de la tôle à la température de ségrégation pt pendant un temps de ségrégation pt d'au moins 50 s., et - le refroidissement de la tôle à la température ambiante.
MA44134A 2015-12-21 2016-12-21 Procédé de production d'une tôle d'acier présentant une résistance, une ductilité et une aptitude au formage améliorées MA44134B1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
PCT/IB2015/059837 WO2017109538A1 (fr) 2015-12-21 2015-12-21 Procédé de production d'une tôle d'acier présentant une résistance, une ductilité et une aptitude au formage améliorées
PCT/EP2016/082192 WO2017108956A1 (fr) 2015-12-21 2016-12-21 Procédé de production d'une tôle d'acier présentant une résistance, une ductilité et une aptitude au formage améliorées

Publications (1)

Publication Number Publication Date
MA44134B1 true MA44134B1 (fr) 2020-06-30

Family

ID=55273296

Family Applications (2)

Application Number Title Priority Date Filing Date
MA49585A MA49585B1 (fr) 2015-12-21 2016-12-21 Procédé de production d'une tôle d'acier présentant une résistance, une ductilité et une aptitude au formage améliorées
MA44134A MA44134B1 (fr) 2015-12-21 2016-12-21 Procédé de production d'une tôle d'acier présentant une résistance, une ductilité et une aptitude au formage améliorées

Family Applications Before (1)

Application Number Title Priority Date Filing Date
MA49585A MA49585B1 (fr) 2015-12-21 2016-12-21 Procédé de production d'une tôle d'acier présentant une résistance, une ductilité et une aptitude au formage améliorées

Country Status (15)

Country Link
US (1) US20190003005A1 (fr)
EP (2) EP3394296B1 (fr)
JP (1) JP6935420B2 (fr)
KR (1) KR102618089B1 (fr)
CN (1) CN108513591B (fr)
BR (1) BR112018012131B1 (fr)
CA (1) CA3008067C (fr)
ES (2) ES2780924T3 (fr)
HU (2) HUE056674T2 (fr)
MA (2) MA49585B1 (fr)
MX (1) MX2018007648A (fr)
PL (2) PL3394296T3 (fr)
RU (1) RU2716920C2 (fr)
WO (2) WO2017109538A1 (fr)
ZA (1) ZA201803917B (fr)

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107597962A (zh) * 2017-08-15 2018-01-19 上海交通大学 一种热冲压与模具修边的集成工艺
WO2019122964A1 (fr) * 2017-12-19 2019-06-27 Arcelormittal Tôle d'acier présentant une ténacité, une ductilité et une résistance excellentes, et son procédé de fabrication
WO2019122961A1 (fr) 2017-12-19 2019-06-27 Arcelormittal Tôle d'acier à haute résistance et haute aptitude au formage et son procédé de fabrication
WO2020058748A1 (fr) * 2018-09-20 2020-03-26 Arcelormittal Tôle d'acier laminée à froid et revêtue et son procédé de fabrication
CA3149331A1 (fr) * 2019-08-07 2021-02-11 United States Steel Corporation Produits en tole d'acier zinguee a ductilite elevee
WO2021123889A1 (fr) * 2019-12-19 2021-06-24 Arcelormittal Feuille d'acier laminée à chaud et traitée thermiquement et son procédé de fabrication

Family Cites Families (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20060011274A1 (en) * 2002-09-04 2006-01-19 Colorado School Of Mines Method for producing steel with retained austenite
FR2850671B1 (fr) * 2003-02-05 2006-05-19 Usinor Procede de fabrication d'une bande d'acier dual-phase a structure ferrito-martensitique, laminee a froid et bande obtenue
EP1749895A1 (fr) * 2005-08-04 2007-02-07 ARCELOR France Procédé de fabrication de tôles d'acier présentant une haute résistance et une excellente ductilité, et tôles ainsi produites
JP5418047B2 (ja) * 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
US10023947B2 (en) * 2009-11-30 2018-07-17 Nippon Steel & Sumitomo Metal Corporation High strength steel plate with ultimate tensile strength of 900 MPa or more excellent in hydrogen embrittlement resistance and method of production of same
JP5333298B2 (ja) * 2010-03-09 2013-11-06 Ｊｆｅスチール株式会社 高強度鋼板の製造方法
KR20130036763A (ko) * 2010-08-12 2013-04-12 제이에프이 스틸 가부시키가이샤 가공성 및 내충격성이 우수한 고강도 냉연 강판 및 그 제조 방법
BR112013024984B1 (pt) * 2011-03-28 2018-12-11 Nippon Steel & Sumitomo Metal Corporation chapa de aço laminada a quente e método de produção da mesma
WO2012168564A1 (fr) * 2011-06-07 2012-12-13 Arcelormittal Investigación Y Desarrollo Sl Tôle d'acier laminée à froid et revêtue de zinc ou d'alliage de zinc, procédé de fabrication et utilisation d'une telle tôle
CA2850045C (fr) * 2011-09-30 2016-04-12 Nippon Steel & Sumitomo Metal Corporation Feuille d'acier galvanisee et son procede de fabrication
EP2762592B1 (fr) * 2011-09-30 2018-04-25 Nippon Steel & Sumitomo Metal Corporation Feuille d'acier galvanisée par immersion à chaud à haute résistance et feuille d'acier galvanisée par immersion à chaud alliée à haute résistance, chacun ayant une résistance à la traction de 980 mpa ou plus, une excellente adhésion de placage, une excellente aptitude au formage et d'excellentes propriétés d'expansion des trous et leur procédé de fabrication
JP5953695B2 (ja) * 2011-09-30 2016-07-20 新日鐵住金株式会社 めっき密着性と成形性に優れた高強度溶融亜鉛めっき鋼板とその製造方法
EP2765212B1 (fr) * 2011-10-04 2017-05-17 JFE Steel Corporation Tôle d'acier à haute résistance et procédé de fabrication associé
JP5348268B2 (ja) * 2012-03-07 2013-11-20 Ｊｆｅスチール株式会社 成形性に優れる高強度冷延鋼板およびその製造方法
WO2014020640A1 (fr) * 2012-07-31 2014-02-06 Ｊｆｅスチール株式会社 Tôle d'acier galvanisée par immersion à chaud à résistance élevée qui présente une excellente aptitude au moulage et une excellente aptitude à la fixation de formes, ainsi que procédé de fabrication de cette dernière
CN102952996A (zh) * 2013-01-04 2013-03-06 鞍钢股份有限公司 一种高延伸率冷轧trip钢板及其制备方法
US20160017472A1 (en) * 2013-03-11 2016-01-21 Tata Steel Ijmuiden Bv High strength hot dip galvanised complex phase steel strip
JP5728115B1 (ja) * 2013-09-27 2015-06-03 株式会社神戸製鋼所 延性および低温靭性に優れた高強度鋼板、並びにその製造方法
EP3167092B1 (fr) * 2014-07-07 2018-03-28 Tata Steel IJmuiden BV Bande d'acier ayant une résistance élevée et une grande aptitude au formage, la bande d'acier ayant un revêtement à base de zinc par immersion à chaud

Also Published As

Publication number Publication date
EP3653737B1 (fr) 2021-10-27
EP3394296B1 (fr) 2020-02-12
HUE049063T2 (hu) 2020-09-28
RU2018122302A3 (fr) 2020-01-28
JP6935420B2 (ja) 2021-09-15
WO2017109538A1 (fr) 2017-06-29
KR20180096638A (ko) 2018-08-29
ES2899448T3 (es) 2022-03-11
CN108513591B (zh) 2020-04-28
BR112018012131B1 (pt) 2021-09-28
MA49585A (fr) 2021-04-28
ES2780924T3 (es) 2020-08-27
US20190003005A1 (en) 2019-01-03
WO2017108956A1 (fr) 2017-06-29
CN108513591A (zh) 2018-09-07
BR112018012131A2 (pt) 2018-12-04
EP3653737A1 (fr) 2020-05-20
PL3394296T3 (pl) 2020-08-10
RU2716920C2 (ru) 2020-03-17
CA3008067A1 (fr) 2017-06-29
ZA201803917B (en) 2019-02-27
MX2018007648A (es) 2018-09-21
PL3653737T3 (pl) 2022-02-07
KR102618089B1 (ko) 2023-12-26
RU2018122302A (ru) 2019-12-25
EP3394296A1 (fr) 2018-10-31
MA49585B1 (fr) 2021-10-29
HUE056674T2 (hu) 2022-02-28
CA3008067C (fr) 2023-09-05
JP2019505692A (ja) 2019-02-28

Similar Documents

Publication Publication Date Title
MA44120B1 (fr) Procédé pour la production d'une tôle d'acier à haute résistance ayant une ductilité et une aptitude au formage améliorées et tôle d'acier ainsi obtenue
MA44134B1 (fr) Procédé de production d'une tôle d'acier présentant une résistance, une ductilité et une aptitude au formage améliorées
MA44107B1 (fr) Procédé de fabrication d'une tôle d'acier à haute résistance présentant une ductilité et une formabilité améliorées et tôle d'acier obtenue par ce procédé
MA44136B1 (fr) Procédé de production d'une tôle d'acier revêtue de haute résistance présentant une ductilité et une aptitude au formage améliorées, et tôle d'acier revêtue ainsi obtenue
MA49159B1 (fr) Procédé de production d'une tôle d'acier à haute résistance présentant une résistance et une aptitude au formage améliorées et tôle d'acier à haute résistance ainsi obtenue
JP6306711B2 (ja) 耐遅れ破壊特性を有するマルテンサイト鋼および製造方法
US9976205B2 (en) Steel, sheet steel product and process for producing a sheet steel product
RU2659549C2 (ru) Горячеформованный элемент и способ его изготовления
EP3556894B1 (fr) Tôle d'acier de résistance ultra-élevée présentant une excellente pliabilité et son procédé de fabrication
RU2550682C1 (ru) Способ изготовления сверхпрочной мартенситной стали и лист, полученный этим способом
CA2935638C (fr) Element forme a chaud et procede de fabrication associe
RU2016110765A (ru) Высокотвердая горячекатаная стальная продукция и способ ее производства
RU2009145940A (ru) Способ изготовления высокопрочных холоднокатаных и отожженных стальных листов и листы, полученные этим способом
CN100510141C (zh) 耐氢脆化特性优良的超高强度薄钢板
MA49777B1 (fr) Procédé de production d'une tôle d'acier à haute résistance présentant une résistance et une aptitude au formage améliorées et tôle ainsi obtenue
KR102222904B1 (ko) 강판
JP5867278B2 (ja) 常中温域での成形性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法
MA47181A (fr) Procédé de fabrication d'une tôle d'acier à ultra-haute résistance revêtue et tôle obtenue
US20160319393A1 (en) Rolled material for high strength spring, and wire for high strength spring using the same
AU2014265214A1 (en) High strength steel exhibiting good ductility and method of production via quenching and partitioning treatment by zinc bath
MX2017000185A (es) Metodo para la fabricacion de una hoja de acero de alta resistencia que tiene formabilidad y ductilidad mejoradas y hoja obtenida.
MA40197A (fr) Procédé de production d'une tôle d'acier revêtue à haute résistance ayant une résistance et une aptitude au formage améliorées
JP2023182698A (ja) 熱間圧延鋼及びその製造方法
US20230287531A1 (en) Heat treated cold rolled steel sheet and a method of manufacturing thereof
JP6037087B1 (ja) 高強度冷延鋼板およびその製造方法