KR970006389A - 열가소성 에라스토머 (elastomer) 조성물 및 그의 제조방법 - Google Patents
열가소성 에라스토머 (elastomer) 조성물 및 그의 제조방법 Download PDFInfo
- Publication number
- KR970006389A KR970006389A KR1019960030270A KR19960030270A KR970006389A KR 970006389 A KR970006389 A KR 970006389A KR 1019960030270 A KR1019960030270 A KR 1019960030270A KR 19960030270 A KR19960030270 A KR 19960030270A KR 970006389 A KR970006389 A KR 970006389A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- elastomer composition
- component
- thermoplastic elastomer
- Prior art date
Abstract
액상 1,2-폴리부타디엔과 EPDM고무, 폴리올레핀 수지, 페놀수지와 퍼옥사이드 가교제의 혼합 가교시스템, 및 가교조제로 이루어지며, 1,2-폴리부타디엔과 EPDM고무는 적어도 부분적으로 가교되어 있는 물성과 탄성, 내열성 등의 균형있는 물성을 보유함은 물론 고온에서의 내유성 및 가공성에 있어서 우수한 효과를 나타내는 열가소성 에라스토머 조성물 및 그의 제조방법에 관한 것이다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (25)
- ⒜ 모노머의 단위의 적어도 70%가 1,2-비닐 단위인 복수의 모노머 단위로 된 중합체이고, 분자량이 1,000~7,000범위인 액상 1,2-폴리부타디엔 2~40중량부, ⒝ 에틸렌 프로필렌 디엔 삼원 공중합체(EPDM)고무 60~98중량부, ⒞ 상기 ⒜ 및 ⒝성분 100중량부에 대하여 폴리올레핀 수지 10~90중량부, ⒟ 상기 ⒜ 및 ⒝성분 100중량부에 대하여 페놀수지 1~5중량부와 상기 ⒜ 및 ⒝성분 100중량부에 대하여 퍼옥사이드 0.05~3중량부로 이루어진 경화시스템 1.05~8중량부; 및 ⒠ 상기 ⒜ 및 ⒝성분 100중량부에 대하여 가교조제 0.5~5중량부로 이루어지고, 170~250℃의 온도에서 1,2-폴리부타디엔과 EPDM고무가 적어도 부분적으로 동적가교된 것을 특징으로 하는 열가소성 에라스토머 조성물.
- 제1항에 있어서, 상기 1,2-폴리부타디엔은 85% 이상의 1,2-비닐 단위로 이루어져 있고 분자량이 1,500~3,500임을 특징으로 하는 열가소성 에라스토머 조성물.
- 제1항에 있어서, 상기 EPDM고무는 에틸렌 프로필렌 에틸리덴노보넨 삼원 공중합체 고무임을 특징으로 하는 열가소성 에라스토머 조성물.
- 제1항에 있어서, 상기 폴리올레핀 수지는 결정성 폴리프로필렌임을 특징으로 하는 열가소성 에라스토머 조성물.
- 제1항에 있어서, 상기 페놀수지는 할로겐화 페놀수지임을 특징으로 하는 열가소성 에라스토머 조성물.
- 제1항에 있어서, 상기 퍼옥사이드는 1,3-비스(t-부틸퍼옥시 이소프로필)벤젠임을 특징으로 하는 열가소성 에라스토머 조성물.
- 제1항에 있어서, 상기 가교조제는 트리메틸을 프로판 트리메틸 메타크릴레이트, 징크 디메타크릴레이트, 및 징크 디아크릴레이트로 이루어진 군으로부터 선택됨을 특징으로 하는 열가소성 에라스토머 조성물.
- 제1항에 있어서, 상기 1,2-폴리부타디엔 및 EPDM고무 100중량부에 대하여 무기충진제 10~250중량부가 더욱 포함됨을 특징으로 하는 열가소성 에라스토머 조성물.
- 제8항에 있어서, 상기 무기충진제는 클레이, 탈크, 및 황산 바륨으로 이루어진 군으로부터 선택됨을 특징으로 하는 열가소성 에라스토머 조성물.
- 제1항에 있어서, 상기 EPDM고무 100중량부에 대하여 미네랄오일 20~200중량부가 더욱 포함됨을 특징으로 하는 열가소성 에라스토머 조성물.
- 제10항에 있어서, 상기 미네랄오일은 파라핀계 오일임을 특징으로 하는 열가소성 에라스토머 조성물.
- 1) ⒜ 모노머 단위의 적어도 70%가 1,2-비닐 단위인 복수의 모노머 단위로 된 폴리머이고, 분자량이 1,000~7,000범위인 액상 1,2-폴리부타디엔 2~40중량부와,⒝ 에틸렌 프로필렌 디엔 삼원 공중합체(EPDM)고무 60~98중량부, ⒞ ⒜ 및 ⒝성분 100중량부에 대하여 폴리올레핀 수지 10~90중량부, ⒟ ⒜ 및 ⒝성분 100중량부에 대하여 가교조제 0.5~5중량부를 170~250℃의 온도 범위에서 5~8분동안 혼련하여 펠렛형의 마스터배치를 제조하는 단계; 2) 1)의 마스터배치에 ⒜ 및 ⒝성분 100중량부에 대하여 페놀수지 1~5중량부를 첨가하여 170~250℃의 온도에서 혼련시키면서 ⒜ 및 ⒝성분을 부분가교시키는 단계; 및 3) 믹서 토크(torque)가 일정해지며, 상기 ⒜ 및 ⒝성분 100중량부에 대하여 퍼옥사이드 가교제 0.05~3중량부를 주입하여 ⒜ 및 ⒝성분을 더욱 가교시키고, 산화방지제 및 가공조제를 부가적으로 첨가하는 단계로 이루어진 것을 특징으로 하는 열가소성 에라스토머 조성물의 제조방법.
- 제12항에 있어서, 상기 1,2-폴리부타디엔은 85%이상의 1,2-비닐 단위로 이루어져 있고, 분자량이 1,500~3,500임을 특징으로 하는 열가소성 에라스토머 조성물의 제조방법.
- 제12항에 있어서, 상기 EPDM고무는 에틸렌 프로필렌 에틸리덴노보덴 삼원 공중합체 고무임을 특징으로 하는 열가소성 에라스토의 조성물의 제조방법.
- 제12항에 있어서, 상기 폴리올레핀 수지는 결정성 폴리프로필렌임을 특징으로 하는 열가소성 에라스토머 조성물의 제조방법.
- 제12항에 있어서, 상기 페놀수지는 할로겐화 페놀수지임을 특징으로 하는 열가소성 에라스토머 조성물의 제조방법.
- 제12항에 있어서, 상기 퍼옥사이드는 1,3-비스(t-부틸퍼옥시 이소프로필)벤젠임을 특징으로 하는 열가소성 에라스토머 조성물의 제조방법.
- 제12항에 있어서, 상기 가교조제는 트리메틸올 프로판 트리메틸 메타크릴레이트, 징크 디메타크릴레이트, 및 징크 디아크릴레이트로 이루어진 군으로부터 선택됨을 특징으로 하는 열가소성 에라스토머 조성물의 제조방법.
- 제12항에 있어서, 상기 1,2-폴리부타디엔 및 EPDM고무 100중량부에 대하여 무기충진제 10~250중량부가 더욱 포함됨을 특징으로 하는 열가소성 에라스토머 조성물의 제조방법.
- 제12항에 있어서, 상기 무기충진제는 클레이, 탈크, 및 황산 바륨으로 이루어진 군으로부터 선택됨을 특징으로 하는 열가소성 에라스토머 조성물의 제조방법.
- 제12항에 있어서, 상기 EPDM고무 100중량부에 대하여 미네랄오일 20~200중량부가 더욱 포함됨을 특징으로 하는 열가소성 에라스토머 조성물의 제조방법.
- 제21항에 있어서, 상기 미네랄오일은 파라핀계 오일임을 특징으로 하는 열가소성 에라스토머 조성물의 제조방법.
- 1) ⒜ 모노머의 단위의 적어도 70%가 1,2-비닐 단위인 복수의 모노머 단위로 된 폴리머이고, 분자량이 1,000~7,000범위인 액상 1,2-폴리부타디엔 2~40중량부와,⒝ 에틸렌 프로필렌 디엔 삼원 공중합체 (EPDM)고무 60~98중량부, ⒞ ⒜ 및 ⒝성분 100중량부에 대하여 폴리올레핀 수지 10~90중량부, ⒟ ⒜ 및 ⒝성분 100중량부에 대하여 폴리올레핀 수지 10~90중량부, ⒟ ⒜ 및 ⒝성분 100중량부에 대하여 가교조제 0.5~5중량부를 170~250℃의 온도범위에서 혼련하여 펠렛형의 마스터배치를 제조하는 단계; 2) 1)의 마스터배치를 175~250℃의 온도범위에서 용융및 혼합하는 단계: 및 3)믹서 토크가 일정해지며, ⒜ 및 ⒝성분 100중량부에 대해 페놀수지 1~5중량부와 상기 ⒜ 및 ⒝성분 100중량부에 대해 퍼옥사이드 가교제 0.05~3중량부를 동시에 주입하여 더욱 가교시키고, 산화방지제 및 가공조제를 부가적으로 첨가하는 단계로 이루어진 것을 특징으로 하는 열가소성 에라스토머 조성물의 제조방법.
- 제23항에 있어서, 상기 1,2-폴리부타디엔 및 EPDM고무 100중량부에 대하여 무기충진제 10~250중량부가 더욱 포함됨을 특징으로 하는 열가소성 에라스토머 조성물의 제조방법.
- 제23항에 있어서, 상기 EPDM고무 100중량부에 대하여 미네랄오일 20~200중량부가 더욱 포함됨을 특징으로 하는 열가소성 에라스토머 조성물의 제조방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.