KR950703663A - 코인용 스테인레스강 및 스테인레스강제 코인의 제조방법(staonless steel for coins and method for manufacturing stainless steel coins) - Google Patents
코인용 스테인레스강 및 스테인레스강제 코인의 제조방법(staonless steel for coins and method for manufacturing stainless steel coins) Download PDFInfo
- Publication number
- KR950703663A KR950703663A KR1019950700924A KR19950700924A KR950703663A KR 950703663 A KR950703663 A KR 950703663A KR 1019950700924 A KR1019950700924 A KR 1019950700924A KR 19950700924 A KR19950700924 A KR 19950700924A KR 950703663 A KR950703663 A KR 950703663A
- Authority
- KR
- South Korea
- Prior art keywords
- less
- stainless steel
- following formula
- content
- value
- Prior art date
Abstract
본발명은 코이닝 가공전은 연질이므로 가공성이 우수하여, 코이닝 가공후는 경도가 높고 또한 약자성을 나타내는, 특히 게임기용 코인을 제공함을 목적으로 하는 것으로, C : 0.03wt% 이하, Si : 0.1∼1.0wt%, Mn : 0.1∼4 wt%, Ni : 5∼15wt%, Cr : 12∼20 wt%, N : 0.03 wt% 이하, O : 50ppm이하를 함유하고, 필요에 따라 Cu : 0.5∼3.0 wt%, Mo : 0.1∼2.0 wt%중 적어도 1종을 함유하고 또한 오스테나이트계 안정화 지수(M치)가 20.0∼23.0의 범위내이고, 페라이트하율(F치)이 6이하인 코인용 스테인레스강 및 스테인레스강의 소재를 50%의 냉간압연, 900∼1100℃의 열처리를 실시한후, 15∼25%의 코이닝 가공을 실시하는 스테인레스강제 코인의 제조방법에 관한 것이다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 21% 코이닝 가공을 시행한 코인의 오스테나이트 안정화치수 M치와 흡인력과의 관계 표시도,
제2도는 21% 코이닝 흡인력의 편차와 페라이트화율 F치와의 관계 표시도이다.
Claims (12)
- C : 0.03wt% 이하, Si : 0.1∼1.0wt%이하, Mn : 0.1∼4 wt%이하, Ni : 5∼15wt%이하, Cr : 12∼20 wt%, N : 0.03 wt% 이하 및 O : 50ppm이하를 함유하고, 전부가 Fe 및 불가피한 불순물로 되고, 또한 하기(1)식;M=Ni + 12.6(C + N) + 0.35Si + 0.7Mn + 0.65Cr …………(1)로 표시되는 오스테아니트계 안정화지수(M치)가 20.0∼23.0의 범위내가 되도록 상기 각 성분의 함유량을 조정하여 코이닝 가공에 의해 약자성을 나타내게 되는 조성으로 한 것을 특징으로 하는 코인용 스테인레스강.
- C : 0.03wt% 이하, Si : 0.1∼1.0wt%이하, Mn : 0.1∼4 wt%이하, Ni : 5∼15wt%, Cr : 12∼20 wt%, N : 0.03 wt% 이하, O : 50ppm이하, Cu : 0.5∼3.0 wt%를 함유하고, 잔부가 Fe 및 불가피한 불순물로 이루어지고, 또한 하기(2)식;M=Ni + 12.6(C + N) + 0.35Si + 0.7Mn + 0.65Cr + 1.2Cu …………(2)로 표시되는 오스테아니트계 안정화지수(M치)가 20.0∼23.0의 범위내가 되도록 상기 각 성분의 함유량을 조정하여 코이닝 가공에 의해 약자성을 나타내게 되는 조성으로 한 것을 특징으로 하는 코인용 스테인레스강.
- C : 0.03wt% 이하, Si : 0.1∼1.0wt%이하, Mn : 0.1∼4 wt%이하, Ni : 5∼15wt%, Cr : 12∼20 wt%, N : 0.03 wt% 이하, O : 50ppm이하, Cu : 0.5∼3.0wt% 및 Mo : 0.1∼2.0wt%를 함유하고, 잔부가 Fe 및 불가피한 불순물로 되고, 또한 하기(3)식;M=Ni + 12.6(C + N) + 0.35Si + 0.7Mn + 0.65Cr + 1.2Cu + 0.98Mo ………(3)로 표시되는 오스테아니트계 안정화지수(M치)가 20.0∼23.0의 범위내가 되도록 상기 각 성분의 함유량을 조정하여 코이닝 가공에 의해 약자성을 나타내게 되는 조성으로 한 것을 특징으로 하는 코인용 스테인레스강.
- C : 0.03wt% 이하, Si : 0.1∼1.0wt%이하, Mn : 0.1∼4 wt%이하, Ni : 5∼15wt%, Cr : 12∼20 wt%, N : 0.03 wt% 이하 및 O : 50ppm이하를 함유하고, 잔부가 Fe 및 불가피한 불순물로 이루어지고, 또한 하기(1)식;M=Ni + 12.6(C + N) + 0.35Si + 0.7Mn + 0.65Cr …………(1)로 표시되는 오스테아니트계 안정화지수(M치)가 20.0∼23.0의 범위내가 되도록 상기 각 성분의 함유량을 조정하여 코이닝 가공에 의해 약자성을 나타내게 되는 조성으로 하고, 하기(4) 식;F = 2.9(Cr + 1.4Si) - (3.5Ni + 1.3Mn + 195C + 10N)-10.9 ……(4)로 표시되는 페라이트화율(F치)이 6이하가 되도록 상기 각 성분의 함유량을 조정한 것을 특징으로 하는 코인용 스테인레스강.
- C : 0.03wt% 이하, Si : 0.1∼1.0wt%이하, Mn : 0.1∼4 wt%이하, Ni : 5∼15wt%, Cr : 12∼20 wt%, N : 0.03 wt% 이하, O : 50ppm이하 및 Cu : 0.5∼3.0wt%를 함유하고, 잔부가 Fe 및 불가피한 불순물로 이루어지고, 또한 하기(2)식;M=Ni + 12.6(C + N) + 0.35Si + 0.7Mn + 0.65Cr + 1.2Cu …………(2)로 표시되는 오스테나이트계 안정화지수(M치)가 20.0∼23.0의 범위내가 되도록 상기 각 성분의 함유량을 조정하여 코이닝 가공에 의해 약자성을 나타내게 되는 조성으로 하고, 하기(5) 식;F = 2.9(Cr + 1.4Si) - (3.5Ni + 1.3Mn + 195C + 10N + 2.4Cu) - 10.9 …(5)로 표시되는 페라이트화율(F치)이 6이하가 되도록 상기 각 성분의 함유량을 조정한 것을 특징으로 하는 코인용 스테인레스강.
- C : 0.03wt% 이하, Si : 0.1∼1.0wt%이하, Mn : 0.1∼4 wt%이하, Ni : 5∼15wt%, Cr : 12∼20 wt%, N : 0.03 wt% 이하, O : 50ppm이하, Cu : 0.5∼3.0wt% 및 Mo : 0.1∼2.0wt%를 함유하고, 잔부가 Fe 및 불가피한 불순물로 되고, 또한 하기(3)식;M=Ni + 12.6(C + N) + 0.35Si + 0.7Mn + 0.65Cr + 1.2Cu + 0.98Mo ………(3)로 표시되는 오스테아니트계 안정화지수(M치)가 20.0∼23.0의 범위내가 되도록 상기 각 성분의 함유량을 조정하여 코이닝 가공에 의해 약자성을 나타내게 되는 조성으로 하고, 또한 하기(6) 식;F = 2.9(Cr + Mo + 1.4Si) - (3.5Ni + 1.3Mn + 195C + 10N + 2.4Cu) - 10.9 …(6)로 표시되는 페라이트화율(F치)이 6이하가 되도록 상기 각 성분의 함유량을 조정한 것을 특징으로 하는 코인용 스테인레스강.
- C : 0.03wt% 이하, Si : 0.1∼1.0wt%이하, Mn : 0.1∼4 wt%이하, Ni : 5∼15wt%, Cr : 12∼20 wt%, N : 0.03 wt% 이하 및 O : 50ppm이하를 함유하고, 잔부가 Fe 및 불가피한 불순물로 이루어지고, 또한 하기(1)식;M=Ni + 12.6(C + N) + 0.35Si + 0.7Mn + 0.65Cr …………(1)로 표시되는 오스테나이트계 안정화지수(M치)가 20.0∼23.0의 범위내가 되도록 상기 각 성분의 함유량을 조정한 스테인레스강을 가공율 50%이상의 냉간압연을 실시하고, 이어서 900∼1100℃에서 열처리한후 그 냉연강판을 펀칭가공에 의해 소정형상으로 하고, 그후, 압하율 15∼25%의 코이닝 가공을 실시하는 것을 특징으로 하는 스테인레스강제 코인의 제조방법.
- C : 0.03wt% 이하, Si : 0.1∼1.0wt%이하, Mn : 0.1∼4 wt%이하, Ni : 5∼15wt%, Cr : 12∼20 wt%, N : 0.03 wt% 이하, O : 50ppm이하 및 Cu : 0.5∼3.0wt%를 함유하고, 잔부가 Fe 및 불가피한 불순물로 이루어지고, 또한 하기(2)식;M=Ni + 12.6(C + N) + 0.35Si + 0.7Mn + 0.65Cr + 1.2Cu …………(2)로 표시되는 오스테나이트계 안정화지수(M치)가 20.0∼23.0의 범위내가 되도록 상기 각 성분의 함유량을 조정한 스테인레스강을 가공율 50%이상의 냉간압연을 실시하고, 이어서 900∼1100℃에서 열처리한후 그 냉연강판을 펀칭가공에 의해 소정 형상으로 하고, 그후, 압하율 15∼25%의 코이닝 가공을 실시하는 것을 특징으로 하는 스테인레스강제 코인의 제조방법.
- C : 0.03wt% 이하, Si : 0.1∼1.0wt%이하, Mn : 0.1∼4 wt%이하, Ni : 5∼15wt%, Cr : 12∼20 wt%, N : 0.03 wt% 이하, O : 50ppm이하, Cu : 0.5∼3.0wt% 및 Mo : 0.1∼2.0wt%를 함유하고, 잔부가 Fe 및 불가피한 불순물로 되고, 또한 하기(3)식;M=Ni + 12.6(C + N) + 0.35Si + 0.7Mn + 0.65Cr + 1.2Cu + 0.98Mo ………(3)으로 표시되는 오스테나이트계 안정화지수(M치)가 20.0∼23.0의 범위내가 되도록 상기 각 성분의 함유량을 조정하여 스테인레스강을 가공율 50%이상의 냉간압연을 실시하고 이어서 900∼1100℃에서 열처리하고, 그 냉연강판을 펀칭가공에 의해 소정 형상으로 하고, 그후, 압하율 15∼25%의 코이닝 가공을 실시하는 것을 특징으로 하는 스테인레스강제 코인의 제조방법.
- C : 0.03wt% 이하, Si : 0.1∼1.0wt%이하, Mn : 0.1∼4 wt%이하, Ni : 5∼15 wt%, Cr : 12∼20 wt%, N : 0.03 wt% 이하 및 O : 50ppm이하를 함유하고, 잔부가 Fe 및 불가피한 불순물로 이루어지고 또한 하기(4)식;F = 2.9(Cr + Mo + 1.4Si) - (3.5Ni + 1.3Mn + 195C + 10N) - 10.9 ……(4)로 표시되는 페라이트화율(F치)이 6이하가 되도록 상기 각 성분의 함유량을 조정한 스테인레스강을 가공율 50%이상의 냉간압연을 실시하고, 이어서 900∼1100℃에서 열처리한후, 그 냉연강판을 펀칭가공에 의해 소정 형상으로 하고, 그후, 압하율 15∼25%의 코이닝 가공을 실시하는 것을 특징으로 하는 스테인레스강제 코인의 제조방법.
- C : 0.03wt% 이하, Si : 0.1∼1.0wt%이하, Mn : 0.1∼4 wt%이하, Ni : 5∼15wt%, Cr : 12∼20 wt%, N : 0.03 wt% 이하, O : 50ppm이하, Cu : 0.5∼3.0wt%를 함유하고, 잔부가 Fe 및 불가피한 불순물로 이루어지고, 또한 하기(2)식;M = Ni + 12.6(C + N) + 0.35Si + 0.7Mn + 0.65Cr + 1.2Cu …………(2)로 표시되는 오스테아니트계 안정화지수(M치)가 20.0∼23.0의 범위내가 되도록 상기 각 성분의 함유량을 조정하고, 또한 하기(5) 식;F = 2.9(Cr + 1.4Si) - (3.5Ni + 1.3Mn + 195C + 10N + 2.4Cu) - 10.9 …(5)로 표시되는 페라이트화율(F치)이 6이하가 되도록 상기 각 성분의 함유량을 조정한 스테인레스강을 가공율 50%이상의 냉간압연을 실시하고 이어서 900∼1100℃에서 열처리하고, 그 냉연강판을 펀칭가공에 의해 소정 형상으로 하고, 그후, 압하율 15∼25%의 코이닝 가공을 실시하는 것을 특징으로 하는 스테인레스강제 코인의 제조방법.
- C : 0.03wt% 이하, Si : 0.1∼1.0wt%이하, Mn : 0.1∼4 wt%이하, Ni : 5∼15 wt%, Cr : 12∼20 wt%, N : 0.03 wt% 이하, O : 50ppm이하, Cu : 0.5∼3.0wt%및 MO : 0.1∼2.0wt%를 함유하고, 잔부가 Fe 및 불가피한 불순물로 되고, 또한 하기(3)식;M = Ni + 12.6(C + N) + 0.35Si + 0.7Mn + 0.65Cr + 1.2Cu + 0.98Mo …(3)로 표시되는 오스테아니트계 안정화지수(M치)가 20.0∼23.0의 범위내가 되도록 상기 각 성분의 함유량을 조정하고, 또한 하기(6) 식;F = 2.9(Cr + Mo +1.4Si)-(3.5Ni + 1.3Mn + 195C + 10N + 2.4Cu)-10.9 …(6)로 표시되는 페라이트화율(F치)이 6이하가 되도록 상기 각 성분의 함유량을 조정한 스테인레스강을 가공율 50%이상의 냉간압연을 실시하고 이어서 900∼1100℃에서 열처리하고, 그 냉연강판을 펀칭가공에 의해 소정 형상으로 하고, 그후, 압하율 15∼25%의 코이닝 가공을 실시하는 것을 특징으로 하는 스테인레스강제 코인의 제조방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.