KR940010090B1 - Process for producing thin glass film by sol-gel method - Google Patents

Process for producing thin glass film by sol-gel method Download PDF

Info

Publication number
KR940010090B1
KR940010090B1 KR1019910018796A KR910018796A KR940010090B1 KR 940010090 B1 KR940010090 B1 KR 940010090B1 KR 1019910018796 A KR1019910018796 A KR 1019910018796A KR 910018796 A KR910018796 A KR 910018796A KR 940010090 B1 KR940010090 B1 KR 940010090B1
Authority
KR
South Korea
Prior art keywords
thin film
hydrolysis solution
metal alkoxide
alcohol
film glass
Prior art date
Application number
KR1019910018796A
Other languages
Korean (ko)
Other versions
KR920007935A (en
Inventor
스미오 호시노
마스미 이또
히로오 카나모리
Original Assignee
스미도모덴기고오교오 가부시기가이샤
쿠라우찌 노리타카
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2285882A external-priority patent/JPH04160020A/en
Priority claimed from JP3148611A external-priority patent/JPH05805A/en
Priority claimed from JP3148610A external-priority patent/JPH054839A/en
Priority claimed from JP3178353A external-priority patent/JPH0523637A/en
Application filed by 스미도모덴기고오교오 가부시기가이샤, 쿠라우찌 노리타카 filed Critical 스미도모덴기고오교오 가부시기가이샤
Publication of KR920007935A publication Critical patent/KR920007935A/en
Application granted granted Critical
Publication of KR940010090B1 publication Critical patent/KR940010090B1/en

Abstract

내용 없음.No content.

Description

졸겔법에 의한 박막유리의 제조방법Method for manufacturing thin film glass by sol-gel method

본 발명은 졸겔법에 의한 박막유리의 제조방법을 개량한 것에 관한 것이다.This invention relates to the improvement of the manufacturing method of the thin film glass by a sol-gel method.

졸겔법은 금속알콕시드, 물, 알코올을 함유한 용액(이하, 가수분해이라 칭한다)에서 금속알콕시드를 가수분해하고 중축합반응을 하여 다공질체를 형성하고, 이 다공질체를 가열하여 유리체를 제조하는 것으로 이루어져 있다. 졸겔법은 가수분해액을 통해 유리를 생성하므로, 넓은 기판에 균일하게 유리를 도포하는 것을 용이하게 할 수 있다. 또한 졸겔법은 기계적, 화학적보호, 광학적특성의 새로운 기능을 가진 유리막을 기판에 도포하는 바람직한 방법이다.In the sol-gel method, metal alkoxides are hydrolyzed in a solution containing metal alkoxide, water and alcohol (hereinafter referred to as hydrolysis) and subjected to a polycondensation reaction to form a porous body. It consists of doing. Since the sol-gel method generates glass through the hydrolysis solution, it can easily apply the glass uniformly to a wide substrate. In addition, the sol-gel method is a preferable method for applying a glass film on a substrate with new functions of mechanical, chemical protection and optical properties.

예를 들면, "YOGYO KYOKAI-SHI(요업협회지)" 90(6), P328∼332(1952)에 기술되어 있는 바와 같이,졸겔법의 일반적인 방법은, 에틸실리케이트, 티타늄이소프로폭시드, 에탄올, 물 및 촉매로서 HCl을 혼합하여 가수분해액(도포액)을 제조하고, 가수분해액에 기판을 침지하여 일정한 속도로 기판을 끌어올려서 기판상에 가수분해액의 막을 형성하고, 형성된 막을 건조하고 가열하여 유리막을 형성하는 것이다.For example, as described in " YOGYO KYOKAI-SHI " 90 (6), P328-332 (1952), the general method of the sol-gel method is ethyl silicate, titanium isopropoxide, ethanol, HCl is mixed with water and a catalyst to prepare a hydrolysis solution (coating solution), the substrate is immersed in the hydrolysis solution, the substrate is pulled up at a constant rate to form a film of the hydrolysis solution on the substrate, and the formed film is dried and heated. To form a glass film.

지금까지, 졸겔법에 의해 두께 0.1∼3.0μm의 투명균일한 도포막을 형성할 수는 있었으나, 유리막의 두께를 0.3μm 이상으로 두껍게 형성할려고 시도하면, 유리막에 크랙, 백색혼탁, 기판으로부터의 박리등의 여러가지 결점이 나타난다. 한편, 막두께를 증가시키기 위하여, 중점제로서 글리세린 또는 에틸에테르를 부가하는 것이 공지되어 있으나, 중점제를 부가함으로서, 도달할 수 있는 최대막 두께는 0.5μm정도이다.Until now, the transparent uniform coating film having a thickness of 0.1-3.0 μm could be formed by the sol-gel method. However, when attempting to form a thick glass film thickness of 0.3 μm or more, cracks, white turbidity, peeling from the substrate, etc. Various drawbacks of On the other hand, in order to increase the film thickness, it is known to add glycerin or ethyl ether as the middle agent, but by adding the middle agent, the maximum film thickness that can be reached is about 0.5 μm.

본 발명의 제 1 목적은 졸겔법에 의해 막두께가 두꺼운 박막유리의 제조방법을 제공하는데 있다.A first object of the present invention is to provide a method for producing a thin film glass having a thick film by the sol-gel method.

본 발명의 제 2 목적은, 막두께를 바람직하게 제어할 수 있는 졸겔법에 의해 균일한 박막유리를 제조하는 방법을 제공하는데 있다.The 2nd object of this invention is to provide the method of manufacturing uniform thin film glass by the sol-gel method which can control a film thickness preferably.

본 발명에 따르면, 금속알콕시드, 물, 알코올 및 산을 함유한 가수분해액을 기판상에 도포하고, 암모니아와 알코올의 혼합물분위기에, 상기 기판상에 도포한 가수분해용액을 접촉시켜서 상기 금속알콕시드를 중축합반응시킨 후에 가열처리하여 박막유리를 형성하는 박막유리의 제조방법을 제공한다.According to the present invention, a hydrolysis solution containing a metal alkoxide, water, alcohol and acid is applied onto a substrate, and the hydrolysis solution applied on the substrate is brought into contact with a mixture atmosphere of ammonia and alcohol to give the metal alkoxy. Provided is a method for producing thin film glass, which is subjected to polycondensation reaction followed by heat treatment to form thin film glass.

종래의 졸겔법에 의하면, 도포된 막은 가열하는 동안 수축하여 고화된다. 이 단계에서, 중축합반응을 충분히 진행시키지 않으면, 막은 수축에 기인한 응력에 견디지 못하고, 특히 막두께가 두꺼울 경우에는 막은 균열하게 된다.According to the conventional sol-gel method, the applied film shrinks and solidifies during heating. At this stage, if the polycondensation reaction is not sufficiently advanced, the film cannot tolerate the stress due to shrinkage, and especially when the film thickness is thick, the film will crack.

본 발명에 따르면, 암모니아와 알코올 혼합물에 접촉시킴으로서 중축합반응을 촉진시킬 수 있기 때문에 두꺼운 막인 경우에도 수축에 기인한 응력에 견딜 수 있으므로 투명균일한 유리막을 얻을 수 있다. 즉, 암모니아와 알코올의 혼합물은 금속알콕시드의 중축합에 대한 촉매로서 작용하고, 그 양은 촉매량이 될 수 있다.According to the present invention, since the polycondensation reaction can be promoted by contacting the ammonia and alcohol mixture, even a thick film can withstand the stress caused by shrinkage, so that a transparent uniform glass film can be obtained. That is, the mixture of ammonia and alcohol serves as a catalyst for the polycondensation of metal alkoxides, the amount of which can be a catalytic amount.

본 발명의 제조방법에 사용되는 가수분해용액에 있어서, 알코올 및 물의 함유량은 낮아야 한다. 알코올과 금속알콕시드의 몰비율은 0.5 : 1 내지 5 : 1이고, 바람직하게는 1 : 1 내지 4 : 1이다. 물과 금속알콕시드의 몰비율은 1 : 1 내지 10 : 1이고, 바람직하게는 2 : 1 내지 5 : 1 이다.In the hydrolysis solution used in the production method of the present invention, the content of alcohol and water should be low. The molar ratio of the alcohol and the metal alkoxide is 0.5: 1 to 5: 1, and preferably 1: 1 to 4: 1. The molar ratio of water and metal alkoxide is 1: 1-1: 10, Preferably it is 2: 1-5: 1.

금속알콕시드로서, 종래에 사용된 알콕시드라면 어느것이든지 사용할 수 있다. 바람직한 예를 들면, 실리콘, 티타늄, 게르마늄, 알루미늄 및 보론의 메톡시드에톡시드 및 프로폭시드 등이 있다.As a metal alkoxide, any alkoxide used conventionally can be used. Preferred examples include methoxide and propoxides of silicon, titanium, germanium, aluminum and boron and the like.

또한, 알코올로서, 종래에 사용된 알코올이면 어느것이든지 사용할 수 있다. 예를 들면, 메탄올, 에탄올, 이소프로판올, 부탄올 등이 있다.Moreover, as alcohol, any alcohol used conventionally can be used. For example, methanol, ethanol, isopropanol, butanol and the like.

가수분해용액에 함유된 산은 금속알콕시드의 가수분해를 가속화시킨다. 산의 특정한 예를 들면 염산, 황산, 질산, 인산등이 있다.The acid contained in the hydrolysis solution accelerates the hydrolysis of the metal alkoxide. Specific examples of acids include hydrochloric acid, sulfuric acid, nitric acid, phosphoric acid, and the like.

용액의 PH를, 예를 들면 PH 1∼6으로 조정하기 위하여, 산의 양을 조절한다.In order to adjust the pH of the solution to, for example, PH 1 to 6, the amount of acid is adjusted.

가수분해액은, 기판에 대한 용액의 부착력을 개선하고 박막유리를 안정하게 형성하기 위하여, 계면활성제(예를 들면, 폴리에틸렌 글리콜 등의 고급알코올)를 함유하고 있다.The hydrolysis solution contains a surfactant (for example, higher alcohol such as polyethylene glycol) in order to improve the adhesion of the solution to the substrate and stably form the thin film glass.

가수분해용액에 회토류원소 또는 이들의 화합물, 혹은 비선형광학재료등을 첨가한다. 희토류원소 또는 이들 화합물의 예로, Er, Nd 또는 이들의 염이 있다. 이들 원소 혹은 화합물을 부가함으로서, 형성된 유리막은 레이저비임을 발생하는데 사용할 수 있다.A rare earth element, a compound thereof, or a nonlinear optical material is added to the hydrolysis solution. Examples of rare earth elements or these compounds include Er, Nd or salts thereof. By adding these elements or compounds, the formed glass film can be used to generate a laser beam.

비선형 광학재료의 예로는 P-NA 및 MNA등의 유기재료 또는 Cds, CuCl,PbS등의 반도체성 입자가 있다. 비선형 광학재료를 부가함으로서, 형성된 유리막은 광학적으로 비선형성을 가지고 있다.Examples of nonlinear optical materials include organic materials such as P-NA and MNA or semiconducting particles such as Cds, CuCl, and PbS. By adding a nonlinear optical material, the formed glass film has optical nonlinearity.

본 발명의 제조방법에 있어서, 기판에 부착한 가수분해용액을, 암모니아 및 알코올(예를들면, 메탄올, 에탄올, 이소프로판올 등)을 함유한 분위기에 접촉시키면서, 중축합반응을 행한다. 온도 및 압력은 실온 및 대기압이지만, 보다 높은 온도와 압력이 더욱 효과적이다. 중축합을 승온에서 행하면, 반응이 가속되어 막이 수축에 기인한 응력에 견딜 수 있게 된다. 그러나, 온도가 300℃ 이상으로 높아지면 용매의 증발현상이 현저해지므로, 중축합반응이 충분히 진행하기전에 막이 수축되어 균열하게 된다.In the production method of the present invention, the polycondensation reaction is carried out while the hydrolysis solution attached to the substrate is brought into contact with an atmosphere containing ammonia and alcohol (for example, methanol, ethanol, isopropanol, and the like). Temperatures and pressures are room temperature and atmospheric pressure, but higher temperatures and pressures are more effective. When the polycondensation is carried out at an elevated temperature, the reaction is accelerated so that the film can withstand the stress due to shrinkage. However, when the temperature rises above 300 ° C., the evaporation of the solvent becomes remarkable, so that the membrane shrinks and cracks before the polycondensation reaction proceeds sufficiently.

또한, 보다 높은 압력은 중축합을 촉진시키고, 용매의 증발현상을 방지하여 5기압까지는 효과가 증가하지만, 그 이상에서는 효과가 현저하게 증가하지 않는다. 또한, 상당히 높은 압력을 사용할 경우에는 설비가 대형화되고 복잡해진다.In addition, the higher pressure promotes polycondensation and prevents the evaporation of the solvent, increasing the effect up to 5 atm, but above that, the effect does not increase significantly. In addition, the use of significantly higher pressures makes the installation larger and more complex.

따라서, 중축합반응은 대기압∼5기압하의 실온∼300℃ 범위에서 바람직하게 진행된다.Therefore, the polycondensation reaction proceeds preferably in the room temperature to 300 degreeC under atmospheric pressure-5 atmospheres.

본 발명의 다른 공정은 종래의 졸겔법과 동일한 조건하에서 실행될 수 있다. 예를 들면, 가수분해액을 딥코우팅 또는 스핀코우팅으로 기판에 도포할 수 있다. 기판은 종래에 사용된 재료(예를 들면, 유리, 금속, 플라스틱)라면 어느것이든지 사용해도 된다.Other processes of the present invention can be carried out under the same conditions as the conventional sol-gel method. For example, the hydrolysis solution can be applied to the substrate by dip coating or spin coating. The substrate may be any material conventionally used (for example, glass, metal, plastic).

딥코우팅에서는, 기판을 가수분해액에 침지하여 기판표면에 가수분해액의 박막이 형성되도록 점차적으로 끌어올린다. 스핀코우팅에서는, 기판을 고속으로 회전할 수 있는 샘플호울더에 설치하고, 500∼5000rpm으로 회전하는 기판상에 가수분해액을 떨어뜨려서 기판표면상에 가수분해액의 균일한 박막을 형성시킨다.In deep coating, the substrate is immersed in the hydrolysis solution and gradually pulled up so that a thin film of the hydrolysis solution is formed on the surface of the substrate. In spin coating, the substrate is placed in a sample holder which can rotate at high speed, and the hydrolysis solution is dropped onto the substrate rotating at 500 to 5000 rpm to form a uniform thin film of the hydrolysis solution on the substrate surface.

바람직하게는, 가수분해액의 점도를 기판에 도포하기전에 증가시킨다.Preferably, the viscosity of the hydrolysis solution is increased before applying to the substrate.

바람직한 실시예에 있어서, 가수분해액을 실온에서 그 점도가 0.1∼10 포이즈로 조정되도록 숙성시켜 둔다. 가수분해액의 점도를 증가시킴으로서, 기판위의 가수분해액의 막두께를 용이하게 제어할 수 있다. 점도가 0.1포이즈 이하이면, 막두께는 증가하지 않고, 점도가 10 포이즈 이상이면 막표면이 불균일하여 최종적으로 형성된 유리막은 균일하지 않다. 점도는 숙성시간을 변경시킴으로 변경될 수 있다.In a preferred embodiment, the hydrolyzate is aged at room temperature so that its viscosity is adjusted to 0.1 to 10 poise. By increasing the viscosity of the hydrolysis solution, the film thickness of the hydrolysis solution on the substrate can be easily controlled. If the viscosity is 0.1 poise or less, the film thickness does not increase. If the viscosity is 10 poise or more, the film surface is nonuniform and the glass film finally formed is not uniform. The viscosity can be changed by changing the aging time.

바람직한 다른 실시예에 있어서, 가수분해액을 -150℃∼+10℃로 냉각시킨 다음 가수분해액과 동일한 온도 또는 그 이하로 냉각시킨 기판상에 도포한다.In another preferred embodiment, the hydrolysis solution is cooled to −150 ° C. to + 10 ° C. and then applied onto a substrate cooled to or below the same temperature as the hydrolysis solution.

냉각온도가 -150℃ 이하일때에는, 점도가 너무 커서 균일한 막을 형성할 수 없게 되며, 기판 온도가 냉각된 가수분해액보다 높을때에는, 도포된 가수분해액의 온도가 상승하여 점도가 떨어진다.When the cooling temperature is -150 ° C or lower, the viscosity is too large to form a uniform film. When the substrate temperature is higher than the cooled hydrolysis liquid, the temperature of the applied hydrolysis liquid rises and the viscosity drops.

바람직한 또다른 실시예에 있어서, 가수분해액에 감소된 압력을 가하면, 예를 들면 10 내지 500 Torr를 가하면, 알코올 등의 휘발성물질이 증발한다.In another preferred embodiment, when a reduced pressure is added to the hydrolyzate, for example, 10 to 500 Torr, volatiles such as alcohols evaporate.

가수분해액의 점도를 증가시킴으로서, 기판에 도포한 가수분해액의 막두께를 증가시킬 수 있다. 수축에 기인하여 형성된 막의 균열을 후속의 막의 가열시 방지할 수 있게 된다.By increasing the viscosity of the hydrolysis solution, the film thickness of the hydrolysis solution applied to the substrate can be increased. Cracks in the formed film due to shrinkage can be prevented upon subsequent heating of the film.

본 발명을 다음 실시예에 의해 보다 상세히 설명하나, 이 실시예는 본 발명의 범위를 제한하는 것은 아니다.The invention is illustrated in more detail by the following examples, which do not limit the scope of the invention.

[실시예 1]Example 1

비이커에 실리콘 에톡시드(50ml), 에탄올(20ml), 물(20ml), 12N-염산(0.6ml) 및 폴리에틸렌 글리콜 (4g)을 넣고서 약 30분동안 교반하여, 가수분해액을 얻은 다음 24시간 동안 실온에서 숙성시킨다.Add silicon ethoxide (50 ml), ethanol (20 ml), water (20 ml), 12N hydrochloric acid (0.6 ml) and polyethylene glycol (4 g) to the beaker and stir for about 30 minutes to obtain a hydrolysis solution and then for 24 hours Aged at room temperature.

소다리임실리카유리판(40mm(폭)×50mm(길이)×1mm(두께))을 기판으로 사용하고, 이 기판을 아세톤으로 세척한 다음, 기판상에 숙성된 가수분해액을 스핀코우팅하였다. 도포하기전에, 가수분해액의 점도는 4포이즈이다.A soda-limic silica glass plate (40 mm (width) x 50 mm (length) x 1 mm (thickness)) was used as a substrate, the substrate was washed with acetone, and then the hydrolyzate aged on the substrate was spin coated. Before application, the viscosity of the hydrolysis solution is 4 poises.

다음에, 가수분해액의 막이 형성된 기판을 60℃로 약 한시간동안 암모니아 및 에탄올의 혼합분위기(1 : 1의 체적비)에서 보존한 다음, 24시간동안 공기중 100℃에서 건조시키고, 공기중 500℃에서 가열하여 1.7μm의 두께를 가지는 고화된 투명유리막을 얻는다.Subsequently, the substrate on which the film of the hydrolysis solution was formed was stored at 60 ° C. for about one hour in a mixed atmosphere of ammonia and ethanol (volume ratio of 1: 1), and then dried at 100 ° C. in air for 24 hours, and 500 ° C. in air Heating to obtain a solidified transparent glass film having a thickness of 1.7 μm.

[실시예 2]Example 2

가수분해액을 -50℃ 또는 -100℃로 냉각시키고 기판을 -50℃ 또는 -100℃로 냉각시킨 것을 제외하고는 실시예 1과 동일한 방법으로, 가수분해액을 기판상에 스핀코우팅하고, 건조 및 가열하여 1.2μm의 두께를 가지는 투명한 박막유리를 얻는다.The hydrolysis solution was spin coated onto the substrate in the same manner as in Example 1 except that the hydrolysis solution was cooled to −50 ° C. or −100 ° C. and the substrate was cooled to −50 ° C. or −100 ° C. Drying and heating give a transparent thin film having a thickness of 1.2 μm.

[비교예 1]Comparative Example 1

가수분해액 및 기판을 모두 -180℃로 냉각시킨 것을 제외하고는 실시예 2와 동일한 방법으로, 박막유리를 형성하였지만 막표면이 균일하지 않았다.A thin film glass was formed in the same manner as in Example 2 except that both the hydrolyzate and the substrate were cooled to −180 ° C., but the film surface was not uniform.

[실시예 3]Example 3

비이커에, 실리콘에톡시드(50ml), 티타늄이소프로폭시드(1ml), 에탄올(10ml), 및 1N-염산(20ml)을 넣고 약 30분동안 교반하여 가수분해액을 얻은 다음, 15분동안 10Torr의 압력하에서 이 가수분해액을 농축시킨다.In a beaker, silicon ethoxide (50 ml), titanium isopropoxide (1 ml), ethanol (10 ml), and 1N hydrochloric acid (20 ml) were added and stirred for about 30 minutes to obtain a hydrolysis solution, followed by 15 minutes. The hydrolysis solution is concentrated under a pressure of 10 Torr.

다음에, 실시예 1과 동일한 방법으로, 농축된 가수분해액을 기판에 스핀코우팅한 다음, 건조하고 가열시켜서 1.5μm의 두께를 가지는 고화된 투명유리막을 얻었다.Next, in the same manner as in Example 1, the concentrated hydrolyzate was spin coated onto a substrate, then dried and heated to obtain a solidified transparent glass film having a thickness of 1.5 탆.

[실시예 4]Example 4

비이커에, 실리콘에톡시드(50ml), 에탄올(10ml), 1N -염산(20ml) 및 염화에르븀(900mg)을 넣은 다음 30분동안 교반하여 가수분해액을 얻었다.In a beaker, silicon ethoxide (50 ml), ethanol (10 ml), 1N hydrochloric acid (20 ml) and erbium chloride (900 mg) were added and stirred for 30 minutes to obtain a hydrolysis solution.

다음에, 석영기판을 가수분해액에 침지하고 일정속도로 끌어올려서 기판을 가수분해액으로 도포하였다. 도포된 가수분해액막을 가지는 기판을 실시예 1과 동일한 방법으로 처리하여 1μm의 두께를 가지는 에르븀이 도우프된 투명유리막을 얻었다.Next, the quartz substrate was immersed in the hydrolysis solution and pulled up at a constant speed to apply the substrate to the hydrolysis solution. The substrate having the applied hydrolysis liquid film was treated in the same manner as in Example 1 to obtain a transparent glass film doped with erbium having a thickness of 1 μm.

Claims (6)

금속알콕시드, 물, 알코올, 산 및 레이져발진작용을 나타내는 Er 또는 Nd의 희토류원소를 함유한 가수분해액을 -150℃∼10℃의 온도범위로 냉각시킨 다음, 상기 가수분해액의 냉각온도와 동일하거나 낮은 온도로 냉각시킨 기판상에 도포하고, 상기 도포된 가수분해액을 암모니아 및 알코올의 혼합물에 접촉시켜서 상기 금속알콕시드를 실온∼300℃, 대기압∼5기압하에서 중축합하고, 중축합된 금속알콕시드를 가열하여 박막유리를 형성하는 박막유리의 제조방법.The hydrolyzate containing metal alkoxide, water, alcohol, acid, and rare earth element of Er or Nd exhibiting laser oscillation is cooled to a temperature range of -150 ° C to 10 ° C, and then the cooling temperature of the hydrolysis solution and It is applied on a substrate cooled to the same or lower temperature, and the applied hydrolysis solution is brought into contact with a mixture of ammonia and alcohol to polycondense the metal alkoxide at room temperature to 300 DEG C and atmospheric pressure to 5 atmospheres, and polycondensed A method for producing thin film glass, wherein the alkoxide is heated to form thin film glass. 제 1 항에 있어서, 상기 가수분해액을 도포하기전에 가수분해액의 점성도를 0.1∼10포이즈로 조절하여 유지시키는 것을 특징으로 하는 박막유리의 제조방법.The method of manufacturing a thin film glass according to claim 1, wherein the viscosity of the hydrolysis solution is adjusted to 0.1 to 10 poises before the hydrolysis solution is applied. 제 1 항에 있어서, 상기 가수분해액을 도포하기전에 상기 용액을 농축시키기 위하여 감압상태에 놓는 것을 특징으로 하는 박막유리의 제조방법.The method of manufacturing a thin film glass according to claim 1, wherein the solution is placed under reduced pressure to concentrate the solution before applying the hydrolysis solution. 제 1 항에 있어서, 상기 알코올과 상기 금속알콕시드의 몰비는 0.5 : 1∼5 : 1이 되고, 물과 상기 알콕시드의 몰비는 1 : 1∼10 : 1이 되는 것을 특징으로 하는 박막유리의 제조방법.The molar ratio of the alcohol and the metal alkoxide is 0.5: 1 to 5: 1, and the molar ratio of water to the alkoxide is 1: 1 to 10: 1. Manufacturing method. 제 1 항에 있어서, 상기 금속알콕시드는, 실리콘, 티타늄, 게르마늄, 알루미늄 및 보론의 메톡시드, 에톡시드 및 프로폭시드를 함유하는 그룹으로부터 선택된 적어도 한개의 금속알콕시드인 것을 특징으로 하는 박막유리의 제조방법.The thin film glass according to claim 1, wherein the metal alkoxide is at least one metal alkoxide selected from the group containing methoxide, ethoxide and propoxide of silicon, titanium, germanium, aluminum and boron. Manufacturing method. 금속알콕시드, 물, 알코올, 산 및 비선형광학재료를 함유한 가수분해액을 -150℃∼10℃의 온도범위로 냉각시킨 다음, 상기 가수분해액의 냉각온도와 동일하거나 낮은 온도로 냉각시킨 기판상에 도포하고, 상기 도포된 가수분해액을 암모니아 및 알코올의 혼합물에 접촉시켜서 상기 금속알콕시드를 실온∼300℃, 대기압∼5기압하에서 중축합하고, 중축합된 금속알콕시드를 가열하여 박막유리를 형성하는 박막유리의 제조방법.A substrate containing a metal alkoxide, water, an alcohol, an acid, and a nonlinear optical material, cooled to a temperature range of -150 ° C to 10 ° C, and then cooled to a temperature equal to or lower than the cooling temperature of the hydrolysis solution. And the applied hydrolyzate is brought into contact with a mixture of ammonia and alcohol to polycondense the metal alkoxide at room temperature to 300 DEG C and atmospheric pressure to 5 atm, and heat the polycondensed metal alkoxide to heat the thin film glass. Method for producing thin film glass to form.
KR1019910018796A 1990-10-25 1991-10-25 Process for producing thin glass film by sol-gel method KR940010090B1 (en)