KR910020206A - 높은 강도, 높은 모듈러스, 낮은 수축률 합성사를 생성시키기 위한 방사 방법 - Google Patents
높은 강도, 높은 모듈러스, 낮은 수축률 합성사를 생성시키기 위한 방사 방법 Download PDFInfo
- Publication number
- KR910020206A KR910020206A KR1019910007573A KR910007573A KR910020206A KR 910020206 A KR910020206 A KR 910020206A KR 1019910007573 A KR1019910007573 A KR 1019910007573A KR 910007573 A KR910007573 A KR 910007573A KR 910020206 A KR910020206 A KR 910020206A
- Authority
- KR
- South Korea
- Prior art keywords
- filament
- compartment
- temperature
- spinneret
- filaments
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 방사 공정의 도식적 정면도이다, 제2도는 연신 공정의 도식적 정면도이다.
Claims (16)
- 중합체를 방사구금을 통해 압출시키고; 방사구금으로 부터의 필라멘트를 긴 구획을 통해 통과시키고; 필라멘트를, 구획내에 약 3m 또는 그 이상의 거리에 걸쳐 중합체의 유리전이 이상의 온도에서 유지시키고; 및 그후 필라멘트를 수렴시키는 단계를 구성된, 유기 합성 용융 방사성 중합체를 방사시키기 위한 방법.
- 제1항에 있어서, 수렴후 필라멘트를 권취시키는 단계가 포함되는 방법.
- 제1항에 있어서, 필라멘트가 3―20필라멘트당 스핀 데니어를 가도록 필라멘트를 방사구금으로부터 방사시키는 단계가 포함되는 방법.
- 제1항에 있어서, 필라멘트가 방사구금을 떠날 때 필라멘트를 뜨거운 기체로 퀀칭시키는 단계가 포함되는 방법.
- 제4항에 있어서, 필라멘트를 260℃ 이하의 온도를 갖는 뜨거운 기체로 퀀칭시키는 단계가 포함되는 방법.
- 제5항에 있어서, 필라멘트를 230℃ 온도를 갖는 뜨거운 기체로 퀀칭시키는 단계가 포함되는 방법.
- 제1항에 있어서, 구획내 온도가 중합체 방사 온도의 최대치에서 주위온도의 최소치까지 구획의 길이에 걸쳐 조절되는, 적어도 5m의 길이를 갖는 긴 구획을 통해, 방사구금으로 부터 필라멘트를 통과시키는 단계가 포함되는 방법.
- 제7항에 있어서, 구획내 온도가 방사구금 가까이 약 155℃에서 방사구금에서 멀리 약 50℃까지 조절되는 긴 구획을 통해 방사구금으로 부터 필라멘트를 통과시키는 단계가 포함되는 방법.
- 제8항에 있어서, 구획내 온도가 방사구금 가까이 약 155℃에서 방사구금에서 멀리 약 50℃까지 조절되고 상기 가까운 점과 먼 점간의 온도가 일반적으로 직선 방식으로 감소되는, 긴 구획을 통해 방사구금으로부터의 필라멘트를 통과시키는 단계가 포함되는 방법.
- 제1항에 있어서, 약 5―약 9m 범위의 길이를 갖는 긴 구획을 통해 방사구금으로부터의 필라멘트를 통과시키는 단계가 포함되는 방법.
- 제2항에 있어서, 분당 적어도 1525m(5,000ft)의 속도에서 필라멘트를 권취시키는 단계가 포함되는 방법.
- 제2항에 있어서, 분당 약 1525m(약 5000ft)―약 5795m(약 19000ft)의 속도에서 필라멘트를 권취시키는 단계가 포함되는 방법.
- 제2항에 있어서, 분당 약 3200m(약 10,500ft)―약 4120m(약 13,500ft)의 속도에서 필라멘트를 권취시키는 단계가 포함되는 방법.
- 제2항에 있어서, 방사구금 가까이의 첫 번째 부분에서 온도가 약 105℃―약110℃ 범위의 온도를 갖고; 첫 번째 구획 가까이의 두 번째 부분에서 온도가 약 110℃―약 115℃ 범위의 온도를 갖고; 두 번째 구획 가까이의 세 번째 부분에서 온도가 약 125℃―약 130℃ 범위의 온도를 가지며; 세 번째 구획 가까이의 네 번째 부분에서 온도가 약 115℃―약 120℃ 범위의 온도를 갖는, 4개의 부분으로 나뉘어진 긴 구획을 통해 방사 구금으로 부터의 필라멘트를 통과시킨 후, 분당 4270m(14,000ft)이상의 속도에서 필라멘트를 권취시키는 단계가 포함되는 방법.
- 중합체를 필라멘트 형성 수단을 통해 압출시키고; 적어도 5개의 길이를 갖는 긴 구획을 제공하고; 상기 긴 구획을 통해 상기 필라멘트 형성 수단으로 부터의 필라멘트를 통과시키고; 및 그후 필라멘트를 수렴시키는 단계로 구성된, 유기 합성 용융 방사성 중합체를 방사시키기 위한 방법.
- 중합체를 필라멘트 형성 수단을 통해 압출시키고; 상기 구획내 온도를 소정의 최대치로부터 소정의 최소치까지 조절하기 위한 수단을 갖는 긴 구획을 제공하고; 상기 긴 구획을 통해 상기 필라멘트 형성 수단으로 부터의 필라멘트를 통과시키고; 및 그후 필라멘트를 수렴시키는 단계로 구성되는 유기 합성 용융 방사성 중합체를 방사시키기 위한 방법.※ 참고사항 : 최초출원 내용에 의하여 공개되는 것임.