KR890701791A - 복합합금 강분 및 소결 합금강 - Google Patents
복합합금 강분 및 소결 합금강Info
- Publication number
- KR890701791A KR890701791A KR1019890700958A KR890700958A KR890701791A KR 890701791 A KR890701791 A KR 890701791A KR 1019890700958 A KR1019890700958 A KR 1019890700958A KR 890700958 A KR890700958 A KR 890700958A KR 890701791 A KR890701791 A KR 890701791A
- Authority
- KR
- South Korea
- Prior art keywords
- alloy
- weight
- steel
- alloy steel
- kgf
- Prior art date
Abstract
내용없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 본 발명자들이 얻은 열처리 소결체의 조성에 대한 밀도와 강도의 과계를 설명하는 그래프. 제2도는 제1도와 동일한 소결체의 조성에 대한 밀도와 샤르피 충격치와의 관계를 설명하는 그래프. 제3도는 Ni, Mo의 함유량이 본 발명의 범위내에 있는 열처리 소결체의 C량과 인장강도의.
Claims (15)
- 합금 성분이 분말상으로 철분입자 표면에 부분적으로 확산 부착된 복합 합금강분에 있어서, 합금 성분으로서, Ni와 Mo를 포함하며 합금 조성이 Ni:0.50-3.50 중량%, Mo:0.65-3.50 중량%이고, 나머지가 Fe 및 불가피 불순물로 구성되며 또한 그 강분중 45μm 이하의 입도에서 Ni 및 Mo의 함유량이 각각 그 강분전체의 평균 함유량의 -4.2배의 범위에 있는 것을 특징으로 하는 분말 야금용 복합 합금강분.
- 최종제품 합금 성분으로서 Ni와 Mo를 포함하고, 합금조성이 Ni:0.50-3.50 중량%, Mo:0.65-3.50 중량%이고, 나머지가 Fe, C 및 불가피 불순물로 되며, 또한 밀도가 7.0g/㎤ 이상이고, 경화, 어니얼링후의 인장강도가 130kgf/㎟ 이상인 것을 특징으로 하는 고강도 소결 합금강.
- 최종 제품 합금성분으로서 C, Ni와 Mo를 포함하여, 합금 조성이 C:0.3-0.8 중량%, N:0.50-3.50 중량%, Mo:0.65-3.50 중량%이고, 나머지가 Fe 및 불가피 불순물로 되며, 또한 밀도가 7.0g/㎤ 이상으로서 경화, 어니일링후의 인장강도가 130kgf/㎟ 이상인 것을 특징으로 하는 고강도 고인성 소결 합금강.
- 제1항에 기재된 복합 합금강분을 사용하여 제조한 소결 합금강으로서, 최종 제품 합금성분으로 Ni와 Mo를 함유하고, 합금조성이 Ni;0.50-3.50 중량%, Mo:0.65-3.50 중량%이고, 나머지가 Fe, C 및 불가피 불순물로 구성되며, 또한 밀도가 7.0g/㎤ 이상으로서 침탄 경화, 어니일링 후의 인장강도가 130kgf/㎟ 이상인 것을 특징으로 하는 고강도 소결 합금강.
- 제1항에 기재된 복합합금강분을 사용하여 제조된 소결 합금강으로서, 최종 제품 합금 성분으로 C, Ni와 Mo를 함유하고, 합금조성이 C:0.3-0.8 중량%, Ni:0.50-3.50 중량%, Mo:0.65-3.50 중량%이고, 나머지가 Fe 및 불가피 불순물로 되며, 또한 밀도가 7.0g/㎤ 이상으로 경화, 어니일링후의 인장강도가 130kgf/㎟ 이상인 것을 특징으로 하는 고강도 고인성 소결 합금강.
- 합금성분이 분말상으로 철분입자표면에 부분적으로 확산 부착된 복합 합금강분에 있어서, 합금상분으로서 Ni와 Mo 또는 W중 적어도 하나를 포함하며, 합금조성이, Ni:0.50-3.50 중량%, Mo+1/2W:0.65-3.50 중량%이고, 나머지가 Fe 및 불가피 불순물로 구성되며 또한 그 강분중 45μm 이하의 입도에서의 Ni 및 Mo+1/2W의 함유량이 각각 그 강분 전체의 평균 함유량의 2.0-4.2배의 범위에 있는 것을 특징응로 하는 분말 야금용 복합 합금강분.
- 최종 제품 합금성분으로서 Ni와 Mo 또는 W를 포함하고, 합금조성이 Ni:0.50-3.50 중량%, Mo+1/2W:0.65-3.50 중량%이고, 나머지가 Fe, C 및 불가피 불순물로 되며, 또한 밀도가 7.0g/㎤ 이상이고 침탄 경화, 어니일링후의 인장강도가 130kgf/㎟ 이상인 것을 특징으로 하는 고강도 소결 합금강.
- 최종 제품 합금성분으로서 C, Ni와 Mo 또는 W를 포함하여, 합금조성이 C:0.3-0.8 중량%, Ni:0.50-3.50 중량%, Mo+1/2W:0.65-3.50 중량 %이고, 나머지가 Fe 및 불가피 불순물로 되며, 또한 밀도가 7.0g/㎤ 이상으로서 경화, 어니일링후의 인장강도가 130kgf/㎟ 이상으로서 침탄 경화, 어니일링후의 인장강도가 130kgf/㎟ 이상인 것을 특징으로 하는 고강도 고인성 소결 합금강.
- 제6항에 기재된 복합 합금강분을 사용하여 제조한 소결합금강으로서, 최종 제품 합금성분으로 Ni와 Mo 또는 W를 함유하고, 합금조성이 Ni:0.50-3.50 중량%, Mo+1/2W:0.65-3.50 중량%이고, 나머지가 Fe, C 및 불가피 불순물로 구성되며, 또한 밀도가 7.0g/㎤ 이상인 것을 특징으로 하는 고강도 고인성 소결 합금강.
- 제6항에 기재된 복합 합금강분을 사용하여 제조된 소결합금강으로서, 최종 제품 합금 성분으로 C, Ni와, Mo 또는 W를 함유하고, 합금조성이 C:0.3-0.8 중량%, Ni:0.50-3.50 중량%, Mo+1/2W:0.65-3.50 중량%이고, 나머지가 Fe 및 불가피 불순물로 되며, 또한 밀도가 7.0g/㎤ 이상으로서 경화, 어니일링 후의 인장강도가 130kgf/㎟ 이상인 것을 특징으로 하는 고강도 고인성 소결 합금강.
- 합금성분이 분말상으로 철분입자 표면에 부분적으로 확산 부착된 복합 합금강분에서 합금성분으로서 Ni와 W를 포함하며, 합금 조성이 Ni:0.50-3.50 중량%, W:1.30-7.00 중량%고 나머지가 Fe 및 불가피 불순물로 구성되며, 또한 그 강분중 45μm 이항의 입도에서의 Ni 및 W의 함유량이 각각 그 강분전체의 평균 함유량의 2.0-4.2 배의 범위에 있는 것을 특징으로 하는 분말 야금용 복합 합금강분.
- 최종 제품 합금성분으로서 Ni와 W를 포함하고 합금조성이 Ni:0.50-3.50 중량%, W:1.30-7.00 중량%이고, 나머지가 Fe, C 및 불가피 불순물로 되며, 또한 밀도가 7.0g/㎤ 및 이상이고 침탄 경화, 어니일링후의 인장강도가 130kgf/㎟ 이상인 것을 특징으로 하는 고강도 소결 합금강.
- 최종 제품 합금성분으로서 C, Ni와 W를 포함하며, 합금조성이 C:0.3-0.8 중량%, Ni:0.50-3.50 중량%, W;1.30-7.00 중량%이고, 나머지가 Fe 및 불가피 불순물로 되며, 또한 밀도가 7.0g/㎤ 이상으로서 경화, 어니일링후의 인장강도가 130kgf/㎟ 이상인 것을 특징으로 하는 고강도 고인성 소결 합금강.
- 제11항에 기재된 복합 합금강분을 사용하여 제조한 소결 합금강으로서, 최종 제품 합금성분으로 Ni와 W를 함유하고, 합금조성이 Ni:0.50-3.50 중량%, W:1.30-7.00 중량%이고, 나머지가 Fe, C 및 불가피 불순물로 구성되며, 또한 밀도가 7.0g/㎤ 이상으로서 침탄 경화, 어니일링후의 인장강도가 130kgf/㎟ 이상인 것을 특징으로 하는 고강도 소결 합금강.
- 제11항에 기재된 복합 합금강분을 사용하여 제조된 소결 합금강으로서, 최종 제품 합금 성분으로 Ni와 W를 함유하고, 합금조성이 C:0.3-0.8 중량%, Ni:0.50-3.50 중량%, W:1.30-7.00 중량%이고, 나머지가 Fe 및 불가피 불순물로 되며, 또한 밀도가 7.0g/㎤ 이상으로서 경화, 어니일링후의 인장강도가 130kgf/㎟ 이상인 것을 특징으로 하는 고강도 고인성 소결 합금강.※ 참고사항:최초출원 내용에 의하여 공개하는 것임.