KR20240010462A - 수성 분산체 - Google Patents
수성 분산체 Download PDFInfo
- Publication number
- KR20240010462A KR20240010462A KR1020237039628A KR20237039628A KR20240010462A KR 20240010462 A KR20240010462 A KR 20240010462A KR 1020237039628 A KR1020237039628 A KR 1020237039628A KR 20237039628 A KR20237039628 A KR 20237039628A KR 20240010462 A KR20240010462 A KR 20240010462A
- Authority
- KR
- South Korea
- Prior art keywords
- aqueous dispersion
- weight
- polysaccharide
- parts
- inorganic powder
- Prior art date
Abstract
본 발명이 해결하고자 하는 과제는, 우수한 보습성을 가짐과 동시에, 분산 안정성도 우수하여, 화장료 등 각종 용도에 사용할 수 있는 수성 분산체를 제공하는 것이다.
본 발명은 황산기를 갖는 다당류 (A) 및 친수화 처리 무기 분체 (B)를 함유하는 것을 특징으로 하는 수성 분산체가 우수한 보습성을 가짐과 동시에, 분산 안정성도 우수하여, 화장료 등 각종 용도에 사용할 수 있다는 것을 발견하였다.
본 발명은 황산기를 갖는 다당류 (A) 및 친수화 처리 무기 분체 (B)를 함유하는 것을 특징으로 하는 수성 분산체가 우수한 보습성을 가짐과 동시에, 분산 안정성도 우수하여, 화장료 등 각종 용도에 사용할 수 있다는 것을 발견하였다.
Description
본 발명은 분산 안정성이 우수한 수성 분산체 및 이것을 함유하는 화장료에 관한 것이다.
화장료 등의 분야에 있어서, 착색제나 충전재, 자외선 흡수제, 자외선 산란제로서 여러 가지 무기 분체가 사용되고 있다. 이들 무기 분체는 상기한 바와 같이 여러 가지 용도에 이용되는 한편, 액체에 첨가한 경우에는 침강이 생기는 등의 문제가 존재한다. 그 때문에 이들 무기 분체를 이용하여 제제화하는 경우에는, 친화성이 좋은 용매를 선택하거나, 분산성을 향상시키는 조성을 검토하거나, 친화성을 향상시키기 위해 무기 분체를 표면 처리하는 등의 각종 검토가 행해지고 있다(예컨대 특허문헌 1∼3 참조).
그러나, 증점성을 갖고 분산 안정성에 기여하는 것이 알려져 있는 다당류와, 친수화 처리 무기 분체를 조합하여 분산체를 제조할 때에도, 다당류와 친수화 처리 무기 분체가 상호 작용함으로써 유사 가교가 생겨, 겔화가 생김으로써 분산계가 불안정해져 무기 분체가 침강하거나, 2층 분리하는 등의 문제가 발생하고 있고, 이들 다당류와 친수성 무기 분체를 조합하여 분산성이 우수한 수성 분산체를 제조하는 것은 현재까지 달성되어 있지 않았다.
본 발명이 해결하고자 하는 과제는, 우수한 보습성을 가짐과 동시에, 분산 안정성도 우수하여, 화장료 등 각종 용도에 사용할 수 있는 수성 분산체를 제공하는 것이다.
본 발명자는, 황산기를 다당류 (A) 및 친수화 처리 무기 분체 (B)를 함유하는 것을 특징으로 하는 수성 분산체에 의해 상기 과제를 해결하였다.
즉, 본 발명은 이하의 양태를 포함하는 것이다.
[1] 황산기를 갖는 다당류 (A), 및 친수화 처리 무기 분체 (B)를 함유하는 것을 특징으로 하는 수성 분산체.
[2] 상기 황산기를 갖는 다당류 (A)가, 중량 평균 분자량이 350만∼2,000만의 범위의 다당류인 것을 특징으로 하는, [1]에 기재된 수성 분산체.
[3] 상기 친수화 처리가, 무기 분체의 표면의 일부 또는 전부를 실리카, 함수 실리카, 함수 알루미나, 지르코니아 등에서 선택되는 1종 이상의 표면 처리제를 사용하여 피복하는 친수화 처리인 것을 특징으로 하는, [1] 또는 [2]에 기재된 수성 분산체.
[4] 상기 무기 분체가, 산화티탄 또는 산화아연에서 선택되는 1종 이상인 것을 특징으로 하는, [1]∼[3] 중 어느 하나에 기재된 수성 분산체.
[5] 상기 수성 분산체에 있어서 황산기를 갖는 다당류 (A) 1 중량부에 대하여, 친수화 처리 무기 분체 (B)가 10∼200 중량부의 범위로 포함되는 것을 특징으로 하는, [1]∼[4] 중 어느 하나에 기재된 수성 분산체.
[6] 상기 황산기를 갖는 다당류 (A)가 스이젠지노리로부터 얻어진 다당류인 것을 특징으로 하는, [1]∼[5] 중 어느 하나에 기재된 수성 분산체.
[7] [1]∼[6] 중 어느 하나에 기재된 수성 분산체를 함유하는 것을 특징으로 하는 화장료.
[8] 자외선 차단 화장료, 또는 보습용 화장료 중 어느 하나인 것을 특징으로 하는 [7]에 기재된 화장료.
본 발명에 의하면, 우수한 분산 안정성을 갖고, 도막 형성성도 우수한 수성 분산체를 제조할 수 있어, 이것을 화장료 등의 용도에 널리 이용할 수 있다.
이하, 본 발명에 대해서 상세하게 설명한다. 또한, 이하에 기재하는 구성 요건의 설명은, 본 발명을 설명하기 위한 예시이고, 본 발명은 이들 내용에 한정되는 것이 아니다.
본 발명에 있어서 사용되는 황산기를 갖는 다당류 (A)로서는, 다당류의 일부에 황산기를 갖는 것이면 좋고, 본 발명의 효과가 얻어지는 범위에서 특별히 제한되는 것은 아니다. 이들 황산기를 갖는 다당류 (A)로서는, 각종 원료로부터 추출된 황산기를 갖는 다당류를 그대로 이용하여도 좋고, 또한 황산기를 갖지 않는 다당류에 공지의 방법에 의해 황산기를 도입한 다당류를 이용하여도 좋다. 또한 본 발명에서 사용되는 구조 중에 황산기를 갖는 다당류 (A)로서는, 이들 다당류의 염을 이용하여도 좋다.
본 발명에 있어서 이용되는 황산기를 갖는 다당류 (A)로서는, 남조류 유래의 황산기를 갖는 다당류가 바람직하고, 특히 스이젠지노리(학명: Aphanothece sacrum)로부터 얻어지는 황산기를 갖는 다당류(사크란)를 이용하면 분산 안정성이 향상하기 때문에 바람직하다.
본 발명에 있어서 황산기를 갖는 다당류 (A)의 원료로서 적합한 스이젠지노리란 남조류이며 크루코커스(Chroococcus)목에 속하는 광합 성능을 갖는 진성 세균의 일종이다. 상기 스이젠지노리는 규슈의 특정 지역에 자생하며, 복수의 세포가 평평한 형상의 군체를 형성하는 담수성 남조류이다. 또한, 그 군체의 외면은 다당류 등에 의해 형성되는 겔형의 분비물에 덮여 있고, 군체의 직경은 50 ㎜ 정도의 크기까지 성장한다.
상기 스이젠지노리로부터 황산기를 갖는 다당류 (A)를 추출하는 방법으로서는, 특별히 한정되지 않고 공지의 방법을 이용하여 추출할 수 있지만, 예컨대 국제 공개 WO2008/062574호 공보의 실시예에 기재된 방법을 들 수 있다.
상기 스이젠지노리로부터 황산기를 갖는 다당류 (A)를 추출하는 구체적인 방법으로서는, 적량의 스이젠지노리를 동결, 수세함으로써 수용성 색소를 제거하고, 이어서 에탄올 등의 유기 용매에 의해 지용성 색소를 제거하고, 스이젠지노리의 조체(藻體)를 건조한다. 그 후 얻어진 스이젠지노리 건조 조체에 0.1 N의 수산화나트륨을 첨가하고, 60∼80℃에서 6시간 교반을 행한다. 상기 조작으로부터 얻어진 당 유도체액을 중화 후 여과하고, 추가로 분화 분자량이 8,000인 투석막으로 처리하여, 투석막 내액을 농축, 건조하는 방법 등을 들 수 있다.
본 발명에 있어서 이용되는 황산기를 갖는 다당류 (A)로서는, 상기 스이젠지노리 유래의 다당류 이외에도 콘드로이틴황산, 덜마탄황산 및 이들의 염으로 이루어지는 군에서 선택되는 1종 이상; D-글루코사민, D-갈락토사민, D-글루쿠론산, L-이두론산, D-갈락투론산, D-글루코오스, D-갈락토오스, D-크실로오스 등으로 구성되는 공지의 다당류의 일부에 황산기를 갖는 다당류 및 이들의 염으로 이루어지는 군에서 선택되는 1종 이상을 이용할 수 있고, 이들 성분을 단독으로 이용하여도 좋고, 2종 이상을 적절하게 조합하여 이용할 수도 있다.
본 발명에 있어서 이용되는 황산기를 갖는 다당류 (A)의 중량 평균 분자량은, 본 발명의 효과가 얻어지는 범위에서 특별히 제한되는 것은 아니지만, 350만∼2,000만이면 수성 분산체의 분산성이 안정되기 때문에 바람직하고, 400만∼1,500만이면 수성 분산체의 점성이 적합한 것이 되기 때문에 보다 바람직하다.
본 발명에 따른 수성 분산체에 있어서, 황산기를 갖는 다당류 (A)의 함유량은 본 발명의 효과가 얻어지는 범위에서 특별히 제한되는 것은 아니지만, 수성 분산체 전체에 대하여 0.005∼1 중량%가 바람직하고, 더욱 0.01∼0.8 중량%이면 수성 분산체의 도막 형성성이 적합해지기 때문에 보다 바람직하다.
본 발명에 있어서 사용되는 친수화 처리 무기 분체 (B)로서는, 공지의 무기 분체를 친수성 물질로 표면 처리한 무기 분체이면 좋고, 본 발명의 효과가 얻어지는 범위에서 특별히 제한되는 것은 아니다.
본 발명의 친수화 처리 무기 분체 (B)를 구성하는 무기 분체로서는, 각종 공지의 무기 분체를 이용할 수 있지만, 예컨대 아연, 티탄, 칼슘, 알루미늄, 실리카, 붕소, 바륨, 탈크, 운모, 카올린, 알루미나 등의 무기 분체 및 이들의 산화물, 수산화물, 탄산화물, 황산화물, 질화물에서 선택되는 1종 이상을 이용하여도 좋다. 이들 무기 분체로서는 산화물을 이용한 경우에 분산성이 향상하는 점에서 바람직하고, 특히 산화아연, 산화티탄 중 어느 1종 이상을 이용하면 현저한 분산성의 향상이 보인다는 점에서 바람직하다.
상기 무기 분체를 본 발명의 친수화 처리 무기 분체 (B)로 하기 위해 행하는 친수화 처리로서는, 본 발명의 효과가 얻어지는 범위에서 특별히 제한되는 것은 아니며, 무기 분체와 물의 친화성을 향상시키는 처리이면 좋다. 이들 친수화 처리의 구체예로서는, 실리카, 함수 실리카, 함수 알루미나, 지르코니아 등에서 선택되는 1종 이상의 표면 처리제를 사용하여 무기 분체의 표면의 일부 또는 전부를 피복하는 처리가 예시되고, 이 중에서도 실리카, 함수 실리카를 이용하여 친수화 처리를 행하면 분산성이 보다 양호해진다는 점에서 바람직하다. 또한 친수화 처리는 다층을 형성하도록 행하여도 좋다.
상기 친수화 처리는, 처리 전의 무기 분체 100 중량부에 대하여 1∼35 중량부의 표면 처리제를 첨가하여 처리를 행하는 것이 바람직하고, 2∼25 중량부이면 분산성이 더욱 적합한 것이 되기 때문에 보다 바람직하다.
본 발명의 수성 분산체에 있어서, 황산기를 갖는 다당류 (A)와 친수화 처리 무기 분체 (B)의 배합 비율은, 본 발명의 효과가 얻어지는 범위에서 특별히 한정되는 것은 아니지만, 황산기를 갖는 다당류 (A) 1 중량부에 대하여, 친수화 처리 무기 분체 (B)가 10∼200 중량부의 범위로 포함되는 것이 바람직하고, 분산성 향상이 현저하게 확인된다는 점에서 20∼150 중량부 포함되는 것이 특히 바람직하다.
본 발명의 수성 분산체는, 분산성이 요구되는 각종 용도에 있어서 적절하게 사용할 수 있다. 그 중에서도 화장료로 하였을 때에는 다당류 유래의 보습성이 적합하게 얻어진다는 점에서 보습용 화장료인 것이 바람직하다. 또한 친수화 처리 무기 분체 (B)는 적합한 자외선 방어 효과를 갖는다는 점에서 자외선 차단 화장료로 하는 것이 바람직하다.
본 발명의 수성 분산체를 화장료로 하는 경우, 화장료 분야에 있어서 사용할 수 있는 임의의 유제, 보습제, 계면 활성제, 자외선 방어제, 식물 및 동물 유래 추출물, 고급 알코올, 산화 방지제, 색재, pH 조정제, 향료, 방부제, (A) 성분 이외의 다당류, 및 (B) 성분 이외의 분체 등의 성분을 첨가하여도 좋다. 본 발명의 수성 분산체를 화장료로 하는 경우, 그 제형은 특별히 한정되지 않고, 화장수, 유액, 크림 등 각종 제형으로 할 수 있고, 이들을 기초 화장료나 메이크업 화장료 등으로서 이용할 수도 있다.
본 발명의 수성 분산체를 얻기 위한 분산 방법에 대해서는, 균일하게 분산시킬 수 있는 공지의 방법이면 좋고 특별히 제한되는 것은 아니다. 이들 분산 방법으로서는 교반기, 자공전식 믹서, 호모 믹서, 호모디스퍼, 초음파 세정기, 페인트 믹서(샌드 밀), 볼 밀, 롤 밀 등을 들 수 있다.
실시예
이하, 본 발명을 실시예에 의해 더욱 상세하게 설명하지만, 본 발명은 이들 실시예에 한정되는 것이 아니다. 또한, 실시예 및 비교예에 이용한 각종 다당류의 중량 평균 분자량은 다각도 산란 겔 침투 크로마토그래피를 이용하여 측정한 개산 수치를 채용하였다.
<수성 분산체의 조제>
(실시예 1)
함수 실리카 처리 미립자 산화티탄(사카이가가쿠고교사 제조. STR-100W) 30 중량부, 사크란(중량 평균 분자량 Mw 약 400만) 0.25 중량부, 물 69.75 중량부, 및 산화티탄의 4배 중량의 지르코니아 비드를 교반자로 하여 덮개를 갖는 폴리프로필렌 용기(100 mL)에 넣고, 덮개를 덮은 후, 페인트 컨디셔너(도요세이키사 제조)로 2시간 분산시켰다. 그 후, 200 마이크론의 폴리에틸렌 메쉬로 여과하여 수성 분산체 1을 얻었다. 얻어진 수성 분산체 1을 실온에서 정치한 후, 육안으로 보아 경시적 분산 상태의 확인을 행한 바, 수성 분산체 1은 3개월 후도 균일화한 상태였다. 또한, 이 수성 분산체 1을 라텍스 시트에 도포하였을 때에는 균일한 도막이 얻어졌다.
(실시예 2)
함수 실리카 처리 미립자 산화티탄(사카이가가쿠고교사 제조. STR-100W) 30 중량부, 사크란(중량 평균 분자량 Mw 약 1200만) 0.25 중량부, 물 69.75 중량부, 산화티탄의 4배 중량의 지르코니아 비드를 교반자로 하여 덮개를 갖는 폴리프로필렌 용기(100 mL)에 넣고, 덮개를 덮은 후, 페인트 컨디셔너로 2시간 분산시켰다. 그 후, 200 마이크론의 폴리에틸렌 메쉬로 여과하여 수성 분산체 2를 얻었다. 얻어진 수성 분산체 2를 실온에서 정치한 후, 육안으로 보아 경시적 분산 상태의 확인을 행한 바, 수성 분산체 2는 3개월 후도 균일화한 상태였다. 또한, 이 수성 분산체 2를 라텍스 시트에 도포하였을 때데는 균일한 도막이 얻어졌다.
(실시예 3)
함수 실리카 처리 미립자 산화아연(사카이가가쿠고교사 제조. Finex52) 30 중량부, 사크란(중량 평균 분자량 Mw 약 400만) 0.35 중량부, 물 69.65 중량부, 산화아연의 4배 중량의 지르코니아 비드를 교반자로 하여 덮개를 갖는 폴리프로필렌 용기(100 mL)에 넣고, 덮개를 덮은 후, 페인트 컨디셔너로 2시간 분산시켰다. 그 후, 200 마이크론의 폴리에틸렌 메쉬로 여과하여 수성 분산체 3을 얻었다. 얻어진 수성 분산체 3을 실온에서 정치한 후, 육안으로 보아 경시적 분산 상태의 확인을 행한 바, 수성 분산체 3은 3개월 후도 균일화한 상태였다. 또한, 이 수성 분산체 3을 라텍스 시트에 도포하였을 때에는 균일한 막이 얻어졌다.
(실시예 4)
함수 실리카 처리 미립자 산화아연(사카이가가쿠고교사 제조. Finex52) 30 중량부, 사크란(중량 평균 분자량 Mw 약 1200만) 0.35 중량부, 물 69.65 중량부, 산화아연의 4배 중량의 지르코니아 비드를 교반자로 하여 덮개를 갖는 폴리프로필렌 용기(100 mL)에 넣고, 덮개를 덮은 후, 페인트 컨디셔너로 2시간 분산시켰다. 그 후, 200 마이크론의 폴리에틸렌 메쉬로 여과하여 수성 분산체 4를 얻었다. 얻어진 수성 분산체 4를 실온에서 정치한 후, 육안으로 보아 경시적 분산 상태의 확인을 행한 바, 수성 분산체 4는 3개월 후도 균일화한 상태였다. 또한, 이 수성 분산체 4를 라텍스 시트에 도포하였을 때에는 균일한 막이 얻어졌다.
(비교예 1)
미처리 미립자 산화티탄 30 중량부, 사크란(중량 평균 분자량 Mw 약 400만) 0.25 중량부, 물 69.75 중량부, 산화티탄의 4배 중량의 지르코니아 비드를 교반자로 하여 덮개를 갖는 폴리프로필렌 용기(100 mL)에 넣고, 덮개를 덮은 후, 페인트 컨디셔너로 2시간 분산시켰다. 그 후, 200 마이크론의 폴리에틸렌 메쉬로 여과하여 비교 수성 분산체 1을 얻었다. 얻어진 비교 수성 분산체 1을 실온에서 정치한 후, 육안으로 보아 경시적 분산 상태의 확인을 행한 바, 1주일 후에 비교 수성 분산체 1은 2층으로 분리되었다. 또한, 이 비교 수성 분산체 1을 라텍스 시트에 도포하였을 때에는 불균일한 막밖에 얻어지지 않았다.
(비교예 2)
미처리 미립자 산화아연 30 중량부, 사크란(중량 평균 분자량 Mw 약 1200만) 0.35 중량부, 물 69.65 중량부, 산화티탄의 4배 중량의 지르코니아 비드를 교반자로 하여 덮개를 갖는 폴리프로필렌 용기(100 mL)에 넣고, 덮개를 덮은 후, 페인트 컨디셔너로 2시간 분산시켰다. 그 후, 200 마이크론의 폴리에틸렌 메쉬로 여과하여 비교 수성 분산체 2를 얻었다. 얻어진 비교 수성 분산체 2를 실온에서 정치한 후, 육안으로 보아 경시적 분산 상태의 확인을 행한 바, 1주일 후에 비교 수성 분산체 2는 2층으로 분리되었다. 또한, 이 비교 수성 분산체 2를 라텍스 시트에 도포하였을 때에는 불균일한 막밖에 얻어지지 않았다.
(비교예 3)
함수 실리카 처리 미립자 산화티탄 30 중량부, 히알루론산나트륨(중량 평균 분자량 약 160만) 0.25 중량부, 물 69.75 중량부, 산화티탄의 4배 중량의 지르코니아 비드를 교반자로 하여 덮개를 갖는 폴리프로필렌 용기(100 mL)에 넣고, 덮개를 덮은 후, 페인트 컨디셔너로 2시간 분산시켰다. 그 후, 200 마이크론의 폴리에틸렌 메쉬로 여과하여 비교 수성 분산체 3을 얻었다. 얻어진 비교 수성 분산체 3을 실온에서 정치한 후, 육안으로 보아 경시적 분산 상태의 확인을 행한 바, 1개월 경과 후에 비교 수성 분산체 3은 분산체의 일부가 분리되었다. 또한, 이 비교 수성 분산체 3을 라텍스 시트에 도포하였을 때에는 불균일한 막밖에 얻어지지 않았다.
(비교예 4)
함수 실리카 처리 미립자 산화아연 30 중량부, 푸코이단(중량 평균 분자량 약 30만) 0.35 중량부, 물 69.65 중량부, 산화아연의 4배 중량의 지르코니아 비드를 교반자로 하여 덮개를 갖는 폴리프로필렌 용기(100 mL)에 넣고, 덮개를 덮은 후, 페인트 컨디셔너로 2시간 분산시켰다. 그 후, 200 마이크론의 폴리에틸렌 메쉬로 여과하여 비교 수성 분산체 4를 얻었다. 얻어진 비교 수성 분산체 4를 실온에서 정치한 후, 육안으로 보아 경시적 분산 상태의 확인을 행한 바, 1개월 경과 후에 비교 수성 분산체 4는 분산체의 일부가 분리되었다. 또한, 이 비교 수성 분산체 4를 라텍스 시트에 도포하여도 일부 불균일이 생긴 막밖에 얻어지지 않았다.
(실시예 5)
세테아릴알코올을 2 중량부, 스테아르산글리세릴을 1.2 중량부, 폴리옥시에틸렌 40 스테아레이트를 0.6 중량부, 스테아레스 20을 0.2 중량부, 호호바 오일을 2 중량부, 라우릴산라우릴을 3 중량부, 혼합하고, 60℃로 가온하여 용해시켜, 용해물 1을 얻었다.
다음에, RO수 47 중량부에 글리세린폴리에틸렌글리콜에테르 3 중량부를 가한 60℃ 용액에, 상기에서 얻어진 용해물 1을 가하였다. 이 용액을 10분간 호모지나이저 교반하고, 그 후, 실시예 1에서 조정한 수성 분산체 1을 40 중량부 가하고, 호모지나이저로 10분 교반하였다.
얻어진 분산액에 1부 페녹시에탄올을 가하고 혼련하여 로션을 얻었다.
상기한 바와 같이 하여 얻어진 로션에 대하여, 이하에 기재하는 평가 방법을 이용하여, SPF(Sun Protect Factor), 피부 도포 시의 감촉, 백탁, 및 뻑뻑함의 각 평가를 행하였다.
<수성 분산체를 사용한 화장품(로션)의 평가 방법>
<<SPF의 평가(SPF 평가)>>
SPF의 평가는, SPF 애널라이저(UV-2000S 미국 Labsphere사 제조)를 사용하여 평가를 실시하였다.
[평가 기준]
◎
SPF가 30 이상임
○
SPF가 25 이상 30 미만임
△
SPF가 20 이상 25 미만임
×
SPF가 20 미만임
<<피부 도포 시의 감촉(피부 감촉성)>>
피부 도포 시의 감촉의 평가는, 제작한 로션을 집게 손가락의 안쪽에 취하여, 팔의 이면에 골고루 도포하였다.
[평가 기준]
◎
5명 중 4명 이상이, 감촉이 좋다고 회답함
○
5명 중 3명이, 감촉이 좋다고 회답함
△
5명 중 2명이, 감촉이 좋다고 회답함
×
5명 중 1명이, 감촉이 좋다고 회답하거나, 혹은 감촉이 좋다는 회답이 없음
<<백탁>>
백탁에 대해서는, 피부에 도포 후, 피부와 비교하여 하기 기준으로 평가하였다.
[평가 기준]
○
백탁이 눈에 띄지 않음
△
백탁이 약간 눈에 띔
×
백탁이 눈에 띔
<<뻑뻑함>>
뻑뻑한 감촉에 대해서는, 제작한 로션을 집게 손가락의 안쪽에 취하여, 팔의 이면에 골고루 도포하였다.
[평가 기준]
◎
5명 중 4명 이상이, 뻑뻑함을 느끼지 않는다고 회답함
○
5명 중 3명이, 뻑뻑함을 느끼지 않는다고 회답함
△
5명 중 2명이, 뻑뻑함을 느끼지 않는다고 회답함
×
5명 중 1명이, 뻑뻑함을 느끼지 않는다고 회답하거나, 혹은 뻑뻑함을 느끼지 않는다는 회답이 없음
실시예 1의 수성 분산체를 사용하여 제작한 실시예 5의 로션에 대한, SPF, 피부 도포 시의 감촉, 백탁, 및 뻑뻑함의 평가 결과를 하기 표 1에 나타낸다.
(실시예 6)
수성 분산체 1 대신에 실시예 2에서 얻어지는 수성 분산체 2로 변경한 것 이외에는, 실시예 5와 동일한 조작을 행하여, 로션을 얻었다.
실시예 6에서 얻어진 로션에 대하여, 실시예 5와 동일한 방법으로, SPF, 피부 도포 시의 감촉, 백탁, 및 뻑뻑함의 평가를 행하였다. 평가 결과를 하기 표 1에 나타낸다.
(실시예 7)
수성 분산체 1 대신에 실시예 4에서 얻어지는 수성 분산체 4로 변경한 것 이외에는, 실시예 5와 동일한 조작을 행하여, 로션을 얻었다.
실시예 7에서 얻어진 로션에 대하여, 실시예 5와 동일한 방법으로, SPF, 피부 도포 시의 감촉, 백탁, 및 뻑뻑함의 평가를 행하였다. 평가 결과를 하기 표 1에 나타낸다.
(비교예 5)
함수 실리카 처리 미립자 산화티탄 30 중량부, 물 70 중량부, 산화티탄의 4배 중량의 지르코니아 비드를 교반자로 하여 덮개를 갖는 폴리프로필렌 용기(100 mL)에 넣고, 덮개를 덮은 후, 페인트 컨디셔너로 2시간 분산시켰다. 그 후, 200 마이크론의 폴리에틸렌 메쉬로 여과하여 비교 수성 분산체 5를 얻었다.
수성 분산체 1 대신에 비교예 5에서 얻어지는 비교 수성 분산체 5로 변경한 것 이외에는, 실시예 5와 동일한 조작을 행하여, 로션을 얻었다.
비교예 5에서 얻어진 로션에 대하여, 실시예 5와 동일한 방법으로, SPF, 피부 도포 시의 감촉, 백탁, 및 뻑뻑함의 평가를 행하였다. 평가 결과를 하기 표 1에 나타낸다.
(비교예 6)
세테아릴알코올을 2 중량부, 스테아르산글리세릴을 1.2 중량부, 폴리옥시에틸렌 40 스테아레이트를 0.6 중량부, 스테아레스 20을 0.2 중량부, 호호바 오일을 2 중량부, 라우릴산라우릴을 3 중량부, 혼합하고, 60℃로 가온하여 용해시켜, 용해물 2를 얻었다.
다음에, RO수 27.5 중량부에 글리세린폴리에틸렌글리콜에테르 3 중량부를 가한 60℃ 용액에, 상기에서 얻어진 용해물 2를 가하였다. 이 용액을 10분간 호모지나이저 교반하고, 그 후, 비교예 5에서 조정한 비교 수성 분산체 5를 40부 가하고, 호모지나이저로 10분 교반하였다. 추가로 0.5% 사크란 수용액을 20 중량부 가하고 10분간 호모지나이저 교반을 행하였다.
얻어진 분산액에 1부 페녹시에탄올을 가하고 혼련하여 로션을 얻었다.
비교예 6에서 얻어진 로션에 대하여, 실시예 5와 동일한 방법으로, SPF, 피부 도포 시의 감촉, 백탁, 및 뻑뻑함의 평가를 행하였다. 평가 결과를 하기 표 1에 나타낸다.
(비교예 7)
함수 실리카 처리 미립자 산화티탄 대신에 함수 실리카 처리 미립자 산화아연을 사용하고, 비교예 5와 동일한 조작을 행하여, 로션을 얻었다.
비교예 7에서 얻어진 로션에 대하여, 실시예 5와 동일한 방법으로, SPF, 피부 도포 시의 감촉, 백탁, 및 뻑뻑함의 평가를 행하였다. 평가 결과를 하기 표 1에 나타낸다.
| 실시예 5 | 실시예 6 | 실시예 7 | 비교예 5 | 비교예 6 | 비교예 7 | |
| SPC 평가 | ◎ | ◎ | ○ | △ | △ | △ |
| 피부 감응성 | ◎ | ◎ | ○ | △ | ○ | △ |
| 백탁 | ○ | ○ | ○ | × | △ | × |
| 뻑뻑함 | ◎ | ◎ | ○ | × | △ | × |
상기 실시예 1∼4 및 비교예 1∼4의 결과로부터, 황산기를 갖는 다당류와 친수화 처리 무기 분체를 함유하는 수성 분산체는, 분산 안정성이 우수하고, 도막 형성성도 우수하다는 것을 알았다.
또한, 상기 실시예 5∼7 및 비교예 5∼7의 결과로부터, 황산기를 갖는 다당류와 친수화 처리 무기 분체를 함유하는 수성 분산체는, 화장품의 SPF 값이나 피부 감촉성 등의 향상에 유효하게 기여한다는 것을 알았다.
Claims (8)
- 황산기를 갖는 다당류 (A),
및 친수화 처리 무기 분체 (B)
를 함유하는 것을 특징으로 하는 수성 분산체. - 제1항에 있어서, 상기 황산기를 갖는 다당류 (A)가, 중량 평균 분자량이 350만∼2,000만의 범위의 다당류인 것을 특징으로 하는 수성 분산체.
- 제1항 또는 제2항에 있어서, 상기 친수화 처리가, 무기 분체의 표면의 일부 또는 전부를 실리카, 함수 실리카, 함수 알루미나, 지르코니아 등에서 선택되는 1종 이상의 표면 처리제를 사용하여 피복하는 친수화 처리인 것을 특징으로 하는 수성 분산체.
- 제1항 내지 제3항 중 어느 한 항에 있어서, 상기 무기 분체가, 산화티탄 또는 산화아연에서 선택되는 1종 이상인 것을 특징으로 하는 수성 분산체.
- 제1항 내지 제4항 중 어느 한 항에 있어서, 상기 수성 분산체에 있어서 황산기를 갖는 다당류 (A) 1 중량부에 대하여, 친수화 처리 무기 분체 (B)가 10∼200 중량부의 범위로 포함되는 것을 특징으로 하는 수성 분산체.
- 제1항 내지 제5항 중 어느 한 항에 있어서, 상기 황산기를 갖는 다당류 (A)가 스이젠지노리로부터 얻어진 다당류인 것을 특징으로 하는 수성 분산체.
- 제1항 내지 제6항 중 어느 한 항에 기재된 수성 분산체를 함유하는 것을 특징으로 하는 화장료.
- 제7항에 있어서, 자외선 차단 화장료, 또는 보습용 화장료 중 어느 하나인 것을 특징으로 하는 화장료.