KR20230069087A - food packaging paper - Google Patents
food packaging paper Download PDFInfo
- Publication number
- KR20230069087A KR20230069087A KR1020237004784A KR20237004784A KR20230069087A KR 20230069087 A KR20230069087 A KR 20230069087A KR 1020237004784 A KR1020237004784 A KR 1020237004784A KR 20237004784 A KR20237004784 A KR 20237004784A KR 20230069087 A KR20230069087 A KR 20230069087A
- Authority
- KR
- South Korea
- Prior art keywords
- resin
- mass
- paper
- coated layer
- styrene
- Prior art date
Abstract
과제는, 내수성, 내유성, 가스 배리어성, 수증기 배리어성 및 플레이버 배리어성을 갖고, 히트 시일 적성 및 접기 가공 적성을 구비하며, 그리고 내블로킹성을 갖는 식품 포장 용지를 제공하는 것이다.
과제는, 종이 지지체와, 상기 종이 지지체의 편면에 제 1 도공층과, 종이 지지체를 기준으로 하여 상기 제 1 도공층의 외측에 제 2 도공층과, 및 종이 지지체를 기준으로 하여 상기 제 2 도공층의 외측에 제 3 도공층을 갖고, 상기 제 1 도공층이 카올린, 그리고 바인더로서 스티렌-부타디엔계 공중합 수지 및 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 상기 제 2 도공층이, 수지의 구성 단위로서 염화비닐리덴 단량체를 주성분으로서 갖는 폴리염화비닐리덴계 중합 수지를 함유하며, 그리고 상기 제 3 도공층이 아크릴계 수지를 함유하는 식품 포장 용지에 의해 해결할 수 있다.An object is to provide food packaging paper that has water resistance, oil resistance, gas barrier properties, water vapor barrier properties and flavor barrier properties, has heat sealability and folding processability, and has blocking resistance.
The problem is a paper support, a first coated layer on one side of the paper support, a second coated layer on the outside of the first coated layer on the basis of the paper support, and the second coating on the basis of the paper support A third coated layer is provided on the outer side of the layer, and the first coated layer contains kaolin and one or two or more selected from the group consisting of a styrene-butadiene copolymer resin and an acrylic resin as a binder, It can be solved by a food wrapping paper in which the coated layer contains a polyvinylidene chloride-based polymeric resin having a vinylidene chloride monomer as a main component as a constituent unit of the resin, and the third coated layer contains an acrylic resin.
Description
본 발명은, 식품의 포장, 식품을 넣는 봉지 또는 식품을 넣는 용기 등의 식품 포장 재료로서, 지지체가 종이인 식품 포장 용지에 관한 것이다.The present invention relates to a food packaging paper whose support is paper, as a food packaging material such as food packaging, a food bag, or a food container.
식품의 포장, 식품을 넣는 봉지 또는 식품을 넣는 용기 등의 식품 포장 재료는, 플라스틱 필름의 적층 구조 또는 금속 증착막을 갖는 필름이 대부분이었다. 한편, 플라스틱 제품의 환경 문제로부터, 식품의 열화를 억제하기 위해 외부로부터의 수증기 및 산소 가스에 대한 배리어성을 갖는, 종이 지지체로 이루어지는 식품 포장 용지가 존재한다. 예를 들면, 수계 도료의 도공에 의해 형성된 수증기 배리어층 및 가스 배리어층을 갖는, 우수한 가스 배리어성과 수증기 배리어성을 겸비한 종이제 배리어 포장 재료로서, 종이 기재 상에 안료 및 수증기 배리어성 수지를 함유하는 수증기 배리어층, 수용성 고분자를 함유하는 가스 배리어층을 이 순서로 형성하고, 수증기 배리어성 수지가 아크릴계 합성 수지인 종이제 배리어 포장 재료가 공지되어 있다 (예를 들면, 특허문헌 1 참조). 또한, 식품류 등의 포장에 사용할 수 있는, 각종 플라스틱 재료, 각종 증착 필름 및 종이 등의 기재에 접착제층 및 피접착제층을 형성하고, 상기 접착제층이, 에틸렌 불포화 카르복실산 공중합체 및 아크릴 중합체를 포함하는 복합 입자의 분산체를 건조시켜 이루어지고, 상기 피접착제층이 폴리염화비닐 및/또는 폴리염화비닐리덴으로 이루어지는 적층체가 공지되어 있다 (예를 들면, 특허문헌 2 참조).Most food packaging materials, such as food packaging, food packaging bags, and food packaging containers, are films having a laminated structure of plastic films or a metal vapor deposition film. On the other hand, from the environmental problem of plastic products, food packaging paper made of a paper support having barrier properties against water vapor and oxygen gas from the outside exists in order to suppress deterioration of food. For example, a paper barrier packaging material having both excellent gas barrier properties and water vapor barrier properties, having a water vapor barrier layer and a gas barrier layer formed by coating of a water-based paint, containing a pigment and a water vapor barrier resin on a paper substrate A paper barrier packaging material in which a water vapor barrier layer and a gas barrier layer containing a water-soluble polymer are formed in this order, and the water vapor barrier resin is an acrylic synthetic resin is known (for example, see Patent Document 1). In addition, an adhesive layer and an adhesive layer are formed on substrates such as various plastic materials, various vapor-deposited films, and paper, which can be used for packaging of foods, and the adhesive layer is composed of an ethylenically unsaturated carboxylic acid copolymer and an acrylic polymer. A laminate is known, which is formed by drying a dispersion of composite particles, wherein the adhesive layer is made of polyvinyl chloride and/or polyvinylidene chloride (see Patent Document 2, for example).
식품의 포장, 식품을 넣는 봉지 또는 식품을 넣는 용기 등의 식품 포장 용지에는, 식품에서 유래하는 수분 및 유분에 대한 내수성 및 내유성이 필요하다. 또한, 식품 포장 용지에는, 수증기, 습기 또는 산소의 투과를 방지하여 식품을 열화로부터 지키는 수증기 배리어성 및 가스 배리어성이 필요하다. 또한, 포장의 형태에 따라서는 식품을 수납하고 나서 식품 포장 용지를 밀봉하는 경우가 있어, 식품 포장 용지에는, 히트 시일 적성이 필요하다. 또한, 포장의 형태에 따라서는 식품이 떨어져 나오지 않도록 용기 형상으로 식품 포장 용지를 접기 가공하는 경우가 있어, 식품 포장 용지에는 접기 가공 적성이 필요하다. 식품 포장 용지는, 접기 가공 적성이 떨어지는 경우에 용지의 접힘부에 있어서, 내수성, 내유성, 가스 배리어성 또는 수증기 배리어성이 저하된다. 또 최근, 향기에 관한 해 (害) 를 주장하는 세간의 동향으로부터, 밀봉에 사용하는 식품 포장 용지에는, 식품으로부터 발생하는 향기가 새는 것을 경감시키는 플레이버 배리어성이 필요하다.BACKGROUND OF THE INVENTION [0002] Food packaging paper, such as food packaging, food packaging bags, or food packaging containers, requires water resistance and oil resistance against moisture and oil derived from food. Further, food packaging paper requires vapor barrier properties and gas barrier properties to protect food from deterioration by preventing permeation of water vapor, moisture or oxygen. In addition, depending on the shape of the packaging, there is a case where the food wrapping paper is sealed after storing the food, and the food wrapping paper requires heat sealability. In addition, depending on the shape of the packaging, food wrapping paper may be folded into a container shape so that food does not fall out, and food wrapping paper requires folding processing aptitude. When the food wrapping paper has poor folding processability, water resistance, oil resistance, gas barrier properties or water vapor barrier properties are reduced in the folded portion of the paper. In addition, in view of the recent trend of insisting on harms related to fragrance, food packaging paper used for sealing is required to have a flavor barrier property that reduces leakage of fragrance generated from food.
또한, 식품 포장 용지는, 식품에 대한 영향으로부터 비교적 저온에서 히트 시일 적성을 갖는 것이 바람직하다. 그러나, 비교적 저온에서 히트 시일 적성을 갖는 식품 포장 용지는, 제조 후의 권취 상태 또는 시트화 후의 적층 상태로 보관할 때에 블로킹을 발생하기 쉽다. 따라서, 히트 시일 적성을 갖는 식품 포장 용지에는, 내블로킹성이 필요하다.In addition, the food packaging paper preferably has heat-sealing properties at relatively low temperatures from the effect on food. However, food packaging paper having heat sealability at a relatively low temperature tends to cause blocking when stored in a coiled state after manufacture or in a laminated state after sheeting. Therefore, blocking resistance is required for food packaging paper having heat sealability.
본 발명의 목적은, 내수성, 내유성, 가스 배리어성, 수증기 배리어성 및 플레이버 배리어성을 갖고, 히트 시일 적성 및 접기 가공 적성을 구비하며, 그리고 내블로킹성을 갖는 식품 포장 용지를 제공하는 것이다.An object of the present invention is to provide food packaging paper that has water resistance, oil resistance, gas barrier properties, water vapor barrier properties and flavor barrier properties, has heat sealability and folding processability, and has blocking resistance.
본 발명자들은 예의 검토를 실시한 결과, 본 발명의 목적은 이하에 의해 달성된다.As a result of the present inventors earnestly examining, the object of the present invention is achieved by the following.
[1] 종이 지지체와, 상기 종이 지지체의 편면에 제 1 도공층과, 종이 지지체를 기준으로 하여 상기 제 1 도공층의 외측에 제 2 도공층과, 및 종이 지지체를 기준으로 하여 상기 제 2 도공층의 외측에 제 3 도공층을 갖고,[1] A paper support, a first coated layer on one side of the paper support, a second coated layer on the outside of the first coated layer based on the paper support, and the second coating based on the paper support having a third coating layer on the outside of the layer;
상기 제 1 도공층이 카올린, 그리고 바인더로서 스티렌-부타디엔계 공중합 수지 및 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고,The first coating layer contains kaolin and one or two or more selected from the group consisting of a styrene-butadiene copolymer resin and an acrylic resin as a binder,
상기 제 2 도공층이, 수지의 구성 단위로서 염화비닐리덴 단량체를 주성분으로서 갖는 폴리염화비닐리덴계 중합 수지를 함유하며, 그리고The second coating layer contains a polyvinylidene chloride-based polymeric resin having a vinylidene chloride monomer as a main component as a resin constituent unit, and
상기 제 3 도공층이 아크릴계 수지를 함유하는,The said 3rd coating layer contains acrylic resin,
식품 포장 용지.Food packaging paper.
[2] 상기 제 1 도공층이, 바인더로서 스티렌-부타디엔계 공중합 수지로 이루어지는 군에서 선택되는 1 종 혹은 2 종 이상, 또는 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 혹은 2 종 이상을 함유하는 상기 [1] 에 기재된 식품 포장 용지.[2] The above first coating layer contains, as a binder, one or two or more types selected from the group consisting of styrene-butadiene-based copolymer resins or one or two or more types selected from the group consisting of acrylic resins. The food packaging paper described in [1].
[3] 상기 제 1 도공층이, 바인더로서 스티렌-부타디엔계 공중합 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 제 1 도공층에 있어서 상기 스티렌-부타디엔계 공중합 수지의 합계 함유량이, 종이 지지체의 편면당 제 1 도공층 중의 카올린 100 질량부에 대하여 40 질량부 이상 400 질량부 이하인 상기 [2] 에 기재된 식품 포장 용지.[3] The first coated layer contains one or more selected from the group consisting of styrene-butadiene-based copolymer resins as a binder, and the total content of the styrene-butadiene-based copolymer resins in the first coated layer The food wrapping paper according to [2] above, wherein the amount is 40 parts by mass or more and 400 parts by mass or less with respect to 100 parts by mass of kaolin in the first coated layer per side of the paper support.
[4] 상기 제 1 도공층이, 바인더로서 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 제 1 도공층에 있어서 상기 아크릴계 수지의 합계 함유량이, 종이 지지체의 편면당 제 1 도공층 중의 카올린 100 질량부에 대하여 40 질량부 이상 400 질량부 이하인 상기 [2] 에 기재된 식품 포장 용지.[4] The first coated layer contains, as a binder, one or two or more kinds selected from the group consisting of acrylic resins, and the total content of the acrylic resins in the first coated layer is the number per one side of the paper support. The food packaging paper according to [2] above, which is 40 parts by mass or more and 400 parts by mass or less with respect to 100 parts by mass of kaolin in one coated layer.
[5] 상기 폴리염화비닐리덴계 중합 수지는, 수지 중의 염화비닐리덴 단량체가 85 질량% 이상 95 질량% 이하의 것인 상기 [1] ∼ [4] 중 어느 하나에 기재된 식품 포장 용지.[5] The food wrapping paper according to any one of [1] to [4] above, wherein the polyvinylidene chloride-based polymeric resin has a vinylidene chloride monomer in the resin of 85% by mass or more and 95% by mass or less.
[6] 제 3 도공층이 함유하는 상기 아크릴계 수지가, 스티렌-아크릴계 공중합 수지인 상기 [1] ∼ [5] 중 어느 하나에 기재된 식품 포장 용지.[6] The food wrapping paper according to any one of [1] to [5], wherein the acrylic resin contained in the third coating layer is a styrene-acrylic copolymer resin.
[7] 상기 제 3 도공층이, 파라핀 왁스를 추가로 함유하는 상기 [1] ∼ [6] 중 어느 하나에 기재된 식품 포장 용지.[7] The food wrapping paper according to any one of [1] to [6], wherein the third coated layer further contains paraffin wax.
[8] 상기 제 3 도공층의 상기 파라핀 왁스가, 융점 50 ℃ 이상 80 ℃ 이하의 것인 상기 [7] 에 기재된 식품 포장 용지.[8] The food wrapping paper according to [7] above, wherein the paraffin wax of the third coated layer has a melting point of 50°C or more and 80°C or less.
[9] 상기 제 1 도공층의 상기 스티렌-부타디엔계 공중합 수지가, 공중합 수지 중의 스티렌계 단량체의 함유 질량 비율이 70 질량% 이상 90 질량% 이하의 것인 상기 [3] 에 기재된 식품 포장 용지.[9] The food packaging paper according to [3] above, wherein the styrene-butadiene-based copolymer resin of the first coated layer has a mass ratio of styrene-based monomers in the copolymer resin of 70% by mass or more and 90% by mass or less.
[10] 상기 제 1 도공층의 상기 아크릴계 수지가, 스티렌-아크릴계 공중합 수지 또는 스티렌-(메트)아크릴로니트릴-아크릴계 공중합 수지인 상기 [4] 에 기재된 식품 포장 용지.[10] The food packaging paper according to [4] above, wherein the acrylic resin of the first coating layer is a styrene-acrylic copolymer resin or a styrene-(meth)acrylonitrile-acrylic copolymer resin.
본 발명에 의해, 내수성, 내유성, 가스 배리어성, 수증기 배리어성 및 플레이버 배리어성을 갖고, 히트 시일 적성 및 접기 가공 적성을 구비하며, 그리고 내블로킹성을 갖는 식품 포장 용지를 제공할 수 있다.According to the present invention, it is possible to provide food packaging paper having water resistance, oil resistance, gas barrier properties, water vapor barrier properties and flavor barrier properties, heat sealability and folding processability, and blocking resistance.
식품 포장 용지는, 종이 지지체와, 상기 종이 지지체의 편면에 제 1 도공층과, 종이 지지체를 기준으로 하여 상기 제 1 도공층의 외측에 제 2 도공층과, 및 종이 지지체를 기준으로 하여 상기 제 2 도공층의 외측에 제 3 도공층을 갖는다. 즉, 식품 포장 용지는, 종이 지지체에 가까운 측에서부터 제 1 도공층, 제 2 도공층 및 제 3 도공층을 갖는다. 식품 포장 용지는, 종이 지지체, 제 1 도공층, 제 2 도공층 및 제 3 도공층의 각각 사이에, 가스 배리어성 및 수증기 배리어성의 향상 또는 도공층 간의 접착성의 향상 등을 목적으로 하여 중간 도공층을 가질 수 있다. 몇 가지 실시양태에 있어서, 식품 포장 용지는, 종이 지지체, 제 1 도공층, 제 2 도공층 및 제 3 도공층의 각각 사이에 중간 도공층을 갖지 않는다. 그 이유는, 식품 포장 용지의 제조 비용이 유리해지기 때문이다. 식품 포장 용지의 실시형태로서, 식품과 대향하는 식품 포장 용지의 면은, 식품 포장 용지의 제 1 도공층, 제 2 도공층 및 제 3 도공층을 갖는 측의 면이다. 또한, 식품 포장 용지는, 제 1 도공층, 제 2 도공층 및 제 3 도공층을 갖는 측에 대한 종이 지지체의 반대측에 있어서, 그라비어 인쇄기 및/또는 디지털 인쇄기에 대한 인쇄 적성을 향상시킬 목적을 위하여 또는 용지의 치수 안정성을 향상시킬 목적을 위하여, 인쇄용 도공층 또는 백코트층을 가질 수 있다. 인쇄용 도공층 또는 백코트층은, 인쇄용 도공지 분야에서 종래 공지된 것이다. 게다가, 식품 포장 용지는, 인쇄용 도공층과 종이 지지체와의 사이에 제 1 도공층, 제 2 도공층 및/또는 제 3 도공층을 가질 수 있다.Food packaging paper includes a paper support, a first coated layer on one side of the paper support, a second coated layer on the outside of the first coated layer based on the paper support, and the first coated layer on the basis of the paper support It has a 3rd coating layer on the outer side of 2 coating layers. That is, the food wrapping paper has a first coated layer, a second coated layer, and a third coated layer from the side closer to the paper support. In food packaging paper, between each of the paper support, the first coated layer, the second coated layer, and the third coated layer, an intermediate coated layer for the purpose of improving gas barrier properties and water vapor barrier properties or improving adhesion between coated layers. can have In some embodiments, the food wrapping paper does not have an intermediate coated layer between the paper support, each of the first coated layer, the second coated layer, and the third coated layer. The reason is that the manufacturing cost of food packaging paper becomes advantageous. As an embodiment of the food wrapping paper, the side of the food wrapping paper facing the food is the side having the first coated layer, the second coated layer and the third coated layer of the food wrapping paper. In addition, the food packaging paper, on the opposite side of the paper support to the side having the first coated layer, the second coated layer and the third coated layer, for the purpose of improving printability for a gravure printer and / or a digital printer Alternatively, for the purpose of improving the dimensional stability of the paper, it may have a coating layer for printing or a backcoat layer. A coated layer for printing or a backcoat layer is conventionally known in the field of coated paper for printing. In addition, the food packaging paper may have a first coated layer, a second coated layer, and/or a third coated layer between the coated layer for printing and the paper support.
종이 지지체는, 목재 펄프 및/또는 비목재 펄프로 이루어지는 슬러리에 대해, 전료 (塡料), 사이즈제, 바인더, 정착제, 수율제 및 지력제 등의 각종 첨가제를 필요에 따라 첨가한 지료 (紙料) 를, 산성, 중성 또는 알칼리성의 조건에서, 종래 공지된 초지 방법에 의해 초조한 원지, 상기 원지를 사이즈 프레스액으로 사이즈 프레스 처리한 상질지, 상기 원지를 표면 처리액으로 표면 처리한 상질지, 또는 상기 원지 혹은 상기 상질지에 대하여 캘린더 처리를 실시한 상질지이다.The paper support is a paper stock in which various additives such as filler, sizing agent, binder, fixing agent, yield agent, and strength agent are added as necessary to a slurry made of wood pulp and/or non-wood pulp.料), base paper prepared by a conventionally known papermaking method under acidic, neutral or alkaline conditions, high-quality paper obtained by size-pressing the base paper with a size press liquid, and high-quality paper obtained by surface-treating the base paper with a surface treatment liquid. , or a quality paper obtained by calendering the base paper or the quality paper.
또한, 상기 지료에는, 그 밖의 첨가제로서, 안료 분산제, 증량제, 증점제, 유동성 개량제, 피치 컨트롤제, 소포제, 억포제, 이형제, 발포제, 침투제, 보습제, 방부제, 방미제 (防黴劑), 내수화제, 습윤 지력 증강제 및 건조 지력 증강제 등에서 선택되는 1 종 또는 2 종 이상을, 본 발명의 원하는 효과를 손상시키지 않는 범위에서, 적절히 첨가할 수 있다.Further, in the stock, as other additives, a pigment dispersant, an extender, a thickener, a fluidity improver, a pitch control agent, an antifoaming agent, an antifoaming agent, a mold release agent, a foaming agent, a penetrant, a humectant, an antiseptic agent, an antifoaming agent, and a water resistance agent. , wet strength agents, dry strength agents, etc., one or more selected from the group consisting of, etc., can be added as appropriate within a range not impairing the desired effect of the present invention.
캘린더 처리란, 롤 사이에 종이를 통과시킴으로써 평활성이나 두께를 평균화하는 처리이다. 캘린더 처리의 장치는, 예를 들면, 머신 캘린더, 소프트 닙 캘린더, 슈퍼 캘린더, 다단 캘린더, 멀티 닙 캘린더 등을 들 수 있다.A calendering process is a process which averages smoothness and thickness by passing paper between rolls. Examples of calendering devices include machine calenders, soft nip calenders, super calenders, multi-stage calenders, and multi-nip calenders.
목재 펄프는, 제지 분야에서 종래 공지된 것이다. 목재 펄프는, 예를 들면, LBKP (Leaf Bleached Kraft Pulp) 및 NBKP (Needle Bleached Kraft Pulp) 등의 화학 펄프, GP (Groundwood Pulp), PGW (Pressure GroundWood pulp), RMP (Refiner Mechanical Pulp), TMP (ThermoMechanical Pulp), CTMP (ChemiThermoMechanical Pulp), CMP (ChemiMechanical Pulp) 및 CGP (ChemiGroundwood Pulp) 등의 기계 펄프, 그리고 DIP (DeInked Pulp) 등의 고지 펄프를 들 수 있다.Wood pulp is conventionally known in the papermaking field. Wood pulp, for example, chemical pulp such as LBKP (Leaf Bleached Kraft Pulp) and NBKP (Needle Bleached Kraft Pulp), GP (Groundwood Pulp), PGW (Pressure GroundWood pulp), RMP (Refiner Mechanical Pulp), TMP ( mechanical pulps such as ThermoMechanical Pulp), ChemiThermoMechanical Pulp (CTMP), ChemiMechanical Pulp (CMP) and ChemiGroundwood Pulp (CGP), and used paper pulp such as DeInked Pulp (DIP).
비목재 펄프는, 제지 분야에서 종래 공지된 비목재 섬유로 이루어지는 펄프이다. 비목재 섬유의 원료는, 예를 들면, 닥나무, 삼지닥나무 및 안피나무 등의 목본 인피, 아마, 대마 및 케나프 등의 초본 인피, 마닐라삼, 아바카 및 사이잘삼 등의 엽섬유, 벼짚, 밀짚, 사탕수수 버개스, 대나무 및 에스파르토 등의 화본과 식물, 그리고 솜 및 린터 등의 종모를 들 수 있다. 목재 펄프 및/또는 비목재 펄프는, 상기 목재 펄프 및 상기 비목재 펄프로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상이다.Non-wood pulp is a pulp composed of non-wood fibers conventionally known in the papermaking field. Raw materials for non-wood fiber include, for example, wooden bast such as paper mulberry, mulberry mulberry, and chinensis, herbaceous bast such as flax, hemp, and kenaf, leaf fibers such as manila hemp, abaca, and sisal hemp, rice straw, and wheat straw. , sugarcane bagasse, flowers and plants such as bamboo and esparto, and seed hairs such as cotton and linters. The wood pulp and/or non-wood pulp is one or two or more selected from the group consisting of the wood pulp and the non-wood pulp.
전료는, 제지 분야에서 종래 공지된 안료이다. 안료는, 예를 들면, 경질 탄산칼슘, 중질 탄산칼슘, 각종 카올린, 탈크, 황산바륨, 이산화티탄, 산화아연, 황화아연, 탄산아연, 새틴 화이트, 실리카, 규산알루미늄, 규조토, 활성백토, 알루미나, 알루미나 수화물, 수산화알루미늄, 리토폰, 제올라이트, 탄산마그네슘, 수산화마그네슘 등의 무기 안료를 들 수 있다. 또한 스티렌계 플라스틱 피그먼트, 아크릴계 플라스틱 피그먼트, 폴리에틸렌계 플라스틱 피그먼트, 우레아 수지, 멜라민 수지 및 마이크로 캡슐 등의 유기 안료를 들 수 있다. 전료는, 상기 무기 안료 및 상기 유기 안료로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상이다.The filler is a conventionally known pigment in the papermaking field. Pigments include, for example, light calcium carbonate, ground calcium carbonate, various kaolins, talc, barium sulfate, titanium dioxide, zinc oxide, zinc sulfide, zinc carbonate, satin white, silica, aluminum silicate, diatomaceous earth, activated clay, alumina, and inorganic pigments such as alumina hydrate, aluminum hydroxide, lithopone, zeolite, magnesium carbonate, and magnesium hydroxide. In addition, organic pigments such as styrene-based plastic pigments, acrylic-based plastic pigments, polyethylene-based plastic pigments, urea resins, melamine resins, and microcapsules are exemplified. A filler is 1 type(s) or 2 or more types selected from the group which consists of the said inorganic pigment and the said organic pigment.
몇 가지 실시양태에 있어서, 식품 포장 용지는, 종이 지지체의 회분량이 8 질량% 이하이다. 그 이유는, 종이 지지체가, 유연성을 얻을 수 있으면서 또한 지력을 저하시키지 않기 때문이다. 여기서, 회분량이란, 연소 처리 전의 종이 지지체의 절건 질량에 대한 종이 지지체를 500 ℃ 에서 1 시간 연소 처리를 실시한 후의 불연물의 질량의 비율 (질량%) 이다. 회분량은, 종이 지지체 중의 전료 함유량을 조정하는 등의 종래 공지된 방법으로 제어할 수 있다.In some embodiments, food wrapping paper has an ash content of the paper support of 8% by mass or less. The reason is that the paper support can obtain flexibility and does not lower the paper strength. Here, the amount of ash is the ratio (mass%) of the mass of the incombustible material after burning the paper support at 500°C for 1 hour to the absolute dry mass of the paper support before combustion. The amount of ash can be controlled by conventionally known methods such as adjusting the content of filler in the paper support.
사이즈제는, 제지 분야에서 종래 공지된 내첨 사이즈제이다. 내첨 사이즈제는, 예를 들면, 산성지이면 로진계 사이즈제, 중성지이면 알케닐 무수 숙신산, 알킬케텐 다이머, 중성 로진계 사이즈제 및 카티온성 스티렌-아크릴계 사이즈제 등을 들 수 있다.The sizing agent is a conventionally known internal addition sizing agent in the papermaking field. Internal addition sizing agents include, for example, rosin-based sizing agents for acidic paper, alkenyl succinic anhydride, alkylketene dimer, neutral rosin-based sizing agents and cationic styrene-acrylic sizing agents for neutral paper.
또한 사이즈 프레스액에 사용하는 표면 사이즈제는, 제지 분야에서 종래 공지된 것이다. 표면 사이즈제는, 예를 들면, 전분계 사이즈제, 셀룰로오스계 사이즈제, 폴리비닐알코올계 사이즈제, 스티렌-아크릴계 사이즈제, 올레핀계 사이즈제, 스티렌-말레산계 사이즈제, 및 아크릴아미드계 사이즈제 등을 들 수 있다.In addition, the surface sizing agent used for the size press liquid is conventionally known in the papermaking field. Surface sizing agents include, for example, starch-based sizing agents, cellulose-based sizing agents, polyvinyl alcohol-based sizing agents, styrene-acrylic sizing agents, olefin-based sizing agents, styrene-maleic acid-based sizing agents, and acrylamide-based sizing agents. etc. can be mentioned.
사이즈 프레스 처리는, 제지 분야에서 종래 공지된 사이즈 프레스 장치를 사용하여 실시한다. 사이즈 프레스 장치의 예로는, 인클라인드 사이즈 프레스, 호리존탈 사이즈 프레스, 필름 트랜스퍼로서 로드 메탈링 사이즈 프레스, 롤 메탈링 사이즈 프레스 및 블레이드 메탈링 사이즈 프레스를, 상기 로드 메탈링 사이즈 프레스로서 심 사이저, 옵티사이저 및 스피드 사이저를, 상기 롤 메탈링 사이즈 프레스로서 게이트 롤 코터를, 또한 빌 블레이드 코터, 트윈 블레이드 코터, 벨바파 코터, 탭 사이즈 프레스, 그리고 캘린더 사이즈 프레스 등을 들 수 있다.The size press treatment is performed using a conventionally known size press device in the papermaking field. Examples of the size press device include an incline size press, a horizontal size press, a rod metal ring size press, a roll metal ring size press, and a blade metal ring size press as a film transfer, a seam sizer as the rod metal ring size press, An optimizer and a speed sizer, a gate roll coater as the roll metalling size press, and also a bill blade coater, a twin blade coater, a Velbafa coater, a tap size press, and a calender size press.
제 1 도공층은, 카올린, 그리고 바인더로서 스티렌-부타디엔계 공중합 수지 및 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유한다. 제 1 도공층은, 종이 지지체가 갖는 공극을 막는 피복층으로서 기능을 갖는다. 또한, 제 1 도공층은, 종이 지지체의 이면 (제 1 도공층, 제 2 도공층 및 제 3 도공층을 갖지 않는 측) 으로부터 수분 및 유분의 확산을 차폐하여 제 2 도공층을 보호하는 보호층으로서 기능을 갖는다. 또한, 제 1 도공층은, 종이 지지체와 제 2 도공층을 접착하는 접착층으로서 기능한다. 식품 포장 용지는, 제 1 도공층이 피복층, 보호층 및 접착층으로서 기능함으로써 결과적으로 가스 배리어성, 플레이버 배리어성 및 접기 가공 적성을 얻을 수 있다.A 1st coating layer contains kaolin and 1 type(s) or 2 or more types selected from the group which consists of a styrene-butadiene system copolymer resin and an acrylic resin as a binder. The first coating layer has a function as a coating layer that blocks voids of the paper support body. Further, the first coated layer is a protective layer that protects the second coated layer by shielding the diffusion of moisture and oil from the back surface of the paper support (the side not having the first coated layer, the second coated layer, and the third coated layer). has a function as Moreover, the 1st coating layer functions as an adhesive layer which adheres the paper support body and the 2nd coating layer. In food wrapping paper, gas barrier properties, flavor barrier properties, and folding processability can be obtained as a result of the first coating layer functioning as a coating layer, a protective layer, and an adhesive layer.
카올린은, 카올리나이트, 내크라이트, 디카이트, 할로이사이트, 가수 할로이사이트 등의 천연에서 산출된 카올린 원광을 공업적으로 정제 및 가공한 것으로서, 분쇄, 세정, 제철 및 분급 등의 공정을 거쳐 제조되는 것이다. 또, 카올린에는, 애스펙트비를 향상시키기 위해 전단력을 가하여 박판상으로 한 디라미네이티드 카올린, 입도 분포가 샤프해지도록 조정한 엔지니어드 카올린, 응집성을 높인 소성 카올린과 같은 가공성이 높은 것도 포함된다.Kaolin is industrially refined and processed kaolin ore produced from nature, such as kaolinite, nacrite, dickite, halloysite, and hydrous halloysite, and is manufactured through processes such as grinding, washing, ironing, and classification. . Further, kaolin includes delaminated kaolin obtained by applying a shearing force to improve the aspect ratio, engineered kaolin adjusted to sharpen particle size distribution, and calcined kaolin having increased cohesiveness.
카올린은, 통상, 평면부와 에지부에서 상이한 전하를 띤다. 카올린은, 전하를 띠기 때문에 다른 안료에 비해 바인더를 흡착하기 쉽다. 그리고, 스티렌-부타디엔계 공중합 수지는 안료에 대한 결합성이 높다. 아크릴계 수지는, 분자 내에 극성을 갖기 때문에, 카올린에 대하여 흡착이 우수하다. 따라서, 카올린과, 스티렌-부타디엔계 공중합 수지 및 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상의 조합을 포함하는 제 1 도공층은, 피막 형성이 우수하다. 그 결과, 피복층, 보호층 및 접착층으로서의 기능을 잘 발현한다.Kaolin usually has different electric charges on the flat surface and on the edge. Since kaolin is charged, it is easier to adsorb binders than other pigments. In addition, the styrene-butadiene-based copolymer resin has high binding properties to pigments. Since acrylic resins have polarity in their molecules, they are excellent in adsorption to kaolin. Accordingly, the first coated layer containing kaolin and one or a combination of two or more selected from the group consisting of styrene-butadiene-based copolymer resins and acrylic resins is excellent in film formation. As a result, functions as a coating layer, a protective layer, and an adhesive layer are well expressed.
몇 가지 실시양태에 있어서, 제 1 도공층은, 바인더로서 스티렌-부타디엔계 공중합 수지로 이루어지는 군에서 선택되는 1 종 혹은 2 종 이상, 또는 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 혹은 2 종 이상을 함유한다. 이 이유는, 스티렌-부타디엔계 공중합 수지로 이루어지는 군에서 선택되는 1 종 혹은 2 종 이상, 또는 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 혹은 2 종 이상이면, 피막 형성이 양화 (良化) 되기 때문이다. 이 이유는, 분자 중에 스티렌계 단량체를 함유하는 수지와 분자 중에 아크릴산계 단량체를 함유하는 수지는 공존하면 상분리되기 쉽기 때문이라고 생각된다.In some embodiments, the first coating layer uses one or two or more types selected from the group consisting of styrene-butadiene-based copolymer resins or one or two or more types selected from the group consisting of acrylic resins as a binder. contain The reason for this is that one or two or more types selected from the group consisting of styrene-butadiene-based copolymer resins, or one or two or more types selected from the group consisting of acrylic resins can improve film formation. am. The reason for this is considered to be because, when a resin containing a styrene-based monomer in its molecule and a resin containing an acrylic acid-based monomer in its molecule coexist, phase separation is likely to occur.
적어도 하나의 실시양태에 있어서, 제 1 도공층은, 바인더로서 스티렌-부타디엔계 공중합 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 또한 제 1 도공층에 있어서, 상기 스티렌-부타디엔계 공중합 수지의 합계 함유량은, 종이 지지체의 편면당 제 1 도공층 중의 카올린 100 질량부에 대하여 40 질량부 이상 400 질량부 이하이다. 그 이유는, 식품 포장 용지의 가스 배리어성, 플레이버 배리어성 및/또는 접기 가공 적성이 양화되기 때문이다.In at least one embodiment, the first coated layer contains one or two or more selected from the group consisting of styrene-butadiene-based copolymer resins as a binder, and in the first coated layer, the styrene-butadiene The total content of the copolymer resin is 40 parts by mass or more and 400 parts by mass or less with respect to 100 parts by mass of kaolin in the first coated layer per side of the paper support. The reason for this is that the gas barrier properties, flavor barrier properties and/or folding processability of the food packaging paper are improved.
스티렌-부타디엔계 공중합 수지는, 스티렌계 단량체와 부타디엔의 공중합 수지이다. 스티렌계 단량체는, 예를 들면, 스티렌 및 α-메틸스티렌 등의 비닐기에 치환기를 갖는 스티렌 유도체, 그리고 비닐톨루엔 및 p-클로르스티렌 등의 벤젠 고리에 치환기를 갖는 유도체를 들 수 있다. 몇 가지 실시양태에 있어서, 스티렌-부타디엔계 공중합 수지는, 공중합 수지 중의 스티렌계 단량체의 함유 질량 비율이 67 질량% 이상 100 질량% 미만인 것이다. 적어도 하나의 실시양태에 있어서, 스티렌-부타디엔계 공중합 수지는, 공중합 수지 중의 스티렌계 단량체의 함유 질량 비율이 70 질량% 이상 90 질량% 이하의 것이다. 이들의 이유는, 식품 포장 용지의 가스 배리어성, 플레이버 배리어성 및 접기 가공 적성이 양화되기 때문이다.A styrene-butadiene copolymer resin is a copolymer resin of a styrene monomer and butadiene. Styrenic monomers include, for example, styrene derivatives having a substituent on a vinyl group, such as styrene and α-methylstyrene, and derivatives having a substituent on a benzene ring, such as vinyltoluene and p-chlorostyrene. In some embodiments, the styrene-butadiene-based copolymer resin has a content mass ratio of styrenic monomers in the copolymer resin of 67% by mass or more and less than 100% by mass. In at least one embodiment, the styrene-butadiene-based copolymer resin has a content mass ratio of the styrenic monomer in the copolymer resin of 70% by mass or more and 90% by mass or less. The reason for these is that the gas barrier properties, flavor barrier properties, and folding processability of the food packaging paper are improved.
또한, 스티렌-부타디엔계 공중합 수지는, 스티렌계 단량체 및 부타디엔 이외에 스티렌계 단량체 및 부타디엔과 공중합 가능한 단량체를 가질 수 있다. 공중합 가능한 단량체의 예로는, (메트)아크릴로니트릴, (메트)아크릴산, (메트)아크릴산염, (메트)아크릴산에스테르, 말레산, 아세트산비닐, 염화비닐, 염화비닐리덴 및 에틸렌 등을 들 수 있다.In addition, the styrene-butadiene-based copolymer resin may have a styrene-based monomer and a monomer copolymerizable with butadiene in addition to the styrene-based monomer and butadiene. Examples of copolymerizable monomers include (meth)acrylonitrile, (meth)acrylic acid, (meth)acrylates, (meth)acrylic acid esters, maleic acid, vinyl acetate, vinyl chloride, vinylidene chloride, and ethylene. .
스티렌-부타디엔계 공중합 수지는, 공지된 유화 중합법에 의해 합성할 수 있다. 합성은, 예를 들면, 소정의 반응 용기에 각 단량체, 유화제 및 물을 배합하고, 라디칼 중합 개시제를 첨가하여 교반 및 가열하는 방법이다. 공중합 수지에 있어서 각 단량체의 함유 질량 비율은, 반응 용기에 배합하는 각 단량체의 배합량으로 조정할 수 있다. 스티렌-부타디엔계 공중합 수지는, 예를 들면, 덴카사, 아사히 화성사, BASF 사 및 JSR 사 등으로부터 시판된다.The styrene-butadiene copolymer resin can be synthesized by a known emulsion polymerization method. Synthesis is, for example, a method in which each monomer, an emulsifier and water are blended in a predetermined reaction vessel, a radical polymerization initiator is added, stirred and heated. The content mass ratio of each monomer in the copolymer resin can be adjusted by the compounding amount of each monomer blended in the reaction vessel. Styrene-butadiene-based copolymer resins are commercially available from, for example, Denkasa, Asahi Kasei, BASF, and JSR.
적어도 하나의 실시양태에 있어서, 제 1 도공층은, 바인더로서 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 또한 제 1 도공층에 있어서, 상기 아크릴계 수지의 합계 함유량은, 종이 지지체의 편면당 제 1 도공층 중의 카올린 100 질량부에 대하여 40 질량부 이상 400 질량부 이하이다. 그 이유는, 식품 포장 용지의 가스 배리어성, 플레이버 배리어성 및/또는 접기 가공 적성이 양화되기 때문이다.In at least one embodiment, the first coated layer contains one or two or more selected from the group consisting of acrylic resins as a binder, and in the first coated layer, the total content of the acrylic resins is, It is 40 parts by mass or more and 400 parts by mass or less with respect to 100 parts by mass of kaolin in the first coated layer per single side of the paper support body. The reason for this is that the gas barrier properties, flavor barrier properties and/or folding processability of the food packaging paper are improved.
몇 가지 실시양태에 있어서, 제 1 도공층의 아크릴계 수지는, 아크릴산계 단량체를 수지 중 50 질량% 초과로 함유하는 수지이다. 그 이유는, 식품 포장 용지의 가스 배리어성, 플레이버 배리어성 및/또는 접기 가공 적성이 양화되기 때문이다.In some embodiments, the acrylic resin of the first coating layer is a resin containing more than 50% by mass of an acrylic acid monomer in the resin. The reason for this is that the gas barrier properties, flavor barrier properties and/or folding processability of the food packaging paper are improved.
아크릴산계 단량체는, 예를 들면, (메트)아크릴산, (메트)아크릴산염 및 (메트)아크릴산알킬에스테르를 들 수 있다. (메트)아크릴산염의 예로는, (메트)아크릴산리튬, (메트)아크릴산나트륨, 메타아크릴산칼륨 및 2-술포에틸(메트)아크릴산나트륨 등을 들 수 있다. (메트)아크릴산알킬에스테르의 예로는, (메트)아크릴산메틸, (메트)아크릴산에틸, (메트)아크릴산n-프로필, (메트)아크릴산이소프로필, (메트)아크릴산n-부틸, (메트)아크릴산이소부틸, (메트)아크릴산t-부틸, (메트)아크릴산n-아밀, (메트)아크릴산이소아밀, (메트)아크릴산헥실, (메트)아크릴산시클로헥실, (메트)아크릴산옥틸, (메트)아크릴산2-에틸헥실, (메트)아크릴산n-노닐, (메트)아크릴산이소노닐, (메트)아크릴산라우릴, (메트)아크릴산스테아릴, (메트)아크릴산데실 및 (메트)아크릴산운데실 등을 들 수 있다. 또한, 아크릴산계 단량체의 예로는, (메트)아크릴산2-하이드록시에틸, (메트)아크릴산2-하이드록시프로필, (메트)아크릴산2-하이드록시부틸, (메트)아크릴산4-하이드록시부틸, 모노(메트)아크릴산폴리에틸렌글리콜, (메트)아크릴산2-하이드록시-3-페녹시프로필, 모노(메트)아크릴산글리세롤, 디(메트)아크릴산에틸렌글리콜, 디(메트)아크릴산디에틸렌글리콜, 디(메트)아크릴산트리에틸렌글리콜, 디(메트)아크릴산(폴리)에틸렌글리콜, 디(메트)아크릴산디프로필렌글리콜, 디(메트)아크릴산1,2-프로필렌글리콜, 디(메트)아크릴산1,3-프로필렌글리콜, 디(메트)아크릴산1,3-부틸렌글리콜, 트리(메트)아크릴산트리메틸올프로판, 테트라(메트)아크릴산테트라메틸올메탄, 디(메트)아크릴산1,4-부탄디올, 디(메트)아크릴산1,6-헥산디올, 디(메트)아크릴산네오펜틸글리콜, 트리(메트)아크릴산트리메틸올프로판, (메트)아크릴산알릴, (메트)아크릴산글리시딜, (메트)아크릴산메틸글리시딜, (메트)아크릴산디아세톤, (메트)아크릴산아세토닐, (메트)아크릴산2-아세토아세톡시에틸, 그리고 (메트)아크릴산3,4-에폭시시클로헥실, (메트)아크릴산벤질, (메트)아크릴산2-메톡시에틸, (메트)아크릴산2-(2-에톡시에톡시)에틸, 폴리카프로락톤 변성 하이드록시알킬(메트)아크릴산에스테르, (메트)아크릴산아세토닐, (메트)아크릴산2-(아세토아세틸옥시)에틸, 및 (메트)아크릴산(3,4-에폭시시클로헥실)메틸 등을 들 수 있다.Examples of the acrylic acid-based monomer include (meth)acrylic acid, (meth)acrylic acid salts, and (meth)acrylic acid alkyl esters. Examples of the (meth)acrylate include lithium (meth)acrylate, sodium (meth)acrylate, potassium methacrylate, and sodium 2-sulfoethyl (meth)acrylate. Examples of the (meth)acrylic acid alkyl ester include methyl (meth)acrylate, ethyl (meth)acrylate, n-propyl (meth)acrylate, isopropyl (meth)acrylate, n-butyl (meth)acrylate, and iso(meth)acrylate. Butyl, t-butyl (meth)acrylate, n-amyl (meth)acrylate, isoamyl (meth)acrylate, hexyl (meth)acrylate, cyclohexyl (meth)acrylate, octyl (meth)acrylate, (meth)acrylic acid 2 -Ethylhexyl, n-nonyl (meth)acrylate, isononyl (meth)acrylate, lauryl (meth)acrylate, stearyl (meth)acrylate, decyl (meth)acrylate and undecyl (meth)acrylate, etc. there is. In addition, examples of the acrylic acid-based monomer include 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 2-hydroxybutyl (meth)acrylate, 4-hydroxybutyl (meth)acrylate, mono Polyethylene glycol (meth)acrylate, 2-hydroxy-3-phenoxypropyl (meth)acrylate, glycerol mono(meth)acrylate, ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, di(meth)acrylate Triethylene glycol acrylate, di(meth)acrylic acid (poly)ethylene glycol, di(meth)acrylic acid dipropylene glycol, di(meth)acrylic acid 1,2-propylene glycol, di(meth)acrylic acid 1,3-propylene glycol, di(meth)acrylic acid 1,3-propylene glycol, (meth)acrylate 1,3-butylene glycol, tri(meth)acrylate trimethylolpropane, tetra(meth)acrylate tetramethylolmethane, di(meth)acrylate 1,4-butanediol, di(meth)acrylate 1,6 -Hexanediol, di(meth)acrylate neopentyl glycol, tri(meth)acrylate trimethylolpropane, allyl (meth)acrylate, glycidyl (meth)acrylate, methylglycidyl (meth)acrylate, di(meth)acrylate Acetone, acetonyl (meth)acrylate, 2-acetoacetoxyethyl (meth)acrylate, and 3,4-epoxycyclohexyl (meth)acrylate, benzyl (meth)acrylate, 2-methoxyethyl (meth)acrylate, ( 2-(2-ethoxyethoxy)ethyl meth)acrylate, polycaprolactone-modified hydroxyalkyl (meth)acrylate ester, acetonyl (meth)acrylate, 2-(acetoacetyloxy)ethyl (meth)acrylate, and ( meth)acrylic acid (3,4-epoxycyclohexyl) methyl; and the like.
아크릴계 수지는, 아크릴산계 단량체 이외에 아크릴산계 단량체와 공중합 가능한 다른 단량체를 함유할 수 있다. 다른 단량체의 예로는, 스티렌, 아세트산비닐, 염화비닐, (메트)아크릴로니트릴, 에틸렌, 프로필렌, 디비닐벤젠, N-메틸올(메트)아크릴아미드, N-메톡시메틸(메트)아크릴아미드, N-부톡시메틸(메트)아크릴아미드, N,N'-메틸렌비스(메트)아크릴아미드, 비닐술폰산나트륨, p-스티렌술폰산나트륨, 2-아크릴아미드-2-메틸프로판술폰산, 3-알릴옥시-2-하이드록시프로판술폰산나트륨, 폴리옥시에틸렌스티렌화페닐황산나트륨, 글리세린모노알릴에테르모노술포숙신산나트륨, (메트)아크릴아미드스테아르산나트륨, 디알릴프탈레이트, 트리알릴시아누레이트, 아크롤레인, 디아세톤(메트)아크릴아미드, 포르밀 스티롤, 비닐메틸케톤, 비닐에틸케톤, (메트)아크릴로일옥시알킬프로펜알 및 디아세톤(메트)아크릴아미드 등을 들 수 있다.The acrylic resin may contain other monomers copolymerizable with the acrylic acid monomer other than the acrylic acid monomer. Examples of other monomers include styrene, vinyl acetate, vinyl chloride, (meth)acrylonitrile, ethylene, propylene, divinylbenzene, N-methylol(meth)acrylamide, N-methoxymethyl(meth)acrylamide, N-butoxymethyl(meth)acrylamide, N,N'-methylenebis(meth)acrylamide, sodium vinylsulfonate, sodium p-styrenesulfonate, 2-acrylamide-2-methylpropanesulfonic acid, 3-allyloxy- Sodium 2-hydroxypropanesulfonate, sodium polyoxyethylene styrenated phenyl sulfate, sodium glycerin monoallylether monosulfosuccinate, sodium (meth)acrylamide stearate, diallylphthalate, triallyl cyanurate, acrolein, diacetone (meth) ) Acrylamide, formyl styrole, vinyl methyl ketone, vinyl ethyl ketone, (meth) acryloyloxyalkyl propenal, and diacetone (meth) acrylamide.
몇 가지 실시양태에 있어서, 아크릴계 수지는, 상기 아크릴산계 단량체로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상의 단량체를 중합하여 이루어지는 수지이다. 또한, 몇 가지 실시양태에 있어서, 아크릴계 수지는, 상기 아크릴산계 단량체로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상의 단량체와, 상기 아크릴산계 단량체 이외의 단량체로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상의 단량체를 공중합하여 이루어지는 수지이다.In some embodiments, the acrylic resin is a resin obtained by polymerizing one or two or more monomers selected from the group consisting of the acrylic acid monomers. In some embodiments, the acrylic resin is one or two or more monomers selected from the group consisting of the acrylic acid monomers and one or two monomers selected from the group consisting of monomers other than the acrylic acid monomers. It is resin formed by copolymerizing the above monomers.
또한, 몇 가지 실시양태에 있어서, 아크릴계 수지는, 아크릴산계 단량체와 스티렌이 공중합한 스티렌-아크릴계 공중합 수지 또는 아크릴산계 단량체와 스티렌과 (메트)아크릴로니트릴이 공중합한 스티렌-(메트)아크릴로니트릴-아크릴계 공중합 수지이다. 적어도 하나의 실시양태에 있어서, 아크릴계 수지는, (메트)아크릴산, (메트)아크릴산염 및 (메트)아크릴산알킬에스테르로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상의 아크릴산계 단량체와 스티렌이 공중합한 스티렌-아크릴계 공중합 수지이다. 또한, 적어도 하나의 실시양태에 있어서, 아크릴계 수지는, (메트)아크릴산, (메트)아크릴산염 및 (메트)아크릴산알킬에스테르로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상의 아크릴산계 단량체와 스티렌과 (메트)아크릴로니트릴이 공중합한 스티렌-(메트)아크릴로니트릴-아크릴계 공중합 수지이다. 이들의 이유는, 식품 포장 용지의 가스 배리어성 및 플레이버 배리어성이 양화되기 때문이다. 아크릴계 수지는, 예를 들면, 미츠이 화학사, 토아 합성사, 다이이치도료 제조소사, DIC 사, PS 재팬사, 니혼 폴리에틸렌사, 아사히 화성사, 도레이사, 미츠이·다우 폴리케미컬사 및 BASF 사 등으로부터 시판된다.In addition, in some embodiments, the acrylic resin is a styrene-acrylic copolymer resin copolymerized with an acrylic acid monomer and styrene or a styrene-(meth)acrylonitrile copolymerized with an acrylic acid monomer and styrene and (meth)acrylonitrile. - It is an acrylic copolymer resin. In at least one embodiment, the acrylic resin is styrene copolymerized with one or two or more acrylic acid monomers selected from the group consisting of (meth)acrylic acid, (meth)acrylates and (meth)acrylic acid alkyl esters and styrene. - It is an acrylic copolymer resin. Further, in at least one embodiment, the acrylic resin is composed of one or two or more acrylic acid monomers selected from the group consisting of (meth)acrylic acid, (meth)acrylates and (meth)acrylic acid alkyl esters, and styrene and ( It is a styrene-(meth)acrylonitrile-acrylic copolymer resin copolymerized with meth)acrylonitrile. The reason for these is that the gas barrier properties and flavor barrier properties of the food wrapping paper are improved. Acrylic resins are commercially available from, for example, Mitsui Chemicals, Toa Chemicals, Daiichi Paints, DIC, PS Japan, Nippon Polyethylene, Asahi Kasei, Toray, Mitsui-Dow Polychemicals, BASF, etc. do.
아크릴계 수지는, 공지된 유화 중합법에 의해 합성할 수 있다. 합성은, 예를 들면, 소정의 반응 용기에 각 단량체, 유화제 및 물을 배합하고, 라디칼 중합 개시제를 첨가하여 교반 및 가열하는 방법이다. 공중합 수지에 있어서 각 단량체의 함유 질량 비율은, 반응 용기에 배합하는 각 단량체의 배합량으로 조정할 수 있다.Acrylic resin is compoundable by a well-known emulsion polymerization method. Synthesis is, for example, a method in which each monomer, an emulsifier and water are blended in a predetermined reaction vessel, a radical polymerization initiator is added, stirred and heated. The content mass ratio of each monomer in the copolymer resin can be adjusted by the compounding amount of each monomer blended in the reaction vessel.
제 1 도공층은, 카올린, 그리고 바인더로서 스티렌-부타디엔계 공중합 수지 및 아크릴계 수지 이외에, 필요에 따라 종래 공지된 각종 첨가제를 함유할 수 있다. 첨가제는, 예를 들면, 카올린 이외의 무기 안료, 유기 안료, 스티렌-부타디엔계 공중합 수지 및 아크릴계 수지 이외의 각종 바인더, 전분류 및 셀룰로오스류 등의 다당류, 계면 활성제, 분산제, 증점제, 보수제, 소포제, 내수화제 등을 들 수 있다.The first coating layer may contain conventionally known various additives as necessary in addition to kaolin and a styrene-butadiene-based copolymer resin and an acrylic resin as binders. Additives include, for example, inorganic pigments other than kaolin, organic pigments, various binders other than styrene-butadiene-based copolymer resins and acrylic resins, polysaccharides such as starches and celluloses, surfactants, dispersants, thickeners, water retention agents, antifoaming agents, A water-resistance agent etc. are mentioned.
제 2 도공층은, 수지의 구성 단위로서 염화비닐리덴 단량체를 주성분으로서 갖는 폴리염화비닐리덴계 중합 수지를 함유한다. 몇 가지 실시양태에 있어서, 제 2 도공층 중의 폴리염화비닐리덴계 중합 수지의 함유량은, 종이 지지체의 편면당, 제 2 도공층의 건조 고형분량에 대하여 85 질량% 이상이다. 그 이유는, 폴리염화비닐리덴계 중합 수지가 배리어제가 되어, 식품 포장 용지의 가스 배리어성, 수증기 배리어성 및 플레이버 배리어성이 양화되기 때문이다.The second coating layer contains a polyvinylidene chloride-based polymerized resin having a vinylidene chloride monomer as a main component as a resin constituent unit. In some embodiments, the content of the polyvinylidene chloride-based polymeric resin in the second coated layer is 85% by mass or more with respect to the dry solid content of the second coated layer per single side of the paper support. The reason is that the polyvinylidene chloride-based polymeric resin serves as a barrier agent, and the gas barrier properties, water vapor barrier properties, and flavor barrier properties of the food packaging paper are improved.
제 2 도공층은, 폴리염화비닐리덴계 중합 수지 이외에, 필요에 따라 종래 공지된 각종 첨가제를 함유할 수 있다. 첨가제는, 예를 들어, 무기 안료, 유기 안료, 폴리염화비닐리덴계 중합 수지 이외의 각종 수지, 전분류 및 셀룰로오스류 등의 다당류, 계면 활성제, 분산제, 증점제, 보수제, 소포제, 내수화제 등을 들 수 있다.The 2nd coating layer can contain conventionally well-known various additives as needed other than polyvinylidene chloride type polymeric resin. Additives include, for example, inorganic pigments, organic pigments, various resins other than polyvinylidene chloride-based polymeric resins, polysaccharides such as starches and celluloses, surfactants, dispersants, thickeners, water retention agents, antifoaming agents, water-resistant agents, and the like. can
수지의 구성 단위로서 염화비닐리덴 단량체를 주성분으로 갖는 폴리염화비닐리덴계 중합 수지는, 수지 중, 염화비닐리덴 단량체가 80 질량% 를 초과하는 것이다. 몇 가지 실시양태에 있어서, 수지의 구성 단위로서 염화비닐리덴 단량체를 주성분으로 갖는 폴리염화비닐리덴계 중합 수지는, 염화비닐리덴 단량체와, 염화비닐리덴 단량체와 공중합할 수 있는 기타 단량체의 1 종 또는 2 종 이상을 공중합하여 얻어지는 수지이다.In the polyvinylidene chloride-based polymeric resin, which has a vinylidene chloride monomer as a main component as a structural unit of the resin, the vinylidene chloride monomer exceeds 80% by mass in the resin. In some embodiments, the polyvinylidene chloride-based polymeric resin having a vinylidene chloride monomer as a main component as a constituent unit of the resin is one of a vinylidene chloride monomer and other monomers copolymerizable with the vinylidene chloride monomer, or It is resin obtained by copolymerizing 2 or more types.
또한, 몇 가지 실시양태에 있어서, 수지의 구성 단위로서 염화비닐리덴 단량체를 주성분으로 갖는 폴리염화비닐리덴계 중합 수지는, 수지 중, 염화비닐리덴 단량체가 85 질량% 이상의 것이다. 그 이유는, 수지 중의 염화비닐리덴 단량체가 85 질량% 이상이면, 식품 포장 용지의 가스 배리어성 및 수증기 배리어성이 양화되기 때문이다. 또한, 몇 가지 실시양태에 있어서, 수지의 구성 단위로서 염화비닐리덴 단량체를 주성분으로 갖는 폴리염화비닐리덴계 중합 수지는, 수지 중, 염화비닐리덴 단량체가 95 질량% 이하의 것이다. 이 이유는, 염화비닐리덴 단량체가 95 질량% 이하이면, 제 2 도공층의 피막 형성시에 빠른 결정화를 억제할 수 있기 때문에 제 2 도공층이 정지 (整地) 할 시간을 얻을 수 있다. 그 결과, 제 2 도공층에 있어서의 결함이 경감되어, 식품 포장 용지의 가스 배리어성 및 수증기 배리어성이 양화되기 때문이다. 적어도 하나의 실시양태에 있어서, 수지의 구성 단위로서 염화비닐리덴 단량체를 주성분으로 갖는 폴리염화비닐리덴계 중합 수지는, 수지 중, 염화비닐리덴 단량체가 85 질량% 이상 95 질량% 이하의 수지이다.In addition, in some embodiments, the polyvinylidene chloride-based polymeric resin having a vinylidene chloride monomer as a main component as a constituent unit of the resin contains 85% by mass or more of the vinylidene chloride monomer. The reason is that when the vinylidene chloride monomer in the resin is 85% by mass or more, the gas barrier properties and water vapor barrier properties of the food wrapping paper are improved. In addition, in some embodiments, the polyvinylidene chloride-based polymeric resin having a vinylidene chloride monomer as a main component as a constituent unit of the resin is a resin having a vinylidene chloride monomer of 95% by mass or less. The reason for this is that if the vinylidene chloride monomer is 95% by mass or less, rapid crystallization can be suppressed at the time of film formation of the second coated layer, so that time for the second coated layer to stop can be obtained. As a result, defects in the second coating layer are reduced, and the gas barrier properties and water vapor barrier properties of the food wrapping paper are improved. In at least one embodiment, the polyvinylidene chloride-based polymeric resin having a vinylidene chloride monomer as a main component as a constituent unit of the resin is a resin having 85% by mass or more and 95% by mass or less of the vinylidene chloride monomer in the resin.
염화비닐리덴 단량체와 공중합할 수 있는 상기 기타 단량체는, 염화비닐리덴 단량체와 공중합할 수 있는 단량체이면 특별히 한정되지 않는다. 기타 단량체는, 예를 들면, (메트)아크릴로니트릴, (메트)아크릴산메틸, (메트)아크릴산에틸, (메트)아크릴산프로필, (메트)아크릴산n-부틸, (메트)아크릴산t-부틸, (메트)아크릴산헥실, (메트)아크릴산2-에틸헥실, (메트)아크릴산노닐, (메트)아크릴산벤질, (메트)아크릴산시클로헥실, (메트)아크릴산라우릴, (메트)아크릴산n-옥틸, (메트)아크릴산2-메톡시에틸, (메트)아크릴산부톡시에틸, (메트)아크릴산메톡시트리에틸렌글리콜, (메트)아크릴산2-하이드록시에틸, (메트)아크릴산2-하이드록시프로필, (메트)아크릴산3-클로로-2-하이드록시프로필, (메트)아크릴산테트라하이드로푸르푸릴, (메트)아크릴산2-하이드록시-3-페녹시프로필, (메트)아크릴산디에틸렌글리콜, (메트)아크릴산폴리에틸렌글리콜, (메트)아크릴산2-(디메틸아미노)에틸, N,N-디메틸아크릴아미드, N-메틸올(메트)아크릴아미드, N-비닐피롤리돈, 프로피온산비닐, 스테아르산비닐, 염화비닐, 아세트산비닐, 및 스티렌 등을 들 수 있다.The other monomer copolymerizable with the vinylidene chloride monomer is not particularly limited as long as it is a monomer copolymerizable with the vinylidene chloride monomer. Other monomers include, for example, (meth)acrylonitrile, methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, n-butyl (meth)acrylate, t-butyl (meth)acrylate, ( Hexyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, nonyl (meth)acrylate, benzyl (meth)acrylate, cyclohexyl (meth)acrylate, lauryl (meth)acrylate, n-octyl (meth)acrylate, (meth)acrylate ) 2-methoxyethyl acrylate, butoxyethyl (meth)acrylate, methoxytriethylene glycol (meth)acrylate, 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, (meth)acrylic acid 3-chloro-2-hydroxypropyl, (meth)acrylate tetrahydrofurfuryl, (meth)acrylate 2-hydroxy-3-phenoxypropyl, (meth)acrylate diethylene glycol, (meth)acrylate polyethylene glycol, ( 2-(dimethylamino)ethyl meth)acrylate, N,N-dimethylacrylamide, N-methylol(meth)acrylamide, N-vinylpyrrolidone, vinyl propionate, vinyl stearate, vinyl chloride, vinyl acetate, and Styrene etc. are mentioned.
몇 가지 실시양태에 있어서, 제 2 도공층의 폴리염화비닐리덴계 중합 수지는, 상기 기타 단량체가 (메트)아크릴로니트릴, (메트)아크릴산메틸, (메트)아크릴산에틸 및 (메트)아크릴산2-하이드록시에틸로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상이다. 몇 가지 실시양태로서, 상기 폴리염화비닐리덴계 중합 수지는, 수지 중, 염화비닐리덴 단량체가 85 질량% 이상 95 질량% 이하, 및 (메트)아크릴로니트릴로 이루어지는 군에서 선택되는 단량체가 2 질량% 이상 10 질량% 이하, 그리고 (메트)아크릴산메틸, (메트)아크릴산에틸 및 (메트)아크릴산2-하이드록시에틸로 이루어지는 군에서 선택되는 단량체가 0.5 질량% 이상 5 질량% 이하의 것이다. 적어도 하나의 실시양태로서, 상기 폴리염화비닐리덴계 중합 수지는, 수지 중, 염화비닐리덴 단량체가 85 질량% 이상 95 질량% 이하, (메트)아크릴로니트릴로 이루어지는 군에서 선택되는 단량체가 2 질량% 이상 10 질량% 이하, 그리고 (메트)아크릴산메틸 및 (메트)아크릴산에틸로 이루어진 군에서 선택되는 단량체가 0.5 질량% 이상 5 질량% 이하의 것이다. 이들의 이유는, 식품 포장 용지의 가스 배리어성 및 수증기 배리어성이 양화되기 때문이다.In some embodiments, the polyvinylidene chloride-based polymeric resin of the second coating layer is such that the other monomers are (meth)acrylonitrile, methyl (meth)acrylate, ethyl (meth)acrylate, and 2- (meth)acrylate. It is 1 type(s) or 2 or more types selected from the group which consists of hydroxyethyl. In some embodiments, the polyvinylidene chloride-based polymeric resin contains 85% by mass or more and 95% by mass or less of vinylidene chloride monomer in the resin, and 2 mass% of a monomer selected from the group consisting of (meth)acrylonitrile. % or more and 10 mass% or less, and a monomer selected from the group consisting of methyl (meth)acrylate, ethyl (meth)acrylate, and 2-hydroxyethyl (meth)acrylate is 0.5 mass% or more and 5 mass% or less. In at least one embodiment, the polyvinylidene chloride-based polymeric resin contains 85% by mass or more and 95% by mass or less of vinylidene chloride monomer in the resin, and 2 mass% of a monomer selected from the group consisting of (meth)acrylonitrile. % or more and 10 mass% or less, and a monomer selected from the group consisting of methyl (meth)acrylate and ethyl (meth)acrylate is 0.5 mass% or more and 5 mass% or less. The reason for these is that the gas barrier properties and water vapor barrier properties of the food wrapping paper are improved.
또한, 폴리염화비닐리덴계 중합 수지 중, 염화비닐리덴 단량체와 상기 기타 단량체의 함유 비율의 합계가 100 질량% 에 미치지 않는 경우에는, 이들 단량체와 공중합 가능한 1 종 또는 2 종 이상의 단량체를 포함해도 된다.In addition, when the total content of the vinylidene chloride monomer and the other monomers is less than 100% by mass in the polyvinylidene chloride-based polymeric resin, one or two or more monomers copolymerizable with these monomers may be included. .
폴리염화비닐리덴계 중합 수지의 분자량은, 특별히 한정되지 않는다. 몇 가지 실시양태에 있어서, 폴리염화비닐리덴계 중합 수지의 분자량은, 분자량이 이미 알려진 폴리스티렌을 표준 물질로 하여 겔 퍼미에이션 크로마토그래피에 의해 측정된 중량 평균 분자량으로 8만 이상이다. 그 이유는, 상기 분자량의 범위이면, 폴리염화비닐리덴계 중합 수지의 열 및 광에 대한 안정성이 좋아지기 때문이다.The molecular weight of the polyvinylidene chloride-based polymeric resin is not particularly limited. In some embodiments, the molecular weight of the polyvinylidene chloride-based polymeric resin is 80,000 or more as a weight average molecular weight measured by gel permeation chromatography using polystyrene, whose molecular weight is already known, as a standard material. The reason is that stability to heat and light of the polyvinylidene chloride-based polymeric resin is improved within the above molecular weight range.
폴리염화비닐리덴계 중합 수지는, 공지된 유화 중합법에 의해 합성할 수 있다. 합성은, 예를 들면, 소정의 반응 용기에 각종 단량체, 유화제 및 물을 배합하고, 라디칼 중합 개시제를 첨가하여 교반 및 가온하는 방법이다. 또한, 폴리염화비닐리덴계 중합 수지는, 예를 들면, 아사히 화성사 등으로부터 시판된다.The polyvinylidene chloride-based polymerization resin can be synthesized by a known emulsion polymerization method. The synthesis is, for example, a method in which various monomers, an emulsifier and water are blended in a predetermined reaction vessel, a radical polymerization initiator is added, and stirred and heated. In addition, polyvinylidene chloride type polymerization resin is commercially available, for example from Asahi Chemical Co., Ltd. and the like.
제 3 도공층은, 아크릴계 수지를 함유한다. 제 3 도공층은, 아크릴계 수지가 내수 내유제가 되어, 내수 내유층으로서 기능한다. 제 3 도공층이 함유하는 아크릴계 수지는, 내수 내유성을 발현하는 수지이면 되고, 제 3 도공층이 함유하는 아크릴계 수지를 구성하는 단량체는, 상기 제 1 도공층에 관한 아크릴계 수지를 구성하는 단량체와 동일하며, 설명을 생략한다. 또한, 제 1 도공층이 아크릴계 수지를 함유하는 경우, 제 1 도공층의 아크릴계 수지와 제 3 도공층의 아크릴계 수지는, 동종의 수지 또는 이종의 수지 중 어느 것이어도 된다.The 3rd coating layer contains acrylic resin. In the third coated layer, the acrylic resin serves as a water- and oil-resistant layer and functions as a water- and oil-resistant layer. The acrylic resin contained in the third coated layer may be a resin exhibiting water resistance and oil resistance, and the monomer constituting the acrylic resin contained in the third coated layer is the same as the monomer constituting the acrylic resin related to the first coated layer. and omit the explanation. In addition, when the 1st coating layer contains acrylic resin, the acrylic resin of the 1st coating layer and the acrylic resin of the 3rd coating layer may either be resin of the same type or resin of a different type.
몇 가지 실시양태에 있어서, 제 3 도공층의 아크릴계 수지는, 아크릴산계 단량체와 스티렌이 공중합한 스티렌-아크릴계 공중합 수지이다. 그 이유는, 제 3 도공층의 아크릴계 수지가 스티렌-아크릴계 공중합 수지이면, 폴리염화비닐리덴계 중합 수지를 함유하는 제 2 도공층에 대하여 밀착성 및 피막 형성성이 좋고, 그 결과, 식품 포장 용지의 접기 가공 적성이 양화되기 때문이다. 또한 이 이유는, 아크릴계 수지가 결정성이 높은 스티렌을 함유함으로써 식품 포장 용지의 내블로킹성이 양화되기 때문이다. 또한, 몇 가지 실시양태에 있어서, 제 3 도공층의 아크릴계 수지는, 수지 중, 아크릴산계 단량체로서 (메트)아크릴산알킬에스테르를 50 질량% 초과로 함유한다. 그 이유는, 내수성 및 내유성이 양화되기 때문이다. 적어도 하나의 실시양태에 있어서, 제 3 도공층의 아크릴계 수지는, 수지 중, 아크릴산계 단량체로서 (메트)아크릴산알킬에스테르를 50 질량% 초과로 함유하면서, (메트)아크릴산알킬에스테르와 스티렌이 공중합한 스티렌-아크릴계 공중합 수지이다.In some embodiments, the acrylic resin of the third coating layer is a styrene-acrylic copolymer resin obtained by copolymerization of an acrylic acid monomer and styrene. The reason is that when the acrylic resin of the third coated layer is a styrene-acrylic copolymer resin, the adhesion and film formation properties to the second coated layer containing the polyvinylidene chloride polymeric resin are good, and as a result, food packaging paper This is because the folding processing aptitude is improved. Further, this reason is that the blocking resistance of the food packaging paper is improved when the acrylic resin contains styrene having high crystallinity. In addition, in some embodiments, the acrylic resin of the third coating layer contains (meth)acrylic acid alkyl ester in an amount of more than 50% by mass as an acrylic acid monomer in the resin. The reason is that water resistance and oil resistance are improved. In at least one embodiment, the acrylic resin of the third coating layer is obtained by copolymerizing (meth)acrylic acid alkyl ester with styrene while containing more than 50% by mass of (meth)acrylic acid alkyl ester as an acrylic acid-based monomer in the resin. It is a styrene-acrylic copolymer resin.
몇 가지 실시양태에 있어서, 제 3 도공층은, 파라핀 왁스를 추가로 함유한다. 그 이유는, 식품 포장 용지의 수증기 배리어성 및/또는 내블로킹성이 양화되기 때문이다. 적어도 하나의 실시양태에 있어서, 제 3 도공층 중의 파라핀 왁스의 함유량은, 종이 지지체의 편면당, 제 3 도공층 중의 아크릴계 수지 100 질량부에 대하여 3 질량부 이상 15 질량부 이하이다. 이 이유는, 파라핀 왁스의 함유량이 이 범위이면, 식품 포장 용지의 히트 시일 적성을 저해하지 않고서 수증기 배리어성 및 내블로킹성을 양화할 수 있기 때문이다. 또한, 몇 가지 실시양태에 있어서, 제 3 도공층 중의 파라핀 왁스는, 융점이 50 ℃ 이상의 것이다. 또한, 몇 가지 실시양태에 있어서, 제 3 도공층 중의 파라핀 왁스는, 융점이 80 ℃ 이하의 것이다. 적어도 하나의 실시양태에 있어서, 제 3 도공층 중의 파라핀 왁스는, 융점이 50 ℃ 이상 80 ℃ 이하의 것이다. 이들의 이유는, 식품 포장 용지의 히트 시일 적성을 저해하지 않고서 수증기 배리어성 및 내블로킹성을 양화할 수 있고, 또, 융점이 80 ℃ 초과인 파라핀 왁스는 입수 곤란하기 때문이다.In some embodiments, the third coating layer further contains paraffin wax. This is because the water vapor barrier properties and/or blocking resistance of the food packaging paper are improved. In at least one embodiment, the content of the paraffin wax in the third coated layer is 3 parts by mass or more and 15 parts by mass or less with respect to 100 parts by mass of the acrylic resin in the third coating layer per side of the paper support. The reason for this is that when the content of the paraffin wax is within this range, the water vapor barrier properties and blocking resistance can be improved without impairing the heat sealability of the food wrapping paper. In some embodiments, the paraffin wax in the third coating layer has a melting point of 50°C or higher. In some embodiments, the paraffin wax in the third coating layer has a melting point of 80°C or less. In at least one embodiment, the paraffin wax in the third coating layer has a melting point of 50°C or more and 80°C or less. These reasons are that the water vapor barrier properties and blocking resistance can be improved without impairing the heat sealability of food packaging paper, and paraffin wax having a melting point of more than 80°C is difficult to obtain.
파라핀 왁스는, 소위 석유 왁스에 속하며, 석유 정제에 있어서 감압 증류 유출유로부터 분리 및 정제하여 제조된다. 석유 왁스는, JIS K2235 : 1991 에 의해, 파라핀 왁스, 마이크로크리스탈린 왁스, 페트롤레이텀의 3 종으로 크게 구별된다. 마찬가지로 분리 및 정제되는 마이크로크리스탈린 왁스가 분자량 500 ∼ 800 이고 탄소수 30 ∼ 60 정도, 큰 주사슬에 측사슬을 갖는 분기 탄화수소 (이소파라핀) 또는 고리형 탄화수소 (시클로파라핀) 가 주성분인 것에 반해, 파라핀 왁스는, 분자량이 300 ∼ 550 으로 좁고, 직사슬형 탄화수소가 주성분으로 탄소수가 대개 20 ∼ 40 의 범위이다. 파라핀 왁스는, 예를 들면, 츄쿄 유지사, 니혼 세이로사 및 빅 케미·재팬사 등으로부터 시판된다.Paraffin wax belongs to so-called petroleum wax and is produced by separation and purification from vacuum distillation distillate in petroleum refining. Petroleum wax is broadly classified into three types: paraffin wax, microcrystalline wax, and petrolatum according to JIS K2235:1991. Similarly, whereas the separated and purified microcrystalline wax has a molecular weight of 500 to 800, carbon atoms of about 30 to 60, and branched hydrocarbons (isoparaffins) or cyclic hydrocarbons (cycloparaffins) having side chains in a large main chain, paraffin Wax has a narrow molecular weight of 300 to 550, mainly composed of linear hydrocarbons, and usually has 20 to 40 carbon atoms. Paraffin wax is commercially available from, for example, Chukyo Yuji Co., Ltd., Nippon Seiro Co., Ltd., Big Chemie Japan Co., Ltd., and the like.
제 3 도공층은, 아크릴계 수지 및 파라핀 왁스 이외에, 필요에 따라 종래 공지된 각종 첨가제를 함유할 수 있다. 첨가제는, 예를 들면, 무기 안료, 유기 안료, 아크릴계 수지 이외의 각종 수지, 전분류 및 셀룰로오스류 등의 다당류, 계면 활성제, 분산제, 증점제, 보수제, 소포제, 내수화제, 착색제, 자외선 흡수제 등을 들 수 있다.The 3rd coating layer can contain conventionally well-known various additives as needed other than acrylic resin and paraffin wax. Examples of additives include inorganic pigments, organic pigments, various resins other than acrylic resins, polysaccharides such as starches and celluloses, surfactants, dispersants, thickeners, water retention agents, antifoaming agents, water-resistance agents, colorants, ultraviolet absorbers, and the like. can
몇 가지 실시양태에 있어서, 식품 포장 용지는, 제 1 도공층이 카올린과, 스티렌-부타디엔계 공중합 수지 및 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 제 2 도공층이 폴리염화비닐리덴계 중합 수지를 함유하며, 그리고 제 3 도공층이 아크릴계 수지로서 스티렌-아크릴계 공중합 수지를 함유한다. 적어도 하나의 실시양태에 있어서, 식품 포장 용지는, 제 1 도공층이 카올린과, 스티렌-부타디엔계 공중합 수지 및 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 제 2 도공층이 폴리염화비닐리덴계 중합 수지를 함유하며, 그리고 제 3 도공층이 아크릴계 수지로서 스티렌-아크릴계 공중합 수지와 융점이 50 ℃ 이상 80 ℃ 이하인 파라핀 왁스를 함유한다.In some embodiments, the food packaging paper contains one or more selected from the group consisting of kaolin, a styrene-butadiene-based copolymer resin, and an acrylic resin in which the first coating layer is contained, and the second coating layer is A polyvinylidene chloride-based polymer resin is contained, and the third coating layer contains a styrene-acrylic copolymer resin as an acrylic resin. In at least one embodiment, the food packaging paper includes a first coating layer containing kaolin, one or two or more selected from the group consisting of a styrene-butadiene copolymer resin and an acrylic resin, and a second coating layer This polyvinylidene chloride-based polymeric resin is contained, and the third coating layer contains a styrene-acrylic copolymer resin as an acrylic resin and a paraffin wax having a melting point of 50°C or more and 80°C or less.
몇 가지 실시양태에 있어서, 식품 포장 용지는, 제 1 도공층이 카올린과, 스티렌-부타디엔계 공중합 수지로 이루어진 군에서 선택되는 1 종 혹은 2 종 이상, 또는 아크릴계 수지로 이루어진 군에서 선택되는 1 종 혹은 2 종 이상을 함유하고, 제 2 도공층이 폴리염화비닐리덴계 중합 수지를 함유하며, 그리고 제 3 도공층이 아크릴계 수지로서 스티렌-아크릴계 공중합 수지를 함유한다. 적어도 하나의 실시양태에 있어서, 식품 포장 용지는, 제 1 도공층이 카올린과, 스티렌-부타디엔계 공중합 수지로 이루어지는 군에서 선택되는 1 종 혹은 2 종 이상 또는 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 혹은 2 종 이상을 함유하고, 제 2 도공층이 폴리염화비닐리덴계 중합 수지를 함유하며, 그리고 제 3 도공층이 아크릴계 수지로서 스티렌-아크릴계 공중합 수지와 융점이 50 ℃ 이상 80 ℃ 이하인 파라핀 왁스를 함유한다.In some embodiments, food packaging paper, the first coating layer is one or two or more selected from the group consisting of kaolin and styrene-butadiene-based copolymer resins, or one selected from the group consisting of acrylic resins Or it contains 2 or more types, the 2nd coating layer contains polyvinylidene chloride system polymeric resin, and the 3rd coating layer contains styrene-acrylic copolymer resin as acrylic resin. In at least one embodiment, in the food packaging paper, the first coating layer is one or more selected from the group consisting of kaolin and styrene-butadiene-based copolymer resins, or one selected from the group consisting of acrylic resins. Or containing two or more types, the second coating layer contains a polyvinylidene chloride-based polymeric resin, and the third coating layer contains a styrene-acrylic copolymer resin as an acrylic resin and a paraffin wax having a melting point of 50 ° C. or more and 80 ° C. or less. contain
몇 가지 실시양태에 있어서, 식품 포장 용지는, 제 1 도공층이 카올린과, 스티렌-부타디엔계 공중합 수지로 이루어진 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 제 2 도공층이 폴리염화비닐리덴계 중합 수지를 함유하며, 그리고 제 3 도공층이 아크릴계 수지로서 스티렌-아크릴계 공중합 수지를 함유한다. 적어도 하나의 실시양태에 있어서, 식품 포장 용지는, 제 1 도공층이 카올린과, 스티렌-부타디엔계 공중합 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 제 2 도공층이 폴리염화비닐리덴계 중합 수지를 함유하며, 그리고 제 3 도공층이 아크릴계 수지로서 스티렌-아크릴계 공중합 수지와 융점이 50 ℃ 이상 80 ℃ 이하인 파라핀 왁스를 함유한다.In some embodiments, the food packaging paper contains one or more selected from the group consisting of kaolin and styrene-butadiene-based copolymer resins in the first coated layer, and the second coated layer is polyvinyl chloride A leadenic polymeric resin is contained, and the third coating layer contains a styrene-acrylic copolymeric resin as an acrylic resin. In at least one embodiment, the food packaging paper contains one or more selected from the group consisting of kaolin and a styrene-butadiene copolymer resin in the first coating layer, and the second coating layer is polychlorinated It contains a vinylidene-based polymeric resin, and the third coating layer contains a styrene-acrylic copolymer resin as an acrylic resin and a paraffin wax having a melting point of 50°C or more and 80°C or less.
몇 가지 실시양태에 있어서, 식품 포장 용지는, 제 1 도공층이 카올린과, 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 제 2 도공층이 폴리염화비닐리덴계 중합 수지를 함유하며, 그리고 제 3 도공층이 아크릴계 수지로서 스티렌-아크릴계 공중합 수지를 함유한다. 적어도 하나의 실시양태에 있어서, 식품 포장 용지는, 제 1 도공층이 카올린과, 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 제 2 도공층이 폴리염화비닐리덴계 중합 수지를 함유하며, 그리고 제 3 도공층이 아크릴계 수지로서 스티렌-아크릴계 공중합 수지와 융점이 50 ℃ 이상 80 ℃ 이하인 파라핀 왁스를 함유한다.In some embodiments, the food packaging paper contains one or more selected from the group consisting of kaolin and acrylic resin in the first coating layer, and the second coating layer is polyvinylidene chloride-based polymeric resin. and the third coating layer contains a styrene-acrylic copolymer resin as an acrylic resin. In at least one embodiment, the food packaging paper has a first coating layer containing one or more selected from the group consisting of kaolin and an acrylic resin, and a second coating layer containing polyvinylidene chloride-based polymerization. resin, and the third coating layer contains a styrene-acrylic copolymer resin as an acrylic resin and a paraffin wax having a melting point of 50°C or more and 80°C or less.
식품 포장 용지는, 종이 지지체에 대하여 제 1 도공층, 제 2 도공층 및 제 3 도공층을 순차 형성함으로써, 제조할 수 있다. 종이 지지체에 대하여 제 1 도공층, 제 2 도공층 및 제 3 도공층을 순차 형성하는 방법은, 특별히 한정되지 않는다. 예로는, 제지 분야에서 종래 공지된 도공 장치 및 건조 장치를 사용하여, 각 도공층을 형성하기 위한 도공액을 도공 및 건조하는 방법을 들 수 있다. 도공 장치의 예로는, 필름 프레스 코터, 로드 코터, 에어 나이프 코터, 로드 블레이드 코터, 바 코터, 블레이드 코터, 그라비어 코터, 커튼 코터, E 바 코터, 필름 트랜스퍼 코터 등을 들 수 있다. 건조 장치의 예로는, 직선 터널 건조기, 아치 드라이어, 에어 루프 드라이어, 사인 커브 에어 플로트 드라이어 등의 열풍 건조기, 적외선 가열 드라이어, 마이크로파 등을 이용한 건조기 등의 각종 건조 장치를 들 수 있다.Food wrapping paper can be manufactured by sequentially forming a first coated layer, a second coated layer, and a third coated layer on a paper support. The method of sequentially forming the first coated layer, the second coated layer, and the third coated layer on the paper support is not particularly limited. As an example, a method of coating and drying a coating solution for forming each coating layer using a conventionally known coating apparatus and drying apparatus in the papermaking field is exemplified. Examples of the coating device include a film press coater, a rod coater, an air knife coater, a rod blade coater, a bar coater, a blade coater, a gravure coater, a curtain coater, an E bar coater, and a film transfer coater. Examples of the drying device include hot air dryers such as linear tunnel dryers, arch dryers, air loop dryers, and sinusoidal air float dryers, various drying devices such as dryers using infrared heating dryers, microwaves, and the like.
제 1 도공층의 도공액이 카올린과, 바인더로서 스티렌-부타디엔계 공중합 수지 및 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하는 것, 제 2 도공층의 도공액이 폴리염화비닐리덴계 중합 수지를 함유하는 것, 그리고 제 3 도공층의 도공액이 아크릴계 수지 또는 아크릴계 수지와 파라핀 왁스를 함유하는 것에 의해, 얻어지는 각 도공층은, 각각, 카올린과, 스티렌-부타디엔계 공중합 수지 및 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을, 폴리염화비닐리덴계 중합 수지를, 그리고 아크릴계 수지 또는 아크릴계 수지와 파라핀 왁스를 함유할 수 있다.The coating liquid of the first coating layer contains kaolin and one or two or more types selected from the group consisting of styrene-butadiene-based copolymer resins and acrylic resins as a binder, and the coating liquid of the second coating layer is polyvinyl chloride Each coating layer obtained by containing a leadene-based polymeric resin and the coating liquid of the third coating layer containing an acrylic resin or an acrylic resin and paraffin wax, respectively, contains kaolin, a styrene-butadiene copolymer resin, and One or two or more selected from the group consisting of acrylic resins, a polyvinylidene chloride-based polymeric resin, and an acrylic resin or an acrylic resin and paraffin wax may be contained.
몇 가지의 실시양태에 있어서, 제 1 도공층의 도공량은, 종이 지지체의 편면당 건조 고형분량으로 3 g/m2 이상 15 g/m2 이하이다.In some embodiments, the coating amount of the first coating layer is 3 g/m 2 or more and 15 g/m 2 or less in terms of dry solid content per side of the paper support.
몇 가지 실시양태에 있어서, 제 2 도공층의 도공량은, 종이 지지체의 편면당 건조 고형분량으로 4 g/m2 이상 15 g/m2 이하이다.In some embodiments, the coating amount of the second coating layer is 4 g/m 2 or more and 15 g/m 2 or less in terms of dry solids per side of the paper support.
몇 가지 실시양태에 있어서, 제 3 도공층의 도공량은, 종이 지지체의 편면당 건조 고형분량으로 4 g/m2 이상 25 g/m2 이하이다.In some embodiments, the coating amount of the third coating layer is 4 g/m 2 or more and 25 g/m 2 or less in terms of dry solids per side of the paper support.
적어도 하나의 실시양태에 있어서, 식품 포장 용지는, 종이 지지체의 편면당, 제 1 도공층의 도공량이 건조 고형분량으로 3 g/m2 이상 15 g/m2 이하, 제 2 도공층의 도공량이 건조 고형분량으로 4 g/m2 이상 15 g/m2 이하, 및 제 3 도공층의 도공량이 건조 고형분량으로 4 g/m2 이상 25 g/m2 이하이다.In at least one embodiment, the food packaging paper has a coating amount of the first coating layer, in terms of dry solids, of 3 g/m 2 or more and 15 g/m 2 or less, and a coating amount of the second coating layer per side of the paper support. The dry solid content is 4 g/m 2 or more and 15 g/m 2 or less, and the coating amount of the third coating layer is 4 g/m 2 or more and 25 g/m 2 or less in terms of dry solid content.
이들의 이유는, 본 발명의 효과가 안정적으로 얻어지면서, 재료 비용이 억제되기 때문이다.The reason for these is that the material cost is suppressed while the effect of the present invention is obtained stably.
식품 포장 용지는, 식품의 포장, 식품을 넣는 봉지 또는 식품을 넣는 용기 등의 식품 포장 재료로서 사용할 수 있다.Food wrapping paper can be used as a food packaging material, such as food packaging, food packaging bags, or food packaging containers.
실시예Example
이하, 실시예에 의해 본 발명을 더욱 상세하게 설명한다. 또한, 본 발명은 이들 실시예에 한정되지 않는다. 여기에서 「질량부」 및 「질량%」는, 건조 고형분량 혹은 실질 성분량의 각각 「질량부」 및 「질량%」를 나타낸다. 도공층의 도공량은 건조 고형분량을 나타낸다.Hereinafter, the present invention will be described in more detail by examples. Also, the present invention is not limited to these examples. Here, "parts by mass" and "% by mass" represent "parts by mass" and "% by mass" of dry solid content or actual component amount, respectively. The coating amount of the coating layer represents the amount of dry solid content.
<종이 지지체><Paper support>
이하의 지료를 조성하였다.The following furnish was formulated.
LBKP (여수도 350 ∼ 480 mlcsf) 50 질량부 LBKP (Yeosu Island 350 ∼ 480 mlcsf) 50 parts by mass
NBKP (여수도 350 ∼ 480 mlcsf) 50 질량부 NBKP (Yeosu Island 350 ∼ 480 mlcsf) 50 parts by mass
황산 밴드 2 질량부 sulfuric acid band 2 parts by mass
경질 탄산칼슘 (TP121, 오쿠타마 공업사) 7 질량부 Precipitated calcium carbonate (TP121, Okutama Industrial Co., Ltd.) 7 parts by mass
로진계 사이즈제 (CC1404, 세이코 PMC 사) 0.3 질량부 Rosin-based sizing agent (CC1404, Seiko PMC) 0.3 parts by mass
지력제 0.6 질량부 intelligence 0.6 parts by mass
상기 배합의 지료를 장망 초지기로 초조하여, 평량 55 g/m2 의 원지를 얻었다. 이것에, 머신 캘린더를 사용하여 온도 60 ℃·처리 속도 500 m/분의 조건으로 캘린더 처리하여 종이 지지체를 얻었다. 종이 지지체의 회분량은 5 질량% 였다.The stock of the above formulation was made with a net paper machine to obtain base paper having a basis weight of 55 g/m 2 . This was calendered using a machine calender under conditions of a temperature of 60°C and a processing speed of 500 m/min to obtain a paper support. The amount of ash in the paper support was 5% by mass.
<제 1 도공층의 도공액><Coating liquid of the first coating layer>
물을 매체로 하여 이하의 도공액을 조제하였다.The following coating liquid was prepared using water as a medium.
안료 종류 및 질량부는 표 1 및 표 2 에 기재 pigment Type and mass part are listed in Table 1 and Table 2
수지 종류 및 질량부는 표 1 및 표 2 에 기재 profit Type and mass part are listed in Table 1 and Table 2
<제 2 도공층의 도공액><Coating liquid of the second coating layer>
물을 매체로 하여 이하의 도공액을 조제하였다.The following coating liquid was prepared using water as a medium.
수지 종류는 표 1 및 표 2 에 기재/100 질량부 profit Types are listed in Table 1 and Table 2/100 parts by mass
<제 3 도공층의 도공액><Coating solution of the 3rd coating layer>
물을 매체로 하여 이하의 도공액을 조제하였다.The following coating liquid was prepared using water as a medium.
수지 종류는 표 1 및 표 2 에 기재/100 질량부 profit Types are listed in Table 1 and Table 2/100 parts by mass
파라핀 왁스 종류 및 질량부는 표 1 및 표 2 에 기재 paraffin wax Type and mass part are listed in Table 1 and Table 2
표 1 및 표 2 에 기재하는 각 재료는 이하이다.Each material described in Table 1 and Table 2 is as follows.
카올린 : 2 ㎛ 이하의 누적 빈도 88 체적% 의 카올린Kaolin: Kaolin with a cumulative frequency of 2 µm or less, 88% by volume
탄산칼슘 : 2 ㎛ 이하의 누적 빈도 87 체적% 의 탄산칼슘Calcium carbonate: Calcium carbonate with a cumulative frequency of 2 μm or less of 87% by volume
스티렌-부타디엔계 1 : 스티렌-부타디엔 공중합 수지Styrene-butadiene type 1: Styrene-butadiene copolymer resin
(스티렌계 단량체 함유 질량 비율 63 질량%) (63% by mass of styrenic monomer-containing mass)
스티렌-부타디엔계 2 : 스티렌-부타디엔 공중합 수지Styrene-butadiene type 2: Styrene-butadiene copolymer resin
(스티렌계 단량체 함유 질량 비율 70 질량%) (Styrene-based monomer-containing mass ratio of 70% by mass)
스티렌-부타디엔계 3 : 스티렌-부타디엔 공중합 수지Styrene-butadiene type 3: Styrene-butadiene copolymer resin
(스티렌계 단량체 함유 질량 비율 88 질량%) (Styrene-based monomer content mass ratio 88% by mass)
스티렌-부타디엔계 4 : 스티렌-부타디엔 공중합 수지Styrene-butadiene type 4: Styrene-butadiene copolymer resin
(스티렌계 단량체 함유 질량 비율 96 질량%) (Styrene-based monomer-containing mass ratio: 96% by mass)
아크릴계 수지 1 : 폴리아크릴산n-부틸 수지Acrylic resin 1: polyacrylic acid n-butyl resin
아크릴계 수지 2 : 메타크릴산메틸-아크릴산2-에틸헥실 공중합 수지Acrylic resin 2: methyl methacrylate-2-ethylhexyl acrylic acid copolymer resin
아크릴계 수지 3 : 스티렌-아크릴로니트릴-아크릴산에틸 공중합 수지Acrylic resin 3: styrene-acrylonitrile-ethyl acrylate copolymer resin
아크릴계 수지 4 : 스티렌-아크릴산에틸 공중합 수지Acrylic resin 4: styrene-ethyl acrylate copolymer resin
아크릴계 수지 5 : 스티렌-아크릴산n-부틸 공중합 수지Acrylic resin 5: styrene-n-butyl acrylic acid copolymer resin
PVDC1 : 폴리염화비닐리덴계 중합 수지PVDC1: polyvinylidene chloride polymeric resin
(단량체의 배합 질량% 비) (Combined mass % ratio of monomers)
염화비닐리덴 : 80 Vinylidene Chloride: 80
메타크릴로니트릴 : 15 Methacrylonitrile: 15
아크릴산에틸 : 5 Ethyl acrylate: 5
PVDC2 : 폴리염화비닐리덴계 중합 수지PVDC2: polyvinylidene chloride polymeric resin
(단량체의 배합 질량% 비) (Combined mass % ratio of monomers)
염화비닐리덴 : 85 Vinylidene Chloride: 85
메타크릴로니트릴 : 10 Methacrylonitrile: 10
아크릴산에틸 : 5 Ethyl acrylate: 5
PVDC3 : 폴리염화비닐리덴계 중합 수지PVDC3: polyvinylidene chloride polymeric resin
(단량체의 배합 질량% 비) (Combined mass % ratio of monomers)
염화비닐리덴 : 90 Vinylidene Chloride: 90
아크릴로니트릴 : 9 Acrylonitrile: 9
아크릴산에틸 : 1 Ethyl acrylate: 1
PVDC4 : 폴리염화비닐리덴계 중합 수지PVDC4: polyvinylidene chloride polymeric resin
(단량체의 배합 질량% 비) (Combined mass % ratio of monomers)
염화비닐리덴 : 95 Vinylidene Chloride: 95
아크릴로니트릴 : 3 Acrylonitrile: 3
아크릴산에틸 : 2 Ethyl acrylate: 2
PVDC5 : 폴리염화비닐리덴계 중합 수지PVDC5: polyvinylidene chloride polymeric resin
(단량체의 배합 질량% 비) (Combined mass % ratio of monomers)
염화비닐리덴 : 98 Vinylidene Chloride: 98
메타크릴로니트릴 : 1.5 Methacrylonitrile: 1.5
아크릴산에틸 : 0.5 Ethyl acrylate: 0.5
PVDC6 : 폴리염화비닐리덴계 중합 수지PVDC6: polyvinylidene chloride polymeric resin
(단량체의 배합 질량% 비) (Combined mass % ratio of monomers)
염화비닐리덴 : 95 Vinylidene Chloride: 95
메타크릴로니트릴 : 2 Methacrylonitrile: 2
아크릴산에틸 : 3 Ethyl acrylate: 3
PVDC7 : 폴리염화비닐리덴계 중합 수지PVDC7: polyvinylidene chloride polymeric resin
(단량체의 배합 질량% 비) (Combined mass % ratio of monomers)
염화비닐리덴 : 94 Vinylidene Chloride: 94
메타크릴로니트릴 : 5.5 Methacrylonitrile: 5.5
아크릴산에틸 : 0.5 Ethyl acrylate: 0.5
PVA : 폴리비닐알코올PVA: polyvinyl alcohol
(무변성, 완전 비누화, 평균 중합도 1700) (No denaturation, complete saponification, average degree of polymerization 1700)
에틸렌-아세트산비닐계 : 에틸렌-아세트산비닐 공중합 수지Ethylene-vinyl acetate type: Ethylene-vinyl acetate copolymer resin
파라핀 왁스 1 : 융점 43 ℃ 의 파라핀 왁스Paraffin wax 1: Paraffin wax having a melting point of 43 ° C.
파라핀 왁스 2 : 융점 51 ℃ 의 파라핀 왁스Paraffin wax 2: Paraffin wax having a melting point of 51 ° C.
파라핀 왁스 3 : 융점 70 ℃ 의 파라핀 왁스Paraffin wax 3: Paraffin wax having a melting point of 70 ° C.
파라핀 왁스 4 : 융점 77 ℃ 의 파라핀 왁스Paraffin wax 4: paraffin wax having a melting point of 77 ° C.
<도공><Swordsmith>
종이 지지체의 편면에 대하여, 제 1 도공층의 도공액을 로드 코터로 도공 및 건조하였다. 도공량은, 10 g/m2 가 되도록 코터 조건을 조정하였다.To one side of the paper support, the coating liquid of the first coating layer was coated with a rod coater and dried. Coater conditions were adjusted so that the amount of coating was 10 g/m 2 .
다음으로, 제 1 도공층에 대하여, 제 2 도공층용의 도공액을 에어 나이프 코터로 도공 및 건조하였다. 도공량은 10 g/m2 가 되도록 코터 조건을 조정하였다. 계속해서, 제 2 도공층에 대하여, 제 3 도공층용의 도공액을 에어 나이프 코터로 도공 및 건조하였다. 도공량은 15 g/m2 가 되도록 코터 조건을 조정하였다.Next, with respect to the 1st coating layer, the coating liquid for 2nd coating layers was coated and dried by the air knife coater. Coater conditions were adjusted so that the amount of coating was 10 g/m 2 . Then, with respect to the 2nd coating layer, the coating liquid for 3rd coating layers was coated and dried by the air knife coater. Coater conditions were adjusted so that the amount of coating was 15 g/m 2 .
<내수성><water resistance>
내수성의 평가는, 식품 포장 용지의 표면 (제 1 도공층, 제 2 도공층 및 제 3 도공층을 갖는 측) 에 약 2 ml 의 붉게 착색된 물방울을 적하하고, 적하된 물이, 식품 포장 용지의 표면에서 스며드는 정도 및 식품 포장 용지의 이면 (제 1 도공층, 제 2 도공층 및 제 3 도공층을 갖지 않는 측) 으로 스며나오는 정도를 육안으로 관찰하여 실시하였다. 관찰 결과로부터, 내수성을 하기의 기준으로 평가하였다. 본 발명에 있어서, 식품 포장 용지는, 평가 A 또는 B 이면 내수성을 갖는 것으로 한다.For evaluation of water resistance, about 2 ml of red-colored water droplets are dropped on the surface of the food packaging paper (on the side having the first coated layer, the second coated layer, and the third coated layer), and the dripped water is the food packaging paper. The degree of permeation from the surface and the degree of permeation to the back side of the food packaging paper (the side without the first coated layer, the second coated layer, and the third coated layer) were visually observed. From the observation results, water resistance was evaluated according to the following criteria. In the present invention, the food wrapping paper has water resistance if it has an evaluation of A or B.
A : 스며듬이 없고, 및 스며나옴이 인정되지 않는다.A: No oozing and no oozing was observed.
B : 스며듬이 약간 인정된다. 그러나, 스며나옴이 인정되지 않는다.B: Slight permeation is observed. However, seepage is not recognized.
C : 스며듬이 인정된다. 또한, 스며나옴이 인정된다.C: Permeation is recognized. Also, seepage is recognized.
<내유성><Oil Resistance>
내유성의 평가는, 식품 포장 용지의 표면 (제 1 도공층, 제 2 도공층 및 제 3 도공층을 갖는 측) 에 약 1 ml 의 기름 방울을 적하하고, 적하된 기름이, 식품 포장 용지의 표면에서 스며드는 정도 및 식품 포장 용지의 이면 (제 1 도공층, 제 2 도공층 및 제 3 도공층을 갖지 않는 측) 으로 스며나오는 정도를 육안으로 관찰하여 실시하였다. 기름에는 샐러드유를 사용하였다. 관찰 결과로부터, 내유성을 하기의 기준으로 평가하였다. 본 발명에 있어서, 식품 포장 용지는, 평가 A 또는 B 이면 내유성을 갖는 것으로 한다.To evaluate the oil resistance, about 1 ml of oil droplets are dropped on the surface of the food packaging paper (on the side having the first coated layer, the second coated layer, and the third coated layer), and the dripped oil is applied to the surface of the food packaging paper. The degree of permeation and the degree of permeation to the back side of the food packaging paper (the side without the first coated layer, the second coated layer, and the third coated layer) were visually observed. Salad oil was used for the oil. From the observation results, the oil resistance was evaluated according to the following criteria. In the present invention, the food wrapping paper has oil resistance if it is rated A or B.
A : 스며듬이 없고, 및 스며나옴이 인정되지 않는다.A: No oozing and no oozing was observed.
B : 스며듬이 약간 인정된다. 그러나, 스며나옴이 인정되지 않는다.B: Slight permeation is observed. However, seepage is not recognized.
C : 스며듬이 인정된다. 또한, 스며나옴이 인정된다.C: Permeation is recognized. Also, seepage is recognized.
<가스 배리어성><Gas barrier properties>
가스 배리어성의 평가는, ISO15105-2 : 2003 「Plastics-Film and sheeting - Determination of gas-transmission rate - Part2 : Equal-pressure method」(JIS K7126-2 : 2006 「플라스틱 -필름 및 시트- 가스 투과도 시험 방법- 제 2 부 : 등압법」) 에 준하여 실시한 측정 결과로부터 행하였다. 측정은, 제 1 도공층, 제 2 도공층 및 제 3 도공층을 갖는 측을 외측으로 하여 실시하였다. 가스 투과도 시험의 가스로는 산소 가스를 사용하여 산소 투과도로 하고, 온습도의 조건은, 23±0.5 ℃ 및 상대 습도 85±2 % 로 하였다. 본 발명에 있어서, 식품 포장 용지는, A, B 또는 C 의 평가이면 가스 배리어성을 갖는 것으로 한다.Evaluation of gas barrier properties is based on ISO15105-2: 2003 "Plastics-Film and sheeting - Determination of gas-transmission rate - Part2: Equal-pressure method" (JIS K7126-2: 2006 "Plastics-Films and Sheets-Gas Permeability Test Method - Part 2: Isobaric method”) was performed based on the measurement results. The measurement was performed with the side having the first coated layer, the second coated layer, and the third coated layer turned outward. Oxygen gas was used as the gas for the gas permeability test to determine the oxygen permeability, and the temperature and humidity conditions were 23±0.5° C. and 85±2% relative humidity. In the present invention, food wrapping paper is assumed to have gas barrier properties if it is evaluated as A, B or C.
A : 산소 투과도 50 cc/m2·24h·atm 이하로, 양호.A: Oxygen permeability of 50 cc/m 2 ·24h·atm or less, which is good.
B : 상기 A 보다 떨어지지만,B: inferior to the above A,
산소 투과도 100 cc/m2·24h·atm 이하로, 대체로 양호.Oxygen permeability 100 cc/m 2 ·24h·atm or less, generally good.
C : 상기 B 보다 떨어지지만,C: inferior to B above,
산소 투과도 150 cc/m2·24h·atm 이하로, 실용 가능.Oxygen permeability of 150 cc/m 2 ·24h·atm or less, practical use is possible.
D : C 보다 떨어지고,D: lower than C,
산소 투과도 150 cc/m2·24h·atm 초과로, 실용 불가능.Oxygen permeability exceeds 150 cc/m 2 ·24h·atm, so it is not practical.
<수증기 배리어성><Water vapor barrier property>
수증기 배리어성의 평가는, JIS Z0208 : 1976 「방습 포장 재료의 투습도 시험 방법 (컵법)」에 준하여 실시한 측정 결과로부터 행하였다. 측정은, 제 1 도공층, 제 2 도공층 및 제 3 도공층을 갖는 측을 내측으로 하여 측정하였다. 수증기 투과도로 하고, 온습도의 조건은, 40±0.5 ℃, 90±2 % 로 하였다. 본 발명에 있어서, 식품 포장 용지는, A, B 또는 C 의 평가이면 수증기 배리어성을 갖는 것으로 한다.Water vapor barrier properties were evaluated based on the results of measurements performed in accordance with JIS Z0208: 1976 “Test method for moisture permeability of moisture-proof packaging materials (cup method)”. The measurement was performed with the side having the first coated layer, the second coated layer, and the third coated layer turned inside. The water vapor permeability was set, and the temperature and humidity conditions were 40±0.5°C and 90±2%. In the present invention, food wrapping paper is considered to have water vapor barrier properties if it is evaluated as A, B or C.
A : 수증기 투과도 30 g/m2·24h 이하로, 양호.A: Water vapor permeability of 30 g/m 2 ·24h or less, which is good.
B : 상기 A 보다 떨어지지만,B: inferior to the above A,
수증기 투과도 50 g/m2·24h 이하로, 대체로 양호.Water vapor permeability 50 g/m 2 ·24h or less, generally good.
C : 상기 B 보다 떨어지지만,C: inferior to B above,
수증기 투과도 100 g/m2·24h 이하로, 실용 가능.Water vapor permeability 100 g/m 2 ·24h or less, practical use.
D : C 보다 떨어지고,D: lower than C,
수증기 투과도 100 g/m2·24h 초과로, 실용 불가능.Water vapor permeability exceeds 100 g/m 2 ·24h, and is not practical.
<플레이버 배리어성><Flavor barrier property>
향기 발생 물질로서 시판되는 레귤러 커피 분말을 사용하였다. 유리컵에 레귤러 커피 분말을 넣고, 컵의 개구부를 식품 포장 용지의 표면 (제 1 도공층, 제 2 도공층 및 제 3 도공층을 갖는 측) 을 내측으로 하여 식품 포장 용지로 덮고, 개구부의 주위를 테이프에 의해 엄중하게 봉하였다. 5 명의 피험자가, 식품 포장 용지로 봉한 컵의 개구부에 있어서 냄새를 맡아, 하기의 기준으로 관능 평가하였다.Commercially available regular coffee powder was used as an aroma generating material. Put regular coffee powder in a glass cup, cover the opening of the cup with the food wrapping paper with the surface of the food wrapping paper (the side having the first coated layer, the second coated layer and the third coated layer) inside, and cover the periphery of the opening was tightly sealed with tape. Five test subjects smelled the smell at the opening of the cup sealed with food wrapping paper, and sensory evaluation was performed according to the following criteria.
3 점 : 냄새를 느끼지 않는다.3 points: I do not feel the smell.
2 점 : 냄새가 느껴지는 것 같은 느낌이 든다.2 points: I feel like I can smell it.
1 점 : 냄새를 느낀다.1 point: feel the smell.
플레이버 배리어성의 평가는, 5 명의 관능 평가의 결과를 기초로 하여 하기의 기준으로 실시하였다. 본 발명에 있어서, 식품 포장 용지는, 평가 A 또는 B 이면 플레이버 배리어성을 갖는 것으로 한다.Evaluation of the flavor barrier property was performed according to the following criteria based on the results of sensory evaluation by five people. In the present invention, the food wrapping paper has flavor barrier properties if it is rated A or B.
A : 평가 3 이 3 명 이상 또한 평가 1 이 0 명이다.A: Evaluation 3 is 3 or more, and evaluation 1 is 0 persons.
B : 평가 2 가 3 명 이상 또한 평가 1 이 0 명이다.B: Evaluation 2 is 3 or more, and Evaluation 1 is 0 persons.
C : 평가 1 이 1 명 이상이다.C: Evaluation 1 is one or more.
<히트 시일 적성><Heat seal aptitude>
2 장의 식품 포장 용지를 사용하여, 식품 포장 용지의 제 1 도공층, 제 2 도공층 및 제 3 도공층을 갖는 측의 면끼리를 대향시켜 히트 실러에 의해 압력 0.5 MPa, 140 ℃, 1 초간의 조건에 따라 히트 시일을 실시하여, 평가용 샘플을 제작하였다.Using two sheets of food packaging paper, the surfaces on the side having the first coated layer, the second coated layer, and the third coated layer of the food packaging paper are opposed to each other, and a heat sealer is applied at a pressure of 0.5 MPa at 140° C. for 1 second. Heat sealing was performed according to the conditions to prepare samples for evaluation.
히트 시일 적성의 평가는, 히트 시일한 식품 포장 용지를 15 mm 폭으로 잘라내고, 23 ℃, 50 %RH 에서 24 시간 정치 (靜置) 후, 인장 시험기를 사용하여, 인장 속도 300 mm/분, 인장 각도 180 도로 히트 시일 지점의 박리 강도를 측정함으로써 실시하였다. 측정은, 샘플수 5 부로 실시하여, 5 부의 평균값으로 하였다. 측정값으로부터, 히트 시일 적성을 하기의 기준으로 평가하였다. 본 발명에 있어서, 식품 포장 용지는, 평가 A, B 또는 C 이면 히트 시일 적성을 갖는 것으로 한다.Heat-sealing suitability was evaluated by cutting heat-sealed food packaging paper into a width of 15 mm, leaving it still at 23°C and 50% RH for 24 hours, using a tensile tester at a tensile speed of 300 mm/min, It was carried out by measuring the peel strength at the heat seal point at a tensile angle of 180 degrees. The measurement was performed with 5 samples, and the average value of 5 samples was taken. From the measured values, the heat sealability was evaluated according to the following criteria. In the present invention, food packaging paper has heat sealability if it is rated A, B or C.
A : 값이 10 N/15 mm 이상.A: The value is 10 N/15 mm or more.
B : 값이 6 N/15 mm 이상 10 N/15 mm 미만.B: A value of 6 N/15 mm or more and less than 10 N/15 mm.
C : 값이 3 N/15 mm 이상 6 N/15 mm 미만.C: A value of 3 N/15 mm or more and less than 6 N/15 mm.
D : 값이 3 N/15 mm 미만.D: Value less than 3 N/15 mm.
<내블로킹성><Blocking resistance>
식품 포장 용지를, 제 3 도공층을 외측으로 하여 직경 150 mm 의 지관에 롤상 (길이 500 m) 으로 권취하였다. 당해 롤을, 바닥에 바로 두기 및 공중에 매달기의 2 종류 방법으로 30 ℃, 80 %RH 에서 24 시간 정치하였다. 내블로킹성의 평가는, 정치 후에 권취로부터 식품 포장 용지를 풀어내는 조작 (언와인더) 을 실시함으로써 행하였다. 언와인더시, 식품 포장 용지의 블로킹 상태를 육안으로 관찰하였다. 관찰 결과로부터, 내블로킹성을 하기의 기준으로 평가하였다. 본 발명에 있어서, 식품 포장 용지는, 평가 A, B 또는 C 이면 내블로킹성을 갖는 것으로 한다.The food packaging paper was wound up in a roll shape (500 m in length) around a paper tube having a diameter of 150 mm with the third coated layer on the outside. The roll was allowed to stand still at 30°C and 80% RH for 24 hours by two methods of placing directly on the floor and hanging in the air. Evaluation of blocking resistance was performed by performing an operation (unwinder) of unwinding the food wrapping paper from winding after stationary. During unwinding, the blocking state of the food packaging paper was visually observed. From the observation results, blocking resistance was evaluated according to the following criteria. In the present invention, the food packaging paper has blocking resistance if it is rated A, B or C.
A : 바닥에 바로 두기 및 공중에 매달기의 2 종류의 방법에서 블로킹이 인정되지 않는다.A: Blocking is not recognized in the two methods of placing directly on the floor and hanging in the air.
B : 바닥에 바로 두기 방법에서 아주 약간의 블로킹이 인정된다.B: Very little blocking is acceptable in the method of placing it directly on the floor.
공중에 매달기 방법에서 블로킹이 인정되지 않는다.Blocking is not permitted in the hanging method.
C : 바닥에 바로 두기 방법에서 약간의 블로킹이 인정된다.C: Some blocking is acceptable in the method of placing it directly on the floor.
공중에 매달기 방법에서 블로킹이 인정되지 않는다.Blocking is not permitted in the hanging method.
D : 상기 C 보다 떨어지고, 바닥에 바로 두기 방법에서 블로킹이 인정된다.D: It is lower than C above, and blocking is recognized in the method of placing it directly on the floor.
또는, 공중에 매달기 방법에서 블로킹이 인정된다.Alternatively, blocking is permitted in the suspended method.
<접기 가공 적성><Folding processing aptitude>
식품 포장 용지를, 제 3 도공층을 내측으로 하여, MD 방향으로 고무 롤러를 사용해서 한번 반으로 접은 다음 펼치고, 다음으로 CD 방향으로 고무 롤러를 사용해서 한번 반으로 접고 나서 펼쳤다. 이것을 10 장의 식품 포장 용지에서 실시하였다. 접기 가공 적성의 평가는, 제 3 도공층측으로부터 접힘 부분에 적색의 체커액을 분사하고, 반대측으로부터 체커액의 누출을 육안으로 관찰하였다. 체커액은, 후지 임펄스사의 퍼펙트 시일 체커를 사용하였다. 관찰 결과로부터, 접기 가공 적성을 하기의 기준으로 평가하였다. 본 발명에 있어서, 식품 포장 용지는, 평가 A, B 또는 C 이면 접기 가공 적성을 갖는 것으로 한다.The food packaging paper, with the third coated layer inside, was folded in half using a rubber roller in the MD direction and then unfolded, and then folded in half and then unfolded in the CD direction with a rubber roller. This was done on 10 sheets of food wrapping paper. For evaluation of the folding processing aptitude, red checker fluid was sprayed on the folded portion from the third coated layer side, and leakage of the checker fluid was visually observed from the opposite side. As the checker fluid, Fuji Impulse's Perfect Seal Checker was used. From the observation results, folding processing aptitude was evaluated according to the following criteria. In the present invention, the food packaging paper has evaluation A, B, or C, and has back-folding processing aptitude.
A : 누출이 관찰된 장수가 0 장이다.A: The number of sheets in which leakage was observed is 0 sheets.
B : 누출이 관찰된 장수가 1 ∼ 2 장이다.B: The number of sheets in which leakage was observed was 1 to 2 sheets.
C : 누출이 관찰된 장수가 3 ∼ 4 장이다.C: The number of sheets in which leakage was observed was 3 to 4 sheets.
D : 누출이 관찰된 장수가 5 장 이상이다.D: The number of sheets in which leakage was observed was 5 or more.
평가 결과를 표 3 및 표 4 에 나타낸다.An evaluation result is shown in Table 3 and Table 4.
표 3 및 표 4 로부터, 본 발명에 해당하는 실시예 1 ∼ 48 은, 내수성, 내유성, 가스 배리어성, 수증기 배리어성 및 플레이버 배리어성을 갖고, 히트 시일 적성 및 접기 가공 적성을 구비하며, 그리고 내블로킹성을 갖는 식품 포장 용지인 것을 알 수 있다. 한편, 본 발명의 구성을 만족하지 않는 비교예 1 ∼ 12 는, 이들 효과 중 적어도 하나를 만족하지 않는 식품 포장 용지인 것을 알 수 있다.From Tables 3 and 4, Examples 1 to 48 corresponding to the present invention have water resistance, oil resistance, gas barrier properties, water vapor barrier properties and flavor barrier properties, have heat seal aptitude and folding process aptitude, and It turns out that it is a food packaging paper with blocking property. On the other hand, it can be seen that Comparative Examples 1 to 12, which do not satisfy the configuration of the present invention, are food packaging papers that do not satisfy at least one of these effects.
주로, 실시예 1, 3 및 6 ∼ 9 간의 대비로부터, 제 1 도공층이 바인더로서 스티렌-부타디엔계 공중합 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 제 1 도공층에 있어서 상기 스티렌-부타디엔계 공중합 수지의 합계 함유량이 종이 지지체의 편면당 제 1 도공층 중의 카올린 100 질량부에 대하여 40 질량부 이상 400 질량부 이하이면, 식품 포장 용지는, 가스 배리어성, 플레이버 배리어성 및/또는 접기 가공 적성이 양화되는 것을 알 수 있다.Mainly, from the comparison between Examples 1, 3 and 6 to 9, the first coated layer contains one or two or more selected from the group consisting of styrene-butadiene copolymer resins as a binder, and in the first coated layer When the total content of the styrene-butadiene-based copolymer resin is 40 parts by mass or more and 400 parts by mass or less with respect to 100 parts by mass of kaolin in the first coated layer per side of the paper support, the food packaging paper has gas barrier properties, flavor barrier properties, and / Or it can be seen that the folding processing aptitude is improved.
주로, 실시예 25 ∼ 30 간의 대비로부터, 제 1 도공층이 바인더로서 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 제 1 도공층에 있어서 상기 아크릴계 수지의 합계 함유량이 종이 지지체의 편면당 제 1 도공층 중의 카올린 100 질량부에 대하여 40 질량부 이상 400 질량부 이하이면, 식품 포장 용지는, 가스 배리어성, 플레이버 배리어성 및/또는 접기 가공 적성이 양화되는 것을 알 수 있다.Mainly, from the comparison between Examples 25 to 30, the first coated layer contains one or two or more types selected from the group consisting of acrylic resin as a binder, and the total content of the acrylic resin in the first coated layer is paper If it is 40 parts by mass or more and 400 parts by mass or less with respect to 100 parts by mass of kaolin in the first coated layer per side of the support, it can be seen that the gas barrier property, flavor barrier property and / or folding processability of the food packaging paper are improved. .
주로, 실시예 7 및 실시예 10 ∼ 15 간의 대비 및 실시예 17 ∼ 23 간의 대비로부터, 제 2 도공층에 있어서, 수지 중의 염화비닐리덴 단량체가 85 질량% 이상 95 질량% 이하의 폴리염화비닐리덴계 중합 수지이면, 식품 포장 용지는, 가스 배리어성 및 수증기 배리어성이 양화되는 것을 알 수 있다.Mainly, from the comparison between Example 7 and Examples 10 to 15 and the comparison between Examples 17 to 23, in the second coating layer, the polyvinylidene chloride monomer in the resin is 85% by mass or more and 95% by mass or less. It can be seen that, if the resin is a polymeric resin, the gas barrier properties and water vapor barrier properties of the food packaging paper are improved.
주로, 실시예 7 과 16, 실시예 18 과 31, 실시예 24 와 32, 실시예 28 과 33, 실시예 39 와 45, 실시예 42 와 46, 실시예 43 과 47, 및 실시예 44 와 48 의 대비로부터, 제 3 도공층에 있어서, 아크릴계 수지가 스티렌-아크릴계 공중합 수지이면, 식품 포장 용지는, 접기 가공 적성 및 내블로킹성이 양화되는 것을 알 수 있다.Mainly, Examples 7 and 16, Examples 18 and 31, Examples 24 and 32, Examples 28 and 33, Examples 39 and 45, Examples 42 and 46, Examples 43 and 47, and Examples 44 and 48 From the comparison of , it can be seen that, in the third coated layer, when the acrylic resin is a styrene-acrylic copolymer resin, the folding processability and blocking resistance of the food wrapping paper are improved.
주로, 실시예 7 과 39, 실시예 18 과 42, 실시예 24 와 43, 실시예 28 과 44, 실시예 16 과 45, 실시예 31 과 46, 실시예 32 와 47, 및 실시예 33 과 48 의 대비로부터, 제 3 도공층이 파라핀 왁스를 함유하면, 식품 포장 용지는, 수증기 배리어성 및/또는 내블로킹성이 양화되는 것을 알 수 있다.Mainly, Examples 7 and 39, Examples 18 and 42, Examples 24 and 43, Examples 28 and 44, Examples 16 and 45, Examples 31 and 46, Examples 32 and 47, and Examples 33 and 48 From the comparison, it is understood that when the third coating layer contains paraffin wax, the water vapor barrier property and/or blocking resistance of the food wrapping paper are improved.
주로, 실시예 35 ∼ 38 간의 대비로부터, 제 3 도공층의 파라핀 왁스가 융점 50 ℃ 이상 80 ℃ 이하의 것이면, 히트 시일 적성을 저해하지 않고서 식품 포장 용지는, 수증기 배리어성 및 내블로킹성이 양화되는 것을 알 수 있다.Mainly, from the comparison between Examples 35 to 38, if the paraffin wax of the third coating layer has a melting point of 50 ° C. or more and 80 ° C. or less, the water vapor barrier property and blocking resistance of the food packaging paper are improved without impairing the heat seal suitability can be known to be
주로, 실시예 2 ∼ 5 간의 대비로부터, 제 1 도공층의 스티렌-부타디엔계 공중합 수지가, 공중합 수지 중의 스티렌계 단량체의 함유 질량 비율이 70 질량% 이상 90 질량% 이하의 것이면, 식품 포장 용지는, 가스 배리어성, 플레이버 배리어성 및 접기 가공 적성이 양화되는 것을 알 수 있다.Mainly, from the comparison between Examples 2 to 5, if the styrene-butadiene-based copolymer resin of the first coating layer has a content mass ratio of styrene-based monomer in the copolymer resin of 70% by mass or more and 90% by mass or less, the food packaging paper , it can be seen that the gas barrier properties, flavor barrier properties, and folding processability are improved.
주로, 실시예 18 과 24 와 28 간, 실시예 31 ∼ 33 간, 실시예 42 ∼ 44 간, 및 실시예 46 ∼ 48 간의 대비로부터, 제 1 도공층의 아크릴계 수지가, 아크릴산계 단량체와 스티렌이 공중합한 스티렌-아크릴계 공중합 수지 또는 아크릴산계 단량체와 스티렌과 (메트)아크릴로니트릴이 공중합한 스티렌-(메트)아크릴로니트릴-아크릴계 공중합 수지이면, 식품 포장 용지는, 가스 배리어성 및 플레이버 배리어성이 양화되는 것을 알 수 있다.Mainly, from the comparison between Examples 18 and 24 and 28, Examples 31 to 33, Examples 42 to 44, and Examples 46 to 48, the acrylic resin of the first coating layer was composed of acrylic acid monomer and styrene. If it is a copolymerized styrene-acrylic copolymer resin or a styrene-(meth)acrylonitrile-acrylic copolymer resin copolymerized with an acrylic acid monomer, styrene and (meth)acrylonitrile, the food packaging paper has gas barrier properties and flavor barrier properties It can be seen that it is positive.
전술한 본 발명의 실시형태에 관해, 추가로 이하의 부기 (付記) 를 개시한다.Regarding the above-described embodiment of the present invention, the following additional remarks are further disclosed.
<1><1>
종이 지지체와, 상기 종이 지지체의 편면에 제 1 도공층과, 종이 지지체를 기준으로 하여 상기 제 1 도공층의 외측에 제 2 도공층과, 및 종이 지지체를 기준으로 하여 상기 제 2 도공층의 외측에 제 3 도공층을 갖고, 상기 제 1 도공층이 카올린, 및 바인더로서 스티렌-부타디엔계 공중합 수지 및 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 상기 제 2 도공층이, 수지의 구성 단위로서 염화비닐리덴 단량체를 주성분으로서 갖는 폴리염화비닐리덴계 중합 수지를 함유하며, 그리고 상기 제 3 도공층이 아크릴계 수지를 함유하는 식품 포장 용지.A paper support, a first coated layer on one side of the paper support, a second coated layer on the outside of the first coated layer on the basis of the paper support, and an outside of the second coated layer on the basis of the paper support has a third coated layer, the first coated layer contains kaolin and one or two or more selected from the group consisting of a styrene-butadiene copolymer resin and an acrylic resin as a binder, and the second coated layer , A food wrapping paper containing a polyvinylidene chloride-based polymeric resin having a vinylidene chloride monomer as a main component as a constituent unit of the resin, and wherein the third coated layer contains an acrylic resin.
상기 식품 포장 용지는, 내수성, 내유성, 가스 배리어성, 수증기 배리어성 및 플레이버 배리어성을 갖고, 히트 시일 적성 및 접기 가공 적성을 구비하며, 그리고 내블로킹성을 갖는다.The food packaging paper has water resistance, oil resistance, gas barrier properties, water vapor barrier properties, and flavor barrier properties, has heat sealing properties and folding processing properties, and has blocking resistance.
<2><2>
상기 제 1 도공층이, 바인더로서 스티렌-부타디엔계 공중합 수지로 이루어지는 군에서 선택되는 1 종 혹은 2 종 이상, 또는 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 혹은 2 종 이상을 함유하는 상기 <1> 에 기재된 식품 포장 용지.The above <1> wherein the first coating layer contains, as a binder, one or two or more types selected from the group consisting of styrene-butadiene-based copolymer resins or one or two or more types selected from the group consisting of acrylic resins. Food packaging papers listed in .
<3><3>
상기 제 1 도공층이, 바인더로서 스티렌-부타디엔계 공중합 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 제 1 도공층에 있어서 상기 스티렌-부타디엔계 공중합 수지의 합계 함유량이, 종이 지지체의 편면당 제 1 도공층 중의 카올린 100 질량부에 대하여 40 질량부 이상 400 질량부 이하인 상기 <2> 에 기재된 식품 포장 용지.The first coated layer contains one or more selected from the group consisting of styrene-butadiene-based copolymer resins as a binder, and the total content of the styrene-butadiene-based copolymer resins in the first coated layer is paper The food packaging paper according to the above <2>, which is 40 parts by mass or more and 400 parts by mass or less with respect to 100 parts by mass of kaolin in the first coated layer per single side of the support.
이로써, 식품 포장 용지는, 가스 배리어성, 플레이버 배리어성 및/또는 접기 가공 적성이 양화된다.Thereby, the gas barrier property, the flavor barrier property, and/or the folding processability of the food wrapping paper are improved.
<4><4>
상기 제 1 도공층이, 바인더로서 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 제 1 도공층에 있어서 상기 아크릴계 수지의 합계 함유량이, 종이 지지체의 편면당 제 1 도공층 중의 카올린 100 질량부에 대하여 40 질량부 이상 400 질량부 이하인 상기 <2> 에 기재된 식품 포장 용지.The first coated layer contains one or more selected from the group consisting of acrylic resins as a binder, and the total content of the acrylic resins in the first coated layer is the first coated layer per one side of the paper support. The food packaging paper according to the above <2>, which is 40 parts by mass or more and 400 parts by mass or less with respect to 100 parts by mass of kaolin in the composition.
이로써, 식품 포장 용지는, 가스 배리어성, 플레이버 배리어성 및/또는 접기 가공 적성이 양화된다.Thereby, the gas barrier property, the flavor barrier property, and/or the folding processability of the food wrapping paper are improved.
<5><5>
상기 폴리염화비닐리덴계 중합 수지는, 수지 중의 염화비닐리덴 단량체가 85 질량% 이상 95 질량% 이하인 상기 <1> ∼ <4> 중 어느 하나에 기재된 식품 포장 용지.The food wrapping paper according to any one of <1> to <4>, wherein the polyvinylidene chloride-based polymeric resin has a vinylidene chloride monomer in the resin of 85% by mass or more and 95% by mass or less.
이로써, 식품 포장 용지는, 가스 배리어성 및 수증기 배리어성이 양화된다.Thereby, the gas barrier property and water vapor barrier property of the food wrapping paper are improved.
<6><6>
제 3 도공층이 함유하는 상기 아크릴계 수지가, 스티렌-아크릴계 공중합 수지인 상기 <1> ∼ <5> 중 어느 하나에 기재된 식품 포장 용지.The food wrapping paper according to any one of <1> to <5>, wherein the acrylic resin contained in the third coating layer is a styrene-acrylic copolymer resin.
이로써, 식품 포장 용지는, 접기 가공 적성 및 내블로킹성이 양화된다.As a result, the folding processability and blocking resistance of the food packaging paper are improved.
<7><7>
상기 제 3 도공층이, 파라핀 왁스를 추가로 함유하는 상기 <1> ∼ <6> 중 어느 하나에 기재된 식품 포장 용지.The food wrapping paper according to any one of <1> to <6>, wherein the third coated layer further contains paraffin wax.
이로써, 식품 포장 용지는, 수증기 배리어성 및/또는 내블로킹성이 양화된다.In this way, the water vapor barrier property and/or blocking resistance of the food wrapping paper is improved.
<8><8>
상기 제 3 도공층의 상기 파라핀 왁스가, 융점 50 ℃ 이상 80 ℃ 이하인 상기 <7> 에 기재된 식품 포장 용지.The food wrapping paper according to the above <7>, wherein the paraffin wax of the third coating layer has a melting point of 50°C or higher and 80°C or lower.
이로써, 식품 포장 용지는, 히트 시일 적성을 악화시키지 않고서 수증기 배리어성 및 내블로킹성이 양화된다.Thereby, the water vapor barrier property and blocking resistance of the food wrapping paper are improved without deteriorating the heat sealability.
<9><9>
상기 제 1 도공층의 상기 스티렌-부타디엔계 공중합 수지가, 공중합 수지 중의 스티렌계 단량체의 함유 질량 비율이 70 질량% 이상 90 질량% 이하인 상기 <3> 에 기재된 식품 포장 용지.The food wrapping paper according to <3> above, wherein the styrene-butadiene-based copolymer resin in the first coated layer has a content mass ratio of a styrene-based monomer in the copolymer resin of 70% by mass or more and 90% by mass or less.
이로써, 식품 포장 용지는, 가스 배리어성, 플레이버 배리어성 및 접기 가공 적성이 양화된다.Thereby, the gas barrier property, the flavor barrier property, and the folding processability of the food wrapping paper are improved.
<10><10>
상기 제 1 도공층의 상기 아크릴계 수지가, 스티렌-아크릴계 공중합 수지 또는 스티렌-(메트)아크릴로니트릴-아크릴계 공중합 수지인 상기 <4> 에 기재된 식품 포장 용지.The food wrapping paper according to <4>, wherein the acrylic resin of the first coating layer is a styrene-acrylic copolymer resin or a styrene-(meth)acrylonitrile-acrylic copolymer resin.
이로써, 식품 포장 용지는, 가스 배리어성 및 플레이버 배리어성이 양화된다.Thereby, the gas barrier property and the flavor barrier property of the food wrapping paper are improved.
<11><11>
상기 제 2 도공층의 상기 폴리염화비닐리덴계 중합 수지는, 수지 중, 염화비닐리덴 단량체가 85 질량% 이상 95 질량% 이하, (메트)아크릴로니트릴로 이루어지는 군에서 선택되는 단량체가 2 질량% 이상 10 질량% 이하, 그리고 (메트)아크릴산메틸 및 (메트)아크릴산에틸로 이루어지는 군에서 선택되는 단량체가 0.5 질량% 이상 5 질량% 이하인 상기 <3> 에 기재된 식품 포장 용지.The polyvinylidene chloride-based polymeric resin of the second coating layer contains 85% by mass or more and 95% by mass or less of a vinylidene chloride monomer, and 2% by mass of a monomer selected from the group consisting of (meth)acrylonitrile. 10% by mass or more, and 0.5% by mass or more and 5% by mass or less of a monomer selected from the group consisting of methyl (meth)acrylate and ethyl (meth)acrylate. The food wrapping paper according to <3> above.
이로써, 식품 포장 용지는, 가스 배리어성 및 수증기 배리어성이 양화된다.Thereby, the gas barrier property and water vapor barrier property of the food wrapping paper are improved.
<12><12>
상기 제 2 도공층의 상기 폴리염화비닐리덴계 중합 수지는, 수지 중, 염화비닐리덴 단량체가 85 질량% 이상 95 질량% 이하, (메트)아크릴로니트릴로 이루어지는 군에서 선택되는 단량체가 2 질량% 이상 10 질량% 이하, 그리고 (메트)아크릴산메틸 및 (메트)아크릴산에틸로 이루어지는 군에서 선택되는 단량체가 0.5 질량% 이상 5 질량% 이하인 상기 <4> 에 기재된 식품 포장 용지.The polyvinylidene chloride-based polymeric resin of the second coating layer contains 85% by mass or more and 95% by mass or less of a vinylidene chloride monomer, and 2% by mass of a monomer selected from the group consisting of (meth)acrylonitrile. 10% by mass or more, and 0.5% by mass or more and 5% by mass or less of a monomer selected from the group consisting of methyl (meth)acrylate and ethyl (meth)acrylate The food wrapping paper according to <4> above.
이로써, 식품 포장 용지는, 가스 배리어성 및 수증기 배리어성이 양화된다.Thereby, the gas barrier property and water vapor barrier property of the food wrapping paper are improved.
<13><13>
상기 제 3 도공층의 상기 아크릴계 수지가, 수지 중, 아크릴산계 단량체로서 (메트)아크릴산알킬에스테르를 50 질량% 초과로 함유하면서, (메트)아크릴산알킬에스테르와 스티렌이 공중합한 스티렌-아크릴계 공중합 수지인 상기 <3> 에 기재된 식품 포장 용지.The acrylic resin of the third coating layer is a styrene-acrylic copolymer resin in which an alkyl (meth)acrylate and styrene are copolymerized while containing an alkyl (meth)acrylate as an acrylic acid monomer in a resin in an amount of more than 50 mass%. The food packaging paper according to the above <3>.
이로써, 식품 포장 용지는, 내수성, 내유성, 접기 가공 적성 및 내블로킹성이 양화된다.As a result, the food packaging paper has improved water resistance, oil resistance, folding processability and blocking resistance.
<14><14>
상기 제 3 도공층의 상기 아크릴계 수지가, 수지 중, 아크릴산계 단량체로서 (메트)아크릴산알킬에스테르를 50 질량% 초과로 함유하면서, (메트)아크릴산알킬에스테르와 스티렌이 공중합한 스티렌-아크릴계 공중합 수지인 상기 <4> 에 기재된 식품 포장 용지.The acrylic resin of the third coating layer is a styrene-acrylic copolymer resin in which an alkyl (meth)acrylate and styrene are copolymerized while containing an alkyl (meth)acrylate as an acrylic acid monomer in a resin in an amount of more than 50 mass%. The food packaging paper according to the above <4>.
이로써, 식품 포장 용지는, 내수성, 내유성, 접기 가공 적성 및 내블로킹성이 양화된다.As a result, the water resistance, oil resistance, folding processability and blocking resistance of the food packaging paper are improved.
<15><15>
상기 제 1 도공층의 상기 스티렌-부타디엔계 공중합 수지가 공중합 수지 중의 스티렌계 단량체의 함유 질량 비율이 70 질량% 이상 90 질량% 이하이고, 상기 제 1 도공층의 상기 아크릴계 수지가 스티렌-아크릴계 공중합 수지 또는 스티렌-(메트)아크릴로니트릴-아크릴계 공중합 수지이고, 상기 제 2 도공층의 상기 폴리염화비닐리덴계 중합 수지가, 수지 중, 염화비닐리덴 단량체 85 질량% 이상 95 질량% 이하, (메트)아크릴로니트릴로 이루어지는 군에서 선택되는 단량체 2 질량% 이상 10 질량% 이하 그리고 (메트)아크릴산메틸 및 (메트)아크릴산에틸로 이루어지는 군에서 선택되는 단량체 0.5 질량% 이상 5 질량% 이하이며, 그리고 상기 제 3 도공층의 아크릴계 수지가 스티렌-아크릴계 공중합 수지인, 상기 <1> 에 기재된 식품 포장 용지.The styrene-butadiene-based copolymer resin of the first coating layer has a content mass ratio of styrene-based monomers in the copolymer resin of 70% by mass or more and 90% by mass or less, and the acrylic resin of the first coating layer is a styrene-acrylic copolymer resin or a styrene-(meth)acrylonitrile-acrylic copolymer resin, wherein the polyvinylidene chloride-based polymeric resin of the second coating layer contains 85% by mass or more and 95% by mass or less of vinylidene chloride monomer in the resin, (meth) 2% by mass or more and 10% by mass or less of a monomer selected from the group consisting of acrylonitrile, and 0.5% by mass or more and 5% by mass or less of a monomer selected from the group consisting of methyl (meth)acrylate and ethyl (meth)acrylate, and 3 The food packaging paper according to <1>, wherein the acrylic resin of the coating layer is a styrene-acrylic copolymer resin.
이로써, 식품 포장 용지는, 가스 배리어성, 수증기 배리어성, 플레이버 배리어성, 접기 가공 적성 및 내블로킹성이 양화된다.As a result, the food wrapping paper has improved gas barrier properties, water vapor barrier properties, flavor barrier properties, folding processability and blocking resistance.
<16><16>
상기 제 3 도공층이, 파라핀 왁스를 추가로 함유하는 상기 <15> 에 기재된 식품 포장 용지.The food wrapping paper according to the above <15>, wherein the third coating layer further contains paraffin wax.
이로써, 식품 포장 용지는, 수증기 배리어성 및/또는 내블로킹성이 양화된다.In this way, the water vapor barrier property and/or blocking resistance of the food wrapping paper is improved.
<17><17>
상기 제 3 도공층의 상기 파라핀 왁스가, 융점 50 ℃ 이상 80 ℃ 이하인 상기 <16> 에 기재된 식품 포장 용지.The food wrapping paper according to the above <16>, wherein the paraffin wax of the third coating layer has a melting point of 50°C or more and 80°C or less.
이로써, 식품 포장 용지는, 히트 시일 적성을 악화시키지 않고서 수증기 배리어성 및 내블로킹성이 양화된다.Thereby, the water vapor barrier property and blocking resistance of the food wrapping paper are improved without deteriorating the heat sealability.
Claims (10)
상기 제 1 도공층이 카올린, 그리고 바인더로서 스티렌-부타디엔계 공중합 수지 및 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고,
상기 제 2 도공층이, 수지의 구성 단위로서 염화비닐리덴 단량체를 주성분으로서 갖는 폴리염화비닐리덴계 중합 수지를 함유하며, 그리고
상기 제 3 도공층이 아크릴계 수지를 함유하는, 식품 포장 용지.A paper support, a first coated layer on one side of the paper support, a second coated layer on the outside of the first coated layer on the basis of the paper support, and an outside of the second coated layer on the basis of the paper support has a third coating layer,
The first coating layer contains kaolin and one or two or more selected from the group consisting of a styrene-butadiene copolymer resin and an acrylic resin as a binder,
The second coating layer contains a polyvinylidene chloride-based polymeric resin having a vinylidene chloride monomer as a main component as a resin constituent unit, and
The food packaging paper in which the said 3rd coating layer contains acrylic resin.
상기 제 1 도공층이, 바인더로서 스티렌-부타디엔계 공중합 수지로 이루어지는 군에서 선택되는 1 종 혹은 2 종 이상, 또는 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 혹은 2 종 이상을 함유하는 식품 포장 용지.According to claim 1,
The food wrapping paper in which the first coated layer contains, as a binder, one or two or more types selected from the group consisting of styrene-butadiene-based copolymer resins or one or two or more types selected from the group consisting of acrylic resins.
상기 제 1 도공층이, 바인더로서 스티렌-부타디엔계 공중합 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 제 1 도공층에 있어서 상기 스티렌-부타디엔계 공중합 수지의 합계 함유량이, 종이 지지체의 편면당 제 1 도공층 중의 카올린 100 질량부에 대하여 40 질량부 이상 400 질량부 이하인 식품 포장 용지.According to claim 2,
The first coated layer contains one or more selected from the group consisting of styrene-butadiene-based copolymer resins as a binder, and the total content of the styrene-butadiene-based copolymer resins in the first coated layer is paper Food packaging paper containing 40 parts by mass or more and 400 parts by mass or less with respect to 100 parts by mass of kaolin in the first coated layer per single side of the support.
상기 제 1 도공층이, 바인더로서 아크릴계 수지로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 함유하고, 제 1 도공층에 있어서 상기 아크릴계 수지의 합계 함유량이, 종이 지지체의 편면당 제 1 도공층 중의 카올린 100 질량부에 대하여 40 질량부 이상 400 질량부 이하인 식품 포장 용지.According to claim 2,
The first coated layer contains one or more selected from the group consisting of acrylic resins as a binder, and the total content of the acrylic resins in the first coated layer is the first coated layer per one side of the paper support. 40 parts by mass or more and 400 parts by mass or less based on 100 parts by mass of kaolin in the food packaging paper.
상기 폴리염화비닐리덴계 중합 수지는, 수지 중의 염화비닐리덴 단량체가 85 질량% 이상 95 질량% 이하의 것인 식품 포장 용지.According to any one of claims 1 to 4,
The food packaging paper in which the polyvinylidene chloride-based polymeric resin has a vinylidene chloride monomer in the resin of 85% by mass or more and 95% by mass or less.
제 3 도공층이 함유하는 상기 아크릴계 수지가, 스티렌-아크릴계 공중합 수지인 식품 포장 용지.According to any one of claims 1 to 5,
A food wrapping paper in which the acrylic resin contained in the third coating layer is a styrene-acrylic copolymer resin.
상기 제 3 도공층이, 파라핀 왁스를 추가로 함유하는 식품 포장 용지.According to any one of claims 1 to 6,
The food wrapping paper in which the said 3rd coating layer further contains paraffin wax.
상기 제 3 도공층의 상기 파라핀 왁스가, 융점 50 ℃ 이상 80 ℃ 이하의 것인 식품 포장 용지.According to claim 7,
The food wrapping paper in which the paraffin wax of the third coating layer has a melting point of 50°C or more and 80°C or less.
상기 제 1 도공층의 상기 스티렌-부타디엔계 공중합 수지가, 공중합 수지 중의 스티렌계 단량체의 함유 질량 비율이 70 질량% 이상 90 질량% 이하의 것인 식품 포장 용지.According to claim 3,
The food wrapping paper in which the styrene-butadiene-based copolymer resin of the first coating layer has a content mass ratio of a styrene-based monomer in the copolymer resin of 70% by mass or more and 90% by mass or less.
상기 제 1 도공층의 상기 아크릴계 수지가, 스티렌-아크릴계 공중합 수지 또는 스티렌-(메트)아크릴로니트릴-아크릴계 공중합 수지인 식품 포장 용지.According to claim 4,
The food packaging paper in which the acrylic resin of the first coating layer is a styrene-acrylic copolymer resin or a styrene-(meth)acrylonitrile-acrylic copolymer resin.