KR20220092382A - Fever alleviation patch using microperforation - Google Patents

Abstract

The present invention relates to a hydrogel antipyretic patch, which is used to reduce fever by being closely attached to a body part such as the forehead when an adult or especially a child suffers from fever due to high temperature in summer, tropical night, cold, and others and, more specifically, to a microperforation antipyretic patch which forms a number of microperforations in a nonwoven fabric used as a support layer without using separate cooling and endothermic chemical materials, so that heat accumulated in hydrogel is efficiently dissipated using natural physical phenomena, and the hydrogel can keep the initial temperature, and to a manufacturing method thereof.

Description

마이크로 천공을 갖는 해열패치 {FEVER ALLEVIATION PATCH USING MICROPERFORATION}Antipyretic patch with micro perforations {FEVER ALLEVIATION PATCH USING MICROPERFORATION}

본 발명은 냉각효과가 뛰어난 하이드로겔 해열패치에 관한 것으로서, 더욱 상세하게는 별도의 냉각성 및 흡열성 화학원료를 첨가하지 않으며, 신체에 닿지 않는 쪽에 다수의 마이크로 천공을 형성시키는 과정을 통해서 자연적 냉각효과를 최대로 하여 뛰어난 해열효과를 얻는 해열패치에 관한 것이다.The present invention relates to a hydrogel antipyretic patch having an excellent cooling effect, and more specifically, does not add a separate cooling and endothermic chemical raw material, and a natural cooling effect through the process of forming a number of micro-perforations on the side that does not touch the body It relates to an antipyretic patch that maximizes and obtains an excellent antipyretic effect.

최근 기후 이상으로 열대야가 지속되고, 신종 바이러스에 의한 초기 발열 증상이 더욱 더 잦아지고 있는데, 이러한 발열로 인해서 신체의 열이 37도를 넘게 되면 체온조절 밸런스가 깨지기 시작해서 각종 질병으로 이어질 수 있으며, 유아의 경우 고열이 지속되면 뇌 손상 등의 심각한 위험을 초래할 수 있기 때문에 최대한 빨리 열을 내려주는 것이 중요하다. 예전에는 열을 낮추기 위해서 수건 등의 천에 물을 적시거나 얼음을 이용하여 열을 내리기도 하였지만, 집 밖에서는 이러한 방법이 용이하지 않다. 수건 등의 방법을 개선하여 콜드팩, 아이스팩 등을 이용하는 특허와 (특허번호 10-1363085, 10-1622078) 제품들이 많이 나왔지만, 마찬가지로 미리 냉각을 시켜 놓거나, 냉장고의 얼음을 직접 이용 또는 구매한 얼음 등을 이용해야 하는 불편함이 있다. 그래서 이러한 불편함을 해소하기 위한 제품으로 냉각시트 또는 해열패치 등의 일회용 제품 관련 특허기술이 다수 소개되고 있다. 하지만 이러한 제품들 중에는 원료에 대한 피부자극 등의 안전성에 대한 보장이 없는 질산 암모늄 등의 화학원료를 사용하거나(특허번호 10-1296427), 패치 및 아이스팩 내에 열전도 및 열 흡수를 위한 화학물질을 사용하는데 (공개번호 1020180076399, 등록번호 1011226410000)이 또한 사용 중에 찢어지거나 압력에 의해서 터질 경우 피부 안전성 및 제품의 화학적 안전성에 대한 우려가 항상 따른다. 특히 민감한 유아들이나 여성의 피부에 오랫동안 밀착하여 방치시켰을 경우, 제품 자체에도 문제발생 여부가 있는데, 이러한 화학물질의 경우 피부에 대한 안전성이 문제가 될 수 있다. 또 최근에는 해열패치 시장이 커지고 있는 상황에서 곰팡이가 핀 중국산 제품들이 국내에 유통되어 사회적 문제가 되기도 하였다.Tropical nights continue due to the recent climate abnormality, and the initial fever symptoms caused by a new virus are becoming more and more frequent. In the case of infants, it is important to bring the fever down as soon as possible, since a high fever can lead to serious risks such as brain damage. In the past, to lower the heat, wet a cloth such as a towel with water or use ice to reduce the heat, but outside the house, this method is not easy. There have been many patents and products (Patent Nos. 10-1363085, 10-1622078) using cold packs and ice packs by improving methods such as towels, but similarly, pre-cooling, using ice from the refrigerator, or purchasing ice, etc. There is an inconvenience of having to use . Therefore, a number of patented technologies related to disposable products such as cooling sheets or heat-reducing patches have been introduced as products to solve such inconvenience. However, some of these products use chemical raw materials such as ammonium nitrate that do not guarantee the safety of raw materials such as skin irritation (Patent No. 10-1296427), or use chemicals for heat conduction and heat absorption in patches and ice packs. (Publication No. 1020180076399, Registration No. 1011226410000) Also, there are always concerns about skin safety and chemical safety of the product if it is torn during use or bursts under pressure. In particular, when left in close contact with sensitive infants or women's skin for a long time, there is a problem with the product itself. Also, recently, in the context of the growing market for antipyretic patches, moldy products from China were distributed in Korea and became a social problem.

본 발명은 상기 내용을 감안하여 이루어진 것으로, 팩 또는 공간을 이용한 화학원료 충전이 필요 없으며, 해열효과가 뛰어난 해열패치를 제공하는 것을 목적으로 한다.The present invention has been made in view of the above, and an object of the present invention is to provide an antipyretic patch having excellent antipyretic effect, which does not require packing of chemical raw materials using a pack or space.

본 발명은, 상기 목적을 달성하기 위해서, 하이드로겔 고분자를 기반으로 하여 안정적인 가교를 통해서 지지층 역할을 하는 부직포와의 충분한 점착성을 얻고, 이 지지층과 하이드로겔에 다수의 마이크로 천공을 통한 자연 발산 해열효과를 유도할 수 있는 제품을 이루고자 하였다.In order to achieve the above object, the present invention, based on a hydrogel polymer, obtains sufficient adhesion with a nonwoven fabric serving as a support layer through stable crosslinking, and naturally radiates antipyretic effect through a plurality of micro-perforations in the support layer and the hydrogel We wanted to achieve a product that can induce

기존 해열패치와 마이크로 천공 해열패치를 비교하였을 때, 일반인에서의 해열효과가 뚜렷하게 차이가 나는 것을 관찰할 수 있다.When comparing the existing antipyretic patch with the micro-perforated antipyretic patch, it can be observed that the antipyretic effect in the general public is clearly different.

도 1은 본 발명의 실시예의 구체적인 제품으로 해열패치의 구성을 나타내는 개략단면도이다. 도1에 나타낸 바와 같이 본 발명의 실시예 제품은 3단으로 이루어져 있으며, a) 부직포, b) 하이드로겔, c) 박리지로 이루어져 있다. 제품사용시 박리지는 제거하고 하이드로겔 층을 피부에 직접 부착하여 사용하는 것으로, 부직포는 이물질이 붙거나 점착 시 다루기 편하게 하기 위해서 냉각시트보다 더 넓게 디자인 되어있는 형태다. 부직포는 가로, 세로 방향으로 2-5mm 정도의 여유공간이 있어서 틈새로 이물질이 들어가지 못하도록 디자인되어 있어서 신체에 점착시킬 때 하이드로겔의 점착성이 다서 떨어지더라도 부직포의 점착성이 이를 보완해준다. 부직포는 도 2의 제조 공정에서 마지막 마이크로 천공작업을 통해서 처리가 완료된다.
도 2는 본 발명의 실시예의 제조공정을 나타내는 개략도이다. a) 박리지와 c) 부직포 사이로 b) 하이드로겔 원료가 주입되면서 제품을 구성하는 공정이다. 이어서 정해진 숙성시간을 거친 후 d) 마이크로 천공 로울러를 이용하여 마이크로 천공작업을 거치게 된다.
도 3은 마이크로 천공 공정을 통해서 얻어진 표면을 나타내는 사진이다.
도 4는 본 발명의 제조공정을 (도2) 거쳐서 생산된 실시예인, 마이크로 천공을 갖는 해열패치를 (두께 2.0mm, 3.5mm) 사용했을 때와 마이크로 천공이 없는 해열패치를 (두께 2.0mm, 3.5mm) 사용했을 때의 체온변화를 비교한 그래프이다.1 is a schematic cross-sectional view showing the configuration of a fever-reducing patch as a specific product according to an embodiment of the present invention. As shown in Fig. 1, the product of the embodiment of the present invention consists of three layers, a) a nonwoven fabric, b) a hydrogel, and c) a release paper. When using the product, the release paper is removed and the hydrogel layer is directly attached to the skin for use. The nonwoven fabric is designed wider than the cooling sheet to make handling easier when foreign substances are attached or adhered. The nonwoven fabric has 2-5mm of free space in the horizontal and vertical directions, so it is designed to prevent foreign substances from entering the gap. The nonwoven fabric is processed through the last micro-perforation operation in the manufacturing process of FIG. 2 .
2 is a schematic diagram showing a manufacturing process of an embodiment of the present invention. It is a process of composing a product while b) a hydrogel raw material is injected between a) release paper and c) nonwoven fabric. Then, after a predetermined aging time, d) micro-perforation is performed using a micro-perforation roller.
3 is a photograph showing the surface obtained through the micro-perforation process.
4 is an example produced through the manufacturing process of the present invention (FIG. 2), when using the antipyretic patch having micro-perforations (thickness 2.0mm, 3.5mm) and the antipyretic patch without micro-perforation (thickness 2.0mm, 3.5mm) is a graph comparing changes in body temperature when used.

본 발명의 마이크로 천공 하이드로겔을 이용한 해열패치는, 도2에 설명한 바와 같이 박리지의 일면에 하이드로겔 조성액을 도포한 후 부직포를 접착시키는 단계, 접착력을 높이기 위해서 구성성분의 환경에 맞게 냉각 또는 가열을 하는 단계, 열처리 후 제품 규격에 맞게 재단하는 단계(제품의 성분에 따라서 재단과정을 생략가능), 제품의 하이드로겔을 숙성시키는 단계, 숙성된 하이드로겔에 마이크로 천공을 뚫는 단계, 제품의 구성성분에 따라서 이전단계에서 재단하지 않은 경우 재단하는 단계, 제품을 포장하는 단계를 거쳐서 마이크로 천공 하이드로겔 해열패치를 제조한다.The antipyretic patch using the micro-perforated hydrogel of the present invention, as described in FIG. 2, after applying the hydrogel composition solution to one side of the release paper, and then adhering the nonwoven fabric, cooling or heating according to the environment of the components to increase the adhesive force After heat treatment, cutting according to product specifications (the cutting process can be omitted depending on the ingredients of the product), aging the hydrogel of the product, drilling micro-perforations in the aged hydrogel, component of the product Accordingly, if it is not cut in the previous step, the micro-perforated hydrogel antipyretic patch is manufactured through the step of cutting and packaging the product.

상기 마이크로 천공 하이드로겔 해열패치는 주 성분이 천연 수용성 고분자 또는 합성 수용성 고분자의 단량체, 글리세린, 첨가제, 정제수를 주 성분으로 한다. 이와 같은 성분으로 구성된 마이크로 천공 하이드로겔 해열패치는, 하이드로겔 층에 다량의 물이 고분자 격자 내에 팽윤된 상태로 채워져 있으며 숙성과정을 거쳐서 안정적으로 형태를 유지하여 액체와 고체의 중간 상태인 젤 타입의 물성을 갖는 제품이다. 본 발명을 통해서 생산된 마이크로 천공 하이드로겔 해열패치는 피부에 지속적인 수분공급을 하는 동시에 부착된 피부부위의 열을 열역학적 법칙에 따라서 상대적으로 낮은 온도 상태의 해열패치로 전달하여 피부 밀착부위의 열을 내려주고, 흡수된 열은 하이드로겔 반대쪽의 부직포의 마이크로 천공을 통해서 더욱 빠르게 발산되고, 동시에 기화열의 차이로 인해서 하이드로겔의 온도가 다시 내려가는 기능을 갖는 마이크로 천공 하이드로겔 해열패치이다. 또한 하이드로겔 내에 안전성이 확인되지 않은 화학물질이 전혀 첨가되지 않은 하이드로겔로서, 피부환경을 해치지 않으면서 피부자극을 완화하는 역할 또한 지니고 있다. The micro-perforated hydrogel antipyretic patch has a natural water-soluble polymer or synthetic water-soluble polymer monomer, glycerin, additives, and purified water as main components. The micro-perforated hydrogel antipyretic patch composed of these components is filled with a large amount of water in the hydrogel layer in a swollen state in the polymer lattice, and through the aging process, it stably maintains its shape, which is a gel type intermediate state between liquid and solid. A product with physical properties. The micro-perforated hydrogel antipyretic patch produced through the present invention provides continuous moisture to the skin and at the same time transfers heat from the attached skin area to the antipyretic patch at a relatively low temperature according to the thermodynamic law to lower the heat of the skin adhesion area It is a micro-perforated hydrogel antipyretic patch that has the function of lowering the temperature of the hydrogel again due to the difference in the heat of vaporization and at the same time dissipating the absorbed heat more rapidly through the micro-perforation of the nonwoven fabric opposite the hydrogel. In addition, as a hydrogel that does not contain any chemical substances whose safety has not been confirmed in the hydrogel, it also has a role of alleviating skin irritation without harming the skin environment.

상기 해열패치는 지지층으로의 부직포 및 박리지를 포함하고 있는데, 이는 제품포장 단계에서 점착성으로 인해서 포장하기 어렵고, 유통이나 보관과정에서 포장지에 점착되는 떨어지지 않거나 떨어질 때 이물질 및 제품형태가 무너지는 문제를 방지하기 위해서이다. 또한 사용시에는 박리지는 제거하고 피부에 붙이지만 부직포는 떨어지지 않는 점착성을 유지해야 한다. 부직포가 없는 경우에는 포장지를 제거한 후에도 일반적인 보관이 힘들며, 피부에 부착시키거나 사용 중에 먼지 등 이물질이 쉽게 달라붙는 문제가 발생하기 때문에 꼭 필요한 요소이다. 이와 같은 이유로 박리지와 부직포를 꼭 사용해야하며, 상기 공정을 통해서 부직포에 다수의 마이크로 천공이 촘촘히 형성되는데, 상기 마이크로 천공을 통해서 하이드로겔에 흡수된 열이 외부로 빠져나가는 원리이다. The antipyretic patch contains a non-woven fabric and release paper as a support layer, which is difficult to pack due to its adhesiveness in the product packaging stage, and prevents the problem of foreign substances and product form collapsing when falling or falling, which adheres to the packaging during distribution or storage. to do In addition, when using, remove the release paper and attach it to the skin, but the non-woven fabric must maintain the adhesiveness that does not fall off. If there is no non-woven fabric, it is difficult to store it in general even after the wrapping paper is removed, and it is a necessary element because foreign substances such as dust easily adhere to the skin or during use. For this reason, release paper and non-woven fabric must be used, and a number of micro-perforations are densely formed in the non-woven fabric through the above process, and the heat absorbed in the hydrogel through the micro-perforations is the principle to escape to the outside.

상기 마이크로 천공 하이드로겔 해열패치의 하이드로겔 구성성분은 천연 수용성 고분자이거나, 합성 수용성 고분자인 아크릴계 수용성 고분자, 다가 알콜계 수용성 고분자, 피롤리돈계 수용성 고분자를 단독 또는 2개 이상의 성분을 혼합하여 사용하는 것으로, 최적의 점착성을 지닌 상태로 제작되어, 피부에 밀착시켜 붙이면 쉽게 떨어지지 않는 동시에, 열이 내린 후 제거하기 위해서 떼어낼 때 특별한 힘을 가해주지 않아도 떨어지는 점착성을 띤 하이드로겔이다.The hydrogel component of the micro-perforated hydrogel antipyretic patch is a natural water-soluble polymer or a synthetic water-soluble polymer, such as an acrylic water-soluble polymer, a polyhydric alcohol-based water-soluble polymer, or a pyrrolidone-based water-soluble polymer alone or by mixing two or more components. , It is a hydrogel with optimum adhesiveness, so it does not come off easily when it is attached to the skin, and at the same time, it is a hydrogel with adhesiveness that falls without applying special force when peeling it off to remove it after the heat has gone down.

상기 마이크로 천공 하이드로겔 해열패치의 하이드로겔 구성성분 중 천연 수용성 고분자로는 로커스트콩검, 카라기난, 한천, 클루코만난, 알긴산나트륨, 펙틴, 젤라틴, 전분, 구아검, 잔탄검, 아라빅검으로 이루어진 군에서 선택된 1종 또는 2종 이상의 혼합물로 구성된 하이드로겔이 될 수 있다. Among the hydrogel components of the micro-perforated hydrogel antipyretic patch, natural water-soluble polymers include locust bean gum, carrageenan, agar, glucomannan, sodium alginate, pectin, gelatin, starch, guar gum, xanthan gum, from the group consisting of arabic gum It may be a hydrogel composed of one selected type or a mixture of two or more types.

상기 마이크로 천공 하이드로겔 해열패치의 하이드로겔 구성성분 중 합성 수용성 고분자로는 폴리아크릴산염, 폴리메타크릴산염, 폴리아크릴아마이드, 폴리우레탄, 폴리올, 폴리비닐알콜, 폴리비닐피롤리돈, 셀룰로스, 카복시메틸셀룰로스, 하이드록시에틸셀룰로스로 이루어진 군에서 선택된 1종 또는 2종 이상의 혼합물로 구성된 하이드로겔이 될 수 있다. Among the hydrogel components of the micro-perforated hydrogel antipyretic patch, synthetic water-soluble polymers include polyacrylate, polymethacrylate, polyacrylamide, polyurethane, polyol, polyvinyl alcohol, polyvinylpyrrolidone, cellulose, carboxymethyl. Cellulose, may be a hydrogel composed of one or a mixture of two or more selected from the group consisting of hydroxyethyl cellulose.

또한 상기 마이크로 천공 하이드로겔 해열패치의 하이드로겔 구성성분으로 중, 상기 천연 수용성 고분자 군과 상기 합성 수용성 고분자로 군에서 선택된 1종 또는 2종 이상의 혼합물로 구성된 하이드로겔이 될 수 있다. 또한 본 발명에서 이루고자하는 기술은 상기에서 언급된 수용성 고분자에 제한되지 않으며, 언급되지 않은 더 많은 천연 또는 합성 수용성 고분자들도 해당되는 것이다. In addition, among the hydrogel components of the micro-perforated hydrogel antipyretic patch, it may be a hydrogel composed of one or a mixture of two or more selected from the natural water-soluble polymer group and the synthetic water-soluble polymer group. In addition, the technology to be achieved in the present invention is not limited to the above-mentioned water-soluble polymers, and more natural or synthetic water-soluble polymers not mentioned above are also applicable.

상기 마이크로 천공 하이드로겔 해열패치의 하이드로겔 구성성분 중 조제용 첨가제 또는 기능성첨가제로는 계면활성제, 방부제, 가교제, 중합개시제, 보습제, 스킨컨디셔닝제, 향료, 콜라겐, 알로에 추출물, 비타민, 아로마 오일, 레티놀, 토코페롤, 글루코펩타이드, 세라마이드로 이루어진 군에서 선택된 1종 또는 2종 이상의 혼합물로 구성된 첨가제를 사용할 수 있다. Among the hydrogel components of the micro-perforated hydrogel antipyretic patch, additives or functional additives for preparation include surfactants, preservatives, crosslinking agents, polymerization initiators, moisturizing agents, skin conditioning agents, fragrances, collagen, aloe extract, vitamins, aroma oil, retinol , Tocopherol, glucopeptide, may be used an additive consisting of one or a mixture of two or more selected from the group consisting of ceramide.

상기 마이크로 천공 하이드로겔 해열패치의 하이드로겔 구성성분 중 박리지로는 폴리에틸렌 테레프탈레이트, 폴리에틸렌, 폴리프로필렌, 나일론, 폴리염화비닐, 폴리이소시아네이트 등의 일반적인 합성수지 필름으로 흡습성이 없는 필름이라면 상기 군에서 선택된 1종 또는 2종 이상의 혼합물로 구성된 박리지가 될 수 있다. Among the hydrogel components of the micro-perforated hydrogel antipyretic patch, the release paper is a general synthetic resin film such as polyethylene terephthalate, polyethylene, polypropylene, nylon, polyvinyl chloride, and polyisocyanate. Or it may be a release paper composed of a mixture of two or more kinds.

상기 마이크로 천공 하이드로겔 해열패치의 하이드로겔 구성성분 중 부직포로는 폴리에틸렌 테레프탈레이트, 폴리에틸렌, 폴리프로필렌, 나일론, 폴리염화비닐, 폴리이소시아네이트 등의 합성수지 류와 면, 펄프섬유, 마, 모, 견, 레이온 등의 천연섬유 류로 볼 수 있는데, 이 중에서 가공에 따라 흡습성이 중간정도의 부직포라면 상기 군에서 선택된 1종 또는 2종 이상의 혼합물로 구성된 부직포가 될 수 있다. 비흡습성인 경우에는 하이드로겔과의 점착성이 떨어지는 문제와 흡수된 열이 빠져나가지 못하는 문제가 있고, 고흡습성이면 하이드로겔의 수분이 빠져나와서 제품의 형태가 무너지는 문제가 있기 때문이다. Among the hydrogel components of the micro-perforated hydrogel antipyretic patch, nonwoven fabrics include synthetic resins such as polyethylene terephthalate, polyethylene, polypropylene, nylon, polyvinyl chloride, polyisocyanate, cotton, pulp fiber, hemp, wool, silk, rayon It can be viewed as natural fibers such as, among them, if the nonwoven fabric has a moderate hygroscopicity depending on processing, it may be a nonwoven fabric composed of one or a mixture of two or more selected from the group. In the case of non-hygroscopicity, there is a problem in that the adhesiveness with the hydrogel is lowered and the absorbed heat cannot escape, and in the case of high hygroscopicity, there is a problem in that the moisture of the hydrogel escapes and the shape of the product collapses.

상기 마이크로 천공 하이드로겔 해열패치의 주성분으로는 수용성고분자 5-50 중량%, 글리세린 20-40 중량%, 물 78-10 중량%로 조성되어, 물성에 따라서 상대적 비중이 자유롭게 달라지는 조성물이다. 수용성 고분자의 100 중량부에서 가교제 등의 기능성 물질 5-15 중량%를 혼합하고, 향료 및 계면활성제 등의 기능성 물질을 5-15 중량%를 혼합하여, 수분을 충분히 담지할 수 있는 하이드로겔로 이루어진 것을 특징으로하는 하이드로겔을 이용한 마이크로 천공 해열패치가 되겠다. As a main component of the micro-perforated hydrogel antipyretic patch, it is composed of 5-50% by weight of water-soluble polymer, 20-40% by weight of glycerin, and 78-10% by weight of water, and the relative specific gravity is freely changed according to physical properties. In 100 parts by weight of the water-soluble polymer, 5-15% by weight of a functional material such as a crosslinking agent is mixed, and 5-15% by weight of a functional material such as a fragrance and a surfactant is mixed to form a hydrogel capable of sufficiently supporting moisture. It will be a micro-perforated antipyretic patch using a hydrogel, characterized in that.

상기 하이드로겔을 이용한 마이크로 천공 해열패치에 하이드로겔 100 중량부 중에서 폴리아크릴레이트 30-60 중량%, 폴리비닐알콜 5-35 중량%, 폴리비닐피롤리돈 30-60 중량%, 젤라틴 5-35 중량%로 이루어진 것을 특징으로 하는 하이드로겔을 이용하여 제조하는데 있어서 제조 과정 중에서 충분히 물을 베어나오거나, 물이 전혀 흡수되지 않는 문제가 발생하지 않도록 중량비율을 조절해야 한다. 30-60 wt% of polyacrylate, 5-35 wt% of polyvinyl alcohol, 30-60 wt% of polyvinylpyrrolidone, 5-35 wt% of gelatin in 100 parts by weight of the hydrogel in the micro-perforated antipyretic patch using the hydrogel In manufacturing using a hydrogel, characterized in that it consists of %, it is necessary to adjust the weight ratio so as not to cause a problem in which water is sufficiently cut out during the manufacturing process or water is not absorbed at all.

공정을 통해서 패치 형태가 1차로 제조되면, 1-3일간 숙성을 시키는데, 충분히 숙성이 되지 않으면 앞에서 언급한 문제들이 발생하므로 조성비율에 맞춰 숙성 시간을 조절해야 한다. 숙성이 되어 원하는 물성을 갖추게 되면 상기 언급한 공정을 이용하여 가로세로 1mm 단위로, 지름 100마이크로미터 니들 로울러를 이용하여 마이크로 천공을 내어 다시 숙성시키는 과정을 거친다. 단위가 너무 좁으면 패치가 무너지고, 너무 넓으면 해열효과를 충분히 얻지 못한다.If the patch form is first manufactured through the process, it is aged for 1-3 days, but if it is not sufficiently aged, the above-mentioned problems occur, so the aging time should be adjusted according to the composition ratio. When it is aged and has the desired properties, it is subjected to a process of re-aging by making micro-perforations using a needle roller with a diameter of 100 micrometers in units of 1 mm in width and length using the above-mentioned process. If the unit is too narrow, the patch will collapse, and if it is too wide, the antipyretic effect will not be sufficiently obtained.

천공이 완료되고 숙성이 끝나면 제품의 두께를 측정하는데, 숙성과정에서 두께가 변하기 때문에반복 실험을 거쳐서 초기 형태를 갖추는 1차 단계에서 미리 예상하여 두께 조절을 해 놓는다. 최종적으로 두께는 0.5-3mm 로 조절한다. 만약 너무 얇으면 열 흡수 효과가 떨어지고, 너무 두꺼우면 열전달이 느려서 열 발산효과가 떨어진다. The thickness of the product is measured when the perforation is completed and the aging is completed. Since the thickness changes during the aging process, the thickness is adjusted in advance by predicting it in the first stage of acquiring the initial shape through repeated experiments. Finally, the thickness is adjusted to 0.5-3mm. If it is too thin, the heat absorption effect is reduced, and if it is too thick, the heat transfer is slow and the heat dissipation effect is reduced.

실시예 Example

도2에서 소개된 공정을 거쳐서, 다음 표와 같은 실시예 시료를 4종 준비한다. 이중 실시예 1이 본 발명에서 설명하고자 하는 시료이다. Through the process introduced in FIG. 2, four types of Example samples as shown in the following table are prepared. Among them, Example 1 is a sample to be described in the present invention.

성분명Ingredient name 실시예 1Example 1 실시예 2Example 2 실시예 3Example 3 실시예 4Example 4 폴리비닐알콜 외other than polyvinyl alcohol 30 중량%30% by weight 30 중량%30% by weight 30 중량%30% by weight 30 중량%30% by weight 글리세린 외 other than glycerin 30 중량%30% by weight 30 중량%30% by weight 30 중량%30% by weight 30 중량%30% by weight 물water 40 중량%40% by weight 40 중량%40% by weight 40 중량%40% by weight 40 중량%40% by weight 하이드로겔 두께 (mm)Hydrogel thickness (mm) 22 22 3.53.5 3.53.5 박리지release paper PETPET PETPET PETPET PETPET 부직포 / 마이크로천공 유무 Non-woven fabric / with or without micro-perforation PET / 유PET/U PET / 무 PET / no PET / 유PET/U PET / 무PET / no

온도 측정 시험temperature measurement test

준비된 실시예 시료들을 성인 이마부위에 부착시켜 2분 간격으로 적외선 체온계를 이용하여 떼어낸 부위의 온도를 측정하였다. 실험을 위해서 제조된 제품을 얇게 절단선을 심어 놓고, 주어진 시간 간격 때마다 제거하며 해당 부위의 온도를 측정하는 방법으로 30분에 걸쳐서 실험을 하였다. 동시에 제거된 하이드로겔 해열패치의 표면 온도는 일반 적외선 온도계로 측정하였고, 해열패치가 붙어있지 않았던 피부부위는 적외선 체온계로 측정하여 온도측정에 대한 오차를 확인하였다. The prepared Example samples were attached to the adult forehead, and the temperature of the removed area was measured using an infrared thermometer at intervals of 2 minutes. For the experiment, a thin cut line was planted on the manufactured product, and the experiment was conducted over 30 minutes by removing it at a given time interval and measuring the temperature of the area. At the same time, the surface temperature of the removed hydrogel antipyretic patch was measured with a general infrared thermometer, and the skin area to which the antipyretic patch was not attached was measured with an infrared thermometer to confirm the error in temperature measurement.

시험결과Test result

시간(분)hours (minutes) 실시예 1Example 1 실시예 1
패치온도Example 1
patch temperature 실시예 2Example 2 실시예 2
패치온도Example 2
patch temperature 실시예 3Example 3 실시예 3
패치온도Example 3
patch temperature 실시예 4Example 4 실시예 4
패치온도Example 4
patch temperature 00 36.636.6 20.020.0 36.636.6 20.020.0 36.636.6 20.020.0 36.636.6 20.020.0 22 36.436.4 22.222.2 36.436.4 21.821.8 36.436.4 21.821.8 36.436.4 21.021.0 44 36.236.2 22.322.3 36.236.2 22.122.1 36.336.3 22.322.3 36.336.3 21.821.8 66 36.136.1 22.422.4 36.136.1 22.522.5 36.336.3 22.622.6 36.336.3 21.821.8 88 35.735.7 22.422.4 36.236.2 22.122.1 36.236.2 22.522.5 36.236.2 22.022.0 1010 35.835.8 22.522.5 36.136.1 22.222.2 36.336.3 22.522.5 36.336.3 22.022.0 1212 35.735.7 22.522.5 36.236.2 21.721.7 36.236.2 22.522.5 36.236.2 22.122.1 1414 35.735.7 22.722.7 36.436.4 21.721.7 36.136.1 22.422.4 36.136.1 22.322.3 1616 35.535.5 23.023.0 36.236.2 22.022.0 36.236.2 22.322.3 36.236.2 22.322.3 1818 35.435.4 23.523.5 36.236.2 22.022.0 36.236.2 22.422.4 36.236.2 22.122.1 2020 35.535.5 22.022.0 36.236.2 21.721.7 36.136.1 22.422.4 36.136.1 22.322.3 2222 35.335.3 22.022.0 36.136.1 21.821.8 36.136.1 22.322.3 36.136.1 22.322.3 2424 35.335.3 22.222.2 36.236.2 21.821.8 36.236.2 22.322.3 36.236.2 22.122.1 2626 35.235.2 22.222.2 36.136.1 21.921.9 36.036.0 22.322.3 36.136.1 22.422.4 2828 35.335.3 22.022.0 36.236.2 21.721.7 36.036.0 22.422.4 36.136.1 22.122.1 3030 35.235.2 22.022.0 36.236.2 21.521.5 36.036.0 22.222.2 36.236.2 22.322.3

실시예들의 시험에서 해열패치가 붙어있지 않았던 부위는, 모든 경우에서, 0분에서의 체온측정 값과 비교하여 0.2도 내외로 나타났고, 이는 기기 오차 수준이기에 실험과정에서의 영향은 없음을 확인하였다. In the tests of the examples, the area where the antipyretic patch was not attached was found to be around 0.2 degrees compared to the temperature measurement value at 0 minutes in all cases, and it was confirmed that there was no effect in the experimental process because it was a level of device error. .

모든 실시예 시험에서 이마부위의 온도내림 현상을 확인하였다. 그 중에서도 실시예 1이 가장 높은 해열효과를 보였다. 또한 해열패치의 온도측정 결과를 보면 중간에 최고온도 피크가 발생하고 다시 내려오는 현상을 볼 수 있다. 예상대로 얇은 두께와 마이크로천공의 해열작용을 확인할 수 있었다. 마이크로 천공이 없는 실시예 2와 비교하면, 실험에서 1도의 차이를 보였다. 이는 작다고 할 수 있으나, 실제로 발열이 있어서 38도 이상의 환자에게는 엄청나게 큰 온도 차이이다. 사람의 체온이 1도만 올라가도 발열 및 감기초기 증상으로 진단하는 것을 고려하면 엄청나게 큰 온도 차이이다. 마찬가지로 실시예 3과 실시예 4의 경우는 실시예1과 비교하여 두께가 더 큰 경우인데 기본적인 해열효과는 있으나 실시예 2와 유사한 결과를 보였다. 하지만 떼어낸 해열패치의 표면 온도를 확인해보면 온도가 떨어지지 않고 있음을 알 수 있는데, 이는 흡수된 열이 바깥으로 방출되지 않고 해열패치 내에 갇혀 있다고 볼 수 있다. 실시예 3과 4는 마이크로 천공의 유무를 떠나서 비슷한 동향을 보이는 것으로 확인하였는데, 이는 30분이라는 짧은 시간에 기화작용을 확인할 수 없는 기간이라고 볼 수 있다. 제품 개발 단계에서 30분 이상의 테스트를 하면 온도가 계속 내려가는 것을 볼 수 있었기에, 이는 장기간 붙여 놓으면 효과를 볼 수 있다고 예상된다. 본 발명에서의 시험들은 본 발명의 특성을 설명하기 위해서 정리한 내용이기에 30분 내의 시간에서 결과가 나빠지지 않는 것을 보여준 사례일 뿐이다. The temperature drop phenomenon of the forehead area was confirmed in all the Example tests. Among them, Example 1 showed the highest antipyretic effect. Also, if you look at the temperature measurement result of the antipyretic patch, you can see that the highest temperature peak occurs in the middle and then comes back down. As expected, it was possible to confirm the antipyretic action of the thin thickness and micro-perforation. Compared with Example 2 without micro-perforation, it showed a difference of 1 degree in the experiment. This may be small, but it is actually a huge temperature difference for a patient with a fever of 38 degrees or higher. Even if a person's body temperature rises by just 1 degree, it is a huge temperature difference considering that it is diagnosed as a fever and early symptoms of a cold. Similarly, in the case of Examples 3 and 4, the thickness was larger than that of Example 1, and although there was a basic antipyretic effect, the results were similar to those of Example 2. However, if you check the surface temperature of the removed antipyretic patch, it can be seen that the temperature is not dropping. Examples 3 and 4 were confirmed to show a similar trend regardless of the presence or absence of micro-perforation, which can be seen as a period in which vaporization cannot be confirmed in a short time of 30 minutes. In the product development stage, if you test for more than 30 minutes, you can see that the temperature continues to drop, so it is expected that it will be effective if you stick it for a long time. Since the tests in the present invention are summarized to explain the characteristics of the present invention, they are only examples that show that the results do not deteriorate within 30 minutes.

실시예의 시험에서 발생하는 온도 측정의 한계는 일반적인 성인에게 실시한 점이다. 즉 체온이 정상온도를 유지하며, 조금이라도 체온이 내려가면 자연적으로 체온이 올라오는 신체현상을 억제하지 않았다는 의미이다. 다시 말해서 체온이 더 내려가면 신체에 문제가 생길 수 있다는 의미이다. 또 다른 접근방법으로 사물에 해열패치를 적용하여 온도를 측정하는 방법이 있을 수 있으나 이는 제품의 특성을 알 수 없게 된다. 결과적으로 이와 같은 시험을 통해서 얻는 결과들은 실제 발열 응급환자에게는 2-3배의 효과를 얻을 수 있게 되므로 충분한 시험이라 하겠다. The limit of temperature measurement that occurs in the test of the example is that it was performed on an ordinary adult. In other words, it means that the body temperature is maintained at a normal temperature, and the body temperature naturally rises when the body temperature goes down even a little. In other words, if your body temperature goes down further, you can have problems with your body. As another approach, there may be a method of measuring the temperature by applying an antipyretic patch to the object, but this will not know the characteristics of the product. As a result, the results obtained through such a test are sufficient tests because the effect can be obtained 2-3 times more effectively for emergency patients with fever.

Claims (1)

비흡습성의 박리지;
상기 박리지의 일면에 위치하는 하이드로겔; 및
상기 하이드로겔 상에 위치하는 흡습성의 부직포를 포함하고,
상기 하이드로겔은 수용성 고분자 5-50 중량%, 글리세린 20-40 중량% 및 잔부의 정제수를 포함하며,
상기 수용성 고분자는 폴리아크릴레이트 30-50 중량%, 폴리비닐알콜 5-25 중량%, 폴리비닐피롤리돈 30-50 중량%, 젤라틴 5-25 중량%, 가교제 5-10 중량%, 중합개시제 2.5-5 중량%, 향료 2.5-5 중량%를 포함하고,
상기 하이드로겔의 두께는 2mm이며,
상기 부직포는 지름이 100㎛인 천공이 0.5㎜ 내지 2㎜의 간격으로 배치되어 있는 것인 마이크로 천공 해열패치.non-hygroscopic release paper;
a hydrogel located on one side of the release paper; and
It includes a hygroscopic nonwoven fabric positioned on the hydrogel,
The hydrogel contains 5-50% by weight of a water-soluble polymer, 20-40% by weight of glycerin, and the remainder of purified water,
The water-soluble polymer is 30-50% by weight of polyacrylate, 5-25% by weight of polyvinyl alcohol, 30-50% by weight of polyvinylpyrrolidone, 5-25% by weight of gelatin, 5-10% by weight of crosslinking agent, 2.5% by weight of polymerization initiator -5% by weight, comprising 2.5-5% by weight of fragrance,
The thickness of the hydrogel is 2mm,
The micro-perforated antipyretic patch in which the nonwoven fabric has a diameter of 100 μm and perforations of 0.5 mm to 2 mm are arranged.

Images