KR20220050506A - Top coat for parking lot floor - Google Patents
Top coat for parking lot floor Download PDFInfo
- Publication number
- KR20220050506A KR20220050506A KR1020200134259A KR20200134259A KR20220050506A KR 20220050506 A KR20220050506 A KR 20220050506A KR 1020200134259 A KR1020200134259 A KR 1020200134259A KR 20200134259 A KR20200134259 A KR 20200134259A KR 20220050506 A KR20220050506 A KR 20220050506A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- parking lot
- coating agent
- methacrylate
- Prior art date
Abstract
Description
본 발명은 주차장 바닥용 코팅제 및 그 제조 방법에 관한 것으로서, 보다 상세하게는 주차장 바닥용 상도 코팅제 및 그 제조 방법에 관한 것이다.The present invention relates to a coating agent for a parking lot floor and a manufacturing method thereof, and more particularly, to a topcoat coating agent for a parking lot floor and a manufacturing method thereof.
차량으로부터 주차장 바닥을 보호하기 위해서 우레탄 바닥 코팅층이 시공된다. 우레탄 코팅층은 주차장 표면에 박막 코팅되는 하도층과, 후막의 중도층, 상도 코팅층으로 이루어진다.To protect the parking lot floor from vehicles, a urethane floor coating layer is installed. The urethane coating layer consists of an undercoat layer coated with a thin film on the parking lot surface, an intermediate layer of a thick film, and a top coat layer.
통상 상도층은 바닥과의 접착력이나 바닥의 수축, 팽창, 또는 갈라짐에 따른 도막 파손을 방지할 수 있도록 우수한 인장 및 신율을 가지는 하도층이나, 상부 하중을 견딜 수 있도록 고경도를 가지는 후막의 중도층과는 달리, 광택 및/또는 칼라와 같은 디자인적인 요소를 담당하게 되어, 통상의 에폭시나 우레탄 도막으로 이루어지는 경우가 많다. In general, the top coat layer is an undercoat layer with excellent tensile and elongation to prevent damage to the coating film due to adhesion to the floor or the shrinkage, expansion, or cracking of the floor, or a thick intermediate layer with high hardness to withstand the upper load. Unlike this, it is responsible for design elements such as gloss and/or color, and is often made of a conventional epoxy or urethane coating film.
하지만, 상도층의 손상에 의한 주차장 보수가 많아짐에 따라 상도층을 보호하거나 상도층을 개량하여 주차장 바닥의 유지 관리의 편의성을 높이고자 하는 시도가 이루어지고 있다. However, as the number of parking lot repairs due to damage to the upper floor increases, attempts are being made to protect the upper floor or improve the upper floor to increase the convenience of maintenance of the parking lot floor.
김우영에게 허여된 대한민국 특허 제2069038호에서는 시공면 상부에 우레탄 프라이머층과, 폴리우레아계 초고경질 후막 중도층과, 우레탄계 탑코팅재로 이루어진 상도층으로 이루어진 주차장 바닥 도막을 개시하며, 상도층의 표면에 침투층, 발열층, 및 보호층으로 이루어진 보호막을 더 형성하는 방안이 개시되어 있다. Korean Patent No. 2069038, granted to Kim Woo-young, discloses a parking lot floor coating comprising a urethane primer layer on the construction surface, a polyurea-based ultra-hard thick intermediate layer, and a top coating layer made of a urethane-based top coating material. A method of further forming a protective film comprising a permeation layer, a heating layer, and a protective layer is disclosed.
주식회사 피앤텍이엔지에 허여된 대한민국 특허 제1418863호에서는 규사 및 엠엠에이계 수지를 주원료로하는 상도층을 가지는 도막층이 개시되어 있다. Republic of Korea Patent No. 1418863 granted to P&Tech ENG Co., Ltd. discloses a coating layer having a top coat layer using silica sand and MMA-based resin as main raw materials.
하지만, 보다 다양하게 내스크래치, 내UV, 고광택, 미끄럼 방지, 내마모 특성 등이 우수한 새로운 상도층에 대한 요구가 계속되고 있다. However, there is a continuing demand for a new top coat layer with excellent scratch resistance, UV resistance, high gloss, anti-slip properties, and abrasion resistance.
본 발명에서 해결하고자 하는 과제는 스크래치, UV, 광택, 및 미끄럼 방지 특성이 우수한 주차장 바닥을 형성할 수 있는 상도용 코팅제를 제공하는 것이다. An object to be solved in the present invention is to provide a coating agent for a top coat that can form a parking lot floor having excellent scratch, UV, gloss, and anti-slip properties.
본 발명에서 해결하고자 하는 과제는 스크래치, UV, 광택, 및 미끄럼 방지 특성이 우수한 주차장 바닥을 형성할 수 있는 상도용 코팅제의 제조 방법을 제공하는 것이다. An object to be solved in the present invention is to provide a method for producing a coating agent for top coating that can form a parking lot floor having excellent scratch, UV, gloss, and anti-slip properties.
본 발명에서 해결하고자 하는 또 다른 과제는 스크래치, UV, 광택, 및 미끄럼 방지 특성이 우수한 상도층을 가지는 주차장 바닥을 제공하는 것이다. Another problem to be solved by the present invention is to provide a parking lot floor having an excellent topcoat layer with excellent scratch, UV, gloss, and anti-slip properties.
본 발명에서 해결하고자 하는 또 다른 과제는 스크래치, UV, 광택, 및 미끄럼 방지 특성이 우수한 상도층을 가지는 주차장 바닥을 시공하는 방법을 제공하는 것이다. Another object to be solved in the present invention is to provide a method for constructing a parking lot floor having an excellent topcoat layer with excellent scratch, UV, gloss, and anti-slip properties.
상기와 같은 과제를 해결하기 위해서, 본 발명은In order to solve the above problems, the present invention
수산기를 포함하는 실리콘아크릴 수지와 무황변 폴리이소시아네이트를 포함하는 것을 특징으로 하는 주차장 바닥용 상도용 코팅제를 제공한다. It provides a coating agent for a top coat for a parking lot floor, characterized in that it contains a silicone acrylic resin containing a hydroxyl group and non-yellowing polyisocyanate.
본 발명에 있어서, 상기 수산기를 포함하는 실리콘아크릴 수지와 무황변 폴리이소시아네이트는 공중합에 의해 실리콘 아크릴계 우레탄 도막을 형성한다. In the present invention, the silicone acrylic resin containing the hydroxyl group and the non-yellowing polyisocyanate form a silicone acrylic urethane coating film by copolymerization.
이론적으로 한정된 것은 아니지만, 본 발명의 수산기를 포함하는 실리콘 아크릴 수지는 실리콘 모노머를 도입하여 도막의 광택, 내스크래치성이 우수하고 고내후성을 발현하면서, 지방족기를 갖는 아크릴계 혹은 메타크릴계 단량체를 사용하여 유리전이 온도를 조정하고, 수산기를 갖는 메타크릴계 단량체를 도입하여 접착성을 증가시키고, 무황변 폴리이소시아네이트와의 가교결합에 의한 가교밀도를 높여 건조속도, 표면경도, 내용제성 등을 향상시켜 내후성을 부여하는 것이 가능하게 된다. Although not limited in theory, the silicone acrylic resin containing a hydroxyl group of the present invention introduces a silicone monomer to exhibit excellent gloss and scratch resistance and high weather resistance of the coating film, while using an acrylic or methacrylic monomer having an aliphatic group. Adjust the glass transition temperature, increase the adhesion by introducing a methacrylic monomer having a hydroxyl group, and increase the crosslinking density by crosslinking with non-yellowing polyisocyanate to improve drying speed, surface hardness, solvent resistance, etc. to improve weather resistance It becomes possible to give
본 발명에 있어서, 수산기를 포함하는 실리콘아크릴 수지는 실리콘 함유 단량체 10~30 중량&와 지방족기를 갖는 아크릴계 혹은 메타크릴계 단량체 60 내지 85 중량%와, 수산기를 갖는 메타크릴계 단량체 5 내지 10 중량%로 이루어질 수 있다.In the present invention, the silicone acrylic resin containing a hydroxyl group includes 10 to 30% by weight of a silicone-containing monomer, 60 to 85% by weight of an acrylic or methacrylic monomer having an aliphatic group, and 5 to 10% by weight of a methacrylic monomer having a hydroxyl group can be made with
본 발명에 있어서, 상기 실리콘 함유 단량체는 도막의 광택, 내스크래치성이 우수하고 고내후성을 발현하기 위해서 사용되고, 제한적이지는 않지만 실리콘 함유 단량체일 수 있으며, 하기 화학식(1)로 표현되는 화합물 중 1종 이상일 수 있다. In the present invention, the silicone-containing monomer is excellent in gloss and scratch resistance of the coating film and is used to express high weather resistance, and may be, but not limited to, a silicone-containing monomer, and is one of the compounds represented by the following formula (1) may be more than one species.
(1) (One)
본 발명에 있어서, 상기 실리콘 함유 단량체의 함량이 너무 낮을 경우에는 내후성이 불량하고 상대적으로 너무 높을 경우에는 가격상승, 도막의 경질화, 저장안정성이 불량할 수 있다.In the present invention, when the content of the silicone-containing monomer is too low, the weather resistance is poor, and when it is relatively high, the price increase, hardening of the coating film, and storage stability may be poor.
본 발명에 있어서, 상기 지방족기를 갖는 아크릴계 혹은 메타크릴계 단량체는 유리전이온도를 조절하여 도막의 경도를 조정하고 광택 및 평활성을 부여하기 위해서 사용되며, 예로는 제한적이지는 않지만, 노말부틸아크릴레이트, 2-에틸헥실아크릴레이트, 에틸아크릴레이트, 노말부틸메타크릴레이트, 노말프로필메타크릴레이트, 메틸메타크릴레이트, 에틸메타크릴레이트, 2-에틸헥실메타크릴레이트, 옥틸메타크릴레이트, 글리시딜메타크릴레이트, 라우릴메타크릴레이트, 이소보닐메타크릴레이트, 또는 이들의 2 이상의 혼합물일 수 있다. In the present invention, the acrylic or methacrylic monomer having an aliphatic group is used to adjust the hardness of the coating film by controlling the glass transition temperature and to impart gloss and smoothness, and examples thereof include, but are not limited to, normal butyl acrylate, 2-ethylhexyl acrylate, ethyl acrylate, normal butyl methacrylate, normal propyl methacrylate, methyl methacrylate, ethyl methacrylate, 2-ethylhexyl methacrylate, octyl methacrylate, glycidyl methacrylate It may be acrylate, lauryl methacrylate, isobornyl methacrylate, or a mixture of two or more thereof.
본 발명에 있어서, 상기 수산기를 갖는 메타크릴계 단량체는 도막의 경도 및 피도물과의 접착성 증진하기 위해서 사용되며, 제한적이지는 않지만, 2-히드록시에틸메타크릴레이트, 2-히드록시프로필메타크릴레이트, 4-히드록시부틸메타크릴레이트 또는 이들의 2 이상의 혼합물을 사용할 수 있다. 수산기가 함유된 메타크릴계 단량체는 이들을 과량 사용시 점성도 상승이 심해지는 문제가 발생한다. In the present invention, the methacrylic monomer having a hydroxyl group is used to enhance the hardness of the coating film and adhesion to the object to be coated, but is not limited thereto, but 2-hydroxyethyl methacrylate, 2-hydroxypropyl methacrylic lactate, 4-hydroxybutylmethacrylate or mixtures of two or more thereof can be used. When the methacrylic monomer containing a hydroxyl group is used in excess, there is a problem that the viscosity increases.
본 발명에 있어서, 상기 수산기를 포함하는 실리콘아크릴 수지는 고품질의 상도층을 형성할 수 있도록, 0 ℃ 이상의 유리전이온도, 바람직하게는 0~50 ℃의 유리전이온도를 가질 수 있으며, 보다 바람직하게는 20~40 ℃, 가장 바람직하게는 25~35 ℃의 유리전이온도를 가질 수 있다. In the present invention, the silicone acrylic resin containing the hydroxyl group may have a glass transition temperature of 0° C. or higher, preferably 0-50° C., more preferably, to form a high-quality topcoat layer. may have a glass transition temperature of 20 to 40 °C, most preferably 25 to 35 °C.
본 발명에 있어서, 상기 실리콘아크릴계 우레탄을 이루는 무황변 폴리이소시아네이트는 지방족 폴리이소시아네이트를 의미하며, 바람직하게는 NCO %가 10이상, 바람직하게는 15이상, 보다 바람직하게는 20 이상일 수 있다. In the present invention, the non-yellowing polyisocyanate constituting the silicone acrylic urethane means an aliphatic polyisocyanate, and preferably has an NCO% of 10 or more, preferably 15 or more, more preferably 20 or more.
본 발명에 있어서, 상기 무황변 폴리이소시아네이트는 독일 Bayer사, 국내 애경화학의 AH 시리즈의 무황변 폴리이소시아네이트를 사용할 수 있다. 본 발명의 실시에 있어서, 화제로 사용되는 무황변형 폴리이소시아네이트는 독일 Bayer사 Desmodur N-3300(NCO=23%)을 사용하였다. In the present invention, the non-yellowing polyisocyanate may be a non-yellowing polyisocyanate of the German Bayer company, AH series of domestic Aekyung Chemical. In the practice of the present invention, as the non-yellowing polyisocyanate used as a topical agent, Desmodur N-3300 (NCO=23%) manufactured by Bayer, Germany was used.
본 발명의 실시에 있어서, 상기 경화제의 사용 함량은 실리콘아크릴수지의 수산기를 감안하여 NCO/OH의 당량비를 1/1로 사용하는 것이 바람직하다. 상기 실리콘아크릴수지의 수산기나 이소시아네이트기가 가교반응에 참여하지 않고 남을 경우에는 치밀한 가교결합을 이루지 못해 도막물성의 저하를 가져올 수 있다. In the practice of the present invention, it is preferable to use an equivalent ratio of NCO/OH to 1/1 in consideration of the hydroxyl group of the silicone acrylic resin for the amount of the curing agent used. If the hydroxyl group or the isocyanate group of the silicone acrylic resin does not participate in the cross-linking reaction, it may not form a dense cross-linking, which may result in deterioration of the physical properties of the coating film.
본 발명에 있어서, 상기 상도용 코팅제는 코팅제 100 중량부에서 실리콘아크릴계 우레탄을 20~50 중량부 포함할 수 있으며, 바람직하게는 25~45 중량부, 보다 바람직하게는 30~40 중량부 포함할 수 있다. 상기 실리콘아크릴계 우레탄의 함량이 적으로면 견고한 상도 도막이 형성되기 어렵게 되며, 상기 실리콘아크릴계 우레탄의 함량이 많으면 용매나 다른 성분들의 함량이 줄어드어 적절한 특성의 도막을 형성하기 어려울 수 있다. In the present invention, the top coating agent may contain 20-50 parts by weight of silicone acrylic urethane based on 100 parts by weight of the coating agent, preferably 25-45 parts by weight, more preferably 30-40 parts by weight. there is. When the content of the silicone acrylic urethane is small, it is difficult to form a strong top coat, and when the content of the silicone acrylic urethane is high, the content of the solvent or other components is reduced, so it may be difficult to form a coating film having appropriate properties.
본 발명에 있어서, 상기 상도용 코팅제는 미끄럼방지와 내마모성을 부여하기 위해 티탄산칼륨을 더 포함할 수 있다. 상기 티탄산 칼륨은 다양한 크기와 형상구조의 기능성 소재로써 K2OㆍnTiO2로 표시되고, 식의 n치는 1, 2, 4, 6, 8로 표시할수 있다. 그중 n이 2, 4, 6, 8일 때 티탄산칼륨은 전부 결정질 섬유로 되고, Mg 등의 첨가에 의한 형상 제어가 가능하고, 특히, 6티탄산칼륨은 화학적 안정성, 내마모성, 열안정성, 내충격성, 적외선 반사, 내절연성 등 탁월한 성능을 가지고 있어, 금속, 플라스틱, 세라믹 등의 강화재로 활용이 가능하여 내마찰재로 널리 사용되는 재료이다. In the present invention, the coating agent for the top coat may further include potassium titanate to provide anti-slip and wear resistance. The potassium titanate is a functional material of various sizes and shapes and is expressed as K 2 O·nTiO 2 , and the n value of the formula can be expressed as 1, 2, 4, 6, 8. Among them, when n is 2, 4, 6, 8, potassium titanate becomes all crystalline fibers, and shape control is possible by addition of Mg, etc. In particular, potassium hexatitanate has chemical stability, abrasion resistance, thermal stability, impact resistance, It has excellent performance such as infrared reflection and insulation resistance, so it can be used as a reinforcing material for metals, plastics, ceramics, etc., and is widely used as a friction-resistant material.
본 발명에 있어서, 상기 티탄산 칼륨은 상도 코팅제 100 중량부에서 9 내지 30 중량부인 것이 바람직하다. 티탄산 칼륨의 함량이 9 중량부 미만일 경우 최종 도막에서 미끄럼방지와 내마모성이 떨어지며, 30 중량부 초과인 경우 분산성이 나빠져 도장이 곤란해진다. 티탄산칼륨은 평균 입도가 25~75㎛인 것이 바람직하며, 티탄산칼륨의 형상은 판상, 봉상, 침상, 휘스커상 등이 사용되며, 이 중에서 1종 또는 그 이상을 사용할 수 있다.In the present invention, the potassium titanate is preferably 9 to 30 parts by weight based on 100 parts by weight of the top coating agent. When the content of potassium titanate is less than 9 parts by weight, the anti-slip and abrasion resistance in the final coating film is deteriorated, and when the content of potassium titanate is more than 30 parts by weight, the dispersibility deteriorates and coating becomes difficult. The potassium titanate preferably has an average particle size of 25 to 75 μm, and the potassium titanate has a plate shape, a rod shape, a needle shape, a whisker shape, and the like, and one or more of them may be used.
본 발명에 있어서, 상기 상도용 코팅제는 상도층의 차열을 위해서 차열안료를 더 포함할 수 있다. 상기 차열안료는 근적외선 파장영역인 300 ~ 2,500 nm 파장을 90% 이상 반사하고, 건조 후 도막 내에 세라믹 거품(bubble)을 생성하여 열에너지를 흡수 및 소멸시킴으로서 열에너지 전도를 차단하는 세라믹 스피어(ceramic spheres)임이 바람직하다. 상기 세라믹 스피어는 세라믹을 4 ~ 10 마이크로미터 크기를 가지는 무공질의 구형태로 제조한 것으로서, 세라믹 구에 의해 빛이 열에너지로 전환되지 못하도록 산란시키는 열반사(reflectance) 기능을 수행하여 차열성능을 발휘하게 된다. In the present invention, the coating agent for the top coat may further include a heat shielding pigment for heat shielding of the top coat layer. The heat-shielding pigment reflects more than 90% of the wavelength of 300 to 2,500 nm, which is the near-infrared wavelength region, and after drying, it creates ceramic bubbles in the coating film to absorb and dissipate thermal energy, thereby blocking the conduction of thermal energy. Ceramic spheres. desirable. The ceramic sphere is manufactured in the form of a nonporous spherical ceramic having a size of 4 to 10 micrometers, and performs a heat reflection function to scatter light so as not to be converted into thermal energy by the ceramic sphere to exhibit heat shielding performance. do.
본 발명에 있어서, 상기 차열안료는 상도용 코팅제 100 중량부에서 5 내지 15 중량부인 것이 바람직하며, 보다 바람직하게는 7~12 중량부일 수 있다. 상기 차열안료의 함량이 5중량부 미만이면 요구되는 단열성능을 발휘하기 어렵고, 15 중량부 초과하면 다른 물성에 영향을 미쳐 차열성능이 유지되나 중도층 도막과의 부착성을 저하시키는 문제점이 있다.In the present invention, the amount of the heat shielding pigment is preferably 5 to 15 parts by weight based on 100 parts by weight of the topcoating agent, and more preferably 7 to 12 parts by weight. If the content of the heat-shielding pigment is less than 5 parts by weight, it is difficult to exhibit the required thermal insulation performance, and if it exceeds 15 parts by weight, other physical properties are affected and the heat-shielding performance is maintained, but there is a problem of lowering the adhesion with the intermediate layer coating film.
본 발명에 있어서, 상기 상도용 코팅제는 상기 차열안료와의 시너지를 위해서 방열성을 지닌 금속성 무기 방열안료를 더 포함할 수 있다. 방열안료로는 산화티탄, 산화아연, 산화인듐, 산화주석, 안티몬 주석 산화물(Antimony Tin Oxide), 인듐 주석 산화물(Indium Tin Oxide), 몰리브덴옥사이드(MoO3), 산화탄탈(Ta2O5), 오산화바나듐(V2O5), 산화니오브(Nb2O5), 보론 니트로나이트(BN), 육방정계 질화붕소(h-BN), 알루미늄 옥사이드(AL2O3)로 이루어진 군에서 선택된 적어도 하나 이상을 포함하여 조성될 수 있다.In the present invention, the coating agent for the top coat may further include a metallic inorganic heat dissipation pigment having heat dissipation properties for synergy with the heat blocking pigment. Heat radiation pigments include titanium oxide, zinc oxide, indium oxide, tin oxide, antimony tin oxide, indium tin oxide, molybdenum oxide (MoO3), tantalum oxide (Ta2O5), vanadium pentoxide (V2O5). ), niobium oxide (Nb2O5), boron nitronite (BN), hexagonal boron nitride (h-BN), and aluminum oxide (AL2O3).
본 발명은 바람직한 실시예로, 무기 방열안료 중에서도 특히 육방정계 질화붕소(hexagonal boron nitride, 이하 h-BN으로 칭함)는 2차원 구조를 갖는 물질로서, 붕소원자와 질소 원자의 육각 배열로 이루어져 있으며, 약 5.9 eV의 큰 밴드갭으로 인해 전기적 절연특성을 가지고, 물리적 및 기계적으로 안정한 물질에 해당한다. h-BN의 결정은 흑연과 유사한 육각방면의 적층 구조를 가져 매우 단단한 결합을 형성하며, 윤활성을 갖는다. 또한 h-BN 시트는 원자 번호가 낮은 원소의 공유결합 물질로서 높은 열전도성을 가지며, 융점을 가지지 않고 약 3,000℃에서 승화되므로 고온에서 높은 안정성을 가지고, 전기 저항이 매우 높아 1,000℃를 넘는 고온 영역에서 105Ω의 저항을 가지며, 매우 안정한 육각면의 결합을 가지므로 높은 화학적 안정성을 가지고, 진비중이 2.26으로서 세라믹 중에서는 매우 낮은 편이므로 항공기, 우주재료 등의 부품 경량화를 유도할 수 있다. 이와 같은 h-BN은 벌크타입의 구조체를 형성한 후 기계적 박리법을 이용하여 분리하여 사용하는데 품질은 우수하나 크기가 5 ㎛ 이하에 불과하다.The present invention is a preferred embodiment, and among inorganic heat dissipation pigments, in particular, hexagonal boron nitride (hereinafter referred to as h-BN) is a material having a two-dimensional structure, and consists of a hexagonal arrangement of boron atoms and nitrogen atoms, Due to the large band gap of about 5.9 eV, it has electrical insulating properties and corresponds to a material that is physically and mechanically stable. The crystals of h-BN have a hexagonal layered structure similar to graphite, forming a very hard bond and having lubricity. In addition, the h-BN sheet has high thermal conductivity as a covalent material of an element with a low atomic number, does not have a melting point, and sublimes at about 3,000 ° C. It has a resistance of 105Ω, has high chemical stability because it has a very stable hexagonal bond, and has a true specific gravity of 2.26, which is very low among ceramics, so it can induce weight reduction of parts such as aircraft and space materials. Such h-BN is used after forming a bulk-type structure and separated using a mechanical peeling method. Although the quality is excellent, the size is only 5 μm or less.
본 발명에 있어서, 상기 방열안료는 상도용 코팅제 100 중량부에서 1 내지 15 중량부인 것이 바람직하다. 1 중량부 미만이면 요구되는 시너지 효과를 발휘하기 어렵고, 15 중량부 초과하면 다른 물성에 영향을 미쳐 차열성능이 유지되나 도막의 부착성이 저하되고 원가가 상승하는 문제점이 발생할 수 있다. In the present invention, it is preferable that the heat dissipation pigment is 1 to 15 parts by weight based on 100 parts by weight of the top coating agent. If it is less than 1 part by weight, it is difficult to exert the required synergistic effect, and if it exceeds 15 parts by weight, other physical properties are affected and the heat shielding performance is maintained, but there may be problems in that the adhesion of the coating film is lowered and the cost is increased.
본 발명에 있어서, 상기 상도용 코팅제는 균일한 도막용 조성물을 형성하도록 용매를 포함할 수 있다. 본 발명에서 사용되는 용매는 톨루엔, 키실렌 등의 방향족계 탄화수소, 노말부틸아세테이트, 에틸렌글리콜에틸에테르아세테이트 등의 에스테르류, 메틸이소부틸케톤, 메틸노말아밀케톤 등의 케톤류, 이소프로판올, 노말부탄올, 이소부탄올 등의 알콜류 및 에틸렌글리콜모노메틸에테르, 프로필렌글리콜모노메틸에테르 등의 글리콜 에테르류 사용할 수 있고, 반응온도가 합성수지의 분자량과 최종점도에 미치는 영향을 감안하여 이들 용매를 단독 또는 혼합 사용할 수 있으며 합성수지의 합성온도, 용해도파라미터, 증발속도 등을 감안하여 용매의 비점이 100~160 ℃인 용매를 사용하여, 적합하게는 비점이 110~150 ℃ 범위인 것을 사용하여 합성하는 것이 바람직하다.In the present invention, the top coating agent may include a solvent to form a uniform coating composition. The solvent used in the present invention includes aromatic hydrocarbons such as toluene and xylene, esters such as normal butyl acetate and ethylene glycol ethyl ether acetate, ketones such as methyl isobutyl ketone and methyl normal amyl ketone, isopropanol, normal butanol, and iso Alcohols such as butanol and glycol ethers such as ethylene glycol monomethyl ether and propylene glycol monomethyl ether can be used. In consideration of the synthesis temperature, solubility parameter, evaporation rate, etc., it is preferable to use a solvent having a boiling point of 100 to 160 ° C.
본 발명에 있어서, 상기 용매는 상도용 코팅제 100 중량부에서 10 내지 40 중량부, 바람직하게는 15~35 중량부일 수 있다. 상기 용매의 함량이 적으면 균일한 박막 도막을 형성하기가 쉽지 않게 되며, 용매의 함량이 많으면 소정 두께의 도막을 형성하기가 어렵게 되며, 많은 유기 용매들이 방출되게 된다. In the present invention, the solvent may be 10 to 40 parts by weight, preferably 15 to 35 parts by weight, based on 100 parts by weight of the top coating agent. When the content of the solvent is small, it is difficult to form a uniform thin film, and when the content of the solvent is large, it is difficult to form a coating film of a predetermined thickness, and a lot of organic solvents are released.
본 발명에 있어서, 상기 상도용 코팅제는 균일한 도막의 형성을 위해서, 소포제 또는 레벨링제와 같은 통상적인 첨가제를 포함할 수 있다. 상기 첨가제는 상도용 코팅제 100 중량부에서 1 내지 5 중량부를 이룰 수 있다. In the present invention, the top coating agent may include conventional additives such as an antifoaming agent or a leveling agent to form a uniform coating film. The additive may constitute 1 to 5 parts by weight in 100 parts by weight of the topcoating agent.
본 발명은 일 측면에서, The present invention in one aspect,
수산기를 포함하는 실리콘아크릴 수지를 용액 중합을 통해서 제조하고, 상기 실리콘아크릴 수지 용액과 무황변형 폴리이소시네이트와, 티탄산칼륨, 차열안료, 방열안료, 및 첨가제와 혼합하여 상도용 코팅제를 제조하는 방법을 제공한다. A method of preparing a silicone acrylic resin containing a hydroxyl group through solution polymerization, and mixing the silicone acrylic resin solution, non-yellowing polyisocyanate, potassium titanate, heat-shielding pigment, heat-dissipating pigment, and additives to prepare a topcoat coating agent to provide.
본 발명에 있어서, 상기 수산기를 포함하는 실리콘아크릴 수지는 비닐형 이중결합을 갖는 단량체들을 열분해 개시제를 사용하여 라디칼 중합시켜 제조될 수 있으며, 상기 라디칼 중합은 용액중합 방법을 이용할 수 있다. In the present invention, the silicone acrylic resin including the hydroxyl group may be prepared by radical polymerization of monomers having a vinyl-type double bond using a thermal decomposition initiator, and the radical polymerization may be performed using a solution polymerization method.
본 발명의 실시에 있어서, 상기 수산기를 포함하는 실리콘아크릴 수지는 실리콘 단량체 10 내지 30 중량부, 지방족기를 갖는 아크릴계 혹은 메타크릴계 단량체 60 내지 85 중량부, 수산기를 갖는 메타크릴계 단량체 5 내지 10 중량부로 이루어진 단량체 100 중량부와 반응 개시제 1 내지 3 중량부를 중비점 용매에 3~5시간 동안 적하하면서, 80~100 ℃의 온도에서 8~12시간 동안 중합시켜, 수지 조성물의 수평균분자량 16,000~20,000, 유리전이온도 +30 ℃, 점도 5~15 cPs 범위를 갖고 고형분 농도가 50%인 실리콘아크릴수지 조성물로 제공한다. In the practice of the present invention, the silicone acrylic resin including a hydroxyl group is 10 to 30 parts by weight of a silicone monomer, 60 to 85 parts by weight of an acrylic or methacrylic monomer having an aliphatic group, 5 to 10 parts by weight of a methacrylic monomer having a hydroxyl group 100 parts by weight of the monomer and 1 to 3 parts by weight of the reaction initiator are added dropwise to a medium boiling point solvent for 3 to 5 hours, and polymerized at a temperature of 80 to 100° C. for 8 to 12 hours, and the number average molecular weight of the resin composition is 16,000 to 20,000 , a glass transition temperature of +30 ℃, a viscosity in the range of 5 to 15 cPs, and is provided as a silicone acrylic resin composition having a solid concentration of 50%.
본 발명에 있어서, 상기 중합에 사용되는 라디칼 중합성 개시제로서 과산화벤조일, 터셔리부틸퍼옥시벤조에이트, 터셔리부틸퍼옥시-2-에틸헥사노에이트, 터셔리아밀퍼옥시-2-에틸헥사노에이트, 아조비스이소부티로니트릴 등을 들 수 있다. 이와같은 라디칼 중합성 개시제는 단독 또는 2종 이상 같이 사용할 수 있다. 개시제의 사용량은 단량체 조성 총중량에 대하여 1 내지 3 중량부가 되도록 사용하며 바람직하게는 1 내지 2 중량부이다. 만약 라디칼 개시제의 함량이 너무 적을 경우에는 점도와 분자량이 커져 실끌림 현상을 발생하여 스프레이 작업성이 불량하고, 상대적으로 너무 많을 경우에는 지나친 분자량 저하에 의한 도막물성의 저하를 가져올 수 있다. In the present invention, as the radical polymerization initiator used for the polymerization, benzoyl peroxide, tert-butylperoxybenzoate, tert-butylperoxy-2-ethylhexanoate, terteriamilperoxy-2-ethylhexano ate, azobisisobutyronitrile, and the like. Such radical polymerization initiators may be used alone or in combination of two or more. The amount of the initiator used is 1 to 3 parts by weight, preferably 1 to 2 parts by weight, based on the total weight of the monomer composition. If the content of the radical initiator is too small, the viscosity and molecular weight increase, resulting in thread drag, resulting in poor spray workability.
본 발명에 있어서, 상기 수지조성물 합성 방법은 위에서 나열한 단량체들과 개시제를 포함하는 혼합용액을 3~5시간 동안 균일한 속도로 반응기 내의 용매 용액에 투입, 적하하면서, 80~100 ℃의 온도에서 8~12시간 동안 중합시켜 진행한다. 상기와 같이, 반응조건을 안정적으로 유도함으로써 수지의 광택이 우수하고, 평활성이 양호하며, 내스크래치성이 양호한 실리콘 함유 아크릴수지 조성물을 수득할 수 있다.In the present invention, in the method for synthesizing the resin composition, a mixed solution containing the above-listed monomers and an initiator is added and dropped into the solvent solution in the reactor at a uniform rate for 3 to 5 hours, while dripping at a temperature of 80 to 100 ° C. Proceed by polymerization for ~12 hours. As described above, by stably inducing the reaction conditions, a silicone-containing acrylic resin composition having excellent gloss, good smoothness, and good scratch resistance can be obtained.
본 발명은 일 측면에 있어서,The present invention in one aspect,
기반층의 표면에 형성되는 프라이머 하도층;a primer undercoat layer formed on the surface of the base layer;
상기 하도층의 표면에 형성되는 중도층; 및an intermediate layer formed on the surface of the undercoat layer; and
상기 중도층의 표면에 형성되는 상도층으로 이루어지고,Consists of a top coat layer formed on the surface of the intermediate layer,
상기 상도층은 실리콘 아크릴계 우레탄 수지를 포함하는 것을 특징으로 하는 주차장 바닥용 도막을 제공한다. The top coat layer provides a coating film for a parking lot floor, characterized in that it contains a silicone acrylic urethane resin.
본 발명에 있어서, 상기 상도층은 상도용 코팅제를 50~100㎛가 되도록 코팅하여 미끄럼방지와 내마모성이 우수하고 차열성능 및 내후성이 우수한 상도 코팅층을 형성할 수 있다. In the present invention, the top coat layer can form a top coat layer with excellent anti-slip and abrasion resistance and excellent heat shielding performance and weather resistance by coating the top coat agent to a thickness of 50 to 100 μm.
본 발명은 일 측면에서, The present invention in one aspect,
주차장 바닥에 코팅되는 프라이머 하도층을 형성하는 단계;forming a primer undercoat layer to be coated on the parking lot floor;
상기 프라이머 하도층 위에 후막의 중도층을 형성하는 단계; 및forming a thick intermediate layer on the primer undercoat layer; and
상기 후막의 중도층 위에 실리콘아크릴계 우레탄을 포함하는 코팅제로 상도층을 형성하는 단계;를 포함하는 주차장 바닥용 도막 시공 방법을 제공한다. It provides a method for constructing a coating film for a parking lot floor, including a; forming a top coat layer with a coating agent containing silicone acrylic urethane on the middle layer of the thick film.
본 발명의 실시에 있어서, 상기 주차장 바닥용 도막 시공 방법은 폴리우레탄 프리폴리머를 도막두께 40 ~ 60 ㎛로 코팅처리하여 하도층을 형성하는 단계와; 그 위에 내충격성과 부착성이 우수한 고경도 폴리우레탄 중도층을 상온에서 도막두께 1 ~ 3 ㎜로 형성시키는 단계와; 실리콘아크릴 수지 조성물을 포함하고 내마모성과 미끄럼방지 기능을 포함하면서 차열성능 및 내후성이 우수한 도막두께 50 ~ 100 ㎛로 상도층을 형성하는 단계를 포함할 수 있다.In the practice of the present invention, the coating film construction method for the parking lot floor comprises the steps of: forming an undercoat layer by coating a polyurethane prepolymer with a film thickness of 40 to 60 μm; forming a high hardness polyurethane intermediate layer having excellent impact resistance and adhesion thereon to a coating film thickness of 1 to 3 mm at room temperature; It may include the step of forming a top coat layer with a coating film thickness of 50 to 100 μm including a silicone acrylic resin composition, including abrasion resistance and anti-slip function, and excellent heat shielding performance and weather resistance.
본 발명에 있어서, 상기 하도층(프라이머)을 형성하기 위한 폴리우레탄 프리폴리머로는 통상의 방법으로 제조된 것을 사용할 수 있으며, 일 실시에 있어서 Crude MDI(4,4'-Diphenylmethane Diisocyanate, 관능기=2.7, 분자량 340)와 PPG-400(Polypropylene Glycol, 관능기=2, 분자량 400)을 반응시켜 제조된 NCO(%)=7.0인 폴리우레탄 프리폴리머를 제조하여 사용하고, 이와 같이 제조된 폴리우레탄 프리폴리머는 통상적으로 첨가되는 소포제, 수분흡수제, 용제 등을 첨가혼합하여 교반한 후 사용시 반응촉매로 디부틸틴디라우레이트(DBTDL)을 0.1중량% 혼합하여 사용하여 프라이머로 제조된다.In the present invention, the polyurethane prepolymer for forming the undercoating layer (primer) may be prepared by a conventional method, and in one embodiment, Crude MDI (4,4'-Diphenylmethane Diisocyanate, functional group = 2.7, Molecular weight 340) and PPG-400 (Polypropylene Glycol, functional group = 2, molecular weight 400) prepared by reacting a polyurethane prepolymer with NCO (%) = 7.0 is prepared and used, and the polyurethane prepolymer prepared in this way is usually added An antifoaming agent, a water absorbent, a solvent, etc. are added and mixed and stirred, and then 0.1 wt% of dibutyltin dilaurate (DBTDL) is mixed and used as a reaction catalyst to prepare a primer.
본 발명의 일 실시예에 있어서, 상기 하도층은 톨루엔 15중량부, Crude MDI(4,4'-Diphenylmethane Diisocyanate) 40부, 반응촉매인 DBTDL(Di-n-butyltindilaurate) 0.02중량부를 4구 flask에 투입하여 가열 교반하면서 57±3 ℃까지 승온시킨 다음, 여기에 PP-400(Polypropylene Glycol, 관능기=2, 분자량 400) 25중량부를 톨루엔 25중량부에 투입하여 혼합한 용액을 2시간 동안 천천히 점액첨가한 후 1시간에 걸쳐 반응온도를 857±3 ℃로 승온시키고, 동일 온도에서 4시간 더 반응시킨 후 반응을 종료하여 폴리우레탄 프리폴리머(고형분 67%, 색상(Gardner) 18, NCO(%)=7.0)를 제조하였다. In one embodiment of the present invention, the undercoating layer is 15 parts by weight of toluene, 40 parts of crude MDI (4,4'-Diphenylmethane Diisocyanate), and 0.02 parts by weight of DBTDL (Di- n -butyltindilaurate), which is a reaction catalyst, in a 4-neck flask. After heating and stirring, the temperature was raised to 57±3 ℃, and then 25 parts by weight of PP-400 (Polypropylene Glycol, functional group = 2, molecular weight 400) was added to 25 parts by weight of toluene, and the mixed solution was slowly added for 2 hours. Then, the reaction temperature was raised to 857±3 ℃ over 1 hour, and after reacting at the same temperature for 4 more hours, the reaction was terminated to complete the polyurethane prepolymer (solid content 67%, color (Gardner) 18, NCO (%) = 7.0). ) was prepared.
상기 폴리우레탄 프리폴리머 50중량부와, 에틸아세테이트 5중량부, 수분흡수제인 Additive TI(Bayer Co.) 2.5중량부, 분산제인 안티테라-유(Anti-Terra-U : BYK-Chemi) 1.5중량부, 체질안료 Talc 35중량부를 혼합하여 30분간 교반한 후, 분산기(Attrition mill)로 입도가 NS(North Standard graduations)단위로 5이상이 되도록 분산한 다음, 후첨으로 소포제 BYK-066N(BYK-Chemie) 0.3중량부, 흐름성 조절제 BYK-410(BYK-Chemie) 0.5중량부, 혼합용제 5중량부를 첨가한 후 30분 교반하여 본 발명에 따른 프라이머 코팅제를 제조하였다. 50 parts by weight of the polyurethane prepolymer, 5 parts by weight of ethyl acetate, 2.5 parts by weight of Additive TI (Bayer Co.) as a moisture absorbent, 1.5 parts by weight of Anti-Terra-U (BYK-Chemi) as a dispersant, 35 parts by weight of the extender pigment Talc was mixed and stirred for 30 minutes, then dispersed with an attrition mill so that the particle size was 5 or more in NS (North Standard graduations) units, and then added with a post-additive antifoaming agent BYK-066N (BYK-Chemie) 0.3 After adding 0.5 parts by weight of flow control agent BYK-410 (BYK-Chemie) and 5 parts by weight of a mixed solvent, the mixture was stirred for 30 minutes to prepare a primer coating agent according to the present invention.
상기 제조된 프라이머 코팅제는 코팅시 반응촉매인 DBTDL을 총조성물에 대하여 0.1중량% 첨가혼합하여 사용하면 프라이머 코팅층을 형성할 수 있다.The prepared primer coating agent can form a primer coating layer by adding and mixing 0.1% by weight of DBTDL, which is a reaction catalyst, with respect to the total composition during coating.
이때, 상기 폴리우레탄 프리폴리머를 사용한 프라이머는 콘크리트 구조물에 코팅시 두께가 40 ∼ 60㎛가 되도록 하는 것이 바람직하다. 이것은 도막의 두께가 40 ㎛ 미만인 경우 피도물인 콘크리트 구조물과의 부착력이 저하하여 상층에 부착되는 폴리우레탄 중도와의 결합력이 부족하여 중간에 들뜨는 현상이 발생할 수 있고, 반대로 도막의 두께가 60 ㎛ 이상인 경우에는 건조시간이 길어져 작업성이 불량하게 되기 때문이다.At this time, it is preferable that the primer using the polyurethane prepolymer has a thickness of 40 to 60 μm when coated on a concrete structure. This is because when the thickness of the coating film is less than 40 μm, the adhesion to the concrete structure to be coated is lowered, and the bonding strength with the polyurethane intermediate attached to the upper layer is insufficient, causing a floating phenomenon in the middle. Conversely, when the thickness of the coating film is 60 μm or more This is because the drying time is long and the workability is poor.
상기 폴리우레탄 프리폴리머는 촉매를 사용하여 로울러나 스프레이법으로 코팅하여 상온에서 30분 내지 1시간에 경화건조를 시킨 후, 곧바로 다음공정인 폴리우레탄 중도를 도포하여 내충격성과 부착성이 우수한 고경도의 중도층을 형성하게 된다.The polyurethane prepolymer is coated with a roller or a spray method using a catalyst, cured and dried at room temperature for 30 minutes to 1 hour, and then immediately applied to the next step, polyurethane intermediate, high hardness medium with excellent impact resistance and adhesion. to form a layer.
본 발명에 있어서, 상기 중도층은 다음, 폴리우레탄 프리폴리머 상층에 코팅되는 고경도의 폴리우레탄 중도 코팅제는 경도가 Shore A 90 이상을 말하며, 1~3㎜로 코팅하는 것이 적합하다. 경도가 낮으면 상층의 압축하중을 견디지 못하기 때문이다. 또한, 고경도의 폴리우레탄 코팅제의 두께가 1㎜ 이하인 경우에는 상부에서 가해지는 차량에 의한 압축하중을 견딜 수 없어 구조적 안정성과 내마모성이 떨어지며, 반대로 폴리우레탄 코팅제의 두께가 3㎜ 이상인 경우에는 내구성과 내마모성은 양호하나, 균일한 표면을 형성하기 어렵고, 기포가 발생되어 오히려 내마모성이 저하되는 문제점과 건조시간의 지연 및 시공비가 많이 소요되는 문제점이 발생한다.In the present invention, the intermediate layer is a high hardness polyurethane intermediate coating agent coated on the upper layer of the polyurethane prepolymer, and the hardness is Shore A 90 or more, and it is suitable to be coated with a thickness of 1 to 3 mm. This is because if the hardness is low, it cannot withstand the compressive load of the upper layer. In addition, if the thickness of the polyurethane coating of high hardness is 1 mm or less, it cannot withstand the compressive load applied from the upper part, so structural stability and abrasion resistance are deteriorated. Although the abrasion resistance is good, it is difficult to form a uniform surface, and there are problems in that the abrasion resistance is lowered due to the generation of air bubbles, and the drying time is delayed and the construction cost is high.
상기 고경도의 폴리우레탄 중도 코팅제는 촉매를 사용하고 흙손이나 전용레기를 사용하여 코팅하여 상온에서 24시간 이내에 경화건조를 시킨 후, 곧바로 다음공정인 상도 코팅을 하게 된다.The high hardness polyurethane intermediate coating agent is coated using a catalyst and using a trowel or a special rag, cured and dried at room temperature within 24 hours, and then the next step, the top coat, is immediately applied.
본 발명의 일 실시에 있어서, 상기 중도 코팅제는 TDI-80(Toluene Diisocyanate) 35중량부, 반응안정제인 Benzoyl Chloride 0.03중량부를 4구 flask에 투입하여 가열 교반하면서 27±3 ℃까지 승온시킨 다음, 여기에 PP-400(Polypropylene Glycol, 관능기=2, 분자량 400) 30중량부, GP-280(Polypropylene Glycol, 관능기=3, 분자량 280) 10중량부, GP-3000(Polypropylene Glycol, 관능기=3, 분자량 3000) 25중량부의 혼합용액을 3시간 동안 균일하게 점액첨가한 후 1시간에 걸쳐 반응온도를 88±3 ℃로 승온시키고, 동일 온도에서 4시간 더 반응시킨 후 반응을 종료하여 이소시아네이트 프리폴리머(고형분 100%, 색상(Gardner) 4, NCO(%)=9.0)를 제조하였으며, 이렇게 제조된 이소시아네이트 프리폴리머를 고경도 폴리우레탄 중도 코팅제의 경화제로 하였다. In one embodiment of the present invention, the intermediate coating agent is added 35 parts by weight of TDI-80 (Toluene Diisocyanate) and 0.03 parts by weight of Benzoyl Chloride, which is a reaction stabilizer, into a four-neck flask, heated to 27±3 ℃ while heating and stirring, and then here PP-400 (Polypropylene Glycol, functional group = 2, molecular weight 400) 30 parts by weight, GP-280 (Polypropylene Glycol, functional group = 3, molecular weight 280) 10 parts by weight, GP-3000 (Polypropylene Glycol, functional group = 3, molecular weight 3000) ) 25 parts by weight of the mixed solution was uniformly added for 3 hours, then the reaction temperature was raised to 88±3 ° C over 1 hour, and after reacting at the same temperature for 4 hours, the reaction was terminated and the isocyanate prepolymer (solid content 100%) , color (Gardner) 4, NCO (%) = 9.0) was prepared, and the thus-prepared isocyanate prepolymer was used as a curing agent for a high hardness polyurethane intermediate coating agent.
이와는 별도로 관능기수가 3이고, 분자량이 4000인 폴리에테르 폴리올(GP-4000) 5중량부에 탄산칼슘 30중량부, Talc 15중량부, BaSO4 8중량부와 인계 난연제 트리스(2, 4-디클로로프로필)포스페이트로 5중량부, 항균제 BIT로 2중량부를 혼합하여 30분간 교반한 후 분산기(Attrition Mill)로 입도가 NS(North Standard Graduations)단위로 5이상이 되도록 분산한 다음, 후첨으로 소포제 BYK-066N(BYK-Chemie) 0.3중량부와 흐름성 조절제 BYK-410(BYK-Chemie) 0.5중량부를 첨가한 후 30분간 더 교반하여 폴리우레탄 중도 코팅제의 주제로 하였다.Separately, 30 parts by weight of calcium carbonate, 15 parts by weight of Talc, 8 parts by weight of BaSO 4 and tris (2,4-dichloropropyl ) After mixing 5 parts by weight of phosphate and 2 parts by weight of antibacterial BIT, stirring for 30 minutes, disperse it with an Attrition Mill so that the particle size becomes 5 or more in NS (North Standard Graduations) unit, and then use a post-addition agent to add antifoaming agent BYK-066N After adding 0.3 parts by weight of (BYK-Chemie) and 0.5 parts by weight of the flow control agent BYK-410 (BYK-Chemie), the mixture was further stirred for 30 minutes to make a polyurethane intermediate coating agent.
상기 제조된 주제와 경화제의 NCO/OH 당량비를 1/1로 혼합하여 사용시 촉매로 DBTDL을 총 조성물에 대하여 0.1중량% 혼합하여 사용하면 Shore A 90 이상인 고경도 폴리우레탄 중도층을 형성할 수 있다. When the prepared base material and the NCO/OH equivalent ratio of the curing agent are mixed at 1/1, DBTDL as a catalyst is mixed in 0.1 wt% with respect to the total composition, and a high hardness polyurethane intermediate layer having a Shore A of 90 or more can be formed.
본 발명의 주차장 바닥용 표면 코팅제 및 표면 코팅방법은, 폴리우레탄 프리폴리머를 도막두께 40 ~ 60 ㎛로 코팅처리하여 하도층을 형성하는 제1단계와; 그 위에 내충격성과 부착성이 우수한 고경도 폴리우레탄 중도층을 상온에서 도막두께 1 ~ 3 ㎜로 형성시키는 제2단계와; 실리콘아크릴레이트 수지 조성물을 사용하여 내마모성과 미끄럼방지 기능을 포함하면서 차열성능 및 내후성이 우수한 도막두께 50 ~ 100 ㎛로 상도층을 형성하는 제3단계의 시스템 코팅방법을 사용하여 KS F 4937의 주차장 바닥용 표면 마감재의 모든 시험 항목을 만족하기 때문에 콘크리트 구조물의 장기간 내구성 확보가 가능하여 환경보호에 이바지할 수 있는 유용한 발명이다. The surface coating agent and surface coating method for a parking lot floor of the present invention comprises: a first step of forming an undercoat layer by coating a polyurethane prepolymer with a film thickness of 40 to 60 μm; a second step of forming a high hardness polyurethane intermediate layer having excellent impact resistance and adhesion thereon with a coating film thickness of 1 to 3 mm at room temperature; The parking lot floor of KS F 4937 using the system coating method of the third step to form a top coat layer with a film thickness of 50 to 100 μm with excellent heat shielding performance and weather resistance while including abrasion resistance and anti-slip function using a silicone acrylate resin composition It is a useful invention that can contribute to environmental protection by ensuring long-term durability of concrete structures because it satisfies all test items for surface finishing materials for use.
이하, 실시예를 통해서 본 발명을 상세하게 설명한다. 하기 실시예는 본 발명을 예시하기 위한 것이며, 본 발명을 한정하기 위한 것은 아니다. Hereinafter, the present invention will be described in detail through examples. The following examples are intended to illustrate the present invention, not to limit the present invention.
실시예 1-3 및 비교예 1Examples 1-3 and Comparative Example 1
온도계, 콘덴서, 적하깔대기, 교반기가 장착된 4구 플라스크에 키실렌 140g, 노말부탄올 60g을 넣은 후, 질소가스로 치환시키고 교반하면서 90 ℃로 온도를 올렸다. 이 후 상기 용매의 온도를 일정하게 유지시키면서 하기한 단량체와 개시제로 아조비스이소부티로니트릴 4g의 혼합용액을 3~5시간에 걸쳐 균일한 속도로 적하하였다. 적하 완료 후 3시간 동안 더 숙성시킨 다음, 후첨 개시제로 아조비스이소부티로니트릴 0.5g을 키실렌 50g에 용해하여 30분에 걸쳐 적하하고 3시간 동안 더 교반하면서 미반응 단량체를 제거하여 반응을 종료하고 키실렌 86.8g과 노말부탄올 58.7g을 넣어 희석하여 유리전이온도 30 ℃, 고형분 50%의 실리콘 함유 아크릴수지를 얻었다.After putting 140 g of xylene and 60 g of n-butanol in a four-neck flask equipped with a thermometer, condenser, dropping funnel, and stirrer, the temperature was raised to 90 °C while substituted with nitrogen gas and stirring. After that, a mixed solution of 4 g of azobisisobutyronitrile as the following monomer and initiator was added dropwise at a uniform rate over 3 to 5 hours while maintaining the temperature of the solvent constant. After completion of the dropping, the mixture was further aged for 3 hours, and then 0.5 g of azobisisobutyronitrile was dissolved in 50 g of xylene as a post-addition initiator and dropped over 30 minutes, and the reaction was terminated by removing unreacted monomers while stirring for a further 3 hours. Then, 86.8 g of xylene and 58.7 g of n-butanol were added and diluted to obtain a silicone-containing acrylic resin having a glass transition temperature of 30° C. and a solid content of 50%.
(cPs)Viscosity
(cPs)
분자량number average
Molecular Weight
(Mw/Mn)polydispersity
(Mw/Mn)
(%)non-volatile matter
(%)
도막의 물성평가Evaluation of the physical properties of the coating film
상기 (실험예 1~3) 및 비교예 1의 (실리콘)아크릴수지를 포함하는 조성물로부터 형성된 도막의 특성을 알아보기 위해 하기표 1과 같이 (실리콘)아크릴수지를 사용한 주제와 경화제로 무황변형 폴리이소시아네이트인 Bayer사 Desmodur N-3300을 사용하여 (실리콘)아크릴/우레탄 백색도료를 제조하였는데 NCO/OH의 당량비를 1/1로 하여 제조하였다. In order to investigate the characteristics of the coating film formed from the composition containing the (silicone) acrylic resin of (Experimental Examples 1 to 3) and Comparative Example 1, as shown in Table 1 below, a non-yellowing poly(silicone) non-yellowing poly A (silicone) acrylic/urethane white paint was prepared using Bayer's Desmodur N-3300, which is an isocyanate, and the NCO/OH equivalent ratio was 1/1.
도막성능 시험 시편은 다음과 같이 제조하였다.The coating film performance test specimen was prepared as follows.
우선 콘크리트 표면의 소지 정리를 한 다음 프라이머로 폴리우레탄 프리폴리머를 사용하여 건조도막두께(DFT) 50㎛으로 분무도장하여 자연 건조시킨 후에, 고경도 폴리우레탄 코팅제를 3mm 도막두께로 도장하여 건조시켰다. 1일 동안 자연건조 시킨 후, 상기 배합에 의해 제조된 상도코팅제를 DFT 75 ㎛으로 분무도장 후 7일간 자연건조시켜 시험도막을 얻은 후 도막성능을 조사하여 표 2에 나타내었다.First, after cleaning the surface of the concrete, using a polyurethane prepolymer as a primer, spray painting to a dry film thickness (DFT) of 50 μm, drying it naturally, and then coating it with a high hardness polyurethane coating to a film thickness of 3 mm and drying it. After drying naturally for 1 day, the top coat prepared by the above formulation was spray coated with DFT 75 μm, and then naturally dried for 7 days to obtain a test film.
(두께 50㎛)Hado
(thickness 50㎛)
프리폴리머Polyurethane
prepolymer
고형분 67%, NCO=7%synthetic
67% solids, NCO=7%
(두께 3mm)midway
(Thickness 3mm)
(주제/경화제)high hardness polyurethane
(Subject/hardener)
NCO/OH=1/1Synthetic product (hardener)
NCO/OH=1/1
(두께 75㎛)normal course
(thickness 75㎛)
우레탄(주제/경화제)(Silicone) Acrylic/
Urethane (substance/hardener)
35Experimental Example 1
35
NCO/OH=1/1Synthetic product (subject)
NCO/OH=1/1
안료heat shield
pigment
스피어ceramic
spear
Microspheres
G-600USA Zeeospheres
Microspheres
G-600
질화붕소hexagonal system
boron nitride
도막 성능시험은 다음과 같이 일반적인 도막물성 평가방법에 따라 평가하였다.The coating film performance test was evaluated according to the general coating film property evaluation method as follows.
1. 윤하중 저항성능 시험은 KS F 4937의 주차장 바닥용 표면 마감재의 시험방법에 따라 300㎏의 수직하중, 주행속도는 5㎞/h에서 80,000회 평가하여 두께 감소 깊이를 측정하였다. 1. For the wheel load resistance performance test, the thickness reduction depth was measured by evaluating 80,000 times at a vertical load of 300 kg and running speed of 5 km/h according to the test method for surface finishing materials for parking lot floors of KS F 4937.
2. 미끄럼저항성 시험2. Slip resistance test
미끄럼저항성 시험은 KS F 2375의 노면의 미끄럼저항성 시험방법에 따라 미끄럼저항 시험기(BPT, british pendulum tester)를 사용하여 미끄럼 저항지수(BPN)를 평가하였다.For the slip resistance test, the slip resistance index (BPN) was evaluated using a slip resistance tester (BPT, british pendulum tester) according to the method for testing the slip resistance of the road surface of KS F 2375.
3. 차열성은 상기 철판(300mm X 300mm X 0.5mm)에 도장한 시편을 스치로폼의 재질로 지붕부분이 개방되게 제작된 모형집(250mm X 250mm X 150mm)의 지붕부분에 외부공기가 유입되지 않도록 밀봉거치시킨다. 시험편 상부 30cm 높이에 적외선 램프(오스람사, E27 screw base, 250W)를 30분간 조사하여 시간대별 지붕내부표면과 실내의 온도를 디지털 온도센서(OMEGA, Model HH21)로 측정하여 초기 및 30분 조사 후의 온도차로서 상대적 차열성능을 측정한다. 이때 이러한 차열 성능 측정기기는 밀폐된 장소에 설치한다.3. Heat shielding is to prevent outside air from flowing into the roof of the model house (250mm X 250mm X 150mm), which is made of a Styrofoam material with the specimen painted on the steel plate (300mm X 300mm X 0.5mm) open. keep it sealed. Infrared lamp (Osram, E27 screw base, 250W) was irradiated to the upper 30cm height of the test piece for 30 minutes, and the temperature of the interior surface of the roof and the room by time was measured with a digital temperature sensor (OMEGA, Model HH21). The relative thermal insulation performance is measured as a temperature difference. At this time, these thermal insulation performance measuring devices are installed in a closed place.
4. 태양방사 반사율 측정은 KSM 5987 차열도료의 태양방사 반사율 측정방법에 따라 가로와 세로가 각각 20cm X 30cm이고, 두께가 3.0mm인 유리기판에 도장한 시편을 UV Visible spectro photometer (분광측정기, Jasco V-670, 파장 250 ~ 2500nm)를 이용하여 태양방사 반사율을 측정하였다.4. Measurement of solar radiation reflectance is according to the method of measuring solar radiation reflectance of KSM 5987 thermal barrier coating, and the specimens coated on a glass substrate with a width and length of 20 cm X 30 cm and a thickness of 3.0 mm are measured using a UV Visible spectro photometer (spectrometer, Jasco). Solar radiation reflectance was measured using V-670, wavelength 250 ~ 2500nm).
5. 촉진내후성 시험5. Accelerated weathering test
촉진내후성 시험은 KS M 5000-3231의 도료의 촉진내후성 시험방법에 따라 sunshine weather-Ometer(Atlas Electric Devices Co., Ci65A형)를 사용하여 1,000, 2,000, 및 3,000 시간대별로 광택보존값 및 색상차를 평가하였다. The accelerated weather resistance test was conducted using a sunshine weather-Ometer (Atlas Electric Devices Co., Ci65A type) according to the accelerated weather resistance test method for paints of KS M 5000-3231 to measure the gloss preservation value and color difference for each time period of 1,000, 2,000, and 3,000. evaluated.
(1) 광택보존값 측정(1) Measurement of gloss retention value
광택보존값은 Glossmeter(Pacific Scientific Co., Glossgard Ⅱ형)를 사용하여 아래의 식에 의하여 계산하였다.The gloss retention value was calculated by the following formula using a Glossmeter (Pacific Scientific Co., Glossgard Ⅱ type).
(2) 색상차 측정(2) Color difference measurement
색상차(color difference)는 2색의 차이를 시각적 개념에서 수치적 개념으로 표현한 것이다. 즉 색공간 좌표에서 두색의 기하학적인 거리를 수치로 표시하게 된다. 확산반사율 측정장치인 Spectro Color Meter(Nippon Denshoku Kogyo Co., SZ-∑80형)를 사용하여 측정하며 색상차는 아래의 식에 의해 계산되었다.The color difference is the expression of the difference between two colors from a visual concept to a numerical concept. That is, the geometric distance of two colors in color space coordinates is expressed numerically. It was measured using a diffuse reflectance measuring device, Spectro Color Meter (Nippon Denshoku Kogyo Co., SZ-∑80 type), and the color difference was calculated by the following equation.
색상차(ΔE) = [ (ΔL)2 + (Δa)2 + (Δb)2 ]1/ Color difference (ΔE) = [ (ΔL) 2 + (Δa) 2 + (Δb) 2 ] 1/
여기에서, L = Hunter 색표시계의 명도지수From here, L = Brightness index of Hunter color indicator
a , b = Hunter 색표시계의 크로마틱네스 계수 a , b = Chromaticness coefficient of Hunter colorimeter
(℃)roof interior surface temperature
(℃)
(℃)room temperature
(℃)
(hrs)1000
(hrs)
(hrs)2000
(hrs)
(hrs)3000
(hrs)
상기 표 3에 나타난 바와 같이, 본 발명의 실시예 1 내지 3의 조성물을 이용했을 때보다 비교예의 조성물을 이용했을 때, 윤하중 저항성능과 미끄럼 저항성이 불량하였으며, 6티탄산칼륨 함량이 높은 실시예 3이 가장 양호한 결과를 나타내었다.As shown in Table 3, when the compositions of Comparative Examples were used rather than when the compositions of Examples 1 to 3 of the present invention were used, the wheel load resistance performance and slip resistance were poor, and Example 3 with a high potassium hexatitanate content This gave the best results.
차열성과 태양방사 반사율의 결과도 비교예의 조성물을 이용했을 때는 30분 동안 지붕표면온도차 및 실내온도차가 더 크고 태양방사 반사율이 낮다는 것을 알 수 있다. 상기 결과를 토대로, 실시예 조성물의 차열안료와 방열을 위한 금속성 무기안료를 병용했을 때 차열성능이 우수하다는 것을 알 수 있다. 또한 태양방사 반사율에서도 실시예 1 내지 3의 조성물에 형성된 도막은 태양방사 반사율이 60% 이상으로 태양광 반사에 우수한 효과를 갖는 것을 확인하였다.It can be seen that the results of heat shielding properties and solar radiation reflectance also show that the difference in roof surface temperature and indoor temperature for 30 minutes is larger and the solar radiation reflectance is low when the composition of Comparative Example is used. Based on the above results, it can be seen that the heat shielding performance is excellent when the heat shielding pigment of the composition of Example and the metallic inorganic pigment for heat dissipation are used together. In addition, it was confirmed that the coating film formed on the compositions of Examples 1 to 3 also had a solar radiation reflectance of 60% or more, and had an excellent effect on sunlight reflection.
내후성은 실리콘 모노머를 도입한(실험예1~3) 실시예 1 내지 3의 조성물은 비교예와 비교해 보면, 광택보존값과 색상차에서 우수한 내후성을 보였으나, 실리콘 모노머를 사용하지 않은 비교예의 경우에는 광택보존값이 불량하고 눈에 띨만큼의 색상차를 보였다. 실시예 1 내지 3에서도 실리콘 모노머 함량이 높은 실시예 1과 실시예 3이 더 우수한 내후성을 지님을 확인하였다.As for the weather resistance, the compositions of Examples 1 to 3 in which a silicone monomer was introduced (Experimental Examples 1 to 3) showed excellent weather resistance in gloss preservation value and color difference compared with Comparative Examples, but in Comparative Examples without using a silicone monomer showed poor gloss preservation value and a noticeable color difference. Also in Examples 1 to 3, it was confirmed that Examples 1 and 3 having a high silicone monomer content had better weather resistance.
본 발명이 속한 분야에서 통상의 지식을 가진 자라면 상기 내용을 바탕으로 하여 본 발명의 범주 내에서 다양한 응용 및 변형이 가능할 것이다. 따라서 본 발명의 기술적 범위는 명세서의 상세한 설명에 기재된 내용으로 한정되는 것이 아니라 특허 청구의 범위에 의해 정하여 져야 할 것이다.Those of ordinary skill in the art to which the present invention pertains will be able to make various applications and modifications within the scope of the present invention based on the above content. Therefore, the technical scope of the present invention should be defined by the claims, not limited to the content described in the detailed description of the specification.
Claims (23)
수산기를 포함하는 실리콘아크릴 수지와 무황변 폴리이소시아네이트는 우레탄 반응을 통해서 도막용 수지를 형성하는 것을 특징으로 하는 주차장 바닥용 상도용 코팅제.According to claim 1,
A silicone acrylic resin containing a hydroxyl group and non-yellowing polyisocyanate form a resin for a coating film through a urethane reaction.
상기 수산기를 포함하는 실리콘아크릴 수지는 실리콘 함유 단량체 10~30 중량%와 지방족기를 갖는 아크릴계 혹은 메타크릴계 단량체 60 내지 85 중량%와, 수산기를 갖는 메타크릴계 단량체 5 내지 10 중량%로 이루어진 것을 특징으로 하는 주차장 바닥용 상도용 코팅제.According to claim 1,
The silicone acrylic resin containing a hydroxyl group is characterized in that it consists of 10 to 30% by weight of a silicone-containing monomer, 60 to 85% by weight of an acrylic or methacrylic monomer having an aliphatic group, and 5 to 10% by weight of a methacrylic monomer having a hydroxyl group. A coating agent for the top coat of the parking lot floor.
상기 실리콘 함유 단량체는 하기 화학식(1)로부터 하나 이상 선택되는 것을 특징으로 하는 주차장 바닥용 상도용 코팅제.
(1)4. The method of claim 3,
The silicone-containing monomer is a coating agent for a topcoat for a parking lot, characterized in that at least one selected from the following formula (1).
(One)
지방족기를 갖는 아크릴계 혹은 메타크릴계 단량체는 노말부틸아크릴레이트, 2-에틸헥실아크릴레이트, 에틸아크릴레이트, 노말부틸메타크릴레이트, 노말프로필메타크릴레이트, 메틸메타크릴레이트, 에틸메타크릴레이트, 2-에틸헥실메타크릴레이트, 옥틸메타크릴레이트, 글리시딜메타크릴레이트, 라우릴메타크릴레이트, 이소보닐메타크릴레이트로 이루어진 그룹에서 하나 이상 선택된 것을 특징으로 하는 주차장 바닥용 상도용 코팅제. 4. The method of claim 3,
Acrylic or methacrylic monomers having an aliphatic group include normal butyl acrylate, 2-ethylhexyl acrylate, ethyl acrylate, normal butyl methacrylate, normal propyl methacrylate, methyl methacrylate, ethyl methacrylate, 2- Ethylhexyl methacrylate, octyl methacrylate, glycidyl methacrylate, lauryl methacrylate, isobornyl methacrylate, characterized in that at least one selected from the group consisting of a top coating for a parking lot floor.
상기 수산기를 갖는 메타크릴계 단량체는 2-히드록시에틸메타크릴레이트, 2-히드록시프로필메타크릴레이트, 4-히드록시부틸메타크릴레이트에서 하나 이상 선택되는 것을 특징으로 하는 주차장 바닥용 상도용 코팅제. 4. The method of claim 3,
The methacrylic monomer having a hydroxyl group is a coating agent for a topcoat for a parking lot floor, characterized in that at least one selected from 2-hydroxyethyl methacrylate, 2-hydroxypropyl methacrylate, and 4-hydroxybutyl methacrylate .
상기 수산기를 포함하는 실리콘아크릴 수지는 0~50 ℃의 유리전이온도를 가지는 것을 특징으로 하는 주차장 바닥용 상도용 코팅제.3. The method of claim 1 or 2,
The silicone acrylic resin containing the hydroxyl group has a glass transition temperature of 0 to 50 ℃, a coating agent for a top coat for a parking lot floor.
상기 무황변 폴리이소시아네이트는 NCO %가 20 이상인 지방족 폴리이소시아네이트인 것을 특징으로 하는 주차장 바닥용 상도용 코팅제.3. The method of claim 1 or 2,
The non-yellowing polyisocyanate is an aliphatic polyisocyanate having an NCO% of 20 or more.
수산기를 포함하는 실리콘아크릴 수지와 무황변 폴리이소시아네이트는 NCO/OH의 당량비가 1:1로 이루어진 것을 특징으로 하는 주차장 바닥용 상도용 코팅제.3. The method of claim 1 or 2,
A silicone acrylic resin containing a hydroxyl group and non-yellowing polyisocyanate have an NCO/OH equivalent ratio of 1:1.
수산기를 포함하는 실리콘아크릴 수지와 무황변 폴리이소시아네이트는 상도용 코팅제 100 중량부에서 20~50 중량부로 포함된 것을 특징으로 하는 주차장 바닥용 상도용 코팅제. 3. The method of claim 1 or 2,
The silicone acrylic resin containing a hydroxyl group and non-yellowing polyisocyanate are included in an amount of 20-50 parts by weight from 100 parts by weight of the topcoating agent.
상기 상도용 코팅제는 티탄산칼륨을 포함하는 것을 특징으로 하는 주차장 바닥용 상도용 코팅제.3. The method of claim 1 or 2,
The top coating agent for a top coating for a parking lot floor, characterized in that it comprises potassium titanate.
상기 티탄산칼륨은 상기 상도용 코팅제 100 중량부에서 9 내지 30 중량부인 것을 특징으로 하는 주차장 바닥용 상도용 코팅제.12. The method of claim 11,
The potassium titanate is a topcoat coating agent for a parking lot floor, characterized in that 9 to 30 parts by weight in 100 parts by weight of the topcoat coating agent.
상기 상도용 코팅제는 차열안료를 포함하는 것을 특징으로 하는 주차장 바닥용 상도용 코팅제. 3. The method of claim 1 or 2,
The top coating agent for a parking lot floor top coating, characterized in that it comprises a heat-shielding pigment.
상기 차열안료는 상기 상도용 코팅제 100 중량부에서 5 내지 15 중량부인 것을 특징으로 하는 주차장 바닥용 상도용 코팅제.14. The method of claim 13,
The heat-shielding pigment is a coating agent for a parking lot floor, characterized in that 5 to 15 parts by weight from 100 parts by weight of the top coating agent.
상기 상도용 코팅제는 산화티탄, 산화아연, 산화인듐, 산화주석, 안티몬 주석 산화물(Antimony Tin Oxide), 인듐 주석 산화물(Indium Tin Oxide), 몰리브덴옥사이드(MoO3), 산화탄탈(Ta2O5), 오산화바나듐(V2O5), 산화니오브(Nb2O5), 보론 니트로나이트(BN), 육방정계 질화붕소(h-BN), 알루미늄 옥사이드(AL2O3)로 이루어진 군에서 하나 이상 선택되는 방열안료를 더 포함하는 것을 특징으로 하는 주차장 바닥용 상도용 코팅제. 14. The method of claim 1 or 13,
The top coating agent is titanium oxide, zinc oxide, indium oxide, tin oxide, antimony tin oxide (Antimony Tin Oxide), indium tin oxide (Indium Tin Oxide), molybdenum oxide (MoO3), tantalum oxide (Ta2O5), vanadium pentoxide ( V2O5), niobium oxide (Nb2O5), boron nitronite (BN), hexagonal boron nitride (h-BN), aluminum oxide (AL2O3) Parking lot characterized in that it further comprises a heat dissipation pigment selected from the group consisting of Coatings for top coats for floors.
상기 방열안료는 상기 상도용 코팅제 100 중량부에서 1 내지 15 중량부인 것을 특징으로 하는 주차장 바닥용 상도용 코팅제. 16. The method of claim 15,
The heat dissipation pigment is a coating agent for a parking lot floor, characterized in that 1 to 15 parts by weight in 100 parts by weight of the top coating agent.
상기 상도용 코팅제는 톨루엔, 키실렌 등의 방향족계 탄화수소, 노말부틸아세테이트, 에틸렌글리콜에틸에테르아세테이트, 메틸이소부틸케톤, 메틸노말아밀케톤, 이소프로판올, 노말부탄올, 이소부탄올, 에틸렌글리콜모노메틸에테르, 프로필렌글리콜모노메틸에테르에서 선택하는 하나 이상의 용매를 포함하는 것을 특징으로 하는 주차장 바닥용 상도용 코팅제. 3. The method of claim 1 or 2,
The top coating agent includes aromatic hydrocarbons such as toluene and xylene, normal butyl acetate, ethylene glycol ethyl ether acetate, methyl isobutyl ketone, methyl normal amyl ketone, isopropanol, normal butanol, isobutanol, ethylene glycol monomethyl ether, and propylene. A coating agent for a top coat for a parking lot floor, characterized in that it contains one or more solvents selected from glycol monomethyl ether.
상기 용매는 상도용 코팅제 100 중량부에서 10 내지 40 중량부인 것을 특징으로 하는 주차장 바닥용 상도용 코팅제.18. The method of claim 17,
The solvent is a topcoat for a parking lot floor, characterized in that 10 to 40 parts by weight in 100 parts by weight of the topcoating coating agent.
상기 상도용 코팅제는 레벨링제 및 소포제를 포함하는 첨가제를 포함하는 것을 특징으로 하는 주차장 바닥용 상도용 코팅제.3. The method of claim 1 or 2,
The top coating agent for a top coating for a parking lot floor, characterized in that it comprises an additive including a leveling agent and an antifoaming agent.
상기 상도용 코팅제는 수산기를 포함하는 실리콘아크릴 수지와 무황변 폴리이소시아네이트와, 티탄산칼륨과, 차열안료와, 방열안료와, 용매 및 첨가제를 포함하는 것을 특징으로 하는 주차장 바닥용 상도용 코팅제.3. The method of claim 1 or 2,
The top coating agent for a parking lot floor, characterized in that it comprises a silicone acrylic resin containing a hydroxyl group, non-yellowing polyisocyanate, potassium titanate, a heat-shielding pigment, a heat-dissipating pigment, a solvent and an additive.
상기 상도용 코팅제 100 중량부는 수산기를 포함하는 실리콘아크릴 수지와 무황변 폴리이소시아네이트 20~50 중량부, 티탄산칼륨 9~30 중량부, 차열안료 5~15 중량부, 방열안료 1~15, 용매 10~40 중량부 및 첨가제 1~5 중량부로 이루어진 것을 특징으로 하는 주차장 바닥용 상도용 코팅제.21. The method of claim 20,
100 parts by weight of the topcoating agent is a silicone acrylic resin containing a hydroxyl group and 20-50 parts by weight of non-yellowing polyisocyanate, 9-30 parts by weight of potassium titanate, 5-15 parts by weight of a heat-shielding pigment, 1-15 parts by weight of a heat dissipation pigment, 10 parts by weight of a solvent A coating agent for a top coat for a parking lot, characterized in that it consists of 40 parts by weight and 1 to 5 parts by weight of additives.
상기 하도층의 표면에 형성되는 중도층; 및
상기 중도층의 표면에 형성되는 상도층으로 이루어지고,
상기 상도층은 실리콘 아크릴계 우레탄 수지를 포함하는 것을 특징으로 하는 주차장 바닥용 도막.a primer undercoat layer formed on the surface of the base layer;
an intermediate layer formed on the surface of the undercoat layer; and
Consists of a top coat layer formed on the surface of the intermediate layer,
The top coat layer is a coating film for a parking lot floor, characterized in that it comprises a silicone acrylic urethane resin.
상기 상도층은 50~100㎛의 두께를 가지며, 티탄산칼륨과, 차열안료와, 및 방열안료를 포함하는 것을 특징으로 하는 주차장 바닥용 도막.23. The method of claim 22,
The top coat layer has a thickness of 50 to 100㎛, a coating film for a parking lot floor, characterized in that it comprises potassium titanate, a heat-shielding pigment, and a heat-dissipating pigment.