KR20210081741A - 포지티브형 감광성 수지 조성물 및 이로부터 제조된 경화막 - Google Patents
포지티브형 감광성 수지 조성물 및 이로부터 제조된 경화막 Download PDFInfo
- Publication number
- KR20210081741A KR20210081741A KR1020190173995A KR20190173995A KR20210081741A KR 20210081741 A KR20210081741 A KR 20210081741A KR 1020190173995 A KR1020190173995 A KR 1020190173995A KR 20190173995 A KR20190173995 A KR 20190173995A KR 20210081741 A KR20210081741 A KR 20210081741A
- Authority
- KR
- South Korea
- Prior art keywords
- resin composition
- photosensitive resin
- group
- compound
- weight
- Prior art date
Abstract
본 발명에 따른 포지티브형 감광성 수지 조성물은 바인더 내 수분 함량을 조절하여, 제조 직후 뿐만 아니라 일정기간 보관 후에 사용하여도 우수한 감도, 해상도 및 잔막율을 갖는 경화막을 제조할 수 있다.
Description
본 발명은 우수한 잔막율 및 해상도를 갖고, 장기간 보관후에 사용하여도 우수한 감도를 유지하는 경화막을 형성할 수 있는 포지티브형 감광성 수지 조성물 및 이로부터 제조되는 경화막에 관한 것이다.
일반적으로 액정표시장치나 유기발광표시장치 등에 있어서, 공정수가 적은 포지티브형 감광성 수지 조성물이 널리 이용되고 있다.
그러나, 종래의 포지티브형 감광성 수지 조성물을 이용한 평탄화막이나 표시소자는 네거티브형 감광성 조성물을 사용한 평탄화막이나 표시소자보다 느린 감도를 가지므로 감도 향상에 대한 개선이 필요한 실정이다.
한편, 종래 알려진 포지티브형 감광성 수지 조성물은 일반적으로 바인더 수지로서 실록산 폴리머, 아크릴 폴리머 등의 알칼리 가용성 수지와, 별도의 감광제, 예를 들면, 퀴논디아지드계 화합물, 방향족 알데히드 등의 감광제를 포함한다(일본 공개번호 제1996―234421호). 그러나, 이러한 포지티브 감광성 수지 조성물을 이용하여 경화막을 제조하는 경우, 현상 공정 중 현상액에 의한 경화막의 두께 손실율이 크고 감도, 잔막율, 해상도 등을 충분히 만족시키기에는 한계가 있다.
따라서, 본 발명은 우수한 감도, 잔막율 및 해상도를 가질 뿐만 아니라, 장기간 보관 후에 경화막을 형성하여도 우수한 감도를 유지할 수 있는 포지티브형 감광성 수지 조성물 및 이로부터 제조되며 유기발광표시장치의 화소정의막 또는 층간절연막으로 적용가능한 경화막을 제공하고자 한다.
상기 목적을 달성하기 위해 본 발명은, (A) 실록산 공중합체; (B) 광활성 화합물; 및 (C) 용매;를 포함하고, 상기 실록산 공중합체(A)의 Volumetric KF 수분결정법(칼-피셔 수분결정법)에 의한 수분 함유율이 1.5% 이하인, 포지티브형 감광성 수지 조성물을 제공한다.
상기 다른 목적을 달성하기 위해 본 발명은, 상기 감광성 수지 조성물로부터 형성된, 경화막을 제공한다.
본 발명에 따른 포지티브형 감광성 수지 조성물은 바인더 내 수분 함량을 조절하여, 제조 직후 뿐만 아니라 일정기간 보관 후에 사용하여도 우수한 감도, 해상도 및 잔막율을 갖는 경화막을 제조할 수 있다.
본 발명은 이하에 개시된 내용에 한정되는 것이 아니라, 발명의 요지가 변경되지 않는 한 다양한 형태로 변형될 수 있다.
본 명세서에서 "포함"한다는 것은 특별한 기재가 없는 한 다른 구성요소를 더 포함할 수 있음을 의미한다. 또한, 본 명세서에 기재된 구성성분의 양, 반응 조건 등을 나타내는 모든 숫자 및 표현은 특별한 기재가 없는 한 모든 경우에 "약"이라는 용어로써 수식되는 것으로 이해하여야 한다.
본 발명은 (A) 실록산 공중합체, (B) 광활성 화합물 및 (C) 용매를 포함하는 감광성 수지 조성물을 제공한다. 이때, 상기 실록산 공중합체(A)의 Volumetric KF 수분결정법(칼-피셔 수분결정법)에 의한 수분 함유율이 1.5% 이하일 수 있고, 이와 관련한 설명은 이하 자세히 하도록 한다. 상기 조성물은 (D) 에폭시 화합물, (E) 계면활성제, (F) 실란 화합물 및 (G) 접착보조제로 이루어진 군에서 선택된 1종 이상을 추가로 포함할 수 있다.
본 명세서에서, "(메트)아크릴"은 "아크릴" 및/또는 "메타크릴"을 의미하고, "(메트)아크릴레이트"는 "아크릴레이트" 및/또는 "메타크릴레이트"를 의미한다
하기 각 구성들에 대한 중량평균분자량은 겔 투과 크로마토그래피(gel permeation chromatography; GPC, 테트라히드로퓨란을 용출용매로 함)로 측정한 폴리스티렌 환산의 중량평균분자량(g/mol 또는 Da)을 말한다.
(A) 실록산 공중합체
상기 실록산 공중합체(실록산 폴리머, A)를 포함하는 감광성 수지 조성물은 노광에서 현상으로 이어지는 공정에 의한 포지티브형 패턴 형성이 가능하다.
상기 실록산 공중합체는 현상 단계에서 현상성을 구현하는 알칼리 가용성 수지이면서, 또한 코팅 후 도막을 형성하는 기저 역할 및 최종 패턴을 구현하는 구조물 및 바인더 역할을 할 수 있다.
상기 실록산 공중합체는 수분 함유율이 2% 이하, 1.5% 이하, 1.3% 이하, 0.1 내지 2%, 0.1 내지 1.5%, 0.2 내지 1.5% 또는 0.2 내지 1.3%일 수 있다.
상기 함량 범위 내일 때, 조성물 제조 직후 뿐만 아니라 일정 기간 보관 후에 경화막을 제조하여도 우수한 해상도, 잔막율 및 감도를 갖는 경화막을 제조할 수 있다.
상기 수분 함유율은 Volumetric KF 수분결정법(칼-피셔 수분결정법)에 의해 결정된다. 상기 Volumetric KF 수분 결정법은 메탄올 등의 저급 알코올 및 피리딘(C5H5N) 등의 유기 염기의 존재 하에서 물이 요오드 및 이산화황과 정량적으로 반응하는 것을 이용하여 수분을 측정하는 방법이다(하기 반응식 참조). 1935년에 칼-피셔 박사에 의해 개발되어, DIN, ISO, ASTM 등에서 수분 정량 표준 방법으로 규정되어 있다.
[반응식]
CH3OH + SO2 + 3C5H5N + I2 + H2O → (C5H5NH)SO4CH3 + 2[C5H5NH]I
상기 Volumetric KF 수분결정법은 710 KF-Titrino 등의 수분 측정기기를 이용하여 실록산 공중합체의 수분 함유율을 결정할 수 있다. 구체적으로, 상기 기기에 H2O를 주입하여 STD 적정(표준 적정)을 한 다음, 실록산 공중합체(샘플)를 주입하여 샘플 내 수분량을 결정(측정)할 수 있다.
상기 실록산 공중합체는 실란 화합물 및/또는 이의 가수분해물의 축합물을 포함할 수 있다. 이때 상기 실란 화합물 또는 이의 가수분해물은 1 내지 4 관능성의 실란 화합물일 수 있다. 그 결과, 상기 실록산 폴리머는 아래의 Q, T, D 및 M 타입 중에서 선택되는 실록산 구성단위들을 포함할 수 있다:
- Q 타입의 실록산 구성단위: 실리콘 원자 및 이에 인접하는 4개의 산소 원자를 포함하는 실록산 구성단위를 의미하며, 예를 들어, 4 관능성의 실란 화합물 또는 4개의 가수분해성기를 갖는 실란 화합물의 가수분해물로부터 유도될 수 있다.
- T 타입의 실록산 구성단위: 실리콘 원자 및 이에 인접하는 3개의 산소 원자를 포함하는 실록산 구성단위를 의미하며, 예를 들어, 3 관능성의 실란 화합물 또는 3개의 가수분해성기를 갖는 실란 화합물의 가수분해물로부터 유도될 수 있다.
- D 타입의 실록산 구성단위: 실리콘 원자 및 이에 인접하는 2개의 산소 원자를 포함하는 실록산 구성단위(즉, 직쇄상 실록산 구성단위)를 의미하며, 예를 들어, 2 관능성의 실란 화합물 또는 2개의 가수분해성기를 갖는 실란 화합물의 가수분해물로부터 유도될 수 있다.
- M 타입의 실록산 구성단위: 실리콘 원자 및 이에 인접하는 1개의 산소 원자를 포함하는 실록산 구성단위를 의미하며, 예를 들어, 1 관능성의 실란 화합물 또는 1개의 가수분해성기를 갖는 실란 화합물의 가수분해물로부터 유도될 수 있다.
구체적으로, 상기 실록산 공중합체는 하기 화학식 1로 표시되는 실란 화합물로부터 유도되는 구성단위를 포함할 수 있다.
[화학식 1]
(R1)mSi(OR2)4-m
상기 화학식 1에서, m은 0 내지 3의 정수이고; R1은 각각 독립적으로 C1-12 알킬기, C2-10 알케닐기, C6-15 아릴기, 3-12원의 헤테로알킬기, 4-10원의 헤테로알케닐기, 또는 6-15원의 헤테로아릴기이고; R2는 각각 독립적으로 수소, C1-6 알킬기, C2-6 아실기, 또는 C6-15 아릴기이며; 상기 헤테로알킬기, 헤테로알케닐기 및 헤테로아릴기는 각각 독립적으로 O, N 및 S로 이루어진 군으로부터 선택된 하나 이상의 헤테로원자를 갖는다.
m = 0인 경우에는 4 관능성 실란 화합물, m = 1인 경우에는 3 관능성 실란 화합물, m = 2인 경우에는 2 관능성 실란 화합물, m = 3인 경우에는 1 관능성 실란 화합물일 수 있다.
이러한 실란 화합물의 구체예로는, 4 관능성 실란 화합물로서 테트라아세톡시실란, 테트라메톡시실란, 테트라에톡시실란, 테트라부톡시실란, 테트라페녹시실란, 테트라벤질옥시실란 및 테트라프로폭시실란; 3 관능성 실란 화합물로서 메틸트리메톡시실란, 메틸트리에톡시실란, 메틸트리이소프로폭시실란, 메틸트리부톡시실란, 에틸트리메톡시실란, 에틸트리에톡시실란, 에틸트리이소프로폭시실란, 에틸트리부톡시실란, 부틸트리메톡시실란, 펜타플로오로페닐트리메톡시실란, 페닐트리메톡시실란, 페닐트리에톡시실란, d3-메틸트리메톡시실란, 노나플루오로부틸에틸트리메톡시실란, 트리플루오로메틸트리메톡시실란, n-프로필트리메톡시실란, n-프로필트리에톡시실란, n-부틸트리에톡시실란, n-헥실트리메톡시실란, n-헥실트리에톡시실란, 데실트리메톡시실란, 비닐트리메톡시실란, 비닐트리에톡시실란, 3-메타크릴옥시프로필트리메톡시실란, 3-메타크릴옥시프로필트리에톡시실란, 3-아크릴옥시프로필트리메톡시실란, 3-아크릴옥시프로필트리에톡시실란, p-히드록시페닐트리메톡시실란, 1-(p-히드록시페닐)에틸트리메톡시실란, 2-(p-히드록시페닐)에틸트리메톡시실란, 4-히드록시-5-(p-히드록시페닐카르보닐옥시)펜틸트리메톡시실란, 트리플루오로메틸트리에톡시실란, 3,3,3-트리플루오로프로필트리메톡시실란, 3-아미노프로필트리메톡시실란, 3-아미노프로필트리에톡시실란, 3-글리시독시프로필트리메톡시실란, 3-글리시독시프로필트리에톡시실란, 2-(3,4-에폭시시클로헥실)에틸트리메톡시실란, 2-(3,4-에폭시시클로헥실)에틸트리에톡시실란, [(3-에틸-3-옥세타닐)메톡시]프로필트리메톡시실란, [(3-에틸-3-옥세타닐)메톡시]프로필트리에톡시실란, 3-메르캅토프로필트리메톡시실란 및 3-트리메톡시실릴프로필숙신산; 2 관능성 실란 화합물로서 디메틸디아세톡시실란, 디메틸디메톡시실란, 디페닐디메톡시실란, 디페닐디에톡시실란, 디페닐디페녹시실란, 디부틸디메톡시실란, 디메틸디에톡시실란, (3-글리시독시프로필)메틸디메톡시실란, (3-글리시독시프로필)메틸디에톡시실란, 3-(2-아미노에틸아미노)프로필디메톡시메틸실란, 3-아미노프로필디에톡시메틸실란, 3-클로로프로필디메톡시메틸실란, 3-메르캅토프로필디메톡시메틸실란, 시클로헥실디메톡시메틸실란, 디에톡시메틸비닐실란, 디메톡시메틸비닐실란 및 디메톡시디-p-톨릴실란; 및 1 관능성 실란 화합물로서 트리메틸메톡시실란, 트리부틸메톡시실란, 트리메틸에톡시실란, 트리부틸에톡시실란, (3-글리시독시프로필)디메틸메톡시실란 및 (3-글리시독시프로필)디메틸에톡시실란 등을 들 수 있다.
이들 중에서, 4 관능성 실란 화합물로서 테트라메톡시실란, 테트라에톡시실란 또는 테트라부톡시실란이 바람직하고; 3 관능성 실란 화합물로서 메틸트리메톡시실란, 메틸트리에톡시실란, 메틸트리이소프로폭시실란, 메틸트리부톡시실란, 페닐트리메톡시실란, 에틸트리메톡시실란, 에틸트리에톡시실란, 에틸트리이소프로폭시실란, 에틸트리부톡시실란, 부틸트리메톡시실란, 3-글리시독시프로필트리메톡시실란, 3-글리시독시프로필트리에톡시실란, 2-(3,4-에폭시시클로헥실)에틸트리메톡시실란 또는 2-(3,4-에폭시시클로헥실)에틸트리에톡시실란이 바람직하고; 2 관능성 실란 화합물로서 디메틸디메톡시실란, 디페닐디메톡시실란, 디페닐디에톡시실란, 디페닐디페녹시실란, 디부틸디메톡시실란 또는 디메틸디에톡시실란이 바람직하다.
상기 화학식 1의 실란 화합물의 가수분해물 또는 이의 축합물을 얻는 조건은 특별히 제한되지 않는다.
상기 화학식 1의 실란 화합물의 가수분해 중합에 의해 수득되는 축합물(실록산 공중합체)의 중량평균분자량은 500 내지 50,000 Da, 1,000 내지 50,000 Da, 2,000 내지 30,000 Da, 2,000 내지 20,000 Da, 2,000 내지 15,000 Da 또는 2,000 내지 10,000 Da일 수 있다. 상기 실록산 공중합체의 중량평균분자량이 상기 범위 내일 때, 막 형성 특성, 용해성 및 현상액에 대한 용해 속도 등에서 보다 유리하다.
상기 실록산 공중합체는 상기 화학식 1에서 m이 0인 실란 화합물로부터 유도되는 구성단위(즉, Q 타입의 구성단위)를 포함할 수 있다. 구체적으로, 상기 실록산 공중합체는 상기 화학식 1에서 m이 0인 실란 화합물로부터 유도된 구성단위를, Si 원자 몰수 기준으로, 10 내지 50 몰% 또는 15 내지 40 몰%로 포함할 수 있다. Q 타입의 구성단위의 함량이 상기 함량 범위 내일 때, 감광성 수지 조성물의 패턴 형성 시 알칼리 수용액에 대한 용해성이 적정 수준을 유지하여 용해성 저하로 인한 불량 발생 또는 용해성의 지나친 상승을 방지할 수 있다.
상기 실록산 공중합체는 상기 화학식 1에서 m이 1인 실란 화합물로부터 유도된 구성단위(즉, T 타입의 구성단위)를 포함할 수 있다. 예를 들어, 상기 실록산 폴리머는 상기 화학식 1에서 m이 1인 실란 화합물로부터 유도된 구성단위를, Si 원자 몰수 기준으로, 40 내지 99 몰% 또는 50 내지 95 몰%로 포함할 수 있다. T 타입의 구성단위의 함량이 상기 함량 범위 내일 때, 정확한 패턴 형성이 보다 유리할 수 있다.
또한, 상기 실록산 공중합체는 아릴기를 갖는 실란 화합물로부터 유도되는 구성단위를 포함하는 것이, 경화막의 경도, 감도, 해상도 및 잔막율의 관점에서 보다 바람직하다. 예를 들어, 상기 실록산 공중합체는 아릴기를 갖는 실란 화합물로부터 유도되는 구성단위를, Si 원자 몰수 기준으로, 20 내지 80 몰%, 30 내지 70 몰%, 또는 30 내지 50 몰%로 포함할 수 있다. 아릴기를 갖는 실란 화합물로부터 유도되는 구성단위의 함량이 상기 함량 범위 내일 때, 실록산 공중합체와 광활성 화합물(B)과의 상용성이 우수하여 경화막의 투명성 면에서 보다 유리하고, 감도가 너무 느려지는 것도 방지할 수 있다.
상기 아릴기를 갖는 실란 화합물로부터 유도되는 구성단위는, 예를 들어, 상기 화학식 1에서 R2가 아릴기인 실란 화합물, 구체적으로, 상기 화학식 1에서 m이 1이고 R2가 아릴기인 실란 화합물, 보다 구체적으로, 상기 화학식 1에서 m이 1이고 R2가 페닐기인 실란 화합물로부터 유도되는 구성단위(즉 T-페닐 타입의 실록산 구성단위)일 수 있다.
여기서 "Si 원자 몰수 기준의 몰%"라 함은, 실록산 공중합체를 이루는 전체 구성단위에 포함된 Si 원자의 총 몰수에 대한, 특정 구성단위에 포함된 Si 원자의 몰수의 백분율을 의미한다.
상기 실록산 공중합체 내의 실록산 단위의 몰 함량은, Si-NMR, 1H-NMR, 13C-NMR, IR, TOF-MS, 원소분석법, 회분 측정 등을 조합하여 측정할 수 있다. 예를 들어, 페닐기를 갖는 실록산 단위의 몰 함량을 측정하고자 할 경우, 전체 실록산 공중합체에 대해 Si-NMR 분석을 실시한 뒤, 페닐기가 결합한 Si의 피크 면적과 페닐기가 결합하지 않은 Si의 피크 면적을 분석한 뒤 이들간의 비율로부터 산출할 수 있다.
본 발명의 감광성 수지 조성물은 이의 총 중량에 대하여, 상기 실록산 공중합체를 3 내지 30 중량%, 5 내지 30 중량%, 10 내지 25 중량% 또는 10 내지 20 중량%의 양으로 포함할 수 있다. 실록산 공중합체의 함량이 상기 함량 범위 내일 때, 현상성이 적절히 조절되어 잔막 형성과 패턴의 해상도가 우수한 장점이 있다.
(B) 광활성 화합물
본 발명에 따른 감광성 수지 조성물은 광활성 화합물로서 1,2-퀴논디아지드계 화합물을 포함할 수 있다. 상기 광활성 화합물은 가시광선, 자외선, 심자외선(deep-ultraviolet radiation) 등에 의하여 경화될 수 있는 단량체들의 중합 반응을 개시하는 역할을 한다.
상기 1,2-퀴논디아지드계 화합물은 포토레지스트 분야에서 감광제로서 사용되고, 1,2-퀴논디아지드계 구조를 갖는 화합물이라면 특별히 한정하지 않는다.
예를 들어, 상기 1,2-퀴논디아지드계 화합물은 페놀 화합물과 1,2-벤조퀴논디아지드-4-설폰산 또는 1,2-벤조퀴논디아지드-5-설폰산의 에스테르 화합물; 페놀 화합물과 1,2-나프토퀴논디아지드-4-설폰산 또는 1,2-나프토퀴논디아지드-5-설폰산의 에스테르 화합물; 페놀 화합물의 수산기를 아미노기로 치환한 화합물과 1,2-벤조퀴논디아지드-4-설폰산 또는 1,2-벤조퀴논디아지드-5-설폰산과의 설폰아미드 화합물; 페놀 화합물의 수산기를 아미노기로 치환한 화합물과 1,2-나프토퀴논디아지드-4-설폰산 또는 1,2-나프토퀴논디아지드-5-설폰산의 설폰아미드 화합물 등을 들 수 있다. 상기의 물질들은 단독으로 사용되거나 둘 이상을 혼합하여 사용될 수도 있다.
상기 페놀 화합물의 예로는, 2,3,4-트리히드록시벤조페논, 2,4,6-트리히드록시벤조페논, 2,2',4,4'-테트라히드록시벤조페논, 2,3,3',4-테트라히드록시벤조페논, 2,3,4,4'-테트라히드록시벤조페논, 비스(2,4-디히드록시페닐)메탄, 비스(p-히드록시페닐)메탄, 트리(p-히드록시페닐)메탄, 1,1,1-트리(p-히드록시페닐)에탄, 비스(2,3,4-트리히드록시페닐)메탄, 2,2-비스(2,3,4-트리히드록시페닐)프로판, 1,1,3-트리스(2,5-디메틸-4-히드록시페닐)-3-페닐프로판, 4,4'-[1-[4-[1-[4-히드록시페닐]-1-메틸에틸]페닐]에틸리덴]비스페놀, 비스(2,5-디메틸-4-히드록시페닐)-2-히드록시페닐메탄, 3,3,3',3'-테트라메틸-1,1'-스피로비인덴-5,6,7,5',6',7'-헥사놀, 2,2,4-트리메틸-7,2',4'-트리히드록시플라반, 비스[4-히드록시-3-(2-히드록시-5-메틸벤질)-5-디메틸페닐]메탄 등을 들 수 있다.
상기 1,2-퀴논디아지드계 화합물의 구체적인 예로는, 2,3,4-트리히드록시벤조페논과 1,2-나프토퀴논디아지드-4-설폰산의 에스테르 화합물, 2,3,4-트리히드록시벤조페논과 1,2-나프토퀴논디아지드-5-설폰산의 에스테르 화합물, 4,4'-[1-[4-[1-[4-히드록시페닐]-1-메틸에틸]페닐]에틸리덴]비스페놀과 1,2-나프토퀴논디아지드-4-설폰산의 에스테르 화합물, 4,4'-[1-[4-[1-[4-히드록시페닐]-1-메틸에틸]페닐]에틸리덴]비스페놀과 1,2-나프토퀴논디아지드-5-설폰산과의 에스테르 화합물, 비스[4-히드록시-3-(2-히드록시-5-메틸벤질)-5-디메틸페닐]메탄과 1,2-나프토퀴논디아지드-5-설폰산과의 에스테르 화합물 등을 들 수 있다. 보다 구체적인 예로는, 1,2-퀴논디아지드 4-술폰산 에스테르, 1,2-퀴논디아지드 5-술폰산 에스테르 및 1,2-퀴논디아지드 6-술폰산 에스테르로 이루어진 군에서 선택되는 1종 이상일 수 있다. 1,2-퀴논디아지드계 화합물로 상기 화합물을 사용할 경우, 감광성 수지 조성물의 투명성이 보다 향상될 수 있다.
본 발명의 감광성 수지 조성물은 이의 총 중량에 대하여, 상기 1,2-퀴논디아지드계 화합물을 0.1 내지 10 중량%, 0.5 내지 10 중량%, 1 내지 10 중량%, 1 내지 7 중량%, 2 내지 7 중량% 또는 2 내지 5 중량%의 양으로 포함할 수 있다.
상기 함량 범위 내일 때, 수지 조성물의 패턴 형성이 보다 용이하고, 도막 형성 후 도막 표면이 거칠어지거나 현상시 하단부에 스컴(scum) 등의 패턴 형상이 발생하는 문제를 억제할 수 있다.
본 발명에 따른 포지티브형 감광성 수지 조성물은 광활성 화합물로서 오르쏘-퀴논디아지드기를 포함하는 고분자 화합물을 추가로 포함할 수 있다.
구체적으로, 상기 광활성 화합물은 하기 화학식 2로 표시되는 반복단위를 포함하는 화합물을 추가로 포함할 수 있다.
[화학식 2]
상기 화학식 2에서, A1 및 A2는 각각 독립적으로 수소, 히드록시기, 페놀기, C1-4 알킬기, C6-15 아릴기, C1-4 알콕시기이고, R3은 수소 또는 이며, n은 3 내지 15의 정수이다.
보다 구체적으로, 상기 화학식 2로 표시되는 반복단위를 포함하는 화합물은 1,2-벤조퀴논디아지드-4-설폰산, 1,2-나프토퀴논디아지드-4-설폰산, 1,2-나프토퀴논디아지드-5-설폰산 등의 에스테르 화합물 및/또는 이들이 수산기를 아미노기로 치환한 화합물일 수 있다.
상기 화학식 2로 표시되는 반복단위를 포함하는 화합물은 단독, 또는 방향족 알데히드계 알칼리 가용성 수지(예: 폴리히드록시 방향족 화합물)와 병용하여 사용할 수 있다.
예를 들면, 글리세린, 펜타에리트리톨 등의 폴리히드록시알킬 화합물, 노볼락 수지, 비스페놀A, 몰식자산 에스테르, 퀘르세틴, 모린, 폴리히드록시벤조페논 등의 폴리히드록시 방향족 화합물과, 1,2-벤조퀴논디아지드-4-설폰산, 1,2-나프토퀴논디아지드-4-설폰산, 1,2-나프토퀴논디아지드-5-설폰산 등의 에스테르를 병용하여 사용할 수 있고, 바람직하게는 노볼락 수지, 및/또는 폴리히드록시 벤조페논과 1,2-나프토퀴논 디아지드-5-설폰산 에스테르 화합물을 사용할 수 있다.
이때, 노볼락 수지의 치환율(에스테르화율)은 10 내지 70%, 또는 25 내지 60%(노볼락 수지 에스테르화물/전체 노볼락 수지X100)일 수 있다. 폴리히드록시 벤조페논의 치환율은 50 내지 95%(폴리히드록시 벤조페논 에스테르화물/전체 폴리히드록시 벤조페논X100)일 수 있다. 상기 범위 내일 때, 조성물의 해상도 및 감도가 보다 향상될 수 있다. 만약 상기 치환율이 저조한 경우 해상도가 떨어지고 치환율이 지나치게 높은 경우에는 감도가 저하될 수 있다.
본 발명의 감광성 수지 조성물은 이의 총 중량에 대하여, 상기 화학식 2로 표시되는 반복단위를 포함하는 화합물을 0.1 내지 10 중량%, 0.5 내지 10 중량%, 1 내지 10 중량%, 1 내지 7 중량%, 2 내지 7 중량% 또는 2 내지 5 중량%의 양으로 포함할 수 있다.
상기 함량 범위 내일 때, 패턴 형성이 용이하고, 도막 형성후 도막 표면이 거칠어지지 않으며 현상 시 하단부에 스컴(scum) 등의 패턴 형상이 발생하는 문제를 억제할 수 있다.
(C) 용매
본 발명의 감광성 수지 조성물은 상기 성분들을 용매와 혼합한 액상 조성물로 제조될 수 있다. 상기 용매는, 예를 들어, 유기 용매일 수 있다.
본 발명에 따른 감광성 수지 조성물 내의 용매의 함량은 특별히 한정되지 않지만, 예를 들어, 감광성 수지 조성물의 총 중량을 기준으로 고형분 함량이 10 내지 90 중량%, 10 내지 85 중량%, 10 내지 70 중량%, 15 내지 60 중량%, 15 내지 50 중량%, 15 내지 40 중량% 또는 15 내지 30 중량%가 되도록 용매를 포함할 수 있다.
상기 고형분은 본 발명의 수지 조성물 중에서 용매를 제외한 조성 성분을 의미한다. 용매의 함량이 상기 함량 범위 내일 때 코팅이 용이하면서도 적정 수준의 흐름성을 유지할 수 있다.
상기 용매는 상술한 바와 같은 성분을 용해시킬 수 있고 화학적으로 안정한 것이면 특별히 제한되지 않는다. 예를 들어, 상기 용매는 알코올, 에테르, 글리콜에테르, 에틸렌글리콜알킬에테르아세테이트, 디에틸렌글리콜, 프로필렌글리콜모노알킬에테르, 프로필렌글리콜알킬에테르아세테이트, 프로필렌글리콜알킬에테르프로피오네이트, 방향족 탄화수소, 케톤, 에스테르 등을 들 수 있다.
구체적으로, 상기 용매는 메탄올, 에탄올, 테트라히드로퓨란, 디옥산, 메틸셀로솔브아세테이트, 에틸셀로솔브아세테이트, 에틸아세토아세테이트, 에틸렌글리콜모노메틸에테르, 에틸렌글리콜모노에틸에테르, 에틸렌글리콜디메틸에테르, 에틸렌글리콜디에틸에테르, 프로필렌글리콜디메틸에테르, 프로필렌글리콜디에틸에테르, 디에틸렌글리콜모노메틸에테르, 디에틸렌글리콜모노에틸에테르, 디에틸렌글리콜디메틸에테르, 디에틸렌글리콜에틸메틸에테르, 프로필렌글리콜모노메틸에테르, 프로필렌글리콜모노에틸에테르, 프로필렌글리콜모노프로필에테르, 디프로필렌글리콜디메틸에테르, 디프로필렌글리콜디에틸에테르, 프로필렌글리콜메틸에테르아세테이트, 프로필렌글리콜에틸에테르아세테이트, 프로필렌글리콜프로필에테르아세테이트, 디프로필렌글리콜메틸에테르아세테이트, 프로필렌글리콜부틸에테르아세테이트, 톨루엔, 크실렌, 메틸에틸케톤, 4-히드록시-4-메틸-2-펜타논, 시클로펜타논, 시클로헥사논, 2-헵타논, γ-부티로락톤, 에틸 2-히드록시프로피온산, 에틸 2-히드록시-2-메틸프로피온산, 에틸에톡시초산, 에틸히드록시초산, 메틸 2-히드록시-3-메틸부탄산, 메틸 2-메톡시프로피온산, 메틸 3-메톡시프로피온산, 에틸 3-메톡시프로피온산, 에틸 3-에톡시프로피온산, 메틸 3-에톡시프로피온산, 메틸 피루빈산, 에틸 피루빈산, 에틸초산, 부틸초산, 에틸젖산, 부틸젖산, N,N-디메틸포름아미드, N,N-디메틸아세트아미드, N-메틸피롤리돈 등을 들 수 있다.
이들 중에서, 에틸렌글리콜알킬에테르아세테이트류, 디에틸렌글리콜류, 프로필렌글리콜모노알킬에테르류, 프로필렌글리콜알킬에테르아세테이트류, 케톤류 등이 바람직하고, 특히, 디에틸렌글리콜디메틸에테르, 디에틸렌글리콜에틸메틸에테르, 디프로필렌글리콜디메틸에테르, 디프로필렌글리콜디에틸에테르, 프로필렌글리콜모노메틸에테르, 프로필렌글리콜모노에틸에테르, 프로필렌글리콜메틸에테르아세테이트, 2-메톡시프로피온산메틸, 감마-부티로락톤, 4-하이드록시-4-메틸-2-펜타논 등이 바람직하다. 상기 예시한 용매들은 단독으로 또는 2종 이상 배합하여 사용될 수 있다.
(D) 에폭시 화합물
본 발명에 따른 감광성 수지 조성물은 에폭시 화합물을 포함할 수 있다.
상기 에폭시 화합물은 실록산 공중합체(A)의 내부 밀도를 증대시키는 역할을 한다. 따라서, 이들을 포함하는 상기 감광성 수지 조성물로부터 형성된 경화막의 내화학성을 보다 향상시킬 수 있다.
상기 에폭시 화합물은 에폭시기를 1개 이상 포함하는 불포화 단량체의 호모 올리고머 또는 헤테로 올리고머일 수 있다.
상기 에폭시기를 1개 이상 포함하는 불포화 단량체의 예로는, 글리시딜(메트)아크릴레이트, 4-히드록시부틸아크릴레이트글리시딜에테르, 3,4-에폭시부틸(메트)아크릴레이트, 4,5-에폭시펜틸(메트)아크릴레이트, 5,6-에폭시헥실(메트)아크릴레이트, 6,7-에폭시헵틸(메트)아크릴레이트, 2,3-에폭시시클로펜틸(메트)아크릴레이트, 3,4-에폭시시클로헥실(메트)아크릴레이트, 3,4-에폭시시클로헥실메틸(메트)아크릴레이트, α-에틸글리시딜아크릴레이트, α-n-프로필글리시딜아크릴레이트, α-n-부틸글리시딜아크릴레이트, N-(4-(2,3-에폭시프로폭시)-3,5-디메틸벤질)아크릴아미드, N-(4-(2,3-에폭시프로폭시)-3,5-디메틸페닐프로필)아크릴아미드, 알릴글리시딜에테르, 2-메틸알릴글리시딜에테르, o-비닐벤질글리시딜에테르, m-비닐벤질글리시딜에테르, p-비닐벤질글리시딜에테르 또는 그 혼합물을 들 수 있으며, 바람직하게는 글리시딜메타크릴레이트일 수 있다.
상기 에폭시 화합물은 이미 알려져 있는 방법으로 합성될 수 있다.
상기 에폭시 화합물의 시판품으로서는 GHP24HP 또는 GHP03HP를 들 수 있다.
상기 에폭시 화합물은 하기 구성단위를 추가로 더 포함할 수 있다.
구체적인 예로는, 스티렌; 메틸스티렌, 디메틸스티렌, 트리메틸스티렌, 에틸스티렌, 디에틸스티렌, 트리에틸스티렌, 프로필스티렌, 부틸스티렌, 헥실스티렌, 헵틸스티렌, 옥틸스티렌 등의 알킬 치환기를 갖는 스티렌; 플루오로스티렌, 클로로스티렌, 브로모스티렌, 요오도스티렌 등의 할로겐을 갖는 스티렌; 메톡시스티렌, 에톡시스티렌, 프로폭시스티렌 등의 알콕시 치환기를 갖는 스티렌; p-히드록시-α-메틸스티렌, 아세틸스티렌; 디비닐벤젠, 비닐페놀, o-비닐벤질메틸에테르, m-비닐벤질메틸에테르, p-비닐벤질메틸에테르 등의 방향족환 함유 에틸렌성 불포화 화합물; 메틸(메트)아크릴레이트, 에틸(메트)아크릴레이트, 부틸(메트)아크릴레이트, 디메틸아미노에틸(메트)아크릴레이트, 이소부틸(메트)아크릴레이트, t-부틸(메트)아크릴레이트, 시클로헥실(메트)아크릴레이트, 에틸헥실(메트)아크릴레이트, 테트라히드로퍼프릴(메트)아크릴레이트, 히드록시에틸(메트)아크릴레이트, 2-히드록시프로필(메트)아크릴레이트, 2-히드록시-3-클로로프로필(메트)아크릴레이트, 4-히드록시부틸(메트)아크릴레이트, 글리세롤(메트)아크릴레이트, 메틸 α-히드록시메틸아크릴레이트, 에틸 α-히드록시메틸아크릴레이트, 프로필 α-히드록시메틸아크릴레이트, 부틸 α-히드록시메틸아크릴레이트, 2-메톡시에틸(메트)아크릴레이트, 3-메톡시부틸(메트)아크릴레이트, 에톡시디에틸렌글리콜(메트)아크릴레이트, 메톡시트리에틸렌글리콜(메트)아크릴레이트, 메톡시트리프로필렌글리콜(메트)아크릴레이트, 폴리(에틸렌글리콜)메틸에테르(메트)아크릴레이트, 페닐(메트)아크릴레이트, 벤질(메트)아크릴레이트, 2-페녹시에틸(메트)아크릴레이트, 페녹시디에틸렌글리콜(메트)아크릴레이트, p-노닐페녹시폴리에틸렌글리콜(메트)아크릴레이트, p-노닐페녹시폴리프로필렌글리콜(메트)아크릴레이트, 테트라플루오로프로필(메트)아크릴레이트, 1,1,1,3,3,3-헥사플루오로이소프로필(메트)아크릴레이트, 옥타플루오로펜틸(메트)아크릴레이트, 헵타데카플루오로데실(메트)아크릴레이트, 트리브로모페닐(메트)아크릴레이트, 이소보닐(메트)아크릴레이트, 디시클로펜타닐(메트)아크릴레이트, 디시클로펜테닐(메트)아크릴레이트, 디시클로펜타닐옥시에틸(메트)아크릴레이트, 디시클로펜테닐옥시에틸(메트)아크릴레이트 등의 불포화 카복실산 에스테르류; N-비닐피롤리돈, N-비닐카바졸, N-비닐모폴린 등의 N-비닐을 갖는 삼차아민류; 비닐메틸에테르, 비닐에틸에테르 등의 불포화 에테르류; N-페닐말레이미드, N-(4-클로로페닐)말레이미드, N-(4-히드록시페닐)말레이미드, N-시클로헥실말레이미드 등의 불포화 이미드류 등으로부터 유도되는 구성단위를 들 수 있다. 상기 예시된 화합물로부터 유도되는 구성단위는 단독으로 또는 2종 이상 조합되어 에폭시 화합물에 포함될 수 있다. 바람직하게는, 이들 중 스티렌계 화합물인 것이 중합성 측면에서 보다 유리하다.
이때, 상기 에폭시 화합물은 카르복실기를 갖는 단량체로부터 유도되는 구성단위를 포함하지 않는다. 즉, 상기 에폭시 화합물이 카르복실기를 포함하지 않는 것이 내화학성 측면에서 보다 유리하다.
상기 구성단위는, 상기 에폭시 화합물을 구성하는 구성단위 총 몰수에 대해서 0 내지 70 몰% 또는 10 내지 60 몰%로 포함될 수 있다. 상기 함량 범위 내일 때 막강도 측면에서 보다 유리할 수 있다.
상기 에폭시 화합물의 중량평균분자량은 100 내지 30,000 Da, 또는 1,000 내지 15,000 Da일 수 있다. 상기 에폭시 화합물의 중량평균분자량이 100 Da 이상일 때 박막의 경도가 보다 우수해질 수 있고, 30,000 Da 이하일 때 박막의 두께가 균일해져서 단차의 평탄화에 적합할 수 있다.
본 발명의 감광성 수지 조성물은 이의 총 중량에 대하여, 상기 에폭시 화합물을 0.01 내지 10 중량%, 0.05 내지 10 중량%, 0.1 내지 10 중량%, 0.3 내지 10 중량%, 0.3 내지 7 중량%, 0.5 내지 7 중량%, 0.5 내지 5 중량%, 1 내지 5 중량% 또는 1 내지 3 중량%의 양으로 포함할 수 있다.
상기 함량 범위 내일 때, 내화학성 및 감도가 우수하다. 만약 상기 범위를 벗어나는 경우, 예컨대, 상기 함량 미만으로 소량 사용하면 내화학성이 크게 저하되고, 과량 사용하는 경우 감도가 저하될 수 있다.
(E) 계면활성제
본 발명의 감광성 수지 조성물은 필요에 따라, 조성물의 도포 성능을 향상시키기 위해 계면활성제를 더 포함할 수 있다.
이러한 계면활성제의 종류는 특별히 한정되지 않으나, 예를 들어, 불소계 계면활성제, 실리콘계 계면활성제, 비이온계 계면활성제 등을 들 수 있다.
상기 계면활성제의 구체적인 예로는, 다우 코닝 도레이사의 FZ-2122, BM CHEMIE사의 BM-1000 및 BM-1100, 다이닛뽄잉크 가가꾸고교 가부시키가이사의 메가팩 F-142 D, F-172, F-173 및 F-183, 스미또모 쓰리엠 리미티드의 플로라드 FC-135, FC-170 C, FC-430 및 FC-431, 아사히 가라스 가부시키가이사의 서프론 S-112, S-113, S-131, S-141, S-145, S-382, SC-101, SC-102, SC-103, SC-104, SC-105 및 SC-106, 신아끼따 가세이 가부시키가이사의 에프톱 EF301, EF303 및 EF352, 도레이 실리콘 가부시키가이사의 SH-28 PA, SH-190, SH-193, SZ-6032, SF-8428, DC-57 및 DC-190 등의 불소계 및 실리콘계 계면활성제; 폴리옥시에틸렌라우릴에테르, 폴리옥시에틸렌스테아릴에테르 및 폴리옥시에틸렌올레일에테르와 같은 폴리옥시에틸렌알킬에테르류, 폴리옥시에틸렌옥틸페닐에테르 및 폴리옥시에틸렌노닐페닐에테르와 같은 폴리옥시에틸렌아릴에테르류, 폴리옥시에틸렌디라우레이트 및 폴리옥시에틸렌디스테아레이트와 같은 폴리옥시에틸렌디알킬에스테르류 등의 비이온계 계면활성제; 유기실록산 폴리머 KP341(신에쓰 가가꾸고교 가부시키가이샤 제조), (메트)아크릴산계 공중합체 폴리플로우 No. 57 및 95(교에이샤 유지 가가꾸고교 가부시키가이샤 제조) 등을 들 수 있다. 이들은 단독으로 또는 2종 이상을 조합하여 사용할 수 있다.
본 발명의 감광성 수지 조성물은 이의 총 중량에 대하여, 상기 계면활성제를 0.001 내지 5 중량%, 0.005 내지 5 중량%, 0.01 내지 5 중량%, 0.01 내지 3 중량% 또는 0.01 내지 1 중량%의 양으로 포함할 수 있다.
상기 함량 범위 내에서 조성물의 코팅 및 레벨링 특성이 원활해진다.
(F) 실란 화합물
본 발명의 감광성 수지 조성물은 실란 화합물을 더 포함하여, 에폭시 화합물과 함께 실록산 공중합체 중 반응성이 높은 실란올기(Si-OH)의 함량을 감소시켜, 후공정 처리시 조성물의 내화학성이 향상될 수 있다.
상기 실란 화합물은 하기 화학식 3으로 표시되는 화합물일 수 있다.
[화학식 3]
(R4)qSi(OR5)4-q
상기 화학식 3에서,
q는 0 내지 3의 정수이고; R4는 각각 독립적으로 각각 독립적으로 C1-12알킬기, C2-10알케닐기, C6-15아릴기, 3-12원의 헤테로알킬기, 4-10원의 헤테로알케닐기, 또는 6-15원의 헤테로아릴기이며; R5는 각각 독립적으로 수소, C1-6알킬기, C2-6아실기, 또는 C6-15아릴기이고, 상기 헤테로알킬기, 헤테로알케닐기 및 헤테로아릴기는 각각 독립적으로 O, N 및 S로 이루어진 군으로부터 선택된 하나 이상의 헤테로원자를 갖는다.
q = 0인 경우에는 4 관능성 실란 화합물, q = 1인 경우에는 3 관능성 실란 화합물, q = 2인 경우에는 2 관능성 실란 화합물, q = 3인 경우에는 1 관능성 실란 화합물일 수 있다.
이러한 실란 화합물의 구체예로는, 4 관능성 실란 화합물로서, 테트라아세톡시실란, 테트라메톡시실란, 테트라에톡시실란, 테트라부톡시실란, 테트라페녹시실란, 테트라벤질옥시실란 및 테트라프로폭시실란; 3 관능성 실란 화합물로서, 메틸트리메톡시실란, 메틸트리에톡시실란, 메틸트리이소프로폭시실란, 메틸트리부톡시실란, 에틸트리메톡시실란, 에틸트리에톡시실란, 에틸트리이소프로폭시실란, 에틸트리부톡시실란, 부틸트리메톡시실란, 펜타플로오로페닐트리메톡시실란, 페닐트리메톡시실란, 페닐트리에톡시실란, d3-메틸트리메톡시실란, 노나플루오로부틸에틸트리메톡시실란, 트리플루오로메틸트리메톡시실란, n-프로필트리메톡시실란, n-프로필트리에톡시실란, n-부틸트리에톡시실란, n-헥실트리메톡시실란, n-헥실트리에톡시실란, 데실트리메톡시실란, 비닐트리메톡시실란, 비닐트리에톡시실란, 3-메타크릴옥시프로필트리메톡시실란, 3-메타크릴옥시프로필트리에톡시실란, 3-아크릴옥시프로필트리메톡시실란, 3-아크릴옥시프로필트리에톡시실란, p-히드록시페닐트리메톡시실란, 1-(p-히드록시페닐)에틸트리메톡시실란, 2-(p-히드록시페닐)에틸트리메톡시실란, 4-히드록시-5-(p-히드록시페닐카르보닐옥시)펜틸트리메톡시실란, 트리플루오로메틸트리에톡시실란, 3,3,3-트리플루오로프로필트리메톡시실란, 3-아미노프로필트리메톡시실란, 3-아미노프로필트리에톡시실란, 3-글리시독시프로필트리메톡시실란, 3-글리시독시프로필트리에톡시실란, 2-(3,4-에폭시시클로헥실)에틸트리메톡시실란, 2-(3,4-에폭시시클로헥실)에틸트리에톡시실란, [(3-에틸-3-옥세타닐)메톡시]프로필트리메톡시실란, [(3-에틸-3-옥세타닐)메톡시]프로필트리에톡시실란, 3-메르캅토프로필트리메톡시실란 및 3-트리메톡시실릴프로필숙신산; 2 관능성 실란 화합물로서, 디메틸디아세톡시실란, 디메틸디메톡시실란, 디페닐디메톡시실란, 디페닐디에톡시실란, 디페닐디페녹시실란, 디부틸디메톡시실란, 디메틸디에톡시실란, (3-글리시독시프로필)메틸디메톡시실란, (3-글리시독시프로필)메틸디에톡시실란, 3-(2-아미노에틸아미노)프로필디메톡시메틸실란, 3-아미노프로필디에톡시메틸실란, 3-클로로프로필디메톡시메틸실란, 3-메르캅토프로필디메톡시메틸실란, 시클로헥실디메톡시메틸실란, 디에톡시메틸비닐실란, 디메톡시메틸비닐실란 및 디메톡시디-p-톨릴실란; 및 1 관능성 실란 화합물로서, 트리메틸메톡시실란, 트리부틸메톡시실란, 트리메틸에톡시실란, 트리부틸에톡시실란, (3-글리시독시프로필)디메틸메톡시실란 및 (3-글리시독시프로필)디메틸에톡시실란 등을 들 수 있다.
이들 중에서, 4 관능성 실란 화합물로서 테트라메톡시실란, 테트라에톡시실란 또는 테트라부톡시실란이 바람직하고; 3 관능성 실란 화합물로서 메틸트리메톡시실란, 메틸트리에톡시실란, 메틸트리이소프로폭시실란, 메틸트리부톡시실란, 페닐트리메톡시실란, 에틸트리메톡시실란, 에틸트리에톡시실란, 에틸트리이소프로폭시실란, 에틸트리부톡시실란, 부틸트리메톡시실란, 3-글리시독시프로필트리메톡시실란, 3-글리시독시프로필트리에톡시실란, 2-(3,4-에폭시시클로헥실)에틸트리메톡시실란 또는 2-(3,4-에폭시시클로헥실)에틸트리에톡시실란이 바람직하고; 2 관능성 실란 화합물로서 디메틸디메톡시실란, 디페닐디메톡시실란, 디페닐디에톡시실란, 디페닐디페녹시실란, 디부틸디메톡시실란 또는 디메틸디에톡시실란이 바람직하다. 이러한 실란 화합물들은 단독으로 또는 2종 이상 조합하여 사용할 수도 있다.
구체적으로, 상기 실란 화합물은 q가 0인 4 관능성 실란 화합물(Q 타입의 실란 화합물) 또는 q가 1인 3 관능성 실란 화합물(T 타입의 실란 화합물)일 수 있다.
본 발명의 감광성 수지 조성물은 이의 총 중량에 대하여, 상기 실란 화합물을 0.05 내지 10 중량%, 0.1 내지 10 중량%, 0.3 내지 10 중량%, 0.5 내지 10 중량%, 0.5 내지 7 중량%, 0.5 내지 5 중량% 또는 0.5 내지 3 중량%의 양으로 포함할 수 있다. 상기 함량 범위 내일, 경화막의 내화학성을 더욱 향상시킬 수 있다.
(G) 접착보조제
본 발명의 감광성 수지 조성물은 기판과의 접착성을 향상시키기 위해 접착보조제를 추가로 포함할 수 있다.
상기 접착보조제는 카르복실기, (메트)아크릴로일기, 이소시아네이트기, 아미노기, 메르캅토기, 비닐기 및 에폭시기로 이루어진 그룹에서 선택되는 적어도 1종 이상의 반응성 그룹을 가질 수 있다.
상기 접착보조제의 종류는 특별히 한정되지 않으나, 예를 들면, 트리메톡시실릴벤조산, γ-메타크릴옥시프로필트리메톡시실란, 비닐트리아세톡시실란, 비닐트리메톡시실란, γ-이소시아네이토프로필트리에톡시실란, γ-글리시독시프로필트리메톡시실란, γ-글리시독시프로필트리에톡시실란, N-페닐아미노프로필트리메톡시실란, β-(3,4-에폭시시클로헥실)에틸트리메톡시실란, 3-이소시아네이트프로필트리에톡시실란 또는 이들의 혼합물을 들 수 있다.
바람직하게는 γ-글리시독시프로필트리에톡시실란, γ-글리시독시프로필트리메톡시실란, 3-이소시아네이트프로필트리에톡시실란 또는 N-페닐아미노프로필트리메톡시실란을 사용하는 것이 잔막율 및 기판과의 접착성을 보다 향상시킬 수 있다.
본 발명의 감광성 수지 조성물은 이의 총 중량에 대하여, 상기 접착보조제를 0.001 내지 5 중량%, 0.005 내지 5 중량%, 0.01 내지 5 중량%, 0.01 내지 3 중량% 또는 0.01 내지 1 중량%의 양으로 포함할 수 있다.
상기 함량 범위 내에서 기판과의 접착성을 보다 향상시킬 수 있다.
이 외에도, 본 발명의 포지티브형 감광성 수지 조성물은 물성을 저하시키지 않는 범위 내에서 산화방지제, 안정제 등의 기타의 첨가제를 포함할 수 있다.
본 발명에 따른 감광성 수지 조성물은 포지티브형 감광성 수지 조성물로서 사용될 수 있다. 나아가, 본 발명은 상기 포지티브형 감광성 수지 조성물로부터 제조된 경화막을 제공한다. 상기 경화막은 유기발광소지 및 양자점 발광소자의 화소정의막일 수 있다. 또한, 상기 경화막은 액정표시장치나 유기EL표시장치 등의 박막 트랜지스터(TFT) 기판용 평탄화막, 유기EL표시장치의 격벽, 반도체 소자의 층간 절연막, 및 광도파로의 코어나 클래딩재로도 사용될 수 있다.
상기 경화막은 당 기술분야에 알려져 있는 방법, 예컨대 기재 위에 상기 감광성 수지 조성물을 도포한 후 경화하는 과정을 거쳐 제조할 수 있다.
보다 구체적으로, 상기 경화는 기재 위에 도포된 감광성 수지 조성물을 예컨대 60 내지 130℃에서 예비경화하여 용매를 제거한 후, 원하는 패턴이 형성된 포토마스크를 이용하여 노광하고, 현상액(예: 테트라메틸암모늄하이드록사이드 용액(TMAH))으로 현상함으로써 코팅층에 패턴을 형성할 수 있다. 이후, 패턴화된 코팅층을 필요에 따라 예컨대 10분 내지 5시간 동안 150 내지 300℃에서 후경화(post-bake)하여 목적하는 경화막을 제조할 수 있다. 상기 노광은 200 내지 500 ㎚의 파장대에서 365 ㎚ 기준으로 10 내지 200 mJ/㎠의 노광량으로 수행할 수 있다. 본 발명의 방법에 의하면 공정 측면에서 용이하게 원하는 패턴을 형성할 수 있다.
감광성 수지 조성물의 기재 위에의 도포는 스핀 또는 슬릿 코팅법, 롤 코팅법, 스크린 인쇄법, 어플리케이터법 등의 방법을 사용하여 원하는 두께, 예를 들어 2 내지 25 ㎛의 두께로 수행할 수 있다. 또한, 노광(조사)에 사용되는 광원으로는 저압 수은등, 고압 수은등, 초고압 수은등, 금속 할로겐화물 램프, 아르곤 가스 레이저 등을 사용할 수 있으며, 경우에 따라 X선, 전자선 등도 이용할 수 있다.
한편, 상기 감광성 수지 조성물은 보다 투명한 경화막을 얻기 위해 노광 및 현상 후 300 내지 2,000 mJ/㎠, 또는 500 내지 1,500 mJ/㎠의 에너지로 포토블리칭(photobleaching)될 수 있다. 구체적으로, 상기 조성물은 기재에 도포된 후 상술한 바와 같은 노광 및 현상 공정 후에 포토블리칭하고 후경화하여 경화막을 형성할 수 있다. 상기 포토블리칭 공정은 상기 포지티브형 감광성 수지 조성물의 주요 성분 중 하나인 실록산 공중합체와 1,2-퀴논디아지드계 화합물 간의 결합을 제거하여 투명한 경화막이 형성되도록 한다. 만약 포토블리칭 공정 없이 후경화되는 경우 붉으스름한 경화막이 얻어지므로 투과율, 예컨대, 400 내지 600 nm 영역에서의 투과율이 저하될 수 있다.
본 발명의 포지티브형 감광성 수지 조성물은 현상 후 및 후경화 후의 감도, 잔막율, 해상도 등의 측면에서 우수한 물성을 갖는 경화막을 형성할 수 있다. 특히, 본 발명에 따른 포지티브형 감광성 수지 조성물은 바인더 내 수분 함량을 조절하여, 제조 직후 뿐만 아니라 일정기간 보관 후에 사용하여도 우수한 감도, 해상도 및 잔막율을 갖는 경화막을 제조할 수 있다. 구체적으로, 본 발명은 조성물 제조 직후 및 상온에서 3일 보관 후에 경화막을 제조하여도, 이들간의 감도 차이(감도 변화율)가 크지 않다. 보다 구체적으로, 20% 미만, 10% 미만 또는 8% 미만의 감도 변화율을 갖는다.
이하, 하기 실시예에 의하여 본 발명을 좀더 상세하게 설명하고자 한다. 단, 하기 실시예는 본 발명을 예시하기 위한 것일 뿐 본 발명의 범위가 이들만으로 한정되는 것은 아니다.
하기 제조예에 기재된 중량평균분자량은 겔 투과 크로마토그래피(GPC)에 의해 측정한 폴리스티렌 환산값이다.
[실시예]
제조예 1. 실록산 공중합체(A-1)의 제조
환류 냉각장치가 갖추어진 반응기에 페닐트리메톡시실란 40 중량%, 메틸트리메톡시실란 15 중량%, 테트라에톡시실란 20 중량%, 순수 20 중량%를 넣고 PGMEA 5중량%를 투입한 다음 0.1 중량%의 옥살산 촉매 하에서 7시간 동안 격렬히 환류 교반하였다. 이후 냉각한 다음 25℃(상온) 및 최저압력 -760 mmHg 조건의 진공 오븐에서 물을 제거하였다(수분 제거). 그 다음, PGMEA로 희석하여 고형분 함량이 40%가 되게 하고 GPC로 분석을 실시한 결과 분자량이 2,000~8,000 Da이고 Volumetric KF 수분 결정법에 의한 수분 함유율이 1.3%인 실록산 공중합체 A-1을 제조하였다.
제조예 2 내지 6. 실록산 공중합체(A-2 ~ A-6)의 제조
수분 제거하는 과정을 다르게 한 것을 제외하고는, 제조예 1과 동일한 방법으로 실록산 공중합체 A-2 ~ A-6를 제조하였다.
실시예 및 비교예: 감광성 수지 조성물의 제조
상기 제조예에서 제조된 화합물들을 이용하여 하기 실시예 및 비교예의 감광성 수지 조성물을 제조하였다.
이하의 실시예 및 비교예에서 사용한 성분들에 대한 정보는 다음과 같다.
실시예 1.
제조예 1의 실록산 공중합체(A-1) 15.93 중량부, 광활성 화합물(B)로서 TPA-517 2.64 중량부, 에폭시 화합물(D)로서 GHP03HP 2.28 중량부, 계면활성제(E) FZ-2122 0.05 중량부 및 실란 화합물(F)로서 OFS-6124 1.1 중량부를 균일하게 혼합하였다. 이때, 상기 각각의 함량들은 모두 용매를 제외한 고형분의 함량이다. 상기 혼합물의 고형분 함량이 22 중량%가 되도록 (C-1) PGMEA 72.54 중량부 및 (C-2) GBL 5.46 중량부를 혼합한 혼합 용매에 용해시켰다. 이를 1~2시간 동안 교반한 후 공경 0.2 ㎛의 멤브레인 필터로 여과하여 고형분 함량 22 중량%인 액상 형태의 감광성 수지 조성물을 얻었다.
실시예 2 내지 4 및 비교예 1 및 2.
각각의 구성성분의 종류 및/또는 함량을 하기 표 3에 기재된 바와 같이 변화시킨 것을 제외하고는, 실시예 1과 동일한 방법으로 감광성 수지 조성물을 얻었다.
[평가예]
상기 실시예 및 비교예에서 제조된 감광성 수지 조성물로부터 경화막을 제조하고 다음과 같이 평가하였다.
평가예 1. 수분 함유율
상기 제조예 1 내지 6에서 얻은 각각의 실록산 공중합체에 대하여 Volumetric KF 수분결정법(칼-피셔 수분결정법)에 의한 수분 함량을 측정하였다.
Metrohm사의 710 KF-Titrino 수분측정기를 이용하여 실록산 공중합체 내 수분 함량을 자동측정하였다. 먼저, 상기 수분측정기에 H2O를 주입하여 STD 적정을 하였다. 그 다음, 상기 실록산 공중합체를 주입하여 실록산 공중합체 내 수분량을 측정하였다. 이때, Double Pt 전극을 사용하고 용매로는 메탄올, KF 시약으로는 Composite 5를 사용하였다. 그 결과를 상기 표 1에 나타내었다.
평가예 2. 감도
상기 실시예 및 비교예에서 얻은 각각의 조성물을 유리 기판 상에 스핀 코팅한 후에 120℃를 유지한 고온플레이트 위에서 90초 동안 예비경화하여 건조막을 형성하였다. 이 막에 1 ㎛에서 30 ㎛까지의 사각형 홀 크기가 있는 마스크를 사용하여 기판과의 간격이 25 ㎛이 되도록 적용하였다. 이후, 200 ㎚에서 450 ㎚의 파장을 내는 어라이너(aligner, 모델명 MA6)를 이용하여, 365 ㎚ 기준으로 0~200 mJ/㎠이 되도록 일정시간 노광한 후, TMAH 2.38 중량%로 희석된 수용액으로 23℃에서 퍼들 노즐을 통해 60초 동안 현상하였다. 이후, 상기 현상막에 200 ㎚에서 450 ㎚의 파장을 내는 어라이너(aligner,모델명 MA6)를 이용하여, 365 ㎚ 기준으로 200 mJ/㎠이 되도록 일정시간 노광한뒤(bleaching 공정), 컨백션 오븐에서 230℃에서 30분 동안 가열하여(후경화) 두께 2 ㎛의 경화막을 얻었다. 그 결과를 하기 표 4에 나타내었다.
상기 방법으로 마스크 크기 10 ㎛에 대해서 패터닝된 홀 패턴의 선폭(critical dimension; CD, 단위: ㎛)이 10 ㎛을 구현하는 시점까지의 노광 에너지량(mJ/㎠)을 구하였다. 노광 에너지량이 작을수록 감도가 우수한 것으로 평가하였다.
평가예 3. 보존 안정성(감도 변화율)
상기 실시예 및 비교예에서 얻은 각각의 조성물에 대하여, 제조 직후 및 상온(25℃)에서 3일 보관 후 상기 평가예 2와 동일한 방법을 경화막을 제조하여 노광 에너지량을 측정하였다. 제조 직후 조성물로 제조된 경화막에 대한 감도(초기 감도) 및 상온에서 3일 보관한 조성물로 제조된 경화막에 대한 감도(후 감도) 간의 변화율을 구하고, 감도 변화율이 작을수록 조성물의 보존 안정성이 우수한 것으로 평가하였다. 그 결과를 하기 표 4에 나타내었다.
감도 변화율(%) = (후 감도-초기 감도)/초기 감도 X 100
○: 감도 변화율이 10% 미만 / Ⅹ: 감도 변화율이 10% 이상
평가예 4. 잔막율
상기 평가에 2와 동일한 방법으로 두께 2 ㎛의 경화막을 얻었다.
예비경화후 막 두께와 후경화 후 얻어진 막의 두께를 막두께 평가장비(SNU Precision)로 측정하여 경화막의 잔막율을 백분율(%)로 나타내었다. 잔막율은 클수록 우사한 것으로 평가하였다. 그 결과를 하기 표 4에 나타내었다
잔막율(%) = (후경화 후 막두께 / 예비경화 후 막두께) X 100
평가예 5. 해상도
실시예 1, 3 및 4, 및 비교예 1 및 2의 조성물을 이용하여 상기 평가에 2와 동일한 방법으로 두께 2 ㎛의 경화막을 얻었다.
상기 경화막에 대하여 잔막이 남지 않는 패턴 중 최소 크기를 측정하고, 패턴의 크기가 작을수록 해상도가 우수한 것으로 평가하였다. 그 결과를 하기 표 5에 나타내었다.
표 4 및 5의 결과를 보면, 본 발명의 범위에 속하는 실시예의 조성물로부터 얻은 경화막은 우수한 감도, 해상도 및 잔막율을 가질 뿐만 아니라, 3일간 보관 후에 경화막을 제조하여도 감도의 변화가 적어 보존 안정성 측면에서도 탁월한 효과를 보였다. 반면, 바인더 내 수분 함유율이 1.5%를 초과하는 비교예의 조성물로부터 얻은 경화막은 해상도 및 잔막율은 유사한 수준을 나타내었으나 감도 측면, 특히 시간 경과에 따른 감도 변화율이 커서 보존 안정성 측면에서 매우 저조한 결과를 나타냈다.
Claims (10)
- (A) 실록산 공중합체;
(B) 광활성 화합물; 및
(C) 용매;를 포함하고,
상기 실록산 공중합체(A)의 Volumetric KF 수분결정법(칼-피셔 수분결정법)에 의한 수분 함유율이 1.5% 이하인, 포지티브형 감광성 수지 조성물. - 제1항에 있어서,
상기 실록산 공중합체(A)가 하기 화학식 1로 표시되는 실란 화합물로부터 유도되는 구성단위를 포함하는, 포지티브형 감광성 수지 조성물:
[화학식 1]
(R1)mSi(OR2)4-m
상기 화학식 1에서,
m은 0 내지 3의 정수이고;
R1은 각각 독립적으로 C1-12 알킬기, C2-10 알케닐기, C6-15 아릴기, 3-12원의 헤테로알킬기, 4-10원의 헤테로알케닐기, 또는 6-15원의 헤테로아릴기이고;
R2는 각각 독립적으로 수소, C1-6 알킬기, C2-6 아실기, 또는 C6-15 아릴기이며;
상기 헤테로알킬기, 헤테로알케닐기 및 헤테로아릴기는 각각 독립적으로 O, N 및 S로 이루어진 군으로부터 선택된 하나 이상의 헤테로원자를 갖는다. - 제1항에 있어서,
상기 실록산 공중합체(A)의 중량평균분자량이 2,000 내지 15,000 Da인, 포지티브형 감광성 수지 조성물. - 제1항에 있어서,
상기 감광성 수지 조성물이 상기 실록산 공중합체(A)를 상기 감광성 수지 조성물 총 중량에 대하여 3 내지 30 중량%의 양으로 포함하는, 포지티브형 감광성 수지 조성물. - 제1항에 있어서
상기 광활성 화합물(B)이 1,2-퀴논디아지드 4-술폰산 에스테르, 1,2-퀴논디아지드 5-술폰산 에스테르 및 1,2-퀴논디아지드 6-술폰산 에스테르로 이루어진 군에서 선택된 1종 이상인, 포지티브형 감광성 수지 조성물. - 제6항에 있어서,
상기 감광성 수지 조성물이 상기 화학식 2로 표시되는 반복단위를 포함하는 화합물을 상기 감광성 수지 조성물 총 중량에 대하여 0.1 내지 10 중량%의 양으로 포함하는, 포지티브형 감광성 수지 조성물. - 제1항에 있어서,
상기 감광성 수지 조성물이 에폭시 화합물(D), 계면활성제(E), 실란 화합물(F) 및 접착보조제(G)로 이루어진 군에서 선택된 1종 이상을 추가로 포함하는, 포지티브형 감광성 수지 조성물. - 제1항의 감광성 수지 조성물로부터 형성된, 경화막.
- 제9항에 있어서,
상기 경화막이 유기발광소자 및 양자점 발광소자의 화소정의막인, 경화막.