KR20210056756A - Hybrid lead-free radiation shielding material and radiation shielding suit using the same - Google Patents
Hybrid lead-free radiation shielding material and radiation shielding suit using the same Download PDFInfo
- Publication number
- KR20210056756A KR20210056756A KR1020190143591A KR20190143591A KR20210056756A KR 20210056756 A KR20210056756 A KR 20210056756A KR 1020190143591 A KR1020190143591 A KR 1020190143591A KR 20190143591 A KR20190143591 A KR 20190143591A KR 20210056756 A KR20210056756 A KR 20210056756A
- Authority
- KR
- South Korea
- Prior art keywords
- radiation shielding
- shielding material
- oxide
- radiation
- outer layer
- Prior art date
Abstract
Description
개시된 내용은 산란 엑스선 및 감마선을 차폐하는 방사선 차폐재 및 이를 이용한 방사선 차폐복에 관한 것이다.Disclosed is a radiation shielding material for shielding scattered X-rays and gamma rays, and a radiation shielding suit using the same.
방사선은 자연적으로 존재하는 방사선과 인위적으로 생성한 인공방사선이 있는데, 인공방사선에는 의료분야의 엑스-선(X-ray) 촬영부터 산업현장에까지 광범하게 활용되고 있다.Radiation is classified into naturally occurring radiation and artificially generated artificial radiation, and artificial radiation is widely used from X-ray imaging in the medical field to industrial sites.
방사선의 종류로는 전리 방사선과 비전리 방사선이 있으며, 전리 방사선은 분자에서 입자를 분리시켜 이온화시킬 수 있는 방사선이다.Types of radiation include ionizing radiation and non-ionizing radiation, and ionizing radiation is radiation that can ionize particles by separating them from molecules.
전리 방사선에는 알파선, 베타선, 엑스선, 감마선 등이 있으며, 알파선은 종이 정도의 두께를 가진 물질로도 막을 수 있고, 베타선은 알루미늄을 투과 할 수 없어 차폐에 어려움이 없다.Ionizing radiation includes alpha rays, beta rays, X-rays, and gamma rays, and alpha rays can be blocked with a material having a thickness of paper, and beta rays cannot penetrate aluminum, so there is no difficulty in shielding.
반면, 엑스선과 감마선은 파장이 짧아 물질을 투과하기 쉽고 피폭시 인체에 위해한 영향을 끼치므로 이를 최소화하기 위한 조치가 필요하다.On the other hand, since X-rays and gamma rays have short wavelengths, they are easy to penetrate substances and have a harmful effect on the human body when exposed, so measures to minimize them are required.
엑스선의 경우 최근 영상 의학의 급격한 발전으로 부품이나 용접부위에 엑스선을 촬영하여 무결성을 검사하거나, 인체 내부의 이상을 알아보기 위해 엑스선 촬영을 하는 등 점점 보편화되어 실시되고 있다. 이와 같은 엑스선 촬영 시에는 직간접적으로 당사자에게 피폭이 이루어지므로 이를 최소화하기 위한 엑스선 차폐제가 필요하다.In the case of X-rays, due to the recent rapid development of imaging medicine, X-rays are photographed on parts or welds to check integrity, or X-rays are taken to identify abnormalities inside the human body. In such X-ray imaging, since exposure is directly or indirectly to the person concerned, an X-ray shielding agent is required to minimize this.
한편, 감마선의 경우 핵의 붕괴나 변환으로부터 발생되고, 원자력 발전소 격납 건물, 원자력 발전소 해체, 의료용 감마선을 취급하는 암환자병동, 가속기 등에 방출 가능성이 상존한다. 감마선은 엑스선 보다 높은 에너지를 갖고 있어 투과력이 매우 강한 특징이 있다. 이러한 감마선은 콘크리트, 또는 철, 납과 같은 밀도가 높은 금속 물질을 통해서 차단할 수 있으나 금속물질을 사용하는 경우, 이들의 고밀도로 인하여 차폐재의 중량이 커지는 문제가 있다.On the other hand, in the case of gamma rays, it is generated from the collapse or transformation of the nucleus, and there is a possibility of emission of the nuclear power plant containment buildings, nuclear power plants dismantling, cancer patient wards, and accelerators handling medical gamma rays. Since gamma rays have higher energy than X-rays, they have very strong penetrating power. Such gamma rays can be blocked through concrete or a dense metal material such as iron or lead, but when metal materials are used, there is a problem that the weight of the shielding material increases due to their high density.
이러한 방사선의 불이익한 영향에서 인간과 환경을 보호하기 위해 방사선 차폐재가 필요하고, 방사선 차폐재는 많은 경우 방사선으로부터 신체를 보호하기 위해 방사선 차폐복의 형태로 가공되어 사용된다.A radiation shielding material is required to protect humans and the environment from such a disadvantageous effect of radiation, and in many cases, a radiation shielding material is processed and used in the form of a radiation shielding suit to protect the body from radiation.
현재까지 사용되는 방사선 차폐재 중에서 가장 보편적인 방사선 차폐 물질은 납(lead)이지만 장기간 반복적으로 접촉하는 경우 인체에 대하여 독성을 나타낼 뿐만 아니라 방사선 차폐복으로 이용하기에는 무게가 무겁고 장시간 착용시 인체에 부담이 되며 또한, 고분자복합재료에 비해 가공성과 유연성이 떨어진다는 단점을 지닌다.Among the radiation shielding materials used so far, the most common radiation shielding material is lead, but it is not only toxic to the human body when contacted repeatedly for a long period of time, it is heavy to use as a radiation shielding clothing, and it is a burden on the human body when worn for a long time. In addition, it has the disadvantage of inferior processability and flexibility compared to polymer composite materials.
개시된 내용은 산란 엑스선 흡수 및 고준위 감마선을 감쇠하는 하이브리드 무연 방사선 차폐재 및 방사선 차폐복을 제공하고자 하는 것이다. Disclosed is to provide a hybrid lead-free radiation shielding material and a radiation shielding suit that absorbs scattered X-rays and attenuates high-level gamma rays.
하나의 일 실시예로서 이 개시의 내용은 산란 방사선 흡수 조성물 및 폴리우레탄으로 이루어지는 외층과 상기 외층의 일면에 적층되며, 감마선 차폐 조성물 및 폴리클로로프렌으로 이루어지는 내층을 포함하는 방사선 차폐재에 대해 기술하고 있다.As an embodiment, the content of this disclosure describes a radiation shielding material comprising an outer layer made of a scattered radiation absorbing composition and polyurethane and an inner layer made of a gamma ray shielding composition and polychloroprene, which is laminated on one surface of the outer layer.
바람직하기로는, 상기 외층과 상기 내층으로 이루어진 적층체의 상부면과 하부면 중 적어도 일면에 방수천 또는 부직포가 열 접착하여 형성된 외피층이 포함될 수 있다.Preferably, an outer skin layer formed by thermally bonding a waterproof cloth or a nonwoven fabric to at least one of an upper surface and a lower surface of the laminate comprising the outer layer and the inner layer may be included.
더 바람직하기로는, 상기 산란 방사선 흡수 조성물은 황산바륨, 산화비스무트 화합물 및 산화마그네슘으로 이루어지는 군에서 선택되는 적어도 하나, 산화철, 탄산스트론튬 및 산화그래핀을 포함할 수 있다.More preferably, the scattered radiation absorbing composition may include at least one selected from the group consisting of barium sulfate, a bismuth oxide compound, and magnesium oxide, iron oxide, strontium carbonate, and graphene oxide.
더욱 바람직하기로는, 상기 감마선 차폐 조성물은 산화비스무트 화합물 및 텅스텐 중 적어도 하나, 황산바륨 및 산화마그네슘 중 적어도 하나, 산화철, 탄산스트론튬 및 산화그래핀을 포함할 수 있다.More preferably, the gamma ray shielding composition may include at least one of a bismuth oxide compound and tungsten, at least one of barium sulfate and magnesium oxide, iron oxide, strontium carbonate, and graphene oxide.
더욱 더 바람직하기로는, 상기 산화철, 탄산스트론튬 및 산화그래핀은 고주파유도 가열에 의해 소결된 것일 수 있다.Even more preferably, the iron oxide, strontium carbonate, and graphene oxide may be sintered by high frequency induction heating.
다른 실시예로서 이 개시의 내용은 상기 방사선 차폐재를 이용하여 착용자의 신체를 가리도록 구성된 방사선 차폐복에 대해 기술하고 있다.As another embodiment, the content of this disclosure describes a radiation shielding suit configured to cover a wearer's body using the radiation shielding material.
바람직하기로는, 갑상선 주위 차폐를 위한 덮개가 더 포함되는 것일 수 있다.Preferably, a cover for shielding around the thyroid gland may be further included.
이상에서와 같은 방사선 차폐재 및 이를 이용한 방사선 차폐복은 고주파유도 가열에 의한 소결로 생산성을 향상시킬 수 있고, 엑스선 및 감마선을 동시에 차폐할 수 있는 효과를 가지면서도, 납을 사용하지 않아 가볍고, 변형성과 가공성이 우수하다. The radiation shielding material described above and the radiation shielding clothing using the same can improve productivity by sintering by high-frequency induction heating, and have the effect of simultaneously shielding X-rays and gamma rays, and are light and deformable because they do not use lead. Excellent processability.
도 1은 개시된 일 실시예에 따른 방사선 차폐재를 나타낸 분해사시도이다.
도 2는 개시된 다른 실시예에 따른 방사선 차폐재를 나타낸 분해사시도이다.
도 3은 개시된 방사선 차폐재를 이용한 방사선 차폐복의 원단이다.
도 4는 개시된 또 다른 실시예에 따른 방사선 차폐복이다.
도 5는 개시된 방사선 차폐복을 착용자가 착용한 상태의 정면도, 측면도, 후면도이다.
도 6은 개시된 방사선 차폐재 중 외층의 제조 방법 공정도이다.
도 7은 개시된 방사선 차폐재 중 내층의 제조 방법 공정도이다.
도 8은 개시된 방사선 차폐재의 시험분석표이다.
도 9는 개시된 방사선 차폐재의 외층의 시험분석표이다.
도 10은 개시된 방사선 차폐재의 물리적, 화학적 내환경성 실험결과표이다.1 is an exploded perspective view showing a radiation shielding material according to an embodiment disclosed.
2 is an exploded perspective view showing a radiation shielding material according to another disclosed embodiment.
3 is a fabric of a radiation shielding suit using the disclosed radiation shielding material.
4 is a radiation shielding suit according to another disclosed embodiment.
5 is a front view, a side view, and a rear view of the wearer wearing the disclosed radiation shielding suit.
6 is a flowchart illustrating a method of manufacturing an outer layer of the disclosed radiation shielding material.
7 is a flowchart illustrating a method of manufacturing an inner layer of the disclosed radiation shielding material.
8 is a test analysis table of the disclosed radiation shielding material.
9 is a test analysis table of the outer layer of the disclosed radiation shielding material.
10 is a table of physical and chemical environmental resistance test results of the disclosed radiation shielding material.
이하에는, 본 발명의 바람직한 실시예와 각 성분의 물성을 상세하게 설명하되, 이는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 발명을 용이하게 실시할 수 있을 정도로 상세하게 설명하기 위한 것이지, 이로 인해 본 발명의 기술적인 사상 및 범주가 한정되는 것을 의미하지는 않는다.Hereinafter, a preferred embodiment of the present invention and the physical properties of each component will be described in detail, but this is for explaining in detail enough that one of ordinary skill in the art can easily carry out the invention, This does not mean that the technical spirit and scope of the present invention are limited.
도 1 또는 도2를 참조하면, 개시된 방사선 차폐재는 산란 방사선 흡수 조성물과 폴리우레탄을 혼합, 성형하여 이루어지는 외층(10)과 상기 외층의 일면에 적층되며, 감마선 차폐 조성물과 폴리클로로프렌(polychloroprene(chloroprene))으로 이루어지는 내층(20)을 포함한다.1 or 2, the disclosed radiation shielding material is laminated on one surface of the
상기 외층(10)과 상기 내층(20)으로 이루어진 적층체의 상부면과 하부면 중 적어도 일면에 방수천 또는 부직포가 열 접착하여 형성된 외피층(30)이 더 형성될 수 있다.An
이때 상기 부직포는 폴리에틸렌테레프탈레이트(polyethylene terephthalate,PET) 부직포인 것이 바람직하다.At this time, the nonwoven fabric is preferably a polyethylene terephthalate (PET) nonwoven fabric.
상기 외층(10) 및 내층(20)의 두께는 합하여 2.0mm 이하이며, 바람직하게는 1.5mm 이하이다. 또한 상기 외피층은 0.5mm 이하인 것이 바람직하다.The total thickness of the
상기 외층(10) 및 내층(20)의 두께 합이 2.0mm를 초과하면 방사성 차폐재를 이용한 성형품 또는 디바이스의 활용도가 떨어진다.If the sum of the thicknesses of the
상기 외층(10)의 산란 방사선 흡수 조성물은 황산바륨(Barium sulfate), 산화마그네슘(Magnesium oxide) 및 산화비스무트(Bismuth oxide) 중 적어도 하나, 산화철(Iron oxide), 탄산스트론튬(Strontianite) 및 산화그래핀(Graphene Oxide)을 포함한다.The scattered radiation absorbing composition of the
바람직하게는 황산바륨 30 내지 60 중량부 또는/및 산화비스무트 화합물 30 내지 60 중량부, 그리고 탄산스트론튬 3 내지 25 중량부, 산화철 5 내지 20 중량부 및 산화그래핀 0.001 내지 5 중량부를 포함한다.Preferably, 30 to 60 parts by weight of barium sulfate or/and 30 to 60 parts by weight of a bismuth oxide compound, and 3 to 25 parts by weight of strontium carbonate, 5 to 20 parts by weight of iron oxide, and 0.001 to 5 parts by weight of graphene oxide are included.
특히 바람직하게는 황산바륨 35 내지 45 중량부 또는/및 산화비스무트 화합물 30 내지 50 중량부, 그리고 탄산스트론튬 3 내지 25 중량부, 산화철 10 내지 15 중량부 및 산화그래핀 0.015 내지 1 중량부를 포함한다.Particularly preferably, 35 to 45 parts by weight of barium sulfate or/and 30 to 50 parts by weight of a bismuth oxide compound, and 3 to 25 parts by weight of strontium carbonate, 10 to 15 parts by weight of iron oxide, and 0.015 to 1 parts by weight of graphene oxide are included.
상기 조성비를 가지는 경우 친환경적이고, 비중이 4.0으로 납(Lead)을 고무등과 하이브리드화하여 제조한 경우의 비중 5.0보다 가벼우며, 부드러워 변형성과 가공성이 우수하다.When it has the above composition ratio, it is eco-friendly, its specific gravity is 4.0, and it is lighter than the specific gravity of 5.0 when it is manufactured by hybridizing lead with rubber, etc., and it is soft and has excellent deformability and workability.
또한 상기 탄산스트론튬, 산화철 및 산화그래핀은 고주파유도 가열에 의하여 소결하는 것이 좋다. 고주파유도 가열에 의하여 소결하는 경우 소결 시간이 2 내지 5분으로, 기존 전기로에서 소결하는 5 내지 16시간에 비하여 소결 시간은 줄일 수 있어 생산성이 매우 향상된다.In addition, the strontium carbonate, iron oxide, and graphene oxide are preferably sintered by high-frequency induction heating. In the case of sintering by high frequency induction heating, the sintering time is 2 to 5 minutes, and the sintering time can be shortened compared to 5 to 16 hours of sintering in an existing electric furnace, thereby greatly improving productivity.
상기 외층(10)의 제조방법은 황산바륨, 산화마그네슘 및 산화비스무트 중 적어도 하나를 혼합 및 분쇄하여 입도를 조절하는 제1혼합분쇄단계(S100), 산화철, 탄산스트론튬 및 산화그래핀을 혼합 및 나노화를 위해 분쇄하는 제2혼합분쇄단계(S130), 제2혼합분쇄단계를 거친 조성물을 1,000 내지 1,600℃로 2 내지 5 분 소결하는 소결단계(S150), 소결단계 후 제1혼합분쇄단계를 거친 조성물과 소결단계를 거친 조성물을 폴리우레탄과 혼합 및 성형하는 혼합성형단계(S170)를 포함한다.The manufacturing method of the
상기 제1 및 제2혼합분쇄단계(S100, S130)는 볼밀(ball mill)등의 분쇄기를 이용할 수 있고, 분산효과와 입도의 균등을 위하여 계면활성제를 사용할 수도 있다. 제1혼합분쇄단계(S100)의 경우 입도 크기는 1 내지 3 ㎛가 바람직하고, 제2혼합분쇄단계(S130)의 경우 입도 크기는 1 내지 10 nm로 하는 것이 바람직하다. 상기 제1 및 제2혼합분쇄단계를 통하여 입도 크기를 줄이면 동일한 무게 대비 분산량이 증가하므로 방사선 차폐효과를 증대 시킬 수 있다. 또한 제2혼합분쇄단계는 나노화를 위하여 최대한 입도크기를 줄이는 것이 바람직하다.In the first and second mixing and pulverizing steps S100 and S130, a grinder such as a ball mill may be used, and a surfactant may be used for dispersing effect and equalization of particle size. In the case of the first mixing and pulverizing step (S100), the particle size is preferably 1 to 3 μm, and in the case of the second mixing and pulverizing step (S130), the particle size is preferably 1 to 10 nm. If the particle size is reduced through the first and second mixing and pulverizing steps, since the dispersion amount is increased relative to the same weight, the radiation shielding effect can be increased. In addition, in the second mixing and pulverizing step, it is preferable to reduce the particle size as much as possible for nano-ization.
상기 소결단계(S150)는 전기로 등을 이용할 수 있으나, 고주파유도 가열에 의한 소결 공정을 이용하는 경우 기존 5 내지 16시간 소요되는 소결공정을 2 내지 5분으로 단축할 수 있으므로 고주파유도 가열에 의한 소결을 하는 것이 바람직하다. 또한, 소결 분위기는 불활성 가스 분위기가 좋다.The sintering step (S150) may use an electric furnace, but if the sintering process by high frequency induction heating is used, the sintering process that takes 5 to 16 hours can be shortened to 2 to 5 minutes, so sintering by high frequency induction heating It is desirable to do. In addition, the sintering atmosphere is preferably an inert gas atmosphere.
상기 소결단계를 통하여 감마선 산란 흡수량을 향상 시킬 수 있으며 공정 시간을 매우 단축할 수 있다.Through the sintering step, the absorption amount of gamma ray scattering can be improved, and the process time can be greatly shortened.
상기 외층(10)을 구성하는 산란 방사선 흡수 조성물과 폴리우레탄의 중량비는 92:8 내지 98: 2인 것이 바람직하다. 상기 조성비로 가공성 및 생산성 측면을 고려하면서도, 방사선 차폐 효율을 극대화할 수 있다.It is preferable that the weight ratio of the scattered radiation absorbing composition constituting the
상기 내층(20)의 감마선 차폐 조성물은 산화비스무트 및 텅스텐(Tungsten) 중 적어도 하나, 황산바륨 및 산화마그네슘 중 적어도 하나, 탄산스트론튬, 산화철 및 산화그래핀을 포함한다.The gamma ray shielding composition of the
바람직하게는 산화비스무트 화합물 30 내지 60 중량부 또는/및 텅스텐 30 내지 95 중량부, 황산바륨 30 내지 60 중량부 또는/및 산화마그네슘 10 내지 25 중량부, 탄산스트론튬 3 내지 25 중량부, 산화철 5 내지 20 중량부 및 산화그래핀 0.001 내지 3 중량부를 포함한다.Preferably, 30 to 60 parts by weight of a bismuth oxide compound or/and 30 to 95 parts by weight of tungsten, 30 to 60 parts by weight of barium sulfate or/and 10 to 25 parts by weight of magnesium oxide, 3 to 25 parts by weight of strontium carbonate, 5 to 25 parts by weight of
특히 바람직하게는 산화비스무트 화합물 30 내지 50 중량부 또는/및 텅스텐 40 내지 90 중량부, 황산바륨 35 내지 50 중량부 또는/및 산화마그네슘 15 내지 25 중량부, 탄산스트론튬 3 내지 10 중량부, 산화철 10 내지 15 중량부 및 산화그래핀 0.015 내지 1 중량부를 포함한다.Particularly preferably, 30 to 50 parts by weight of a bismuth oxide compound or/and 40 to 90 parts by weight of tungsten, 35 to 50 parts by weight of barium sulfate or/and 15 to 25 parts by weight of magnesium oxide, 3 to 10 parts by weight of strontium carbonate, 10 parts by weight of iron oxide To 15 parts by weight and 0.015 to 1 part by weight of graphene oxide.
또한, 상기 탄산스트론튬, 산화철 및 산화그래핀은 고주파유도 가열에 의하여 소결하는 것이 좋다. 고주파유도 가열에 의하여 소결하는 경우 소결 시간이 2 내지 5분으로, 기존 전기로에서 소결하는 5 내지 16시간에 비하여 소결 시간은 줄일 수 있어 생산성이 매우 향상된다.In addition, the strontium carbonate, iron oxide, and graphene oxide are preferably sintered by high-frequency induction heating. In the case of sintering by high frequency induction heating, the sintering time is 2 to 5 minutes, and the sintering time can be shortened compared to 5 to 16 hours of sintering in an existing electric furnace, thereby greatly improving productivity.
상기 조성비를 가지는 경우 가공성이 우수하며, 감마선을 양호하게 차폐할 수 있으며, 비중이 가벼워 성형품 및 디바이스로서 활용성이 우수하다.When it has the above composition ratio, it is excellent in processability, it can shield gamma rays well, and its specific gravity is light, so it is excellent in usability as molded products and devices.
상기 감마선 차폐 조성물의 성상은 차폐재의 용도에 따라 입상, 필름, 시트, 원단등이 될 수 있으며, 여러 차폐 용도에 사용이 가능하다. 예를 들면, 방호 에이프런, 의료용 에이프런, 차폐복, 가운, 벽지, 건축 자재, 의료기기 등에 사용할 수 있다.The properties of the gamma ray shielding composition may be granular, film, sheet, fabric, etc. depending on the use of the shielding material, and can be used for various shielding purposes. For example, it can be used for protective aprons, medical aprons, shielding clothes, gowns, wallpaper, building materials, medical devices, and the like.
또한, 조성물 단독으로 사용하거나 물 또는 유기 용제, 계면활성제, 수지 바인더, 무기 입자, 유기 입자 등의 첨가제와 함께 사용할 수 있다.In addition, the composition may be used alone or in combination with additives such as water or organic solvents, surfactants, resin binders, inorganic particles, and organic particles.
상기 내층(20)의 제조방법은 산화비스무트 화합물 및 텅스텐 중 적어도 하나, 황산바륨 및 산화마그네슘의 적어도 하나를 혼합 및 분쇄하여 입도를 조절하는 제1혼합분쇄단계(S200), 산화철, 탄산스트론튬 및 산화그래핀을 혼합 및 나노화를 위해 분쇄하는 제2혼합분쇄단계(S230), 제2혼합분쇄단계를 거친 조성물을 1,000 내지 1,600℃로 2 내지 5 분 소결하는 소결단계(S250), 소결단계 후 제1혼합분쇄단계를 거친 조성물과 소결단계를 거친 조성물을 폴리클로로프렌(polychloroprene(chloroprene))과 혼합 및 성형하는 혼합성형단계(S270)를 포함한다.The manufacturing method of the
상기 제1 및 제2혼합분쇄단계(S200,S230)는 볼밀(ball mill)등을 이용할 수 있고, 분산효과와 입도의 균등을 위하여 계면활성제를 사용할 수도 있다. In the first and second mixing and pulverizing steps S200 and S230, a ball mill or the like may be used, and a surfactant may be used for dispersing effect and equalization of particle size.
이때, 제1혼합분쇄단계(S200)의 경우 입도 크기는 1 내지 3 ㎛가 바람직하고, 제2혼합분쇄단계(S230)의 경우 입도 크기는 1 내지 10 nm로 하는 것이 바람직하다. 상기 제1 및 제2혼합분쇄단계를 통하여 입도 크기를 줄이면 동일한 무게 대비 분산량이 증가하므로 방사선 차폐효과를 증대 시킬 수 있다. 또한 제2혼합분쇄단계는 나노화를 위하여 최대한 입도크기를 줄이는 것이 바람직하다.At this time, in the case of the first mixing and pulverizing step (S200), the particle size is preferably 1 to 3 μm, and in the case of the second mixing and pulverizing step (S230), the particle size is preferably 1 to 10 nm. When the particle size is reduced through the first and second mixing and pulverizing steps, since the dispersion amount is increased relative to the same weight, the radiation shielding effect can be increased. In addition, in the second mixing and pulverizing step, it is desirable to reduce the particle size as much as possible for nano-ization.
상기 소결단계(S250)는 전기로 등을 이용할 수 있으나, 고주파유도 가열에 의한 소결 공정을 이용하는 경우 기존 5 내지 16시간 소요되는 소결공정을 2 내지 5분으로 단축할 수 있으므로 고주파유도 가열에 의한 소결을 하는 것이 바람직하다. 또한, 소결 분위기는 불활성 가스 분위기가 좋다.The sintering step (S250) may use an electric furnace, but if the sintering process by high frequency induction heating is used, the sintering process that takes 5 to 16 hours can be shortened to 2 to 5 minutes, so sintering by high frequency induction heating It is desirable to do. In addition, the sintering atmosphere is preferably an inert gas atmosphere.
상기 소결단계(S250)는 금속 간 반응에 의하여 전자 이동이 용이하여 전리 흡수 작용을 촉진하므로 감마선 차폐 능력을 향상 시킬 수 있다.The sintering step (S250) facilitates the movement of electrons by a reaction between metals, thereby promoting an ionization absorption effect, thereby improving gamma ray shielding ability.
내층(20)을 구성하는 감마선 차폐 조성물과 폴리클로로프렌의 중량비는 92:8 내지 98:2인 것이 바람직하다. 상기 조성비로 가공성 및 생산성 측면을 고려하면서도, 방사선 차폐 효율을 극대화할 수 있다.It is preferable that the weight ratio of the gamma-ray shielding composition constituting the
방사선 차폐재의 제조방법은 먼저 상기 외층(10)을 제조한 후, 내층(20) 제조 시 혼합성형공정에서 외층(10)을 적층하고 열과 압력을 가하여 가교 반응에 의하여 제조한다. 가교 반응시 온도는 160 내지 180 ℃가 바람직하다. 이때, 외피층(30)을 더 포함하는 경우 방수천 또는 부직포를 카렌다 롤을 이용하여 열 접착한다.In the method of manufacturing the radiation shielding material, first, the
이때, 상기 외층(10)과 내층(20)의 중량비는 40:60 내지 50:50인 것이 바람직하다.In this case, the weight ratio of the
제조된 방사선 차폐재의 외층(10)은 산란 방사선을 흡수하고, 내층(20)은 감마선을 차폐한다. 감마선이 물질에 접촉하면 광전 효과 및 컴프턴 산란(Compton scattering)으로 산란 방사선을 발생시키는데 개시된 방사선 차폐재는 내층에 의하여 감마선을 차폐시 생기는 산란 방사선을 외층(10)에 의하여 효과적으로 흡수할 수 있다. 특히, 철 성분과 스트론튬 성분을 하니웰 구조를 가지는 산화그래핀과 고온 아몰퍼스(amorphous) 영역에서 물리적 반응을 시켜 기가 헤르츠(giga HZs)대 전자파 전리선을 차단 및 흡수하는 효과가 우수하다.The
따라서, 상기 방사선 차폐재를 이용하여 방사선 구역에서 방사선 차폐를 위한 방사선 차폐복으로 활용이 가능하다. 이때, 방사선 차폐재를 방사선 차폐복으로 활용하기 위해서는 양호한 부착성을 위하여 네오디움 자석(neodymium magnet)을 방사선 차폐재의 외층(10)과 내층(20) 사이에 삽입하는 것이 바람직하다.Therefore, it is possible to use the radiation shielding material as a radiation shielding suit for radiation shielding in a radiation area. At this time, in order to use the radiation shielding material as a radiation shielding suit, it is preferable to insert a neodymium magnet between the
또한, 상기 방사선 차폐복을 갑상선 주위의 방사선 차폐를 위하여 덮개를 더 포함할 수 있으며, 갑상선과 임파선 주위에 소아 턱 받이용 띠 모양으로 착용이 용이하게 하는 것이 바람직하다. 또한, 목 부분의 착용감을 부드럽게 하기 위하여 얇은 방사선 차폐재를 2 또는 3겹으로 묶어서 구성할 수 있다.In addition, the radiation shielding suit may further include a cover for radiation shielding around the thyroid gland, and it is preferable to easily wear it in the shape of a pediatric bib around the thyroid gland and lymph nodes. In addition, in order to soften the fit of the neck, it can be configured by bundling a thin radiation shielding material in two or three layers.
개시된 방사선 차폐재를 이용한 방사선 차폐복은 필요에 따라 외층(10) 또는 내층(20) 중 하나의 층만을 사용하여 단독 또는 외피층과 결합한 형태로 방사선 차폐복의 원단으로 사용할 수 있다.The radiation shielding suit using the disclosed radiation shielding material may be used as a fabric of a radiation shielding suit in a form in which only one of the
<실시예 1> 외층의 제조<Example 1> Preparation of outer layer
산화마그네슘 2.58 중량부, 삼산화비스무트 44.85 중량부, 황산바륨 37.20 중량부를 볼밀에 넣어 1시간 혼합 했다.2.58 parts by weight of magnesium oxide, 44.85 parts by weight of bismuth trioxide, and 37.20 parts by weight of barium sulfate were placed in a ball mill and mixed for 1 hour.
탄산스트론튬 10.22 중량부, 산화철 5.0 중량부 및 산화그래핀 0.15 중량부를 볼밀에 넣어 1시간 혼합 한 후. 고주파유도 가열 소결기에 넣어 질소 분위기로, 1600℃에서 5분 소결하였다. 소결 후, 상온에서 냉각하고 볼밀 혼합기에서 입자 크기 평균 값이 9nm 내지 10nm를 갖도록 분쇄 한 후, 조성물 전부를 폴리우레탄과 혼합하여 0.6mm의 외층을 제조하였다.After 10.22 parts by weight of strontium carbonate, 5.0 parts by weight of iron oxide, and 0.15 parts by weight of graphene oxide were put into a ball mill and mixed for 1 hour. It was put into a high-frequency induction heating sintering machine and sintered at 1600°C for 5 minutes in a nitrogen atmosphere. After sintering, cooling at room temperature and grinding in a ball mill mixer to have an average particle size of 9 nm to 10 nm, the entire composition was mixed with polyurethane to prepare an outer layer of 0.6 mm.
<실시예 2> 내층의 제조<Example 2> Preparation of inner layer
비스무트 32.58 중량부, 텅스텐 53.85 중량부 및 황산바륨 42.12 중량부를 볼밀에 넣어 1시간 혼합하였다. 탄산스트론튬 8.42 중량부, 산화철 5.0 중량부 및 산화그래핀 0,15 중량부를 볼밀에 넣어 1시간 혼합하였다. 혼합 후 고주파유도 가열 소결기를 이용하여 1600℃에서 약 5분 소결하고, 조성물 전부를 폴리클로로프렌과 혼합하여 1mm 내층을 제조하였다.32.58 parts by weight of bismuth, 53.85 parts by weight of tungsten, and 42.12 parts by weight of barium sulfate were put into a ball mill and mixed for 1 hour. 8.42 parts by weight of strontium carbonate, 5.0 parts by weight of iron oxide, and 0,15 parts by weight of graphene oxide were put into a ball mill and mixed for 1 hour. After mixing, sintering was performed at 1600° C. for about 5 minutes using a high frequency induction heating sintering machine, and the entire composition was mixed with polychloroprene to prepare a 1 mm inner layer.
<실시예 3><Example 3>
상기 실시예 1 외층의 두께를 1 mm로 제조한 후, 실시예 2에서 제조된 내층과 적층하여 2 mm의 방사선 차폐재를 제조하였다.After the thickness of the outer layer of Example 1 was prepared to be 1 mm, and laminated with the inner layer prepared in Example 2, a radiation shielding material of 2 mm was prepared.
<실시예 4><Example 4>
상기 실시예 1 외층의 두께를 1.5 mm로 제조하고, 실시예 2 내층의 두께를 1.5 mm로 제조한 후 적층하여 3 mm의 방사선 차폐재를 제조하였다.The thickness of the outer layer of Example 1 was prepared to be 1.5 mm, and the thickness of the inner layer of Example 2 was prepared to be 1.5 mm, and then laminated to prepare a radiation shielding material of 3 mm.
<시험예 1><Test Example 1>
원자력연구원/표준과학 연구원에 의뢰하여 실시예 1 내지 4의 시료에 감마선을 조사해, 차폐율을 측정했다. 비교예 1 내지 3은 납을 사용했을 때 차폐율이다. 결과는 [표 1]에 나타내었다.The samples of Examples 1 to 4 were irradiated with gamma rays by requesting the Atomic Energy Research Institute/Research Institute of Standards and Science to measure the shielding rate. Comparative Examples 1 to 3 are the shielding rates when lead is used. The results are shown in [Table 1].
[표 1][Table 1]
[표 1]에 나타난 바와 같이, 차폐율이 납에 비하여 상당히 우수한 것을 알 수 있다. 상기 감마선 차폐재는 비중이 납의 비중(11.34)보다도 가볍고, 부드러워 변형성과 가공성이 우수하며, 다양한 용도나 형태로 사용 가능하다.As shown in [Table 1], it can be seen that the shielding rate is considerably superior to that of lead. The gamma ray shielding material is lighter and softer than the specific gravity of lead (11.34), so that it has excellent deformability and workability, and can be used in various uses or forms.
10 ; 외층
20 ; 내층
30 ; 외피층
S100 ; 제1혼합분쇄단계(외층)
S130 ; 제2혼합분쇄단계(외층)
S150 ; 소결단계(외층)
S170 ; 혼합성형단계(외층)
S200 ; 제1혼합분쇄단계(내층)
S230 ; 제2혼합분쇄단계(내층)
S250 ; 소결단계(내층)
S270 ; 혼합성형단계(내층)10; Outer layer
20; Inner layer
30; Outer layer
S100; 1st mixing and grinding step (outer layer)
S130; 2nd mixing and grinding step (outer layer)
S150; Sintering step (outer layer)
S170; Mixed molding step (outer layer)
S200; 1st mixing and grinding step (inner layer)
S230; 2nd mixing and grinding step (inner layer)
S250; Sintering step (inner layer)
S270; Mixed molding step (inner layer)
Claims (15)
상기 외층의 일면에 형성되며, 감마선 차폐 조성물 및 폴리클로로프렌으로 이루어지는 내층;을 포함하는 방사선 차폐재.
An outer layer made of a scattered radiation absorbing composition and polyurethane; And
Radiation shielding material comprising; an inner layer formed on one surface of the outer layer and made of a gamma ray shielding composition and polychloroprene.
상기 외층과 상기 내층으로 이루어진 적층체의 상부면과 하부면 중 적어도 일면에 방수천 또는 부직포가 열 접착하여 형성된 외피층이 포함된 것을 특징으로 하는 방사선 차폐재.
The method according to claim 1,
A radiation shielding material comprising an outer skin layer formed by thermally bonding a waterproof cloth or a nonwoven fabric to at least one of an upper surface and a lower surface of the laminate comprising the outer layer and the inner layer.
상기 산란 방사선 흡수 조성물은 황산바륨, 산화비스무트 및 산화마그네슘으로 이루어지는 군에서 선택되는 적어도 하나, 산화철, 탄산스트론튬 및 산화그래핀을 포함하는 것을 특징으로 하는 방사선 차폐재.
The method according to claim 1,
The scattered radiation absorbing composition comprises at least one selected from the group consisting of barium sulfate, bismuth oxide, and magnesium oxide, iron oxide, strontium carbonate, and graphene oxide.
상기 감마선 차폐 조성물은 산화비스무트 화합물 및 텅스텐 중 적어도 하나, 황산바륨 및 산화마그네슘 중 적어도 하나, 산화철, 탄산스트론튬 및 산화그래핀을 포함하는 것을 특징으로 하는 방사선 차폐재.
The method according to claim 1,
The gamma-ray shielding composition comprises at least one of a bismuth oxide compound and tungsten, at least one of barium sulfate and magnesium oxide, iron oxide, strontium carbonate, and graphene oxide.
상기 산화철, 탄산스트론튬 및 산화그래핀은 고주파유도 가열에 의해 소결된 것을 특징으로 하는 방사선 차폐재.
The method according to claim 3 or 4,
The radiation shielding material, characterized in that the iron oxide, strontium carbonate and graphene oxide are sintered by high frequency induction heating.
상기 외층의 산란 방사선 흡수 조성물과 폴리우레탄의 중량비는 92:8 내지 98:2인 것을 특징으로 하는 방사선 차폐재.
The method according to claim 1,
Radiation shielding material, characterized in that the weight ratio of the scattered radiation absorbing composition of the outer layer and the polyurethane is 92:8 to 98:2.
상기 내층의 감마선 차폐 조성물과 폴리클로로프렌의 중량비는 92:8 내지 98:2인 것을 특징으로 하는 방사선 차폐재.
The method according to claim 1,
Radiation shielding material, characterized in that the weight ratio of the gamma-ray shielding composition and polychloroprene of the inner layer is 92:8 to 98:2.
상기 외층과 내층의 중량비는 40:60 내지 50:50 인 것을 특징으로 하는 방사선 차폐재.
The method according to claim 1,
Radiation shielding material, characterized in that the weight ratio of the outer layer and the inner layer is 40:60 to 50:50.
상기 외층과 내층 사이에 네오디움 자석이 삽입된 것을 특징으로 하는 방사선 차폐재.
The method according to claim 1,
A radiation shielding material, characterized in that a neodymium magnet is inserted between the outer layer and the inner layer.
A radiation shielding suit configured to cover the wearer's body by using the radiation shielding material of any one of claims 1 to 9.
상기 방사선 차폐복에 갑상선 주위 차폐를 위한 덮개가 더 포함되는 것을 특징으로 하는 방사선 차폐복.
The method of claim 10,
A radiation shielding suit, characterized in that the radiation shielding suit further comprises a cover for shielding around the thyroid gland.
(A) 황산바륨, 산화마그네슘 및 산화비스무트 중 적어도 하나를 분쇄하는 단계;
(B) 산화철, 탄산스트론튬 및 산화그래핀을 포함하는 조성물을 혼합 및 분쇄한 후 소결하는 단계;
(C) (A)단계를 거친 분쇄물과 (B)단계를 거친 소결물을 폴리우레탄과 혼합 및 성형하는 단계;
(D) 산화비스무트 및 텅스텐(Tungsten) 중 적어도 하나, 황산바륨 및 산화마그네슘 중 적어도 하나를 혼합 및 분쇄하는 단계;
(E) 산화철, 탄산스트론튬 및 산화그래핀을 포함하는 조성물을 혼합 및 분쇄한 후 소결하는 단계;
(F) (D)단계를 거친 분쇄물, (E)단계를 거친 소결물 및 폴리클로로프렌을 (C) 단계를 거친 성형물 상에서 혼합 및 가교 반응시키는 단계;
A method of manufacturing a radiation shielding material comprising the following steps:
(A) grinding at least one of barium sulfate, magnesium oxide and bismuth oxide;
(B) mixing and pulverizing a composition comprising iron oxide, strontium carbonate, and graphene oxide, followed by sintering;
(C) mixing and molding the crushed product through step (A) and the sintered product through step (B) with polyurethane;
(D) mixing and grinding at least one of bismuth oxide and tungsten, at least one of barium sulfate and magnesium oxide;
(E) mixing and pulverizing a composition containing iron oxide, strontium carbonate, and graphene oxide, followed by sintering;
(F) mixing and crosslinking the pulverized product through step (D), the sintered product through step (E) and polychloroprene on the molded product through step (C);
상기 (B) 또는 (E) 단계의 소결은 1,000 내지 1,600℃에서 2 내지 5 분 동안 고주파유도 가열에 의하여 이루어지는 것을 특징으로 하는 방사선 차폐재의 제조방법.
The method of claim 12,
The sintering of the step (B) or (E) is a method of manufacturing a radiation shielding material, characterized in that the sintering is performed by high-frequency induction heating at 1,000 to 1,600° C. for 2 to 5 minutes.
상기 (F)단계를 거친 성형물의 상부면과 하부면 중 적어도 일면에 방수천 또는 부직포를 열 접착하여 외피층을 형성하는 단계를 더 포함하는 것을 특징으로 하는 방사선 차폐재의 제조방법.
The method of claim 12,
The method of manufacturing a radiation shielding material, further comprising the step of forming an outer skin layer by thermally bonding a waterproof cloth or a nonwoven fabric to at least one of an upper surface and a lower surface of the molded product after step (F).
A radiation shielding suit configured to cover the wearer's body by using a radiation shielding material manufactured by the method of any one of claims 12 to 14.