KR20200126687A - Interior decoration for interior air quality improvement using environmentally friendly functional inorganic paint Embo wallpaper Finishing method - Google Patents

Interior decoration for interior air quality improvement using environmentally friendly functional inorganic paint Embo wallpaper Finishing method Download PDF

Info

Publication number
KR20200126687A
KR20200126687A KR1020190050643A KR20190050643A KR20200126687A KR 20200126687 A KR20200126687 A KR 20200126687A KR 1020190050643 A KR1020190050643 A KR 1020190050643A KR 20190050643 A KR20190050643 A KR 20190050643A KR 20200126687 A KR20200126687 A KR 20200126687A
Authority
KR
South Korea
Prior art keywords
weight
eco
inorganic paint
friendly functional
functional inorganic
Prior art date
Application number
KR1020190050643A
Other languages
Korean (ko)
Other versions
KR102241151B1 (en
Inventor
이희덕
김찬식
Original Assignee
주식회사 피움
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 피움 filed Critical 주식회사 피움
Priority to KR1020190050643A priority Critical patent/KR102241151B1/en
Publication of KR20200126687A publication Critical patent/KR20200126687A/en
Application granted granted Critical
Publication of KR102241151B1 publication Critical patent/KR102241151B1/en

Abstract

The present invention relates to an interior embossing wallpaper finishing construction method for indoor air quality improvement using an eco-friendly functional inorganic paint. The method comprises the steps of: (a) preparing an eco-friendly functional inorganic paint; (b) after the step (a), arranging an adherend of an indoor concrete surface to which the eco-friendly functional inorganic paint is to be applied; (c) after the step (b), constructing an embossing wallpaper having an uneven surface to the adherend; (d) after the step (c), enabling an application means to form an inclination angle of 40° to 50° with respect to the surface of the embossing wallpaper, and to apply the eco-friendly functional inorganic paint with a thickness of 0.1 mm to 0.5 mm when applying the paint once; (e) examining whether or not the eco-friendly functional inorganic paint applied to the adherend is applied evenly at the predetermined thickness; and (f) curing the surface of the embossing wallpaper applied with the eco-friendly functional inorganic paint.

Description

친환경 기능성 무기질 도료를 이용한 실내 공기질 개선용 인테리어 엠보 벽지 마감 시공방법{Interior decoration for interior air quality improvement using environmentally friendly functional inorganic paint Embo wallpaper Finishing method}Interior decoration for interior air quality improvement using environmentally friendly functional inorganic paint Embo wallpaper Finishing method}

본 발명은 친환경 기능성 무기질 도료를 이용한 실내 공기질 개선용 인테리어 엠보 벽지 마감 시공방법에 관한 것으로, 더욱 상세하게는 실내 벽면의 인테리어 마감시 요철면이 형성된 엠보 벽지의 표면에 도포하여 최종 마감면의 외관품질을 향상시키고, 엠보 벽지의 기본 성능을 극대화시킬 수 있음은 물론, 환경 유해물질의 흡착 및 흡방습, 항균, 항곰팡이 효과로 인한 세균 저항력을 높이고, 실내 공기환경을 지속적으로 쾌적하게 유지할 수 있는 친환경 기능성 무기질 도료를 이용한 실내 공기질 개선용 인테리어 엠보 벽지 마감 시공방법에 관한 것이다. The present invention relates to an interior embossing wallpaper finishing construction method for improving indoor air quality using an eco-friendly functional inorganic paint, and more specifically, the appearance quality of the final finished surface by applying it to the surface of the embossed wallpaper formed on the uneven surface when finishing the interior of the interior wall. It is an eco-friendly environment that can enhance the resistance of bacteria due to the adsorption and moisture absorption and desorption, antibacterial, and anti-fungal effects of environmentally harmful substances, as well as maximizing the basic performance of the embossed wallpaper, and continuously maintaining a pleasant indoor air environment. It relates to an interior embossing wallpaper finishing construction method for improving indoor air quality using functional inorganic paints.

일반적으로, 주택의 벽체가 시멘트를 주성분으로 하는 콘크리트 벽체인 경우 주택 시공 직후 VOC, 폼알데히드, 톨루엔, 벤젠, 자일렌, 암모니아, 라돈 등의 유해성분이 방출되는 것으로 알려져 있으며, 콘크리트 벽체를 외관상 아름답게 꾸미기 위해 사용되는 벽지의 부착시 벽지와 콘트리트 벽체 간의 결합력을 강화시키기 위해 포름알데히드 성분을 포함하는 접착제를 사용하고 있어서, 아토피, 천식, 두통, 소화불량 및 각종 기관지 질환을 유발함에 따라 이를 해결하기 위한 원인 규명과 대책 마련에 부심하고 있다.In general, if the wall of a house is a concrete wall with cement as its main component, it is known that harmful components such as VOC, formaldehyde, toluene, benzene, xylene, ammonia, and radon are released immediately after the construction of the house, and the concrete wall is decorated with a beautiful appearance. When attaching the wallpaper used for the purpose, an adhesive containing formaldehyde is used to strengthen the bonding strength between the wallpaper and the concrete wall, which causes atopy, asthma, headache, indigestion, and various bronchial diseases. They are striving to identify and prepare measures.

일 예로, 대한민국 공개특허 제10-2013-0121587호에는, 콘크리트 내지는 시멘트 표면에 마감제로 천연 광물인 양구 방산 백색 고령토에서 추출한 화이트이온미네랄과 백색 고령토 분말을 이용하여 액상세라믹 얇은 바름제를 사용 할 경우 실내 대기중에 함유된 냄새와 유해가스의 흡착율이 우수하며, 분진 발생을 억제해 주고, 다른 물리 화학적 특성이 저해됨이 없이 항균, 탈취작용과 원적외선 방출에 의한 인체의 건강한 삶을 유지하는데, 유익한 효과를 제공하는 천연 광물 양구 방산 백색 고령토에서 추출한 화이트 이온 미네랄과 백색 고령토 분말을 이용한 새 집 증후군 제거용 얇은 바름제로서의 액상 세라믹 조성물 및 그 제조방법이 게재된 바 있다. For example, in Korean Patent Application Publication No. 10-2013-0121587, when using a liquid ceramic thin varnish using white ion mineral and white kaolin powder extracted from white kaolin from Yanggu Bangsan, a natural mineral as a finishing agent on the surface of concrete or cement. It has excellent adsorption rate of odors and harmful gases contained in the indoor air, suppresses dust generation, and maintains a healthy life of the human body by antibacterial, deodorizing and far-infrared radiation without impairing other physicochemical properties. A liquid ceramic composition and a method for manufacturing the same as a thin coating agent for removing sick house syndrome using white ionic minerals and white kaolin powder extracted from white kaolin and white kaolin, a natural mineral provided, have been published.

그러나, 전술한 선행기술문헌에 의하면, 콘크리트 벽체에서 나오는 유해성분의 흡착 및 분해 성능 등이 건축자재가 갖는 기능성 측면에 대하여 상대적으로 미흡하고, 벽지 자체도 친환경적이라고 할 수 없으며, 콘크리트 벽체의 결로 현상에 의한 습기 문제 및 이로 인한 곰팡이 서식 문제 등을 근본적으로 해결이 어려운 문제점이 있다.However, according to the above-described prior art literature, the adsorption and decomposition performance of harmful components from the concrete wall is relatively insufficient in terms of the functionality of the building material, and the wallpaper itself cannot be said to be eco-friendly, and the condensation phenomenon of the concrete wall. There is a problem that it is difficult to fundamentally solve the moisture problem caused by the problem and the mold problem caused by it.

또한, 전술한 선행기술문헌의 경우, 액상 세라믹 조성물을 도포하기 위해서는 벽지와 콘크리트 표면 사이에 부직포의 시공이 동반되어야 하기 때문에 부직포를 접착하기 위한 추가 공정이 발생하게 되어 시공성이 떨어지는 문제점이 있다. In addition, in the case of the above-described prior art document, in order to apply the liquid ceramic composition, since the construction of the non-woven fabric must be accompanied between the wallpaper and the concrete surface, an additional process for adhering the non-woven fabric occurs, resulting in poor workability.

대한민국 공개특허 제10-2013-0121587호Republic of Korea Patent Publication No. 10-2013-0121587

이와 같은 문제점을 해결하기 위하여 본 발명은 전술한 배경기술에 의해서 안출된 것으로, 실내 벽면의 인테리어 마감시 요철면이 형성된 엠보 벽지의 표면에 도포하여 최종 마감면의 외관품질을 향상시키고, 엠보 벽지의 기본 성능을 극대화시킬 수 있는 친환경 기능성 무기질 도료를 이용한 실내 공기질 개선용 인테리어 엠보 벽지 마감 시공방법을 제공하는데 그 목적이 있다.In order to solve such a problem, the present invention was conceived by the above-described background technology, and applied to the surface of the embossed wallpaper on which the uneven surface is formed when interior finishing of the interior wall surface to improve the appearance quality of the final finished surface, and Its purpose is to provide an interior embossing wallpaper finishing construction method for improving indoor air quality using an eco-friendly functional inorganic paint that can maximize basic performance.

또한, 본 발명은 환경 유해물질의 흡착 및 흡방습, 항균, 항곰팡이 효과로 인한 세균 저항력 뿐만 아니라, 황사 및 미세먼지로 환기가 불가능한 실내 공기 정화 및 탈취가 이루어지도록 함으로써, 실내 공기환경을 지속적으로 쾌적하게 유지할 수 있는 친환경 기능성 무기질 도료를 이용한 실내 공기질 개선용 인테리어 엠보 벽지 마감 시공방법을 제공하는데 그 목적이 있다.In addition, the present invention provides not only bacterial resistance due to the adsorption, absorption and desorption of environmentally harmful substances, antibacterial, and antifungal effects, but also purifying and deodorizing indoor air that cannot be ventilated by yellow sand and fine dust, thereby continuously maintaining the indoor air environment. Its purpose is to provide an interior embossing wallpaper finishing construction method for improving indoor air quality using an eco-friendly functional inorganic paint that can keep comfortably.

또한, 본 발명은 엠보 벽지, 또는 콘크리트 벽면에 요철면을 형성하고, 상기 요철면 상에 무기질 도료 조성물을 도포함으로써, 요철면이 형성된 벽지, 또는 엠보 벽지의 사용 여부와 무관하게 최종 마감면의 외관품질을 향상시킬 수 있음은 물론, 시공 공정을 단순화하여 시공비를 절감할 수 있고, 도포 표면면적 향상을 통해 기본성능을 극대화시킬 수 있는 친환경 기능성 무기질 도료를 이용한 실내 공기질 개선용 인테리어 엠보 벽지 마감 시공방법을 제공하는데 그 목적이 있다.In addition, the present invention forms an uneven surface on the embossed wallpaper or concrete wall, and by applying an inorganic paint composition on the uneven surface, the appearance of the final finished surface regardless of whether the uneven surface is formed or the embossed wallpaper is used. Interior embossing wallpaper finishing construction method for indoor air quality improvement using eco-friendly functional inorganic paints that can improve quality, as well as simplify the construction process to reduce construction costs and maximize basic performance by improving the applied surface area Its purpose is to provide.

다만, 본 발명의 목적은 이에만 제한되는 것은 아니며, 명시적으로 언급하지 않더라도 과제의 해결수단이나 실시 형태로부터 파악될 수 있는 목적이나 효과도 이에 포함됨은 물론이다. However, the object of the present invention is not limited thereto, and objects or effects that can be grasped from the solutions or embodiments of the problem are also included therein even if not explicitly mentioned.

이와 같은 과제를 달성하기 위한 본 발명의 일 실시예에 따르면, (a) 친환경 기능성 무기질 도료를 제조하는 단계; (b) 상기 (a) 단계 이후, 친환경 기능성 무기질 도료를 도포할 실내 콘크리트 표면의 피착면을 정리하는 단계; (c) 상기 (b) 단계 이후, 표면에 요철면이 형성된 엠보 벽지를 상기 피착면에 시공하는 단계; (d) 상기 (c) 단계 이후, 도포수단을 상기 엠보 벽지의 표면과 40°~50°의 경사각을 이루도록 하고, 1회 도포 시 0.1mm ~ 0.5mm의 두께로 상기 친환경 기능성 무기질 도료를 도포하는 단계; (e) 피착면에 도포된 상기 친환경 기능성 무기질 도료가 일정한 두께로 평탄하게 도포가 이루어졌는지 여부를 검사하는 단계; 및 (f) 상기 친환경 기능성 무기질 도료가 도포된 엠보 벽지 표면의 보양이 이루어지도록 하는 단계;를 포함하는 것을 특징으로 한다.According to an embodiment of the present invention for achieving such a problem, (a) preparing an eco-friendly functional inorganic paint; (b) after step (a), arranging the adherend surface of the indoor concrete surface to which the eco-friendly functional inorganic paint is to be applied; (c) after the step (b), applying an embossed wallpaper with an uneven surface formed on the adherend surface; (d) After the step (c), the application means is made to form an inclination angle of 40° to 50° with the surface of the embossed wallpaper, and the eco-friendly functional inorganic paint is applied to a thickness of 0.1 mm to 0.5 mm when applied once. step; (e) examining whether or not the eco-friendly functional inorganic paint applied to the adherend is applied evenly to a predetermined thickness; And (f) maintaining the surface of the embossed wallpaper on which the eco-friendly functional inorganic paint is applied.

본 발명의 일 실시예에 따르면, 상기 (d) 단계는, 요철면이 형성된 엠보 벽지의 표면에 도포가 이루어질 때, 색상안료를 더 혼합하여 도포하는 것을 특징으로 한다.According to an embodiment of the present invention, the step (d) is characterized in that when the application is made on the surface of the embossed wallpaper on which the uneven surface is formed, a color pigment is further mixed and applied.

본 발명의 일 실시예에 따르면, 상기 (a) 단계에 있어서, (a1) 규산 소다 15중량% ~ 60중량%와, 규산 칼륨 15중량% ~60중량%와, 규산 리튬 5중량% ~10중량%를 교반하여 액상 결합제를 제조하는 단계; (a2) 활성탄, 실리카겔, 맥반석, 펄라이트, 버미큘라이트(Vermiculite), 규조토, 제올라이트가 일정 중량비로 혼합되는 다공성 무기물과, 은(Ag), 아연(Zn)이 일정 중량비로 혼합되는 무기 항균제를 각각 제조하는 단계; (a3) 상기 다공성 무기물 및 무기 항균제와 글리신(Glycine), 다이에틸렌트라이아민(Deithylenetriamine), 하이드록실아민(Hydroxyamine), 사이클로덱스트린(Cyclodextrin), 요소(Urea)가 혼합되게 구성되며, 파우더 혼합물의 총 중량에 있어서, 상기 글리신(Glycine), 다이에틸렌트라이아민(Deithylenetriamine), 하이드록실아민(Hydroxyamine), 사이클로덱스트린(Cyclodextrin) 및 요소(Urea)를 각각 일정 중량비로 혼합하여 파우더 혼합물을 제조하는 단계; 및 (a4) 상기 액상 결합제 및 상기 파우더 혼합물에 D-소르비톨(D-Sorbitol)를 일정 중량비로 혼합하여 친환경 기능성 무기질 도료를 제조하는 단계;를 포함하는 것을 특징으로 한다.According to an embodiment of the present invention, in the step (a), (a1) 15% to 60% by weight of sodium silicate, 15% to 60% by weight of potassium silicate, and 5% to 10% by weight of lithium silicate Stirring% to prepare a liquid binder; (a2) To prepare an inorganic antimicrobial agent in which activated carbon, silica gel, elvan, pearlite, vermiculite, diatomaceous earth, and zeolite are mixed in a certain weight ratio, and silver (Ag) and zinc (Zn) are mixed in a certain weight ratio. step; (a3) The porous inorganic material and inorganic antibacterial agent and glycine, diethylenetriamine, hydroxylamine, cyclodextrin, and urea are mixed. In terms of weight, preparing a powder mixture by mixing the glycine (Glycine), diethylenetriamine (Deithylenetriamine), hydroxylamine (Hydroxyamine), cyclodextrin (Cyclodextrin) and urea (Urea) in a predetermined weight ratio, respectively; And (a4) preparing an eco-friendly functional inorganic paint by mixing D-Sorbitol with the liquid binder and the powder mixture at a predetermined weight ratio.

본 발명의 일 실시예에 따르면, 상기 무기질 도료는 총 중량에 있어서, 상기 액상 결합제 30중량% ~70중량%, 상기 파우더 혼합물 25중량% ~ 60중량%, 1중량% ~10중량%의 D-소르비톨(D-Sorbitol)로 구성되는 것을 특징으로 한다.According to an embodiment of the present invention, the inorganic paint is based on the total weight of the liquid binder 30% to 70% by weight, the powder mixture 25% to 60% by weight, 1% to 10% by weight of D- It is characterized by consisting of sorbitol (D-Sorbitol).

본 발명의 일 실시예에 따르면, 상기 파우더 혼합물은, 다공성 무기물 40.0중량% ~99.0중량%와, 무기 항균제 0.5중량% ~ 10중량%와, 글리신(Glycine) 0.1중량% ~ 5.0중량%와, 다이에틸렌트라이아민(Deithylenetriamine) 0.1중량% ~ 5.0중량%와, 하이드록실아민(Hydroxyamine) 0.1중량% ~ 5.0중량%와, 사이클로덱스트린(Cyclodextrin) 0.1중량% ~ 5.0중량%와, 요소(Urea) 0.1중량% ~ 5.0중량%로 이루어지는 것을 특징으로 한다.According to an embodiment of the present invention, the powder mixture comprises 40.0% by weight to 99.1% by weight of a porous inorganic material, 0.5% by weight to 10% by weight of an inorganic antimicrobial agent, 0.1% by weight to 5.0% by weight of glycine, and Ethylene triamine (Deithylenetriamine) 0.1% to 5.0% by weight, hydroxylamine (Hydroxyamine) 0.1% to 5.0% by weight, cyclodextrin (Cyclodextrin) 0.1% to 5.0% by weight, and urea 0.1% by weight It is characterized in that consisting of% ~ 5.0% by weight.

이와 같은 본 발명의 실시예에 의하면, 실내 벽면의 인테리어 마감시 요철면이 형성된 엠보 벽지의 표면에 도포하여 최종 마감면의 외관품질을 향상시키고, 엠보 벽지의 기본 성능을 극대화시킬 수 있는 효과가 있다.According to such an embodiment of the present invention, it is possible to improve the appearance quality of the final finished surface and maximize the basic performance of the embossed wallpaper by applying it to the surface of the embossed wallpaper on which the uneven surface is formed when the interior of the interior wall of the interior is finished. .

또한, 본 발명의 실시예에 의하면, 환경 유해물질의 흡착 및 흡방습, 항균, 항곰팡이 효과로 인한 세균 저항력 뿐만 아니라, 황사 및 미세먼지로 환기가 불가능한 실내 공기 정화 및 탈취가 이루어지도록 함으로써, 실내 공기환경을 지속적으로 쾌적하게 유지할 수 있는 효과가 있다.In addition, according to an embodiment of the present invention, indoor air purification and deodorization that cannot be ventilated by yellow sand and fine dust as well as bacteria resistance due to the adsorption and absorption and desorption of environmentally harmful substances, antibacterial, and anti-fungal effects are performed. It has the effect of continuously maintaining a pleasant air environment.

또한, 본 발명의 실시예에 의하면, 엠보 벽지, 또는 콘크리트 벽면에 요철면을 형성하고, 상기 요철면 상에 무기질 도료 조성물을 도포함으로써, 요철면이 형성된 엠보 벽지의 사용 여부와 무관하게 최종 마감면의 외관품질을 향상시킬 수 있음은 물론, 시공 공정을 단순화하여 시공비를 절감할 수 있고, 도포 표면면적 향상을 통해 기본성능을 극대화시킬 수 있는 효과가 있다.In addition, according to an embodiment of the present invention, by forming an embossed wallpaper or an uneven surface on a concrete wall, and applying an inorganic paint composition on the uneven surface, the final finished surface regardless of whether or not the embossed wallpaper with the uneven surface is used. Not only can the exterior quality of the product be improved, but also construction costs can be reduced by simplifying the construction process, and the basic performance can be maximized by improving the coated surface area.

더불어, 본 발명의 다양하면서도 유익한 장점과 효과는 상술한 내용에 한정되지 않으며, 본 발명의 구체적인 실시 형태를 설명하는 과정에서 보다 쉽게 이해될 수 있을 것이다. In addition, various and beneficial advantages and effects of the present invention are not limited to the above description, and will be more easily understood in the course of describing specific embodiments of the present invention.

도 1은 본 발명의 일 실시예에 따른 친환경 기능성 무기질 도료를 이용한 실내 공기질 개선용 인테리어 엠보 벽지 마감 시공방법을 나타낸 순서도,
도 2는 본 발명의 일 실시예에 따른 친환경 기능성 무기질 도료의 유해물질 흡착율 시험, 흡방습 시험, 항균 시험, 항곰팡이 시험 결과를 나타낸 표이다.1 is a flow chart showing a method of finishing interior embossed wallpaper for improving indoor air quality using an eco-friendly functional inorganic paint according to an embodiment of the present invention;
2 is a table showing the results of a harmful substance adsorption rate test, moisture absorption and desorption test, antibacterial test, and anti-fungal test of an eco-friendly functional inorganic paint according to an embodiment of the present invention.

이하, 본 발명의 바람직한 실시예를 첨부된 도면들을 참조하여 상세히 설명한다. 우선 각 도면의 구성요소들에 참조 부호를 부가함에 있어서, 동일한 구성요소들에 대해서는 비록 다른 도면상에 표시되더라도 가능한 동일한 부호를 가지도록 하고 있음에 유의해야 한다. 또한, 본 발명을 설명함에 있어, 관련된 공지 구성 또는 기능에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명은 생략한다. Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. First of all, in adding reference numerals to elements of each drawing, it should be noted that the same elements are assigned the same numerals as possible even if they are indicated on different drawings. In addition, in describing the present invention, if it is determined that a detailed description of a related known configuration or function may obscure the subject matter of the present invention, a detailed description thereof will be omitted.

또한, 본 발명의 구성 요소를 설명하는 데 있어서, 제 1, 제 2, A, B, (a), (b) 등의 용어를 사용할 수 있다. 이러한 용어는 그 구성 요소를 다른 구성 요소와 구별하기 위한 것일 뿐, 그 용어에 의해 해당 구성 요소의 본질이나 차례 또는 순서 등이 한정되지 않는다. 어떤 구성 요소가 다른 구성요소에 "연결", "결합" 또는 "접속" 된다고 기재된 경우, 그 구성 요소는 그 다른 구성요소에 직접적으로 연결되거나 또는 접속될 수 있지만, 각 구성 요소 사이에 또 다른 구성 요소가 "연결", "결합" 또는 "접속"될 수도 있다고 이해되어야 할 것이다.In addition, in describing the constituent elements of the present invention, terms such as first, second, A, B, (a), (b) may be used. These terms are only used to distinguish the component from other components, and the nature, order, or order of the component is not limited by the term. When a component is described as being "connected", "coupled" or "connected" to another component, the component may be directly connected or connected to that other component, but another component between each component It should be understood that elements may be “connected”, “coupled” or “connected”.

또한, 본 발명에 기재된 벽지, 또는 엠보 벽지는 건축물의 콘크리트 면을 마감하는 마감재로서 활용되는 것으로, 상기 마감재는 전술한 벽지, 또는 문양이나 무늬가 형성된 벽지 뿐만 아니라, 부직포나 요철면이 형성된 건축용 부재를 모두 포함할 수 있다.In addition, the wallpaper or embossed wallpaper described in the present invention is used as a finishing material for finishing the concrete surface of a building, and the finishing material is not only the above-described wallpaper, or wallpaper with patterns or patterns, but also a non-woven fabric or an uneven surface formed building member Can include all.

본 발명의 친환경 기능성 무기질 도료는 액상 결합제와, 일정 중량비의 다공성 무기물과, 무기 항균제와, 글리신(Glycine), 다이에틸렌트라이아민(Deithylenetriamine), 하이드록실아민(Hydroxyamine), 사이클로덱스트린(Cyclodextrin), 요소(Urea)가 혼합 구성되는 기능성 혼합물을 포함하는 파우더와, 흡,방습 기능을 제공하는 D-소르비톨(D-Sorbitol)이 혼합 구성되는 것이다.The eco-friendly functional inorganic paint of the present invention includes a liquid binder, a porous inorganic material in a certain weight ratio, an inorganic antibacterial agent, glycine, diethylenetriamine, hydroxylamine, cyclodextrin, and urea. Powder containing a functional mixture in which (Urea) is mixed, and D-Sorbitol, which provides absorption and desorption functions, are mixed.

여기서, 액상 결합제는 규산 소다(Sodium Silicate), 규산 칼륨(Potassium Silicate), 규산 리튬(Lithium Silicate)가 일정 중량비로 혼합되는 혼합물로 이루어지는 것으로, 무기질 도료의 바인더 역할을 수행하며, 콘크리트 표면에 도포 시 소정의 점착성, 및 균질 접합성 등을 향상시키는 역할을 한다. Here, the liquid binder is made of a mixture in which sodium silicate, potassium silicate, and lithium silicate are mixed at a certain weight ratio, and serves as a binder for inorganic paints, and when applied to the concrete surface It serves to improve predetermined adhesiveness and homogeneous bonding properties.

이러한 액상 결합제는 규산 소다 15중량% ~ 60중량%와, 규산 칼륨 15중량% ~60중량%와, 규산 리튬 5중량% ~10중량%의 혼합물로 이루어짐이 바람직하다.Such a liquid binder is preferably composed of a mixture of 15% to 60% by weight of sodium silicate, 15% to 60% by weight of potassium silicate, and 5% to 10% by weight of lithium silicate.

이때, 상기 규산 소다는 고유의 접착력을 가지고 있으며, 다른 유기 접착제와 달리 공해를 유발시키지 않아 환경친화적인 성분으로 그 최소 함량이 15중량% 미만으로 혼합되는 경우, 수분이나 물에 접촉되면 친수성으로 변화되어 수분에 의해 풀어짐 현상이 발생되고 강도가 저하되어 바인더로서의 역할을 수행하지 못하게 된다는 문제점이 발생하게 된다. 이에, 본 발명에서는 수분이나 물에 접촉된다 하더라도 일정 강도를 유지할 수 있는 최소 범위에 해당하는 15중량%를 초과하여 혼합함이 바람직하다. At this time, the sodium silicate has its own adhesive strength, and unlike other organic adhesives, it is an environmentally friendly component, and when its minimum content is less than 15% by weight, it changes to hydrophilicity when it comes into contact with moisture or water. As a result, there is a problem that loosening occurs due to moisture and the strength is lowered so that it cannot perform the role as a binder. Accordingly, in the present invention, even if it is in contact with moisture or water, it is preferable to mix it in excess of 15% by weight corresponding to the minimum range capable of maintaining a certain strength.

또한, 상기 규산 소다의 최대 함량이 60중량%를 초과하여 혼합되는 경우에는 상기 규산 소다의 과함유에 의해 규산 칼륨 및 규산 리튬과의 혼합시 액상으로 형성되는 것이 아닌 고상, 결정질 또는 비정질 분말로 형성되면서 바인더로서의 역할을 수행하지 못할 뿐만 아니라, 요철면이 형성된 엠보 벽지의 표면이나, 콘크리트 벽면에 도포 시 뭉침 현상이 발생하면서 일정한 두께로의 도포가 이루어지지 못하여 발림성에 대한 효과가 현저하게 떨어지는 문제점이 발생하게 된다. 이에 본 발명에서는 액상 결합제가 분말화 및 발림성의 저하를 방지할 수 있도록 규산 소다의 최대 함량을 60중량% 미만으로 혼합함이 바람직하다.In addition, when the maximum content of the soda silicate is mixed in excess of 60% by weight, it is not formed in a liquid state when mixing with potassium silicate and lithium silicate due to the excessive content of the soda silicate, but is formed into a solid, crystalline or amorphous powder. As a result, it does not play a role as a binder, and when it is applied to the surface of embossed wallpaper with uneven surfaces or concrete walls, agglomeration occurs and the application to a certain thickness is not achieved, so the effect on spreadability is significantly reduced. Will occur. Accordingly, in the present invention, it is preferable to mix the maximum content of soda silicate to less than 60% by weight so that the liquid binder can prevent powdering and deterioration of spreadability.

아울러, 상기 규산 칼륨은 액상 결합제에 높은 점성을 부여하여 무기성 물질들이 서로 엉기게 하면서 액상 결합제의 강도를 증가시키고, 마모, 수분 저항력을 향상시키는 것으로, 규산(SiO2)과 산화칼륨(K2O)을 무게 비율 2:0.5 ~ 2:1.5의 무게비로 혼합하여 물에 용해한 액상 혼합물로 이루어지는 것을 사용하며, 액상 결합제의 총 중량에 있어서, 15중량% ~60중량%의 비율로 혼합이 이루어진다. In addition, the potassium silicate imparts high viscosity to the liquid binder to increase the strength of the liquid binder while making inorganic substances coagulate with each other, and to improve abrasion and moisture resistance.Silic acid (SiO 2 ) and potassium oxide (K 2 O) is mixed in a weight ratio of 2:0.5 to 2:1.5 and a liquid mixture dissolved in water is used, and the mixture is made in a ratio of 15% to 60% by weight based on the total weight of the liquid binder.

여기서, 상기 규산 칼륨은 액상 결합제의 도포 시 얇은 막을 형성시키면서 순간적으로 수분 증발에 의한 건조가 이루어지도록 하는 특성을 제공하며, 이때 상기 규산과 산화칼륨 간의 혼합 비율 중 규산의 혼합양이 산화칼륨의 무게 비율 대비 2배 이하로 혼합되는 경우, 알칼리 성분인 산화칼륨양이 많아지면서 알칼리성 산화칼륨의 특성을 보이게 되며, 이는 물과의 친화력이 커지면서 건조속도를 지연시켜 액상 결합제의 높은 점성을 부여하기 어려운 문제점이 있으며, 이와 반대로 상기 산화칼륨의 혼합량이 규산의 무게 비율 대비 0.5 보다 적은 무게로 혼합되는 경우, 건조가 빠르게 진행될 수는 있으나, 도포가 이루어진 액상 결합제의 표면에 크랙이 발생하게 되는 문제점이 있다. Here, the potassium silicate provides a property of instantaneously drying by evaporation of moisture while forming a thin film when the liquid binder is applied, and at this time, the amount of silicate in the mixing ratio between the silicate and potassium oxide is the weight of potassium oxide. If it is mixed less than twice the ratio, the amount of potassium oxide, which is an alkali component, increases and shows the characteristics of alkaline potassium oxide, which increases the affinity with water and delays the drying speed, making it difficult to impart high viscosity of the liquid binder. On the contrary, when the amount of potassium oxide is mixed with a weight less than 0.5 compared to the weight ratio of silicic acid, drying may proceed quickly, but there is a problem in that cracks are generated on the surface of the coated liquid binder.

또한, 상기 규산 칼륨은 액상 결합제를 제조하기 위한 최저 혼합비가 15중량% 미만인 경우, 규산 칼륨 성분이 너무 낮기 때문에 결합 강도가 저하되어 액상 결합제로서 사용하기 힘들고, 최대 혼합비가 60중량%를 초과하면 수분에 취약한 규산 칼륨 성분의 함량이 너무 높기 때문에 내수성 개선에 대한 효과가 미비한 문제점이 발생하게 되므로, 본 발명에서는 액상 결합제의 총 중량에 있어서, 15중량% ~ 60중량%의 비율로 혼합이 이루어지도록 구성된다.In addition, when the minimum mixing ratio for preparing the liquid binder is less than 15% by weight, the potassium silicate component is too low to reduce the bonding strength, making it difficult to use as a liquid binder.If the maximum mixing ratio exceeds 60% by weight, moisture Since the content of the potassium silicate component, which is vulnerable to, is too high, there is a problem that the effect of improving water resistance is insufficient, so in the present invention, the mixture is made in a ratio of 15% to 60% by weight based on the total weight of the liquid binder. do.

또한, 액상 결합제에 일정 중량비로 혼합되는 규산 리튬은 규산 칼륨의 바인더 강도를 향상시키기 위해서 첨가하며, 그 첨가되는 양이 5중량% 미만으로 혼합되는 경우에는 규산 칼륨의 강도향상 효과가 미비하고, 10중량%를 초과하더라도 규산 칼륨의 강도 향상에 대한 효과가 미비하므로, 바람직하게는 액상 결합제의 총 중량에 있어서, 5중량% ~10중량%의 범위로 혼합이 이루어지게 된다.In addition, lithium silicate mixed at a certain weight ratio in the liquid binder is added to improve the binder strength of potassium silicate, and when the amount is mixed with less than 5% by weight, the effect of improving the strength of potassium silicate is insufficient. Even if it exceeds the weight %, since the effect of improving the strength of potassium silicate is insufficient, the mixing is preferably made in the range of 5% to 10% by weight based on the total weight of the liquid binder.

이와 같이 구성된 액상 결합제는 본 발명의 친환경 기능성 무기질 도료의 총 중량에 있어서, 30중량% 내지 70중량%의 범위로 혼합되게 구성된다. The liquid binder configured as described above is configured to be mixed in the range of 30% by weight to 70% by weight, based on the total weight of the eco-friendly functional inorganic paint of the present invention.

이때, 상기 액상 결합제가 30중량% 미만으로 파우더와 혼합되는 경우, 도막 강도가 낮아질 수 있고 70중량%를 초과하여 혼합되는 경우에는 파우더 혼합물에 포함된 다공성 무기물의 기공을 막아 유해물질의 흡착 기능이 저하될 수 있다. At this time, when the liquid binder is mixed with the powder in an amount of less than 30% by weight, the strength of the coating film may be lowered, and when it is mixed in more than 70% by weight, the pores of the porous inorganic material contained in the powder mixture are blocked, thereby preventing the adsorption function of harmful substances. It can be degraded.

한편, 본 발명의 친환경 기능성 무기질 도료는 액상 결합제가 일정 비율로 혼합되어 VOC, 폼알데히드, 톨루엔, 벤젠, 자일렌, 암모니아, 라돈 등의 유해물질을 차단, 흡착 및 제거하는 파우더 혼합물의 제조가 이루어지며, 상기 파우더 혼합물은 친환경 기능성 무기질 도료의 총 중량에 있어서, 25중량% ~ 60중량%의 혼합비로 상기 액상 결합제와 혼합된다.Meanwhile, in the eco-friendly functional inorganic paint of the present invention, a liquid binder is mixed in a certain ratio to block, adsorb and remove harmful substances such as VOC, formaldehyde, toluene, benzene, xylene, ammonia, and radon. The powder mixture is mixed with the liquid binder at a mixing ratio of 25% to 60% by weight based on the total weight of the eco-friendly functional inorganic paint.

이때, 파우더 혼합물은 일정 중량비로 혼합되는 다공성 무기물과, 무기 항균제와, 글리신(Glycine), 다이에틸렌트라이아민(Deithylenetriamine), 하이드록실아민(Hydroxyamine), 사이클로덱스트린(Cyclodextrin), 요소(Urea)가 일정 중량비로 혼합 구성되는 기능성 혼합물을 포함하여 구성된다. At this time, the powder mixture is a porous inorganic material mixed at a certain weight ratio, an inorganic antibacterial agent, glycine, diethylenetriamine, hydroxylamine, cyclodextrin, and urea. It is composed of a functional mixture composed of a mixture by weight.

이때, 다공성 무기물은 활성탄, 실리카겔, 맥반석, 펄라이트, 버미큘라이트(Vermiculite), 규조토, 제올라이트가 일정 중량비로 혼합 구성되는 것이고, 무기 항균제는 은(Ag), 아연(Zn)이 일정 중량비로 혼합 구성되는 것이다. At this time, the porous inorganic material is composed of activated carbon, silica gel, elvan, pearlite, vermiculite, diatomaceous earth, and zeolite in a certain weight ratio, and the inorganic antimicrobial agent is composed of silver (Ag) and zinc (Zn) in a certain weight ratio. .

다공성 무기물은 그 혼합 비율이 총 중량에 있어서, 활성탄 10중량% ~ 50중량%, 실리카겔 20중량% ~ 30중량%, 맥반석 10중량% ~ 20중량%, 펄라이트 10중량% ~ 20중량%, 버미큘라이트 5중량% ~ 10중량%, 규조토 2.5중량% ~ 5중량%, 제올라이트 2.5중량% ~ 5중량%로 혼합된다. The porous inorganic material has a mixing ratio of 10% to 50% by weight of activated carbon, 20% to 30% by weight of silica gel, 10% to 20% by weight of elvan, 10% to 20% by weight of pearlite, and 5% by weight of vermiculite. It is mixed with weight% to 10% by weight, diatomaceous earth 2.5% to 5% by weight, zeolite 2.5% to 5% by weight.

이때, 상기 활성탄은 활성탄의 입자크기는 약 1㎛ ~ 약 100㎛인 것이 혼합될 수 있으며, 바람직하게는 활성탄의 입자크기가 5㎛ 이상 60㎛ 미만인 것이 혼합될 수 있다. 이는, 다공성 무기물의 도포 시 요철면이 형성된 엠보 벽지의 표면이나, 콘크리트 벽면에 인위적인 요철면을 더 형성하여 최종 마감면의 외관품질을 향상시키며, 표면 면적을 향상시켜 다공성 무기물의 성능을 극대화시키기 위함이다.At this time, the activated carbon may be mixed with activated carbon having a particle size of about 1 μm to about 100 μm, and preferably having a particle size of 5 μm or more and less than 60 μm. This is to improve the appearance quality of the final finished surface by further forming an artificial uneven surface on the surface of the embossed wallpaper on which the uneven surface is formed when the porous inorganic material is applied or the concrete wall, and to maximize the performance of the porous inorganic material by improving the surface area. to be.

또한, 실리카겔 및 맥반석 역시 활성탄과 동일한 5㎛ 이상 60㎛ 미만의 입자크기로 구성되어 혼합될 수 있으며, 이에 따라 본 발명의 이미 요철면이 형성된 상태의 엠보 벽지 표면이나, 콘크리트 표면에 보다 다양한 요철면을 더 형성할 수 있으며, 상기 활성탄, 실리카겔 및 맥반석의 입자 크기를 다양한 조합하여 혼합함으로써, 별도의 엠보 벽지 시공을 동반하지 않는다 하더라도 실내 벽면에 대한 다양한 엠보성 디자인을 적용할 수 있어 실내 벽면에 대한 외관미의 소비자 만족도를 향상시킬 수 있을 것이다. In addition, silica gel and elvan stone may also be mixed with a particle size of 5 μm or more and less than 60 μm, which is the same as the activated carbon, and accordingly, the embossed wallpaper surface or concrete surface in which the uneven surface of the present invention is already formed, Can be further formed, and by mixing the particle sizes of the activated carbon, silica gel, and elvan stone in various combinations, various embossing designs can be applied to the indoor wall even if it is not accompanied by a separate embossing wallpaper construction. It will be possible to improve the customer satisfaction of the appearance.

또한, 펄라이트는 다공성 무기물에 함유되는 최소 혼합 중량비가 10중량% 미만으로 형성되는 경우, 입자의 강도가 약해져 보온재로서의 강도가 떨어지게 되는 문제가 있고, 20중량%를 초과하여 혼합되는 경우에는 펄라이트의 밀도가 올라가 전도에 의한 열전달이 높아지는 문제점이 있다. 이에, 본 발명에서는 펄라이트가 보온재로서의 기능을 최대한 발휘할 수 있도록 다공성 무기물의 총 중량에 있어서 10중량% ~ 20중량%의 범위로 혼합이 이루어지도록 구성되는 것이다. In addition, pearlite has a problem that when the minimum mixing weight ratio contained in the porous inorganic material is less than 10% by weight, the strength of the particles is weakened and the strength as an insulating material decreases, and when it is mixed in more than 20% by weight, the density of pearlite There is a problem that heat transfer by conduction increases as it rises. Accordingly, in the present invention, the pearlite is configured to be mixed in a range of 10% by weight to 20% by weight based on the total weight of the porous inorganic material so that it can maximize its function as a heat insulating material.

버미큘라이트(Vermiculite)는 열처리에 의해 팽창이 이루어진 팽창버미큘라이트(expanded vermiculite)일 수 있으며, 상기 펄라이트와 함께 단열재로서의 역할과 함께 충진제 및 흡음제로서의 기능을 동시에 제공하는 것으로, 본 발명에서는 150메쉬의 입자크기로 이루어지는 것을 사용한다. Vermiculite (Vermiculite) may be expanded vermiculite (expanded vermiculite) is expanded by heat treatment, and provides a function as a filler and sound absorbing agent as well as a role as an insulating material together with the perlite.In the present invention, the particle size of 150 mesh Use what is done.

규조토 및 제올라이트는 내부의 미세 기공을 통해 온도 변화나 기타 외부조건의 변화에 따른 우수한 접착력을 제공하고, 실내에서 배출되는 유해 화학물질, 특히 휘발성 유기화합물(VOCs)을 흡착, 분해하여 저감시키는 기능을 수행하는 역할을 한다. Diatomaceous earth and zeolite provide excellent adhesion according to changes in temperature or other external conditions through fine pores inside, and absorb and decompose harmful chemicals, especially volatile organic compounds (VOCs) discharged indoors. It has a role to play.

이와 같이 구성된 본 발명의 다공성 무기물은 파우더를 제조하기 위한 파우더 혼합물의 총 중량에 있어서, 40.0중량% ~99.0중량%로 혼합이 이루어진다. The porous inorganic material of the present invention configured as described above is mixed in an amount of 40.0% by weight to 99.0% by weight, based on the total weight of the powder mixture for preparing the powder.

이때, 다공성 무기물 입자의 함량이 40.0중량% 미만인 경우에는 흡방습 및 유해물질의 흡착 성능 효과가 미비하고, 99.0중량%를 초과하는 경우에는 갈라짐이 발생하는 등 내구성에 문제가 발생할 수 있다.At this time, when the content of the porous inorganic particles is less than 40.0% by weight, the effect of absorption and desorption and adsorption of harmful substances is insufficient, and when it exceeds 99.0% by weight, a problem may occur in durability such as cracking.

한편, 무기 항균제는 은(Ag), 아연(Zn)이 일정 중량비로 혼합 구성되는 것으로, 혼합 시 제올라이트 내부에 존재되도록 소듐과 치환반응되어 빛과 직접 접촉하는 것을 막아 도막 변색을 방지하도록 구성된다. 파우더 혼합물에서 무기 항균제가 10.0 중량%를 초과하여 함유될 경우 재료비 상승을 초래할 수 있고 0.5중량% 미만으로 함유될 경우 항균 및 항곰팡이 성능을 제공하지 못할 수 있다. 이에, 본 발명에서는 무기 항균제가 0.5중량% ~ 10.0중량%의 혼합비로 다공성 무기물과 혼합이 이루어지도록 구성된다. On the other hand, the inorganic antimicrobial agent is composed of a mixture of silver (Ag) and zinc (Zn) at a certain weight ratio, and is configured to prevent discoloration of the coating film by replacing reaction with sodium so as to exist inside the zeolite when mixing to prevent direct contact with light. If the powder mixture contains more than 10.0% by weight of the inorganic antimicrobial agent, it may cause an increase in material cost, and if it is contained in less than 0.5% by weight, it may not provide antibacterial and antifungal performance. Accordingly, in the present invention, the inorganic antimicrobial agent is configured to be mixed with the porous inorganic material at a mixing ratio of 0.5% to 10.0% by weight.

아울러, 본 발명의 파우더 혼합물은 다공성 무기물 및 무기 항균제와 함께 글리신(Glycine), 다이에틸렌트라이아민(Deithylenetriamine), 하이드록실아민(Hydroxyamine), 사이클로덱스트린(Cyclodextrin), 요소(Urea)가 혼합되게 구성되며, 파우더 혼합물의 총 중량에 있어서, 상기 글리신(Glycine), 다이에틸렌트라이아민(Deithylenetriamine), 하이드록실아민(Hydroxyamine), 사이클로덱스트린(Cyclodextrin) 및 요소(Urea)가 각각 0.1중량% ~ 5.0중량%로 혼합이 이루어진다. In addition, the powder mixture of the present invention is composed of a mixture of glycine, diethylenetriamine, hydroxylamine, cyclodextrin, and urea together with a porous inorganic material and an inorganic antibacterial agent. , In the total weight of the powder mixture, the glycine (Glycine), diethylene triamine (Deithylenetriamine), hydroxylamine (Hydroxyamine), cyclodextrin (Cyclodextrin) and urea (Urea) are each 0.1% to 5.0% by weight. Mixing takes place.

즉, 본 발명의 파우더 혼합물은 다공성 무기물 40.0중량% ~99.0중량%, 무기 항균제 0.5중량% ~ 10.0중량%, 글리신 0.1중량% ~ 5.0중량%, 다이에틸렌트라이아민 0.1중량% ~ 5.0중량%, 하이드록실아민 0.1중량% ~ 5.0중량%, 사이클로덱스트린 0.1중량% ~ 5.0중량% 및 요소 0.1중량% ~ 5.0중량%로 혼합되는 것이다.That is, the powder mixture of the present invention is a porous inorganic material 40.0% by weight to 99.1% by weight, inorganic antimicrobial agent 0.5% by weight to 10.0% by weight, glycine 0.1% by weight to 5.0% by weight, diethylenetriamine 0.1% by weight to 5.0% by weight, hide It is a mixture of 0.1% to 5.0% by weight of loxylamine, 0.1% to 5.0% by weight of cyclodextrin, and 0.1% to 5.0% by weight of urea.

아울러, 본 발명의 친환경 기능성 무기질 도료는 실내 유해물질의 흡착성, 습도 조절 등의 기능을 향상시키도록 상기 액상 결합제 및 파우더 혼합물에 D-소르비톨(D-Sorbitol)가 1중량% ~10중량%의 비율로 혼합된다. In addition, the eco-friendly functional inorganic paint of the present invention has a ratio of 1% to 10% by weight of D-Sorbitol in the liquid binder and powder mixture to improve functions such as absorption of harmful indoor substances and humidity control. Is mixed with.

즉, 본 발명의 친환경 기능성 무기질 도료는 액상 결합제 30중량% ~ 70중량%, 파우더 혼합물 25중량% ~ 60중량%, D-소르비톨(D-Sorbitol)가 1중량% ~10중량%의 비율로 혼합되어 제조되는 것이다.That is, the eco-friendly functional inorganic paint of the present invention is mixed in a ratio of 30% to 70% by weight of a liquid binder, 25% to 60% by weight of a powder mixture, and 1% to 10% by weight of D-sorbitol (D-Sorbitol). It is made and manufactured.

이와 같이 구성된 본 발명의 친환경 기능성 무기질 도료는 제품의 물성을 개선하는 증점제 및 상기 증점제와 동일한 중량비로 혼합되는 소포제를 더 첨가 할 수 있다.The eco-friendly functional inorganic paint of the present invention configured as described above may further include a thickener for improving the physical properties of the product and an antifoaming agent mixed in the same weight ratio as the thickener.

여기서, 증점제는 무기질도료 조성물의 점도를 조절하기 위해 사용하며, 0.1 중량% 내지 5 중량%인 증점제 수용액의 형태로 혼합되어 상기 친환경 기능성 무기질 도료의 점도를 1,000~10,000cps로 유지하도록 한다. Here, the thickener is used to control the viscosity of the inorganic paint composition, and is mixed in the form of an aqueous thickener solution of 0.1% to 5% by weight to maintain the viscosity of the eco-friendly functional inorganic paint at 1,000 to 10,000 cps.

이때, 상기 친환경 기능성 무기질 도료의 점도가 1,000cps보다 낮을 경우 엠보 벽지에 도포시 퍼짐성과 흘러내림이 심하여 작업성에 문제를 야기시키고, 점도가 10,000cps 보다 높을 경우 작업의 시공성이 떨어지고, 시공 후 액상 결합제의 갈라짐 현상이 발생될 수 있다.At this time, when the viscosity of the eco-friendly functional inorganic paint is lower than 1,000 cps, the spreading and flowing down are severe when applied to the embossed wallpaper, causing a problem in workability, and when the viscosity is higher than 10,000 cps, the workability of the work decreases, and the liquid binder after construction May cause cracking.

이와 같이 구성된 본 발명의 무기질 도료에는 음각, 또는 양각 형태의 요철면(또는 엠보)이(가) 형성된 엠보 벽지의 표면에 도포 시 사용자의 요구에 따라 다양한 색상으로 이루어진 안료를 더 혼합하여 도포가 이루어지도록 함으로써, 사용자의 색상 취향에 맞게 엠보 벽지의 시공이 가능하도록 구성된다. When applied to the surface of embossed wallpaper on which an intaglio or embossed surface (or emboss) is formed, the inorganic paint of the present invention configured as described above is applied by further mixing pigments of various colors according to the user's request. By making it possible to construct the embossed wallpaper according to the color preference of the user.

이와 같이 구성된 본 발명의 친환경 기능성 무기질 도료는 유해물질 흡착율 시험, 흡방습 시험, 항균 시험, 항곰팡이 시험을 실시하였으며, 그 결과는 도 2에 도시된 바와 같다.The eco-friendly functional inorganic paint of the present invention constructed as described above was subjected to a harmful substance adsorption rate test, moisture absorption and desorption test, antibacterial test, and anti-mold test, and the results are as shown in FIG. 2.

예를 들어, 본 발명의 친환경 기능성 무기질 도료의 유해물질 중 폼알데하이드의 흡착율은 본 발명의 무기질 도료가 도포되지 않은 상태의 엠보 벽지에 비해 무기질 도료가 일정 두께로 도포된 상태에서 월등히 높음을 알 수 있다. For example, it can be seen that the adsorption rate of formaldehyde among the harmful substances of the eco-friendly functional inorganic paint of the present invention is significantly higher in the state where the inorganic paint is applied to a certain thickness compared to the embossed wallpaper in the state where the inorganic paint of the present invention is not applied. .

즉, 요철면이 형성된 엠보 벽지만을 시공하는 경우, 그 흡착율이 1일차에 14.5%의 흡착율을 보이고, 7일차일 때 13.80%의 흡착율을 보이는 반면, 본 발명의 무기질 도료를 도포한 경우, 1일차 흡착율이 72.8%의 흡착율을 보이면서 7일차가 되어서도 70.9%의 흡착율을 유지하고 있음이 파악되었다. That is, when only embossed wallpaper with an uneven surface is constructed, the adsorption rate is 14.5% on the first day and 13.80% on the 7th day, whereas when the inorganic paint of the present invention is applied, the first day It was found that the adsorption rate was 72.8%, and the adsorption rate was maintained at 70.9% even on the 7th day.

특히, 흡착된 폼알데하이드의 재방출율의 경우, 통상의 무기질 도료는 0.204%의 비율로 재방출이 발생하는데 반해, 본 발명의 무기질 도료의 경우에는 0.001%의 재방출율만이 발생함을 확인하였다.In particular, in the case of the re-release rate of the adsorbed formaldehyde, it was confirmed that the re-release rate occurred in the case of the inorganic coating material of the present invention at a rate of 0.204%, whereas the re-release rate of only 0.001% occurred in the conventional inorganic paint.

또한, 본 발명의 친환경 기능성 무기질 도료의 흡방습 시험을 실시한 결과, 흡습량은 110.08g/㎡, 방습량은 106.88g/㎡, 흡습 및 방습차는 3.20g/㎡로 나타남이 확인되었으며, 이는 무기질 도료가 도포되지 않은 상태의 엠보 벽지에 비해 무기질 도료가 일정 두께로 도포된 상태에서 흡습 및 방습 성능이 월등히 높음을 알 수 있다. In addition, as a result of conducting a moisture absorption and desorption test of the eco-friendly functional inorganic paint of the present invention, it was confirmed that the moisture absorption amount was 110.08g/㎡, the moisture absorption amount was 106.88g/㎡, and the moisture absorption and moisture resistance difference was 3.20g/㎡. It can be seen that the moisture absorption and moisture-proof performance is significantly higher in the state where the inorganic paint is applied in a certain thickness compared to the embossed wallpaper in the state where is not applied.

또한, 본 발명의 친환경 기능성 무기질 도료의 항균 및 항곰팡이 시험 역시 무기질 도료가 도포되지 않은 상태의 엠보 벽지에 비해 무기질 도료가 일정 두께로 도포된 상태에서 항균 및 항곰팡이 성능이 월등히 높음을 알 수 있다. In addition, it can be seen that the antibacterial and antifungal tests of the eco-friendly functional inorganic paint of the present invention also have significantly higher antibacterial and anti-fungal performance in the state where the inorganic paint is applied at a certain thickness compared to the embossed wallpaper in the state where the inorganic paint is not applied. .

이하에서는 본 발명의 친환경 기능성 무기질 도료를 이용한 시공방법에 대해 설명하도록 한다. Hereinafter, a construction method using the eco-friendly functional inorganic paint of the present invention will be described.

친환경 기능성 무기질 도료를 이용한 시공방법은 도 1에 도시된 바와 같이, 친환경 기능성 무기질 도료를 제조하는 바름제 제조단계(S110)가 수행된다. As for the construction method using an eco-friendly functional inorganic paint, as shown in FIG. 1, a varum agent manufacturing step (S110) of manufacturing an eco-friendly functional inorganic paint is performed.

무기질 도료 제조단계(S110)는 규산 소다 15중량% ~ 60중량%와, 규산 칼륨 15중량% ~60중량%와, 규산 리튬 5중량% ~10중량%를 교반하여 액상 결합제를 제조하는 액상 결합제 제조단계를 수행한다. Inorganic paint manufacturing step (S110) is a liquid binder manufacturing a liquid binder by stirring 15% by weight to 60% by weight of sodium silicate, 15% to 60% by weight of potassium silicate, and 5% to 10% by weight of lithium silicate Follow the steps.

이후, 무기질 도료 제조단계(S110)는 액상 결합제와 일정 비율로 혼합되는 파우더 혼합물을 제조하는 단계를 수행한다. Thereafter, the inorganic paint manufacturing step (S110) performs a step of preparing a powder mixture mixed with a liquid binder in a predetermined ratio.

이때, 파우더 혼합물 제조단계는, 다공성 무기물, 무기 항균제를 각각 제조하는 단계를 수행하며, 상기 다공성 무기물은 활성탄 10중량% ~ 50중량%, 실리카겔 20중량% ~ 30중량%, 맥반석 10중량% ~ 20중량%, 펄라이트 10중량% ~ 20중량%, 버미큘라이트 5중량% ~ 10중량%, 규조토 2.5중량% ~ 5중량%, 제올라이트 2.5중량% ~ 5중량%로 혼합하여 제조한다. At this time, in the powder mixture manufacturing step, each of a porous inorganic material and an inorganic antibacterial agent are prepared, and the porous inorganic material is activated carbon 10% to 50% by weight, silica gel 20% to 30% by weight, elvan stone 10% to 20% It is prepared by mixing with weight%, pearlite 10% to 20% by weight, vermiculite 5% to 10% by weight, diatomaceous earth 2.5% to 5% by weight, zeolite 2.5% to 5% by weight.

이후, 파우더 혼합물 제조단계는 다공성 무기물 40.0중량% ~99.0중량%, 무기 항균제 0.5중량% ~ 10.0중량%, 글리신 0.1중량% ~ 5.0중량%, 다이에틸렌트라이아민 0.1중량% ~ 5.0중량%, 하이드록실아민 0.1중량% ~ 5.0중량%, 사이클로덱스트린 0.1중량% ~ 5.0중량% 및 요소 0.1중량% ~ 5.0중량%로 교반하여 상기 파우더 혼합물의 제조가 이루어지도록 한다. Thereafter, the powder mixture manufacturing step is a porous inorganic material 40.0% by weight ~ 99.1% by weight, inorganic antimicrobial agent 0.5% by weight ~ 10.0% by weight, glycine 0.1% by weight ~ 5.0% by weight, diethylenetriamine 0.1% by weight ~ 5.0% by weight, hydroxyl The powder mixture is prepared by stirring with 0.1% to 5.0% by weight of amine, 0.1% to 5.0% by weight of cyclodextrin, and 0.1% to 5.0% by weight of urea.

무기질 도료 제조단계(S110)는 전술한 액상 결합제와 파우더 혼합물 및 D-소르비톨(D-Sorbitol)을 일정 중량비로 교반에 의해 혼합하여 친환경 기능성 무기질 도료의 제조가 이루어지도록 한다. In the inorganic paint manufacturing step (S110), the above-described liquid binder, powder mixture, and D-sorbitol are mixed by agitation at a predetermined weight ratio to prepare an eco-friendly functional inorganic paint.

이때, 액상 결합제 30중량% ~ 70중량%, 파우더 혼합물 25중량% ~ 60중량%, D-소르비톨(D-Sorbitol)가 1중량% ~10중량%의 비율로 교반하여 혼합이 이루어지도록 구성됨이 바람직하다. At this time, the liquid binder 30% to 70% by weight, the powder mixture 25% to 60% by weight, D-Sorbitol (D-Sorbitol) is preferably configured to be mixed by stirring in a ratio of 1% to 10% by weight Do.

한편, 본 발명의 무기질 도료 제조단계(S110)는 상기 액상 결합제 30중량% ~ 70중량%, 파우더 혼합물 25중량% ~ 60중량%, D-소르비톨(D-Sorbitol)가 1중량% ~ 10중량%의 비율로 교반하여 혼합된 혼합물에 0.1 중량% 내지 5 중량%의 중량비로 증점제와 소포제를 각각 더 혼합할 수 있다. On the other hand, the inorganic paint manufacturing step (S110) of the present invention is the liquid binder 30% by weight to 70% by weight, the powder mixture 25% by weight to 60% by weight, D-sorbitol (D-Sorbitol) is 1% by weight to 10% by weight The mixture may be further mixed with a thickener and a defoaming agent in a weight ratio of 0.1% to 5% by weight in the mixture by stirring at a ratio of.

이후, 본 발명은 상기 S110 단계에 의해 제조된 친환경 기능성 무기질 도료를 도포할 실내 콘크리트 표면의 피착면을 정리하는 피착면 정리단계(S120)를 수행한다. Thereafter, the present invention performs the adhered surface arrangement step (S120) of arranging the adhered surface of the indoor concrete surface to which the eco-friendly functional inorganic paint prepared by the step S110 is applied.

피착면 정리단계(S120)는 콘크리트 표면에 남아 있는 오염물질을 제거하고, 퍼티 공정 등을 통해 콘크리트 표면의 평탄화 작업이 이루어지도록 하는 단계이다. In the step of arranging the adherend surface (S120), the contaminants remaining on the concrete surface are removed, and the concrete surface is flattened through a putty process.

이때, 상기 피착면 정리단계(S120)는 퍼티 공정 수행시 콘크리트 표면에 요철면을 형성하는 요철면 형성단계를 더 수행할 수 있으며, 상기 콘크리트 표면에 요철면을 형성하는 경우, 무기질 도료가 직접 상기 콘크리트 표면에 도포가 이루어지도록 구성될 수 있다. In this case, the step of arranging the adherend surface (S120) may further perform a step of forming an uneven surface of forming an uneven surface on the concrete surface when performing the putty process, and when forming the uneven surface on the concrete surface, the inorganic paint is directly applied to the It can be configured to be applied to the concrete surface.

이후, 본 발명은 상기 피착면 정리단계(S120)가 완료되면, 표면에 요철면이 형성된 벽지를 상기 피착면에 시공하는 벽지 시공단계(S130)를 수행한다.Thereafter, the present invention performs a wallpaper construction step (S130) of constructing a wallpaper with an uneven surface formed on the adherend surface when the adherend arrangement step (S120) is completed.

이때, 요철면이 형성된 벽지는 통상의 엠보 벽지일 수 있으며, 사용자의 요구에 따라 다양한 형태의 요철면(엠보)이 형성될 수 있다. In this case, the wallpaper on which the uneven surface is formed may be a conventional embossed wallpaper, and various types of uneven surface (emboss) may be formed according to a user's request.

다음으로, S110 단계에 의해 제조된 친환경 기능성 무기질 도료를 상기 엠보 벽지의 표면에 도포하는 무기질 도료 도포단계(S140)가 수행된다. Next, the inorganic paint coating step (S140) of applying the eco-friendly functional inorganic paint prepared by step S110 to the surface of the embossed wallpaper is performed.

이때, 상기 무기질 도료 도포단계(S140)는 무기질 도료를 도포할 해라, 스프레이 분사장치와 같은 도포수단을 요철면이 형성된 벽지의 표면과 40°~50°의 경사각을 이루도록 하고, 1회 도포 시 0.1mm ~ 0.5mm의 두께로 도포가 이루어지도록 한다. At this time, in the inorganic paint application step (S140), the inorganic paint is applied. An application means such as a spray spraying device is used to form an inclination angle of 40° to 50° with the surface of the wallpaper on which the uneven surface is formed, and 0.1 The application should be made in a thickness of mm ~ 0.5mm.

본 발명에서는 무기질 도료의 도포를 1~2회 도포함이 바람직하나, 이에 요철면이 형성된 벽지의 면적에 따라 도포 두께 및 횟수는 달라질 수 있을 것이다.In the present invention, it is preferable to apply the inorganic paint once or twice, but the thickness and number of applications may vary depending on the area of the wallpaper on which the uneven surface is formed.

아울러, 무기질 도료 도포단계(S140)는 음각, 또는 양각 형태의 요철면이 형성된 벽지의 표면에 도포가 이루어질 때, 사용자의 요구에 따라 다양한 색상으로 이루어진 색상안료를 더 혼합하여 도포가 이루어지도록 함으로써, 사용자의 색상 취향에 맞게 엠보 벽지의 시공이 가능하도록 구성된다. In addition, in the inorganic paint application step (S140), when coating is performed on the surface of the wallpaper on which the intaglio or embossed surface is formed, the application is made by further mixing color pigments of various colors according to the user's request, It is configured to allow the construction of embossed wallpaper according to the user's color preference.

다음으로, 무기질 도료가 일정한 두께로 평탄하게 도포가 이루어졌는지 여부를 검사하는 품질 검사단계(S150)가 수행된다. Next, a quality inspection step (S150) of checking whether or not the inorganic paint has been applied evenly with a predetermined thickness is performed.

품질 검사단계(S150)는 육안에 의한 검사로 이루어질 수 있으나, 이에 한정하는 것은 아니며, 평탄화 검사장치를 통해 무기질 도료의 도포 두계를 측정하는 방식을 통해 실시될 수도 있을 것이다. The quality inspection step (S150) may be performed by visual inspection, but is not limited thereto, and may be performed through a method of measuring the thickness of the inorganic paint applied through a planarization inspection device.

이후, 상기 품질 검사단계(S150)가 완료되면, 무기질 도료가 도포된 엠보 벽지의 보양이 이루어지도록 하는 마감 작업단계(S160)를 수행한다.Thereafter, when the quality inspection step (S150) is completed, a finishing operation step (S160) of maintaining the embossed wallpaper on which the inorganic paint is applied is performed.

이상에서 기재된 "포함하다", "구성하다" 또는 "가지다" 등의 용어는, 특별히 반대되는 기재가 없는 한, 해당 구성 요소가 내재될 수 있음을 의미하는 것이므로, 다른 구성 요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것으로 해석되어야 하며, 기술적이거나 과학적인 용어를 포함한 모든 용어들은, 다르게 정의되지 않는 한, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가진다. Terms such as "include", "consist of", or "have" described above, unless otherwise stated, mean that the corresponding component may be included, and thus other components are not excluded. It should be construed as being able to further include other components, and all terms including technical or scientific terms are generally understood by those of ordinary skill in the technical field to which the present invention belongs, unless otherwise defined. Has the same meaning as

또한, 이상의 설명은 본 발명의 기술 사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. 따라서, 본 발명에 개시된 실시예들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.In addition, the above description is merely illustrative of the technical idea of the present invention, and those of ordinary skill in the art to which the present invention pertains will be able to make various modifications and variations without departing from the essential characteristics of the present invention. . Accordingly, the embodiments disclosed in the present invention are not intended to limit the technical idea of the present invention, but to explain the technical idea, and the scope of the technical idea of the present invention is not limited by these embodiments. The scope of protection of the present invention should be interpreted by the following claims, and all technical ideas within the scope equivalent thereto should be interpreted as being included in the scope of the present invention.

Claims (5)

(a) 친환경 기능성 무기질 도료를 제조하는 단계;
(b) 상기 (a) 단계 이후, 친환경 기능성 무기질 도료를 도포할 실내 콘크리트 표면의 피착면을 정리하는 단계;
(c) 상기 (b) 단계 이후, 표면에 엠보 벽지를 상기 피착면에 시공하는 단계;
(d) 상기 (c) 단계 이후, 도포수단을 상기 엠보 벽지의 표면과 40°~50°의 경사각을 이루도록 하고, 1회 도포 시 0.1mm ~ 0.5mm의 두께로 상기 친환경 기능성 무기질 도료를 도포하는 단계;
(e) 피착면에 도포된 상기 친환경 기능성 무기질 도료가 일정한 두께로 평탄하게 도포가 이루어졌는지 여부를 검사하는 단계; 및
(f) 상기 친환경 기능성 무기질 도료가 도포된 엠보 벽지 표면의 보양이 이루어지도록 하는 단계;
를 포함하는 것을 특징으로 하는 친환경 기능성 무기질 도료를 이용한 실내 공기질 개선용 인테리어 엠보 벽지 마감 시공방법.
(a) preparing an eco-friendly functional inorganic paint;
(b) after step (a), arranging the adherend surface of the indoor concrete surface to which the eco-friendly functional inorganic paint is to be applied;
(c) after the step (b), applying embossed wallpaper on the surface to the adherend;
(d) After the step (c), the application means is made to form an inclination angle of 40° to 50° with the surface of the embossed wallpaper, and the eco-friendly functional inorganic paint is applied to a thickness of 0.1 mm to 0.5 mm when applied once. step;
(e) examining whether or not the eco-friendly functional inorganic paint applied to the adherend is applied evenly to a predetermined thickness; And
(f) maintaining the surface of the embossed wallpaper on which the eco-friendly functional inorganic paint is applied;
Interior embossing wallpaper finishing construction method for improving indoor air quality using an eco-friendly functional inorganic paint comprising a.
 제1항에 있어서,
상기 (d) 단계는, 상기 엠보 벽지의 표면에 도포가 이루어질 때, 색상안료를 더 혼합하여 도포하는 것을 특징으로 하는 친환경 기능성 무기질 도료를 이용한 엠보 벽지 시공방법.
The method of claim 1,
In the step (d), when the embossed wallpaper is coated on the surface, a color pigment is further mixed and applied. The embossed wallpaper construction method using an eco-friendly functional inorganic paint.
 제1항에 있어서,
상기 (a) 단계에 있어서,
(a1) 규산 소다 15중량% ~ 60중량%와, 규산 칼륨 15중량% ~60중량%와, 규산 리튬 5중량% ~10중량%를 교반하여 액상 결합제를 제조하는 단계;
(a2) 활성탄, 실리카겔, 맥반석, 펄라이트, 버미큘라이트(Vermiculite), 규조토, 제올라이트가 일정 중량비로 혼합되는 다공성 무기물과, 은(Ag), 아연(Zn)이 일정 중량비로 혼합되는 무기 항균제를 각각 제조하는 단계;
(a3) 상기 다공성 무기물 및 무기 항균제와 글리신(Glycine), 다이에틸렌트라이아민(Deithylenetriamine), 하이드록실아민(Hydroxyamine), 사이클로덱스트린(Cyclodextrin), 요소(Urea)가 혼합되게 구성되며, 파우더 혼합물의 총 중량에 있어서, 상기 글리신(Glycine), 다이에틸렌트라이아민(Deithylenetriamine), 하이드록실아민(Hydroxyamine), 사이클로덱스트린(Cyclodextrin) 및 요소(Urea)를 각각 일정 중량비로 혼합하여 파우더 혼합물을 제조하는 단계; 및
(a4) 상기 액상 결합제 및 상기 파우더 혼합물에 D-소르비톨(D-Sorbitol)를 일정 중량비로 혼합하여 친환경 기능성 무기질 도료를 제조하는 단계;
를 포함하는 것을 특징으로 하는 친환경 기능성 무기질 도료를 이용한 엠보 벽지 시공방법.
The method of claim 1,
In step (a),
(a1) preparing a liquid binder by stirring 15% to 60% by weight of sodium silicate, 15% to 60% by weight of potassium silicate, and 5% to 10% by weight of lithium silicate;
(a2) To prepare an inorganic antimicrobial agent in which activated carbon, silica gel, elvan, pearlite, vermiculite, diatomaceous earth, and zeolite are mixed in a certain weight ratio, and silver (Ag) and zinc (Zn) are mixed in a certain weight ratio. step;
(a3) The porous inorganic material and inorganic antibacterial agent and glycine, diethylenetriamine, hydroxylamine, cyclodextrin, and urea are mixed. In terms of weight, preparing a powder mixture by mixing the glycine (Glycine), diethylenetriamine (Deithylenetriamine), hydroxylamine (Hydroxyamine), cyclodextrin (Cyclodextrin) and urea (Urea) in a predetermined weight ratio, respectively; And
(a4) preparing an eco-friendly functional inorganic paint by mixing D-Sorbitol with the liquid binder and the powder mixture at a predetermined weight ratio;
Emboss wallpaper construction method using an eco-friendly functional inorganic paint comprising a.
 제1항에 있어서,
상기 무기질 도료는 총 중량에 있어서, 상기 액상 결합제 30중량% ~70중량%, 상기 파우더 혼합물 25중량% ~ 60중량%, 1중량% ~10중량%의 D-소르비톨(D-Sorbitol)로 구성되는 것을 특징으로 하는 친환경 기능성 무기질 도료를 이용한 엠보 벽지 시공방법.
The method of claim 1,
The inorganic paint is composed of D-sorbitol (D-Sorbitol) of 30% by weight to 70% by weight of the liquid binder, 25% by weight to 60% by weight of the powder mixture, and 1% by weight to 10% by weight of the inorganic paint. Embossing wallpaper construction method using an eco-friendly functional inorganic paint, characterized in that.
 제4항에 있어서,
상기 파우더 혼합물은, 다공성 무기물 40.0중량% ~99.0중량%와, 무기 항균제 0.5중량% ~ 10중량%와, 글리신(Glycine) 0.1중량% ~ 5.0중량%와, 다이에틸렌트라이아민(Deithylenetriamine) 0.1중량% ~ 5.0중량%와, 하이드록실아민(Hydroxyamine) 0.1중량% ~ 5.0중량%와, 사이클로덱스트린(Cyclodextrin) 0.1중량% ~ 5.0중량%와, 요소(Urea) 0.1중량% ~ 5.0중량%로 이루어지는 것을 특징으로 하는 친환경 기능성 무기질 도료를 이용한 엠보 벽지 시공방법.
The method of claim 4,
The powder mixture includes 40.0% by weight to 99.1% by weight of a porous inorganic material, 0.5% by weight to 10% by weight of an inorganic antimicrobial agent, 0.1% by weight to 5.0% by weight of glycine, and 0.1% by weight of diethylenetriamine It is characterized by consisting of ~ 5.0% by weight, 0.1% by weight to 5.0% by weight of hydroxylamine, 0.1% by weight to 5.0% by weight of cyclodextrin, and 0.1% by weight to 5.0% by weight of urea Embossing wallpaper construction method using eco-friendly functional inorganic paint.
KR1020190050643A 2019-04-30 2019-04-30 Interior decoration for interior air quality improvement using environmentally friendly functional inorganic paint Embo wallpaper Finishing method KR102241151B1 (en)