KR20200079689A - Name plate for cosmetic containers and manufacturing method of the same - Google Patents

Name plate for cosmetic containers and manufacturing method of the same Download PDF

Info

Publication number
KR20200079689A
KR20200079689A KR1020180169085A KR20180169085A KR20200079689A KR 20200079689 A KR20200079689 A KR 20200079689A KR 1020180169085 A KR1020180169085 A KR 1020180169085A KR 20180169085 A KR20180169085 A KR 20180169085A KR 20200079689 A KR20200079689 A KR 20200079689A
Authority
KR
South Korea
Prior art keywords
layer
cosmetic container
nameplate
name plate
cosmetic
Prior art date
Application number
KR1020180169085A
Other languages
Korean (ko)
Inventor
김근하
최정아
이은아
Original Assignee
인탑스 주식회사
김근하
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 인탑스 주식회사, 김근하 filed Critical 인탑스 주식회사
Priority to KR1020180169085A priority Critical patent/KR20200079689A/en
Priority to CN201911232027.2A priority patent/CN111376637A/en
Publication of KR20200079689A publication Critical patent/KR20200079689A/en

Abstract

The present invention relates to a name plate for a cosmetic container and a manufacturing method thereof and, more specifically, to a name plate for a cosmetic container, which is coupled to the outer surface of a cap of the cosmetic control to form an appearance of the cosmetic container and a manufacturing method thereof. According to the present invention, the name plate for a cosmetic container comprises an adhesive layer, a cushion layer disposed on the upper part of the adhesive layer, and an appearance layer disposed on the upper part of the cushion layer, thereby forming a beautiful and luxurious appearance when being attached to the cosmetic container. Moreover, since there is need to make an injection mold required for manufacturing an existing plastic name plate, the name plate can be manufactured at low costs in a short time. Since all layers, such as the appearance layer, the cushion layer, the adhesive layer, and the like, forming the name plate can be manufactured in an all-in-one process, an inconvenient process for separately coating adhesive or manually bonding both-side adhesive tape is not required. Moreover, since the name plate for a cosmetic container can be manufactured in a simple process through stacking and welding steps, excellent competitiveness can be secured due to reduction of processing costs, and mass production is possible.

Description

화장품 용기용 명판 및 이의 제조 방법{Name plate for cosmetic containers and manufacturing method of the same}Name plate for cosmetic containers and manufacturing method of the same}

본 발명은 화장품 용기용 명판 및 이의 제조 방법에 관한 것으로서, 구체적으로는, 화장품 용기의 뚜껑 외측면에 결합되어 화장품 용기의 외관을 형성하는 명판 및 이를 간단하고 용이하게 제조할 수 있는 제조방법에 관한 것이다.The present invention relates to a name plate for a cosmetic container and a method for manufacturing the same, specifically, a name plate that is coupled to the outer surface of the lid of the cosmetic container to form the appearance of the cosmetic container and a manufacturing method that can be produced simply and easily will be.

일반적으로　화장품, 특히 기초 화장품인 콤팩트는 휴대성이 좋기 때문에 간편하게 들고 다니며 화장을 수정할 수 있고, 화장할 때에 화장료를 손에 묻히지 않아도 되기 때문에 사용상의 편리한 장점을 가지고 있다.In general, compacts, which are cosmetic products, especially basic cosmetics, have good portability, so they can be easily carried around and corrected for makeup.

이러한 콤팩트　용기는 뚜껑에 명판을 형성시켜, 이에 문구나 그림 등을 인쇄하는 방식을 통해 사용자에게 상표 또는 브랜드명 등의 정보 전달을 하고, 사용자의 시각적 심미성을 충족시킬 수 있게 하여 소비자의 만족도를 향상시킨다.This compact container can form a name plate on the lid, thereby conveying information such as a brand or brand name to the user through a method such as printing a phrase or picture, and improving the customer's satisfaction by satisfying the user's visual aesthetics. Order.

명판의 종래기술로는, 투명판 하부에 인쇄층을 형성하여 인쇄층이 외부로 드러나지 않게 함으로서, 인쇄된 문구나 그림이 벗겨지거나 지워지지 않도록 하여 제조한 명판이 있다. 그러나, 이 경우에는, 인쇄 공정, 후처리 공정 등 공정이 복잡해지는 문제점이 있다. 또한, 명판의 종래기술로서, 자개칠 명판이 있는데, 이 경우에는, 자개를 이용하여 명판을 제작함에 있어서, 수작업으로 제작해야 하고, 재료가 고가이기 때문에, 제작 비용이 매우 증가하고, 공정 또한 복잡해지며, 파손의 위험이 있다. As a prior art of a name plate, there is a name plate manufactured by forming a printing layer on a lower portion of the transparent plate so that the printing layer is not exposed to the outside, so that printed text or pictures are not peeled off or erased. However, in this case, there is a problem that processes such as a printing process and a post-treatment process are complicated. In addition, as a conventional technique of a name plate, there is a name plate to be covered with mother-of-pearl, in this case, in manufacturing the name plate using mother-of-pearl, it has to be produced manually, and since the material is expensive, the manufacturing cost is very high and the process is complicated. There is a risk of damage.

또한, 기존의 대부분의 명판은 플라스틱 수지를 이용하여 제조하는 것으로, 명판 제작 시, 사출을 위한 금형이 필요하기 때문에, 금형 제작비가 매우 고가이며, 금형을 제작하는데 오랜 시간이 걸린다. 또한, 제조한 플라스틱재의 명판을 화장품 용기의 뚜껑에 접착하기 위해서는 접착제를 별도로 도포하거나, 양면 테이프를 부착하여야 하기 때문에, 부착 공정이 별도로 요구되며, 부착 공정은 수작업으로 작업해야 하므로, 번거롭고, 인건비가 증가하며, 시간이 오래 걸리기 때문에, 대량 생산에 어려움이 있고, 경쟁력을 확보하기 어려웠다.In addition, most of the existing nameplates are manufactured using plastic resin, and since the molds for injection are required during the production of the nameplates, the mold production cost is very expensive, and it takes a long time to manufacture the molds. In addition, to adhere the manufactured plastic nameplate to the lid of the cosmetic container, an adhesive is separately applied or a double-sided tape must be attached, so the attaching process is required separately, and the attaching process must be performed manually, which is cumbersome and labor costly. As it increases and takes a long time, there is difficulty in mass production, and it is difficult to secure competitiveness.

이와 같이, 종래의 화장품 용기용 명판은, 제조 공정이 복잡함에 따라 단가 상승으로 인해 가격 경쟁력이 떨어지며, 떨어뜨리거나, 단단한 물체에 부딪히는 충격으로 인한 파손의 위험이 있다는 문제점이 있다.As described above, the conventional nameplate for cosmetic containers has a problem that the price competitiveness decreases due to the increase in unit cost as the manufacturing process is complicated, and there is a risk of damage due to impact of dropping or hitting a hard object.

본 발명은 화장품 용기용 명판 및 이의 제조 방법에 관한 것으로서, 기존의 복잡한 제조 공정과 고가의 금형 사출의 제작 필요 등의 문제점을 개선하는데 그 목적이 있다.The present invention relates to a name plate for a cosmetic container and a method for manufacturing the same, and has an object to improve problems such as the existing complicated manufacturing process and the need to manufacture expensive mold injection.

본 발명의 기술적 과제들은 이상에서 언급한 기술적 과제들로 제한되지 않으며, 언급되지 않은 또 다른 기술적 과제들은 아래의 기재들로부터 당업자에게 명확하게 이해될 수 있을 것이다.The technical problems of the present invention are not limited to the technical problems mentioned above, and other technical problems not mentioned will be clearly understood by those skilled in the art from the following descriptions.

본 발명의 일 실시예에 따른 화장품 용기용 명판은 일면 또는 양면에 대해서 접착력을 갖도록 형성된 접착층; 접착층의 상부에 배치되는 쿠션층; 및 쿠션층의 상부에 배치되는 외형층을 포함하며, 상기 명판은 화장품 용기의 뚜껑 외측면에 결합되어 화장품 용기의 외관을 형성할 수 있다.Name plate for a cosmetic container according to an embodiment of the present invention is an adhesive layer formed to have an adhesive force on one or both sides; A cushion layer disposed on the adhesive layer; And it includes an outer layer disposed on top of the cushion layer, the name plate can be coupled to the outer surface of the lid of the cosmetic container to form the appearance of the cosmetic container.

바람직하게는, 쿠션층은, 스펀지, 솜, 직물 및 발포폼으로 이루어진 군으로부터 선택된 1종 이상을 포함할 수 있다.Preferably, the cushion layer may include one or more selected from the group consisting of sponge, cotton, fabric, and foam.

바람직하게는, 외형층은, 천연 가죽, 인조 가죽, 패브릭, PET 필름으로 이루어지는 군으로부터 선택되는 1종 이상을 포함할 수 있다.Preferably, the outer layer may include one or more selected from the group consisting of natural leather, artificial leather, fabric, and PET film.

더욱 바람직하게는, 외형층은, 염화비닐 가죽, 합성피혁, 및 인공피혁으로 이루어진 군으로부터 선택된 1종 이상의 인조 가죽을 포함할 수 있다. More preferably, the outer layer may include at least one artificial leather selected from the group consisting of vinyl chloride leather, synthetic leather, and artificial leather.

바람직하게는, 접착층은, 폴리프로필렌, 폴리에틸렌, 폴리이미드 및 폴리아미드로 이루어진 군으로부터 선택된 1종 이상을 포함할 수 있다.Preferably, the adhesive layer may include at least one selected from the group consisting of polypropylene, polyethylene, polyimide and polyamide.

또한, 바람직하게는, 접착층과 쿠션층 사이에 기재층을 포함할 수 있고, 기재층은 폴리에틸렌　테레프탈레이트(polyethylene terephthalate),　폴리에틸렌　나프탈레이트(polyethylene naphthalate), 폴리아크릴레이트(polyacrylate), 폴리카보네이트(polycarbonate), 폴리에테르이미드(polyetherimide) 및 폴리이미드(polyimide)로 이루어진 군으로부터 선택된 1종 이상을 포함할 수 있다.In addition, preferably, a base layer may be included between the adhesive layer and the cushion layer, and the base layer may be polyethylene terephthalate, polyethylene naphthalate, polyacrylate, or polycarbonate. ), polyetherimide (polyetherimide) and polyimide (polyimide) may include one or more selected from the group consisting of.

또한, 바람직하게는, 쿠션층과 외형층 사이에 성형층을 포함할 수 있고, 성형층은 폴리우레탄, 열가소성 폴리우레탄, 폴리에틸렌, 폴리프로필렌, 폴리에스터, 폴리에터, 폴리스티렌, 폴리카보네이트,　폴리비닐　클로라이드, 아크릴로니트릴-부타다이엔-스티렌 공중합체, 아크릴 에스터-스티렌-아크릴로니트릴 공중합체, 스티렌-아크릴로니트릴 공중합체, 폴리아크릴로니트릴, 에틸렌 비닐 아세테이트, 폴리부틸렌 테레프탈레이트, 폴리에틸렌 테레프탈레이트 및 폴리옥시메틸렌으로 이루어진 군으로부터 선택된 1종 이상을 포함할 수 있다.In addition, preferably, a molded layer may be included between the cushion layer and the outer layer, and the molded layer may be polyurethane, thermoplastic polyurethane, polyethylene, polypropylene, polyester, polyether, polystyrene, polycarbonate, polypolyvinyl. Chloride, acrylonitrile-butadiene-styrene copolymer, acrylic ester-styrene-acrylonitrile copolymer, styrene-acrylonitrile copolymer, polyacrylonitrile, ethylene vinyl acetate, polybutylene terephthalate, polyethylene tere It may include one or more selected from the group consisting of phthalates and polyoxymethylene.

바람직하게는, 성형층은 외형층의 하단에서 외형층의 형상 또는 배치를 유지 또는 보조할 수 있다.Preferably, the molded layer may maintain or assist the shape or arrangement of the outer layer at the bottom of the outer layer.

바람직하게는, 외형층은, 적어도 일부에 문양이 형성될 수 있다.Preferably, the outer layer, the pattern may be formed at least in part.

바람직하게는, 접착층이 형성된 면은, 1개 이상의 절개 영역을 포함할 수 있다.Preferably, the surface on which the adhesive layer is formed may include one or more incision regions.

바람직하게는, 절개 영역은 평균 길이가 1 내지 5 mm 범위일 수 있다.Preferably, the incision area may have an average length in the range of 1 to 5 mm.

본 발명의 일 실시예에서, 화장품 용기용 명판을 포함하는 화장품 용기를 제공할 수 있다.In one embodiment of the present invention, it is possible to provide a cosmetic container comprising a name plate for a cosmetic container.

본 발명의 일 실시예에 따른 화장품 용기용 명판의 제조 방법은, 접착층, 쿠션층 및 외형층을 순차적으로 적층하는 단계; 적층체를 가압하여 융착하는 단계를 포함할 수 있다.Method for manufacturing a name plate for a cosmetic container according to an embodiment of the present invention, sequentially stacking the adhesive layer, the cushion layer and the outer layer; It may include the step of pressing the laminate to fuse.

본 발명의 또 다른 실시예에 따른 화장품 용기용 명판의 제조 방법은, 접착층, 기재층, 쿠션층, 성형층 및 외형층을 순차적으로 적층하는 단계; 적층체를 가압하여 융착하는 단계를 포함할 수 있다.According to another embodiment of the present invention, a method for manufacturing a nameplate for a cosmetic container includes sequentially stacking an adhesive layer, a base layer, a cushion layer, a molding layer, and an outer layer; It may include the step of pressing the laminate to fuse.

바람직하게는, 접착층, 기재층, 쿠션층, 성형층 및 외형층을 순차적으로 적층하는 단계 이전에, 접착증, 기재층, 쿠션층, 성형층 및 외형층으로 이루어진 군에서 선택된 2 이상의 층을 융착하는 1차 융착 단계를 더 포함할 수 있다.Preferably, prior to the step of sequentially laminating the adhesive layer, the base layer, the cushion layer, the molded layer and the outer layer, two or more layers selected from the group consisting of adhesion, base layer, cushion layer, molded layer and outer layer are fused. It may further include a primary fusion step.

더욱 바람직하게는, 접착층, 기재층, 쿠션층, 성형층 및 외형층을 순차적으로 적층하는 단계 이전에, 성형층과 외형층을 융착하는 1차 융착 단계를 더 포함할 수 있다.More preferably, prior to the step of sequentially laminating the adhesive layer, the base layer, the cushion layer, the molding layer, and the outer layer, the first welding step of fusing the molding layer and the outer layer may be further included.

바람직하게는, 적층체를 가압하여 융착하는 단계에서, 외형층의 적어도 일부에 문양이 형성될 수 있다.Preferably, in the step of pressing and welding the laminate, a pattern may be formed on at least a portion of the outer layer.

바람직하게는, 적층체를 가압하여 융착하는 단계에서, 또는 적층체를 가압하여 융착하는 단계 이후에, 접착층이 형성된 면에 절개 영역을 형성할 수 있다.Preferably, in the step of pressing and welding the laminate, or after the step of pressing and welding the laminate, an incision region may be formed on the surface on which the adhesive layer is formed.

본 발명에 따른 화장품 용기용 명판은, 접착층, 쿠션층 및 외형층을 구비함으로써, 화려하고 고급스러운 심미감을 형성함과 동시에, 쿠션층의 완충 작용으로 인해 용기의 파손을 방지할 수 있는 효과가 있다.The name plate for a cosmetic container according to the present invention has an effect of preventing damage to the container due to the cushioning action of the cushion layer while forming a luxurious and luxurious aesthetic feeling by providing an adhesive layer, a cushion layer, and an outer layer. .

또한, 본 발명은 기존의 플라스틱 명판을 제작하는 데 요구되는 사출용 금형을 제작할 필요가 없기 때문에, 저비용으로 단시간에 제작이 가능하며, 외형층, 쿠션층 및 접착층 등 본 발명에 따른 명판을 구성하는 모든 층을 올인원(All-In-One) 공정을 통해 제작이 가능하기 때문에, 접착제를 별도로 도포하거나, 수작업으로 양면 테이프를 부착하는 번거로운 공정이 요구되지 않는다.In addition, since the present invention does not need to manufacture an injection mold required for manufacturing an existing plastic nameplate, it can be manufactured in a short time at a low cost, and constitutes a nameplate according to the present invention such as an outer layer, a cushion layer and an adhesive layer. Since all layers can be manufactured through an all-in-one process, no cumbersome process of applying an adhesive separately or manually attaching double-sided tape is required.

또한, 본 발명은 화장품 용기용 명판을 제조하는데 있어서, 적층 및 융착하는 단계와 같은 간단한 공정으로 제조가 가능하기 때문에, 공정 비용이 감소하여 우수한 경쟁력을 확보할 수 있으며, 대량 생산이 가능할 수 있다.In addition, in the manufacture of a name plate for a cosmetic container, the present invention can be manufactured by a simple process such as lamination and fusing, so that process cost can be reduced to secure excellent competitiveness, and mass production may be possible.

본 발명의 상세한 설명에서 인용되는 도면을 보다 충분히 이해하기 위하여 각 도면의 간단한 설명이 제공된다.
도 1은, 화장품 용기용 명판이 부착된 콤팩트 용기를 나타낸 모식도이다.
도 2 및 3은, 본 발명의 각각의 실시예에 따른 화장품 용기용 명판을 화장품 용기에 부착한 구조의 모식도이다.
도 4 및 5는, 본 발명의 각각의 실시예에 따른 화장품 용기용 명판의 단면도이다.
도 6은, 본 발명의 일 실시예에서, 접착증에 절개 영역이 형성된 모습을 나타낸 도면이다.
도 7은, 본 발명의 일 실시예에 따른 화장품 용기용 명판을 포함하는 화장품 용기의 사진이다.BRIEF DESCRIPTION OF THE DRAWINGS In order to better understand the drawings cited in the detailed description of the present invention, a brief description of each drawing is provided.
1 is a schematic view showing a compact container with a nameplate for a cosmetic container attached.
2 and 3 are schematic diagrams of a structure in which a nameplate for a cosmetic container according to each embodiment of the present invention is attached to a cosmetic container.
4 and 5 are cross-sectional views of the nameplate for a cosmetic container according to each embodiment of the present invention.
FIG. 6 is a view showing a state in which an incision region is formed in an adhesion symptom in an embodiment of the present invention.
7 is a photograph of a cosmetic container including a name plate for a cosmetic container according to an embodiment of the present invention.

다른 식으로 정의되지 않는 한, 본 명세서에서 사용된 모든 기술적 및 과학적 용어들은 본 발명이 속하는 기술 분야에서 숙련된 전문가에 의해서 통상적으로 이해되는 것과 동일한 의미를 갖는다. 일반적으로, 본 명세서에서 사용된 명명법은 본 기술 분야에서 잘 알려져 있고 통상적으로 사용되는 것이다. 또한, 본 발명의 실시예를 설명함에 있어, 관련된 공지 구성 또는 기능에 대한 구체적인 설명이 본 발명의 실시예에 대한 이해를 방해한다고 판단되는 경우에는 그 상세한 설명은 생략한다. 또한, 이하에서 본 발명의 실시예들을 설명할 것이나, 본 발명의 기술적 사상은 이에 한정되거나 제한되지 않고 당업자에 의해 변형되어 다양하게 실시될 수 있다.Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by a person skilled in the art to which the present invention pertains. In general, the nomenclature used herein is well known and commonly used in the art. In addition, in describing the embodiments of the present invention, when it is determined that detailed descriptions of related well-known configurations or functions interfere with the understanding of the embodiments of the present invention, detailed descriptions thereof will be omitted. In addition, although the embodiments of the present invention will be described below, the technical spirit of the present invention is not limited or limited thereto, and can be variously implemented by a person skilled in the art.

이하, 본 발명에 대해서 구체적으로 설명하기로 한다.Hereinafter, the present invention will be described in detail.

본 발명에 따른 화장품 용기용 명판은, 일면 또는 양면에 대해서 접착력을 갖도록 형성된 접착층; 접착층의 상부에 배치되는 쿠션층; 및 쿠션층의 상부에 배치되는 외형층을 포함하며, 상기 명판은 화장품 용기의 뚜껑 외측면에 결합되어 화장품 용기의 외관을 형성할 수 있다. Nameplate for a cosmetic container according to the present invention, an adhesive layer formed to have adhesive force on one or both sides; A cushion layer disposed on the adhesive layer; And it includes an outer layer disposed on top of the cushion layer, the name plate can be coupled to the outer surface of the lid of the cosmetic container to form the appearance of the cosmetic container.

본 발명에 따른 화장품 용기용 명판은, 일면 또는 양면에 대해서 접착력을 갖도록 형성된 접착층, 쿠션층 및 외형층이 순차 적층된 구조를 가질 수 있다. The name plate for a cosmetic container according to the present invention may have a structure in which an adhesive layer, a cushion layer, and an outer layer formed to have adhesive force on one or both surfaces are sequentially stacked.

구체적으로, 외형층은 화장품 용기용 명판의 최상부에 형성된 층으로, 명판의 외형을 형성하는 역할을 한다.Specifically, the outer layer is a layer formed on the top of the name plate for the cosmetic container, and serves to form the outer shape of the name plate.

예를 들어, 외형층은 천연 가죽, 인조 가죽, 패브릭, PET 필름으로 이루어지는 군으로부터 선택되는 1종 이상을 포함할 수 있다. 외형층이 가죽으로 형성되는 경우, 가죽 고유의 고급스러움으로 화장품 용기의 외부를 장식하여, 외관의 미려함을 구현할 수 있다. 외형층이 패브릭 재질로 형성되는 경우, 부드럽고 따뜻하며 폭신한 느낌을 구현할 수 있다. 이 외에도 PET 필름, 섬유, 제지 등이 외형층으로 활용될 수 있다. 외형층은 프레스로 성형할 수 있고 소정의 두께를 가지는 재질이면 가능하며 본 발명의 예시에 제한되지 않는다.For example, the outer layer may include one or more selected from the group consisting of natural leather, artificial leather, fabric, and PET film. When the outer layer is formed of leather, the exterior of the cosmetic container can be decorated with the luxury of leather, thereby realizing the beauty of the exterior. When the outer layer is formed of a fabric material, it can realize a soft, warm and fluffy feeling. In addition to this, PET film, fiber, paper, etc. can be used as the outer layer. The outer layer can be formed by press and can be any material having a predetermined thickness and is not limited to the example of the present invention.

또한, 외형층은, 염화비닐 가죽, 합성피혁, 및 인공피혁으로 이루어진 군으로부터 선택된 1종 이상의 인조 가죽을 포함할 수 있다.Further, the outer layer may include at least one artificial leather selected from the group consisting of vinyl chloride leather, synthetic leather, and artificial leather.

구체적으로, 인조 가죽은 천연 가죽에 대응되는 용어로서, 염화비닐 가죽, 합성피혁, 및 인공피혁 등을 총칭한다. 본 발명에 사용되는 인조가죽은 공지된 것이라면 그 종류가 크게 제한되지 않으며, 예를 들어 부직포와 폴리우레탄을 소재로 하여 인공적으로 만든 가죽을 들 수 있으나, 이에 한정되지는 않는다. 경우에 따라서, 외형층은, 베이스 원단을 포함할 수 있으며, 베이스 원단의 적어도 일면은 합성 수지로 이루어질 수 있다. 예를 들어, 베이스 원단의 표면을 형성하는 합성 수지는 폴리비닐클로라이드, 폴리우레탄 및 열가소성 폴리우레탄으로 이루어지는 군으로부터 선택된 1종 이상을 포함할 수 있으나, 이에 한정되는 것은 아니다. 또한, 외형층의 색 또는 질감에 대해서는 특별히 한정하지 않는다.Specifically, artificial leather is a term corresponding to natural leather, and generically refers to vinyl chloride leather, synthetic leather, and artificial leather. The artificial leather used in the present invention is not limited in its kind as long as it is known, for example, artificial leather made of non-woven fabric and polyurethane, but is not limited thereto. In some cases, the outer layer may include a base fabric, and at least one surface of the base fabric may be made of synthetic resin. For example, the synthetic resin forming the surface of the base fabric may include one or more selected from the group consisting of polyvinyl chloride, polyurethane, and thermoplastic polyurethane, but is not limited thereto. In addition, the color or texture of the outer layer is not particularly limited.

외형층은, 적어도 일부에 문양이 형성될 수 있으며, 문양은 문양을 구성하는 부분이 함몰되거나 볼록하게 돌출되어 음각 또는 양각 형태로 형성될 수 있다. 문양은 화장품 용기의 외관을 수려하게 하도록 다양한 형상으로 형성될 수 있다. 예를 들어, 문구나 그림 등을 형성시켜 사용자에게 상표 또는 브랜드명 등의 정보 전달을 하고, 사용자의 시각적 심미성을 충족시킬 수 있게 하여 소비자의 만족도를 향상시킬 수 있다.In the outer layer, a pattern may be formed on at least a portion, and the pattern may be formed in an engraved or embossed shape by concave or convex portions constituting the pattern. The pattern may be formed in various shapes to enhance the appearance of the cosmetic container. For example, it is possible to improve customer satisfaction by forming a phrase or picture to transfer information such as a brand or brand name to the user, and to satisfy the user's visual aesthetics.

쿠션층은 접착층과 외형층 사이에 형성된 것으로, 화장품 용기의 우수한 쿠션감 및 볼륨감을 구현함과 동시에, 화장품 용기가 바닥, 벽, 테이블 등 단단한 외부 물체와 충돌 시, 화장품 용기 자체의 파손을 방지할 수 있고, 만약, 화장품 용기에 고상의 화장료가 수용된 경우, 고상의 화장료가 충돌에 의해 쉽게 깨지는 현상을 방지할 수 있다. The cushion layer is formed between the adhesive layer and the outer layer, and realizes an excellent cushioning and volume feeling of the cosmetic container, and prevents the cosmetic container itself from being damaged when the cosmetic container collides with a hard external object such as a floor, wall, or table. If, in the cosmetic container, the solid cosmetic is accommodated, it is possible to prevent the phenomenon that the solid cosmetic is easily broken by collision.

쿠션층은, 스펀지, 솜, 직물 및 발포폼으로 이루어진 군으로부터 선택된 1종 이상을 포함할 수 있다. The cushion layer may include one or more selected from the group consisting of sponge, cotton, fabric, and foam.

예를 들어, 스펀지는, 천연 고무, 합성수지, 폴리우레탄, 라텍스, 아크릴로니트릴-부타디엔 고무(NBR), 부타디엔 고무(BR), 스티렌-부타디엔 고무(SBR), 클로로프렌 고무(CR), 부틸고무(IIR), 이소프렌 고무(IR), 가황 에틸렌-프로필렌 고무(EPR), 다황화물 고무, 실리콘 고무, 플루오로 고무, 우레탄 고무, 아크릴 고무, 에틸렌 프로필렌 디엔 모노머(Ethylene propylene diene monomer, EPDM) 고무, 폴리비닐알코올(PVA), 에틸렌비닐아세테이트(EVA), 및 니트릴 고무로 이루어진 군으로부터 선택된 1종 이상의 재질로 이루어질 수 있으나, 이에 한정되는 것은 아니다. For example, sponge, natural rubber, synthetic resin, polyurethane, latex, acrylonitrile-butadiene rubber (NBR), butadiene rubber (BR), styrene-butadiene rubber (SBR), chloroprene rubber (CR), butyl rubber ( IIR), isoprene rubber (IR), vulcanized ethylene-propylene rubber (EPR), polysulfide rubber, silicone rubber, fluoro rubber, urethane rubber, acrylic rubber, ethylene propylene diene monomer (EPDM) rubber, poly It may be made of at least one material selected from the group consisting of vinyl alcohol (PVA), ethylene vinyl acetate (EVA), and nitrile rubber, but is not limited thereto.

또한, 솜의 원료가 되는 섬유는, 천연 섬유 및 합성 섬유로 이루어진 군으로부터 선택된 1종 이상을 포함할 수 있으나, 이에 한정되는 것은 아니다. 예를 들어, 천연섬유는 면화, 케이폭면, 코이어, 마닐라삼, 사이잘삼, 아마, 저마, 대마, 케나프, 아바카, 사이설삼, 카폭, 모시풀, 황마, 삼, 양모, 산양모, 캐시미어, 낙타모, 낙타털, 알파카, 모섬유, 가잠견, 야잠견, 석면 및 셀룰로오스계 섬유로 이루어진 군으로부터 선택된 1종 이상을 포함할 수 있다. 이 때, 마는 보통 솜의 형태로 제조가 불가능하지만, 마와 합성 섬유를 혼합한 후 저융점 섬유(Low Melting Fiber)를 혼합하여 열처리를 함으로써 솜의 형태로 제조할 수 있다. 예를 들어, 합성 섬유는 폴리노직 레이온, 비스코스 레이온, 류프라 레이온, 아세테이트, 트라이아세테이트, 폴리에스터계 섬유, 폴리우레탄계 섬유, 폴리에틸렌계 섬유, 폴리염화비닐계 섬유, 폴리비닐리덴계 섬유, 폴리테트라플루오로에틸렌계 섬유, 폴리올리펜계 섬유, 폴리아미드계 섬유, 카제인 섬유, 알긴산 섬유, 셀루로오스계 섬유, 고무 섬유, SBR 및 NR로 이루어진 군으로부터 선택된 1종 이상을 포함할 수 있으나, 이에 한정되는 것은 아니다. In addition, the fiber as a raw material of the cotton may include one or more selected from the group consisting of natural fibers and synthetic fibers, but is not limited thereto. For example, natural fibers are cotton, kapok cotton, coir, manila hemp, sisal hemp, flax, germa, hemp, kenaf, abaca, sisulsam, kapok, ramie grass, jute, hemp, wool, goat hair, cashmere , Camel hair, camel hair, alpaca, wool fibers, tentative dogs, nocturnal dogs, asbestos, and cellulose-based fibers. At this time, the hemp is usually impossible to manufacture in the form of cotton, but after mixing the hemp and synthetic fibers and mixing the low melting fiber (Low Melting Fiber) heat treatment can be produced in the form of a cotton. For example, synthetic fibers include polynosic rayon, viscose rayon, leupra rayon, acetate, triacetate, polyester fiber, polyurethane fiber, polyethylene fiber, polyvinyl chloride fiber, polyvinylidene fiber, polytetra Fluoroethylene-based fiber, poly-olipene-based fiber, polyamide-based fiber, casein fiber, alginic acid fiber, cellulose-based fiber, rubber fiber, SBR and NR may include one or more selected from the group consisting of, but not limited to It does not work.

또한, 직물은 상술한 천연 섬유 및 합성 섬유로 이루어진 군으로부터 선택된 1종 이상의 섬유를 직조하여 형성될 수 있다. In addition, the fabric may be formed by weaving one or more fibers selected from the group consisting of natural fibers and synthetic fibers described above.

또한, 발포폼은 고분자 수지를 이용하여 압출 발포 또는 비드 발포 방법을 통해 제조되는 것으로, 발포폼을 형성하는 고분자 수지는 예를 들어, 우레탄 수지, 아크릴 수지, 실리콘 수지, 에폭시 수지 및 합성 고무로 이루어진 군으로부터 선택되는 1종 이상을 포함할 수 있으나, 이에 한정되는 것은 아니다.In addition, the foamed foam is manufactured by extrusion foaming or bead foaming using a polymer resin, and the polymer resin forming the foamed foam is made of, for example, urethane resin, acrylic resin, silicone resin, epoxy resin and synthetic rubber. It may include one or more selected from the group, but is not limited thereto.

접착층은 화장품 용기용 명판의 최하부에 형성되는 것으로, 화장품 용기와 화장품 용기용 명판을 결합시키는 역할을 한다. 구체적으로, 화장품 용기용 명판은 접착층을 형성된 부분을 화장품 용기의 뚜껑 외측면에 결합시켜 화장품 용기의 외관을 형성할 수 있다.The adhesive layer is formed on the bottom of the nameplate for the cosmetic container, and serves to bond the cosmetic container with the nameplate for the cosmetic container. Specifically, the name plate for a cosmetic container can form the appearance of the cosmetic container by combining the portion formed with the adhesive layer on the outer surface of the lid of the cosmetic container.

접착층은, 열가소성, 열경화성 또는 광경화성 수지로 이루어진 군으로부터 선택된 1종 이상을 포함할 수 있다. 예를 들어, 접착층은, 폴리프로필렌(polypropylene), 폴리에틸렌(polyethylene), 폴리이미드(polyimide) 및 폴리아미드(polyamide)로 이루어진 군으로부터 선택된 1종 이상을 포함할 수 있으나, 이에 한정되는 것은 아니다. 이 때, 접착층은 일면 또는 양면에 대해서 접착력을 가지며, 바람직하게는, 양면에 대해서 접착력을 가질 수 있다. 구체적으로, 접착층은 양면 테이프의 구조로 형성될 수 있다. 접착층이 양면 테이프의 구조로 형성될 경우, 화장품 용기용 명판에 있어서, 접착층의 이형지를 제거하고 화장품 용기의 뚜껑 외측면에 부착하는 단순한 방법으로 화장품 용기에 명판을 형성할 수 있다.The adhesive layer may include one or more selected from the group consisting of thermoplastic, thermosetting or photocurable resins. For example, the adhesive layer may include at least one selected from the group consisting of polypropylene, polyethylene, polyimide, and polyamide, but is not limited thereto. At this time, the adhesive layer has an adhesive force to one side or both sides, and preferably, an adhesive force to both sides. Specifically, the adhesive layer may be formed of a double-sided tape structure. When the adhesive layer is formed of a double-sided tape structure, in the nameplate for a cosmetic container, the nameplate can be formed on the cosmetic container by a simple method of removing the release paper of the adhesive layer and attaching it to the outer surface of the lid of the cosmetic container.

본 발명의 일 실시예에 따른 화장품 용기용 명판은, 접착층과 쿠션층 사이에 기재층을 포함할 수 있다.The nameplate for a cosmetic container according to an embodiment of the present invention may include a base layer between the adhesive layer and the cushion layer.

기재층은 폴리에틸렌　테레프탈레이트(polyethylene terephthalate),　폴리에틸렌　나프탈레이트(polyethylene naphthalate), 폴리아크릴레이트(polyacrylate), 폴리카보네이트(polycarbonate), 폴리에테르이미드(polyetherimide) 및 폴리이미드(polyimide)로 이루어진 군으로부터 선택된 1종 이상을 포함할 수 있으나, 이에 한정되는 것은 아니다. The base layer is selected from the group consisting of polyethylene terephthalate, polyethylene naphthalate, polyacrylate, polycarbonate, polyetherimide and polyimide. It may include more than one species, but is not limited thereto.

이 때, 화장품 용기용 명판은 접착층과 쿠션층 사이에 기재층을 포함함으로써, 외형층과 접착층 사이의 쿠션층이 융착되는 과정에서 외부로 탈락되는 것을 방지할 수 있고, 쿠션층에 형성된 물질이 쿠션감을 잃고 볼륨감을 상실하는 것을 방지하며, 화장품 용기용 명판을 화장품 용기의 뚜껑에 부착할 경우에 안정감을 향상시킬 수 있다.At this time, the name plate for the cosmetic container includes a base layer between the adhesive layer and the cushion layer, so that the cushion layer between the outer layer and the adhesive layer can be prevented from falling out during the fusion process, and the material formed on the cushion layer is cushioned. It prevents loss of volume and loss of volume, and can improve stability when a nameplate for a cosmetic container is attached to the lid of a cosmetic container.

또한, 본 발명의 일 실시예에 따른 화장품 용기용 명판은, 쿠션층과 외형층 사이에 성형층을 포함할 수 있다.In addition, the name plate for a cosmetic container according to an embodiment of the present invention may include a molding layer between the cushion layer and the outer layer.

성형층은 폴리우레탄(poly urethane), 열가소성 폴리우레탄(thermoplastic polyurethane), 폴리에틸렌(polyethylene), 폴리프로필렌(polypropylene), 폴리에스터(polyester), 폴리에테르(polyether), 폴리스티렌(polystylene), 폴리카보네이트(polycarbonate), 폴리비닐 클로라이드(polyvinyl chloride), 아크릴로니트릴-부타다이엔-스티렌 공중합체(acrylonitrile-butadien-stylene copolymer), 아크릴에스터-스티렌-아크릴로니트릴 공중합체(acrylester-stylene-acrylonitrile copolymer), 스티렌-아크릴로니트릴 공중합체(stylene-acrylonitrile copolymer), 폴리아크릴로니트릴(polyacrylonitrile), 에틸렌 비닐 아세테이트(ethylene vinyl acetate), 폴리부틸렌 테레프탈레이트(polybuthylene therepthalate), 폴리에틸렌 테레프탈레이트(polyethylene therepthalate) 및 폴리옥시메틸렌(polyoxymethylene)으로 이루어진 군으로부터 선택된 1종 이상을 포함할 수 있으나, 이에 한정되는 것은 아니다. Molding layer is polyurethane (poly urethane), thermoplastic polyurethane (thermoplastic polyurethane), polyethylene (polyethylene), polypropylene (polypropylene), polyester (polyester), polyether (polyether), polystyrene (polystylene), polycarbonate (polycarbonate) ), polyvinyl chloride, acrylonitrile-butadien-stylene copolymer, acrylester-stylene-acrylonitrile copolymer, styrene -Acrylonitrile copolymer (stylene-acrylonitrile copolymer), polyacrylonitrile (polyacrylonitrile), ethylene vinyl acetate (ethylene vinyl acetate), polybutylene terephthalate (polybuthylene therepthalate), polyethylene terephthalate (polyethylene therepthalate) and polyoxy It may include one or more selected from the group consisting of methylene (polyoxymethylene), but is not limited thereto.

이 때, 쿠션층과 외형층 사이에 성형층은, 외형층의 하단에서 외형층의 형상 또는 배치를 유지 또는 보조할 수 있다. 구체적으로, 화장품 용기용 명판은 외형층과 쿠션층 사이에 성형층을 배치함으로써, 융착하는 과정에서 발생할 수 있는 외형층의 형태 변형과 외형층의 일부가 내려 앉는 문제를 방지하고, 외형층에 문양을 패터닝할 경우, 문양 주위가 쭈그러지는 현상을 방지할 수 있다.At this time, the molding layer between the cushion layer and the outer layer can maintain or assist the shape or arrangement of the outer layer at the lower end of the outer layer. Specifically, the name plate for the cosmetic container is disposed between the outer layer and the cushion layer to prevent the shape deformation of the outer layer that may occur during the fusion process and the problem of the part of the outer layer sitting down, and the pattern on the outer layer. In the case of patterning, it is possible to prevent the phenomenon of crushing around the pattern.

본 발명의 일 실시예에 따른 화장품 용기용 명판은, 접착층이 형성된 면에 1개 이상의 절개 영역을 더 포함할 수 있다. 절개 영역은 적층된 층 내부에 찬 공기를 외부로 빼냄으로써, 여러 개의 층을 올인원 공정으로 융착 시, 쿠션층 내부에 공기가 차 명판의 형태가 매끄럽게 형성되지 않으며, 이로 인해, 화장품 용기의 뚜껑에 부착시 명판의 엣지 부분이 들뜨는 현상을 방지할 수 있다.The nameplate for a cosmetic container according to an embodiment of the present invention may further include one or more incision regions on a surface on which an adhesive layer is formed. The incision region draws cold air inside the laminated layer to the outside, and when multiple layers are fused in an all-in-one process, the air inside the cushion layer does not form smoothly in the form of a name plate, and this causes the lid of the cosmetic container to When attaching, it is possible to prevent the phenomenon that the edge portion of the name plate is lifted up.

구체적으로, 절개 영역은 접착층이 형성된 면의 일부에 형성될 수 있고, 바람직하게는 접착층의 가장자리에 형성될 수 있다. 보다 구체적으로, 절개 영역은 접착층이 형성된 면의 임의의 중심점을 기준으로, 서로 대향하는 방향의 가장자리에, 하나 이상의 쌍으로 형성될 수 있다.Specifically, the incision region may be formed on a part of the surface on which the adhesive layer is formed, and preferably may be formed on the edge of the adhesive layer. More specifically, the incision regions may be formed in one or more pairs, on edges of directions facing each other, based on an arbitrary center point of the surface on which the adhesive layer is formed.

절개 영역의 평균 길이는 1 내지 5 mm 범위, 바람직하게는 2 내지 3 mm 범위로 형성될 수 있다. 또한, 절개 영역의 형상은, 명판의 외관에 영향을 미치지 않는 범위에서 다양한 형상으로 형성될 수 있다.The average length of the incision region may be formed in the range of 1 to 5 mm, preferably in the range of 2 to 3 mm. In addition, the shape of the incision region may be formed in various shapes within a range that does not affect the appearance of the name plate.

절개 영역의 깊이는, 외형층에 영향을 미치지 않는 범위에서 특별히 한정되지 않는다. 절개 영역은 접착층이 형성된 면에서 외형층 방향으로 깊이를 형성할 수 있으며, 필요에 따라, 접착층 및 기재층까지 절개 영역이 형성될 수 있다.The depth of the incision region is not particularly limited as long as it does not affect the outer layer. The incision region may form a depth in the direction of the outer layer from the surface on which the adhesive layer is formed, and if necessary, an incision region may be formed up to the adhesive layer and the base layer.

절개 영역의 개수, 형상, 길이, 깊이는 본 발명의 예시에 제한되지 않으며, 제조하고자 하는 명판의 형상 또는 조건에 따라 적절히 변형되어 형성될 수 있다.The number, shape, length, and depth of the incision regions are not limited to the examples of the present invention, and may be formed by appropriately deforming according to the shape or conditions of the nameplate to be manufactured.

본 발명은 상술한 화장품 용기용 명판을 포함하는 화장품 용기를 제공할 수 있다.The present invention can provide a cosmetic container comprising the name plate for the cosmetic container described above.

예를 들어, 화장품 용기는 콤팩트 용기, 스킨 용기, 로션 용기, 영양 크림 용기, 에센스 용기, 자외선 차단제 용기, 립스틱 용기, 향수 용기 및 색조 화장 용기 등을 포함할 수 있으나, 이에 한정되지는 않는다. 구체적으로, 본 발명에 따른 화장품 용기용 명판은 다양한 종류의 화장품을 수용할 수 있는 다양한 디자인의 용기에 모두 적용할 수 있다. For example, the cosmetic container may include, but is not limited to, a compact container, a skin container, a lotion container, a nutrition cream container, an essence container, a sunscreen container, a lipstick container, a perfume container, and a color makeup container. Specifically, the nameplate for a cosmetic container according to the present invention can be applied to all containers of various designs that can accommodate various types of cosmetics.

도 1을 참조하면, 본 발명의 일 실시예에 따른 화장품 용기용 명판을 포함하는 화장품 용기의 구조를 확인할 수 있다. 본 발명의 일 실시예에 따른 화장품 용기는, 용기 본체(10)와 용기 뚜껑(20)이 형성된 콤팩트 용기로서, 화장품 용기용 명판의 접착층이 형성된 면을 콤팩트 용기 뚜껑의 외측면에 부착시키는 간단한 방법으로 제조할 수 있다.1, the structure of a cosmetic container including a name plate for a cosmetic container according to an embodiment of the present invention can be confirmed. The cosmetic container according to an embodiment of the present invention is a compact container in which the container body 10 and the container lid 20 are formed, a simple method of attaching the surface on which the adhesive layer of the nameplate for the cosmetic container is formed to the outer surface of the compact container lid. Can be produced.

또한, 도 2를 참조하면, 용기 뚜껑(20)의 외측면에 본 발명에 따른 화장품 용기용 명판의 접착층(31)이 형성된 면이 부착된 구조를 확인할 수 있다. 구체적으로, 용기 뚜껑(20)의 외측면에 접착층(31), 쿠션층(32) 및 외형층(33)이 순차 적층된 것을 확인할 수 있다.In addition, referring to Figure 2, it can be seen the structure in which the adhesive layer 31 of the nameplate for a cosmetic container according to the present invention is attached to the outer surface of the container lid 20. Specifically, it can be seen that the adhesive layer 31, the cushion layer 32, and the outer layer 33 are sequentially stacked on the outer surface of the container lid 20.

또한, 도 3을 참조하면, 본 발명의 또 다른 실시예에 따른 화장품 용기용 명판이 부착된 화장품 용기의 구조를 확인할 수 있다. 구체적으로, 용기 뚜껑(20)의 외측면에 접착층(31), 기재층(34), 쿠션층(32), 성형층(35) 및 외형층(33)이 순차 적층된 화장품 용기용 명판이 부착된 것을 확인할 수 있다.In addition, referring to FIG. 3, it is possible to confirm the structure of a cosmetic container with a nameplate for a cosmetic container according to another embodiment of the present invention. Specifically, an adhesive layer 31, a base layer 34, a cushion layer 32, a molded layer 35, and an outer layer 33 are sequentially laminated on the outer surface of the container lid 20 to attach the nameplate for a cosmetic container. You can see that it has been done.

본 발명은 상술한 화장품 용기용 명판의 제조방법을 제공할 수 있다.The present invention can provide a method for manufacturing a name plate for a cosmetic container as described above.

본 발명의 일 실시예에 따른 화장품 용기용 명판 제조 방법으로서, 접착층, 쿠션층 및 외형층을 순차적으로 적층하는 단계; 적층체를 가압하여 융착하는 단계를 포함하는 방법을 제공할 수 있다.A method for manufacturing a name plate for a cosmetic container according to an embodiment of the present invention, sequentially stacking an adhesive layer, a cushion layer, and an outer layer; It is possible to provide a method comprising pressing and pressing a laminate.

본 발명의 또 다른 실시예에 따른 화장품 용기용 명판 제조 방법으로서, 접착층, 기재층, 쿠션층, 성형층 및 외형층을 순차적으로 적층하는 단계; 적층체를 가압하여 융착하는 단계를 포함하는 방법을 제공할 수 있다.A method for manufacturing a nameplate for a cosmetic container according to another embodiment of the present invention, sequentially stacking an adhesive layer, a base layer, a cushion layer, a molding layer, and an outer layer; It is possible to provide a method comprising pressing and pressing a laminate.

본 발명의 일 실시예에 따른 화장품 용기용 명판의 제조방법에 있어서, 적층체를 가압하여 융착하는 단계는 고주파 융착법에 의해 수행될 수 있다. 예를 들어, 고주파 융착법은, 상금형과 하금형으로 이루어진 융착 몰드를 이용할 수 있다. 이 때, 상금형과 하금형의 몰드 구조는, 상금형은 가운데 부분이 약간 볼록한 구조로 제작할 수 있고, 하금형은 평평한 구조로 제작할 수 있다. In the method of manufacturing a name plate for a cosmetic container according to an embodiment of the present invention, the step of pressing the laminate to fuse it may be performed by a high-frequency welding method. For example, as the high-frequency welding method, a fusion mold composed of an upper mold and a lower mold can be used. At this time, the mold structure of the upper mold and the lower mold can be produced with a slightly convex structure in the middle of the upper mold, and the lower mold can be produced with a flat structure.

구체적으로, 상금형과 하금형 사이에 접착층, 쿠션층 및 외형층을 순차 적층한 적층체 또는 접착층, 기재층, 쿠션층, 성형층 및 외형층이 순차 적층된 적층체를 장입할 수 있다. 그런 다음, 적층체가 장입된 상금형과 하금형에 가압 및 고주파를 가하여 적층체를 고주파 융착시키고, 적층체의 온도를 연화점까지 가열하여 원하는 형태로 소성 변형을 일으켜 본 발명에 따른 화장품 용기용 명판을 형성할 수 있다.Specifically, a laminate in which an adhesive layer, a cushion layer, and an outer layer are sequentially stacked between an upper mold and a lower mold or a laminate in which an adhesive layer, a base layer, a cushion layer, a molded layer, and an outer layer are sequentially stacked may be charged. Then, by applying pressure and high frequency to the upper and lower molds in which the laminate is loaded, the laminate is subjected to high-frequency fusion, and the temperature of the laminate is heated to a softening point to cause plastic deformation in a desired shape to produce a nameplate for a cosmetic container according to the present invention. Can form.

본 발명의 일 실시예에 따른 화장품 용기용 명판의 제조방법에 있어서, 접착층, 기재층, 쿠션층, 성형층 및 외형층을 순차적으로 적층하는 단계 이전에, 접착증, 기재층, 쿠션층, 성형층 및 외형층으로 이루어진 군에서 선택된 2 이상의 층을 융착하는 1차 융착 단계를 더 포함할 수 있다. In the method of manufacturing a name plate for a cosmetic container according to an embodiment of the present invention, prior to the step of sequentially laminating the adhesive layer, the base layer, the cushion layer, the molding layer and the outer layer, adhesion, base layer, cushion layer, molding A first fusing step of fusing two or more layers selected from the group consisting of a layer and an outer layer may be further included.

구체적으로, 접착층, 기재층, 쿠션층, 성형층 및 외형층을 가압하여 융착하는데 있어서, 접착증, 기재층, 쿠션층, 성형층 및 외형층으로 이루어진 군에서 선택된 2 이상의 층을 먼저 가압하여 1차 융착하고, 1차 융착한 층과, 1차 융착하지 않은 층들을 다시 적층한 후 가압하여 2차 융착하는 방법으로 본 발명에 따른 화장품 용기용 명판을 제조할 수 있다.Specifically, in pressing and bonding the adhesive layer, the substrate layer, the cushion layer, the molding layer, and the outer layer, first two or more layers selected from the group consisting of adhesion, base layer, cushion layer, molding layer, and outer layer are pressed first. Secondary fusion, primary fusion layer and non-primary fusion layer are laminated again and then pressurized to secondary fusion to produce a nameplate for cosmetic container according to the present invention.

구체적으로, 접착층, 기재층, 쿠션층, 성형층 및 외형층을 순차적으로 적층하는 단계 이전에, 성형층 및 외형층을 먼저 1차 융착시킬 수 있다. 그런 다음, 1차 융착 단계에서 융착하지 않은 층들인 접착층, 기재층, 쿠션층 위에 1차 융착 단계에서 융착시킨 성형층 및 외형층을 순차적으로 적층한 뒤, 2차 융착시킬 수 있다. Specifically, before the step of sequentially laminating the adhesive layer, the base layer, the cushion layer, the molding layer and the outer layer, the molding layer and the outer layer may be first fused. Then, the molding layer and the outer layer fused in the first welding step may be sequentially laminated on the adhesive layer, the base layer, and the cushion layer, which are the layers not fused in the first welding step, and then subjected to secondary welding.

본 발명의 일 실시예에서, 1차 융착 단계에서 사용하는 상금형과 하금형의 몰드 구조는, 상금형과 하금형 모두 가운데 부분이 약간 볼록한 구조로 제작하거나, 상금형은 가운데 부분이 약간 볼록한 구조로 제작하고, 하금형은 평평한 구조로 제작할 수 있다. 또한, 2차 융착 단계에서 사용하는 상금형과 하금형의 몰드 구조는, 상금형은 가운데 부분이 약간 볼록한 구조로 제작하고, 하금형은 평평한 구조로 제작할 수 있다. 이를 통해, 상부는 약간 볼록하게 튀어나온 형상을 가지고, 하부면은 평평한 형상을 가지는 본 발명에 따른 화장품 용기용 명판을 제조할 수 있다. 또한, 테두리 부분은 연화점에서 안쪽으로 말리는 깔끔한 마감 구조로 형성할 수 있다. 상금형과 하금형의 몰드 구조는 제작하고자 하는 명판의 형태에 따라 변형하여 제작할 수 있다.In one embodiment of the present invention, the mold structure of the upper mold and the lower mold used in the first fusion step is made of a structure with a slightly convex center in both the upper and lower molds, or a structure with a slightly convex center in the upper mold. It can be manufactured with and can be produced with a flat structure. In addition, the mold structure of the upper mold and the lower mold used in the second welding step, the upper mold may be manufactured with a slightly convex structure in the middle, and the lower mold may be manufactured with a flat structure. Through this, it is possible to manufacture a nameplate for a cosmetic container according to the present invention having a slightly convex protruding shape, and a lower surface having a flat shape. In addition, the border portion may be formed with a clean finishing structure that dries inward at the softening point. The mold structure of the upper mold and the lower mold can be manufactured by deforming according to the shape of the name plate to be produced.

예를 들어, 본 발명의 일 실시예에서, 1차 융착 단계에서 사용하는 상금형과 하금형의 몰드 구조는, 상금형과 하금형 모두 가운데 부분이 약간 볼록한 구조로 제작하고, 2차 융착 단계에서 사용하는 상금형과 하금형의 몰드 구조는, 상금형은 가운데 부분이 약간 볼록한 구조로 제작하고, 하금형은 평평한 구조로 제작할 수 있다. 이를 통해, 상부는 약간 볼록하게 튀어나온 형상을 가지고, 하부면은 평평한 형상을 가지는 본 발명에 따른 화장품 용기용 명판을 제조할 수 있으며, 쿠션층이 1차 융착 단계를 통해 약간 볼록하게 형성된 부분의 안쪽으로 채워지는 형상이 되어, 쿠션층의 일부가 외부로 탈락되는 것을 방지할 수 있다.For example, in one embodiment of the present invention, the mold structure of the upper mold and the lower mold used in the first fusion step is manufactured in a slightly convex structure in the middle of both the upper mold and the lower mold, and in the secondary fusion step The mold structure of the upper mold and the lower mold to be used can be produced with a slightly convex structure in the middle of the upper mold and a lower mold with a flat structure. Through this, the upper portion may have a slightly convexly protruding shape, and the lower surface may produce a nameplate for a cosmetic container according to the present invention having a flat shape, and the cushion layer may be slightly convexly formed through the primary welding step. It becomes a shape filled inward, and it is possible to prevent a part of the cushion layer from falling out.

본 발명의 일 실시예에 따른 화장품 용기용 명판의 제조방법에 있어서, 적층체를 가압하여 융착하는 단계에서, 외형층의 적어도 일부에 문양이 형성될 수 있다. 구체적으로, 적층체를 가압하여 융착하는 단계는 고주파 융착법으로 이루어지는데, 적층체에 대하여 고주파 융착 시, 상금형의 내면에 원하는 문양을 음각 또는 양각으로 형성한 융착 몰드를 사용하는 간단한 방법으로 외형층의 일부에 문양을 형성할 수 있다. 예를 들어, 1차 융착 및 2차 융착 단계를 수행하는 경우에는, 2차 융착하는 단계에서 외형층의 일부에 문양을 형성할 수 있다. In the method of manufacturing a name plate for a cosmetic container according to an embodiment of the present invention, in a step of pressing and fusion-bonding a laminate, a pattern may be formed on at least a part of the outer layer. Specifically, the step of pressing and welding the laminate is made of a high-frequency fusion method. When a high-frequency fusion is performed on the laminate, a simple method of using a fusion mold in which a desired pattern is formed in an intaglio or embossed shape on the inner surface of the upper mold is outlined. A pattern can be formed on a part of the layer. For example, in the case of performing the first fusion and the second fusion steps, a pattern may be formed on a part of the outer layer in the second fusion step.

이를 통해, 기존의 박음질을 통한 가죽의 패턴 형성과정에서, 박음질 주변의 가죽 표면이 쭈그러지는 등의 손상이 빈번하여 상품성이 저하되는 문제를 해결할 수 있고, 간단한 방법으로, 사용자에게 상표 또는 브랜드명 등의 정보 전달을 하고, 사용자의 시각적 심미성을 충족시킬 수 있게 하여 소비자의 만족도를 향상시킬 수 있다.Through this, in the process of forming the pattern of the leather through the existing lockstitch, it is possible to solve the problem that the productability is deteriorated due to frequent damage such as crushing of the leather surface around the lockstitch. It is possible to improve the satisfaction of consumers by delivering information and satisfying the visual aesthetics of users.

본 발명의 일 실시예에 따른 화장품 용기용 명판의 제조방법에 있어서, 적층체를 가압하여 융착하는 단계에서, 또는 적층체를 가압하여 융착하는 단계 이후에, 접착층이 형성된 면에 절개 영역을 형성할 수 있다. In the manufacturing method of the name plate for a cosmetic container according to an embodiment of the present invention, in the step of pressing the laminate to fuse, or after the step of pressing the laminate to fuse, an incision region is formed on the surface on which the adhesive layer is formed. Can.

구체적으로, 절개 영역은, 적층체를 가압하여 융착하는 단계에서 형성할 수 있다. 구체적으로, 적층체를 가압하여 융착하는 단계에서, 특정 형상을 가지며, 소정의 길이를 갖는 절개 부재가 형성된 하금형 융착 몰드를 사용함으로써, 적층체를 융착함과 동시에, 접착층이 형성된 면에 절개 영역을 올인원 공정으로 형성할 수 있다. Specifically, the incision region may be formed in the step of pressing and welding the laminate. Specifically, in the step of pressing and welding the laminate, by using a lower mold fusion mold having a specific shape and a cutting member having a predetermined length, the laminate is fused and a cut area is formed on the surface where the adhesive layer is formed. Can be formed by an all-in-one process.

또한, 절개 영역은, 적층체를 가압하여 융착하는 단계 이후에, 접착층이 형성된 면에 절개 영역을 형성하는 별도의 공정을 통해 형성될 수 있다. 구체적으로, 접착층이 형성된 면에 절개 영역을 형성하는 별도의 공정은, 특정 형상을 가지며, 소정의 길이를 갖는 절개 부재가 형성된 금형 융착 몰드를 사용하는 융착 공정을 통해 수행되거나, 명판 제조 완료 후 별도의 커팅 공정을 통해 수행될 수 있다.In addition, the incision region may be formed through a separate process of forming an incision region on the surface on which the adhesive layer is formed, after the step of pressing the fusion body to fuse. Specifically, a separate process of forming an incision region on the surface on which the adhesive layer is formed is performed through a fusing process using a mold fusing mold having a specific shape and an incision member having a predetermined length, or separately after completion of name plate production It can be performed through the cutting process.

본 발명의 일 실시예에 따른 화장품 용기용 명판의 제조방법에 있어서, 적층 또는 융착 단계 전 또는 후 단계에, 적층체를 원하는 형태로 절삭하는 단계를 더 포함할 수 있다. 이를 통해, 본 발명에 따른 화장품 용기용 명판은 다양한 형태로 제작될 수 있어, 다양한 디자인의 용기에 모두 적용될 수 있다. In the manufacturing method of the name plate for a cosmetic container according to an embodiment of the present invention, before or after the lamination or fusing step, the step of cutting the laminate to a desired shape may be further included. Through this, the nameplate for a cosmetic container according to the present invention can be manufactured in various forms, and thus can be applied to all containers of various designs.

이하 실시예를 통하여 본 발명을 더욱 상세히 설명하고자 한다. 이들 실시예는 오로지 본 발명을 예시하기 위한 것으로서, 본 발명의 범위가 이들 실시예에 의해 제한되는 것으로 해석되지는 않는 것은 당업계에서 통상의 지식을 가진 자에게 있어서 자명할 것이다.The present invention will be described in more detail through the following examples. These examples are only for illustrating the present invention, it will be apparent to those skilled in the art that the scope of the present invention is not to be construed as limited by these examples.

실시예Example 1: 화장품 용기용 명판 제조 1: Manufacture of nameplate for cosmetic container

접착층, 쿠션층 및 외형층을 순차적으로 적층한 뒤 적층체를 고주파 융착법을 이용하여 융착함으로써 본 발명에 따른 화장품 용기용 명판을 제조하였다. 구체적으로, 도 4를 참조하면, 상금형과 하금형 사이에, 접착층, 쿠션층 및 외형층을 순차 적층시킨 뒤, 고주파 융착을 통해 적층체를 융착하였다. 그 결과, 접착층(110), 쿠션층(120) 및 외형층(130)이 순차 적층된 구조의 본 발명에 따른 화장품 용기용 명판(100)이 제조되었다.An adhesive layer, a cushion layer, and an outer layer were sequentially stacked, and then the laminate was fused using a high-frequency welding method to prepare a nameplate for a cosmetic container according to the present invention. Specifically, referring to FIG. 4, an adhesive layer, a cushion layer, and an outer layer were sequentially stacked between the upper mold and the lower mold, and then the laminate was fused through high-frequency welding. As a result, the nameplate 100 for a cosmetic container according to the present invention was manufactured in a structure in which the adhesive layer 110, the cushion layer 120, and the outer layer 130 were sequentially stacked.

실시예Example 2: 화장품 용기용 명판 제조 2: Manufacture of nameplate for cosmetic container

상술한 고주파 융착법을 이용하여 본 발명에 따른 화장품 용기용 명판을 제조하였다. 구체적으로, 하기 도 5를 참조하면, 성형필름 PVC(250)와 인조가죽(230)을 적층한 뒤 고주파 융착을 통해 1차 융착을 하였다. 그 다음 양면테이프(210), PET(240), 스펀지(220)가 적층된 적층체 위에, 가접된 PVC(250)와 인조가죽(230)을 적층한 뒤, 2차 융착을 시켰다. 그 결과, 양면테이프(210), PET(240), 스펀지(220), PVC(250) 및 인조가죽(230)이 순차 적층된 구조의 화장품 용기용 명판이 제조되었다. 이 때, 상금형 내면에 문양을 형성시켜 2차 융착 시 인조가죽(230)에 문양이 형성되도록 하였다.The nameplate for a cosmetic container according to the present invention was manufactured using the above-described high-frequency fusion method. Specifically, referring to FIG. 5, the molding film PVC 250 and the artificial leather 230 were laminated, and then primary welding was performed through high-frequency welding. Then, a double-sided tape 210, PET 240, and sponge 220 were laminated on the laminated body, and then laminated PVC 250 and artificial leather 230 were laminated, followed by secondary welding. As a result, a nameplate for a cosmetic container having a structure in which double-sided tape 210, PET 240, sponge 220, PVC 250, and artificial leather 230 was sequentially stacked was manufactured. At this time, a pattern was formed on the inner surface of the upper mold so that the pattern was formed on the artificial leather 230 during the second welding.

화장품 용기용 명판 제조 후, 양면테이프(210) 및 PET(240) 층에 약 2 내지 3mm 길이의 절개 영역 4개를 형성시켰다. 도 6을 참조하면, 절개 영역(300)은 양면테이프(210) 면의 가장자리에 상하좌우로 4개 형성될 수 있다. 절개 영역(300)은 적층된 층 내부에 찬 공기를 외부로 빼냄으로써, 명판 내부에 찬 공기로 인해 화장품 용기의 뚜껑에 부착시 명판의 엣지 부분이 들뜨는 현상을 방지할 수 있다.After preparing the nameplate for the cosmetic container, four incision regions having a length of about 2 to 3 mm were formed on the double-sided tape 210 and the PET 240 layer. Referring to FIG. 6, four incision regions 300 may be formed on the edge of the surface of the double-sided tape 210 in the vertical direction. The incision region 300 can prevent the edge portion of the nameplate from being lifted when attached to the lid of the cosmetic container due to the cold air inside the nameplate by drawing the cold air inside the laminated layer to the outside.

이렇게 제조된 화장품 용기용 명판(200)의 양면테이프(210)의 이형지를 제거한 뒤 콤팩트 용기의 뚜껑 외측면에 접착하여 화장품 용기를 제조하였다. 그 사진은 도 7에서 확인할 수 있다. 도 7을 보면, 명판이 쿠션층을 포함하기 때문에 볼륨감이 있고 볼록하며, 외형층의 표면에 문양이 형성된 것을 확인할 수 있다. After removing the release paper of the double-sided tape 210 of the nameplate 200 for the cosmetic container thus prepared, it was adhered to the outer surface of the lid of the compact container to prepare a cosmetic container. The picture can be seen in FIG. 7. Referring to FIG. 7, it can be seen that since the name plate includes a cushion layer, there is volume and convexity, and a pattern is formed on the surface of the outer layer.

이처럼, 본 발명에 따르면 외형층, 쿠션층 및 접착층 등 명판을 구성하는 모든 층을 올인원(All-In-One) 공정으로 제작이 가능하기 때문에, 접착제를 별도로 도포하거나, 수작업으로 양면 테이프를 부착하는 번거로운 공정이 요구되지 않는다. 또한, 융착 시 쿠션층에 문양까지 형성시킬 수 있기 때문에, 한번의 공정으로 패턴 형성뿐만 아니라 접착층까지 부여된 화장품용 명판을 제조할 수 있는 장점이 있다.As described above, according to the present invention, since all layers constituting the nameplate such as the outer layer, the cushion layer, and the adhesive layer can be manufactured by an all-in-one process, an adhesive is separately applied or a double-sided tape is attached manually. No cumbersome process is required. In addition, since it is possible to form a pattern on the cushion layer during fusion, there is an advantage in that it is possible to manufacture a nameplate for cosmetics provided with an adhesive layer as well as pattern formation in one step.

이상으로 본 발명의 내용의 특정한 부분을 상세히 기술하였는바, 당업계의 통상의 지식을 가진 자에게 있어서, 이러한 구체적 기술은 단지 바람직한 실시양태일 뿐이며, 이에 의해 본 발명의 범위가 제한되는 것이 아닌 점은 명백할 것이다. 따라서, 본 발명의 실질적인 범위는 첨부된 청구항들과 그것들의 등가물에 의하여 정의된다고 할 것이다.The specific parts of the present invention have been described in detail above. For those skilled in the art, this specific technique is only a preferred embodiment, and the scope of the present invention is not limited thereby. It will be obvious. Accordingly, the substantial scope of the present invention will be defined by the appended claims and their equivalents.

10: 용기 본체
20: 용기 뚜껑
31: 접착층
32: 쿠션층
33: 외형층
34: 기재층
35: 성형층
100, 200: 화장품 용기용 명판
110, 210: 접착층
120, 220: 쿠션층
130, 230: 외형층
240: 기재층
250: 성형층
300: 절개 영역10: container body
20: container lid
31: adhesive layer
32: cushion layer
33: outer layer
34: base layer
35: molding layer
100, 200: nameplate for cosmetic container
110, 210: adhesive layer
120, 220: cushion layer
130, 230: outer layer
240: base layer
250: molding layer
300: incision area

Claims (17)

화장품 용기용 명판으로서,
일면 또는 양면에 대해서 접착력을 갖도록 형성된 접착층;
상기 접착층의 상부에 배치되는 쿠션층; 및
상기 쿠션층의 상부에 배치되는 외형층을 포함하며,
상기 명판은 상기 화장품 용기의 뚜껑 외측면에 결합되어 화장품 용기의 외관을 형성하는 것인, 화장품 용기용 명판.As a nameplate for cosmetic containers,
An adhesive layer formed to have adhesive force on one side or both sides;
A cushion layer disposed on the adhesive layer; And
It includes an outer layer disposed on the cushion layer,
The name plate is coupled to the outer surface of the lid of the cosmetic container to form the appearance of the cosmetic container, nameplate for cosmetic containers. 제 1 항에 있어서,
상기 쿠션층은, 스펀지, 솜, 직물 및 발포폼으로 이루어진 군으로부터 선택된 1종 이상을 포함하는 것을 특징으로 하는, 화장품 용기용 명판.According to claim 1,
The cushion layer is a nameplate for cosmetic containers, characterized in that it comprises at least one selected from the group consisting of sponge, cotton, fabric and foam. 제 1 항에 있어서,
상기 외형층은, 천연 가죽, 인조 가죽, 패브릭, PET 필름으로 이루어지는 군으로부터 선택되는 1종 이상을 포함하는 것을 특징으로 하는, 화장품 용기용 명판.According to claim 1,
The outer layer, natural leather, artificial leather, fabric, characterized in that it comprises at least one member selected from the group consisting of PET film, nameplate for cosmetic containers. 제 3 항에 있어서,
상기 외형층은, 염화비닐 가죽, 합성피혁 및 인공피혁으로 이루어진 군으로부터 선택된 1종 이상의 인조 가죽을 포함하는 것을 특징으로 하는, 화장품 용기용 명판.The method of claim 3,
The outer layer, vinyl chloride leather, characterized in that it comprises at least one artificial leather selected from the group consisting of synthetic leather and artificial leather, nameplate for cosmetic containers. 제 1 항에 있어서,
상기 접착층은, 폴리프로필렌(polypropylene), 폴리에틸렌(polyethylene), 폴리이미드(polyimide) 및 폴리아미드(polyamide)로 이루어진 군으로부터 선택된 1종 이상을 포함하는 것을 특징으로 하는, 화장품 용기용 명판.According to claim 1,
The adhesive layer is characterized in that it comprises at least one selected from the group consisting of polypropylene (polypropylene), polyethylene (polyethylene), polyimide (polyimide) and polyamide (polyamide), nameplate for cosmetic containers. 제 1 항에 있어서,
상기 접착층과 상기 쿠션층 사이에 기재층을 포함하고,
상기 기재층은 폴리에틸렌　테레프탈레이트(polyethylene terephthalate),　폴리에틸렌　나프탈레이트(polyethylene naphthalate), 폴리아크릴레이트(polyacrylate), 폴리카보네이트(polycarbonate), 폴리에테르이미드(polyetherimide) 및 폴리이미드(polyimide)로 이루어진 군으로부터 선택된 1종 이상을 포함하는 것을 특징으로 하는, 화장품 용기용 명판.According to claim 1,
A base layer between the adhesive layer and the cushion layer,
The base layer is selected from the group consisting of polyethylene terephthalate, polyethylene naphthalate, polyacrylate, polycarbonate, polyetherimide and polyimide. A name plate for a cosmetic container, comprising one or more kinds. 제 1 항에 있어서,
상기 쿠션층과 상기 외형층 사이에 성형층을 포함하고,
상기 성형층은 폴리우레탄(poly urethane), 열가소성 폴리우레탄(thermoplastic polyurethane), 폴리에틸렌(polyethylene), 폴리프로필렌(polypropylene), 폴리에스터(polyester), 폴리에테르(polyether), 폴리스티렌(polystylene), 폴리카보네이트(polycarbonate), 폴리비닐 클로라이드(polyvinyl chloride), 아크릴로니트릴-부타다이엔-스티렌 공중합체(acrylonitrile-butadien-stylene copolymer), 아크릴에스터-스티렌-아크릴로니트릴 공중합체(acrylester-stylene-acrylonitrile copolymer), 스티렌-아크릴로니트릴 공중합체(stylene-acrylonitrile copolymer), 폴리아크릴로니트릴(polyacrylonitrile), 에틸렌 비닐 아세테이트(ethylene vinyl acetate), 폴리부틸렌 테레프탈레이트(polybuthylene therepthalate), 폴리에틸렌 테레프탈레이트(polyethylene therepthalate) 및 폴리옥시메틸렌(polyoxymethylene)으로 이루어진 군으로부터 선택된 1종 이상을 포함하는 것을 특징으로 하는, 화장품 용기의 명판.According to claim 1,
A molding layer between the cushion layer and the outer layer,
The molding layer is polyurethane (poly urethane), thermoplastic polyurethane (thermoplastic polyurethane), polyethylene (polyethylene), polypropylene (polypropylene), polyester (polyester), polyether (polyether), polystyrene (polystylene), polycarbonate ( polycarbonate), polyvinyl chloride, acrylonitrile-butadien-stylene copolymer, acrylester-stylene-acrylonitrile copolymer, Styrene-acrylonitrile copolymer, polyacrylonitrile, ethylene vinyl acetate, polybuthylene therepthalate, polyethylene therepthalate and poly Characterized in that it comprises at least one selected from the group consisting of oxymethylene (polyoxymethylene), name plate of a cosmetic container. 제 1 항에 있어서,
상기 외형층은, 적어도 일부에 문양이 형성된 것을 특징으로 하는, 화장품 용기용 명판.According to claim 1,
The outer layer, characterized in that the pattern is formed on at least a portion, nameplate for cosmetic containers. 제 1 항에 있어서,
상기 접착층이 형성된 면은, 1개 이상의 절개 영역을 포함하는 것을 특징으로 하는, 화장품 용기용 명판.According to claim 1,
The adhesive layer is formed, characterized in that it includes at least one incision area, nameplate for cosmetic containers. 제 9 항에 있어서,
상기 절개 영역의 평균 길이는 1 내지 5 mm 범위인 것을 특징으로 하는, 화장품 용기용 명판.The method of claim 9,
The average length of the incision region is characterized in that in the range of 1 to 5 mm, nameplate for cosmetic containers. 제 1 항에 따른 화장품 용기용 명판을 포함하는 화장품 용기.Cosmetic container comprising the nameplate for the cosmetic container according to claim 1. 화장품 용기용 명판 제조 방법으로서,
접착층, 쿠션층 및 외형층을 순차적으로 적층하는 단계;
상기 적층체를 가압하여 융착하는 단계를 포함하는,
화장품 용기용 명판 제조 방법.As a method for manufacturing a nameplate for cosmetic containers,
Sequentially stacking the adhesive layer, the cushion layer and the outer layer;
Comprising the step of pressing and welding the laminate,
Method for manufacturing nameplate for cosmetic container. 화장품 용기용 명판 제조 방법으로서,
접착층, 기재층, 쿠션층, 성형층 및 외형층을 순차적으로 적층하는 단계;
상기 적층체를 가압하여 융착하는 단계를 포함하는,
화장품 용기용 명판 제조 방법.As a method for manufacturing a nameplate for cosmetic containers,
Sequentially stacking the adhesive layer, the base layer, the cushion layer, the molding layer and the outer layer;
Comprising the step of pressing and welding the laminate,
Method for manufacturing nameplate for cosmetic container. 제 13 항에 있어서,
상기 접착층, 기재층, 쿠션층, 성형층 및 외형층을 순차적으로 적층하는 단계 이전에,
접착증, 기재층, 쿠션층, 성형층 및 외형층으로 이루어진 군에서 선택된 2 이상의 층을 융착하는 1차 융착 단계를 더 포함하는 것을 특징으로 하는,
화장품 용기용 명판 제조 방법.The method of claim 13,
Before the step of sequentially laminating the adhesive layer, the base layer, the cushion layer, the molding layer and the outer layer,
Characterized in that it further comprises a first welding step of fusing two or more layers selected from the group consisting of adhesion, substrate layer, cushion layer, molding layer and outer layer,
Method for manufacturing nameplate for cosmetic container. 제 13 항에 있어서,
상기 접착층, 기재층, 쿠션층, 성형층 및 외형층을 순차적으로 적층하는 단계 이전에,
상기 성형층과 상기 외형층을 융착하는 1차 융착 단계를 더 포함하는 것을 특징으로 하는,
화장품 용기용 명판 제조 방법.The method of claim 13,
Before the step of sequentially laminating the adhesive layer, the base layer, the cushion layer, the molding layer and the outer layer,
It characterized in that it further comprises a first fusion step of fusion the molding layer and the outer layer,
Method for manufacturing nameplate for cosmetic container. 제 12 항 또는 제 13 항에 있어서,
상기 적층체를 가압하여 융착하는 단계에서, 상기 외형층의 적어도 일부에 문양이 형성되는 것을 특징으로 하는, 화장품 용기용 명판 제조 방법.The method of claim 12 or 13,
In the step of pressing and welding the laminate, a pattern is formed on at least a portion of the outer layer, a method for manufacturing a name plate for a cosmetic container. 제 12 항 또는 제 13 항에 있어서,
상기 적층체를 가압하여 융착하는 단계에서, 또는 상기 적층체를 가압하여 융착하는 단계 이후에, 상기 접착층이 형성된 면에 절개 영역을 형성하는 것을 특징으로 하는, 화장품 용기용 명판 제조 방법.The method of claim 12 or 13,
In the step of pressing and welding the laminate, or after the step of pressing and welding the laminate, a cut-out area is formed on a surface on which the adhesive layer is formed.
KR1020180169085A 2018-12-26 2018-12-26 Name plate for cosmetic containers and manufacturing method of the same KR20200079689A (en)