KR20200060621A - Composition for sun block - Google Patents

Abstract

The present invention provides a UV-blocking composition capable of maximizing UV-blocking strength while reducing a white cast and preventing skin penetration. According to one aspect of the present invention, the UV-blocking composition comprises zinc oxide and titanium dioxide, wherein the zinc oxide and the titanium dioxide are formed in a non-nano size. Here, the zinc oxide and the titanium dioxide may be formed to have an average particle size of 100-400 nm, and in order to prevent blocking materials from penetrating the skin and to prevent a white cast, more preferably, the zinc oxide may be formed to have an average particle size of 100-200 nm, and the titanium dioxide may be formed to have an average particle size of 100-300 nm.

Description

자외선 차단 조성물{COMPOSITION FOR SUN BLOCK}Sun protection composition {COMPOSITION FOR SUN BLOCK}

본 발명은 자외선 차단 조성물에 대한 것으로서, 보다 상세하게는 논나노(Non-nano) 무기분체가 포함된 자외선 차단 조성물에 대한 것이다.
The present invention relates to a sunscreen composition, and more particularly, to a sunscreen composition containing a non-nano inorganic powder.

일반적으로 자외선 차단제에 사용되는 자외선 차단 원료에는 자외선 차단 원리에 따라 유기 자외선 차단 원료와 무기 자외선 차단 원료로 분류된다. In general, sunscreen materials used in sunscreens are classified into organic sunscreen materials and inorganic sunscreen materials according to the sunscreen principle.

유기 자외선 차단 원료는 자외선이 조사되는 경우 분자 결합에 의한 화학적인 원리로 자외선을 흡수하며 투명한 외관과 부드러운 사용 감을 가지지만 피부 위에서 화학적 차단이 이루어지는 메커니즘에 따라 피부자극이나 눈시림을 유발함에 따라 화장품의 유해성이 중시되는 현 시장에서는 기피되는 경향이 있다. Organic sunscreen raw materials absorb ultraviolet rays by the chemical principle of molecular bonding when irradiated with ultraviolet rays, and have a transparent appearance and soft feeling, but they cause irritation or eye irritation due to the mechanism of chemical blocking on the skin. It tends to be avoided in the current market where hazards are important.

이에 최근에는 무기 자외선 차단 원료인 티타늄디옥사이드와 징크옥사이드를 이용하여 피부에 조사되는 자외선을 물리적으로 반사하여 자외선을 차단하는 기술이 소비자들의 요구에 부응하는 실정이다. Accordingly, recently, a technology that physically reflects ultraviolet rays irradiated to the skin by using titanium dioxide and zinc oxide, which are inorganic sunscreen raw materials, to block ultraviolet rays meets the needs of consumers.

하지만 이러한 무기 자외선 차단원료는 백색 판상의 파우더로서 가시광선 또한 반사하므로 피부에 도포하였을 경우에 바람직하지 않은 백색을 나타나게 하는 단점이 있다. 이 현상을 최소화하기 위하여 자외선 차단 원료를 적게 처방하면 충분한 자외선 차단 수치를 얻을 수 없는 문제가 발생된다. However, these inorganic sunscreen ingredients are powders on a white plate and also reflect visible light, so there is a disadvantage in that undesirable white color appears when applied to the skin. In order to minimize this phenomenon, if a small amount of sunscreen ingredients is prescribed, a problem that sufficient sunscreen values cannot be obtained occurs.

이에, 나노 사이즈의 무기 자외선 차단 원료를 이용하면 비교적 부드러운 사용감과 백탁이 적은 자외선 차단제를 만들 수 있으나 나노 무기 자외선 차단 원료의 작은 입자 사이즈로 인해 피부에 침투하여 모공이 석폐되는 위험성이 발생된다. Thus, the use of a nano-sized inorganic UV-blocking material can produce a relatively soft feeling of use and less sun-blocking sunscreen, but due to the small particle size of the nano-inorganic UV-blocking material, there is a risk of penetrating and penetrating the skin.

따라서, 나노 사이즈를 지양하여 피부 침투 및 모공 석폐의 위험성이 없으면서 자외선 차단력을 극대화시키는 무기차단 원료의 개발이 요구되는 실정이다.
Accordingly, there is a need to develop an inorganic barrier material that maximizes UV protection while avoiding the risk of skin penetration and pore depletion by avoiding nano size.

[선행기술문헌][Advanced technical literature]

한국공개특허 10-2015-0133110 (2015. 11. 27.)
Korea Patent Publication 10-2015-0133110 (2015. 11. 27.)

본 발명은 상기한 종래기술의 문제점을 해결하기 위한 것으로서, 본 발명의 목적은 자외선 차단력을 극대화하고 백탁을 감소시키면서도 피부 침투를 막는 자외선 차단 조성물을 제공한다.
The present invention is to solve the problems of the prior art described above, the object of the present invention is to provide a sunscreen composition that prevents skin penetration while maximizing sunscreen power and reducing cloudiness.

본 발명의 일 측면에 따른 자외선 차단 조성물은 징크옥사이드 및 티타늄디옥사이드를 포함하고, 상기 징크옥사이드 및 타타늄디옥사이드는 논나노(non-nano) 사이즈로 형성된다. The sunscreen composition according to an aspect of the present invention includes zinc oxide and titanium dioxide, and the zinc oxide and titanium dioxide are formed in a non-nano size.

이때, 상기 징크옥사이드 및 상기 티타늄디옥사이드의 평균입자크기는 100 내지 400nm로 형성될 수 있고, 차단 원료의 피부 침투를 막고 백탁을 방지하기 위해 더욱 바람직하게 상기 징크옥사이드의 평균입자크기는 100 내지 200nm이며, 상기 티타늄디옥사이드의 평균입자크기는 100 내지 300nm으로 형성될 수 있다. At this time, the average particle size of the zinc oxide and the titanium dioxide may be formed of 100 to 400nm, more preferably the average particle size of the zinc oxide is 100 to 200nm in order to prevent skin penetration of the blocking raw material and prevent clouding , The average particle size of the titanium dioxide may be formed of 100 to 300nm.

이때, 상기 징크옥사이드의 함량은 상기 티타늄디옥사이드의 함량보다 크게 형성되는데, 이는 티타늄디옥사이드가 주로 UVB차단을, 징크옥사이드는 UVA차단을 주로 담당하는데 UVB보다 UVA의 침투력이 더 강함에 기인하여 UVA차단을 주로 담당하는 징크옥사이드의 함량을 더 크게 하여 고른 UV차단을 하기 위함이다. 이때, 상기 징크옥사이드와 상기 티타늄디옥사이드의 함량비는 2.5:1 내지 3.8:1로 형성되는 것이 바람직하다. At this time, the content of the zinc oxide is formed to be larger than the content of the titanium dioxide, which is mainly titanium dioxide blocking UVB, zinc oxide mainly responsible for blocking UVA, but UVA blocking due to the stronger penetration of UVA than UVB. The main purpose is to provide even UV blocking by increasing the content of zinc oxide in charge. At this time, the content ratio of the zinc oxide and the titanium dioxide is preferably formed from 2.5: 1 to 3.8: 1.

또한, 상기 징크옥사이드와 상기 티타늄디옥사이드는 코팅제를 더 포함하고, 이들은 상기 자외선 차단제 조성물 중에서 0.65 내지 0.75wt%로 형성되는 것이 바람직하다. 이러한 코팅제는 금속산화물인 징크옥사이드와 티타늄디옥사이드가 제형 내에서 수분과 직접적으로 닿아 더 산화되거나 변화되는 것을 막아 자외선 차단력을 더욱 상승시킨다. In addition, the zinc oxide and the titanium dioxide further includes a coating agent, they are preferably formed of 0.65 to 0.75wt% of the sunscreen composition. Such a coating agent further increases the UV blocking power by preventing zinc oxide and titanium dioxide, which are metal oxides, from directly contacting moisture in the formulation to further oxidize or change.

이때, 바람직하게 징크옥사이드의 코팅제는 스타아릭애씨드를 0.10 내지 0.20wt%를 포함하고, 상기 티타늄디옥사이드의 코팅제는 실리카 0.10 내지 0.14wt% 또는 라우로일라이신 0.05 내지 0.10wt%중 적어도 어느 하나를 포함하도록 한다. At this time, preferably, the coating agent of zinc oxide contains 0.10 to 0.20wt% of the star aric acid, and the coating agent of titanium dioxide contains at least one of silica 0.10 to 0.14wt% or laurolysine 0.05 to 0.10wt%. Do it.

또한, 자외선 차단제 조성물은 액정유화원료 0.25 내지 1.65wt%를 더 포함하는 것이 바람직한데, 액정은 그 구조가 생체 세포막간지질의 구성 형태와 비슷하여 피부보호막 형성 및 보습 기능뿐만 아니라 여러 수용성, 유용성 효능 성분들의 보존성 및 안정성을 높여주고, 이들 성분들의 효과적인 전달매체로 응용되고 있다. 따라서, 조성물에서 상기 원료는 제형의 액정유화를 이루어 자외선 차단 원료가 효과적으로 피부 위에서 보존되도록 도와주고 안정적으로 자외선이 차단되도록 돕기 때문이다. In addition, it is preferable that the sunscreen composition further comprises 0.25 to 1.65 wt% of the liquid crystal emulsifying raw material, and the liquid crystal has a structure similar to that of the bio-membrane interstitial lipid, as well as a skin protective film forming and moisturizing function, as well as several water-soluble and useful efficacy components. It enhances the preservation and stability of them, and has been applied as an effective delivery medium for these ingredients. Therefore, in the composition, the raw material is formed by emulsifying the liquid crystal of the formulation, so that the UV blocking raw material is effectively preserved on the skin and stably blocking the UV.

이때 바람직하게 상기 액정유화원료는 세테에릴올리베이트 0.2 내지 1.2wt% 또는 솔비탄올리베이트 0.05 내지 1.45 wt으로 이루어질 수 있다. At this time, preferably, the liquid crystal emulsifying material may be made of 0.2 to 1.2 wt% of cetearyl oleate or 0.05 to 1.45 wt of sorbitan oleate.

또한, 자외선 차단제 조성물은 점증제를 0.15 내지 1.20wt% 더 포함하는 것이 바람직하고, 이 경우 더욱 바람직하게 점증제는 암모늄아크릴로일다이메틸타우레이트/베헤네스-25메타크라일레이트크로스폴리머로 형성될 수 있다. 점증제는 자외선차단원료인 징크옥사이드와 티타늄디옥사이드는 응집성이 강한 판상 파우더이므로 피부 위에 도포 시 파우더끼리 응집되어 비표면적이 줄어들어 자외선 차단 효과가 떨어지게 되므로 이를 분산시키고 그 상태를 유지하기 위함이다. In addition, the sunscreen composition preferably further comprises 0.15 to 1.20 wt% of a thickener, and in this case, more preferably, the thickener is formed of ammonium acryloyl dimethyl taurate / behenes-25 methacrylate cross polymer. Can be. The thickener is a plate powder with strong cohesive properties such as zinc oxide and titanium dioxide, which are cohesive when powdered on the skin.

나아가, 자외선 차단 조성물은 부틸렌글라이콜, 다이프로필렌글라이콜, 및 글리세린을 더 포함하는 것이 바람직한데 이는 제형의 보습을 도와주어 자외선 차단 원료의 피부에서 탈락을 방지하여주고 오랜 시간 자외선 차단력을 유지하도록 하기 위함이다.
Furthermore, it is preferable that the sunscreen composition further includes butylene glycol, dipropylene glycol, and glycerin, which helps moisturize the formulation, prevents the skin from falling off of the sunscreen raw material and maintains the sunscreen power for a long time. It is to do so.

본 발명에 따른 자외선 차단 조성물은 논-나노 사이즈의 무기 차단 원료를 이용하여 화학적으로 안전하며 나아가 모공 석폐와 피부 침투 위험성을 없앤다. The sunscreen composition according to the present invention is chemically safe using a non-nano sized inorganic barrier material and further eliminates the risk of pore decay and skin penetration.

나아가, 본 발명은 최적화 조성을 도출하여 이 경우 부족할 수 있는 자외선 차단력을 현저히 상승시킨다. Furthermore, the present invention derives an optimized composition and significantly increases the UV blocking power that may be lacking in this case.

또한, 본 발명은 거북한 백색 외관을 가지지 않으면서도 피부에 안전하며 충분한 자외선 차단 수치를 가진다.
In addition, the present invention is safe for the skin without having an unpleasant white appearance and has a sufficient UV protection level.

도 1은 본 발명의 실시예에 따른 자외선 차단 조성물을 피부에 도포한 경우의 백탁도를 보여주는 사진이다.
도 2a 내지 도 2c는 비교예1 내지 3에 따른 자외선 차단 조성물을 피부에 도포한 경우의 백탁도를 보여주는 사진이다. 1 is a photograph showing the cloudiness when the sunscreen composition according to an embodiment of the present invention is applied to the skin.
2A to 2C are photographs showing the cloudiness when the sunscreen composition according to Comparative Examples 1 to 3 is applied to the skin.

이하, 첨부한 도면을 참조하여 본 발명의 실시예에 대하여 당업자가 용이하게 실시할 수 있도록 상세히 설명한다. 본 발명은 다양한 변경을 가할 수 있고 여러 가지 실시예를 가질 수 있는 바, 특정 실시예들을 도면에 예시하여 상세하게 설명한다. 그러나, 이는 본 발명을 특정한 실시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변경, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings so that those skilled in the art can easily implement them. The present invention can be applied to various changes and can have various embodiments, and specific embodiments will be described in detail with reference to the drawings. However, this is not intended to limit the present invention to specific embodiments, and should be understood to include all modifications, equivalents, and substitutes included in the spirit and scope of the present invention.

제1, 제2 등과 같이 서수를 포함하는 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 상기 구성요소들은 상기 용어들에 의해 한정되지는 않는다. 상기 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다. Terms including ordinal numbers such as first and second may be used to describe various components, but the components are not limited by the terms. The terms are used only for the purpose of distinguishing one component from other components.

예를 들어, 본 발명의 권리 범위를 벗어나지 않으면서 제1 구성요소는 제2 구성요소로 명명될 수 있고, 유사하게 제2 구성요소도 제1 구성요소로 명명될 수 있다. 및/또는 이라는 용어는 복수의 관련된 기재된 항목들의 조합 또는 복수의 관련된 기재된 항목들 중의 어느 항목을 포함한다.For example, the first component may be referred to as a second component without departing from the scope of the present invention, and similarly, the second component may be referred to as a first component. The term and / or includes a combination of a plurality of related described items or any one of a plurality of related described items.

다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥 상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.
Unless otherwise defined, all terms used herein, including technical or scientific terms, have the same meaning as commonly understood by a person skilled in the art to which the present invention pertains. Terms, such as those defined in a commonly used dictionary, should be interpreted as having meanings consistent with meanings in the context of related technologies, and should not be interpreted as ideal or excessively formal meanings unless explicitly defined in the present application. Does not.

이하, 본 발명의 일 실시예에 따른 자외선 차단 조성물에 대하여 설명한다. 본 실시예에서는 주된 자외선 차단 원료로 징크옥사이드를 스테아릭애씨드로 코팅한 것과, 티타늄디옥사이드를 실리카와 라우로일라이신으로 코팅한 것을 사용하였으며, 여기에 액정유화원료로 세테아릴올리베이트와 솔비탄올리베이트를 사용하였다. 또한, 점증제로서 암모늄아크릴로일다이메틸타우레이트/베헤네스-25메타크라일레이트크로스폴리머를 사용하였다. 여기에 원료의 탈락을 방지하도록 부틸렌글라이콜, 다이프로필렌글라이콜, 글리세린을 더 혼입하였다. 한편, 백탁 현상 및 피부 침투를 방지하기 위해 징크옥사이드의 평균입자크기는 100 내지 200nm 사이의 것을 사용했으며, 티타늄디옥사이드의 평균입자크기는 100 내지 300nm 사이의 것을 사용하였다. Hereinafter, a sunscreen composition according to an embodiment of the present invention will be described. In this embodiment, zinc oxide is coated with stearic acid as the main UV-blocking material, and titanium dioxide is coated with silica and laurolysine. Here, cetearyl oleate and sorbitanol are used as liquid crystal emulsifiers. Rebates were used. In addition, ammonium acryloyl dimethyl taurate / behenes-25 methacrylate cross polymer was used as a thickener. Butylene glycol, dipropylene glycol, and glycerin were further mixed to prevent dropping of the raw materials. On the other hand, in order to prevent clouding and skin penetration, the average particle size of zinc oxide was used between 100 and 200 nm, and the average particle size of titanium dioxide was used between 100 and 300 nm.

실험예1Experimental Example 1

다음 [표 1]과 같이 실시예와 비교예1 내지 7의 조성물을 제조하였으며, [표 2]와 같이 자외선 차단지수 및 자외선 A 차단등급을 측정하였다. 본 실험예 1은 식약처 고시 '기능성 화장품 기준 및 시험방법' 중 '자외선 차단 기능성 시험법'에 따라 실시예 및 비교예 1 내지 7의 조성물에 대한 자외선 차단지수(SPF)를 측정하였다. 시료가 2mg/cm2 수준이 되도록 비트로스킨(VitroSkin)에 도포하고 15분 건조 후 SPF 290 S 측정기로 측정하였다. 자외선 차단지수는 3회 실험치의 평균값으로 정리하였고, 그 결과를 아래 [표 2]에 나타내었다.The compositions of Examples and Comparative Examples 1 to 7 were prepared as shown in [Table 1], and the UV blocking index and UV A blocking grade were measured as shown in [Table 2]. In Experimental Example 1, the sunscreen index (SPF) for the compositions of Examples and Comparative Examples 1 to 7 was measured according to the 'UV Protection Functional Test Method' among the 'Functional Cosmetic Standards and Test Methods' announced by the Ministry of Food and Drug Safety. The sample was applied to VitroSkin so that it was at the level of 2 mg / cm2, dried for 15 minutes, and measured with an SPF 290 S meter. The UV protection index was summarized as the average value of three experiments, and the results are shown in [Table 2] below.

성분ingredient 실시예Example 비교예1Comparative Example 1 비교예2Comparative Example 2 비교예3Comparative Example 3 비교예4Comparative Example 4 비교예5Comparative Example 5 비교예6Comparative Example 6 비교예7Comparative Example 7 징크옥사이드Zinc oxide 2.85000 2.85000 0.00000 0.00000 0.95000 0.95000 2.85000 2.85000 2.85000 2.85000 2.85000 2.85000 2.85000 2.85000 2.85000 2.85000 스테아릭애씨드Stearic Acid 0.15000 0.15000 0.00000 0.00000 0.05000 0.05000 0.15000 0.15000 0.15000 0.15000 0.15000 0.15000 0.15000 0.15000 0.15000 0.15000 티타늄디옥사이드Titanium dioxide 0.78500 0.78500 0.78500 0.78500 0.78500 0.78500 0.00000 0.00000 0.39250 0.39250 0.78500 0.78500 0.78500 0.78500 0.78500 0.78500 실리카Silica 0.13500 0.13500 0.13500 0.13500 0.13500 0.13500 0.00000 0.00000 0.06750 0.06750 0.13500 0.13500 0.13500 0.13500 0.13500 0.13500 라우로일라이신Laurolysine 0.08000 0.08000 0.08000 0.08000 0.08000 0.08000 0.00000 0.00000 0.04000 0.04000 0.08000 0.08000 0.08000 0.08000 0.08000 0.08000 세테아릴올리베이트Cetearyl Olivet 0.48000 0.48000 0.48000 0.48000 0.48000 0.48000 0.48000 0.48000 0.48000 0.48000 0.00000 0.00000 0.24000 0.24000 0.48000 0.48000 솔비탄올리베이트Sorbitan olive 0.32000 0.32000 0.32000 0.32000 0.32000 0.32000 0.32000 0.32000 0.32000 0.32000 0.00000 0.00000 0.16000 0.16000 0.32000 0.32000 암모늄아크릴로일다이메틸타우레이트/베헤네스-25메타크라일레이트크로스폴리머Ammonium acryloyl dimethyl taurate / behenes-25 methacrylate crosspolymer 0.70000 0.70000 0.70000 0.70000 0.70000 0.70000 0.70000 0.70000 0.70000 0.70000 0.70000 0.70000 0.70000 0.70000 0.30000 0.30000 정제수Purified water 75.49510 75.49510 78.49510 78.49510 77.49510 77.49510 76.49510 76.49510 75.99510 75.99510 76.29510 76.29510 75.95100 75.95100 75.89510 75.89510 세틸에틸헥사노에이트Cetylethylhexanoate 7.00000 7.00000 7.00000 7.00000 7.00000 7.00000 7.00000 7.00000 7.00000 7.00000 7.00000 7.00000 7.00000 7.00000 7.00000 7.00000 부틸렌글라이콜Butylene Glycol 6.00440 6.00440 6.00440 6.00440 6.00440 6.00440 6.00440 6.00440 6.00440 6.00440 6.00440 6.00440 6.00440 6.00440 6.00440 6.00440 글리세린glycerin 3.00050 3.00050 3.00050 3.00050 3.00050 3.00050 3.00050 3.00050 3.00050 3.00050 3.00050 3.00050 3.00050 3.00050 3.00050 3.00050 다이프로필렌글라이콜Dipropylene glycol 3.00000 3.00000 3.00000 3.00000 3.00000 3.00000 3.00000 3.00000 3.00000 3.00000 3.00000 3.00000 3.00000 3.00000 3.00000 3.00000

성분ingredient 실시예Example 비교예1Comparative Example 1 비교예2Comparative Example 2 비교예3Comparative Example 3 비교예4Comparative Example 4 비교예5Comparative Example 5 비교예6Comparative Example 6 비교예7Comparative Example 7 SPF in-vitroSPF in-vitro 78.378.3 69.269.2 72.1172.11 18.6118.61 34.234.2 58.2458.24 68.5668.56 64.3564.35 PFA in-vitroPFA in-vitro 19.3319.33 4.544.54 9.249.24 13.2513.25 15.3115.31 13.2513.25 15.4415.44 13.613.6

우선, 비교예1 및 2는 징크옥사이드가 미포함되거나 함량이 작아 PFA 등급이 현저하게 감소함을 확인할 수 있다. 나아가, 비교예3 및 4는 티타늄디옥사이드가 불포함되거나 함량이 작아서 PFA의 현저한 감소는 나타나지 않았지만 SFC 지수가 실시예에 비해 현저하게 떨어지는 결과를 얻을 수 있었다. First, Comparative Examples 1 and 2 can be confirmed that the zinc oxide is not included or the content is small, the PFA grade is significantly reduced. Further, in Comparative Examples 3 and 4, the titanium dioxide was not included or the content was small, so there was no significant decrease in PFA, but the SFC index was significantly lower than in the Examples.

비교예5 및 6은 액정유화원료가 불포함되거나 함량이 작은 경우인데, 비교예 1 내지 4에 비해서 SPF 지수 및 PFA 등급을 높게 나타났지만 무기 차단 원료 제형의 액정 유화가 효과적으로 이루어지지 못해 자외선 차단 원료가 효과적으로 피부 위에서 보존되지 못함에 기인한다. 단, 비교예 6의 경우에는 논나노 크기의 자외선 차단 원료를 사용했음에 기인하여 종래보다 자외선 차단 효과가 큰 것은 주목할 만하다. In Comparative Examples 5 and 6, when the liquid crystal emulsifying material is not included or the content is small, the SPF index and PFA grade were higher than those in Comparative Examples 1 to 4, but the liquid crystal emulsification of the inorganic blocking raw material formulation was not effective, and the UV blocking raw material was It is due to the inability to be effectively preserved on the skin. However, in the case of Comparative Example 6, it is noteworthy that the UV-blocking effect is greater than that of the prior art due to the use of a non-nano-size UV-blocking raw material.

비교예7은 점증제인 암모늄아크릴로일다이메틸타우레이트/베헤네스-25메타크라일레이트크로스폴리머의 함량을 작게 설정한 경우인데, 원료인 징크옥사이드와 티타늄디옥사이드가 응집성이 강한 판상 파우더임을 고려할 때, 비교예7의 조성물을 피부 위에 도포하였을 시 파우더끼리 응집되어 비표면적이 줄어들어 자외선 차단 효과가 떨어지지 않도록 분산되어있는 상태를 유지하는 정도가 떨어져 실시예보다 차단 지수가 작게 나온 것으로 해석된다. Comparative Example 7 is a case where the content of the thickening agent ammonium acryloyl dimethyl taurate / behenes-25 methacrylate cross polymer is set small, considering that the raw material zinc oxide and titanium dioxide are plate-like powders with strong cohesiveness. , When the composition of Comparative Example 7 is applied on the skin, it is interpreted that the powders are aggregated with each other and the specific surface area is reduced, so that the degree of maintaining the dispersed state is not lowered so that the UV-blocking effect is not reduced.

또한, 비교예 3 내지 7은 모두 부틸렌글라이콜, 다이프로필렌글라이콜, 및 글리세린을 포함하고 있어, 제형의 보습을 도와주어 자외선차단원료의 피부에서 탈락을 방지하여주고 오랜 시간 자외선 차단력을 유지하도록 도와주는 역할을 수행하도록 하였음에 기인하여 종래보다 모두 우수한 자외선 차단 능력이 확보된 것으로 판단된다.
In addition, Comparative Examples 3 to 7 all contain butylene glycol, dipropylene glycol, and glycerin, which help moisturize the formulation to prevent the skin from falling off of the sunscreen raw material and maintain the sunscreen for a long time Because it was intended to perform the role of helping to do so, it is judged that all of them have excellent UV protection ability.

실험예2Experimental Example 2

실험예1에서의 실시예와 비교예1 내지 3에 의해 제조된 자외선 차단 조성물 0.5g을 피부에 도포하여 백탁도에 대해 관능평가를 실시하였다. 도 1은 본 발명의 실시예에 따른 자외선 차단 조성물을 피부에 도포한 경우의 백탁도를 보여주는 사진이며, 도 2a 내지 도 2c는 비교예1 내지 3에 따른 자외선 차단 조성물을 피부에 도포한 경우의 백탁도를 보여주는 사진이다. Sensory evaluation was performed for the turbidity by applying 0.5 g of the sunscreen composition prepared in Examples 1 and 3 of Experimental Example 1 to the skin. 1 is a photograph showing the turbidity when the sunscreen composition according to an embodiment of the present invention is applied to the skin, and FIGS. It is a picture showing turbidity.

본 발명의 실시예에 의하는 경우에는 뛰어난 백탁 억제 효과를 보여준다. 그러나, 비교예에서는 모두 백탁 현상이 두드러지게 보임을 알 수 있다. 나아가, 비교예3의 경우에는 더 작은 자외선 차단 수치를 가짐에도 불구하고 실시예에 따른 조성물보다 더 백탁 현상이 두드러짐을 알 수 있다. 이는 실시예에 따른 조성물이 더 적은 무기차단제를 함유해도 더욱 높은 자외선 차단력을 갖는 효율성이 있음을 반증한다. According to the embodiment of the present invention, it shows excellent turbidity suppression effect. However, in the comparative example, it can be seen that the cloudiness phenomenon is prominently seen. Furthermore, it can be seen that in the case of Comparative Example 3, the whitening phenomenon was more pronounced than that of the composition according to the Example despite having a smaller UV blocking value. This demonstrates that even if the composition according to the embodiment contains less inorganic blocking agent, it has an efficiency with higher UV blocking power.

이상과 같이, 본 명세서와 도면에는 본 발명의 바람직한 실시예에 대하여 개시하였으며, 비록 특정 용어들이 사용되었으나, 이는 단지 본 발명의 기술 내용을 쉽게 설명하고 발명의 이해를 돕기 위한 일반적인 의미에서 사용된 것이지, 본 발명의 범위를 한정하고자 하는 것은 아니다. 여기에 개시된 실시예 외에도 본 발명의 기술적 사상에 바탕을 둔 다른 변형 예들이 실시 가능하다는 것은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 자명한 것이다.
As described above, in the present specification and drawings, preferred embodiments of the present invention have been disclosed, and although specific terms have been used, they are merely used in a general sense to easily describe the technical contents of the present invention and to help understand the invention. , It is not intended to limit the scope of the present invention. It is obvious to those skilled in the art to which the present invention pertains that other modified examples based on the technical idea of the present invention can be implemented in addition to the embodiments disclosed herein.

Claims (12)

징크옥사이드 및 티타늄디옥사이드를 포함하고, 상기 징크옥사이드 및 타타늄 옥사이드는 논나노(non-nano) 사이즈로 형성되는 것을 특징으로 하는 자외선 차단제 조성물.
A sunscreen composition comprising zinc oxide and titanium dioxide, wherein the zinc oxide and titanium oxide are formed in a non-nano size.
제1항에 있어서,
상기 징크옥사이드 및 상기 티타늄디옥사이드의 평균입자크기는 100 내지 400nm로 형성된 것을 특징으로 하는 자외선 차단제 조성물.
According to claim 1,
The average particle size of the zinc oxide and the titanium dioxide is a sunscreen composition, characterized in that formed in 100 to 400nm.
제2항에 있어서,
상기 징크옥사이드의 평균입자크기는 100 내지 200nm이며, 상기 티타늄디옥사이드의 평균입자크기는 100 내지 300nm으로 형성된 것을 특징으로 하는 자외선 차단제 조성물.
According to claim 2,
The zinc oxide has an average particle size of 100 to 200 nm, and the titanium dioxide has an average particle size of 100 to 300 nm.
제1항에 있어서,
상기 징크옥사이드의 함량은 상기 티타늄디옥사이드의 함량보다 크게 형성되는 것을 특징으로 하는 자외선 차단제 조성물.
According to claim 1,
The content of the zinc oxide is a sunscreen composition, characterized in that formed larger than the content of the titanium dioxide.
제4항에 있어서,
상기 징크옥사이드와 상기 티타늄디옥사이드의 함량비는 2.5:1 내지 3.8:1로 형성되는 것을 특징으로 하는 자외선 차단제 조성물.
The method of claim 4,
The content of the zinc oxide and the titanium dioxide is a sunscreen composition, characterized in that formed from 2.5: 1 to 3.8: 1.
제5항에 있어서,
상기 징크옥사이드와 상기 티타늄디옥사이드는 코팅제를 더 포함하고, 상기 자외선 차단제 조성물 중에서 0.65 내지 0.75wt%로 형성되는 것을 특징으로 하는 자외선 차단제 조성물.
The method of claim 5,
The zinc oxide and the titanium dioxide further comprises a coating agent, the sunscreen composition, characterized in that formed from 0.65 to 0.75wt% of the sunscreen composition.
제6항에 있어서,
상기 자외선 차단제 조성물은 징크옥사이드의 코팅제로서 스타아릭애씨드를 0.10 내지 0.20wt%를 포함하고, 상기 티타늄디옥사이드의 코팅제로서 실리카 0.10 내지 0.14wt% 또는 라우로일라이신 0.05 내지 0.10wt%중 적어도 어느 하나를 포함하는 것을 특징으로 하는 자외선 차단제 조성물.
The method of claim 6,
The sunscreen composition comprises 0.10 to 0.20wt% of star aric acid as a coating agent of zinc oxide, and 0.10 to 0.14wt% of silica as a coating agent of titanium dioxide or 0.05 to 0.10wt% of laurolysine It characterized in that it comprises a sunscreen composition.
제1항에 있어서,
상기 자외선 차단제 조성물은 액정유화원료 0.25 내지 1.65wt%를 더 포함하는 것을 특징으로 하는 자외선 차단제 조성물.
According to claim 1,
The sunscreen composition is a sunscreen composition characterized in that it further comprises a liquid crystal emulsifying raw material 0.25 to 1.65wt%.
제8항에 있어서,
상기 액정유화원료는 세테아릴올리베이트 0.2 내지 1.2wt% 또는 솔비탄올리베이트 0.05 내지 1.45 wt인 것을 특징으로 하는 자외선 차단제 조성물.
The method of claim 8,
The liquid crystal emulsifying raw material is a sunscreen composition, characterized in that 0.2 to 1.2wt% of cetearyl oleate or 0.05 to 1.45 wt of sorbitan oleate.
제1항에 있어서,
상기 자외선 차단제 조성물은 점증제를 0.5 내지 1.2wt% 더 포함하는 것을 특징으로 하는 자외선 차단 조성물.
According to claim 1,
The sunscreen composition is a sunscreen composition characterized in that it further comprises 0.5 to 1.2wt% of a thickener.
제10항에 있어서,
상기 점증제는 암모늄아크릴로일다이메틸타우레이트/베헤네스-25메타크라일레이트크로스폴리머인 것을 특징으로 하는 자외선 차단 조성물.
The method of claim 10,
The thickener is an ammonium acryloyl dimethyl taurate / behenes-25 methacrylate cross-polymer, characterized in that the sunscreen composition.
제1항에 있어서,
상기 자외선 차단 조성물에 부틸렌글라이콜, 다이프로필렌글라이콜, 및 글리세린 중 적어도 어느 하나가 더 포함되어 있는 것을 특징으로 하는 자외선 차단 조성물.
According to claim 1,
A sunscreen composition comprising at least one of butylene glycol, dipropylene glycol, and glycerin in the sunscreen composition.