KR20190107347A - Base film having improved resistance to tension fatigue - Google Patents
Base film having improved resistance to tension fatigue Download PDFInfo
- Publication number
- KR20190107347A KR20190107347A KR1020180028485A KR20180028485A KR20190107347A KR 20190107347 A KR20190107347 A KR 20190107347A KR 1020180028485 A KR1020180028485 A KR 1020180028485A KR 20180028485 A KR20180028485 A KR 20180028485A KR 20190107347 A KR20190107347 A KR 20190107347A
- Authority
- KR
- South Korea
- Prior art keywords
- base film
- film
- touch sensor
- stretchable
- tensile
- Prior art date
Abstract
Description
본 발명은 기재 필름에 관한 것이다. 보다 구체적으로, 본 발명은 기재 필름의 스트래처블 특성과 관련한 신뢰할 수 있는 물성 파라미터를 사전 정의하고, 이 물성 파라미터를 충족하는 기재 필름에 한하여 터치 센서에 적용함으로써, 터치 센서의 불량을 줄이고 제품 공정 수율을 향상시킬 수 있도록 하는 기술에 관한 것이다.The present invention relates to a base film. More specifically, the present invention predefine reliable property parameters related to the stretchable properties of the base film and apply them to the touch sensor only for the base film that meets these property parameters, thereby reducing the failure of the touch sensor and producing the product process. It relates to a technique that allows to improve the yield.
최근 디스플레이 관련 기술의 발달과 함께, 접거나 롤(Roll) 형상으로 말 수 있는 플렉서블한 디스플레이 장치들이 연구 및 개발되고 있으며, 한발 더 나아가 다양한 형태로의 변화가 가능한 스트레처블(stretchable) 디스플레이 장치에 대한 연구개발이 활발히 진행되고 있다.Recently, with the development of display-related technology, flexible display devices that can be folded or rolled into a roll shape have been researched and developed. Further, stretchable display devices that can be transformed into various forms are further developed. Korea's research and development is actively progressing.
이러한 스트레처블 디스플레이 장치에는 역시 스트레처블 특성을 갖는 터치 센서가 적용되어 사용자 입력을 터치 방식으로 감지하여 처리한다.The stretchable display device also has a touch sensor having a stretchable property to sense and process a user input by a touch method.
한편, 스트래처블 터치 센서의 구성요소 중의 하나인 기재 필름은 터치 센서 및 이 터치 센서가 적용된 디스플레이의 스트래처블 특성에 미치는 영향이 크며, 터치 센서의 다른 구성요소들이 스트래처블 특성과 관련한 물성 조건을 충족하여도 기재 필름이 이 물성 조건을 충족시키지 못하는 경우에는, 터치 센서의 스트래처블 특성이 크게 저하된다는 문제점이 있다.Meanwhile, the base film, which is one of the components of the stretchable touch sensor, has a large influence on the stretchable characteristics of the touch sensor and the display to which the touch sensor is applied, and the other components of the touch sensor are related to the stretchable characteristics. If the base film does not meet these physical property conditions even if the conditions are met, there is a problem that the stretchable characteristics of the touch sensor are greatly reduced.
따라서, 기재 필름을 터치 센서에 적용하기에 앞서 미리 기재 필름의 스트래처블 특성과 관련한 물성을 정의할 필요가 있으며, 이 물성을 충족하는 기재 필름에 한하여 터치 센서에 적용함으로써, 터치 센서의 불량을 줄이고 공정 수율을 향상시킬 필요성이 있다.Therefore, prior to applying the base film to the touch sensor, it is necessary to define the physical properties related to the stretchable properties of the base film in advance, and by applying the touch film only to the base film that satisfies this property, the defect of the touch sensor is prevented. There is a need to reduce and improve process yield.
본 발명은 기재 필름의 스트래처블 특성과 관련한 신뢰할 수 있는 물성 파라미터를 사전 정의하고, 이 물성 파라미터를 충족하는 기재 필름에 한하여 터치 센서에 적용함으로써, 터치 센서의 불량을 줄이고 제품 공정 수율을 향상시킬 수 있도록 하는 것을 기술적 과제로 한다.The present invention can predefine reliable property parameters related to the stretchable properties of the base film and apply them to the touch sensor only for the base film that meets these property parameters, thereby reducing the failure of the touch sensor and improving the product process yield. It is technical problem to make it possible.
이러한 기술적 과제를 해결하기 위한 본 발명에 따른 기재 필름의 내변형성 계수는 0 초과 0.1 미만이다.The deformation resistance coefficient of the base film according to the present invention for solving this technical problem is more than 0 and less than 0.1.
여기서, 내변형성 계수 = εN/ΔσN, εN은 기재 필름의 인장에 따른 영구변형길이 비율, ΔσN는 인장응력 변화량이다.Here, the deformation resistance coefficient = ε N / Δσ N , ε N is the ratio of the permanent strain length according to the tension of the base film, Δσ N is the amount of change in tensile stress.
본 발명에 따른 기재 필름의 두께는 50㎛ 내지 300㎛이다.The thickness of the base film which concerns on this invention is 50 micrometers-300 micrometers.
본 발명에 따른 기재 필름에 있어서, 상기 영구변형길이 비율(εN)은 인장 전후의 기재 필름의 길이 변화량에 대한 인장 전 기재 필름의 길이의 비이다.In the base film according to the present invention, the permanent deformation length ratio ε N is a ratio of the length of the base film before stretching to the amount of change in the length of the base film before and after stretching.
본 발명에 따른 기재 필름에 있어서, 상기 영구변형길이 비율(εN)은 0 초과 0.005 미만이다.In the base film according to the present invention, the permanent strain length ratio ε N is greater than 0 and less than 0.005.
본 발명에 따른 기재 필름에 있어서, 상기 인장응력 변화량(ΔσN)은 0 초과 0.1 미만이다.In the base film according to the present invention, the amount of change in tensile stress (Δσ N ) is greater than 0 and less than 0.1.
본 발명에 따른 기재 필름은 PDMS(Polydimethylsiloxane), PET(Polyehtylene-terephthalate), PES(Polyether sulfone),PEN(Polyethylenenaphthalate), PI(Polyimide), PMMA(PolymethymethAcrylate), PC(Polycarbonate)로 이루어진 군에서 선택된 하나 이상을 포함한다.The base film according to the present invention is one selected from the group consisting of PDMS (Polydimethylsiloxane), PET (Polyehtylene-terephthalate), PES (Polyether sulfone), PEN (Polyethylenenaphthalate), PI (Polyimide), PMMA (Polymethymethacrylate), PC (Polycarbonate) It includes the above.
본 발명에 따른 터치 스크린은 본 발명에 따른 기재 필름을 포함한다.The touch screen according to the invention comprises the base film according to the invention.
본 발명에 따르면, 기재 필름의 스트래처블 특성과 관련한 신뢰할 수 있는 물성 파라미터를 사전 정의하고, 이 물성 파라미터를 충족하는 기재 필름에 한하여 터치 센서에 적용함으로써, 터치 센서의 불량을 줄이고 제품 공정 수율을 향상시킬 수 있는 효과가 있다.According to the present invention, it is possible to predefine reliable property parameters related to the stretchable properties of the base film, and to apply them to the touch sensor only for the base film meeting the property parameters, thereby reducing the defect of the touch sensor and improving the product process yield. There is an effect that can be improved.
도 1은 본 발명의 일 실시 예에 있어서, 인장/회복 시험을 거치지 않은 기재 필름을 나타낸 도면이고,
도 2는 본 발명의 일 실시 예에 있어서, 인장/회복 시험 과정에서 기재 필름에 인장력이 인가되어 기재 필름이 인장된 상태를 나타낸 도면이고,
도 3은 본 발명의 일 실시 예에 있어서, 인장/회복 시험이 종료된 이후의 기재 필름을 나타낸 도면이다.1 is a view showing a base film that is not subjected to a tensile / recovery test in one embodiment of the present invention,
2 is a view showing a state in which the base film is tensioned by applying a tensile force to the base film in the tensile / recovery test process in an embodiment of the present invention,
3 is a view showing the base film after the tensile / recovery test in one embodiment of the present invention.
본 명세서에 개시되어 있는 본 발명의 개념에 따른 실시 예들에 대해서 특정한 구조적 또는 기능적 설명은 단지 본 발명의 개념에 따른 실시 예들을 설명하기 위한 목적으로 예시된 것으로서, 본 발명의 개념에 따른 실시 예들은 다양한 형태들로 실시될 수 있으며 본 명세서에 설명된 실시 예들에 한정되지 않는다.Specific structural or functional descriptions of the embodiments according to the inventive concept disclosed herein are provided only for the purpose of describing the embodiments according to the inventive concept. It may be embodied in various forms and is not limited to the embodiments described herein.
본 발명의 개념에 따른 실시 예들은 다양한 변경들을 가할 수 있고 여러 가지 형태들을 가질 수 있으므로 실시 예들을 도면에 예시하고 본 명세서에서 상세하게 설명하고자 한다. 그러나, 이는 본 발명의 개념에 따른 실시 예들을 특정한 개시 형태들에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변경, 균등물, 또는 대체물을 포함한다.Embodiments according to the inventive concept may be variously modified and have various forms, so embodiments are illustrated in the drawings and described in detail herein. However, this is not intended to limit the embodiments in accordance with the concept of the invention to the specific forms disclosed, it includes all changes, equivalents, or substitutes included in the spirit and scope of the present invention.
제1 또는 제2 등의 용어는 다양한 구성 요소들을 설명하는데 사용될 수 있지만, 상기 구성 요소들은 상기 용어들에 의해 한정되어서는 안 된다. 상기 용어들은 하나의 구성 요소를 다른 구성 요소로부터 구별하는 목적으로만, 예컨대 본 발명의 개념에 따른 권리 범위로부터 벗어나지 않은 채, 제1 구성 요소는 제2 구성 요소로 명명될 수 있고 유사하게 제2구성 요소는 제1구성 요소로도 명명될 수 있다.Terms such as first or second may be used to describe various components, but the components should not be limited by the terms. The terms are used only for the purpose of distinguishing one component from another, for example without departing from the scope of the rights according to the inventive concept, and the first component may be called a second component and similarly the second component. The component may also be referred to as the first component.
어떤 구성 요소가 다른 구성 요소에 "연결되어" 있다거나 "접속되어" 있다고 언급된 때에는, 그 다른 구성 요소에 직접적으로 연결되어 있거나 또는 접속되어 있을 수도 있지만, 중간에 다른 구성 요소가 존재할 수도 있다고 이해되어야 할 것이다. 반면에, 어떤 구성 요소가 다른 구성 요소에 "직접 연결되어" 있다거나 "직접 접속되어" 있다고 언급된 때에는 중간에 다른 구성 요소가 존재하지 않는 것으로 이해되어야 할 것이다. 구성 요소들 간의 관계를 설명하는 다른 표현들, 즉 "~사이에"와 "바로 ~사이에" 또는 "~에 이웃하는"과 "~에 직접 이웃하는" 등도 마찬가지로 해석되어야 한다.When a component is said to be "connected" or "connected" to another component, it may be directly connected to or connected to that other component, but it may be understood that other components may exist in the middle. Should be. On the other hand, when a component is said to be "directly connected" or "directly connected" to another component, it should be understood that no other component exists in the middle. Other expressions describing the relationship between components, such as "between" and "immediately between" or "neighboring to" and "directly neighboring", should be interpreted as well.
본 명세서에서 사용한 용어는 단지 특정한 실시 예를 설명하기 위해 사용된 것으로서, 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 명세서에서, "포함하다" 또는 "가지다" 등의 용어는 본 명세서에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성 요소, 부분품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.The terminology used herein is for the purpose of describing particular example embodiments only and is not intended to be limiting of the invention. Singular expressions include plural expressions unless the context clearly indicates otherwise. In this specification, terms such as "comprise" or "have" are intended to indicate that there is a feature, number, step, action, component, part, or combination thereof described herein, but one or more other features. It is to be understood that the present invention does not exclude the possibility of the presence or the addition of numbers, steps, operations, components, parts, or combinations thereof.
다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 나타낸다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥상 가지는 의미와 일치하는 의미를 갖는 것으로 해석되어야 하며, 본 명세서에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.Unless defined otherwise, all terms used herein, including technical or scientific terms, have the same meaning as commonly understood by one of ordinary skill in the art. Terms such as those defined in the commonly used dictionaries should be construed as having meanings consistent with the meanings in the context of the related art, and are not construed in ideal or excessively formal meanings unless expressly defined herein. Do not.
이하에서는, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 상세히 설명한다.Hereinafter, with reference to the accompanying drawings will be described in detail a preferred embodiment of the present invention.
도 1은 본 발명의 일 실시 예에 있어서, 인장/회복 시험을 거치지 않은 기재 필름을 나타낸 도면이고, 도 2는 본 발명의 일 실시 예에 있어서, 인장/회복 시험 과정에서 기재 필름에 인장력이 인가되어 기재 필름이 인장된 상태를 나타낸 도면이고, 도 3은 본 발명의 일 실시 예에 있어서, 인장/회복 시험이 종료된 이후의 기재 필름을 나타낸 도면이다.1 is a view showing a base film that is not subjected to a tensile / recovery test in one embodiment of the present invention, Figure 2 is a tensile force is applied to the base film during the tensile / recovery test in an embodiment of the present invention 3 is a view showing a state in which the base film is tensioned, and FIG. 3 is a view showing the base film after the tensile / recovery test is finished in one embodiment of the present invention.
도 1 내지 도 3을 참조하면, 본 발명의 일 실시 예는 인장 피로에 대한 내변형성이 향상된 기재 필름으로서, 기재 필름에 대한 복수 회의 인장/회복 시험 후의 기재 필름의 영구변형길이 비율(εN)과 인장응력 변화량(ΔσN)의 비인 내변형성 계수(εN/ΔσN)가 0 보다 크고 0.1 보다 작다.1 to 3, an embodiment of the present invention is a substrate film having improved deformation resistance to tensile fatigue, and a permanent deformation length ratio of the substrate film after a plurality of tensile / recovery tests on the substrate film (ε N ) The deformation resistance coefficient (ε N / Δσ N ), which is the ratio of the change in tensile stress (Δσ N ), is greater than 0 and less than 0.1.
배경기술을 설명하는 과정에서 설명한 바 있지만, 예를 들어, 스트래처블 터치 센서의 구성요소 중의 하나인 기재 필름은 터치 센서 및 이 터치 센서가 적용된 디스플레이의 스트래처블 특성에 미치는 영향이 매우 크며, 터치 센서의 다른 구성요소들이 스트래처블 특성과 관련한 물성 조건을 충족하여도 기재 필름이 이 물성 조건을 충족시키지 못하는 경우에는, 터치 센서의 스트래처블 특성이 크게 저하된다는 문제점이 있다.Although described in the process of describing the background art, for example, the substrate film, which is one of the components of the stretchable touch sensor, has a great influence on the stretchable characteristics of the touch sensor and the display to which the touch sensor is applied. Even if other components of the touch sensor satisfy the physical property condition related to the stretchable property, when the base film does not satisfy the physical property condition, there is a problem that the stretchable property of the touch sensor is greatly degraded.
따라서, 기재 필름을 터치 센서에 적용하기에 앞서 미리 기재 필름의 스트래처블 특성과 관련한 물성을 정의할 필요가 있으며, 이 물성을 충족하는 기재 필름에 한하여 터치 센서에 적용함으로써, 터치 센서의 불량을 줄이고 공정 수율을 향상시킬 필요성이 있다.Therefore, prior to applying the base film to the touch sensor, it is necessary to define the physical properties related to the stretchable properties of the base film in advance, and by applying the touch film only to the base film that satisfies this property, the defect of the touch sensor is prevented. There is a need to reduce and improve process yield.
본 발명의 일 실시 예에 있어서, 내변형성 계수(εN/ΔσN)는 이와 같은 배경에서 도출된 기재필름의 스트래처블 특성을 높은 신뢰성으로 사전 정의할 수 있도록 하는 신규한 물성 파라미터이다.In one embodiment of the present invention, the deformation resistance (ε N / Δσ N ) is a novel physical property parameter that enables to predefine the stretchable properties of the base film derived from such a background with high reliability.
내변형성 계수(εN/ΔσN)에 대하여 보다 구체적으로 설명하면 다음과 같다.The deformation resistance coefficient (ε N / Δσ N ) is described in more detail as follows.
내변형성 계수(εN/ΔσN)는 기재 필름에 대한 복수 회의 인장/회복 시험 후의 기재 필름의 영구변형길이 비율(εN)과 인장응력 변화량(ΔσN)의 비이다.The deformation resistance (ε N / Δσ N ) is a ratio of the permanent strain length ratio (ε N ) and the tensile stress change amount (Δσ N ) of the base film after a plurality of tensile / recovery tests on the base film.
예를 들어, 영구변형길이 비율(εN)은 인장 전후의 기재 필름의 길이 변화량에 대한 인장 전 기재 필름의 길이의 비일 수 있다. 도 3에 개시된 예를 참조하면, 인장 전의 기재 필름의 길이가 L, 인장 후 영구변형되어 늘어난 기재 필름의 길이가 L+2L1이며, 영구변형길이 비율(εN)은 2×L1/L이다. 예를 들어, 인장응력 변화량(ΔσN)의 단위는 MPa일 수 있다.For example, the permanent strain length ratio ε N may be a ratio of the length of the base film before stretching to the amount of change in the length of the base film before and after stretching. Referring to the example disclosed in FIG. 3, the length of the base film before stretching is L, the length of the base film which is permanently stretched after stretching is L + 2L1, and the permanent strain length ratio ε N is 2 × L1 / L. For example, the unit of the change in tensile stress amount Δσ N may be MPa.
본 발명의 일 실시 예에 따른 기재 필름은 내변형성 계수(εN/ΔσN)가 0 보다 크고 0.1 보다 작은 조건을 충족한다.The base film according to an embodiment of the present invention satisfies the condition that the deformation resistance (ε N / Δσ N ) is greater than 0 and less than 0.1.
예를 들어, 스트레처블 필름의 주재료인 PDMS(Polydimethylsiloxane)는 신축성, 즉, 스트래처블 특성이 뛰어나지만, N회 이상 인장/회복 시험을 반복하였을 경우 영구 변형으로 성능이 저하되는 경향이 있다. 50% 인장 후 회복 시, 임의의 N회에서의 필름의 영구변형길이 비율(εN)과 인장응력 변화량(ΔσN)의 비가 0.1 미만이면, 변형에 대한 내성이 있는 것으로 볼 수 있다. 변형에 대한 내성이 있으면, 초기 대비 물리적 변형에 대한 변화가 없는 것을 뜻한다. 즉 내변형성이 있는 것으로 판단되면, 스트레처블 기재로서 상용 가능하며, 이 기재가 터치 센서에 적용되는 경우, 터치 센서의 스트래처블 특성 또한 안정적으로 확보할 수 있다.For example, PDMS (Polydimethylsiloxane), which is a main material of the stretchable film, has excellent elasticity, that is, a stretchable property, but when the tensile / recovery test is repeated N times or more, the performance tends to decrease due to permanent deformation. Upon recovery after 50% tension, if the ratio of the permanent strain length (ε N ) and tensile stress change (Δσ N ) of the film at any N times is less than 0.1, it may be considered to be resistant to deformation. Tolerance to deformation means no change to initial physical deformation. That is, if it is determined that there is deformation resistance, it is commercially available as a stretchable base material, and when the base material is applied to the touch sensor, the stretchable property of the touch sensor can be secured stably.
예를 들어, 안정적이고 신뢰할 수 있는 스트래처블 특성을 확보하기 위하여, 기재 필름의 두께는 50㎛ - 300㎛인 것이 바람직하다.For example, in order to ensure stable and reliable stretchable properties, the thickness of the base film is preferably 50 µm-300 µm.
예를 들어, 영구변형길이 비율(εN)은 0 초과 0.005 미만이고, 인장응력 변화량(ΔσN)은 0 초과 0.1 미만일 수 있다. 이러한 조건들을 충족시키는 기재 필름은 반복되는 인장 및 회복 후에도 안정적이고 신뢰할 수 있는 스트래처블 특성을 확보할 수 있다.For example, the permanent strain length ratio ε N may be greater than 0 and less than 0.005, and the amount of change in tensile stress Δσ N may be greater than 0 and less than 0.1. A base film that meets these conditions can ensure stable and reliable stretchable properties even after repeated stretching and recovery.
예를 들어, 기재 필름은 PDMS(Polydimethylsiloxane), PET(Polyehtylene-terephthalate), PES(Polyether sulfone),PEN(Polyethylenenaphthalate), PI(Polyimide), PMMA(PolymethymethAcrylate), PC(Polycarbonate)로 이루어진 군에서 선택된 하나 이상을 포함할 수 있다.For example, the base film is one selected from the group consisting of polydimethylsiloxane (PDMS), polyethylene-terephthalate (PET), polyether sulfone (PES), polyethylenenaphthalate (PEN), polyimide (PI), polymethymethacrylate (PMMA), and polycarbonate (PC). It may contain the above.
보다 구체적인 예로, 기재 필름은 스트래처블 특성과 광 투과성이 우수한 임의의 물질로 구성될 수 있다.As a more specific example, the base film may be composed of any material having excellent stretchable properties and light transmittance.
예를 들어, 기재 필름은 투명 광학 필름 또는 편광판 등일 수 있다.For example, the base film may be a transparent optical film or a polarizing plate.
예를 들어, 투명 광학 필름으로는 투명성, 기계적 강도, 열 안정성이 우수한 필름이 사용될 수 있으며, 구체적인 예로는, 폴리에틸렌테레프탈레이트, 폴리에틸렌이소프탈레이트, 폴리에틸렌나프탈레이트, 폴리부틸렌테레프탈레이트 등의 폴리에스테르계 수지; 디아세틸셀룰로오스, 트리아세틸셀룰로오스 등의 셀룰로오스계 수지; 폴리카보네이트계 수지; 폴리메틸(메타)아크릴레이트, 폴리에틸(메타)아크릴레이트 등의 아크릴계 수지; 폴리스티렌, 아크릴로니트릴-스티렌 공중합체 등의 스티렌계 수지; 폴리에틸렌, 폴리프로필렌, 시클로계 또는 노보넨 구조를 갖는 폴리올레핀, 에틸렌-프로필렌 공중합체 등의 폴리올레핀계 수지; 염화비닐계 수지; 나일론, 방향족 폴리아미드 등의 아미드계 수지; 이미드계 수지; 폴리에테르술폰계 수지; 술폰계 수지; 폴리에테르에테르케톤계 수지; 황화 폴리페닐렌계 수지; 비닐알코올계 수지; 염화비닐리덴계 수지; 비닐부티랄계 수지; 알릴레이트계 수지; 폴리옥시메틸렌계 수지; 에폭시계 수지 등과 같은 열가소성 수지로 구성된 필름을 들 수 있으며, 상기 열가소성 수지의 블렌드물로 구성된 필름도 사용할 수 있다. 또한, (메타)아크릴계, 우레탄계, 아크릴우레탄계, 에폭시계, 실리콘계 등의 열경화성 수지 또는 자외선 경화형 수지로 된 필름을 이용할 수도 있다. 이와 같은 투명 광학 필름의 두께는 적절히 결정될 수 있지만, 일반적으로는 강도나 취급성 등의 작업성, 박층성 등을 고려하여, 1 ∼ 500㎛로 결정될 수 있다. 특히 1 ∼ 300㎛가 바람직하고, 5 ∼ 200㎛가 보다 바람직하다.For example, a film having excellent transparency, mechanical strength, and thermal stability may be used as the transparent optical film, and specific examples thereof include polyesters such as polyethylene terephthalate, polyethylene isophthalate, polyethylene naphthalate, and polybutylene terephthalate. Suzy; Cellulose resins such as diacetyl cellulose and triacetyl cellulose; Polycarbonate resins; Acrylic resins such as polymethyl (meth) acrylate and polyethyl (meth) acrylate; Styrene resins such as polystyrene and acrylonitrile-styrene copolymers; Polyolefin-based resins such as polyethylene, polypropylene, cyclo-based or norbornene-structured polyolefins, ethylene-propylene copolymers; Vinyl chloride-based resins; Amide resins such as nylon and aromatic polyamides; Imide resin; Polyether sulfone resin; Sulfone resins; Polyether ether ketone resins; Sulfided polyphenylene resins; Vinyl alcohol-based resins; Vinylidene chloride-based resins; Vinyl butyral resin; Allyl resins; Polyoxymethylene resin; And films composed of thermoplastic resins such as epoxy resins, and the like, and films composed of blends of the above thermoplastic resins may also be used. Moreover, the film of thermosetting resin or ultraviolet curable resin, such as (meth) acrylic-type, urethane type, acrylurethane type, epoxy type, and silicone type, can also be used. Although the thickness of such a transparent optical film can be suitably determined, generally, it can be determined to 1-500 micrometers in consideration of workability, thinness, etc., such as intensity | strength and handleability. 1-300 micrometers is especially preferable, and 5-200 micrometers is more preferable.
이러한 투명 광학 필름은 적절한 1종 이상의 첨가제가 함유된 것일 수도 있다. 첨가제로는, 예컨대 자외선흡수제, 산화방지제, 윤활제, 가소제, 이형제, 착색방지제, 난연제, 핵제, 대전방지제, 안료, 착색제 등을 들 수 있다. 투명 광학 필름은 필름의 일면 또는 양면에 하드코팅층, 반사방지층, 가스배리어층과 같은 다양한 기능성층을 포함하는 구조일 수 있으며, 기능성층은 전술한 것으로 한정되는 것은 아니며, 용도에 따라 다양한 기능성층을 포함할 수 있다.Such a transparent optical film may contain an appropriate one or more additives. As an additive, a ultraviolet absorber, antioxidant, a lubricant, a plasticizer, a mold release agent, a coloring agent, a flame retardant, a nucleating agent, an antistatic agent, a pigment, a coloring agent, etc. are mentioned, for example. The transparent optical film may have a structure including various functional layers such as a hard coating layer, an antireflection layer, and a gas barrier layer on one or both surfaces of the film, and the functional layer is not limited to the above-described ones, and various functional layers may be formed depending on the purpose. It may include.
또한, 필요에 따라 투명 광학 필름은 표면 처리된 것일 수 있다. 이러한 표면 처리로는 플라즈마(plasma) 처리, 코로나(corona) 처리, 프라이머(primer) 처리 등의 건식 처리, 검화 처리를 포함하는 알칼리 처리 등의 화학 처리 등을 들 수 있다.In addition, the transparent optical film may be surface-treated as needed. Such surface treatments include, for example, plasma treatments, corona treatments, dry treatments such as primer treatments, and chemical treatments such as alkali treatments including saponification treatments.
또한, 투명 광학 필름은 등방성 필름, 위상차 필름 또는 보호필름(Protective Film)일 수 있다.In addition, the transparent optical film may be an isotropic film, a retardation film or a protective film.
등방성 필름인 경우 면내 위상차(Ro, Ro=[(nx-ny)ⅹd], nx, ny는 필름 평면 내의 주굴절률, d는 필름 두께이다.)가 40nm 이하이고, 15nm 이하가 바람직하며, 두께방향 위상차(Rth, Rth=[(nx+ny)/2-nz]ⅹd, nx, ny는 필름 평면 내의 주굴절률, nz는 필름 두께 방향의 굴절률, d는 필름 두께이다.)가 -90nm ∼ +75nm 이며, 바람직하게는 -80nm ∼ +60nm, 특히 -70nm ∼ +45nm 가 바람직하다.In the case of an isotropic film, in-plane retardation (Ro, Ro = [(nx-ny) ⅹd], nx, ny are principal refractive indices in the film plane, and d is film thickness) is 40 nm or less, preferably 15 nm or less, and the thickness direction Retardation (Rth, Rth = [(nx + ny) / 2-nz] _d, nx, ny are principal refractive index in a film plane, nz is refractive index of a film thickness direction, d is film thickness.) -90nm-+ 75nm It is preferably -80 nm to +60 nm, particularly -70 nm to +45 nm.
위상차 필름은 고분자 필름의 일축 연신, 이축 연신, 고분자 코팅, 액정 코팅의 방법으로 제조된 필름이며, 일반적으로 디스플레이의 시야각 보상, 색감 개선, 빛샘 개선, 색미 조절 등의 광학 특성 향상 및 조절을 위하여 사용된다. 위상차 필름의 종류에는 1/2 이나 1/4 등의 파장판, 양의 C플레이트, 음의 C플레이트, 양의 A플레이트, 음의 A플레이트, 이축성 파장판을 포함한다.Retardation film is a film produced by the method of uniaxial stretching, biaxial stretching, polymer coating, liquid crystal coating of a polymer film, and is generally used for improving and controlling optical properties such as viewing angle compensation, color improvement, light leakage, and color taste control of a display. do. Types of the retardation film include a wave plate such as 1/2 or 1/4, a positive C plate, a negative C plate, a positive A plate, a negative A plate, and a biaxial wave plate.
보호필름은 고분자 수지로 이루어진 필름의 적어도 일면에 점착층을 포함하는 필름이거나 폴리프로필렌 등의 자가 점착성을 가진 필름일 수 있으며, 터치 센서 표면의 보호, 공정성 개선을 위하여 사용될 수 있다.The protective film may be a film including an adhesive layer on at least one surface of a film made of a polymer resin, or a film having a self-adhesive property such as polypropylene, and may be used to protect the touch sensor surface and improve processability.
편광판은 표시 패널에 사용되는 공지의 것이 사용될 수 있다. 구체적으로는, 폴리비닐알코올 필름을 연신하여 요오드나 이색성 색소를 염색한 편광자의 적어도 일면에 보호층을 설치하여 이루어진 것, 액정을 배향하여 편광자의 성능을 갖도록 하여 만든 것, 투명필름에 폴리비닐알코올 등의 배향성 수지를 코팅하고 이것을 연신 및 염색하여 만든 것을 들 수 있으며, 이에 한정되는 것은 아니다.As a polarizing plate, a well-known thing used for a display panel can be used. Specifically, a polyvinyl alcohol film is drawn to form a protective layer on at least one surface of a polarizer dyed iodine or a dichroic dye, made by orienting the liquid crystal to have the performance of the polarizer, polyvinyl film on a transparent film And coating the alignment resin such as alcohol, stretching and dyeing the same, and the like, but are not limited thereto.
이상에서 상세히 설명한 바와 같이 본 발명에 따르면, 기재 필름의 스트래처블 특성과 관련한 신뢰할 수 있는 물성 파라미터를 사전 정의하고, 이 물성 파라미터를 충족하는 기재 필름에 한하여 터치 센서에 적용함으로써, 터치 센서의 불량을 줄이고 제품 공정 수율을 향상시킬 수 있는 효과가 있다.According to the present invention as described in detail above, the touch sensor defects by pre-defining reliable property parameters related to the stretchable properties of the base film, and applying to the touch sensor only to the base film satisfying this property parameter It has the effect of reducing the yield and improving the product process yield.
< 실험예 >Experimental Example
표 1을 참조하여, 본 발명의 일 실시 예에 적용된 인장/회복 시험 및 그 결과에 대하여 설명하면 다음과 같다.Referring to Table 1, the tensile / recovery test applied to an embodiment of the present invention and the results are described as follows.
인장/회복 시험 장치로는 Autograph(shimadzu社)를 이용하였으며, 시편을 12mm/min의 속도로 인장하였고, 시편으로는 10mm 폭을 갖는 PDMS(Polydimethylsiloxane)를 사용하였고, 표점 거리는 50mm로 설정하였다. 인장 신율 0↔50% 구간을 12mm/min의 속도로 10만회 반복하며 인장 피로 시험을 진행하였다.Autograph (shimadzu Co., Ltd.) was used as the tension / recovery test device, the specimen was stretched at a speed of 12 mm / min, PDMS (Polydimethylsiloxane) having a width of 10 mm was used, and the gage distance was set to 50 mm. Tensile elongation was repeated 100,000 times at a rate of 12 mm / min in the tensile elongation 0↔50% section was carried out tensile test.
실시예 1, 2의 PDMS는 레진과 경화제의 혼합물인 Sylgard184(Dow Corning社)로 제조되었으며, 폴리실란 계열의 레진과 Sylgard184용 경화제가 사용되었고, 비교예 1, 2의 PDMS는 레진과 경화제의 혼합물인 MS1002(Dow Corning社)로 제조되었으며, 폴리실란 계열의 레진과 MS1002용 경화제가 사용되었고, 비교예 3의 PDMS는 레진과 경화제의 혼합물인 Silicone RTV 615(General Electronic社)로 제조되었으며, 폴리실란 계열의 레진과 Silicone RTV 615용 경화제가 사용되었으며, 각각의 예에 있어서의 레진과 경화제의 중량비는 표 1에 개시되어 있다.PDMS of Examples 1 and 2 were made of Sylgard184 (Dow Corning), which is a mixture of a resin and a curing agent, and a polysilane-based resin and a curing agent for Sylgard184 were used. The PDMS of Comparative Examples 1 and 2 was a mixture of a resin and a curing agent. It was made of MS1002 (Dow Corning Co., Ltd.), a polysilane-based resin and a curing agent for MS1002 were used. The PDMS of Comparative Example 3 was made of Silicone RTV 615 (General Electronic Co., Ltd.), a mixture of resin and hardener, and polysilane. A series of resins and curing agents for Silicone RTV 615 were used, the weight ratios of resins and curing agents in each example are shown in Table 1.
(레진(중량%)/
경화제(중량%))Resin and Hardener
(Resin (wt%) /
Hardener (% by weight))
기재필름
길이(mm)Early
Base Film
Length (mm)
영구변형된
기재필름
길이(mm)After 100,000 times of tension
Permanently deformed
Base Film
Length (mm)
인장응력
(MPa)Early
Tensile stress
(MPa)
인장후
인장응력
(MPa)
100,000 times
After tension
Tensile stress
(MPa)
(90/10)Sylgard184
(90/10)
(80/20)Sylgard184
(80/20)
(90/10)MS1002
(90/10)
(80/20)MS1002
(80/20)
(90/10)Silicone RTV 615
(90/10)
표 2에 개시된 크랙평가는 인장/회복 시험 후의 샘플을 광학현미경(ECLIPSE LV100ND, NIKON社)으로 크랙 발생 여부를 관찰한 결과이며, 1) 크랙이 발생하지 않은 경우 ○으로 표기하였고, 2) 크랙의 수가 1~5개 관찰된 경우 △으로 표기하였고, 3) 크랙의 수가 6개 이상 관찰된 경우 X로 표기하였다.The crack evaluation disclosed in Table 2 is a result of observing the crack after the sample after the tensile / recovery test with an optical microscope (ECLIPSE LV100ND, NIKON Corporation), 1) when no crack occurred, marked with ○, 2) crack When 1-5 were observed, it was indicated by △, and 3) when 6 or more cracks were observed, it was indicated by X.
비율
(εN)Permanent deformation
ratio
(ε N )
변화량
(ΔσN)Tensile stress
Change
(Δσ N )
계수Deformation resistance
Coefficient
표 2를 참조하면, 실시예 1, 2의 경우, 0 < 내변형성 계수 < 0.1 를 만족하며, 인장/회복 반복 피로 시험이 수행된 이후, 시료에 외관 변화가 없으며 크랙평가 결과도 양호하다는 것을 확인할 수 있었다.Referring to Table 2, in Examples 1 and 2, 0 <Strain coefficient <0.1 was satisfied, after the tensile / recovery repeated fatigue test was performed, it was confirmed that the sample does not change the appearance and the crack evaluation results are also good Could.
비교예 1, 2, 3의 경우, 0 < 내변형성 계수 < 0.1 를 만족하지 않으며, 인장/회복 반복 피로 시험이 수행된 이후, 시료가 늘어나거나 외관 변화가 있거나, 크랙평가 결과가 불량하다는 것을 확인할 수 있었다.In Comparative Examples 1, 2, and 3, 0 <the strain resistance <0.1 was not satisfied, and after the tensile / recovery repeated fatigue test was performed, the sample was stretched, the appearance was changed, or the crack evaluation result was confirmed to be poor. Could.
Claims (7)
(내변형성 계수 = εN/ΔσN, εN은 기재 필름의 인장에 따른 영구변형길이 비율, ΔσN는 인장응력 변화량)
The base film whose deformation resistance coefficient is more than 0 and less than 0.1.
(Strain resistance = ε N / Δσ N , ε N is the ratio of permanent strain length according to the tension of the base film, Δσ N is the amount of change in tensile stress)
상기 기재 필름의 두께는 50㎛ 내지 300㎛인, 기재 필름.
The method of claim 1,
The thickness of the said base film is a base film of 50 micrometers-300 micrometers.
상기 영구변형길이 비율(εN)은 인장 전후의 기재 필름의 길이 변화량에 대한 인장 전 기재 필름의 길이의 비인, 기재 필름.
The method of claim 1,
The permanent deformation length ratio ε N is a ratio of the length of the base film before tension to the amount of change in the length of the base film before and after tension.
상기 영구변형길이 비율(εN)은 0 초과 0.005 미만인, 기재 필름.
The method of claim 3,
The permanent deformation length ratio (ε N ) is greater than 0 and less than 0.005, the base film.
상기 인장응력 변화량(ΔσN)은 0 초과 0.1 미만인, 기재 필름.
The method of claim 1,
The amount of change in tensile stress (Δσ N ) is greater than 0 and less than 0.1, the base film.
상기 기재 필름은 PDMS(Polydimethylsiloxane), PET(Polyehtylene-terephthalate), PES(Polyether sulfone), PEN(Polyethylenenaphthalate), PI(Polyimide), PMMA(PolymethymethAcrylate), PC(Polycarbonate)로 이루어진 군에서 선택된 하나 이상을 포함하는, 기재 필름.
The method of claim 1,
The base film may include at least one selected from the group consisting of polydimethylsiloxane (PDMS), polyethylene-terephthalate (PET), polyether sulfone (PES), polyethylenenaphthalate (PEN), polyimide (PI), polymethymethacrylate (PMMA), and polycarbonate (PC). Base film to say.
A touch screen comprising the base film of any one of claims 1 to 6.