KR20190027703A - Fire proof interior wall panel with color of bond - Google Patents
Fire proof interior wall panel with color of bond Download PDFInfo
- Publication number
- KR20190027703A KR20190027703A KR1020180065154A KR20180065154A KR20190027703A KR 20190027703 A KR20190027703 A KR 20190027703A KR 1020180065154 A KR1020180065154 A KR 1020180065154A KR 20180065154 A KR20180065154 A KR 20180065154A KR 20190027703 A KR20190027703 A KR 20190027703A
- Authority
- KR
- South Korea
- Prior art keywords
- flame
- flame retardant
- retardant
- color
- panel
- Prior art date
Abstract
Description
본 발명은 월 패널에 관한 것으로, 더 상세하게는 월 패널의 색상을 다양화하고 내스크래치성과 내연성을 강화한 난연 인테리어 월 패널에 관한 것이다.
FIELD OF THE INVENTION The present invention relates to a wall panel, and more particularly, to a flame retarded interior wall panel having various colors of a wall panel and enhanced scratch resistance and flame resistance.
한국 등록특허 제10-0912675호에는, 원목, MDF 등의 판 형태의 폴리우레탄 폼의 상면에 PVC 시트를 합지하여 원판을 형성하는 합지단계와, 상기 합지단계에서 형성된 원판 표면에 실리콘오일을 도포하고 25~30℃에서 건조시키는 오일 도포단계와, 상기 실리콘 오일이 도포된 원판을 금형으로 열과 압력을 가하며 성형하는 발포단계와,상기 금형에서 발포된 원판을 탈형하는 탈형단계와, 상기 탈형단계에서 탈형된 원판을 재단하여 패널을 형성하는 패널형성단계를 포함하는 인테리어용 패널 제조방법 및 그 방법에 의해 제조되어 표면에 입체적 형상이 구현된 인테리어용 패널이 개시되어 있다.
Korean Patent No. 10-0912675 discloses a method for producing a polyurethane foam, which comprises a lapping step of laminating a PVC sheet on a polyurethane foam in the form of a plate of wood, MDF or the like to form an original plate, An oil application step of drying at 25 to 30 DEG C, a foaming step of molding the raw sheet coated with the silicone oil by applying heat and pressure with a mold, a de-molding step of demolding the raw foil from the mold, And a panel forming step of forming a panel by cutting an original plate, and an interior panel manufactured by the method and having a three-dimensional shape implemented on the surface thereof.
그러나, 한국 등록특허 제10-0912675호 발명은 인테리어 패널 표면에 다양하고 선명하고 컬러풀한 색상을 내기 어렵다는 단점과, 표면의 긁힘(scratch)이 발생하기 쉽다는 단점과, 인화성(引火性) 크다는 단점이 있다.
However, Korean Patent No. 10-0912675 has a disadvantage in that it is difficult to give a variety of clear and colorful colors to the surface of an interior panel, a disadvantage that scratches easily occur on the surface, and a disadvantage that a flammable There are disadvantages.
한국 등록실용신안 제20-0466998호에는, 투명 베이스 수지부; 및 상기 투명 베이스 수지부 내부에 함유된 천연 소재를 포함하는 수지층을 갖는 인테리어 패널이 개시되어 있다. 한국 등록실용신안 제20-0466998호 발명은 천연 소재의 미감을 살릴 수 있지만, 인화성(引火性)이 크고, 표면의 긁힘이 발생하기 쉬울 뿐만 아니라, 다양한 원색과 디자인의 표현이 어려운 단점이 있다.
Korean Utility Model Registration No. 20-0466998 discloses a transparent base resin part; And a resin layer including a natural material contained in the transparent base resin portion. Korean Utility Model Registration No. 20-0466998 Although the invention can make use of the natural feel of a natural material, it has a disadvantage in that it is difficult to express various primary colors and designs as well as a large flammability and scratches on the surface.
한국 등록특허 제10-1283868호에는, 경화 전 요변도가 1.2 내지 3.0인 베이스 수지부; 및 상기 베이스 수지부 내에 함유되어 외부로 무늬를 구현하는 무늬부를 가지는 수지층을 포함하는 인테리어 패널이 개시되어 있다. 한국 등록특허 제10-1283868호 발명은 무늬부를 통하여 다양한 무늬를 표현할 수 있지만, 인화성(引火性)이 매우 크고, 표면의 긁힘이 발생하기 쉬운 단점이 있다.
Korean Patent No. 10-1283868 discloses a base resin part having a shrinkage before shrinkage of 1.2 to 3.0; And a resin layer contained in the base resin portion and having a pattern portion for embodying an outward pattern. Korean Patent No. 10-1283868 discloses that although various patterns can be expressed through the fringe portion, there is a disadvantage that flammability is very large and scratches on the surface are easily generated.
한국 등록특허 제10-0946667호에는, 베이스플레이트와, 상기 베이스플레이트 상에 적층형성되는 화장층과, 상기 화장층 상에 적층되고 각종 문양 또는 색상을 나타내는 문양인쇄층과, 상기 문양인쇄층 상에 적층형성되며 상기 문양인쇄층의 표면을 보호함과 동시에 물의 침투를 방지하는 보호코팅층을 포함하여 이루어지는 인테리어 패널이 개시되어 있다. 한국 한국 등록특허 제10-0946667호는 다양한 문양과 색상을 나타낼 수 있지만, 문양 및 색상이 선명하지 않고, 인화성(引火性)이 매우 클 뿐만 아니라, 표면의 긁힘이 발생하기 쉬운 단점이 있다.
Korean Patent No. 10-0946667 discloses an inkjet printer comprising a base plate, a makeup layer laminated on the base plate, a pattern print layer laminated on the makeup layer and exhibiting various patterns or colors, And a protective coating layer laminated to protect the surface of the pattern printing layer and to prevent penetration of water. Korean Korean Patent No. 10-0946667 can exhibit various patterns and colors but has a disadvantage in that the pattern and color are not clear, the flammability is very large, and the surface is easily scratched.
본 발명은, 상술한 인테리어용 패널의 문제점을 해결하기 위하여 이루어진 것으로, 본 발명이 해결하고자 하는 제1과제는 표면 경도를 강화하여 스크래치(scratch) 발생을 방지하면서도 다양하고 선명한 색상을 구현할 수 있는 인테리어 월 패널을 제공하는 데 있다.
The present invention has been made to solve the above problems of the interior panel. The first problem to be solved by the present invention is to provide an interior panel capable of enhancing the surface hardness and preventing various scratches, Month panel.
본 발명이 해결하고자 하는 제2과제는 화재 발생시 인화되기 어려운 난연 인테리어 월 패널을 제공하는 데 있다.
A second problem to be solved by the present invention is to provide a flame retarded interior wall panel which is difficult to be printed when a fire occurs.
상술한 본 발명의 과제들은, 난연 패널과, 상기 난연 패널 위에 도포 되어 형성되는 접착제층이고 불포화 폴리에스테르 수지에 적어도 1종의 안료와 난연제를 첨가하여 난연 패널의 표면 색을 가릴 수 있는 불투명 색을 갖게 한 색발현 난연 접착제층과, 상기 색발현 난연 접착제층에 의하여 상기 난연 패널 표면에 일체로 부착되어 색발현 난연 접착제층의 안료 색상이 외부로 드러나게 하는 투명한 2축연신 OPET(oriented polyethylene terephthalate)필름과, UV 도료에 난연제를 첨가하여 상기 2축연신 OPET필름 표면에 코팅하여 형성한 UV 난연 코팅층을 포함하는 난연 인테리어 월 패널에 의하여 해결할 수 있다.
The above-described problems to be solved by the present invention are attained by a flame retardant panel comprising: a flame retardant panel; and an adhesive layer formed on the flame retardant panel, wherein at least one pigment and a flame retardant are added to the unsaturated polyester resin to form an opaque color And a transparent biaxially oriented oriented polyethylene terephthalate (OPET) film which is integrally adhered to the surface of the flame retardant panel by the color-imparting flame-retardant adhesive layer so that the pigment color of the color- And a UV flame retardant coating layer formed by coating a surface of the biaxially oriented OPET film with a flame retardant to UV paint.
상기 난연 패널로는, 탄산칼륨(CaCO3)과 PVC 수지를 6:4 내지 8:2의 중량비로 혼합하여 압출 성형한 판재를 사용하는 것이 바람직하다.
As the flame retardant panel, it is preferable to use a plate material obtained by mixing potassium carbonate (CaCO 3 ) and PVC resin at a weight ratio of 6: 4 to 8: 2 and extrusion molding.
상기 색발현 난연 접착제층에 첨가되는 난연제로는, 수산화알루미늄 또는 염소화파라핀을 사용하는 것이 바람직하다.
As the flame retardant added to the color-rendering flame-retardant adhesive layer, aluminum hydroxide or chlorinated paraffin is preferably used.
상기 UV 난연 코팅층에 첨가되는 난연제로는, 인산에스테르, 함할로겐 인산에스테르, 비할로겐 축합인계난연제 가운데 선택된 하나 또는 2이상의 난연제를 사용하는 것이 바람직하다.
As the flame retardant added to the UV flame retardant coating layer, it is preferable to use one or two or more flame retardants selected from among phosphoric ester, halogen halide phosphoric acid ester and non-halogen condensation phosphorous flame retardant.
상술한 본 발명에 의하면, 불포화 폴리에스테르 수지에 다양한 색상의 안료와 난연제를 투입하여 수요자의 다양한 색채 요구에 부합할 뿐만 아니라 난연성을 갖는 인테리어 월 패널을 제공할 수 있고, 이러한 색발현 난연 접착제를 난연 패널 표면에 펼치면서 특유의 표면 경도 및 광택을 갖는 2축연신 OPET필름을 부착함으로써, 난연 패널의 소재 색이 접착제에 의하여 차단되면서 외부 표면에는 선명한 접착제의 색채가 2축연신 OPET필름을 통하여 드러나고, 2축연신 OPET필름의 고경도 및 고광택이 더해져서 매우 고급스러운 난연 인테리어 월 패널를 얻을 수 있게 된다.
According to the present invention described above, it is possible to provide an interior wall panel that not only meets various color demands of a consumer by injecting various colors of pigment and flame retardant into an unsaturated polyester resin, but also can provide a flame retardant interior wall panel. By attaching a biaxially oriented OPET film having a unique surface hardness and gloss while spreading on the surface of the panel, the color of the flame retardant panel is blocked by the adhesive, and the color of the clear adhesive is exposed on the outer surface through the biaxially oriented OPET film, The high hardness and high gloss of the axially stretched OPET film are added to obtain a very luxurious interior flame retardant wall panel.
도 1은 본 발명에 따른 난연 인테리어 월 패널의 단면도이다.
도 2는 본 발명의 일 실시 예에 따른 난연 인테리어 월 패널의 제조 공정도이다.
도 3은 본 발명의 다른 실시 예에 따른 난연 인테리어 월 패널의 제조 공정도이다.1 is a sectional view of a flame-retarded interior wall panel according to the present invention.
2 is a manufacturing process diagram of a flame-retarded interior wall panel according to an embodiment of the present invention.
3 is a manufacturing process diagram of a flame-retardant interior wall panel according to another embodiment of the present invention.
이하, 첨부한 도면을 참조하여 본 발명에 따른 난연 인테리어 월 패널의 구체적인 실시 예를 상세히 설명한다.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, a specific embodiment of a flame-retarded interior wall panel according to the present invention will be described in detail with reference to the accompanying drawings.
도 1에 도시된 바와 같이, 본 발명은 난연 패널(1) 표면 위에 색발현 난연 접착제(3)와 2축연신 OPET(oriented polyethylene terephthalate)필름(5)과 UV(ultraviolet) 난연 코팅층(7)을 이용하여 컬러풀한 고경도 고광도 난연 표피층을 형성하여 컬러풀한 난연 인테리어 월 패널을 만든다. 본 발명에 따른 난연 인테리어 월 패널은, 난연 패널(1) 표면에, 불포화 폴리에스테르 수지에 안료 및 난연제를 첨가한 색발현 난연 접착제(3)를 투입하여, 색발현 난연 접착제(3)를 균일한 두께로 도포하는 과정에서 접착제 상부에 2축연신 OPET(oriented polyethylene terephthalate)필름(5)을 적층한 후 난연 패널(1)과 접착시켜, 난연 패널(1)와 2축연신 OPET필름(5)이 일체화 되게 하고, 2축연신 OPET필름(5) 표면에 난연제를 참가한 UV 도료에 의하여 UV 난연 코팅층(7)을 형성한 것이다.
1, the present invention is characterized in that a color developing flame
상기 난연 패널(1)은 1mm 내지 22mm의 두께를 가진 판재이다. 상기 난연 패널(1)은 탄산칼슘과 PVC 수지를 6:4 내지 8:2의 중량비로 혼합하여 판재형상으로 성형하는 것이 바람직하다.
The flame
본 발명의 특징은, 투명한 불포화 폴리에스테르 수지에, 적어도 1종의 안료와 난연제를 첨가하여 색채와 난연성을 갖게 함으로써, 접착제 기능을 함과 동시에 난연 패널 소재색의 표면 노출을 차단하고 컬러풀한 장식층 기능을 하게 할 뿐만 아니라, 그 자체로 난연 소재 기능을 하게 한 데 있다. 본 발명에서 유색이라 함은 유채색(빨강, 노랑, 파랑, 이들의 혼합색)과 무채색(흑색, 백색)을 모두 포함하는 의미로 사용한다.
It is a feature of the present invention that at least one kind of pigment and a flame retardant are added to a transparent unsaturated polyester resin to have a color and a flame retardancy so as to function as an adhesive and to prevent surface exposure of the flame- Not only does it function as a layer, it also functions as a flame retardant material itself. In the present invention, the term "colored" includes both chromatic colors (red, yellow, and blue, mixed colors thereof) and achromatic colors (black, white).
상기 안료로는 백색안료(산화아연·산화타이타늄·실버화이트 등), 적색안료(벵갈라·버밀리온·카드뮴레드 등), 황색안료(크롬옐로·황토·카드뮴옐로 등), 녹색안료(에메랄드녹·산화크로뮴녹 등), 청색안료(프러시안블루·코발트청 등), 자색안료(망가니즈자색, 마아즈자색 등), 흑색안료(카본블랙·철흑 등)를 단일하게 또는 혼합하여 사용할 수 있다. 본 발명은 투명한 불포화 폴리에스테르 수지에 안료를 적절히 혼합하는 것만으로 기존 패널이나 벽지로 낼 수 없는 색깔을 모두 낼 수 있기 때문에 소비자의 다양한 인테리어 벽 색상 요구를 만족시킬 수 있다. 투명한 불포화 폴리에스테르 수지에 첨가되는 안료의 양은 난연 패널 소재의 색을 모두 가릴 수 있는 불투명 색깔이 될 수 있는 양으로, 색발현 난연 접착제 전체 중량에 대하여 안료의 혼합량은 1 중량% - 50 중량%이다. 안료의 양이 1중량% 미만이면 난연 패널 소재의 색을 가릴 수 없고, 안료의 양이 50중량% 이상이면, 접착성이 크게 떨어진다.
Examples of the pigments include white pigments (such as zinc oxide, titanium oxide, silver white and the like), red pigments (such as Bengala, Vermilion, and cadmium red), yellow pigments (such as chrome yellow, yellow cadmium, and cadmium yellow), green pigments (Black, cobalt blue, etc.), blue pigments (Prussian blue, cobalt blue, etc.), purple pigments (manganese purple, magenta purple, etc.) and black pigments (carbon black, iron black and the like). The present invention can meet various interior wall color requirements of a consumer since it is possible to produce a color that can not be produced by conventional panels or wallpaper by properly mixing the pigment with a transparent unsaturated polyester resin. The amount of the pigment to be added to the transparent unsaturated polyester resin is an amount that can be an opaque color capable of hiding the color of the flame retardant panel material, and the mixing amount of the pigment is 1 wt% to 50 wt% based on the total weight of the color- . When the amount of the pigment is less than 1% by weight, the color of the flame retardant panel material can not be obscured. When the amount of the pigment is 50% by weight or more, adhesiveness is greatly deteriorated.
상기 색발현 난연 접착제(3)에 첨가되는 난연제로는 수산화알루미늄 또는 염소화파라핀 가운데 선택된 난연제를 사용할 수 있다. 이들 난연제는 상기 안료들의 색발현을 방해하지 않을 뿐만 아니라 난연성이 매우 우수하다. 색발현 난연 접착제 전체 중량에 대하여 난연제의 혼합량은 3중량% - 30중량%이다. 난연제의 양이 3%미만이면 가연성이 크고, 난연제의 양이 30중량%이상이면 접착성이 크게 떨어진다.
As the flame retardant to be added to the color-rendering flame-retardant adhesive (3), a flame retardant selected from aluminum hydroxide or chlorinated paraffin can be used. These flame retardants not only hinder the color development of the pigments but also have excellent flame retardancy. The mixing amount of the flame retardant with respect to the total weight of the color-developing and flame-retardant adhesive is 3 wt% to 30 wt%. When the amount of the flame retardant is less than 3%, the flammability is high, and when the amount of the flame retardant is more than 30% by weight, the adhesiveness is greatly deteriorated.
상기 색발현 난연 접착제층는 건조 및 경화 될 경우 그 압축 강도 및 경도가 매우 클 뿐만 아니라 난연성이 매우 우수하다. 따라서, 난연 패널 표면 강도 및 경도를 크게 개선할 뿐만 아니라, 불연 월 패널 표면을 구현하게 한다.
When the color-rendering flame-retardant adhesive layer is dried and cured, its compression strength and hardness are very large, and its flame retardancy is excellent. Therefore, not only the flame retardant panel surface strength and hardness are greatly improved, but also the surface of the incombustible wall panel is realized.
상기 2축연신 OPET필름(5)은, PET 필름을 제조하는 과정에서 다이로부터 압출된 미배향 상태의 필름을 융점 이하, 2차 전이점 이상의 온도에서 2축방향으로 늘려 PET 분자를 2 방향으로 배향시킨 것으로 결정화도가 높은 투명 필름이다. 2축연신 OPET필름(5)은 필름의 충격강도, 내스크래치성과 내연성, 투명성, 평활도, 내열도 및 액체 차단성이 매우 우수하여, 자체적인 난연성을 가짐으로 인하여, 월 패널 표면재로 매우 우수한 기능을 발휘하는 것을 반복적인 시험을 통해 확인하였다.
The biaxially
상기 2축연신 OPET필름(5) 표면에는, 난연 패널에 부착하기 전(도 2)이나 후(도 3)에, UV 도료에 난연제를 첨가한 UV 난연 도료에 의하여 UV 난연 코팅층(7)을 형성한다. 상기 UV 난연 코팅층(7)은, 무광 UV(Ultra Violet) 도료에 난연제를 첨가하여 형성한 무광 UV(Ultra Violet) 난연 코팅층이거나, 유광 UV(Ultra Violet) 도료에 난연제를 첨가하여 형성한 유광 UV(Ultra Violet) 난연 코팅층이다. 상기 UV 난연 코팅층에 첨가되는 난연제는 인산에스테르, 함할로겐 인산에스테르, 비할로겐 축합인계난연제 가운데 선택된 하나 또는 2이상의 난연제이고, 첨가량은 UV 난연 도료 전체 중량에 대하여 1중량% -30중량%이다. 난연제의 양이 1중량% 미만이면 가연성이 크고, 난연제의 양이 30중량%이상이면 표면 경도가 크게 떨어진다.
The UV flame
2축연신 OPET필름(5)의 이면에는 다양한 이미지를 포함하는 인쇄층을 더 형성할 수 있다. 2축연신 OPET필름(5)의 이면에는 인쇄층을 갈음하거나 인쇄층과 함께 알루미늄, 은 등의 메탈을 증착시킨 메탈증착층을 더 형성할 수 있다. 이와 같은 인쇄층과 메탈증착층에 의하여 다양한 월 패널 이미지를 구현할 수 있다.
A printing layer containing various images can be further formed on the back surface of the biaxially
유광 UV 난연 코팅층 또는 무광 UV 난연 코팅층을 형성하기 전에 2축연신 OPET필름(5) 표면에 대리석 패턴, 우드 패턴 등의 자연물 사진을 인쇄한 자연물 사진 인쇄층을 형성할 수도 있다. 또한, 유광 UV 코팅층 또는 무광 UV 코팅층을 형성하기 전에 2축연신 OPET 표면에 펄잉크를 이용하여 펄(pearl) 인쇄층을 형성할 수 있다. 이때 색발현 난연 접착제(3)는 이들 자연물 사진 인쇄층이나 펄 인쇄층의 바탕색을 제공하게 된다. 상기 펄잉크로는 분쇄유리 24중량%-28중량%, 이산화티타늄 8중량%-10중량%, 수지(비닐계, 폴리우레탄계) 12중량%-20중량%, 접착제 4.3중량%-6.6중량%, 솔벤트(메틸에틸케톤, 에틸아세테이트) 40중량%-50중량%인 수지계 잉크를 사용할 수 있다. 펄잉크로는 펄(pearl) 효과(보는 방향에 따라 다른 빛과 색이 나는 효과)를 낼 수 있는 진주 분말, 인조다이아몬드 분말 등을 포함한 수지계 잉크를 사용할 수 있다. 특히 인조다이아몬드 분말을 사용할 경우 광채가 화려하고 매우 고급스럽다.
A natural photographic print layer may be formed by printing natural photographs such as a marble pattern and a wood pattern on the surface of the biaxially oriented
도 2 및 도 3을 참조하여, 본 발명에 따른 난연 인테리어 월 패널의 제조 방법을 설명하면 다음과 같다.
Referring to FIGS. 2 and 3, a method of manufacturing a flame-retarded interior wall panel according to the present invention will now be described.
도 2에 도시된 제조 방법은 2축연신 OPET필름(5)을 난연 패널(1)의 표면에 부착하기 전에, 2축연신 OPET필름(5) 표면에 UV 난연 코팅층(7)을 형성한 실시 예이고, 도 3에 도시된 제조 방법은 2축연신 OPET필름(5)을 난연 패널(1)의 표면에 부착한 후에, 2축연신 OPET필름(5) 표면에 UV 난연 코팅층(7)을 형성한 실시 예이다. 2가지 실시 예 모두, UV 도료에 난연제를 혼합하여 UV 난연 코팅층(7)을 형성하는 점에서 같다.
The manufacturing method shown in Fig. 2 is an example in which the UV-flame
우선 도 2를 참조하면 알 수 있는 바와 같이, 본 발명에 따른 난연 인테리어 월 패널의 제조 방법은, 1mm ~ 22mm 두께의 탄산칼슘과 PVC수지로 이루어진 난연 패널을 준비하는 단계(100)와, 원하는 색깔의 안료와 난연제를 불포화 폴리에스테르 수지에 혼합하여 색발현 난연 접착제를 만드는 단계(101)와, UV 도료와 난연제를 혼합하는 단계(102)와, 난연제가 첨가된 UV도료를 2축연신 OPET필름 표면에 도포한 후 자외선(UV)에 의하여 경화시켜 2축연신 OPET필름 표면에 UV 난연 코팅층을 형성하는 단계(103)와, 난연 패널(1)의 표면에 색발현 난연 접착제(3)를 덩어리 상태로 투입하는 단계(104)와, 투입된 색발현 난연 접착제(3) 위에 UV 난연 코팅층(7)이 형성된 2축연신 OPET필름(5)을 덮어 적층하는 단계(105)와, 적층된 2축연신 OPET필름(5) 상면을 롤러에 의하여 왕복 압착하여 색발현 난연 접착제(3)를 2축연신 OPET필름(5) 표면에 얇고 균일한 두께로 평탄화하는 단계(106)와, 평탄화된 색발현 난연 접착제(3)를 2축연신 OPET필름(5)이 부착된 상태로 건조 및 경화시키는 단계(107)와, 2축연신 OPET필름(5)이 부착된 난연 패널을 적당한 크기로 절단하고 조립부를 성형하는 절단 및 조립부 성형 단계(108)를 포함한다.
2, the method of manufacturing a flame retarded interior wall panel according to the present invention includes a
색발현 난연 접착제를 만드는 단계(101)에서는, 불포화 폴리에스테르 수지에 단일 색상의 안료 또는 혼합 색상의 안료를 투입하고 혼합하여 접착제가 전체적으로 균일한 색채를 갖게 한다.
In step 101 of making a color-evolving flame-retardant adhesive, a single color pigment or a mixed color pigment is added to the unsaturated polyester resin and mixed to make the adhesive have a uniform uniform color.
난연 패널(1)의 표면에 색발현 난연 접착제(3)를 투입하는 단계(104)에서는, 난연 패널(1) 표면에 색발현 난연 접착제(3)를 반액상의 덩어리 상태로 투입하여 롤러에 의하여 난연 패널(1) 표면에 펼쳐질 수 있게 한다.
In the
색발현 난연 접착제(3)의 건조 경화 단계(107)에서는 2축연신 OPET필름(5)이 난연 패널(1)에 부착된 상태로 색발현 난연 접착제(3)를 건조 경화시켜 2축연신 OPET필름(5)과 난연 패널(1)을 일체화시킨다.
In the drying and curing
절단 및 조립부 성형 단계(108)에서는 2축연신 OPET필름(5)이 부착된 난연 패널(1)을 시공하기 편한 판재 크기로 절단하고, 조립되는 엣지(edge) 면을 가공하여 조립 단차부를 형성하거나 텅앤그루브(tongue and groove)를 형성하는 단계이다. 패널 크기를 300mm x 600mm로 절단하고 조립 단차부를 형성할 수도 있고, 패널 크기를 원판 크기인 590mm x 2,400mm로 절단하고 엣지면을 가공하지 않을 수도 있다. 패널 크기 및 엣지면 가공은 이에 한정되지 않으며, 다양한 크기로 절단 및 가공할 수 있다.
In the cutting and assembling
도 3에 도시된 바와 같이, 본 발명에 따른 난연 인테리어 월 패널은, 2축연신 OPET필름(5)에 UV 난연 코팅층(7)을 형성하지 않고, 색발현 난연 접착제(3)에 의하여 난연 패널(1) 표면에 부착한 상태에서, 최종적으로 UV 도료에 난연제를 혼합하여 UV 난연 코팅층(7)을 형성할 수도 있다.
3, the flame retarded interior wall panel according to the present invention is a flame retarded panel having a biaxially stretched
본 발명에 따른 난연 인테리어 월 패널은, 인테리어 시공을 하는 데 있어서, 기존 벽 표면에 부착하는 용도로 사용한다. 난연 인테리어 월 패널을 벽에 부착함에 있어서는 에폭시 접착제를 사용한다. 엣지면을 가공하지 않은 원판을 이용하여 시공할 경우에는 각 패널 사이에 약간의 간격을 두고, 그 사이에 T형 몰드를 삽입하여 함께 접착하는 것이 바람직하다.
The flame retarded interior wall panel according to the present invention is used for the interior wall construction to be attached to the existing wall surface. Epoxy adhesives are used to attach flame retardant interior wall panels to walls. It is preferable to insert the T-shaped mold therebetween and to bond them together with a slight gap between the panels.
본 발명에 의하면, 난연 패널(1) 표면에 도색을 하지 않아도, 불포화 폴리에스테르 수지에 안료를 투입하여 일반 벽지나 목재 판재에서는 불가능한 다양하고 화려한 색상을 만들 수 있다. 또한, 이러한 색발현 난연 접착제(3)를 난연 패널 표면(1)에 펼치면서 2축연신 OPET필름(5)을 부착하므로써, 난연 패널(1)의 소재 색상이 접착제에 의하여 차단되면서 외부 표면에는 화려한 색발현 난연 접착제의 색채가 2축연신 OPET필름을 통하여 드러나고, 2축연신 OPET필름(5)의 고경도 및 고광택이 더해져서 내스크래치성과 내연성이 높고 매우 고급스러울 뿐만 아니라, 눌림 등이 발생하지 않는 난연 인테리어 월 패널를 얻을 수 있게 된다. 또한, 난연 패널(1) 뿐만 아니라, 색발현 난연 접착제(3), 2축연신 OPET필름(5) 및 UV 난연 코팅층(7)이 모두 난연성을 가지므로, 난연성을 요구하는 인테리어 월 패널로 유용하게 사용될 수 있다.
According to the present invention, even when the surface of the flame-
1 : 난연 패널
3 : 색발현 난연 접착제층
5 : 2축연신 OPET필름
7 : UV 난연 코팅층1: Flame Retardant Panel
3: Color-developing flame-retardant adhesive layer
5: Biaxially oriented OPET film
7: UV flame retardant coating layer
Claims (3)
상기 난연 접착제층에는 상기 난연 패널의 표면 색을 가릴 수 있는 적어도 1종의 안료를 첨가하고 상기 2축연신 OPET필름은 투명한 것을 사용하여 난연 접착제층의 안료 색상이 외부에 그대로 드러나게 함으로써, 접착제 색에 의하여 패널의 색을 결정하는, 접착제 색 외부 발현 난연 인테리어 월 패널.
A flame-retardant resin composition comprising: a flame-retardant panel; a flame-retardant adhesive layer formed by applying an unsaturated polyester resin added with a flame retardant agent to the flame-retardant panel; a biaxially-stretched OPET film integrally adhered to the flame- A UV flame retardant coating layer coated on the surface of an axially oriented OPET film,
Wherein at least one kind of pigment capable of hiding the surface color of the flame retardant panel is added to the flame-retardant adhesive layer and the pigment color of the flame-retardant adhesive layer is exposed to the outside using the transparent biaxially oriented OPET film, Determine the color of the panel by glue color, exterior paneling, flame retardant interior wall panel.
상기 2축연신 OPET필름 표면에 난연 UV 코팅층을 형성하기 전에, 상기 2축연신 OPET필름 표면에 자연물 사진을 인쇄한 자연물 사진 인쇄층을 형성하거나 펄잉크를 이용한 펄(pearl) 인쇄층을 형성한 것을 특징으로 하는 접착제 색 외부 발현 난연 인테리어 월 패널.
The method according to claim 1,
Before forming a flame-retardant UV coating layer on the surface of the biaxially oriented OPET film, a natural photo print layer printed with natural photographs or a pearl print layer formed with pearl ink was formed on the surface of the biaxially oriented OPET film Features Adhesive color Outer appearance Flame retardant Interior wall panel.
상기 난연 패널은 탄산칼슘과 PVC 수지를 6:4 내지 8:2의 중량비로 혼합하여 판재형상으로 성형한 것을 특징으로 하는 접착제 색 외부 발현 난연 인테리어 월 패널.
The method according to claim 1,
Wherein the flame retardant panel is formed by mixing calcium carbonate and PVC resin in a weight ratio of 6: 4 to 8: 2 and shaping it into a plate material.