KR20190011210A - Preparation Method for Gdot-Pd Hybrid with Nanosponge Structure and Gdot-Pd Hybrid Catalyst - Google Patents

Preparation Method for Gdot-Pd Hybrid with Nanosponge Structure and Gdot-Pd Hybrid Catalyst Download PDF

Info

Publication number
KR20190011210A
KR20190011210A KR1020180084246A KR20180084246A KR20190011210A KR 20190011210 A KR20190011210 A KR 20190011210A KR 1020180084246 A KR1020180084246 A KR 1020180084246A KR 20180084246 A KR20180084246 A KR 20180084246A KR 20190011210 A KR20190011210 A KR 20190011210A
Authority
KR
South Korea
Prior art keywords
palladium
hybrid
gdot
carbon
catalyst
Prior art date
Application number
KR1020180084246A
Other languages
Korean (ko)
Other versions
KR102108907B1 (en
Inventor
최호석
반토안 나구연
Original Assignee
충남대학교산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 충남대학교산학협력단 filed Critical 충남대학교산학협력단
Publication of KR20190011210A publication Critical patent/KR20190011210A/en
Application granted granted Critical
Publication of KR102108907B1 publication Critical patent/KR102108907B1/en

Abstract

The present invention relates to a method of manufacturing a palladium nano catalyst which has a wide effective surface area, is stable and has high catalytic activity, and the palladium nano catalyst manufactured by the same. More specifically, the present invention relates to the method of manufacturing a graphenedot-palladium hyprid with a nonosponge structure which has a feature of reducing a palladium precursor in a mixed state with carbondot and sodium bromide.

Description

나노스폰지 구조의 그래핀닷-팔라듐 하이브리드의 제조방법 및 그에 의해 제조된 그래핀닷-팔라듐 하이브리드 촉매{Preparation Method for Gdot-Pd Hybrid with Nanosponge Structure and Gdot-Pd Hybrid Catalyst}The present invention relates to a method for producing a graphene-palladium hybrid having a nano-sponge structure and a grapindot-palladium hybrid catalyst prepared thereby.

본 발명은 유효표면적이 넓고, 안정하며, 촉매활성이 높은 팔라듐 나노 촉매의 제조방법과 이에 따라 제조된 팔라듐 나노 촉매에 관한 것이다.The present invention relates to a process for preparing a palladium nanocatalyst having a wide effective surface area, stable and high catalytic activity, and a palladium nanocatalyst produced thereby.

연료전지는 연료의 화학에너지를 전기 화학적 반응에 의해 전기 및 열 에너지로 직접 변환시키는 장치로, 신규 에너지 요구에 대한 해결책으로 고려되고 있다. 연료전지는 고효율성, 고에너지 밀도, 낮은 작동온도, 낮은 독성과 탄화수소 연소 시 발생하는 부산물과 같은 공해물질의 발생이 없이 전력을 생산할 수 있다는 것을 가장 큰 장점으로 들 수 있다. 다양한 유형의 연료전지 중에서 고분자 전해질 연료전지(PEMFC)는 다양한 전력 응용을 위한 실행 가능한 후보로서, PEMFC의 상업화는 에너지 수요의 급속한 증가와 환경 오염의 심화에 가장 유망한 해결책으로 간주된다. PEMFC는 음극(anode)에서의 촉매에 의한 연료의 산화와 양극(cathode)에서의 산소의 환원(ORR)을 결합시킴으로써 전력을 생성한다. 산소 환원 반응은 매우 느리기 때문에 연료전지가 실용 가능한 수준에 도달할 수 있도록 산소 환원 속도를 높이기 위해서는 양극 ORR 촉매가 필요하다.Fuel cells are devices that convert the chemical energy of fuel directly into electricity and heat energy by electrochemical reaction and are considered as a solution to new energy demands. The biggest advantage of fuel cells is that they can produce electricity without generating pollutants such as high efficiency, high energy density, low operating temperature, low toxicity and by-products generated by hydrocarbon combustion. Among various types of fuel cells, polymer electrolyte fuel cells (PEMFC) are viable candidates for various power applications. Commercialization of PEMFC is regarded as the most promising solution for the rapid increase of energy demand and deepening of environmental pollution. PEMFCs generate power by combining the oxidation of fuel by the catalyst at the anode and the reduction of the oxygen at the cathode (ORR). Since the oxygen reduction reaction is very slow, a bipolar ORR catalyst is needed to increase the oxygen reduction rate so that the fuel cell can reach a practical level.

수소 역시 깨끗하고 큰 에너지 용량을 갖는 유망한 재생에너지원으로 주목을 받고 있다. 수소 발생 반응(HER, hydrogen evolution reaction)은 수소를 경제적이고 효율적으로 생산할 수 있는 현실적인 방법 중 하나이다. Hydrogen is also attracting attention as a promising renewable energy source with a clean and large energy capacity. Hydrogen evolution reaction (HER) is one of the practical ways to produce hydrogen economically and efficiently.

산소 환원 반응이나 수소 발생 반응에 대해서는 현재까지 백금(Pt)계 물질이 활성이 높고, 과전압이 낮으며, 타펠(Tafel) 기울기가 작아 가장 실용적인 촉매이지만, 너무 비싸고 내구성이 낮으며 입수가 어렵다는 단점으로 인하여 더 많은 범위 및 대량의 상업 공정에의 응용에 제한이 되고 있다. As for the oxygen reduction reaction and the hydrogen generation reaction, platinum (Pt) -based materials have high activity, low overvoltage, and small tafel slope, which are the most practical catalysts, but they are too expensive, have low durability and are difficult to obtain Which limits its application to a wider range of commercial processes.

팔라듐(Palladium, Pd)은 백금족 원소의 하나로, 산소 환원 반응이나, 알칼리 전해질 용액에서 메탄올 및 포름산의 산화 반응, 수소 발생 반응 등, 백금이 촉매 활성을 갖는 것으로 알려진 반응에 대해 백금과 유사한 활성을 나타내면서도, 상대적으로 값이 싸고, 내구성이 우수하며 입수가 용이하다. 이러한 특성으로 인하여 각종 형태의 수소가스 센서나 수소저장용 합금, 수소분리장치, 수소반응기 등에 응용되고 있다. 거친 표면을 갖거나, 수지상 또는 다공성 구조를 갖는 팔라늄 나노입자는 종래의 다결정상인 팔라듐에 비해 촉매반응에 노출되는 표면적이 넓기 때문에 촉매활성이 더욱 우수하다. 이에 팔라듐 촉매의 표면적을 증가시키면서도 응집을 방지하여 촉매 활성을 높이기 위한 연구들이 진행되고 있다.Palladium (Pd) is one of the elements of the platinum group, and exhibits similar activity to platinum for reactions known to have catalytic activity of platinum, such as oxygen reduction reaction, oxidation reaction of methanol and formic acid in alkaline electrolyte solution, and hydrogen generation reaction Is also relatively cheap, has excellent durability and is easy to obtain. Due to these characteristics, various types of hydrogen gas sensors, alloys for hydrogen storage, hydrogen separators, hydrogen reactors, and the like have been applied. Palladium nanoparticles having a rough surface or having a dendritic or porous structure are more excellent in catalytic activity because they have a larger surface area exposed to a catalytic reaction than conventional polycrystalline palladium. Studies have been conducted to increase the surface area of the palladium catalyst while preventing agglomeration and thereby increasing the catalytic activity.

상기와 같은 연구의 한 축은 다공선 3차원 구조를 갖는 팔라듐 촉매를 제조하는 것이다. 그러나 종래의 대부분의 방법은 계면활성제나 첨가제, 강한 환원제나 독성 시약 또는 고온의 반응 조건을 필요로 한다. 반응 조건이 격렬한 것을 제외하더라도, 계면활성제나 첨가제들은 다공성 구조와 고분자 물질의 상호작용으로 인하여 제거가 용이하지 않으며, 잔류의 계면활성제나 첨가제는 반응 활성을 저하시키는 문제가 있다. One axis of such a study is to produce a palladium catalyst having a multi-pore three-dimensional structure. However, most conventional methods require surfactants or additives, strong reducing agents, toxic reagents, or high temperature reaction conditions. Even if the reaction conditions are not vigorous, the surfactants and additives are not easy to remove due to the interaction of the porous structure and the polymer material, and residual surfactants and additives have a problem of lowering the reaction activity.

또 다른 연구의 한 축은 팔라듐 나노입자 촉매의 응집을 감소시키고, 전도도를 증가시켜 반응에 의해 발생되는 전류를 효율적으로 흐르게 하도록, 카본 블랙, 카본 나노튜브, 그래핀, 그래핀 옥사이드의 환원물, 무정형 카본과 같은 높은 표면적을 갖는 탄소지지체에 팔라듐 나노입자를 담지시킨 촉매들을 개발하는 것이다(등록특허 10-1144107, 등록특허 10-1515677, 등록특허 10-0914991). 그러나 탄소지지체 표면 위에 균일한 입자간 거리를 가진 우수한 입자 분포를 보이면서도 고농도로 담지된 팔라듐 나노입자를 제조하기는 쉽지 않은데, 이는 팔라듐이 엉김(agglomeration)현상이 심하기 때문이다. 또한 탄소지지체에 담지된 촉매는 연료전지의 작동 동안 탄소지지체로부터 촉매금속 나노입자들이 분리, 용해되며, 이는 촉매의 유효표면적을 크게 감소시켜 연료전지 성능 저하의 주된 원인이 된다. 더 나아가, 탄소지지체들은 다른 물질들과 결합하는 성질이 있어, 작업 전극의 제조 시에 많은 나노결정들 사이에 끼어들기 때문에 유효표면적이 감소하는 결과를 낳는다. Another axis of further research is the reduction of aggregation of palladium nanoparticle catalysts and the reduction of carbon black, carbon nanotubes, graphene and graphene oxide, amorphous carbon nanotubes, The present inventors developed catalysts in which palladium nanoparticles were supported on a carbon support having a high surface area such as carbon (Patent No. 10-1144107, Registration No. 10-1515677, Registration No. 10-0914991). However, it is not easy to produce palladium nanoparticles loaded with high concentration while showing a good particle distribution with a uniform inter-particle distance on the surface of the carbon support, because palladium is agglomeration phenomenon. Also, the catalyst supported on the carbon support may separate and dissolve the catalyst metal nanoparticles from the carbon support during operation of the fuel cell, which significantly reduces the effective surface area of the catalyst, thereby causing deterioration of fuel cell performance. Furthermore, the carbon supports have the property of bonding with other materials, resulting in reduced effective surface area since they intercalate between many nanocrystals in the production of the working electrode.

한편, 카본닷(carbondot, Cdot)은 독특한 성질을 가진 새로운 카본 소재로서 광전자, 에너지 저장 및 변환 장비, 태양전지, 바이오센서, 바이오테크에서 잠재적인 적용가능성이 인정되어 많은 관심을 받고 있다. 카본닷은 산소를 함유하는 준-구형(quasi-spherical shape)의 탄소질 나노입자로 그 크기는 10nm 이하이다. 카본닷은 표면에 산소를 포함하는 작용기를 다량으로 함유하고 있기 때문에 친수성이 높고, 전자 공여체 및 전자 수여체 모두로서 작용할 수 있다. 카본닷은 또한 아스코빅산과 같은 환원제와 결합하여 수용액에서 금속 나노입자를 안정시키는 구조체로 이용될 수 있다. 카본닷은 생체적합성은 물론 높은 전기전도도 특성과, 매우 큰 표면적, 낮은 독성 및 화학적 안정성을 지니며, 카본닷과 금속 나노입자의 융합은 새로운 혼성체(hybrid)에서 고유의 성질 변화를 야기하여 촉매, 전기, 광학 성능의 향상을 가져올 수 있다. 그러나, 카본닷/금속 복합체에 대해서는 아직까지 극히 제한된 연구만이 행해져 있다. 예로, Guo 등(ACS Catalysis 2015, 5, 2903.)은 카본닷이 백금 나노입자의 표면을 캡슐화(encapsulating)하여 안정성을 크게 증가시킴을 보고하였으나, 이는 탄소나노튜브에 담지된 상태의 촉매로서 카본닷/금속 복합체 자체가 3차원 구조를 형성하는 것은 아니었다. On the other hand, carbondot (Cdot) is a new carbon material with unique properties and has attracted much attention because of its potential application in optoelectronics, energy storage and conversion equipment, solar cell, biosensor, and biotech. Carbon Dot is a quasi-spherical carbonaceous nanoparticle containing oxygen that is less than 10 nm in size. Since carbon dots contain a large amount of functional groups containing oxygen on their surface, they have high hydrophilicity and can act as both an electron donor and an electron acceptor. Carbon Dots can also be used as a structure to stabilize metal nanoparticles in aqueous solution by combining with a reducing agent such as ascorbic acid. Carbon dot has high electrical conductivity, high surface area, low toxicity and chemical stability as well as biocompatibility. The fusion of carbon dot and metal nanoparticles causes intrinsic property changes in new hybrids, Electrical and optical performance can be improved. However, very limited research has been conducted on the carbon dot / metal composite yet. For example, Guo et al. ( ACS Catalysis 2015, 5 , 2903.) reported that carbon dots encapsulate the surface of platinum nanoparticles to greatly increase stability. However, carbon nanotubes The dot / metal composite itself did not form a three-dimensional structure.

등록특허 10-1144107Patent No. 10-1144107 등록특허 10-1515677Patent No. 10-1515677 등록특허 10-0914991Patent No. 10-0914991

Guo 등(ACS Catalysis 2015, 5, 2903.)Guo et al. (ACS Catalysis 2015, 5, 2903.)

본 발명은 상기와 같은 종래기술의 문제점을 해결하기 위하여 팔라듐 촉매가 표면에 높은 농도로 존재하며, 표면적이 넓어 촉매활성이 우수하고, 안정성과 내피독성이 높아 내구성 역시 우수한 팔라듐 촉매의 제조방법 및 이에 의해 제조된 팔라듐 촉매를 제공하는 것을 목적으로 한다.DISCLOSURE OF THE INVENTION The present invention has been made in order to solve the problems of the prior art as described above and to provide a palladium catalyst having a high concentration of palladium catalyst on the surface thereof and having a high surface area and excellent catalytic activity and high stability and endotoxicity, The present invention also provides a palladium catalyst prepared by the above method.

또한 본 발명은 상기 팔라듐 촉매를 간단한 방법에 의해 온화한 조건에서 경제적으로 제조할 수 있는 합성 방법을 제공하는 것을 다른 목적으로 한다.Another object of the present invention is to provide a method for producing the palladium catalyst economically in a mild condition by a simple method.

본 발명의 또 다른 목적은 상기 팔라듐 촉매를 포함하는 연료전지용 전극을 제공하는 것이다. Still another object of the present invention is to provide an electrode for a fuel cell comprising the palladium catalyst.

전술한 목적을 달성하기 위한 본 발명은 팔라듐 전구체를 카본닷과 브롬화 나트륨과 혼합된 상태에서 환원시키는 것을 특징으로 하는 나노스폰지 구조의 그래핀닷(Gdot, graphenedot)-팔라듐 하이브리드의 제조방법에 관한 것이다.In order to accomplish the above object, the present invention relates to a method for producing a graphenedot-palladium hybrid of nano sponge structure, characterized in that a palladium precursor is reduced in a state mixed with carbon dot and sodium bromide.

본 발명에서 "하이브리드(hybrid)"는 종래 금속의 나노구조물이 탄소지지체에 단순히 담지되어 있는 "복합체(complex)"와 구분되는 용어이다. 통상 탄소지지체에 담지되는 경우에는 탄소지지체의 형상이 유지되면서, 그 표면에 나노구조물이 물리적 또는 화학적으로 결합되어 있는 것이다. 예를 들면 탄소나노튜브(CNT)에 백금합금이 담지되면, 표면에 백금합금 나노입자가 흡착되어 있으나 전체의 큰 형상은 탄소나노튜브의 형상을 유지한다. 이에 비해, 본 발명의 하이브리드는 카본닷의 형상이 전체 형상을 이루면서 그 표면에 팔라듐 나노입자가 흡착되어 있는 것이 아니라, 반응 과정에서 카본닷의 박리에 의해 생성된 그래핀닷과 팔라듐이 함께 새로운 3차원 구조를 형성하는 것에 특징이 있다. 카본닷이 없는 경우 제조되는 팔라듐 합금이 단순히 응집된 구조를 갖는 반면, 카본닷 존재 하에서는 나노스폰지 구조를 형성하였다. 특히, 본 발명에서 브롬화 나트륨이 없는 경우에는 다공성 나노스폰지 구조가 아닌 나노라스베리 구조가 형성되어, 브롬화 나트륨은 카본닷과 함께 나노스폰지 구조의 구조유도제(structure directing agent)로 작용함을 시사하였다. 상기 나노라스베리는 촉매활성이나 내구성이 본 발명의 나노스폰지 구조의 Gdot-Pd 하이브리드에 비해 크게 저하되었다.The term "hybrid" in the present invention is a term different from a "complex" in which a metal nanostructure is simply supported on a carbon support. Usually, when the carbon support is supported on a carbon support, the nanostructure is physically or chemically bonded to the surface of the carbon support while maintaining the shape of the carbon support. For example, when a platinum alloy is supported on a carbon nanotube (CNT), platinum alloy nanoparticles are adsorbed on the surface, but the overall shape of the carbon nanotube retains the shape of the carbon nanotube. In contrast, in the hybrid of the present invention, the shape of the carbon dot is the entire shape, and the palladium nanoparticles are not adsorbed on the surface thereof. Instead, the graphene dot and palladium produced by the carbon dot separation in the reaction process together with the three- Structure. ≪ / RTI > In the absence of carbon dots, the palladium alloy produced had a merely aggregated structure, but formed a nanosponge structure in the presence of carbon dot. In particular, in the present invention, when sodium bromide is not present, a nano-raspberry structure rather than a porous nano-sponge structure is formed, suggesting that sodium bromide acts as a structure directing agent of nano-sponge structure together with carbon dot. The catalytic activity and durability of the nano raspberry were greatly lowered compared to the Gdot-Pd hybrid of the nano sponge structure of the present invention.

특히 본 발명에 의해 제조된 상기 그래핀닷-팔라듐 하이브리드는 나노스폰지 구조가 Gdot에 의해 캡슐화(encapsulating)되어 있음을 확인할 수 있었다. 즉, 에지 부분의 구조에서 매우 얇은 층상 구조를 갖는 그래핀닷이 둘러싸고 있는 것을 확인할 수 있었는데, 이는 준구형의 카본닷의 다층구조가 반응 과정에서 시트상의 그래핀닷으로 박리되어 하이브리드를 형성함을 의미한다. 이러한 캡슐화된 구조로 인해 종래의 상용화된 cPt/C 촉매나 브롬화 나트륨이 없는 경우에 생성된 나노라스베리 구조의 Cdot-Pd 하이브리드에 비해 촉매로 사용 시 내구성이 우수하였다. 브롬화 나트륨이 없는 경우에는 Gdot에 의해 캡슐화된 구조가 형성되지 않았다. In particular, it was confirmed that the graphene dot-palladium hybrid prepared according to the present invention encapsulates the nanospond structure by Gdot. In other words, it was confirmed that the graphen dots having a very thin layered structure in the structure of the edge portion surround the multi-layered structure of the semi-spherical carbon dot, which is peeled off from the graphene dot on the sheet in the course of the reaction to form a hybrid . Due to such an encapsulated structure, durability was excellent when used as a catalyst as compared with a natto raspberry-type Cdot-Pd hybrid produced in the absence of commercially available cPt / C catalyst or sodium bromide. In the absence of sodium bromide, no encapsulated structure was formed by Gdot.

상기 카본닷은 이종 원자(hetero atom)가 도핑된 카본닷인 것이 더욱 바람직하다. 상기 이종 원자는 예를 들면, 질소, 황, 인 및 붕소로 이루어진 군으로부터 선택된 하나 이상일 수 있다. 상기와 같은 이종 원자의 도핑은 표면의 친수성을 증가시킬 뿐 아니라, 전자 공여체와 전자 수여체로서의 특성을 향상시키고 작용기 도입을 용이하게 하는 등 Cdot의 특성을 개선하는 효과가 있다. 따라서 이종 원자가 도핑되는 경우에는 이종 원자가 도핑되지 않은 카본닷을 사용한 경우보다 이에 의해 제조된 그래핀닷-팔라듐 하이브리드의 촉매활성이 더욱 증가한다. 하기 실시예에서는 이종 원자가 도핑된 카본닷으로서 N-Cdot에 대한 결과를 상세히 기술하였으나, 실시예에 기재된 Cdot이나 다른 이종 원자가 도핑된 Cdot의 경우에도 유사한 나노스폰지 구조를 형성하는 것을 확인할 수 있었다. Cdot의 제조방법이나, 이종 원자가 도핑된 Cdot의 제조방법은 종래 기술에서 다양한 제조방법들이 보고되어 있으며, 본 발명은 Cdot이나 이종 원자가 도핑된 Cdot 자체의 제조방법에 관한 것은 아니므로, 어떠한 방법에 의해 제조된 것을 사용하여도 무관하다. 따라서 본 명세서에서는 이의 제조방법에 대해서는 상세한 설명을 생략한다.It is more preferable that the carbon dot is a carbon dot doped with a hetero atom. The heteroatom may be at least one selected from the group consisting of, for example, nitrogen, sulfur, phosphorus, and boron. Such doping of hetero atoms not only increases the hydrophilicity of the surface but also improves the properties of the electron donor and the electron acceptor, facilitates introduction of the functional group, and improves the properties of the Cdot. Therefore, when heteroatom doping is performed, the catalytic activity of the grapindot-palladium hybrid produced thereby is further increased as compared with the case where carbon atoms not doped with heteroatoms are used. In the following examples, results for N-Cdot were described in detail as heteroatom-doped carbon dots. However, it was confirmed that similar nanosponge structures were formed in the case of Cdot or other hetero-atom-doped Cdot described in the examples. Various manufacturing methods have been reported in the prior art for the manufacturing method of Cdot or the method for manufacturing heteroatom-doped Cdot. Since the present invention is not related to the manufacturing method of Cdot or the heteroatom-doped Cdot itself, It is also possible to use a manufactured one. Therefore, a detailed description thereof will be omitted in this specification.

이종 원자가 도핑된 Cdot을 사용하는 경우 이종 원자의 도핑량은 탄소 대비 20 중량%이하인 것이 바람직하다. 이종 원자의 도핑량이 너무 많은 경우 Cdot 형성이 어려울 뿐 아니라 팔라듐 전구체의 환원 시 구조유도제로서의 효능이 저하되었다. When heteroatom-doped Cdot is used, the doping amount of hetero atoms is preferably 20 wt% or less with respect to carbon. When the doping amount of heteroatoms is too large, the formation of Cdot is difficult and the effect as a structure-directing agent is reduced when the palladium precursor is reduced.

상기 팔라듐 전구체는 팔라듐 이온을 포함하는 것으로, 환원 반응에 의해 팔라듐으로 환원될 수 있는 것이라면 어느 것이라도 사용 가능하다. 팔라듐 전구체의 예로는, 테트로클로로팔라듐산나트륨(Na2PdCl4), 테트라클로로팔라듐산칼륨(K2PdCl4), 헥사클로로팔라듐산칼륨(K2PdCl6), 테트라클로로팔라듐산암모늄((NH4)2PdCl4), 헥사클로로팔라듐산암모늄((NH4)2PdCl6), 염화팔라듐(PdCl2) 또는 이들의 혼합물을 사용할 수 있으며, 역시 이에 한정되는 것은 아니다.The palladium precursor includes palladium ions, and any palladium precursor can be used as long as it can be reduced to palladium by a reduction reaction. Examples of palladium precursors include sodium tetrochloropalladate (Na 2 PdCl 4 ), potassium tetrachloropalladate (K 2 PdCl 4 ), potassium hexachloropalladate (K 2 PdCl 6 ), ammonium tetrachloropalladium (( NH 4 ) 2 PdCl 4 ), ammonium hexachloropalladate ((NH 4 ) 2 PdCl 6 ), palladium chloride (PdCl 2 ), or mixtures thereof.

상기 반응은 백금 전구체 100 중량부에 대하여 카본닷 1~200 중량부, 브롬화 나트륨 50~2000 중량부를 사용하는 것이 바람직하였다. 카본닷 또는 브롬화 나트륨의 함량이 너무 적으면 구조유도제로서의 작용이 충분하지 않아 나노스폰지 구조의 형성이 어려웠다. 반면, 카본닷의 함량이 너무 많은 경우에는 촉매활성을 나타내는 금속의 함량이 상대적으로 작아지기 때문에 촉매활성이 저하되었다. 브롬화 나트륨의 사용량이 너무 많은 경우에는 제조 비용이 상승할 뿐 아니라 역시 나노스폰지 구조의 형성에 영향을 주었다. The reaction is preferably carried out using 1 to 200 parts by weight of carbon black and 50 to 2,000 parts by weight of sodium bromide based on 100 parts by weight of the platinum precursor. If the content of carbon dots or sodium bromide is too small, the function as a structure directing agent is not sufficient and it is difficult to form a nano sponge structure. On the other hand, when the content of carbon dot is too large, the catalytic activity is lowered because the content of the metal exhibiting catalytic activity is relatively small. If the amount of sodium bromide used is too high, not only the manufacturing cost is increased but also the formation of the nano sponge structure is affected.

상기 팔라듐 전구체의 환원은 종래 팔라듐 나노입자의 제조 시 사용되는 어떠한 방법을 사용하여도 무방하다. 즉, 단순 가열반응에 의하거나, 환원제를 추가로 투여하여 이루어질 수 있다. 환원제로서는 포름산, 아스코르브산, 시트릭산, 올레일아민, 포름알데히드, 소듐보로하이드라이드, 알미늄보로하이드라이드, 리튬알미늄하이드라이드, 2-메틸-2-피롤리딘으로 이루어진 군으로부터 선택된 하나 또는 둘 이상의 혼합물을 사용하는 것이 가능하며, 이에 한정되지 않는다. 환원 반응 시의 온도는 20~180℃로 환원제의 사용 유무나, 사용하는 환원제의 종류에 따라 적절한 조건을 선택할 수 있다. The palladium precursor may be reduced by any method conventionally used in the production of palladium nanoparticles. That is, this may be accomplished by a simple heating reaction or by additionally adding a reducing agent. Examples of the reducing agent include one selected from the group consisting of formic acid, ascorbic acid, citric acid, oleylamine, formaldehyde, sodium borohydride, aluminum borohydride, lithium aluminum hydride and 2-methyl- It is possible to use a mixture of two or more, but is not limited thereto. The temperature for the reduction reaction is 20 to 180 占 폚, and suitable conditions may be selected depending on the use of the reducing agent and the type of the reducing agent to be used.

본 발명은 또한 나노스폰지 구조의 그래핀닷-팔라듐 하이브리드 촉매 및 상기 촉매가 적용된 촉매 전극에 관한 것이다. 상기 그래핀닷-팔라듐 하이브리드는 나노스폰지 구조가 그래핀닷에 의해 캡슐화된 것으로서, 상기 그래핀닷은 이종 원자가 도핑된 그래핀닷인 것이 더욱 바람직하다. 본 발명의 그래핀닷-팔라듐 하이브리드 촉매는 백금계 금속 촉매가 사용되는 모든 분야에 사용될 수 있다. 즉, 연료전지의 양극(cathode)에서의 산소 환원 반응의 촉매로 사용되거나, 메탄올 또는 포름산의 산화반응, 수소 발생 반응 등을 예시할 수 있으나, 이에 한정되는 것이 아님은 당연하다. 본 발명에 의한 그래핀닷-팔라듐 하이브리드는 다공성 나노스폰지 구조를 갖기 때문에 전기화학적 유효표면적이 넓고, 그래핀닷의 추가적인 전기전도도 특성으로 인하여 촉매활성이 높다. 그래핀닷-팔라듐 하이브리드는 수소 발생 반응과 메탄올 산화 반응을 예로 평가해 본 결과, 상용의 탄소지지체에 담지되어 있는 백금 촉매보다도 우수한 활성을 나타내었다. 또한 크로노암페로메트리나 CO stripping test 결과 시간의 경과에 따른 전자밀도의 변화가 적고 내피독성을 나타내어 내구성이 우수함을 확인할 수 있었다.The present invention also relates to a graphene-palladium hybrid catalyst having a nano sponge structure and a catalyst electrode to which the catalyst is applied. The grapindole-palladium hybrid is one in which the nano sponge structure is encapsulated by grapindod, and it is more preferable that the grapindot is a hetero-doped graphene dot. The grapindow-palladium hybrid catalyst of the present invention can be used in all fields where a platinum group metal catalyst is used. That is, the catalyst may be used as a catalyst for an oxygen reduction reaction at the cathode of a fuel cell, an oxidation reaction of methanol or formic acid, a hydrogen generation reaction, and the like, but is not limited thereto. Since the grapindow-palladium hybrid according to the present invention has a porous nano-sponge structure, the electrochemically effective surface area is wide and the catalytic activity is high due to the additional electrical conductivity characteristic of the grapindock. As a result of evaluating the hydrogen generation reaction and the methanol oxidation reaction, the grapindod - palladium hybrid showed better activity than the platinum catalyst supported on the commercial carbon support. Also, it was confirmed that chronoam ferrometry and CO stripping test showed less change of electron density with time and showed endotoxic effect and durability.

이상과 같이 본 발명의 방법에 의해 제조되는 그래핀닷-팔라듐 하이브리드는 나노스폰지 구조로 인하여 유효표면적이 넓고, 그래핀닷의 전기전도도로 인하여 전자의 이동을 가속화시키기 때문에 상용의 cPt/C 촉매에 비해서도 촉매활성이 매우 우수하다. 또한 표면이 Gdot으로 캡슐화되어 있어 내피독성이 우수하고 시간 경과에 따른 전자밀도의 변화가 적어 내구성이 현저하므로 고가의 백금 촉매의 대체제로서 유용하게 사용될 수 있다. As described above, since the graphene dot-palladium hybrid produced by the method of the present invention has a wide effective surface area due to the nano sponge structure and accelerates electron transfer due to the electrical conductivity of the grapindot, The activity is very good. Also, since the surface is encapsulated with Gdot, endotoxic toxicity is excellent and durability is remarkable due to little change in electron density with time, which can be usefully used as an alternative to expensive platinum catalysts.

또한 본 발명의 그래핀닷-팔라듐은 제조방법이 간단할 뿐 아니라, 반응 조건이 온화하여 경제적인 촉매의 제조가 가능하다. In addition, the process of the present invention is not only simple but also facilitates the production of economical catalysts due to mild reaction conditions.

도 1은 실시예 및 비교예의 나노구조체의 제조방법을 보여주는 개략도.
도 2는 본 발명의 일실시예에 의해 제조된 Gdot-Pd 하이브리드 및 비교예의 나노입자들의 HR-TEM 이미지 및 XRD 스펙트럼.
도 3은 Gdot-Pd 하이브리드의 구조적 특성을 보여주는 HR-TEM 이미지 및 스펙트럼.
도 4는 Gdot-Pd 하이브리드의 전기화학적 특성을 보여주는 CV 곡선과 그로부터 계산된 유효표면적의 그래프.
도 5는 전기화학 임피던스 분광기(EIS)를 이용한 Nyquist plot.
도 6은 수소 발생 반응에 대한 Gdot-Pd 하이브리드의 전기화학적 촉매 특성을 보여주는 그래프.
도 7은 메탄올 산화 반응에 대한 Gdot-Pd 하이브리드의 전기화학적 촉매 특성을 보여주는 그래프.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a schematic view showing a method for producing nanostructures of Examples and Comparative Examples. FIG.
Figure 2 shows HR-TEM images and XRD spectra of Gdot-Pd hybrids prepared according to one embodiment of the present invention and nanoparticles of a comparative example.
Figure 3 is an HR-TEM image and spectrum showing the structural characteristics of a Gdot-Pd hybrid.
4 is a graph of CV curves showing the electrochemical properties of Gdot-Pd hybrids and the calculated effective surface area therefrom.
5 is a Nyquist plot using an electrochemical impedance spectroscope (EIS).
6 is a graph showing electrochemical catalytic properties of Gdot-Pd hybrids for the hydrogen evolution reaction.
7 is a graph showing the electrochemical catalytic properties of the Gdot-Pd hybrid for the methanol oxidation reaction.

이하 첨부된 실시예를 들어 본 발명을 보다 상세히 설명한다. 그러나 이러한 실시예는 본 발명의 기술적 사상의 내용과 범위를 쉽게 설명하기 위한 예시일 뿐, 이에 의해 본 발명의 기술적 범위가 한정되거나 변경되는 것은 아니다. 이러한 예시에 기초하여 본 발명의 기술적 사상의 범위 안에서 다양한 변형과 변경이 가능함은 당업자에게는 당연할 것이다. Hereinafter, the present invention will be described in more detail with reference to the following examples. However, these embodiments are merely examples for explaining the content and scope of the technical idea of the present invention, and thus the technical scope of the present invention is not limited or changed. It will be apparent to those skilled in the art that various changes and modifications can be made within the scope of the technical idea of the present invention based on these examples.

[실시예][Example]

실시예 1 : 그래핀닷-팔라듐 하이브리드의 제조Example 1: Preparation of grapindot-palladium hybrid

1) 질소 도핑 그래핀닷-팔라듐 하이브리드의 제조1) Preparation of nitrogen doped grapindot-palladium hybrid

질소 도핑 카본닷(Cdot)의 제조Preparation of nitrogen doped carbon dot (Cdot)

Angewandte Chemie International Edition 2013, 52, 7800에 기재된 방법에 따라 질소 도핑된 카본닷(N-Cdot)을 제조하였다. 간략하게는, 구연산(citric acid mohohydrate) 4g과 글리신 1.24g을 10 mL의 DI수에 용해시켰다. 용액을 70℃에서 12시간 처리하여 용매를 증발시키고, 남은 잔사를 오토클레이브에 넣고 4.3℃/분의 속도로 승온하여 200℃에서 3시간동안 수열반응하였다. 검은색 시럽 상태의 산물을 1.0M NaOH 용액을 사용하여 중화하고, 100mL DI수로 희석하였다. 희석용액을 투석막(5kDa MWCO)을 통하여 이차 DI수에 대해 투석하였다. 투석액을 동결건조하여 노란색의 Cdot을 수득하였다. 제조된 N-Cdot은 TEM으로 관측한 결과, 직경이 1.5~2.5nm인 구형이었다. Nitrogen doped carbon dot (N-Cdot) was prepared according to the method described in Angewandte Chemie International Edition 2013, 52 , 7800. Briefly, 4 g of citric acid mohohydrate and 1.24 g of glycine were dissolved in 10 mL of DI water. The solution was treated at 70 DEG C for 12 hours to evaporate the solvent. The remaining residue was placed in an autoclave, heated at a rate of 4.3 DEG C / min, and hydrothermally reacted at 200 DEG C for 3 hours. The black syrupy product was neutralized with 1.0 M NaOH solution and diluted with 100 mL DI water. The diluted solution was dialyzed against a secondary DI number through a dialysis membrane (5 kDa MWCO). The dialysis solution was lyophilized to obtain yellow Cdot. The N-Cdot thus prepared was found to have a spherical shape with a diameter of 1.5 to 2.5 nm as a result of TEM observation.

질소 도핑 그래핀닷-팔라듐 하이브리드(Gdot-Pd)의 제조Preparation of Nitrogen-Doped Grading-Pd Hybrid (Gdot-Pd)

100mL 둥근 플라스크에 DI수 50 ml, 위에서 제조한 29mg의 질소 도핑 Cdot, 브롬화 나트륨(NaBr, Sigma Aldrich) 400mg, 테트라클로로팔라듐산칼륨(K2PdCl4, Sigma-Aldrich) 34mg을 넣고 초음파로 20분간 처리한 후, 혼합액에 28.4 mM L-아스콜빅산(L-aa, ascorbic acid, Sigma Aldrich) 수용액 20 ml를 빠르게 투여하였다. 반응 혼합물을 2분간 교반한 후, 30℃ 오븐에서 45분간 방치하였다. 반응액의 색상이 황갈색의 투명한 용액에서 검은색으로 변하면, 800rpm에서 5분간 원심분리하여 수득하고 물과 에탄올로 수회 세척한 후 70℃에서 2시간 건조하였다. In a 100 mL round flask, 50 mL of DI water, 29 mg of the above-prepared nitrogen-doped Cdot, 400 mg of sodium bromide (NaBr, Sigma Aldrich) and 34 mg of potassium tetrachloropalladate (K 2 PdCl 4 , Sigma-Aldrich) After the treatment, 20 ml of an aqueous solution of 28.4 mM L-ascorbic acid (L-aa, ascorbic acid, Sigma Aldrich) was rapidly administered to the mixed solution. The reaction mixture was stirred for 2 minutes and then left in an oven at 30 ° C for 45 minutes. When the color of the reaction solution changed from a yellowish brown transparent solution to black, it was obtained by centrifugation at 800 rpm for 5 minutes, washed several times with water and ethanol, and dried at 70 ° C for 2 hours.

2) 그래핀닷-팔라듐 하이브리드의 제조2) Preparation of grapindot-palladium hybrid

카본닷(Cdot)의 제조Manufacture of carbon dot (Cdot)

Carbon 2016, 96, 139-144에 기재된 방법에 따라 마이크로 웨이브를 사용하여 카본닷(Cdot)을 제조하였다. 간략하게는, 10mL의 DI수에 구연산(덕산화학) 3g과 우레아(Shinyo Chemical) 3g을 넣고 격렬히 교반한 후 마이크로웨이브 오븐(700W)에서 4분간 처리하였다. 그 결과 얻어진 진한 갈색의 용액을 상온으로 냉각한 후 7000rpm에서 30분간 원심분리하여 검은색의 큰 응집체(aggregate)를 제거하였다. Cdot을 포함하는 상등액은 중탄산수로 중화하고 DI수로 수차례 세척하였다. 검은색의 Cdot을 수거한 후 진공 오븐에서 건조하였다. Carbon Dot (Cdot) was prepared using microwaves according to the method described in Carbon 2016, 96, 139-144. Briefly, 3 g of citric acid (Duksan Chemical) and 3 g of urea (Shinyo Chemical) were added to 10 mL of DI water and vigorously stirred, followed by treatment in a microwave oven (700 W) for 4 minutes. The resulting dark brown solution was cooled to room temperature and centrifuged at 7000 rpm for 30 minutes to remove large black aggregates. The supernatant containing Cdot was neutralized with bicarbonate water and washed several times with DI water. The black Cdots were collected and dried in a vacuum oven.

건조된 Cdot을 에탄올에 분산시켜 마이카 기판(mica substrate)에 떨어뜨려 시료를 제조한 후 MultiMod 8 (Bruker) 현미경을 사용하여 탭핑모드로 AFM 이미지를 얻었다. 관측 결과 제조된 Cdot은 평균 입경이 1.2nm이고, 가우시안 분포를 나타내는 구형임을 확인할 수 있었다. The dried Cdot was dispersed in ethanol and dropped on a mica substrate to prepare a sample. AFM images were obtained in a tapping mode using a MultiMod 8 (Bruker) microscope. As a result of the observation, it was confirmed that the prepared Cdot had an average particle diameter of 1.2 nm and a spherical shape showing a Gaussian distribution.

그래핀닷-팔라듐 하이브리드(Gdot-Pd)의 제조Preparation of Graded-Palladium Hybrid (Gdot-Pd)

질소 도핑 Cdot 대신 위에서 제조한 Cdot을 사용한 것을 제외하고는 질소 도핑 Gdot-Pd 하이브리드의 제조와 동일한 방법에 의해 Gdot-Pd 하이브리드를 제조하였다.A Gdot-Pd hybrid was prepared in the same manner as in the preparation of the nitrogen-doped Gdot-Pd hybrid except that the Cdot prepared above was used instead of the nitrogen-doped Cdot.

비교예 1 : Pd 나노구조체의 제조Comparative Example 1: Preparation of Pd nanostructure

100mL 둥근 플라스크에 DI수 50 ml를 넣고 테트라클로로팔라듐산칼륨(K2PdCl4) 34mg을 용해시킨 후, 28.4 mM L-아스콜빅산 수용액 20 mL를 빠르게 투여하였다. 반응 혼합물을 2분간 교반하고 30℃ 오븐에서 5분간 방치하였다. 반응액의 색상이 황갈색의 투명한 용액에서 회갈색으로 변하면, 800rpm에서 5분간 원심분리하여 수득하고 물과 에탄올로 수회 세척한 후 70℃에서 2시간 건조하였다. In a 100 mL round flask, 50 mL of DI water was added, and 34 mg of potassium tetrachloropalladate (K 2 PdCl 4 ) was dissolved. 20 mL of 28.4 mM aqueous solution of L-ascorbic acid was rapidly administered. The reaction mixture was stirred for 2 minutes and allowed to stand in an oven at 30 DEG C for 5 minutes. When the color of the reaction solution changed from a yellowish brown transparent solution to a grayish brown color, it was obtained by centrifugation at 800 rpm for 5 minutes, washed several times with water and ethanol, and then dried at 70 ° C for 2 hours.

비교예 2 : Pd 나노구조체의 제조Comparative Example 2: Preparation of Pd nanostructure

브롬화 나트륨 400 mg 테트라클로로팔라듐산칼륨과 함께 용해시켜 30℃에서 20분간 반응시킨 것을 제외하고는 비교예 1과 동일한 방법에 의해 Pd 나노구조체를 제조하였다.Pd nanostructure was prepared in the same manner as in Comparative Example 1, except that sodium bromide was dissolved in 400 mg of potassium tetrachloropalladate and reacted at 30 ° C for 20 minutes.

비교예 3 : 카본닷-팔라듐 하이브리드의 제조Comparative Example 3: Preparation of carbon dot-palladium hybrid

NaBr을 첨가하지 않고 30℃에서 20분간 반응시킨 것을 제외하고는 실시예 1과 동일한 방법에 의해 카본닷-팔라듐 하이브리드를 제조하였다.A carbon dot-palladium hybrid was prepared in the same manner as in Example 1, except that NaBr was not added and the reaction was carried out at 30 ° C for 20 minutes.

반응액의 색상이 황갈색의 투명한 용액에서 회갈색으로 변하면, 800rpm에서 5분간 원심분리하여 수득하고 물과 에탄올로 수회 세척한 후 70℃에서 2시간 건조하였다. When the color of the reaction solution changed from a yellowish brown transparent solution to a grayish brown color, it was obtained by centrifugation at 800 rpm for 5 minutes, washed several times with water and ethanol, and then dried at 70 ° C for 2 hours.

실시예 및 비교예의 나노입자 제조 시 NaBr을 사용한 실시예 1과 비교예 2는 NaBr을 사용하지 않은 비교예 1과 비교예 3에 비해 반응액의 색상 변화가 느려, NaBr에 의해 Pd 전구체의 환원 속도가 지연됨을 보여주었다. In Example 1 and Comparative Example 2 using NaBr in the preparation of the nanoparticles of Examples and Comparative Examples, the color change of the reaction solution was slower than that of Comparative Example 1 and Comparative Example 3 in which NaBr was not used and the reduction rate of the Pd precursor Was delayed.

도 1에 실시예 1 및 비교예의 반응을 비교하여 도시하였다.Fig. 1 shows a comparison of the reactions of Example 1 and Comparative Example.

실시예 2 : 그래핀닷-팔라듐 하이브리드의 구조 특성 분석Example 2: Structural characterization of grapindot-palladium hybrid

실시예 1에서 제조한 Gdot/Pd의 모포로지 특성을 필드방사 주사전자현미경(FE-SEM, JSM-7000F, JEOL, Japan)과 투과전자현미경(TEM, JEM-2010HR) 및 고해상도 투과전자현미경(HRTEM, JEM-2100F, JEOL, Japan)으로 분석하였다. 시료는 에탄올에 분산시켜 카본으로 코팅된 구리 TEM 그리드(Ted Pella, Redding, USA)에 적가한 후 상온상압에서 건조하였다. The morphology of Gdot / Pd prepared in Example 1 was analyzed by field emission scanning electron microscope (FE-SEM, JSM-7000F, JEOL, Japan), transmission electron microscope (TEM, JEM- 2010HR) and high resolution transmission electron microscope , JEM-2100F, JEOL, Japan). Samples were dispersed in ethanol and dropped onto carbon coated copper TEM grid (Ted Pella, Redding, USA) and dried at normal temperature and pressure.

도 2의 a)는 비교예 1, b)는 비교예 2, c)와 d)는 비교예 3, e)와 f)는 실시예 1의 1)에서 제조한 나노구조체들의 HR-TEM 이미지이며, g)는 XRD 패턴을 나타내는 것이다. 실시예 1의 Gdot-Pd 하이브리드는 전체적으로 다공성 나노스폰지 구조를 형성하는 것을 보여준다. 이에 반해 Cdot이 없는 조건에서 Pd 전구체를 환원시킨 경우에는 NaBr의 존재와 무관하게 Pd 입자들이 치밀하게 응집되어 있는 것을 확인할 수 있다. NaBr이 없는 상태에서 환원되어 제조된 Pd 나노입자는 입자의 크기가 거의 균일하였으며, 나노-이십면체(icosahedrons) 구조에 해당하는 전형적인 d-간격을 나타내었다(도 2의 a). Pd의 환원 시 NaBr을 첨가한 비교예 2의 경우에는 표면에 돌기가 형성된 모양의 나노구조체가 형성되었으나, 역시 치밀한 응집 구조를 나타내었다(도 2의 b). Pd 전구체의 환원 시 C-dot만을 함께 첨가한 비교예 3의 경우에는 아주 작은 구형의 나노입자들이 응집되어 있는 약 50~100 nm 크기의 나노라스베리 구조를 나타내었다(도 2의 c 및 d). Pd 나노라스베리의 d-간격은 Pd의 (111) 면에 기인한 약 0.226 nm로 XRD 데이터에서도 (111)면이 우세함을 확인할 수 있었다. 이는 Cdot이 구조 형성에 중요한 역할을 함을 시사한다. Cdot과 함께 NaBr이 함께 첨가된 실시예 1의 Gdot-Pd 하이브리드는 e)와 f)에서 확인할 수 있듯이 3차원 나노스폰지 구조를 나타내었다. HR-TEM 이미지에서 d-간격은 0.226으로 Pd의 (111)면에 해당하였다. XRD 패턴은 나노스폰지 구조의 Gdot-Pd 하이브리드의 결정성이 비교예의 나노입자에 비해 우수함을 나타낸다. 2 (a) is a HR-TEM image of the nanostructures prepared in 1) of Example 1, b) of Comparative Example 2, c) and d) is Comparative Example 3 and e) , g) represents an XRD pattern. The Gdot-Pd hybrids of Example 1 show overall formation of a porous nanosponge structure. On the other hand, when the Pd precursor is reduced under the absence of Cdot, it can be confirmed that the Pd particles are densely aggregated irrespective of the presence of NaBr. The Pd nanoparticles produced by reduction in the absence of NaBr had almost uniform particle size and typical d-spacings corresponding to the nano-icosahedrons structure (FIG. 2 a). In the case of Comparative Example 2 in which NaBr was added during the reduction of Pd, nanostructures having protrusions on the surface were formed, but also dense aggregation structures were shown (FIG. 2 b). In the case of Comparative Example 3 in which only the C-dot was added during the reduction of the Pd precursor, nano-raspberry structure having a size of about 50 to 100 nm in which very small spherical nanoparticles aggregated (c and d in FIG. The d-spacing of Pd nano-raspberry was found to be about 0.226 nm due to the (111) plane of Pd, and the (111) plane was dominant in XRD data. This suggests that Cdot plays an important role in structure formation. The Gdot-Pd hybrid of Example 1 in which NaBr was added together with Cdot showed a three-dimensional nano-sponge structure as shown in e) and f). In the HR-TEM image, the d-spacing was 0.226, corresponding to the (111) plane of Pd. The XRD pattern shows that the crystallinity of the Gdot-Pd hybrid of the nano sponge structure is superior to that of the comparative nanoparticles.

상기 구조는 도 3의 HRTEM 이미지와 라만 스펙트럼, XPS 스펙트럼 및 XRD 스펙트럼으로부터 추가 확인이 가능하였다. 도 3의 a)~c)는 실시예 1에서 제조한 Gdot-Pd 하이브리드의 HR-TEM 이미지로 나노입자들이 서로 연결되어 나노스폰지 구조의 3차원 네트워크를 형성하는 것을 확인할 수 있다. 이는 비교예에서 제조된 나노입자들과 전혀 상이한 구조로 Cdot과 NaBr 모두가 나노스폰지 구조의 형성에 중요한 역할을 담당하는 것을 시사한다.The structure was further confirmed from the HRTEM image of FIG. 3 and Raman spectrum, XPS spectrum and XRD spectrum. 3 (a) to 3 (c) illustrate HR-TEM images of the Gdot-Pd hybrid prepared in Example 1, showing that the nanoparticles are connected to each other to form a three-dimensional network of a nano-sponge structure. This suggests that both of Cdot and NaBr play an important role in the formation of the nanosponge structure with a completely different structure from the nanoparticles prepared in the comparative example.

나노스폰지 구조는 확대된 도면인 도 3의 c에서 다공성의 나노스폰지 구조는 얇은 층상의 환원된 Gdot으로 둘러쌓여 있음을 확인할 수 있다. 이는 반응 공정에서 다층구조를 갖는 준구형의 Cdot이 박리되어 시트상의 Gdot이 생성되며, 이에 의해 나노스폰지 구조를 캡슐화함을 보여준다. 반면 비교예 3에서 NaBr을 사용하지 않고 제조한 Cdot-Pd 하이브리드는 확대된 도면에서도 나노입자가 Cdot 또는 Gdot으로 둘러쌓여 있지 않았다(데이터 미도시). 라만 스펙트럼(도 3의 d)에서는 무질서한 카본의 D 피크와 그라파이트 카본의 G 피크가 관측되어 나노입자에 Gdot 층이 형성되었음을 보여주었다. XRD 스펙트럼(도 3의 g)에서도 Pd의 결정구조를 보여주는 피크와 함께 20° 부근에서 탄소물질의 신호가 검출되어 나노스폰지 내에 Gdot이 포함되어 있음을 알 수 있다. 탄소의 피크는 매우 브로드하여 그라파이트 형태의 카본만이 포함되어 있고 결정상은 함유되어 있지 않으며 Gdot의 크기가 매우 작음을 시사하였다. 도 3의 h는 Gdot-Pd 하이브리드의 제조에 사용한 Cdot의 TEM 이미지와 XRD 스펙트럼을 보여주는 것으로, 2~5 nm 크기의 구형 입자로 매우 브로드한 XRD 피크를 보여준다. 도 3의 e와 f는 각각 Gdot-Pd 하이브리드에서 Pd 3d와 C 1s에 대한 XPS 스펙트럼이며, i는 하이브리드 제조 시 사용한 Cdot의 XPS 스펙트럼이다. 도 3의 f와 i를 비교하면, sp2 그라파이트 C(C-C)에 대한 피크가 Cdot에서보다 하이브리드에서 약간 블루 시프트(blue shift)된 것을 확인할 수 있는데, 이는 Pd 전구체의 환원과정에서 생성된 Gdot 역시 일부 환원되었음을 의미한다.The nano sponge structure is enlarged in FIG. 3C. It can be seen that the porous nano sponge structure is surrounded by a thin layer of reduced Gdot. This shows that in the reaction process, the semi-spherical Cdot with a multi-layer structure is peeled off to produce Gdot on the sheet, thereby encapsulating the nanosponge structure. On the other hand, in the Cdot-Pd hybrid prepared without using NaBr in Comparative Example 3, the nanoparticles were not surrounded by Cdot or Gdot in the enlarged drawing (data not shown). In the Raman spectrum (Fig. 3 (d)), disordered D peaks of carbon and G peaks of graphite carbon were observed to show that a Gdot layer was formed on the nanoparticles. Also in the XRD spectrum (g in FIG. 3), a signal of a carbon material was detected at around 20 ° along with a peak showing the crystal structure of Pd, indicating that Gdot was contained in the nanospond. The peak of carbon was very broad, containing only graphite carbon, no crystalline phase, and a very small Gdot size. FIG. 3 h shows the TEM image and XRD spectrum of the Cdot used in the preparation of the Gdot-Pd hybrid, showing a very broad XRD peak with spherical particles of 2 to 5 nm in size. 3 e and f are XPS spectra of Pd 3d and C 1s in the Gdot-Pd hybrid, respectively, and i is the XPS spectrum of the Cdot used in the hybrid production. Comparing f and i in FIG. 3, it can be seen that the peak for sp2 graphite C (CC) is slightly blue-shifted in hybrid than in Cdot because Gdot generated in the reduction of Pd precursor is also partly It means that it has been reduced.

실시예 3 : Gdot-Pd의 촉매 활성 평가Example 3: Evaluation of catalytic activity of Gdot-Pd

작업전극의 제조Manufacture of working electrode

10 ml 2-프로파놀과 29.8 ml DI수(DI) 및 0.2 ml 5w% Nafion 용액을 혼합하여 스톡 용액을 제조하였다. 0.5 ml의 스톡용액과 실시예 1의 1)에서 제조한 Gdot-Pd 나노스폰지 하이브리드 0.5 mg 를 2 ml 바이알에 넣고 볼텍스 믹서-KMC-1300V를 사용하여 5분간 혼합하였다. 이후 30℃ 이하의 온도에서 30분간 소니케이터로 처리하여 균질한 촉매 잉크를 제조하였다. A stock solution was prepared by mixing 10 ml 2-propanol with 29.8 ml DI water (DI) and 0.2 ml 5w% Nafion solution. 0.5 ml of the stock solution and 0.5 mg of the Gdot-Pd nano-sponge hybrid prepared in 1) of Example 1 were placed in a 2 ml vial and mixed using a Vortex mixer-KMC-1300V for 5 minutes. And then treated with a sonicator at a temperature of 30 캜 or less for 30 minutes to prepare a homogeneous catalyst ink.

글래시 카본 회전 디스크 전극을 1 ㎛ 연마 다이아몬드 현탁액으로 연마하고, 이어서 0.05 ㎛ Al2O3 입자 현탁액으로 연마하였다. 연마된 전극은 DI수로 세척하고, DI수와 함께 5분간 소니케이션한 후 다시 DI수로 세척하였으며, 30분간 상온에서 건조하였다.The glacier carbon rotating disk electrode was polished with a 1 탆 polished diamond suspension and then polished with a 0.05 탆 Al 2 O 3 particle suspension. The polished electrode was washed with DI water, sonicated for 5 minutes with DI water, washed again with DI water, and dried at room temperature for 30 minutes.

위에서 제조한 3 ㎕의 촉매 잉크를 건조한 글래시 카본 전극에 드랍-캐스팅한 후 촉매 필름을 상온에서 30분간 건조하여 작업전극을 제조하였다.3 [mu] l of the catalyst ink prepared above was drop-cast onto a dry glacier carbon electrode, and the catalyst film was dried at room temperature for 30 minutes to prepare a working electrode.

전기화학적 측정Electrochemical measurement

전기화학적 측정은 ALS 회전 디스크 전극(RDE) 장치와 IVIUM 전위가변기(potentiostat)를 갖는 3전극 셀 내에서 수행하였다. 백금흑부 백금(platinized Pt) 메쉬를 상대전극으로, Ag/AgCl(3M Cl-)을 기준전극으로, 질소가 포화된 0.5M H2SO4 수용액을 전해질로 사용하였다. Electrochemical measurements were performed in a three electrode cell with an ALS rotary disk electrode (RDE) device and an IVIUM potential potentiostat. An aqueous solution of 0.5M H 2 SO 4 saturated with nitrogen was used as a counter electrode with a platinum Pt mesh and Ag / AgCl (3M Cl - ) as a reference electrode.

사이클릭 볼타모그램(CV, cyclic volatmogram) 측정을 위하여 3전극 셀을 초순도의 질소로 30분간 퍼징하고, 측정 중에서 질소를 퍼징하면서 0.05V 내지 1.20V의 범위 내에서 50 mV/s의 스캔 속도로 수행하였다. The three-electrode cell was purged with ultra-pure nitrogen for 30 minutes to measure the cyclic voltamogram (CV), and a scanning speed of 50 mV / s within the range of 0.05 V to 1.20 V .

비교를 위하여, Gdot-Pd 나노스폰지 대신 상용화된 Pt/C(c-Pt/C) 촉매(20% Pt on Vulcan XC-72, Alfa Aesar) 또는 비교예 1 또는 비교예 3의 나노입자를 사용하여 작업전극을 제조하고, 동일한 방법에 의해 전기화학적 측정을 실시하였다.For comparison, a commercially available Pt / C (c-Pt / C) catalyst (20% Pt on Vulcan XC-72, Alfa Aesar) or a nanoparticle of Comparative Example 1 or Comparative Example 3 was used instead of Gdot- A working electrode was prepared and subjected to electrochemical measurements by the same method.

도 4는 상기 방법에 의해 측정된 CV 곡선(a)과 이로부터 계산된 전기화학적 유효표면적(ECSA, electrochemical surface area)(b)이다. 양극(anodic) 스캔에서 Pd-O의 생성에 대한 개시전위(onset potential)는 0.7 V였으며, Pd-O의 환원에 대한 양극 전위는 0.7 V였다. Cdot-Pd 나노스폰지 작업전극의 표면에서의 수소 흡착과 탈착 피크는 각각 0.13 V 및 0.18 V에 위치하였으며, 수소 흡착과 탈착 피크 간의 ΔEp 값은 비교예 3의 작업전극보다 작았다. 따라서 Gdot-Pd 나노스폰지 하이브리드는 비교예 3의 Cdot-Pd 하이브리드에 비해 가역성이 높고, 수소 미달전위 석출(hydrogen underpotential deposition) 속도가 빠름을 알 수 있다. 이는 3차원 나노네트워크 구조로 인하여 기공 내에 수소 분자를 쉽게 포획할 뿐 아니라 쉽게 재산화할 수 있기 때문으로 생각된다. Fig. 4 shows the CV curve (a) measured by the above method and the calculated electrochemical surface area (ECSA) (b). The onset potential for the generation of Pd-O in the anodic scan was 0.7 V and the positive potential for the reduction of Pd-O was 0.7 V. The hydrogen adsorption and desorption peaks at the surface of the Cdot-Pd nano sponge working electrode were located at 0.13 V and 0.18 V, respectively, and the ΔE p value between the hydrogen adsorption and desorption peaks was smaller than that of the working electrode of Comparative Example 3. Therefore, the Gdot-Pd nano sponge hybrid is more reversible than the Cdot-Pd hybrid of Comparative Example 3, and the hydrogen underpotential deposition rate is faster. This is thought to be due to the fact that the hydrogen molecule can be easily trapped and easily reoxidized in the pore due to the three dimensional nano network structure.

실시예 1의 Gdot-Pd 나노스폰지 하이브리드는 3차원 네트워크 구조로 인하여 유효표면적이 매우 넓으며, 전기화학적으로도 Cdot이 없는 상태에서 제조된 비교예 1의 Pd는 물론 c-PtC와 NaBr이 없는 상태에서 제조된 비교예 3의 Cdot-Pd 하이브리드에 비해서도 더욱 민감함을 보여주어, 전자촉매로서 매우 유용함을 나타내었다.The Gdot-Pd nano-sponge hybrid of Example 1 has a very wide effective surface area due to its three-dimensional network structure, and has no c-PtC and NaBr as well as Pd of Comparative Example 1 prepared in the absence of Cdot electrochemically , Which is more sensitive than the Cdot-Pd hybrid prepared in Comparative Example 3, and thus it is very useful as an electrocatalyst.

도 5의 (a)는 전기화학 임피던스 분광기(EIS)를 이용한 Nyquist plot으로, 0.0VRHE에서 측정한 임피던스 스펙트럼이며, 도 5의 (b)는 고주파 영역에서의 Nyquist plot의 확대도이다. Nyquist plot은 두 개의 반원으로 이루어져 있으며, 고주파 영역의 첫 번째 반원은 표면의 다공성과 관련되어 있고, 저주파 영역의 반원은 전하이동 특성과 관련되어 있다. 다공성과 관련된 저항값 Rp의 크기는 비교예 1 > cPt/C > 비교예 3 > 실시예 1의 순서였으며, 구체적인 수치는 각각 6.65Ω > 4.133 Ω > 2.526 Ω > 2.222 Ω이었다. 전하이동과 관련된 저항값 Rct의 크기 역시 비교예 1이 19.18 Ω으로 가장 컸으며, 실시예 1이 0.50으로 가장 작았다. 비교예 1 > 비교예 3 > cPt/C > 실시예 1의 순서로, 구체적인 수치는 각각 19.18 Ω > 7.318 Ω > 0.66 Ω > 0.50 Ω이었다. 5 (a) is an Nyquist plot using an electrochemical impedance spectroscope (EIS), which is an impedance spectrum measured at 0.0 V RHE , and FIG. 5 (b) is an enlarged view of a Nyquist plot in a high frequency region. The Nyquist plot consists of two semicircles, the first semicircle of the high frequency region being related to the porosity of the surface, and the semicircle of the low frequency region being related to the charge transfer characteristic. The magnitude of the resistance value R p related to porosity was the order of Comparative Example 1> cPt / C> Comparative Example 3> Example 1, and specific values were 6.65Ω>4.133Ω>2.526Ω> 2.222Ω. The magnitude of the resistance value R ct associated with charge transfer was also greatest at 19.18 Ω in Comparative Example 1 and the smallest at 0.50 in Example 1. Comparative Example 1> Comparative Example 3> cPt / C> In the procedure of Example 1, specific values were 19.18?>7.318?>0.66?> 0.50?.

하기 표 1과 표 2는 각각 여러 가지 촉매들의 HER 파라메타와, 과전압 -0.1 V에서 Nyquist plot으로부터 계산된 촉매들의 EIS(electrochemical impedence spectroscopy) 데이터 피팅 매개 변수를 정리한 것이다. The following Tables 1 and 2 summarize the HER parameters of various catalysts and the electrochemical impedence spectroscopy (EIS) data fitting parameters of catalysts calculated from the Nyquist plot at over-voltage -0.1 V, respectively.

Figure pat00001
Figure pat00001

Figure pat00002
Figure pat00002

도 6은 질소가 포화된 0.5M H2SO4에서 HER 반응에 대한 촉매 활성을 선형주사전위법(LSV, linear sweep voltammetry)에 의해 추가적으로 확인한 것이며, 상세한 데이터는 표 3에 기재하였다. 도 6에서 (a) 분극 곡선과 10mA/㎠에서의 과전위(내부 도면), (b) 0.5M H2SO4 수용액에서, 스캔 속도 10 mV/s, 회전 속도 1600 rpm에서 측정한 Tafel plot, (c) Gdot-Pd 나노스폰지 전극의 첫 번째 및 3000 사이클 이후의 LSV 곡선, (d) -120 mVRHE의 과전위에서 측정한 크로노암페로메트리(chronoamperometry) 그래프이다. Figure 6 is a further verification of the catalytic activity for HER reaction in nitrogen-saturated 0.5 MH 2 SO 4 by linear sweep voltammetry (LSV) and detailed data are given in Table 3. (B) a Tafel plot measured at a scan speed of 10 mV / s and a rotation speed of 1600 rpm in a 0.5 M H 2 SO 4 aqueous solution, (a) a polarizing curve and an overvoltage (internal drawing) at 10 mA / c) LSV curve after the first and 3000 cycles of the Gdot-Pd nano-sponge electrode, and (d) chronoamperometry plot of the chronoam above-120 mV RHE .

Figure pat00003
Figure pat00003

도 6에서 Gdot-Pd 나노스폰지는 비교예의 나노입자는 물론 cPt/C 보다도 수소발생반응(HER)에 대한 성능이 우수하여 전자촉매로서의 유용성을 확인할 수 있었다. 10 mA/㎠에서의 과전압은 연료전지 디자인에서 고려될 주요한 변수로, 표준 변수로 사용된다. 도 6의 a)의 내부도면은 상기 과전압을 도시한 것으로, 표 3의 값에서 확인할 수 있듯이 Gdot-Pt 나노스폰지의 과전압은 -32 mV로 상용의 cPt/C의 -40 mV보다도 낮았다. 또한 Tafel plot에서의 기울기 역시 수소 발생 반응이 Gdot-Pd 나노스폰지에서 다른 촉매에서보다 향상되는 것을 보여주어 수소 발생 반응 촉매 활성이 높은 것을 확인할 수 있다. 크로노암페로메트리에 의한 교환전류밀도나 비교환전류밀도 값 역시 Gdot-Pd 나노스폰지에서 가장 높아서 촉매 활성이 가장 우수함을 나타내었다. 또한, 크로노암페로메트리에서 비교예 1은 전류밀도가 급격하게 감소하는 반면, cPt/C와 비교예 3 및 Gdot-Pd 나노스폰지는 전류밀도의 변화가 비교적 완만하였다. 특히 Gdot-Pd 나노스폰지는 시간의 변화에 따른 전류밀도가 안정적이어서, 촉매의 내구성이 우수함을 나타내었다. Gdot-Pd 나노스폰지 촉매의 내구성은 (c)의 LSV 곡선에서도 확인할 수 있다. 통상 촉매는 산성 조건에서 장기간 작동함에 따라 활성이 저하되기 때문에 HER 촉매에서 내구성은 가장 중요한 특성의 하나이다. Gdot-Pd 나노스폰지의 LSV 곡선은 3000 사이클의 동작 후에도 개시전위나, 전류밀도에 거의 변화가 없어 내구성이 우수함을 확인할 수 있었다. 이는 나노스폰지 구조의 표면을 둘러싼 Gdot이 Pd 촉매를 보호하는 역할을 하기 때문으로 생각된다. 이에 반해 비교예 3이나 cPt/C 촉매는 3000 사이클 이후 전류밀도가 크게 감소하였다(데이터 미도시).  In FIG. 6, the Gdot-Pd nano sponge exhibited better hydrogen generation reaction (HER) performance than cPt / C as well as the nanoparticles of the comparative example, confirming its usefulness as an electrocatalyst. The overvoltage at 10 mA / cm 2 is a key parameter to be considered in fuel cell design and is used as a standard parameter. 6 shows the overvoltage. As shown in Table 3, the overvoltage of the Gdot-Pt nano sponge was -32 mV, which was lower than -40 mV of the commercial cPt / C. In addition, the slope of the Tafel plot shows that the hydrogen generation reaction is improved in the Gdot-Pd nanosponge than in the other catalysts, so that the hydrogen generation reaction catalyst activity is high. The exchange current density and the non-exchange current density value by Chronoam ferrometry were also highest in the Gdot-Pd nanosponge, indicating that the catalytic activity was the highest. Also, in the chronoam ferrometry, the current density was drastically decreased in Comparative Example 1, while the cPt / C and Comparative Example 3 and the Gdot-Pd nanosponge showed relatively slow changes in the current density. Especially, Gdot-Pd nanosponge shows stable durability of catalyst due to stable current density with time. The durability of the Gdot-Pd nano-sponge catalyst can be seen in the LSV curve of (c). Durability is one of the most important characteristics in HER catalysts, since the activity is usually lowered as the catalyst is operated for a long period under acidic conditions. The LSV curve of the Gdot-Pd nano sponge showed good durability because there was little change in the starting current and current density after 3000 cycles of operation. This is thought to be due to the fact that Gdot surrounding the surface of the nano sponge structure protects the Pd catalyst. On the contrary, the current density of Comparative Example 3 or cPt / C catalyst was greatly reduced after 3000 cycles (data not shown).

도 7의 (a)는 메탄올 산화 반응(MOR)에 대한 촉매 활성을 평가하기 위하여 0.1 M KOH + 1.0 M CH3OH 용액에서 50 mV/s의 스캔 속도로 측정한 CV 곡선이며, (b)는 0.1M KOH 용액에서 50 mV/s의 스캔 속도로 측정한 CO stripping CV 곡선이다. FIG. 7 (a) is a CV curve measured at a scan rate of 50 mV / s in a 0.1 M KOH + 1.0 M CH 3 OH solution to evaluate the catalytic activity for the methanol oxidation reaction (MOR) CO stripping CV curves measured at a scan rate of 50 mV / s in 0.1 M KOH solution.

도 7의 (a)를 참고하면 Gdot-Pd는 다른 촉매들에 비해 전기화학적 활성이 우수함을 알 수 있다. 또한 도 7의 (b)는 Gdot-Pd 촉매가 CO에 대한 저항력이 우수하여 내피독성이 있음을 보여준다. Referring to FIG. 7 (a), it can be seen that Gdot-Pd is superior in electrochemical activity to other catalysts. Also, FIG. 7 (b) shows that the Gdot-Pd catalyst is excellent in resistance to CO and endotoxic.

Claims (8)

팔라듐 전구체를 카본닷과 브롬화 나트륨과 혼합된 상태에서 환원시키는 것을 특징으로 하는 나노스폰지 구조의 그래핀닷-팔라듐 하이브리드의 제조방법.
Wherein the palladium precursor is reduced in the state of being mixed with carbon dot and sodium bromide.
제 1 항에 있어서,
상기 그래핀닷-팔라듐 하이브리드는 나노스폰지 구조가 그래핀닷에 의해 캡슐화(encapsulating)된 것을 특징으로 하는 나노스폰지 구조의 그래핀닷-팔라듐 하이브리드의 제조방법.
The method according to claim 1,
Wherein the grapindow-palladium hybrid is characterized in that the nanosponge structure is encapsulated by grapindod. ≪ RTI ID = 0.0 > 8. < / RTI >
제 1 항 또는 제 2 항에 있어서,
상기 카본닷은 질소, 황, 인 및 붕소로 이루어진 군으로부터 선택된 하나 이상의 이종 원자가 도핑되어 있는 것을 특징으로 하는 나노스폰지 구조의 그래핀닷-팔라듐 하이브리드의 제조방법.
3. The method according to claim 1 or 2,
Wherein the carbon dot is doped with at least one hetero atom selected from the group consisting of nitrogen, sulfur, phosphorus, and boron.
제 1 항 또는 제 2 항에 있어서,
상기 팔라듐 전구체 100 중량부에 대하여 카본닷 1~200 중량부, 브롬화 나트륨 50~2000 중량부를 사용하는 것을 특징으로 하는 나노스폰지 구조의 그래핀닷-팔라듐 하이브리드의 제조방법.
3. The method according to claim 1 or 2,
Palladium hybrid having a nano-sponge structure, wherein 1 to 200 parts by weight of carbon dots and 50 to 2000 parts by weight of sodium bromide are used relative to 100 parts by weight of the palladium precursor.
나노스폰지 구조의 그래핀닷-팔라듐 하이브리드 촉매.
Nano sponge - structured grapindot - palladium hybrid catalysts.
제 5 항에 있어서,
상기 그래핀닷-팔라듐 하이브리드는 나노스폰지 구조가 그래핀닷에 의해 캡슐화(encapsulating)된 것을 특징으로 하는 나노스폰지 구조의 그래핀닷-팔라듐 하이브리드 촉매.
6. The method of claim 5,
Wherein the grapindow-palladium hybrid is characterized in that the nano sponge structure is encapsulated by grapindot.
제 5 항 또는 제 6 항에 있어서,
상기 그래핀닷은 질소, 황, 인 및 붕소로 이루어진 군으로부터 선택된 하나 이상의 이종 원자가 도핑되어 있는 것을 특징으로 하는 나노스폰지 구조의 그래핀닷-팔라듐 하이브리드 촉매.
The method according to claim 5 or 6,
Wherein the graphene dot is doped with at least one hetero atom selected from the group consisting of nitrogen, sulfur, phosphorus, and boron, and the graphene dot-palladium hybrid catalyst having a nano sponge structure.
제 5 항 또는 제 6 항의 그래핀닷-팔라듐 하이브리드 촉매를 포함하는 촉매 전극.A catalyst electrode comprising the grapindot-palladium hybrid catalyst of claim 5 or 6.
KR1020180084246A 2017-07-24 2018-07-19 Preparation Method for Gdot-Pd Hybrid with Nanosponge Structure and Gdot-Pd Hybrid Catalyst KR102108907B1 (en)