KR20180111086A - Artificial leather having suede touch and manufactruing method of the same - Google Patents
Artificial leather having suede touch and manufactruing method of the same Download PDFInfo
- Publication number
- KR20180111086A KR20180111086A KR1020170041508A KR20170041508A KR20180111086A KR 20180111086 A KR20180111086 A KR 20180111086A KR 1020170041508 A KR1020170041508 A KR 1020170041508A KR 20170041508 A KR20170041508 A KR 20170041508A KR 20180111086 A KR20180111086 A KR 20180111086A
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- artificial leather
- binder
- skin layer
- coating
- Prior art date
Abstract
Description
본 발명은 스웨이드질감을 갖는 인조가죽 제조방법 및 그에 의해 제조된 인조가죽에 관한 것이고, 보다 구체적으로 미세엠보가 폴리우레탄수지에 전사되어 스웨이드의 질감을 갖는 인조가죽 및 그의 제조방법 제조방법에 관한 것이다.TECHNICAL FIELD The present invention relates to a process for producing artificial leather having a suede texture and a synthetic leather produced thereby, and more particularly to a synthetic leather having a suede texture transferred to a polyurethane resin and a process for producing the synthetic leather .
일반적으로 오랜 옛날부터 천연피혁은 우리 인간에게 필요 불가결한 물건으로 쓰여왔다. 그러나 천연피혁의 자원은 한정되어 있으므로 해서 그 수요를 충분히 충족시키지 못할 뿐만 아니라 각종 환경문제와 유럽 등지에서 시작된 동물보호운동의 확산으로 수급이 점차 감소되는 추세이다.In general, natural leather has long been used as an indispensable item for human beings. However, since natural leather resources are limited, not only does it not meet the demand, but also the supply and demand is gradually decreasing due to various environmental problems and the proliferation of animal protection campaigns started in Europe and elsewhere.
그리고 천연피혁의 대체품을 찾기 위하여 나일론 레더(nylon Leather), 폴리염화비닐 레더(PVC Leather), 폴리우레탄 건식 레더(PU Dry type Leather) 등 많은 인조·합성피혁이 개발되었지만, 천연피혁으로서의 물리적 강도, 구조, 성능, 외관 등에 비하여 퀄리티가 현저히 저하되고 있다.Many artificial and synthetic leather such as nylon leather, PVC leather and PU dry type leather have been developed to find a substitute for natural leather. However, Quality, performance, appearance, and the like.
일반적으로 부직포를 이용한 인조피혁의 제조방법은 나일론(nylon)-폴리스티렌(polystyrene; PS), 폴리에틸렌 테레프탈레이트(polyethylene terephthalate; PET)-폴리스티렌(PS) 등으로 된 혼합섬유를 부직포를 제작하며, 피혁의 바닥부가 되는 부직포 상에 수용성 용제로 용융된 폴리우레탄(polyurethane)용액을 나이프 코팅하여 피혁의 육부가 되는 은면층을 형성하고, 별도로 피혁무늬가 부각되어 있는 박리지(release paper)에 폴리우레탄(PU) 용액을 코팅하여 시트를 만들고, 이 시트를 상기 은면층 위에 전사방식으로 접합한 다음, 이를 수중에서 폴리우레탄 (PU)용액을 응고시켜 수세한 다음 박리지를 제거하고 건조하면, 표면에는 피혁 무늬의 피막이 형성되고, 그 하위에는 전사층과 은면층이 결합된 피혁의 육면층과 섬유층이 순차적으로 적층된 일체의 인조피혁이 완성된다.Generally, a method for producing artificial leather using nonwoven fabric is to make nonwoven fabrics of blended fibers of nylon-polystyrene (PS), polyethylene terephthalate (PET) -polystyrene (PS) A polyurethane solution is knife coated on a nonwoven fabric which is a bottom part and is melted with a water soluble solvent to form a silver surface layer which becomes a thick part of the leather and a polyurethane (PU) is applied to a releasing paper, (PU) solution is coagulated in water to remove water, followed by removing the release paper and drying it. Thereafter, a leather-like film is formed on the surface of the sheet And a synthetic leather layer having a skin layer and a fibrous layer successively laminated with a transfer layer and a silver layer bonded to each other is completed All.
그러나 상기한 방식으로 제조된 종래기술에 따른 인조피혁은 피혁자체가 부드럽지 못하고 뻣뻣한 느낌으로 품질이 저하될 뿐만 아니라, 대량생산에도 어려운 문제점을 지니고 있다.However, the artificial leather according to the related art manufactured by the above-described method has a problem that the leather itself is not smooth, stiff and deteriorates in quality, and is also difficult to mass-produce.
본 발명의 일 관점은 폴리우레탄의 표면에 미세엠보를 전사시켜 기모와 부드러운 촉감으로 스웨이드질감을 느낄 수 있는 인조가죽 및 그의 제조방법을 제공하기 위한 것이다.One aspect of the present invention is to provide an artificial leather which can transfer a fine emboss to a surface of a polyurethane to feel a suede texture by brushed and soft touch, and a method of manufacturing the same.
본 발명의 다른 관점은 미세엠보가 인쇄된 박리지에 수성우레탄수지의 스킨층을 코팅하고, 박리지를 제거하는 방식으로 미세엠보를 전사시킴에 따라 대량생산이 가능하고, 차량용으로 구현 가능한 인조가죽 및 그의 제조방법을 제공하기 위한 것이다.Another aspect of the present invention is to provide an artificial leather which can be mass-produced by coating a skin layer of an aqueous urethane resin on a release paper on which fine embosses are printed and transferring the microemboss in such a manner as to remove the release paper, And a method for manufacturing the same.
본 발명의 일실시예에 따른 인조가죽 제조방법은 복수개의 미세엠보가 인쇄된 박리지에 스킨층을 코팅하는 단계와, 상기 스킨층에 바인더를 코팅하는 단계와, 상기 바인더에 배킹클로스(Backing cloth)를 접착하는 단계와, 상기 박리지를 제거하는 단계를 포함한다. A method of manufacturing artificial leather according to an embodiment of the present invention includes coating a skin layer on a release paper on which a plurality of micro-embossments are printed, coating a binder on the skin layer, forming a backing cloth on the binder, , And removing the peeling paper.
또한, 상기 인조가죽 제조방법은 상기 바인더에 배킹클로스를 접착하는 단계 다음으로 상기 스킨층, 바인더 및 배킹클로스를 건조시키는 건조단계를 더 포함한다. In addition, the artificial leather manufacturing method further includes a drying step of drying the skin layer, the binder and the backing cloth, followed by bonding the backing cloth to the binder.
또한, 상기 인조가죽 제조방법에 있어서, 상기 건조단계는 70도 ~ 90도에서 24시간 동안 진행된다.Further, in the artificial leather manufacturing method, the drying step is performed at 70 to 90 degrees for 24 hours.
또한, 상기 인조가죽 제조방법에 있어서, 상기 박리지를 제거하는 단계 다음으로 상기 미세엠보가 형성된 상기 스킨층에 코팅층을 형성하는 단계를 더 포함할 수 있다.Further, in the artificial leather manufacturing method, the step of removing the release paper may further include forming a coating layer on the skin layer on which the micro-emboss is formed.
또한, 상기 인조가죽 제조방법에 있어서, 상기 미세엠보 하나의 크기는 40~50㎛(마이크로미터)로 이루어지고, 상기 박리지의 일면에 코팅된다.In addition, in the artificial leather manufacturing method, the size of the fine emboss is 40 to 50 탆 (micrometer), and is coated on one side of the release paper.
본 발명의 일실시예에 따른 인조가죽은 복수개의 미세엠보가 형성된 엠보층와, 상기 엠포층이 일면에 코팅된 스킨층과, 상기 스킨층의 타면에 코팅된 바인더층과, 상기 바인더층이 접착된 배킹클로스층을 포함한다.The artificial leather according to an embodiment of the present invention includes an emboss layer having a plurality of micro embosses formed thereon, a skin layer coated on one side of the emulsion layer, a binder layer coated on the other side of the skin layer, And a backing cloth layer.
또한, 상기 인조가죽에 있어서 상기 미세엠보 하나의 크기는 40 ~ 50㎛로 이루어질 수 있다.In addition, in the artificial leather, the size of the fine emboss may be 40 to 50 탆.
또한, 상기 인조가죽에 있어서 상기 스킨층은 수성폴리우레탄 40 ~ 80%, 가교제 1~ 5%, 왁스 및 소광제 8 ~ 12%, 증점제 3~7% 및 습윤제 0.5 ~ 2%를 포함할 수 있다. Also, in the artificial leather, the skin layer may comprise 40 to 80% of an aqueous polyurethane, 1 to 5% of a crosslinking agent, 8 to 12% of a wax and a quenching agent, 3 to 7% of a thickener and 0.5 to 2% of a wetting agent .
또한, 상기 인조가죽에 있어서 상기 바인더는 수성폴리우레탄 40 ~ 85%, 가교제, 1 ~ 5%, 증점제 3 ~ 7%, 습윤제 0.5 ~ 2% 및 발포제 2 ~ 4%를 포함할 수 있다.Also, in the artificial leather, the binder may include 40 to 85% of an aqueous polyurethane, 1 to 5% of a crosslinking agent, 3 to 7% of a thickener, 0.5 to 2% of a wetting agent and 2 to 4% of a foaming agent.
기타 실시 예들의 구체적인 사항들은 상세한 설명 및 도면들에 포함되어 있다.The details of other embodiments are included in the detailed description and drawings.
본 발명에 의하면 폴리우레탄의 표면에 미세엠보를 전사시켜 기모와 같은 부드러운 촉감으로 스웨이드질감을 느낄 수 있을 뿐만 아니라, 대량생산이 가능하고, 견고함이 유지되어 차량용으로 구현가능한 인조가죽 및 그의 제조방법을 얻을 수 있다.Industrial Applicability According to the present invention, artificial leather that can be mass-produced and maintained in a solid state and can be implemented in a vehicle can be obtained by transferring fine embosses to the surface of polyurethane to feel a suede texture with a soft touch like brushed, Can be obtained.
본 발명의 기술적 사상의 실시예는, 구체적으로 언급되지 않은 다양한 효과를 제공할 수 있다는 것이 충분히 이해될 수 있을 것이다. It will be appreciated that embodiments of the technical idea of the present invention can provide various effects not specifically mentioned.
도 1은 본 발명의 일실시예에 따른 인조가죽 제조방법의 제조방법을 개략적으로 도시한 순서도이다.
도 2는 본 발명의 다른 실시예에 따른 인조가죽 제조방법의 제조방법을 개략적으로 도시한 순서도이다.
도 3은 본 발명의 일실시예에 따른 인조가죽의 개략적인 구성도이다.
도 4는 본 발명의 제1 실시예에 따른 인조가죽의 개략적인 표면 및 단면 SEM 사진이다.
도 5는 본 발명의 제2 실시예에 따른 인조가죽의 개략적인 표면 및 단면 SEM 사진이다.1 is a flowchart schematically showing a method of manufacturing a synthetic leather according to an embodiment of the present invention.
2 is a flowchart schematically showing a method of manufacturing a synthetic leather according to another embodiment of the present invention.
3 is a schematic structural view of artificial leather according to an embodiment of the present invention.
4 is a schematic top and cross-sectional SEM photograph of artificial leather according to a first embodiment of the present invention.
5 is a schematic top and cross-sectional SEM photograph of artificial leather according to a second embodiment of the present invention.
본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예를 참조하면 명확해질 것이다. 그러나 본 발명은 여기서 설명되는 실시예들에 한정되지 않고 다른 형태로 구체화될 수도 있다. 오히려, 여기서 소개되는 실시예들은 개시된 내용이 철저하고 완전해질 수 있도록 그리고 당업자에게 본 발명의 사상이 충분히 전달될 수 있도록 하기 위해 제공되는 것이다. BRIEF DESCRIPTION OF THE DRAWINGS The advantages and features of the present invention, and how to accomplish them, will become apparent by reference to the embodiments described in detail below with reference to the accompanying drawings. However, the present invention is not limited to the embodiments described herein but may be embodied in other forms. Rather, the embodiments disclosed herein are provided so that the disclosure can be thorough and complete, and will fully convey the scope of the invention to those skilled in the art.
본 출원에서 사용한 용어는 단지 특정한 실시예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 출원에서, "포함하다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.The terminology used in this application is used only to describe a specific embodiment and is not intended to limit the invention. The singular expressions include plural expressions unless the context clearly dictates otherwise. In this application, the terms "comprises", "having", and the like are used to specify that a feature, a number, a step, an operation, an element, a part or a combination thereof is described in the specification, But do not preclude the presence or addition of one or more other features, integers, steps, operations, components, parts, or combinations thereof.
다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미가 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥상 가지는 의미와 일치하는 의미가 있는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.Unless otherwise defined, all terms used herein, including technical or scientific terms, have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. Terms such as those defined in commonly used dictionaries are to be interpreted as having a meaning consistent with the meaning in the context of the relevant art and are to be construed as ideal or overly formal in meaning unless explicitly defined in the present application Do not.
이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 상세하게 설명한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.
도 1은 본 발명의 일실시예에 따른 인조가죽 제조방법을 개략적으로 도시한 순서도이다.1 is a flowchart schematically showing a method of manufacturing artificial leather according to an embodiment of the present invention.
도시한 바와 같이, 인조가죽 제조방법(S1000)은 미세엠보가 인쇄된 박리지에 스킨층 코팅단계(S1100)와, 바인더 코팅단계(S1200)와, 배킹클로스(Backing cloth) 접착단계(S1300)와, 박리지 제거단계(S1400)를 포함한다. As shown in the figure, the artificial leather manufacturing method (S1000) includes a skin layer coating step (S1100), a binder coating step (S1200), a backing cloth bonding step (S1300) Removal step (S1400).
보다 구체적으로, 미세엠보가 인쇄된 박리지에 스킨층 코팅단계 (S1100)는 복수개의 미세엠보가 인쇄된 박리지인 PET에 우레탄수지의 스킨층을 코팅하는 단계이다. More specifically, the skin layer coating step (S1100) on the release paper on which the fine embossing is printed is a step of coating a skin layer of urethane resin on PET, which is a peeling paper on which a plurality of fine embossments are printed.
또한, PET는 기존 종이 이형지에 비하여 미세엠보 뿐만 아니라 다양한 패턴의 엠보를 인쇄할 수 있다. 이에 따라 엠보 패턴의 다양성이 확보된다. In addition, PET can print embosses of various patterns as well as fine embossed paper compared to conventional paper release paper. Thus, diversity of the emboss pattern is ensured.
또한, 스킨층은 수성폴리우레탄(PUD: Polyurethane Dispersions) 40~80%, 가교제 1~ 5%, 왁스(Wax), 소광제 8 ~ 12%, 증점제 3~7%, 습윤제 0.5~ 2%를 포함하여 이루어질 수 있다. Also, the skin layer contains 40 to 80% of aqueous polyurethane (PUD), 1 to 5% of crosslinking agent, wax, 8 to 12% of quenching agent, 3 to 7% of thickener and 0.5 to 2% of wetting agent .
그리고 한 개 엠보의 크기는 40~50㎛(마이크로미터)로 이루어질 수 있다.And the size of one emboss may be 40 to 50 탆 (micrometer).
다음으로 바인더 코팅단계(S1200)는 상기 스킨층에 우레탄수지의 바인더층을 코팅하는 단계이다.Next, the binder coating step (S1200) is a step of coating the binder layer of the urethane resin on the skin layer.
또한, 바인더층은 수성폴리우레탄(PUD: Polyurethane Dispersions) 40~85%, 가교제 1~ 5%, 증점제 3~7%, 습윤제 0.5~ 2%, 발포제 2~ 4%를 포함할 수 있다. The binder layer may also include 40 to 85% of aqueous polyurethane (PUD), 1 to 5% of a crosslinking agent, 3 to 7% of a thickener, 0.5 to 2% of a wetting agent and 2 to 4% of a foaming agent.
다음으로 배킹클로스 접착단계(S1300)는 직물 또는 편물 타입의 배킹클로스에 바인더층을 접착시키는 단계이다.Next, the backing cloth adhesion step (S1300) is a step of bonding the binder layer to the backing cloth of the woven or knitted type.
다음으로, 박리지 제거단계(S1400)는 배킹클로스에 접착된 스킨층 및 바인더층으로부터 바리지인 PET를 분리하는 단계이다.Next, the release paper removing step (S1400) is a step of separating the PET, which is the barriers, from the skin layer and the binder layer bonded to the backing cloth.
상기한 바와 같이 이루어짐에 따라 본 발명의 일실시예에 따른 인조가죽 제조방법은 미세엠보의 코팅 및 전사를 통해 스웨이드 느낌을 얻을 수 있는 인조가죽 제조방법으로 구현될 수 있고, 대량생산이 가능할 뿐만 아니라 견고함이 유지되어 차량용 시트로 구현될 수 있다. As described above, the artificial leather manufacturing method according to an embodiment of the present invention can be realized as a method of manufacturing artificial leather capable of obtaining a suede feeling through coating and transferring of fine embossing, and mass production is possible The rigidity can be maintained and the vehicle seat can be realized.
도 2는 본 발명의 다른 실시예에 따른 인조가죽 제조방법의 제조방법을 개략적으로 도시한 순서도이다.2 is a flowchart schematically showing a method of manufacturing a synthetic leather according to another embodiment of the present invention.
도시한 바와 같이, 상기 인조가죽 제조방법은 도 1에 도시한 인조가죽 제조방법에 비하여 건조공정 및 상단코팅공정을 더 포함하여 이루어진다.As shown in the figure, the artificial leather manufacturing method further includes a drying step and an upper coating step in comparison with the artificial leather manufacturing method shown in FIG.
보다 구체적으로, 인조가죽 제조방법은 미세엠보가 인쇄된 박리지에 스킨층 코팅단계(S2100)와, 바인더 코팅단계(S2200)와, Backing cloth 접착단계(S2300), 건조단계(S2400), 박리지 제거단계(S2500) 및 상면 코팅단계(2600)를 포함한다.More specifically, the artificial leather manufacturing method includes a skin layer coating step (S2100), a binder coating step (S2200), a backing cloth adhesion step (S2300), a drying step (S2400), a peeling removal Step S2500 and an upper surface coating step 2600. [
그리고 복수개의 미세엠보가 인쇄된 박리지에 스킨층 코팅단계 (S2100)는 미세엠보가 인쇄된 PET에 우레탄수지의 스킨층을 코팅하는 단계이다. The skin layer coating step (S2100) on the release paper on which the plurality of fine embosses are printed is a step of coating the skin layer of the urethane resin on the PET on which the fine embossing is printed.
그리고 한 개 엠보의 크기는 40~50㎛로 이루어질 수 있다.And the size of one emboss may be 40 ~ 50 탆.
다음으로 바인더 코팅단계(S2200)는 상기 스킨층에 우레탄수지의 바인더층을 코팅하는 단계이다. 또한, 상기 바인더층은 발포제를 포함한다.Next, the binder coating step S2200 is a step of coating the binder layer of the urethane resin on the skin layer. Further, the binder layer includes a foaming agent.
다음으로 배킹클로스(Backing cloth)접착단계(S2300)는 직물 또는 편물 타입의 Backing cloth에 바인더층을 접착시키는 단계이다.Next, a backing cloth adhesion step (S2300) is a step of bonding a binder layer to a backing cloth of a woven or knitted type.
다음으로 건조단계(S2400)는 접착단계(S2300) 후에 상기 스킨층, 바이더 및 배킹클로스를 건조시키는 단계이고, 이를 통해 결합력을 보다 향상시킬 수 있다. Next, the drying step (S2400) is a step of drying the skin layer, the vender and the backing cloth after the adhesion step (S2300), and thereby the bonding force can be further improved.
그리고 건조단계(S2400)는 70도 ~ 90도에서 24시간 동안 건조시키는 방식으로 구현될 수 있다.And the drying step (S2400) may be carried out by drying for 24 hours at 70 to 90 degrees.
다음으로, 박리지 제거단계(S2500)는 배킹클로스에 접착된 스킨층 및 바인더 층으로부터 박리지인 PET를 분리하는 단계이다.Next, the release paper removing step (S2500) is a step of separating PET, which is a release paper, from the skin layer and the binder layer bonded to the backing cloth.
다음으로, 상면 코팅단계(2600)는 미세엠보가 형성된 스킨층에 코팅층을 형성하는 단계이다. 이에 따라 미세엠보는 보다 견고히 유지될 수 있다. Next, the top surface coating step 2600 is a step of forming a coating layer on the skin layer on which the fine emboss is formed. As a result, the fine emboss can be maintained more firmly.
도 3은 본 발명의 일실시예에 따른 인조가죽의 개략적인 구성도이다.3 is a schematic structural view of artificial leather according to an embodiment of the present invention.
도시한 바와 같이 상기 인조가죽(100)은 엠보층(110), 스킨층(120), 바인더층(130) 및 backing cloth층(140)를 포함한다.As shown, the
보다 구체적으로, 상기 인조가죽(100)은 배킹클로스(backing cloth)층(140)에 바인더층(130), 스킨층(120) 및 엠보층(110)이 순차적으로 적층된 구조로 이루어진다.More specifically, the
또한, 엠보층(110)은 미세엠보가 복수가 형성되어 있고, 미세엠보의 크기는 40~ 50㎛로 이루어질 수 있다. The
그리고 스킨층(120)은 수성우레탄수지로 이루어질 수 있다. 또한, 스킨층(120)은 수성폴리우레탄(PUD: Polyurethane Dispersions) 40~80%, 가교제1~ 5%, 왁스(Wax), 소광제 8 ~ 12%, 증점제 3~7%, 습윤제 0.5~ 2%를 포함하여 이루어질 수 있다.The
또한, 상기 스킨층(120)은 두 개의 층으로 이루어질 수 있다.In addition, the
또한, 바인더층(130)은 수성우레탄수지로 이루어질 수 있다. 또한, 바인더층(130)은 수성폴리우레탄(PUD: Polyurethane Dispersions) 40~85%, 가교제 1~ 5%, 증점제 3~7%, 습윤제 0.5~ 2%, 발포제 2~ 4%를 포함하여 이루어질 수 있다.Further, the
그리고 배킹클로스층(140)은 극세사 부직포에 폴리우레탄을 함침시키거나 직조하여 이루어질 수 있고, 직물 또는 편물로 이루어질 수 있다.The
도 4는 본 발명의 제1 실시예에 따른 인조가죽의 개략적인 표면 및 단면 SEM 사진이고, 도 5는 본 발명의 제2 실시예에 따른 인조가죽의 개략적인 표면 및 단면 SEM 사진이다.Fig. 4 is a schematic top and cross-sectional SEM image of a synthetic leather according to a first embodiment of the present invention, and Fig. 5 is a schematic surface and cross-sectional SEM photograph of artificial leather according to a second embodiment of the present invention.
보다 구체적으로, 도 4의 (a)는 제1 실시예에 따른 인조가죽의 개략적인 표면 SEM 사진이고, 도 4의 (b)는 제1 실시예에 따른 인조가죽의 개략적인 단면 SEM 사진이다. More specifically, Fig. 4 (a) is a schematic SEM photograph of a synthetic leather according to the first embodiment, and Fig. 4 (b) is a schematic cross-sectional SEM photograph of a synthetic leather according to the first embodiment.
또한, 도 5의 (a)은 제2 실시예에 따른 인조가죽의 개략적인 표면 SEM 사진이고, 도 5의 (b)은 제2 실시예에 따른 인조가죽의 개략적인 단면 SEM 사진이다.5A is a schematic SEM photograph of a synthetic leather according to a second embodiment, and FIG. 5B is a schematic cross-sectional SEM photograph of a synthetic leather according to the second embodiment.
도시한 바와 같이, 본 발명에 따른 인조가죽은 인쇄되는 미세패턴을 달리하여 원하는 스웨이드질감을 얻을 수 있다.As shown, the artificial leather according to the present invention can obtain a desired suede texture by varying the fine pattern to be printed.
이상, 첨부된 도면을 참조하여 본 발명의 바람직한 일 실시예를 설명하였지만, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 본 발명이 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 일 실시예는 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.While the present invention has been described in connection with what is presently considered to be practical exemplary embodiments, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, It will be understood that the invention may be practiced. It is therefore to be understood that one embodiment described above is illustrative in all aspects and not restrictive.
100: 상기 인조가죽
110: 엠보층
120: 스킨층
130: 바인더층
140: 배킹클로스층100: artificial leather 110: embossed layer
120: Skin layer 130: Binder layer
140: backing cloth layer
Claims (9)
상기 스킨층에 바인더를 코팅하는 단계;
상기 바인더에 배킹클로스(Backing cloth)를 접착하는 단계; 및
상기 박리지를 제거하는 단계를 포함하는
인조가죽 제조방법.
Coating a skin layer on a release paper on which a plurality of micro embosses are printed;
Coating a binder on the skin layer;
Bonding a backing cloth to the binder; And
And removing the release paper
Method for manufacturing artificial leather.
상기 바인더에 배킹클로스를 접착하는 단계 다음으로 상기 스킨층, 바인더 및 배킹클로스를 건조시키는 건조단계를 더 포함하는
인조가죽 제조방법.
The method according to claim 1,
Further comprising the step of bonding the backing cloth to the binder, followed by drying the skin layer, the binder and the backing cloth
Method for manufacturing artificial leather.
상기 건조단계는 70도 ~ 90도에서 24시간 동안 진행되는
인조가죽 제조방법.
3. The method of claim 2,
The drying step is carried out at 70 to 90 degrees for 24 hours
Method for manufacturing artificial leather.
상기 박리지를 제거하는 단계 다음으로 상기 미세엠보가 형성된 상기 스킨층에 코팅층을 형성하는 단계를 더 포함하는
인조가죽 제조방법.
The method according to claim 1,
Removing the release paper, and then forming a coating layer on the skin layer on which the micro emboss has been formed
Method for manufacturing artificial leather.
상기 미세엠보 하나의 크기는 40 ~ 50㎛(마이크로미터)로 이루어지고, 상기 박리지의 일면에 코팅된
인조가죽 제조방법.
The method according to claim 1,
The size of the fine emboss is 40 to 50 mu m (micrometer), and the one side of the release paper is coated with
Method for manufacturing artificial leather.
상기 엠포층이 일면에 코팅된 스킨층;
상기 스킨층의 타면에 코팅된 바인더층; 및
상기 바인더층이 접착된 배킹클로스층을 포함하는
인조가죽.
An emboss layer formed with a plurality of fine embosses;
A skin layer coated on one side of the whitening layer;
A binder layer coated on the other surface of the skin layer; And
And a backing cloth layer to which the binder layer is bonded
Leatherette.
상기 미세엠보 하나의 크기는 40 ~ 50㎛로 이루어진
인조가죽.
The method according to claim 6,
The size of the micro-embossment is 40 to 50 mu m
Leatherette.
상기 스킨층은
수성폴리우레탄 40 ~ 80%, 가교제 1 ~ 5%, 왁스 및 소광제 8 ~ 12%, 증점제 3 ~ 7% 및 습윤제 0.5~ 2%를 포함하는
인조가죽.
The method according to claim 6,
The skin layer
Containing 40 to 80% of an aqueous polyurethane, 1 to 5% of a crosslinking agent, 8 to 12% of a wax and a quencher, 3 to 7% of a thickener and 0.5 to 2% of a wetting agent
Leatherette.
상기 바인더는
수성폴리우레탄 40 ~ 85%, 가교제, 1 ~ 5%, 증점제 3 ~ 7%, 습윤제 0.5 ~ 2% 및 발포제 2~ 4%를 포함하는
인조가죽.
The method according to claim 6,
The binder
Wherein the composition comprises 40 to 85% of an aqueous polyurethane, 1 to 5% of a crosslinking agent, 3 to 7% of a thickener, 0.5 to 2% of a wetting agent and 2 to 4%
Leatherette.