KR20180088077A - A wrapping paper and its manufacturing method - Google Patents
A wrapping paper and its manufacturing method Download PDFInfo
- Publication number
- KR20180088077A KR20180088077A KR1020170012674A KR20170012674A KR20180088077A KR 20180088077 A KR20180088077 A KR 20180088077A KR 1020170012674 A KR1020170012674 A KR 1020170012674A KR 20170012674 A KR20170012674 A KR 20170012674A KR 20180088077 A KR20180088077 A KR 20180088077A
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- adhesive
- film
- paper
- laminated
- Prior art date
Abstract
Description
본 발명은 포장지에 관한 것으로, 더욱 상세하게는 씨앗, 과일, 화장품 용액, 마스크팩 등을 포장하기 위한 적층시트로 이루어진 포장지 및 이의 제조방법에 관한 것이다.More particularly, the present invention relates to a wrapper made of a laminated sheet for packaging a seed, a fruit, a cosmetic solution, a mask pack and the like, and a method for producing the wrapper.
일반적으로, 씨앗, 과일, 화장품 용액, 마스크팩 등을 포장하기 위해서 특성이 있는 몇 가지 포장 재료를 복합시켜 각 재료의 결점을 보완하고, 새로운 포장 성능을 가지는 재료로 만든 투명 플라스틱 필름의 일면에 알루미늄 박막을 포함하는 필름이 포장지로 널리 사용되고 있다.In general, it is common to combine several packaging materials with characteristics to package seeds, fruits, cosmetic solutions, mask packs, etc., to compensate for defects in each material, and to provide aluminum A film containing a thin film is widely used as a wrapping paper.
이러한 알루미늄 포장지는 포장지 내부 제품이 외부로 노출되지 않고 습기를 차단해 주며 금속 고유의 컬러와 질감을 나타내므로 고급스럽고 깔끔한 효과를 준다.This aluminum wrapper protects the inside of the wrapping paper from exposure to moisture and protects it from moisture, and it shows the unique color and texture of the metal, which gives a luxurious and refreshing effect.
그러나, 상기와 같은 포장지의 경우, 포장 후 포장지가 크랙이 발생될 수 있는 단점이 있다.However, in the case of the wrapping paper as described above, there is a drawback that cracks may occur in the wrapping paper after wrapping.
또한, 사용자가 가위와 같은 도구 사용 없이 손으로 직접 개봉하기 위해서 손이 미끄럽지 않도록 하기 위해서 손에 유분 또는 수분이 존재하지 않도록 해야 하며, 상당한 악력이 필요하다.In addition, in order to prevent the user from slipping the hand in order to open the hand by hand without using a tool such as scissors, oil or moisture should not be present in the hand, and a considerable grip is required.
상기와 같은 문제점을 보완하기 위한 종래의 기술을 살펴보면, 등록특허 제10-1496393호 "포장필름, 포장소재 및 이를 이용한 포장봉투"에서는, 나일론 이외의 저가의 외부 필름에 대해서도 향상된 유연성, 고탄성, 내충격성 및 진공형성을 보이는 포장소재 및 이를 이용한 포장봉투에 대해 개시하고 있다.In order to overcome the above-mentioned problems, according to the Korean Patent No. 10-1496393 entitled " Packaging film, packaging material and packaging bag using the same, " And a packaging bag using the packaging material.
그러나, 상기와 같은 포장봉투는 사용자가 손으로 직접 포장봉투를 개봉해야 할 경우, 손이 미끄럽지 않도록 손에 유분 또는 수분이 존재하지 않는 상태에서 개봉을 시행해야 하는 번거로움이 있었다.However, when the user needs to open the packaging bag manually by hand, there is a need to open the packaging bag in a state in which there is no oil or moisture in the hand so that the hand is not slippery.
상기와 같은 문제점을 보완하기 위한 또 다른 종래의 기술을 살펴보면, 등록특허 제10-1680871호 "종이질감을 갖는 방수성 적층시트"에서는, 종이질감을 갖는 종이질감층을 구비하여 종이질감층을 시각과 촉각으로 확인할 수 있도록 구비된 적층시트에 대해 개시하고 있다.According to another conventional technique for solving the above-mentioned problems, Japanese Patent Application No. 10-1680871 entitled " Waterproof laminated sheet having paper texture " has a paper texture layer having paper texture, Discloses a laminated sheet provided so as to be confirmed by a tactile sense.
상기와 같은 적층시트를 이용할 경우, 차광층으로 알루미늄을 사용함으로써 포장 후 포장지의 크랙이 발생되어 가스배리어성이 떨어지는 문제점이 있었다.When such a laminated sheet is used, the use of aluminum as the light-shielding layer causes a crack in the wrapping paper after packaging, resulting in poor gas barrier properties.
상기와 같은 문제점을 해결하기 위한 본 발명의 목적은, 합성수지 필름 사이에 종이류와 알루미늄을 적층시킨 포장지를 제공함으로써, 사용자에게 종이질감을 제공하고, 유분 또는 수분을 함유한 손으로 개봉이 용이하고, 내용물의 차광 및 산화방지가 용이한 적층시트로 이루어진 포장지 및 이의 제조방법을 제공하는데 있다.It is an object of the present invention to solve the above problems and to provide a wrapping paper in which paper and aluminum are laminated between synthetic resin films to provide a paper texture to a user and easy to open with hand containing oil or moisture, A package sheet made of a laminated sheet whose contents are easily shielded from light and oxidation, and a method for producing the same.
상기와 같은 문제점을 해결하기 위한 본 발명의 다른 목적은, 색상 및 외관이 미려한 효과가 구비될 수 있고, 포장 후에도 가스배리어성을 유지할 수 있는 적층시트로 이루어진 포장지 및 이의 제조방법을 제공하는데 있다.Another object of the present invention is to provide a packaging sheet made of a laminated sheet which can be provided with an effect of being beautiful in color and appearance and can maintain gas barrier properties even after packaging, and a method for manufacturing the same.
상기와 같은 문제점을 해결하기 위한 본 발명의 또 다른 목적은, AL, AL-합지필름, 착색안료를 포함하는 EVOH필름 또는 실리카필름 등이 구비됨으로써 재활용이 가능한 친환경 소재로 구비된 적층시트로 이루어진 포장지 및 이의 제조방법을 제공하는데 있다.It is another object of the present invention to solve the above-mentioned problems, and it is an object of the present invention to provide a packaging sheet made of a laminated sheet comprising an AL, an AL-laminated film, an EVOH film containing a coloring pigment, And a method for producing the same.
상기와 같은 문제점을 해결하기 위한 본 발명의 또 다른 목적은, 상기 적층시트로 이루어진 포장지의 각 층을 적층시키기 위해 라미네이션 공법을 이용함으로써, 다종류 필름 점착이 가능하고, 고기능성 복합필름의 제조가 가능해질 수 있는 적층시트로 이루어진 포장지 및 이의 제조방법을 제공하는데 있다.Another object of the present invention to solve the above problems is to provide a multilayer film which is capable of adhering various kinds of films by using a lamination method for laminating layers of the wrapping paper made of the laminated sheet, And a method for manufacturing the same.
씨앗, 과일, 화장품 용액, 마스크팩을 포장하기 위한 적층시트로 이루어진 포장지에 있어서, PET(Polyethylene phthalate)를 포함하는 제1층(100), PE(Polyethylene)를 포함하는 제2층(200), 노루지, 한지, 크라프트지, 백판지 또는 박엽지 중 선택되는 적어도 한가지를 포함하는 제3층(300), PE(Polyethylene)를 포함하는 제4층(400), AL(Aluminium), AL(Aluminium)-합지필름, 착색안료를 포함하는 EVOH필름 또는 실리카필름 중 선택되는 적어도 한가지를 포함하는 제5층(500) 및 LLDPE, LDPE, PP, HDPE 또는 CPP 중 선택되는 적어도 한가지를 포함하는 제6층(600)이 순차적으로 적층되어 이루어지고, 상기 제1층(100) 내지 제6층(600)을 적층시키기 위해 라미네이션 공법 중 선택되는 적어도 한가지에 의해 접착되는 것을 특징으로 한다.A wrapping paper comprising a laminated sheet for packaging a seed, a fruit, a cosmetic solution and a mask pack, comprising: a first layer (100) comprising PET (polyethylene phthalate); a second layer (200) A
또한, 상기 AL-합지필름은 AL 필름의 일면에 EVOH필름, 실리카필름, 유기물증착필름 또는 무기물증착필름을 합지시킨 것이고, 상기 Al-합지필름에 사용되는 합지필름의 두께는, 전체층의 합에 대하여, 1:0.01~0.04의 비율로 구비되며, 상기 접착제는, 폴리우레탄계 접착제, 2액형 폴리우레탄계 접착제, 무용제형폴리우레탄계 접착제, 호모 폴리머, 폴리아크릴산에스테르계 접착제, 시아토아크릴레이트계 접착제, 에틸렌 공중합체계 접착제, 셀루로오스계 접착제, 폴리에스테르계 접착제, 폴리아미드계 접착제, 아미노 수지계 접착제, 페놀 수지계 접착제, 에폭시계 접착제, 반응형아크릴계 접착제, 반응형 메타 아크릴계 접착제, 고무계 접착제, 실리콘계 접착제, 무기계 접착제로 이루어진 군 중에서 선택되는 적어도 한가지의 접착제를 이용하고, 상기 라미네이션 공법은 드라이 라미네이션, 웨트(Wet) 라미네이션, 압출 라미네이션 또는 핫멜트라미네이션 공법에 의해 접착되는 것을 특징으로 한다.The AL-laminated film is obtained by laminating an EVOH film, a silica film, an organic substance-deposited film or an inorganic substance-deposited film on one side of an AL film, and the thickness of the laminated film used for the Al- 0.01 to 0.04, and the adhesive may be at least one selected from the group consisting of a polyurethane-based adhesive, a two-component polyurethane-based adhesive, a solventless polyurethane-based adhesive, a homopolymer, a polyacrylate ester-based adhesive, a cyanoacrylate- Epoxy adhesive, reactive acrylic adhesive, reactive methacrylic adhesive, rubber adhesive, silicone adhesive, inorganic adhesive, epoxy adhesive, epoxy resin adhesive, epoxy adhesive, And at least one adhesive selected from the group consisting of adhesives, The seam method is characterized in that it is adhered by dry lamination, wet lamination, extrusion lamination or hot melt lamination.
상기 적층시트로 이루어진 포장지의 제조방법은, 씨앗, 과일, 화장품 용액, 마스크팩을 포장하기 위한 포장용 적층시트에 있어서, 그라비아인쇄용 잉크, 제1층(100)에 사용될 PET, 제2층(200)에 사용될 PE, 제3층(300)에 사용될 노루지, 한지, 크라프트지, 백판지 또는 박엽지 중 선택되는 적어도 한가지, 제4층(400)에 사용될 PE, 제5층(500)에 사용될 AL, AL-합지필름, 착색안료를 포함하는 EVOH필름 또는 실리카필름 중 선택되는 적어도 한가지, 제6층(600)에 사용될 LLDPE, LDPE, PP, HDPE 또는 CPP 중 선택되는 적어도 한가지 및 접착제를 준비하는 재료준비단계(S100), 상기 제1층(100)의 타측면에 그라비아 인쇄를 실행하는 인쇄단계(S200), 상기 인쇄단계(S200)를 거친 상기 제1층(200)과 상기 제2층(200) 내지 제6층(600)을 라미네이션 공법으로 접착시키는 접합공정 단계(S300), 상기 접합공정 단계(S300)를 거친 필름을 후공정 작업에 적합하도록 규격별 또는 형태별로 절단하는 제단공정단계(S400) 및 상기 제단공정단계(S400)를 거친 필름을 용도에 맞도록 절단 또는 가공하는 포장지 제작 단계(S500)를 포함하는 것을 특징으로 한다.The method for producing a wrapping paper comprising the laminated sheet is a laminated sheet for packaging a seed, a fruit, a cosmetic solution, and a mask pack. The laminated sheet for packaging includes a gravure printing ink, PET to be used for the
더욱이, 상기 AL-합지필름은 AL의 일면에 EVOH필름, 실리카필름, 유기물증착 필름 또는 무기물증착 필름 중 선택되는 적어도 한가지를 합지시킨 것이고, 상기 Al-합지필름에 사용되는 합지필름의 두께는, 전체층의 합에 대하여, 1:0.01~0.04의 비율로 구비되며, 상기 접착제는, 폴리우레탄계 접착제, 2액형 폴리우레탄계 접착제, 무용제형 폴리우레탄계 접착제, 호모 폴리머, 폴리아크릴산에스테르계 접착제, 시아토아크릴레이트계 접착제, 에틸렌 공중합체계 접착제, 셀루로오스계 접착제, 폴리에스테르계 접착제, 폴리아미드계 접착제, 아미노수지계 접착제, 페놀 수지계 접착제, 에폭시계 접착제, 반응형아크릴계 접착제, 반응형 메타 아크릴계 접착제, 고무계 접착제, 실리콘계 접착제 및 무기계 접착제로 이루어진 군 중에서 선택되는 적어도 한가지의 접착제를 이용하고, 상기 라미네이션 공법은 드라이 라미네이션, 웨트(Wet) 라미네이션, 압출 라미네이션 또는 핫멜트라미네이션 공법 중 선택되는 적어도 한가지에 의해 접착되는 것을 특징으로 한다.Further, the AL-laminated film is obtained by laminating at least one selected from the group consisting of an EVOH film, a silica film, an organic substance deposited film and an inorganic substance deposited film on one side of the AL, and the thickness of the laminated film used for the Al- Layer adhesive, a two-component polyurethane adhesive, a solvent-free polyurethane adhesive, a homopolymer, a polyacrylate ester adhesive, a cyanoacrylate-based adhesive, Based adhesives, epoxy-based adhesives, reactive-type acrylic adhesives, reactive-type methacrylic adhesives, rubber-based adhesives, epoxy adhesives, ethylene-based adhesives, ethylene-based adhesive adhesives, cellulosic adhesives, At least one adhesive selected from the group consisting of silicone adhesives and inorganic adhesives The use, and the lamination process is a dry lamination, wet (Wet) lamination, characterized in that the adhesion by the at least one selected from extrusion lamination or hot melt lamination method.
상기와 같은 본 발명에 따른 적층시트로 이루어진 포장지를 이용할 경우에는 사용자에게 종이질감을 제공함으로써 유분 또는 수분을 함유한 손으로 쉽게 개봉할 수 있고, 외관이 미려하여 심미감이 향상되는 효과가 있다.In the case of using the wrapping paper made of the laminated sheet according to the present invention as described above, the paper can be easily opened with hands containing oil or moisture by providing the paper texture to the user, and the appearance is good and the aesthetic feeling is improved.
또한, AL-합지필름, 착색안료를 포함하는 EVOH필름, 실리카필름, 유기물증착필름 또는 무기물증착필름 등이 구비됨으로써 재활용이 가능한 친환경 소재로 구비되어 재활용이 용이하며, 포장지의 유통과정 또는 외부충격으로 인해 Al의 깨짐현상으로 기인하는 누액발생률이 저하되는 장점이 있다.Further, since the EVOH film, the silica film, the organic vapor deposition film, or the inorganic vapor deposition film including the AL-shrink film, the color pigment, and the like are provided, it is provided as an environmentally friendly material that can be recycled, and is easily recycled. There is an advantage that the leakage rate caused by the cracking phenomenon of Al is lowered.
도 1은 본 발명에 따른 적층시트로 이루어진 포장지의 단면도이다.
도 2는 본 발명에 따른 적층시트로 이루어진 포장지 및 이의 제조방법의 공정도이다. 1 is a sectional view of a wrapping paper made of a laminated sheet according to the present invention.
2 is a process diagram of a wrapper made of a laminated sheet according to the present invention and a method of manufacturing the same.
이하, 본 발명에 따른 바람직한 실시예를 첨부된 도면을 참조하여 상세하게 설명한다.Hereinafter, preferred embodiments according to the present invention will be described in detail with reference to the accompanying drawings.
도 1은 본 발명에 따른 적층시트로 이루어진 포장지의 단면도이다.1 is a sectional view of a wrapping paper made of a laminated sheet according to the present invention.
본 발명은 씨앗, 과일, 화장품 용액, 마스크팩을 포장하기 위한 적층시트로 이루어진 포장지에 있어서, PET(Polyethylene phthalate)를 포함하는 제1층(100), PE(Polyethylene)를 포함하는 제2층(200), 노루지, 한지, 크라프트지, 백판지 또는 박엽지를 포함하는 제3층(300), PE(Polyethylene)를 포함하는 제4층(400), AL(Aluminium), AL(Aluminium)-합지필름, 착색안료를 포함하는 EVOH필름 또는 실리카필름을 포함하는 제5층(500) 및 LLDPE, LDPE, PP, HDPE 또는 CPP를 포함하는 제6층(600)이 순차적으로 적층되어 이루어지고, 상기 제1층(100) 내지 제6층(600)을 적층시키기 위해 라미네이션 공법에 의해 접착되는 것을 특징으로 한다.The present invention relates to a packaging sheet made of a laminated sheet for packaging a seed, a fruit, a cosmetic solution and a mask pack, comprising a
더욱 상세하게 설명하면, 씨앗, 과일, 화장품 용액, 마스크팩 등을 포장하기 위한 포장용 적층시트에 있어서, 베이스가 되는 제1층(100)에는 PET(Polyethylene phthalate), OPP(Oriented polypropylene), ONY(Oriented nylon), NY(Nylon) 중 적어도 한가지로 이루어 질 수 있다.More specifically, in a laminated sheet for packaging a seed, a fruit, a cosmetic solution, a mask pack and the like, a PET (polyethylene phthalate), an OPP (Oriented Polypropylene), an ONY Oriented nylon, and NY (Nylon).
그러나 바람직하게는, PET필름을 이용하는 것이 바람직하다.However, it is preferable to use a PET film.
상기 PET필름은 얇은 두께에서도 높은 인장강도를 유지하고, 열 안정성과 치수 안정성이 우수하며, 다양한 온도 범위에 걸친 우수한 약품 저항성이 우수하고, 플라스틱 중에서도 가장 높은 인장강도를 보이며, 강성도 높아야 하고, 내열성, 융점 및 연화점 모두 플라스틱 필름에서 가장 좋은 부류에 속해 있으며, 60~150℃의 넓은 사용가능 온도 범위를 갖고 있고, 가열에 의해 연화와 수축을 일으키는 조건에서도 외관상의 변화가 없기에 인쇄시 수축율이 적은 장점이 있다.The PET film maintains high tensile strength even at a thin thickness, has excellent thermal stability and dimensional stability, has excellent resistance to chemicals over various temperature ranges, exhibits the highest tensile strength among plastics, has high rigidity, Both melting point and softening point belong to the best class of plastic film. It has a wide usable temperature range of 60 ~ 150 ℃ and it does not change appearance even under the conditions of softening and shrinking by heating. have.
또한, 종이 또는 AL 등과 같은 포장 재료와 함께 라미네이션 공법을 이용하여 본 발명인 적층시트로 이루어진 포장지(이하, 포장지라 한다.)를 구성하는데 용이한 장점이 있다.In addition, there is an advantage that it is easy to construct a wrapping paper (hereinafter referred to as wrapping paper) made of a laminated sheet of the present invention by using a lamination method together with a packaging material such as paper or AL.
특히, 상기 PET는 상기 포장지의 최외층에 구비되어 상기 제1층(100)에 인쇄작업이 수행될 수 있다.In particular, the PET is provided on the outermost layer of the wrapping paper so that the printing operation can be performed on the
상기 인쇄작업은 그라비아인쇄, 오프셋인쇄 등이 수행될 수 있는데, 바람직하게는 미리 고르게 정량된 균일한 두께의 잉크를 패턴 상에 그대로 부착시키므로 복잡한 형상이라도 잉크를 균일하게 충전시키기가 쉬워 균일한 인쇄두께를 얻을 수 있는 인쇄방법으로써, 판이나 롤러에 요(凹)형의 화선부를 형성하여 화선부에 잉크를 채우고, 그 외주면의 튀어나온 부분에 묻은 불필요한 잉크를 긁개라고 하는 금속제 기구로 긁어내고, 음푹 들어간 부분의 잉크에 압력을 가하여 피인쇄물에 전이시키는 방식인 그라비아 인쇄가 수행될 수 있다.The printing operation may be carried out by gravure printing, offset printing, or the like. Preferably, uniformly pre-determined ink of a uniform thickness is adhered to the pattern as it is, so that it is easy to uniformly fill the ink even in a complicated shape. A method of forming a concave-shaped line portion on a plate or a roller to fill in the ink on the line portion, and unnecessary ink adhering to the protruding portion of the outer circumferential surface is scratched with a metal tool called a scratching, Gravure printing can be performed in such a manner that pressure is applied to the ink of the portion and transferred to the object.
상기 제1층(100)의 경우, 상기 포장지의 전체 층의 합에 대하여, 1:0.05~0.12의 두께비를 갖는 것이 바람직하다.In the case of the
만약, 상기 제1층의 두께가 상기 포장지의 전체 층의 합에 대하여, 두께비가 1:0.05 미만으로 구비되면, 상기 포장지의 지지체로써 너무 얇게 구비되어 인쇄시 문제가 생기거나 내열성이 떨어지는 단점이 있다. If the thickness of the first layer is less than 1: 0.05 with respect to the sum of all the layers of the wrapping paper, it is too thin as a support of the wrapping paper, causing problems in printing or deteriorating heat resistance .
또한, 두께비가 1:0.12 이상으로 구비되면, 상기 제1층(100)이 너무 두껍게 구비되어 건조하는데 시간이 오래 걸릴 수 있는 단점이 있다.In addition, if the thickness ratio is 1: 0.12 or more, the
다음으로는, 상기 제1층(100)의 일면에 구비되고, PE(Polyethylene), PP(Polypropylene) 중 적어도 한가지를 포함하는 제2층(200)이 구비될 수 있다.Next, the
그러나, 바람직하게는 -20℃까지 견딜 수 있는 내한성이 있으며, 흡수성이 거의 없기 때문에 방수가 높고, 전기 절연성이 높으며, 내약품성, 내유성 등이 우수한 소재인 PE가 구비될 수 있다.However, it can be provided with PE, which is a material excellent in water resistance, high electrical insulation, excellent chemical resistance, oil resistance and the like because it has cold resistance which can endure to -20 deg.
상기 제2층(200)의 경우, 상기 포장지의 전체 층 합에 대하여, 1:0.10~0.18의 두께비를 갖는 것이 바람직하다.In the case of the
만약, 상기 PE의 두께비가 전체 층의 합에 대하여, 1:0.10미만으로 구비될 경우, 최종적으로 만들어지는 포장지의 방수가 용이하게 이루어지지 않아, 포장지로써 가치가 떨어질 수 있는 단점이 있다.If the thickness ratio of the PE is less than 1: 0.10 with respect to the sum of all layers, waterproofing of the finally produced packaging paper is not easily performed, and the value of the packaging paper may deteriorate.
만약 두께비가 1:0.18이상으로 구비될 경우, 접착성이 낮아 접착이 용이하게 이루어지지 않는 단점이 있다.If the thickness ratio is 1: 0.18 or more, there is a disadvantage that adhesion is low and adhesion is not easy.
다음으로는, 상기 제2층(200)의 일면에 구비되고, 상기 포장지의 외측에 종이질감과 결을 부여하여, 외력의 영향에 의해 상기 포장지가 쉽게 파손되거나 찢기지 않고, 결방향으로 절단을 수행할 경우, 절단성이 우수하여 유분 또는 수분을 함유한 손으로 쉽게 개봉할 수 있도록 종이류를 포함하는 제3층(300)이 구비될 수 있다.Next, the paper is provided on one side of the
더욱 자세하게는, 상기 제3층(300)은 노루지, 한지, 크라프트지, 백판지, 박엽지 등과 같은 종이류로 구비될 수 있는데, 이에 한정되지 않음은 물론이다.More specifically, the
그러나, 바람직하게는 상기 노루지 또는 크라프트지가 선택적으로 구비될 수 있다.However, it is preferable that the herringbone or the kraft paper is optionally provided.
상기 노루지는 롤지의 일본어 표기를 한글화 한 것으로써, 한쪽 면에 광택을 주어 초지한 비교적 얇은 포장지의 일종이다. 원료로는 화학펄프와 크라프트펄프를 사용한다. 표백 크라프트를 주원료로 한 순백롤, 미표백 또는 반표백 화학펄프를 주원료로 하는 S롤, 화학펄프 30%이상에 나머지는 쇄목펄프를 주원료로 하는 G롤과, 줄 든 크라프트, 편명광 크라프트 등의 종류가 있는데, 이에 한정되지 않고 사용될 수 있음은 물론이다. The porridge is a type of relatively thin wrapping paper which is made by translating the Japanese notation of the roll paper into Korean and giving a gloss to one side. Chemical pulp and kraft pulp are used as raw materials. White roll with bleaching kraft as main raw material, S roll with main bleached or semi-bleached chemical pulp as main raw material, G roll with main pulp more than 30% as chemical pulp, shredded kraft, But the present invention is not limited thereto.
상기 노루지는 소형의 지대와 봉투, 간단한 포장지로 애용되며, 하급전단 광고에도 쓰인다.The rouge is favored as a small zone, envelope, simple wrapping paper, and also used for low-grade flyer advertising.
더욱이, 상기 크라프트지는 화학펄프의 일종인 미표백 크라프트를 주원료로 하는 포장용지로서, 대부분 지대로 가공하여 밀가루, 설탕, 비료, 사료, 곡물 등의 포장에 사용된다.Furthermore, the kraft paper is a wrapping paper made mainly of unbleached kraft, which is a type of chemical pulp, and is mainly used for packaging of flour, sugar, fertilizer, feed, grain and the like.
또한, 선택적으로, 상기 제3층(300)의 타측면 즉, 상기 제2층(200)과 닿는 면에 인쇄작업이 수행될 수 있다. 상기 3층(300)의 인쇄작업은 그라비아 인쇄, 오프셋인쇄 등이 수행될 수 있는데, 바람직하게는 그라비아 인쇄가 수행될 수 있다.Alternatively, a printing operation may be performed on the other side of the
더욱이, 상기 제3층(300)은 상기 포장지의 전체 층의 합에 대하여, 1:0.24~0.32의 두께비를 갖는 것이 바람직하다.Furthermore, it is preferable that the
만약 두께비가 1:0.24미만이면, 최종적으로 제조되는 포장지의 종이질감을 충분히 낼 수 없고, 유분 또는 물기가 있는 손으로 용이하게 개봉하기 어려운 단점이 있고, 1:0.32이상이면, 최종적으로 제조되는 포장지의 두께가 두꺼워지고, 제조단가가 높아지는 단점이 있다.If the thickness ratio is less than 1: 0.24, the paper texture of the finally produced wrapping paper can not be sufficiently obtained and it is difficult to open easily with a hand with oil or water. If the ratio is 1: 0.32 or more, And the manufacturing cost is increased.
상기 종이류를 사용할 경우, 상기 포장지의 종이질감을 충분히 내고, 균일한 두께의 상기 제3층(300)을 적층하기 위해 선택적으로, 압연기로 펴는 공정이 수행될 수 있다.When the paper sheet is used, a process of rolling the paper sheet into a rolling mill may be performed to selectively stack the
다음으로는, 상기 제3층(300)의 일면에 구비되고, PE(Polyethylene), PP(Polypropylene) 중 적어도 한가지를 포함하는 제4층(400)이 구비될 수 있다.Next, a
그러나, 바람직하게는 -20℃까지 견딜 수 있는 내한성이 있으며, 흡수성이 거의 없기 때문에 방수가 높고, 전기 절연성이 높으며, 내약품성, 내유성 등이 우수한 소재인 PE가 구비될 수 있다. However, it can be provided with PE, which is a material excellent in water resistance, high electrical insulation, excellent chemical resistance, oil resistance and the like because it has cold resistance which can endure to -20 deg .
상기 제4층(400)의 경우, 상기 포장지의 전체 층 합에 대하여, 1:0.10~0.18의 두께비를 갖는 것이 바람직하다.In the case of the
만약, 상기 PE의 두께비가 전체 층의 합에 대하여, 1:0.10미만으로 구비될 경우, 최종적으로 만들어지는 포장지의 방수가 용이하게 이루어지지 않아, 포장지로써 가치가 떨어질 수 있는 단점이 있다.If the thickness ratio of the PE is less than 1: 0.10 with respect to the sum of all layers, waterproofing of the finally produced packaging paper is not easily performed, and the value of the packaging paper may deteriorate.
만약 두께비가 1:0.18이상으로 구비될 경우, 접착성이 낮아 접착이 용이하게 이루어지지 않는 단점이 있다.If the thickness ratio is 1: 0.18 or more, there is a disadvantage that adhesion is low and adhesion is not easy.
다음으로는, 상기 제4층(400)의 일면에 구비되고, AL(Aluminium), AL(Aluminium)-합지필름, 착색안료를 포함하는 EVOH((Ethylene Vinyl Alcohol)필름 및 실리카필름 중 적어도 한가지를 포함하는 제5층(500)이 구비될 수 있다.Next, at least one of an EVOH ((Ethylene Vinyl Alcohol) film and a silica film, which is provided on one surface of the
일반적으로 우수한 가스차단성, 차광성과 광택에 따른 장식성이 뛰어난 상기 AL이 사용될 수 있다.In general, the above-mentioned AL having excellent gas-shielding property, light-shielding property and decorative property due to gloss can be used.
또한, 선택적으로 높은 가스차단성을 가진 열가소성 결정성 수지로, 에틸렌-비닐 공중합체로서 폴리에틸렌보다 약 100,000배정도 산소 차단성과 가스베리어성이 높은 EVOH필름이 사용될 수 있다. 상기 착색안료는 실리카 필름에도 적용될 수 있다.Further, an EVOH film having oxygen barrier property and gas barrier property of about 100,000 times that of polyethylene as the ethylene-vinyl copolymer can be used as the thermoplastic crystalline resin having high gas-barrier property selectively. The colored pigment can also be applied to a silica film.
상기 EVOH필름을 포함함으로써, 외부충격에 의해 Al이 깨지는 현상을 방지할 수 있고, 더욱 유연해지는 장점이 있다. By including the EVOH film, it is possible to prevent the Al from being broken due to an external impact, which is advantageous in that it is more flexible.
상기 EVOH필름을 사용할 경우, 상기 EVOH의 접착력을 위하여 폴리프로필렌을 접착제 수지에 끼워 적층하여 제조한다.When the EVOH film is used, polypropylene is laminated on the adhesive resin for the adhesive strength of the EVOH.
상기 EVOH필름은 에틸렌의 함량에 따라 가스베리어성이 달라질 수 있는 장점이 있다. 일반적으로 상기 EVOH 100중량부에 대하여, 에틸렌의 함량이 5~95 중량부 범위에서 선택하여 사용되지만, 바람직하게는 25~64 중량부가 사용될 수 있다. The EVOH film has an advantage that the gas barrier property can be changed according to the content of ethylene. Generally, ethylene is used in an amount of 5 to 95 parts by weight, preferably 25 to 64 parts by weight, based on 100 parts by weight of the EVOH.
만약, 상기 EVOH 필름의 에틸렌의 함량이 25중량부미만일 경우, 에틸렌의 함량이 너무 낮아 가스가 용이하게 차단되지 않는 단점이 발생할 수 있고, 64중량부 이상일경우, 상기 포장지의 제조단가가 높아지는 단점이 있을 수 있다.If the ethylene content of the EVOH film is less than 25 parts by weight, the ethylene content may be too low to prevent the gas from being easily blocked. On the other hand, when the content of ethylene is more than 64 parts by weight, Can be.
더욱 바람직하게는 에틸렌 함량이 40~65중량부인 것이 구비될 수 있다.More preferably, the ethylene content is 40 to 65 parts by weight.
이 때, 선택적으로 상기 포장지의 심미감과 차광성을 상승시킬 수 있는 착색안료가 포함된 EVOH필름이 사용될 수 있다.At this time, an EVOH film containing a coloring pigment capable of selectively increasing the aesthetics and light shielding properties of the wrapping paper can be used.
상기 착색안료는 백색, 적색, 흑색 등 상기 포장지의 용도와 사용목적에 맞게 구비될 수 있다.The colored pigment may be provided in accordance with the purpose of use of the wrapping paper such as white, red, black, and the like.
바람직하게는, 상기 Al의 차광성을 유지하기 위해 적색 또는 흑색을 바탕으로 한 착색안료가 구비될 수 있다.Preferably, a coloring pigment based on red or black may be provided to maintain the light shielding property of Al.
더욱이, Al필름을 실리카필름으로 대체할 경우, Al필름을 사용할 경우와 대비하였을 때, 포장의 기능 및 형태 등의 외형적 차이가 없는 장점이 있다.Furthermore, when the Al film is replaced with a silica film, there is no difference in appearance and function between the Al film and the case where the Al film is used.
또한, 상기 EVOH 필름 또는 실리카필름을 사용할 경우, Al필름을 포함하는 포장지의 재활용공정에서 Al이 완전 분리되지 않아 재활용된 펄프를 이용한 재생제품에 검은색 또는 회색 점의 형태로 구비되는 문제를 보완할 수 있고, 더욱 유연한 포장지를 제조할 수 있는 장점이 있다.In addition, when the EVOH film or the silica film is used, since the Al is not completely separated in the recycling process of the wrapping paper including the Al film, the problem of being provided in the form of black or gray dots in the recycled product using the recycled pulp is compensated There is an advantage that a more flexible wrapping paper can be manufactured.
더욱이, Al을 사용함으로써 종이와 Al막의 분리공정이 더 필요하게 되므로 재활용률이 30%이하인 단점이 있는데, Al대신 합성수지를 구비함으로써 경제적으로 효과적일 수 있는 장점이 있다.In addition, since the use of Al requires a separate process of separating the paper and the Al film, there is a disadvantage that the recycling rate is 30% or less. In addition, there is an advantage that it is economically effective to provide synthetic resin instead of Al.
또한, 상기 Al에 의해 크랙이 발생되고, 상기 포장지의 유통과정 또는 외부충격으로 인해 알루미늄의 깨짐현상으로 기인하는 누액발생률이 저하되는 장점이 있다.Also, there is an advantage that a crack is generated by the Al, and the leakage rate caused by cracking of the aluminum due to the circulation process or external impact of the wrapping paper is lowered.
상기 제5층(500)의 경우, 상기 포장지의 전체 층 합에 대하여, 1:0.01~0.08의 두께비를 갖는 것이 바람직하다.In the case of the
만약, 두께비가 전체 층의 합에 대하여, 1:0.01미만으로 구비될 경우, 최종적으로 만들어지는 포장지의 산소차단 및 차광이 용이하게 이루어지지 않아 포장된 물품의 보존기간이 짧아질 수 있는 문제점이 발생될 수 있고, 만약 두께비가 1:0.08 이상으로 구비될 경우, 외부 충격에 의해 쉽게 깨지는 현상이 발성되고, 제조단가가 높아지는 문제점이 발생될 수 있다.If the thickness ratio is less than 1: 0.01 with respect to the sum of all the layers, oxygen shielding and shielding of the final packaging paper can be easily performed The storage period of the packaged product may be shortened. If the thickness ratio is 1: 0.08 or more, a phenomenon that is easily broken by the external impact is generated and the manufacturing cost is increased Lt; / RTI >
또한, 선택적으로 AL-합지필름이 이용될 수 있는데, 상기 AL-합지필름은 AL의 일면에 EVOH필름, 실리카필름, 유기물증착필름 및 무기물증착필름 중 적어도 하나의 필름을 합지시킨 것을 포함할 수 있다.Alternatively, an AL-laminated film may be used, which may comprise one or more films of an EVOH film, a silica film, an organic vapor deposited film and an inorganic vapor deposited film laminated on one side of the AL .
이 때, 상기 AL-합지필름에 사용되는 합지필름의 두께는, 전체층의 합에 대하여, 1:0.01~0.04로 구비될 수 있다.In this case, the thickness of the laminated film used in the AL-laminated film may be 1: 0.01 to 0.04 with respect to the sum of the total layers.
만약, 두께비가 전체층의 합에 대하여, 1:0.01미만으로 구비될 경우, 가스배리어성이 낮아지는 단점이 있고, 1:0.04이상으로 구비될 경우, 제조단가가 높아지는 단점이 있다.If the thickness ratio is less than 1: 0.01 with respect to the total sum of all layers, the gas barrier property is lowered. If the thickness ratio is 1: 0.04 or more, the manufacturing cost is increased.
다음으로는, 상기 제5층(500)의 일면에 구비되고, LLDPE(Linear low density polyethylene), LDPE(Low density polyethylene), PP(Polypropylene), HDPE(High density polyethylene), CPP(casting polypropylene) 중 적어도 한가지를 포함하는 제6층(600)이 구비될 수 있다.Next, the
바람직하게는 제3의 폴리에틸렌으로 불리며 포장재료나 공업용, 농업용 필름에 적합하도록 개발된 합성수지인 LLDPE가 구비될 수 있다.Preferably LLDPE, which is a synthetic resin developed to be suitable for packaging materials, industrial and agricultural films, which is referred to as third polyethylene.
상기 LLDPE는 LDPE와 HDPE의 중간 정도의 물성을 가지나 뛰어난 강인성과 투명성의 밸런스가 좋으며, 내열성 및 저렴한 가격 등의 장점이 있다. The LLDPE has a somewhat physical property between LDPE and HDPE, but has excellent balance of excellent toughness and transparency, heat resistance and low cost.
상기 제6층(500)의 두께는 상기 포장지의 전체 층 합에 대하여, 1:0.24~0.32의 두께비를 갖는 것이 바람직하다.The
만약, 상기 LLDPE의 두께가 상기 포장지 전체 층의 합에 대하여, 두께비가 1:0.24 미만으로 구비되면, 상기 포장지의 LLDPE층을 제외한 층의 두께가 두껍게 구비되어 제조단가가 높아지는 단점이 있고, 두께비가 1:0.32 이상으로 구비되면, 네크인(neck-in)이 발생하기 쉬운 단점이 있다.If the thickness of the LLDPE layer is less than 1: 0.24 with respect to the sum of all the layers of the wrapping paper, the thickness of the layer excluding the LLDPE layer is increased to increase the manufacturing cost, 1: 0.32 or more, neck-in tends to occur.
또한, 상기 제1층(100) 내지 제6층(600)을 적층시키기 위해 라미네이션 공법으로 이루어질 수 있다.In addition, the
이때, 상기 라미네이션 공법은 드라이 라미네이션, 웨트(wet) 라미네이션, 압출라미네이션(T-Die), 핫멜트라미네이션 중 선택되는 적어도 한가지 방법으로 제조될 수 있다.At this time, the lamination method may be manufactured by at least one method selected from dry lamination, wet lamination, extrusion lamination (T-die) and hot melt lamination.
바람직하게는 다종류의 필름 점착과 고기능성 복합필름 제조에 용이한 드라이 라미네이션 공법으로 제조될 수 있다.And can be produced by dry lamination method which is easy to manufacture various kinds of film adhesion and high functional composite film.
상기 드라이 라미네이션 공법을 이용할 경우, 드라이 라미네이션 공법용 접착제가 사용될 수 있다.When the dry lamination method is used, an adhesive for a dry lamination method may be used.
상기 드라이 라미네이션용 접착제는 폴리우레탄계 접착제, 2액형 폴리우레탄계 접착제, 무용제형 폴리우레탄계 접착제, 호모 폴리머, 폴리아크릴산에스테르계 접착제, 시아토아크릴레이트계 접착제, 에틸렌 공중합체계 접착제, 셀루로오스계 접착제, 폴리에스테르계 접착제, 폴리아미드계 접착제, 아미노 수지계 접착제, 페놀 수지계 접착제, 에폭시계 접착제, 반응형 아크릴계 접착제, 반응형 메타 아크릴계 접착제, 고무계 접착제, 실리콘계 접착제, 무기계 접착제 중 선택되는 하나 이상의 접착제를 이용할 수 있다.The dry lamination adhesive may be at least one selected from the group consisting of a polyurethane adhesive, a two-component polyurethane adhesive, a solventless polyurethane adhesive, a homopolymer, a polyacrylate ester adhesive, a cyanoacrylate adhesive, an ethylene copolymer adhesive, a cellulosic adhesive, One or more adhesives selected from ester adhesives, polyamide adhesives, amino resin adhesives, phenol resin adhesives, epoxy adhesives, reactive acrylic adhesives, reactive methacrylic adhesives, rubber adhesives, silicone adhesives and inorganic adhesives can be used .
바람직하게는, 드라이 라미네이션 공법에 주로 사용되는 2액형 폴리우레탄계 접착제가 사용될 수 있다.Preferably, a two-pack type polyurethane adhesive mainly used in the dry lamination method can be used.
이는 용제의 증발이 끝난 시점의 유동성과 그 이후의 경화반응으로 내열, 내수, 내한성 등이 풍부하며 유연하고 강인한 막을 만들고 또한 충분한 접착력을 유지할 수 있기 때문이다.This is because the flowability at the end of the evaporation of the solvent and the subsequent curing reaction are rich in heat resistance, water resistance, cold resistance, etc., and a flexible and strong film can be formed and sufficient adhesion can be maintained.
도 2는 본 발명에 따른 적층시트로 이루어진 포장지의 공정도이다. 2 is a process diagram of a wrapping paper made of a laminated sheet according to the present invention.
이하, 본 발명인 적층시트로 이루어진 포장지의 제조공정을 설명하기로 한다.Hereinafter, a process for producing a wrapper made of a laminated sheet of the present invention will be described.
상기 제조공정은 재료준비단계(S100), 인쇄단계(S200), 접합공정 단계(S300), 제단공정단계(S400), 포장지 제작 단계(S500)를 포함할 수 있다.The manufacturing process may include a material preparing step (S100), a printing step (S200), a bonding process step (S300), an alginating process step (S400), and a packaging material producing step (S500).
각 층의 두께 및 성분에 대한 설명은 상기하였으므로 생략하기로 한다.The thickness and the components of each layer have been described above, and therefore, the description thereof will be omitted.
상기 재료준비단계(S100)는, 상기 포장지의 재료를 준비하는 단계로서, 그라비아인쇄용 잉크, 제1층(100)에 사용될 PET, 제2층(200)에 사용될 PE, 제3층(300)에 사용될 노루지, 한지, 크라프트지, 백판지 또는 박엽지, 제4층(400)에 사용될 PE, 제5층(500)에 사용될 AL, AL-합지필름, 착색안료를 포함하는 EVOH필름 또는 실리카필름, 제6층(600)에 사용될 LLDPE, LDPE, PP, HDPE 또는 CPP 및 접착제 등을 준비하는 단계이다. The material preparing step S100 is a step of preparing a material for the wrapping paper, which is a step of preparing the material for the wrapping paper, the ink for gravure printing, the PET to be used for the
상기 재료준비단계(S100)를 거친후, 인쇄단계(S200)를 수행한다. 상기 인쇄단계(S200)는, 상기 그라비아인쇄용 잉크와 제1층(100)의 필름을 구비하여 그라비아 인쇄방법으로 상기 제1층(100)의 타측면에 수행될 수 있다.After the material preparing step (S100), a printing step (S200) is performed. The printing step S200 may be performed on the other side of the
다음으로, 상기 인쇄단계(S200)를 거친 상기 제1층(100)을 상기 제2층(200) 내지 제6층(600)과 적층시키는 접합공정 단계(S300)가 수행될 수 있는데, 접착제 안의 용제를 전부 증발시킨 후에 미경화 액상 또는 열 용융상태에 있는 접착제를 사용하여 팽팽하게 하는 방법인 라미네이션 공법이 수행될 수 있다.Next, a bonding process step (S300) of laminating the first layer (100) through the printing step (S200) with the second layer (200) to the sixth layer (600) may be performed. A lamination method can be carried out in which all the solvent is evaporated and then the film is tensed using an adhesive in an uncured liquid state or a hot melt state.
더욱 자세하게는, 드라이 라미네이션 공법이 수행될 수 있는데, 상기한 접착제 중 2액형 폴리우레탄계 접착제를 사용하여 제1층(100) 내지 제6층(600)에 도포한 후, 용매를 휘발시키고, 각각 필름을 접합시켜 적층제를 얻을 수 있다. More specifically, a dry lamination method can be carried out. After the two-component polyurethane adhesive of the above-mentioned adhesive is applied to the first layer (100) to the sixth layer (600), the solvent is volatilized, To obtain a laminate.
이 때 필름을 적층시키는 방법은 50~120℃로 가열된 금속롤과 고무롤 사이에 압착 라미네이션하여 냉각롤을 통과시킨다.At this time, a method of laminating a film is to press-laminate between a metal roll heated at 50 to 120 ° C and a rubber roll, and to pass through a cooling roll.
만약 상기 금속롤이 50℃미만으로 가열될 경우, 각 층의 필름의 압착이 이루어지지 않아 분리될 수 있는 문제점이 있고, 120℃이상으로 가열되면, 일정한 두께로 생산이 어려운 문제점이 생길 수 있다.If the metal roll is heated to less than 50 캜, there is a problem that the film of each layer is not pressed and can be separated, and when heated to 120 캜 or more, it may be difficult to produce the film with a certain thickness.
다음으로, 상기 접합공정 단계(S300)를 거친 필름을 후공정 작업에 적합하도록 규격별 또는 형태별로 절단하는 재단공정(S400)이 수행될 수 있다.Next, a cutting process (S400) may be performed in which the film passed through the joining process step (S300) is cut into standard sizes or types so as to be suitable for a post-process.
다음으로, 상기 제단공정단계(S400)를 거친 필름을 용도에 맞도록 절단가공하는 공정인 포장지 제작 단계(S500)가 수행될 수 있다.Next, a wrapping paper manufacturing step (S500) may be performed, which is a process of cutting the film that has undergone the above-described steps (S400).
<실시예1> 본 발명에 따른 적층시트로 이루어진 포장지의 제조. ≪ Example 1 > Preparation of a wrapping paper made of a laminated sheet according to the present invention .
1. 그라비아인쇄용 잉크, 제1층(100)에 사용될 PET, 제2층(200)에 사용될 PE, 제3층(300)에 사용될 노루지, 제4층(400)에 사용될 PE, 제5층(500)에 사용될 AL, 제6층(600)에 사용될 LLDPE, 2액형 폴리우레탄계 접착제 등을 준비한다.1. PET for use in the
2. 상기 제1층의 타측면에 그라비아 인쇄방법을 통해 인쇄한다.2. Print on the other side of the first layer through a gravure printing method.
3. 상기 인쇄된 제1층과 상기 제2층 내지 제6층을 2액형 폴리우레탄계 접착제를 포함하여 드라이라미네이션 공법으로 적층한다.3. The printed first layer and the second to sixth layers are laminated by a dry lamination method including a two-pack type polyurethane adhesive.
4. 상기 드라이라미네이션 공법이 수행된 필름을 규격별 또는 형태별로 절단하여 재단한다.4. The film subjected to the dry lamination method is cut by size or type and cut.
5. 상기 재단된 필름을 용도에 맞도록 절단 가공하여 일측이 개구된 포장지를 제작한다.5. The cut film is cut to meet the application, and a wrapping paper having one side opened is produced.
<비교예1> AL- 합지필름을 포함한 적층시트로 이루어진 포장지의 제조. ≪ Comparative Example 1 > Production of a wrapping paper made of a laminated sheet containing an AL- laminated film .
포장지의 제조시 상기 제2층(200)에 Al대신 Al-합지필름으로써 Al의 일면에 EVOH필름을 합지한 Al-합지필름을 사용한 것을 제외하고 실시예 1과 동일하게 제조하였다.The same procedure as in Example 1 was carried out except for using an Al-laminated film prepared by adding an EVOH film to one side of Al as an Al-laminated film in place of Al in the
<시험예1> LDPE를 포함하는 적층시트로 이루어진 포장지의 제조. ≪ Test Example 1 > Production of a wrapping paper made of a laminated sheet containing LDPE .
포장지의 제조시 LLDPE대신 LDPE를 첨가한 것을 제외하고 실시예 1과 동일하게 제조하였다.The procedure of Example 1 was repeated except that LDPE was added instead of LLDPE in the preparation of the wrapping paper.
<시험예2> HDPE를 포함하는 적층시트로 이루어진 포장지의 제조. ≪ Test Example 2 > Production of a wrapping paper made of a laminated sheet containing HDPE .
포장지의 제조시 LLDPE대신 HDPE를 첨가한 것을 제외하고 실시예 1과 동일하게 제조하였다.The procedure of Example 1 was repeated except that HDPE was added instead of LLDPE in the preparation of the wrapping paper.
<시험예3> PP를 포함하는 적층시트로 이루어진 포장지의 제조. ≪ Test Example 3 > Preparation of a wrapping paper made of a laminated sheet containing PP .
포장지의 제조시 LLDPE대신 PP를 첨가한 것을 제외하고 실시예 1과 동일하게 제조하였다.The procedure of Example 1 was repeated except that PP was added instead of LLDPE in the preparation of the wrapping paper.
<시험예4> CPP를 포함하는 적층시트로 이루어진 포장지의 제조. ≪ Test Example 4 > Production of a wrapping paper made of a laminated sheet containing CPP .
포장지의 제조시 LLDPE대신 CPP를 첨가한 것을 제외하고 실시예 1과 동일하게 제조하였다.The procedure of Example 1 was repeated except that CPP was added instead of LLDPE in the preparation of the wrapping paper.
상기 온도별 과망간산칼륨소비량의 시험방법은 기구 및 용기포장 공전에 기재된 시험법을 준수하여 실험하였다.The test method for the consumption of potassium permanganate by the above temperature was carried out in compliance with the test method described in the apparatus and the container packaging.
상기 표1에 나타낸 바와 같이, 전반적으로 규격기준치인 10mg/L보다 낮게 소비되었다. 상기 과망간산칼륨소비량 측정은 산화되기 쉬운 물질의 양을 측정하는 것으로써, 상기 실시예1과 비교예1을 비교하면, 고온에서 비교예1이 실시예1보다 과망간산칼륨소비량이 적은 것으로 나타났다.As shown in Table 1 above, overall consumption was lower than the standard reference value of 10 mg / L. The above-described potassium permanganate consumption measurement showed that the amount of potassium permanganate consumed in Comparative Example 1 was lower than that in Example 1 at a high temperature by comparing the amount of the easily oxidizable substance with that of Example 1 and Comparative Example 1.
따라서, Al을 단독으로 사용하는 것보다 Al의 일측에 필름을 합지한 Al-합지필름의 과망간산칼륨소비량이 적은 것을 알 수 있다.Therefore, it can be seen that the consumed amount of potassium permanganate in the Al-laminated film laminated with a film on one side of Al is smaller than the case where Al is used alone.
상기 제5층(500) 재료에 따른 증발잔류물비교의 시험방법은 기구 및 용기포장 공전에 기재된 시험법을 준수하여 실험하였다.The test method of the comparison of the evaporation residue according to the material of the fifth layer (500) was performed in compliance with the test method described in the apparatus and the packing operation.
상기 표 2에 나타낸 바와 같이, 침출용매(물, 4%초산, 20%알코올, n-헵탄)의 종류에 관계 없고, 100℃를 넘는 사용온도에서 모두 30ppm인 증발잔류물의 기준치를 넘지 않는 것으로 나타났다.As shown in the above Table 2, it was found that the content did not exceed the reference value of the evaporation residue of 30 ppm in all of the use temperatures exceeding 100 캜 regardless of the kind of the leaching solvent (water, 4% acetic acid, 20% alcohol and n-heptane) .
그러나, 전반적으로 실시예 1이 시험예 1,3 및 4에 비해 낮은 수치를 나타냈지만, 시험예 2 보다 높은 수치를 나타내었다.However, overall Example 1 showed lower values than Test Examples 1, 3 and 4, but higher values than Test Example 2.
이는 제5층(500)이 HDPE로 이루어 짐으로써, 연화점이 높고, 강성, 경도 등이 우수한 HDPE의 특성에 의한 결과라고 사료된다. This is because the
그러나, HDPE를 사용할 경우, HDPE의 충격강도와 인열강도의 열세에 의해 사용범위가 좁아지는 단점이 발생될 수 있다.However, when HDPE is used, there may be a disadvantage that the use range is narrowed due to the impact strength and tear strength of HDPE.
또한, LDPE를 사용할 경우, 수증기 및 가스투과성이 높아 상기 포장지 내 제품을 오래 보관하지 못하는 단점이 있으므로 LDPE와 HDPE의 중간 정도의 물성을 갖는 LLDPE를 사용하는 것이 바람직하다.In addition, when LDPE is used, it is preferable to use LLDPE having intermediate properties between LDPE and HDPE because it has a disadvantage in that the product in the wrapping paper can not be stored for a long time because of high vapor permeability and gas permeability.
상기에서는 본 발명의 바람직한 실시 예를 설명하였지만, 통상의 기술자는 아래의 특허 청구의 범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다. While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it will be understood by those skilled in the art that various changes and modifications may be made therein without departing from the spirit and scope of the invention as defined by the appended claims. There will be.
100: 제1층
200: 제2층
300: 제3층
400: 제4층
500: 제5층
600: 제6층
S100: 재료준비단계
S200: 인쇄단계
S300: 접합공정 단계
S400: 제단공정단계
S500: 포장지 제작 단계100: 1st layer
200: Second layer
300: Third floor
400: fourth floor
500: fifth floor
600: Sixth floor
S100: Material preparation step
S200: Printing step
S300: Bonding step
S400: Altar process step
S500: Wrapping paper production step
Claims (4)
PET(Polyethylene phthalate)를 포함하는 제1층(100);
PE(Polyethylene)를 포함하는 제2층(200);
노루지, 한지, 크라프트지, 백판지 또는 박엽지 중 선택되는 적어도 한가지를 포함하는 제3층(300);
PE(Polyethylene)를 포함하는 제4층(400);
AL(Aluminium), AL(Aluminium)-합지필름, 착색안료를 포함하는 EVOH필름 또는 실리카필름 중 선택되는 적어도 한가지를 포함하는 제5층(500); 및
LLDPE, LDPE, PP, HDPE 또는 CPP 중 선택되는 적어도 한가지를 포함하는 제6층(600);이 순차적으로 적층되어 이루어지고,
상기 제1층(100) 내지 제6층(600)을 적층시키기 위해 라미네이션 공법에 의해 접착되는 것을 특징으로 하는 적층시트로 이루어진 포장지.
1. A wrapping paper comprising a laminated sheet for packing seeds, fruit, cosmetic solution and mask pack,
A first layer 100 comprising PET (Polyethylene phthalate);
A second layer 200 comprising PE (polyethylene);
A third layer (300) comprising at least one selected from the group consisting of corundum, korean paper, kraft paper, white board paper or foil paper;
A fourth layer 400 comprising PE (Polyethylene);
A fifth layer 500 comprising at least one selected from the group consisting of AL (Aluminum), AL (Aluminum) -shaped film, EVOH film containing colored pigment, or silica film; And
A sixth layer 600 including at least one selected from the group consisting of LLDPE, LDPE, PP, HDPE, and CPP;
Wherein the first layer (100) to the sixth layer (600) are laminated by a lamination method to laminate the first layer (100) to the sixth layer (600).
상기 AL-합지필름은 AL 필름의 일면에 EVOH필름, 실리카필름, 유기물증착필름 또는 무기물증착필름 중 선택되는 적어도 한가지를 합지시킨 것이고,
상기 Al-합지필름에 사용되는 합지필름의 두께는, 전체층의 합에 대하여, 1:0.01~0.04의 비율로 구비되며,
상기 접착제는,
폴리우레탄계 접착제, 2액형 폴리우레탄계 접착제, 무용제형폴리우레탄계 접착제, 호모 폴리머, 폴리아크릴산에스테르계 접착제, 시아토아크릴레이트계 접착제, 에틸렌 공중합체계 접착제, 셀루로오스계 접착제, 폴리에스테르계 접착제, 폴리아미드계 접착제, 아미노 수지계 접착제, 페놀 수지계 접착제, 에폭시계 접착제, 반응형아크릴계 접착제, 반응형 메타 아크릴계 접착제, 고무계 접착제, 실리콘계 접착제, 무기계 접착제로 이루어진 군 중에서 선택되는 하나 또는 둘 이상의 접착제를 이용하고,
상기 라미네이션 공법은 드라이 라미네이션, 웨트(Wet) 라미네이션, 압출 라미네이션 또는 핫멜트 라미네이션 공법 중 선택되는 적어도 한가지 공법에 의해 접착되는 것을 특징으로 하는 적층시트로 이루어진 포장지.
The method according to claim 1,
The AL-laminated film is obtained by laminating at least one selected from the group consisting of an EVOH film, a silica film, an organic substance-deposited film and an inorganic substance-deposited film on one surface of an AL film,
The thickness of the laminated film used in the Al-laminated film is in the range of 1: 0.01 to 0.04 with respect to the sum of all layers,
Preferably,
A polyurethane adhesive, a two-component polyurethane adhesive, a solventless polyurethane adhesive, a homopolymer, a polyacrylate ester adhesive, a cyanoacrylate adhesive, an ethylene copolymer adhesive, a cellulosic adhesive, a polyester adhesive, Wherein one or more adhesives selected from the group consisting of an adhesive agent, an amino resin adhesive, a phenol resin adhesive, an epoxy adhesive, a reactive acrylic adhesive, a reactive methacrylic adhesive, a rubber adhesive, a silicone adhesive,
Wherein the lamination method is bonded by at least one method selected from dry lamination, wet lamination, extrusion lamination or hot melt lamination.
그라비아인쇄용 잉크, 제1층(100)에 사용될 PET, 제2층(200)에 사용될 PE, 제3층(300)에 사용될 노루지, 한지, 크라프트지, 백판지 또는 박엽지 중 선택되는적어도 한가지, 제4층(400)에 사용될 PE, 제5층(500)에 사용될 AL, AL-합지필름, 착색안료를 포함하는 EVOH필름 또는 실리카필름 중 선택되는 적어도 한가지, 제6층(600)에 사용될 LLDPE, LDPE, PP, HDPE 또는 CPP중 선택되는 적어도 한가지 및 접착제를 준비하는 재료준비단계(S100);
상기 제1층(100)의 타측면에 그라비아 인쇄를 실행하는 인쇄단계(S200);
상기 인쇄단계(S200)를 거친 상기 제1층(200)과 상기 제2층(200) 내지 제6층(600)을 라미네이션 공법으로 접착시키는 접합공정 단계(S300);
상기 접합공정 단계(S300)를 거친 필름을 후공정 작업에 적합하도록 규격별 또는 형태별로 절단하는 제단공정단계(S400); 및
상기 제단공정단계(S400)를 거친 필름을 용도에 맞도록 절단 또는 가공하는 포장지 제작 단계(S500);
를 포함하는 것을 특징으로 하는 적층시트로 이루어진 포장지의 제조방법.
1. A laminated sheet for packaging a seed, a fruit, a cosmetic solution, and a mask pack,
At least one of gravure printing ink, PET to be used for the first layer 100, PE to be used for the second layer 200, noruji to be used for the third layer 300, kraft paper, kraft paper, At least one selected from the PE to be used for the fourth layer 400, the AL, the AL-laminated film to be used for the fifth layer 500, the EVOH film or the silica film including the coloring pigment, the LLDPE , A material preparation step (SlOO) for preparing at least one selected from LDPE, PP, HDPE or CPP and an adhesive;
A printing step (S200) of performing gravure printing on the other side of the first layer (100);
A bonding process step (S300) of bonding the first layer (200) through the printing step (S200) and the second layer (200) to the sixth layer (600) by a lamination method;
An altar process step (S400) of cutting the film passed through the joining process step (S300) by size or type so as to be suitable for a post-process operation; And
A packaging paper manufacturing step (S500) of cutting or processing the film having undergone the heating process step (S400) so as to meet the application;
Wherein the laminated sheet is a laminated sheet.
상기 AL-합지필름은 AL의 일면에 EVOH필름, 실리카필름, 유기물증착 필름 또는 무기물증착 필름 중 선택되는 적어도 한가지를 합지시킨 것이고,
상기 Al-합지필름에 사용되는 합지필름의 두께는, 전체층의 합에 대하여, 1:0.01~0.04의 비율로 구비되며,
상기 접착제는,
폴리우레탄계 접착제, 2액형 폴리우레탄계 접착제, 무용제형 폴리우레탄계 접착제, 호모 폴리머, 폴리아크릴산에스테르계 접착제, 시아토아크릴레이트계 접착제, 에틸렌 공중합체계 접착제, 셀루로오스계 접착제, 폴리에스테르계 접착제, 폴리아미드계 접착제, 아미노수지계 접착제, 페놀 수지계 접착제, 에폭시계 접착제, 반응형아크릴계 접착제, 반응형 메타 아크릴계 접착제, 고무계 접착제, 실리콘계 접착제 및 무기계 접착제로 이루어진 군 중에서 선택되는 하나 또는 둘 이상의 접착제를 이용하고,
상기 라미네이션 공법은,
드라이 라미네이션, 웨트(Wet) 라미네이션, 압출 라미네이션 또는 핫멜트라미네이션 공법에 의해 접착되는 것을 특징으로 하는 적층시트로 이루어진 포장지의 제조방법.
The method of claim 3,
The AL-laminated film is obtained by laminating at least one selected from the group consisting of an EVOH film, a silica film, an organic substance-deposited film and an inorganic substance-deposited film on one side of an AL,
The thickness of the laminated film used in the Al-laminated film is in the range of 1: 0.01 to 0.04 with respect to the sum of all layers,
Preferably,
A polyurethane adhesive, a two-component polyurethane adhesive, a solventless polyurethane adhesive, a homopolymer, a polyacrylate ester adhesive, a cyanoacrylate adhesive, an ethylene copolymer adhesive, a cellulosic adhesive, a polyester adhesive, Based adhesive, an amino resin adhesive, a phenol resin adhesive, an epoxy adhesive, a reactive acrylic adhesive, a reactive methacrylic adhesive, a rubber adhesive, a silicone adhesive and an inorganic adhesive,
In the lamination method,
Wherein the laminated sheet is adhered by dry lamination, wet lamination, extrusion lamination or hot melt lamination.