KR20180057953A - 2 component type liquids for temporary tattoo and printing method on skin thereof - Google Patents

Abstract

The present invention relates to a two-component type solution for temporary tattoos, which comprises: a first liquid including a solvent, a coloring agent, and a surfactant; and a second liquid including a solvent, and a skin applying type film forming agent. The first liquid is an ink liquid, and the second liquid is an ink fixing agent. The solvent of the first liquid contains water and an organic solvent in a weight ratio of 1 : 0.01 to 1.3, and the solvent of the second liquid contains an organic solvent. An objective of the present invention is to provide the solution for temporary tattoos which uses materials harmless to the human body so as to allow users to draw various colors directly into the skin.

Description

일회성 문신용 2액형 용액 및 이의 인쇄방법{2 component type liquids for temporary tattoo and printing method on skin thereof}[0001] The present invention relates to a two-component, two-component solution for a tattoo,

본 발명은 일회성 문신용 2액형 용액 및 이의 인쇄방법에 관한 것으로서, 보다 상세하게는 장기 저장이 가능하고, 내번짐성, 내마모성 및 내수성이 우수하며, 비누로 쉽게 지울 수 있는 동시에 노즐 막힘이 발생하지 않는 효과를 갖는 일회성 문신용 2액형 용액 및 이의 인쇄방법에 관한 것이다.More particularly, the present invention relates to a two-component, two-part solution for tattooing, which can be stored for a long period of time, has excellent flame retardancy, abrasion resistance and water resistance, can be easily removed with soap, The present invention relates to a two-component solution for a one-time tattooing having an effect and a printing method thereof.

화장과 더불어 인류역사와 함께한 문신(타투)은 인류역사와 함께한 신체장식의 한 방법으로 젊은 세대를 중심으로 확대되고 있다. 세계적 대중스타들의 문신에 대한 기호와 이를 보는 이들의 동경은 스타의 이미지와 문신이 동일시되어 더욱 급속한 문신인구의 팽창을 가져오고 있다. 타임스에 따르면 21~39세 성인 중 14%가 문신 또는 타투를 하고 있으며 이 중 16%는 문신한 것을 후회하고 있는 것으로 보도되기도 하였다.Tattoos (tattoos) with makeup and human history are expanding around the younger generation as a method of body decoration with human history. The symbol of the tattoo of the global popular stars and the longing of those who see it are bringing a swift increase of the tattoo population with the identification of the star image and the tattoo. According to the Times, 14% of adults aged 21 to 39 are tattooing or tattooing, and 16% of them are reported to be regretting tattoos.

전통적 타투 문신은 피부의 진피층까지 색소를 침투시키는 시술방식으로 초기 시술비용도 비용이지만 한번 시술하면 영구적이어서 제거가 용이하지 않으며, 단색(흑갈색) 위주의 문양으로 부작용 및 타인에게 혐오감을 주기도 하며, 특히 우리나라의 경우 문화적인 차이로 인해 문신한 사람들에 대한 평판이 좋지 않아 고비용과 시간 및 노력을 투자한 문신을 보여주지 못한 채 감추게 되어 자기 만족도가 떨어질 뿐만 아니라 색상 또한 컬러풀하지 못하다는 단점이 있다. 그리하여 전통 타투 문신의 제거 즉, 피부 복원을 위해서 레이저 시술방식이 최적이지만 이 경우 초기 시술비용의 수 십배에 해당하는 의료비용과 치료과정의 고통을 이겨내야 하는 문제점을 안고 있다.Traditional tattoo tattoo is a procedure that penetrates pigment to the skin's dermis. It is costly for initial treatment but it is permanent because it is permanent and it is not easy to remove. It is a monochrome (dark brown) pattern and gives side effects and dislike to others. In Korea, because of the cultural differences, tattoos are not well reputed and tattoos that have costly and time and effort invested are not shown and are hidden, resulting in a decrease in self-satisfaction and a lack of color. Thus, laser treatment is optimal for the removal of tattoo tattoos, that is, skin restoration. However, in this case, it is necessary to overcome the medical costs and the pain of the treatment process which is several tens of times higher than the initial treatment cost.

최근에는 전통적 타투의 시술 후 영구성을 보완하기 위한 유사상품으로 출시되는 헤나타투(잉크를 이용해 몸에 그리는 방식), 수전사 스티커(물을 이용해 몸에 전사지를 붙이는 형태), 도장과 잉크를 이용해 몸에 문양을 찍는 방법 등 다양한 방법들이 제안되기도 하였다.In recent years, it has been used as a similar product to complement the permanence after the practice of traditional tattoo, such as a henat tatu (a method of drawing on the body using ink), a water transfer sticker (a form of attaching a transfer sheet to the body using water) And a variety of methods have been proposed.

하지만 피부에 부착하는 스티커 형태의 제품은 접착제를 사용함에 따라 접착제의 용제인 벤젠이나 솔벤트의 잔유물이 피부에 영향을 주어 발진 등을 일으키는 원인으로 작용하고, 접착제 사용원료인 접착수지가 인체피부에 결합하면서 피부 호흡을 차단하여 피부대사를 방해하는 부작용이 있다.However, sticky products attached to the skin stick to the skin due to the use of the adhesive, which causes the residue of benzene or solvent, which is the solvent of the adhesive, to cause skin rashes, There is a side effect that interrupts skin metabolism by blocking skin respiration.

한편, 종래의 문신스티커용 감광잉크의 조성물 및 이 컬러문신스티커의 제조방법은 빛 및 그 빛의 세기에 의해 문신스티커의 색상이 다양하게 변화되어 화려한 색상이 조화를 이루며 유지되는 효과가 있다. 그러나, 문신스티커용 감광잉크의 경우 피부 자극 등의 문제를 유발할 수 있으므로 피부에 직접 인쇄하여 사용하지 못하는 단점이 있었다. Meanwhile, the conventional composition of the photosensitive ink for a tattoo sticker and the method of manufacturing the color tattoo sticker have various effects that the color of the tattoo sticker is variously changed due to the intensity of the light and the light intensity, and the colorful colors are kept harmonious. However, since the photosensitive ink for tattoo stickers may cause problems such as skin irritation, there is a disadvantage that it can not be directly used for printing on the skin.

또한, 인체에 무해한 성분의 조합으로 잉크를 제조하여 피부에 직접 인쇄 할 경우 번짐으로 인한 화상 구현이 어렵고, 마모 및 물에 대한 내구성이 부족하므로 이를 해결하기 위해 접착 성분을 첨가하게 되면 장기 저장 시 점도가 급격히 상승하고, 인쇄 기기의 노즐 막힘이 발생하는 등의 사용하기 어려운 문제가 있었다.In addition, when an ink is produced by a combination of harmless components and directly printed on the skin, it is difficult to realize an image due to blurring and the durability against wear and water is insufficient. Therefore, There is a problem that it is difficult to use such as clogging of nozzles of the printing apparatus.

이러한 문신스티커용 감광잉크 기술과 관련하여, 선행기술인 한국공개특허 제 10-2007-0048679호(발명의 명칭: 컬러 문신스티커용 감광잉크의 조성물 및 컬러문신스티커의 제조방법)에 대해 개시하고 있다.With respect to such photosensitive ink technology for tattoo stickers, Korean Patent Laid-Open No. 10-2007-0048679 (the title of the invention: composition of photosensitive ink for color tattoo stickers and method of producing color tattoo stickers) is disclosed.

본 발명은 상기와 같은 문제점을 해결하기 위하여 안출된 것으로, 본 발명의 해결하려는 과제는 인체에 무해한 소재를 활용하여 피부에 직접 다양한 컬러 색상을 그릴 수 있고, 장기 저장이 가능하고, 내번짐성, 내마모성 및 내수성이 우수하며, 비누로 쉽게 지울 수 있는 동시에 노즐 막힘이 발생하지 않는 효과를 갖는 일회성 문신용 2액형 용액 및 이의 인쇄방법을 제공하는 것이다.Disclosure of Invention Technical Problem [8] Accordingly, the present invention has been made keeping in mind the above problems occurring in the prior art, Which is excellent in abrasion resistance and water resistance, can be easily cleansed with soap, and has no clogging of nozzles, and a printing method of the same.

상술한 과제를 해결하기 위해 본 발명은 용매, 착색제 및 계면활성제를 포함하는 제1액 및 용매 및 피부도포형 필름형성제를 포함하는 제2액을 포함하고, 상기 제1액은 잉크액이며, 상기 제2액은 잉크 고정화제이고, 상기 제1액의 용매는 물 및 유기용매를 1 : 0.01 ~ 1.3 의 중량비로 포함하며, 제2액의 용매는 유기용매인 것을 특징으로 하는 일회성 문신용 2액형 용액을 제공한다.In order to solve the above-mentioned problems, the present invention provides a film forming apparatus comprising a first liquid containing a solvent, a colorant and a surfactant, and a second liquid comprising a solvent and a skin-formable film former, Wherein the second liquid is an ink immobilizing agent and the solvent of the first liquid contains water and an organic solvent in a weight ratio of 1: 0.01 to 1.3, and the solvent of the second liquid is an organic solvent. Solution.

본 발명의 바람직한 일실시예에 따르면, 상기 피부도포형 필름형성제는 카르복시비닐폴리머, 카르복시메틸셀룰로오스, 메틸셀룰로오스, 에틸셀룰로오스, 히드록시알킬셀룰로오스, 하이드록시프로필셀룰로오스, 하이드록시프로필메틸셀룰로오스, 하이드록시 에틸 셀룰로오스, 알킬셀룰로오스, 폴리우레탄, 폴리우레탄과 아크릴레이트 공중합체, 폴리에스테르 우레탄, 폴리비닐피롤리돈, 폴리비닐아세테이트, 비닐피롤리돈-비닐아세테이트 공중합체, 폴리비닐알코올, 폴리아크릴산, 폴리아크릴산나트륨, 아크릴레이트 폴리머, 아크릴레이트 공중합체, 폴리아크릴산 부분중화물, 폴리아크릴산 전분, 카멜로스나트륨, 카르복시비닐폴리머, N-비닐아세테이트아미드, 알킬 올레핀산, 알킬 올레핀산 에스테르 공중합체, 아미드/올레핀산, 아미드/올레핀산 공중합체 또는 이들의 혼합물로부터 선택된 1종 이상을 포함할 수 있다.According to a preferred embodiment of the present invention, the skin-formable film-forming agent is selected from the group consisting of carboxyvinyl polymer, carboxymethylcellulose, methylcellulose, ethylcellulose, hydroxyalkylcellulose, hydroxypropylcellulose, hydroxypropylmethylcellulose, Polyvinylpyrrolidone, polyvinyl acetate, vinylpyrrolidone-vinyl acetate copolymer, polyvinyl alcohol, polyacrylic acid, polyacrylic acid, polyacrylic acid, polyacrylic acid, But are not limited to, sodium, acrylate polymers, acrylate copolymers, polyacrylic acid partially saponified, polyacrylic acid starch, camelose sodium, carboxyvinyl polymer, N-vinyl acetate amide, alkyl olefinic acid, alkyl olefinic acid ester copolymer, amide / olefinic acid , Amide / olefinic acid Copolymers, or mixtures thereof.

본 발명의 바람직한 다른 일실시예에 따르면, 상기 잉크 고정화제는 용매 100 중량부에 대하여 피부도포형 필름형성제를 0.1 ~ 80 중량부 포함할 수 있다.According to another preferred embodiment of the present invention, the ink immobilizing agent may contain 0.1 to 80 parts by weight of the skin-applying film forming agent per 100 parts by weight of the solvent.

본 발명의 바람직한 또 다른 일실시예에 따르면, 상기 착색제는 안료 및 염료를 포함할 수 있고, 상기 계면활성제는 비이온성 계면활성제 및 이온성 계면활성제 중에서 선택된 1종 이상을 포함할 수 있다.According to another preferred embodiment of the present invention, the colorant may include a pigment and a dye, and the surfactant may include at least one selected from a nonionic surfactant and an ionic surfactant.

본 발명의 바람직한 또 다른 일실시예에 따르면, 상기 잉크액은 용매 100 중량부에 대하여 착색제 0.5 ~ 10 중량부 및 계면활성제 0.01 ~ 8 중량부로 포함할 수 있다.According to another preferred embodiment of the present invention, the ink liquid may include 0.5 to 10 parts by weight of a colorant and 0.01 to 8 parts by weight of a surfactant based on 100 parts by weight of the solvent.

본 발명의 바람직한 또 다른 일실시예에 따르면, 상기 유기용매는 에틸 알콜, n-프로필알콜, 이소프로필알콜, n-부틸알콜, sec-부틸알콜, t-부틸알콜, 이소부틸알콜, 에틸락테이트, 에틸렌글리콜, 디에틸렌글리콜, 트리에틸렌글리콜, 프로필렌글리콜, 디프로필렌글리콜 부틸렌글리콜, 1,4-부탄디올, 1,2,4-부탄트리올, 1,5-펜탄디올, 1,6-헥산디올, 1,2-헥산디올, 1,2,6-헥산트리올, 헥실렌글리콜, 글리세롤, 글리세롤 에톡실레이트, 트리메틸롤프로판 에톡실레이트, 소디움 2-피롤리돈-5-카르복실레이트, 메틸 피롤리돈, 카프릴릴 피롤리돈, 에트리올, 에틸렌글리콜 노메틸 에테르, 에틸렌글리콜 노에틸 에테르, 디에틸렌글리콜 메틸 에테르, 디에틸렌글리콜 에틸 에테르, 트리에틸렌글리콜 노메틸 에테르, 트리에틸렌글리콜 노에틸 에테르, 디메틸 술폭사이드, 테트라메틸렌술폰, 티오글리콜 및 중량평균분자량이 150 ~ 1000인 폴리에틸렌글리콜 중에서 선택된 1종 이상을 포함할 수 있다.According to another preferred embodiment of the present invention, the organic solvent is selected from ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol, , Ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol butylene glycol, 1,4-butanediol, 1,2,4-butanetriol, 1,5-pentanediol, Diol, 1,2-hexanediol, 1,2,6-hexanetriol, hexylene glycol, glycerol, glycerol ethoxylate, trimethylolpropaneethoxylate, sodium 2-pyrrolidone- Propylene glycol monomethyl ether, ethylene glycol nonyl ether, diethylene glycol methyl ether, diethylene glycol ethyl ether, triethylene glycol nonyl ether, triethylene glycol nonyl ether, Ethyl ether, dimethyl sulfoxide, tetra The methylene sulfone, thioglycolic, and the weight average molecular weight may include at least one selected from polyethylene glycol 150-1000.

한편, 상술한 과제를 해결하기 위해 본 발명은, 용매, 착색제 및 계면활성제를 포함하는 잉크액과 용매 및 피부도포형 필름형성제를 포함하는 잉크 고정화제를 각각 제조하는 단계;를 포함하는 것을 특징으로 하는 일회성 문신용 2액형 용액 제조방법을 제공한다.On the other hand, in order to solve the above-mentioned problems, the present invention includes a step of separately preparing an ink immobilizing agent comprising an ink liquid containing a solvent, a colorant and a surfactant, a solvent and a skin- To provide a two-component solution for one-time tattooing.

본 발명의 바람직한 일실시예에 따르면, 상기 잉크액은 용매 100 중량부에 대하여 착색제 0.5 ~ 10 중량부 및 계면활성제 0.01 ~ 8 중량부를 포함할 수 있고, 상기 잉크 고정화제는 용매 100 중량부에 대하여 피부도포형 필름형성제를 0.1 ~ 10 중량부 포함할 수 있다.According to a preferred embodiment of the present invention, the ink liquid may include 0.5 to 10 parts by weight of a coloring agent and 0.01 to 8 parts by weight of a surfactant based on 100 parts by weight of the solvent, and the ink immobilizing agent may be added to 100 parts by weight of the solvent And 0.1 to 10 parts by weight of a skin-formable film-forming agent.

한편, 상술한 과제를 해결하기 위해 본 발명은, (a) 잉크 고정화제를 피부에 도포하는 단계, (b) 도포한 잉크 고정화제를 건조하는 단계 및 (c) 상기 잉크 고정화제를 도포한 영역의 상부에 잉크액을 도포하는 단계;를 포함하되,상기 잉크액은 용매, 착색제 및 계면활성제를 포함하는 제 1 액이고, 상기 잉크 고정화제는 용매 및 피부도포형 필름형성제를 포함하는 제 2 액인 것을 특징으로 하는 일회성 문신용 2액형 용액의 인쇄방법을 제공한다.In order to solve the above-described problems, the present invention provides a method for manufacturing a liquid immersion medium, comprising the steps of (a) applying an ink immobilizing agent to skin, (b) drying the applied ink immobilizing agent, and (c) Wherein the ink liquid is a first liquid comprising a solvent, a colorant and a surfactant, and the ink immobilizing agent is a second liquid comprising a solvent and a second coating composition containing a skin- Wherein the two-component solution for a one-time tattooing is a liquid.

본 발명의 바람직한 일실시예에 따르면, 상기 건조는 0.1 ~ 60 초 동안 수행할 수 있다.According to a preferred embodiment of the present invention, the drying may be performed for 0.1 to 60 seconds.

본 발명의 바람직한 다른 일실시예에 따르면, 상기 잉크액을 도포하는 단계는 잉크 고정화제를 도포한 영역의 전부 또는 일부 영역에 잉크액을 도포할 수 있다.According to another preferred embodiment of the present invention, the step of applying the ink liquid may apply the ink liquid to all or a part of the area to which the ink immobilizing agent is applied.

또한, 상기의 잉크액으로 인쇄한 후 잉크 고정화제를 추가로 도포하게되면 광택의 향상과 더불어 내수성, 내마모성 등 내구성을 더욱 더 향상시킬 수 있다.Further, when the ink fixing agent is further applied after printing with the above-described ink liquid, durability such as water resistance and abrasion resistance can be further improved as well as gloss.

본 발명의 일회성 문신용 2액형 용액 및 이의 인쇄방법으로 피부에 원하는 이미지나 텍스트를 손쉽게 그리는 것이 가능하다. 일회성 문신용 잉크는 장기 저장안정성이 우수하여 노즐이 잘 막히지 않으며 내번짐성이 우수하고, 인쇄된 화상은 내마모성, 내수성이 우수하며, 비누로 쉽게 지울 수 있다.It is possible to easily draw a desired image or text on the skin by the one-time two-component solution for tattooing and the printing method of the present invention. The one-time tattoo ink has excellent long-term storage stability, so that the nozzles are not clogged well and the ink is excellent in bleed resistance. The printed image is excellent in abrasion resistance, water resistance, and can be easily wiped with soap.

아래에서는 첨부한 도면을 참조하여 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 실시예를 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다. 그리고 도면에서 본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였으며, 명세서 전체를 통하여 유사한 부분에 대해서는 유사한 도면 부호를 붙였다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings, which will be readily apparent to those skilled in the art. The present invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth herein. In order to clearly illustrate the present invention, parts not related to the description are omitted, and similar parts are denoted by like reference characters throughout the specification.

명세서 전체에서, 어떤 부분이 다른 부분과 "연결"되어 있다고 할 때, 이는 "직접적으로 연결"되어 있는 경우뿐 아니라, 그 중간에 다른 소자를 사이에 두고 "전기적으로 연결"되어 있는 경우도 포함한다. 또한 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 포함할 수 있는 것을 의미하며, 하나 또는 그 이상의 다른 특징이나 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.Throughout the specification, when a part is referred to as being "connected" to another part, it includes not only "directly connected" but also "electrically connected" with another part in between . Also, when an element is referred to as "including" an element, it is to be understood that the element may include other elements as well as other elements, And does not preclude the presence or addition of one or more other features, integers, steps, operations, components, parts, or combinations thereof.

이하, 본 발명을 보다 상세히 설명한다.Hereinafter, the present invention will be described in more detail.

상술한 바와 같이 종래의 구성은 빛 및 그 빛의 세기에 의해 문신스트커의 색상이 다양하게 변화되어 화려한 색상이 조화를 이루며 유지되는 효과가 있었지만, 피부 자극 등으로 피부에 직접 인쇄하지 못하는 단점이 있었다. 또한, 인체에 무해한 성분의 조합으로 잉크를 제조하여 피부에 직접 인쇄 할 경우 번짐으로 인한 화상 구현이 어렵고, 마모 및 물에 대한 내구성이 부족하므로 이를 해결하기 위해 접착 성분을 첨가하게 되면 장기 저장 시 점도가 급격히 상승하고, 인쇄 기기의 노즐 막힘이 발생하는 등의 사용하기 어려운 문제가 있었다. As described above, in the conventional configuration, the colors of the tattoo sticker are variously changed due to the intensity of the light and the light, and the colorful colors are maintained in harmony. However, the disadvantage that the tattoo sticker can not be directly printed on the skin due to skin irritation there was. In addition, when an ink is produced by a combination of harmless components and directly printed on the skin, it is difficult to realize an image due to blurring and the durability against wear and water is insufficient. Therefore, There is a problem that it is difficult to use such as clogging of nozzles of the printing apparatus.

이에 본 발명은 용매, 착색제 및 계면활성제를 포함하는 제1액 및 용매 및 피부도포형 필름형성제를 포함하는 제2액을 포함하고, 상기 제1액은 잉크액이며, 상기 제2액은 잉크 고정화제이고, 상기 제1액의 용매는 물 및 유기용매를 1 : 0.01 ~ 1.3 의 중량비로 포함하며, 제2액의 용매는 유기용매인 것을 특징으로 하는 일회성 문신용 2액형 용액을 제공하여 상술한 문제의 해결을 모색하였다. 이를 통해 종래의 발명과는 달리 피부에 무해하고, 장기 저장이 가능하고, 내번짐성, 내마모성 및 내수성이 우수하며, 비누로 쉽게 지울 수 있는 동시에 노즐 막힘이 발생하지 않는 효과를 달성할 수 있다.Accordingly, the present invention provides a method for producing an ink composition comprising a first liquid comprising a solvent, a colorant and a surfactant, and a second liquid comprising a solvent and a skin-formable film former, wherein the first liquid is an ink liquid, Wherein the solvent of the first solution comprises water and the organic solvent in a weight ratio of 1: 0.01 to 1.3, and the solvent of the second solution is an organic solvent. I sought to solve the problem. As a result, unlike the prior art, it is harmless to the skin, can be stored for a long period of time, is excellent in flammability, abrasion resistance and water resistance, can be easily removed with soap, and nozzle clogging does not occur.

먼저, 상기 용매, 착색제 및 계면활성제를 포함하는 제1액을 설명한다.First, a first liquid containing the solvent, the colorant and the surfactant will be described.

상기 제1액은 잉크액이며, 상기 용매는 통상적으로 화장품에 사용되는 용매라면 제한 없이 사용할 수 있으며, 바람직하게는 물 및 유기용매일 수 있다. 한편, 상기 유기용매는 통상적으로 화장품에 사용되는 유기용매라면 제한 없이 사용할 수 있으며, 바람직하게는 에틸 알콜, n-프로필알콜, 이소프로필알콜, n-부틸알콜, sec-부틸알콜, t-부틸알콜, 이소부틸알콜, 에틸락테이트, 에틸렌글리콜, 디에틸렌글리콜, 트리에틸렌글리콜, 프로필렌글리콜, 디프로필렌글리콜, 부틸렌글리콜, 1,4-부탄디올, 1,2,4-부탄트리올, 1,5-펜탄디올, 1,6-헥산디올, 1,2-헥산디올, 1,2,6-헥산트리올, 헥실렌글리콜, 글리세롤, 글리세롤 에톡실레이트, 트리메틸롤프로판 에톡실레이트, 소디움 2-피롤리돈-5-카르복실레이트, 메틸 피롤리돈, 카프릴릴 피롤리돈, 에트리올, 에틸렌글리콜 노메틸 에테르, 에틸렌글리콜 노에틸 에테르, 디에틸렌글리콜 메틸 에테르, 디에틸렌글리콜 에틸 에테르, 트리에틸렌글리콜 노메틸 에테르, 트리에틸렌글리콜 노에틸 에테르, 디메틸 술폭사이드, 테트라메틸렌술폰, 티오글리콜 및 중량평균분자량이 150 ~ 1000인 폴리에틸렌글리콜 중에서 선택된 1종 이상일 수 있으며, 보다 바람직하게는 디에틸렌글리콜,글리세롤,폴리에틸렌글리콜, 이소프로필알콜 및 부틸렌글리콜 중에서 선택된 1종이상일 수 있으며, 더욱 바람직하게는 글레세롤, 이소프로필알콜, 폴리에틸렌글리콜 중에서 선택된 1종이상일 수 있다. 한편, 상기 용매는 물 및 유기용매를 1 : 0.01 ~ 1.3 의 중량비로, 바람직하게는 1 : 0.1 ~ 0.6 의 중량비로 포함한다. 만일 상기 물 및 유기용매의 중량비가 1 : 0.01 미만이면 휘발로 인한 노즐건조로 노즐막힘 문제가 발생할 수 있고, 물 및 유기용매의 중량비가 1 : 1.3를 초과하면 점도가 상승하여 인쇄하기 어려운 문제가 발생할 수 있다.The first liquid is an ink liquid, and the solvent is not particularly limited as long as it is a solvent commonly used in cosmetics, preferably water and organic solvents. On the other hand, the organic solvent is not limited as long as it is an organic solvent usually used in cosmetics, and preferably ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol, , Isobutyl alcohol, ethyl lactate, ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, butylene glycol, 1,4-butanediol, - pentanediol, 1,6-hexanediol, 1,2-hexanediol, 1,2,6-hexanetriol, hexyleneglycol, glycerol, glycerol ethoxylate, trimethylolpropaneethoxylate, sodium 2- Propylene glycol monomethyl ether, ethylene glycol nonyl ether, diethylene glycol methyl ether, diethylene glycol ethyl ether, triethylene glycol monomethyl ether, diethylene glycol monomethyl ether, Glycol non-methyl ether, triethylene Recurring nonyl ether, dimethyl sulfoxide, tetramethylene sulfone, thioglycol and polyethylene glycol having a weight average molecular weight of 150 to 1000, and more preferably at least one selected from the group consisting of diethylene glycol, glycerol, polyethylene glycol, isopropyl alcohol And butylene glycol, and more preferably at least one selected from the group consisting of glycerol, isopropyl alcohol, and polyethylene glycol. On the other hand, the solvent includes water and an organic solvent in a weight ratio of 1: 0.01 to 1.3, preferably 1: 0.1 to 0.6. If the weight ratio of the water and the organic solvent is less than 1: 0.01, the nozzle may be clogged due to drying of the nozzle due to volatilization. If the weight ratio of water and the organic solvent is more than 1: 1.3, Lt; / RTI >

상기 착색제는 통상적으로 화장품에 사용하는 성분이라면 제한 없이 사용할 수 있으며, 바람직하게는 안료 및 염료를 포함할 수 있다. 한편, 상기 제1액은 용매 100 중량부에 대하여 착색제를 0.5 ~ 10 중량부 포함할 수 있으며, 바람직하게는 1 ~ 9 중량부 포함할 수 있다. 만일 상기 용매 100 중량부에 대하여 착색제가 0.5 중량부 미만이면 목적하는 색상이 나타나지 않는 문제가 발생할 수 있고, 10 중량부를 포함하면 착색제가 상대적으로 과하게 포함되어 인쇄하기 어렵고, 내마모성이 좋지 않은 문제가 발생할 수 있다.The colorant can be used without limitation as long as it is a component commonly used in cosmetics, and it may preferably include pigments and dyes. Meanwhile, the first liquid may contain 0.5 to 10 parts by weight, preferably 1 to 9 parts by weight, of a coloring agent based on 100 parts by weight of the solvent. If the amount of the coloring agent is less than 0.5 parts by weight based on 100 parts by weight of the solvent, there may arise a problem that the desired color is not exhibited. If the amount of the coloring agent is 10 parts by weight, .

상기 계면활성제는 통상적으로 화장품에 사용하는 성분이라면 제한 없이 사용할 수 있으며, 바람직하게는 비이온성 계면활성제 및 이온성 계면활성제 중에서 선택된 1종 이상을 사용할 수 있고, 보다 바람직하게는 비이온성 계면활성제를 사용할 수 있으며, 더욱 바람직하게는 폴리옥시에틸렌 올레일 에테르를 사용할 수 있다. 한편, 상기 제1액은 용매 100 중량부에 대하여 계면활성제를 0.01 ~ 8 중량부, 바람직하게는 0.1 ~ 3 중량부 포함할 수 있다. 만일 상기 용매 100 중량부에 대하여 계면활성제가 0.01 중량부 미만이면 표면장력이 높아 잉크 방울 토출이 어려워 문제가 발생할 수 있고, 8 중량부를 초과하면 거품이 많이 발생하여 잉크의 연속 공급이 부족한 문제가 발생할 수 있다.The surfactant is not particularly limited as long as it is a component commonly used in cosmetics, and preferably at least one selected from a nonionic surfactant and an ionic surfactant can be used. More preferably, a nonionic surfactant is used And more preferably, polyoxyethylene oleyl ether can be used. Meanwhile, the first liquid may contain 0.01 to 8 parts by weight, preferably 0.1 to 3 parts by weight, of a surfactant per 100 parts by weight of the solvent. If the amount of the surfactant is less than 0.01 part by weight based on 100 parts by weight of the solvent, problems may arise because the surface tension is high and ink droplets are difficult to be discharged. If the amount exceeds 8 parts by weight, .

다음, 상기 용매 및 피부도포형 필름형성제를 포함하는 제2액을 설명한다.Next, the second liquid containing the solvent and the skin-application type film forming agent will be described.

상기 제2액은 잉크 고정화제이다.The second liquid is an ink fixing agent.

한편, 제2액에 포함되는 용매에 대한 설명은, 상기 제1액에 포함되는 용매에 대한 설명과 동일하여 생략하도록 한다. On the other hand, the description of the solvent contained in the second liquid is the same as the description of the solvent included in the first liquid, and is omitted.

상기 피부도포형 필름형성제는 통상적으로 잉크액을 고정할 수 있는 성분이라면 제한 없이 사용할 수 있으며, 바람직하게는 카르복시비닐폴리머, 카르복시메틸셀룰로오스, 메틸셀룰로오스, 에틸셀룰로오스, 히드록시알킬셀룰로오스, 하이드록시프로필셀룰로오스, 하이드록시프로필메틸셀룰로오스, 하이드록시 에틸 셀룰로오스, 알킬셀룰로오스, 폴리우레탄, 폴리우레탄과 아크릴레이트 공중합체, 폴리에스테르 우레탄, 폴리비닐피롤리돈, 폴리비닐아세테이트, 비닐피롤리돈-비닐아세테이트 공중합체, 폴리비닐알코올, 폴리아크릴산, 폴리아크릴산나트륨, 아크릴레이트 폴리머, 아크릴레이트 공중합체, 폴리아크릴산 부분중화물, 폴리아크릴산 전분, 카멜로스나트륨, 카르복시비닐폴리머, N-비닐아세테이트아미드, 알킬 올레핀산, 알킬 올레핀산 에스테르 공중합체, 아미드/올레핀산, 아미드/올레핀산 공중합체 또는 이들의 혼합물로부터 선택된 1종 이상일 수 있으며, 보다 바람직하게는 폴리우레탄, 폴리에스터 우레탄, 카르복시메틸셀룰로오스, 하이드록시 에틸 셀룰로오스, 폴리우레탄과 아크릴레이트 공중합체 및 폴리비닐알코올 중에서 선택된 1종 이상일 수 있으며, 더욱 바람직하게는 폴리우레탄, 폴리에스터 우레탄 및 폴리우레탄과 아크릴레이트 공중합체 중에서 선택된 1종 이상일 수 있다. 한편 상기 제2액은 용매 100 중량부에 대하여 피부도포형 필름형성제를 0.1 ~ 80 중량부, 바람직하게는 10 ~ 40 중량부 포함할 수 있다. 만일 상기 용매 100 중량부에 대하여 피부도포형 필름형성제가 0.1 중량부 미만이면 착색제를 피부에 고정하는데 문제가 발생할 수 있고, 80 중량부를 초과하면 높은 점도로 인하여 공급에 문제가 발생할 수 있다.The skin-formable film-forming agent can be used without limitation as long as it is a component capable of fixing the ink liquid, and is preferably selected from the group consisting of carboxyvinyl polymer, carboxymethyl cellulose, methyl cellulose, ethyl cellulose, hydroxyalkyl cellulose, Cellulose, hydroxypropylmethylcellulose, hydroxyethylcellulose, alkylcellulose, polyurethane, polyurethane and acrylate copolymer, polyester urethane, polyvinylpyrrolidone, polyvinylacetate, vinylpyrrolidone-vinyl acetate copolymer , Polyvinyl alcohols, polyacrylic acid, sodium polyacrylate, acrylate polymers, acrylate copolymers, polyacrylic acid partially saponified, polyacrylic starch, camelose sodium, carboxyvinyl polymer, N-vinyl acetate amide, alkyl olefinic acid, alkyl Olefinic acid It may be at least one kind selected from a terpolymer, an amide / olefinic acid, an amide / olefinic acid copolymer, or a mixture thereof, more preferably at least one selected from the group consisting of polyurethane, polyester urethane, carboxymethyl cellulose, hydroxyethyl cellulose, Acrylate copolymer and polyvinyl alcohol, and more preferably at least one selected from the group consisting of polyurethane, polyester urethane, and polyurethane and acrylate copolymer. On the other hand, the second liquid may contain 0.1 to 80 parts by weight, preferably 10 to 40 parts by weight, of the skin-spreading film-forming agent per 100 parts by weight of the solvent. If the amount of the skin-forming film-forming agent is less than 0.1 parts by weight based on 100 parts by weight of the solvent, there may arise a problem in fixing the coloring agent to the skin. If the amount is more than 80 parts by weight,

다음으로, 상기 일회성 문신용 2액형 용액을 인쇄하는 방법을 설명한다.Next, a description will be given of a method for printing the one-component two-component type solution for tattooing.

상기 일회성 문신용 2액형 용액의 인쇄방법은 (a) 잉크 고정화제를 피부에 도포하는 단계, (b) 도포한 잉크 고정화제를 건조하는 단계 및 (c) 상기 잉크 고정화제를 도포한 영역의 상부에 잉크액을 도포하는 단계를 포함한다. 이때, 상기 잉크액은 용매, 착색제 및 계면활성제를 포함하는 제 1 액이고, 상기 잉크 고정화제는 용매 및 피부도포형 필름형성제를 포함하는 제 2 액을 포함할 수 있다.The method for printing the one-time two-part solution for tattooing comprises the steps of (a) applying an ink immobilizing agent to the skin, (b) drying the applied ink immobilizing agent, and (c) And applying an ink liquid. In this case, the ink liquid is a first liquid containing a solvent, a colorant and a surfactant, and the ink immobilizing agent may include a solvent and a second liquid containing a skin-application type film forming agent.

상기 (a) 단계는 잉크 고정화제를 스프레이 방식으로 분사하거나 스포이드에 의해 떨어뜨거나 거즈 및 솜에 묻혀 피부에 접촉시키는 방법 중 적어도 하나 이상을 포함할 수 있다. 즉, 잉크 고정화제는 비접촉 방식으로서, 스프레이 용기, 스포이드를 이용하여, 잉크 고정화제를 분사시키거나 떨어뜨려 피부에 도포할 수 있으며, 접촉식 방식으로서, 거즈 또는 솜에 잉크 고정화제를 적신후 피부에 접촉시켜서 사용할 수도 있다. 더불어, 두 가지 중 한 가지 방식을 사용하거나 두 가지를 혼합하여 사용할 수도 있다.The step (a) may include at least one of a method of spraying the ink fixing agent in a spraying manner, a dropping by a syringe, or a method in which the ink is immersed in gauze and cotton to contact the skin. That is, the ink immobilizing agent is a noncontact type, and can be applied to the skin by spraying or dropping the ink immobilizing agent using a spray container or a syringe. In a contact type, after wetting the ink immobilizing agent with gauze or cotton, Or the like. In addition, you can use one or the other of the two.

상기 건조는 0.1 ~ 60 초 동안 수행할 수 있으며, 바람직하게는 1 ~ 30초 동안 수행할 수 있다. 만일 상기 건조 시간이 0.1 초 미만이면 잉크액 도포 시 잉크가 잘 고정되지 않는 문제가 발생할 수 있고, 60 초를 초과하면 잉크 고정화제가 과하게 건조되어 잉크가 흘러내리는 문제가 발생할 수 있다.The drying can be performed for 0.1 to 60 seconds, preferably for 1 to 30 seconds. If the drying time is less than 0.1 second, the ink may not be fixed properly when the ink liquid is applied. If the drying time is more than 60 seconds, the ink immobilizing agent may overdry and the ink may flow down.

한편, 상기 잉크액은 상기 잉크 고정화제를 도포한 영역에 대응하는 일부 영역에 도포될 수 있으며, 이를 통해 잉크액을 더욱 용이하게 고정할 수 있다.On the other hand, the ink liquid can be applied to a part of the area corresponding to the area to which the ink immobilizing agent is applied, whereby the ink liquid can be more easily fixed.

또한, 본 발명의 일회성 문신용 2액형 용액의 인쇄방법은 (a) 잉크액을 피부에 도포하는 단계, (b) 도포한 잉크액을 건조하는 단계 및 (c) 잉크액을 도포한 영역의 상부에 잉크 고정화제를 도포하는 단계를 포함할 수 있다. 즉, 잉크 고정화제를 피부에 도포하기 이전에 잉크액을 피부에 도포하고, 도포한 잉크액을 건조한 후에 잉크액을 도포한 영역의 상부에 잉크 고정화제를 도포할 수도 있다.(B) drying the applied ink liquid; and (c) drying the applied ink solution on the upper portion of the area to which the ink solution is applied. The method for printing a two-component, two-component solution for tattooing according to the present invention comprises the steps of And applying an ink fixing agent. That is, the ink immobilizing agent may be applied to the upper part of the area to which the ink liquid is applied after the ink liquid is applied to the skin before the ink immobilizing agent is applied to the skin, and the applied ink liquid is dried.

따라서, 상기의 잉크액으로 인쇄한 후 잉크 고정화제를 추가로 도포하게되면 인쇄된 화상에 필름이 형성되게 하여 인쇄농도와 광택의 향상과 더불어 내수성, 내마모성 등 내구성을 더욱 더 향상시킬 수 있다.Therefore, when the ink fixing agent is further applied after printing with the ink liquid, a film is formed on the printed image to improve the printing density and gloss, and further improve durability such as water resistance and abrasion resistance.

이하, 본 발명을 하기 실시예들을 통해 설명한다. 이때, 하기 실시예들은 발명을 예시하기 위하여 제시된 것일 뿐, 본 발명의 권리범위가 하기 실시예들에 의해 한정되는 것은 아니다.Hereinafter, the present invention will be described with reference to the following examples. The following examples are provided to illustrate the invention, but the scope of the present invention is not limited by the following examples.

[실시예][Example]

제조예 1 : 잉크액 제조Production Example 1: Ink Liquid Preparation

용매 100 중량부에 대하여 파란 안료(C.I. Pigment Blue 15:1, TGI) 5 중량부 및 계면활성제로 비이온성 계면활성제인 폴리옥시에틸렌 올레일 에테르를 0.8 중량부 교반기에 넣고, 300 rpm 으로 30 분 동안 교반하여 잉크 혼합액을 제조하였다. 그 후 상기 잉크 혼합액을 기공 0.45 ㎛의 필터로 여과하여 잉크액을 제조하였다. 상기 용매는 물 및 유기용매를 1 : 0.4 의 중량비로 혼합하여 사용하였으며, 상기 유기용매는 디프로필렌글리콜, 폴리에틸렌글리콜 200 및 글레세롤를 1 : 1 : 1.3 의 중량비로 혼합하여 사용하였다.5 parts by weight of a blue pigment (CI Pigment Blue 15: 1, TGI) and 0.8 part by weight of a nonionic surfactant polyoxyethylene oleyl ether as a surfactant were added to a stirrer, and the mixture was stirred at 300 rpm for 30 minutes Followed by stirring to prepare an ink mixture. Thereafter, the ink mixture was filtered through a filter having pores of 0.45 mu m to prepare an ink solution. The solvent used was a mixture of water and an organic solvent at a weight ratio of 1: 0.4. The organic solvent was a mixture of dipropylene glycol, polyethylene glycol 200, and glycerol in a weight ratio of 1: 1: 1.3.

제조예 2Production Example 2

상기 파란안료를 붉은안료(C.I. Pigment Red 5, Winchem Industrial)로 변경한 것을 제외하면 제조예 1과 동일하게 잉크액을 제조하였다.An ink solution was prepared in the same manner as in Preparation Example 1, except that the blue pigment was changed to a red pigment (CI Pigment Red 5, Winchem Industrial).

제조예 3Production Example 3

상기 파란안료를 노란안료(C.I. Pigment Yellow 1, Hangzhou Han-Color Chemical)로 변경한 것을 제외하면 제조예 1과 동일하게 잉크액을 제조하였다An ink solution was prepared in the same manner as in Production Example 1 except that the blue pigment was changed to a yellow pigment (CI Pigment Yellow 1, Hangzhou Han-Color Chemical)

제조예 4Production Example 4

용매 100 중량부에 대하여 노란염료(FD&C Yellow No 6, Flavorchem) 1 중량부 및 계면활성제로 0.6 중량부를 교반기에 넣고, 300 rpm 으로 30 분 동안 교반하여 잉크 혼합액을 제조하였다. 그 후 상기 잉크 혼합액을 기공 0.45 ㎛의 필터로 여과하여 잉크액을 제조하였다. 상기 용매는 물 및 유기용매를 1 : 0.3의 중량비로 혼합하여 사용하였으며, 상기 유기용매는 에탄올, 글리세롤 및 디에틸렌글리토를 1 : 0.5 : 1.5 의 중량비로 혼합하여 사용하였다.1 part by weight of a yellow dye (FD & C Yellow No 6, Flavorchem) and 0.6 part by weight of a surfactant were added to a stirrer and stirred at 300 rpm for 30 minutes to prepare an ink mixture solution. Thereafter, the ink mixture was filtered through a filter having pores of 0.45 mu m to prepare an ink solution. The solvent used was a mixture of water and an organic solvent at a weight ratio of 1: 0.3. The organic solvent was a mixture of ethanol, glycerol and diethylene glycol in a weight ratio of 1: 0.5: 1.5.

제조예 5Production Example 5

상기 노란염료를 붉은염료(FD&C RED No 4, Kishi Kasei)로 변경한 것을 제외하면 제조예 4과 동일하게 잉크액을 제조하였다.An ink solution was prepared in the same manner as in Production Example 4, except that the yellow dye was changed to a red dye (FD & C RED No 4, Kishi Kasei).

제조예 6Production Example 6

상기 노란염료를 파란염료(FD&C Blue No 9, Kishi Kasei)로 변경한 것을 제외하면 제조예 4과 동일하게 잉크액을 제조하였다.An ink solution was prepared in the same manner as in Production Example 4, except that the yellow dye was changed to a blue dye (FD & C Blue No. 9, Kishi Kasei).

제조예 7 : 잉크 고정화제 제조Production Example 7: Ink fixing agent preparation

용매 100 중량부에 대하여 폴리우레탄 1 중량부를 교반기에 넣고, 500rpm 으로 30 분 동안 교반하여 잉크 고정화제를 제조하였다. 상기 용매는 에탄올, 에틸렌 글리콜, 트리에틸렌글리콜을 1 : 1 : 1 의 중량비로 혼합하여 사용하였다.1 part by weight of polyurethane was added to a stirrer with respect to 100 parts by weight of the solvent and stirred at 500 rpm for 30 minutes to prepare an ink fixing agent. Ethanol, ethylene glycol, and triethylene glycol were mixed at a weight ratio of 1: 1: 1.

제조예 8Production Example 8

용매 100 중량부에 대하여 폴리에스테르 우레탄 1 중량부를 교반기에 넣고, 600 rpm 으로 30 분 동안 교반하여 잉크 고정화제를 제조하였다. 상기 용매는 이소부틸알콜, 에틸렌 글리콜, 글리세린을 1 : 0.5 : 1 의 중량비로 혼합하여 사용하였다.1 part by weight of polyester urethane with respect to 100 parts by weight of the solvent was placed in a stirrer and stirred at 600 rpm for 30 minutes to prepare an ink fixing agent. The solvent used was a mixture of isobutyl alcohol, ethylene glycol, and glycerin in a weight ratio of 1: 0.5: 1.

제조예 9Production Example 9

용매 100 중량부에 대하여 카르복시 메틸 셀룰로오스 1 중량부를 교반기에 넣고, 400 rpm 으로 30 분 동안 교반하여 잉크 고정화제를 제조하였다. 상기 유기용매는 디에틸렌글리콜, 1,6-헥산디올 및 글리세린을 1 : 1.15 : 1.3 의 중량비로 혼합하여 사용하였다.1 part by weight of carboxymethylcellulose was added to a stirrer with respect to 100 parts by weight of the solvent and stirred at 400 rpm for 30 minutes to prepare an ink fixing agent. The organic solvent used was a mixture of diethylene glycol, 1,6-hexanediol, and glycerin in a weight ratio of 1: 1.15: 1.3.

제조예 10Production Example 10

용매 100 중량부에 대하여 하이드록시 메틸 셀룰로오스 1 중량부를 교반기에 넣고, 500 rpm 으로 30 분 동안 교반하여 잉크 고정화제를 제조하였다. 상기 용매는 에탄올만을 사용하였다.One part by weight of hydroxymethylcellulose was added to a stirrer with respect to 100 parts by weight of the solvent, and the mixture was stirred at 500 rpm for 30 minutes to prepare an ink fixing agent. Only ethanol was used as the solvent.

제조예 11Production Example 11

용매 100 중량부에 대하여 폴리비닐피롤리돈 1 중량부를 교반기에 넣고, 600 rpm 으로 30 분 동안 교반하여 잉크 고정화제를 제조하였다. 상기 용매는 이소부틸알콜만을 사용하였다.One part by weight of polyvinyl pyrrolidone was added to a stirrer with respect to 100 parts by weight of the solvent, and the mixture was stirred at 600 rpm for 30 minutes to prepare an ink fixing agent. As the solvent, only isobutyl alcohol was used.

제조예 12Production Example 12

용매 100 중량부에 대하여 폴리비닐알콜 1 중량부를 교반기에 넣고, 700 rpm 으로 30 분 동안 교반하여 잉크 고정화제를 제조하였다. 상기 용매는 이소부틸알콜과 에탄올을 1:1로 혼합하여 사용하였다.One part by weight of polyvinyl alcohol relative to 100 parts by weight of the solvent was placed in a stirrer and stirred at 700 rpm for 30 minutes to prepare an ink fixing agent. The solvent was a mixture of isobutyl alcohol and ethanol in a ratio of 1: 1.

제조예 13Production Example 13

상기 파란안료를 0.2 중량부로 변경한 것을 제외하면 제조예 1과 동일하게 잉크액을 제조하였다.An ink solution was prepared in the same manner as in Preparation Example 1, except that the blue pigment was changed to 0.2 part by weight.

제조예 14Production Example 14

상기 파란안료를 8.5 중량부로 변경한 것을 제외하면 제조예 1과 동일하게 잉크액을 제조하였다.An ink solution was prepared in the same manner as in Preparation Example 1 except that the blue pigment was changed to 8.5 parts by weight.

제조예 15Production Example 15

상기 파란안료를 12 중량부로 변경한 것을 제외하면 제조예 1과 동일하게 잉크액을 제조하였다.An ink solution was prepared in the same manner as in Preparation Example 1 except that the blue pigment was changed to 12 parts by weight.

제조예 16Production Example 16

상기 폴리우레탄 0.05 중량부로 변경한 것을 제외하면 제조예 7과 동일하게 잉크액을 제조하였다.An ink solution was prepared in the same manner as in Preparation Example 7, except that the polyurethane was changed to 0.05 part by weight.

제조예 17Production Example 17

상기 폴리우레탄 7.5 중량부로 변경한 것을 제외하면 제조예 7과 동일하게 잉크액을 제조하였다.An ink solution was prepared in the same manner as in Preparation Example 7 except that 7.5 parts by weight of the polyurethane was used.

제조예 18Production Example 18

상기 폴리우레탄 12 중량부로 변경한 것을 제외하면 제조예 7과 동일하게 잉크액을 제조하였다.An ink solution was prepared in the same manner as in Preparation Example 7, except that the polyurethane was changed to 12 parts by weight.

비교제조예 1Comparative Preparation Example 1

용매 100 중량부에 대하여 파란 안료(C.I. Pigment Blue 15:1, TGI) 1 중량부, 계면활성제로 계면활성제로 비이온성 계면활성제인 폴리옥시에틸렌 올레일 에테르를 0.8 중량부 및 폴리우레탄 1 중량부를 교반기에 넣고, 300 rpm 으로 30 분 동안 교반하여 잉크 혼합액을 제조하였다. 그 후 상기 잉크 혼합액을 기공 0.45 ㎛의 필터로 여과하여 1액형 피부프린트용 잉크를 제조하였다. 상기 용매는 물 및 유기용매를 1 : 0.4 의 중량비로 혼합하여 사용하였으며, 상기 유기용매는 디프로필렌글리콜, 폴리에틸렌글리콜 200 및 글레세롤를 1 : 1 : 1.3 의 중량비로 혼합하여 사용하였다.1 part by weight of a blue pigment (CI Pigment Blue 15: 1, TGI) as a surfactant, 0.8 part by weight of a nonionic surfactant polyoxyethylene oleyl ether as a surfactant and 1 part by weight of a polyurethane were added to 100 parts by weight of a solvent, , And the mixture was stirred at 300 rpm for 30 minutes to prepare an ink mixture. Thereafter, the ink mixture was filtered through a filter having a pore size of 0.45 mu m to prepare a one-pack type skin printing ink. The solvent used was a mixture of water and an organic solvent at a weight ratio of 1: 0.4. The organic solvent was a mixture of dipropylene glycol, polyethylene glycol 200, and glycerol in a weight ratio of 1: 1: 1.3.

비교제조예 2Comparative Production Example 2

상기 파란안료를 붉은안료(C.I. Pigment Red 5, Winchem Industrial)로 변경하고, 폴리우레탄을 폴리에스터우레탄으로 변경한 것을 제외하면 비교제조예 1과 동일하게 실시하여 1액형 피부프린트용 잉크를 제조하였다.A one-pack type skin printing ink was prepared in the same manner as in Comparative Production Example 1 except that the blue pigment was changed to red pigment (CI Pigment Red 5, Winchem Industrial) and the polyurethane was changed to polyester urethane.

비교제조예 3Comparative Production Example 3

상기 파란안료를 노란안료(C.I. Pigment Yellow 1, Hangzhou Han-Color Chemical)로 변경하고, 폴리우레탄을 폴리비닐피롤리돈으로 변경한 것을 제외하면 비교제조예 1과 동일하게 실시하여 1액형 피부프린트용 잉크를 제조하였다.The procedure of Comparative Production Example 1 was repeated except that the blue pigment was changed to a yellow pigment (CI Pigment Yellow 1, Hangzhou Han-Color Chemical) and the polyurethane was changed to polyvinyl pyrrolidone. Ink.

비교제조예 4Comparative Production Example 4

용매 100 중량부에 대하여 노란 염료(FD&C Yellow No 6, Flavorchem) 1 중량부, 계면활성제로 0.6 중량부 및 하이드록시 에틸셀룰로오스 1 중량부를 교반기에 넣고, 300 rpm 으로 30 분 동안 교반하여 잉크 혼합액을 제조하였다. 그 후 상기 잉크 혼합액을 기공 0.45 ㎛의 필터로 여과하여 1액형 피부프린트용 잉크를 제조하였다. 상기 용매는 물 및 유기용매를 1 : 0.3 의 중량비로 혼합하여 사용하였으며, 상기 유기용매는 에탄올, 글리세롤 및 디에틸렌글리토를 1 : 0.5 : 1.5 의 중량비로 혼합하여 사용하였다.1 part by weight of a yellow dye (FD & C Yellow No. 6, Flavorchem), 0.6 part by weight of a surfactant and 1 part by weight of hydroxyethylcellulose were added to a stirrer and stirred at 300 rpm for 30 minutes to prepare an ink mixture Respectively. Thereafter, the ink mixture was filtered through a filter having a pore size of 0.45 mu m to prepare a one-pack type skin printing ink. The solvent used was a mixture of water and an organic solvent at a weight ratio of 1: 0.3. The organic solvent was a mixture of ethanol, glycerol and diethylene glycol in a weight ratio of 1: 0.5: 1.5.

비교제조예 5Comparative Preparation Example 5

상기 노란염료를 붉은 염료(FD&C Red No 4, Kishi Kasei)로 변경하고, 하이드록시 에틸셀룰로오스를 폴리비닐피롤리돈으로 변경한 것을 제외하면 비교제조예 4와 동일하게 실시하여 1액형 피부프린트용 잉크를 제조하였다.The same procedure as in Comparative Preparation Example 4 was carried out except that the yellow dye was changed to a red dye (FD & C Red No 4, Kishi Kasei), and hydroxyethylcellulose was changed to polyvinylpyrrolidone. .

비교제조예 6Comparative Preparation Example 6

상기 노란염료를 파란 염료(D&C Blue No.9, Kishi Kasei)로 변경하고, 하이드록시 에틸셀룰로오스를 폴리비닐알콜로 변경한 것을 제외하면 비교제조예 4와 동일하게 실시하여 1액형 피부프린트용 잉크를 제조하였다.The one-pack type skin printing ink was prepared in the same manner as in Comparative Production Example 4 except that the yellow dye was changed to a blue dye (D & C Blue No. 9, Kishi Kasei) and hydroxyethylcellulose was changed to polyvinyl alcohol. .

실험예 1 : 장기저장 안정성 및 노즐 막힘 평가Experimental Example 1: Long-term storage stability and nozzle clogging evaluation

상기 제조예 및 비교제조예에서 조성물에 대하여 하기의 항목을 측정하여, 하기 표 1에 나타내었다.The following items were measured for the compositions in the preparation examples and comparative preparation examples, and the results are shown in the following Table 1.

(1) 장기저장 안정성 평가(1) Evaluation of long-term storage stability

제조예 1 ~ 18 및 비교제조예 1 ~ 6 의 조성물에 대하여 장기저장 안정성을 평가하였다. 구체적으로 상기 피부프린트용 잉크 각각을 내열성 유리병에 100 ml씩 넣고, 입구를 밀봉하고 60℃의 항온조에 저장하였다. 이를 1개월 동안 방치한 후 바닥의 침전유무를 확인하였다.(○ ― 침전물 있음, × ― 침전물 없음)The long-term storage stability of the compositions of Production Examples 1 to 18 and Comparative Production Examples 1 to 6 was evaluated. Specifically, 100 ml of each of the skin print inks was put into a heat-resistant glass bottle, and the mouth was sealed and stored in a thermostatic chamber at 60 ° C. After standing for 1 month, the presence of sediment on the floor was confirmed (○ - sediment, × sediment)

(2) 노즐 막힘 평가(2) Evaluation of nozzle clogging

제조예 1 ~ 18 및 비교제조예 1 ~ 6 의 조성물에 에 대하여 노즐 막힘을 평가하였다. 구체적으로 상기 피부프린트용 잉크 각각을 카트리지(HP C9387, )에 각각 상온(25℃) 및 저온(-18℃)에서 2주씩 방치한 후 프린팅을 하였을 때의 노즐 막힘을 평가하였다.( ○ ― 모든 노즐에서 막힘이 관찰되지 않음, △ ― 1 ~ 5 개의 노즐에서 막힘이 관찰됨, × ― 6 개 이상의 노즐에서 막힘이 관찰됨.)Nozzle clogging was evaluated for the compositions of Production Examples 1 to 18 and Comparative Production Examples 1 to 6. Specifically, the clogging of the nozzles was evaluated when the respective inks for skin printing were left in a cartridge (HP C9387) at room temperature (25 ° C) and low temperature (-18 ° C) for 2 weeks, respectively, No clogging was observed in the nozzle, - Clogging was observed in 1 to 5 nozzles, - Clogging was observed in more than 6 nozzles.)

구분division 장기저장 안정성Long-term storage stability 노즐 막힘
(상온/저온)Nozzle clogging
(Room temperature / low temperature) 제조예1Production Example 1 ○○ ○/○○ / ○ 제조예2Production Example 2 ○○ ○/○○ / ○ 제조예3Production Example 3 ○○ ○/○○ / ○ 제조예4Production Example 4 ○○ ○/○○ / ○ 제조예5Production Example 5 ○○ ○/○○ / ○ 제조예6Production Example 6 ○○ ○/○○ / ○ 제조예7Production Example 7 ○○ ○/○○ / ○ 제조예8Production Example 8 ○○ ○/○○ / ○ 제조예9Production Example 9 ○○ ○/○○ / ○ 제조예10Production Example 10 ○○ ○/○○ / ○ 제조예11Production Example 11 ○○ ○/○○ / ○ 제조예12Production Example 12 ○○ ○/○○ / ○ 제조예13Production Example 13 ○○ ○/○○ / ○ 제조예14Production Example 14 ○○ ○/○○ / ○ 제조예15Production Example 15 ○○ ○/○○ / ○ 제조예16Production Example 16 ○○ ○/○○ / ○ 제조예17Production Example 17 ○○ ○/○○ / ○ 제조예18Production Example 18 ○○ ○/○○ / ○ 비교제조예1Comparative Preparation Example 1 ×× △/×△ / × 비교제조예2Comparative Production Example 2 ×× ×/×× / × 비교제조예3Comparative Production Example 3 ×× ×/×× / × 비교제조예4Comparative Production Example 4 ×× △/×△ / × 비교제조예5Comparative Preparation Example 5 ×× △/△△ / △ 비교제조예6Comparative Preparation Example 6 ×× ×/×× / ×

상기 표 1에서 알 수 있듯이, 2액형으로 사용하기 위하여 잉크액과 잉크 고정화제를 분리하여 제조한 제조예 1 ~ 18이, 잉크액과 잉크 고정화제를 1액형으로 제조한 비교제조예 1 ~ 6에 비하여 장기저장 안정성이 우수하였고, 상온 및 저온에서의 노즐 막힘이 전혀 나타나지 않았다.As can be seen from Table 1, Production Examples 1 to 18, which were prepared by separating an ink liquid and an ink immobilizing agent for use as a two-liquid type, were prepared in the same manner as in Comparative Production Examples 1 to 6 , And the nozzle was not clogged at room temperature or low temperature.

실시예 1Example 1

상기 제조예 1의 잉크액 및 제조예 7의 잉크 고정화제 카트리지(HP C9387)에 각각 넣고 피부전사용 프린터(SO-3, SketchOn)로 잉크 고정화제를 1.5×2.5 cm 크기의 직사각형 형태로 먼저 인쇄하고, 4초 동안 건조시킨 뒤 잉크액으로 상기 직사각형 영역의 내부에 1×2 cm 크기의 직사각형을 인쇄하였다.The ink fixing agent was firstly printed in a rectangular shape of 1.5 x 2.5 cm with the use of a printer for skin application (SO-3, SketchOn) in the ink solution of Production Example 1 and the ink fixing agent cartridge (HP C9387) Dried for 4 seconds, and then a rectangle of 1 x 2 cm in size was printed inside the rectangular area with the ink solution.

실시예 2 ~ 12 및 비교예 1 ~ 6Examples 2 to 12 and Comparative Examples 1 to 6

실시예 1과 동일하게 실시하되, 하기 표 2와 같이 잉크액 및 잉크 고정화제의 구성, 조성비 및 인쇄 순서를 변경하여 실시하였다.The composition, composition ratio, and printing order of the ink liquid and the ink immobilizing agent were changed in the same manner as in Example 1, as shown in Table 2 below.

구분division 인쇄1Print 1 인쇄2Print 2 실시예1Example 1 제조예7Production Example 7 제조예1Production Example 1 실시예2Example 2 제조예8Production Example 8 제조예2Production Example 2 실시예3Example 3 제조예9Production Example 9 제조예3Production Example 3 실시예4Example 4 제조예4Production Example 4 제조예10Production Example 10 실시예5Example 5 제조예5Production Example 5 제조예11Production Example 11 실시예6Example 6 제조예6Production Example 6 제조예12Production Example 12 실시예7Example 7 제조예7Production Example 7 제조예13Production Example 13 실시예8Example 8 제조예7Production Example 7 제조예14Production Example 14 실시예9Example 9 제조예7Production Example 7 제조예15Production Example 15 실시예10Example 10 제조예16Production Example 16 제조예1Production Example 1 실시예11Example 11 제조예17Production Example 17 제조예1Production Example 1 실시예12Example 12 제조예18Production Example 18 제조예1Production Example 1 비교예1Comparative Example 1 비교제조예1Comparative Preparation Example 1 비교예2Comparative Example 2 비교제조예2Comparative Production Example 2 비교예3Comparative Example 3 비교제조예3Comparative Production Example 3 비교예4Comparative Example 4 비교제조예4Comparative Production Example 4 비교예5Comparative Example 5 비교제조예5Comparative Preparation Example 5 비교예6Comparative Example 6 비교제조예6Comparative Preparation Example 6

실험예 2 : 내번짐성, 내마모성 및 지움성 평가Experimental Example 2: Evaluation of flammability, abrasion resistance and erasure

상기 실시예 및 비교예에 대하여 하기의 항목을 측정하여, 하기 표 3에 나타내었다.The following items were measured for the above Examples and Comparative Examples, and are shown in Table 3 below.

(1) 내번짐성 평가 (1) Evaluation of spreading property

실시예 1 ~ 12 및 비교예 1 ~ 6에 대하여 내번짐성을 평가하였다. 구체적으로 상기 최종 인쇄 30분 후 인접한 두 칼라간의 경계선을 기준으로 칼라 믹싱(color mixing)이 일어나는 도트 라인 위치를 현미경으로 측정하였다. (5 ― 경계선 전체에서 칼라 믹싱이 나타나지 않음, 4 ― 1dot 직경에 해당하는 너비에서 칼라 믹싱이 일어남, 3 ― 2dot 직경에 해당하는 너비에서 칼라 믹싱이 일어남, 2 ― 3dot 직경에 해당하는 너비에서 칼라 믹싱이 일어남, 1 ― 4dot 직경에 해당하는 너비에서 칼라 믹싱이 일어남. 상기 dot은 600 dpi 기준 시, 1dot 직경 = 100㎛) The anti-smudge properties of Examples 1 to 12 and Comparative Examples 1 to 6 were evaluated. Specifically, the dot line position at which color mixing occurs based on the boundary between two adjacent colors after 30 minutes of the final printing was measured with a microscope. (5 - no color mixing is seen across the border, color mixing occurs at a width of 4 - 1 dot diameter, color mixing takes place at a width of 3 - 2 dot diameter, 2 - color width at the width corresponding to 3dot diameter Mixing takes place, and color mixing occurs at a width corresponding to 1 - 4 dots diameter. The dot has a 1 dot diameter = 100 m at 600 dpi standard.

(2) 내마모성 평가(2) Evaluation of abrasion resistance

실시예 1 ~ 12 및 비교예 1 ~ 6에 대하여 내마모성을 평가하였다. 구체적으로 상기 최종 인쇄 5분 후 테스트기(Rub. Tester, 스케치온)로 5회 문지른 후, 문지르기 전의 면적에 대하여 남아있는 면적의 비율을 측정하였다. (○ ― 90% 초과, △ ― 70% ~ 90%, × ― 70% 미만) The abrasion resistance of each of Examples 1 to 12 and Comparative Examples 1 to 6 was evaluated. Specifically, after five minutes of the final printing, the rubbing was conducted five times with a tester (Rub. Tester, sketch-on), and the ratio of the remaining area to the area before rubbing was measured. (O - over 90%, - 70 - 90%, X - less than 70%

(3) 지움성 평가(3) Evaluation of erasure

실시예 1 ~ 12 및 비교예 1 ~ 6에 대하여 지움성을 평가하였다. 구체적으로 최종 인쇄 5분 후 10ml의 비눗물을 1 ml/s 의 속도로 모두 떨어뜨렸다. 그 후 테스트기(Rub. Tester, 스케치온)으로 5회 문지른 후, 문지르기 전의 면적에 대하여 남아있는 면적의 비율을 측정하였다. (○ ― 10% 미만, △ ― 10% ~ 30%, × ― 30% 초과) The erasability was evaluated for Examples 1 to 12 and Comparative Examples 1 to 6. Specifically, after 5 minutes of the final printing, 10 ml of soapy water was dropped at a rate of 1 ml / s. After rubbing 5 times with a tester (Rub. Tester, Sketchon), the ratio of the remaining area to the area before rubbing was measured. (○ - less than 10%, △ - 10% ~ 30%, × - more than 30%)

구분division 내번짐성Spreadability 내마모성Abrasion resistance 지움성Erasure 실시예1Example 1 55 ○○ ○○ 실시예2Example 2 55 ○○ ○○ 실시예3Example 3 55 ○○ ○○ 실시예4Example 4 55 △△ △△ 실시예5Example 5 44 ○○ △△ 실시예6Example 6 44 △△ △△ 실시예7Example 7 44 ○○ ○○ 실시예8Example 8 55 △△ ○○ 실시예9Example 9 44 ×× △△ 실시예10Example 10 44 ×× ○○ 실시예11Example 11 55 ○○ ○○ 실시예12Example 12 55 ○○ ×× 비교예1Comparative Example 1 33 △△ △△ 비교예2Comparative Example 2 22 △△ △△ 비교예3Comparative Example 3 22 ×× ×× 비교예4Comparative Example 4 33 △△ △△ 비교예5Comparative Example 5 33 ×× ×× 비교예6Comparative Example 6 22 △△ △△

상기 표 3에서 알 수 있듯이, 본 발명의 잉크액 및 잉크 고정화제의 구성, 조성비 및 인쇄 순서를 모두 만족하는 실시예 1 ~ 3이, 이를 만족하지 못하는 실시예 4 ~ 12 및 비교예 1 ~ 6에 비하여 내번짐성, 내마모성 및 지움성이 모두 우수하였다.As can be seen from the above Table 3, Examples 1 to 3 satisfying all the composition, composition ratio and printing order of the ink liquid and the ink immobilizing agent of the present invention, Examples 4 to 12 and Comparative Examples 1 to 6 , The abrasion resistance, the abrasion resistance and the erosion resistance were both excellent.

구체적으로, 제조예 7에 따른 잉크 고정화제를 도포한 후 제조예 1에 따른 잉크액을 도포한 실시예 1, 제조예 8에 따른 잉크 고정화제를 도포한 후 제조예 2에 따른 잉크액을 도포한 실시예 2 및 제조예 9에 따른 잉크 고정화제를 도포한 후 제조예 3에 따른 잉크액을 도포한 실시예 3이, 제조예 4에 따른 잉크액을 먼저 도포한 후 제조예 10에 따른 잉크 고정화제를 도포한 실시예 4에 비하여 내마모성 및 지움성이 우수하였고, 제조예 5에 따른 잉크액을 먼저 도포한 후 제조예 11에 따른 잉크 고정화제를 도포한 실시예 5에 비하여 내번짐성 및 지움성이 우수하였으며, 제조예 6에 따른 잉크액을 먼저 도포한 후 제조예 12에 따른 잉크 고정화제를 도포한 실시예 6에 비하여 내번짐성, 내마모성 및 지움성이 우수하였다.Specifically, the ink immobilizing agent according to Production Example 2 was applied, then the ink immobilizing agent according to Example 1 or 8 was applied, and the ink liquid according to Preparation Example 2 was applied Example 3 in which the ink liquid according to Production Example 3 was applied after applying the ink immobilizing agent according to Example 2 and Production Example 9 was first applied with the ink liquid according to Production Example 4, Compared to Example 4 in which an immobilizing agent was applied, the abrasion resistance and erasability were superior to those in Example 4, and in comparison with Example 5 in which the ink liquid according to Production Example 5 was applied first and then the ink immobilizing agent according to Production Example 11 was applied, And excellent in anti-fogging property, abrasion resistance and erasability in comparison with Example 6 in which the ink liquid according to Production Example 6 was first applied and then the ink fixing agent according to Production Example 12 was applied.

또한, 착색제를 1 중량부 포함하는 잉크액을 사용한 실시예 1 및 착색제를 8.5 중량부 포함하는 잉크액을 사용한 실시예 8이, 착색제를 0.2 중량부 포함하는 잉크액을 사용한 실시예 7에 비하여 색농도가 우수하여 선명한 화상을 구현하였고, 착색제를 12 중량부 포함하는 잉크액을 사용한 실시예 9에 비하여 내마모성이 우수하였다. 상기 실시예 7은 착색제의 양이 적어서 색이 잘 나타나지 않았다.Example 8 using ink solution containing 1 part by weight of a coloring agent and Example 8 using ink solution containing 8.5 parts by weight of a coloring agent were compared with Example 7 using an ink solution containing 0.2 parts by weight of a colorant, The image was clear and excellent in abrasion resistance as compared with Example 9 using an ink solution containing 12 parts by weight of a colorant. In Example 7, the amount of the colorant was small and the color did not appear well.

또한, 피부도포형 필름형성제를 1 중량부 포함하는 잉크 고정화제를 사용한 실시예 1 및 피부도포형 필름형성제를 7.5 중량부 포함하는 잉크 고정화제를 사용한 실시예 11이, 피부도포형 필름형성제를 0.05 중량부 포함하는 잉크 고정화제를 사용한 실시예 10에 비하여 내마모성 가 우수하였고, 피부도포형 필름형성제를 12 중량부 포함하는 잉크 고정화제를 사용한 실시예 12에 비하여 지움성이 우수하였다.In addition, Example 1 using an ink immobilizing agent containing 1 part by weight of a skin-applying film-forming agent and Example 11 using an ink-immobilizing agent containing 7.5 parts by weight of a skin- Was excellent in wear resistance as compared with Example 10 using an ink immobilizing agent containing 0.05 parts by weight of a coloring agent, and excellent in erasure as compared with Example 12 using an ink immobilizing agent containing 12 parts by weight of a skin coating film forming agent.

또한, 2액형으로 잉크액 및 잉크 고정화제를 포함하는 일회성 문신용 용액을 제조한 실시예 1 ~ 3이, 1액형으로 일회성 문신용 용액을 제조한 비교예 1 ~ 6에 비하여 내번짐성, 내마모성 및 지움성이 모두 우수하였다.In addition, Examples 1 to 3, in which a single-use solution for a writing solution containing an ink liquid and an ink immobilizing agent were prepared in a two-liquid type, exhibited anti-creasing properties, abrasion resistance, and erosion resistance in comparison with Comparative Examples 1 to 6 in which a single- Sex was excellent.

전술한 본 발명의 설명은 예시를 위한 것이며, 본 발명이 속하는 기술분야의 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 쉽게 변형이 가능하다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다. 예를 들어, 단일형으로 설명되어 있는 각 구성 요소는 분산되어 실시될 수도 있으며, 마찬가지로 분산된 것으로 설명되어 있는 구성 요소들도 결합된 형태로 실시될 수 있다.It will be understood by those skilled in the art that the foregoing description of the present invention is for illustrative purposes only and that those of ordinary skill in the art can readily understand that various changes and modifications may be made without departing from the spirit or essential characteristics of the present invention. will be. It is therefore to be understood that the above-described embodiments are illustrative in all aspects and not restrictive. For example, each component described as a single entity may be distributed and implemented, and components described as being distributed may also be implemented in a combined form.

본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위에 의하여 나타내어지며, 특허청구범위의 의미 및 범위 그리고 그 균등 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.The scope of the present invention is defined by the appended claims rather than the detailed description and all changes or modifications derived from the meaning and scope of the claims and their equivalents are to be construed as being included within the scope of the present invention do.

Claims (12)

용매, 착색제 및 계면활성제를 포함하는 제1액; 및
용매 및 피부도포형 필름형성제를 포함하는 제2액;을 포함하고,
상기 제1액은 잉크액이며,
상기 제2액은 잉크 고정화제이고,
상기 제1액의 용매는 물 및 유기용매를 1 : 0.01 ~ 1.3 의 중량비로 포함하며, 제2액의 용매는 유기용매인 것을 특징으로 하는 일회성 문신용 2액형 용액.A first liquid comprising a solvent, a colorant and a surfactant; And
A second liquid comprising a solvent and a skin-formable film former,
Wherein the first liquid is an ink liquid,
Wherein the second liquid is an ink immobilizing agent,
Wherein the solvent of the first liquid comprises water and the organic solvent in a weight ratio of 1: 0.01 to 1.3, and the solvent of the second liquid is an organic solvent. 제1항에 있어서,
상기 피부도포형 필름형성제는 카르복시비닐폴리머, 카르복시메틸셀룰로오스, 메틸셀룰로오스, 에틸셀룰로오스, 히드록시알킬셀룰로오스, 하이드록시프로필셀룰로오스, 하이드록시프로필메틸셀룰로오스, 하이드록시 에틸 셀룰로오스, 알킬셀룰로오스, 폴리우레탄, 폴리우레탄과 아크릴레이트 공중합체, 폴리에스테르 우레탄, 폴리비닐피롤리돈, 폴리비닐아세테이트, 비닐피롤리돈-비닐아세테이트 공중합체, 폴리비닐알코올, 폴리아크릴산, 폴리아크릴산나트륨, 아크릴레이트 폴리머, 아크릴레이트 공중합체, 폴리아크릴산 부분중화물, 폴리아크릴산 전분, 카멜로스나트륨, 카르복시비닐폴리머, N-비닐아세테이트아미드, 알킬 올레핀산, 알킬 올레핀산 에스테르 공중합체, 아미드/올레핀산, 아미드/올레핀산 공중합체 또는 이들의 혼합물로부터 선택된 1종 이상을 포함하는 것을 특징으로 하는 일회성 문신용 2액형 용액.The method according to claim 1,
The skin-spreading film-forming agent is selected from the group consisting of carboxyvinyl polymer, carboxymethylcellulose, methylcellulose, ethylcellulose, hydroxyalkylcellulose, hydroxypropylcellulose, hydroxypropylmethylcellulose, hydroxyethylcellulose, alkylcellulose, polyurethane, poly Urethane and acrylate copolymer, polyester urethane, polyvinylpyrrolidone, polyvinyl acetate, vinylpyrrolidone-vinyl acetate copolymer, polyvinyl alcohol, polyacrylic acid, sodium polyacrylate, acrylate polymer, acrylate copolymer , Polyacrylic acid partial condensate, polyacrylic acid starch, camelose sodium, carboxyvinyl polymer, N-vinyl acetate amide, alkyl olefin acid, alkyl olefin acid ester copolymer, amide / olefin acid, amide / olefin acid copolymer, From the mixture, A first one-time Tattooing two-component solution comprising the or more. 제1항에 있어서,
상기 잉크 고정화제는 용매 100 중량부에 대하여 피부도포형 필름형성제를 0.1 ~ 80 중량부 포함하는 것을 특징으로 하는 일회성 문신용 2액형 용액.The method according to claim 1,
Wherein the ink immobilizing agent comprises 0.1 to 80 parts by weight of a skin-formable film-forming agent per 100 parts by weight of the solvent. 제1항에 있어서,
상기 착색제는 안료 및 염료를 포함하고,
상기 계면활성제는 비이온성 계면활성제 및 이온성 계면활성제 중에서 선택된 1종 이상을 포함하는 것을 특징으로 하는 일회성 문신용 2액형 용액.The method according to claim 1,
Wherein the colorant comprises a pigment and a dye,
Wherein the surfactant comprises at least one selected from a nonionic surfactant and an ionic surfactant. 제1항에 있어서,
상기 잉크액은 용매 100 중량부에 대하여 착색제 0.5 ~ 10 중량부 및 계면활성제 0.01 ~ 8 중량부를 포함하는 것을 특징으로 하는 일회성 문신용 2액형 용액.The method according to claim 1,
Wherein the ink liquid comprises 0.5 to 10 parts by weight of a coloring agent and 0.01 to 8 parts by weight of a surfactant based on 100 parts by weight of the solvent. 제1항에 있어서,
상기 유기용매는 에틸 알콜, n-프로필알콜, 이소프로필알콜, n-부틸알콜, sec-부틸알콜, t-부틸알콜, 이소부틸알콜, 에틸락테이트, 에틸렌글리콜, 디에틸렌글리콜, 트리에틸렌글리콜, 프로필렌글리콜, 디프로필렌글리콜 부틸렌글리콜, 1,4-부탄디올, 1,2,4-부탄트리올, 1,5-펜탄디올, 1,6-헥산디올, 1,2-헥산디올, 1,2,6-헥산트리올, 헥실렌글리콜, 글리세롤, 글리세롤 에톡실레이트, 트리메틸롤프로판 에톡실레이트, 소디움 2-피롤리돈-5-카르복실레이트, 메틸 피롤리돈, 카프릴릴 피롤리돈, 에트리올, 에틸렌글리콜 노메틸 에테르, 에틸렌글리콜 노에틸 에테르, 디에틸렌글리콜 메틸 에테르, 디에틸렌글리콜 에틸 에테르, 트리에틸렌글리콜 노메틸 에테르, 트리에틸렌글리콜 노에틸 에테르, 디메틸 술폭사이드, 테트라메틸렌술폰, 티오글리콜 및 중량평균분자량이 150 ~ 1000인 폴리에틸렌글리콜 중에서 선택된 1종 이상을 포함하는 것을 특징으로 하는 일회성 문신용 2액형 용액.The method according to claim 1,
Wherein the organic solvent is selected from the group consisting of ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol, t-butyl alcohol, isobutyl alcohol, ethyl lactate, ethylene glycol, diethylene glycol, Propylene glycol, dipropylene glycol butylene glycol, 1,4-butanediol, 1,2,4-butanetriol, 1,5-pentanediol, 1,6-hexanediol, 1,2- , Hexanetriol, hexylene glycol, glycerol, glycerol ethoxylate, trimethylolpropaneethoxylate, sodium 2-pyrrolidone-5-carboxylate, methylpyrrolidone, caprylylpyrrolidone, Ethylene glycol monomethyl ether, ethylene glycol nonyl ether, diethylene glycol methyl ether, diethylene glycol ethyl ether, triethylene glycol nonyl ether, triethylene glycol nonyl ether, dimethyl sulfoxide, tetramethylene sulfone, thio Glycol and a weight average molecular weight of 1 Polyethylene glycol having a number average molecular weight of 50 to 1,000. (a) 잉크 고정화제를 피부에 도포하는 단계;
(b) 도포한 잉크 고정화제를 건조하는 단계; 및
(c) 상기 잉크 고정화제를 도포한 영역의 상부에 잉크액을 도포하는 단계;를 포함하되,
상기 잉크액은 용매, 착색제 및 계면활성제를 포함하는 제 1 액이고,
상기 잉크 고정화제는 용매 및 피부도포형 필름형성제를 포함하는 제 2 액인 일회성 문신용 2액형 용액의 인쇄방법.(a) applying an ink immobilizing agent to the skin;
(b) drying the applied ink immobilizing agent; And
(c) applying an ink liquid to an upper portion of the area to which the ink immobilizing agent is applied,
Wherein the ink liquid is a first liquid containing a solvent, a colorant, and a surfactant,
Wherein the ink immobilizing agent is a second solution comprising a solvent and a skin-spreading film-forming agent. 제7항에 있어서,
상기 (a) 단계는
상기 잉크 고정화제를 스프레이 방식으로 분사하거나 스포이드에 의해 떨어뜨거나 거즈 또는 솜에 묻혀 상기 피부에 접촉시키는 방법 중 적어도 하나 이상을 포함하되,
상기 잉크 고정화제는 용매 100 중량부에 대하여 피부도포형 필름형성제를 0.1 ~ 80 중량부 포함하고, 상기 제2액의 용매는 유기용매로 이루어지는 것을 특징으로 하는 일회성 문신용 2액형 용액의 인쇄방법.8. The method of claim 7,
The step (a)
A method in which the ink fixing agent is sprayed by a spraying method, dropped by a syringe, or put on a gauze or cotton to contact the skin,
Wherein the ink immobilizing agent comprises 0.1 to 80 parts by weight of a skin-spreading film forming agent per 100 parts by weight of the solvent, and the solvent of the second liquid is an organic solvent. 제7항에 있어서,
상기 (b) 단계에서,
상기 건조는 0.1 ~ 60초 동안 수행하는 것을 특징으로 하는 일회성 문신용 2액형 용액의 인쇄방법.8. The method of claim 7,
In the step (b)
Wherein the drying is performed for 0.1 to 60 seconds. 제7항에 있어서,
상기 (c) 단계에서,
상기 잉크액은 용매 100 중량부에 대하여 착색제 0.5 ~ 10 중량부 및 계면활성제 0.01 ~ 8 중량부를 포함하고,
상기 제1액의 용매는 물 및 유기용매를 1 : 0.01 ~ 1.3 의 중량비로 포함하고,
상기 착색제는 안료 및 염료를 포함하며,
상기 계면활성제는 비이온성 계면활성제 및 이온성 계면활성제 중에서 선택된 1종 이상을 포함하는 것을 특징으로 하는 일회성 문신용 2액형 용액의 인쇄방법.8. The method of claim 7,
In the step (c)
Wherein the ink liquid comprises 0.5 to 10 parts by weight of a colorant and 0.01 to 8 parts by weight of a surfactant based on 100 parts by weight of the solvent,
Wherein the solvent of the first liquid comprises water and an organic solvent in a weight ratio of 1: 0.01 to 1.3,
Wherein the colorant comprises a pigment and a dye,
Wherein the surfactant comprises at least one selected from a nonionic surfactant and an ionic surfactant. 제7항에 있어서,
상기 (c) 단계 이후에
상기 잉크액 도포액의 상부에 상기 잉크 고정화제를 재도포하는 단계를 더 포함하는 일회성 문신용 2액형 용액의 인쇄방법.8. The method of claim 7,
After the step (c)
Further comprising the step of re-coating the ink immobilizing agent on the ink liquid applying liquid. (a) 잉크액을 피부에 도포하는 단계;
(b) 도포한 잉크액을 건조하는 단계; 및
(c) 상기 잉크액을 도포한 영역의 상부에 잉크 고정화제를 도포하는 단계;를 포함하되,
상기 잉크액은 용매, 착색제 및 계면활성제를 포함하는 제 1 액이고,
상기 잉크 고정화제는 용매 및 피부도포형 필름형성제를 포함하는 제 2 액인 일회성 문신용 2액형 용액의 인쇄방법.(a) applying an ink liquid to the skin;
(b) drying the applied ink liquid; And
(c) applying an ink immobilizing agent to an upper portion of the area to which the ink liquid is applied,
Wherein the ink liquid is a first liquid containing a solvent, a colorant, and a surfactant,
Wherein the ink immobilizing agent is a second solution comprising a solvent and a skin-spreading film-forming agent.