KR20170033491A - Ink Composition for Light Guiding Pattern and Light Guide Plate and Backlight Unit using the same - Google Patents

Ink Composition for Light Guiding Pattern and Light Guide Plate and Backlight Unit using the same Download PDF

Info

Publication number
KR20170033491A
KR20170033491A KR1020150131117A KR20150131117A KR20170033491A KR 20170033491 A KR20170033491 A KR 20170033491A KR 1020150131117 A KR1020150131117 A KR 1020150131117A KR 20150131117 A KR20150131117 A KR 20150131117A KR 20170033491 A KR20170033491 A KR 20170033491A
Authority
KR
South Korea
Prior art keywords
light
light guide
guide plate
green
bead
Prior art date
Application number
KR1020150131117A
Other languages
Korean (ko)
Other versions
KR102350686B1 (en
Inventor
민주훈
배준호
고대훈
Original Assignee
엘지디스플레이 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 엘지디스플레이 주식회사 filed Critical 엘지디스플레이 주식회사
Priority to KR1020150131117A priority Critical patent/KR102350686B1/en
Publication of KR20170033491A publication Critical patent/KR20170033491A/en
Application granted granted Critical
Publication of KR102350686B1 publication Critical patent/KR102350686B1/en

Abstract

The present invention relates to an ink composition for light guiding patterns, and to a backlight unit and a light guide plate using the same. By using the ink composition for light guiding patterns containing at least one of polystyrene (PS) diffusion bead having higher refractive index than polymethyl methacrylate (PMMA) and green light conversion bead capable of converting blue light into green light, it is possible to produce high brightness backlight units and light guide plate by increasing intensity of output white light.

Description

도광패턴용 잉크 조성물 및 그를 이용한 도광판과 백라이트 유닛 {Ink Composition for Light Guiding Pattern and Light Guide Plate and Backlight Unit using the same}BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an ink composition for a light guide pattern and a light guide plate and a backlight unit using the same,

본 발명은 표시장치에 사용되는 도광패턴용 잉크 조성물 및 그를 이용한 도광판과 백라이트 유닛, 더 구체적으로는 고굴절 확산 비드와 광변환 비드를 포함하는 도광판용 잉크와 그를 사용한 백라이트 유닛용 도광판 등에 관한 것이다.The present invention relates to an ink composition for a light guide pattern used in a display device, and a light guide plate and a backlight unit using the same, and more specifically to an ink for a light guide plate including a high refractive index diffusion bead and a light conversion bead and a light guide plate for a backlight unit using the same.

정보화 사회가 발전함에 따라 화상을 표시하기 위한 표시장치에 대한 요구가 다양한 형태로 증가하고 있으며, 근래에는 액정표시장치(LCD: Liquid Crystal Display), 플라즈마표시장치(PDP: Plasma Display Panel), 유기전계발광표시장치(OLED: Organic Light Emitting Diode Display Device)와 같은 여러 가지 표시장치가 활용되고 있다.2. Description of the Related Art [0002] As an information-oriented society develops, there have been various demands for display devices for displaying images. Recently, liquid crystal displays (LCDs), plasma display panels (PDPs) Various display devices such as an OLED (Organic Light Emitting Diode Display Device) have been utilized.

이러한 표시장치 중 액정 표시장치(LCD)는 화소영역 각각을 온(on)/오프(off) 제어하기 위한 스위칭 소자인 박막 트랜지스터를 포함하는 어레이 기판과, 컬러필터 및/또는 블랙매트릭스 등을 구비한 상부기판과, 그 사이에 형성되는 액정물질층을 포함하는 표시패널과, 박막 트랜지스터를 제어하기 위한 구동부와, 표시패널로 광을 제공하는 백라이트 유닛(Back Light Unit; BLU) 등을 포함하여 구성되며, 화소 영역에 구비된 화소(Pixel; PXL) 전극 및 공통 전압(Vcom) 전극 사이에 인가되는 전계에 따라 액정층의 배열 상태가 조절되고 그에 따라 광의 투과도가 조절되어 화상이 표시되는 장치이다.Among these display devices, a liquid crystal display (LCD) has an array substrate including a thin film transistor, which is a switching element for controlling on / off each pixel region, and an array substrate including a color filter and / or a black matrix A display panel including a top substrate, a liquid crystal material layer formed therebetween, a driving unit for controlling the thin film transistor, a backlight unit (BLU) for providing light to the display panel, and the like , A pixel (PXL) electrode provided in a pixel region, and a common voltage (Vcom) electrode, and the transmittance of light is adjusted accordingly, thereby displaying an image.

이러한 액정 표시장치의 경우에는 외부에서 광을 제공하는 백라이트 장치가 있어야 하며, 이러한 백라이트 유닛은 광원과, 도광판, 반사판, 상부 시트 등의 서브 유닛들을 포함할 수 있으며, 표시장치의 측면 및 후면을 지지하기 위한 지지구조로서의 1 이상의 프레임(Frame) 또는 샤시(Chassis)를 포함할 수 있다.In the case of such a liquid crystal display device, there is a backlight unit for providing light from the outside. Such a backlight unit may include a light source, a light guide plate, a reflection plate, an upper sheet, One or more frames or a chassis as a support structure for supporting the display device.

이러한 백라이트 유닛을 구성하는 부품 중에서 도광판은 광원으로부터의 광을 표시장치 전체에 균일하게 도광시키기 위하여 사용되는 판상 부재로서, 광의 균일한 분포 등을 위하여 판상 부재의 일면 이상에 일정한 도트 패턴 형상의 도광패턴이 형성될 수 있다.Among the components constituting such a backlight unit, the light guide plate is a plate-like member used to uniformly guide light from the light source to the entire display device. The light guide plate is provided with a light guide pattern Can be formed.

이러한 도트 패턴은 도광판의 일면에 인쇄 또는 임프린팅되어 형성되며, 도트 패턴 형성을 위하여 일정한 조성물인 도광패턴용 잉크가 사용된다.Such a dot pattern is formed by printing or imprinting on one side of a light guide plate, and ink for a light guide pattern, which is a constant composition, is used for forming a dot pattern.

도광패턴은 도광판 내부로 전반사되는 광을 확산시켜 도광판 일면으로의 입사각을 작게함으로써, 광이 도광판을 벗어나 표시패널측으로 출사되는 기능을 한다.The light guiding pattern functions to diffuse the light totally reflected to the inside of the light guide plate so as to reduce the incident angle to one surface of the light guide plate, so that the light exits from the light guide plate to the display panel side.

이러한 도광패턴 제작을 위한 잉크는 도광판에 대한 부착성을 조정할 수 있는 바인더(Binder)와, 용매, 첨가제 이외에 광을 산란(확산)을 시킬 수 있는 광확산 비드 또는 광확산 입자를 포함하는 조성물일 수 있다.The ink for producing the light guide pattern may be a composition comprising a binder capable of adjusting the adhesion to the light guide plate and a light diffusion bead or light diffusion particles capable of scattering light in addition to a solvent and an additive have.

한편, 표시장치의 백라이트 유닛에 사용되는 도광판은 도광패턴의 형상 이외에도 그를 형성하는 도광패턴용 잉크의 물성에 따라 광확산 성능 등에 영향을 미치므로, 도광판의 광학적 성능을 향상시키기 위하여 도광패턴용 잉크 조성물이 여러 방면으로 개발되고 있다.On the other hand, since the light guide plate used in the backlight unit of the display device influences the light diffusion performance in addition to the shape of the light guide pattern depending on the physical properties of the ink for the light guide pattern forming the light guide plate, Are being developed in many ways.

본 발명은 이러한 점에 착안한 것으로서, 도광판의 광효율 및 휘도를 향상시킬 수 있는 도광패턴용 잉크 재료를 새롭게 제안한다.
The present invention addresses this problem and proposes a new ink material for a light guide pattern capable of improving light efficiency and luminance of a light guide plate.

이러한 배경에서, 본 발명의 목적은, 표시장치의 백라이트 유닛에 사용되는 도광판의 도광패턴용 잉크 조성물을 제공하는 것이다.In view of the foregoing, it is an object of the present invention to provide an ink composition for a light guide pattern of a light guide plate used for a backlight unit of a display device.

본 발명의 다른 목적은 고굴절율을 가지는 폴리스티렌(Poly Styrene; PS) 재료의 확산 비드(Bead)를 포함하는 도광패턴용 잉크를 이용함으로써, 광의 확산 또는 산란을 증가시켜 고휘도 구현이 가능한 도광판 및 그를 이용한 백라이트 유닛을 제공하는 것이다.Another object of the present invention is to provide a light guide plate capable of realizing high brightness by increasing diffusion or scattering of light by using an ink for a light guide pattern including a diffusion bead of a polystyrene (PS) material having a high refractive index Thereby providing a backlight unit.

본 발명의 다른 목적은 청색영역의 광을 녹색광 파장대역의 광으로 변환하는 광변환 비드를 포함하는 도광패턴용 잉크를 이용함으로써, 출력되는 백색광의 강도를 증가시켜 고휘도 구현이 가능한 도광판 및 그를 이용한 백라이트 유닛을 제공하는 것이다. Another object of the present invention is to provide a light guide plate capable of increasing intensity of output white light and realizing high luminance by using ink for light guide pattern including a light converting bead for converting light in a blue region into light in a green light wavelength band, Unit.

본 발명의 다른 목적은, 폴리스티렌(Poly Styrene; PS) 재료의 20μm 이하 크기를 가지는 확산 비드(Bead)와, 약420~470nm의 파장대역의 광을 520~560nm 파장대역의 광으로 변환하는 약20 μm 이하 크기를 가지는 광변환 비드를 약1~30중량% 함유한 도광패턴용 잉크를 이용함으로써, 출력되는 백색광의 강도를 증가시켜 고휘도 구현이 가능한 도광판 및 그를 이용한 백라이트 유닛을 제공하는 것이다.
Another object of the present invention is to provide a light emitting device having a diffusion bead having a size of 20 탆 or less of a polystyrene (PS) material and a light emitting diode having a wavelength of about 420 nm to about 470 nm, The present invention provides a light guide plate capable of increasing the intensity of white light output by using an ink for a light guide pattern containing about 1 to 30 wt% of a light converting bead having a size of not more than 1 μm and a high luminance, and a backlight unit using the same.

전술한 목적을 달성하기 위하여, 본 발명의 일실시예는, 폴리스티렌(Poly Styrene; PS) 확산비드 1~30중량%와, 청색계열 파장대역의 광을 흡수하여 녹색계열 파장대역의 광을 방출하는 녹색 광변환 비드 1~30중량%와, 바인더로서의 아크릴레이트 수지 20~25중량%, 및 용제 45~55중량%를 포함하는 도광패턴용 잉크 조성물을 제공한다.In order to achieve the above object, an embodiment of the present invention provides a light emitting device comprising: 1 to 30% by weight of a polystyrene (PS) diffusion bead; and a light emitting layer that emits light in a green wavelength band by absorbing light in a blue wavelength band 1 to 30% by weight of green light converting beads, 20 to 25% by weight of an acrylate resin as a binder, and 45 to 55% by weight of a solvent.

본 발명의 다른 실시예는 표시장치용 백라이트 유닛에 사용되는 도광판으로서, 상기 도광판의 일면에는 다수의 도광패턴이 배치되며, 상기 도광패턴은 폴리스티렌(Poly Styrene; PS) 확산비드 1~30중량%과, 청색계열 파장대역의 광을 흡수하여 녹색계열 파장대역의 광을 방출하는 녹색 광변환 비드 1~30중량%과, 바인더로서의 아크릴레이트 수지 20~25중량%과, 용제 45~55중량%를 포함하는 잉크 조성물로 구성되는 백라이트 유닛용 도광판을 제공한다.Another embodiment of the present invention is a light guide plate for use in a backlight unit for a display device, wherein a plurality of light guide patterns are disposed on one side of the light guide plate, the light guide pattern comprises 1 to 30 wt% of polystyrene (PS) 1 to 30% by weight of a green light-converting bead which absorbs light in a blue-based wavelength band and emits light in a green-based wavelength band, 20 to 25% by weight of an acrylate resin as a binder, and 45 to 55% A light guide plate for a backlight unit is provided.

본 발명의 또다른 실시예에 의하면, 광원부와; 상기 광원부로부터의 광을 확산하기 위하여 폴리스티렌(Poly Styrene; PS) 확산비드 1~30중량%과, 청색계열 파장대역의 광을 흡수하여 녹색계열 파장대역의 광을 방출하는 녹색 광변환 비드 1~30중량%과, 바인더로서의 아크릴레이트 수지 20~25중량%과, 용제 45~55중량%를 포함하는 잉크 조성물로 구성된 다수의 도광패턴을 일면에 포함하는 도광판과; 상기 도광판 하부에 배치되어 광을 표시패널측으로 반사하는 반사판;을 포함하는 표시장치용 백라이트 유닛을 제공한다.
According to another embodiment of the present invention, there is provided a light source device comprising: a light source; 1 to 30% by weight of polystyrene (PS) diffusion beads and green light converting beads 1 to 30 for absorbing light of a blue series wavelength band and emitting light of a green series wavelength band for diffusing light from the light source A light guide plate including a plurality of light guide patterns on one surface, the light guide plate being made of an ink composition comprising 20 to 25% by weight of an acrylate resin as a binder and 45 to 55% by weight of a solvent; And a reflective plate disposed under the light guide plate and reflecting the light toward the display panel.

아래에서 설명할 본 발명의 실시예에 의하면, 고굴절율을 가지는 폴리스티렌(Poly Styrene; PS) 재료의 확산 비드(Bead)를 포함하는 도광패턴용 잉크를 이용함으로써, 광의 확산 또는 산란을 증가시켜 도광판의 고휘도 구현이 가능한 효과가 있다. According to the embodiment of the present invention to be described below, diffusion or scattering of light is increased by using ink for a light guide pattern including a diffusion bead of a polystyrene (PS) material having a high refractive index, There is an effect that a high brightness can be realized.

또한, 청색영역의 광을 녹색광 파장대역의 광으로 변환하는 광변환 비드를 포함하는 도광패턴용 잉크를 이용함으로써, 출력되는 백색광의 강도를 증가시켜 도광판 및 백라이트 유닛의 고휘도 구현이 가능하다는 효과가 있다.Further, by using the ink for the light-guide pattern including the light-converting bead for converting the light in the blue region into light in the green light wavelength band, there is an effect that the intensity of the outputted white light is increased and high brightness of the light guide plate and the backlight unit can be realized .

또한, 도광패턴용 잉크에 포함되는 폴리스티렌(Poly Styrene; PS) 확산비드 및 광변환 비드의 크기 및 조성비를 최적화함으로써, 도광패턴의 코팅 신뢰성 및 색재현 등에 영향을 최소화하면서도 도광판 및 그를 이용한 백라이트 유닛이 기존에 비하여 약30% 이상 휘도를 증가시킬 수 있는 효과가 있다. Further, by optimizing the size and the composition ratio of the polystyrene (PS) diffusion beads and the photoconversion beads contained in the inks for the light guide pattern, the light guide plate and the backlight unit using the light guide plate are minimized while minimizing the coating reliability and color reproduction of the light guide pattern. It is possible to increase the luminance by about 30% or more as compared with the conventional one.

도 1은 본 발명이 적용될 수 있는 표시장치의 입광부측 단면도를 도시한다.
도 2는 일반적인 도트형 도광패턴을 가지는 도광판의 평면 및 단면 형상과, 그러한 도광패턴에 따른 광분산 효과를 설명하기 위한 도면이다.
도 3은 본 발명의 실시예에 의한 도광패턴용 잉크에 포함된 비드가 표시된 도광패턴의 확대 단면도와, PS 확산 비드 및 녹색 광변환 비드의 크기를 표시하는 도면이다.
도 4는 본 발명의 실시예에 의한 잉크로 형성된 도광패턴을 가지는 도광판 및 그를 포함하는 백라이트 유닛의 확대 단면도와, 기존의 도광판와의 휘도 비교 실험 결과를 도시한다.
도 5는 본 발명의 실시예에 의한 잉크에 포함된 PS 확산 비드에 의한 광경로와, 휘도 향상 원리 및 그 실험결과를 도시한다.
도 6은 일반적인 광원의 광속(Flux)와 색매칭 함수(Color Matching Function; y)에 따른 휘도(Y) 산출 원리를 도시한다.
도 7은 본 발명의 실시예에 의한 잉크에 포함된 녹색 광변환 비드에 의한 휘도 향상 원리를 도시하는 도면이다.Fig. 1 shows a cross-sectional view of a light-incoming portion side of a display device to which the present invention can be applied.
Fig. 2 is a diagram for explaining the planar and cross-sectional shapes of a light guide plate having a general dot-type light guide pattern and the light dispersion effect according to such light guide patterns.
FIG. 3 is an enlarged cross-sectional view of a light guide pattern in which beads included in ink for a light guide pattern according to an embodiment of the present invention are displayed, and shows the sizes of PS diffusion beads and green light conversion beads.
4 is an enlarged cross-sectional view of a light guide plate having a light guide pattern formed of ink according to an embodiment of the present invention and a backlight unit including the light guide plate, and FIG. 4 shows a result of brightness comparison with a conventional light guide plate.
FIG. 5 shows the optical path, the brightness enhancement principle, and the experimental result of the PS diffusion beads included in the ink according to the embodiment of the present invention.
FIG. 6 shows the principle of calculating the luminance (Y) according to the flux of a general light source and a color matching function (y).
7 is a diagram showing a principle of brightness enhancement by green light converting beads included in ink according to an embodiment of the present invention.

이하, 본 발명의 일부 실시예들을 예시적인 도면을 참조하여 상세하게 설명한다. 각 도면의 구성요소들에 참조부호를 부가함에 있어서, 동일한 구성요소들에 대해서는 비록 다른 도면상에 표시되더라도 가능한 한 동일한 부호를 가질 수 있다. 또한, 본 발명을 설명함에 있어, 관련된 공지 구성 또는 기능에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명은 생략할 수 있다.Hereinafter, some embodiments of the present invention will be described in detail with reference to exemplary drawings. In the drawings, like reference numerals are used to denote like elements throughout the drawings, even if they are shown on different drawings. In the following description of the present invention, a detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present invention rather unclear.

또한, 본 발명의 구성 요소를 설명하는 데 있어서, 제 1, 제 2, A, B, (a), (b) 등의 용어를 사용할 수 있다. 이러한 용어는 그 구성 요소를 다른 구성 요소와 구별하기 위한 것일 뿐, 그 용어에 의해 해당 구성 요소의 본질, 차례, 순서 또는 개수 등이 한정되지 않는다. 어떤 구성 요소가 다른 구성요소에 "연결", "결합" 또는 "접속"된다고 기재된 경우, 그 구성 요소는 그 다른 구성요소에 직접적으로 연결되거나 또는 접속될 수 있지만, 각 구성 요소 사이에 다른 구성 요소가 "개재"되거나, 각 구성 요소가 다른 구성 요소를 통해 "연결", "결합" 또는 "접속"될 수도 있다고 이해되어야 할 것이다.In describing the components of the present invention, terms such as first, second, A, B, (a), and (b) may be used. These terms are intended to distinguish the components from other components, and the terms do not limit the nature, order, order, or number of the components. When a component is described as being "connected", "coupled", or "connected" to another component, the component may be directly connected or connected to the other component, Quot; intervening "or that each component may be" connected, "" coupled, "or " connected" through other components.

도 1은 본 발명이 적용될 수 있는 표시장치의 입광부측 단면도를 도시한다1 shows a cross-sectional view of a light-incoming portion side of a display device to which the present invention can be applied

본 발명이 적용될 수 있는 표시장치는 액정 표시패널 등의 표시패널(140)과 그 하부에 배치되어 표시패널에 광을 조사하는 백라이트 유닛(120)을 포함하며, 백라이트 유닛(120)을 지지하고 표시장치의 후면 전체에 걸쳐 연장되는 금속 또는 플라스틱 재질의 커버 버텀(Cover Bottom; 110)을 포함할 수 있다.A display device to which the present invention can be applied includes a display panel 140 such as a liquid crystal display panel and a backlight unit 120 disposed below the display panel 140 to irradiate light to the display panel, And a cover bottom 110 of metal or plastic that extends across the entire rear surface of the apparatus.

또한, 표시장치는 커버 버텀과 고정되어 백라이트 유닛(120)과 표시패널(140)을 연결하는 구조인 플라스틱 재질의 가이드 패널(Guide Panel; 130)이 추가로 구비될 수 있으며, 가이드 패널(130)의 상면 일부에는 양면 테이프가 부착되고 그 상부에 표시패널(140)이 배치됨으로써 표시패널이 고정 장착될 수 있다.The display device may further include a guide panel 130 made of a plastic material that is fixed to the cover bottom and connects the backlight unit 120 and the display panel 140. The guide panel 130 may further include a light- A double-sided tape is attached to a part of an upper surface of the display panel 140, and a display panel 140 is disposed on the upper surface thereof.

또한, 표시장치는 최외곽에 배치된 커버 버텀 및 가이드 패널의 측면부를 덮고 표시패널의 전면 일부까지 절곡 연장되어 표시패널의 전면 가장자리를 보호하는 케이스 탑(Case Top; 150)이 추가로 포함될 수 있다.Further, the display device may further include a case top 150 covering the cover bottom disposed at the outermost portion and the side surface portion of the guide panel and extending to a part of the front surface of the display panel to protect the front edge of the display panel .

이러한 케이스 탑(150)은 표시장치의 측면 부분을 둘러싸서 표시패널(140)의 전방부 일부 영역까지 확장됨으로써 표시패널을 보호함과 동시에 커버 버텀 후방에 배치되는 표시장치 구동을 위한 인쇄회로기판(PCB)인 시스템 보드부를 표시패널과 연결하기 위한 연결 회로인 칩-온-필름(Chip-On-Film; COF) 회로부를 보호하는 기능 등을 수행한다.The case top 150 covers the side surface of the display device 140 to extend to a part of the front portion of the display panel 140 to protect the display panel, On-film (COF) circuit part, which is a connection circuit for connecting the system board part, which is a PCB, with the display panel.

표시패널(140)은 액정 표시패널인 경우에는 다시 다수의 게이트 라인과 데이터 라인 및 그 교차 영역에 정의되는 픽셀(Pixel)과, 각 픽셀에서의 광투과도를 조절하기 위한 스위칭 소자인 박막 트랜지스터를 포함하는 어레이 기판과, 컬러필터 및/또는 블랙매트릭스 등을 구비한 상부기판과, 그 사이에 형성되는 액정물질층을 포함하여 구성될 수 있다.In the case of a liquid crystal display panel, the display panel 140 includes a plurality of gate lines, a data line, a pixel defined in the intersecting region, and a thin film transistor serving as a switching element for adjusting light transmittance in each pixel An upper substrate provided with a color filter and / or a black matrix, and a liquid crystal material layer formed therebetween.

또한, 표시장치는 각각 표시패널(140 )에 광을 제공하기 위한 백라이트 유닛(120 )을 포함하며, 백라이트 유닛은 광원의 배치 및 광의 전달 형태에 따라서 엣지형(Edge-Type) 또는 직하형(Direct-Type) 등으로 구분될 수 있다.The display devices each include a backlight unit 120 for providing light to the display panel 140. The backlight unit may be an edge-type or a direct-type, depending on the arrangement of the light sources and the transmission mode of light. -Type).

도 1에 도시된 백라이트 유닛은 엣지형 백라이트 유닛으로서, LED 등의 광원(128)과 광원을 고정하기 위한 홀더 및 광원 구동 회로 등을 포함하는 광원 모듈(127)과, 광을 패널 영역 전체로 확산시키기 위한 도광판(124; Light Guide Plate)과, 빛을 표시패널 방향으로 반사하기 위한 반사판(122)과, 도광판 상부에 배치되어 휘도 향상, 광의 확산 및 보호 등의 용도로 배치되는 1 이상의 광학필름 또는 시트(126) 등과 같은 서브 유닛들을 포함할 수 있다.The backlight unit shown in Fig. 1 is an edge-type backlight unit, which includes a light source module 127 including a light source 128 such as an LED, a holder for fixing the light source and a light source driving circuit, A light guide plate 124 (light guide plate) for reflecting the light toward the display panel, a reflection plate 122 for reflecting light in the direction of the display panel, at least one optical film disposed above the light guide plate for the purpose of brightness enhancement, Such as sheet 126, and the like.

이러한 표시장치는 표시패널과 표시패널을 구동하기 위한 구동부를 포함하는 액정 모듈(Liquid Crystal Module; LCM)과 같은 협의의 표시장치는 물론, 그러한 LCM을 포함하는 완제품인 노트북 컴퓨터, 텔레비전, 컴퓨터 모니터, 스마트폰 또는 전자패드와 같은 모바일 전자장치 등과 같은 세트 전자 장치 또는 세트 장치까지도 포함하는 개념이다.Such a display device is not limited to a display device such as a liquid crystal module (LCM) including a display panel and a driving unit for driving the display panel, but also a notebook computer, a television, a computer monitor, A set electronic device or set device such as a mobile electronic device such as a smart phone or an electronic pad.

즉, 본 명세서에서의 표시장치는 LCM과 같은 협의의 디스플레이 장치는 물론, 그를 포함하는 응용제품인 세트 장치까지 포함하는 의미로 사용한다.That is, the display device in this specification is used to mean not only a conferring display device such as LCM but also a set device which is an application including the display device.

한편, 표시장치에 사용되는 백라이트 유닛의 구성요소 중에서 도광판(124)은 광원으로부터의 광을 표시장치 전체 면적으로 고르게 전파시키는 기능을 하는 평판 부재로서, 광의 전파나 표시패널로의 광의 집광 등을 위하여 도광판의 양면 중 하나 이상에는 특정한 도광패턴이 형성될 수 있다.On the other hand, among the components of the backlight unit used in the display device, the light guide plate 124 is a flat plate member that functions to uniformly spread the light from the light source over the entire area of the display device. In order to propagate light, A specific light guide pattern may be formed on at least one of both surfaces of the light guide plate.

이러한 도광패턴은 표시패널측으로 출사되는 광의 집광성을 향상시키거나 광이 표시패널 전체로 균일하게 전파되도록 하는 것으로서, 원형 등의 도트패턴이나, 특정한 단면 형상을 가지면서 일방향으로 길게 형성되는 단면 패턴 등을 포함할 수 있다.Such a light guiding pattern enhances the light collecting property of light emitted to the display panel side or uniformly propagates the light to the entire display panel. The light guiding pattern may be a dot pattern such as a circle or a cross section pattern having a specific cross- . ≪ / RTI >

도 2는 일반적인 도트형 도광패턴을 가지는 도광판의 평면 및 단면 형상과, 그러한 도광패턴에 따른 광분산 효과를 설명하기 위한 도면이다.Fig. 2 is a diagram for explaining the planar and cross-sectional shapes of a light guide plate having a general dot-type light guide pattern and the light dispersion effect according to such light guide patterns.

도 2에서와 같이, 백라이트 유닛에 포함된 도광판(200)의 일면, 더 구체적으로 반사판에 접하는 면에는 도 2의 (a)와 같이 수백 μm 크기를 가지는 원형 도트 패턴(210)이 형성되어 있다.As shown in FIG. 2, a circular dot pattern 210 having a size of several hundreds of micrometers is formed on one surface of the light guide plate 200 included in the backlight unit, more specifically, on a surface contacting the reflection plate, as shown in FIG.

이러한 도트 패턴(210)은 도광판 일면 전체에 걸쳐 일정한 분포방식에 따라서 분포되며, 인쇄 타입 또는 임프린팅 방식에 의하여 형성된다.The dot pattern 210 is distributed according to a uniform distribution method over the entire surface of the light guide plate, and is formed by a printing type or imprinting method.

이러한 도트 패턴(210)은 도광판(200)이 사출 또는 압출된 이후에 일정한 조성물로 구성된 잉크를 이용하여 도광판의 일면에 인쇄 또는 임프린팅된다.The dot pattern 210 is printed or imprinted on one side of the light guide plate using ink composed of a certain composition after the light guide plate 200 is injected or extruded.

이와 같이, 도광패턴 또는 도트패턴(210)을 형성하기 위하여 사용되는 잉크를 도광패턴용 잉크 조성물이라 정의할 수 있으며, 도광패턴용 잉크 조성물은 인쇄 도막막을 형성시킴과 동시에 도광판에 대한 부착성을 조정할 수 있는 아크릴레이트기를 가지는 아크릴 공중합체와, 광을 산란(확산)을 시킬 수 있는 폴리메타아크릴레이트(polymethyl methacrylate:PMMA) 비드와, 잉크의 점도 및 실크스크린 작업성을 조정하기 위한 용매 또는 용제 등을 일정한 중량 %에 따라 포함하여 구성될 수 있다.As described above, the ink used for forming the light guide pattern or the dot pattern 210 can be defined as an ink composition for a light guide pattern, and the ink composition for a light guide pattern can form a printed film film and adjust the adhesion to the light guide plate A polymethyl methacrylate (PMMA) bead capable of scattering light, a solvent or a solvent for adjusting viscosity and silk screen workability of the ink, and the like Based on a certain weight%.

예를 들면, 일반적인 도광패턴용 잉크 조성물의 일 예로서, 폴리메타아크릴레이트(polymethyl methacrylate: PMMA) 비드 약25~35 wt%(중량%), 바인더로서의 변형 아크릴 수지(Modified Acrylate) 약 20~25wt%, 용매(Cellusolve)로서의 디아베이직 에스터(Diabasic Ester) 약45~55wt%, 첨가제 약 0.5~1.0wt% 등을 포함하여 구성될 수 있다.For example, about 25 to 35 wt% (wt%) of polymethyl methacrylate (PMMA) beads and about 20 to 25 wt% of modified acrylate resin as a binder About 45 to 55 wt% of a diabasic ester as a solvent (Cellusolve), about 0.5 to 1.0 wt% of an additive, and the like.

이러한 잉크 조성물로 도광판의 일면에 형성되는 도광패턴(210)은 광원으로부터 전달되어 도광판 내부에서 전반사되는 광 중 일부를 산란 또는 굴절시켜 전반사되지 않고 도광판 외부로 출사시키는 기능을 한다.The light guide pattern 210 formed on one surface of the light guide plate with the ink composition functions to scatter or refract a part of the light transmitted from the light source and totally reflected within the light guide plate to the outside of the light guide plate without being totally reflected.

즉, 도 2의 (b)와 같이, 광원으로부터의 광(L) 중 도광패턴(210)에서 굴절된 제1굴절광(L1')이 42도 이하의 입사각 θ로 도광판의 경계면으로 입사되고, 결과적으로 출광각 θ'로 도광판 외부로 출사되어 백라이트광으로 사용되는 것이다.2B, the first refracted light L1 'refracted in the light guide pattern 210 among the light L from the light source is incident on the boundary plane of the light guide plate at an incident angle? Of 42 degrees or less, As a result, the light is emitted to the outside of the light guide plate at the light output angle &thetas; 'and used as backlight.

본 명세서에서 도광판 표면을 벗어나는 출사광의 출광각은 도광판의 법선방향과 출사광이 이루는 각도로 정의한다.In this specification, the outgoing angle of outgoing light deviated from the surface of the light guide plate is defined as the angle between the normal direction of the light guide plate and the outgoing light.

더 구체적으로 설명하면, 도 2의 (b)와 같이, LED로부터의 광 중 일부(L1)가 위와 같은 잉크 조성물로 형성된 도광패턴(210)으로 입사되며, 도광패턴으로 입사된 광은 도광패턴에 포함된 PMMA 확산 비드(212)에 의하여 확산된다.More specifically, as shown in FIG. 2B, a part (L1) of the light from the LED is incident on the light guide pattern 210 formed of the ink composition as described above, and the light incident on the light guide pattern is incident on the light guide pattern Is diffused by the included PMMA diffusion beads 212.

PMMA 확산 비드(212)에 의해 확산된 광 중 일부광(L1')은 도광판의 타측면을 향하며, 이 때 도광판의 법선 기준으로 42도 이하의 입사각(θ)으로 도광판 상면에 입사되는 광은 도광판 내부로 전반사되지 않고, 입사각보다 큰 출광각을 가지면서 도광판 외부로 출사(L1")하여 백라이트 광원으로 사용된다.The light that is incident on the upper surface of the light guide plate at an incidence angle (?) Of 42 degrees or less with respect to the normal line of the light guide plate is transmitted through the light guide plate (L1 ") to the outside of the light guide plate with an exit angle larger than the incident angle, and is used as a backlight light source.

한편, LED로부터의 광 중에서 도광패턴으로 향하지 않는 광(L2)은 도광판의 일면에서 전반사되어 도광판 내부에서 진행하게 된다. On the other hand, the light L2 not directed to the light guide pattern among the light from the LED is totally reflected on one surface of the light guide plate and proceeds inside the light guide plate.

이와 같이, 도광패턴 형성에 사용된 잉크에는 일정한 굴절율을 가지는 확산 비드가 사용되며, 이러한 확산비드에 의하여 전반사되던 광을 확산/산란시켜 전반사를 이기고 외부로 출사되는 것이다.As described above, a diffusion bead having a constant refractive index is used for the ink used for forming the light guide pattern, and the light totally diffused / scattered by the diffusion beads is deflected by total diffusion to be emitted to the outside.

지금까지 도광패턴용 잉크 조성물에 포함되는 확산 비드 또는 확산 입자의 재료로는 도광판과 동등한 재료인 폴리메타아크릴레이트(polymethyl methacrylate: PMMA)가 사용되었다.Up to now, polymethyl methacrylate (PMMA), which is a material equivalent to a light guide plate, has been used as the material of the diffusion beads or diffusion particles contained in the ink composition for a light guide pattern.

이에 본 발명의 실시예에서는 도광패턴용 잉크 조성물에 포함되는 확산 비드의 재료로서, 기존의 PMMA 보다 굴절율이 더 큰 폴리스티렌(Poly Styrene; PS)를 사용함으로써, 확산 비드에서의 광확산 성능을 향상시켜 결과적으로 고휘도의 도광판을 제공할 수 있도록 한다.Therefore, in the embodiment of the present invention, by using polystyrene (PS) having a refractive index larger than that of the existing PMMA as the material of the diffusion beads contained in the ink composition for the light guide pattern, the light diffusion performance in the diffusion beads is improved As a result, it is possible to provide a high-brightness light guide plate.

또한, 일반적으로 광휘도는 파장대별 광원의 광속(Flux; C(λ))과 색매칭 함수(Color Matching Function;

Figure pat00001
)로 결정되는데, 일반적으로 백색광원의 광속은 녹색광에서 아주 약한 반면, 녹색광인 경우 색매칭 함수(Color Matching Function;
Figure pat00002
) 값이 가장 큰점을 고려하여, 결과적으로 본 발명에서는 청색 주변의 광을 흡수하여 녹색광 대역의 광을 출사하는 녹색 광변환 비드를 도광패턴용 잉크에 포함시킴으로써 최종적인 도광판 휘도를 향상시킬 수 있는 기술을 제안한다.In general, the luminous intensity is a luminous flux (C (λ)) of a light source according to a wavelength band and a color matching function (color matching function;
Figure pat00001
In general, the light flux of the white light source is very weak in the green light, while in the case of the green light, the color matching function (Color Matching Function) is used.
Figure pat00002
As a result, in the present invention, by incorporating a green light-converting bead that absorbs light around the blue color and emits light in the green light band into the ink for the light-guide pattern, the final light-guide plate luminance can be improved .

도 3은 본 발명의 실시예에 의한 도광패턴용 잉크에 포함된 비드가 표시된 도광패턴의 확대 단면도와, PS 확산 비드 및 녹색 광변환 비드의 크기를 표시하는 도면이다.FIG. 3 is an enlarged cross-sectional view of a light guide pattern in which beads included in ink for a light guide pattern according to an embodiment of the present invention are displayed, and shows the sizes of PS diffusion beads and green light conversion beads.

도 4는 본 발명의 실시예에 의한 잉크로 형성된 도광패턴을 가지는 도광판 및 그를 포함하는 백라이트 유닛의 확대 단면도와, 기존의 도광판와의 휘도 비교 실험 결과를 도시한다.4 is an enlarged cross-sectional view of a light guide plate having a light guide pattern formed of ink according to an embodiment of the present invention and a backlight unit including the light guide plate, and FIG. 4 shows a result of brightness comparison with a conventional light guide plate.

도 3 및 도 4에 도시한 바와 같이, 본 발명의 실시예에 의한 도광패턴용 잉크 조성물은 약1.59 이상의 광굴절율을 가지는 폴리스티렌(Poly Styrene; PS) 확산비드와, 청색계열 파장대역의 광을 흡수하여 녹색계열 파장대역의 광을 방출하는 녹색 광변환 비드를 포함하여 구성된다.3 and 4, the ink composition for a light-guiding pattern according to an embodiment of the present invention includes a polystyrene (PS) diffusion bead having a light refractive index of about 1.59 or more, and a light- And a green light converting bead for emitting light of a green system wavelength band.

더 구체적으로는, 폴리스티렌(Poly Styrene; PS) 확산비드 1~30중량%와, 청색계열 파장대역의 광을 흡수하여 녹색계열 파장대역의 광을 방출하는 녹색 광변환 비드 1~30중량%와, 바인더로서의 아크릴레이트 수지 20~25중량%와, 용제 45~55중량% 등으로 구성되는 도광패턴용 잉크 조성물을 제공한다.More specifically, it comprises 1 to 30% by weight of polystyrene (PS) diffusion beads, 1 to 30% by weight of green photoconversion beads which absorb light in the blue wavelength band and emit light in the green wavelength band, 20 to 25% by weight of an acrylate resin as a binder, 45 to 55% by weight of a solvent, and the like.

본 실시예에 사용되는 폴리스티렌(PS) 확산 비드를 구성하는 폴리스티렌 스티렌의 라디칼 중합으로 얻어지는 비결정성의 고분자 물질로서, 무색 투명한 열가소성 수지를 의미한다.Means a non-crystalline polymeric material obtained by radical polymerization of polystyrene styrene constituting the polystyrene (PS) diffusion beads used in the present embodiment, which means a colorless transparent thermoplastic resin.

이러한 폴리스티렌은 스티롤 수지라고 표현될 수도 있으며, 끓는점이 약145℃로서 비교적 낮지만, 약품에 잘 침식되지 않으며, 전기 절연성을 가지는 특성이 있다. Such polystyrene may be expressed as a styrol resin and has a boiling point of about 145 캜, which is comparatively low, but is not eroded well by chemicals and has electrical insulating properties.

특히, 본 실시예에 사용되는 폴리스티렌 수지는 플라스틱 중에서 가장 높은 편에 속하는 약1.59의 광굴절율을 가지므로, 후술할 바와 같이, 도광패턴용 잉크로 사용된 경우 도광패턴에서의 광확산 및 광산란 특성을 향상시켜서 결과적으로 도광판의 고휘도에 기여할 수 있다.In particular, since the polystyrene resin used in this embodiment has a light refractive index of about 1.59, which belongs to the highest part of the plastic, when used as an ink for a light guide pattern, light diffusion and light scattering characteristics Thereby contributing to the high luminance of the light guide plate as a result.

이와 같이, 도광패턴용 잉크 조성물의 확산비드로서 기존의 PMMA 비드 대신 폴리스티렌(PS) 확산비드를 사용하게 되면, PS 재료의 고굴절율 특성으로 인하여 PMMA 비드에 비하여 광확산 및 광산란 특성이 증가되고, 결과적으로 도광패턴이 더 많은 광을 전반사로부터 이탈시켜 도광판 외부로 출사시켜 고휘도 도광판을 구현할 수 있게 된다.When the polystyrene (PS) diffusion beads are used instead of the conventional PMMA beads as the diffusion beads of the ink composition for the light guide pattern, the light diffusing and light scattering characteristics are increased as compared with the PMMA beads due to the high refractive index properties of the PS material, The light having a larger light-guiding pattern is emitted from the total reflection to the outside of the light guide plate, thereby realizing a high-luminance light guide plate.

이와 같은 PS 확산 비드를 사용한 경우의 효과에 대해서는, 아래에서 도 5를 참고로 더 상세하게 설명한다.The effect of using such a PS diffusion bead will be described in more detail below with reference to FIG.

한편, 본 실시예에 의하면, 폴리스티렌 재료료 구성되는 PS 확산비드(312)는 약 1~20μm의 크기(d1)를 가지는 것이 바람직하다. On the other hand, according to the present embodiment, the PS diffusion beads 312 constituting the polystyrene material preferably have a size (d1) of about 1 to 20 μm.

PS 확산 비드(312)의 크기가 1μm 이하인 경우에는 도광패턴의 충분한 광확산 성능을 확보할 수 없고, PS 확산 비드의 크기가 20μm 이상인 경우에는 잉크가 도광판에 흡착되는 코팅성능이 떨어질 뿐 아니라, 확산비드가 일정한 입자로서 시인될 우려가 있고, 인쇄 또는 임프린팅(Imprinting)된 도광패턴의 신뢰성을 열화시킬 수 있다.When the size of the PS diffusion beads 312 is less than 1 mu m, sufficient light diffusion performance of the light guide pattern can not be ensured. When the size of the PS diffusion beads is more than 20 mu m, not only the coating performance in which ink is adsorbed on the light guide plate is reduced, The beads may be visually recognized as regular particles, and the reliability of the light-projecting pattern printed or imprinted may be deteriorated.

따라서, 본 실시예에 의하면, 잉크 조성물에 포함되는 PS 확산 비드의 크기(d1)를 1~20μm로 함으로써, 잉크에 포함된 입자가 시인되지 않으면서, 도광패턴의 코팅 신뢰성을 확보하고, 기존의 PMMA 비드 대비 광확산 성능을 향상시켜, 결과적으로 도광판 및 백라이트 유닛의 고휘도를 구현할 수 있게 된다.Therefore, according to the present embodiment, by setting the size d1 of the PS diffusion beads included in the ink composition to 1 to 20 m, the coating reliability of the light guide pattern can be ensured without observing the particles contained in the ink, The light diffusion performance of the PMMA bead is improved, and as a result, high brightness of the light guide plate and the backlight unit can be realized.

또한, 본 실시예에 의한 도광패턴용 잉크 조성물에 포함되는 폴리스티렌(Poly Styrene; PS) 확산 비드의 조성비는 1~30중량% 범위일 수 있지만, 약25~30중량%인 것이 바람직하다.In addition, the composition ratio of the polystyrene (PS) diffusion beads contained in the ink composition for light guide pattern according to this embodiment may be in the range of 1 to 30 wt%, but preferably about 25 to 30 wt%.

PS 확산비드의 조성비가 30중량%를 초과하는 경우에는 확산 비드의 크기가 큰 경우와 마찬가지로 잉크의 도광판 흡착성 및 코팅 신뢰성이 약해지고, 확산비드가 시인될 우려가 있으므로, 약30중량% 이하인 것이 바람직하다.When the composition ratio of the PS diffusion beads is more than 30% by weight, as in the case where the size of the diffusion beads is large, the adsorption of the light guide plate and the coating reliability of the ink become weak and the diffusion beads may be visually recognized, .

그러나, PS 확산비드의 조성비가 너무 작은 경우에는 도광패턴의 충분한 광확산 성능을 확보할 수 없게 되므로, 약25중량 % 이상의 조성비를 가지는 것이 바람직하다.However, when the composition ratio of the PS diffusion beads is too small, sufficient light diffusion performance of the light guide pattern can not be ensured, and therefore it is preferable that the composition ratio is about 25 wt% or more.

이와 같이, PS 확산 비드의 조성비를 1~30중량%, 바람직하게는 25~30중량%로 함으로써, 잉크에 포함된 확산비드가 시인되지 않으면서도, 도광패턴의 코팅 신뢰성을 확보하고, 기존의 PMMA 비드 대비 광확산 성능을 향상시켜, 결과적으로 도광판 및 백라이트 유닛의 고휘도를 구현할 수 있게 된다.By setting the composition ratio of the PS diffusion beads to 1 to 30 wt%, preferably 25 to 30 wt%, the coating reliability of the light-guiding pattern can be ensured while the diffusion beads contained in the ink are not visually recognized, The light diffusion performance of the light guide plate and the backlight unit can be improved as a result.

또한, 본 실시예에 의한 청색계열 파장대역의 광을 흡수하여 녹색계열 파장대역의 광을 방출하는 녹색 광변환 비드(314)를 약1~30중량% 포함한다.In addition, the green light converting bead 314 absorbing light in the blue wavelength band according to the present embodiment and emitting green light in a wavelength band of about 1 to 30% by weight.

더 구체적으로, 본 실시예에 의한 도광패턴용 잉크 조성물에 포함되는 녹색 광변환 비드(314)는 420~470nm의 주흡수 파장대역과 520~560nm의 주발광 파장대역을 가질 수 있으며, 주흡수 파장피크 또는 주흡수 파장평균값은 약450nm이고 주방출 파장피크 또는 주방출 파장평균값은 약540nm일 수 있다.More specifically, the green light-converting bead 314 included in the ink composition for a light-guiding pattern according to the present embodiment may have a main absorption wavelength band of 420 to 470 nm and a main emission wavelength band of 520 to 560 nm, The peak or main absorption wavelength average value may be about 450 nm and the main emission wavelength peak or the main emission wavelength average value may be about 540 nm.

본 실시예에 사용되는 녹색 광변환 비드(314)는 녹색 형광체로 표현될 수도 있으며, 규산염계 녹색 형광체, 알루민산염계 녹색 형광체, 질화물계 녹색 형광체, 황산염계 녹색 형광체, 옥시-질화물계 녹색 형광체, 옥시-황산염계 녹색 형광체, 가넷(garnet) 재료, 일반조성이 A3Si(OD)5인 규산염계 녹색 형광체(여기서, Si는 규소, O는 산소, A는 스트론튬(Sr), 바륨(Ba), 마그네슘(Mg) 또는 칼슘(Ca)을 포함하며, D는 염소(Cl), 불소(F), 질소(N) 또는 황(S)을 포함한다), 일반조성이 A2Si(OD)4인 규산염계 녹색 형광체(여기서, A는 Sr, Ba, Mg 또는 Ca를 포함하며, D는 Cl, F, N 또는 S를 포함한다), 또는 화학식이 M1-xEuxAlyO[1+3y/2]인 알루민산염 녹색 형광체(여기서 M은 Ba, Sr, Ca, Mg, Mn, Zn, Cu, Cd, Sm 또는 툴륨(Tm)을 포함하는 2가 금속 중의 적어도 하나이다) 등이 사용될 수 있으나 그에 한정되는 것은 아니다.The green light converting bead 314 used in this embodiment may be represented by a green phosphor or may be a silicate-based green phosphor, an aluminate-based green phosphor, a nitride-based green phosphor, a sulfate-based green phosphor, an oxy- , oxy-sulfate-based green phosphor, a garnet (garnet) material, the general composition a 3 Si (OD) 5 a silicate-based green phosphor (where, Si is silicon, O is oxygen, a is strontium (Sr), barium (Ba ), magnesium oxide (including a Mg) or calcium (Ca), D comprises chlorine (Cl), fluorine (F), nitrogen (N) or sulfur (S)), the general composition a 2 Si (OD) 4 silicate-based green phosphor (where, a is Sr, Ba, and containing Mg or Ca, D is Cl, F, N or include S), or the formula M 1-x Eu x Al y O [1 + 3y / 2] in aluminate green phosphor, etc. (where M is at least one of the divalent metals including Ba, Sr, Ca, Mg, Mn, Zn, Cu, Cd, Sm or thulium (Tm)) used However, .

또한, 본 실시예에 사용될 수 있는 녹색 광변환 비드의 재료로는 (Bax, Sry, Caz)2SiO4:Eu (0≤x≤1, 0≤y≤1, 0≤z≤1)와 같은 실리케이트 계열, (Bax, Sry, Caz)Ga2S4:Eu (0≤x≤1, 0≤y≤1, 0≤z≤1)와 같은 티오갈레이트 계열 또는 (Bax, Sry, Caz)Al2S4:Eu (0≤x≤1, 0≤y≤1, 0≤z≤1)와 같은 티오알루미네이트 계열 등의 녹색 형광 물질을 포함할 수 있으며, 더 구체적으로, Sr2SiO4:Eu, Ba2SiO4:Eu, Ca2SiO4:Eu, SrGa2S4:Eu, BaGa2S4:Eu, CaGa2S4:Eu, Sr2Ga2S5:Eu, SrAl2S4:Eu, BaAl2S4:Eu, Sr2Al2S5:Eu, SiAlON:Eu, CaSc2O4:Ce 중에서 선택될 수도 있을 것이다.(Ba x , Sr y , Ca z ) 2 SiO 4 : Eu (0? X ? 1, 0? Y ? 1, 0? Z ? 1 ), A thiogallate series such as (Ba x , Sr y , Ca z ) Ga 2 S 4 : Eu (0 ≦ x ≦ 1, 0 ≦ y ≦ 1, 0 ≦ z ≦ 1) a phosphor such as a thioaluminate series such as x , Sr y , Ca z ) Al 2 S 4 : Eu (0? x? 1, 0? y? 1, 0? z? 1) more specifically, Sr 2 SiO 4: Eu, Ba 2 SiO 4: Eu, Ca 2 SiO 4: Eu, SrGa 2 S 4: Eu, BaGa 2 S 4: Eu, CaGa 2 S 4: Eu, Sr 2 Ga 2 S 5 : Eu, SrAl 2 S 4 : Eu, BaAl 2 S 4 : Eu, Sr 2 Al 2 S 5 : Eu, SiAlON: Eu and CaSc 2 O 4 : Ce.

본 실시예에 의한 도광패턴용 잉크 조성물에 포함되는 녹색 광변환 비드를 구성하는 재료는 전술한 재료들에 한정되는 것은 아니며, 약420~470nm의 청색계열의 광을 흡수하여 약520~560nm의 녹색 계열을 광을 방출하는 한 다른 광변환 재료가 사용될 수 있을 것이다.The material constituting the green light-converting beads included in the ink composition for a light-guiding pattern according to the present embodiment is not limited to the above-described materials. The green light-converting beads include green Other photo-conversion materials may be used as long as they emit light to the series.

이상의 녹색 광변환 비드에 의하여, 백라이트 유닛으로부터의 백색광 중에서 휘도에 영향을 미치는 색매칭 함수(Color Matching Function;

Figure pat00003
) 값이 작은 블루 계열의 광을 색매칭 함수(Color Matching Function;
Figure pat00004
) 값이 큰 녹색 계열의 광으로 변환하여 출력함으로써, 결과적으로 백색광의 유지하면서도 전체적인 출력 휘도를 향상시킬 수 있게 된다.By the above green light converting beads, a color matching function (color matching function) that affects brightness in the white light from the backlight unit is obtained.
Figure pat00003
) Is a color matching function (Color Matching Function;
Figure pat00004
Is converted into green light having a large value, and then the green light is output. As a result, the overall output brightness can be improved while maintaining the white light.

이와 같이, 도광패턴용 잉크 조성물에 녹색 광변환 비드(314)를 사용한 경우의 효과에 대해서는, 아래에서 도 6 및 도 7을 참고로 더 상세하게 설명한다. The effect when the green light-converting bead 314 is used in the ink composition for the light-guiding pattern is described in more detail below with reference to FIGS. 6 and 7. FIG.

또한, 도 3에 도시된 바와 같이, 본 실시예에 의한 도광패턴용 잉크 조성물에 포함되는 녹색 광변환 비드(314) 역시 PS 확산 비드(312)와 유사하게 약 1~20μm의 크기(d2)를 가지는 것이 바람직하다. 3, the green light-converting bead 314 included in the ink composition for a light-shading pattern according to the present embodiment also has a size d2 of about 1 to 20 μm similar to the PS diffusion bead 312 .

PS 확산 비드(312)의 경우와 유사하게, 녹색 광변환 비드(314)의 크기가 1μm 이하인 경우에는 원하는 광변환 특성을 확보할 수 없고, 녹색 광변환 비드(314)의 크기가 20μm 이상인 경우에는 잉크가 도광판에 흡착되는 코팅성능이 떨어질 뿐 아니라, 확산비드가 일정한 입자로서 시인될 우려가 있고, 인쇄 또는 임프린팅(Imprinting)된 도광패턴의 신뢰성을 열화시킬 수 있다.Similarly to the case of the PS diffusion bead 312, when the size of the green light conversion bead 314 is 1 μm or less, desired light conversion characteristics can not be secured. When the size of the green light conversion bead 314 is 20 μm or more Not only the coating performance in which the ink is adsorbed to the light guide plate is deteriorated but also the diffusion beads are visually recognized as the constant particles and the reliability of the printed or imprinted light guide pattern can be deteriorated.

따라서, 본 실시예에 의하면, 잉크 조성물에 포함되는 녹색 광변환 비드의 크기(d2)를 1~20μm로 함으로써, 잉크에 포함된 입자가 시인되지 않고 도광패턴의 코팅 신뢰성을 확보하면서도, 광원으로부터의 백색광 중에서 휘도향상에 기여하는 정도가 큰 녹색 광을 증가시켜 도광판 및 백라이트 유닛의 고휘도를 구현할 수 있게 된다.Therefore, according to the present embodiment, by setting the size d2 of the green light-converting bead included in the ink composition to 1 to 20 mu m, particles contained in the ink are not visually recognized and the coating reliability of the light- The brightness of the light guide plate and the backlight unit can be increased by increasing the amount of green light that contributes to brightness improvement in the white light.

또한, 본 실시예에 의한 도광패턴용 잉크 조성물에 포함되는 녹색 광변환 비드의 조성비는 1~30중량% 범위일 수 있지만, 약1~10중량%인 것이 바람직하다.The composition ratio of the green light-converting beads contained in the ink composition for a light-guiding pattern according to the present embodiment may be in the range of 1 to 30 wt%, preferably about 1 to 10 wt%.

녹색 광변환 비드의 조성비가 30중량%를 초과하는 경우에는 확산 비드의 크기가 큰 경우와 마찬가지로 잉크의 도광판 흡착성 및 코팅 신뢰성이 약해지고, 녹색 광변환 비드가 시인될 우려가 있으므로, 약30중량% 이하인 것이 바람직하다.When the composition ratio of the green light-converting beads is more than 30% by weight, as in the case where the size of the diffusion beads is large, the adsorption of the light guide plate and the coating reliability of the ink become weak and the green light- .

특히, 녹색 광변환 비드의 조성비가 약30중량%를 초과하는 경우에는 광변환 이후 백색광에 포함된 녹색계열광의 비율이 너무 커져서, 순수 화이트보다는 녹색광에 가까운 백색광이 출력되는 문제가 발생될 수 있다. Particularly, when the composition ratio of the green light-converting beads is more than about 30 wt%, the ratio of the green light included in the white light after photo-conversion becomes too large, so that white light closer to the green light than pure white may be output.

한편, 녹색 광변환 비드의 조성비가 너무 작은 경우에는 청색광으로부터 녹색광으로의 광변환 성능을 충분히 확보할 수 없게 되므로, 약1중량 % 이상의 조성비를 가지는 것이 바람직하다.On the other hand, when the composition ratio of the green light conversion beads is too small, it is impossible to sufficiently secure the light conversion performance from the blue light to the green light, and therefore it is preferable that the composition ratio is about 1 wt% or more.

이와 같이, 녹색 광변환 비드의 조성비를 1~30중량%, 바람직하게는 1~10중량%로 함으로써, 잉크에 포함된 녹색 광변환 비드가 시인되지 않게 하고 백색광의 색변화를 방지하면서도, 도광패턴의 코팅 신뢰성을 확보함과 동시에 결과적으로 도광판 및 백라이트 유닛의 고휘도를 구현할 수 있게 된다.In this manner, by setting the composition ratio of the green light-converting beads to 1 to 30 wt%, preferably 1 to 10 wt%, it is possible to prevent the green light-converting beads included in the ink from being visually recognized and prevent the change in the color of the white light, The coating reliability of the light guide plate and the backlight unit can be secured.

또한, 본 실시예에 의한 도광패턴용 잉크 조성물은, 전술한 PS 확산비드와 녹색 광변환 비드 이외에, 상기 입자들을 결착시키고 잉크의 도광판 흡착성을 확보하기 위한 바인더(binder)와, 용제 또는 용매와, 각종 첨가제 등을 더 포함할 수 있다.The ink composition for a light guide pattern according to this embodiment may further comprise a binder for binding the particles and securing adsorption of the ink to the light guide plate in addition to the above PS diffusion beads and green light conversion beads, Various additives, and the like.

바인더(Binder)는 인쇄 도막막을 형성시킴과 동시에 도광판에 대한 부착성을 조정할 수 있는 아크릴레이트기를 가지는 아크릴 공중합체가 사용될 수 있으며, 본 실시예에서는 광굴절률이 약1.47인 변형 아크릴레이트 수지(Modified Acrylate Resin)이 사용되었다.The binder may be an acrylic copolymer having an acrylate group capable of forming a print film and adjusting adhesion to a light guide plate. In this embodiment, a modified acrylate resin having a refractive index of about 1.47 Resin) was used.

바인더는 열경화 또는 UV 경화특성을 가지며, 이러한 바인더의 재료로는 메틸메타아크릴레이트, 에틸아크릴레이트, 부틸메타아크릴레이트, 부틸아크릴레이트, 스틸렌, 아크릴산으로 이루어진 군 중에서 선택되는 어느 하나 또는 둘 이상의 화합물로 합성한 중합체일 수 있으나 그에 한정되는 것은 아니다.The binder has a thermosetting or UV curing property. Examples of the material of the binder include any one or two or more compounds selected from the group consisting of methyl methacrylate, ethyl acrylate, butyl methacrylate, butyl acrylate, styrene, But the present invention is not limited thereto.

이러한 바인더 재료의 적정 조성비는 약20~25wt%일 수 있으며, 25wt% 이상이면 고휘도 잉크의 점도 조정이 어렵고 인쇄 시 미세패턴 제판의 판막힘 현상이 발생하게 되고, 20wt% 이하이면 미세패턴의 도트 형상이 퍼져 원하는 미세패턴용 도트 형태의 도광판을 얻기 힘들 수 있다.The optimum composition ratio of such a binder material may be about 20 to 25 wt%, and if it is 25 wt% or more, it is difficult to adjust the viscosity of the high-luminance ink and the plate clogging of the fine patterned plate occurs during printing. It may be difficult to obtain a light guide plate in the form of a dot for a desired fine pattern.

용제 또는 용매는 도광패턴용 잉크 조성물의 전체적인 점도와 관련되고, 도광판에 도광패턴을 인쇄 또는 임프린팅할 때의 작업성을 조정하기 위하여 사용되는 것으로서, 저비점 용제로는 벤젠, 톨루엔, 키실렌, 메틸이소부틸카비톨, 이소부틸아세테이트, 노르말부틸아세테이트, 메틸이소부틸 케톤, 에틸셀로솔브, 메틸셀로솔브 등이 사용될 수 있고, 중비점 용제로는 솔벤트, 에틸헥실아세테이트, 메톡시부틸아세테이트, 시클로헥실아세테이트, 부틸셀로솔브, 부틸셀로솔브아세테이트, 셀로솔브아세테이트, 메틸 카비톨, 시클로헥산논 등이 사용될 수 있다.The solvent or solvent is related to the overall viscosity of the ink composition for the light guide pattern and is used for adjusting the workability in printing or imprinting the light guide pattern on the light guide plate. Examples of the low boiling point solvent include benzene, toluene, Isobutyl acetate, n-butyl acetate, methyl isobutyl ketone, ethyl cellosolve, and methyl cellosolve. Examples of the medium boiling point solvent include solvent, ethylhexyl acetate, methoxybutyl acetate, cyclohexane Hexyl acetate, butyl cellosolve, butyl cellosolve acetate, cellosolve acetate, methyl carbitol, cyclohexanone and the like can be used.

또한, 디메틸에테르, 부틸카비톨, 디메틸글루타레이트, 디메틸석시네이트, 이소프론, 카비톨아세테이트, 에틸헥실글리콜, 부틸카비톨아세테이트, 에틸카비톨, 헥실셀로솔브 등과 같은 고비점 용제가 사용될 수도 있다.Also, a high boiling solvent such as dimethyl ether, butyl carbitol, dimethyl glutarate, dimethyl succinate, isofuron, carbitol acetate, ethylhexyl glycol, butyl carbitol acetate, ethyl carbitol, hexyl cellosol, etc. is used It is possible.

이러한 용제 또는 용매의 조성비는 약45~55중량%인 것이 바람직하며, 55wt% 잉크의 점도가 낮아져 도광패턴의 퍼짐 현상이 발생할 수 있고, 50wt% 이하이면 상대적으로 점도가 높아져 인쇄 또는 임프린팅 과정에서 제판의 판막힘 현상이 발생할 우려가 있다.The composition ratio of the solvent or solvent is preferably about 45 to 55% by weight, the viscosity of the 55% by weight ink is lowered, and the spreading phenomenon of the light guide pattern may occur. When the content of the solvent is 50% by weight or less, The plate clogging of the plate may occur.

기타, 본 실시예에 의한 도광패턴용 잉크 조성물에 포함되는 기타 첨가제로는, 조성 재료의 적절한 분산 또는 점성 조정을 위한 분산제, 잉크 도막의 레벨링성(도막균일성)을 향상을 위한 레벨링제, 잉크 인쇄 시 발생 될 수 있는 기포의 파괴 및 기포생성억제를 위한 소포제, 색상 변화를 방지하기 위한 변색제 등이 포함될 수 있다.Other additives included in the ink composition for light-guiding pattern according to this embodiment include a dispersing agent for proper dispersion or viscosity adjustment of the composition material, a leveling agent for improving the leveling property (coating film uniformity) of the ink coating, A defoaming agent for inhibiting bubble formation and bubble formation which may occur during printing, a coloring agent for preventing color change, and the like.

이러한 기타 첨가제는 일반적으로 도광패턴용 잉크 조성물에 사용되는 재료가 사용될 수 있으며, 첨가제의 조성비는 약0.5~1.0wt%일 수 있다.These other additives may be generally used in an ink composition for a light guide pattern, and the composition ratio of the additives may be about 0.5 to 1.0 wt%.

예를 들면, 분산제는 실리카, 비드와 친화력이 우수한 블록화된 공중합수지 계열의 첨가제를 사용하는 것이 바람직하며, 원하는 입도까지 분산할 수 있는 조제로 극성 산에스테르와 장쇄 폴리아미노 아마이드 염 용액인 디스퍼비와케이-101, 저분자량 산성 폴리에스테르와 불포화 폴리아민 아마이드 염 용액인 안티테라-유 등이 사용될 수 있다. For example, it is preferable to use a block copolymer resin-based additive having good affinity with silica and beads. As a dispersant capable of dispersing to a desired particle size, a polar acid ester and a long chain polyaminoamide salt solution, K-101, a low molecular weight acidic polyester, and an anti-tar oil, which is an unsaturated polyamine amide salt solution, can be used.

레벨링제로는 실리콘 또는 불소화합물 계통의 플루로라드 에프씨-430, 이베크릴 350, BYK-330 등이 사용될 수 있고, 소포제로는 실리콘이 함유된 아크릴 중합물 계통의 플로렌 AC-901, 비실리콘 계통의 BYK-051, BYK-052, BYK-066, BYK-088 및 모다 플로우 등이 사용될 수 있다.As the leveling agent, fluororad F-430, ibcryl 350, BYK-330 and the like based on silicon or fluorine compounds can be used. As the defoaming agent, acrylonitrile-based acrylonitrile-based fluorene AC-901, BYK-051, BYK-052, BYK-066, BYK-088, and Modaflow.

도 4는 본 발명의 실시예에 의한 잉크로 형성된 도광패턴을 가지는 도광판 및 그를 포함하는 백라이트 유닛의 확대 단면도와, 기존의 도광판와의 휘도 비교 실험 결과를 도시한다.4 is an enlarged cross-sectional view of a light guide plate having a light guide pattern formed of ink according to an embodiment of the present invention and a backlight unit including the light guide plate, and FIG. 4 shows a result of brightness comparison with a conventional light guide plate.

도 4와 같이, 본 실시예에 의한 백라이트 유닛은 LED와 같은 개별 광원(410)을 포함하는 광원부와, 광원부로부터의 광을 확산하기 위한 도광패턴(310)이 일면에 형성된 도광판(300)과, 도광판 하부에 배치되어 광을 표시패널측으로 반사하는 반사판(420) 등을 포함하여 구성되며, 도광패턴(310)은 폴리스티렌(Poly Styrene; PS) 확산비드 1~30중량%과, 청색계열 파장대역의 광을 흡수하여 녹색계열 파장대역의 광을 방출하는 녹색 광변환 비드 1~30중량%과, 바인더로서의 아크릴레이트 수지 20~25중량%과, 용제 45~55중량%를 포함하는 잉크 조성물로 형성된다.4, the backlight unit according to the present embodiment includes a light source unit including an individual light source 410 such as an LED, a light guide plate 300 having a light guide pattern 310 for diffusing light from the light source unit, And a reflection plate 420 disposed at a lower portion of the light guide plate and reflecting the light toward the display panel. The light guide pattern 310 may include 1 to 30% by weight of polystyrene (PS) diffusion beads, 1 to 30% by weight of a green light-converting bead which absorbs light and emits light in a green wavelength band, 20 to 25% by weight of an acrylate resin as a binder, and 45 to 55% by weight of a solvent .

또한, 본 실시예에 의한 백라이트 유닛은 도광판 상부에 배치되어, 도광판으로부터 출사되는 광의 특성을 변화시키는 1 이상의 광학시트(430)을 추가로 포함할 수 있다.Further, the backlight unit according to the present embodiment may further include one or more optical sheets 430 disposed on the light guide plate and changing the characteristics of light emitted from the light guide plate.

본 실시예에 의한 백라이트 유닛에 포함되는 광원부는 LED 등과 같은 개별 광원(또는 광원소자 또는 광원칩; 410)과, 그 개별 광원을 지지하는 광원홀더 또는 광원모듈(미도시)로 구성될 수 있다. 또한 개별 광원의 구동을 위한 LED 구동 회로가 포함될 수 있으며 이 경우에는 광원모듈은 광원 PCB 등과 같은 다른 용어로 표현될 수 있다.The light source unit included in the backlight unit according to the present embodiment may include an individual light source (or a light source device or a light source chip) 410 such as an LED, and a light source holder or a light source module (not shown) for supporting the individual light source. Also, an LED driving circuit for driving an individual light source may be included, in which case the light source module may be represented by another term such as a light source PCB.

광원부에 포함되는 개별 광원(410)은 발광 다이오드(LED) 또는 발광 다이오드 스트립 등이 사용될 수 있으나 그에 한정되는 것은 아니며, 표시패널에 필요한 광을 제공할 수 있는 한 모든 형태의 광원이 사용될 수 있을 것이다.The individual light source 410 included in the light source unit may be a light emitting diode (LED) or a light emitting diode strip, but the present invention is not limited thereto. Any type of light source can be used as long as it can provide necessary light to the display panel .

본 실시예에 의한 도광판(300)은 전술한 잉크 조성물로 형성되는 도광패턴(310)이 일면에 다수 형성된 판상 광학부재로서, 일반적으로 플라스틱 시트로부터 다이 커팅되거나, 압출되거나, 사출 성형된 직사각형의 투명한 플라스틱(clear plastic) 시트로 형성될 수 있다.The light guide plate 300 according to the present embodiment is a plate-shaped optical member formed with a plurality of light guide patterns 310 formed on the one surface by the above-described ink composition, and is generally formed of a rectangular transparent plate die cut, extruded, And may be formed of a clear plastic sheet.

발광 다이오드 어레이 등과 같은 광원으로부터의 광은 도광판의 가장자리로 출사되어 도광판 내부에서 전반사되면서 표시패널의 배면을 가로질러 확산되며, 도광판의 평탄한 상면을 통해 출사되는 광이 표시패널의 백라이트로서 기능한다.Light emitted from a light source such as a light emitting diode array or the like is emitted to the edge of the light guide plate and totally diffused across the back surface of the display panel while being totally reflected inside the light guide plate and the light emitted through the flat upper surface of the light guide plate functions as a backlight of the display panel.

이러한 도광판(300)을 구성하는 재료로는, 폴리메틸메타크릴레이트(polymethyl methacrylate: PMMA), MS(methlystylene)수지, 폴리스티렌(polystyrene:PS), 폴리프로필렌(Polypropylene:PP), 폴리에틸렌 테레프탈레이트(polyethylene terephthalate:PET) 및 폴리카보네이트(polycarbonate:PC), 글래스(Glass) 등이 될 수 있다.The material of the light guide plate 300 may be selected from the group consisting of polymethyl methacrylate (PMMA), MS (methystylene) resin, polystyrene (PS), polypropylene (PP), polyethylene terephthalate terephthalate (PET), polycarbonate (PC), glass, and the like.

폴리메틸메타크릴레이트(polymethyl methacrylate: PMMA) 재료는 약90%의 광투과율과 약1.49~1.50의 굴절율을 가지며, 폴리카보네이트(Poly Carbonate; PC) 재료는 약 86~89%의 광투과율과 약1.57 이상의 굴절률을 가진다.The polymethyl methacrylate (PMMA) material has a light transmittance of about 90%, a refractive index of about 1.49 to 1.50, and a polycarbonate (PC) material has a light transmittance of about 86 to 89% and a transmittance of about 1.57 Or more.

또한, 폴리에테르 술폰(Poly Ether Sulfone; PES) 재료는 약73%의 광투과율과 약1.65의 굴절율을 가지며, 메타크릴레이트스티렌(Methacrylate Styrene; MS) 재료는 약 90%의 광투과율과 약1.5677의 굴절률을 가진다. 또한, 글래스(Glass)는 약1.89이상의 굴절율을 가진다Also, the polyether sulfone (PES) material has a light transmittance of about 73% and a refractive index of about 1.65, and the methacrylate styrene (MS) material has a light transmittance of about 90% and a transmittance of about 1.5677 Refractive index. Further, the glass has a refractive index of about 1.89 or more

특히, 본 발명의 일실시예에서는 도광패턴(310)에 포함되는 확산비드가 굴절률이 약1.59인 폴리스티렌(PS) 재료로 구성되므로, 도광판(300)의 재료로는 PS 확산비드보다 낮은 약1.49의 굴절률을 가지는 폴리메틸메타크릴레이트(polymethyl methacrylate: PMMA)를 이용하는 것이 바람직하다.Particularly, in an embodiment of the present invention, the diffusion beads included in the light guide pattern 310 are made of a polystyrene (PS) material having a refractive index of about 1.59, so that the material of the light guide plate 300 is about 1.49 It is preferable to use polymethyl methacrylate (PMMA) having a refractive index.

이와 같이, 도광판(300)의 주재료로서 도광패턴용 잉크 조성물에 포함된 PS 확산 비드의 굴절률보다 낮은 굴절률을 가지는 PMMA를 사용함으로써, 도광패턴(310)에서 확산된 광이 도광판의 타측 표면으로 입사되는 입사각을 감소시키고 도광판을 이탈하는 광이 도광판의 법선 방향에 가깝도록 하여, 결과적으로 도광판의 휘도를 증가시키는 효과가 있다.As described above, by using PMMA having a refractive index lower than the refractive index of the PS diffusion beads included in the ink composition for the light-guiding pattern, light diffused in the light-guiding pattern 310 is incident on the other surface of the light- The incident angle is reduced and the light that deviates from the light guide plate is brought close to the normal direction of the light guide plate, resulting in the effect of increasing the brightness of the light guide plate.

반사판(420)은 도광판(300)의 배면, 즉 본 실시에에 의한 도광패턴(310)이 형성된 측면에 위치하여, 도광판의 배면을 통과한 광을 표시패널(미도시) 쪽으로 반사시킴으로써 광의 휘도를 향상시키는 기능을 한다.The reflection plate 420 is disposed on the back surface of the light guide plate 300, that is, on the side surface on which the light guide pattern 310 according to the present embodiment is formed and reflects the light that has passed through the back surface of the light guide plate toward the display panel (not shown) It improves function.

도광판(300) 상부에 배치되는 광학시트부(430)는 집광시트, 확산시트, 반사형 편광필름 등에서 선택되는 1 이상의 개별 광학시트들로 구성될 수 있다.The optical sheet portion 430 disposed on the light guide plate 300 may be composed of one or more individual optical sheets selected from a light-collecting sheet, a diffusion sheet, and a reflective polarizing film.

광학시트부(430)를 구성하는 개별 광학시트의 예로는 집광 기능을 하는 집광시트 또는 프리즘 시트(Prism Sheet; PS)와, 광을 확산시키는 확산시트(Diffusing Sheet; DS)와, 이중 휘도 향상필름(dual brightness enhancement film; DBEF) 또는 APF(Advanced Polarizer Film)라 불리는 휘도 향상을 위한 반사형 편광필름 등 각종 기능성 시트 등이 포함될 수 있으나, 그에 한정되는 것은 아니다.Examples of the individual optical sheets constituting the optical sheet portion 430 include a light collecting sheet or prism sheet PS having a condensing function, a diffusing sheet DS for diffusing light, but is not limited to, various functional sheets such as a dual brightness enhancement film (DBEF) or a reflection type polarizing film for brightness enhancement called APF (Advanced Polarizer Film).

통상적으로, 광학시트부를 구성하는 기능성 개별 시트 중에서 집광시트 또는 프리즘 시트(Prism Sheet; PS)는 투명필름 형태의 시트에 일정한 집광 패턴 등이 포함됨으로써, 입사되는 광을 일정한 방향으로 모아주는 집광 기능을 한다.In general, a light collecting sheet or a prism sheet (PS) among the individual functional sheets constituting the optical sheet portion includes a light collecting pattern or the like in a sheet of a transparent film type so that a condensing function for collecting incident light in a certain direction do.

한편, 광을 확산시키는 확산시트(Diffusing Sheet; DS)는 입사되는 광을 여러 방향으로 확산시키는 기능을 하는 광학시트로서, 투명필름 형태의 시트에 일정한 확산패턴 또는 확산입자 등을 포함하여 구성될 수 있다.On the other hand, a diffusing sheet (DS) for diffusing light is an optical sheet having a function of diffusing incident light in various directions, and may be constituted by including a diffusion pattern or a diffusion particle in a transparent sheet have.

또한, 반사형 편광필름은 여러 방향으로 진동하면서 입사되는 자연광중 한쪽 방향으로 진동하는 빛만 투과시키고 다른 방향으로 진동하는 빛은 반사하는 광학 필름으로서, DBEF(dual brightness enhancement film; DBEF)라 불리는 휘도 향상 필름을 포함하는 개념이다.In addition, the reflection type polarizing film is an optical film that transmits only light that vibrates in one direction among natural incident lights while vibrating in various directions, and reflects light that vibrates in the other direction, and has a luminance enhancement called DBEF (dual brightness enhancement film Film.

도시하지는 않았지만, 도광판의 상측에는 표시패널이 배치된다.Although not shown, a display panel is disposed on the upper side of the light guide plate.

표시패널이 액정 표시패널인 경우에는 다시 다수의 게이트 라인과 데이터 라인 및 그 교차 영역에 정의되는 픽셀(Pixel)과, 각 픽셀에서의 광투과도를 조절하기 위한 스위칭 소자인 박막 트랜지스터를 포함하는 어레이 기판과, 컬러필터 및/또는 블랙매트릭스 등을 구비한 상부기판과, 그 사이에 형성되는 액정물질층을 포함하여 구성될 수 있다.When the display panel is a liquid crystal display panel, a pixel is defined again in a plurality of gate lines, a data line and a crossing region thereof, and a thin film transistor, which is a switching element for adjusting light transmittance in each pixel, An upper substrate provided with a color filter and / or a black matrix, and a liquid crystal material layer formed therebetween.

물론, 본 실시예에 의한 백라이트 유닛이 적용될 수 있는 표시패널은 이러한 액정표시패널에 한정되는 것은 아니며, 플라즈마 디스플레이 등과 같은 표시장치는 물론이고, 후면에서 백라이트 유닛에 의한 광을 제공받아 영상을 표시하는 모든 형태의 표시패널을 포함할 수 있다.Of course, the display panel to which the backlight unit according to the present embodiment can be applied is not limited to such a liquid crystal display panel. In addition to a display device such as a plasma display, a backlight unit And may include any type of display panel.

본 명세서에서 "표시장치"라는 용어는 표시패널과 표시패널을 구동하기 위한 구동부를 포함하는 액정 모듈(Liquid Crystal Module; LCM)과 같은 협의의 표시장치는 물론, 그러한 LCM을 포함하는 완제품인 노트북 컴퓨터, 텔레비전, 컴퓨터 모니터, 스마트폰 또는 전자패드와 같은 모바일 전자장치 등과 같은 세트 전자 장치 또는 세트 장치까지도 포함하는 개념으로 사용한다.The term "display device" is used herein to refer to a display device such as a liquid crystal module (LCM) including a display panel and a driver for driving the display panel, as well as a notebook computer , A set of electronic devices or set devices such as a television, a computer monitor, a mobile electronic device such as a smart phone or an electronic pad, and the like.

즉, 본 명세서에서의 표시장치는 LCM과 같은 협의의 디스플레이 장치는 물론, 그를 포함하는 응용제품인 세트 장치까지 포함하는 의미로 사용한다.That is, the display device in this specification is used to mean not only a conferring display device such as LCM but also a set device which is an application including the display device.

한편, 도 4의 (a)에 도시한 바와 같이, 광원(410)으로부터 출사된 광 R 중에서 일부는 본 실시예에 의한 잉크 조성물로 형성된 도광패턴(310)으로 입사된다. 4A, a part of the light R emitted from the light source 410 is incident on the light guide pattern 310 formed of the ink composition according to the present embodiment.

도광패턴(310)으로 입사된 광은 PS 확산 비드(312)에서 산란 또는 확산되고 그 중 일부의 광 R1이 도광판의 타측 표면 방향으로 42도보다 낮은 θ의 입사각으로 진행하여, 결과적으로 출광각 θ'로 도광판 상부로 출사된다(R1').The light incident on the light guide pattern 310 is scattered or diffused by the PS diffusion beads 312 and some of the light R1 travels at an incident angle of? Lower than 42 degrees in the direction toward the other surface of the light guide plate, '(R1').

이러한 광경로에 따르면, 본 실시예에 의한 고굴절률의 PS 확산 비드(312)를 사용하는 경우에는 기존의 PMMA 확산비드에 비하여 입사광의 확산성이 커지고, 결과적으로 도광판의 상면으로의 입사각(도 4의 θ)이 42도 이하여서 도광판 외부로 출사될 수 있는 광의 비율이 증가된다. According to this optical path, when the PS diffusing bead 312 of high refractive index according to this embodiment is used, the diffusing property of the incident light becomes larger than that of the existing PMMA diffusing bead, and consequently the incident angle to the upper surface of the light guide plate Is less than 42 degrees, the ratio of light that can be emitted to the outside of the light guide plate is increased.

또한, 본 실시예에 의한 고굴절률의 PS 확산 비드(312)에 의한 광굴절 정도가 더 커지게 되므로, 도광판 외부로 출사되는 출광각(도 4의 θ')이 감소하여 도광판의 법선에 가깝도록 출사되므로, 도광판의 휘도를 증가시킬 수 있게 된다.Further, since the degree of light refraction by the high-refractive-index PS diffusing bead 312 according to the present embodiment becomes larger, the outgoing angle (&thetas; 'in Fig. 4) emitted to the outside of the light guide plate decreases and becomes close to the normal line of the light guide plate The brightness of the light guide plate can be increased.

구체적인 실험결과, 도 4의 (b)에 도시된 바와 같이, 본 실시예에 의한 PS 확산비드(312)를 포함하는 잉크 조성물로 형성된 도광패턴을 이용하는 경우에는 기존의 PMMA 확산 비드를 사용한 경우에 비하여 약30% 이상 휘도가 증가됨을 확인하였다.As a result of a specific experiment, as shown in FIG. 4 (b), in the case of using the light guide pattern formed of the ink composition including the PS diffusion bead 312 according to this embodiment, as compared with the case of using the existing PMMA diffusion beads It is confirmed that the brightness is increased by about 30% or more.

또한, 도광패턴(310)으로 입사된 광은 PS 확산 비드(312)에서 확산됨과 동시에, 녹색 광변환 비드(314)에서 청색계열의 광이 녹색계열의 광으로 변환된다.The light incident on the light guide pattern 310 is diffused by the PS diffusion beads 312 and the blue light is converted into the green light by the green light conversion bead 314.

녹색 광변환 비드(314)에 의하여 520~560nm 파장대역의 광속(Flux)이 증가되고, 그에 따라 도광판 외부로 출사되는 광 R1'의 휘도가 증가된다. 이러한 효과에 대해서는 아래에서 도 6을 참고로 더 설명한다.The flux of light in the wavelength band of 520 to 560 nm is increased by the green light converting bead 314 and the luminance of the light R1 'emitted to the outside of the light guide plate is increased accordingly. These effects will be further described below with reference to FIG.

도 5는 본 발명의 실시예에 의한 잉크에 포함된 PS 확산 비드에 의한 광경로와, 휘도 향상 원리 및 그 실험결과를 도시한다.FIG. 5 shows the optical path, the brightness enhancement principle, and the experimental result of the PS diffusion beads included in the ink according to the embodiment of the present invention.

도 5는 본 실시예에 의한 도광패턴용 잉크 조성물의 광학 특성을 시험한 결과로서, 250μm 두께를 가지는 폴리에틸렌 테레프탈레이트(polyethylene terephthalate:PET) 필름층(510) 일면에 본 실시예에 의한 PS 비드를 포함하는 잉크 조성물층(520)을 형성하고, 여러 입사각(AOI)를 가지는 광을 PET 필름층(510)에 투사한 후, 이등방 반사광(Bidirectional Reflection Distribution Function; BRDF)과 이등방 투과광(Bidirectional Transmission Distribution Function; BTDF)의 광분포(Contour Chart)와 광프로파일을 측정한 결과이다.5 shows the result of testing the optical characteristics of the ink composition for a light-guiding pattern according to the present embodiment. As shown in FIG. 5, on one surface of a polyethylene terephthalate (PET) film layer 510 having a thickness of 250 m, And then the light having a plurality of incident angles AOI is projected onto the PET film layer 510. Thereafter, the light is reflected by the Bireirectional Reflection Distribution Function (BRDF) and the Bireirectional Transmission (BTDF) distribution profile and optical profile.

도 5의 실험에서는 대조군으로서 기존과 같이 굴절률 1.49이고 직경 약4~7μm의 PMMA 비드를 포함하는 잉크 조성물을 사용하였으며, 본 실시예에 대한 잉크 조성물에는 굴절률이 1.59이고 직경 약4~7μm인 구형 PS 비드를 사용하였다.5, an ink composition containing a PMMA bead having a refractive index of 1.49 and a diameter of about 4 to 7 탆 was used as a control. In the ink composition for this example, a spherical PS having a refractive index of 1.59 and a diameter of about 4 to 7 탆 Beads were used.

실험결과, 도 5의 (b)와 같이 기존의 PMMA 비드를 사용한 대조군에 비하여, 본 실시예에 의한 PS 확산 비드를 사용하는 경우, 입사각(AOI)이 각각 40, 50, 60도인 투사광에 대하여 이등방 투과광(Bidirectional Transmission Distribution Function; BTDF)의 광분포(Contour Chart)가 더 넓고, 광프로파일 역시 더 넓게 되는 것을 알 수 있다.As shown in FIG. 5 (b), when the PS diffusion bead according to the present embodiment is used, the incident angle (AOI) is 40, 50 and 60 degrees, respectively, compared with the control using the conventional PMMA bead. The contour chart of the bidirectional transmission distribution function (BTDF) is wider, and the optical profile is also wider.

즉, 본 실시예에 의한 PS 확산 비드를 사용하는 경우, 이등방 투과광(Bidirectional Transmission Distribution Function; BTDF)의 광프로파일은 기존 PMMA 비드를 사용하는 경우와 비교할 때, 최대 피크의 세기는 유사하지만, 반치폭(Full Width at Half Maximum; FWHM; 최대 휘도대비 1/2되는 지점의 스펙트럼 폭)이 증가됨을 알 수 있다.That is, in the case of using the PS diffusion bead according to this embodiment, the optical profile of the bidirectional transmission distribution function (BTDF) is similar to that of the conventional PMMA bead, but the half peak width The full width at half maximum (FWHM) is increased at a half of the maximum luminance.

따라서, 최대 휘도는 유사하지만, 반치폭이 증가함으로써 전체적인 광휘도를 증가하는 것이다.Therefore, although the maximum luminance is similar, the half brightness increases, thereby increasing the overall brightness.

이러한 결과로서, 도 4의 (b)에 도시한 바와 같이, 본 실시예에 의한 PS 확산비드(312)를 포함하는 잉크 조성물로 형성된 도광패턴을 이용하는 경우에는 기존의 PMMA 확산 비드를 사용한 경우에 비하여 약130%의 휘도를 구현할 수 있는 것으로 나타났다.As a result, as shown in FIG. 4 (b), in the case of using the light guide pattern formed of the ink composition including the PS diffusion bead 312 according to the present embodiment, as compared with the case of using the existing PMMA diffusion beads It is possible to realize a luminance of about 130%.

도 6은 일반적인 광원의 광속(Flux)와 색매칭 함수(Color Matching Function; y)에 따른 휘도(Y) 산출 원리를 도시하며, 도 7은 본 발명의 실시예에 의한 잉크에 포함된 녹색 광변환 비드에 의한 휘도 향상 원리를 도시하는 도면이다.FIG. 6 illustrates a principle of calculating a luminance Y according to a flux of a general light source and a color matching function (y), and FIG. 7 is a graph showing the relationship between a green light conversion Fig. 8 is a diagram showing a principle of brightness enhancement by beads.

도6및 아래 수학식 1에 도시된 바와 같이, 일반적으로 백색광의 휘도(Y)는 백색광에 포함된 광의 주파수대역별 광속(Flux)인 C(λ)와 각 파장대역별 색매칭 함수(Color Matching Function;

Figure pat00005
) 또는 색좌표값(
Figure pat00006
)의 적분값으로 결정된다.As shown in FIG. 6 and the following Equation (1), the luminance Y of white light is generally expressed by C (?), Which is the flux according to the frequency band of the light included in the white light, and the color matching function for each wavelength band.
Figure pat00005
) Or a color coordinate value (
Figure pat00006
).

Figure pat00007
Figure pat00007

그런데, 색매칭 함수(Color Matching Function;

Figure pat00008
) 또는 색좌표값(
Figure pat00009
)는 약550 nm 부근에서 가장 큰 값을 가지면서 정규분포에 가까운 값의 분포를 가지는 반면, 주파수 대역별 광속(Flux)인 C(λ)는 550nm 부근에서 가장 작은 것을 알 수 있다.However, the color matching function (Color Matching Function;
Figure pat00008
) Or a color coordinate value (
Figure pat00009
) Has the largest value at about 550 nm and has a distribution close to the normal distribution, whereas C (?), Which is flux per frequency band, is the smallest at around 550 nm.

따라서, 도 6의 (b)에 도시된 바와 같이, 일반적인 백색광의 휘도(Y)는 약600nm 부근에서 가장 큰 값을 가지지만, 550nm 부근에서는 비교적 작은 값을 가진다.Therefore, as shown in FIG. 6 (b), the luminance Y of the ordinary white light has the largest value in the vicinity of about 600 nm, but has a relatively small value in the vicinity of 550 nm.

한편, 본 발명의 실시예에 의한 도광패턴용 잉크 조성물에 포함되는 녹색 광변환 비드는 백색광에 포함된 약420~470nm파장대역을 가지는 청색계열의 광을 흡수하여 약520~560nm 파장대역 광을 방출한다.Meanwhile, the green photoconversion bead included in the ink composition for a light guide pattern according to an embodiment of the present invention absorbs blue light having a wavelength band of about 420 to 470 nm included in white light, and emits light in a wavelength band of about 520 to 560 nm do.

따라서, 도 7의 (a)에 도시된 바와 같이, 기존의 주파수 대역별 광속(Flux; C(λ)) 분포 중에서 약420~470nm파장대역의 A 영역의 광속이 감소하고, 약520~560nm 파장대역의 B 영역의 광속이 증가된다.Therefore, as shown in FIG. 7A, the light flux of the A region in the wavelength band of about 420 to 470 nm is reduced in the conventional distribution of the flux (C (?)) For each frequency band, and the light flux of about 520 to 560 nm The light flux of the B region of the band is increased.

따라서, 수학식 1에 의하여 도 7의 (b)와 같은 색매칭 함수(Color Matching Function;

Figure pat00010
)와 적분되어 산출된 총 휘도의 분포는 도 7의 (c)와 같이 기존의 총 휘도 분포에 비하여 약520~560nm 파장대역의 B 영역의 휘도가 증가한다.Therefore, the color matching function (Color Matching Function) shown in FIG.
Figure pat00010
), The luminance of the B region in the wavelength band of about 520 to 560 nm increases as compared with the conventional total luminance distribution as shown in FIG. 7 (c).

물론, 약420~470nm파장대역의 A 영역의 휘도는 감소하지만 그 영역의 색매칭함수값(

Figure pat00011
)이 작아서 휘도 감소분은 작은 반면, 약520~560nm 파장대역의 B 영역의 색매칭함수값(
Figure pat00012
)은 크기 때문에 녹색 광변환 비드의 광변환에 따른 휘도 증가분이 더 크게 되는 것이다.Of course, the luminance of the A region in the 420 to 470 nm wavelength band is reduced, but the color matching function value (
Figure pat00011
) Is small and the luminance reduction is small, the color matching function value of the B region in the wavelength band of about 520 to 560 nm (
Figure pat00012
) Is so large that the luminance increase due to the light conversion of the green light conversion bead becomes larger.

결과적으로, 도 7의 (c)에 도시된 바와 같이, 일반적인 백색광의 총 휘도(Y)에 비하여 본 실시예에 의한 녹색 광변환 비드를 포함한 잉크 조성물을 통과한 백색광의 총 휘도가 증가하게 되며, 이로써 본 실시예에서 요구하는 도광판의 고휘도를 구현할 수 있게 되는 것이다.As a result, as shown in FIG. 7 (c), the total luminance of the white light passing through the ink composition including the green light-converting bead according to this embodiment is increased as compared with the total luminance Y of general white light, This makes it possible to realize the high brightness of the light guide plate required in the present embodiment.

이상 설명한 실시예와 같이, 본 발명의 실시예에 의하면, 기존의 PMMA에 비하여 굴절율이 큰 폴리스티렌(PS) 확산 비드와, 청색계열의 광을 녹색계열의 광으로 변환하는 녹색 광변환 비드 중 하나 이상을 포함하는 도광패턴용 잉크 조성물을 이용함으로써, 출력되는 백색광의 강도를 증가시켜 도광판 및 백라이트 유닛의 고휘도 구현이 가능하다는 효과가 있다. As described above, according to the embodiment of the present invention, a polystyrene (PS) diffusion bead having a higher refractive index than that of the existing PMMA and a green light conversion bead for converting blue light into green light It is possible to increase the intensity of the outputted white light, thereby realizing high brightness of the light guide plate and the backlight unit.

특히, 도광패턴용 잉크에 포함되는 폴리스티렌(Poly Styrene; PS) 확산비드 및 광변환 비드의 크기 및 조성비를 최적화함으로써, 도광패턴의 코팅 신뢰성 및 색재현 등에 영향을 최소화하면서도 도광판 및 그를 이용한 백라이트 유닛이 기존에 비하여 약30% 이상 휘도를 증가시킬 수 있는 효과가 있다.In particular, by optimizing the size and composition ratio of the polystyrene (PS) diffusion beads and the photoconversion beads contained in the inks for the light guide pattern, the light guide plate and the backlight unit using the light guide plate are minimized while minimizing the coating reliability and color reproduction of the light guide pattern. It is possible to increase the luminance by about 30% or more as compared with the conventional one.

이상에서의 설명 및 첨부된 도면은 본 발명의 기술 사상을 예시적으로 나타낸 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 구성의 결합, 분리, 치환 및 변경 등의 다양한 수정 및 변형이 가능할 것이다. 따라서, 본 발명에 개시된 실시예들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.
It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the present invention as defined by the appended claims. , Separation, substitution, and alteration of the invention will be apparent to those skilled in the art. Therefore, the embodiments disclosed in the present invention are intended to illustrate rather than limit the scope of the present invention, and the scope of the technical idea of the present invention is not limited by these embodiments. The scope of protection of the present invention should be construed according to the following claims, and all technical ideas within the scope of equivalents should be construed as falling within the scope of the present invention.

300 : 도광판 310 : 도광패턴
312 : 폴리스티렌(PS) 확산 비드 314 : 녹색 광변환 비드
410 : 광원 420 : 반사판
430 : 광학시트부300: light guide plate 310: light guiding pattern
312: polystyrene (PS) diffusion bead 314: green light conversion bead
410: light source 420: reflector
430: Optical sheet part

Claims (13)

도광패턴용 잉크 조성물로서,
폴리스티렌(Poly Styrene; PS) 확산비드 1~30중량%;
청색계열 파장대역의 광을 흡수하여 녹색계열 파장대역의 광을 방출하는 녹색 광변환 비드 1~30중량%;
바인더로서의 아크릴레이트 수지 20~25중량%;
용제 45~55중량%;
를 포함하는 도광패턴용 잉크 조성물.As an ink composition for a light guide pattern,
1 to 30% by weight of polystyrene (PS) diffusion beads;
1 to 30% by weight of a green light-converting bead which absorbs light in a blue-based wavelength band and emits light in a green-based wavelength band;
20-25% by weight of an acrylate resin as a binder;
45 to 55% by weight of a solvent;
And an ink composition for a light guide pattern. 제1항에 있어서,
상기 폴리스티렌(Poly Styrene; PS) 확산비드는 1.59 이상의 광굴절률을 가지고, 상기 녹색 광변환 비드는 420~470nm의 주흡수 파장대역과 520~560nm의 주발광 파장대역을 가지는 도광패턴용 잉크 조성물.The method according to claim 1,
Wherein the polystyrene (PS) diffusion bead has a refractive index of 1.59 or more, and the green photoconversion bead has a main absorption wavelength band of 420 to 470 nm and a main emission wavelength band of 520 to 560 nm. 제2항에 있어서,
상기 PS 확산비드 및 상기 녹색 광변환 비드는 1~20μm의 크기를 가지는 도광패턴용 잉크 조성물.3. The method of claim 2,
Wherein the PS diffusion bead and the green light conversion bead have a size of 1 to 20 占 퐉. 제3항에 있어서,
상기 폴리스티렌(Poly Styrene; PS) 확산 비드의 조성비는 25~30중량%이고, 상기 녹색 광변환 비드의 조성비는 1~10중량%인 도광패턴용 잉크 조성물.The method of claim 3,
The composition ratio of the polystyrene (PS) diffusion beads is 25 to 30 wt%, and the composition ratio of the green photoconversion beads is 1 to 10 wt%. 제4항에 있어서,
조성 재료의 적절한 분산 또는 점성 조정을 위한 분산제, 잉크 도막의 레벨링성(도막균일성)을 향상을 위한 레벨링제, 잉크 인쇄 시 발생 될 수 있는 기포의 파괴 및 기포생성억제를 위한 소포제, 색상 변화를 방지하기 위한 변색제 중 하나 이상의 첨가제를 약0.5~1.0wt% 더 포함하는 도광패턴용 잉크 조성물.5. The method of claim 4,
A leveling agent for improving the leveling property (coating film uniformity) of the ink film, a defoaming agent for inhibiting bubble formation and bubble formation which may occur in ink printing, a coloring agent for improving the color change By weight based on the total weight of the ink composition. 표시장치용 백라이트 유닛에 사용되는 도광판으로서,
상기 도광판의 일면에는 다수의 도광패턴이 배치되며, 상기 도광패턴은 폴리스티렌(Poly Styrene; PS) 확산비드 1~30중량%과, 청색계열 파장대역의 광을 흡수하여 녹색계열 파장대역의 광을 방출하는 녹색 광변환 비드 1~30중량%과, 바인더로서의 아크릴레이트 수지 20~25중량%과, 용제 45~55중량%를 포함하는 잉크 조성물로 구성되는 백라이트 유닛용 도광판.A light guide plate for use in a backlight unit for a display device,
A light guide pattern is formed on one surface of the light guide plate, and the light guide pattern comprises 1 to 30% by weight of polystyrene (PS) diffusion beads and light of a blue series wavelength band and emits light of a green series wavelength band 1 to 30% by weight of a green light-converting bead, 20 to 25% by weight of an acrylate resin as a binder, and 45 to 55% by weight of a solvent. 제6항에 있어서,
상기 폴리스티렌(Poly Styrene; PS) 확산비드는 1.59 이상의 광굴절률을 가지고, 상기 녹색 광변환 비드는 420~470nm의 주흡수 파장대역과 520~560nm의 주발광 파장대역을 가지는 백라이트 유닛용 도광판.The method according to claim 6,
Wherein the green light-converting bead has a main absorption wavelength band of 420 to 470 nm and a main emission wavelength band of 520 to 560 nm, wherein the poly-styrene (PS) diffusion bead has a refractive index of 1.59 or more. 제7항에 있어서,
상기 PS 확산비드 및 상기 녹색 광변환 비드는 1~20μm의 크기를 가지는 백라이트 유닛용 도광판.8. The method of claim 7,
Wherein the PS diffusion bead and the green light conversion bead have a size of 1 to 20 占 퐉. 제8항에 있어서,
폴리스티렌(Poly Styrene; PS) 확산 비드의 조성비는 25~30중량%이고, 상기 녹색 광변환 비드의 조성비는 1~10중량%인 백라이트 유닛용 도광판.9. The method of claim 8,
Wherein a composition ratio of polystyrene (PS) diffusion beads is 25 to 30% by weight, and a composition ratio of the green photoconversion beads is 1 to 10% by weight. 광원부;
상기 광원부로부터의 광을 확산하기 위하여 폴리스티렌(Poly Styrene; PS) 확산비드 1~30중량%과, 청색계열 파장대역의 광을 흡수하여 녹색계열 파장대역의 광을 방출하는 녹색 광변환 비드 1~30중량%과, 바인더로서의 아크릴레이트 수지 20~25중량%과, 용제 45~55중량%를 포함하는 잉크 조성물로 구성된 다수의 도광패턴을 일면에 포함하는 도광판;
상기 도광판 하부에 배치되어 광을 표시패널측으로 반사하는 반사판;
을 포함하는 표시장치용 백라이트 유닛.A light source;
1 to 30% by weight of polystyrene (PS) diffusion beads and green light converting beads 1 to 30 for absorbing light of a blue series wavelength band and emitting light of a green series wavelength band for diffusing light from the light source A light guide plate including a plurality of light guide patterns on one surface, the light guide plate being made of an ink composition comprising 20 to 25% by weight of an acrylate resin as a binder and 45 to 55% by weight of a solvent;
A reflection plate disposed below the light guide plate and reflecting the light toward the display panel;
And a backlight unit for a display device. 제10항에 있어서,
상기 폴리스티렌(Poly Styrene; PS) 확산비드는 1.59 이상의 광굴절률을 가지고, 상기 녹색 광변환 비드는 420~470nm의 주흡수 파장대역과 520~560nm의 주발광 파장대역을 가지는 표시장치용 백라이트 유닛.11. The method of claim 10,
Wherein the green light conversion bead has a main absorption wavelength band of 420 to 470 nm and a main emission wavelength band of 520 to 560 nm. 제11항에 있어서,
상기 PS 확산비드 및 상기 녹색 광변환 비드는 1~20μm의 크기를 가지는 표시장치용 백라이트 유닛.12. The method of claim 11,
Wherein the PS diffusion bead and the green light conversion bead have a size of 1 to 20 占 퐉. 제12항에 있어서,
폴리스티렌(Poly Styrene; PS) 확산 비드의 조성비는 25~30중량%이고, 상기 녹색 광변환 비드의 조성비는 1~10중량%인 표시장치용 백라이트 유닛.13. The method of claim 12,
Wherein the composition ratio of polystyrene (PS) diffusion beads is 25 to 30 wt%, and the composition ratio of the green photoconversion beads is 1 to 10 wt%.
KR1020150131117A 2015-09-16 2015-09-16 Ink Composition for Light Guiding Pattern and Light Guide Plate and Backlight Unit using the same KR102350686B1 (en)