KR20170027403A - Secondary Battery Comprising Binder having High Swelling Ratio - Google Patents
Secondary Battery Comprising Binder having High Swelling Ratio Download PDFInfo
- Publication number
- KR20170027403A KR20170027403A KR1020150123955A KR20150123955A KR20170027403A KR 20170027403 A KR20170027403 A KR 20170027403A KR 1020150123955 A KR1020150123955 A KR 1020150123955A KR 20150123955 A KR20150123955 A KR 20150123955A KR 20170027403 A KR20170027403 A KR 20170027403A
- Authority
- KR
- South Korea
- Prior art keywords
- secondary battery
- carbonate
- binder
- negative electrode
- battery according
- Prior art date
Abstract
Description
본 발명은 높은 팽윤도를 가진 바인더를 포함하는 이차전지에 관한 것이다.The present invention relates to a secondary battery comprising a binder having a high degree of swelling.
화석연료 사용의 급격한 증가로 인하여 대체 에너지나 청정에너지의 사용에 대한 요구가 증가하고 있으며, 그 일환으로 가장 활발하게 연구되고 있는 분야가 전기화학을 이용한 발전, 축전 분야이다.Due to the rapid increase in the use of fossil fuels, the demand for the use of alternative energy or clean energy is increasing. As a part of this, the most active field of research is electric power generation and storage.
현재 이러한 전기화학적 에너지를 이용하는 전기화학 소자의 대표적인 예로 이차전지를 들 수 있으며, 점점 더 그 사용 영역이 확대되고 있는 추세이다.At present, a typical example of an electrochemical device utilizing such electrochemical energy is a secondary battery, and the use area thereof is gradually increasing.
최근에는 휴대용 컴퓨터, 휴대용 전화기, 카메라 등의 휴대용 기기에 대한 기술 개발과 수요가 증가함에 따라 에너지원으로서 이차전지의 수요가 급격히 증가하고 있고, 그러한 이차전지 중 높은 에너지 밀도와 작동 전위를 나타내고 사이클 수명이 길며 자기방전율이 낮은 리튬 이차전지에 대해 많은 연구가 행해져 왔고, 또한 상용화되어 널리 사용되고 있다.2. Description of the Related Art [0002] Recently, as technology development and demand for portable devices such as portable computers, portable phones, and cameras have increased, the demand for secondary batteries as energy sources has increased sharply. Among such secondary batteries, they exhibit high energy density and operating potential, Many studies have been made on a lithium secondary battery having a long self discharge rate, and it has been commercialized and widely used.
일반적으로, 리튬 이차전지는, 양극의 리튬 이온이 음극으로 삽입되고 탈리되는 과정을 반복하면서 충전과 방전이 진행된다. 이러한 리튬 이온의 삽입, 탈리가 반복적으로 진행되면서, 전극 활물질 또는 도전재 사이의 결합이 느슨해지고, 입자간 접촉저항이 증가하게 된다. 그 결과 전극의 옴저항이 상승하여 전지 특성이 저하될 수 있다. 따라서, 바인더는 전극에서의 리튬 이온의 삽입, 탈리에 따른 전극 활물질의 팽창, 수축에 대해 완충작용을 할 수 있어야 하므로, 탄성을 갖는 고분자인 것이 바람직하다. Generally, in a lithium secondary battery, charging and discharging proceed while repeating the process in which lithium ions in the positive electrode are inserted into the negative electrode and desorbed. Such insertion and desorption of lithium ions repeatedly progresses, so that the bond between the electrode active material or the conductive material is loosened and the contact resistance between the particles is increased. As a result, the ohmic resistance of the electrode rises and the battery characteristics may deteriorate. Therefore, the binder is preferably a polymer having elasticity, since it is required to be capable of buffering against the expansion and contraction of the electrode active material due to insertion and desorption of lithium ions in the electrode.
또한, 바인더는 극판 건조 과정에서 전극 활물질과 집전체 사이의 결착력이 유지될 수 있을 정도의 접착력이 요구된다. 특히, 방전 용량을 높이기 위해, 이론적 방전 용량이 372 mAh/g인 천연 흑연에 방전 용량이 큰 실리콘, 주석, 실리콘-주석 합금 등과 같은 재료를 복합하여 사용하는 경우, 충전 및 방전이 진행됨에 따라 재료의 부피 팽창이 현저히 증가하게 되고, 이로 인해 음극재의 이탈이 발생하여, 결과적으로, 반복적인 사이클이 진행되면서 전지의 용량이 급격히 저하될 수 있다.Further, the binder is required to have an adhesive strength enough to maintain the binding force between the electrode active material and the current collector during the drying process of the electrode plate. Particularly, in order to increase the discharge capacity, when a material such as silicon, tin, silicon-tin alloy having a large discharging capacity is mixed with natural graphite having a theoretical discharge capacity of 372 mAh / g is used, The volume expansion of the negative electrode material significantly increases. As a result, deterioration of the negative electrode material occurs. As a result, the capacity of the battery may be drastically deteriorated as a repetitive cycle progresses.
또한, 리튬 이온 전지는 전지 내부 전해질 분해 시 발생하는 가스에 의해 부풀어 오르는 현상이 생기게 되는데, 이러한 전해질의 분해는 고온에서 촉진되므로, 전지를 고온에서 방치할 경우, 전지가 부풀어오르는 현상을 촉진된다. 이는 전지의 온도가 올라가면 전해액이 분해하거나 부반응이 일어나 이산화탄소나 일산화탄소와 같은 가스가 발생하여 전지의 두께가 증가하기 때문이다. 한편, 고온 저장에서의 두께 증가는 소형전지에서 중요하게 고려되는 사항으로서, 소형 기기 사용에 따라 전지의 온도가 급격히 올라가게 되어 고온에서의 두께 및 안정성의 문제가 되고 있다.In addition, the lithium ion battery has a phenomenon of swelling due to the gas generated upon decomposition of the electrolyte inside the battery. Such decomposition of the electrolyte is promoted at a high temperature, so that when the battery is left at a high temperature, the phenomenon of swelling of the battery is promoted. This is because when the temperature of the battery is increased, the electrolytic solution is decomposed or a side reaction occurs to generate gas such as carbon dioxide or carbon monoxide, thereby increasing the thickness of the battery. On the other hand, the increase in thickness in high-temperature storage is an important consideration in a small-sized battery, and as the use of a small-sized device increases, the temperature of the battery sharply increases, causing thickness and stability at high temperatures.
최근 전극조립체의 변형을 방지하기 위해 전극과 분리막간의 접착력을 증가시키는 형태로 이를 해결하고자 하는 시도들이 이루어지고 있다. 예를 들면, 바인더와 별도로 분리막에 접착력이 우수한 코팅층을 형성시켜 전극조립체의 팽창, 수축에 따른 응력 축적으로 인한 전극조립체의 구조적 변형을 방지하는 기술이 시도되고 있다.Recently, attempts have been made to solve this problem by increasing the adhesive force between the electrode and the separator in order to prevent deformation of the electrode assembly. For example, attempts have been made to prevent the structural deformation of the electrode assembly due to stress accumulation due to expansion and contraction of the electrode assembly by forming a coating layer having excellent adhesion to the separation membrane separately from the binder.
그러나, 별도의 코팅층을 부가하는 등의 추가적인 부재를 형성시키는 방법은 이러한 구성이 전지 내부의 전기적 저항 요소로 작용할 수 있고, 추가 공정에 따른 제조비용이 상승하여 현실적으로 적용하기 어려운 문제가 있었다.However, such a method of forming an additional member such as adding a separate coating layer has such a problem that such a configuration can act as an electrical resistance element inside the battery, and the manufacturing cost increases due to the additional process, which is difficult to be practically applied.
따라서, 이러한 문제점을 근본적으로 해결할 수 있는 기술에 대한 필요성이 높은 실정이다.Therefore, there is a high need for a technique capable of fundamentally solving such problems.
본 발명은 상기와 같은 종래기술의 문제점과 과거로부터 요청되어온 기술적 과제를 해결하는 것을 목적으로 한다.SUMMARY OF THE INVENTION It is an object of the present invention to solve the above-mentioned problems of the prior art and the technical problems required from the past.
본 출원의 발명자들은 심도 있는 연구와 다양한 실험을 거듭한 끝에, 이후 설명하는 바와 같이, 음극 시트의 음극 합제가 탄소계 활물질 및 규소계 활물질 중의 적어도 하나와 전해액을 흡수하여 팽윤(swelling)되는 성질을 가진 바인더를 포함할 경우, 충방전시 음극의 팽창 및 수축에 따라 축적된 응력을 전해액을 흡수하여 팽윤된 바인더를 통해 분산시켜 줌으로써, 전극조립체의 변형을 효과적으로 방지할 수 있는 바, 전지의 안정성 및 내구성이 우수한 이차전지를 제공할 수 있음을 확인하고, 본 발명을 완성하기에 이르렀다.The inventors of the present application have conducted intensive research and various experiments and have found that the negative electrode mixture of the negative electrode sheet absorbs and swells at least one of the carbonaceous active material and the silicon based active material When the binder contains a binder, deformation of the electrode assembly can be effectively prevented by absorbing the stress accumulated due to the expansion and contraction of the negative electrode during charging and discharging and dispersing the electrolyte through the swollen binder. As a result, It is possible to provide a secondary battery excellent in durability, and the present invention has been accomplished.
상기한 목적을 달성하기 위한, 본 발명에 따른 이차전지는,According to an aspect of the present invention, there is provided a secondary battery comprising:
양극 시트 및 음극 시트를 분리막 시트가 개재된 상태로 권취한 구조의 전극조립체를 포함하고 있는 이차전지로서,A secondary battery comprising an electrode assembly having a structure in which a positive electrode sheet and a negative electrode sheet are wound with a separator sheet interposed therebetween,
상기 음극 시트의 음극 합제는 탄소계 활물질 및 규소계 활물질 중의 적어도 하나와 전해액을 흡수하여 팽윤(swelling)되는 성질을 가진 바인더를 포함하고 있고,Wherein the negative electrode mixture of the negative electrode sheet includes a binder having a property of absorbing at least one of the carbon-based active material and the silicon-based active material and swelling the electrolyte,
상기 전극조립체는 비수계 유기 용매를 포함하는 전해액에 침지되어 전지케이스의 내부에 수납되어 있으며,The electrode assembly is immersed in an electrolytic solution containing a non-aqueous organic solvent and stored in a battery case,
상기 바인더는 전해액에 침지되기 전과 후의 부피를 비교하여 팽윤도가 100% 내지 300%를 나타내는 것을 특징으로 한다.The binder is characterized by exhibiting a degree of swelling of 100% to 300% by comparing volumes before and after being immersed in an electrolytic solution.
여기서, 팽윤도는 바인더가 전해액에 침지되기 전의 부피를 측정하고, 전해액에 침지된 후의 부피를 비교하여 부피가 증가된 비율을 의미하며, 예를 들어, 팽윤도가 100%일 경우, 전해액에 침지되기 전의 바인더의 부피의 두배 크기로 팽창한 것을 의미한다.Here, the degree of swelling refers to a rate at which the volume is measured by measuring the volume before the binder is immersed in the electrolytic solution and comparing the volume after immersion in the electrolytic solution. For example, when the degree of swelling is 100% It means that it has expanded to twice the volume of the binder.
따라서, 본 발명에 따른 이차전지는, 분리막 일면 또는 양면에 아크릴계 수지를 포함하는 접착층이 코팅되어 있고, 음극 시트의 음극 합제가 탄소계 활물질 및 규소계 활물질 중의 적어도 하나와 전해액을 흡수하여 팽윤(swelling)되는 성질을 가진 바인더를 포함하며, 상기 바인더는 전해액에 침지되기 전과 후의 부피를 비교하여 팽윤도가 100% 내지 300%를 나타냄으로써, 충방전시 음극의 팽창 및 수축에 따라 축적된 응력을 전해액을 흡수하여 팽윤된 바인더를 통해 분산시켜 줌으로써, 전극조립체의 변형을 효과적으로 방지할 수 있는 효과를 발휘한다.Accordingly, the secondary battery according to the present invention is characterized in that the separator has an adhesive layer coated on one side or both sides thereof with an acrylic resin, and the negative electrode mixture of the negative electrode sheet absorbs at least one of the carbonaceous active material and the silicon- ), And the binder exhibits a degree of swelling of 100% to 300% by comparing the volume before and after immersion in the electrolyte, so that the accumulated stress due to the expansion and contraction of the negative electrode during charging and discharging is referred to as " Dispersed through a binder which is swollen by absorption, thereby exhibiting an effect of effectively preventing deformation of the electrode assembly.
하나의 구체적인 예에서, 상기 전극조립체는, 적층된 양극 시트, 음극 시트, 및 분리막 시트가 롤(roll) 형상으로 권취된 구조이거나, 또는 롤 형상으로 권취된 후 일측 방향으로 압축되어 있는 구조일 수 있으며, 즉, 전극조립체는 수직 단면상으로 타원형으로 형성될 수 있다.In one specific example, the electrode assembly may be a structure in which the stacked positive electrode sheet, negative electrode sheet, and separator sheet are wound in a roll shape or wound in a roll shape and then compressed in one direction That is, the electrode assembly may be formed in an elliptical shape in a vertical section.
하나의 구체적인 예에서, 상기 전지케이스는 수지층과 금속층을 포함하는 라미네이트 시트의 전지 케이스, 또는 각형 전지에 사용되는 금속 캔일 수 있다.In one specific example, the battery case may be a battery case of a laminate sheet including a resin layer and a metal layer, or a metal can used for a prismatic battery.
하나의 구체적인 예에서, 상기 탄소계 활물질은 결정질 인조 흑연, 결정질 천연 흑연, 비정질 하드카본, 저결정질 소프트카본, 카본 블랙, 아세틸렌 블랙, 케첸 블랙, 수퍼-P, 그래핀(graphene), 및 섬유상 탄소로 이루어진 군으로부터 선택되는 하나 이상일 수 있고, 상세하게는 상기 탄소계 활물질은 결정질 천연 흑연일 수 있다. 또한, 상기 규소계 활물질은 규소, 산화규소 및 규소-탄소 복합체로 이루어진 군에서 선택되는 하나 이상일 수 있고, 상세하게는 산화규소일 수 있다.In one specific example, the carbonaceous active material is selected from the group consisting of crystalline graphite, crystalline natural graphite, amorphous hard carbon, low crystalline soft carbon, carbon black, acetylene black, Ketjenblack, Super-P, graphene, The carbon-based active material may be at least one selected from the group consisting of crystalline natural graphite. In addition, the silicon-based active material may be at least one selected from the group consisting of silicon, silicon oxide, and silicon-carbon composites, and may be silicon oxide in detail.
하나의 구체적인 예에서, 상기 바인더는 스티렌부타디엔 고무(styrene-butadiene rubber, SBR), 및 둘 이상의 아크릴레이트계 단량체들이 중합되어 이루어진 공중합체를 포함하고 있을 수 있고, 구체적으로, 상기 스티렌부타디엔 고무와 공중합체가 바인더에 함유된 비율은 30 : 70 내지 70 : 30의 범위일 수 있으며, 더욱 구체적으로, 40 : 60 내지 60 : 40일 수 있다.In one specific example, the binder may comprise a copolymer of styrene-butadiene rubber (SBR) and two or more acrylate monomers polymerized, and more specifically, the styrene-butadiene rubber The proportion of the coalescent contained in the binder may be in the range of from 30:70 to 70:30, and more specifically, from 40:60 to 60:40.
하나의 구체적인 예에서, 상기 아크릴레이트계 단량체는 메타아크릴록시 에틸에틸렌우레아, β-카르복시 에틸아크릴레이트, 알리파틱 모노아크릴레이트, 디프로필렌 디아크릴레이트, 디트리메틸로프로판 테트라아크릴레이트, 하이드록시에틸 아크릴레이트, 디펜타에리트리올 헥사아크릴레이트, 펜타에리트리올 트리아크릴레이트, 펜타에리트리올 테트라아크릴레이트, 라우릴 아크릴레이트, 세릴 아크릴레이트, 스테아릴 아크릴레이트, 라우릴 메타 아크릴레이트, 세릴 메타 아크릴레이트, 부틸 아크릴레이트, 글리시딜 메타 아크릴레이트, 알릴 메타 아크릴레이트 및 스테아릴 메타 아크릴레이트로 이루어진 군으로부터 선택되는 둘 이상일 수 있다.In one specific example, the acrylate-based monomer is selected from the group consisting of methacryloxyethylethylene urea,? -Carboxyethyl acrylate, aliphatic monoacrylate, dipropylene diacrylate, ditrimethylpropane tetraacrylate, hydroxyethyl acrylate Acrylate, stearyl acrylate, lauryl methacrylate, cerium methacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate, lauryl acrylate, And may be two or more selected from the group consisting of butyl acrylate, butyl acrylate, glycidyl methacrylate, allyl methacrylate and stearyl methacrylate.
또한, 상기 공중합체는 중량 평균 분자량이 10,000 내지 1,000,000을 가지고 있을 수 있고, 중합도는 1,000 내지 100,000을 가지고 있을 수 있다. 즉, 본 발명에 따른 상기 공중합체를 포함하는 바인더는 공중합체의 분자량 및 중합도에 따라 전해액을 흡수(uptake)하는 성질이 변화될 수 있고, 상기와 같은 중합도 및 분자량을 가질 경우, 본 발명이 요구하는 적정 범위의 스웰링을 발휘할 수 있다.In addition, the copolymer may have a weight average molecular weight of 10,000 to 1,000,000, and a degree of polymerization of 1,000 to 100,000. That is, the binder comprising the copolymer according to the present invention can change the property of uptake of the electrolyte depending on the molecular weight and the degree of polymerization of the copolymer, and when the polymerization degree and the molecular weight are as described above, It is possible to exhibit swelling in an appropriate range.
반면에, 상기 공중합체의 중량 평균 분자량이 10,000 미만이고, 중합도가 1,000 미만인 경우, 전해액 흡수하는 성질이 너무 커져 과도한 스웰링이 발생할 수 있고, 더불어 바인더의 강성이 약해 적절한 접착력을 발휘하기 어려우며, 또한, 상기 공중합체의 중량 평균 분자량이 1,000,000 초과이고, 중합도는 100,000를 초과하는 경우, 전해액 흡수하는 성질이 너무 작아 적정 범위의 스웰링 형상을 일으키지 못하며, 전극의 팽창 수축에 따른 응력을 적절히 분산시키기 어렵다.On the other hand, when the weight average molecular weight of the copolymer is less than 10,000 and the degree of polymerization is less than 1,000, the property of absorbing the electrolyte becomes excessively large, excessive swelling may occur, and the rigidity of the binder is weak, , When the weight average molecular weight of the copolymer exceeds 1,000,000 and the degree of polymerization exceeds 100,000, the property of absorbing the electrolyte is too small to cause an appropriate range of swelling, and it is difficult to appropriately disperse the stress due to the expansion and contraction of the electrode .
하나의 구체적인 예에서, 상기 바인더의 함량은 음극 합제 전체 중량을 기준으로 0.5 중량% 내지 5 중량%일 수 있다.In one specific example, the content of the binder may be from 0.5 wt% to 5 wt%, based on the total weight of the anode mix.
또한, 상기 음극 합제는 분산제를 더 포함할 수 있고, 상기 분산제는 카르복시메틸셀룰로오스나트륨(CMC-Na) 또는 도데실벤젠설폰산나트륨일 수 있다. 상세하게는, 상기 분산제는 음극 합제 전체 중량을 기준으로 0.02 중량% 내지 5 중량%로 포함될 수 있다.The negative electrode material mixture may further include a dispersant, and the dispersant may be carboxymethylcellulose sodium (CMC-Na) or sodium dodecylbenzenesulfonate. Specifically, the dispersing agent may be contained in an amount of 0.02 wt% to 5 wt% based on the total weight of the negative electrode material mixture.
하나의 구체적인 예에서, 상기 음극 시트에 코팅된 음극 합제는 건조 및 압연 후 두께가 50 ㎛ 내지 300 ㎛로 형성될 수 있다.In one specific example, the negative electrode mixture coated on the negative electrode sheet may be formed to a thickness of 50 mu m to 300 mu m after drying and rolling.
한편, 상기 이차전지에서 바인더의 팽윤도는 바인더를 필름형태로 제조한 후, 상온(섭씨 15도 내지 섭씨 25도)에서 24시간 동안 전해액에 침지한 후, 상기 필름의 부피 변화를 측정하여 산정할 수 있고, 이때, 전해액은 비수계 유기 용매인 에틸렌카보네이트(EC), 프로필렌카보네이트(PC), 및 디에틸카보네이트(DEC)의 혼합물로 이루어질 수 있으며, 상기 비수계 유기 용매의 에틸렌카보네이트(EC), 프로필렌카보네이트(PC), 및 디에틸카보네이트(DEC)의 혼합 비율은 3 : 2 : 5일 수 있다.Meanwhile, the degree of swelling of the binder in the secondary battery can be calculated by measuring the volume change of the film after the binder is formed into a film form, immersed in an electrolytic solution for 24 hours at room temperature (15 degrees Celsius to 25 degrees Celsius) (EC), propylene carbonate (PC), and diethyl carbonate (DEC). The non-aqueous organic solvent may be ethylene carbonate (EC), propylene carbonate The mixing ratio of carbonate (PC) and diethyl carbonate (DEC) may be 3: 2: 5.
하나의 구체적인 예에서, 상기 비수계 유기 용매는 에틸렌카보네이트(EC), 프로필렌카보네이트(PC), 에틸메틸카보네이트(EMC), 디메틸카보네이트(DMC), 디에틸카보네이트(DEC), 플루오로에틸렌카보네이트(FEC), 메틸프로필카보네이트(MPC), 에틸프로필카보네이트(EPC), 메틸에틸 카보네이트(MEC), 부틸렌카보네이트(BC), 에틸아세테이트(ethyl acetate), 메틸아세테이트(methyl acetate), 프로필아세테이트(propyl acetate), 에틸프로피오네이트(ethyl propionate), 메틸프로피오네이트(methyl propionate), 프로필프로피오네이트(propyl propionate) 및 이들의 혼합물로 이루어진 군에서 선택되는 어느 하나일 수 있고, 상세하게는 상기 비수계 유기 용매는 에틸렌카보네이트(EC), 프로필렌카보네이트(PC), 및 디에틸카보네이트(DEC)의 혼합물로 이루어질 수 있으며, 더욱 상세하게는, 상기 비수계 유기 용매의 에틸렌카보네이트(EC), 프로필렌카보네이트(PC), 및 디에틸카보네이트(DEC)의 혼합 비율은 3 : 2 : 5 내지 2 : 3 : 5일 수 있다.In one specific example, the non-aqueous organic solvent is selected from the group consisting of ethylene carbonate (EC), propylene carbonate (PC), ethyl methyl carbonate (EMC), dimethyl carbonate (DMC), diethyl carbonate (DEC), fluoroethylene carbonate ), Methylpropyl carbonate (MPC), ethyl propyl carbonate (EPC), methyl ethyl carbonate (MEC), butylene carbonate (BC), ethyl acetate, methyl acetate, propyl acetate Ethyl propionate, methyl propionate, propyl propionate, and mixtures thereof. In particular, the non-aqueous organic solvent may be selected from the group consisting of water, The solvent may be composed of a mixture of ethylene carbonate (EC), propylene carbonate (PC), and diethyl carbonate (DEC), and more specifically, The mixing ratio of ethylene carbonate (EC), propylene carbonate (PC), and diethyl carbonate (DEC) in the base solvent may be 3: 2: 5 to 2: 3: 5.
한편, 본 발명의 이차전지는 하나 이상의 이차전지용 음극, 양극, 상기 음극과 양극 사이에 개재된 분리막 및 비수 전해질을 포함하는 리튬 이차전지일 수 있다.Meanwhile, the secondary battery of the present invention may be a lithium secondary battery including at least one negative electrode for a secondary battery, a positive electrode, a separator interposed between the negative electrode and the positive electrode, and a nonaqueous electrolyte.
이러한 리튬 이차전지는, 예를 들면, 양극, 분리막, 음극 구조의 전극조립체가 전해액과 함께 전지케이스의 내부에 밀봉되어 있는 파우치형 전지셀일 수 있고, 전체적으로 폭 대비 두께가 얇은 대략 직육면체 구조인 판상형으로 이루어져 있다. 이러한 파우치형 전지셀은 일반적으로 파우치형의 전지케이스로 이루어져 있으며, 상기 전지케이스는 내구성이 우수한 고분자 수지로 이루어진 외부 피복층; 수분, 공기 등에 대해 차단성을 발휘하는 금속 소재로 이루어진 차단층; 및 열융착될 수 있는 고분자 수지로 이루어진 내부 실란트층이 순차적으로 적층되어 있는 라미네이트 시트 구조로 구성되어 있다.Such a lithium secondary battery may be, for example, a pouch-shaped battery cell in which an electrode assembly having an anode, a separator, and a cathode structure is sealed inside a battery case together with an electrolytic solution, and is a plate- consist of. Such a pouch-shaped battery cell is generally composed of a battery case of a pouch type, and the battery case is composed of an outer coating layer made of a polymer resin having excellent durability; A barrier layer made of a metal material exhibiting barrier properties against moisture, air, and the like; And an inner sealant layer composed of a polymer resin that can be thermally fused, are laminated in this order.
상기 양극은, 예를 들어, 양극 집전체 상에 양극 활물질, 도전재 및 바인더의 혼합물을 도포한 후 건조하여 제조되며, 필요에 따라서는, 상기 혼합물에 충진제를 더 첨가하기도 한다.The positive electrode is prepared, for example, by coating a mixture of a positive electrode active material, a conductive material and a binder on a positive electrode current collector, and then drying the mixture. Optionally, a filler may be further added to the mixture.
상기 양극 집전체는 일반적으로 3 마이크로미터 내지 500 마이크로미터의 두께로 만든다. 이러한 양극 집전체는, 당해 전지에 화학적 변화를 유발하지 않으면서 높은 도전성을 가지는 것이라면 특별히 제한되는 것은 아니며, 예를 들어, 스테인리스 스틸, 알루미늄, 니켈, 티탄, 소성 탄소, 또는 알루미늄이나 스테인리스 스틸의 표면에 카본, 니켈, 티탄, 은 등으로 표면 처리한 것 등이 사용될 수 있다. 집전체는 그것의 표면에 미세한 요철을 형성하여 양극 활물질의 접착력을 높일 수도 있으며, 필름, 시트, 호일, 네트, 다공질체, 발포체, 부직포체 등 다양한 형태가 가능하다.The cathode current collector generally has a thickness of 3 micrometers to 500 micrometers. Such a positive electrode current collector is not particularly limited as long as it has high conductivity without causing chemical change in the battery, and may be formed of a material such as stainless steel, aluminum, nickel, titanium, sintered carbon, or a surface of aluminum or stainless steel Treated with carbon, nickel, titanium, silver or the like may be used. The current collector may have fine irregularities on the surface thereof to increase the adhesive force of the cathode active material, and various forms such as a film, a sheet, a foil, a net, a porous body, a foam, and a nonwoven fabric are possible.
상기 양극 활물질은 전기화학적 반응을 일으킬 수 있는 물질로서, 리튬 전이금속 산화물로서, 2 이상의 전이금속을 포함하고, 예를 들어, 1 또는 그 이상의 전이금속으로 치환된 리튬 코발트 산화물(LiCoO2), 리튬 니켈 산화물(LiNiO2) 등의 층상 화합물; 1 또는 그 이상의 전이금속으로 치환된 리튬 망간 산화물; 화학식 LiNi1-yMyO2 (여기서, M = Co, Mn, Al, Cu, Fe, Mg, B, Cr, Zn 또는 Ga이고 상기 원소 중 하나 이상의 원소를 포함, 0.01≤y≤0.7 임)으로 표현되는 리튬 니켈계 산화물; Li1+zNi1/3Co1/3Mn1/3O2, Li1+zNi0.4Mn0.4Co0.2O2 등과 같이 Li1+zNibMncCo1-(b+c+d)MdO(2-e)Ae (여기서, -0.5≤z≤0.5, 0.1≤b≤0.8, 0.1≤c≤0.8, 0≤d≤0.2, 0≤e≤0.2, b+c+d<1 임, M = Al, Mg, Cr, Ti, Si 또는 Y 이고, A = F, P 또는 Cl 임)으로 표현되는 리튬 니켈 코발트 망간 복합산화물; 화학식 Li1+xM1-yM'yPO4-zXz(여기서, M = 전이금속, 바람직하게는 Fe, Mn, Co 또는 Ni 이고, M' = Al, Mg 또는 Ti 이고, X = F, S 또는 N 이며, -0.5≤x≤+0.5, 0≤y≤0.5, 0≤z≤0.1 임)로 표현되는 올리빈계 리튬 금속 포스페이트 등을 들 수 있지만, 이들만으로 한정되는 것은 아니다.The cathode active material is a material capable of causing an electrochemical reaction. Examples of the lithium transition metal oxide include lithium cobalt oxide (LiCoO 2 ) containing two or more transition metals and substituted with one or more transition metals, lithium Layered compounds such as nickel oxide (LiNiO 2 ); Lithium manganese oxide substituted with one or more transition metals; Formula LiNi 1-y M y O 2 ( where, M = Co, Mn, Al , Cu, Fe, Mg, B, Cr, Zn or Ga and Lim, 0.01≤y≤0.7 include one or more elements of the element) A lithium nickel-based oxide represented by the following formula: Li 1 + z Ni 1/3 Co 1/3 Mn 1/3 O 2, Li 1 + z Ni 0.4 Mn 0.4 Co 0.2 O 2 , such as Li 1 + z Ni b Mn c Co 1- (b + c + d ) M d O (2-e ) A e ( where, -0.5≤z≤0.5, 0.1≤b≤0.8, 0.1≤c≤0.8, 0≤d≤0.2 , 0≤e≤0.2, b + c + d <1, M = Al, Mg, Cr, Ti, Si or Y, and A = F, P or Cl; lithium nickel cobalt manganese composite oxide; And the formula Li 1 + x M 1-y M 'y PO 4-z X z ( wherein, M = a transition metal, preferably Fe, Mn, Co or Ni, M' = Al, Mg or Ti, X = F, S or N, and -0.5? X? +0.5, 0? Y? 0.5, and 0? Z? 0.1), but the present invention is not limited thereto.
상기 도전재는 통상적으로 양극 활물질을 포함한 혼합물 전체 중량을 기준으로 1 내지 20 중량%로 첨가된다. 이러한 도전재는 당해 전지에 화학적 변화를 유발하지 않으면서 도전성을 가진 것이라면 특별히 제한되는 것은 아니며, 예를 들어, 천연 흑연이나 인조 흑연 등의 흑연; 카본블랙, 아세틸렌 블랙, 케첸 블랙, 채널 블랙, 퍼네이스 블랙, 램프 블랙, 서머 블랙 등의 카본블랙; 탄소 섬유나 금속 섬유 등의 도전성 섬유; 불화 카본, 알루미늄, 니켈 분말 등의 금속 분말; 산화아연, 티탄산 칼륨 등의 도전성 위스키; 산화 티탄 등의 도전성 금속 산화물; 폴리페닐렌 유도체 등의 도전성 소재 등이 사용될 수 있다.The conductive material is usually added in an amount of 1 to 20 wt% based on the total weight of the mixture including the cathode active material. Such a conductive material is not particularly limited as long as it has electrical conductivity without causing chemical changes in the battery, for example, graphite such as natural graphite or artificial graphite; Carbon black such as carbon black, acetylene black, ketjen black, channel black, furnace black, lamp black, and summer black; Conductive fibers such as carbon fiber and metal fiber; Metal powders such as carbon fluoride, aluminum, and nickel powder; Conductive whiskey such as zinc oxide and potassium titanate; Conductive metal oxides such as titanium oxide; Conductive materials such as polyphenylene derivatives and the like can be used.
상기 충진제는 양극의 팽창을 억제하는 성분으로서 선택적으로 사용되며, 당해 전지에 화학적 변화를 유발하지 않으면서 섬유상 재료라면 특별히 제한되는 것은 아니며, 예를 들어, 폴리에틸렌, 폴리프로필렌 등의 올리핀계 중합체; 유리섬유, 탄소섬유 등의 섬유상 물질이 사용된다.The filler is optionally used as a component for suppressing the expansion of the anode, and is not particularly limited as long as it is a fibrous material without causing a chemical change in the battery. Examples of the filler include olefin polymers such as polyethylene and polypropylene; Fibrous materials such as glass fibers and carbon fibers are used.
상기 음극 집전체는 일반적으로 3 마이크로미터 내지 500 마이크로미터의 두께로 만들어진다. 또한, 양극 집전체와 마찬가지로, 표면에 미세한 요철을 형성하여 음극 활물질의 결합력을 강화시킬 수도 있으며, 필름, 시트, 호일, 네트, 다공질체, 발포체, 부직포체 등 다양한 형태로 사용될 수 있다.The negative electrode current collector is generally made to have a thickness of 3 micrometers to 500 micrometers. In addition, like the positive electrode collector, fine unevenness can be formed on the surface to enhance the bonding force of the negative electrode active material, and it can be used in various forms such as films, sheets, foils, nets, porous bodies, foams and nonwoven fabrics.
상기 분리막은 양극과 음극 사이에 개재되며, 높은 이온 투과도와 기계적 강도를 가지는 절연성의 얇은 박막이 사용된다. 분리막의 기공 직경은 일반적으로 0.01 마이크로미터 내지 10 마이크로미터이고, 두께는 일반적으로 5 마이크로미터 내지 300 마이크로미터이다. 이러한 분리막으로는, 예를 들어, 내화학성 및 소수성의 폴리프로필렌 등의 올레핀계 폴리머; 유리섬유 또는 폴리에틸렌 등으로 만들어진 시트나 부직포 등이 사용된다. 전해질로서 폴리머 등의 고체 전해질이 사용되는 경우에는 고체 전해질이 분리막을 겸할 수도 있다.The separation membrane is interposed between the anode and the cathode, and an insulating thin film having high ion permeability and mechanical strength is used. The pore diameter of the separator is generally 0.01 micrometer to 10 micrometers, and the thickness is generally 5 micrometers to 300 micrometers. Such separation membranes include, for example, olefinic polymers such as polypropylene, which are chemically resistant and hydrophobic; A sheet or nonwoven fabric made of glass fiber, polyethylene or the like is used. When a solid electrolyte such as a polymer is used as an electrolyte, the solid electrolyte may also serve as a separation membrane.
본 발명은, 또한 상기 이차전지를 포함하고 있는 것을 특징으로 하는 전지팩을 제공한다.The present invention also provides a battery pack characterized by including the secondary battery.
본 발명은, 또한 상기 전지팩을 전원으로 포함하고 있는 디바이스를 제공한다. 구체적으로, 상기 디바이스는 예를 들어, 휴대폰, 휴대용 컴퓨터, 웨어러블 전자기기, 태플릿 PC, 스마트 패드, 넷북, LEV(Light Electronic Vehicle), 전기자동차, 하이브리드 전기자동차, 플러그-인 하이브리드 전기자동차, 및 전력저장장치로 이루어진 군에서 선택될 수 있다.The present invention also provides a device including the battery pack as a power source. Specifically, the device may be, for example, a cellular phone, a portable computer, a wearable electronic device, a tablet PC, a smart pad, a netbook, a LEV (Light Electronic Vehicle), an electric vehicle, a hybrid electric vehicle, a plug- And a power storage device.
이러한 디바이스의 구조 및 제작 방법은 당업계에 공지되어 있으므로, 본 명세서에서는 그에 대한 자세한 설명을 생략한다.The structure and manufacturing method of such a device are well known in the art, so a detailed description thereof will be omitted herein.
이상의 설명과 같이, 본 발명에 따른 이차전지는, 분리막 일면 또는 양면에 아크릴계 수지를 포함하는 접착층이 코팅되어 있고, 음극 시트의 음극 합제가 탄소계 활물질 및 규소계 활물질 중의 적어도 하나와 전해액을 흡수하여 팽윤(swelling)되는 성질을 가진 바인더를 포함하며, 상기 바인더는 전해액에 침지되기 전과 후의 부피를 비교하여 팽윤도가 100% 내지 300%를 나타냄으로써, 충방전시 음극의 팽창 및 수축에 따라 축적된 응력을 전해액을 흡수하여 팽윤된 바인더를 통해 분산시켜 줌으로써, 전극조립체의 변형을 효과적으로 방지할 수 있는 효과를 발휘한다.As described above, the secondary battery according to the present invention is characterized in that an adhesive layer comprising an acrylic resin is coated on one side or both sides of the separator, and the negative electrode mixture of the negative electrode absorbs at least one of the carbonaceous active material and the silicon- Wherein the binder exhibits a degree of swelling of 100% to 300% by comparing the volume before and after being immersed in the electrolyte, whereby the accumulated stress due to the expansion and contraction of the negative electrode during charging and discharging Absorbing the electrolyte solution and dispersing the electrolyte solution through the swollen binder, thereby effectively preventing deformation of the electrode assembly.
이하의 실시예, 비교예 및 실험예에서 본 발명의 내용을 보다 구체적으로 설명하지만, 본 발명이 이에 제한되는 것은 아니다.In the following Examples, Comparative Examples and Experimental Examples, the contents of the present invention will be described in more detail, but the present invention is not limited thereto.
<실시예 1> ≪ Example 1 >
<1-1 전극의 제조>≪ Production of 1-1 electrode >
음극은 전체 고형분 100 g 중량 기준으로 천연 흑연 97.0 g (MS46, BTR ENERGY MATERIALS CO., LTD.), 바인더로 스티렌-부타디엔계 고무 30 중량%와, 중량 평균 분자량이 30,000이고 중합도가 10,000이 되도록 부틸 아크릴레이트 단량체 및 글리시딜 메타아크릴레이트 단량체를 중합한 공중합체 70 중량%를 혼합하여 이루어진 혼합물 1.5 g, 및 분산제로 카르복시메틸셀룰로오스나트륨 1.5 g (CMC-Na, BG-L01, ㈜지엘켐)을 혼합하고, 전체 고형분 함량이 55 중량%가 되도록 용매로서 N-메틸피롤리돈(NMP)을 첨가하여 음극용 슬러리를 제조하며, 준비된 슬러리를 구리 호일에 도포한 후 진공 건조 및 압연하여 두께가 149 마이크로미터인 음극을 제조하였다.The negative electrode was prepared by mixing 97.0 g of natural graphite (MS46, BTR ENERGY MATERIALS CO., LTD.), 30 weight% of a styrene-butadiene rubber as a binder with a weight average molecular weight of 30,000 and a degree of polymerization of 10,000 1.5 g of a mixture prepared by mixing 70% by weight of a copolymer of an acrylate monomer and a glycidyl methacrylate monomer, and 1.5 g of carboxymethylcellulose sodium (CMC-Na, BG-L01, (NMP) as a solvent so as to have a total solid content of 55% by weight to prepare a slurry for a cathode. The prepared slurry was applied to a copper foil, followed by vacuum drying and rolling to obtain a slurry having a thickness of 149 A micrometer cathode was prepared.
양극은, NMP(N-methyl-2-pyrrolidone)를 분산매로 사용하고, 활물질인 LiCoO2 96 g, 아세틸렌 블랙 2 g 및 PVDF 바인더2 g를 혼합하여 슬러리를 제조한 후 알루미늄 호일에 100 마이크로미터의 두께로 코팅하여 건조한 후 압착하여 양극을 제조하였다.The anode was prepared by mixing 96 g of active material LiCoO 2 , 2 g of acetylene black and 2 g of PVDF binder with NMP (N-methyl-2-pyrrolidone) as a dispersion medium to prepare a slurry, And dried to form a positive electrode.
<1-2 리튬 이차전지의 제조>≪ Preparation of 1-2 lithium secondary battery &
제조된 음극 극판을 표면적 13.33 cm2로 뚫고, 양극 극판은 표면적 12.60 cm2로 뚫어 단일셀(mono-cell)을 제작하였다. 탭을 상기 양극의 상부 및 상기 음극의 상부에 부착하고, 음극과 양극 사이에 폴리올레핀 미세 다공막으로 만들어진 분리막으로 개재시켜 상기 결과물을 알루미늄 파우치에 적재한 후, 전해액 500 mg을 파우치 내부에 주입하였다. 전해액은, EC(Ethyl Carbonate): PC(Propylene Carbonate): DEC(Diethyl Carbonate) = 3:2:5(체적비) 혼합용매를 사용하여 LiPF6 전해질을 1M의 농도로 용해시켜 제조하였다. 이후, 진공포장기를 이용하여 상기 파우치를 밀봉하고 상온에서 12시간 동안 유지시킨 후, 약 0.05도 비율로 정전류 충전하고 전류의 약 1/6이 될 때까지 전압을 유지시켜주는 정전압 충전 과정을 거친다. 이때, 셀 내부에 가스가 발생하므로, 탈 가스(degassing)와 재실링(resealing)과정을 수행하여 리튬 이차전지를 완성하였다.The prepared negative electrode plate was drilled at a surface area of 13.33 cm 2 , and the positive electrode plate was drilled at a surface area of 12.60 cm 2 to prepare a single cell (mono-cell). A tab was attached to the upper part of the positive electrode and the upper part of the negative electrode. The resultant was placed between the negative electrode and the positive electrode with a separator made of a polyolefin microporous membrane, and the resultant was placed in the aluminum pouch. Then, 500 mg of the electrolytic solution was injected into the pouch. The electrolytic solution was prepared by dissolving LiPF 6 electrolyte at a concentration of 1M using a mixed solvent of EC (Ethyl Carbonate): PC (Propylene Carbonate): DEC (Diethyl Carbonate) = 3: 2: 5 (volume ratio) Thereafter, the pouch is sealed using a vacuum packing machine, and the pouch is maintained at room temperature for 12 hours, and then subjected to a constant voltage charging process in which a constant current is charged at a rate of about 0.05 degree and a voltage is maintained until the voltage becomes about 1/6 of a current. At this time, since gas is generated inside the cell, degassing and resealing are performed to complete the lithium secondary battery.
<비교예 1> ≪ Comparative Example 1 &
음극 제조시, 음극 합제의 바인더로 스티렌-부타디엔계 고무 및 부틸 아크릴레이트 단량체 및 글리시딜 메타아크릴레이트 단량체를 중합한 공중합체로 이루어진 혼합물 대신에 아크릴계 공중합체로 이루어진 바인더(CSB130, Toyo ink社)를 사용한 것을 제외하고는, 실시예 1과 동일한 방법으로 리튬 이차전지를 제조하였다.(CSB130, manufactured by Toyo ink) instead of a mixture of a copolymer obtained by polymerizing a styrene-butadiene rubber, a butyl acrylate monomer and a glycidyl methacrylate monomer as a binder of the negative electrode mixture in the preparation of a negative electrode, , A lithium secondary battery was produced in the same manner as in Example 1. The results are shown in Table 1. < tb > < TABLE >
<비교예 2> ≪ Comparative Example 2 &
음극 제조시, 음극 합제의 바인더로 스티렌-부타디엔계 고무 및 부틸 아크릴레이트 단량체 및 글리시딜 메타아크릴레이트 단량체를 중합한 공중합체로 이루어진 혼합물 대신에 부타디엔 공중합체로 이루어진 바인더(BD53, ㈜LG화학)를 사용한 것을 제외하고는, 실시예 1과 동일한 방법으로 리튬 이차전지를 제조하였다.(BD53, manufactured by LIG Chemical Co., Ltd.) instead of a mixture of a copolymer of a styrene-butadiene rubber, a butyl acrylate monomer and a glycidyl methacrylate monomer as a binder for an anode mix in the production of a negative electrode, , A lithium secondary battery was produced in the same manner as in Example 1. The results are shown in Table 1. < tb > < TABLE >
<실험예 1> (바인더의 전해액 침지에 따른 부피 변화 측정)≪ Experimental Example 1 > (Measurement of volume change due to immersion of electrolyte in electrolyte)
우선 제조된 이차전지 실시예 1, 비교예 1, 및 비교예 2의 각각에서 사용된 바인더를 건조 후 두께가 20 ㎛되도록 필름을 바코딩으로 형성하고, 반지름이 8 mm인 원형으로 절단하여 원기둥 형태의 시편을 취하였다.First, the binder used in each of the secondary batteries of Example 1, Comparative Example 1, and Comparative Example 2 was dried, bar-coded to form a film having a thickness of 20 탆, cut into a circular shape having a radius of 8 mm, .
상기 준비된 시편들을 EC(Ethyl Carbonate): PC(Propylene Carbonate): DEC(Diethyl Carbonate) = 3 : 2 : 5 (체적비) 혼합용매를 사용하고 LiPF6 전해질을 1M의 농도로 용해시켜 제조된 전해액에 침지한 뒤, 섭씨 25도로 설정된 항온 챔버에 48시간 보관 후 변화된 부피를 측정하였고, 부피 변화량을 산정한 결과를 하기 표 1에 나타내었다.The prepared specimens were immersed in an electrolytic solution prepared by dissolving a LiPF 6 electrolyte at a concentration of 1 M using a mixed solvent of EC (Ethyl Carbonate): PC (Propylene Carbonate): DEC (Diethyl Carbonate) = 3: 2: 5 After changing the volume, the volume was measured after being stored in a constant-temperature chamber set at 25 DEG C for 48 hours. The volume change was calculated and the results are shown in Table 1 below.
상기 표 1의 결과와 같이, 실시예 1의 바인더는, 비교예 1 및 비교예 2에 비해 팽윤률이 매우 크므로, 비교예들의 바인더들에 비해 전해액을 흡수(uptake)하는 성질이 매우 큰 것을 알 수 있고, 전해액의 흡수량이 커짐에 따라 바인더의 기계적 성질이 더욱 소프트해짐으로 음극의 체적변화에 충분한 완충작용을 수행할 것이 예상된다.As shown in Table 1, since the binder of Example 1 has a much higher swelling rate than that of Comparative Examples 1 and 2, it has a very high property of uptaking the electrolyte compared to the binders of the comparative examples It is expected that the mechanical property of the binder becomes more soft as the amount of absorption of the electrolyte becomes larger, thereby performing a sufficient buffering action for the volume change of the negative electrode.
<실험예 2> (이차전지의 고온 저장시 두께변화 측정)≪ Experimental Example 2 > (Measurement of Thickness Change at High Temperature Storage of Secondary Battery)
우선 제조된 이차전지 실시예 1, 비교예 1, 및 비교예 2의 각각의 음극의 두께를 측정한 후, 실시예 1, 비교예 1 및 비교예 2를 섭씨 90도로 설정된 항온 챔버에 4시간 보관 후 전지를 분해하여 음극의 두께를 측정하였고, 이러한 두께 변화량을 산정한 결과를 하기 표 2에 나타내었다.First prepared secondary batteries The thicknesses of the cathodes of Example 1, Comparative Example 1 and Comparative Example 2 were measured, and then Example 1, Comparative Example 1 and Comparative Example 2 were stored in a constant temperature chamber set at 90 degrees Celsius for 4 hours The thickness of the cathode was measured by disassembling the battery, and the thickness variation was calculated. The results are shown in Table 2 below.
음극의 두께(㎛)Early
Thickness of cathode (탆)
음극의 두께 (㎛)After high temperature storage
Thickness of cathode (탆)
상기 표 2의 결과와 같이, 본 발명에 따른 이차전지용 음극을 사용한 실시예 1은, 비교예 1에 비해 두께 변화량이 적은 바, 음극의 팽창 및 수축에 따른 응력 발생에 대한 음극 바인더의 완충 능력이 향상됨으로써, 충방전시 음극의 팽창 및 수축으로 인해 유발되는 전극조립체의 변형을 효과적으로 방지할 수 있고, 전지의 안정성 및 내구성이 향상될 것을 예상할 수 있다.As shown in Table 2, Example 1 using the negative electrode for a secondary battery according to the present invention had a small amount of change in thickness as compared with Comparative Example 1, and the buffering capacity of the negative electrode binder against stress generation due to the expansion and contraction of the negative electrode It is possible to effectively prevent the deformation of the electrode assembly caused by the expansion and contraction of the negative electrode during charging and discharging and to improve the stability and durability of the battery.
앞서 설명하였듯이, 본 발명에 따른 이차전지는, 음극 시트에 전해액을 흡수하여 팽윤도가 100% 내지 300%으로 팽윤(swelling)되는 성질을 가진 바인더를 적용함으로써, 충방전시 음극의 팽창 및 수축에 따라 축적된 응력을 전해액을 흡수하여 팽윤된 바인더를 통해 분산시켜 줌으로써, 전극조립체의 변형을 효과적으로 방지할 수 있는 효과를 발휘한다.As described above, the secondary battery according to the present invention uses a binder having a property of swelling the positive electrode sheet by absorbing the electrolytic solution to have a degree of swelling of 100% to 300%, so that the negative electrode sheet can be swollen and contracted The accumulated stress is absorbed and dispersed through the swollen binder, thereby effectively preventing deformation of the electrode assembly.
본 발명이 속한 분야에서 통상의 지식을 가진 자라면 내용을 바탕으로 본 발명의 범주내에서 다양한 응용 및 변형을 행하는 것이 가능할 것이다.Those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims.
Claims (19)
상기 음극 시트의 음극 합제는 탄소계 활물질 및 규소계 활물질 중의 적어도 하나와 전해액을 흡수하여 팽윤(swelling)되는 성질을 가진 바인더를 포함하고 있고,
상기 전극조립체는 비수계 유기 용매를 포함하는 전해액에 침지되어 전지케이스의 내부에 수납되어 있으며,
상기 바인더는 전해액에 침지되기 전과 후의 부피를 비교하여 팽윤도가 100% 내지 300%를 나타내는 것을 특징으로 하는 이차전지.A secondary battery comprising an electrode assembly having a structure in which a positive electrode sheet and a negative electrode sheet are wound with a separator sheet interposed therebetween,
Wherein the negative electrode mixture of the negative electrode sheet includes a binder having a property of absorbing at least one of the carbon-based active material and the silicon-based active material and swelling the electrolyte,
The electrode assembly is immersed in an electrolytic solution containing a non-aqueous organic solvent and stored in a battery case,
Wherein the binder exhibits a degree of swelling of 100% to 300% by comparing the volume before and after being immersed in the electrolytic solution.