KR20150114086A - Coating Composition of Aluminum Sheet for Heat Discharge Plate of Television and Pre-coated Aluminum Sheet Using the same - Google Patents

Coating Composition of Aluminum Sheet for Heat Discharge Plate of Television and Pre-coated Aluminum Sheet Using the same Download PDF

Info

Publication number
KR20150114086A
KR20150114086A KR1020140037802A KR20140037802A KR20150114086A KR 20150114086 A KR20150114086 A KR 20150114086A KR 1020140037802 A KR1020140037802 A KR 1020140037802A KR 20140037802 A KR20140037802 A KR 20140037802A KR 20150114086 A KR20150114086 A KR 20150114086A
Authority
KR
South Korea
Prior art keywords
resin
weight
aluminum
steel sheet
acid
Prior art date
Application number
KR1020140037802A
Other languages
Korean (ko)
Other versions
KR101590942B1 (en
Inventor
노진균
Original Assignee
포스코강판 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 포스코강판 주식회사 filed Critical 포스코강판 주식회사
Priority to KR1020140037802A priority Critical patent/KR101590942B1/en
Publication of KR20150114086A publication Critical patent/KR20150114086A/en
Application granted granted Critical
Publication of KR101590942B1 publication Critical patent/KR101590942B1/en

Abstract

The present invention relates to a pre-coated metal (PCM) paint composition of an aluminum plating steel plate for a television radiation plate and an aluminum plating steel plate produced thereby. A radiation function is more improved, and flexibility and processability can be simultaneously improved. To this end, according to the present invention, the PCM paint composition of an aluminum plating steel plate used as a television radiation plate includes a resin, a cross-linking agent, a hardening catalyst, a solvent, and an additive. The resin is produced by mixing an A resin and a B resin at the same weight ratio, and 15-35 wt% of each of the same is added with respect to a total composition. The A resin is a polyester resin having reinforced flexibility and has a weight average molecular weight of 15,000-20,000, a hydroxyl value of 20-40 mgKOH/g, an acid value of 1-5 mgKOH/g, and a glass transition temperature of 10-20°C. The B resin has 40-60 wt% of an aromatic component in an overall combination to improve adhesion, a weight average molecular weight of 30,000-35,000, a hydroxyl value of 10-30 mgKOH/g, an acid value of 1-3 mgKOH/g, and a glass transition temperature of 25-35°C. 1.0-2.0 wt% of boron nitride is added as a radiation filler with respect to the total composition.

Description

텔레비젼 방열판용 알루미늄 도장강판의 피씨엠 도료 조성물 및 이에 의해 제조된 알루미늄 도장강판{Coating Composition of Aluminum Sheet for Heat Discharge Plate of Television and Pre-coated Aluminum Sheet Using the same}TECHNICAL FIELD The present invention relates to an aluminum-coated steel sheet for a TV heat sink and an aluminum-coated steel sheet produced by the method.

본 발명은 텔레비젼 방열판용 알루미늄 도장강판의 피씨엠 도료 조성물 및 이에 의해 제조된 알루미늄 도장강판에 관한 것으로서, 더욱 상세하게는, 텔레비젼 의 리어 패널로 사용되는 알루미늄 시트 또는 알루미늄 도장강판의 방열성능, 가공성 및 도료 부착성을 향상시킴으로써, 텔레비젼 내부에서 발생한 열을 효과적으로 방열할 수 있도록 한 텔레비젼 방열판용 알루미늄 도장강판의 피씨엠 도료 조성물 및 이에 의해 제조된 알루미늄 도장강판에 관한 것이다. The present invention relates to an aluminum-coated steel sheet for an aluminum-coated steel sheet for a TV heat sink, and to an aluminum-coated steel sheet produced by the method. More particularly, the present invention relates to an aluminum- To an aluminum-coated steel sheet for an aluminum heat-sealed steel sheet for a TV heat-radiating plate, which is capable of effectively dissipating heat generated in a television by improving paint adhesion, and an aluminum-coated steel sheet produced thereby.

최근의 텔레비젼은 대부분 디스플레이 장치가 얇은 평면으로 이루어진 평판형으로 제조되고 있다. [0003] In recent years, most of the televisions are manufactured in a flat plate shape in which the display device is thin and flat.

현재 평판형 텔레비젼에 사용되는 디스플레이 장치로는, 플라즈마 디스플레이 장치(PDP: Plasma Disply Panel), 액정표시장치(LCD: Liquid Crystal Display), 발광다이오드(LED: Light Emitting Diode), 유기발광 다이오드(OLED: Organic Light Emitting Diode)를 이용한 디스플레이 장치 등이 알려져 있다.2. Description of the Related Art Currently, display devices used in flat panel televisions include a plasma display panel (PDP), a liquid crystal display (LCD), a light emitting diode (LED), an organic light emitting diode (OLED) Organic Light Emitting Diodes) are known.

상기한 플라즈마 디스플레이 장치(이하 간단히 'PDP'라 한다)는, 전면유리와 배면유리 및 그 사이의 칸막이에 의해 밀폐된 유리 사이에 Ne+Ar, Ne+Xe 등의 가스를 주입한 후, 양극과 음극의 전극에 의해 전압을 인가하여 네온광을 발광시킨다. The plasma display device (hereinafter, simply referred to as 'PDP') has a structure in which a gas such as Ne + Ar or Ne + Xe is injected between a front glass and a rear glass and a glass sealed by a partition therebetween, A voltage is applied by the cathode electrode to emit neon light.

즉, PDP는 마주보고 대향하는 전극 사이에 가스를 봉입한 후, 전압을 인가함으로써 발생하는 가스방전을 이용하여 정보를 표시한다.That is, the PDP displays information by using a gas discharge generated by applying a voltage after sealing a gas between opposed electrodes facing each other.

또한, 액정표시장치(이하 'LCD'라 한다)는 액정 표시 패널의 내부에 주입된 액정 물질의 전기적, 광학적 성질을 이용하여 정보를 표시하는 장치로서, 텔레비젼 뿐만 아니라 컴퓨터의 모니터, 휴대용 비디오 카메라, 디지털 카메라 등 각종 정보화기기 및 통신기기에 광범위하게 사용되고 있다.In addition, a liquid crystal display (hereinafter, referred to as 'LCD') is an apparatus for displaying information using electrical and optical properties of a liquid crystal material injected into a liquid crystal display panel, Digital cameras, and the like.

상기 LCD는, 정보처리장치로부터 영상신호를 인가받아 액정제어용 신호로 변환한 후, 액정을 통해 광의 투과량을 조절하여 전기적 형태의 영상신호를 육안으로 인식할 수 있도록 한 것이다.The LCD receives an image signal from an information processing apparatus, converts the image signal into a liquid crystal control signal, and adjusts the amount of light transmitted through the liquid crystal to visually recognize an image signal of an electrical form.

LED TV는, LCD TV에서 백라이트의 광원으로 발광다이오드(Light Emitting Diode)를 사용한 것이다. The LED TV uses a light emitting diode as a light source of a backlight in an LCD TV.

또한 최근에는 유기발광 다이오드(Organic Light Emitting Diode)를 이용한 디스플레이 장치가 주목을 받고 있다(이하 'OLED'라 한다).In recent years, a display device using an organic light emitting diode (OLED) has attracted attention.

상기한 OLED는 빛을 발광하는 층이 유기 화합물로 되어 있는 발광 다이오드로서 PM(Passive Matrix)OLED(수동형 유기발광 다이오드)와 AM(Active Matrix)OLED(능동형 유기발광 다이오드)로 구분할 수 있다. The OLED may be classified into a passive matrix OLED (passive matrix OLED) and an active matrix OLED (active matrix OLED) as a light emitting diode in which the light emitting layer is an organic compound.

상기한 디스플레이 장치를 채용한 텔레비젼은, 전면의 프런트 패널(Front Panel)과 배면의 리어 패널(Rear Panel) 사이에 각종 부품들을 내장하고 있다. [0003] In the television adopting the above-described display device, various components are embedded between a front panel on the front side and a rear panel on the rear side.

그런데 최근의 텔레비젼은 화면이 대형화되면서 두께가 얇아지고 있어, 내부에서 발생하는 열을 효과적으로 방열시키는 것이 중요한 과제로 대두되고 있다.However, recent TVs have become thinner as the screen becomes larger, and it is becoming an important task to effectively dissipate the heat generated from the inside.

즉, 텔레비젼의 화면이 대형화되면 그 내부에서 발생하는 열도 증가하게 되는데, 최근의 텔레비젼은 두께도 얇아지고 있어 방열성능의 확보가 문제가 되고 있는 것이다. In other words, when the screen of a television becomes large, the heat generated inside the TV increases. In recent years, the thickness of a television becomes thin, and it is a problem to secure heat radiation performance.

텔레비젼 내부에서 발생된 열이 외부로 원활하게 배출되지 못하면, 화면에 잔상을 발생시켜 화면의 품질을 떨어뜨리고 각종 전기부품에도 악영향을 미치게 된다. If the heat generated inside the TV can not be discharged smoothly to the outside, a residual image is generated on the screen, which degrades the quality of the screen and adversely affects various electric parts.

이러한 문제점을 개선하기 위하여, 텔레비젼 리어 패널(이하 '방열판'이라 한다)의 소재로서 일반 강판보다 방열성이 양호한 알루미늄 소재 또는 알루미늄을 도금한 알루미늄 도금강판(이하 통칭하여 '알루미늄 도금강판'이라 한다)을 사용하기도 한다. In order to solve such a problem, an aluminum-plated steel sheet (hereinafter collectively referred to as an "aluminum-plated steel sheet") plated with an aluminum material or aluminum having a better heat dissipation than a general steel sheet as a material for a television rear panel It is also used.

그러나 상기한 종래의 알루미늄 도금강판은 PCM(Pre-coated Metal)용으로 제조할 때 가공성이 저하되고 방열성능이 미흡하다는 문제점이 있다.However, the above-mentioned conventional aluminum-coated steel sheet has a problem in that when it is manufactured for PCM (Pre-coated Metal), the workability is lowered and the heat radiation performance is insufficient.

또한 종래의 알루미늄 도금강판은 도료의 부착성이 저하된다는 문제점이 지적되고 있다.In addition, it has been pointed out that the conventional aluminum-plated steel sheet is deteriorated in the adhesion of the paint.

: 한국 공개특허 제10-2005-0006378호(2005. 1. 17. 공개): Korean Patent Publication No. 10-2005-0006378 (disclosed on January 17, 2005) : 한국 공개특허 제10-2009-0063367호(2009. 6. 18. 공개): Korean Published Patent No. 10-2009-0063367 (disclosed on June 18, 2009)

본 발명은 상기한 종래기술의 문제점을 해결하기 위해 제안하는 것으로서, 텔레비젼의 방열판으로 사용되는 알루미늄 도금강판의 방열성능을 대폭 향상시키는데 그 목적이 있다.SUMMARY OF THE INVENTION The present invention has been made in order to solve the problems of the prior art described above, and it is an object of the present invention to significantly improve the heat radiation performance of an aluminum-plated steel sheet used as a heat sink of a television.

본 발명의 다른 목적은, 알루미늄 도금강판을 피씨엠용으로 제조할 때, 유연성을 강화시킬 수 있는 수지와 도료 부착성을 향상시킬 수 있는 수지를 혼합한 도료를 혼합하여 도포함으로써, 가공성 및 도료 부착성을 동시에 향상시키는 데 있다.It is another object of the present invention to provide a method for producing an aluminum-plated steel sheet by mixing and applying a mixture of a resin capable of enhancing flexibility and a resin capable of improving paint adhesion to produce an aluminum- At the same time.

본 발명의 또 다른 목적은, 텔레비젼 방열판의 외관을 미려하게 마무리하여 상품성을 향상시키는 데 있다.It is still another object of the present invention to improve the merchantability by finely finishing the appearance of the TV heat sink.

상기한 목적을 달성하기 위하여 본 발명은, 수지, 가교제, 경화 촉매, 용제 및 첨가제를 포함하여 구성되어, 텔레비젼 방열판으로 사용되는 알루미늄 도장강판의 피씨엠(PCM: Pre-coated Metal) 도료 조성물에 있어서, 상기 수지는, A 수지와 B 수지가 동일 중량비로 혼합되어 전체 조성물에 대하여 각각 15∼35 중량% 첨가되고, 상기 A 수지는, 유연성이 강화된 폴리에스테르 수지로서, 중량평균 분자량 15,000∼20,000, 수산가 20∼40 mgKOH/g, 산가 1∼5 mgKOH/g, 유리전이온도 10∼20℃이고, 상기 B 수지는, 부착성을 높이기 위해 전체 배합에서 방향족 성분을 40~60 중량%로 하고, 중량평균 분자량 30,000∼35,000, 수산가 10∼30 mgKOH/g, 산가 1∼3 mgKOH/g, 유리전이온도 25∼35℃이며, 방열성능을 향상시키기 위한 방열 필러(Filler)로서 질화붕소(Boron Nitride)가 전체 조성물에 대하여 1.0~2.0 중량% 첨가되는 것을 특징으로 한다. In order to achieve the above object, the present invention provides a PCM (Pre-coated Metal) coating composition comprising a resin, a crosslinking agent, a curing catalyst, a solvent and an additive and used as a TV heat sink, , And the resin A is mixed with the resin A and the resin B at the same weight ratio and added in an amount of 15 to 35 wt% with respect to the total composition, and the resin A is a polyester resin having enhanced flexibility and a weight average molecular weight of 15,000 to 20,000, The acid value is 20 to 40 mgKOH / g, the acid value is 1 to 5 mgKOH / g, and the glass transition temperature is 10 to 20 占 폚. The B resin has an aromatic component in an amount of 40 to 60% Boron nitride is used as a heat dissipating filler to improve the heat radiation performance, and the glass transition temperature is in the range of 30 to 35,000, the acid value is 10 to 30 mgKOH / g, the acid value is 1 to 3 mgKOH / g, 1.0 to 2.0 < RTI ID = 0.0 > It characterized in that the percent by weight is added.

또한, 도막의 가공성을 유지하기 위해 분자 구조 내에 프로판디올(Propanediol), 헥산디올(Hexanediol), 부단디올(Butanediol) 중 어느 하나의 모노머가 25~40 중량% 함유되는 것을 특징으로 한다. In order to maintain the processability of the coating film, 25 to 40% by weight of a monomer selected from the group consisting of propanediol, hexanediol, and butanediol is contained in the molecular structure.

또한, 상기 가교제는, 메톡시기를 갖는 메틸에테르화 멜라민 수지가 3∼7 중량%, 우레탄 가교제가 1∼3 중량% 함유되는 것을 특징으로 한다. The crosslinking agent is characterized by containing 3 to 7% by weight of a methyl etherified melamine resin having a methoxy group and 1 to 3% by weight of a urethane crosslinking agent.

또한, 상기 경화 촉매는, p-톨루엔 술폰산(p-TSA), 디노닐나프탈렌 술폰산(DNNSA), 디나프탈렌 디술폰산(DNNDSA), 플루오로 술폰산 중 어느 하나의 술폰산을 2차 아민 또는 에폭시로 중화시켜 얻은 중화 생성물이고, 우레탄 가교 결합을 위해 Tin촉매(DBTDL)를 적용하는 특징으로 한다.The curing catalyst may be prepared by neutralizing a sulfonic acid of any one of p-toluenesulfonic acid (p-TSA), dinonylnaphthalenesulfonic acid (DNNSA), dinaphthalene disulfonic acid (DNNDSA), and fluorosulfonic acid with a secondary amine or epoxy The resulting neutralized product is characterized by the application of a Tin catalyst (DBTDL) for urethane crosslinking.

또한, 본 발명에 따른 텔레비젼 방열판용 알루미늄 도장강판은 상기 피씨엠 도료 조성물을 도포하여 제조되는 것을 특징으로 한다. Further, the aluminum coated steel sheet for a TV heat sink according to the present invention is characterized in that it is manufactured by applying the PC M coating composition.

본 발명에 의하면, 피씨엠용 도료 조성물에 방열 필러를 첨가하여 방열기능을 더욱 향상시킴으로써 텔레비젼 내부에서 발생되는 열을 효과적으로 방열시킬 수 있는 효과가 있다. According to the present invention, a heat radiating filler is added to the coating composition for PCM to further improve the heat radiating function, thereby effectively dissipating heat generated in the television.

또한, 유연성을 강화시킬 수 있는 수지와 도료 부착성을 향상시킬 수 있는 수지를 혼합한 도료를 혼합하여 도포함으로써, 가공성 및 도료 부착성을 동시에 향상시킬 수 있는 효과가 있다.In addition, there is an effect that both the workability and the paint adhesion can be improved by mixing and applying a paint in which a resin capable of enhancing flexibility and a resin capable of improving paint adhesion is mixed and applied.

또한, 텔레비젼 방열판의 외관을 미려하게 마무리하여 상품성을 향상시킬 수 있는 효과가 있다. In addition, there is an effect that the appearance of the TV heat sink is finely finished and the merchantability is improved.

도 1은 본 발명에 따른 알루미늄 도장강판의 개략적인 단면도.1 is a schematic sectional view of an aluminum-coated steel sheet according to the present invention.

이하 본 발명에 따른 바람직한 실시예를 도 1을 참조하여 상세히 설명한다. Hereinafter, preferred embodiments according to the present invention will be described in detail with reference to FIG.

본 발명에 따른 알루미늄 도장강판의 도료 조성물은, 도 1에 도시된 바와 같이, 알루미늄 시트 또는 알루미늄 도장강판(이하 통칭하여 '알루미늄 도장강판'이라 한다)의 소지강판(10)에 일반적인 피씨엠 도료와 같이 하도 도막층(30)과 상도 도막층(40)으로 도포된다.As shown in FIG. 1, the coating composition of the aluminum-coated steel sheet according to the present invention can be applied to a base steel sheet 10 of an aluminum sheet or an aluminum-coated steel sheet (hereinafter collectively referred to as an aluminum-coated steel sheet) And is applied with the coating layer 30 and the top coat layer 40 as well.

즉, 소지강판(10)의 양면에 전처리층(20)을 형성하고, 하도 도막층(30)과 상도 도막층(40)을 차례로 형성하며, 배면에는 배면층(50)을 형성한다. That is, the pretreatment layer 20 is formed on both sides of the base steel sheet 10, the undercoat layer 30 and the overcoat layer 40 are formed in order, and the back layer 50 is formed on the back surface.

상기한 전처리층(20) 및 배면층(50)을 형성하는 것은 공지의 기술이므로 이에 대한 상세한 설명은 생략하고, 이하 하도 도막층(30)과 상도 도막층(40)을 형성하는 본 발명에 따른 도료 조성물에 대해서만 살펴보기로 한다. Since the pretreatment layer 20 and the back layer 50 are formed by a known technique, a detailed description thereof will be omitted, and the following description will be given of the present invention in which the undercoat layer 30 and the top coat layer 40 are formed. Only the coating composition will be discussed.

본 발명에 따른 텔레비젼 방열판용 알루미늄 도장강판의 도료 조성물은, 수지, 가교제, 경화 촉매, 용제 및 첨가제를 포함하여 구성되는 피씨엠(PCM: Pre-coated Metal) 도료 조성물에 있어서, 상기 수지는, 'A 수지'와 'B 수지'가 동일 중량비로 혼합되어 전체 조성물에 대하여 각각 15∼35 중량% 첨가된다. The coating composition for an aluminum-coated steel sheet for a TV heat sink according to the present invention is a PCM (Pre-coated Metal) coating composition comprising a resin, a crosslinking agent, a curing catalyst, a solvent and an additive, A resin " and " B resin " are mixed in the same weight ratio and added in an amount of 15 to 35 wt% with respect to the total composition.

상기 피씨엠은 하도 도료와 상도 도료가 미리 도장된 상태로 제조되는 것으로서, 이를 성형하여 가공하면 바로 완제품이 제조될 수 있다. The PCM is manufactured in a state in which the undercoat paint and the topcoat are coated in advance, and the finished product can be manufactured immediately after molding and processing.

여기서 상기 'A 수지'는, 유연성이 강화된 폴리에스테르 수지로서, 분자량 15,000∼20,000, 수산가 20∼40 mgKOH/g, 산가 1∼5 mgKOH/g, 유리전이온도 10∼20℃인 것이 바람직하다.The 'A resin' is preferably a flexible polyester resin having a molecular weight of 15,000 to 20,000, a hydroxyl value of 20 to 40 mg KOH / g, an acid value of 1 to 5 mg KOH / g and a glass transition temperature of 10 to 20 ° C.

또한, 상기 'B 수지'는, 도료의 부착성을 높이기 위해 전체 배합에서 방향족 성분을 40-60 중량%로 하고, 중량평균 분자량 30,000∼35,000, 수산가 10∼30 mgKOH/g, 산가 1∼3 mgKOH/g, 유리전이온도 25∼35℃인 것이 바람직하다.In order to improve the adhesion of the paint, the 'B resin' is used in an amount of 40 to 60% by weight in terms of aromatic components in the total blend, and has a weight average molecular weight of 30,000 to 35,000, a hydroxyl value of 10 to 30 mgKOH / g, / g, and a glass transition temperature of 25 to 35 캜.

본 발명은 유연성을 강화하여 가공성을 향상시키는 'A 수지'와 도료 부착성을 강화시키는 'B 수지'를 각각 제조한 후 이를 혼합하여 도포함으로써, 가공성 향상과 동시에 도료 부착성을 향상시켰다는데 그 특징이 있다.The present invention improves the workability and paint adhesion by preparing 'A resin' for enhancing flexibility and improving 'B resin' for enhancing workability and mixing, .

즉 본 발명은, 기존의 일반적인 도료는 배제하고 수지 Backbone의 유연성을 최대한 증가시켜 가공성을 향상시킨 'A 수지'와, 기존 수지의 분자량보다 최대 2~3배 증가되도록 하여 부착성을 향상시킨 분자구조를 갖는 'B 수지'를 혼합하여 사용한다. That is, the present invention relates to a resin composition comprising a resin A that improves workability by eliminating conventional coatings and maximizes the flexibility of a resin backbone and a molecular structure that improves adhesiveness by increasing the molecular weight by 2 to 3 times 'B resin' having a specific gravity is used.

또한 본 발명은 필러(Filler)로서 백색의 흑연이라 불리는 질화붕소(Boron Bitride)를 1.0~2.0 중량% 첨가함으로써, 방열성능을 대폭 향상시켰다는데 그 특징이 있다. Further, the present invention is characterized in that 1.0 to 2.0 wt% of boron nitride, which is called a white graphite, is added as a filler, thereby significantly improving the heat radiation performance.

그리고 본 발명에 따른 도료 조성물에는, 상기 수지 성분 외에 가교제 5∼10 중량%, 경화 촉매 0.5∼2.0 중량%, 용제 30∼50 중량%, Tacky성 개선 첨가제 0.3∼1.0 중량%, 레벨링제 0.5∼ 1.0 중량%, 소포제 0.5∼1.0 중량% 및 안료 2∼5 중량%가 더 첨가된다. The coating composition according to the present invention may further contain, in addition to the resin component, 5 to 10 wt% of a crosslinking agent, 0.5 to 2.0 wt% of a curing catalyst, 30 to 50 wt% of a solvent, 0.3 to 1.0 wt% of a tackiness improving additive, 0.5 to 1.0% by weight of an antifoaming agent and 2 to 5% by weight of a pigment are further added.

현재 피씨엠(PCM: Pre-coated Metal)도료는, 대부분 하도 코팅과 상도 코팅의 2 Coat 시스템으로 이루어지며, 도막 두께는 20~30㎛ 범위로 도포된다.Currently, PCM (Pre-coated Metal) coatings consist mostly of undercoat and topcoat 2 Coat systems, and coating thickness is 20 ~ 30㎛.

그러나 본 발명에 의하면, 도막 두께를 13~17㎛의 박막형으로 형성하면서도, 가공성 및 도료 부착성을 향상시킴과 동시에 방열성능을 대폭 향상시킬 수가 있다.However, according to the present invention, it is possible to improve the workability and paint adhesion while improving the heat radiation performance, while forming the film thickness of 13 to 17 mu m in a thin film form.

이하 본 발명에 따른 피씨엠 도료 조성물의 각 성분에 대하여 설명한다. Hereinafter, each component of the PCM paint composition according to the present invention will be described.

<폴리에스테르 수지><Polyester resin>

본 발명에 따른 'A 수지'는 중량평균 분자량 15,000~20,000, 수산가 20∼40 mgKOH/g, 산가 1∼5 mgKOH/g, 유리전이온도 10∼20℃인 것을 사용하는 것이 바람직하다.The 'A resin' according to the present invention preferably has a weight average molecular weight of 15,000 to 20,000, a hydroxyl value of 20 to 40 mg KOH / g, an acid value of 1 to 5 mg KOH / g and a glass transition temperature of 10 to 20 ° C.

상기 중량평균 분자량이 20,000을 초과하게 되면 작업성이 저하되고, 15,000 미만이 되면 도막의 가공성 및 내구성을 유지하기가 어려워진다. When the weight average molecular weight exceeds 20,000, the workability is deteriorated. When the weight average molecular weight is less than 15,000, it is difficult to maintain the workability and durability of the coating film.

또한 도막의 가공성을 유지하기 위해, 상기 분자구조 내에 프로판디올(Propanediol), 헥산디올(Hexanediol), 부탄디올(Bbutanediol) 등의 모노머(Monomer)를 25~40 중량%, 바람직하게는 30 중량% 함유하는 것이 좋다. In order to maintain the processability of the coating film, 25 to 40% by weight, preferably 30% by weight, of monomers such as propanediol, hexanediol and butanediol are contained in the molecular structure It is good.

상기 모노머의 함량이 40 중량%를 초과하게 되면 작업성이 저하되고, 25 중량% 미만이 되면 도막의 가공성 및 내구성을 유지하기가 어려워진다. When the content of the monomer exceeds 40 wt%, the workability is deteriorated. When the content of the monomer is less than 25 wt%, it is difficult to maintain the workability and durability of the coating film.

상기 'B 수지'는, 전체 배합에서 방향족 성분을 40-60 중량%로 하고, 중량평균 분자량 30,000∼35,000, 수산가 10∼30 mgKOH/g, 산가 1∼3 mgKOH/g, 유리전이온도 25∼35℃ 인 것을 사용하는 것이 바람직하다.The 'B resin' has a weight average molecular weight of 30,000 to 35,000, a hydroxyl value of 10 to 30 mgKOH / g, an acid value of 1 to 3 mgKOH / g, a glass transition temperature of 25 to 35 Lt; 0 &gt; C.

상기 중량평균 분자량이 35,000을 초과하게 되면 작업성이 저하되고, 30,000 미만이 되면 도막의 부착성을 유지하기가 어려워진다. When the weight average molecular weight exceeds 35,000, the workability is deteriorated. When the weight average molecular weight is less than 30,000, it is difficult to maintain the adhesion of the coating film.

또한 방향족 모노머의 함량이 60 중량%를 초과하게 되면 작업성이 저하되고, 40 중량% 미만이 되면 도막의 부착성을 유지하기가 어렵다. When the content of the aromatic monomer is more than 60% by weight, workability is deteriorated. When the content of the aromatic monomer is less than 40% by weight, it is difficult to maintain the adhesion of the coating film.

상기 'A 수지'와 'B 수지'가 혼합된 혼합수지 함량은, 전체 도료 조성물에 대하여 30∼70 중량%인 것이 바람직하다.The mixed resin content in which the 'A resin' and the 'B resin' are mixed is preferably 30 to 70% by weight based on the total coating composition.

상기 혼합 수지의 함량이 70 중량%를 초과하게 되면 도료 내에 수지분이 지나치게 많아지게 되어 도막의 건조도가 저하되고, 30 중량% 미만이 되면 도막의 가공성 및 부착성이 저하되는 문제가 있다.When the content of the mixed resin exceeds 70% by weight, the amount of the resin component in the coating becomes excessively large and the drying degree of the coating film decreases. When the content of the mixed resin is less than 30% by weight, the processability and adhesion of the coating film deteriorate.

다음의 [표 1]은 본 발명에 따른 'A 수지'의 실시예 및 기존 수지와의 비교예, [표 2]는 본 발명에 따른 'B 수지'의 실시예, [표 3]은 본 발명에 따른 'A 수지'와 'B 수지'를 기존의 상도형 수지와 비교한 비교예를 나타낸 것이다.[Table 1] shows examples of 'A resin' according to the present invention and comparative examples with existing resins, [Table 2] shows examples of 'B resin' according to the present invention, and [Table 3] A resin &quot; and &quot; B resin &quot; according to the present invention are compared with the conventional top-form resin.

A 수지의 실시예 및 비교예Examples of resin A and comparative examples 실시예Example 1One 22 33 44 비교예(기존수지)Comparative Example (existing resin) 항목Item 알코올Alcohol EGEG 5.05.0 5.05.0 3.03.0 3.03.0 NPGNPG 14.014.0 12.012.0 12.012.0 9.09.0 34.034.0 1,6HD1.6HD 26.026.0 3030 6.06.0 PDPD 28.028.0 30.030.0 산mountain IPAIPA 32.032.0 37.037.0 25.025.0 35.035.0 35.035.0 TPATPA 15.015.0 18.018.0 20.020.0 2323 5.05.0 AAAA 8.08.0 10.010.0 2020 첨가제additive DBTODBTO 0.10.1 0.10.1 0.10.1 0.10.1 0.10.1 희석용제Diluting solvent CH/K150=4/6CH / K150 = 4/6 비중importance 1.051.05 1.051.05 1.051.05 1.051.05 1.051.05 점도Viscosity WW XX WW XX XX 고형분Solids 50.350.3 50.750.7 50.250.2 60.060.0 60.060.0 산가Acid value 2.52.5 2.12.1 2.12.1 5.05.0 5.05.0 분자량Molecular Weight 17,00017,000 17,00017,000 18,00018,000 15,00015,000 12,00012,000 수산기값Hydroxyl value 2929 2828 2727 2626 4040 NPG:네오펜틸글리콜, EG:에틸렌글리콜, 1,6HD:1,6헥산디올, PD:프로판디올
IPA:이소프탈산, TPA:테레프탈산, AA:아디핀산
점도:50%용액(25℃ 가드너)
분자량: 중량평균 분자량(GPC)NPG: neopentyl glycol, EG: ethylene glycol, 1,6HD: 1,6 hexanediol, PD: propanediol
IPA: isophthalic acid, TPA: terephthalic acid, AA: adipic acid
Viscosity: 50% solution (25 캜 Gardner)
Molecular weight: weight average molecular weight (GPC)

B 수지의 실시예B resin 실시예Example 1One 22 33 44 항목Item 알코올Alcohol EGEG 2.02.0 2.02.0 2.02.0 NPGNPG 10.010.0 14.014.0 13.013.0 20.020.0 1,6HD1.6HD 2727 25.025.0 25.025.0 18.018.0 TMPTMP 1.01.0 1.01.0 1.01.0 산mountain IPAIPA 33.033.0 34.034.0 30.030.0 35.035.0 TPATPA 20.020.0 21.021.0 23.023.0 19.019.0 AAAA 7.07.0 5.05.0 7.07.0 6.06.0 첨가제additive Fascat4100Fascat4100 0.10.1 0.10.1 0.10.1 0.10.1 희석용제Diluting solvent K100/PMA=1/1K100 / PMA = 1/1 비중importance 1.051.05 1.051.05 1.051.05 1.051.05 점도Viscosity Z3Z3 Z4Z4 Z3Z3 Z4+Z4 + 고형분Solids 40.040.0 40.240.2 40.140.1 40.540.5 산가Acid value 1.51.5 1.61.6 1.11.1 1.21.2 분자량Molecular Weight 34,20034,200 33,90033,900 33,50033,500 33,60033,600 수산기값Hydroxyl value 1818 2020 1919 2020 NPG:네오펜틸글리콜, EG:에틸렌글리콜, 1,6HD:1,6헥산디올, TMP:트리메칠올프로판
IPA:이소프탈산, TPA:테레프탈산, AA:아디핀산
점도:40%용액(25℃ 가드너)
분자량: 중량평균분자량(GPC)NPG: neopentyl glycol, EG: ethylene glycol, 1,6HD: 1,6hexanediol, TMP: trimethylolpropane
IPA: isophthalic acid, TPA: terephthalic acid, AA: adipic acid
Viscosity: 40% solution (25 캜 Gardner)
Molecular weight: weight average molecular weight (GPC)

A 수지와 B 수지의 기존 상도형 수지와의 비교예Comparative Example of Resin A and Resin B with Existing Topical Resin 기존 상도형 수지Existing top resin A수지A resin B수지B resin 고형분(%)Solid content (%) 6060 5050 4040 점도Viscosity V-XV-X W-YW-Y Z3-Z5Z3-Z5 분자량Molecular Weight 11,000-13,00011,000-13,000 15,000-20,00015,000-20,000 25,000-30,00025,000-30,000 수산기값Hydroxyl value 10-6010-60 20-4020-40 10-3010-30 TgTg 20-40℃20-40 ° C 10-20℃10-20 ° C 25-35℃25-35 ℃

<가교제> <Cross-linking agent>

본 발명에서는 상기한 수지성분과 도막을 형성하기 위한 가교제로서, 멜라민 수지와 이소시아네이트 수지를 동시에 적용하였다. In the present invention, a melamine resin and an isocyanate resin are simultaneously applied as a crosslinking agent for forming a coating film with the resin component.

기존의 피씨엠 도료에 적용되는 대부분의 가교제는 멜라민 수지이나, 멜라민 수지를 단독으로 적용하면, 도막 강도는 우수하나 도막의 가공성 및 부착성이 상대적으로 취약한 단점이 있다.Most of the cross-linking agents applied to conventional PCM paints have a disadvantage in that the melamine resin or melamine resin is applied alone, but the processability and adhesion of the coating film are relatively weak.

반면에 이소시아네이트 수지를 단독으로 적용하게 되면, 가공성 및 부착성은 우수하나 상대적으로 도막 경도가 저하되는 단점이 있다.On the other hand, when the isocyanate resin is used alone, it has an excellent workability and adhesion, but has a drawback that the hardness of the coating film is lowered relatively.

이러한 문제점을 해결하기 위해 본 발명에서는, 산촉매 적용시 경화 반응속도가 빠르고 경화 반응성이 우수한 메톡시 멜라민 수지를 적용함과 동시에 Blocked된 이소시아네이트 수지를 1:0.2~0.4로 혼합하여 사용하였다.In order to solve these problems, a methoxymelamine resin having a fast curing reaction rate and excellent curing reactivity was applied to the acid catalyst, and blocked isocyanate resin was mixed in a ratio of 1: 0.2 to 0.4.

상기 두 경화제 수지의 혼합비가 1:0.4 를 초과하게 되면 도막의 표면 경화가 저하되고, 1:0.2 미만이 되면 도막의 가공성 및 부착성이 저하되는 단점이 있다. When the mixing ratio of the two hardener resins exceeds 1: 0.4, the surface hardening of the coating film is lowered. When the mixing ratio is less than 1: 0.2, the workability and adhesion of the coating film are deteriorated.

<경화 촉매><Curing Catalyst>

본 발명에서는 경화 촉매로서, p-톨루엔 술폰산(p-TSA), 디노닐나프탈렌 술폰산(DNNSA), 디나프탈렌 디술폰산(DNNDSA), 플루오로 술폰산 중에서 선택된 어느 하나의 술폰산을 아민 또는 에폭시로 중화시킨 것을 사용하였고, 우레탄 가교결합을 위해 Tin촉매(DBTDL)를 사용하였다.In the present invention, as a curing catalyst, one obtained by neutralizing an sulfonic acid selected from p-toluenesulfonic acid (p-TSA), dinonylnaphthalenesulfonic acid (DNNSA), dinaphthalene disulfonic acid (DNNDSA), and fluorosulfonic acid with an amine or epoxy , And Tin catalyst (DBTDL) was used for urethane crosslinking.

상기한 경화촉매는 전체 도료 조성물에 대하여 0.5∼2.0 중량% 범위로 함유시키는 것이 바람직하다. The curing catalyst is preferably contained in an amount of 0.5 to 2.0 wt% based on the total coating composition.

<특수 방열 필러(Filler)><Special Heat Filler>

본 발명에서는 방열 필러로서 질화붕소(Boron Nitride)를 1.0~2.0 중량% 사용하였다.In the present invention, boron nitride (Boron Nitride) is used as a heat dissipation filler in an amount of 1.0 to 2.0 wt%.

질화붕소란 백색의 흑연이라고 불리는 신소재 세라믹스로서, 기계가공성이 뛰어나고 흑연과 비슷한 방정계 구조를 갖고 있어 화학적 및 물리적 성질이 흑연과 비슷하다는 특징이 있다.Boron nitride is a new material ceramics called white graphite. It is excellent in machinability and has a crystal structure similar to that of graphite. Its chemical and physical properties are similar to graphite.

상기한 질화붕소는 열전도성이 우수하고 전기적으로 절연성이어서 방열도료로 아주 적합하다.The above-mentioned boron nitride is excellent in thermal conductivity and electrically insulating, and thus is very suitable as a heat radiation paint.

이에 비하여 흑연(탄소)계 필러는, 열전도성은 우수하지만 전기적으로 전도성이 있으므로 텔레비젼 방열판용으로는 적합하지 않다. On the other hand, the graphite (carbon) filler has excellent thermal conductivity but is electrically conductive, and thus is not suitable for a TV heat sink.

<용제> <Solvent>

본 발명에 따른 피씨엠 도료 조성물은, 취급 및 피복 작업 시의 특성 등을 고려하여 적당량의 유기 용제를 함유한다. The PC M coating composition according to the present invention contains an appropriate amount of an organic solvent in consideration of characteristics during handling and coating.

상기 유기용제로는, 방향족 탄화수소계, 글리콜 에스테르계, 글리콜 에테르계, 알코올계 용제 등을 적절히 혼합하여 사용하는 것이 바람직하다.As the organic solvent, an aromatic hydrocarbon-based, glycol ester-based, glycol ether-based, or alcohol-based solvent is suitably mixed and used.

상기 방향족 탄화수소계 용제로는 SK사의 코코졸 #100, 코코졸 #150이 있고, 글리콜 에스테르계 용제로는 유니온 카바이드사의 에틸 아세테이트, n-부틸 아세테이트, 셀로솔브 아세테이트, 프로필렌 글리콜 모노메틸 아세테이트, 3-메톡시 부틸 아세테이트 등을 예로 들 수 있다. Examples of the aromatic hydrocarbon-based solvent include cocosol # 100 and cocosol # 150 manufactured by SK Corporation. Examples of the glycol ester solvent include ethylacetate, n-butyl acetate, cellosolve acetate, propylene glycol monomethyl acetate, 3- Methoxybutyl acetate, and the like.

글리콜 에테르계 용제로는 유니온 카바이드 사의 메틸 셀로솔브, 에틸 셀로솔브, 에틸렌 글리콜 부틸 에테르, 디에틸렌 글리콜 메틸 에테르, 디에틸렌 글리콜 에틸에테르, 디에틸렌 글리콜부틸 에테르 등이 있으며, 알코올계 용제로는 에탄올, 이소프로판올, n-부탄올, 아밀알콜, 사이클로 헥산올 등을 예로 들 수 있다. Examples of the glycol ether-based solvent include methyl cellosolve, ethyl cellosolve, ethylene glycol butyl ether, diethylene glycol methyl ether, diethylene glycol ethyl ether, and diethylene glycol butyl ether of Union Carbide. Examples of the alcohol- Isopropanol, n-butanol, amyl alcohol, cyclohexanol and the like.

상기한 용제는 전체 도료 조성물에 대하여 30∼50 중량% 범위로 함유시키는 것이 바람직하다. It is preferable that the above-mentioned solvent is contained in the range of 30 to 50 wt% with respect to the whole coating composition.

기존의 피씨엠 도료에서는 하이드로카본계 용제와 셀로솔브아세테이트 용제가 주로 사용되었으나, 본 발명에서는 에스테르계와 케톤계 용제를 주로 사용하여 도료의 저장성 및 작업성을 향상시켰다. In the conventional PCM paint, a hydrocarbon solvent and a cellosolve acetate solvent were mainly used. In the present invention, ester and ketone solvents were mainly used to improve the storage stability and workability of the paint.

<첨가제( 레벨링제, 소포제 및 안료)> <Additives (leveling agents, antifoaming agents and pigments)>

본 발명에서는 도막의 평활성을 유지하고 도장 작업시 소포성 향상을 위하여 아크릴계나 비닐계 또는 실리콘계 레벨링제와 소포제를 각각 0.5∼1.0 중량% 사용하였다.In the present invention, 0.5 to 1.0% by weight of an acryl-based, vinyl-based or silicone-based leveling agent and a defoaming agent are respectively used for maintaining the smoothness of the coating film and improving the defoaming property in the coating operation.

이러한 레벨링제와 소포제로는 쿠수모토 케미칼사의 디스파론 L-1980, 디스파론 L-1984, 디스파론 AP-30, BYK사의 BYK356, BYK410 등을 예로 들 수 있다. Examples of the leveling agent and antifoaming agent include Diparron L-1980, Diparron L-1984, Diparron AP-30, BYK356 and BYK410 of BYK, which are manufactured by Kusumoto Chemical Co.,

또한, 본 발명의 도료 조성물은 안료를 함유하지 않는 투명 도료 조성물로도 사용될 수 있지만, 일반적으로는 착색 안료를 첨가하여 사용한다. Further, the coating composition of the present invention can be used as a clear coating composition containing no pigment, but generally, a coloring pigment is added and used.

이 경우 착색 안료로는, 피복 조성물 분야에서 사용 가능한 티타늄 옥사이드, 카본블랙 등이 사용될 수 있다. In this case, titanium oxide, carbon black and the like which can be used in the coating composition field may be used as the coloring pigment.

또한, 본 발명의 도료 조성물은, 활석, 점토, 실리카, 운모, 알루미나 등과 같은 체질안료 또는 충진제 등을 포함할 수 있다. 상기한 안료는 전체 도료 조성물에 대하여 2∼5 중량% 함유시킨다.Further, the coating composition of the present invention may contain extender pigments such as talc, clay, silica, mica, alumina, or fillers. The above-mentioned pigment is contained in an amount of 2 to 5% by weight based on the whole coating composition.

다음의 [표 4]는 본 발명에 따른 도료 선정시험의 결과를 나타낸 것이다. The following Table 4 shows the results of the paint selection test according to the present invention.

방열판 수지 적용 도료Heat Resistant Resin Coating 조성(중량%)
Composition (% by weight)
방열판 텍스쳐 수지 적용 도료Paint for heat sink texture resin 1One 22 33 44 수지Suzy 600600 600600 600600 600600 분산첨가제Dispersant additive 1.01.0 1.01.0 1.01.0 1.01.0 카본 블랙Carbon black 2020 2020 2020 2020 방열 FillerHeat Filler 1One 1One 1One 1One 실리카Silica 22 22 22 22 에폭시 수지Epoxy resin 1010 1010 1010 1010 멜라민Melamine 4040 4040 4040 4040 이소시아네이트Isocyanate 1515 1515 1515 1515 레벨링제Leveling agent 2525 2525 2525 2525 산촉매Acid catalyst 1616 1616 1616 1616 Tin촉매Tin Catalyst 1One 1One 1One 1One DBEDBE 3030 3030 3030 3030 PMAPMA 4040 4040 4040 4040 CYCLOHEXANONECYCLOHEXANONE 5050 5050 5050 5050 KOCOSOL 100KOCOSOL 100 4040 4040 4040 4040 KOCOSOL 150KOCOSOL 150 4040 4040 4040 4040

위 도료선정 시험에서는, 1.5T의 AL강판을 메틸에틸케톤으로 탈지하고, 각 수지의 실시예 1 ∼ 4 도료를 건조도막두께 12㎛가 되도록 바코팅한 뒤, 300℃의 분위기 온도에서 60초간 소부하여 물성 시험 시편을 작성하였다.In the upper paint selection test, an AL steel sheet of 1.5 T was degreased with methyl ethyl ketone, and the paints of Examples 1 to 4 of each resin were bar coated so as to have a dry film thickness of 12 탆 and then sintered for 60 seconds at an ambient temperature of 300 캜 To prepare test specimens.

아래의 [표 5]는 그 시험 결과를 나타낸 것으로서, 실시예 1이 도막 가공성, 부착성, 약품성, 내식성 등의 물성이 우수한 것으로 나타났다. Table 5 below shows the results of the tests. Example 1 showed excellent physical properties such as coatability, adhesion, chemical resistance and corrosion resistance.

시험 결과Test result 조성(중량%)
Composition (% by weight)
방열판 텍스쳐 수지 적용 도료Paint for heat sink texture resin 1One 22 33 44 비중importance 1.051.05 1.051.05 1.051.05 1.051.05 고형분Solids 37.037.0 37.037.0 37.037.0 37.037.0 점도(sec/25' C)Viscosity (sec / 25 'C) 100100 100100 100100 100100 광택Polish 4242 4242 4242 4242 경화도Degree of hardening 5050 5050 5050 5050 연필경도Pencil hardness FF FF FF FF 가공성Processability ◎◎ ◎◎ ◎◎ ◎◎ 부착성Attachment ◎◎ ○○ △△ △△ 약품성Chemical ◎◎ △△ ○○ ○○ 내식성Corrosion resistance ○○ ○○ ○○ △△

상술한 바와 같이, 본 발명에 따른 피씨엠 도료 조성물을 텔레비젼 방열판 용의 알루미늄 도장강판에 적용할 경우, 기존의 피씨엠 도장시스템(하도+상도의 2 Coat 시스템)과 동등한 물성(가공성, 내식성, 약품성, 부착성 등)을 유지하면서, 방열성능을 향상시킬 수가 있다. As described above, when the PCM paint composition according to the present invention is applied to an aluminum coated steel sheet for a TV heat sink, the physical properties (workability, corrosion resistance, and chemical resistance) of the conventional PCM coating system (Hado + , Adherence, etc.) while maintaining the heat dissipation performance.

또한 기존의 피씨엠 도막 두께(20~30㎛) 보다도 얇은 박막형 도막 두께(13~17㎛)를 유지하면서 방열성능을 더 향상시킬 수가 있다.Further, the heat radiation performance can be further improved while maintaining the thin film thickness (13 to 17 mu m) thinner than the conventional PCM coating thickness (20 to 30 mu m).

이상에서는 본 발명의 바람직한 실시예를 예시적으로 설명한 것으로서 본 발명은 상기한 실시예에 의해 한정되지 아니한다.The foregoing description of exemplary embodiments of the present invention has been presented for purposes of illustration and description, and is not intended to be exhaustive or to limit the invention to the precise forms disclosed.

본 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 본 발명의 기술적 사상의 범위를 벗어남이 없이 다양한 수정 및 변형이 가능하다는 것을 이해할 수 있을 것이다. It will be understood by those skilled in the art that various changes and modifications may be made without departing from the scope of the present invention.

예컨대 본 발명은 텔레비젼 방열판 뿐만 아니라 방열을 필요로 하는 각종 전기 전자부품의 패널로로 사용될 수가 있다. For example, the present invention can be used not only as a TV heat sink but also as a panel for various electric and electronic parts requiring heat dissipation.

10: 소지강판
20: 전처리층
30: 하도 도막층
40: 상도 도막층
50: 배면층10: Substrate steel
20: Pre-treatment layer
30: Lower coating layer
40: top coat layer
50: backside layer

Claims (5)

수지, 가교제, 경화 촉매, 용제 및 첨가제를 포함하여 구성되어, 텔레비젼 방열판으로 사용되는 알루미늄 도장강판의 피씨엠(PCM: Pre-coated Metal) 도료 조성물에 있어서,
상기 수지는, A 수지와 B 수지가 동일 중량비로 혼합되어 전체 조성물에 대하여 각각 15∼35 중량% 첨가되고,
상기 A 수지는, 유연성이 강화된 폴리에스테르 수지로서, 중량평균 분자량 15,000∼20,000, 수산가 20∼40 mgKOH/g, 산가 1∼5 mgKOH/g, 유리전이온도 10∼20℃이고,
상기 B 수지는, 부착성을 높이기 위해 전체 배합에서 방향족 성분을 40~60 중량%로 하고, 중량평균 분자량 30,000∼35,000, 수산가 10∼30 mgKOH/g, 산가 1∼3 mgKOH/g, 유리전이온도 25∼35℃이며,
방열성능을 향상시키기 위한 필러(Filler)로서 질화붕소(Boron Nitride)가 전체 조성물에 대하여 1.0~2.0 중량% 첨가되는 것을 특징으로 하는 텔레비젼 방열판용 알루미늄 도장강판의 피씨엠 도료 조성물. A pre-coated metal (PCM) coating composition for an aluminum-coated steel sheet comprising a resin, a crosslinking agent, a curing catalyst, a solvent and an additive and used as a TV heat sink,
Wherein the resin A and the resin B are mixed at the same weight ratio and added in an amount of 15 to 35 wt%
The A resin is a polyester resin having enhanced flexibility and has a weight average molecular weight of 15,000 to 20,000, a hydroxyl value of 20 to 40 mg KOH / g, an acid value of 1 to 5 mg KOH / g, a glass transition temperature of 10 to 20 캜,
The resin B has a weight average molecular weight of 30,000 to 35,000, a hydroxyl value of 10 to 30 mgKOH / g, an acid value of 1 to 3 mgKOH / g, an aromatic component of 40 to 60% by weight in the total blend, Lt; / RTI &gt;
Characterized in that boron nitride is added as a filler in an amount of 1.0 to 2.0 wt% based on the whole composition to improve the heat radiation performance of the aluminum heat-treated steel sheet. 제 1 항에 있어서,
도막의 가공성을 유지하기 위해 분자 구조 내에 프로판디올(Propanediol), 헥산디올(Hexanediol), 부단디올(Butanediol) 중 어느 하나의 모노머가 25~40 중량% 함유되는 것을 특징으로 하는 텔레비젼 방열판용 알루미늄 도장강판의 피씨엠 도료 조성물. The method according to claim 1,
An aluminum coated steel sheet for a TV heat sink, characterized in that the molecular structure contains 25 to 40% by weight of any one of propanediol, hexanediol, and butanediol in order to maintain the processability of the coating film. By weight. 제 1 항에 있어서,
상기 가교제는, 메톡시기를 갖는 메틸에테르화 멜라민 수지가 3∼7 중량%, 우레탄 가교제가 1∼3 중량% 함유되는 것을 특징으로 하는 텔레비젼 방열판용 알루미늄 도장강판의 피씨엠 도료 조성물. The method according to claim 1,
Wherein the cross-linking agent comprises 3 to 7% by weight of a methyl etherified melamine resin having a methoxy group and 1 to 3% by weight of a urethane cross-linking agent. 제 1 항에 있어서,
상기 경화 촉매는, p-톨루엔 술폰산(p-TSA), 디노닐나프탈렌 술폰산(DNNSA), 디나프탈렌 디술폰산(DNNDSA), 플루오로 술폰산 중 어느 하나의 술폰산을 2차 아민 또는 에폭시로 중화시켜 얻은 중화 생성물이고,
우레탄 가교 결합을 위해 Tin촉매(DBTDL)를 적용하는 특징으로 하는 텔레비젼 방열판용 알루미늄 도장강판의 피씨엠 도료 조성물. The method according to claim 1,
The curing catalyst is a neutralization catalyst obtained by neutralizing a sulfonic acid of any one of p-toluenesulfonic acid (p-TSA), dinonylnaphthalenesulfonic acid (DNNSA), dinaphthalene disulfonic acid (DNNDSA), and fluorosulfonic acid with a secondary amine or epoxy Product,
(DBTDL) is applied for urethane crosslinking. The aluminum-coated steel sheet for LCD heat-shrinkable steel plate according to claim 1, 제 1 항 내지 제 4 항 중 어느 한 항에 기재된 피씨엠 도료 조성물을 도포하여 제조되는 것을 특징으로 하는 텔레비젼 방열판용 알루미늄 도장강판. An aluminum-coated steel sheet for a TV heat sink, which is produced by applying the PCM coating composition according to any one of claims 1 to 4.
KR1020140037802A 2014-03-31 2014-03-31 Coating Composition of Aluminum Sheet for Heat Discharge Plate of Television and Pre-coated Aluminum Sheet Using the same KR101590942B1 (en)