KR20150058883A - polymer blend composition with highly electrical conductivity and method of manufacturing the same - Google Patents

polymer blend composition with highly electrical conductivity and method of manufacturing the same Download PDF

Info

Publication number
KR20150058883A
KR20150058883A KR1020130142193A KR20130142193A KR20150058883A KR 20150058883 A KR20150058883 A KR 20150058883A KR 1020130142193 A KR1020130142193 A KR 1020130142193A KR 20130142193 A KR20130142193 A KR 20130142193A KR 20150058883 A KR20150058883 A KR 20150058883A
Authority
KR
South Korea
Prior art keywords
resin
carbon
polyamide
poly
phenylene
Prior art date
Application number
KR1020130142193A
Other languages
Korean (ko)
Other versions
KR102130295B1 (en
Inventor
최우진
이재흥
김광제
이창재
Original Assignee
한국화학연구원
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한국화학연구원 filed Critical 한국화학연구원
Priority to KR1020130142193A priority Critical patent/KR102130295B1/en
Publication of KR20150058883A publication Critical patent/KR20150058883A/en
Application granted granted Critical
Publication of KR102130295B1 publication Critical patent/KR102130295B1/en

Abstract

The present invention can provide a polymer blend composition containing carbon nanoparticles. The polymer blend composition includes different types of resins having affinities for the carbon nanoparticles which are diffident from each other to maximize dispersible properties and thus can increase electrical conductivity. The present invention also provides a method for producing the same polymer blend composition. The method includes the steps of: a) producing a master batch by melting and kneading a first resin and the carbon nanoparticles; and b) melting and kneading the master batch and a second resin.

Description

전기전도도가 향상된 고분자 블렌드 조성물 및 이의 제조방법{polymer blend composition with highly electrical conductivity and method of manufacturing the same}TECHNICAL FIELD [0001] The present invention relates to a polymer blend composition having improved electrical conductivity and a method of manufacturing the polymer blend composition.

본 발명은 탄소나노입자의 분산성을 높이면서 전기전도도가 향상된 고분자 블렌드 조성물 및 이의 제조방법에 관한 것이다.The present invention relates to a polymer blend composition having improved electrical conductivity while improving dispersibility of carbon nanoparticles and a method for producing the same.

탄소나노튜브는 높은 전기전도도 및 기계적 물성을 가지고 있어 고분자와 혼합하여 사용할 경우, 탄소나노튜브의 분산성이 전기전도도나 기계적 물성에 큰 영향을 미친다. Carbon nanotubes have high electrical conductivity and mechanical properties. When they are mixed with polymers, the dispersibility of carbon nanotubes greatly affects electrical conductivity and mechanical properties.

한국등록특허 제10-1137162호(특허문헌 1)는 전도성이 부여된 폴리카보네이트를 제조하기 위해 용매를 이용하여 마스터배치를 제조하는 방법에 관하여 기술하고 있으나, 제조 공정상 용매를 사용해야 하고 시간이 많이 걸리는 한계가 있는 문제점이 있다. Korean Patent No. 10-1137162 (Patent Document 1) describes a method for producing a master batch using a solvent for producing a polycarbonate having conductivity, but a solvent is required to be used in the manufacturing process and a time There is a problem with the limit to take.

또한, 한국공개특허 제10-2009-0090738호(특허문헌 2)는 전도성이 향상된 탄소나노튜브-고분자 나노복합체에 관한 것으로, 마스터배치를 이용하여 용융혼련시 혼련 온도 및 속도 조절을 통한 제조 기술에 관하여 기술하고 있으나, 마스터배치와 같은 수지에 재용융혼련만으로는 고분자 매트릭스내에서 탄소나노튜브의 분산에 한계가 있는 문제점이 있다. Korean Patent Laid-Open Publication No. 10-2009-0090738 (Patent Document 2) relates to a carbon nanotube-polymer nanocomposite having improved conductivity, and it relates to a manufacturing technique by controlling a kneading temperature and a speed during melt- However, there is a problem that dispersion of carbon nanotubes within a polymer matrix is limited by merely melt-kneading a resin such as a master batch.

따라서, 적은 양의 탄소나노입자를 사용하면서도 분산성을 향상시킴으로써 기계적 강도 및 내열성뿐만 아니라 전기전도도를 극대화시킬 수 있는 고분자 블렌드 조성물에 대한 개선이 필요하다. Accordingly, there is a need to improve the polymer blend composition that can maximize electrical conductivity as well as mechanical strength and heat resistance by using a small amount of carbon nanoparticles while improving dispersibility.

한국등록특허 제10-1137162호(2012.04.09)Korean Registered Patent No. 10-1137162 (Apr. 04, 2012) 한국공개특허 제10-2009-0090738호(2009.08.26)Korean Patent Laid-Open No. 10-2009-0090738 (Aug. 26, 2009)

본 발명은 상기와 같은 문제점을 해결하기 위하여 안출된 것으로서, 탄소나노입자의 분산성을 극대화함으로써 전기전도도를 향상시킬 수 있는 탄소나노입자를 포함하는 고분자 블렌드 조성물을 제공하는 것을 목적으로 한다. Disclosure of Invention Technical Problem [8] Accordingly, the present invention has been made keeping in mind the above problems occurring in the prior art, and an object of the present invention is to provide a polymer blend composition containing carbon nanoparticles capable of improving electrical conductivity by maximizing dispersibility of carbon nanoparticles.

상기와 같은 목적을 달성하기 위하여, 본 발명은탄소나노입자, 상기 탄소나노입자에 대한 친화도가 하기 식 1을 만족하는 제1수지 및 제2수지를 포함하는 전기전도도가 향상된 고분자 블렌드 조성물을 제공할 수 있다.In order to achieve the above object, the present invention provides a polymer blend composition having improved electrical conductivity including carbon nanoparticles, a first resin having an affinity for carbon nanoparticles satisfying the following formula 1, and a second resin: can do.

(식 1)

Figure pat00001
(Equation 1)
Figure pat00001

(상기 식 1에서,

Figure pat00002
,
Figure pat00003
이다. 이때,
Figure pat00004
은 물질 1과 2사이의 계면장력을 나타낸다. 또한,
Figure pat00005
이며, νd : 비극성성분의 표면에너지값, νp: 극성성분의 표면에너지값을 의미한다.)(In the above formula 1,
Figure pat00002
,
Figure pat00003
to be. At this time,
Figure pat00004
Represents the interfacial tension between materials 1 and 2. Also,
Figure pat00005
V d : surface energy value of the non-polar component, and v p : surface energy value of the polar component.)

본 발명의 일 실시예에 따른 고분자 블렌드 조성물에 있어서, 상기 조성물은 제1수지 5 ~ 50중량% 및 제2수지 50 ~ 95중량%로 이루어진 기초 수지 100중량부에 대하여 탄소나노입자 0.1 ~ 10중량부를 포함할 수 있다. In the polymer blend composition according to an embodiment of the present invention, the composition may contain 0.1 to 10 wt% of carbon nanoparticles relative to 100 wt% of the base resin composed of 5 to 50 wt% of the first resin and 50 to 95 wt% Section.

본 발명의 일 실시예에 따른 고분자 블렌드 조성물에 있어서, 제1수지는 폴리(2,6-디메틸-1,4-페닐렌)에테르, 폴리(2,6-디에틸-1,4-페닐렌)에테르, 폴리(2,6-디프로필-1,4-페닐렌)에테르, 폴리(2-메틸-6-에틸-1,4-페닐렌)에테르, 폴리(2-메틸-6-프로필-1,4-페닐렌)에테르, 폴리(2-에틸-6-프로필-1,4-페닐렌)에테르, 폴리(2,6-디페닐-1,4-페닐렌)에테르, 폴리(2,6-디메틸-1,4-페닐렌)에테르와 폴리(2,3,6-트리메틸-1,4-페닐렌)에테르의 공중합체, 폴리(2,6-디메틸-1,4-페닐렌)에테르와 폴리(2,3,6-트리에틸-1,4-페닐렌)에테르의 공중합체 및 이들의 조합으로 이루어진 군에서 선택되는 폴리페닐렌에테르계 수지일 수 있다.In the polymer blend composition according to one embodiment of the present invention, the first resin may be selected from the group consisting of poly (2,6-dimethyl-1,4-phenylene) ether, poly (2,6-diethyl- ) Ether, poly (2,6-dipropyl-1,4-phenylene) ether, poly (2-methyl- Poly (2,6-diphenyl-1,4-phenylene) ether, poly (2-ethyl- (2,6-dimethyl-1,4-phenylene) ether and a poly (2,3,6-trimethyl-1,4-phenylene) ether, Ether and a poly (2,3,6-triethyl-1,4-phenylene) ether, and combinations thereof.

본 발명의 일 실시예에 따른 고분자 블렌드 조성물에 있어서, 제2수지는 폴리카프로락탐(폴리아미드 6), 폴리(11-아미노운데칸산)(폴리아미드 11), 폴리라우릴락탐(폴리아미드 12), 폴리헥사메틸렌 아디프아미드(폴리아미드 66), 폴리헥사에틸렌 아젤아미드(폴리아미드 69), 폴리헥사에틸렌 세바카미드(폴리아미드 610), 폴리헥사에틸렌 도데카노디아미드(폴리아미드 612), 이들의 공중합체 및 이들의 조합으로 이루어진 군에서 선택되는 폴리아미드계 수지일 수 있다.In the polymer blend composition according to an embodiment of the present invention, the second resin may be at least one selected from the group consisting of polycaprolactam (polyamide 6), poly (11-aminoundecanoic acid) (polyamide 11), polylauryl lactam (polyamide 12) , Polyhexamethylene adipamide (polyamide 66), polyhexylene ethylene amide (polyamide 69), polyhexaethylene sebacamide (polyamide 610), polyhexethylene dodecanodiamide (polyamide 612) And copolymers thereof, and combinations thereof.

본 발명의 일 실시예에 따른 고분자 블렌드 조성물에 있어서, 탄소나노입자는 카본블랙, 탄소나노튜브, 탄소나노 구, 탄소나노섬유, 탄소나노막대, 탄소나노뿔, 그라핀, 그라핀 옥사이드 및 이들의 조합으로부터 선택될 수 있다. In the polymer blend composition according to an embodiment of the present invention, the carbon nanoparticles may be selected from the group consisting of carbon black, carbon nanotubes, carbon nanospheres, carbon nanofibers, carbon nanorods, carbon nanohorns, graphene, Can be selected from combinations.

본 발명의 일 실시예에 따른 고분자 블렌드 조성물에 있어서, 탄소나노입자는 표면개질된 것일 수 있다. In the polymer blend composition according to an embodiment of the present invention, the carbon nanoparticles may be surface-modified.

본 발명의 일 실시예에 따른 고분자 블렌드 조성물에 있어서, 탄소나노입자는 평균입경이 10nm 내지 100nm일 수 있다.In the polymer blend composition according to an embodiment of the present invention, the carbon nanoparticles may have an average particle diameter of 10 nm to 100 nm.

본 발명의 일 실시예에 따른 고분자 블렌드 조성물에 있어서, 카본블랙은 아세틸렌의 열분해에 의해 제조된 것일 수 있다.In the polymer blend composition according to one embodiment of the present invention, the carbon black may be one produced by pyrolysis of acetylene.

본 발명의 일 실시예에 따른 고분자 블렌드 조성물에 있어서, 탄소나노튜브는 단일벽 탄소나노튜브, 다중벽 탄소나노튜브, 다발형 탄소나노튜브 및 이들의 조합 중에서 선택될 수 있다.In the polymer blend composition according to one embodiment of the present invention, the carbon nanotubes may be selected from single-walled carbon nanotubes, multi-walled carbon nanotubes, multi-walled carbon nanotubes, and combinations thereof.

본 발명의 일 실시예에 따른 고분자 블렌드 조성물에 있어서, 탄소나노섬유는 헤링본 구조, 플레이트릿 구조 또는 튜블라 구조를 갖는 것일 수 있다.In the polymer blend composition according to an embodiment of the present invention, the carbon nanofiber may have a herringbone structure, a planar structure, or a tubular structure.

본 발명은 a) 제1수지 및 탄소나노입자를 용융혼련하여 마스터배치를 제조하는 단계 및The present invention relates to a method for preparing a master batch, comprising the steps of: a) melt kneading a first resin and carbon nanoparticles to prepare a master batch; and

b) 상기 마스터배치 및 제2수지를 재용융혼련하는 단계b) re-melt-kneading the masterbatch and the second resin

를 포함하며, 상기 제1수지 및 제2수지는 탄소나노입자에 대한 친화도가 하기 식 1을 만족하는 전기전도도가 향상된 고분자 블렌드 조성물의 제조방법을 제공할 수 있다.Wherein the first resin and the second resin can provide a method of producing a polymer blend composition having an improved electrical conductivity with an affinity for carbon nanoparticles satisfying Equation 1 below.

(식 1)

Figure pat00006
(Equation 1)
Figure pat00006

(상기 식 1에서,

Figure pat00007
,
Figure pat00008
이다. 이때,
Figure pat00009
은 물질 1과 2사이의 계면장력을 나타낸다. 또한,
Figure pat00010
이며, νd : 비극성성분의 표면에너지값, νp: 극성성분의 표면에너지값을 의미한다.)(In the above formula 1,
Figure pat00007
,
Figure pat00008
to be. At this time,
Figure pat00009
Represents the interfacial tension between materials 1 and 2. Also,
Figure pat00010
V d : surface energy value of the non-polar component, and v p : surface energy value of the polar component.)

본 발명은 상기 고분자 블렌드 조성물을 포함하는 고분자 블렌드를 제공할 수 있다.The present invention can provide a polymer blend comprising the polymer blend composition.

본 발명은 탄소나노입자의 분산성을 극대화함으로써 기계적 물성 및 내열특성뿐만 아니라 전기전도도를 향상시킬 수 있는 고분자 블렌드 조성물 및 이의 제조방법을 제공할 수 있는 장점이 있다. The present invention has an advantage of being able to provide a polymer blend composition capable of improving not only mechanical properties and heat resistance characteristics but also electric conductivity by maximizing the dispersibility of carbon nanoparticles and a method for producing the same.

도 1 및 2는 각각 실시예 및 비교예에 따른 탄소나노튜브의 분산 개략도를 나타낸 것이다.
도 3은 본 발명에 따른 실시예 1에서 마스터배치 제조공정상 탄소나노튜브의 분산을 보여주는 투과전자현미경 사진을 나타낸 것이다.
도 4는 비교예 1에서 마스터배치 제조공정상 탄소나노튜브의 분산을 보여주는 투과전자현미경 사진을 나타낸 것이다. 1 and 2 are schematic views showing the dispersion of carbon nanotubes according to Examples and Comparative Examples, respectively.
FIG. 3 is a transmission electron microscope photograph showing the dispersion of the master batch manufacturing normal carbon nanotubes in Example 1 according to the present invention.
4 is a transmission electron micrograph showing dispersion of normal carbon nanotubes in the masterbatch manufacturing process in Comparative Example 1. FIG.

이하 본 발명의 고분자 블렌드 조성물 및 이의 제조방법을 상세히 설명한다. 다음에 소개되는 실시예들은 당업자에게 본 발명의 사상이 충분히 전달될 수 있도록 하기 위해 예로서 제공되는 것이다. 또한, 사용되는 기술 용어 및 과학 용어에 있어서 다른 정의가 없다면, 이 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 통상적으로 이해하고 있는 의미를 가지며, 하기의 설명 및 첨부 도면에서 본 발명의 요지를 불필요하게 흐릴 수 있는 공지 기능 및 구성에 대한 설명은 생략한다.Hereinafter, the polymer blend composition of the present invention and its production method will be described in detail. The following embodiments are provided by way of example so that those skilled in the art can fully understand the spirit of the present invention. Further, it is to be understood that, unless otherwise defined, technical terms and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. Descriptions of known functions and configurations that may be unnecessarily blurred are omitted.

본 발명의 발명자들은 탄소나노입자와의 친화도가 상이한 서로 다른 수지를 포함하여 탄소나노입자의 분산성을 극대화함으로써 전기전도도를 향상시킬 수 있음을 발견하여 본 발명을 완성하였다. The inventors of the present invention have discovered that it is possible to improve the electrical conductivity by maximizing the dispersibility of carbon nanoparticles including different resins having different affinities with carbon nanoparticles, thus completing the present invention.

본 명세서에서 특별히 언급이 없는 한, 고분자 A, 고분자 B는 각각 제1수지 및 제2수지를 말하며, 탄소나노입자와의 친화도는 친화도 값이 1 미만이면 낮고, 1 초과이면 높은 것을 의미한다.
Polymer A and Polymer B refer to the first resin and the second resin, respectively, and the affinity with carbon nanoparticles means that the affinity value is low when the affinity value is less than 1, and high when the affinity value is less than 1 .

본 발명에 따른 고분자 블렌드 조성물은 탄소나노입자와 친화도가 상이한 서로 다른 수지, 제1수지 및 제2수지를 포함한다. 이때, 제1수지 및 제2수지는 탄소나노입자와의 친화도가 하기 식 1을 만족하는 것이 탄소나노입자의 분산성을 극대화시킬 수 있어 바람직하다. The polymer blend composition according to the present invention comprises different resins having different affinities with carbon nanoparticles, a first resin and a second resin. At this time, it is preferable that the affinity of the first resin and the second resin with the carbon nanoparticles satisfies the following formula (1) because the dispersibility of the carbon nanoparticles can be maximized.

(식 1)

Figure pat00011
(Equation 1)
Figure pat00011

상기 식 1에서,

Figure pat00012
,
Figure pat00013
이다. 이때,
Figure pat00014
은 물질 1과 2사이의 계면장력을 나타낸다. 또한,
Figure pat00015
이며, νd : 비극성성분의 표면에너지값, νp: 극성성분의 표면에너지값을 의미한다.In Equation (1)
Figure pat00012
,
Figure pat00013
to be. At this time,
Figure pat00014
Represents the interfacial tension between materials 1 and 2. Also,
Figure pat00015
V d is the surface energy value of the non-polar component, and v p is the surface energy value of the polar component.

본 발명에서 제1수지는 바람직하게는 폴리페닐렌에테르계 수지일 수 있다.In the present invention, the first resin may preferably be a polyphenylene ether resin.

상기 폴리페닐렌에테르계 수지는 폴리페닐렌에테르 수지를 단독으로 사용하거나 폴리페닐렌에테르 수지 및 방향족 비닐계 공중합체를 혼합한 것을 사용할 수 있다. 바람직하게는 폴리페닐렌에테르 수지에 방향족 비닐계 공중합체를 혼합한 것을 사용할 수 있으며, 일예로 폴리페닐렌에테르 수지에 폴리스티렌을 혼합한 혼합물을 사용할 수 있다. 이때, 폴리페닐렌에테르계 수지와 혼합되는 방향족 비닐계 공중합체의 함량은 제1수지 내의 20 내지 90중량%일 수 있다. As the polyphenylene ether-based resin, a polyphenylene ether resin alone or a mixture of a polyphenylene ether resin and an aromatic vinyl-based copolymer may be used. Preferably, a mixture of a polyphenylene ether resin and an aromatic vinyl copolymer may be used. For example, a mixture of polyphenylene ether resin and polystyrene may be used. At this time, the content of the aromatic vinyl-based copolymer mixed with the polyphenylene ether-based resin may be 20 to 90% by weight in the first resin.

상기 폴리페닐렌에테르계 수지로는 폴리(2,6-디메틸-1,4-페닐렌)에테르, 폴리(2,6-디에틸-1,4-페닐렌)에테르, 폴리(2,6-디프로필-1,4-페닐렌)에테르, 폴리(2-메틸-6-에틸-1,4-페닐렌)에테르, 폴리(2-메틸-6-프로필-1,4-페닐렌)에테르, 폴리(2-에틸-6-프로필-1,4-페닐렌)에테르, 폴리(2,6-디페닐-1,4-페닐렌)에테르, 폴리(2,6-디메틸-1,4-페닐렌)에테르와 폴리(2,3,6-트리메틸-1,4-페닐렌)에테르의 공중합체, 폴리(2,6-디메틸-1,4-페닐렌)에테르와 폴리(2,3,6-트리에틸-1,4-페닐렌)에테르의 공중합체 및 이들의 조합으로 이루어진 군에서 선택될 수 있으며, 반드시 이에 제한되지는 않는다.Examples of the polyphenylene ether resin include poly (2,6-dimethyl-1,4-phenylene) ether, poly (2,6-diethyl- (2-methyl-6-ethyl-1,4-phenylene) ether, poly Poly (2,6-dimethyl-1,4-phenylene) ether, poly (2,6- Copolymers of poly (2,6-dimethyl-1,4-phenylene) ether and poly (2,3,6-trimethyl-1,4-phenylene) ether, -Triethyl-1,4-phenylene) ether, and combinations thereof, but not always limited thereto.

상기 비닐 방향족 중합체는 스티렌, -메틸 스티렌, a-메틸 스티렌, 4-N-프로필 스티렌 등의 비닐 방향족 단량체를 서로 중합한 것을 사용할 수 있으며, 바람직하게는 스티렌을 이 중 좋게는 스티렌, a-메틸 스티렌 및 이들의 조합 중에서 선택된 어느 하나를 중합한 것을 사용할 수 있다.The vinyl aromatic polymer may be one obtained by polymerizing vinyl aromatic monomers such as styrene, -methylstyrene, a-methylstyrene, and 4-N-propylstyrene, preferably styrene, styrene, a-methyl Styrene, and a combination thereof.

상기 폴리페닐렌에테르계 수지의 수평균 분자량은 특별히 제한되지는 않으나, 조성물의 내열특성 및 작업성을 고려하여 5,000 내지 100,000일 수 있으며, 바람직하게는 9,600 내지 40,000 일 수 있다.The number average molecular weight of the polyphenylene ether-based resin is not particularly limited, but may be 5,000 to 100,000, preferably 9,600 to 40,000, in consideration of heat resistance and workability of the composition.

본 발명에서 제2수지는 고분자 주쇄에 아미드기를 함유하는 폴리아미드계 수지일 수 있다. 이는 아미노산, 락탐 또는 디아민과 디카르복실산을 주요 구성성분으로 하여 중합된 것일 수 있다. In the present invention, the second resin may be a polyamide-based resin containing an amide group in the polymer main chain. It may be an amino acid, a lactam, or a polymer which is mainly composed of a diamine and a dicarboxylic acid.

상기 폴리아미드 수지는 구체적인 예로, 폴리카프로락탐(폴리아미드 6), 폴리(11-아미노운데칸산)(폴리아미드 11), 폴리라우릴락탐(폴리아미드 12), 폴리헥사메틸렌 아디프아미드(폴리아미드 66), 폴리헥사에틸렌 아젤아미드(폴리아미드 69), 폴리헥사에틸렌 세바카미드(폴리아미드 610), 폴리헥사에틸렌 도데카노디아미드(폴리아미드 612) 등과, 이들의 공중합체인 폴리아미드 6/610, 폴리아미드 6/66, 폴리아미드 6/12 등을 단독으로 사용하거나 2종 이상을 적정 비율로 혼합하여 사용할 수 있으며, 반드시 이에 제한되지는 않는다.Specific examples of the polyamide resin include polycaprolactam (polyamide 6), poly (11-aminoundecanoic acid) (polyamide 11), polylauryl lactam (polyamide 12), polyhexamethylene adipamide (Polyamide 610), polyhexylene dodecanediamide (polyamide 612), and the like, and polyamides 6/610 and 6/610, which are copolymers thereof, Polyamide 6/66, polyamide 6/12, etc. may be used singly or two or more of them may be mixed in an appropriate ratio, and the present invention is not limited thereto.

상기 폴리아미드계 수지는 융점이 250 이상인 것이 우수한 기계적 물성 및 내열성을 얻을 수 있어 바람직하다. The polyamide-based resin preferably has a melting point of 250 or more, because excellent mechanical properties and heat resistance can be obtained.

본 발명에서 전기전도도를 향상시키기 위하여 탄소나노입자를 포함할 수 있다. 상기 탄소나노입자는 조성물 내 분산되어 전기전도도뿐만 아니라 다른 성분과의 조합으로 기계적 물성 및 열적 안정성을 향상시킬 수 있다.In the present invention, carbon nanoparticles may be included to improve electrical conductivity. The carbon nanoparticles may be dispersed in the composition to improve mechanical properties and thermal stability in combination with other components as well as electrical conductivity.

상기 탄소나노입자는 카본블랙, 탄소나노튜브, 탄소나노 구, 탄소나노섬유, 탄소나노막대, 탄소나노뿔, 그라핀, 그라핀 옥사이드 및 이들의 조합으로부터 선택될 수 있으며, 반드시 이에 제한되지는 않는다.The carbon nanoparticles may be selected from carbon black, carbon nanotubes, carbon nanospheres, carbon nanofibers, carbon nanorods, carbon nanotubes, graphene, graphen oxide, and combinations thereof, but are not limited thereto .

본 발명에서 탄소나노입자는 친화도 조절을 위하여 표면개질된 것을 사용할 수 있다. 또한, 상기 탄소나노입자는 평균입경이 10nm 내지 100nm일 수 있다.In the present invention, the carbon nanoparticles may be surface-modified for the purpose of controlling affinity. The carbon nanoparticles may have an average particle diameter of 10 nm to 100 nm.

상기 카본블랙은 바람직하게는 아세틸렌블랙을 사용할 수 있다. 상기 아세틸렌블랙은 아세틸렌의 열분해에 의해 제조될 수 있으며, 사슬구조로 되어 있어 전기전도도를 향상시킬 수 있어 바람직하다. The carbon black may preferably be acetylene black. The acetylene black can be prepared by pyrolysis of acetylene and has a chain structure, which is preferable because it can improve the electric conductivity.

상기 탄소나노섬유는 헤링본(herringbone) 구조, 플레이트릿(platelet) 구조 또는 튜블라(tubelar) 구조를 갖는 것일 수 있다.The carbon nanofiber may have a herringbone structure, a platelet structure, or a tubelar structure.

본 발명에 따른 고분자 블렌드 조성물은 각 용도에 따라 항균제, 열안정제, 산화방지제, 이형제, 광안정제, 무기물 첨가제, 계면활성제, 커플링제, 가소제, 혼화제, 안정제, 활제, 정전기방지제, 조색제, 방염제, 내후제, 착색제, 자외선 흡수제, 자외선 차단제, 난연제, 충전제, 핵 형성제, 접착 조제, 점착제 및 이들의 혼합물로 이루어진 군에서 선택되는 첨가제를 더 포함할 수 있다. The polymer blend composition according to the present invention can be suitably used in various fields such as an antibacterial agent, a heat stabilizer, an antioxidant, a release agent, a light stabilizer, an inorganic additive, a surfactant, a coupling agent, a plasticizer, an admixture, a stabilizer, a lubricant, an antistatic agent, An additive selected from the group consisting of ultraviolet absorbers, ultraviolet absorbers, ultraviolet light blocking agents, flame retardants, fillers, nucleating agents, adhesion promoters, pressure-sensitive adhesives, and mixtures thereof.

상기 산화방지제로는 페놀형, 포스파이트(phosphite)형, 티오에테르형 또는 아민형 산화방지제를 사용할 수 있으며, 상기 이형제로는 불소 함유 중합체, 실리콘 오일, 스테아린산(stearic acid)의 금속염, 몬탄산(montanic acid)의 금속염, 몬탄산 에스테르 왁스 또는 폴리에틸렌 왁스를 사용할 수 있다. 또한, 상기 내후제로는 벤조페논형 또는 아민형 내후제를 사용할 수 있고, 상기 착색제로는 염료 또는 안료를 사용할 수 있다. 또한, 상기 자외선 차단제로는 산화티탄(TiO2) 또는 카본블랙을 사용할 수 있고, 상기 충전제로는 유리섬유, 탄소섬유, 실리카, 마이카, 알루미나, 점토, 탄산칼슘, 황산칼슘 또는 유리 비드를 사용할 수 있으며, 상기와 같은 충전제를 첨가할 경우 기계적 강도 및 내열성 등의 물성을 향상시킬 수 있다. 또한, 상기 핵 형성제로는 탈크 또는 클레이를 사용할 수 있다. Examples of the antioxidant include phenol type, phosphite type, thioether type or amine type antioxidants. Examples of the releasing agent include fluorine-containing polymers, silicone oil, metal salts of stearic acid, montanic acid, montanic ester wax or polyethylene wax may be used. As the weather resistance agent, benzophenone type or amine type weathering agent can be used, and as the coloring agent, a dye or pigment can be used. As the ultraviolet ray blocking agent, titanium oxide (TiO2) or carbon black can be used. As the filler, glass fiber, carbon fiber, silica, mica, alumina, clay, calcium carbonate, calcium sulfate or glass beads can be used When such a filler is added, physical properties such as mechanical strength and heat resistance can be improved. As the nucleating agent, talc or clay may be used.

본 발명은 The present invention

a) 제1수지 및 탄소나노입자를 용융혼련하여 마스터배치를 제조하는 단계 및a) preparing a master batch by melt kneading the first resin and the carbon nanoparticles, and

b) 상기 마스터배치 및 제2수지를 재용융혼련하는 단계b) re-melt-kneading the masterbatch and the second resin

를 포함하며, 상기 제1수지 및 제2수지는 탄소나노입자에 대한 친화도가 하기 식 1을 만족하는 전기전도도가 향상된 고분자 블렌드 조성물의 제조방법을 제공할 수 있다.Wherein the first resin and the second resin can provide a method of producing a polymer blend composition having an improved electrical conductivity with an affinity for carbon nanoparticles satisfying Equation 1 below.

(식 1)

Figure pat00016
(Equation 1)
Figure pat00016

상기 식 1에서,

Figure pat00017
,
Figure pat00018
이다. 이때,
Figure pat00019
은 물질 1과 2사이의 계면장력을 나타낸다. 또한,
Figure pat00020
이며, νd : 비극성성분의 표면에너지값, νp: 극성성분의 표면에너지값을 의미한다.In Equation (1)
Figure pat00017
,
Figure pat00018
to be. At this time,
Figure pat00019
Represents the interfacial tension between materials 1 and 2. Also,
Figure pat00020
V d is the surface energy value of the non-polar component, and v p is the surface energy value of the polar component.

상기 고분자 블렌드 조성물은 상술한 본 발명의 구성성분을 혼합한 후 압출기 내에서 용융압출한 후 펠렛 형태로 제조하는 통상의 방법으로 제조하는 것과 달리, 탄소나노입자와의 친화도가 낮은 제1수지를 탄소나노입자와 용융혼련하여 마스터배치를 제조하는 것을 특징으로 한다. 상기 제조된 마스터배치에 탄소나노입자와 친화도가 높은 제2수지와 재용융혼련하는 것을 포함함으로써 조성물의 분산성을 극대화할 수 있다. The polymer blend composition may be prepared by mixing a first resin having a low affinity with the carbon nanoparticles and a second resin having a low affinity with the carbon nanoparticles, unlike the conventional method of mixing the components of the present invention and then melt-extruding the mixture into an extruder, Characterized in that the master batch is produced by melt kneading with the carbon nanoparticles. The masterbatch thus prepared is re-melted and kneaded with a second resin having high affinity with the carbon nanoparticles, thereby maximizing the dispersibility of the composition.

도 1 및 2는 본 발명에 따른 실시예, 즉, 탄소나노입자와의 친화도가 낮은 제1수지를 탄소나노입자와 용융혼련하여 마스터배치를 제조한 후, 상기 마스터배치와 제2수지를 재용융혼련하는 공정과, 이의 대조군으로서 비교예, 탄소나노입자와의 친화도가 높은 제2수지를 탄소나노입자와 용융혼련하여 마스터배치를 제조한 후, 상기 마스터배치와 제1수지를 재용융혼련하는 공정에 따른 탄소나노튜브의 분산 개략도를 나타낸 것이다. 구체적으로, CNT가 mPPE에 분산된 후, PA66가 재용융혼련될 때 CNT가 친화도가 더 높은 PA66로 이동하려고 한다. 이때, 종횡비가 크고 직경이 작은 CNT는 mPPE 내에서의 확산속도 및 mPPE/PA66 계면에서의 이동속도가 높으므로 CNT 응집체보다는 CNT 입자들이 mPPE에서 PA66로 분산하게 된다. 이와 같은 입자이동에 의한 분산으로 분산성을 극대화함으로써 전기전도도를 획기적으로 향상시킬 수 있다. FIGS. 1 and 2 are schematic cross-sectional views illustrating a method of producing a master batch according to an embodiment of the present invention, that is, a first resin having a low affinity with carbon nanoparticles is melt-kneaded with carbon nanoparticles to prepare a master batch, Melting and kneading the master batch and the first resin with a carbon nano-particle to melt-knead the second resin having a high affinity with the carbon nanoparticles as a control group thereof, FIG. 2 is a schematic view showing the dispersion of carbon nanotubes according to the process of FIG. Specifically, when the CNT is dispersed in mPPE and the PA66 is remelted and kneaded, the CNTs try to migrate to the higher affinity PA66. At this time, CNTs having a large aspect ratio and a small diameter disperse CNT particles from mPPE to PA66 rather than CNT agglomerates because the diffusion rate in mPPE and the migration speed at the mPPE / PA66 interface are high. By such dispersion of particles, the dispersibility can be maximized and the electric conductivity can be improved remarkably.

이때, 상기 a) 단계의 용융혼련 공정은 바람직하게는 260 ~ 300, 압출속도 50 ~ 300rpm의 조건에서 실시할 수 있으며, 반드시 이에 제한되지 않는다. At this time, the melt-kneading step in step a) may be carried out at a temperature of preferably 260 to 300 and an extrusion rate of 50 to 300 rpm, but is not limited thereto.

본 발명은 상술한 조성물을 포함하는 고분자 블렌드를 제공할 수 있다.
The present invention can provide a polymer blend comprising the above-mentioned composition.

이하, 본 발명을 보다 구체적으로 설명하기 위하여 하기 일 예를 들어 설명하는 바, 본 발명이 하기 실시예에 한정되는 것은 아니다. Hereinafter, the present invention will be described in more detail with reference to the following examples. However, the present invention is not limited to the following examples.

하기 실시예 및 비교예에서 사용된 각 성분의 사양은 다음과 같다.The specifications of each component used in the following examples and comparative examples are as follows.

(A) 변성 폴리페닐렌에테르(mPPE ; modified Poly(phenylene ether))(A) modified poly (phenylene ether) (mPPE)

PPE:PS(중량비)=2:8(PPE : Mitsubishi EP사 PX-100F, PS : LG화학의 15NF)인 것을 사용하였다. PPE: PS (weight ratio) = 2: 8 (PPE: Mitsubishi EP PX-100F, PS: 15NF of LG Chem) was used.

(B) 폴리아미드 66(B) Polyamide 66

Basf사의 A4H를 사용하였다. A4H from Basf was used.

(C) 탄소나노튜브(C) Carbon nanotubes

(C1) Nanocyl사의 NC7000을 사용하였다. (C1) Nanocyl NC7000 was used.

(C2) 제일모직의 MWNT을 사용하였다.
(C2) Cheil Industries' MWNT was used.

(실시예 1)(Example 1)

mPPE(친화도mPPE = 0.42)에 탄소나노튜브를 압출공정을 통해 용융혼련하여 mPPE/CNT 마스터배치를 만든 후, mPPE/CNT 마스터배치를 PA66(친화도PA66 = 2.39)와 재용융혼련하여 복합 수지를 제조하였다. 이를 사출공정을 통해 시편을 제조하였다. 이때, 압출공정은 이축스크류압출기(5mm co-rotating twin screw extruder, L/D=36, Screw speed : 200rpm, 압출온도 260~300)을 사용하였으며, 사출공정은 사출온도 280~300, 금형온도 : 90~100 조건으로 실시하였다.
The mPPE / CNT master batch was re-melted and kneaded with PA66 (affinity PA66 = 2.39) to prepare a mPPE / CNT master batch by melt kneading the carbon nanotubes in an mPPE (affinity mPPE = 0.42) . The specimens were prepared through the injection process. In this case, the extrusion process was performed using a 5 mm co-rotating twin screw extruder (L / D = 36, screw speed: 200 rpm, extrusion temperature 260 to 300) 90 to 100.

(실시예 2)(Example 2)

실시예 1에서 mPPE:PA66비율을 4:6에서 6:4로 변화시킨 것 외에는 동일하게 제조하였다.
Except that the mPPE: PA66 ratio in Example 1 was changed from 4: 6 to 6: 4.

(실시예 3)(Example 3)

실시예 1에서 Nanocyl사 NC7000 대신 제일모직 MWNT를 사용한 것 외에는 동일하게 제조하였다.
Except that Cheil Industries MWNT was used instead of Nanocyl Corp. NC7000 in Example 1.

(비교예 1)(Comparative Example 1)

PA66에 Nanocyl사 NC7000를 압출기를 통해 용융혼련하여 PA66/CNT 마스터배치를 만든 후, PA66/CNT 마스터배치를 mPPE와 재용융혼련하여 복합수지를 제조하여 사출을 통해 시편을 제조하였다.
The PA66 / CNT master batch was melted and kneaded with mPPE to produce a composite resin, and the specimen was prepared by injection molding.

(비교예 2)(Comparative Example 2)

비교예 1에서 Nanocyl사 NC7000 대신 제일모직 MWNT를 사용한 것 외에는 동일하게 제조하였다.
Except that Cheil Industries MWNT was used in place of Nanocyl Corp. NC7000 in Comparative Example 1.

Figure pat00021

Figure pat00021

Figure pat00022

Figure pat00022

Figure pat00023

Figure pat00023

도 3은 실시예 1의 투과전자현미경 사진으로서 마스터배치 제조 과정에서 변성폴리페닐렌에테르 수지(mPPE)에 탄소나노튜브(CNT)를 분산시켰음에도 불구하고 시간이 지남에 따라 mPPE 부분에 존재하던 CNT가 폴리아미드 66(PA66)로 이동하여 결과적으로 PA66에 고르게 분산되어 있음을 확인할 수 있었다. 이는 본 발명에 따른 실시예에서 사용한 CNT 및 PA66 간의 친화도가 높아(친화도PA66 = 2.39 > 1) mPPE에 분산된 CNT가 재용융혼련 시 PA66로 이동하였기 때문이다. 이는 입자이동에 의한 분산(filler transfer-induced dispersion)으로 인한 것으로, 재용융혼련 시 CNT의 이동으로 분산성이 향상된 것이다. FIG. 3 is a transmission electron microscope photograph of Example 1 showing that although carbon nanotubes (CNTs) were dispersed in a modified polyphenylene ether resin (mPPE) during the master batch production process, CNTs Was transferred to polyamide 66 (PA66), and as a result, it was confirmed that PA66 was uniformly dispersed in PA66. This is because the affinity between CNT and PA66 used in the examples of the present invention (affinity PA66 = 2.39 > 1) was high and the CNT dispersed in mPPE migrated to PA66 during remelting and kneading. This is due to the dispersion of filler transfer-induced dispersion, and the dispersibility is improved by the movement of CNT during re-melt-kneading.

반면, 도 4에서 볼 수 있는 바와 같이, 비교예 1은 CNT가 mPPE에 있지 않고 PA66에 선택적으로 분산되어 있으나 CNT들이 뭉쳐서 분산되어 있는 것을 확인할 수 있으며, 이는 실시예1에 비해 분산성이 떨어지므로 전기전도도가 훨씬 낮게 나타난 것으로 확인할 수 있다.
On the other hand, as can be seen from FIG. 4, in Comparative Example 1, CNTs were not dispersed in mPPE but selectively dispersed in PA66, but CNTs were clustered and dispersed. And the electrical conductivity is much lower.

이상과 같이 본 발명에서는 한정된 실시예에 의해 설명되었으나 이는 본 발명의 보다 전반적인 이해를 돕기 위해서 제공된 것일 뿐, 본 발명은 상기의 실시예에 한정되는 것은 아니며, 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 이러한 기재로부터 다양한 수정 및 변형이 가능하다. While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, Various modifications and variations are possible in light of the above teachings.

따라서, 본 발명의 사상은 설명된 실시예에 국한되어 정해져서는 아니되며, 후술하는 특허청구범위뿐 아니라 이 특허청구범위와 균등하거나 등가적 변형이 있는 모든 것들은 본 발명 사상의 범주에 속한다고 할 것이다.
Accordingly, the spirit of the present invention should not be construed as being limited to the embodiments described, and all of the equivalents or equivalents of the claims, as well as the following claims, belong to the scope of the present invention .

Claims (15)

a) 제1수지 및 탄소나노입자를 용융혼련하여 마스터배치를 제조하는 단계 및
b) 상기 마스터배치 및 제2수지를 재용융혼련하는 단계
를 포함하며, 상기 제1수지 및 제2수지는 탄소나노입자에 대한 친화도가 하기 식 1을 만족하는 전기전도도가 향상된 고분자 블렌드 조성물의 제조방법.
(식 1)
Figure pat00024

(상기 식 1에서,
Figure pat00025
,
Figure pat00026
이다. 이때,
Figure pat00027
은 물질 1과 2사이의 계면장력을 나타낸다. 또한,
Figure pat00028
이며, νd : 비극성성분의 표면에너지값, νp: 극성성분의 표면에너지값을 의미한다.)a) preparing a master batch by melt kneading the first resin and the carbon nanoparticles, and
b) re-melt-kneading the masterbatch and the second resin
Wherein the first resin and the second resin have an affinity for carbon nanoparticles satisfying Equation (1), and the electrical conductivity is improved.
(Equation 1)
Figure pat00024

(In the above formula 1,
Figure pat00025
,
Figure pat00026
to be. At this time,
Figure pat00027
Represents the interfacial tension between materials 1 and 2. Also,
Figure pat00028
V d : surface energy value of the non-polar component, and v p : surface energy value of the polar component.) 제1항에 있어서,
상기 제1수지는 폴리(2,6-디메틸-1,4-페닐렌)에테르, 폴리(2,6-디에틸-1,4-페닐렌)에테르, 폴리(2,6-디프로필-1,4-페닐렌)에테르, 폴리(2-메틸-6-에틸-1,4-페닐렌)에테르, 폴리(2-메틸-6-프로필-1,4-페닐렌)에테르, 폴리(2-에틸-6-프로필-1,4-페닐렌)에테르, 폴리(2,6-디페닐-1,4-페닐렌)에테르, 폴리(2,6-디메틸-1,4-페닐렌)에테르와 폴리(2,3,6-트리메틸-1,4-페닐렌)에테르의 공중합체, 폴리(2,6-디메틸-1,4-페닐렌)에테르와 폴리(2,3,6-트리에틸-1,4-페닐렌)에테르의 공중합체 및 이들의 조합으로 이루어진 군에서 선택되는 폴리페닐렌에테르계 수지인 전기전도도가 향상된 고분자 블렌드 조성물의 제조방법.The method according to claim 1,
Wherein the first resin is selected from the group consisting of poly (2,6-dimethyl-1,4-phenylene) ether, poly (2,6-diethyl- , 4-phenylene) ether, poly (2-methyl-6-ethyl-1,4-phenylene) ether, Ethyl-6-propyl-1,4-phenylene) ether, poly (2,6-diphenyl-1,4-phenylene) ether, poly (2,6- Copolymers of poly (2,3,6-trimethyl-1,4-phenylene) ether, poly (2,6-dimethyl-1,4-phenylene) 1,4-phenylene) ether, and combinations thereof. The present invention also provides a method for producing a polymer blend composition having improved electrical conductivity, which is a polyphenylene ether-based resin. 제1항에 있어서,
상기 제2수지는 폴리카프로락탐(폴리아미드 6), 폴리(11-아미노운데칸산)(폴리아미드 11), 폴리라우릴락탐(폴리아미드 12), 폴리헥사메틸렌 아디프아미드(폴리아미드 66), 폴리헥사에틸렌 아젤아미드(폴리아미드 69), 폴리헥사에틸렌 세바카미드(폴리아미드 610), 폴리헥사에틸렌 도데카노디아미드(폴리아미드 612), 이들의 공중합체 및 이들의 조합으로 이루어진 군에서 선택되는 폴리아미드계 수지인 전기전도도가 향상된 고분자 블렌드 조성물의 제조방법.The method according to claim 1,
The second resin may be selected from the group consisting of polycaprolactam (polyamide 6), poly (11-aminoundecanoic acid) (polyamide 11), polylauryl lactam (polyamide 12), polyhexamethylene adipamide (polyamide 66) (Polyamide 69), polyhexethylene sebacamide (polyamide 610), polyhexethylene dodecanodiamide (polyamide 612), copolymers thereof, and combinations thereof A method for producing a polymer blend composition having improved electrical conductivity, which is a polyamide-based resin. 제1항에 있어서,
상기 탄소나노입자는 카본블랙, 탄소나노튜브, 탄소나노 구, 탄소나노섬유, 탄소나노막대, 탄소나노뿔, 그라핀, 그라핀 옥사이드 및 이들의 조합으로부터 선택되는 전기전도도가 향상된 고분자 블렌드 조성물의 제조방법.The method according to claim 1,
The carbon nanoparticles may be prepared from a polymer blend composition having improved electrical conductivity selected from carbon black, carbon nanotubes, carbon nanospheres, carbon nanofibers, carbon nanorods, carbon nanotubes, graphene, Way. 탄소나노입자, 상기 탄소나노입자에 대한 친화도가 하기 식 1을 만족하는 제1수지 및 제2수지를 포함하는 전기전도도가 향상된 고분자 블렌드 조성물.
(식 1)
Figure pat00029

(상기 식 1에서,
Figure pat00030
,
Figure pat00031
이다. 이때,
Figure pat00032
은 물질 1과 2사이의 계면장력을 나타낸다. 또한,
Figure pat00033
이며, νd : 비극성성분의 표면에너지값, νp: 극성성분의 표면에너지값을 의미한다.)1. A polymer blend composition having improved electrical conductivity comprising carbon nanoparticles, a first resin having an affinity to the carbon nanoparticles satisfying the following formula (1), and a second resin.
(Equation 1)
Figure pat00029

(In the above formula 1,
Figure pat00030
,
Figure pat00031
to be. At this time,
Figure pat00032
Represents the interfacial tension between materials 1 and 2. Also,
Figure pat00033
V d : surface energy value of the non-polar component, and v p : surface energy value of the polar component.) 제5항에 있어서,
상기 조성물은 제1수지 5 ~ 50중량% 및 제2수지 50 ~ 95중량%로 이루어진 기초 수지 100중량부에 대하여 탄소나노입자 0.1 ~ 10중량부를 포함하는 전기전도도가 향상된 고분자 블렌드 조성물.6. The method of claim 5,
Wherein the composition comprises 0.1 to 10 parts by weight of carbon nanoparticles based on 100 parts by weight of the base resin comprising 5 to 50% by weight of the first resin and 50 to 95% by weight of the second resin. 제5항에 있어서,
상기 제1수지는 폴리(2,6-디메틸-1,4-페닐렌)에테르, 폴리(2,6-디에틸-1,4-페닐렌)에테르, 폴리(2,6-디프로필-1,4-페닐렌)에테르, 폴리(2-메틸-6-에틸-1,4-페닐렌)에테르, 폴리(2-메틸-6-프로필-1,4-페닐렌)에테르, 폴리(2-에틸-6-프로필-1,4-페닐렌)에테르, 폴리(2,6-디페닐-1,4-페닐렌)에테르, 폴리(2,6-디메틸-1,4-페닐렌)에테르와 폴리(2,3,6-트리메틸-1,4-페닐렌)에테르의 공중합체, 폴리(2,6-디메틸-1,4-페닐렌)에테르와 폴리(2,3,6-트리에틸-1,4-페닐렌)에테르의 공중합체 및 이들의 조합으로 이루어진 군에서 선택되는 폴리페닐렌에테르계 수지인 전기전도도가 향상된 고분자 블렌드 조성물.6. The method of claim 5,
Wherein the first resin is selected from the group consisting of poly (2,6-dimethyl-1,4-phenylene) ether, poly (2,6-diethyl- , 4-phenylene) ether, poly (2-methyl-6-ethyl-1,4-phenylene) ether, Ethyl-6-propyl-1,4-phenylene) ether, poly (2,6-diphenyl-1,4-phenylene) ether, poly (2,6- Copolymers of poly (2,3,6-trimethyl-1,4-phenylene) ether, poly (2,6-dimethyl-1,4-phenylene) 1,4-phenylene) ether, and combinations thereof. The polymer blend composition of the present invention is a polyphenylene ether-based resin having improved electrical conductivity. 제5항에 있어서,
상기 제2수지는 폴리카프로락탐(폴리아미드 6), 폴리(11-아미노운데칸산)(폴리아미드 11), 폴리라우릴락탐(폴리아미드 12), 폴리헥사메틸렌 아디프아미드(폴리아미드 66), 폴리헥사에틸렌 아젤아미드(폴리아미드 69), 폴리헥사에틸렌 세바카미드(폴리아미드 610), 폴리헥사에틸렌 도데카노디아미드(폴리아미드 612), 이들의 공중합체 및 이들의 조합으로 이루어진 군에서 선택되는 폴리아미드계 수지인 전기전도도가 향상된 고분자 블렌드 조성물.6. The method of claim 5,
The second resin may be selected from the group consisting of polycaprolactam (polyamide 6), poly (11-aminoundecanoic acid) (polyamide 11), polylauryl lactam (polyamide 12), polyhexamethylene adipamide (polyamide 66) (Polyamide 69), polyhexethylene sebacamide (polyamide 610), polyhexethylene dodecanodiamide (polyamide 612), copolymers thereof, and combinations thereof A polymer blend composition having improved electrical conductivity, which is a polyamide-based resin. 제5항에 있어서,
상기 탄소나노입자는 카본블랙, 탄소나노튜브, 탄소나노 구, 탄소나노섬유, 탄소나노막대, 탄소나노뿔, 그라핀, 그라핀 옥사이드 및 이들의 조합으로부터 선택되는 전기전도도가 향상된 고분자 블렌드 조성물.6. The method of claim 5,
Wherein the carbon nanoparticles are selected from the group consisting of carbon black, carbon nanotubes, carbon nanospheres, carbon nanofibers, carbon nanorods, carbon nanotubes, graphene, graphen oxide, and combinations thereof. 제5항에 있어서,
상기 탄소나노입자는 표면개질한 것을 포함하는 전기전도도가 향상된 고분자 블렌드 조성물.6. The method of claim 5,
Wherein the carbon nanoparticles are surface-modified, and the electrical conductivity is improved. 제5항에 있어서,
상기 탄소나노입자는 평균입경이 10nm내지 100nm인 전기전도도가 향상된 고분자 블렌드 조성물.6. The method of claim 5,
Wherein the carbon nanoparticles have an average particle diameter of 10 nm to 100 nm. 제9항에 있어서,
상기 카본블랙은 아세틸렌의 열분해에 의해 제조되는 전기전도도가 향상된 고분자 블렌드 조성물.10. The method of claim 9,
Wherein the carbon black is produced by pyrolysis of acetylene, wherein the electrical conductivity is improved. 제9항에 있어서,
상기 탄소나노튜브는 단일벽 탄소나노튜브, 다중벽 탄소나노튜브, 다발형 탄소나노튜브 및 이들의 조합 중에서 선택되는 전기전도도가 향상된 고분자 블렌드 조성물.10. The method of claim 9,
Wherein the carbon nanotubes are selected from single wall carbon nanotubes, multi wall carbon nanotubes, multiple carbon nanotubes, and combinations thereof. 제9항에 있어서,
상기 탄소나노섬유는 헤링본 구조, 플레이트릿 구조 또는 튜블라 구조를 갖는 것인 전기전도도가 향상된 고분자 블렌드 조성물.10. The method of claim 9,
Wherein the carbon nanofibers have a herringbone structure, a planar structure, or a tubular structure. 제5항 내지 제14항 중에서 선택되는 조성물을 포함하는 고분자 블렌드.

14. A polymer blend comprising a composition selected from the group consisting of those of claims 5 to 14.

KR1020130142193A 2013-11-21 2013-11-21 polymer blend composition with highly electrical conductivity and method of manufacturing the same KR102130295B1 (en)