KR20140037160A - Protective film and adhesive tape using the same - Google Patents

Protective film and adhesive tape using the same Download PDF

Info

Publication number
KR20140037160A
KR20140037160A KR1020140008862A KR20140008862A KR20140037160A KR 20140037160 A KR20140037160 A KR 20140037160A KR 1020140008862 A KR1020140008862 A KR 1020140008862A KR 20140008862 A KR20140008862 A KR 20140008862A KR 20140037160 A KR20140037160 A KR 20140037160A
Authority
KR
South Korea
Prior art keywords
film layer
adhesive
film
layer
thickness
Prior art date
Application number
KR1020140008862A
Other languages
Korean (ko)
Inventor
안창덕
나영수
정일두
Original Assignee
세계화학공업(주)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 세계화학공업(주) filed Critical 세계화학공업(주)
Priority to KR1020140008862A priority Critical patent/KR20140037160A/en
Publication of KR20140037160A publication Critical patent/KR20140037160A/en

Abstract

Disclosed are a protective film with improved processability and an adhesive tape using the same. The disclosed protective film includes a first film layer including a polyethylene terephthalate resin, a first adhesive layer, and a second film layer including at least one among a polyethylene resin and a polyvinyl chloride resin.

Description

보호필름 및 이를 이용한 점착테이프{PROTECTIVE FILM AND ADHESIVE TAPE USING THE SAME}PROTECTIVE FILM AND ADHESIVE TAPE USING THE SAME}

본 발명은 보호필름 및 이를 이용한 점착테이프에 관한 것으로서, 보다 상세하게는 가공성이 우수한 보호필름 및 이를 이용한 점착테이프에 관한 것이다. The present invention relates to a protective film and an adhesive tape using the same, and more particularly, to a protective film excellent in processability and an adhesive tape using the same.

철판의 절곡(bending)은 평판인 철판에 다양한 모양을 만들기 위해 사용되는 대표적인 성형법으로서, 절곡시 수직 혹은 180도에 가까운 각도로 철판을 접어주면서 다양한 모양의 형태를 만들어 주는 가공법이다. Bending of the iron plate (bending) is a typical forming method used to make a variety of shapes on the plate, a plate is a processing method to form a variety of shapes while folding the iron plate at an angle of vertical or close to 180 degrees when bending.

이러한 가공법에서는 철판을 접어주는 과정에서 철판의 표면을 절곡기로부터 보호해주기 위해 표면 보호용 테이프를 사용한다. 이때, 두께 1mm 이하의 얇은 철판은 절곡시 가해지는 힘이 적어 보호용 테이프의 표면에 손상 없이 가공이 가능하다. 하지만, 두께 1mm 이상의 철판은 절곡시에 가해지는 힘이 커서 일반적인 보호용 테이프를 사용하면 표면이 손상되어 보호하고자 하는 철판의 표면에 압입 또는 스크래치 등의 손상을 주게 되어 보호용 테이프로써의 역할을 할 수 없게 되는 문제점이 발생하였다.In this process, the surface protection tape is used to protect the surface of the iron plate from the bending machine during the folding of the iron plate. At this time, the thin iron plate of less than 1mm thickness is less applied to the bending can be processed without damaging the surface of the protective tape. However, steel plates with a thickness of 1mm or more have a large force applied during bending, and if a general protective tape is used, the surface may be damaged, causing damage to the surface of the steel sheet to be protected, such as indentation or scratches, and thus cannot serve as a protective tape. There was a problem.

이러한 문제점을 해결하기 위하여, 보호용 테이프를 2중으로 부착한 후 가공공정을 거치는 방법이 고려되었다. 현재 보호용 테이프에는 폴리에틸렌 수지(PolyEthylene, PE) 또는 폴리염화비닐 수지(PolyVinyl Chloride, PVC)가 사용되는데, 이에 따라 보호용 테이프를 2중으로 사용할 때는 PE 및 PVC를 함께 사용하거나 또는 PVC 및 PVC를 사용하고 있다. In order to solve this problem, a method of applying a protective tape in duplicate and then going through a processing process was considered. Polyethylene resin (PolyEthylene, PE) or polyvinyl chloride resin (PolyVinyl Chloride, PVC) is currently used for the protective tape. Therefore, when the protective tape is doubled, PE and PVC are used together or PVC and PVC are used. .

그러나 보호용 테이프의 2중 부착으로 인한 원가상승 및 부착면의 탈리로 인한 불량률의 증가가 발생하였고, 나아가 가공 후 상부에 부착된 테이프의 손상으로 인한 2차 가공의 어려움이나 파손된 테이프로 인한 가공 중 압입 발생 또는 금형의 청소 문제 등의 또 다른 문제점이 발생하였다. However, the cost increase due to the double attachment of the protective tape and the increase of the defective rate due to the detachment of the attachment surface occurred, and furthermore, the difficulty of secondary processing due to the damage of the tape attached to the upper part after the processing, or during the processing due to the broken tape. Another problem, such as the occurrence of indentation or cleaning of the mold, has arisen.

본 발명은 상술한 문제점을 해결하기 위한 것으로, 본 발명의 목적은 가공성이 우수한 보호필름 및 이를 이용한 점착테이프를 제공하는 데 있다.The present invention is to solve the above problems, an object of the present invention to provide a protective film excellent in workability and an adhesive tape using the same.

이상과 같은 목적을 달성하기 위한 본 발명의 일 측면에 따른 보호필름은 폴리에틸렌테레프탈레이트 수지를 포함하는 제1 필름층; 제1 필름층 상의 제1 접착층; 및 제1 접착층 상의 폴리에틸렌 수지 및 폴리염화비닐 수지 중 적어도 하나를 포함하는 제2 필름층;을 포함한다. Protective film according to an aspect of the present invention for achieving the above object is a first film layer comprising a polyethylene terephthalate resin; A first adhesive layer on the first film layer; And a second film layer comprising at least one of a polyethylene resin and a polyvinyl chloride resin on the first adhesive layer.

제1 필름층의 두께는 보호필름의 전체 두께를 기준으로 하여 10 %내지 40 %이하인 것이 바람직하다. 또한, 제1 필름층은 UV안정제, UV흡수제, 안료 및 무기제 중 적어도 하나의 첨가제를 더 포함할 수 있는데, 첨가제는 폴리에틸렌테레프탈레이트 수지 100중량부를 기준으로 하여 5중량부 이하로 첨가되는 것이 바람직하다. The thickness of the first film layer is preferably 10% to 40% or less based on the total thickness of the protective film. In addition, the first film layer may further include at least one additive of a UV stabilizer, a UV absorber, a pigment, and an inorganic agent. The additive may be added in an amount of 5 parts by weight or less based on 100 parts by weight of polyethylene terephthalate resin. Do.

제1 접착층의 두께는 보호필름의 전체 두께를 기준으로 하여 10 %이하인 것이 바람직하다. 또한, 제1 접착층은 에폭시계 접착제, 이소시안계 접착제, 아크릴계 접착제, 고무계 접착제 및 실리콘계 접착제 중 적어도 하나를 포함할 수 있다. The thickness of the first adhesive layer is preferably 10% or less based on the total thickness of the protective film. In addition, the first adhesive layer may include at least one of an epoxy adhesive, an isocyanate adhesive, an acrylic adhesive, a rubber adhesive, and a silicone adhesive.

제2 필름층의 두께는 보호필름의 전체 두께를 기준으로 하여 55 % 내지 85 %인 것이 바람직하다. 또한, 제2 필름층은 UV안정제, UV흡수제, 안료 및 무기제 중 적어도 하나의 첨가제를 더 포함할 수 있는데, 첨가제는 제2 필름층에 포함된 폴리에틸렌 수지 및 폴리염화비닐 수지 전체 중량부를 100중량부를 기준으로 하여 5중량부 이하로 첨가되는 것이 바람직하다. The thickness of the second film layer is preferably 55% to 85% based on the total thickness of the protective film. In addition, the second film layer may further include at least one additive of a UV stabilizer, a UV absorber, a pigment, and an inorganic agent, wherein the additive is 100 parts by weight of the total weight of the polyethylene resin and the polyvinyl chloride resin included in the second film layer. It is preferable to add 5 parts by weight or less based on parts.

본 발명의 다른 측면에 따르면, 폴리에틸렌테레프탈레이트 수지를 포함하는 제1 필름층; 제1 필름층 상의 제1 접착층; 제1 접착층 상의 폴리에틸렌 수지 및 폴리염화비닐 수지 중 적어도 하나를 포함하는 제2 필름층; 및 제2 필름층 상의 제2 접착층;을 포함하는 점착테이프가 제공된다. According to another aspect of the invention, the first film layer comprising a polyethylene terephthalate resin; A first adhesive layer on the first film layer; A second film layer comprising at least one of a polyethylene resin and a polyvinyl chloride resin on the first adhesive layer; And a second adhesive layer on the second film layer.

본 발명에 따르면, 1mm 이상의 두꺼운 철판을 가공할 때에도 보호용 점착테이프로서 사용되어, 철판의 절곡 등의 가공시 소재의 표면을 효과적으로 보호할 수 있다. According to the present invention, it is used as a protective adhesive tape even when processing a thick iron plate of 1mm or more, it is possible to effectively protect the surface of the raw material during processing such as bending of the iron plate.

또한, 본 발명에 따른 보호필름이나 점착테이프는 미끄럼성이 좋고 표면 경질성이 우수하면서도 강도가 높은 PET층과 신장성이 우수한 PE 또는 PVC 층을 모두 포함하고 있어 찢김이나 눌림, 압입자국이 남지 않고, 점착성과 신율이 우수하여 소재로부터 쉽게 탈리되지 않아 2차 이상의 가공이 용이한 효과가 있다.In addition, the protective film or the adhesive tape according to the present invention includes both a PET layer and a PE or PVC layer having excellent strength and extensibility while having excellent surface rigidity and excellent elongation, without tearing, crushing or indentation. Excellent adhesiveness and elongation, so that it is not easily detached from the material, there is an effect that the second or more processing is easy.

도 1은 실시예 1과 같이 제조된 본 발명에 따른 보호필름을 철판에 부착하여 가공(절곡)한 후 측정한 사진이다.
도 2는 실시예 6과 같이 제조된 본 발명에 따른 보호필름을 철판에 부착하여 가공(절곡)한 후 측정한 사진이다.
도 3은 비교예 1과 같이 제조된 보호필름을 철판에 부착하여 가공한 후 측정한 사진이다.
도 4는 비교예 5와 같이 제조된 보호필름을 철판에 부착하여 가공한 후 측정한 사진이다.1 is a photograph measured after the processing (bending) by attaching a protective film according to the present invention prepared in Example 1 to the iron plate.
Figure 2 is a photograph measured after the processing (bending) by attaching a protective film according to the invention prepared in Example 6 to the iron plate.
3 is a photograph measured after the protective film prepared as in Comparative Example 1 attached to the iron plate processed.
4 is a photograph measured after the protective film prepared as in Comparative Example 5 attached to the iron plate processed.

이하, 본 발명의 실시형태를 설명한다. 그러나, 본 발명의 실시형태는 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 이하 설명하는 실시형태로 한정되는 것은 아니다. 본 발명의 실시형태는 당업계에서 통상의 지식을 가진 자에게 본 발명을 보다 완전하게 설명하기 위해서 제공되는 것이다.
EMBODIMENT OF THE INVENTION Hereinafter, embodiment of this invention is described. However, embodiments of the present invention may be modified in various other forms, and the scope of the present invention is not limited to the embodiments described below. Embodiments of the present invention are provided to more fully describe the present invention to those skilled in the art.

본 발명의 일실시예에 따른 보호필름은 폴리에틸렌테레프탈레이트(polyethyleneterephthalate) 수지(이하, PET라고 함)를 포함하는 제1 필름층; 제1 필름층 상의 제1 접착층; 및 제1 접착층 상의 폴리에틸렌(PolyEthylene) 수지(이하, PE라고 함) 및 폴리염화비닐(Polyvinyl chloride) 수지(이하 PVC라고 함) 중 적어도 하나를 포함하는 제2 필름층;을 포함한다. 즉, 본 실시예에서, 보호필름은 PET 재질로 이루어져 표면의 경질성이 우수한 PET 필름층과, PE나 PVC를 포함하여 신율(Elongation)이 우수한 PE/PVC필름층과, 양 필름층을 접착시키기 위한 접착성분을 포함하는 점착층을 포함한다. Protective film according to an embodiment of the present invention is a first film layer containing a polyethylene terephthalate (polyethyleneterephthalate) resin (hereinafter referred to as PET); A first adhesive layer on the first film layer; And a second film layer including at least one of a polyethylene (polyethylene) resin (hereinafter referred to as PE) and a polyvinyl chloride resin (hereinafter referred to as PVC) on the first adhesive layer. That is, in the present embodiment, the protective film is made of a PET material, the surface of the PET film layer having excellent surface rigidity, PE / PVC including PE or PVC film with excellent elongation (Elongation), and bonding both film layers It includes an adhesive layer containing an adhesive component for.

본 실시예에 따른 보호필름은 그 일면에 접착층을 더 추가하여 점착테이프로서 사용될 수 있는데, 이러한 점착테이프는 스테인리스 스틸이나 도장용 강판과 같이 철판 등의 가공 소재의 표면에 부착되어, 소재의 표면 보호를 위하여 사용될 수 있다. 특히 이러한 점착테이프는 건축구조물, 제어반구조물, 엘리베이터 등에 사용되는 2mm 정도의 철판(스테인리스 스틸, 도장용 강판 등)의 가공 공정에서 바람직하게 사용될 수 있다. The protective film according to the present embodiment may be used as an adhesive tape by adding an adhesive layer on one surface thereof, and the adhesive tape is attached to the surface of a workpiece such as an iron plate, such as stainless steel or a steel sheet for painting, to protect the surface of the material. Can be used for In particular, the adhesive tape can be preferably used in the processing of the steel plate (stainless steel, steel plate for painting, etc.) of about 2mm used in building structures, control panel structures, elevators and the like.

본 실시예에서 보호필름은 PET를 포함하는 제1 필름층을 포함한다. 제1 필름층은 PET를 포함하는데, PET 재질은 표면의 경질성이 우수하다. 또한, PET는 합성폴리머로서, 강도가 높고 내열성이 높으며, 표면의 미끄럼성이 좋다. In this embodiment, the protective film includes a first film layer containing PET. The first film layer includes PET, but the PET material has excellent surface rigidity. In addition, PET is a synthetic polymer, which has high strength, high heat resistance, and good surface slipperiness.

제1 필름층은 점착테이프의 최상위에 위치하는데, PET의 물성에 따라 제1 필름층은 절곡 등의 가공시 수십에서 수백톤의 압력이 가해지더라도 소재의 표면에 압입 자국이나, 눌림 현상이 발생하지 않는다. 또한, 제1 필름층은 미끄럼성이 좋아 찢어짐이나 터짐 현상이 생기지 않게 되고, 들뜸 현상이 없어 불량률을 낮출 수 있다. The first film layer is located at the top of the adhesive tape. Depending on the physical properties of PET, the first film layer does not cause indentation or crushing on the surface of the material even when pressures of several tens to hundreds of tons are applied during bending or the like. Do not. Moreover, since a 1st film layer has good slipperiness | lubricacy, it does not generate | occur | produce a tearing or bursting phenomenon, and there is no lifting phenomenon and can lower a defective rate.

이러한 제1 필름층의 두께는 보호필름의 전체 두께를 기준으로 하여 50% 이하인 것이 바람직한데, 인장강도가 강한 PET 층의 두께가 50%를 초과하면 가공 후 가공소재의 표면에서 들뜰 수 있기 때문이다. 바람직하게는 제1 필름층의 두께는 10 %내지 40 %이하이다. The thickness of the first film layer is preferably 50% or less based on the total thickness of the protective film, because if the thickness of the PET layer having a strong tensile strength exceeds 50%, it may be lifted from the surface of the processed material after processing. . Preferably the thickness of the first film layer is 10% to 40% or less.

또한, 제1 필름층은 UV안정제, UV흡수제, 안료 및 무기제(예를 들면, TiO2, CaCO3) 중 적어도 하나의 첨가제를 더 포함하여 원하는 물성을 보강할 수 있다. 첨가제 중, UV안정제는 PET 100중량부를 기준으로 0.1 ~ 5중량부, UV흡수제는 0.1 ~ 5중량부, 안료는 0.1~5중량부 및 무기제는 0.1~5중량부를 포함시키는 것이 바람직하다. In addition, the first film layer may further include at least one additive of a UV stabilizer, a UV absorber, a pigment, and an inorganic agent (eg, TiO 2 , CaCO 3 ) to reinforce desired physical properties. Among the additives, the UV stabilizer is preferably 0.1 to 5 parts by weight based on 100 parts by weight of PET, 0.1 to 5 parts by weight of the UV absorber, 0.1 to 5 parts by weight of the pigment and 0.1 to 5 parts by weight of the inorganic agent.

다만, 첨가제는 PET 100중량부를 기준으로 하여 5중량부 이하로 첨가되는 것이 바람직한데, 5 중량부 이상 첨가하면 PET 수지와의 혼합성이 떨어져 외부의 조건(빛, 열, 가공압 등)에 의해 가공성이 나빠지기 때문이다. 특히 접착층과의 부착면에서 과량의 첨가제는 점착제의 탈리를 발생시켜 가공물의 표면에 점착제의 오염을 유발할 수 있다.However, the additive is preferably added in an amount of 5 parts by weight or less based on 100 parts by weight of PET. When 5 parts by weight or more is added, the additives are inferior in compatibility with PET resins due to external conditions (light, heat, processing pressure, etc.). This is because workability deteriorates. In particular, an excessive amount of additives in the adhesion surface with the adhesive layer may cause detachment of the adhesive, which may cause contamination of the adhesive on the surface of the workpiece.

제1 필름층 상에는 제2 필름층과의 접착을 위한 제1 접착층이 형성된다. 제1 접착층은 PET를 포함하는 필름층과 PE 또는 PVC를 포함하는 필름층을 서로 부착시킬 수 있는 접착성분을 포함한다. 제1 접착층에는 폴리올레핀(PO) 계열의 접착제를 사용할 수 있고, 예를 들면, 에폭시계 접착제, 이소시안계 접착제, 아크릴계 접착제, 고무계 접착제 또는 실리콘계 접착제를 사용할 수 있다. The first adhesive layer for bonding with the second film layer is formed on the first film layer. The first adhesive layer includes an adhesive component capable of adhering the film layer including PET and the film layer including PE or PVC to each other. A polyolefin (PO) -based adhesive may be used for the first adhesive layer, and for example, an epoxy adhesive, an isocyanate adhesive, an acrylic adhesive, a rubber adhesive, or a silicone adhesive may be used.

제1 접착층의 두께는 보호필름의 전체 두께를 기준으로 하여 10 %이하인 것이 바람직하다. 제1 접착층의 두께가 너무 두꺼우면, 필름층의 두께비율이 낮아져 적절한 가공성을 나타내지 못하고, 접착층의 함몰로 인하여 가공소재에 압입 및 보호필름에 주름이 발생할 수 있다. The thickness of the first adhesive layer is preferably 10% or less based on the total thickness of the protective film. If the thickness of the first adhesive layer is too thick, the thickness ratio of the film layer is lowered, thereby not exhibiting proper workability, and the indentation of the adhesive layer and wrinkles in the protective film may occur due to the depression of the adhesive layer.

제1 접착층 상에는 PE 및 PVC 중 적어도 하나를 포함하는 제2 필름층이 형성된다. PET를 포함하는 제1 필름층은 표면의 미끄럼성이 우수하고, 강도가 PE와 PVC에 비해 강한 PET를 기재로 하고 있으나, PET는 인장강도가 PE 및 PVC에 비해 매우 높아 절곡후 PET의 인장강도를 점착제가 극복하지 못하고 철판의 표면에서 들뜨는 현상이 발생할 수 있다. 이에 따라 본 실시예에서는 보호필름을 PET를 포함하는 제1 필름층 및 PE/PVC를 포함하는 제2 필름층을 함께 사용하고 있다. PE 또는 PVC는 신율(Elongation)이 우수하므로 이러한 문제점을 보완할 수 있고, 절곡 등의 1차 가공을 한 후에도 가공 성형물의 표면으로부터 점착테이프가 쉽게 탈리되지 않아 2차, 3차 가공이 가능하다. A second film layer including at least one of PE and PVC is formed on the first adhesive layer. The first film layer containing PET has excellent surface sliding property, and the strength is based on PET, which is stronger than PE and PVC. However, the tensile strength of PET after bending is very high compared to PE and PVC. The pressure-sensitive adhesive may not be lifted off the surface of the iron plate may occur. Accordingly, in the present embodiment, the protective film uses a first film layer including PET and a second film layer including PE / PVC. Since PE or PVC has excellent elongation, this problem can be compensated for, and even after the primary processing such as bending, the adhesive tape is not easily detached from the surface of the processed molding, so that secondary and tertiary processing can be performed.

PE는 저밀도폴리에틸렌LDPE(Low density polyethylene), 선형저밀도폴리에틸렌LLDPE(Linear Low Density Polyethylene), 고밀도폴리에틸렌HDPE(High density polyethylene) 및 이들의 혼합물일 수 있다. PVC는 PVC 수지에 50% 이하의 가소제가 포함된 연질 PVC 필름을 사용하는 것이 바람직하다. PE may be low density polyethylene (LDPE), linear low density polyethylene (LLDPE), high density polyethylene (HDPE) and mixtures thereof. PVC preferably uses a flexible PVC film containing up to 50% plasticizer in the PVC resin.

제2 필름층의 두께는 보호필름의 전체 두께를 기준으로 하여 90%이하인 것이 바람직하고, 더욱 바람직하게는 55 % 내지 85 %이다. 제2 필름층의 두께비율이 너무 높으면 강도 및 미끄럼성이 우수한 PET를 포함하는 제1 필름층의 두께비율이 낮아져 가공시 압입현상 및 점착테이프의 손상등이 발생할 수 있다. The thickness of the second film layer is preferably 90% or less, more preferably 55% to 85% based on the total thickness of the protective film. If the thickness ratio of the second film layer is too high, the thickness ratio of the first film layer including PET having excellent strength and sliding properties may be lowered, such that indentation and damage to the adhesive tape may occur during processing.

또한, 제2 필름층은 UV안정제, UV흡수제, 안료 및 무기제(예를 들면, TiO2, CaCO3) 중 적어도 하나의 첨가제를 더 포함하여 원하는 물성을 보강할 수 있다. 첨가제 중, UV안정제는 제2 필름층에 포함된 PE 또는 PVC 100중량부를 기준으로 0.1 ~ 5중량부, UV흡수제는 0.1 ~ 5중량부, 안료는 0.1~5중량부 및 무기제는 0.1~5중량부를 포함시키는 것이 바람직하다. In addition, the second film layer may further include at least one additive of a UV stabilizer, a UV absorber, a pigment, and an inorganic agent (eg, TiO 2 , CaCO 3 ) to reinforce desired properties. Among the additives, the UV stabilizer is 0.1 to 5 parts by weight based on 100 parts by weight of PE or PVC contained in the second film layer, 0.1 to 5 parts by weight of UV absorber, 0.1 to 5 parts by weight of pigment and 0.1 to 5 parts of inorganic agent. It is preferred to include parts by weight.

다만, 첨가제는 제2 필름층에 포함된 PE 또는 PVC 100중량부를 기준으로 하여 5중량부 이하로 첨가되는 것이 바람직한데, 5 중량부 이상 첨가하면 PE 또는 PVC 수지와의 혼합성이 떨어져 외부의 조건(빛, 열, 가공압 등)에 의해 가공성이 나빠지기 때문이다. 특히 접착층과의 부착면에서 과량의 첨가제는 점착제의 탈리를 발생시켜 가공물의 표면에 점착제의 오염을 유발할 수 있다.However, the additive is preferably added in an amount of 5 parts by weight or less based on 100 parts by weight of PE or PVC contained in the second film layer. This is because workability deteriorates due to (light, heat, work pressure, etc.). In particular, an excessive amount of additives in the adhesion surface with the adhesive layer may cause detachment of the adhesive, which may cause contamination of the adhesive on the surface of the workpiece.

본 발명의 다른 측면에 따르면, 폴리에틸렌테레프탈레이트 수지를 포함하는 제1 필름층; 제1 필름층 상의 제1 접착층; 제1 접착층 상의 폴리에틸렌 수지 및 폴리염화비닐 수지 중 적어도 하나를 포함하는 제2 필름층; 및 제2 필름층 상의 제2 접착층;을 포함하는 점착테이프가 제공된다.
According to another aspect of the invention, the first film layer comprising a polyethylene terephthalate resin; A first adhesive layer on the first film layer; A second film layer comprising at least one of a polyethylene resin and a polyvinyl chloride resin on the first adhesive layer; And a second adhesive layer on the second film layer.

본 발명에 따른 보호필름 중 제2 필름층 상에 접착층을 추가적으로 두어 점착테이프로서 사용할 수 있다. 제1 접착층이 제1 필름층 및 제2 필름층을 접착시키기 위한 것이라면, 추가적인 접착층인 제2 접착층은 보호필름을 가공소재에 부착시키기 위한 접착층이다. 따라서, 제2 접착층은 제2 필름층과 가공소재에 따라 적절한 접착제를 사용할 수 있다. Among the protective films according to the present invention, an adhesive layer may be additionally placed on the second film layer to be used as an adhesive tape. If the first adhesive layer is for bonding the first film layer and the second film layer, the second adhesive layer, which is an additional adhesive layer, is an adhesive layer for attaching the protective film to the workpiece. Therefore, a suitable adhesive can be used for the second adhesive layer depending on the second film layer and the workpiece.

제2 필름층이 PE 또는 PVC를 포함하고, 가공소재가 철판인 경우, 제2 접착층은 고무계 접착제, 아크릴계 접착제 또는 실리콘계 접착제 중 적어도 어느 하나를 포함할 수 있다. 이 중 내열성 및 응집성이 우수한 아크릴계 접착제를 사용하는 것이 바람직하다. When the second film layer includes PE or PVC, and the processed material is an iron plate, the second adhesive layer may include at least one of a rubber adhesive, an acrylic adhesive, or a silicone adhesive. It is preferable to use the acrylic adhesive excellent in heat resistance and cohesion among these.

이하, 실시예에 의해 본 발명을 더욱 상세하게 설명하지만, 본 발명은 이들 예에 의해 한정되는 것이 아니다. Hereinafter, although an Example demonstrates this invention still in detail, this invention is not limited by these examples.

[실시예 1]Example 1

PET를 포함하는 제1 필름층의 두께를 전체 보호필름의 두께를 기준으로 하여 10%, 제1 접착층의 두께를 10%, 그리고, PE 또는 PVC를 포함하는 제2 필름층의 두께를 80%로 하여 보호필름을 제조하고, 제2필름층 상에 접착층을 추가하여 점착테이프를 제조하였다. 10% of the thickness of the first film layer containing PET based on the thickness of the entire protective film, 10% of the thickness of the first adhesive layer, and 80% of the thickness of the second film layer containing PE or PVC The protective film was prepared, and the adhesive tape was prepared by adding an adhesive layer on the second film layer.

[실시예 2][Example 2]

제1 필름층의 두께를 20%, 제2 필름층의 두께를 70%로 한 것을 제외하고는 실시예 1과 동일하게 점착테이프를 제조하였다. An adhesive tape was prepared in the same manner as in Example 1 except that the thickness of the first film layer was 20% and the thickness of the second film layer was 70%.

[실시예 3][Example 3]

제1 필름층의 두께를 40%, 제2 필름층의 두께를 50%로 한 것을 제외하고는 실시예 1과 동일하게 점착테이프를 제조하였다. An adhesive tape was prepared in the same manner as in Example 1 except that the thickness of the first film layer was 40% and the thickness of the second film layer was 50%.

[실시예 4]Example 4

제1 접착층의 두께를 5%, 제2 필름층의 두께를 85%로 한 것을 제외하고는 실시예 1과 동일하게 점착테이프를 제조하였다. An adhesive tape was prepared in the same manner as in Example 1 except that the thickness of the first adhesive layer was 5% and the thickness of the second film layer was 85%.

[실시예 5][Example 5]

제1 필름층의 두께를 20%, 제1 접착층의 두께를 5%, 제2 필름층의 두께를 75%로 한 것을 제외하고는 실시예 1과 동일하게 점착테이프를 제조하였다. An adhesive tape was prepared in the same manner as in Example 1 except that the thickness of the first film layer was 20%, the thickness of the first adhesive layer was 5%, and the thickness of the second film layer was 75%.

[실시예 6][Example 6]

제1 필름층의 두께를 40%, 제1 접착층의 두께를 5%, 제2 필름층의 두께를 55%로 한 것을 제외하고는 실시예 1과 동일하게 점착테이프를 제조하였다.
An adhesive tape was prepared in the same manner as in Example 1 except that the thickness of the first film layer was 40%, the thickness of the first adhesive layer was 5%, and the thickness of the second film layer was 55%.

[비교예 1]Comparative Example 1

제1 필름층의 두께를 100%로 하여 제1 접착층 및 제2 필름층을 사용하지 않은 점착테이프를 제조하였다. An adhesive tape having no thickness of the first adhesive layer and the second film layer was prepared using the thickness of the first film layer as 100%.

[비교예 2][Comparative Example 2]

제1 접착층의 두께를 20%, 제2 필름층의 두께를 70%로 한 것을 제외하고는 실시예 1과 동일하게 점착테이프를 제조하였다. An adhesive tape was prepared in the same manner as in Example 1 except that the thickness of the first adhesive layer was 20% and the thickness of the second film layer was 70%.

[비교예 3][Comparative Example 3]

제1 필름층의 두께를 60%, 제2 필름층의 두께를 30%로 한 것을 제외하고는 실시예 1과 동일하게 점착테이프를 제조하였다. A pressure-sensitive adhesive tape was prepared in the same manner as in Example 1 except that the thickness of the first film layer was 60% and the thickness of the second film layer was 30%.

[비교예 4][Comparative Example 4]

제1 필름층의 두께를 50%, 제2 필름층의 두께를 40%로 한 것을 제외하고는 실시예 1과 동일하게 점착테이프를 제조하였다. An adhesive tape was prepared in the same manner as in Example 1 except that the thickness of the first film layer was 50% and the thickness of the second film layer was 40%.

[비교예 5][Comparative Example 5]

제2 필름층의 두께를 100%로 하여, 제1 접착층 및 제1 필름층을 사용하지 않은 점착테이프를 제조하였다.
An adhesive tape was prepared in which the thickness of the second film layer was 100% and the first adhesive layer and the first film layer were not used.

이하의 표 1에는 실시예 1 내지 6 및 비교예 1 내지 5의 보호필름에서의 각 층의 두께 비율이 나타나있다.Table 1 below shows the thickness ratio of each layer in the protective films of Examples 1 to 6 and Comparative Examples 1 to 5.

제1 필름층두께(%)First film layer thickness (%) 제1 접착층두께(%)First adhesive layer thickness (%) 제2 필름층두께(%)Second film layer thickness (%) 실시예1Example 1 1010 1010 8080 실시예2Example 2 2020 1010 7070 실시예3Example 3 4040 1010 5050 실시예4Example 4 1010 55 8585 실시예5Example 5 2020 55 7575 실시예6Example 6 4040 55 5555 비교예1Comparative Example 1 100100 00 00 비교예2Comparative Example 2 1010 2020 7070 비교예3Comparative Example 3 6060 1010 3030 비교예4Comparative Example 4 5050 1010 4040 비교예5Comparative Example 5 00 00 100100

[시험예][Test Example]

실시예 1 내지 6 및 비교예 1 내지 5의 점착테이프를 사용하여 도장용 강판에 부착한 후 절곡가공을 수행하였다. 여기서, 실시예 1 내지 6에서는 PET를 포함하는 제1 필름층 및 PE 또는 PVC를 포함하는 제2 필름층을 모두 포함하는 보호필름을 이용하여 점착테이프를 제조하였다. 그리고, 가공 후 가공성, 가공 후 강판의 상태 및 가공 후의 필름층의 상태를 표 2에 나타내었다. Using the adhesive tapes of Examples 1 to 6 and Comparative Examples 1 to 5 were attached to the steel sheet for coating and then bent. Here, in Examples 1 to 6, an adhesive tape was prepared using a protective film including both a first film layer including PET and a second film layer including PE or PVC. And the workability after processing, the state of the steel plate after processing, and the state of the film layer after processing are shown in Table 2.

실험결과Experiment result 가공성Processability 강판 상태Steel plate condition 필름층 상태Film layer status 실시예1Example 1 양호Good 양호Good 양호Good 실시예2Example 2 양호Good 양호Good 양호Good 실시예3Example 3 양호Good 양호Good 양호Good 실시예4Example 4 양호Good 양호Good 양호Good 실시예5Example 5 양호Good 양호Good 양호Good 실시예6Example 6 양호Good 양호Good 양호Good 비교예1Comparative Example 1 들뜸Lifting 양호Good 양호Good 비교예2Comparative Example 2 양호Good 압입Indentation 주름발생Wrinkle 비교예3Comparative Example 3 들뜸Lifting 압입Indentation 양호Good 비교예4Comparative Example 4 들뜸Lifting 압입Indentation 양호Good 비교예5Comparative Example 5 양호Good 압입Indentation 터짐Burst

표 2에서 확인할 수 있는 바와 같이, 가공성, 강판 상태 및 필름층 상태가 모두 양호한 경우는 실시예의 경우이다. As can be seen from Table 2, the case where the workability, the steel sheet state and the film layer state are all good is the case of the example.

즉, 실시예 1 내지 6을 실험한 결과, 가공성이 양호하고, 가공 후 강판에 압입이 없고, 보호필름에 주름이 발생하는 등의 문제점 없이 모두 양호함을 알 수 있다. That is, as a result of experimenting Examples 1 to 6, it can be seen that the workability is good, there is no indentation in the steel sheet after processing, and all of them are good without problems such as wrinkles in the protective film.

특히, 실시예 1 내지 6에서는 제1 필름층의 두께는 전체 보호필름 두께의 10 % 내지 40 %이었고, 제2 필름층의 두께는 55 % 내지 85%이었으며, 제1 접착층의 두께는 10% 이하였다. In particular, in Examples 1 to 6, the thickness of the first film layer was 10% to 40% of the total protective film thickness, the thickness of the second film layer was 55% to 85%, and the thickness of the first adhesive layer was 10% or less. It was.

이에 반해 비교예 1에서 보호필름은 PET를 포함하는 제1 필름층만으로 구성되어 있으므로 보호필름 전체의 강성이 높아 가공 후 점착제의 응집력이 PET를 포함하는 제1 필름층의 수축성을 극복하지 못하고 들뜨는 현상이 발생하였다.On the contrary, in Comparative Example 1, since the protective film is composed of only the first film layer containing PET, the rigidity of the entire protective film is high, so that the cohesive force of the adhesive after processing does not overcome the shrinkage of the first film layer containing PET. This occurred.

비교예 2는 제1 접착층의 두께가 전체 테이프 두께의 20%를 차지함으로써, 적절한 가공성을 나타내지 못하고, 점착층의 함몰로 인한 압입 및 보호필름에 주름이 발생하였다. In Comparative Example 2, since the thickness of the first adhesive layer accounted for 20% of the total tape thickness, it did not exhibit proper processability, and wrinkles occurred in the indentation and the protective film due to the depression of the adhesive layer.

비교예 3은 PE 또는 PVC를 포함하는 제2 필름층의 두께가 30%로써 PET를 포함하는 제1 필름층의 물성이 보호필름에 강하게 영향을 미쳐 비교예 1과 유사하게 들뜸 현상이 발생하였고, 제2 필름층이 제1 필름층에 의해 눌림이 발생하여 철판에 압입이 발생되었다. In Comparative Example 3, the thickness of the second film layer containing PE or PVC was 30%, so that physical properties of the first film layer containing PET strongly influenced the protective film, and thus the lifting phenomenon occurred similarly to Comparative Example 1. The second film layer was pressed by the first film layer to indent into the iron plate.

비교예 4는 비교예 3에 비하여 제2 필름층의 두께를 40%로 증가시켰음에도 불구하고, 비교예 3과 유사한 결과를 나타내어 제2 필름층이 소정두께를 유지하여야 가공성 및 가공 후 강판의 상태 등이 우수할 것이라고 알 수 있다. In Comparative Example 4, although the thickness of the second film layer was increased to 40% compared to Comparative Example 3, the second film layer exhibited similar results to Comparative Example 3 so that the second film layer had to maintain a predetermined thickness. It can be seen that the back is excellent.

비교예 5는 PET를 포함하는 제1 필름층 및 제1 접착층이 없이, PE 또는 PVC를 포함하는 제2 필름층만을 포함하는 보호필름으로서, 가공시 압입 및 가공 후 보호용 테이프가 터지는 현상이 발생하였다.Comparative Example 5 is a protective film including only the second film layer including PE or PVC, without the first film layer and the first adhesive layer containing PET, a phenomenon that the protective tape burst during the press-fitting and processing during processing .

따라서, 본 발명에서와 같이 보호필름에 미끄럼성 및 표면경질성이 우수하고 강도가 높은 PET를 포함하는 필름층과 신율이 우수한 PE 또는 PVC를 포함하는 필름층을 모두 포함하되, 전체 필름 두께에 대비하여 PET 필름을 10~40%로 형성하고, PE 또는 PVC를 포함하는 필름을 55~85%로 형성하고, 두 필름 사이에 접착층을 5~10%로 형성함으로써, 가공성이 양호하고 가공 후 강판의 상태 및 필름층의 상태 또한 양호하여 재가공이 가능하였음을 알 수 있다. Therefore, as in the present invention, the protective film includes both a film layer including PET having excellent sliding property and surface hardness and high strength, and a film layer including PE or PVC having excellent elongation, but compared to the overall film thickness. By forming a PET film at 10 to 40%, forming a film containing PE or PVC at 55 to 85%, and forming an adhesive layer at 5 to 10% between the two films, so that workability is good and State and state of the film layer In addition, it can be seen that the reprocessing was good.

이와 같이, 본 발명에 따른 보호필름은 두께 1mm 이상의 철판 절곡시에 가해지는 힘에도 철판의 표면에 압입 또는 스크래치 등의 손상을 주지 않는다.
As described above, the protective film according to the present invention does not damage the surface of the iron plate even if the force applied when bending the iron plate 1 mm or more in thickness or the like.

시험예에 대한 가공 결과를 도 1 내지 도 4에 나타내었다. Processing results for the test examples are shown in FIGS. 1 to 4.

도 1 및 도 2은 실시예 1 및 실시예2와 같이 제조된 본 발명에 따른 보호필름을 철판에 부착하여 가공(절곡)한 후 측정한 사진이다. 도 1 및 도 2를 참조하면, 실시예 1 및 실시예 6의 경우, 가공성, 강판상태 및 필름층의 상태가 모두 양호함을 알 수 있다.
1 and 2 are photographs measured after processing (bending) by attaching a protective film according to the present invention prepared in Example 1 and Example 2 to the iron plate. 1 and 2, in the case of Example 1 and Example 6, it can be seen that the workability, the steel sheet state and the state of the film layer are all good.

도 3은 비교예 1과 같이 제조된 보호필름을 철판에 부착하여 가공한 후 측정한 사진이다. 도 3을 참조하면, 비교예 1의 경우, PET을 100% 사용하였기에 경질도가 매우 높아 가공성에서 들뜸 현상(붉은색 원형 표시)이 발생하였음을 알 수 있다.
3 is a photograph measured after the protective film prepared as in Comparative Example 1 attached to the iron plate processed. Referring to FIG. 3, in the case of Comparative Example 1, 100% of PET was used, and thus the hardness was very high, and thus the lifting phenomenon (red circular display) occurred in workability.

도 4는 비교예 5와 같이 제조된 보호필름을 철판에 부착하여 가공한 후 측정한 사진이다. 도 4를 참조하면, 비교예 5의 경우, PE 또는 PVC를 100% 사용하였기에 신율이 매우 좋아 가공 후 압입(붉은색 원형 표시)이 발생하였음을 알 수 있다.
4 is a photograph measured after the protective film prepared as in Comparative Example 5 attached to the iron plate processed. Referring to FIG. 4, in the case of Comparative Example 5, 100% of PE or PVC was used, and thus the elongation was very good, indicating that indentation (red circle display) occurred after processing.

발명은 상술한 실시형태 및 첨부된 도면에 의해 한정되는 것이 아니라, 첨부된 청구범위에 의해 해석되어야 한다. 또한, 본 발명에 대하여 청구범위에 기재된 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 다양한 형태의 치환, 변형 및 변경이 가능하다는 것은 당해 기술분야의 통상의 지식을 가진 자에게 자명할 것이다.
The invention is not to be limited by the foregoing embodiments and the accompanying drawings, but should be interpreted by the appended claims. In addition, it will be apparent to those skilled in the art that various forms of substitution, modification, and alteration are possible within the scope of the present invention without departing from the technical spirit of the present invention.

Claims (10)

폴리에틸렌테레프탈레이트 수지를 포함하는 제1 필름층;
상기 제1 필름층 상의 제1 접착층; 및
상기 제1 접착층 상의 폴리에틸렌 수지 및 폴리염화비닐 수지 중 적어도 하나를 포함하는 제2 필름층;을 포함하는 보호필름.A first film layer comprising polyethylene terephthalate resin;
A first adhesive layer on the first film layer; And
And a second film layer comprising at least one of a polyethylene resin and a polyvinyl chloride resin on the first adhesive layer. 청구항 1에 있어서,
상기 제1 필름층의 두께는 상기 보호필름의 전체 두께를 기준으로 하여 10 %내지 40 %이하인 것을 특징으로 하는 보호필름.The method according to claim 1,
The thickness of the first film layer is a protective film, characterized in that less than 10% to 40% based on the total thickness of the protective film. 청구항 1에 있어서,
상기 제1 필름층은,
UV안정제, UV흡수제, 안료 및 무기제 중 적어도 하나의 첨가제를 더 포함하는 것을 특징으로 하는 보호필름.The method according to claim 1,
The first film layer,
Protective film, characterized in that it further comprises at least one additive of a UV stabilizer, UV absorbers, pigments and inorganic agents. 청구항 3에 있어서,
상기 첨가제는 상기 폴리에틸렌테레프탈레이트 수지 100중량부를 기준으로 하여 5중량부 이하로 첨가되는 것을 특징으로 하는 보호필름.The method according to claim 3,
The additive is a protective film, characterized in that added to 5 parts by weight or less based on 100 parts by weight of the polyethylene terephthalate resin. 청구항 1에 있어서,
상기 제1 접착층의 두께는 상기 보호필름의 전체 두께를 기준으로 하여 10 %이하인 것을 특징으로 하는 것을 특징으로 하는 보호필름.The method according to claim 1,
The thickness of the first adhesive layer is a protective film, characterized in that less than 10% based on the total thickness of the protective film. 청구항 1에 있어서,
상기 제1 접착층은 에폭시계 접착제, 이소시안계 접착제, 아크릴계 접착제, 고무계 접착제 및 실리콘계 접착제 중 적어도 하나를 포함하는 것을 특징으로 하는 보호필름.The method according to claim 1,
The first adhesive layer is a protective film comprising at least one of an epoxy adhesive, an isocyanate adhesive, an acrylic adhesive, a rubber adhesive and a silicone adhesive. 청구항 1에 있어서,
상기 제2 필름층의 두께는 상기 보호필름의 전체 두께를 기준으로 하여 55 % 내지 85 %인 것을 특징으로 하는 것을 특징으로 하는 보호필름.The method according to claim 1,
The thickness of the second film layer is a protective film, characterized in that 55 to 85% based on the total thickness of the protective film. 청구항 1에 있어서,
상기 제2 필름층은,
UV안정제, UV흡수제, 안료 및 무기제 중 적어도 하나의 첨가제를 더 포함하는 것을 특징으로 하는 보호필름.The method according to claim 1,
The second film layer,
Protective film, characterized in that it further comprises at least one additive of a UV stabilizer, UV absorbers, pigments and inorganic agents. 청구항 8에 있어서,
상기 첨가제는 상기 제2 필름층에 포함된 상기 폴리에틸렌 수지 및 상기 폴리염화비닐 수지 전체 중량부를 100중량부를 기준으로 하여 5중량부 이하로 첨가되는 것을 특징으로 하는 보호필름.The method according to claim 8,
The additive is a protective film, characterized in that added to 5 parts by weight or less based on 100 parts by weight of the total weight of the polyethylene resin and the polyvinyl chloride resin contained in the second film layer. 폴리에틸렌테레프탈레이트 수지를 포함하는 제1 필름층;
상기 제1 필름층 상의 제1 접착층;
상기 제1 접착층 상의 폴리에틸렌 수지 및 폴리염화비닐 수지 중 적어도 하나를 포함하는 제2 필름층; 및
상기 제2 필름층 상의 제2 접착층;을 포함하는 점착테이프.A first film layer comprising polyethylene terephthalate resin;
A first adhesive layer on the first film layer;
A second film layer comprising at least one of a polyethylene resin and a polyvinyl chloride resin on the first adhesive layer; And
And a second adhesive layer on the second film layer.
KR1020140008862A 2014-01-24 2014-01-24 Protective film and adhesive tape using the same KR20140037160A (en)