KR20130008993A - Bio interior sheet and and manufacturing method thereof - Google Patents

Bio interior sheet and and manufacturing method thereof Download PDF

Info

Publication number
KR20130008993A
KR20130008993A KR1020110069747A KR20110069747A KR20130008993A KR 20130008993 A KR20130008993 A KR 20130008993A KR 1020110069747 A KR1020110069747 A KR 1020110069747A KR 20110069747 A KR20110069747 A KR 20110069747A KR 20130008993 A KR20130008993 A KR 20130008993A
Authority
KR
South Korea
Prior art keywords
resin
bio
interior sheet
weight
parts
Prior art date
Application number
KR1020110069747A
Other languages
Korean (ko)
Other versions
KR101387887B1 (en
Inventor
윤수형
신교훈
백대종
Original Assignee
(주)엘지하우시스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)엘지하우시스 filed Critical (주)엘지하우시스
Priority to KR1020110069747A priority Critical patent/KR101387887B1/en
Publication of KR20130008993A publication Critical patent/KR20130008993A/en
Application granted granted Critical
Publication of KR101387887B1 publication Critical patent/KR101387887B1/en

Abstract

PURPOSE: A bio resin-added car interior sheet capable of enhancing indoor air quality of vehicles and a manufacturing method thereof are provided to enhance sewing performance. CONSTITUTION: A bio resin-added car interior sheet comprises 5-100.0 parts by weight of bio resin obtained from starch extracted from one or more natural plants selected from corn, potatoes, ipomoea batatas, cane, bamboo or species which is similar to the same, 30-100.0 parts by weight of thermoplastic polyolefin resin or thermoplastic polyurethane resin, 5-40 parts by weight of compatibilizing agents, 0.1-1.5 parts by weight of lubricant, and 0.5-5 parts by weight of cross-linking agent.

Description

바이오수지가 첨가된 자동차용 인테리어시트 및 그 제조방법{Bio interior sheet and and manufacturing method thereof}Interior sheet for automobile with bio resin added and manufacturing method thereof

본 발명은, 바이오수지가 첨가된 자동차용 인테리어시트 및 그 제조방법에 관한 것으로서, 특히 다양한 기계적 특성이 요구되는 차량용 표피재의 상품 성능, 엠보싱 품질, 촉감등의 감성 품질은 물론 CO2 및 총휘발성유기화합물(TVOC)의 저감에 탁월한 성능을 발휘함으로써, 자동차의 인스투르먼트 패널(Instrument Panel), 하부패널(Lower Panel), 콘솔박스(Console Box), 시트커버(seat cover), 도어(door)등의 표피재 등의 제조에 적합한 바이오수지가 첨가된 자동차용 인테리어시트 및 그 제조방법에 관한 발명이다.The present invention relates to a car interior sheet to which bio-resin is added and to a method for manufacturing the same, in particular, the product quality, embossing quality, touch quality, etc. of CO2 and total volatile organic compounds of a vehicle skin material requiring various mechanical properties. Excellent performance in reducing TVOC, such as automotive instrument panel, lower panel, console box, seat cover, door, etc. The present invention relates to an automobile interior sheet to which a bio resin suitable for manufacturing such products is added, and a method of manufacturing the same.

일반적으로, 자동차의 인스투르먼트 패널(Instrument Panel), 하부패널(Lower Panel), 콘솔박스(Console Box), 시트커버(seat cover), 도어(door)등의 표피재의 스킨 중 시트커버를 제외한 제품은 PVC(폴리 염화비닐) 혹은 TPO(열가소성 폴리 올레핀)로 만들어진 시트를 진공성형 하거나, PVC, TPU(열가소성 폴리 우레탄) 파우더 슬러쉬 몰딩 공법으로 제조하는 것이 대부분 이었다. In general, products of skins of skin materials such as instrument panel, lower panel, console box, seat cover, and door of the vehicle except PVC are PVC Mostly, sheets made of (polyvinyl chloride) or TPO (thermoplastic polyolefin) were vacuum molded or manufactured by PVC or TPU (thermoplastic polyurethane) powder slush molding.

또한, 시트커버의 경우 PVC, PU(폴리 우레탄) 인조가죽 혹은 texture, 가죽등의 재료룰 사용하여 가공하는 것이 일반적이다. In addition, the seat cover is generally processed using a material such as PVC, PU (polyurethane) artificial leather or texture, leather.

반면, 바이오시트(Bio sheet)는 종래의 표면재 스킨과 대비할때, 요구물성, 작업성의 저하없이 식물에서 유래된 수지를 사용함으로써, 친환경적이고, 인체 무해한 내장용 자재의 제조에 기여한다. On the other hand, bio sheet (Bio sheet), as compared to the conventional surface material skin, by using a resin derived from plants without deterioration of the required properties, workability, contributes to the production of environmentally friendly, harmless interior materials.

현재, 바이오(bio) 수지는 그 특성상 연질화 시키기가 매우 어려운 것으로 알려져 있으며, 일광, 물에 의해 분해되는 성질로 인해, 주로 일회용품으로 많이 사용되고, 내구성이 요구되는 산업용 플라스틱으로는 주로 빛이 닿지 않는 곳(바닥 매트, 트렁크)에 많이 사용되고 있다. Currently, bio resins are known to be very hard to soften due to their characteristics, and due to their properties decomposed by sunlight and water, they are mainly used as disposable products, and are not mainly exposed to industrial plastics requiring durability. It is used a lot in place (floor mat, trunk).

따라서, 식물로부터 유래되는 바이오(bio) 수지와 내장 자재로서의 성능이 인정된 TPU. TPO 수지를 혼합한 후, 전자선 (Electro Beam, EB) 가교를 통해 그 물성을 배가시킴으로써, 물성의 저하 없이 CO2 발생 저감 및 공기질 향상을 구현시킬 수 있는 자동차용 내장 표피재로서의 자동차용 인테리어시트가 절실하게 요구되어 왔다.
Therefore, the TPU which recognized the performance as a bio resin derived from a plant and an interior material. After mixing TPO resins, the physical properties are doubled through cross-linking of an Electron Beam (EB), which reduces the need for CO2 emissions and improves air quality without deteriorating physical properties. Has been required.

본 발명은 상기한 바와 같은 종래 기술의 문제점을 감안하여 안출된 것으로, 본 발명의 목적은, 진공 성형이 가능하고, 재봉성능도 우수하여, 다양한 기계적 특성이 요구되는 차량용 표피재의 상품 성능, 엠보싱 품질, 촉감 등의 감성품질은 물론 CO2 및 총휘발성 유기화합물(TVOC)의 저감에 있어서 탁월한 성능을 발휘할 수 있는 바이오수지가 첨가된 자동차용 인테리어시트 및 그 제조방법을 제공하는데 있다.
The present invention has been made in view of the above-described problems of the prior art, and an object of the present invention is to enable vacuum molding, excellent sewing performance, and product performance and embossing quality of a vehicle skin material requiring various mechanical properties. To provide a car interior sheet with a bio resin that can exhibit excellent performance in the reduction of CO2 and total volatile organic compounds (TVOC), as well as sensation quality, such as touch, and the like, and a manufacturing method thereof.

상기한 바와 같은 목적을 달성하기 위한 본 발명의 특징에 따르면, 본 발명의 일실시예에 따른 바이오수지가 첨가된 자동차용 인테리어시트(100)는, 옥수수, 감자, 고구마, 사탕수수, 대나무, 그리고 이들과 유사한 품종 중의 어느 하나 이상의 천연식물에서 추출한 전분에서 얻어진 바이오수지 5 ~ 100중량부; 열가소성폴리올레핀(Thermoplas tic Polyole fin,TPO)수지 또는 열가소성폴리우레탄(Thermoplastic Polyureth ane,TPU)수지 30 ~ 100 중량부; 상용화제 5 ~ 40중량부; 활제 0.1 ~ 1.5중량부; 및 가교제 0.5 ~ 5중량부;로 이루어지는 것을 특징으로 한다.According to a feature of the present invention for achieving the object as described above, the interior sheet for automobile 100 is added bio-resin according to an embodiment of the present invention, corn, potatoes, sweet potatoes, sugar cane, bamboo, and 5 to 100 parts by weight of a bio resin obtained from starch extracted from any one or more natural plants of similar varieties; 30 to 100 parts by weight of a thermoplastic polyolefin (TPO) resin or a thermoplastic polyurethane (TPU) resin; 5 to 40 parts by weight of a compatibilizer; 0.1 to 1.5 parts by weight of lubricant; And 0.5 to 5 parts by weight of a crosslinking agent.

상기 바이오수지는, 폴리유산(Poly Lactic Acid,PLA), 폴리부틸렌 석시네이트(poly butylene succinate,PBS), 바이오폴리에틸렌(bio-Polyethy lene), 옥수수, 감자, 고구마, 사탕수수, 대나무, 그리고 이들과 유사한 품종 중의 어느 하나 이상의 천연식물에서 추출한 수지, 또는 폴리하이드록시알카노에이트(Poly-hydroxy alkanoate,PHA) 중에서 어느 하나 이상을 사용할 수 있다.The bio resin, poly lactic acid (PLA), poly butylene succinate (PBS), bio-poly (poly-polyethy lene), corn, potatoes, sweet potatoes, sugar cane, bamboo, and these It is possible to use any one or more of resins extracted from any one or more natural plants, or poly-hydroxyalkanoate (PHA).

상기 열가소성폴리올레핀(Thermoplastic Polyolefin,TPO)수지는, 에틸렌옥텐고무(ethylene octene rubber,EOR), 폴리프로필렌(polypropy lene,PP)-base의 열가소성가황물(Thermoplastic Vulcanizate,TPV) 또는 P-base의 열가소성가황물(Thermo plastic Vulcanizate,TPV) 중에서 어느 하나일 수 있다.The thermoplastic polyolefin (TPO) resin is ethylene octene rubber (EOR), polypropylene (polypropy lene, PP) -base thermoplastic vulcanizate (Thermoplastic Vulcanizate, TPV) or P-base thermoplastic vulcanization It may be any one of water (Thermo plastic Vulcanizate, TPV).

상기 열가소성폴리우레탄(Thermoplastic Polyurethane,TPU)수지는, 폴리올(polyol)이 폴리카보네이트(poly carbonate,PC)계, 에테르(ether)계 및 에스테르(ester)계 중에서 어느 하나일 수 있다.The thermoplastic polyurethane (TPU) resin, the polyol may be any one of polycarbonate (PC), ether (ether) and ester (ester).

상기 상용화제는, 글리시딜메타크릴레이트(glycidylmethacrylate,GMA), 말레산 무수물(maleic anhydride,MAH), 말레산(maleic acid,MA), EMMA 중에서 어느 하나일 수 있다.The compatibilizer may be any one of glycidyl methacrylate (GMA), maleic anhydride (MAH), maleic acid (MA), and EMMA.

상기 가교제는, 트리알릴 이소시누아누레이트(triallyl isocyanurate,TAIC), 트리메틸로프로판 트리아크릴레이트(trimethylolpropane triacrylate,TMPTA), 헥산디올 디아크릴레이트(hexandiol diacrylate,HDDA), 트리아릴시아누레이트(triallyl cynurate,TAC), 트리프로필렌 글리콜 디아크릴레이트(tripropylene glycol di acry late,TPGDA) 중에서 어느 하나일 수 있다.The crosslinking agent is triallyl isocyanurate (TAIC), trimethylolpropane triacrylate (TMPTA), hexanediol diacrylate (HDDA), triallyl cynurate , TAC), and tripropylene glycol diacrylate (TPGDA).

그리고, 본 발명의 일실시예에 따른 바이오수지가 첨가된 자동차용 인테리어시트의 제조방법은, 바이오수지, 열가소성폴리올레핀수지 또는 열가소성폴리우레탄수지, 상용화제, 활제, 가교제를 배합하는 단계(S10); 배합된 상기 소재를 펠릿(pellet)으로 만드는 단계(S20); 상기 펠릿을 압출기 또는 카렌더로써 시트(sheet)로 만드는 단계(S30); 및 상기 시트(sheet)타입의 소재를 경화시키는 단계(S40);를 포함하는 것을 특징으로 한다.In addition, the manufacturing method of the interior sheet for automobiles in which the bio resin is added according to an embodiment of the present invention includes: mixing a bio resin, a thermoplastic polyolefin resin or a thermoplastic polyurethane resin, a compatibilizer, a lubricant, and a crosslinking agent (S10); Making the blended material into pellets (S20); Making the pellets into sheets using an extruder or a calendar (S30); And hardening the sheet-type material (S40).

상기 배합하는 단계(S10)는, 가압 반죽기, 반바리(Bnbary) 혼합기, 또는 압출기로써 이루어질 수 있다.The compounding step (S10) may be made of a pressure kneader, a Bnbary mixer, or an extruder.

상기 경화시키는 단계(S40)는, 전자선(Electro Beam, EB)조사기로써 이루어질 수 있다.The curing step (S40) may be made of an electron beam (EB) irradiator.

상기 경화시키는 단계(S40)에서, 상기 전자선조사기에 의해 흡수된 방사선에너지의 양은 10~100kGy 의 범위에 속할 수 있다.In the curing step (S40), the amount of radiation energy absorbed by the electron beam irradiator may be in the range of 10 ~ 100kGy.

그리고, 본 발명의 일실시예에 따른 바이오수지가 첨가된 자동차용 인테리어시트의 제조방법은, 경화된 상기 소재의 표면에 아크릴(Acryl) 계열 또는 우레탄(Urethane) 계열의 수지를 코팅하는 단계(S50); 및 코팅된 상기 소재의 표면을 엠보싱처리하는 단계(S60);를 더 포함하는 것을 특징으로 한다.
In addition, the manufacturing method of a car interior sheet is added bio-resin according to an embodiment of the present invention, the step of coating an acrylic (acryl) -based or urethane (urethane) -based resin on the surface of the cured material (S50 ); And embossing the surface of the coated material (S60).

상기한 바와 같은 본 발명에 따르면, 기존의 사용물성 저하 없이, 진공 성형이 가능하고, 재봉성능도 우수할 뿐만 아니라, 다양한 기계적 특성을 갖는 차량용 표피재로서의 상품성능, 엠보싱품질, 촉감 등의 감성품질을 만족시킬 수 있는 바이오수지가 첨가된 자동차용 인테리어시트 및 그 제조방법을 제공할 수 있다.According to the present invention as described above, it is possible to vacuum forming, deterioration of the existing usable properties, excellent sewing performance, as well as sensitivity, such as product performance, embossing quality, touch, etc. as a vehicle skin material having various mechanical properties It is possible to provide a car interior sheet and a manufacturing method is added to the bio resin that can satisfy the.

그리고, 본 발명에 따르면, CO2배출 저감 및 총휘발성 유기화합물(TVOC)의 저감에 있어서 탁월한 성능을 발휘할 수 있음은 물론, 자동차 실내 공기질을 향상시킬 수 있고, 신체 접촉시 피부에 유해한 영향을 주지 않아, 알러지(Allergy) 유발도 방지할 수 있음으로써, 국내외적으로 이슈인 친환경 자동차(green car)에 기여할 수 있는 진정한 의미의 친환경적인 자동차에 소요되는 바이오수지가 첨가된 자동차용 인테리어시트 및 그 제조방법을 제공할 수 있다.In addition, according to the present invention, it is possible to exhibit excellent performance in reducing CO 2 emissions and reducing total volatile organic compounds (TVOC), as well as to improve the air quality in the automobile, and does not have a harmful effect on the skin when in contact with the body. In addition, it can prevent allergy, and it can also contribute to eco-friendly cars, which are issues at home and abroad. Can be provided.

또한, 본 발명에 따르면, 최고급 사양으로 얄려진 PU-spray공정을 대체할 수 있음으로써, 적은 비용으로도 다양한 성능을 향상시킬 수 있는 바이오수지가 첨가된 자동차용 인테리어시트 및 그 제조방법을 제공할 수 있다.
In addition, according to the present invention, it is possible to replace the PU-spray process made in the finest specifications, to provide a car interior sheet with a bio-resin that can improve a variety of performance at a low cost and a manufacturing method thereof Can be.

도 1은 본 발명의 일실시예에 따른 바이오수지가 첨가된 자동차용 인테리어시트의 제조과정을 나타낸 공정도이다.
도 2는 본 발명의 일실시예에 따른 바이오수지가 첨가된 자동차용 인테리어시트의 제조방법을 나타낸 흐름도이다.1 is a process chart showing a manufacturing process of a car interior sheet is added bio-resin according to an embodiment of the present invention.
2 is a flowchart illustrating a method of manufacturing an interior seat for a vehicle in which a bio resin is added according to an embodiment of the present invention.

기타 실시예들의 구체적인 사항들은 상세한 설명 및 도면들에 포함되어 있다.Specific details of other embodiments are included in the detailed description and the drawings.

본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다.Advantages and features of the present invention, and methods of achieving the same will become apparent with reference to the embodiments described below in detail in conjunction with the accompanying drawings.

그러나, 본 발명은 이하에서 개시되는 실시예들에 한정되는 것이 아니라, 서로 다른 다양한 형태로 구현될 수 있으며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하고, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다.However, the present invention is not limited to the embodiments disclosed below, but may be embodied in various different forms, and only the embodiments are intended to complete the disclosure of the present invention, and are commonly used in the art. It is provided to fully inform the scope of the invention to those skilled in the art, the invention being defined only by the scope of the claims.

명세서 전체에 걸쳐 동일 참조 부호는 동일 구성 요소를 지칭한다.Like reference numerals refer to like elements throughout.

이하, 본 발명의 실시예들에 의하여 바이오수지가 첨가된 자동차용 인테리어 시트 및 그 제조방법을 설명하기 위한 도면들을 참고하여, 본 발명에 대해 설명하도록 한다.Hereinafter, the present invention will be described with reference to the drawings for describing the interior sheet for a car and a method for manufacturing the same, in which a bio resin is added according to embodiments of the present invention.

본 발명의 일실시예에 따른 바이오수지가 첨가된 자동차용 인테리어시트(100)는, 옥수수, 감자, 고구마, 사탕수수, 대나무, 또는 이들과 유사한 품종 중의 어느 하나 이상의 천연식물에서 추출한 전분에서 얻어진 바이오수지 5 ~ 100중량부, 열가소성폴리올레핀(Thermoplas tic Polyolefin,TPO)수지 또는 열가소성폴리우레탄(Thermoplastic Polyureth ane,TPU)수지 30 ~ 100 중량부, 상용화제 5 ~ 40중량부, 활제 0.1 ~ 1.5중량부 및 가교제 0.5 ~ 5중량부로 이루어지는 것을 특징으로 한다.Car interior sheet 100 is a bio-resin is added according to an embodiment of the present invention, bio, obtained from starch extracted from any one or more natural plants of corn, potatoes, sweet potatoes, sugar cane, bamboo, or similar varieties 5 to 100 parts by weight of resin, 30 to 100 parts by weight of Thermoplastic Polyolefin (TPO) resin or Thermoplastic Polyureth ane (TPU) resin, 5 to 40 parts by weight of compatibilizer, 0.1 to 1.5 parts by weight of lubricant It consists of 0.5-5 weight part of crosslinking agents.

여기서, 상기 바이오수지는, 폴리유산(Poly Lactic Acid,PLA), 폴리부틸렌 석시네이트(poly butylene succinate,PBS), 바이오폴리에틸렌(bio-Polyethy lene), 옥수수, 감자, 고구마, 사탕수수, 대나무, 그리고 이들과 유사한 품종 중의 어느 하나 이상의 천연식물에서 추출한 수지, 또는 폴리하이드록시알카노에이트(Poly-hydroxy alkanoate,PHA) 중에서 어느 하나 이상을 사용할 수 있다.Here, the bio resin, poly lactic acid (PLA), polybutylene succinate (poly butylene succinate, PBS), bio-polyethylene (bio-Polyethy lene), corn, potatoes, sweet potatoes, sugar cane, bamboo, And any one or more of resins extracted from any one or more natural plants of similar varieties, or poly-hydroxy alkanoate (PHA) can be used.

그리고, 상기 열가소성폴리올레핀(Thermoplastic Polyolefin,TPO)수지는, 에틸렌옥텐고무(ethylene octene rubber,EOR), 폴리프로필렌(polypropy lene,PP)-base의 열가소성가황물(Thermoplastic Vulcanizate,TPV) 또는 P-base의 열가소성가황물(Thermo plastic Vulcanizate,TPV) 중에서 어느 하나일 수 있다.In addition, the thermoplastic polyolefin (TPO) resin is made of ethylene octene rubber (EOR), polypropylene (polypropy lene, PP) -base thermoplastic vulcanizate (Thermoplastic Vulcanizate, TPV) or P-base. The thermoplastic vulcanizate (Thermo plastic Vulcanizate, TPV) may be any one.

또한, 상기 열가소성폴리우레탄(Thermoplastic Polyurethane,TPU)수지는, 폴리올(polyol)이 폴리카보네이트(poly carbonate,PC)계, 에테르(ether)계 및 에스테르(ester)계 중에서 어느 하나일 수 있다.In addition, the thermoplastic polyurethane (TPU) resin, the polyol may be any of polycarbonate (PC), ether (ether) and ester (ester).

그리고, 상기 상용화제는, 글리시딜메타크릴레이트(glycidylmethacry late,GMA), 말레산 무수물(maleic anhydride,MAH), 말레산(maleic acid,MA), EMMA 중에서 어느 하나일 수 있다.The compatibilizer may be any one of glycidyl methacrylate (GMA), maleic anhydride (MAH), maleic acid (MA), and EMMA.

또한, 상기 가교제는, 트리알릴 이소시누아누레이트(triallyl isocyanu rate,TAIC), 트리메틸로프로판 트리아크릴레이트(trimethylolpropane triacry late,TMPTA), 헥산디올 디아크릴레이트(hexandiol diacrylate,HDDA), 트리아릴시아누레이트(triallylcynurate,TAC), 트리프로필렌 글리콜 디아크릴레이트(tripropy lene glycol di acry late,TPGDA) 중에서 어느 하나일 수 있다.In addition, the crosslinking agent, triallyl isocyanu rate (TAIC), trimethylolpropane triacry late (TMPTA), hexanediol diacrylate (hexandiol diacrylate, HDDA), triarylcyanu It may be any one of the rate (triallylcynurate, TAC), tripropylene glycol diacrylate (TPGDA).

그리고, 본 발명의 일실시예에 따른 바이오수지가 첨가된 자동차용 인테리어시트의 제조방법은, 바이오수지, 열가소성폴리올레핀수지 또는 열가소성폴리우레탄수지, 상용화제, 활제, 가교제를 배합하는 단계(S10); 배합된 상기 소재를 펠릿(pellet)으로 만드는 단계(S20); 상기 펠릿을 압출기 또는 카렌더로써 시트(sheet)로 만드는 단계(S30); 및 상기 시트(sheet)타입의 소재를 경화시키는 단계(S40);를 포함하는 것을 특징으로 한다.In addition, the manufacturing method of the interior sheet for automobiles in which the bio resin is added according to an embodiment of the present invention includes: mixing a bio resin, a thermoplastic polyolefin resin or a thermoplastic polyurethane resin, a compatibilizer, a lubricant, and a crosslinking agent (S10); Making the blended material into pellets (S20); Making the pellets into sheets using an extruder or a calendar (S30); And hardening the sheet-type material (S40).

여기서, 상기 배합하는 단계(S10)는, 가압 반죽기, 반바리(Bnbary) 혼합기, 또는 압출기로써 이루어지며, 상기 경화시키는 단계(S40)는, 전자선(Electro Beam, EB)조사기로써 이루어지고, 이때 상기 경화시키는 단계(S40)에 있어서, 상기 전자선조사기에 의해 흡수된 방사선에너지의 양은 10~100kGy 의 범위에 속하는 것을 특징으로 한다. Here, the blending step (S10) is made of a pressure kneader, a half-barrier (Bnbary) mixer, or an extruder, the curing step (S40) is made of an electron beam (Electro Beam, EB) irradiation, wherein the In the curing step (S40), the amount of radiation energy absorbed by the electron beam irradiator is characterized in that in the range of 10 ~ 100kGy.

상기와 같이, 전자선조사기(40)를 이용하여 경화시키는 단계(S40)에 따르면, 상기 전자선조사기(40)에서 방사되는 방사선이 상기 시트(sheet)타입의 소재에 조사(照射)됨으로써, 소재를 구성하는 각 고분자 하나하나의 가닥이 그물모양의 분자구조로 변하게 됨에 따라서, 인장강도 등과 같은 기계적 특성이 제고(提高)된다.As described above, according to the step (S40) of curing using the electron beam irradiator 40, the radiation emitted from the electron beam irradiator 40 is irradiated on the sheet (sheet) of the material (beam), As each strand of each polymer constituting the is changed into a net-like molecular structure, mechanical properties such as tensile strength is improved.

그리고, 본 발명의 일실시예에 따른 바이오수지가 첨가된 자동차용 인테리어시트의 제조방법은, 경화된 소재의 표면에 아크릴(Acryl) 계열 또는 우레탄(Urethane) 계열의 수지를 코팅하는 단계(S50); 및 코팅된 소재의 표면을 엠보싱처리하는 단계(S60);를 더 포함하는 것을 특징으로 한다.
In addition, the manufacturing method of the automotive interior sheet is added bio-resin according to an embodiment of the present invention, the step of coating an acrylic (acryl) -based or urethane (urethane) -based resin on the surface of the cured material (S50) ; And embossing the surface of the coated material (S60).

여기서, 상기 코팅하는 단계(S50)에 의하면, 표면 Scratch 및 UV로부터 소재의 보호, 그리고 광택효과를 제고할 수 있으며, 상기 엠보싱처리하는 단계(S60)에 의하면, 천연가죽 무늬나 기하학 무늬 등을 구현할 수 있다.Here, according to the coating step (S50), it is possible to enhance the protection of the material from the surface scratch and UV, and the gloss effect, and according to the embossing step (S60), to implement a natural leather pattern or geometric pattern Can be.

본 발명이 속하는 기술분야의 통상의 지식을 가진 자는 본 발명이 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다.It will be understood by those skilled in the art that the present invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof.

그러므로, 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며, 한정적이 아닌 것으로 이해해야만 한다.Therefore, it is to be understood that the embodiments described above are exemplary in all respects and not restrictive.

본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구의 범위에 의하여 나타내어지며, 특허청구의 범위의 의미 및 범위 그리고 그 균등 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.
The scope of the present invention is defined by the appended claims rather than the foregoing detailed description, and all changes or modifications derived from the meaning and scope of the claims and the equivalents thereof are included in the scope of the present invention Should be interpreted.

10 : 배합기 20 : 펠릿제조기
40 : 전자선조사기
100 : 바이오수지가 첨가된 자동차용 인테리어시트10: compounding machine 20: pellet maker
40: electron beam irradiator
100: Car interior sheet with bio resin

Claims (11)

옥수수, 감자, 고구마, 사탕수수, 대나무, 또는 이들과 유사한 품종 중의 어느 하나 이상의 천연식물에서 추출한 전분에서 얻어진 바이오수지 5 ~ 100중량부;
열가소성폴리올레핀(Thermoplastic Polyolefin,TPO)수지 또는 열가소성폴리우레탄(Thermoplastic Polyurethane,TPU)수지 30 ~ 100 중량부;
상용화제 5 ~ 40중량부;
활제 0.1 ~ 1.5중량부; 및
가교제 0.5 ~ 5중량부;로 이루어지는 것을 특징으로 하는 바이오수지가 첨가된 자동차용 인테리어시트.
5 to 100 parts by weight of bio resin obtained from starch extracted from any one or more natural plants of corn, potato, sweet potato, sugar cane, bamboo, or similar varieties;
30 to 100 parts by weight of a thermoplastic polyolefin (TPO) resin or a thermoplastic polyurethane (TPU) resin;
5 to 40 parts by weight of a compatibilizer;
0.1 to 1.5 parts by weight of lubricant; And
0.5 to 5 parts by weight of a crosslinking agent; Interior sheet for a car with a bio resin added.
제 1항에 있어서,
상기 바이오수지는, 폴리유산(Poly Lactic Acid,PLA), 폴리부틸렌 석시네이트(poly butylene succinate,PBS), 바이오폴리에틸렌(bio-Polyethy lene), 또는 옥수수, 감자, 고구마, 사탕수수, 대나무, 그리고 이들과 유사한 품종 중의 어느 하나 이상의 천연식물에서 추출한 수지, 또는 폴리하이드록시알카노에이트(Poly-hydroxy alkanoate,PHA) 중에서 어느 하나 이상을 사용하는 것을 특징으로 하는 바이오수지가 첨가된 자동차용 인테리어시트.
The method of claim 1,
The bio resin, poly Lactic Acid (PLA), poly butylene succinate (PBS), bio-Polyethy lene, or corn, potatoes, sweet potatoes, sugar cane, bamboo, and Interior sheet for automobiles with a bio resin added, characterized in that any one or more of resins extracted from any one or more natural plants, or poly-hydroxy alkanoate (PHA).
제 1항에 있어서,
상기 열가소성폴리올레핀(Thermoplastic Polyolefin,TPO)수지는, 에틸렌옥텐고무(ethylene octene rubber,EOR), 폴리프로필렌(polypropy lene,PP)-base의 열가소성가황물(Thermoplastic Vulcanizate,TPV) 또는 P-base의 열가소성가황물(Thermo plastic Vulcanizate,TPV) 중에서 어느 하나인 것을 특징으로 하는 바이오수지가 첨가된 자동차용 인테리어시트.
The method of claim 1,
The thermoplastic polyolefin (TPO) resin is ethylene octene rubber (EOR), polypropylene (polypropy lene, PP) -base thermoplastic vulcanizate (Thermoplastic Vulcanizate, TPV) or P-base thermoplastic vulcanization Car interior sheet with a bio-resin, characterized in that any one of water (Thermo plastic Vulcanizate, TPV).
제 1항에 있어서,
상기 열가소성폴리우레탄(Thermoplastic Polyurethane,TPU)수지는, 폴리올(polyol)이 폴리카보네이트(poly carbonate,PC)계, 에테르(ether)계 및 에스테르(ester)계 중에서 어느 하나인 것을 특징으로 하는 바이오수지가 첨가된 자동차용 인테리어시트.
The method of claim 1,
The thermoplastic polyurethane (TPU) resin, the polyol (polyol) is a bio resin, characterized in that any one of polycarbonate (PC), ether (ether) and ester (ester) type Car interior sheet added.
제 1항에 있어서,
상기 상용화제는, 글리시딜메타크릴레이트(glycidylmethacrylate,GMA), 말레산 무수물(maleic anhydride,MAH), 말레산(maleic acid,MA), EMMA 중에서 어느 하나인 것을 특징으로 하는 자동차용 바이오수지가 첨가된 인테리어시트.
The method of claim 1,
The compatibilizing agent is a car bioresin, characterized in that any one of glycidyl methacrylate (Glycidylmethacrylate, GMA), maleic anhydride (MAH), maleic acid (MA), EMMA Added interior sheet.
제 1항에 있어서,
상기 가교제는, 트리알릴 이소시누아누레이트(triallyl isocyanurate,TAIC), 트리메틸로프로판 트리아크릴레이트(trimethylolpropane triacrylate,TMPTA), 헥산디올 디아크릴레이트(hexandiol diacrylate,HDDA), 트리아릴시아누레이트(triallyl cynurate,TAC), 트리프로필렌 글리콜 디아크릴레이트(tripropylene glycol diacry late,TPGDA) 중에서 어느 하나인 것을 특징으로 하는 바이오수지가 첨가된 자동차용 인테리어시트.
The method of claim 1,
The crosslinking agent is triallyl isocyanurate (TAIC), trimethylolpropane triacrylate (TMPTA), hexanediol diacrylate (HDDA), triallyl cynurate (triallyl cynurate). , TAC), tripropylene glycol diacrylate (tripropylene glycol diacry late, TPGDA) is a car interior is added to the interior sheet for cars.
바이오수지, 열가소성폴리올레핀수지 또는 열가소성폴리우레탄수지, 상용화제, 활제, 가교제를 배합하는 단계(S10);
배합된 상기 소재를 펠릿(pellet)으로 만드는 단계(S20);
상기 펠릿을 압출기 또는 카렌더로써 시트(sheet)로 만드는 단계(S30); 및
상기 시트(sheet)타입의 소재를 경화시키는 단계(S40);
를 포함하는 것을 특징으로 하는 바이오수지가 첨가된 자동차용 인테리어시트의 제조방법.
Blending a bio resin, a thermoplastic polyolefin resin or a thermoplastic polyurethane resin, a compatibilizer, a lubricant, and a crosslinking agent (S10);
Making the blended material into pellets (S20);
Making the pellets into sheets using an extruder or a calendar (S30); And
Curing the sheet-type material (S40);
Method of manufacturing an interior sheet for a car with a bio resin added, comprising a.
제 7항에 있어서,
상기 배합하는 단계(S10)는, 가압 반죽기, 반바리(Bnbary) 혼합기, 또는 압출기로써 이루어지는 것을 특징으로 하는 바이오수지가 첨가된 자동차용 인테리어시트의 제조방법.
8. The method of claim 7,
The step of blending (S10), the manufacturing method of the interior sheet for a car with a bio-resin, characterized in that consisting of a press kneader, a Bnbary mixer, or an extruder.
제 7항에 있어서,
상기 경화시키는 단계(S40)는, 전자선(Electro Beam, EB)조사기로써 이루어지는 것을 특징으로 하는 바이오수지가 첨가된 자동차용 인테리어시트의 제조방법.
8. The method of claim 7,
The curing step (S40), the manufacturing method of the interior sheet for a car with a bio-resin, characterized in that made of an electron beam (EB) irradiator.
제 9항에 있어서,
상기 경화시키는 단계(S40)에서, 상기 전자선조사기에 의해 흡수된 방사선에너지의 양은 10~100kGy 의 범위에 속하는 것을 특징으로 하는 바이오수지가 첨가된 자동차용 인테리어시트의 제조방법.
The method of claim 9,
In the curing step (S40), the amount of radiation energy absorbed by the electron beam irradiator is a manufacturing method of the interior sheet for cars with bio resins, characterized in that in the range of 10 ~ 100kGy.
제 7항에 있어서,
경화된 상기 소재의 표면에 아크릴(Acryl) 계열 또는 우레탄(Urethane) 계열의 수지를 코팅하는 단계(S50); 및 코팅된 상기 소재의 표면을 엠보싱처리하는 단계(S60);를 더 포함하는 것을 특징으로 하는 바이오수지가 첨가된 자동차 인테리어시트의 제조방법.8. The method of claim 7,
Coating an acryl-based or urethane-based resin on the surface of the cured material (S50); And embossing the surface of the coated material (S60). 6.
KR1020110069747A 2011-07-14 2011-07-14 Bio interior sheet and and manufacturing method thereof KR101387887B1 (en)