KR20130006046A - Base materials coating non-conducting materials and coating method thereof - Google Patents

Base materials coating non-conducting materials and coating method thereof Download PDF

Info

Publication number
KR20130006046A
KR20130006046A KR1020110067851A KR20110067851A KR20130006046A KR 20130006046 A KR20130006046 A KR 20130006046A KR 1020110067851 A KR1020110067851 A KR 1020110067851A KR 20110067851 A KR20110067851 A KR 20110067851A KR 20130006046 A KR20130006046 A KR 20130006046A
Authority
KR
South Korea
Prior art keywords
base material
composition
material coated
film
conductive
Prior art date
Application number
KR1020110067851A
Other languages
Korean (ko)
Other versions
KR101884279B1 (en
Inventor
이광필
이호연
Original Assignee
삼성전자주식회사
(주)이오젠
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 삼성전자주식회사, (주)이오젠 filed Critical 삼성전자주식회사
Priority to KR1020110067851A priority Critical patent/KR101884279B1/en
Publication of KR20130006046A publication Critical patent/KR20130006046A/en
Application granted granted Critical
Publication of KR101884279B1 publication Critical patent/KR101884279B1/en

Abstract

PURPOSE: A based material coated with a non-conductive composition is provided to exhibit non-conductivity and metal texture, and to prevent the interference of radio property by not requiring silver which is a conventional conductive material. CONSTITUTION: A based material coated with a non-conductive composition material(10) comprises: a lower coating layer(a) formed by spraying a first curing paint on the surface of the base material; a pretreatment liquid sprayed on the lower coating film; a black hard coating layer(13) formed by simultaneously spraying reductant composition and black hard coating layer composition which contains a non-conductive silver oxide; cleaning water cleaning the black hardness layer; a middle coating layer(b) formed by spraying the color paint; and an upper coating layer(c) formed by spraying the second curing paint on the surface of the middle coating layer. [Reference numerals] (12) First curing paint; (13) Black hard coating layer; (14) Color paint; (15) Second curing paint; (a) Lower coating layer; (b) Middle coating layer; (c) Upper coating layer

Description

비전도성 조성물이 코팅된 모재 및 그의 코팅 방법{BASE MATERIALS COATING NON-CONDUCTING MATERIALS AND COATING METHOD THEREOF}Base material coated with non-conductive composition and coating method thereof BASE MATERIALS COATING NON-CONDUCTING MATERIALS AND COATING METHOD THEREOF

본 발명은 비전도성 조성물이 코팅된 모재 및 그의 코팅 방법에 관한 것으로서, 특히, 모재의 표면상에 비전도성 특성을 갖는 산화은이 함유된 흑경도막을 코팅한 비전도성 조성물이 코팅된 모재 및 그의 코팅 방법에 관한 것이다.
The present invention relates to a base material coated with a non-conductive composition and a coating method thereof, and in particular, a base material coated with a non-conductive composition coated with a black hard film containing silver oxide having non-conductive properties on the surface of the base material and a coating method thereof. It is about.

통상적으로, 플라스틱 사출 모재의 용도가 화장품, 휴대용 통신 장치, 전기/전자 제품, 윈도우, 자동차 및 전자장비등의 분야에서 그 사용량이 점차 증가되고 있다. Typically, the use of plastic injection base material is gradually increasing its use in the fields of cosmetics, portable communication devices, electrical / electronic products, windows, automobiles and electronic equipment.

상기 제품들은 표면이 유리나 금속에 비해 내구성 및 경도가 떨어져 상품가치에 손실을 가져오게 된다. 이러한 플라스틱 사출 모재의 표면 손상 보호 및 경도 광택 향상을 위해 여러 가지 도장기법이 개발되고 있다. 가장 범용적으로 사용되어지는 도장기법들로는 자연건조방법, 저온소부 방법, 자외선 경화방법등을 들 수 있다.These products have a lower surface durability and hardness than glass or metal, resulting in a loss of commodity value. Various coating techniques have been developed to protect the surface of the plastic injection base material and improve the hardness gloss. The most widely used coating techniques include natural drying methods, low temperature baking methods, UV curing methods, and the like.

최근 들어, 상기 사출 모재는 차별화된 디자인 외관 구현을 위한 신소재 및 표면 처리 기술을 적용하고 있다. 특히, 금속의 고급질감에 대한 소비자의 요구가 증가되고 있다.Recently, the injection base material is applying a new material and surface treatment technology for implementing a differentiated design appearance. In particular, consumer demand for high quality metals is increasing.

따라서, 상기 사출 모재의 내, 외장 기구물에는 금속성 색상 및 금속성 질감을 구현하고 있다. 이러한 금속 질감의 표면 처리 방법으로는, 통상적인 도금 및 진공 증착 방법 또는 금속 소재를 이용한 박막 코팅 및 실링 방법등이 사용된다.Therefore, the inner and outer fixtures of the injection base material implement a metallic color and metallic texture. As the surface treatment method of such a metal texture, a conventional plating and vacuum deposition method or a thin film coating and sealing method using a metal material is used.

그러나, 종래의 도금 및 진공 증착 방법은 사출 모재에 금속 질감을 위해 전도성 물질인 질산(HNO₃), 알루미늄(Al) 및 은(Ag)등을 사용하여 은색을 바탕으로 후공정을 진행하기 때문에 전기의 전도성이 높은 제품을 생산하였고, 이로인해, 전도성을 갖는 제품이 휴대용 통신 장치일 경우, 은의 전파 특성을 방해로 인해 휴대용 통신 장치의 안테나 수신율이 감소되어 제품의 기능을 저하시키고, 또한, 전도성을 갖는 상기 휴대용 통신 장치 및 상기 전기/전자 제품들은 회로 파손 및 제품의 오작동이 발생되는 단점이 있었다. However, the conventional plating and vacuum deposition method uses an electrically conductive material such as nitric acid (HNO₃), aluminum (Al) and silver (Ag) for the metallic texture of the injection base material, so that the post-process is performed based on the silver color. When the product having high conductivity was produced, and thus the product having the conductivity is a portable communication device, the antenna reception rate of the portable communication device is reduced due to the interference of silver propagation characteristics, thereby degrading the function of the product and also having the conductivity. The portable communication device and the electrical / electronic products have disadvantages in that circuit breakage and product malfunction occur.

또한, 종래의 도금 방법은 도금 공정시 강산 및 강염기성 용액을 사용하기 때문에 폐수처리의 비용상승, 환경 오염 발생 및 인체에 치명적인 영향을 유발시키는 단점이 있었다.In addition, the conventional plating method uses a strong acid and a strong base solution during the plating process has the disadvantage of causing a cost increase of wastewater treatment, environmental pollution and a fatal effect on the human body.

따라서, 제품에 비전도성 및 금속 질감을 구현하기 위해 비전도성 물질을 함유한 조성물의 코팅이 필요한 실정이다.
Therefore, there is a need for a coating of a composition containing a nonconductive material in order to realize a nonconductive and metallic texture in a product.

본 발명은 모재에 비전도성 특성을 갖는 산화은이 함유된 흑경도막을 코팅함으로써, 제품의 비전도성 및 금속 질감 구현이 가능할 뿐만 아니라, 제품의 흑경 도금 효과도 구현가능하도록 한 비전도성 조성물이 코팅된 모재 및 그의 코팅 방법을 제공하는데 있다.The present invention is a coating of a non-conductive composition which enables not only the non-conductive and metallic texture of the product, but also the black plating effect of the product by coating a black light coating film containing silver oxide having non-conductive properties on the base material. And a coating method thereof.

또한, 본 발명은 모재에 비전도성 특성을 갖는 산화은이 함유된 흑경도막을 코팅함으로써, 기존의 전도성 물질인 은(Ag)이 필요없어 은으로 인한 제품의 전파 특성 방해를 방지하여 제품의 기능을 향상시킬뿐만 아니라, 회로의 파손 및 오작동을 방지할 수 있도록 한 비전도성 조성물이 코팅된 모재 및 그의 코팅 방법을 제공하는데 있다.In addition, the present invention by coating a black light film containing a silver oxide having a non-conductive property on the base material, there is no need for a conventional conductive material silver (Ag) to prevent the interference of the propagation characteristics of the product due to silver to improve the function of the product In addition, the present invention provides a base material coated with a non-conductive composition and a coating method thereof, which can prevent breakage and malfunction of a circuit.

또한, 본 발명은 모재에 비전도성 특성을 갖는 산화은이 함유된 흑경도막을 코팅함으로써, 기존의 도금시 사용되던 강산 및 강염기성액이 필요없어 폐수처리비용을 절감하고, 이로인해 제품의 제조원가를 절감하며, 또한, 환경 오염 및 인체에 치명적인 영향 유발을 방지할 수 있도록 한 비전도성 조성물이 코팅된 모재 및 그의 코팅 방법을 제공하는데 있다.
In addition, the present invention by coating a black hard coating film containing a silver oxide having a non-conductive property in the base material, there is no need for strong acid and strong base liquid used in the existing plating to reduce the waste water treatment cost, thereby reducing the manufacturing cost of the product In addition, the present invention provides a base material coated with a non-conductive composition and a coating method thereof, which can prevent environmental pollution and harmful effects on the human body.

본 발명은, 비전도성 조성물이 코팅된 모재에 있어서,The present invention is a base material coated with a non-conductive composition,

상기 모재의 표면에 제 1 경화 도료를 분사하여 형성되는 하도막;An undercoat formed by spraying a first cured paint on the surface of the base material;

상기 하도막에 분사되는 전처리액;A pretreatment liquid sprayed on the undercoat;

상기 하도막의 표면에 비전도성 산화은이 함유된 흑경막 조성물과 환원제 조성물을 동시 분사하여 형성되는 흑경도막;A black hard coating film formed by simultaneously spraying a black film composition containing a non-conductive silver oxide and a reducing agent composition on the surface of the undercoat;

상기 흑경도막을 세척하는 정제수;Purified water for washing the black hard film;

칼라 도료를 분사하여 형성하는 중도막; 및An intermediate coating formed by spraying a color paint; And

상기 중도막의 표면에 제 2 경화 도료를 분사하여 형성하는 상도막을 포함함을 특징으로 한다.
And an upper coating film formed by spraying a second cured paint on the surface of the intermediate coating film.

본 발명의 코팅 방법은, 비전도성 조성물이 코팅된 모재의 코팅 방법에 있어서,The coating method of the present invention, in the coating method of the base material coated with a non-conductive composition,

상기 모재의 표면에 제 1 경화 도료를 분사하여 하도막을 형성하는 제 1 단계;A first step of forming a undercoat by spraying a first cured paint on the surface of the base material;

상기 제 1 단계로부터 상기 하도막에 전처리액을 분사하는 제 2 단계;A second step of spraying a pretreatment liquid onto the undercoat from the first step;

상기 제 2 단계로부터 상기 하도막의 표면에 비전도성 산화은이 함유된 흑경막 조성물과 환원제 조성물을 동시 분사하여 흑경도막을 형성하는 제 3 단계;A third step of simultaneously forming a black hard coat film by simultaneously spraying a black film composition and a reducing agent composition containing non-conductive silver oxide on the surface of the undercoat from the second step;

상기 제 3 단계로부터 상기 흑경도막을 세척하는 제 4 단계;A fourth step of washing the black hard coating film from the third step;

상기 제 4 단계로부터 칼라 도료를 분사하여 중도막을 형성하는 제 5 단계; 및A fifth step of forming a middle coating film by spraying the color paint from the fourth step; And

상기 제 5 단계로부터 상기 중도막의 표면에 제 2 경화 도료를 분사하여 상도막을 형성하는 제 6 단계를 포함함을 특징으로 한다.
And a sixth step of forming a top coat by spraying a second cured paint on the surface of the middle coat from the fifth step.

상술한 바와 같이 본 발명에 의한 비전도성 조성물이 코팅된 모재 및 그의 코팅 방법에 의하면, As described above, according to the base material coated with the non-conductive composition according to the present invention and a coating method thereof,

모재에 비전도성 특성을 갖는 산화은이 함유된 흑경도막을 코팅하여 제품의 비전도성 및 금속 질감 구현이 가능할 뿐만 아니라, 제품의 흑경 도금 효과도 구현가능하고, 또한, 기존의 전도성 물질인 은(Ag)이 필요없으므로 은으로 인한 제품의 전파 특성 방해를 방지하여 제품의 기능을 향상시킬뿐만 아니라, 회로의 파손 및 오작동을 방지할 수 있으며, 또한, 기존의 도금시 사용되던 강산 및 강염기성액이 필요없어 폐수처리비용을 절감하고, 이로인해 제품의 제조원가를 절감하며, 또한, 환경 오염 및 인체에 치명적인 영향 유발을 방지할 수 있는 효과가 있다.
It is possible not only to realize the non-conductive and metal texture of the product by coating the black hard coating film containing silver oxide having non-conductive property on the base material, but also to realize the black plating effect of the product, and also to the existing conductive material silver (Ag) This prevents the product from interfering with the propagation characteristics of the product due to silver, thereby improving the product's function, preventing damage and malfunction of circuits, and eliminating the need for strong acid and strong base liquids. It reduces the processing cost, thereby reducing the manufacturing cost of the product, and also has the effect of preventing environmental pollution and harmful effects on the human body.

도 1은 본 발명의 바람직한 일 실시예에 따른 비전도성 조성물이 코팅된 모재의 구성을 나타낸 도면.
도 2는 본 발명의 바람직한 일 실시예에 따른 비전도성 조성물이 코팅된 모재의 코팅 방법을 나타낸 흐름도.1 is a view showing the configuration of a base material coated with a non-conductive composition according to an embodiment of the present invention.
Figure 2 is a flow chart showing a coating method of the base material coated with a non-conductive composition according to an embodiment of the present invention.

이하에서는 첨부도면을 참조하여 본 발명의 가장 바람직한 실시예들을 상세히 설명하기로 한다. 이에 앞서 본 명세서에 기재된 실시예와 도면에 도시된 구성은 본 발명의 가장 바람직한 실시예들에 불과할 뿐이고, 본 출원시점에 있어서 이들을 대체할 수 있는 다양한 변형예들이 있음을 이해하여야 한다.Hereinafter, with reference to the accompanying drawings will be described in detail the most preferred embodiments of the present invention. In the foregoing description, only the most preferred embodiments of the present invention and the configurations shown in the drawings are understood, and it should be understood that there are various modifications that can replace them at the time of the present application.

도 1에 도시된 바와 같이, 비전도성 조성물이 코팅된 모재(11)는 하도막(a), 전처리액(미도시 됨)과, 흑경도막(13)과, 정제수(미도시 됨)와, 중도막(b) 및 상도막(c)으로 구성되어 있고, 상기 하도막(a)은 후술하는 칼라 도료(14) 및 제 2 경화 도료(14)의 부착력 및 평탄도를 확보하기 위해 상기 모재(11)의 표면에 후술하는 제 1 경화 도료(12)를 분사하도록 되어 있으며, 상기 전처리액은 상기 하도막(a)에 유분성을 수용성으로 변형하여 전처리하도록 상기 하도막(a)에 분사되고, 상기 흑경도막(13)은 상기 모재(11)의 비전도성 및 금속감을 구현하기 위해 상기 하도막(a)의 표면에 비전도성 특성을 갖는 산화은이 함유된 흑경막 조성물과 환원제 조성물을 동시에 분사하도록 되어 있으며, 상기 정제수는 상기 흑경도막(13)을 세척하도록 되어 있고, 상기 중도막(b)은 상기 모재(11)의 칼라를 구현하기 위해 상기 흑경도막(13)의 표면에 칼라 도료(14)를 분사하도록 되어 있으며, 상기 상도막(c)은 상기 하도막(a), 상기 흑경도막(13), 상기 칼라 도료(14) 및 상기 중도막(b)을 보호하기 위해 상기 중도막(b)의 표면에 후술하는 제 2 경화 도료(15)를 분사하도록 되어 있다.As shown in FIG. 1, the base material 11 coated with the non-conductive composition includes a undercoat (a), a pretreatment liquid (not shown), a black hard film (13), purified water (not shown), It consists of the film | membrane (b) and the top coat film (c), The said undercoat film (a) is the said base material 11 in order to ensure the adhesive force and flatness of the color paint 14 and the 2nd hardening paint 14 which are mentioned later. The first cured paint 12, which will be described later, is sprayed on the surface of the c), and the pretreatment liquid is sprayed onto the undercoating film a so as to pre-treat the water-soluble property of the undercoating film a. The black hard film 13 is sprayed simultaneously with the black film composition and the reducing agent composition containing silver oxide having non-conductive properties on the surface of the undercoat (a) to realize the non-conductive and metallic feeling of the base material (11) , The purified water is to wash the black hard film 13, the middle film (b) is In order to implement the color of the base material 11, the color coating 14 is sprayed on the surface of the black hard coating film 13, and the top coat c is the lower coating film a and the black hard coating film 13 In order to protect the said collar paint 14 and the said intermediate film b, the 2nd hardening paint 15 mentioned later is sprayed on the surface of the said intermediate film b.

도 1에 도시된 바와 같이, 상기 모재(11)는 사출 성형물과, 금속 제품과, 목재 제품과, 유리 제품 및 세라믹 제품들 중 어느 하나로 이루어져 있고, 상기 모재(11)는 사출 성형물과, 금속 제품과, 목재 제품과, 유리 제품 및 세라믹 제품들 이외에 다른 제품도 가능하다.As shown in FIG. 1, the base material 11 is made of any one of an injection molding, a metal product, a wood product, a glass product, and a ceramic product, and the base material 11 is an injection molding, and a metal product. In addition to wood, wood, glass and ceramic products, other products are also possible.

상기 제 1 경화 도료(12)는 이산화규소(SiO2)와, 우레탄 및 유브이(UV) 경화형 도료들 중 어느 하나로 이루어져 있고, 상기 제 1 경화 도료(12)는 이산화규소(SiO2)와, 우레탄 및 유브이(UV) 경화형 도료들 이외에 다른 도료도 가능하다. 상기 제 2 경화 도료(15)는 이산화규소(SiO2)와, 우레탄 및 유브이(UV) 경화형 도료들 중 어느 하나로 이루어져 있다. 상기 제 2 경화 도료(15)는 이산화규소(SiO2)와, 우레탄 및 유브이(UV) 경화형 도료들 이외에 다른 도료도 가능하다.The first cured paint 12 is made of any one of silicon dioxide (SiO 2), urethane and UV (UV) curable paints, and the first cured paint 12 is silicon dioxide (SiO 2), urethane and UV In addition to (UV) curable paints, other paints are possible. The second cured paint 15 is made of any one of silicon dioxide (SiO 2), and urethane and UV (UV) curable paints. The second cured paint 15 may be other paint in addition to silicon dioxide (SiO 2) and urethane and UV (UV) curable paints.

상기 이산화규소의 조성물은 실리카졸 5~40g과, 오르가노졸 5~20g과, 정제수 5~30g 및 솔벤트등으로 이루어져 있다.The composition of the silicon dioxide is composed of silica sol 5 ~ 40g, organosol 5 ~ 20g, purified water 5 ~ 30g, solvent and the like.

상기 전처리액의 조성물은 소듐염과, 톨류엔과, 염화주석 및 벤조아졸로 구성된 제 1 군과, 계면활성제 및 암모늄염으로 구성된 제 2 군을 혼합하여 이루어져 있고, 상기 제 1 군의 중량은 5~30g으로 이루어져 있으며, 상기 제 2 군의 중량은 5~30g으로 이루어져 있다.The composition of the pretreatment solution is a mixture of a first group consisting of sodium salt, toluene, tin chloride and benzoazole, and a second group consisting of surfactant and ammonium salt, the weight of the first group is 5 ~ It consists of 30g, the weight of the second group consists of 5 ~ 30g.

상기 흑경막 조성물은 산화은 5~50g과, 암모니아수 10~50g과, 티타눔 0.01~0.2g과, 실란 0.01~0.2g 및 비닐실란 0.01~0.2g으로 이루어져 있다.The black film composition is composed of 5-50 g of silver oxide, 10-50 g of ammonia water, 0.01-0.2 g of titanum, 0.01-0.2 g of silane, and 0.01-0.2 g of vinylsilane.

상기 환원제 조성물은 펙틴과, 프로필렌디아임과, 메틸알콜과, 에틸알콜과, 포름산과, 메틸아민 및 구아검등으로 이루어져 있다The reducing agent composition comprises pectin, propylene dime, methyl alcohol, ethyl alcohol, formic acid, methylamine, guar gum, and the like.

상기 하도막(a)의 두께는 5~30㎛로 이루어져 있고, 상기 하도막(a)의 두께는 5㎛ 이하 또는 30㎛이상도 가능하다.The thickness of the undercoat (a) is made of 5 ~ 30㎛, the thickness of the undercoat (a) may be 5㎛ or less or 30㎛ or more.

상기 상도막(a)의 두께는 5~30㎛로 이루어져 있고, 상기 상도막(a)의 두께는 5㎛ 이하 또는 30㎛이상도 가능하다.The thickness of the top coat (a) is made of 5 ~ 30㎛, the thickness of the top coat (a) may be 5㎛ or less or 30㎛ or more.

상기 흑경도막(13)의 두께는 50~200nm로 이루어져 있고, 상기 흑경도막(13)의 두께는 50nm이하 또는 200nm이상도 가능하다. The thickness of the black light film 13 is made of 50 ~ 200nm, the thickness of the black light film 13 may be 50nm or less or 200nm or more.

상기 칼라 도료(14)의 두께는 3~10㎛로 이루어져 있고, 상기 칼라 도료(14)의 두께는 3㎛이하 또는 10㎛이상도 가능하다.
The thickness of the color paint 14 is made of 3 ~ 10㎛, the thickness of the color paint 14 may be 3㎛ or less or 10㎛ or more.

상기와 같은 구성을 가지는 본 발명의 바람직한 일 실시 예에 의한 비전도성 조성물이 코팅된 모재의 동작과정을 첨부된 도 1을 참조하여 더욱 상세히 설명하면 다음과 같다.Referring to Figure 1 attached to the operation of the non-conductive composition coated base material according to an embodiment of the present invention having the configuration as described above in more detail as follows.

도 1에 도시된 바와 같이, 비전도성 조성물이 코팅된 모재(10)는, 먼저, 사출 성형(미도시 됨)에 의해 사출 모재(11)를 제조하고, 상기 사출 모재(11)의 표면에 제 1 경화 도료(12)를 분사하여 하도막(a)을 형성한다.As shown in FIG. 1, the base material 10 coated with the non-conductive composition may first prepare an injection base material 11 by injection molding (not shown), and may be formed on the surface of the injection base material 11. 1 The hardened paint 12 is sprayed to form the undercoat film a.

상기 제 1 경화 도료(12)는 이산화규소(SiO2)와, 우레탄 및 유브이(UV) 경화형 도료들 중 어느 하나로 이루어지고, 상기 이산화규소의 조성물은 실리카졸 5~40g과, 오르가노졸 5~20g과, 정제수 5~30g 및 솔벤트등으로 이루어진다.The first cured paint 12 is made of any one of silicon dioxide (SiO2), urethane and UV (UV) curable paints, the composition of the silicon dioxide is 5 to 40g silica sol, 5 to 20g organosol and , Consists of purified water 5 ~ 30g and solvents.

여기서, 상기 하도막(a)의 두께는 5~30㎛로 이루어진다. Here, the thickness of the undercoat (a) is made of 5 ~ 30㎛.

이 상태에서, 상기 하도막(a)에 유분성을 수용성으로 변형하는 전처리액(미도시 됨)을 분사한다. In this state, the pretreatment liquid (not shown) which inject | pours the oil property into water solubility is sprayed on the undercoat film a.

여기서, 상기 전처리액(미도시 됨)의 조성물은 소듐염과, 톨류엔과, 염화주석 및 벤조아졸로 구성된 제 1 군과, 계면활성제 및 암모늄염으로 구성된 제 2 군을 혼합하여 이루어지고, 상기 제 1 군의 중량은 5~30g으로 이루어지며, 상기 제 2 군의 중량은 5~30g으로 이루어진다.Here, the composition of the pretreatment liquid (not shown) is made by mixing a first group composed of sodium salt, toluene, tin chloride and benzoazole, and a second group composed of surfactant and ammonium salt, The weight of the first group is made of 5 ~ 30g, the weight of the second group is made of 5 ~ 30g.

전처리된 상기 하도막(a)의 표면에 비전도성 특성을 갖는 산화은이 함유된 흑경막 조성물과 환원제 조성물을 동시 분사하여 흑경도막(13)을 형성한다.The black hard coating film 13 is formed by simultaneously spraying the black film composition and the reducing agent composition containing silver oxide having non-conductive properties on the surface of the precoated film (a).

여기서, 상기 흑경막 조성물은 산화은 5~50g과, 암모니아수 10~50g과, 티타눔 0.01~0.2g과, 실란 0.01~0.2g 및 비닐실란 0.01~0.2g으로 이루어지고, 상기 환원제 조성물은 펙틴과, 프로필렌디아임과, 메틸알콜과, 에틸알콜과, 포름산과, 메틸아민 및 구아검등으로 이루어진다.Here, the black film composition is composed of 5-50 g of silver oxide, 10-50 g of ammonia water, 0.01-0.2 g of titanum, 0.01-0.2 g of silane, and 0.01-0.2 g of vinylsilane, and the reducing agent composition includes pectin, Propylene dimethyl, methyl alcohol, ethyl alcohol, formic acid, methylamine, guar gum, and the like.

여기서, 상기 흑경도막(13)의 두께는 50~200nm로 이루어진다.Here, the thickness of the black light film 13 is made of 50 ~ 200nm.

이 상태에서, 도 1에 도시된 바와 같이, 상기 흑경도막(13)은 정제수(미도시 됨)를 이용하여 세척하고, 칼라 도료(14)를 분사하여 중도막(b)을 형성한다. 여기서, 상기 칼라 도료(14)의 두께는 3~10㎛로 이루어진다.In this state, as shown in FIG. 1, the black light coating film 13 is washed with purified water (not shown), and the color coating 14 is sprayed to form the middle coating film b. Here, the thickness of the color paint 14 is made of 3 ~ 10㎛.

도 1에 도시된 바와 같이, 상기 중도막(b)의 표면에 제 2 경화 도료(15)를 분사하여 상도막(c)을 형성한다.As shown in FIG. 1, a second cured paint 15 is sprayed on the surface of the middle coating film b to form a top coating film c.

여기서, 상기 제 2 경화 도료(15)는 이산화규소(SiO2)과, 우레탄 및 유브이(UV) 경화형 도료들 중 어느 하나로 이루어지고, 상기 이산화규소의 조성물은 실리카졸 5~40g과, 오르가노졸 5~20g과, 정제수 5~30g 및 솔벤트등으로 이루어진다.Here, the second cured paint 15 is made of any one of silicon dioxide (SiO 2), urethane and UV (UV) curable paints, the composition of the silicon dioxide is silica sol 5 ~ 40g, organosol 5 ~ 20 g, purified water 5-30 g, solvent and the like.

여기서, 도 1에 도시된 바와 같이, 상기 상도막(c)의 두께는 5~30㎛로 이루어진다.Here, as shown in Figure 1, the thickness of the top coat (c) is made of 5 ~ 30㎛.

여기서, 상기 모재(10)는 휴대용 통신 장치(미도시 됨)로 이루어지고, 상기 흑경도막(13)은 비전도성 및 금속질감을 갖도록 상기 휴대용 통신 장치의 외관 테두리 또는 상기 휴대용 통신 장치에 구비된 키부의 외관 테두리에 형성된다.
Here, the base material 10 is made of a portable communication device (not shown), the black light film 13 is a key portion provided in the outer edge of the portable communication device or the portable communication device to have a non-conductive and metallic texture Is formed on the exterior border.

상기와 같은 구성을 가지는 본 발명의 바람직한 일 실시 예에 의한 비전도성 조성물이 코팅된 모재의 코팅 방법의 동작과정을 첨부된 도 2를 참조하여 더욱 상세히 설명하면 다음과 같다.The operation of the coating method of the base material coated with the non-conductive composition according to the preferred embodiment of the present invention having the configuration as described above will be described in more detail with reference to FIG. 2.

도 2에 도시된 바와 같이, 비전도성 조성물이 코팅된 모재(10)의 코팅 방법은, 먼저, 사출 성형(미도시 됨)에 의해 사출 모재(11)를 제조하고, 상기 사출 모재(11)의 표면에 제 1 경화 도료(12)를 분사하여 하도막(a)을 형성한다.(S1)As shown in FIG. 2, in the coating method of the base material 10 coated with the non-conductive composition, first, an injection base material 11 is manufactured by injection molding (not shown), and the injection base material 11 is formed. The first hardened paint 12 is sprayed on the surface to form the undercoat film a. (S1)

상기 제 1 경화 도료(12)는 이산화규소(SiO2)와, 우레탄 및 유브이(UV) 경화형 도료들 중 어느 하나로 이루어진다.The first cured paint 12 is made of any one of silicon dioxide (SiO 2) and urethane and UV (UV) curable paints.

여기서, 상기 이산화규소의 조성물은 실리카졸 5~40g과, 오르가노졸 5~20g과, 정제수 5~30g 및 솔벤트등으로 이루어진다.Here, the composition of the silicon dioxide is composed of silica sol 5-40g, organosol 5-20g, purified water 5-30g, solvent and the like.

여기서, 상기 하도막(a)의 두께는 5~30㎛로 이루어진다. Here, the thickness of the undercoat (a) is made of 5 ~ 30㎛.

상기 S1으로부터 상기 하도막(a)에 유분성을 수용성으로 변형하는 전처리액(미도시 됨)을 분사한다.(S2)From S1, a pretreatment liquid (not shown) is sprayed onto the undercoat a to change oiliness into water-soluble (S2).

여기서, 상기 전처리액(미도시 됨)의 조성물은 소듐염과, 톨류엔과, 염화주석 및 벤조아졸로 구성된 제 1 군과, 계면활성제 및 암모늄염으로 구성된 제 2 군을 혼합하여 이루어지고, 상기 제 1 군의 중량은 5~30g으로 이루어지며, 상기 제 2 군의 중량은 5~30g으로 이루어진다.Here, the composition of the pretreatment liquid (not shown) is made by mixing a first group composed of sodium salt, toluene, tin chloride and benzoazole, and a second group composed of surfactant and ammonium salt, The weight of the first group is made of 5 ~ 30g, the weight of the second group is made of 5 ~ 30g.

상기 S2로부터 상기 하도막(a)의 표면에 비전도성 특성을 갖는 산화은이 함유된 흑경막 조성물과 환원제 조성물을 동시 분사하여 흑경도막(13)을 형성한다.(S3)From the S2, the black film composition containing silver oxide having a non-conductive property and the reducing agent composition are simultaneously sprayed on the surface of the undercoat film (a) to form a black light coating film (13).

여기서, 상기 흑경막 조성물은 산화은 5~50g과, 암모니아수 10~50g과, 티타눔 0.01~0.2g과, 실란 0.01~0.2g 및 비닐실란 0.01~0.2g으로 이루어지고, 상기 환원제 조성물은 펙틴과, 프로필렌디아임과, 메틸알콜과, 에틸알콜과, 포름산과, 메틸아민 및 구아검등으로 이루어진다.Here, the black film composition is composed of 5-50 g of silver oxide, 10-50 g of ammonia water, 0.01-0.2 g of titanum, 0.01-0.2 g of silane, and 0.01-0.2 g of vinylsilane, and the reducing agent composition includes pectin, Propylene dimethyl, methyl alcohol, ethyl alcohol, formic acid, methylamine, guar gum, and the like.

여기서, 상기 흑경도막(13)의 두께는 50~200nm로 이루어진다.Here, the thickness of the black light film 13 is made of 50 ~ 200nm.

상기 S3으로부터 상기 흑경도막(13)은 정제수(미도시 됨)를 이용하여 세척한다.(S4)From the S3, the black hard film 13 is washed with purified water (not shown). (S4)

상기 S4로부터 칼라 도료(14)를 분사하여 중도막(b)을 형성한다.(S5)The color coating 14 is sprayed from S4 to form a middle coating film b.

여기서, 상기 칼라 도료(14)의 두께는 3~10㎛로 이루어진다.Here, the thickness of the color paint 14 is made of 3 ~ 10㎛.

상기 S5로부터 상기 중도막(b)의 표면에 제 2 경화 도료(15)를 분사하여 상도막(c)을 형성한다.(S6)The second curing paint 15 is sprayed onto the surface of the intermediate coating film b from S5 to form the top coating film c.

여기서, 상기 제 2 경화 도료(15)는 이산화규소(SiO2), 우레탄 및 유브이(UV) 경화형 도료들 중 어느 하나로 이루어지고, 상기 이산화규소의 조성물은 실리카졸 5~40g과 오르가노졸 5~20g과, 정제수 5~30g과 솔벤트등으로 이루어진다.Here, the second cured paint 15 is made of any one of silicon dioxide (SiO 2), urethane and UV (UV) curable paints, the composition of the silicon dioxide is 5 to 40g silica sol and 5 to 20g organosol and , 5-30g of purified water and solvent.

여기서, 상기 상도막(c)의 두께는 5~30㎛로 이루어진다.Here, the thickness of the upper coating film (c) is made of 5 ~ 30㎛.

상기와 같이, 사출 모재(11)에 비전도성 특성을 갖는 산화은이 함유된 흑경도막(13)을 코팅함으로써, 제품의 비전도성 및 금속 질감 구현이 가능할 뿐만 아니라, 제품의 흑경 도금 효과도 구현가능하고, 기존의 전도성 물질인 은(Ag)이 필요없어 은으로 인한 제품의 전파 특성 방해를 방지하여 제품의 기능을 향상시킬뿐만 아니라, 회로의 파손 및 오작동을 방지할 수 있고, 또한, 기존의 도금시 사용되던 강산 및 강염기성액이 필요없어 폐수처리비용을 절감하고, 이로인해 제품의 제조원가를 절감하며, 또한, 환경 오염 및 인체에 치명적인 영향 유발을 방지할 수 있다.As described above, by coating the black hard coating film 13 containing the silver oxide having non-conductive properties on the injection base material 11, it is possible not only to realize the non-conductive and metal texture of the product, but also to realize the black plating effect of the product It does not require silver (Ag), which is a conventional conductive material, and prevents interference with the propagation characteristics of the product due to silver, thereby improving the function of the product, and also preventing breakage and malfunction of the circuit. There is no need for strong acid and strong base liquids, which reduces the cost of wastewater treatment, thereby reducing the manufacturing cost of the product, and can also prevent environmental pollution and harmful effects on the human body.

여기서, 상기 모재(10)는 휴대용 통신 장치(미도시 됨)로 이루어지고, 상기 흑경도막(13)은 비전도성 및 금속질감을 갖도록 상기 휴대용 통신 장치의 외관 테두리 또는 상기 휴대용 통신 장치에 구비된 다수의 키부의 외관 테두리에 형성된다.Here, the base material 10 is made of a portable communication device (not shown), the black hard film 13 is provided in the outer edge of the portable communication device or a plurality of the mobile communication device to have a non-conductive and metallic texture Is formed on the outer edge of the key portion.

또한, 본 발명의 실시예에 따른 비전도성 조성물이 코팅된 모재는 대표적인 적용예로 휴대용 통신 장치에 적용 가능하다. 하지만, 반드시 휴대용 통신 장치에만 한정되는 것은 아니며, 사출 성형물이외에 다른 모든 성형 제품에 적용 가능하다.(예컨대, 화장품, 금속 제품, 유리 제품, 목재 제품 및 세라믹 제품등)In addition, the base material coated with the nonconductive composition according to the embodiment of the present invention is applicable to a portable communication device as a representative application. However, it is not necessarily limited to portable communication devices, and can be applied to all molded products other than injection molded products (for example, cosmetics, metal products, glass products, wood products and ceramic products).

이러한 본 발명의 실시 예에 따른 휴대용 통신 장치의 예시로는, 다양한 통신 시스템들에 대응되는 통신 프로토콜들에 의거하여 동작하는 모든 이동통신 단말기(mobile communication terminal)를 비롯하여, PMP(Portable Multimedia Player), MP3 플레이어, 네비게이션, 게임기, 노트북, 광고판, 티브이(TV), 디지털방송 플레이어, PDA(Personal Digital Assistant) 및 스마트 폰(Smart Phone) 등 모든 정보통신기기, 전기/전자 제품과 멀티미디어 기기 및 그에 대한 응용기기를 포함할 수 있다.
Examples of the portable communication device according to the embodiment of the present invention include all mobile communication terminals (PMPs) operating based on communication protocols corresponding to various communication systems, including Portable Multimedia Player (PMP), All information and communication devices such as MP3 players, navigation, game consoles, notebooks, billboards, TVs, digital broadcasting players, personal digital assistants (PDAs), and smart phones, electrical / electronic products and multimedia devices, and their applications It may include a device.

이상에서 설명한 본 발명의 비전도성 조성물이 코팅된 모재 및 그의 코팅 방법은 전술한 실시 예 및 도면에 의해 한정되는 것은 아니고, 여러 가지 치환, 변형 및 변경이 가능함은 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 있어 명백할 것이다.
The base material and the coating method thereof coated with the non-conductive composition of the present invention described above are not limited to the above-described embodiments and drawings, and various substitutions, modifications, and changes are possible in the art to which the present invention pertains. It will be apparent to those who have knowledge.

모재 : 11 제 1, 2 경화 도료 : 12, 15
흑경도막 : 13 칼라 도료 : 14
하도막 : a 중도막 : b
상도막 : cBase material: 11 1st, 2 hardening paint: 12, 15
Black coating: 13 Color paint: 14
Subfilm: a Midcoat: b
Top coat: c

Claims (22)

비전도성 조성물이 코팅된 모재에 있어서,
상기 모재의 표면에는 비전도성 산화은이 함유된 흑경막 조성물을 분사하여 흑경도막이 형성됨을 특징으로 하는 비전도성 조성물이 코팅된 모재.
In the base material coated with the non-conductive composition,
The base material coated with the non-conductive composition, characterized in that the black film is formed by spraying a black film composition containing a non-conductive silver oxide on the surface of the base material.
제 1 항에 있어서, 상기 흑경도막은 상기 모재의 외관 테두리 또는 상기 모재에 구비된 다수의 키부의 외관 테두리에 형성됨을 특징으로 하는 비전도성 조성물이 코팅된 모재.
The base material coated with a non-conductive composition according to claim 1, wherein the black hard film is formed on an outer edge of the base material or an outer edge of a plurality of key parts provided in the base material.
비전도성 조성물이 코팅된 모재에 있어서,
상기 모재의 표면에 제 1 경화 도료를 분사하여 형성되는 하도막;
상기 하도막에 분사되는 전처리액;
상기 하도막의 표면에 비전도성 산화은이 함유된 흑경막 조성물과 환원제 조성물을 동시 분사하여 형성되는 흑경도막;
상기 흑경도막을 세척하는 정제수;
칼라 도료를 분사하여 형성하는 중도막; 및
상기 중도막의 표면에 제 2 경화 도료를 분사하여 형성하는 상도막을 포함함을 특징으로 하는 비전도성 조성물이 코팅된 모재.
In the base material coated with the non-conductive composition,
An undercoat formed by spraying a first cured paint on the surface of the base material;
A pretreatment liquid sprayed on the undercoat;
A black hard coating film formed by simultaneously spraying a black film composition containing a non-conductive silver oxide and a reducing agent composition on the surface of the undercoat;
Purified water for washing the black hard film;
An intermediate coating formed by spraying a color paint; And
The base material coated with a non-conductive composition, characterized in that it comprises a top coating film formed by spraying a second cured paint on the surface of the intermediate coating film.
제 3 항에 있어서, 상기 모재는 사출 성형물과, 금속 물품과, 목재 제품과, 유리 제품 및 세라믹 제품들 중 어느 하나로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
4. The base material coated with a nonconductive composition according to claim 3, wherein the base material is made of any one of an injection molding, a metal article, a wood product, a glass product, and a ceramic product.
제 3 항에 있어서, 상기 제 1, 2 경화 도료는 이산화규소, 우레탄 및 유브이(UV) 경화형 도료들 중 어느 하나로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
The base material coated with the non-conductive composition according to claim 3, wherein the first and second cured paints are made of any one of silicon dioxide, urethane, and UV curable paints.
제 5 항에 있어서, 상기 이산화규소의 조성물은 실리카졸 5~40g과 오르가노졸 5~20g과, 정제수 5~30g 및 솔벤트등으로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
The base material coated with a non-conductive composition according to claim 5, wherein the silicon dioxide composition is composed of 5-40 g of silica sol, 5-20 g of organosol, 5-30 g of purified water, and a solvent.
제 3 항에 있어서, 상기 전처리액의 조성물은 소듐염과, 톨류엔과, 염화주석 및 벤조아졸로 구성된 제 1 군과, 계면활성제 및 암모늄염으로 구성된 제 2 군을 혼합하여 이루어지고,
상기 제 1, 2 군의 중량은 각각 5~30g으로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
The composition of claim 3, wherein the composition of the pretreatment liquid is made by mixing a first group composed of sodium salt, toluene, tin chloride and benzoazole, and a second group composed of surfactant and ammonium salt,
The base material coated with a non-conductive composition, characterized in that the weight of the first and second groups consists of 5 to 30g, respectively.
제 3 항에 있어서, 상기 흑경막 조성물은 산화은 5~50g과, 암모니아수 10~50g과, 티타눔 0.01~0.2g과, 실란 0.01~0.2g 및 비닐실란 0.01~0.2g으로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
The vision of claim 3, wherein the black film composition comprises 5 to 50 g of silver oxide, 10 to 50 g of ammonia water, 0.01 to 0.2 g of titanum, 0.01 to 0.2 g of silane, and 0.01 to 0.2 g of vinylsilane. Base material coated with a conductive composition.
제 3 항에 있어서, 상기 환원제 조성물은 펙틴과, 프로필렌디아임과, 메틸알콜과, 에틸알콜과, 포름산과, 메틸아민 및 구아검등으로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
4. The base material coated with a non-conductive composition according to claim 3, wherein the reducing agent composition comprises pectin, propylene diametic, methyl alcohol, ethyl alcohol, formic acid, methylamine, guar gum, and the like.
제 3 항에 있어서, 상기 상, 하도막의 두께는 각각 5~30㎛로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
The base material coated with a non-conductive composition according to claim 3, wherein the upper and lower coating layers each have a thickness of 5 to 30 µm.
제 3 항에 있어서, 상기 흑경도막의 두께는 50~200nm로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
The base material coated with a non-conductive composition according to claim 3, wherein the black hard film has a thickness of 50 nm to 200 nm.
제 3 항에 있어서, 상기 칼라 도료의 두께는 3~10㎛로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
The base material coated with a non-conductive composition according to claim 3, wherein the color of the color paint is 3 to 10 µm.
비전도성 조성물이 코팅된 모재의 코팅 방법에 있어서,
상기 모재의 표면에 제 1 경화 도료를 분사하여 하도막을 형성하는 제 1 단계;
상기 제 1 단계로부터 상기 하도막에 전처리액을 분사하는 제 2 단계;
상기 제 2 단계로부터 상기 하도막의 표면에 비전도성 산화은이 함유된 흑경막 조성물과 환원제 조성물을 동시 분사하여 흑경도막을 형성하는 제 3 단계;
상기 제 3 단계로부터 상기 흑경도막을 세척하는 제 4 단계;
상기 제 4 단계로부터 칼라 도료를 분사하여 중도막을 형성하는 제 5 단계; 및
상기 제 5 단계로부터 상기 중도막의 표면에 제 2 경화 도료를 분사하여 상도막을 형성하는 제 6 단계를 포함함을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.
In the coating method of the base material coated with a non-conductive composition,
A first step of forming a undercoat by spraying a first cured paint on the surface of the base material;
A second step of spraying a pretreatment liquid onto the undercoat from the first step;
A third step of simultaneously forming a black hard coat film by simultaneously spraying a black film composition and a reducing agent composition containing non-conductive silver oxide on the surface of the undercoat from the second step;
A fourth step of washing the black hard coating film from the third step;
A fifth step of forming a middle coating film by spraying the color paint from the fourth step; And
And a sixth step of forming a top coat by spraying a second cured paint on the surface of the middle coat from the fifth step.
제 13 항에 있어서, 상기 모재는 사출 성형물과, 금속 제품과, 목재 제품과, 유리 제품 및 세라믹 제품들 중 어느 하나로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.
15. The method of claim 13, wherein the base material comprises one of an injection molding, a metal product, a wood product, a glass product, and a ceramic product.
제 13 항에 있어서, 상기 제 1, 2 경화 도료는 이산화규소, 우레탄 및 유브이(UV) 경화형 도료들 중 어느 하나로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.
15. The method of claim 13, wherein the first and second cured paints are made of any one of silicon dioxide, urethane, and UV curable paints.
제 15 항에 있어서, 상기 이산화규소의 조성물은 실리카졸 5~40g과, 오르가노졸 5~20g과, 정제수 5~30g 및 솔벤트등으로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.
The method of claim 15, wherein the silicon dioxide composition is composed of 5-40 g of silica sol, 5-20 g of organosol, 5-30 g of purified water, solvent, and the like.
제 13 항에 있어서, 상기 전처리액의 조성물은 소듐염과, 톨류엔과, 염화주석 및 벤조아졸로 구성된 제 1 군과, 계면활성제 및 암모늄염으로 구성된 제 2 군을 혼합하여 이루어지고,
상기 제 1, 2 군의 중량은 각각 5~30g으로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.
The composition of claim 13, wherein the composition of the pretreatment liquid is made by mixing a first group composed of sodium salt, toluene, tin chloride and benzoazole, and a second group composed of surfactant and ammonium salt,
The weight of the first and second groups is a coating method of the base material coated with a non-conductive composition, characterized in that each consisting of 5 ~ 30g.
제 13 항에 있어서, 상기 흑경막 조성물은 산화은 5~50g과, 암모니아수 10~50g과, 티타눔 0.01~0.2g과, 실란 0.01~0.2g 및 비닐실란 0.01~0.2g으로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.
The vision of claim 13, wherein the black film composition comprises 5 to 50 g of silver oxide, 10 to 50 g of ammonia water, 0.01 to 0.2 g of titanum, 0.01 to 0.2 g of silane, and 0.01 to 0.2 g of vinylsilane. A coating method of a base material coated with a conductive composition.
제 13 항에 있어서, 상기 환원제 조성물은 펙틴과, 프로필렌디아임과, 메틸알콜과, 에틸알콜과, 포름산과, 메틸아민 및 구아검등으로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.
14. The coating of a base material coated with a non-conductive composition according to claim 13, wherein the reducing agent composition comprises pectin, propylene diametic, methyl alcohol, ethyl alcohol, formic acid, methylamine, guar gum, and the like. Way.
제 13 항에 있어서, 상기 상, 하도막의 두께는 각각 5~30㎛로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.
The method of claim 13, wherein the thickness of the upper and lower coating layers is 5 to 30㎛, respectively.
제 13 항에 있어서, 상기 흑경도막의 두께는 50~200nm로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.
The method of claim 13, wherein the thickness of the black hard coating film is made of 50 ~ 200nm.
제 13 항에 있어서, 상기 칼라 도료의 두께는 3~10㎛로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.The method of claim 13, wherein the thickness of the color paint is 3 ~ 10㎛ characterized in that the coating of the base material coated with a non-conductive composition.
KR1020110067851A 2011-07-08 2011-07-08 Base materials coating non-conducting materials and coating method thereof KR101884279B1 (en)