KR101884279B1 - Base materials coating non-conducting materials and coating method thereof - Google Patents

Base materials coating non-conducting materials and coating method thereof Download PDF

Info

Publication number
KR101884279B1
KR101884279B1 KR1020110067851A KR20110067851A KR101884279B1 KR 101884279 B1 KR101884279 B1 KR 101884279B1 KR 1020110067851 A KR1020110067851 A KR 1020110067851A KR 20110067851 A KR20110067851 A KR 20110067851A KR 101884279 B1 KR101884279 B1 KR 101884279B1
Authority
KR
South Korea
Prior art keywords
base material
composition
nonconductive
film
black
Prior art date
Application number
KR1020110067851A
Other languages
Korean (ko)
Other versions
KR20130006046A (en
Inventor
이광필
이호연
Original Assignee
삼성전자주식회사
(주)이오젠
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 삼성전자주식회사, (주)이오젠 filed Critical 삼성전자주식회사
Priority to KR1020110067851A priority Critical patent/KR101884279B1/en
Publication of KR20130006046A publication Critical patent/KR20130006046A/en
Application granted granted Critical
Publication of KR101884279B1 publication Critical patent/KR101884279B1/en

Abstract

본 발명은 모재의 표면상에 비전도성 특성을 갖는 산화은이 함유된 흑경도막을 코팅한 비전도성 조성물이 코팅된 모재 및 그의 코팅 방법에 관한 것이다.
이를 위해, 비전도성 조성물이 코팅된 모재에 있어서, 상기 모재의 표면에 제 1 경화 도료를 분사하여 형성되는 하도막과, 상기 하도막에 분사되는 전처리액과, 상기 하도막의 표면에 비전도성 산화은이 함유된 흑경막 조성물과 환원제 조성물을 동시 분사하여 형성되는 흑경도막과, 상기 흑경도막을 세척하는 정제수와, 칼라 도료를 분사하여 형성하는 중도막과, 상기 중도막의 표면에 제 2 경화 도료를 분사하여 형성하는 상도막을 포함함을 특징으로 하며, 이에 따라, 제품의 비전도성 및 금속 질감 구현이 가능할 뿐만 아니라, 제품의 흑경 도금 효과도 구현가능하고, 기존의 전도성 물질인 은(Ag)이 필요없으므로 은으로 인한 제품의 전파 특성 방해를 방지하여 제품의 기능을 향상시킬뿐만 아니라, 회로의 파손 및 오작동을 방지할 수 있고, 또한, 기존의 도금시 사용되던 강산 및 강염기성액이 필요없어 폐수처리비용을 절감하고, 이로인해 제품의 제조원가를 절감하며, 또한, 환경 오염 및 인체에 치명적인 영향 유발을 방지할 수 있는 이점이 있다.The present invention relates to a base material coated with a non-conductive composition coated with a black coating film containing silver oxide having a non-conductive property on the surface of a base material and a coating method thereof.
To this end, there is provided a base material coated with a nonconductive composition, comprising a base film formed by spraying a first curing paint on the surface of the base material, a pretreatment liquid sprayed onto the base film, A black ink coat formed by simultaneously spraying a black ink film composition containing a black ink and a reducing agent composition, purified water for washing the black ink coat, a mid coat formed by spraying a color paint, and a second cured paint sprayed onto the surface of the intermediate coat And thus it is possible to realize the nonconductive and metallic texture of the product and also to realize the black plating effect of the product and since silver (Ag), which is a conventional conductive material, is not required, It is possible to prevent breakage and malfunction of the circuit as well as improve the function of the product by preventing the propagation characteristic disturbance of the product due to You do not need a strong and Orders Received gangyeom that was used during the plating and reduce wastewater treatment costs, thereby reducing the manufacturing cost of the product, but also has the advantage of preventing the harmful effects caused to the environment and humans.

Description

비전도성 조성물이 코팅된 모재 및 그의 코팅 방법{BASE MATERIALS COATING NON-CONDUCTING MATERIALS AND COATING METHOD THEREOF}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a base material coated with a nonconductive composition,

본 발명은 비전도성 조성물이 코팅된 모재 및 그의 코팅 방법에 관한 것으로서, 특히, 모재의 표면상에 비전도성 특성을 갖는 산화은이 함유된 흑경도막을 코팅한 비전도성 조성물이 코팅된 모재 및 그의 코팅 방법에 관한 것이다.
The present invention relates to a base material coated with a nonconductive composition and a coating method thereof, and more particularly to a base material coated with a non-conductive composition coated with a black coating film containing silver oxide having a non- .

통상적으로, 플라스틱 사출 모재의 용도가 화장품, 휴대용 통신 장치, 전기/전자 제품, 윈도우, 자동차 및 전자장비등의 분야에서 그 사용량이 점차 증가되고 있다. Typically, the use of plastic injection base materials is increasingly used in the fields of cosmetics, portable communication devices, electric / electronic products, windows, automobiles, and electronic equipment.

상기 제품들은 표면이 유리나 금속에 비해 내구성 및 경도가 떨어져 상품가치에 손실을 가져오게 된다. 이러한 플라스틱 사출 모재의 표면 손상 보호 및 경도 광택 향상을 위해 여러 가지 도장기법이 개발되고 있다. 가장 범용적으로 사용되어지는 도장기법들로는 자연건조방법, 저온소부 방법, 자외선 경화방법등을 들 수 있다.These products have durability and hardness on the surface compared to glass or metal, which leads to loss of product value. Various coating techniques have been developed to protect the surface of the plastic injection base material and to improve the hardness gloss. The most commonly used painting techniques include natural drying methods, low-temperature baking methods, and ultraviolet curing methods.

최근 들어, 상기 사출 모재는 차별화된 디자인 외관 구현을 위한 신소재 및 표면 처리 기술을 적용하고 있다. 특히, 금속의 고급질감에 대한 소비자의 요구가 증가되고 있다.In recent years, the injection-molded base material has been applied to new material and surface treatment technology for differentiated design appearance. In particular, there is an increasing demand from consumers for the high-quality texture of metals.

따라서, 상기 사출 모재의 내, 외장 기구물에는 금속성 색상 및 금속성 질감을 구현하고 있다. 이러한 금속 질감의 표면 처리 방법으로는, 통상적인 도금 및 진공 증착 방법 또는 금속 소재를 이용한 박막 코팅 및 실링 방법등이 사용된다.Accordingly, the internal and external structures of the injection-molded base material have metallic color and metallic texture. As a surface treatment method of such a metal texture, a conventional plating and vacuum deposition method or a thin film coating and sealing method using a metal material are used.

그러나, 종래의 도금 및 진공 증착 방법은 사출 모재에 금속 질감을 위해 전도성 물질인 질산(HNO₃), 알루미늄(Al) 및 은(Ag)등을 사용하여 은색을 바탕으로 후공정을 진행하기 때문에 전기의 전도성이 높은 제품을 생산하였고, 이로인해, 전도성을 갖는 제품이 휴대용 통신 장치일 경우, 은의 전파 특성을 방해로 인해 휴대용 통신 장치의 안테나 수신율이 감소되어 제품의 기능을 저하시키고, 또한, 전도성을 갖는 상기 휴대용 통신 장치 및 상기 전기/전자 제품들은 회로 파손 및 제품의 오작동이 발생되는 단점이 있었다. However, in the conventional plating and vacuum deposition method, since a post-process is carried out based on silver using nitric acid (HNO3), aluminum (Al) and silver (Ag) When the product having conductivity is a portable communication device, the antenna reception ratio of the portable communication device is lowered due to interference with the propagation characteristics of silver, thereby deteriorating the function of the product, The portable communication apparatus and the electric / electronic products have disadvantages such as circuit breakage and malfunction of the product.

또한, 종래의 도금 방법은 도금 공정시 강산 및 강염기성 용액을 사용하기 때문에 폐수처리의 비용상승, 환경 오염 발생 및 인체에 치명적인 영향을 유발시키는 단점이 있었다.In addition, since the conventional plating method uses a strong acid and strong basic solution in the plating process, it has a disadvantage that it raises the cost of wastewater treatment, causes environmental pollution, and has a fatal effect on the human body.

따라서, 제품에 비전도성 및 금속 질감을 구현하기 위해 비전도성 물질을 함유한 조성물의 코팅이 필요한 실정이다.
Therefore, it is necessary to coat a composition containing a nonconductive material in order to realize a nonconductive and metallic texture in the product.

본 발명은 모재에 비전도성 특성을 갖는 산화은이 함유된 흑경도막을 코팅함으로써, 제품의 비전도성 및 금속 질감 구현이 가능할 뿐만 아니라, 제품의 흑경 도금 효과도 구현가능하도록 한 비전도성 조성물이 코팅된 모재 및 그의 코팅 방법을 제공하는데 있다.The present invention relates to a non-conductive composition which is capable of realizing a non-conductive and metallic texture of a product by coating a black coating film containing silver oxide having a non-conductive property on the base material, And a coating method thereof.

또한, 본 발명은 모재에 비전도성 특성을 갖는 산화은이 함유된 흑경도막을 코팅함으로써, 기존의 전도성 물질인 은(Ag)이 필요없어 은으로 인한 제품의 전파 특성 방해를 방지하여 제품의 기능을 향상시킬뿐만 아니라, 회로의 파손 및 오작동을 방지할 수 있도록 한 비전도성 조성물이 코팅된 모재 및 그의 코팅 방법을 제공하는데 있다.In addition, the present invention can improve the function of the product by preventing the interference of the propagation characteristics of the product due to the silver because silver (Ag), which is a conventional conductive material, is coated by coating the black coating film containing silver oxide having non- And to prevent breakage and malfunction of the circuit, as well as to provide a method of coating the base material coated with the nonconductive composition.

또한, 본 발명은 모재에 비전도성 특성을 갖는 산화은이 함유된 흑경도막을 코팅함으로써, 기존의 도금시 사용되던 강산 및 강염기성액이 필요없어 폐수처리비용을 절감하고, 이로인해 제품의 제조원가를 절감하며, 또한, 환경 오염 및 인체에 치명적인 영향 유발을 방지할 수 있도록 한 비전도성 조성물이 코팅된 모재 및 그의 코팅 방법을 제공하는데 있다.
Further, by coating a black coating film containing silver oxide having a nonconductive property on a base material, a strong acid and a strong base solution used in conventional plating are not needed, thereby reducing the waste water treatment cost, thereby reducing the manufacturing cost of the product , And also to provide a base material coated with a nonconductive composition which can prevent environmental pollution and a lethal influence on the human body, and a coating method thereof.

본 발명은, 비전도성 조성물이 코팅된 모재에 있어서,The present invention relates to a base material coated with a nonconductive composition,

상기 모재의 표면에 제 1 경화 도료를 분사하여 형성되는 하도막;A base film formed by spraying a first curing paint on a surface of the base material;

상기 하도막에 분사되는 전처리액;A pretreatment liquid sprayed onto the primer film;

상기 하도막의 표면에 비전도성 산화은이 함유된 흑경막 조성물과 환원제 조성물을 동시 분사하여 형성되는 흑경도막;A black coating film formed by simultaneously spraying a black ink film composition containing nonconductive silver oxide on the surface of the undercoat and a reducing agent composition;

상기 흑경도막을 세척하는 정제수;Purified water for washing the black coat;

칼라 도료를 분사하여 형성하는 중도막; 및A middle film formed by spraying a color paint; And

상기 중도막의 표면에 제 2 경화 도료를 분사하여 형성하는 상도막을 포함함을 특징으로 한다.
And a top coat formed by spraying a second cured paint onto the surface of the intermediate coat.

본 발명의 코팅 방법은, 비전도성 조성물이 코팅된 모재의 코팅 방법에 있어서,The coating method of the present invention is a method for coating a base material coated with a nonconductive composition,

상기 모재의 표면에 제 1 경화 도료를 분사하여 하도막을 형성하는 제 1 단계;A first step of spraying a first cured paint on the surface of the base material to form a base film;

상기 제 1 단계로부터 상기 하도막에 전처리액을 분사하는 제 2 단계;A second step of injecting a pretreatment liquid into the undercoat film from the first step;

상기 제 2 단계로부터 상기 하도막의 표면에 비전도성 산화은이 함유된 흑경막 조성물과 환원제 조성물을 동시 분사하여 흑경도막을 형성하는 제 3 단계;A third step of simultaneously forming a black coating film on the surface of the undercoat layer from the second step by simultaneously spraying the black ink film composition containing nonconductive silver oxide and the reducing agent composition;

상기 제 3 단계로부터 상기 흑경도막을 세척하는 제 4 단계;A fourth step of washing the black coating from the third step;

상기 제 4 단계로부터 칼라 도료를 분사하여 중도막을 형성하는 제 5 단계; 및A fifth step of spraying a color paint from the fourth step to form a mid coat; And

상기 제 5 단계로부터 상기 중도막의 표면에 제 2 경화 도료를 분사하여 상도막을 형성하는 제 6 단계를 포함함을 특징으로 한다.
And a sixth step of spraying a second cured paint onto the surface of the intermediate coating from the fifth step to form a top coat.

상술한 바와 같이 본 발명에 의한 비전도성 조성물이 코팅된 모재 및 그의 코팅 방법에 의하면, As described above, according to the base material coated with the nonconductive composition of the present invention and the coating method thereof,

모재에 비전도성 특성을 갖는 산화은이 함유된 흑경도막을 코팅하여 제품의 비전도성 및 금속 질감 구현이 가능할 뿐만 아니라, 제품의 흑경 도금 효과도 구현가능하고, 또한, 기존의 전도성 물질인 은(Ag)이 필요없으므로 은으로 인한 제품의 전파 특성 방해를 방지하여 제품의 기능을 향상시킬뿐만 아니라, 회로의 파손 및 오작동을 방지할 수 있으며, 또한, 기존의 도금시 사용되던 강산 및 강염기성액이 필요없어 폐수처리비용을 절감하고, 이로인해 제품의 제조원가를 절감하며, 또한, 환경 오염 및 인체에 치명적인 영향 유발을 방지할 수 있는 효과가 있다.
It is possible to realize a non-conductive and metallic texture of a product by coating a black coating film containing silver oxide having a nonconductive property on the base material and also to realize a black plating effect of the product, It is possible to prevent breakage and malfunction of the circuit as well as to improve the function of the product by preventing the product from being disturbed by the propagation characteristics of the product due to the silver. Further, since the strong acid and strong base solution used in the conventional plating are not required, It is possible to reduce the processing cost, thereby to reduce the manufacturing cost of the product, and to prevent the environmental pollution and the fatal influence on the human body.

도 1은 본 발명의 바람직한 일 실시예에 따른 비전도성 조성물이 코팅된 모재의 구성을 나타낸 도면.
도 2는 본 발명의 바람직한 일 실시예에 따른 비전도성 조성물이 코팅된 모재의 코팅 방법을 나타낸 흐름도.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a view showing the configuration of a base material coated with a nonconductive composition according to a preferred embodiment of the present invention. FIG.
2 is a flow chart illustrating a method of coating a base material coated with a nonconductive composition according to a preferred embodiment of the present invention.

이하에서는 첨부도면을 참조하여 본 발명의 가장 바람직한 실시예들을 상세히 설명하기로 한다. 이에 앞서 본 명세서에 기재된 실시예와 도면에 도시된 구성은 본 발명의 가장 바람직한 실시예들에 불과할 뿐이고, 본 출원시점에 있어서 이들을 대체할 수 있는 다양한 변형예들이 있음을 이해하여야 한다.Hereinafter, the most preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. It should be understood that the embodiments described herein and the configurations shown in the drawings are only the most preferred embodiments of the present invention, and that various modifications are possible at the time of filing of the present application.

도 1에 도시된 바와 같이, 비전도성 조성물이 코팅된 모재(11)는 하도막(a), 전처리액(미도시 됨)과, 흑경도막(13)과, 정제수(미도시 됨)와, 중도막(b) 및 상도막(c)으로 구성되어 있고, 상기 하도막(a)은 후술하는 칼라 도료(14) 및 제 2 경화 도료(14)의 부착력 및 평탄도를 확보하기 위해 상기 모재(11)의 표면에 후술하는 제 1 경화 도료(12)를 분사하도록 되어 있으며, 상기 전처리액은 상기 하도막(a)에 유분성을 수용성으로 변형하여 전처리하도록 상기 하도막(a)에 분사되고, 상기 흑경도막(13)은 상기 모재(11)의 비전도성 및 금속감을 구현하기 위해 상기 하도막(a)의 표면에 비전도성 특성을 갖는 산화은이 함유된 흑경막 조성물과 환원제 조성물을 동시에 분사하도록 되어 있으며, 상기 정제수는 상기 흑경도막(13)을 세척하도록 되어 있고, 상기 중도막(b)은 상기 모재(11)의 칼라를 구현하기 위해 상기 흑경도막(13)의 표면에 칼라 도료(14)를 분사하도록 되어 있으며, 상기 상도막(c)은 상기 하도막(a), 상기 흑경도막(13), 상기 칼라 도료(14) 및 상기 중도막(b)을 보호하기 위해 상기 중도막(b)의 표면에 후술하는 제 2 경화 도료(15)를 분사하도록 되어 있다.1, the base material 11 coated with the nonconductive composition includes a base film (a), a pretreatment liquid (not shown), a black coating film 13, purified water (not shown) (A) is composed of a film (b) and an upper film (c), and the base film (a) is composed of the base material (11) to secure adhesion force and flatness of the color coating material (14) And the pretreatment liquid is sprayed onto the primer layer (a) so as to pretreat the primer layer (a) by water-soluble modification of the oil property, and the pretreatment liquid is sprayed onto the primer layer In order to realize the nonconductive and metallic feel of the base material 11, the black ink coat film 13 simultaneously emits the black ink film composition containing the silver oxide having the nonconductive property and the reducing agent composition on the surface of the undercoat film (a) , The purified water is adapted to clean the black ink coat (13), and the intermediate coat (b) The color film 14 is sprayed onto the surface of the black coating film 13 to realize the color of the base material 11. The top coating film c is formed on the surface of the base film a, A second cured paint 15 described later is sprayed onto the surface of the intermediate film (b) to protect the color paint 14 and the intermediate film (b).

도 1에 도시된 바와 같이, 상기 모재(11)는 사출 성형물과, 금속 제품과, 목재 제품과, 유리 제품 및 세라믹 제품들 중 어느 하나로 이루어져 있고, 상기 모재(11)는 사출 성형물과, 금속 제품과, 목재 제품과, 유리 제품 및 세라믹 제품들 이외에 다른 제품도 가능하다.1, the base material 11 is made of an injection-molded product, a metal product, a wood product, a glass product and a ceramic product, and the base material 11 is made of an injection- Other products besides wooden products, glass products and ceramic products are also possible.

상기 제 1 경화 도료(12)는 이산화규소(SiO2)와, 우레탄 및 유브이(UV) 경화형 도료들 중 어느 하나로 이루어져 있고, 상기 제 1 경화 도료(12)는 이산화규소(SiO2)와, 우레탄 및 유브이(UV) 경화형 도료들 이외에 다른 도료도 가능하다. 상기 제 2 경화 도료(15)는 이산화규소(SiO2)와, 우레탄 및 유브이(UV) 경화형 도료들 중 어느 하나로 이루어져 있다. 상기 제 2 경화 도료(15)는 이산화규소(SiO2)와, 우레탄 및 유브이(UV) 경화형 도료들 이외에 다른 도료도 가능하다.The first curing coating 12 is composed of silicon dioxide (SiO 2) and urethane and UV curing coatings. The first curing coating 12 is composed of silicon dioxide (SiO 2), urethane and uv (UV) curing type paints. The second curing coating 15 is composed of silicon dioxide (SiO2) and either urethane or UV curable paints. The second curing coating 15 may be a coating material other than silicon dioxide (SiO 2) and urethane and UV curing coatings.

상기 이산화규소의 조성물은 실리카졸 5~40g과, 오르가노졸 5~20g과, 정제수 5~30g 및 솔벤트등으로 이루어져 있다.The composition of silicon dioxide is composed of 5 to 40 g of silica sol, 5 to 20 g of organosol, 5 to 30 g of purified water, a solvent and the like.

상기 전처리액의 조성물은 소듐염과, 톨류엔과, 염화주석 및 벤조아졸로 구성된 제 1 군과, 계면활성제 및 암모늄염으로 구성된 제 2 군을 혼합하여 이루어져 있고, 상기 제 1 군의 중량은 5~30g으로 이루어져 있으며, 상기 제 2 군의 중량은 5~30g으로 이루어져 있다.Wherein the composition of the pretreatment liquid is a mixture of a first group consisting of sodium salt, tallen ene, tin chloride and benzoazole, and a second group consisting of a surfactant and an ammonium salt, And the weight of the second group is 5 to 30 g.

상기 흑경막 조성물은 산화은 5~50g과, 암모니아수 10~50g과, 티타눔 0.01~0.2g과, 실란 0.01~0.2g 및 비닐실란 0.01~0.2g으로 이루어져 있다.The black film composition comprises 5 to 50 g of silver oxide, 10 to 50 g of ammonia water, 0.01 to 0.2 g of titanum, 0.01 to 0.2 g of silane and 0.01 to 0.2 g of vinylsilane.

상기 환원제 조성물은 펙틴과, 프로필렌디아임과, 메틸알콜과, 에틸알콜과, 포름산과, 메틸아민 및 구아검등으로 이루어져 있다The reducing agent composition is composed of pectin, propylene diamine, methyl alcohol, ethyl alcohol, formic acid, methylamine, guar gum and the like

상기 하도막(a)의 두께는 5~30㎛로 이루어져 있고, 상기 하도막(a)의 두께는 5㎛ 이하 또는 30㎛이상도 가능하다.The thickness of the undercoat film (a) is 5 to 30 占 퐉, and the thickness of the undercoat film (a) can be 5 占 퐉 or less or 30 占 퐉 or more.

상기 상도막(a)의 두께는 5~30㎛로 이루어져 있고, 상기 상도막(a)의 두께는 5㎛ 이하 또는 30㎛이상도 가능하다.The thickness of the top coat (a) is 5 to 30 占 퐉, and the thickness of the top coat (a) can be 5 占 퐉 or less or 30 占 퐉 or more.

상기 흑경도막(13)의 두께는 50~200nm로 이루어져 있고, 상기 흑경도막(13)의 두께는 50nm이하 또는 200nm이상도 가능하다. The thickness of the black coating layer 13 may be 50 to 200 nm, and the thickness of the black coating layer 13 may be 50 nm or less or 200 nm or more.

상기 칼라 도료(14)의 두께는 3~10㎛로 이루어져 있고, 상기 칼라 도료(14)의 두께는 3㎛이하 또는 10㎛이상도 가능하다.
The color paint 14 has a thickness of 3 to 10 μm, and the color paint 14 may have a thickness of 3 μm or less or 10 μm or more.

상기와 같은 구성을 가지는 본 발명의 바람직한 일 실시 예에 의한 비전도성 조성물이 코팅된 모재의 동작과정을 첨부된 도 1을 참조하여 더욱 상세히 설명하면 다음과 같다.The operation of the base material coated with the nonconductive composition according to a preferred embodiment of the present invention will be described in more detail with reference to FIG.

도 1에 도시된 바와 같이, 비전도성 조성물이 코팅된 모재(10)는, 먼저, 사출 성형(미도시 됨)에 의해 사출 모재(11)를 제조하고, 상기 사출 모재(11)의 표면에 제 1 경화 도료(12)를 분사하여 하도막(a)을 형성한다.1, the base material 10 coated with the nonconductive composition is produced by first producing an injection base material 11 by injection molding (not shown) and forming a base material 10 on the surface of the injection base material 11 1 curing paint 12 is sprayed to form a primer film (a).

상기 제 1 경화 도료(12)는 이산화규소(SiO2)와, 우레탄 및 유브이(UV) 경화형 도료들 중 어느 하나로 이루어지고, 상기 이산화규소의 조성물은 실리카졸 5~40g과, 오르가노졸 5~20g과, 정제수 5~30g 및 솔벤트등으로 이루어진다.Wherein the first cured paint 12 is comprised of silicon dioxide (SiO2) and urethane and UV curable paints, wherein the composition of silicon dioxide comprises 5 to 40 grams of silica sol, 5 to 20 grams of organosol, 5 to 30 g of purified water, and a solvent.

여기서, 상기 하도막(a)의 두께는 5~30㎛로 이루어진다. Here, the thickness of the primer film (a) is 5 to 30 占 퐉.

이 상태에서, 상기 하도막(a)에 유분성을 수용성으로 변형하는 전처리액(미도시 됨)을 분사한다. In this state, a pretreatment liquid (not shown) for dispersing the water-soluble property into water is sprayed onto the undercoating film (a).

여기서, 상기 전처리액(미도시 됨)의 조성물은 소듐염과, 톨류엔과, 염화주석 및 벤조아졸로 구성된 제 1 군과, 계면활성제 및 암모늄염으로 구성된 제 2 군을 혼합하여 이루어지고, 상기 제 1 군의 중량은 5~30g으로 이루어지며, 상기 제 2 군의 중량은 5~30g으로 이루어진다.Here, the composition of the pretreatment liquid (not shown) is a mixture of a first group consisting of sodium salt, tall oil ene, tin chloride and benzoazole, and a second group composed of a surfactant and ammonium salt, The weight of the first group is 5 to 30 g, and the weight of the second group is 5 to 30 g.

전처리된 상기 하도막(a)의 표면에 비전도성 특성을 갖는 산화은이 함유된 흑경막 조성물과 환원제 조성물을 동시 분사하여 흑경도막(13)을 형성한다.A black film 13 is formed by simultaneously spraying a black film composition containing silver oxide having a nonconductive property on the surface of the pretreated underlying film (a) and a reducing agent composition.

여기서, 상기 흑경막 조성물은 산화은 5~50g과, 암모니아수 10~50g과, 티타눔 0.01~0.2g과, 실란 0.01~0.2g 및 비닐실란 0.01~0.2g으로 이루어지고, 상기 환원제 조성물은 펙틴과, 프로필렌디아임과, 메틸알콜과, 에틸알콜과, 포름산과, 메틸아민 및 구아검등으로 이루어진다.Wherein the reducing agent composition comprises 5 to 50 g of silver oxide, 10 to 50 g of ammonia water, 0.01 to 0.2 g of titanum, 0.01 to 0.2 g of silane and 0.01 to 0.2 g of vinylsilane, Propylenediamine, methyl alcohol, ethyl alcohol, formic acid, methylamine, guar gum and the like.

여기서, 상기 흑경도막(13)의 두께는 50~200nm로 이루어진다.Here, the thickness of the black coating film 13 is 50 to 200 nm.

이 상태에서, 도 1에 도시된 바와 같이, 상기 흑경도막(13)은 정제수(미도시 됨)를 이용하여 세척하고, 칼라 도료(14)를 분사하여 중도막(b)을 형성한다. 여기서, 상기 칼라 도료(14)의 두께는 3~10㎛로 이루어진다.In this state, as shown in FIG. 1, the black coating film 13 is washed using purified water (not shown), and the color coating 14 is sprayed to form the intermediate film (b). Here, the thickness of the color paint 14 is 3 to 10 탆.

도 1에 도시된 바와 같이, 상기 중도막(b)의 표면에 제 2 경화 도료(15)를 분사하여 상도막(c)을 형성한다.As shown in Fig. 1, a second cured paint 15 is sprayed onto the surface of the intermediate film (b) to form a top coat (c).

여기서, 상기 제 2 경화 도료(15)는 이산화규소(SiO2)과, 우레탄 및 유브이(UV) 경화형 도료들 중 어느 하나로 이루어지고, 상기 이산화규소의 조성물은 실리카졸 5~40g과, 오르가노졸 5~20g과, 정제수 5~30g 및 솔벤트등으로 이루어진다.The second curing coating 15 is made of silicon dioxide (SiO2) and urethane or UV curable paints. The composition of the silicon dioxide comprises 5 to 40 g of silica sol, 5 to 40 g of organosol, , 5 to 30 g of purified water, a solvent and the like.

여기서, 도 1에 도시된 바와 같이, 상기 상도막(c)의 두께는 5~30㎛로 이루어진다.Here, as shown in FIG. 1, the thickness of the top coat (c) is 5 to 30 μm.

여기서, 상기 모재(10)는 휴대용 통신 장치(미도시 됨)로 이루어지고, 상기 흑경도막(13)은 비전도성 및 금속질감을 갖도록 상기 휴대용 통신 장치의 외관 테두리 또는 상기 휴대용 통신 장치에 구비된 키부의 외관 테두리에 형성된다.
Here, the base material 10 is made of a portable communication device (not shown), and the black coating film 13 may have a non-conductive and metallic texture so that the outer frame of the portable communication device, As shown in Fig.

상기와 같은 구성을 가지는 본 발명의 바람직한 일 실시 예에 의한 비전도성 조성물이 코팅된 모재의 코팅 방법의 동작과정을 첨부된 도 2를 참조하여 더욱 상세히 설명하면 다음과 같다.The operation of the method of coating the base material coated with the nonconductive composition according to a preferred embodiment of the present invention will be described in more detail with reference to FIG.

도 2에 도시된 바와 같이, 비전도성 조성물이 코팅된 모재(10)의 코팅 방법은, 먼저, 사출 성형(미도시 됨)에 의해 사출 모재(11)를 제조하고, 상기 사출 모재(11)의 표면에 제 1 경화 도료(12)를 분사하여 하도막(a)을 형성한다.(S1)2, the method of coating the base material 10 coated with the nonconductive composition is as follows. First, the injection base material 11 is produced by injection molding (not shown) And the first cured paint 12 is sprayed onto the surface to form a primer film (a). (S1)

상기 제 1 경화 도료(12)는 이산화규소(SiO2)와, 우레탄 및 유브이(UV) 경화형 도료들 중 어느 하나로 이루어진다.The first curing coating 12 is made of silicon dioxide (SiO2) and either urethane or UV curable coatings.

여기서, 상기 이산화규소의 조성물은 실리카졸 5~40g과, 오르가노졸 5~20g과, 정제수 5~30g 및 솔벤트등으로 이루어진다.Here, the composition of silicon dioxide is composed of 5 to 40 g of silica sol, 5 to 20 g of organosol, 5 to 30 g of purified water, a solvent and the like.

여기서, 상기 하도막(a)의 두께는 5~30㎛로 이루어진다. Here, the thickness of the primer film (a) is 5 to 30 占 퐉.

상기 S1으로부터 상기 하도막(a)에 유분성을 수용성으로 변형하는 전처리액(미도시 됨)을 분사한다.(S2)A pretreatment liquid (not shown) which deforms the water-soluble property to water is sprayed from the above S1 to the above-mentioned subbing layer (a) (S2)

여기서, 상기 전처리액(미도시 됨)의 조성물은 소듐염과, 톨류엔과, 염화주석 및 벤조아졸로 구성된 제 1 군과, 계면활성제 및 암모늄염으로 구성된 제 2 군을 혼합하여 이루어지고, 상기 제 1 군의 중량은 5~30g으로 이루어지며, 상기 제 2 군의 중량은 5~30g으로 이루어진다.Here, the composition of the pretreatment liquid (not shown) is a mixture of a first group consisting of sodium salt, tall oil ene, tin chloride and benzoazole, and a second group composed of a surfactant and ammonium salt, The weight of the first group is 5 to 30 g, and the weight of the second group is 5 to 30 g.

상기 S2로부터 상기 하도막(a)의 표면에 비전도성 특성을 갖는 산화은이 함유된 흑경막 조성물과 환원제 조성물을 동시 분사하여 흑경도막(13)을 형성한다.(S3)From the above step S2, the black film composition containing the silver oxide having the nonconductive property and the reducing agent composition is simultaneously sprayed on the surface of the undercoat film (a) to form the black coat film 13. (S3)

여기서, 상기 흑경막 조성물은 산화은 5~50g과, 암모니아수 10~50g과, 티타눔 0.01~0.2g과, 실란 0.01~0.2g 및 비닐실란 0.01~0.2g으로 이루어지고, 상기 환원제 조성물은 펙틴과, 프로필렌디아임과, 메틸알콜과, 에틸알콜과, 포름산과, 메틸아민 및 구아검등으로 이루어진다.Wherein the reducing agent composition comprises 5 to 50 g of silver oxide, 10 to 50 g of ammonia water, 0.01 to 0.2 g of titanum, 0.01 to 0.2 g of silane and 0.01 to 0.2 g of vinylsilane, Propylenediamine, methyl alcohol, ethyl alcohol, formic acid, methylamine, guar gum and the like.

여기서, 상기 흑경도막(13)의 두께는 50~200nm로 이루어진다.Here, the thickness of the black coating film 13 is 50 to 200 nm.

상기 S3으로부터 상기 흑경도막(13)은 정제수(미도시 됨)를 이용하여 세척한다.(S4)From step S3, the black coating film 13 is cleaned using purified water (not shown). (S4)

상기 S4로부터 칼라 도료(14)를 분사하여 중도막(b)을 형성한다.(S5)The color film 14 is sprayed from the above S4 to form the intermediate film (b) (S5)

여기서, 상기 칼라 도료(14)의 두께는 3~10㎛로 이루어진다.Here, the thickness of the color paint 14 is 3 to 10 탆.

상기 S5로부터 상기 중도막(b)의 표면에 제 2 경화 도료(15)를 분사하여 상도막(c)을 형성한다.(S6)(C) is formed by spraying the second cured paint 15 onto the surface of the intermediate film (b) from step S5. (S6)

여기서, 상기 제 2 경화 도료(15)는 이산화규소(SiO2), 우레탄 및 유브이(UV) 경화형 도료들 중 어느 하나로 이루어지고, 상기 이산화규소의 조성물은 실리카졸 5~40g과 오르가노졸 5~20g과, 정제수 5~30g과 솔벤트등으로 이루어진다.Wherein the second cured paint 15 comprises one of silicon dioxide (SiO2), urethane and UV curable paints, the composition of silicon dioxide comprises 5 to 40 g of silica sol, 5 to 20 g of organosol, , 5 ~ 30g of purified water and a solvent.

여기서, 상기 상도막(c)의 두께는 5~30㎛로 이루어진다.Here, the thickness of the top coat (c) is 5 to 30 占 퐉.

상기와 같이, 사출 모재(11)에 비전도성 특성을 갖는 산화은이 함유된 흑경도막(13)을 코팅함으로써, 제품의 비전도성 및 금속 질감 구현이 가능할 뿐만 아니라, 제품의 흑경 도금 효과도 구현가능하고, 기존의 전도성 물질인 은(Ag)이 필요없어 은으로 인한 제품의 전파 특성 방해를 방지하여 제품의 기능을 향상시킬뿐만 아니라, 회로의 파손 및 오작동을 방지할 수 있고, 또한, 기존의 도금시 사용되던 강산 및 강염기성액이 필요없어 폐수처리비용을 절감하고, 이로인해 제품의 제조원가를 절감하며, 또한, 환경 오염 및 인체에 치명적인 영향 유발을 방지할 수 있다.As described above, by coating the black ink coat 13 containing silver oxide having nonconductive properties in the injection base material 11, it is possible to realize the nonconductive and metallic texture of the product and also realize the black plating effect of the product , Ag, which is a conventional conductive material, is not required, thereby preventing interference of the product propagation characteristics due to silver, thereby improving the function of the product, preventing breakage and malfunction of the circuit, It is possible to reduce the cost of treating wastewater, thereby reducing the manufacturing cost of the product, and preventing environmental pollution and a fatal influence on the human body.

여기서, 상기 모재(10)는 휴대용 통신 장치(미도시 됨)로 이루어지고, 상기 흑경도막(13)은 비전도성 및 금속질감을 갖도록 상기 휴대용 통신 장치의 외관 테두리 또는 상기 휴대용 통신 장치에 구비된 다수의 키부의 외관 테두리에 형성된다.In this case, the base material 10 is made of a portable communication device (not shown), and the black coating film 13 has a nonconductive and metallic texture so that the outer frame of the portable communication device or a plurality As shown in Fig.

또한, 본 발명의 실시예에 따른 비전도성 조성물이 코팅된 모재는 대표적인 적용예로 휴대용 통신 장치에 적용 가능하다. 하지만, 반드시 휴대용 통신 장치에만 한정되는 것은 아니며, 사출 성형물이외에 다른 모든 성형 제품에 적용 가능하다.(예컨대, 화장품, 금속 제품, 유리 제품, 목재 제품 및 세라믹 제품등)Further, the base material coated with the nonconductive composition according to the embodiment of the present invention is applicable to a portable communication apparatus as a typical application example. However, it is not necessarily limited to a portable communication device, but can be applied to all other molded products other than an injection molded product (for example, cosmetics, metal products, glass products, wood products, and ceramic products)

이러한 본 발명의 실시 예에 따른 휴대용 통신 장치의 예시로는, 다양한 통신 시스템들에 대응되는 통신 프로토콜들에 의거하여 동작하는 모든 이동통신 단말기(mobile communication terminal)를 비롯하여, PMP(Portable Multimedia Player), MP3 플레이어, 네비게이션, 게임기, 노트북, 광고판, 티브이(TV), 디지털방송 플레이어, PDA(Personal Digital Assistant) 및 스마트 폰(Smart Phone) 등 모든 정보통신기기, 전기/전자 제품과 멀티미디어 기기 및 그에 대한 응용기기를 포함할 수 있다.
Examples of the portable communication apparatus according to the embodiment of the present invention include all mobile communication terminals operating based on communication protocols corresponding to various communication systems, a portable multimedia player (PMP) All information communication devices such as MP3 players, navigation devices, game devices, notebooks, billboards, TVs, digital broadcasting players, PDAs (personal digital assistants) and smart phones, electric / electronic products and multimedia devices and their applications Device.

이상에서 설명한 본 발명의 비전도성 조성물이 코팅된 모재 및 그의 코팅 방법은 전술한 실시 예 및 도면에 의해 한정되는 것은 아니고, 여러 가지 치환, 변형 및 변경이 가능함은 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 있어 명백할 것이다.
It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the present invention as defined by the appended claims. It will be clear to those who have knowledge.

모재 : 11 제 1, 2 경화 도료 : 12, 15
흑경도막 : 13 칼라 도료 : 14
하도막 : a 중도막 : b
상도막 : cBase material: 11 1st and 2nd hardened paint: 12, 15
Black paint film: 13 color paint: 14
Bottom: a middle b: b
Top coat: c

Claims (22)

비전도성 조성물이 코팅된 모재에 있어서,
상기 모재의 표면에는 비전도성 산화은이 함유된 흑경막 조성물을 분사하여 흑경도막이 형성되고,
상기 흑경막 조성물은 산화은 5~50g과, 암모니아수 10~50g과, 티타눔 0.01~0.2g과, 실란 0.01~0.2g 및 비닐실란 0.01~0.2g으로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
In the base material coated with the nonconductive composition,
A black coating film is formed on the surface of the base material by spraying a black film composition containing nonconductive silver oxide,
Wherein the black film composition comprises 5 to 50 g of silver oxide, 10 to 50 g of ammonia water, 0.01 to 0.2 g of titanum, 0.01 to 0.2 g of silane and 0.01 to 0.2 g of vinylsilane. .
제 1 항에 있어서, 상기 흑경도막은 상기 모재의 외관 테두리 또는 상기 모재에 구비된 다수의 키부의 외관 테두리에 형성됨을 특징으로 하는 비전도성 조성물이 코팅된 모재.
The preform coated with a nonconductive composition according to claim 1, wherein the black coating layer is formed on an outer rim of the base material or an outer rim of a plurality of key parts provided on the base material.
비전도성 조성물이 코팅된 모재에 있어서,
상기 모재의 표면에 제 1 경화 도료를 분사하여 형성되는 하도막;
상기 하도막에 분사되는 전처리액;
상기 하도막의 표면에 비전도성 산화은이 함유된 흑경막 조성물과 환원제 조성물을 동시 분사하여 형성되는 흑경도막;
상기 흑경도막을 세척하는 정제수;
칼라 도료를 분사하여 형성하는 중도막; 및
상기 중도막의 표면에 제 2 경화 도료를 분사하여 형성하는 상도막을 포함하고,
상기 흑경막 조성물은 산화은 5~50g과, 암모니아수 10~50g과, 티타눔 0.01~0.2g과, 실란 0.01~0.2g 및 비닐실란 0.01~0.2g으로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
In the base material coated with the nonconductive composition,
A base film formed by spraying a first curing paint on a surface of the base material;
A pretreatment liquid sprayed onto the primer film;
A black coating film formed by simultaneously spraying a black ink film composition containing nonconductive silver oxide on the surface of the undercoat and a reducing agent composition;
Purified water for washing the black coat;
A middle film formed by spraying a color paint; And
And a top coat formed by spraying a second cured paint on the surface of the intermediate coat,
Wherein the black film composition comprises 5 to 50 g of silver oxide, 10 to 50 g of ammonia water, 0.01 to 0.2 g of titanum, 0.01 to 0.2 g of silane and 0.01 to 0.2 g of vinylsilane. .
제 3 항에 있어서, 상기 모재는 사출 성형물과, 금속 물품과, 목재 제품과, 유리 제품 및 세라믹 제품들 중 어느 하나로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
The base material coated with a nonconductive composition according to claim 3, wherein the base material is one of an injection-molded product, a metal product, a wood product, a glass product, and a ceramic product.
제 3 항에 있어서, 상기 제 1, 2 경화 도료는 이산화규소, 우레탄 및 유브이(UV) 경화형 도료들 중 어느 하나로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
4. The preform coated with a nonconductive composition according to claim 3, wherein the first and second curing paints are made of silicon dioxide, urethane and UV curable paints.
제 5 항에 있어서, 상기 이산화규소의 조성물은 실리카졸 5~40g과 오르가노졸 5~20g과, 정제수 5~30g 및 솔벤트로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
The base material coated with a nonconductive composition according to claim 5, wherein the composition of silicon dioxide comprises 5 to 40 g of silica sol, 5 to 20 g of organosol, 5 to 30 g of purified water and a solvent.
제 3 항에 있어서, 상기 전처리액의 조성물은 소듐염과, 톨류엔과, 염화주석 및 벤조아졸로 구성된 제 1 군과, 계면활성제 및 암모늄염으로 구성된 제 2 군을 혼합하여 이루어지고,
상기 제 1, 2 군의 중량은 각각 5~30g으로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
The pretreatment liquid composition according to claim 3, wherein the composition of the pretreatment liquid is a mixture of a first group consisting of sodium salt, tall oil ene, tin chloride and benzoazole, and a second group consisting of a surfactant and an ammonium salt,
Wherein the weights of the first and second groups are respectively 5 to 30 g.
삭제delete 제 3 항에 있어서, 상기 환원제 조성물은 펙틴과, 프로필렌디아임과, 메틸알콜과, 에틸알콜과, 포름산과, 메틸아민 및 구아검으로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
The base material coated with a nonconductive composition according to claim 3, wherein the reducing agent composition comprises pectin, propylene diamine, methyl alcohol, ethyl alcohol, formic acid, methylamine and guar gum.
제 3 항에 있어서, 상기 상, 하도막의 두께는 각각 5~30㎛로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
4. The preform coated with a nonconductive composition according to claim 3, wherein the thickness of the upper and lower coating layers is 5 to 30 占 퐉.
제 3 항에 있어서, 상기 흑경도막의 두께는 50~200nm로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
4. The preform coated with a nonconductive composition according to claim 3, wherein the black coating layer has a thickness of 50 to 200 nm.
제 3 항에 있어서, 상기 칼라 도료의 두께는 3~10㎛로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재.
4. The preform coated with a nonconductive composition according to claim 3, wherein the color paint has a thickness of 3 to 10 mu m.
비전도성 조성물이 코팅된 모재의 코팅 방법에 있어서,
상기 모재의 표면에 제 1 경화 도료를 분사하여 하도막을 형성하는 제 1 단계;
상기 제 1 단계로부터 상기 하도막에 전처리액을 분사하는 제 2 단계;
상기 제 2 단계로부터 상기 하도막의 표면에 비전도성 산화은이 함유된 흑경막 조성물과 환원제 조성물을 동시 분사하여 흑경도막을 형성하는 제 3 단계;
상기 제 3 단계로부터 상기 흑경도막을 세척하는 제 4 단계;
상기 제 4 단계로부터 칼라 도료를 분사하여 중도막을 형성하는 제 5 단계; 및
상기 제 5 단계로부터 상기 중도막의 표면에 제 2 경화 도료를 분사하여 상도막을 형성하는 제 6 단계를 포함하고,
상기 흑경막 조성물은 산화은 5~50g과, 암모니아수 10~50g과, 티타눔 0.01~0.2g과, 실란 0.01~0.2g 및 비닐실란 0.01~0.2g으로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.
In a method of coating a base material coated with a nonconductive composition,
A first step of spraying a first cured paint on the surface of the base material to form a base film;
A second step of injecting a pretreatment liquid into the undercoat film from the first step;
A third step of simultaneously forming a black coating film on the surface of the undercoat layer from the second step by simultaneously spraying the black ink film composition containing nonconductive silver oxide and the reducing agent composition;
A fourth step of washing the black coating from the third step;
A fifth step of spraying a color paint from the fourth step to form a mid coat; And
And a sixth step of forming a top coat by spraying a second cured paint onto the surface of the intermediate coat from the fifth step,
Wherein the black film composition comprises 5 to 50 g of silver oxide, 10 to 50 g of ammonia water, 0.01 to 0.2 g of titanum, 0.01 to 0.2 g of silane and 0.01 to 0.2 g of vinylsilane. Lt; / RTI >
제 13 항에 있어서, 상기 모재는 사출 성형물과, 금속 제품과, 목재 제품과, 유리 제품 및 세라믹 제품들 중 어느 하나로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.
14. The method of claim 13, wherein the base material comprises at least one of an extruded product, a metal product, a wood product, a glass product, and a ceramic product.
제 13 항에 있어서, 상기 제 1, 2 경화 도료는 이산화규소, 우레탄 및 유브이(UV) 경화형 도료들 중 어느 하나로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.
14. The method of claim 13, wherein the first and second curing paints are made of silicon dioxide, urethane, and UV curable paints.
제 15 항에 있어서, 상기 이산화규소의 조성물은 실리카졸 5~40g과, 오르가노졸 5~20g과, 정제수 5~30g 및 솔벤트로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.
16. The method of claim 15, wherein the composition of silicon dioxide comprises 5 to 40 g of silica sol, 5 to 20 g of organosol, 5 to 30 g of purified water and a solvent.
제 13 항에 있어서, 상기 전처리액의 조성물은 소듐염과, 톨류엔과, 염화주석 및 벤조아졸로 구성된 제 1 군과, 계면활성제 및 암모늄염으로 구성된 제 2 군을 혼합하여 이루어지고,
상기 제 1, 2 군의 중량은 각각 5~30g으로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.
14. The method of claim 13, wherein the composition of the pretreatment liquid is a mixture of a first group consisting of sodium salt, tall oil ene, tin chloride and benzoazole, and a second group consisting of a surfactant and an ammonium salt,
Wherein the weights of the first and second groups are respectively 5 to 30 g.
삭제delete 제 13 항에 있어서, 상기 환원제 조성물은 펙틴과, 프로필렌디아임과, 메틸알콜과, 에틸알콜과, 포름산과, 메틸아민 및 구아검으로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.
The method of claim 13, wherein the reducing agent composition comprises pectin, propylene diamine, methyl alcohol, ethyl alcohol, formic acid, methylamine and guar gum. .
제 13 항에 있어서, 상기 상, 하도막의 두께는 각각 5~30㎛로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.
14. The method of claim 13, wherein the thickness of the upper and lower coating layers is 5 to 30 占 퐉, respectively.
제 13 항에 있어서, 상기 흑경도막의 두께는 50~200nm로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.
14. The method of claim 13, wherein the black coating has a thickness of 50 to 200 nm.
제 13 항에 있어서, 상기 칼라 도료의 두께는 3~10㎛로 이루어짐을 특징으로 하는 비전도성 조성물이 코팅된 모재의 코팅 방법.14. The method of claim 13, wherein the color paint has a thickness of 3 to 10 mu m.
KR1020110067851A 2011-07-08 2011-07-08 Base materials coating non-conducting materials and coating method thereof KR101884279B1 (en)