KR20120124880A - Disperse Dyes Composites and Methods of Dyeing Fiber Using the Same - Google Patents
Disperse Dyes Composites and Methods of Dyeing Fiber Using the Same Download PDFInfo
- Publication number
- KR20120124880A KR20120124880A KR1020110042784A KR20110042784A KR20120124880A KR 20120124880 A KR20120124880 A KR 20120124880A KR 1020110042784 A KR1020110042784 A KR 1020110042784A KR 20110042784 A KR20110042784 A KR 20110042784A KR 20120124880 A KR20120124880 A KR 20120124880A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- dye composition
- formula
- compound
- fiber
- Prior art date
Abstract
Description
본 발명은 분산염료 조성물 및 이를 이용한 섬유의 염색방법에 관한 것으로, 더욱 상세하게는 특정한 화합물들의 조합을 포함하고 있어서, 우수한 염착률 및 일광 견뢰도를 가지므로, 특히, 폴리에스테르의 혼방 섬유를 염색하는데 유용한 분산염료 조성물 및 이를 이용한 섬유의 염색방법에 관한 것이다.The present invention relates to a disperse dye composition and a method for dyeing fibers using the same, and more particularly, to include a combination of specific compounds, and thus to have excellent dyeing rate and light fastness. A useful disperse dye composition and a method of dyeing fibers using the same.
아세테이트, 폴리에스테르 등의 합성 섬유는 종래의 셀룰로오스 및 단백질 섬유에 비하여 소수성이 매우 크기 때문에 종래의 친수성이 큰 염료에 의해 염색되기가 매우 힘들었다.Synthetic fibers such as acetate and polyester have a very high hydrophobicity as compared with conventional cellulose and protein fibers, making it very difficult to be dyed with conventional hydrophilic dyes.
이러한 소수성 섬유의 염색은 수용성 그룹을 함유하지 않으며, 물에 녹지 않은 염료로서 물에 분산하여 이용하는 분산염료가 사용되어 왔다. 그러나 분산염료는, 그 특성상 우수한 염착률 및 고일광 견뢰도를 충분히 실현할 수 없으며, 더욱이, 폴리에스테르의 혼방섬유 등에 대한 친화성도 명확하지 않다.The dyeing of such hydrophobic fibers does not contain water-soluble groups, and has been used as a disperse dye which is dispersed in water as a dye insoluble in water. However, the disperse dyes cannot sufficiently realize excellent dyeing rate and high daylight fastness in view of their properties, and furthermore, the affinity of polyester to blended fibers and the like is not clear.
이러한 문제점을 해결하기 위해 한국 특허출원공개 제2007-0004638호 및 미국 특허출원공개 제2005-0155163호에서는 일광 견뢰도가 우수한 염료를 개시하고 있으나, 상기 염료는 염착성 및 제품 농도가 떨어지거나 일광 견뢰도가 좋지 않은 것으로 확인되었다.In order to solve this problem, Korean Patent Application Publication No. 2007-0004638 and US Patent Application Publication No. 2005-0155163 disclose a dye having excellent daylight fastness, but the dye has a low dyeing property, a low product concentration, or a good daylight fastness. Was confirmed.
이에, 일광 견뢰도 뿐만 아니라 발색성 및 염착률을 향상시키기 위하여, 분산염료 조성물들을 혼합하는 시도가 있지만, 우수한 고일광 견뢰도 및 염착률을 발휘하면서, 소망하는 발색성 등을 가지는 다양한 색상의 염료는 개발되지 못하고 있다.Thus, in order to improve color fastness and dyeing rate as well as daylight fastness, attempts have been made to mix disperse dye compositions, but dyes of various colors having excellent color fastness and desired color development, while exhibiting excellent high light fastness and dyeing rate, have not been developed. .
따라서, 본 발명은 상기와 같은 종래기술의 문제점과 과거로부터 요청되어온 기술적 과제를 해결하는 것을 목적으로 한다.SUMMARY OF THE INVENTION Accordingly, the present invention has been made to solve the above-mentioned problems of the prior art and the technical problems required from the past.
본 출원의 발명자들은 심도 있는 연구와 다양한 실험을 거듭한 끝에, 이후 설명하는 바와 같이, 특정한 화합물들의 조합을 포함하는 분산염료 조성물을 이용하여 폴리에스테르 등을 포함하는 혼방 섬유 재료를 염색 또는 날염하는 방법을 개발하기에 이르렀고, 이 경우, 우수한 염착률 및 고일광 견뢰도를 얻을 수 있음을 발견하고, 본 발명을 완성하기에 이르렀다.After extensive research and various experiments, the inventors of the present application have a method of dyeing or printing mixed fiber materials including polyester using a disperse dye composition including a combination of specific compounds as described below. In this case, it was found that excellent dyeing rate and high daylight fastness were obtained, and thus the present invention was completed.
따라서, 본 발명은 하기 화학식 1의 화합물 20 내지 70 중량% 및 화학식 2의 화합물 20 내지 70 중량%와, 화학식 3 및 4의 화합물들로 이루어진 군에서 선택되는 하나 이상의 화합물들을 5 내지 40 중량% 포함하여 황색 계열의 색상을 발현하는 분산염료 조성물을 제공한다.Accordingly, the present invention comprises 20 to 70% by weight of the compound of Formula 1 and 20 to 70% by weight of the compound of Formula 2, and 5 to 40% by weight of one or more compounds selected from the group consisting of compounds of Formulas 3 and 4 By providing a disperse dye composition expressing a yellow-based color.
(1) (One)
(2) (2)
(3) (3)
(4). (4).
상기 화학식 1 및 2의 화합물들과, 상기 화학식 3 및 4의 화합물들로 이루어진 군에서 선택되는 하나 이상의 화합물들을 특정 함량으로 혼합할 경우, 기존의 염료 조성물보다 뛰어난 발색력, 일광 견뢰도 등을 가지는 황색 계열의 분산염료 조성물을 제조할 수 있다.When the compounds of Formulas 1 and 2 and one or more compounds selected from the group consisting of the compounds of Formulas 3 and 4 are mixed in a specific amount, a yellow-based color having superior color development, daylight fastness, etc. than the conventional dye composition Disperse dye composition of can be prepared.
상기 화학식 1 내지 4의 화합물들은 모두 황색을 나타내는 공지된 물질로서, 종래 화학식 1 및 화학식 3의 화합물을 혼합하여 제조된 황색 계열의 분산염료 조성물은 일광 견뢰도가 떨어졌고, 화학식 1과 화학식 3 또는 화학식 4의 화합물을 혼합하여 제조된 황색 계열의 분산염료 조성물은 염착성 및 제품 농도가 떨어지는 문제점이 있었다. The compounds of Chemical Formulas 1 to 4 are all known to be yellow, and the yellow-based dispersion dye compositions prepared by mixing the compounds of Chemical Formulas 1 and 3 have poor daylight fastness, and have the following Chemical Formulas 1 and 3 or Dispersion dye composition of the yellow series prepared by mixing the compound of 4 had a problem of low dyeability and product concentration.
이에, 본원발명에 따른 황색 계열의 분산염료 조성물은 특정한 함량의 화학식 1 및 2의 화합물들과, 화학식 3 및 4의 화합물들로 이루어진 군에서 선택되는 하나 이상의 화합물들의 배합에 의해 소망하는 수준의 일광 견뢰도 및 염착성을 제공할 수 있다.Thus, the yellow-based dispersion dye composition according to the present invention is a desired level of sunlight by combining a specific amount of compounds of Formulas 1 and 2 with one or more compounds selected from the group consisting of compounds of Formulas 3 and 4 Fastness and dyeing can be provided.
구체적으로, 상기 황색 계열의 분산염료 조성물은, 바람직하게는, 상기 화학식 1의 화합물 30 내지 60 중량% 및 화학식 2의 화합물 20 내지 50 중량%와, 화학식 3 및 4의 화합물들로 이루어진 군에서 선택되는 하나 이상의 화합물들을 5 내지 40 중량% 포함하는 구성에 의해 제조할 수 있다.Specifically, the yellow-based dispersion dye composition is preferably selected from the group consisting of 30 to 60% by weight of the compound of Formula 1 and 20 to 50% by weight of the compound of Formula 2 and the compounds of Formulas 3 and 4 It can be prepared by a composition comprising 5 to 40% by weight of one or more compounds.
상기 함량은 황색 계열에 해당하는 색을 발현하기 위한 최적의 혼합비로서 상기 범위를 벗어날 경우, 소망하는 수준의 염색강도 및 일광 견뢰도를 얻을 수 없으므로, 바람직하지 않다.When the content is outside the above range as the optimum mixing ratio for expressing the color corresponding to the yellow series, the desired level of dyeing strength and daylight fastness cannot be obtained, which is not preferable.
본원발명은, 또한, 상기 황색 계열의 분산 염료 조성물 30 내지 60 중량%, 하기 화학식 5의 화합물 10 내지 40 중량%, 및 화학식 6의 화합물 10 내지 40 중량%를 포함하여 베이지 계열의 색상을 발현하는 분산염료 조성물을 제공한다.The present invention also comprises a beige-based color including 30 to 60% by weight of the yellow-based disperse dye composition, 10 to 40% by weight of the compound of Formula 5, and 10 to 40% by weight of the compound of Formula 6 It provides a disperse dye composition.
(5) (5)
(6). (6).
상기 황색 계열의 분산 염료 조성물과, 상기 화학식 5 및 6의 화합물들로 이루어진 군에서 선택되는 하나 이상의 화합물들을 특정 함량으로 혼합할 경우, 기존의 염료 조성물보다 뛰어난 발색력, 일광 견뢰도 등을 가지는 베이지 계열의 분산염료 조성물을 제조할 수 있다.When the yellow-based disperse dye composition and one or more compounds selected from the group consisting of the compounds of Formulas 5 and 6 are mixed in a specific amount, the beige-based dye having superior color development, daylight fastness, etc. than the conventional dye composition Disperse dye compositions can be prepared.
상기 화학식 5 내지 6의 화합물들은 각각 적색, 청색을 나타내는 공지된 물질이지만, 상기 황색 계열의 분산 염료 조성물과, 상기 화학식 5 및 6의 화합물들로 이루어진 군에서 선택되는 하나 이상의 화합물들은 다양한 조합에 의해 소망하는 분산염료 조성물을 제공할 수 있다.Although the compounds of Formulas 5 to 6 are known materials each showing a red color and a blue color, the yellow-based disperse dye composition and one or more compounds selected from the group consisting of the compounds of Formulas 5 and 6 may be formed by various combinations. The desired disperse dye composition can be provided.
구체적으로, 상기 베이지 계열의 분산염료 조성물은, 바람직하게는, 상기 황색 계열의 분산 염료 조성물 30 내지 60 중량%, 상기 화학식 5의 화합물 20 내지 30 중량%, 및 화학식 6의 화합물 20 내지 30 중량%를 포함하는 구성에 의해 제조할 수 있다.Specifically, the beige-based dispersion dye composition, preferably, 30 to 60% by weight of the yellow-based dispersion dye composition, 20 to 30% by weight of the compound of Formula 5, and 20 to 30% by weight of the compound of Formula 6 It can manufacture by the structure containing.
상기 함량은 베이지 계열에 해당하는 색을 발현하기 위한 최적의 혼합비로서 상기 범위를 벗어날 경우, 소망하는 수준의 염색강도 및 일광 견뢰도를 얻을 수 없으므로, 바람직하지 않다.When the content is outside the above range as an optimal mixing ratio for expressing the color corresponding to the beige series, the desired level of dyeing strength and daylight fastness cannot be obtained, which is not preferable.
또한, 본원발명은, 상기 황색 계열의 분산 염료 조성물 10 내지 50 중량%, 상기 화학식 5의 화합물 10 내지 40 중량%, 및 화학식 6의 화합물 30 내지 60 중량%를 포함하여 그레이 계열의 색상을 발현하는 분산염료 조성물을 제공한다. In addition, the present invention, including 10 to 50% by weight of the yellow-based disperse dye composition, 10 to 40% by weight of the compound of Formula 5, and 30 to 60% by weight of the compound of Formula 6 to express the gray-based color It provides a disperse dye composition.
상기 황색 계열의 분산 염료 조성물과, 상기 화학식 5 및 6의 화합물들로 이루어진 군에서 선택되는 하나 이상의 화합물들을 특정 함량으로 혼합할 경우, 기존의 염료 조성물보다 뛰어난 발색력, 일광 견뢰도 등을 가지는 그레이 계열의 분산염료 조성물을 제조할 수 있다.When the yellow-based disperse dye composition and one or more compounds selected from the group consisting of the compounds of Formulas 5 and 6 are mixed in a specific amount, the gray-based dye having superior color development, daylight fastness, etc. than the conventional dye composition Disperse dye compositions can be prepared.
앞서 설명한 바와 같이, 상기 황색 계열의 분산 염료 조성물과, 상기 화학식 5 및 6의 화합물들로 이루어진 군에서 선택되는 하나 이상의 화합물들은 다양한 조합에 의해 소망하는 분산염료 조성물을 제공할 수 있다.As described above, the yellow-based disperse dye composition and one or more compounds selected from the group consisting of the compounds of Formulas 5 and 6 may provide a desired disperse dye composition by various combinations.
구체적으로, 상기 그레이 계열의 분산염료 조성물은 바람직하게는, 황색 계열의 분산 염료 조성물 20 내지 40 중량%, 상기 화학식 5의 화합물 20 내지 30 중량%, 및 화학식 6의 화합물 40 내지 50 중량%를 포함하는 구성에 의해 제조할 수 있다.Specifically, the gray-based dispersion dye composition preferably comprises 20 to 40% by weight of the yellow-based dispersion dye composition, 20 to 30% by weight of the compound of Formula 5, and 40 to 50% by weight of the compound of Formula 6 It can manufacture by the structure to make.
상기 함량은 그레이 계열에 해당하는 색을 발현하기 위한 최적의 혼합비로서 상기 범위를 벗어날 경우, 소망하는 수준의 염색강도 및 일광 견뢰도를 얻을 수 없으므로, 바람직하지 않다.If the content is outside the above range as an optimal mixing ratio for expressing the color corresponding to the gray series, the desired level of dyeing strength and daylight fastness cannot be obtained, which is not preferable.
상기 화학식 1 내지 6의 화합물은 각각 공지된 물질로서, 그에 대한 자세한 제조방법은 생략한다. Compounds of Chemical Formulas 1 to 6 are known materials, and detailed preparation methods thereof will be omitted.
본 발명의 조성물에는 발명의 목적 및 효과를 저해하지 않는 범위 내에서 가용화제, 완충제, 빙결방지제 등의 기타 성분을 첨가할 수 있다. 이러한 기타 첨가제는 조성물 전체 중량을 기준으로 대략 1 내지 20 중량%의 범위에서 첨가될 수 있다. Other components, such as a solubilizer, a buffer, an antifreezing agent, can be added to the composition of this invention within the range which does not impair the objective and effect of this invention. Such other additives may be added in the range of approximately 1 to 20 weight percent based on the total weight of the composition.
상기 가용화제는 염료의 뭉침을 방지하고 용해를 도와 주는 첨가제 성분으로서, 대표적인 예로는 우레아, 티오우레아, 카프로락탐 등을 들 수 있다. 상기 완충제는 저장 보관시 염료의 분해를 막아주기 위하여 pH를 완충하는 역할을 하는 성분으로서, 대표적인 예로는 인산나트륨, 인산칼륨, 초산나트륨 등을 들 수 있다. 상기 빙결방지제는 액상 냉동보관시 어는 점을 낮춰주어 액상 염료가 얼지 않게 하는 역할을 하는 성분으로서, 대표적인 예로는 에틸렌글리콜, 폴리에틸렌글리콜, 다가알콜 화합물 등을 들 수 있다.The solubilizer is an additive component that prevents agglomeration of dyes and helps dissolution, and typical examples thereof include urea, thiourea, and caprolactam. The buffer is a component that buffers the pH to prevent degradation of the dye during storage and storage, and representative examples thereof include sodium phosphate, potassium phosphate, sodium acetate and the like. The freezing inhibitor lowers the freezing point during liquid freezing and serves as a component that does not freeze the liquid dye. Representative examples include ethylene glycol, polyethylene glycol, and polyalcohol compounds.
본 발명은 또한, 상기 분산염료 조성물들을 사용하여 섬유재료를 염색 또는 날염하는 방법을 제공한다. The present invention also provides a method of dyeing or printing a fiber material using the dispersion dye compositions.
상기 섬유재료의 예로는 반합성 섬유, 합성 섬유, 재생 섬유, 또는 합성 섬유와 천연 섬유의 혼방 섬유가 있으며, 이러한 반합성 섬유로는, 예를 들어, 아세테이트, 합성 섬유로는 폴리에스테르, 폴리아미드, 폴리 비닐, 폴리 우레탄계 섬유, 재생 섬유로는 셀루로우즈 등이 있다. Examples of the fibrous material include semisynthetic fibers, synthetic fibers, regenerated fibers, or blended fibers of synthetic fibers and natural fibers. Examples of such semisynthetic fibers include, for example, acetate, synthetic fibers such as polyester, polyamide, poly Vinyl, polyurethane-based fibers, and recycled fibers include cellulose and the like.
상기 분산염료 조성물은 또한, 폴리에스테르 섬유의 혼방 섬유, 예를 들어, 폴리에스테르와 셀루로우즈 섬유를 포함하는 혼방 섬유 등을 염색 또는 날염에 적용되어 높은 염착률 및 우수한 습윤 견뢰도를 나타낸다.The disperse dye composition is also subjected to dyeing or printing of blended fibers of polyester fibers, for example blended fibers comprising polyester and cellulose fibers, to exhibit high dyeing rates and good wet fastnesses.
본 발명에 따른 염료 조성물은 예를 들어, 콜드패드배치법, 연속 염색법, 침염법, 날염법, 발염법 등 여러 방법에 사용될 수 있으며, 바람직하게는 연속 염색법, 침염법에 사용될 수 있다.The dye composition according to the present invention can be used in various methods, for example, cold pad placement method, continuous dyeing method, dyeing method, printing method, printing method, and preferably used for continuous dyeing method and dyeing method.
특히, 상기 연속 염색법으로는, 산결합제(예를 들어, 탄산나트륨, 중탄산나트륨 등)를 패딩액에 혼합하고, 공지의 방법으로 패딩하여 건열 또는 증열에 의해 염색하는 일욕 패딩법, 및 염료 패딩 후 무기중성염(예를 들어, 무수황산나트륨, 식염 등)과 산결합제(예를 들어, 가성소다, 규산소다 등)를 패딩액에 혼합하여 패딩하고, 공지의 방법으로 건열 또는 증열에 의해 염색하는 이욕 패딩법이 사용될 수 있다. In particular, as the continuous dyeing method, an acid-binding agent (for example, sodium carbonate, sodium bicarbonate, etc.) is mixed with a padding liquid, padded by a known method and dyed by dry heat or steaming, and after the dye padding, inorganic Neutral salts (e.g., anhydrous sodium sulfate, salt, etc.) and acid binders (e.g., caustic soda, sodium silicate, etc.) are mixed and padded in the padding solution, and the bathing padding is dyed by dry heat or steaming by a known method. Law can be used.
본 발명에 따라 수득된 염색물 및 날염물은 축적성(build-up) 및 균염성(levelness)이 뛰어나다. 또한, 착색도가 뛰어나고, 섬유-염료 결합 안정성이 높으며, 일광 견뢰도 뿐만 아니라 타 섬유로의 오염 방지성도 뛰어나다.The dyeings and printings obtained according to the present invention are excellent in build-up and leveling. In addition, it is excellent in coloration, high fiber-dye bonding stability, and excellent in light fastness as well as prevention of contamination to other fibers.
이상에서 설명한 바와 같이, 본 발명에 따른 분산염료 조성물은 특정한 화합물들의 조합을 포함하므로, 폴리에스테르 등을 포함하는 혼방 섬유 재료를 염색 또는 날염시 우수한 염착률을 나타내며, 일광 견뢰도가 우수하다.As described above, since the disperse dye composition according to the present invention includes a combination of specific compounds, it shows excellent dyeing rate when dyeing or printing blended fiber materials including polyester and the like, and has excellent daylight fastness.
이하, 실시예를 통해 본 발명을 더욱 상술하지만, 하기 실시예는 본 발명을 예시하기 위한 것이며, 본 발명의 범주가 이들만으로 한정되는 것은 아니다.
Hereinafter, the present invention will be described in more detail with reference to Examples, but the following Examples are provided to illustrate the present invention, and the scope of the present invention is not limited thereto.
[제조예 1] 화학식 1로 표현되는 황색 분산염료 조성물의 제조 Preparation Example 1 Preparation of Yellow Disperse Dye Composition Represented by Chemical Formula 1
하기 화학식 1의 화합물을 리그닌 설폰산계 분산제를 사용하여 입자크기가 1 ㎛ 이하가 90% 이상 되도록 분쇄한 후 스프레이 드라이 건조하여 하기 화학식 1의 화합물을 포함하는 황색의 분산염료 조성물을 얻었다.The compound of Formula 1 was ground to a particle size of 1 μm or less by 90% or more using a lignin sulfonic acid dispersant, followed by spray drying to obtain a yellow dispersion dye composition comprising the compound of Formula 1 below.
(1)
(One)
[제조예 2] 화학식 2로 표현되는 황색 분산염료 조성물의 제조 Preparation Example 2 Preparation of Yellow Disperse Dye Composition Represented by Chemical Formula 2
하기 화학식 2의 화합물을 상기 제조예 1과 동일한 방법을 사용하여 하기 화학식 2의 화합물을 포함하는 황색의 분산염료 조성물을 얻었다.Using the same method as in Preparation Example 1 to the compound of formula 2 to obtain a yellow dispersion dye composition comprising the compound of formula (2).
(2)
(2)
[제조예 3] 화학식 3로 표현되는 황색 분산염료 조성물의 제조 Preparation Example 3 Preparation of Yellow Disperse Dye Composition Represented by Chemical Formula 3
하기 화학식 3의 화합물을 상기 제조예 1과 동일한 방법을 사용하여 하기 화학식 3의 화합물을 포함하는 황색의 분산염료 조성물을 얻었다.Using the same method as in Preparation Example 1 to the compound of formula 3 to obtain a yellow disperse dye composition comprising the compound of formula (3).
(3)
(3)
[제조예 4] 화학식 4로 표현되는 황색 분산염료 조성물의 제조 Preparation Example 4 Preparation of Yellow Disperse Dye Composition Represented by Chemical Formula 4
하기 화학식 4의 화합물을 상기 제조예 1과 동일한 방법을 사용하여 하기 화학식 4의 화합물을 포함하는 황색의 분산염료 조성물을 얻었다.Using the same method as in Preparation Example 1 to the compound of Formula 4 to obtain a yellow disperse dye composition comprising the compound of formula (4).
(4)
(4)
[제조예 5] 화학식 5로 표현되는 적색 분산염료 조성물의 제조 Preparation Example 5 Preparation of Red Disperse Dye Composition Represented by Chemical Formula 5
하기 화학식 5의 화합물을 상기 제조예 1과 동일한 방법을 사용하여 하기 화학식 5의 화합물을 포함하는 적색의 분산염료 조성물을 얻었다.Using the same method as in Preparation Example 1 to the compound of the formula (5) to obtain a red dispersion dye composition comprising a compound of the formula (5).
(5)
(5)
[제조예 6] 화학식 6로 표현되는 청색 분산염료 조성물의 제조 Preparation Example 6 Preparation of Blue Disperse Dye Composition Represented by Chemical Formula 6
하기 화학식 6의 화합물을 상기 제조예 1과 동일한 방법을 사용하여 하기 화학식 6의 화합물을 포함하는 청색의 분산염료 조성물을 얻었다.Using the same method as Preparation Example 1 to the compound of the formula (6) to obtain a blue disperse dye composition comprising the compound of the formula (6).
(6)
(6)
[실시예 1 내지 6][Examples 1 to 6]
제조예 1 및 2의 화합물과, 제조예 3 및 4의 화합물들로 이루어진 군에서 선택되는 하나 이상의 화합물들을 포함하는 황색 계열의 분산염료 조성물들을 하기 표 1과 같이 제조하였다.
Yellow-based dispersion dye compositions including the compounds of Preparation Examples 1 and 2 and one or more compounds selected from the group consisting of Compounds of Preparation Examples 3 and 4 were prepared as shown in Table 1 below.
[비교예 1 내지 3][Comparative Examples 1 to 3]
제조예 1 내지 4의 화합물들로 이루어진 군에서 선택되는 하나 이상의 화합물들을 포함하는 황색 계열의 분산염료 조성물들을 하기 표 1과 같이 제조하였다.
Yellow-based dispersion dye compositions including one or more compounds selected from the group consisting of compounds of Preparation Examples 1 to 4 were prepared as shown in Table 1 below.
[실시예 7 내지 12][Examples 7 to 12]
제조예 1 및 2의 화합물과, 제조예 3 및 4의 화합물들로 이루어진 군에서 선택되는 하나 이상의 화합물들에, 추가로 제조예 5 및 6의 화합물을 포함하는 베이지 계열의 분산염료 조성물들을 하기 표 2과 같이 제조하였다.
Beige-based dispersion dye compositions comprising the compounds of Preparation Examples 1 and 2 and one or more compounds selected from the group consisting of the compounds of Preparation Examples 3 and 4, further comprising the compounds of Preparation Examples 5 and 6 Prepared as 2.
[비교예 4 내지 6][Comparative Examples 4 to 6]
제조예 1 내지 6의 화합물들로 이루어진 군에서 선택되는 하나 이상의 화합물들을 포함하는 베이지 계열의 분산염료 조성물들을 하기 표 2와 같이 제조하였다.
Beige-based dispersion dye compositions comprising one or more compounds selected from the group consisting of compounds of Preparation Examples 1 to 6 were prepared as shown in Table 2 below.
[실시예 13 내지 18][Examples 13 to 18]
제조예 1 및 2의 화합물과, 제조예 3 및 4의 화합물들로 이루어진 군에서 선택되는 하나 이상의 화합물들에, 추가로 제조예 5 및 6의 화합물을 포함하는 그레이 계열의 분산염료 조성물들을 하기 표 3과 같이 제조하였다.
Gray-based dispersion dye compositions comprising the compounds of Preparation Examples 1 and 2, and one or more compounds selected from the group consisting of Compounds of Preparation Examples 3 and 4, further comprising the compounds of Preparation Examples 5 and 6 It was prepared as in 3.
[비교예 7 내지 9][Comparative Examples 7 to 9]
제조예 1 내지 6의 화합물들로 이루어진 군에서 선택되는 하나 이상의 화합물들을 포함하는 그레이 계열의 분산염료 조성물들을 하기 표 3와 같이 제조하였다.
Gray-based dispersion dye compositions including one or more compounds selected from the group consisting of the compounds of Preparation Examples 1 to 6 were prepared as shown in Table 3 below.
[실험예 1] 황색 계열의 분산염료 조성물의 제조 Experimental Example 1 Preparation of Yellow-Based Disperse Dye Composition
폴리에스테르 100 g, 실온에서 80% 초산에 의해 pH 4.0 ~ pH 4.5로 조절시킨 실시예 1 내지 6 및 비교예 1 내지 3의 황색 분산염료 조성물 1 g, 균염화제 0.5 g/l를 포함하는 액중에 1:20의 액비로 침지시킨다. 3℃/분의 속도로 60℃로 가열한 후 1~2℃/분의 속도로 130℃까지 가열하여 60 분 동안 염색을 수행한다. 이어서, 염액을 40℃로 냉각시키고, 염색된 폴리에스테르 직물을 수세한 다음, 30%수산화나트륨 용액 5 ml/l, 황산수소나트륨 용액 2 g/l 및 시판중인 세제 1 g/l를 포함하는 욕중에서 20 분 동안 70~80℃의 온도 하에 환원 세정 한다. 이어서 가공된 염색물을 수세하고 건조시킨다.A liquid comprising 100 g of polyester, 1 g of the yellow dispersion dye composition of Examples 1 to 6 and Comparative Examples 1 to 3, adjusted to pH 4.0 to pH 4.5 by 80% acetic acid at room temperature, and 0.5 g / l of leveling agent In a liquid ratio of 1:20. The dyeing is carried out for 60 minutes by heating to 60 ℃ at a rate of 3 ℃ / min and then to 130 ℃ at a rate of 1 ~ 2 ℃ / min. The salt solution is then cooled to 40 ° C. and the dyed polyester fabric washed, followed by a bath comprising 5 ml / l 30% sodium hydroxide solution, 2 g / l sodium hydrogen sulfate solution and 1 g / l commercial detergent Reduction and washing at a temperature of 70 ~ 80 ℃ for 20 minutes in. The processed dyeings are then washed with water and dried.
일광 견뢰도는 SAE J1885방법으로 진행하여 하기 표 1에 나타내었다.
Daylight fastness is shown in Table 1 by the SAE J1885 method.
<표 1>TABLE 1
상기 표 1에서 보는 바와 같이, 특정 함량을 가지는 제조예 1 내지 4의 화합물들의 특정 조합을 포함하는 실시예 1 내지 6의 황색 계열의 분산염료 조성물을 이용하여 폴리에스테르를 염색하는 경우, 비교예 1 내지 3의 분산염료 조성물을 이용한 경우보다, 우수한 제품 농도와 높은 염착률을 나타내며, 또한, 고일광 견뢰도를 보이는 것을 확인할 수 있다.
As shown in Table 1, in the case of dyeing the polyester using the yellow-based dispersion dye composition of Examples 1 to 6 containing a specific combination of compounds of Preparation Examples 1 to 4 having a specific content, Comparative Example 1 Compared with the case of using the disperse dye composition of 3 to 3, it can be seen that it shows excellent product concentration and high dyeing rate, and also exhibits high daylight fastness.
[실험예 2] 베이지 계열의 분산염료 조성물의 제조상기 실시예 7 내지 12 및 비교예 4 내지 6의 분산염료 조성물을 상기 실험예 1과 동일한 방법을 사용하여 하기 표 2에 나타내었다.Experimental Example 2 Preparation of Beige-Based Disperse Dye Compositions The disperse dye compositions of Examples 7 to 12 and Comparative Examples 4 to 6 were shown in Table 2 below using the same method as in Experimental Example 1.
<표 2><Table 2>
상기 표 2에서 보는 바와 같이, 특정 함량을 가지는 제조예 1 내지 6의 화합물들의 특정 조합을 포함하는 실시예 7 내지 12의 베이지 계열의 분산염료 조성물을 이용하여 폴리에스테르를 염색하는 경우, 비교예 4 내지 6의 분산염료 조성물을 이용한 경우보다, 우수한 제품 농도와 높은 염착률을 나타내며, 또한, 고일광 견뢰도를 보이는 것을 확인할 수 있다.
As shown in Table 2, when dyeing the polyester using the dye-based dispersion dye composition of Examples 7 to 12 containing a specific combination of compounds of Preparation Examples 1 to 6 having a specific content, Comparative Example 4 Compared with the case of using the disperse dye composition of 6 to 6, it can be seen that it shows excellent product concentration and high dyeing rate, and also exhibits high daylight fastness.
[실험예 3] 그레이 계열의 분산염료 조성물의 제조 Experimental Example 3 Preparation of Gray-Based Disperse Dye Composition
상기 실시예 13 내지 18 및 비교예 7 내지 9의 분산염료 조성물을 상기 실험예 1과 동일한 방법을 사용하여 하기 표 3에 나타내었다.The dispersion dye compositions of Examples 13 to 18 and Comparative Examples 7 to 9 are shown in Table 3 below using the same method as Experimental Example 1.
<표 3><Table 3>
상기 표 3에서 보는 바와 같이, 특정 함량을 가지는 제조예 1 내지 6의 화합물들의 특정 조합을 포함하는 실시예 13 내지 18의 그레이 계열의 분산염료 조성물을 이용하여 폴리에스테르를 염색하는 경우, 비교예 7 내지 9의 분산염료 조성물을 이용한 경우보다, 우수한 제품 농도와 높은 염착률을 나타내며, 또한, 고일광 견뢰도를 보이는 것을 확인할 수 있다.
As shown in Table 3, when dyeing the polyester using a gray-based dispersion dye composition of Examples 13 to 18 containing a specific combination of compounds of Preparation Examples 1 to 6 having a specific content, Comparative Example 7 Compared with the case of using the disperse dye composition of 9 to 9, it can be seen that exhibits excellent product concentration and high dyeing rate, and also exhibits high daylight fastness.
본 발명이 속한 분야에서 통상의 지식을 가진 자라면 상기 내용을 바탕으로 본 발명의 범주 내에서 다양한 응용 및 변형을 행하는 것이 가능할 것이다.
Those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims.
Claims (8)
(1)
(2)
(3)
(4).20 to 70% by weight of the compound of Formula 1 and 20 to 70% by weight of the compound of Formula 2, and 5 to 40% by weight of one or more compounds selected from the group consisting of the compounds of Formulas 3 and 4 Disperse dye composition, characterized in that to express:
(One)
(2)
(3)
(4).
(5)
(6).Dispersion dye composition comprising a beige-based color comprising 30 to 60% by weight of the composition according to claim 1, 10 to 40% by weight of the compound of Formula 5, and 10 to 40% by weight of the compound of Formula 6 :
(5)
(6).
8. The method of claim 7, wherein the blended fibers comprise polyester fibers and cellulose fibers.