KR20120008135A - 접착증진제를 함유하는 저온소성용 열경화성 전극 페이스트 - Google Patents
접착증진제를 함유하는 저온소성용 열경화성 전극 페이스트 Download PDFInfo
- Publication number
- KR20120008135A KR20120008135A KR1020100068806A KR20100068806A KR20120008135A KR 20120008135 A KR20120008135 A KR 20120008135A KR 1020100068806 A KR1020100068806 A KR 1020100068806A KR 20100068806 A KR20100068806 A KR 20100068806A KR 20120008135 A KR20120008135 A KR 20120008135A
- Authority
- KR
- South Korea
- Prior art keywords
- thermosetting
- electrode paste
- silane
- weight
- electrode
- Prior art date
Abstract
본 발명은 접착증진제를 함유하는 저온소성용 열경화성 전극 페이스트에 관한 것으로서, 본 발명에 따른 전극 페이스트는 우수한 부착력, 고해상도, 낮은 접촉저항, 우수한 보관 안정성 및 전기 비저항을 나타내어 무선인식태그, 인쇄 회로 기판, 태양전지 등 폭넓은 분야에 적용 가능하다.
Description
본 발명은 접착증진제를 함유하는 저온소성용 열경화성 전극 페이스트에 관한 것으로서, 본 발명에 따른 전극 페이스트는 우수한 부착력, 고해상도, 낮은 접촉저항, 우수한 보관 안정성 및 전기 비저항을 나타낼 수 있다.
종래에는 도전성 분말, 에폭시 또는 우레탄 등의 열경화 수지, 단량체, 경화제, 및 용매 등을 혼합하여 전극 페이스트를 제조하였다. 그러나 이러한 전극 페이스트를 가열 경화하여 생성된 전극은 세라믹기판, 실리콘기판에서 밀착성이 우수하지 못하는 단점이 있다. 또한, 종래 전극 페이스트의 제조에 사용되었던 폴리이소시아네이트(polyisocyanate)의 경우, 가열 경화에 의하여 생성되는 우레탄(urethane) 화합물은 반응속도가 느려 장시간의 경화시간을 필요로 할 뿐만 아니라 세라믹 기판에 대해 밀착성이 저하되는 문제점이 있다.
또한, 아민계 경화제를 사용하는 경우 상온(25 ℃) 보관 중에 점차 경화가 진행되어 페이스트 점도가 상승하는 안정성 문제를 나타내기도 한다. 에폭시 수지나 단량체를 사용하는 경우, 열 경화반응시 페이스트의 급격한 수축에 의해 패턴 전극의 갈라짐 현상이 발생하거나 기재(또는 기판)로부터 벗겨지는 단점이 있다. 또한, 소성과정에서 부여되는 열에너지(200-300 ℃ 미만)에 의해 수지의 산화분해가 발생하여 전극의 탈락현상이 일어나는 문제가 있었다.
이에, 본 발명자들은 상술한 문제점을 해결하고자 예의 연구를 계속한 결과, 열경화성 올리고머, 열경화 개시제 및 티올계(-SH) 또는 실란계(-Si-) 접착증진제의 특정 조합을 포함하는 전극 페이스트가 우수한 보관 안정성을 가져오고 고해상도 패턴 구현에 유리하며 내부 응력을 줄이고 기판과의 부착성을 높이는 데에 효과적임을 발견하고 본 발명을 완성하게 되었다.
따라서, 본 발명의 목적은 우수한 부착력, 고해상도, 낮은 접촉저항, 우수한 보관 안정성 및 전기 비저항을 나타내어 무선인식태그(radio frequency identification: RFID), 인쇄 회로 기판(printed circuit board: PCB), 태양전지(solar cell) 등 폭넓은 분야에 적용 가능한 저온소성용 열경화성 전극 페이스트를 제공하는 것이다.
상기 목적을 달성하기 위해 본 발명은,
(a) 도전성 분말;
(b) 열경화성 올리고머;
(c) 열경화 개시제;
(d) 바인더; 및
(e) 접착증진제
를 포함하는 저온소성용 열경화성 전극 페이스트를 제공한다.
또한, 본 발명은 상기 저온소성용 열경화성 전극 페이스트를 기재 위에 인쇄한 후 건조 및 소성하여 형성된 전극; 및 상기 전극을 포함하는 전자재료를 제공한다.
본 발명에 따른 저온소성용 열경화성 전극 페이스트는 하기와 같은 효과를 나타낸다:
첫째, 경화도가 우수하여 저온 (300 ℃ 이하)에서도 우수한 전기 비저항 특성을 나타낸다.
둘째, 건조온도 (100-200 ℃)에서 페이스트의 경화가 빨리 진행되기 때문에 전극 선폭의 퍼짐현상이 없다.
셋째, 페이스트 내 티올계 또는 실란계 화합물이 도전성 분말 주위를 -S- 또는 -Si- 형태로 감싸고 있다가 열을 가하면 방향족 탄소 고리가 끊어지면서 기판과의 부착력을 증대시킨다.
넷째, 페이스트 내 티올계 또는 실란계 화합물이 도전성 분말 주위를 감싸고 있어 분산성이 좋으며, 점도 변화가 적어 보관 안정성이 우수하다.
다섯째, 태양전지의 전극 형성에 이용한 경우, 유리프릿이 없는 페이스트이기 때문에 형성된 전극에서의 접촉 저항을 감소시킬 수 있다.
여섯째, 페이스트의 레올로지 특성이 우수하여 높은 종횡비 (aspect ratio)를 구현할 수 있다.
일곱째, 폴리머, 유리, 금속, 세라믹 등 기판 재질에 관계없이 높은 접착력을 나타내어 무선인식태그(radio frequency identification: RFID), 인쇄 회로 기판(printed circuit board: PCB), 태양전지(solar cell) 등 폭넓은 응용분야에 적용 가능하다.
본 발명의 전극 페이스트는 양이온 또는 라디칼(특히 아조비스(azobis)계) 열경화 개시제를 포함함으로써 상온(25 ℃) 보관 중에 경화반응이 발생하지 않고 건조온도(100 ℃~200 ℃) 영역에서부터 경화반응이 진행되므로 전극패턴의 퍼짐현상이 억제되어 고해상도 패턴 구현에 매우 유리하다. 또한, 본 발명의 전극 페이스트는 열경화성 올리고머를 포함함으로써 전극 형성시 전극 페이스트의 수축에 의해 발생하는 내부 응력을 줄일 수 있고, 단량체에 비해 많은 작용기를 포함하는 열경화성 올리고머로 인해 같은 양의 개시제 사용시 경화시간을 단축시킬 수 있다. 나아가, 본 발명의 전극 페이스트는 기판과의 부착성을 높이고자 티올계(-SH) 화합물 또는 실란계(-Si-) 접착증진제를 사용하였다. 이 접착증진제는 페이스트 내 도전성 분말의 표면에 -S- 혹은 -Si- 형태로 결합하고 있다가 열을 가하면(저온: 200 ℃ 이내) 방향족 탄소화합물의 고리가 끊어지면서 기판에 화학적 결합을 함으로써 부착력을 증진하는 효과가 있다. 따라서, 기판을 별도로 표면 개질할 필요가 없으며, 열을 가하기 전에는 전극 내 분산성도 좋고 상온에서도 안정한 상태를 유지한다. 또한, 전극 도막의 강도가 우수하고 치밀하여 기판 부착력을 증진시켜 전극과 솔더리본의 결합력도 증진시키는 장점이 있다. 이로써, 전극 내 기판과의 부착력을 증진시켜 페이스트의 품질 개선 및 공정시간 단축에 의한 생산성을 향상시킬 수 있다.
즉, 본 발명에 따른 저온소성용 열경화성 전극 페이스트는,
(a) 도전성 분말;
(b) 열경화성 올리고머;
(c) 열경화 개시제;
(d) 바인더; 및
(e) 접착증진제
를 포함한다.
바람직하게는, 본 발명에 따른 전극 페이스트는 (a) 도전성 분말 30-95 중량%, (b) 열경화성 올리고머 1-30 중량%, (c) 열경화 개시제 0.01-10 중량%, (d) 바인더 0.1-30 중량% 및 (e) 접착증진제 0.1-30 중량% 를 포함한다.
본 발명의 '저온소성용 열경화성 전극 페이스트'는 적층 구조체로 이루어지는 전자 디바이스나, 단층 또는 다층으로 이루어지는 배선판과 같은 회로형성용 재료로서 사용되는 페이스트를 포함한다. 따라서, 태양전지, 디스플레이 소자 및 RFID 소자 등에 사용되는 전극뿐만 아니라 이들 장치에 사용되는 전기배선도 여기에 해당한다.
이하 각 성분에 대하여 상세히 설명한다.
(a) 도전성 분말
본 발명에서 사용가능한 분말로는 금(Au), 은(Ag), 니켈(Ni), 구리(Cu) 등 통상 전극의 제조시 도전성 분말로서 사용되는 것이라면 특별한 제한없이 사용할 수 있다. 바람직하게는 은 분말을 사용할 수 있다.
상기 도전성 분말은 평균입경은 0.05 내지 10 ㎛의 분말을 사용할 수 있으며, 바람직하게는 0.1 내지 5 ㎛의 분말을 사용할 수 있다. 상기 도전성 분말은 다양한 입자 크기와 형상을 갖는 2종 이상 혼합하여 사용할 수 있으며, 이 경우 평균입경이 0.05-2 ㎛의 분말과 평균입경이 2-10 ㎛의 평균입경을 갖는 분말을 2종 이상 혼합하여 사용할 수 있다. 상기 도전성 분말의 형상은 구형, 비구형 그리고, 판상(플레이크상)을 사용할 수 있으며 이들을 2종 이상 혼합하여 사용할 수 있다.
다양한 입자 형상과 크기를 갖는 금속 분말을 혼합하여 사용하는 것이 인쇄의 정밀성을 높이고, 태양전지에 적용시 태양전지의 Fill Factor(이하 "FF"라 한다)를 크게 향상시켜 효율을 높일 수 있기 때문에 바람직하다.
이러한 도전성 분말은 고형분 중에 30 내지 95 중량%로 포함될 수 있다. 상기 금속분말의 양이 30 중량% 미만일 때는 페이스트의 점도가 너무 낮아 인쇄하여 고해상도의 전극패턴을 형성하는 것이 어려우며, 기판에 전극이 형성 되더라도 전극의 퍼짐 현상이 매우 심하여 패턴의 종횡비가 매우 낮아지며, 또한 금속분말의 양이 95 중량%를 초과할 때는 점도가 매우 높아 인쇄가 용이하지 않기 때문에 기판 위에서의 전극 형성이 어려울 뿐만 아니라, 유기물 함량이 낮아 기판과의 접착력이 좋지 않아 건조 후 전극의 탈락 현상이 생긴다.
(b) 열경화성 올리고머
본 발명에서 사용가능한 열경화성 올리고머로는 아크릴계 올리고머, 에폭시 아크릴레이트계 올리고머(에폭시 아크릴레이트 공중합체), 폴리에스테르 아크릴레이트계 올리고머, 우레탄 아크릴레이트계 올리고머 등을 단독 또는 2종 이상 혼합하여 사용할 수 있다. 상기 아크릴계 올리고머의 중량평균분자량은 500-1500의 범위가 적합하다.
상기 아크릴계 올리고머로는 다관능 디펜타에리스리톨헥사아크릴레이트 올리고머, 글리시딜메타아크릴레이트, (메타)아크릴산, (메타)아크릴산 알킬 에스테르, 폴리에틸렌 글리콜 (메타)아크릴레이트, 프로필렌 글리콜 (메타)아크릴레이트를 사용할 수 있다. 또한, 펜타에리스리톨트리 (메타)아크릴레이트, 펜타에리스리톨펜타 (메타)아크릴레이트, 디펜타에리스리톨헥사 (메타)아크릴레이트를 이용한 공중합체를 사용 할 수도 있다.
또한 상기 아크릴계 올리고머를 포함하는 혼합물로는 상업적으로 시판되는 EBECRYL 1200(제품명, 싸이텍사, 미국), HSOL-500(제품명, 한수화학, 한국)등을 사용할 수 있다.
상기 에폭시 아크릴레이트계 올리고머를 포함하는 혼합물로는 상업적으로 시판되고 있는 Miramer ME 2010(제품명, 미원 상사, 한국), CN 150/80(제품명, Sartomer 사, 미국), EPA 1300(제품명, 한수화학, 한국) 또는 3020-A80(제품명, AGI 사, 미국), 가교밀도가 높은 비스페놀A 디아크릴레이트 올리고머 등을 사용할 수 있다.
상기 열경화성 올리고머의 함량은 1-30 중량%가 포함될 수 있다. 상기 열경화성 올리고머 함량이 1 중량% 미만일 경우에는 경화반응이 충분치 않아 기판과의 부착력이 불충분하며, 올리고머의 함량이 30 중량%를 초과할 경우에는 올리고머의 잔존으로 인하여 전기적인 절연체의 역할을 하게 되어 접촉저항을 높게 한다.
(c) 열경화 개시제
본 발명에서 사용가능한 열경화 개시제로는 양이온 또는 라디칼 개시제를 사용할 수 있다.
상기 양이온 개시제는 올리고머의 열경화를 저온에서 고속으로 수행되도록 한다. 이의 구체적인 예로는 암모늄/안티몬 헥사플루오라이드, 트리아릴설포늄 헥사플루오로안티모네이트염, 트리아닐설포늄 헥사플루오로안티모네이트, (톨리큐밀) 아이오도늄 테트라키스(펜타플루오로페닐)보레이트, 비스(도데실페닐)아이오도늄 헥사플루오로안티모네이트, 아이오도늄 (4-메틸페닐)(4-(2-메틸프로필)페닐) 헥사플루오로포스페이트, 옥틸 디페닐아이오도늄 헥사플루오로안티모네이트, 디아릴아이오도늄염, 벤질설포늄염, 페나실설포늄염, N-벤질피리디늄염, N-벤질피라지늄염, N-벤질암모늄염, 포스포늄염, 하이드라지늄염, 암모늄 보레이트염, 트리페닐 메틸 클로라이드 및 이들의 혼합물을 들 수 있으며, 바람직하게는 암모늄/안티몬 헥사플루오라이드, 트리아닐설포늄 헥사플루오로안티모네이트, 트리페닐 메틸 클로라이드 등을 들 수 있다.
상기 라디칼 개시제의 구체적인 예로는, 벤조일퍼옥사이드(benzoylperoxide), 라우로일퍼옥사이드(lauroylperoxide), 디아세틸퍼옥사이드(diacetylperoxide), 또는 디-t-부틸퍼옥사이드(di-tert-butylperoxide) 등의 퍼옥사이드계 화합물(peroxides); 큐밀하이드로퍼옥사이드(cumylhydroperoxide) 등의 하이드로 퍼옥사이드계 화합물(hydroperoxides); 및 시아노(-CN)관능기를 가지는 α,α'-아조비스이소부티로니트릴(α,α'-azobisisobutyronitrile, AIBN), 2,2'-아조비스[2-메틸-N-(2-(1-히드록시부틸))피로피온아미드], 2,2'-아조비스[2-메틸-N-(2-히드록시에틸)프로피온아미드], 2,2'-아조비스[N-부틸-2-메틸프로피온아미드], 2,2'-아조비스[N-시클로헥실-2-메틸프로피온아미드] 및 디메틸-2,2'-아조비스(2-메틸프로피오네이트) 등의 아조계 화합물 등을 들 수 있다. 이중에서도 아조비스(cyclohexane-carbonitrile)계 화합물은 100 ℃ 이상에서 분해되어 반응하기 때문에 건조온도(100-200 ℃ 미만) 영역에서부터 경화반응이 진행되어 전극 패턴의 퍼짐현상이 억제되고 그 결과 고해상도 패턴을 구현할 수 있으며, 또한 상온에서는 경화반응이 억제되어 25-40 ℃ 보관 조건하에서 점도변화가 없어 보다 바람직하다.
상기 열경화 개시제의 함량은 0.01 내지 10 중량%가 포함될 수 있다. 상기 열경화 개시제의 함량이 0.01 중량% 미만일 경우 올리고머와의 가교화가 충분하지 않아 미반응 올리고머에 의한 경화도 저하가 발생하게 되며, 개시제의 함량이 30 중량%를 초과할 경우 불필요한 개시제의 잔존으로 접촉저항을 높게 할 뿐만 아니라 비경제적이다.
(d) 바인더
본 발명에서 사용가능한 바인더로는 에틸셀룰로오스, 메틸셀룰로오스, 니트로셀룰로오스, 하이드록시셀룰로오스 등의 셀룰로오스 유도체, 이소부틸메타아크릴레이트, n-부틸 메타아크릴레이트, 또는 이들의 공중합체인 아크릴계 수지를 들 수 있다.
또한 상업적으로 시판되는 아크릴계 수지는 ELVACITE 2045(제품명, ELVACITE사, 미국), ELVACITE 2046(제품명, ELVACITE사, 미국) 등을 사용할 수 있다.
본 발명에서 상기 바인더의 함량은 0.1-30 중량%를 포함할 수 있다. 상기 바인더 함량이 0.1 중량% 미만일 경우에는 인쇄성이 좋지 못하여 전극형성에 어려움이 있으며, 기판과의 부착력도 좋지 못하다. 또한 바인더 함량이 30 중량%를 초과할 경우에는 소성 후 바인더의 잔존량 증가로 인하여 전도성 분말간의 밀착도 저하를 야기시켜 비저항 특성을 저하시키고, 태양전지 셀에서의 접촉저항을 높여 전지의 효율을 떨어뜨린다.
(e) 접착증진제
본 발명에서 사용가능한 접착증진제는 바람직하게는 티올계 또는 실란계 방향족 탄소화합물일 수 있다. 이 접착증진제는 페이스트 내 도전성 분말의 표면에 -S- 혹은 -Si- 형태로 결합하고 있다가 열을 가하면(저온: 200 ℃ 이내) 방향족 탄소화합물의 고리가 끊어지면서 기판에 화학적 결합을 함으로써 부착력을 증진하는 효과가 있다. 따라서, 기판을 별도로 표면 개질할 필요가 없으며, 열을 가하기 전에는 전극 내 분산성도 좋고 상온에서도 안정한 상태를 유지한다.
상기 접착증진제의 구체적인 예로는 티올계 화합물로서 부탄티올, 펜탄티올 및 이들의 혼합물을 들 수 있고; 알콕시 실란계 화합물로서 비닐트리메톡시실란, 비닐트리에톡시실란, 비닐부틸렌트리에톡시실란, 비닐트리(베타-메톡시)실란, 비닐트리(베타-에톡시)실란, 아크릴록시프로필트리메톡시실란, 아크릴록시프로필트리에톡시실란, 아크릴록시프로필메틸디메톡시실란, 감마-메타아크릴록시프로필트리메톡시실란, 감마-메타아크릴록시프로필트리에톡시실란, 감마-메타아크릴록시프로필메틸디메톡시실란, 감마-메타아크릴록시프로필메틸디이소프로폭시실란, 감마-메타아크릴록시카비톨트리메톡시실란테트라메톡시실란, 테트라에톡시실란, 테트라프로폭시실란, 테트라이소프로폭시실란, 테트라-n-부톡시실란, 테트라-sec-부톡시실란, 테트라-tert-부톡시실란, 메틸트리메톡시실란, 메틸트리에톡시실란, 메틸트리부톡시실란, 에틸트리메톡시실란, 에틸트리이소프록폭시실란, 에틸트리부톡시실란, 부틸트리메톡시실란, 페닐트리메톡시실란, 3-메틸트리메톡시실란, 디메틸디메톡시실란, 디페닐디메톡시실란, 디부틸디메톡시실란, 트리메딜메톡시실란, 트리메틸에톡시실란, 트리부틸메톡시실란, 트리부틸에톡시실란, 트리플루오로메틸트리메톡시실란, 트리플루오로메틸트리에톡시실란, 트리플루오로프로필트리메톡시실란, 트리플루오로프로필트리에톡시실란, 노나플루오로부틸에틸트리메톡시실란, 노나플루오로부틸에틸트리에톡시실란, 노나플루오로헥실트리메톡시실란, 노나플루오로헥실트리에톡시실란, 트리데카플루오로옥틸트리메톡시실란, 트리데카플루오로옥틸트리에톡시실란, 헵타데카플루오로데실트리메톡시실란, 헵타데카플루오로데실트리에톡시실란, 헵타데카플루오로데실트리이소프로필실란, 3-트리메톡시실릴프로필펜타데카플루오로옥테이트, 3-트리에톡시실릴프로필펜타데카플루오로옥테이트, 3-트리메톡시실릴프로필펜타데카플루오로옥틱아미드, 3-트리에톡시실릴프로필펜타데카플루오로옥틱아미드, 2-트리메톡시실릴에틸펜타데카플루오로데실술피드, 2-트리에톡시실릴에틸펜타데카플루오로데실술피드, 펜타플루오로페닐트리메톡시실란, 펜타플루오로페닐트리에톡시실란, 4-(퍼플루오로토릴)트리메톡시실란, 4-(퍼플루오로토릴)트리에톡시실란, 디메톡시비스(펜타플루오로페닐)실란, 디에톡시비스(4-펜타플루오로토릴)실란, 2-(3,4-에폭시사이클로헥실)에틸트리메톡시실란 및 이들의 혼합물을 들 수 있으며; 상기 알콕시기 대신에 비닐기, 에폭시기, 메타크릴기, 머캡토기 또는 이소시아네이트기 등의 치환기를 1개 이상 갖는 실란계 화합물도 사용할 수 있다.
본 발명에서 상기 접착증진제는 0.1-30 중량%의 양으로 포함될 수 있다. 상기 접착증진제의 함량이 0.1 중량% 미만일 경우에는 목적하는 효과를 볼 수 없고, 30 중량%를 초과할 경우에도 더 이상 부착력이 증가하지 않는다.
(f) 용매
상기 (a)-(e)의 성분들은 용매 중에서 혼합 분산되어 사용된다.
이때 사용가능한 용매로는 부틸카비톨아세테이트, 부틸카비톨, 부틸 셀루솔브, 프필렌글리콜모노메틸에테르, 디프로필렌글리콜모노메틸에테르, 프로필렌글리콜모노메틸에테르프로피오네이트, 에틸에테르프로피오네이트, 테르피네올, 텍사놀, 프로필렌글리콜모노메틸에테르아세테이트, 디메틸아미노 포름알데히드, 메틸에틸케톤, 감마부티로락톤, 에틸락테이트, 에틸렌 글리콜, N-메틸 피롤리돈, N-에틸 피롤리돈, N-부틸 피롤리돈, 테트라 하이드로퓨란 및 셀루솔브 유도체 등을 단독 또는 2 종 이상 혼합하여 사용할 수 있다. 바람직하게는 부틸카비톨아세테이트, 테르피네올 또는 이들의 혼합물을 사용할 수 있다.
상기 용매는 (a)-(e)의 성분들을 제외한 잔량을 포함할 수 있다.
(g) 모노머
본 발명에 따른 전극 페이스트는 상기 성분 외에 모노머를 선택적으로 더 포함할 수 있다.
상기 모노머로는 (메타)아크릴계 모노머로서 메타아크릴레이트 모노머, 또는 에폭시 모노머, 또는 이들의 혼합물을 사용할 수 있으며, 구체적인 예로는 메틸메타크릴레이트, 에틸메타크릴레이트, 트리시클로데칸디메타놀디메타크릴레이트, 메틸아크릴레이트, 에틸아크릴레이트, 이소프로필아크릴레이트, 이소보닐아크릴레이트, 아크릴로일옥시에틸숙시네이트, 페녹시에틸렌글리콜아크릴레이트, 페녹시에틸아크릴레이트,2-하이드록시에틸 아크릴레이트, 하드록시프로필 아크릴레이트, 디에틸렌 글리콜 디메타아크릴레이트, 아릴 메타아크릴레이트, 에틸렌 글리콜 디메타아크릴레이트, 디에틸렌 글리콜 디메타아크릴레이트, 트리에틸렌 글리콜 디메타아크릴레이트, 테트라에틸렌 글리콜 디메타아크릴레이트, 글리세롤 디메타아크릴레이트, 펜타메틸 기페리딜 메타아크릴레이트, 라우릴 아크릴레이트, 테트라하이드로퍼퓨릴 아크릴레이트, 하이드록시 에틸 아크릴레이트, 하이드록시 프로필 아크릴레이트, 이소보닐 아크릴레이트, 헥산디올 디아크릴레이트, 1,6-헥산디올 디아크릴레이트, 디에틸렌 글리콜 디아크릴레이트, 트리프로필렌 글리콜 디아크릴레이트, 디프로필렌 글리콜 디아크릴레이트, 폴리에틸렌 글리콜 디아크릴레이트, 네오펜틸 글리콜 디아크릴레이트, 트리메틸올프로판 트라아크릴레이트, 네오펜틸 글리콜 디아크릴레이트, 에톡시레이티드 트리메틸올프로판 트리아크릴레이트, 프로폭시레이티드 트리메틸올프로판 트리아크릴레이트, 트리메틸올프로판 에폭실레이트 트리아크릴레이트, 트리메틸올프로판 트리메타아크릴레이트, 펜타에리스리톨 트리아크릴레이트, 펜타에리스리톨 테트라아크릴레이트, 디펜타에리스리톨 헥사아크릴레이트, 글리세린프로폭시레이티드 트리아크릴레이트 및 메톡시에틸렌글리콜아크릴레이트로 이루어진 군에서 선택되는 1종 이상인 것이 바람직하다.
상기 모노머는 20 중량% 이하로 사용되는 것이 바람직하다. 상기 함량 범위를 벗어날 경우 반응에 참여하지 못한 모노머가 불순물로 잔존하여 경화 속도가 저하될 우려가 있다. 바람직하기로는 0.01 내지 15 중량%로 포함되는 것이 좋다.
(h) 기타 첨가제
상기 외에도 본 발명에 따른 전극 페이스트는 통상적으로 페이스트에 포함될 수 있는 첨가제들을 필요에 따라 더욱 포함할 수 있다. 상기 첨가제로의 예로는 증점제, 안정화제, 분산제, 탈포제, 계면활성제 및 이들의 혼합물을 들 수 있으며, 이들 성분들은 0.1-5 중량%로 사용되는 것이 바람직하다.
상기와 같은 조성을 갖는 본 발명의 전극 페이스트는 상기 기재한 필수성분과 임의의 성분을 소정의 비율에 따라 배합하고, 이를 블렌더 또는 3축 롤 등의 혼련기로 균일하게 분산하여 얻어질 수 있다.
바람직하기로는 본 발명의 페이스트는 브룩필드(Brookfield) HBT 점도계를 사용하여 #51 스핀들로서 온도 25 ℃하에서 shear rate 3.84 sec-1조건으로 측정하는 경우 1 내지 300 Pa . S의 점도를 가질 수 있다.
본 발명에 따른 전극 페이스트는 접착증진제의 작용에 의해 기판과의 부착력이 우수하고, 건조온도 (100 ℃-200 ℃ 미만)에서 페이스트가 빨리 경화되어 전극의 퍼짐현상이 없기 때문에 고해상도(high resolution)를 나타낼 수 있다. 또한 건조온도 (200 ℃ 미만)에서 경화도가 우수하여 저온(300 ℃ 이하)에서도 우수한 전기 비저항 특성을 얻을 수 있다. 이에 따라 본 발명의 전극 페이스트는 폭넓은 분야에 적용 가능하다. 이중에서도 태양전지 분야에 적용했을 경우 유리프릿이 없는 페이스트로 소성 후 은 분말의 밀집성이 높으므로 전극의 접촉 저항을 감소시킬 수 있으며, 특히 비정질/결정질 실리콘 이종접합 태양전지에 적용할 경우 효과가 더욱 크다.
본 발명은 또한 상기 전극 페이스트를 기재 위에 인쇄한 후 건조 및 소성하여 형성된 전극, 및 상기 전극을 포함하는 전자재료를 제공한다. 상기 전자재료는 무선인식태그, 인쇄 회로 기판, 또는 태양전지일 수 있으며, 바람직하기로 태양전지이며, 더욱 바람직하기는 비정질/결정질 실리콘 이종접합 태양전지이다.
본 발명의 전자재료 전극 형성시, 본 발명의 상기 저온소성용 열경화성 전극 페이스트를 사용하는 것을 제외하고는, 기재, 인쇄, 건조 및 소성은 통상적으로 전자재료의 전극 제조에 사용되는 방법들이 사용될 수 있음은 물론이다. 일예로 상기 기재는 Si 기판일 수 있으며, 상기 전극은 실리콘 태양전지의 전면, 후면 전극일 수 있으며, 상기 인쇄는 스크린 인쇄일 수 있으며, 상기 건조는 100-250 ℃에서 이루어질 수 있으며, 상기 소성은 150-300 ℃의 저온에서 10분 내지 60분간 이루어지는 저온소성을 하는 것이 좋으며, 상기 인쇄는 10 내지 50 ㎛의 두께로 인쇄를 하는 것이 좋다.
이와 같이 형성된 본 발명의 전극은 정밀성이 높으며, 이 전극을 포함하는 태양전지는 고효율, 고해상도로서 특히 저온소성에 적합하여 양상성이 뛰어나며, 비정질/결정질 실리콘 이종접합 태양전지에 적용할 경우 효과가 더욱 좋은 장점이 있다.
이하, 본 발명의 이해를 돕기 위하여 바람직한 실시예를 제시하나, 하기 실시예는 본 발명을 예시하는 것일 뿐 본 발명의 범위가 하기 실시예에 한정되는 것은 아니다.
실시예 1 및 2, 및 비교예 1 및 2
하기 표 1에 기재된 성분 및 함량으로 혼합한 후 3롤 혼련기로 혼합 분산시켜 전극 페이스트를 제조하였다.(단위는 중량부이다)
실시예 1 | 실시예 2 | 비교예 1 | 비교예 2 | ||
도전성 분말 |
은 분말 | 70 | 85 | 30 | 85 |
바인더 | 셀룰로오스계 수지 | 6 | 2 | - | 2 |
아크릴계 수지 | - | 1 | - | - | |
에폭시 수지 | - | - | 10 | 5 | |
열경화성 올리고머 | 아크릴계와 에폭시계 올리고머 | 7 | 5 | - | - |
모노머 | 아크릴계 모노머 | - | - | 10 | - |
경화제 | 아민계 | - | - | 1 | 0.5 |
열경화 개시제 |
라디칼 개시제 | 1 | 1 | 1 | - |
용매 |
테르피네올 | 13 | 3 | 25 | 4 |
부틸카비톨 아세테이트 |
2 | 2.5 | 20 | 2 | |
접착 증진제 |
티올계 화합물 | 1 | - | - | - |
실란계 화합물 | - | 0.5 | - | - | |
첨가제 | 탈포제 | - | - | 2 | 0.5 |
분산제 | - | - | 1 | 1 |
상기 표 1에 기재된 구체적인 성분명은 다음과 같다.
- 은 분말: 평균입도 2.5 ㎛를 갖는 판상형 은 분말
- 셀룰로오스계 수지: 하이드록시셀룰로오스
- 아크릴계 수지: ELVACITE 2045
- 에폭시 수지: 비스페놀 A계 수지
- 아크릴계와 에폭시계 올리고머: EBECRYL-1200와 Miramer ME 2010을 4:1 중량비율로 혼합
- 아크릴계 모노머: TMPTA와 HDDA를 7:3 중량비율로 혼합
- 아민계 경화제: 폴리아마이드
- 라디칼 개시제: 아조비스이소부티로니트릴(azobisisobutyronitrile)
- 티올계 화합물: 부탄티올 : 펜탄티올 = 5 : 5 중량비의 혼합물
- 실란계 화합물: 2-(3,4-에폭시사이클로헥실)에틸트리메톡시실란
- 탈포제: 실리콘계 탈포제
- 분산제: 알킬올 암모늄염
상기 실시예 1 및 2, 및 비교예 1 및 2에서 제조된 전극 페이스트에 대하여 하기와 같은 방법으로 비저항, 기판 부착력, 전극/솔더리본 부착력, 해상도, 접촉저항, 종횡비 및 점도 변화율을 각각 측정하였다. 그 결과를 하기 표 2에 나타내었다.
1) 비저항(*10-5Ω.cm)
전극 페이스트를 각각 기재에 인쇄한 후 180 ℃에서 15분, 200 ℃에서 15분 및 220 ℃에서 15분 으로 경화시킨 후 4-포인트 프로브(4-point probe)를 사용하여 비저항을 측정하였다.
2) 기판 부착력
격자부착성 평가(ASTM D3359)에 의거하여, 기재 위에 인쇄되어 경화된 페이스트에 crosscut knife로 100개의 격자 무늬를 만들어서 금속부착력 전용 테이프(3M, #610)를 붙였다가 띄어내어 떨어진 격자수를 기록하였다.
3) 해상도(㎛)
선폭이 60-110 ㎛ 패턴을 가지는 해상도 마스크로 인쇄, 건조, 소성한 후 패턴의 선폭변화율이 10% 이내인 경우를 해상도로 기록하였다.
4) 접촉 저항(mΩ.cm)
전극 페이스트를 태양전지 셀(cell)의 후면에 스크린 프린팅기법으로 인쇄하고 열풍식 건조로를 사용하여 건조시켰다. 그리고, 전면에 선폭 110 ㎛의 전극패턴을 인쇄하여 160 ℃에서 5분간 건조시켰다. 상기 과정으로 제조된 셀(cell)을 소성로를 사용하여 220 ℃에서 15분간 소성하였다. 이렇게 제조된 cell에 대해 코어스캔(Correscan)을 이용하여 접촉 저항을 측정하였다.
5) 종횡비(%)
소성 후 전극패턴의 높이 및 패턴 선폭을 각각 SEM으로 측정하고, 패턴의 높이/패턴선폭 비율을 구하여 종횡비(%)를 기록하였다.
6) 점도 변화율(%)
상기 실시예 1 내지 4, 및 비교예 1, 2에서 제조된 전극 페이스트를25 ℃에서 1개월간 보관후 점도 변화를 브룩필드(Brookfield) HBT 점도계를 사용하여 #51 스핀들로서 온도 25 ℃하에서 shear rate 3.84 sec-1조건으로 측정하여 점도 변화율을 관찰하였다.
7) 전극/솔더리본 부착력(N)
접착강도 측정기 (모델명 SS-30WD, 제조사 SEISHIN)를 사용하여 수평방향으로 이동속도가 0.5 mm/sec인 stage 위에 솔더리본(solder ribbon)이 부착된 셀(cell)을 올려놓고 셀과 헤드(Head)가 90°가 되게 하였다. 헤드를 셀 위에 부착된 솔더리본과 수직방향으로 상승시키면서 셀과 솔더리본의 파괴점을 측정하였다.
실시예 1 | 실시예 2 | 비교예 1 | 비교예 2 | ||
비저항 (*10-5Ω?cm) |
180 ℃에서 15분 경화 | 2 | 2.45 | 33.4 | 10.7 |
200 ℃에서 15분 경화 | 1.43 | 1.78 | 30.1 | 4.33 | |
220 ℃에서 15분 경화 | 1 | 1.22 | 14.2 | 3.2 | |
기판부착력 | 테이프 부착력 (ASTM D3359) |
0 | 0 | 10 | 30 |
전극/솔더리본 부착력(N) | pull test | 180 | 178 | 130 | 130 |
해상도 (㎛) |
인쇄 후 선폭변화율 10 % 이내 구현 | 70 | 70 | 90 | 90 |
접촉저항 (mΩ?cm) |
태양전지 셀 평가 | 7 | 7 | 9 | 9 |
종횡비 (%) |
소성후 패턴높이/패턴선폭 비율 | 30 | 31.06 | 7.11 | 14.6 |
점도변화율 (%) |
25 ℃-1개월 보관후 점도 변화율 | 3 | 4 | 완전 경화 | 완전 경화 |
상기 표 2에 나타난 바와 같이, 본 발명에 따른 실시예 1 및 2에 따른 전극 페이스트는, 열경화성 올리고머 및 접착증진제를 포함하지 않는 비교예 1 및 2의 전극 페이스트와 비교하여 전기 비저항, 기판 부착력, 전극/솔더리본 부착력, 해상도, 접촉저항, 종횡비 및 점도변화율 면에서 현저히 개선된 효과를 나타내었다.
Claims (15)
- (a) 도전성 분말;
(b) 열경화성 올리고머;
(c) 열경화 개시제;
(d) 바인더; 및
(e) 접착증진제
를 포함하는 저온소성용 열경화성 전극 페이스트. - 제 1 항에 있어서,
(a) 도전성 분말 30-95 중량%;
(b) 열경화성 올리고머 1-30 중량%;
(c) 열경화 개시제 0.01-10 중량%;
(d) 바인더 0.1-30 중량%; 및
(e) 접착증진제 0.1-30 중량%
를 포함하는 것을 특징으로 하는 저온소성용 열경화성 전극 페이스트. - 제 1 항에 있어서,
상기 도전성 분말이 은 분말인 것을 특징으로 하는 저온소성용 열경화성 전극 페이스트. - 제 1 항에 있어서,
상기 열경화성 올리고머가 아크릴계 올리고머, 에폭시 아크릴레이트계 올리고머, 우레탄 아크릴레이트계 올리고머, 폴리에스테르 아크릴레이트계 올리고머 및 이들의 혼합물로 이루어진 군에서 선택되는 것을 특징으로 하는 저온소성용 열경화성 전극 페이스트. - 제 1 항에 있어서,
상기 열경화 개시제가 양이온 또는 라디칼 개시제인 것을 특징으로 하는 저온소성용 열경화성 전극 페이스트. - 제 1 항에 있어서,
상기 열경화 개시제가 아조비스계 화합물인 것을 특징으로 하는 저온소성용 열경화성 전극 페이스트. - 제 1 항에 있어서,
상기 바인더가 셀룰로오스계 유도체 또는 아크릴계 수지인 것을 특징으로 하는 저온소성용 열경화성 전극 페이스트. - 제 1 항에 있어서,
상기 접착증진제가 부탄티올, 펜탄티올, 비닐트리메톡시실란, 비닐트리에톡시실란, 비닐부틸렌트리에톡시실란, 비닐트리(베타-메톡시)실란, 비닐트리(베타-에톡시)실란, 아크릴록시프로필트리메톡시실란, 아크릴록시프로필트리에톡시실란, 아크릴록시프로필메틸디메톡시실란, 감마-메타아크릴록시프로필트리메톡시실란, 감마-메타아크릴록시프로필트리에톡시실란, 감마-메타아크릴록시프로필메틸디메톡시실란, 감마-메타아크릴록시프로필메틸디이소프로폭시실란, 감마-메타아크릴록시카비톨트리메톡시실란테트라메톡시실란, 테트라에톡시실란, 테트라프로폭시실란, 테트라이소프로폭시실란, 테트라-n-부톡시실란, 테트라-sec-부톡시실란, 테트라-tert-부톡시실란, 메틸트리메톡시실란, 메틸트리에톡시실란, 메틸트리부톡시실란, 에틸트리메톡시실란, 에틸트리이소프록폭시실란, 에틸트리부톡시실란, 부틸트리메톡시실란, 페닐트리메톡시실란, 3-메틸트리메톡시실란, 디메틸디메톡시실란, 디페닐디메톡시실란, 디부틸디메톡시실란, 트리메딜메톡시실란, 트리메틸에톡시실란, 트리부틸메톡시실란, 트리부틸에톡시실란, 트리플루오로메틸트리메톡시실란, 트리플루오로메틸트리에톡시실란, 트리플루오로프로필트리메톡시실란, 트리플루오로프로필트리에톡시실란, 노나플루오로부틸에틸트리메톡시실란, 노나플루오로부틸에틸트리에톡시실란, 노나플루오로헥실트리메톡시실란, 노나플루오로헥실트리에톡시실란, 트리데카플루오로옥틸트리메톡시실란, 트리데카플루오로옥틸트리에톡시실란, 헵타데카플루오로데실트리메톡시실란, 헵타데카플루오로데실트리에톡시실란, 헵타데카플루오로데실트리이소프로필실란, 3-트리메톡시실릴프로필펜타데카플루오로옥테이트, 3-트리에톡시실릴프로필펜타데카플루오로옥테이트, 3-트리메톡시실릴프로필펜타데카플루오로옥틱아미드, 3-트리에톡시실릴프로필펜타데카플루오로옥틱아미드, 2-트리메톡시실릴에틸펜타데카플루오로데실술피드, 2-트리에톡시실릴에틸펜타데카플루오로데실술피드, 펜타플루오로페닐트리메톡시실란, 펜타플루오로페닐트리에톡시실란, 4-(퍼플루오로토릴)트리메톡시실란, 4-(퍼플루오로토릴)트리에톡시실란, 디메톡시비스(펜타플루오로페닐)실란, 디에톡시비스(4-펜타플루오로토릴)실란, 2-(3,4-에폭시사이클로헥실)에틸트리메톡시실란 및 이들의 혼합물, 및 상기 알콕시기 대신에 비닐기, 에폭시기, 메타크릴기, 머캡토기 또는 이소시아네이트기를 1개 이상 갖는 실란계 화합물로 이루어진 군에서 선택되는 것을 특징으로 하는 저온소성용 열경화성 전극 페이스트. - 제 1 항에 있어서,
상기 전극 페이스트가 용매를 추가로 포함하는 것을 특징으로 하는 저온소성용 열경화성 전극 페이스트. - 제 1 항에 있어서,
상기 전극 페이스트가 아크릴계 모노머를 추가로 포함하는 것을 특징으로 하는 저온소성용 열경화성 전극 페이스트. - 제 1 항에 있어서,
상기 전극 페이스트가 증점제, 안정화제, 분산제, 탈포제, 계면활성제 및 이들의 혼합물로 이루어진 군에서 선택되는 첨가제를 추가로 포함하는 것을 특징으로 하는 저온소성용 열경화성 전극 페이스트. - 제 1 항 내지 제 11 항 중 어느 한 항의 전극 페이스트를 기재 위에 인쇄한 후 건조 및 소성하여 형성된 전극.
- 제 12 항의 전극을 포함하는 전자재료.
- 제 13 항에 있어서,
상기 전자재료가 태양전지인 것을 특징으로 하는 전자재료. - 제 14 항에 있어서,
상기 태양전지가 비정질/결정질 실리콘 이종접합 태양전지인 것을 특징으로 하는 전자재료.