KR20090123186A - Light collecting sheet-laminated light diffuser plate - Google Patents

Light collecting sheet-laminated light diffuser plate Download PDF

Info

Publication number
KR20090123186A
KR20090123186A KR1020080049140A KR20080049140A KR20090123186A KR 20090123186 A KR20090123186 A KR 20090123186A KR 1020080049140 A KR1020080049140 A KR 1020080049140A KR 20080049140 A KR20080049140 A KR 20080049140A KR 20090123186 A KR20090123186 A KR 20090123186A
Authority
KR
South Korea
Prior art keywords
light
collecting sheet
laminated
diffusing plate
light diffusing
Prior art date
Application number
KR1020080049140A
Other languages
Korean (ko)
Inventor
히로유키 구마사와
아키요시 가네미츠
Original Assignee
스미또모 가가꾸 가부시끼가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 스미또모 가가꾸 가부시끼가이샤 filed Critical 스미또모 가가꾸 가부시끼가이샤
Priority to KR1020080049140A priority Critical patent/KR20090123186A/en
Publication of KR20090123186A publication Critical patent/KR20090123186A/en

Abstract

PURPOSE: A light collecting sheet-laminated light diffusing plate is provided to transmit a transmitting light with high transmittance by forming a cavity between a bonding layer and a heterogeneity floor of a laminated surface. CONSTITUTION: A light collecting sheet-laminated light diffusing plate(1) includes a light diffusing plate(2), a collecting sheet(4), and a bonding layer. The collecting sheet is laminated in one side of the light diffusing plate through the bonding layer. The light diffusing plate is composed of a plate-type molding body including a permeable material and a light diffusing agent dispersed to a permeable material. The permeable material comprises an inorganic glass, a permeable resin, and a permeable thermoplastic resin. The light diffusing agent is made of a powder having a refractive index different from a refractive index of the permeable material. The collecting sheet is laminated in one side of the light diffusing plate.

Description

집광 시트적층 광확산판{LIGHT COLLECTING SHEET-LAMINATED LIGHT DIFFUSER PLATE}Light condensing sheet laminated light diffusing plate {LIGHT COLLECTING SHEET-LAMINATED LIGHT DIFFUSER PLATE}

본 발명은 집광 시트적층 광확산판에 관한것이다.The present invention relates to a light collecting sheet laminated light diffusing plate.

직접형 액정 표시 장치 (8) 는 백라이트 장치 (6) 와 백라이트 장치의 전방측에 배치된 액정셀 (7) 을 포함하는 표시 장치이다. 백라이트 장치 (6) 로 예를 들면, 광확산판 (2) 과 이 광확산판의 후방측에 배치된 냉음극선관과 같은 광원 (5) 을 포함하는 것이 광범위하게 사용된다 (일본 미심사 특허공보 (공개) 제 7-141908 호 참조). 매끄러운 표면을 갖는 광확산판 (2) 이 일반적으로 사용된다.The direct type liquid crystal display device 8 is a display device including a backlight device 6 and a liquid crystal cell 7 arranged on the front side of the backlight device. As the backlight device 6, for example, a light diffusing plate 2 and a light source 5 such as a cold cathode ray tube disposed on the rear side of the light diffusing plate are widely used. (Japanese Unexamined Patent Publication) (Public) No. 7-141908). A light diffuser plate 2 having a smooth surface is generally used.

상기 백라이트 장치 (6) 는 광원 (5) 에서 나온 빛 (L) 을 충분히 확산시키고, 더 높은 투과율로 투과시키도록 요구되며, 이로써 더 높은 휘도로 액정셀 (7) 의 조명을 가능하게 한다. 그러한 요구를 충족시키기 위해 일본 미심사 특허 공보 (공개) 제 7-141908 호는, 광확산판 (2) 과 집광 시트 (4) 가 공기층을 통해 서로 적층된 상태로 사용되는 것을 제안한다.The backlight device 6 is required to sufficiently diffuse the light L from the light source 5 and to transmit it at a higher transmittance, thereby enabling illumination of the liquid crystal cell 7 with higher luminance. In order to meet such a demand, Japanese Unexamined Patent Publication (Publication) No. 7-141908 proposes that the light diffusing plate 2 and the light collecting sheet 4 are used in a state of being laminated with each other through an air layer.

그러나, 광확산판 (2) 과 집광 시트 (4) 가 공기층을 통해 서로 적층되는 경 우, 광확산판 (2) 과 집광 시트 (4) 는 서로에 대해 마찰하여 쉽게 긁히게된다.However, when the light diffusing plate 2 and the light collecting sheet 4 are laminated to each other through the air layer, the light diffusing plate 2 and the light collecting sheet 4 are rubbed against each other and easily scratched.

이러한 문제를 해결하기 위해, 집광 시트적층 광확산판이 제안되었으며, 집광 시트 (4) 는 공동이 형성되지 않도록 광확산판 (2) 의 전체 표면에 적층된다 (일본 특허 제 3,123,006 참조). 그러나, 이러한 종래 집광 시트적층 광확산판은 반드시 향상된 휘도를 나타내는 것은 아니다. In order to solve this problem, a light collecting sheet laminated light diffusing plate has been proposed, and the light collecting sheet 4 is laminated on the entire surface of the light diffusing plate 2 so that no cavity is formed (see Japanese Patent No. 3,123,006). However, such a conventional light collecting sheet laminated light diffuser does not necessarily exhibit improved luminance.

본 발명의 발명자들은 광확산판 (2) 과 집광 시트 (4) 가 서로에 대해 마찰시키지 않으면서 충분한 휘도로 투과광 (L) 을 확산적으로 투과시킬 수 있는 집광 시트적층 광확산판 (1) 을 개발하기 위해 집중적으로 연구해왔으며, 이로써 본 발명이 완성되었다.The inventors of the present invention provide a light collecting sheet laminated light diffusing plate 1 which can diffusely transmit transmitted light L with sufficient luminance without causing the light diffusing plate 2 and the light collecting sheet 4 to rub against each other. Intensive research has been conducted to develop the present invention.

본 발명은 광확산판 (2) 과 집광 시트 (4) 및 접착층 (3) 으로 구성되어 있는 집광 시트적층 광확산판 (1) 을 제공한다.The present invention provides a light collecting sheet laminated light diffusing plate 1 composed of a light diffusing plate 2, a light collecting sheet 4, and an adhesive layer 3.

상기 집광 시트는 접착층을 통하여 광확산판의 일 측 (2a) 상에 적층되고,The light collecting sheet is laminated on one side 2a of the light diffusion plate through an adhesive layer,

상기 일 측 (2a) 에는 요철이 제공되며, The one side (2a) is provided with irregularities,

상기 접착층 (3) 이 요철의 바닥 (2a1) 에 접촉되지 않도록 상기 일 측 (2a) 에 집광 시트 (4) 가 적층된다.The light collecting sheet 4 is laminated on the one side 2a so that the adhesive layer 3 does not contact the bottom 2a1 of the unevenness.

본 발명의 집광 시트적층 광확산판 (1) 에서, 집광 시트 (2) 와 집광 시트 (4) 가 접착층을 매개로 하고 서로 적층되기 때문에, 집광 시트 (2) 와 집광 시트 (4) 사이에 위치상에 이탈 또는 서로에 대해 마찰되어 발생되는 긁힘이 존재하지 않는다. 적층 표면의 불균질 바닥 (2a1) 은 접착층 (3) 에 접촉되지 않기 때문에, 바닥 (2a1) 과 접착층 (3) 사이에 공동 (9) 이 형성되고, 이 공동 (9) 과 접착층 (3) 은 더 높은 투과율로 투과광 (L) 을 투과할 수 있으며, 이로써, 앞면을 조 명한다.In the light collecting sheet laminated light diffusing plate 1 of the present invention, since the light collecting sheet 2 and the light collecting sheet 4 are laminated to each other via an adhesive layer, they are positioned between the light collecting sheet 2 and the light collecting sheet 4. There are no scratches caused by deviations in the phase or friction with each other. Since the heterogeneous bottom 2a1 of the laminated surface is not in contact with the adhesive layer 3, a cavity 9 is formed between the bottom 2a1 and the adhesive layer 3, and the cavity 9 and the adhesive layer 3 are It is possible to transmit the transmitted light L with a higher transmittance, thereby illuminating the front face.

이하 도 1 을 참조하여 본 발명의 집광 시트적층 광확산판 (1) 을 설명한다. 본 발명의 집광 시트적층 광확산판 (1) 을 구성하는 광확산판 (2) 으로, 예를 들어 투과성 물질과 이 투과성 물질에 분산되는 광확산제를 포함하는 판형 성형체가 일반적으로 사용된다.Hereinafter, the light condensing sheet laminated light diffusing plate 1 of the present invention will be described with reference to FIG. 1. As the light diffusing plate 2 constituting the light collecting sheet laminated light diffusing plate 1 of the present invention, for example, a plate-shaped molded body containing a transparent material and a light diffusing agent dispersed in the transparent material is generally used.

투과성 물질 예를 들어, 무기 유리, 투과성 수지 및 투과성 열가소성 수지가 성형의 용이성 면에서 투과성 수지로 사용된다. 투과성 열가소성 수지의 예로는 폴리카보네이트 수지, ABS 수지 (아크릴로니트릴 - 부타디엔 - 스티렌 공중합체), 메타크릴 수지, 메틸 메타크릴레이트 - 스티렌 공중합체 수지, 폴리 스티렌 수지, 아크릴로 니트릴 - 스티렌 공중합체 (AS) 수지 및 폴리에틸렌 수지 또는 폴리프로필렌 수지와 같은 폴리올레핀 수지를 포함한다.Permeable materials For example, inorganic glass, permeable resins and permeable thermoplastic resins are used as permeable resins in terms of ease of molding. Examples of permeable thermoplastic resins include polycarbonate resins, ABS resins (acrylonitrile-butadiene-styrene copolymers), methacryl resins, methyl methacrylate-styrene copolymer resins, polystyrene resins, acrylonitrile-styrene copolymers ( AS) resins and polyolefin resins such as polyethylene resins or polypropylene resins.

광확산제는 투과성 물질과 양립할수 없으며, 투과성 물질의 굴절률과는 다른 굴절률을 보이는 분말이며, 광확산판 (2) 을 투과하는 투과광 (L) 을 확산시키는 기능도 갖는다. 광확산제는 무기 물질로 만들어진 무기 분말이거나 유기 물질로 이루어진 유기 분말일 수 있다.The light diffusing agent is a powder which is incompatible with the transparent material and exhibits a refractive index different from that of the transparent material, and also has a function of diffusing the transmitted light L passing through the light diffusing plate 2. The light diffusing agent may be an inorganic powder made of an inorganic material or an organic powder made of an organic material.

무기 분말을 구성하는 무기 물질의 예는 이산화규소, 탄산칼슘, 황산바륨, 산화티타늄, 수산화 알루미늄, 무기 유리, 운모, 활석, 화이트 카본, 산화 마그네슘, 산화아연을 포함한다.Examples of inorganic materials constituting the inorganic powder include silicon dioxide, calcium carbonate, barium sulfate, titanium oxide, aluminum hydroxide, inorganic glass, mica, talc, white carbon, magnesium oxide, zinc oxide.

유기 분말을 구성하는 유기 물질의 예는 메타크릴 교차결합 수지 입자, 메타 크릴 고분자량 수지 입자, 스티렌 교차결합 수지 입자 및 실록산계 교차결합 수지 입자를 포함한다.Examples of the organic material constituting the organic powder include methacryl crosslinked resin particles, methacryl high molecular weight resin particles, styrene crosslinked resin particles, and siloxane based crosslinked resin particles.

광확산제로 사용되는 무기 및 유기 입자의 입자 직경은 보통 0.1 ~ 50 ㎛ 이다.The particle diameter of the inorganic and organic particles used as the light diffusing agent is usually 0.1 ~ 50 ㎛.

광확산제의 양은 투과광 (L) 의 목표하는 확산의 정도에 따라 변하며, 이 양은 투과 수지의 100 질량부를 기준으로 0.01 ~ 20 질량부 바람직하게는 0.1 ~ 10 질량부이다.The amount of the light diffusing agent varies depending on the desired degree of diffusion of the transmitted light L, and this amount is 0.01 to 20 parts by mass and preferably 0.1 to 10 parts by mass based on 100 parts by mass of the transmissive resin.

광확산판 (2) 의 두께는 보통 0.1 ~ 10 ㎜ 이다. 광확산판 (2) 의 면적 은 목표하는 백라이트 장치 (6) 의 크기, 다시 말해, 액정 표시 장치 (8) 의 크기에 따라 변하며 보통 20 ㎝ × 30 ㎝ ~ 150 ㎝ × 200 ㎝ 의 크기이다.The thickness of the light diffusion plate 2 is usually 0.1 to 10 mm. The area of the light diffusion plate 2 varies depending on the size of the target backlight device 6, that is, the size of the liquid crystal display device 8, and is usually in the range of 20 cm × 30 cm to 150 cm × 200 cm.

광확산판 (2) 의 일 측 (2a) 상에, 집광 시트 (4) 가 적층되고, 일 측 (2a) 에는 요철이 제공된다. 일 측 (2a) 의 요철은 무작위 요철로 구성된 매트되는 (matted) 표면일 수 있으며, 전체 표면에 걸쳐 V 형홈을 갖는 구조를 갖을 수도 있다.On one side 2a of the light diffusion plate 2, a light collecting sheet 4 is laminated, and one side 2a is provided with irregularities. The unevenness on one side 2a may be a matted surface composed of random unevenness, and may have a structure having a V-shaped groove over the entire surface.

요철이 매트되는 면이면, 요철의 10 점 평균 거칠기는 보통 5 ~ 100 ㎛ 이다.If it is a surface by which unevenness | corrugation is a mat, the 10-point average roughness of unevenness | corrugation is 5-100 micrometers normally.

요철이 전체 표면에 걸쳐 V 형 홈을 갖는 구조를 갖으면, 깊이 (H) 는 보통 5 ㎛ ~ 1 ㎜ 이고, 정점각 (α) 은 보통 40 ~ 120 °이며, 피치 (P) 는 보통 3 ㎛ ~ 3.5 ㎜ 이다.If the unevenness has a structure having a V-shaped groove over the entire surface, the depth H is usually 5 μm to 1 mm, the peak angle α is usually 40 to 120 °, and the pitch P is usually 3 μm. ˜ 3.5 mm.

광확산판 (2) 의 일 측 (2a) 에 적층될 집광 시트 (4) 는 투과 물질로 만들 어지고, 프리즘 마이크로 렌즈 또는 볼록 마이크로 렌즈 또는 수정체형 렌즈와 같은 집광 마이크로 렌즈 (41) 가 광확산판 (2) 으로 적층되는 측의 반대측의 전체 표면에 배치된다. 시트는 확산하면서 광확산판 (2) 을 투과하는 투과광 (L) 을 정상 (normal) 방향으로 모으고, 따라서 전방측이 고 휘도로 조명된다.The light condensing sheet 4 to be laminated on one side 2a of the light diffusing plate 2 is made of a transmissive material, and the light condensing microlens 41 such as a prism micro lens or a convex micro lens or a lens-shaped lens is light diffused. It is arrange | positioned at the whole surface on the opposite side to the side laminated | stacked by the board | plate 2. The sheet collects the transmitted light L passing through the light diffusion plate 2 in the normal direction while diffusing, so that the front side is illuminated with high brightness.

집광 시트 (4) 로서, 열가소성 수지, 예를 들어 폴리카보네이트 수지, ABS 수지 (아크릴로니트릴 - 부타디엔 - 스티렌 공중합체), 메타크릴 수지, 메틸 메타크릴레이트 - 스티렌 공중합체 수지, 폴리 스티렌 수지, 아크릴로니트릴 - 스티렌 공중합체 (AS) 수지 및 폴리에틸렌 수지 또는 폴리프로필렌 수지와 같은 폴리올레핀 수지와 같은 기재로 만들어진 것을 사용한다. 집광 시트 (4) 의 두께는 일반적으로 0.02 ~ 5 mm 이며, 바람직하게는 2 mm 이하이다. 상업적으로 이용가능한 시트가 집광시트로 사용될 수 있으며, 상업적으로 이용가능한 집광 시트 (4)는 예를 들어, Sumitomo 3M Ltd. 의 "BEF" (125 ㎛ 의 두께를 갖는 폴리에스테르 필름과, 이 폴리에스테르 필름상에 형성되어 30 ㎛ 의 두께를 갖는 아크릴 수지층을 포함하며, 25 ㎛ 의 깊이와 90°의 정점각 (α) 을 각을 갖는 V 형홈이 아크릴 수지층에 50 ㎛ 의 피치로 형성되어 있음) 와 Sekisui Film Co,.Ltd. 의 "ESTINA" 가 포함된다.As the light collecting sheet 4, a thermoplastic resin such as polycarbonate resin, ABS resin (acrylonitrile-butadiene-styrene copolymer), methacryl resin, methyl methacrylate-styrene copolymer resin, polystyrene resin, acrylic Uses made of substrates such as ronitrile-styrene copolymer (AS) resins and polyolefin resins such as polyethylene resins or polypropylene resins. The thickness of the light collecting sheet 4 is generally 0.02 to 5 mm, preferably 2 mm or less. Commercially available sheets can be used as the light collecting sheet, and the commercially available light collecting sheet 4 is, for example, Sumitomo 3M Ltd. "BEF" (polyester film having a thickness of 125 μm, and an acrylic resin layer formed on the polyester film having a thickness of 30 μm, having a depth of 25 μm and a peak angle of 90 ° (α) V-shaped grooves each having an angle of 50 μm in the acrylic resin layer) and Sekisui Film Co, .Ltd. "ESTINA" is included.

집광 시트 (4) 는 접착층 (3) 을 통하여 광확산층 (2) 에 적층된다. 접착층 (3) 은 아크릴 접착제, 우레탄계 접착제, 폴리에테르계 접착제 또는 실리콘계 접착제와 같은 접착제로 만들어진 층이다. 일반적으로 두께는 집광 시트 (4) 의 적층 강도의 관점에서 10 ㎛ 이상이며, 접착층 (3) 에 요철 바닥 (2a1) 이 접촉 하는 것을 쉽게 방지하기 위해 보통 30 ㎛ 이하이다.The light collecting sheet 4 is laminated on the light diffusing layer 2 via the adhesive layer 3. The adhesive layer 3 is a layer made of an adhesive such as an acrylic adhesive, a urethane adhesive, a polyether adhesive or a silicone adhesive. In general, the thickness is 10 µm or more in view of the stacking strength of the light collecting sheet 4, and is usually 30 µm or less in order to easily prevent the uneven bottom 2a1 from contacting the adhesive layer 3.

일 측 (2a) 에 제공된 요철의 바닥 (2a1) 에 접착층 (3) 이 접촉하지 않도록 집광 시트 (4) 가 광확산층 (2) 의 일 측상에 적층된다.The light collecting sheet 4 is laminated on one side of the light diffusing layer 2 so that the adhesive layer 3 does not contact the bottom 2a1 of the unevenness provided on one side 2a.

요철의 바닥 (2a1) 에 접착층 (3) 이 접촉하지 않도록 집광 시트 (4) 가 적층될 때, 접착층 (3) 은 집광 시트 (4) 의 전체 적층표면 (4a) 에 형성될 수 있으며, 접착층 (3) 은 공기중에서 광확산판 (2) 의 일 측 (2a) 쪽으로 집광 시트 (4) 상에 적층될 수 있으며, 이어서 예를 들어, 압력을 가할 수 있다. 광확산판 (2) 의 일 측 (2a) 에 제공되는 요철의 깊이 (H) 를 증가하고, 접착층 (3) 의 두께를 감소하며, 접착층 (3) 을 구성하는 접착제로 상대적으로 고점성을 갖는 접착제를 사용하고, 또는 집광 시트 (4) 가 적층될 때 가해지는 압력을 낮춤으로써, 접착층 (3) 을 바닥 (2a1) 과 접촉시키지 않고 집광 시트 (4) 를 광확산판 (2) 의 일 측 (2a) 상에 적층시킬수 있다.When the light collecting sheet 4 is laminated so that the adhesive layer 3 does not contact the bottom 2a1 of the unevenness, the adhesive layer 3 can be formed on the entire laminated surface 4a of the light collecting sheet 4, and the adhesive layer ( 3) may be laminated on the light collecting sheet 4 toward one side 2a of the light diffusing plate 2 in air, and then may be pressurized, for example. It has a relatively high viscosity with the adhesive which comprises the depth H of the unevenness | corrugation provided in the one side 2a of the light-diffusion plate 2, the thickness of the contact bonding layer 3, and comprises the contact bonding layer 3; By using an adhesive or by lowering the pressure applied when the light collecting sheets 4 are laminated, the light collecting sheet 4 is brought into one side of the light diffusing plate 2 without bringing the adhesive layer 3 into contact with the bottom 2a1. It can be laminated on (2a).

본 발명의 이 집광 시트적층 광확산판 (1) 에 관하여, 광학산판 (2) 의 일 측 (2a) 상에 제공된 요철의 바닥 (2a1) 과 접착층 (3) 이 접촉하지 않으므로, 공동 (9) 이 바닥 (2a1) 에 존재한다. 공동 (9) 의 전체 면적 (S9) 은, 고 휘도로 전방측이 조명될 수 있도록 일반적으로 집광 시트적층 광확산판 (1) 의 전체 면적 (S1) 의 10 % 이상 바람직하게는 30 % 이상을 차지하며, 집광 시트 (4) 와 광확산판 (2) 사이의 적층 강도의 관점에서 보통 90 % 이하, 바람직하게는 70 % 이하를 차지한다.With respect to this light collecting sheet laminated light diffusing plate 1 of the present invention, since the bottom 2a1 of the unevenness provided on one side 2a of the optical diffusing plate 2 and the adhesive layer 3 do not contact, the cavity 9 is provided. This is present at the bottom 2a1. The total area S 9 of the cavity 9 is generally at least 10% and preferably at least 30% of the total area S 1 of the light collecting sheet laminated light diffusing plate 1 so that the front side can be illuminated with high brightness. It occupies the above, and usually occupies 90% or less, preferably 70% or less from the viewpoint of the lamination strength between the light collecting sheet 4 and the light diffusing plate 2.

공동 (9) 의 전체면적 (S9) 이 크면, 집광 시트 (4) 의 적층강도는 불충분할 수 있다. 이러한 경우, 공동 (9) 이 형성되지 않도록 광확산판 (1) 의 주변부에서 요철의 바닥 (2a1) 과 충분히 접촉시킴으로써 광확산판의 크기는 목표하는 액정 표시 장치 (8) 의 스크린 크기보다 더 클 수 있으며, 또한 접착층 (3) 은 집광 시트 (4) 상에 적층될 수 있다. 광확산판 (1) 의 주변부에서의 접착층 (3) 의 두께가 증가할 때, 접착층 (3) 은 요철의 바닥 (2a1) 과 충분히 접촉함으로써 접착층 (3) 이 적층될 수 있다.When the total area S 9 of the cavity 9 is large, the lamination strength of the light collecting sheet 4 may be insufficient. In this case, the size of the light diffusion plate is larger than the screen size of the target liquid crystal display device 8 by sufficiently contacting the bottom 2a1 of the unevenness at the periphery of the light diffusion plate 1 so that the cavity 9 is not formed. It is also possible for the adhesive layer 3 to be laminated on the light collecting sheet 4. When the thickness of the adhesive layer 3 at the periphery of the light diffusion plate 1 increases, the adhesive layer 3 can be laminated by sufficiently contacting the bottom 2a1 of the unevenness.

광확산판 (1) 의 주변부에서, 집광 시트 (4) 는 프레임 바디 (미 도시) 를 이용하여 광확산판 (1) 에 고정될 수 있다.At the periphery of the light diffusing plate 1, the light collecting sheet 4 can be fixed to the light diffusing plate 1 using a frame body (not shown).

도 1 에서 나타낸 바와 같이, 본 발명의 집광 시트적층 광확산판 (1) 은 사용될 때 백라이트 장치 (6) 에 조립될 수 있다. 백라이트 장치 (6) 는 본 발명의 집광 시트적층 광확산판 (1) 과, 이 집광 시트적층 광확산판 (1) 의 후방측에 배치된 광원 (5) 을 포함하며, 집광 시트적층 광확산판 (1) 은 전방측에 집광 시트 (4) 가 위치되도록 배치된다.As shown in Fig. 1, the light collecting sheet laminated light diffusing plate 1 of the present invention can be assembled to the backlight device 6 when used. The backlight device 6 includes the light collecting sheet laminated light diffusing plate 1 of the present invention and a light source 5 arranged on the rear side of the light collecting sheet laminated light diffusing plate 1, and the light collecting sheet laminated light diffusing plate 1 is arrange | positioned so that the condensing sheet 4 may be located in the front side.

도 1 에서 나타낸 바와 같이, 백라이트 장치 (6) 는 직접형 액정 표시 장치 (8) 에 조립될 수 있다. 직접형 액정 표시 장치 (8) 는 백라이트 장치 (6) 와, 이 백라이트 장치 (6) 의 전방측에 배치된 액정셀 (7) 을 포함한다.As shown in FIG. 1, the backlight device 6 can be assembled to the direct type liquid crystal display device 8. The direct type liquid crystal display device 8 includes a backlight device 6 and a liquid crystal cell 7 arranged on the front side of the backlight device 6.

실시예Example

본 발명은 이하 실시예를 통해 더 상세히 설명될 것이지만, 본 발명을 이하 의 실시예로 제한하는 것은 아니다.The present invention will be described in more detail with reference to the following examples, but the present invention is not limited to the following examples.

실시예 1Example 1

집광 시트 (4) 를 매트되는 광확산판 (2) 상에 적층하여 집광 시트적층 광확산판 (1) 을 얻었고 (사용시 이 광확산판은 상업적으로 이용가능한 액정 표시 장치 (8) 를 구성하는 백라이트 장치 (6) 에 조립되었으며, 90°의 정점각 (α) 과 25 ㎛ 의 깊이를 갖는 V 형홈은 두께 150 ㎛ 를 갖는 폴리에스테르 필름의 일 측상에 50 ㎛ 의 피치로 형성하였음), 이 매트되는 광확산판의 일 측 (2a) 은 무색 투과성 접착층 (3) 을 통하여 무작위 요철로 구성된다. 광확산판의 일 측 (2a) 상에 형성된 매트되는 표면의 요철의 10 점 평균 거칠기 (Rz)는 JIS B0601:2001 에 따라 25.3 ㎛ 으로 측정되었다.The light collecting sheet 4 was laminated on the mating light diffusing plate 2 to obtain a light collecting sheet laminated light diffusing plate 1 (in use, the light diffusing plate is a backlight constituting a commercially available liquid crystal display device 8). Assembled into the apparatus 6, a V-shaped groove having a vertex angle α of 90 ° and a depth of 25 μm was formed at a pitch of 50 μm on one side of the polyester film having a thickness of 150 μm), One side 2a of the light diffusion plate is composed of random irregularities through the colorless transparent adhesive layer 3. The 10-point average roughness Rz of the unevenness of the mated surface formed on one side 2a of the light diffusion plate was measured to be 25.3 μm in accordance with JIS B0601: 2001.

집광 시트적층 광확산판 (1) 에 있어서, 일 측의 요철의 바닥 (2a1) 은 접착층 (3) 에 접촉되지 않으며, 공동 (9) 이 존재하고, 이 공동 (9) 의 전체 면적 (S9) 는 집광 시트적층 광확산판 (1) 의 전체 면적 (S1) 의 50 % 를 차지한다.In the light condensing sheet laminated light-diffusing plate 1, the bottom 2a1 of the uneven surface on one side does not contact the adhesive layer 3, the cavity 9 exists, and the total area S 9 of the cavity 9 is present. ) Occupies 50% of the total area S 1 of the light collecting sheet laminated light diffusing plate 1.

냉 음극선관 (5) 이 집광 시트적층 광확산판 (1) 의 집광 시트 (4) 의 반대측에 배치되었다. 조명 이후에, 집광 시트 (4) 측으로 방산된 빛 (L) 의 휘도가 9,136 cd/㎠ 로 측정되었다.The cold cathode ray tube 5 was disposed on the opposite side of the light collecting sheet 4 of the light collecting sheet laminated light diffusion plate 1. After the illumination, the luminance of the light L emitted to the light collecting sheet 4 side was measured at 9,136 cd / cm 2.

비교예 1Comparative Example 1

집광 시트적층 광확산판 (1) 은, 실시예 1 에서 사용되는 것과 동일한 집광 시트 (4) 를 매트되는 광확산판 (2) 상에 적층하여 얻어지며, 이 광확산판의 일측 (2a) 은 무색의 투과성 접착층 (3) 을 통하여 무작위 요철로 구성되어 있다. 광확산판 (2a) 의 일 측에 형성된 매트되는 표면의 요철의 10 점 평균 거칠기 (Rz) 는 JIS B0601:2001 에 따라 1.79 ㎛ 로 측정되었다. 집광 시트적층 광확산판 (1) 에 있어서, 일 측의 요철의 바닥 (2a1) 은 접착층 (3) 과 접촉되었고, 공동 (9) 은 거의 존재하지 않았으며, 공동 (9) 의 전체 면적 (S9) 은 집광 시트적층 광확산판 (1) 의 전체 면적 (S1) 의 1 % 이하를 차지했다.The light condensing sheet laminated light diffusing plate 1 is obtained by laminating the same light condensing sheet 4 as used in Example 1 on the light diffusing plate 2 to be mated, and one side 2a of the light diffusing plate is Random unevenness is formed through the colorless and transparent adhesive layer 3. The 10-point average roughness (Rz) of the irregularities of the mated surface formed on one side of the light diffusion plate 2a was measured to 1.79 µm in accordance with JIS B0601: 2001. In the light condensing sheet laminated light diffusing plate 1, the bottom 2a1 of the unevenness on one side was in contact with the adhesive layer 3, the cavity 9 was hardly present, and the total area S of the cavity 9 (S). 9 ) occupied 1% or less of the total area S 1 of the light condensing sheet laminated light-diffusing plate 1.

집광 시트적층 광확산판 (1) 의 집광 시트 (4) 의 반대측에 냉 음극선관 (5) 이 배치되었다. 조명후에, 집광 시트 (4) 로 방사된 빛 (L) 의 휘도가 7,005 cd/㎠ 로 측정되었다.The cold cathode ray tube 5 was arrange | positioned on the opposite side to the light condensing sheet 4 of the light condensing sheet laminated light-diffusion plate 1. After illumination, the luminance of the light L emitted to the light collecting sheet 4 was measured to be 7,005 cd / cm 2.

도 1 은 본 발명의 집광 시트적층 광확산판과 이 판에 조립된 상기 광확산판을 포함하는 백라이트 장치와 직접형 액정 표시 장치를 개략적으로 나타내는 단면도이다.1 is a cross-sectional view schematically showing a backlight device and a direct liquid crystal display device including the light collecting sheet laminated light diffusing plate of the present invention and the light diffusing plate assembled to the plate.

도 2 는 본 발명의 집광 시트적층 광확산판의 구성을 개략적으로 나타내는 단면도이다.2 is a cross-sectional view schematically showing the configuration of the light collecting sheet laminated light diffusing plate of the present invention.

[도면 부호의 간단한 설명]BRIEF DESCRIPTION OF THE DRAWINGS

1: 집광 시트적층 광확산판1: Condensing Sheet Laminated Light Diffusion Plate

2: 광확산판2: light diffusion plate

2a: 일 측2a: one side

3: 접착층3: adhesive layer

4: 집광 시트4: condensing sheet

5: 광원5: light source

6: 백라이트 장치6: backlight device

7: 액정셀7: liquid crystal cell

8: 직접형 액정 표시 장치8: direct liquid crystal display

9: 공동9: joint

L: 빛L: light

Claims (3)

광확산판과 집광 시트 및 접착층을 포함하는 집광 시트적층 광확산판으로서,A light collecting sheet laminated light diffusing plate comprising a light diffusing plate, a light collecting sheet, and an adhesive layer, 상기 집광 시트는 접착층을 통하여 광확산판의 일 측상에 적층되고,The light collecting sheet is laminated on one side of the light diffusion plate through an adhesive layer, 상기 일 측에는 요철이 제공되며,The one side is provided with irregularities, 접착층이 상기 요철의 바닥에 접촉되지 않도록 상기 일 측에 집광 시트가 적층되는 집광 시트적층 광확산판.A light collecting sheet laminated light diffusing plate, wherein a light collecting sheet is stacked on the one side so that an adhesive layer does not contact the bottom of the unevenness. 제 1 항의 집광 시트적층 광확산판과 이 집광 시트적층 광확산판의 후방측에 배치된 광원을 포함하며, 상기 집광 시트적층 광확산판은 집광 시트가 전방측에 위치되도록 배치되는 백라이트 장치.2. A backlight device comprising: the light collecting sheet laminated light diffusing plate of claim 1 and a light source disposed on a rear side of the light collecting sheet laminated light diffusing plate, wherein the light collecting sheet laminated light diffusing plate is disposed such that the light collecting sheet is positioned at the front side. 제 2 항의 백라이트 장치와 이 백라이트 장치의 전방측에 배치된 액정셀을 포함하는 직접형 액정 표시 장치.A direct type liquid crystal display comprising the backlight device of claim 2 and a liquid crystal cell disposed in front of the backlight device.
KR1020080049140A 2008-05-27 2008-05-27 Light collecting sheet-laminated light diffuser plate KR20090123186A (en)