KR20090020619A - 내하성 구조물 - Google Patents
내하성 구조물 Download PDFInfo
- Publication number
- KR20090020619A KR20090020619A KR1020087030659A KR20087030659A KR20090020619A KR 20090020619 A KR20090020619 A KR 20090020619A KR 1020087030659 A KR1020087030659 A KR 1020087030659A KR 20087030659 A KR20087030659 A KR 20087030659A KR 20090020619 A KR20090020619 A KR 20090020619A
- Authority
- KR
- South Korea
- Prior art keywords
- load
- resistant platform
- platform
- weight
- styrene
- Prior art date
Abstract
기반부분 및 기반부분의 한 면에서 연장된 다수의 다리를 포함하고, 적어도 일부가 폴리올레핀 및 동일 공정에서 중합된 비닐 방향족 단량체의 공중합체(interpolymer)를 포함하는 팽창성 중합체 매트릭스로 제조된 내하성 플렛폼(platform).
내하성플렛폼, 팔레트, 팽창성중합체, 폴리올레핀, 비닐방향족
Description
본 발명은 일반적으로 저장 및/또는 선적을 위해 물품을 쌓는데 사용하는, 예컨대 팔레트(pallets)와 같은 내하성 구조물에 관한 것이다.
선적용 팔레트(pallets)는 잘 알려진 내하성 이동 플렛폼(platform)으로, 이 위에 물품이 저장 및/또는 선적을 위해 놓여진다. 팔레트에는 통상적으로 판지 상자 또는 상자와 같은 다양한 아이템이 적재된다. 적재된 팔레트는 통상적으로 팔레트 트럭 또는 지게차의 도움으로 이동할 수 있다. 일반적으로, 팔레트는 나무로 만들어진다.
상기 나무 팔레트의 중량은 40 내지 70 파운드의 범위에 있다. 그러므로, 나무 팔레트에 선적된 화물의 중량은 나무 팔레트의 중량에 대비해 40 내지 70 파운드로 감소된다. 특히 항공으로 선적될 때의 물품량은 엄격하게 제한된다.
추가로, 나무 팔레트를 다루는 사람들 사이에서는 나무 파편 및 징으로 인한 수 많은 부상이 빈번하게 발생한다. 따라서, 나무 팔레트의 처분은 고질적인 문제다.
각국 사이에는 아시안 딱정벌레(Asian Longhornd Beetle), 아시아 하늘소(Asian Cerambycid Beetle), 소나무선충(Pine Wood Nematode), 소나무재선 충(Pine Wilt Nematode) 및 유리알락하늘소(Anoplophora glabripennis)를 포함하는 나무에 구멍을 내는 곤충을 수입해야 하는 나무 팔레트의 사용에 대한 우려가 있어왔다. 수입된 곤충으로 인한 전형적인 손상은 미국에서의 밤나무의 죽음이다. 이 때는 다람쥐가 땅을 닿지 않고도 밤나무의 돌출부를 통해 미국을 횡단할 수 있다고 하던 시기였다. 곤충의 침략은 미국에서 밤나무의 멸종을 초래했다.
나무 팔레트의 이러한 단점을 극복하기 위한 노력은 성형 플라스틱 팔레트에 이르게 했다. 예컨대, 미국 특허번호 제 6,786,992호는 팽창된 폴리스티렌 중심체(core) 및 이 중심체의 일부를 덮은 고강도 폴리스티렌 층을 보유하는 팔레트를 개시한다.
미국 특허번호 공개번호 제 2005/0,263,044호는 볼록렌즈 특성 및 중심체 외주(perimeter)를 포함하는 하나 이상의 표면을 보유하는 압축성 중심체; 및 볼록한 표면 및 중심체 경계선의 가장자리(edge)를 연장한 첫 반째 시트 가장자리로 성형된 내부를 보유하는 첫 번째 유연한 열가소성 시트, 및 두 번째 시트 내부 및 중심체의 외주를 밖으로 연장한 두 번째 시트 가장자리를 보유한 두 번째 유연한 열가소성 시트를 포함하는, 외관 내부 및 외관 가강자리를 보유하는 열가소성 외관으로 정의되는 성형물을 포함하는 팔레트에 대해 개시한다.
일반적으로, 플라스틱, 특히 발포성 플라스틱으로 제조된 팔레트는 통상적인 나무 팔레트만큼 강하지 않기 때문에 사용시 적용된 하중 압력으로 인해 파손되므로 이를 바람직하지 않은 것으로 만든다.
그러므로, 당업계에서는 통상적으로 나무 팔레트 중량에서 볼 수 있었던 물 품의 선적 및/또는 저장의 연속된 사용시의 내하성 스트레스를 견딜 수 있는 가벼운 중량의 팔레트를 제공하는 것이 필요하다.
발명의 개요
본 발명은 기반부분 및 기반부분의 한 면에서 연장된 다수의 다리를 포함하고, 적어도 일부가 폴리올레핀 및 동일 공정(in-situ)에서 중합된 비닐 방향족 단량체의 공중합체(intepolymer)를 포함하는 팽창성 중합체 매트릭스로 제조된 내하성 플렛폼을 제공한다.
발명의 자세한 설명
본 명세서에서의 설명의 목적으로, "상부", "하부", "내부", "외부", "오른쪽", "왼쪽", "수직", "수평", "최상부", "바닥"이라는 용어 및 이의 유래어는 도면 그림에 기인한 본 발명에 관한 것이어야 한다. 그러나, 본 발명은 반대로 표현된 것을 제외하고는 선택적인 변화 및 단계 순서를 추정할 수 있을 것으로 이해된다. 또한, 첨부된 도면으로 예증되거나 하기 명세서에 기술된 특정 장치 및 공정은 본 발명의 대표적인 양태이다. 그러므로, 본원에 개시된 양태에 관한 특정 차원 및 다른 물리적 특성은 본 발명을 제한하는 것으로 간주되어서는 안된다. 본 발명의 양태를 기술하는데 있어서, 도면에는 유사 숫자가 본 발명의 유사 특징물을 지시하는데 사용될 것이다.
실시예의 실행시 또는 달리 지시된 것 외에, 본 명세서 및 청구항에서 사용되는 반응 조건등의 구성물의 양을 언급하는 모든 수 및 표현은 모든 경우에 "약(about)"이라는 용어로 수정된 것으로 이해된다. 따라서, 반대로 지시된 것이 아니라면, 하기 명세서 및 첨부된 청구항에 기술된 수적 변수는 본 발명이 수득하기를 원하는 소기의 특성에 따라 달라질 수 있는 근사치이다. 아주 적어도, 청구항의 범주와 동일한 교리의 출원범위를 제한하지 않기 위한 의도가 아닌 한, 각각의 수적 변수는 적어도 통상적인 라운딩(rounding) 기술을 적용하고, 보고된 의미있는 자연수의 개념으로 해석되야 한다.
본 발명의 광범한 기술된 수 범위 및 변수가 근사치임에도 불구하고, 특정 실시예에 기술된 수적 수치는 가능한 정확한 것으로 보고된다. 그러나, 임의의 수적 수치는 본래 각각의 시험 측정에서 발견되는 표준 편차로부터 필수적으로 기인하는 특정 오차를 포함한다.
또한, 본원에 기술된 임의의 수 범위는 포함된 모든 하위 범위를 포함하도록 한다. 예컨대, "1 내지 10"의 범위는 기술된 최저값인 1 및 기술된 최고값인 10을 포함하며 그 사이의 모든 하위 범위를 포함하도록 하고; 이는 즉 1 이상의 최소값 및 10 이하의 최대값을 보유한다. 개시된 수 범위는 연속적이므로, 최저값 및 최고값 사이의 모든 값을 포함한다. 달리 지시되지 않는다면, 본 출원에 기술된 다양한 수 범위는 근사치이다.
본원에서 사용된 "팽창성 중합체 매트릭스"란 용어는 발포제로 함침되는 입자 또는 구슬 형태의 중합물질을 언급하는 것으로 입자 및/또는 구슬이 몰드에 놓여져 열이 가해질 때 발포제(하기 기술됨)의 증발이 입자 및/또는 구슬로 된 다공질 구조 및/또는 팽창 다공질 구조의 형성, 및 입자 및/또는 구슬의 외표면이 서로 융합되어서 몰드의 형태를 갖춘 연속 질량(continuous mass)의 중합물질을 형성케 한다.
본 발명에서 "중합체"란 용어는 단일중합체, 혼성중합체(copolymer) 및 그래프트 혼성중합체를 제한없이 포함하는 것을 의미한다.
본 발명에서 "폴리올레핀"이란 용어는 알파 비포화 C2-C32 직쇄형 또는 분지쇄형 올레핀계 단량체로부터 제조된 중합체를 의미하고, 이의 비제한 예로는 에틸렌, 프로필렌, 1-부텐, 1-헥센 및 1-옥텐을 포함한다.
본 발명에서, "폴리에틸렌"이란 용어는 에틸렌 단일중합체만을 언급하고 포함하는 것이 아니라, 50 mol% 이상, 일부 경우 70 mol% 이상, 및 다른 경우 80 mol% 이상의 에틸렌 단위 및 이에 상응하는 비율의 에틸렌과 혼성중합할 수 있는 단량체 단위를 포함하는 에틸렌 혼성중합체, 및 에틸렌 단일중합체 또는 또 다른 중합체와의 혼성중합체를 50 중량% 이상, 일부 경우 60 중량% 이상 그리고 다른 경우 75 중량% 이상을 함유하는 배합물을 포함한다.
에틸렌과 혼성중합할 수 있는 단량체의 비제한 예로는 비닐 아세테이트, 비닐 클로라이드, 프로필렌, 1-부텐, 1-헥센, 및 (메트) 아크릴산 그리고 이의 에스테르를 포함한다.
에틸렌 단일중합체 또는 혼성중합체와 배합될 수 있는 중합체는 에틸렌 단일중합체 또는 혼성중합체에 친화성인 임의의 중합체를 포함한다. 에틸렌 단일중합체 또는 혼성중합체와 배할될 수 있는 중합체의 비제한 예로는 폴리프로필렌, 폴리부타디엔, 폴리이소프렌, 폴리클로로프렌, 염소화 폴리에틸렌, 폴리비닐 클로라이드, 스티렌/부타디엔 혼성중합체, 스티렌/부타디엔/아크릴로니트릴 혼성중합체, 및 비닐 클로라이드/비닐 아세테이트 혼성중합체를 포함한다.
본원에서 사용된 "스티렌계 중합체"란 용어는 스티렌계 단량체의 단일중합체, 및 스티렌계 단량체 그리고 또 다른 혼성중합할 수 있는 단량체의 혼성중합체를 지시하고, 스티렌계 단량체는 이 혼성중합체에서 50 mol% 이상의 단량체 단위를 차지한다. 스티렌계 단량체의 비제한 예로는 스티렌, p-메틸 스티렌, α-메틸 스티렌, 3차 부틸 스티렌, 디메틸 스티렌, 이의 핵 브롬화 또는 염소화된 유도체 및 이의 혼합물을 포함한다. 적합한 혼성중합할 수 있는 단량체의 비제한 예는 1,3-부타디엔, C1-C32 직쇄형, 고리형 또는 분지쇄형 알킬 (메트)아크릴레이트 (상세한 비제한 예는 부틸 (메트)아크릴레이트, 에틸 (메트)아크릴레이트, 메틸 (메트)아크릴레이트, 및 2-에틸헥실 (메트)아크릴레이트를 포함한다), 아크릴로니트릴, 비닐 아세테이트, 알파-메틸에틸렌, 디비닐 벤젠, 말레산무수물, 말레산, 퓨마르산, 말레산의 C1-C12 직쇄형, 분지쇄형 또는 고리형 모노- 및 디- 알킬 에스테르, 퓨마르산의 C1-C12 직쇄형, 분지쇄형 또는 고리형 모노- 및 디- 알킬 에스테르, 이타콘산, 이타콘산의 C1-C12 직쇄형, 분지쇄형 또는 고리형 모노- 및 디- 알킬 에스테르, 이타콘산무수물 및 이의 혼합물을 포함한다.
본원에서 사용된 "(메트)아크릴" 및 "(메트)아크릴레이트"란 용어는 아크릴레이트 및 (메트)아크릴레이트로 빈번하게 언급되는 해당 알킬 에스테르와 같이 아크릴산 및 메트아크릴산 유도체 모두를 포함하는 것으로, "(메트)아크릴레이트"는 포괄하는 것으로 의도되었다.
본원에서 사용된 "몰딩"이란 용어는 새로운 소기의 형태를 만들기 위한 유연성 물질의 성형을 지시한다. 몰딩은 수(male) 및 암(female) 몰딩 도구, 조각된 압반(platen), 및 이의 유사물과 같은 특정 몰딩 도구의 사용을 수반할 수 있다. 또한, 열경화성 물질의 적어도 일부를 소기의 형태로 만드는데 사용된 압축성 중심체를 포함하는 특정 성형된 중심체의 사용을 포함할 수 있다.
본원에서 사용된 "팽창 인자"란 용어는 cc/g으로 표현되는 팽창된 중합체 구슬의 일정 중량이 차지하는 부피를 지시한다.
본 발명은 기반부분 및 이 기반부분의 한 명으로부터 연장된 다수의 다리를 포함하는 내하성 플렛폼을 제공한다.
본 내하성 플렛폼은 폴리올레핀 및 동일 공정에서 중합된 비닐 방향족 단량체의 공중합체 그리고 선택적으로 다른 팽창성 중합체를 포함하는 팽창성 중합체 매트릭스로부터 제조된다.
본 발명의 양태에서, 폴리올레핀 및 동일 공정에서 중합된 비닐 방향족 단량체의 공중합체는 미국 특허번호 3,959,189; 4,168,353; 4,303,756, 4,303,757 및 6,908,949에서 기술된 것 중 하나 이상의 것으로, 이의 상당 부분이 본원에 참고인용된다. 본 발명에서 사용될 수 있는 상기 공중합체의 비제한 예는 펜실베니아 피츠버그의 노바 케미컬스 인코포레이티드로부터 구매 가능한 상표명 ARCEL® 및 일본 도쿄의 세키슈이 플라스틱스 코포레이션 리미티드의 PIOCELAN® 을 포함한다.
본 발명의 양태에서, 폴리올레핀 및 동일 공정에서 중합된 비닐 방향족 단량체의 공중합체는 입자 또는 수지 구슬이고, 이는 순차적으로 팔레트를 생성하기 위해 본 발명에 따라 처리된다. 본 발명에서 사용된 공중합체 입자는 폴리올레핀 및 동일 공정에서 중합된 비닐 방향족 수지를 포함하고, 폴리올레핀 및 비닐 방향족 수지 입자의 상호침투 망을 형성한다. 공중합체 입자는 발포제 및 선택적으로 가소제로 함침된다.
상기 공중합체 입자는 폴리올레핀 입자 및 비닐 방향족 단량체나 단량체 혼합물을 수성 서스펜션에 부유시키는 단계, 및 이 단량체 또는 단량체 혼합물을 폴리올레핀 입자 내부에 중합시키는 단계를 포함하는 공정으로 수득될 수 있다. 상기 공정의 비제한 예는 미국 특허번호 3,959,189, 4,168,353, 및 6,908,949에 개시된다.
본 발명의 양태에서, 폴리올레핀은 저-, 중-, 고-밀도 폴리에틸렌, 에틸렌 비닐 아세테이트 혼성중합체, 에틸렌/프로필렌 혼성중합체, 폴리에틸렌과 폴리프로필렌의 배합물, 폴리에틸렌과 에틸렌/비닐 아세테이트 혼성중합체의 배합물 및 폴리에틸렌과 에틸렌/프로필렌 혼성중합체의 배합물 중에서 선택된 하나 이상의 폴리 에틸렌 수지를 포함한다. 에틸렌-부틸 아크릴레이트 혼성중합체 및 에틸렌-메틸 메트아크릴레이트 혼성중합체가 또한 사용될 수 있다.
본 발명의 공중합체 수지 입자에서 폴리올레핀의 양은 공중합체 수지 입자의 중량을 기준으로 20 중량% 이상, 일부 경우에는 25 중량% 이상 그리고 다른 경우에는 30 중량% 이상일 수 있고, 80 중량% 이하, 일부 경우에는 70 중량% 이하, 다른 경우에는 60 중량% 이하 그리고 일부 예에서는 55 중량% 이하일 수 있다. 공중합체 수지 입자에서 폴리올레핀의 양은 상기 언급된 수치 사이의 임의의 수치 또는 범위일 수 있다.
본 발명의 공중합체 수지 입자에서 중합된 비닐 방향족 수지의 양은 공중합체 수지 입자의 중량을 기준으로 20 중량% 이상, 일부 경우에는 30 중량% 이상, 다른 경우에는 40 중량% 이상, 그리고 일부 예에서는 45 중량% 이상일 수 있고, 80 중량% 이하, 일부 경우에는 75 중량% 이하, 그리고 다른 경우에는 70 중량% 이하일 수 있다. 공중합체 수지 입자에서 중합된 비닐 방향족 수지의 양은 상기 언급된 임의의 수치 사이의 임의의 수치 또는 범위일 수 있다.
비닐 방향족 수지는 중합된 비닐 방향족 단량체로 구성되거나, 비닐 방향족 단량체 및 혼성중합 가능한 공단량체의 단량체 단위를 포함하는 혼성중합체일 수 있다. 본 발명에서 사용될 수 있는 비닐 방향족 단량체의 비제한 예로는 스티렌, 알파-메틸스티렌, 에틸스티렌, 클로로스티렌, 브로모스티렌, 비닐톨루엔, 비닐벤젠 및 이소프로필자일렌을 포함한다. 이러한 단량체는 단독 또는 혼합물로 사용될 수 있다.
혼성중합할 수 있는 공단량체의 비제한 예로는 1,3-부타디엔, C1-C32 측쇄형, 고리형 또는 분지쇄형 알킬 (메트)아크릴레이트 (상세한 비제한 예로는 부틸 (메트)아크릴레이트, 에틸 (메트)아크릴레이트 및 2-에틸헥실 (메트)아크릴레이트를 포함한다), 아크릴로니트릴, 비닐 아세테이트, 알파-메틸에틸렌, 디비닐 벤젠, 말레산무수물, 이타콘산무수물, 디메틸 말레에이트 및 디에틸 말레에이트를 포함한다.
본 발명에 사용될 수 있는 비닐 방향족 혼성중합체의 비제한 예로는 U.S. 특허번호 4,049,594에 개시된 것을 포함한다. 적합한 비닐 방향족 혼성중합체의 비제한 예는 스티렌을 중합한 것으로부터의 반복 단위, 및 1,3-부타디엔, C1-C32 측쇄형, 고리형 또는 분지쇄형 알킬 (메트)아크릴레이트 (특정 비제한 예로는 부틸 (메트)아크릴레이트, 에틸 (메트)아크릴레이트 및 2-에틸헥실 (메트)아크릴레이트를 포함한다), 아크릴로니트릴, 비닐 아세테이트, 알파-메틸에틸렌, 디비닐 벤젠, 말레산무수물, 이타콘산무수물, 디메틸 말레에이트 및 디에틸 말레에이트 중에서 선택된 단량체를 중합한 것으로부터의 반복 단위를 보유하는 혼성중합체를 포함한다.
본 발명의 특정 양태에서, 비닐 방향족 수지는 폴리스티렌 또는 스티렌-부틸 아크릴레이트 혼성중합체를 포함한다.
일반적으로, 공중합체 수지 입자는 하기에 따라 생성된다: 폴리올레핀 입자를 침강방지제 예컨대, 수성 고분자 물질로 폴리비닐 알콜 또는 메틸 셀룰로오즈이거나, 약간 수성인 무기 물질로 칼슘 포스페이트 또는 마그네슘 피로포스페이트, 그리고 비누인 소듐 도데실 벤젠 설포네이트를 물 중량을 기준으로 0.01 내지 5 중량%, 일부 경우에는 2 내지 3 중량%를 첨가해서 제조될 수 있는 수성 매질에 분산시키고, 비닐 방향족 단량체를 이 서스펜션에 첨가하면, 폴리올레핀 입자 안에서 중합된다.
비닐 방향족 단량체의 중합을 위한 임의의 통상적으로 알려지고 보편적으로 사용되는 침감방지제가 사용될 수 있다. 이러한 침강방지제는 당업계에 잘 공지되고 당업자에 의해 자유롭게 선택될 수 있다. 처음에, 물은 일반적으로 수성 서프펜션에 적용된 초기 폴리올레핀 입자의 양보다 중량 기준으로 0.7 내지 5배, 바람직하게는 3 내지 5배의 양이고, 점차적으로 중합체 입자 대 물의 비율은 약 1:1에 이를 수 있다.
폴리올레핀 입자에 흡수도니 비닐 방향족 단량체의 중합은 개시제를 사용해서 수행된다.
비닐 방향족 단량체의 서스펜션 중합체 적합한 개시제는 일반적으로 비닐 방향족 단량체의 중량을 기준으로 약 0.05 내지 2 중량%, 일부 경우에는 0.1 내지 1 중량%의 양으로 사용된다. 적합한 개시제의 비제한 예는 벤조일 퍼옥사이드, 라우로일 퍼옥사이드, t-부틸 퍼벤조에이트와 같은 유기 퍼옥사이드, 및 아조비스이소부틸로니트릴 및 아조비스디메틸발레로니트릴과 같은 아조 화합물을 포함한다.
이러한 개시제는 단독으로 사용될 수 있거나, 2종 이상의 개시제가 같이 사용될 수 있다. 다수의 경우, 개시제는 비닐 방향족 단량체에 용해되서 폴리올레핀 입자에 흡수된다. 다른 경우, 개시제는 톨루엔, 벤젠, 및 1,2-디클로로프로판과 같은 용매에 용해될 수 있다.
비닐 방향족 단량체의 동일 공정 중합반응이 완료될 때, 중합된 비닐 방향족 수지는 폴리올레핀 입자 내부에 균일하게 분산된다.
다수의 경우, 폴리올레핀 입자는 가교된다. 이 가교는 폴리올레핀 입자에서 비닐 방향족 단량체의 중합과 동시 그리고 발포제 및/또는 가소제의 함침 전에 달성될 수 있다. 이러한 목적으로, 가교제가 사용된다. 상기 가교제는 디-t-부틸-퍼옥사이드, t-부틸-큐밀퍼옥사이드, 디큐밀-퍼옥사이드, .알파., .알파.-비스-(t-부틸퍼옥시)-p-디이소프로필벤젠, 2,5-디메틸-2,5-디-(t-부틸-퍼옥시)-헥신-3,2,5-디메틸-2,5-디-(벤조일퍼옥시)-헥산 및 t-부틸-퍼옥시이소프로필-카보네이트를 포함하되, 이에 제한되지는 않는다. 상기 가교제는 가교제를 물에 부유된 폴리올레핀 입자의 중량을 기준으로 약 0.1 내지 2 중량% 및 일부 경우 0.5 내지 1 중량%의 양으로 용해시켜서 비닐 방향족 단량체와 함께 폴리올레핀 입자에 흡수된다. 가교제의 추가적인 세부사항 및 가교제를 폴리올레핀 입자에 흡수시키는 방법은 U.S. 특허번호 3,959,189에 제공된다.
본 발명의 양태에서, 폴리올레핀 및 동일 공정에서 중합된 비닐 방향족 단량체의 공중합체는 수지내 연속상이 고무이고, 분산상이 스티렌계 중합체인 고무 개질된 스티렌계 중합체를 포함하고, 이는 본원에 상당 부분이 참고인용된 동시 출원 중인 U.S. 특허출원 공개번호 2006/0,276,558에 기술된다.
상기 양태에서, 고무 개질된 스티렌계 중합체는,
Ⅰ) 수성상에서 유기 액상의 액적을 분산시키는 단계로, 이는 고정 또는 유동일 수 있고, 상기 유기상은 하나 이상의 아릴 중합할 수 있는 단량체를 보유하는 단량체 용액에 용해된 하나 이상의 탄성 중합체를 보유하는 유기 용액을 보유하고, 유기 액적은 약 0.001 mm 내지 약 10 mm의 평균 지름을 보유하고;
Ⅱ) 단량체를 유기 액적에 저 전단 유동 패턴으로 중합하는 단계를 통해 제조된다.
본 양태의 일 관점에서, 유기 액적의 분산은 유기상을 수성상의 자유 표면적(free surface) 미만으로 원자화하는 압력으로 생성되고, 이는 고정 또는 유동일 수 있다.
본 양태의 또 다른 관점에서, 수성상에서의 유기 액상의 유기 액적 분산은 고정 또는 유동일 수 있고, 기계 교반으로 생성된다.
스티렌계 중합체는 스티렌, 알파-메틸스티렌, 에틸스티렌, 클로로스티렌, 브로모스티렌, 비닐톨루엔, 비닐벤젠, 및 이소프로필자일렌 그리고 이의 혼합물 중에서 선택된 비닐 방향족 단량체의 중합으로부터의 잔류물을 포함할 수 있다.
탄성 중합체는 예컨대, 비제한적으로 부타디엔, 이소프렌 (즉, 2-메틸-1,3-부타디엔), 3-부타디엔, 2,3-디메틸-1,3-부타디엔 및 1,3-펜타디엔과 같은 하나 이상의 공액 디엔, 및 아크릴로니트릴 또는 메트아크릴로니트릴과 같은 하나 이상의 적합한 비포화 니트릴, 선택적으로 아크릴산, 메트아크릴레이트 및 부틸 아크릴레이트와 같은 비포화 카복실산의 알킬 에스테르; 메톡시 아크릴레이트, 에톡시에틸 아크릴레이트, 메톡시에틸 아크릴레이트, 아크릴아미드, 메트아크릴아미드와 같은 비포화 카복실산의 알콕시알킬 에스테르; N-메틸올아크릴아미드, N,N'-디메틸올아크릴아미드 및 N-에톡시메틸올아크릴아미드와 같은 N-치환된 아크릴아미드; N-메틸올메트아크릴아미드, N,N'-디메틸올메트아크릴아미드, N-에톡시-메틸메트아크릴아미드와 같은 N-치환된 메트아크릴아미드 및 비닐 클로라이드의 혼성중합체를 포함할 수 있다. 상기 혼성중합체는 또한 스티렌, o-, m-, p-메틸 스티렌, 디메틸스티렌 및 에틸 스티렌과 같은 하나 이상의 방향족 비닐 단량체의 중합으로부터의 반복 단위를 포함할 수 있다. 혼성중합체의 이러한 타입은 "아크릴로니트릴-부타디엔 고무" 또는 "아크릴로니트릴-부타디엔-스티렌 고무" 또는 총칭하여 "니트릴 고무"로 당업자에게 공지된다.
본 발명의 일부 양태에서, 니트릴 고무는 수소의 존재하에 바람직하게는 적합한 수소화 촉매로 부분 수소화될 수 있다.
본 발명의 팽창성 중합체 매트릭스는 발포 물품을 생성하는 원료로 사용될 수 있다. 발포제 및/또는 가소제는 팽창성 중합체 매트릭스 수지 입자에 도입되어서 발포성 또는 팽창성 입자나 수지 구슬을 생성하고, 몰드 발포 물품에 사용된다.
발포제는 폴리올레핀의 연화점보다 낮은 끓는점을 보유해야 하고, 상온(약 20 내지 30℃) 및 상압(약 대기압)에서 기체 또는 액체여야 한다. 발포제는 당업계에 널리 알려지고, 일반적으로 -42℃ 내지 80℃, 보다 일반적으로는 -10 내지 36℃ 범위의 끓는점을 보유한다. 적합한 탄화수소 발포제는 n-프로판, n-부탄, 이소-부탄, n-펜탄, 이소-펜탄, n-헥산, 및 네오펜탄과 같은 지방족 탄화수소, 및 사이클로부탄 및 사이클로펜탄과 같은 사이클로지방족 탄화수소, 및 메틸 클로라이드, 에틸 클로라이드, 메틸렌 클로라이드, 트리클로로디플루오로메탄, 클로로디플루오로메탄 및 디클로로테트라플루오로에탄 등과 같은 할로겐화 탄화수소를 포함하되, 이에 제한되지는 않는다. 이러한 발포제는 단독 또는 혼합물로 사용될 수 있다. 상온 및 상압에서 기체성인 n-부탄, 에틸 클로라이드, 및 디클로로테트라플루오로에탄이 혼합물로 사용된다면 발포를 낮은 벌크 밀도로 획득하는 것이 가능하다. 휘발성 발포제의 특정 종류로는 U.S. 특허 번호 3,959,180에 교시된다. 본 발명의 특정 양태에서 발포제는 n-펜탄, 이소-펜탄, 네오펜탄, 사이클로펜탄, 및 이의 혼합물 중에서 선택된다.
발포제의 양은 팽창성 중합체 매트릭스의 중량 기준 약 1.5 중량% 내지 약 20 중량%, 일부 경우에는 약 1.5 중량% 내지 15 중량% 및 다른 경우 5 중량% 내지 15 중량% 범위이다.
가소제는 본원에서 상기 기술된 바, 발포제와 함께 사용될 수 있고, 본 발명에서는 발포 보조제로 작용한다.
적합한 가소제는 벤젠, 톨루엔, 리모넨, 측쇄형이나 분지쇄형 또는 고리형 C5 내지 C20 알켄, 백색유, 측쇄형이나 분지쇄형 또는 고리형 C1 내지 C20 디알킬프탈레이트, 스티렌, 스티렌의 올리고머, 폴리스티렌보다 낮은 유리전이온도를 보유하는 (메트)아크릴레이트의 올리고머 및 이의 혼합물을 포함하되, 이에 제한되지는 않는다.
본 발명의 특정 양태에서, 가소제는 식물계에 존재하는 리모넨, 모노-테르펜 탄화수소를 포함한다. 알려진 종류로는 d-리모넨, 1-리모넨, 및 디-리모넨이다. D-리모넨은 시트러스 과일 껍질에 함유되고, 향취제로 식품 첨가제에 사용되며; 이의 끓는점은 약 176℃이고; 이의 인화력은 낮다. D-리모넨은 오렌지색 향기를 가진 무색 액체이고, 식품 첨가제로 승인되고 향수의 원료로 널리 사용된다. 리모넨은 유해한 공기 오염물은 아니다.
가소제의 양은 팽창성 중합체 매트릭스의 중량을 기준으로 약 0.1 내지 5 중량부이고, 일부 경우에는 약 0.1 내지 약 1 중량부의 범위일 수 있다.
본 발명의 양태에서, 공중합체 입자는 하기와 같이 제조될 수 있다: 첫 번째 반응기에서, 폴리올레핀 입자는 분산제를 포함하는 수성 매질에 부유된다. 분산제는 폴리비닐 알콜, 메틸셀룰로오즈, 칼슘 포스페이트, 마그네슘 피로포스페이트, 칼슘 카보네이트, 트리칼슘 포르페이트 등일 수 있다. 적용되는 분산제의 양은 물의 양을 기준으로 0.01 내지 5 중량%일 수 있다. 계면활성제는 수성 매질에 첨가될 수 있다. 일반적으로, 계면활성제는 서스펜션의 표면 장력을 낮추는데 사용되고, 사용된다면 개시제 및 왁스 혼합에서 혼합물의 물/비닐 방향족 단량체의 유화를 돕는다. 적합한 왁스는 폴리에틸렌 왁스 및 에틸렌 비스티어아미드를 포함한다. 수성 매질은 일반적으로 비닐 방향족 단량체가 중합될 수 있는 온도, 즉 약 60℃ 내지 약 120℃에서 예컨대 12 내지 20 시간동안 가열된다. 이 12 내지 20 시간동안, 비닐 방향족 단량체, 비닐 방향족 중합 개시제, 및 가교제는 수성 매질에 분산된 폴리올레핀 입자를 보유하는 결과 서스펜션에 첨가된다. 이러한 물질은 한번에 모두 첨가되거나, 개별 분량으로 점진적으로 첨가될 수 있다.
공중합체 입자는 산화된 후 탈수되고 스크린(screen)된 후 두 번째 반응기로 투입되서 발포제 및/또는 가소제로 함침된다.
상기 함침 단계는 수성 매질에서 공중합체 입자를 부유시키고, 결과 서스펜션에 발포제 및/또는 가소제를 첨가한 후 바람직하게는 약 40℃ 내지 80℃의 온도에서 교반함으로써 수행될 수 있다. 발포제 및/또는 가소제는 같이 배합되서 공중합체 입자에 첨가되거나, 공중합체 입자에 개별적으로 첨가될 수 있다.
대안적으로, 발포제 및/또는 가소제는 중합 반응시 또는 이후에 첫 번째 반응기에 첨가될 수 있다.
상기 공정은 공중합체 입자의 함침을 위한 습식 공정을 기술한다. 대안적으로, 공중합체 입자는 U.S. 특허번호 4,429,059의 4번째 단락 20-36줄에 교시된 것과 유사한 무수 공정을 통해 함침될 수 있다.
본 발명의 양태에서, 발포제는 압출기에 있는 팽창성 중합체 매트릭스에 투여되서 수지 팰랫(pellets) 또는 구슬을 생성할 수 있다. 상기 압출기는 혼합물 가닥을 압출하기 전에 발포제를 팽창성 중합체 매트릭스에 혼합시키는 작용을 한다. 이 가닥은 예컨대, 수중용 표면 절단기(underwater face cutter)와 같은 적합한 장치를 사용해서 구슬 또는 팰랫 길이로 절단된다.
공중합체 수지 및/또는 팽창성 중합체 매트릭스 미립자는 또한 당업계에 알려진 다른 첨가물, 예컨대 비제한적으로 대전방지 첨가제; 인화 억제제; 착색제 또는 염료; 충진제 물질 및 이의 혼합물을 포함한다. 또한, 다른 첨가제는 사슬이동제로 예컨대, n-도데실 메르캅탄, t-도데실 메르캅탄, t-부틸 메르캅탄 및 n-부틸 메르캅탄과 같은 C2-15 알킬 메르캅탄, 및 다른 작용제로 예컨대, 펜타페닐 에탄 및 알파-메틸 스티렌의 이합체를 포함할 수 있다. 다른 첨가제로는 추가로 기핵제, 비제한 예로 폴리올레핀 왁스, 즉 폴리에틸렌 왁스를 포함할 수 있다.
팽창성 중합체 매트릭스는 폴리올레핀 공중합체 및 동일 공정에서 중합된 비닐 방향족 단량체 그리고 선택적으로 다른 팽창성 중합체를 포함한다. 다른 팽창성 중합체는 본 발명의 내하성 플렛폼에 소기의 특성을 제공할 수 있고, 폴리올레핀 및 동일 공정에서 중합된 비닐 방향족 단량체의 공중합체와 친화성인 중합체를 포함한다. 본 발명에 사용될 수 있는 다른 팽창성 중합체의 비제한 예는 팽창성 폴리 스티렌(EPS), 팽창성 폴리올레핀, 본원에 상당 부분이 참고인용된 동시출원 중인 U.S. 특허출원 공개번호 2006/0,276,558에 기술된 바, 수지내 연속상인 스티렌 중합체이고 분산상이 고무인 고무 개질된 스티렌 중합체, 수지내 연속상이 고무이고 분산상이 스티렌 중합체인 고무 개질된 스티렌 중합체, 폴리페닐렌 옥사이드, 및 이의 혼합물 및 배합물을 포함한다.
팽창성 중합체 매트릭스는 폴리올레핀 및 동일 공정에서 중합된 비닐 방향족 단량체의 공중합체를 100% 포함하거나, 폴리올레핀 및 동일 공정에서 중합된 비닐 방향족 단량체 공중합체의 팽창성 중합체 매트릭스의 중량을 기준으로 99 중량% 이하, 일부 경우에는 95 중량% 이하, 다른 경우에는 90 중량% 이하이거나, 일부 예에서는 80 중량% 이하 및 다른 예에서는 75 중량% 이하로 포함될 수 있다. 또한, 팽창성 중합체 매트릭스는 폴리올레핀 및 동일 공정에서 중합된 비닐 방향족 단량체 공중합체의 팽창성 중합체 매트릭스의 중량을 기준으로 25 중량% 이상, 일부 경우에는 30 중량% 이상, 다른 경우에는 40 중량% 이상이고 일부 예에서는 50 중량% 이상을 포함할 수 있다. 팽창성 중합체 매트릭스에서 폴리올레핀 및 동일 공정에서 중합된 비닐 방향족 단량체 공중합체의 양은 상기 언급된 임의의 수치 사이의 임의의 수치 또는 범위일 수 있다.
다른 팽창성 중합체가 팽창성 중합체 매트릭스에 포함될 때, 이 중합체는 팽창성 중합체 매트릭스의 중량 기준으로 1 중량% 이상, 일부 경우에는 5 중량% 이상, 다른 경우에는 10 중량% 이상이고, 일부 예에서는 20 중량% 이상 그리고 다른 예에서는 25 중량% 이상으로 존재할 수 있다. 또한, 다른 팽창성 중합체는 팽창성 중합체 매트릭스 내에 이의 중량을 기준으로 75 중량% 이하, 일부 경우에는 70 중량% 이하, 다른 경우에는 60 중량% 이하이고, 일부 예에서는 50 중량% 이하로 존재할 수 있다.
본 발명에 따른 내하성 구조물의 양태는 도 1 및 2에 나타나고, 내하성 구조물 8은 1 내지 25 cm, 일부 경우에는 2 내지 20 cm, 다른 경우에는 2.5 내지 15 cm일 수 있는 너비 14를 보유하는 가장자리 12의 일반적으로 직사각형 판 형태인 팽창성 중합체 매트릭스 중심체를 포함한다. 중심체 10은 75 내지 150 cm, 일부 경우에는 90 내지 140 cm, 다른 경우에는 100 내지 130 cm이고, 일부 경우에는 80 내지 130 cm이며, 다른 경우에는 90 내지 120 cm의 40 인치 너비일 수 있는 최상부 16을 보유한다. 중심체 10의 바닥 부분 18은 바닥 부분 10에서 연결된 8 내지 15 cm, 일부 경우에는 9 내지 13 cm 길이의 다리 20-28을 포함한다.
다리 20-28 및 바닥 부분 18은 가장자리 12에 근접한 공간 42, 44, 46 및 48을 한정한다. 공간 42, 44, 46, 48은 다리 26-28, 다리 20, 23, 26, 다리 20-22 및 다리 22, 25, 28을 각각 가장자리 12로부터 분리시킨다.
본 발명의 양태에서, 공간 42, 44, 46, 48은 지게차 트럭의 튀어나온 부분(tongues)을 수용하기 위해 적용된다. 비제한 예로써, 포크리프트의 첫 번째 튀어나온 부분은 다리 20 및 다리 23 사이, 다리 21 및 다리 24 사이 및/또는 다리 22 및 다리 25 사이의 바닥 부분 18에 위치할 수 있고, 지게차의 두 번째 튀어나온 부분은 다리 26 및 다리 23 사이, 다리 27 및 다리 24 및/또는 다리 28 및 다리 25 사이에 위치할 수 있다. 지게차 트럭이 첫 번째 및 두 번째 튀어나온 부분을 올릴 때 각각의 튀어나온 부분의 표면은 바닥 부분 18의 표면과 접촉하고, 내하성 구조물 8 및 최상부 16에 쌓아올린 임의의 물품을 들어올리는 작용을 한다.
중심체 10은 상기 기술된 팽창성 중합체 매트릭스로부터 제조될 수 있기 때문에, 내하성 플렛폼으로 사용되는 충분한 구조적 강도를 보유한다.
소기의 표면 마감처리 및/또는 질감을 제공하고/하거나 반복된 사용으로 인한 인열을 최소화하기 위해서는 적합한 층 재료가 최상부 16 및 선택적으로 가장자리 12에 적용될 수 있다.
적용될 수 있는 적합한 층 재료는 고무 개질된 스티렌 중합체, 나일론과 같은 폴리아미드, 폴리프로필렌, 폴리에틸렌 및 이의 혼합물을 포함한다.
중심체 10에서 팽창성 중합체 매트릭스의 밀도는 5 이상, 일부 경우에는 10 이상 그리고 다른 경우에는 15 kg/m3 이상일 수 있고, 40 이하, 일부 경우에는 35 이하 그리고 다른 경우에는 30 kg/m3 이하일 수 있다. 본 발명의 양태에서 공간 42, 44, 46, 48에 근접한 부분에 해당하는 중심체 10에서의 팽창성 중합체 매트릭스의 밀도는 중심체 10의 나머지 부분에서의 팽창성 중합체 매트릭스 밀도보다 높다. 이러한 특징은 내하성 구조물 8의 가장 얇은 부분에서의 압력으로 인한 파손을 방지하는데 도움이 된다.
내하성 구조물은 스팀과 같은 가열 매체를 사용해서 팽창성 중합체 매트릭스 구슬을 가열함으로서 제조될 수 있다. 내하성 구조물의 임의의 부분의 소기의 밀도에 따라 상기 구슬은 5 내지 100, 일부 경우에느 10 내지 90, 다른 경우에는 20 내지 80, 일부 예에서는 30 내지 75 그리고 다른 예에서는 40 내지 70의 팽창 비율(팽창된 구슬 부피/최초 구슬 부피)로 팽창된다.
본 발명에 따른 팽창성 중합체 매트릭스 구슬은 구슬을 팽창하고 추가로 몰드 캐비티(cavity)에 이들을 팽창하고 성형해서 소기의 형태의 내하성 구조물로 생성될 수 있다. 생성된 내하성 구조물은 EPS 팔레트와 비교해서 탁월한 열 안전성, 내약품성 (예컨대, 내유성) 및 휨 강도를 보유한다.
본 발명의 양태에서(도시되지 않음), 홈 또는 채널이 최상부 16의 외주를 따르고, 홈 또는 채널의 첫 번째 가장자리가 모서리 12로부터 떨어져 있도록 홈 또는 채널이 몰드되거나 최상부 16의 표면에서 식각될 수 있다. 모서리 12로부터의 홈 또는 채널의 거리는 1 cm 이상, 일부 경우에는 2 cm 이상일 수 있고, 10 cm 이하, 일부 경우에는 8 cm 이하일 수 있다. 홈 또는 채널은 연속 또는 불연속일 수 있다.
본 발명의 특정 양태에서, 홈 또는 채널은 발포 패널(panel)을 수용해서 적용하기에 알맞은 너비 및 깊이를 보유한다. 발포 패널은 다리 20, 22, 28 및/또는 26의 일부의 바로 위에 최상부 16의 코너 섹션을 맞추기 위한 각도 및 아크(arc)를 형성할 수 있다.
대안적으로, 발포 패널은 다리 20 위에서 시작해서 다리 22 위에서 끝나고 다리 22 위에서 시작해서 다리 28 위에서 끝나며 다리 28 위에서 시작해서 다리 26 위에서 끝나고/끝나거나 다리 26 위에서 시작해서 다리 20 위에서 끝나는 최상부 16의 측면을 따라 연장될 수 있다. 패널의 길이는 상기 기술된 내하성 플렛폼 8의 넓이에 맞을 것이다. 패널의 높이는 5 cm 이상, 일부 경우에는 10 cm 이상 그리고 다른 경우에는 15 cm 이상일 수 있고, 450 cm 이하, 일부 경우에는 400 cm 이하, 다른 경우에는 350 cm 이하이고 일부 예에서는 310 cm 이하일 수 있다. 패널의 높이는 상기 언급된 임의의 수치 사이의 임의의 수치 또는 범위일 수 있다.
추가적인 양태에서, 최상부 패널은 내하성 구조물 8의 길이 및 너비와 거의 일치하는 것을 포함할 수 있다. 최상부 패널은 최상부 16에서의 홈 또는 채널과 일치하는 홈 또는 패널을 포함하고, 패널의 최상부 표면을 수용하기 위해 개조된다.
조립될 때, 내하성 구조물, 패널 및 최상부 패널은 박스 또는 오픈 박스 구조를 형성한다. 버클 또는 적합한 패스너(fastener)가 패널 및 구조물을 같이 고정하기 위해 사용될 수 있다. 대안적으로, 수축 포장이 제자리에 부품을 고정하기 위해 박스 또는 오픈 박스 구조물의 외부에 적용될 수 있다.
본 발명의 양태에서, 최상부 패널은 다리 20, 21, 22, 25, 28, 27, 26 및/또는 23의 해당 바닥 표면을 지나가는 홈 또는 채널을 포함하는 내하성 구조물 8일 수 있다.
본 발명의 또 다른 양태에서, 패널 및 최상부 패널은 본원에서 기술된 팽창성 중합체 매트릭스로 제조된다.
본 발명의 다른 양태에서, 패널 및 최상부 패널은 상기 기술된 하나 이상의 다른 팽창성 중합체로 제조된다.
패널 및/또는 최상부 패널은 내하성 구조물 8일 이동할 때 최상부 16에 놓여지거나 쌓인 물품을 미끄럼으로부터 방지한다.
본 발명은 특정 양태의 특정 세부사항을 참고로 기술되었다. 상기 세부사항은 본 발명의 범주를 제한하는 것으로 간주되지 않도록 한다.
도 1은 본 발명에 따른 내하성 플렛품 최상부의 전반적인 모습이다.
도 2는 본 발명에 따른 내하성 플렛폼 바닥의 전반적인 모습이다.
Claims (19)
- 기반부분 및 기반부분의 한 면에서 연장된 다수의 다리를 포함하는 내하성 플렛폼(platform)으로, 폴리올레핀 및 동일 공정에서 중합된 비닐 방향족 단량체의 공중합체(interpolymer)를 포함하는 팽창성 중합체 매트릭스를 포함하는 내하성 플렛폼.
- 제1항에 있어서, 팽창성 중합체 매트릭스가 다른 팽창성 중합체를 포함하는 내하성 플렛폼.
- 제1항에 있어서, 폴리올레핀이 저밀도 폴리에틸렌, 중밀도 폴리에틸렌, 고밀도 폴리에틸렌, 에틸렌 비닐 아세테이트 혼성중합체(copolymer), 에틸렌/프로필렌 혼성중합체, 폴리에틸렌과 폴리프로필렌의 배합물, 폴리에틸렌과 에틸렌/비닐 아세테이트 혼성중합체의 배합물, 및 폴리에틸렌과 에틸렌/프로필렌 혼성중합체의 배합물, 에틸렌-부틸 아크릴레이트 혼성중합체, 에틸렌-메틸 메트아크릴레이트 혼성중합체 및 이의 혼합물로 구성된 그룹 중에서 선택된 내하성 플렛폼.
- 제1항에 있어서, 비닐 방향족 단량체가 스티렌, 알파-메틸-스티렌, 에틸스티렌, 클로로스티렌, 브로모스티렌, 비닐톨루엔, 비닐벤젠, 및 이소프로필자일렌 및 이의 혼합물로 구성된 그룹 중에서 선택된 내하성 플렛폼.
- 제1항에 있어서, 폴리올레핀이 공중합체 수지 입자의 중량을 기준으로 20 중량% 내지 80 중량% 수준으로 공중합체 수지 입자에 존재하고, 비닐 방향족 단량체 또는 결과 중합체가 공중합체 수지 입자의 중량을 기준으로 20 중량% 내지 80 중량% 수준으로 공중합체 수지 입자에 존재하는 내하성 플렛폼.
- 제1항에 있어서, 팽창성 중합체 매트릭스가 발포제 및/또는 가소제를 포함하는 내하성 플렛폼.
- 제2항에 있어서, 다른 팽창성 중합체가 팽창성 폴리스티렌, 팽창성 폴리올레핀, 수지내 연속상이 스티렌계 중합체이고 분산상이 고무인 고무 개질된 스티렌계 중합체, 수지내 연속상이 고무이고 분산상이 스티렌계 중합체인 고무 개질된 스티렌계 중합체, 폴리페닐렌 옥사이드, 및 이의 혼합물 그리고 배합물로 구성된 그룹 중에서 선택된 내하성 플렛폼.
- 제2항에 있어서, 팽창성 중합체를, 폴리올레핀과 동일 공정에서 중합된 비닐 방향족 단량체의 공중합체인 팽창성 중합체 매트릭스의 중량을 기준으로 25 내지 99 중량% 및 다른 팽창성 중합체의 팽창성 중합체 매트릭스의 중량을 기준으로 1 내지 75 중량%로 포함하는 내하성 플렛폼.
- 제2항에 있어서, 내하성 플렛폼이 1 내지 25 cm의 가장자리, 75 내지 150 cm의 길이 및 65 내지 140 cm의 너비를 보유한 직사각형 형태인 내하성 플렛폼.
- 제1항에 있어서, 층 재료가 플렛폼의 최상부에 적용된 내하성 플렛폼.
- 제1항에 있어서, 연속이거나 비연속인 홈 또는 채널이 기반부분의 최상부 표면에 몰드되거나 식각되서, 홈 또는 채널이 최상부의 외주를 따르고 홈 또는 채널의 첫 번째 가장자리가 기반부분의 외부 가장자리와 이격되어 있는 내하성 플렛폼.
- 제11항에 있어서, 홈 또는 채널에 맞도록 개조된 다수의 패널을 포함하는 내하성 플렛폼.
- 제12항에 있어서, 내하성 구조물의 너비 및 길이와 일치하고, 최상부의 홈 또는 채널과 일치하는 홈 또는 채널을 포함하며, 패널의 최상부 표면을 수용하도록 개조된 최상부 패널을 포함하여 박스 또는 오픈 박스 구조물을 생성하는 내하성 플렛폼.
- 기반부분 및 기반부분의 한 면에서 연장된 다수의 다리를 포함하는 내하성 플렛폼으로, 고무가 연속상이고 스티렌계 중합체는 분산상인 고무 개질된 스티렌계 중합체를 포함하는 팽창성 중합체 매트릭스를 포함하는 내하성 플렛폼.
- 제14항에 있어서, 스티렌계 중합체가 스티렌, 알파-메틸스티렌, 에틸스티렌, 클로로스티렌, 브로모스티렌, 비닐톨루엔, 비닐벤젠, 및 이소프로필자일렌 및 이의 혼합물로 구성된 그룹 중에서 선택된 비닐 방향족 단량체의 중합반응으로부터의 잔류물을 포함하는 것인 내하성 플렛폼.
- 제14항에 있어서, 탄성 중합체가 하나 이상의 공액 디엔 및 하나 이상의 불포화 니트릴, 하나 이상의 극성 단량체, 불포화 카복실산의 알킬 에스테르, 불포화 카복실산의 알콕시알킬 에스테르, 아크릴아미드, 메트아크릴아미드; N-치환된 아크릴아미드, 비닐 클로라이드; 방향족 비닐 단량체 및 이의 혼합물을 포함하는 혼성 중합체로 구성된 그룹 중에서 선택된 내하성 플렛폼.
- 제14항에 있어서, 팽창성 중합체 매트릭스가 발포제 및/또는 가소제를 포함하는 내하성 플렛폼.
- 제14항에 있어서, 내하성 플렛폼이 1 내지 25 cm의 가장자리, 75 내지 150 cm의 길이 및 65 내지 140 cm의 너비를 보유하는 직사각형 형태인 내하성 플렛폼.
- 제14항에 있어서, 플렛폼의 최상부에 적용된 층 재료를 포함하는 내하성 플 렛폼.