KR20070099271A - A phosphor paste composition, a phosphor layer prepared therefrom and a plasma displaly panel comprising the same - Google Patents

A phosphor paste composition, a phosphor layer prepared therefrom and a plasma displaly panel comprising the same Download PDF

Info

Publication number
KR20070099271A
KR20070099271A KR1020060030505A KR20060030505A KR20070099271A KR 20070099271 A KR20070099271 A KR 20070099271A KR 1020060030505 A KR1020060030505 A KR 1020060030505A KR 20060030505 A KR20060030505 A KR 20060030505A KR 20070099271 A KR20070099271 A KR 20070099271A
Authority
KR
South Korea
Prior art keywords
phosphor
paste composition
polyethylene glycol
phosphor paste
surfactant
Prior art date
Application number
KR1020060030505A
Other languages
Korean (ko)
Inventor
유영길
이성용
Original Assignee
삼성에스디아이 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 삼성에스디아이 주식회사 filed Critical 삼성에스디아이 주식회사
Priority to KR1020060030505A priority Critical patent/KR20070099271A/en
Publication of KR20070099271A publication Critical patent/KR20070099271A/en

Abstract

A phosphor paste composition, a phosphor layer prepared therefrom, and a plasma display panel comprising the same are provided to improve brightness of a total panel by improving a filling ratio of a blue phosphor having a plate-shaped structure. A phosphor paste composition includes phosphor powder, a binder resin, and a solvent. The solvent includes a polyethylene glycol type nonionic surfactant, a sorbitan ester, a polycarboxyl acid salt type polymer surfactant or a mixture of the polyethylene glycol type nonionic surfactant, the sorbitan ester, and the polycarboxyl acid salt type polymer surfactant. The content of the polyethylene glycol type nonionic surfactant, the sorbitan ester, the polycarboxyl acid salt type polymer surfactant, and the mixture of the polyethylene glycol type nonionic surfactant, the sorbitan ester, and the polycarboxyl acid salt type polymer surfactant corresponds to 3 weight percent to 20 weight percent of the total amount of the phosphor paste composition.

Description

형광체 페이스트 조성물, 그로부터 제조된 형광체층 및 이를 포함하는 플라즈마 디스플레이 패널 {A phosphor paste composition, a phosphor layer prepared therefrom and a plasma displaly panel comprising the same} A phosphor paste composition, a phosphor layer prepared there from and a plasma displaly panel comprising the same}

도 1은 본 발명에 따라서 제조된 형광체층을 포함하는 플라즈마 디스플레이 패널을 도시하는 부분절개 분리사시도이다.1 is a partial cutaway perspective view showing a plasma display panel including a phosphor layer prepared according to the present invention.

<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>

110: 전면 패널 111: 전면 기판110: front panel 111: front substrate

112: Y 전극 113: X 전극112: Y electrode 113: X electrode

114: 유지 전극쌍 115: 전방 유전체층114: sustain electrode pair 115: front dielectric layer

116: 보호막 120: 배면 패널116: protective film 120: back panel

121: 배면 기판 122: 어드레스 전극121: back substrate 122: address electrode

123: 후방 유전체층 124: 격벽123: rear dielectric layer 124: partition wall

125: 형광체층 126: 발광 셀125: phosphor layer 126: light emitting cell

본 발명은 형광체 페이스트 조성물, 그로부터 제조된 형광체층 및 이를 포함 하는 플라즈마 디스플레이 패널에 관한 것으로서, 더욱 구체적으로는 형광체 분말 중 판상 형광체 분말의 비율이 40 내지 60 중량%이고, 폴리에틸렌 글리콜형 비이온 계면활성제, 솔비탄 에스테르, 폴리카르복실산염형 고분자 계면활성제 또는 그 혼합물을 페이스트 중에 포함함으로써, 형광막내 형광체의 충진율이 획기적으로 개선된 형광체 페이스트 조성물, 그로부터 제조된 형광체층 및 이를 포함하는 플라즈마 디스플레이 패널에 관한 것이다.The present invention relates to a phosphor paste composition, a phosphor layer prepared therefrom, and a plasma display panel including the same. More specifically, the ratio of the plate-like phosphor powder in the phosphor powder is 40 to 60% by weight, and the polyethylene glycol type nonionic surfactant is used. , By containing a sorbitan ester, a polycarboxylate-type polymer surfactant or a mixture thereof in a paste, to significantly improve the filling rate of the phosphor in the fluorescent film, a phosphor layer prepared therefrom, and a plasma display panel comprising the same will be.

플라즈마 디스플레이 패널은 액정 패널과 비교할 때에 응답속도가 빠르고, 대형화가 용이하여 현재 다양한 분야에 이용되고 있다.Plasma display panels are used in various fields because they are faster in response and larger in size than liquid crystal panels.

이러한 플라즈마 디스플레이 패널은 유리 기판 상에 어드레스 전극, 유전체층, 및 격벽을 형성하고, 격벽으로 구분되는 방전셀 내에 형광체층을 형성한 배면판과 유리 기판 상에 유지 전극, 유전체, 및 보호막인 MgO층을 형성한 전면판을 봉착하여 패널을 제작하고, 그 내부에 Xe, Ne 등의 불활성 가스를 봉입한 구조로 되어 있다. 여기에 구동용 집적회로를 실장하고 모듈화한 뒤, 영상 처리회로 또는 튜너를 세트화시킴으로써 디스플레이 장치가 완성된다.The plasma display panel includes an address electrode, a dielectric layer, and a partition wall formed on a glass substrate, and a back plate on which a phosphor layer is formed in a discharge cell divided into partition walls, and a sustain electrode, a dielectric, and a protective film MgO layer on a glass substrate. The formed front plate is sealed to form a panel, and the structure is such that inert gas such as Xe or Ne is sealed therein. The display device is completed by mounting and modularizing a driving integrated circuit therein and then setting an image processing circuit or tuner.

일반적으로, 플라즈마 디스플레이 패널의 형광체층은 격벽으로 구분된 홈 또는 공간에 형광체 페이스트를 스크린 인쇄 방법 또는 디스펜서법 등으로 충전시킨 다음, 건조 및 소성 공정을 수행함으로써, 상기 격벽의 측면 및 바닥부에 형성된다.In general, the phosphor layer of the plasma display panel is formed by filling a phosphor paste into a groove or a space separated by a partition by a screen printing method or a dispenser method, and then performing a drying and baking process to form the side and bottom portions of the partition. do.

기존의 형광체 페이스트는 형광체 분말, 셀룰로오스 수지 및 용매를 혼합한 것이 일반적으로 사용되어 왔으며, 이는 스크린 인쇄법에 의해서 형광체층을 형성 하는 경우가 가장 빈번하였기 때문이다. 일반적으로, 이러한 상이 다른 비이클과 형광체 분말 및 유기 용제를 골고루 혼합하기 위해서 믹서 또는 3롤 밀과 같은 혼합기를 이용하여 페이스트화하였다.In the conventional phosphor paste, a mixture of phosphor powder, cellulose resin, and a solvent has been generally used, since the phosphor layer is most frequently formed by screen printing. Generally, these phases were pasted using a mixer or mixer such as a three roll mill to evenly mix different vehicles with phosphor powder and organic solvent.

그러나, 형광체 분말의 제특성으로 인해서 형광체끼리 응집이 일어나, 이를 도포할 경우 인쇄시 막히는 등의 원인으로 인해서 셀내 형광막의 두께에 불균형을 초래하는 문제점이 있었고, 청색 형광체 중 대표적 형광체인 BAM (BaMgAl10017:Eu) 형광체의 경우는 그 구조가 판상인 관계로 셀 내 충진율이 양호하지 못하다는 문제점이 있었다. 이와 같이, 충진율이 좋지 못한 형광체는 셀내 형광막을 치밀하게 구성하지 못하고, 발광 휘도를 낮추는 문제점이 있다.However, due to various characteristics of the phosphor powder, agglomeration between the phosphors occurs, and when the coating is applied, there is a problem of causing an imbalance in the thickness of the fluorescent film in the cell due to clogging during printing, and BAM (BaMgAl10017: In the case of Eu) phosphor, there is a problem in that the filling rate in the cell is not good because its structure is plate-shaped. As described above, the phosphor having poor filling rate does not form a fluorescent film in a cell precisely, and has a problem of lowering luminance.

따라서, 종래에는 이러한 문제점을 해결하기 위해서 페이스트 내의 형광체 분말량을 증가시키려는 등의 시도도 있었지만, 이 경우 판상인 형광체 분말 자체의 특성으로 인해서 점도가 비약적으로 증가하여 많은 단점들을 초래하였다.Therefore, in order to solve such a problem, there have been attempts to increase the amount of phosphor powder in the paste. However, in this case, due to the characteristics of the plate-shaped phosphor powder itself, the viscosity is dramatically increased, resulting in many disadvantages.

따라서, 본 발명은 상기 종래기술의 문제점을 해결하여, 형광막내 형광체의 충진율을 효과적으로 개선할 수 있으며, 특히 판상의 구조를 갖는 청색 형광체의 충진율을 개선하여 형광체 분말을 45 중량% 이상으로 혼합시킬 수 있고, 결과적으로 형성된 형광체막은 단위 셀에서 발광하는 광량이 증가하여 전체 패널의 휘도를 현저히 향상시킬 수 있는 형광체 페이스트 조성물, 그로부터 제조된 형광체층 및 이를 포함하는 플라즈마 디스플레이 패널을 제공하고자 한다.Accordingly, the present invention can solve the problems of the prior art, and can effectively improve the filling rate of the phosphor in the fluorescent film, in particular to improve the filling rate of the blue phosphor having a plate-like structure can be mixed with the phosphor powder at 45% by weight or more The resultant phosphor film is to provide a phosphor paste composition, a phosphor layer manufactured therefrom, and a plasma display panel including the same, in which the amount of light emitted from a unit cell is increased to significantly improve the brightness of the entire panel.

본 발명의 일 구현예는 상기 기술적 과제를 달성하기 위하여,One embodiment of the present invention to achieve the above technical problem,

형광체 분말, 바인더 수지 및 용매를 포함하는 형광체 페이스트 조성물에 있어서, 상기 용매가 폴리에틸렌 글리콜형 비이온 계면활성제, 솔비탄 에스테르, 폴리카르복실산염형 고분자 계면활성제 또는 그 혼합물을 포함하는 것을 특징으로 하는 형광체 페이스트 조성물을 제공한다.A phosphor paste composition comprising a phosphor powder, a binder resin, and a solvent, wherein the solvent comprises a polyethylene glycol nonionic surfactant, a sorbitan ester, a polycarboxylate type polymer surfactant, or a mixture thereof. It provides a paste composition.

본 발명은 또한 상기 형광체 페이스트 조성물을 이용하여 제조된 형광체층을 제공한다.The present invention also provides a phosphor layer prepared using the phosphor paste composition.

본 발명은 또한 상기 형광체층을 포함하는 플라즈마 디스플레이 패널을 제공한다.The present invention also provides a plasma display panel including the phosphor layer.

이하, 본 발명에 대하여 더욱 상세하게 설명하기로 한다.Hereinafter, the present invention will be described in more detail.

본 발명에 따른 형광체 페이스트 조성물은, 형광체 분말, 바인더 수지 및 용매를 포함하는 형광체 페이스트 조성물에 있어서, 상기 용매가 폴리에틸렌 글리콜형 비이온 계면활성제, 솔비탄 에스테르, 폴리카르복실산염형 고분자 계면활성제 또는 그 혼합물을 포함하는 것을 특징으로 한다.The phosphor paste composition according to the present invention is a phosphor paste composition comprising a phosphor powder, a binder resin and a solvent, wherein the solvent is a polyethylene glycol type nonionic surfactant, a sorbitan ester, a polycarboxylate type polymer surfactant, or a It is characterized by including a mixture.

본 발명에서는 형광막내 형광체의 충진율을 높이고, 페이스트의 분산성을 개선하기 위해서 폴리에틸렌 글리콜형 비이온 계면활성제, 솔비탄 에스테르, 폴리카르복실산염형 고분자 계면활성제 또는 그 혼합물을 첨가한다. 이러한 첨가에 의해서 본 발명에 따른 형광체 페이스트 조성물은 형광체 분말을 40 중량% 이상으로 포함하면서도 우수한 가소성을 유지할 수 있게 된다.In the present invention, polyethylene glycol type nonionic surfactants, sorbitan esters, polycarboxylate type polymer surfactants or mixtures thereof are added to increase the filling rate of the phosphor in the fluorescent film and to improve the dispersibility of the paste. By such addition, the phosphor paste composition according to the present invention can maintain the excellent plasticity while including the phosphor powder in more than 40% by weight.

본 발명은, 특히 판상의 구조를 갖는 청색 형광체의 충진율을 개선하여 형광 체 분말을 45 중량% 이상으로 혼합시킬 수 있고, 결과적으로 형성된 형광체막은 단위 셀에서 발광하는 광량이 증가하여 전체 패널의 휘도가 현저히 향상된다. 또한, 격벽을 착색하여 사용하는 경우에, 격벽에서의 반사를 저감시켜 휘도가 줄어드는 것을 방지할 수 있을 뿐만 아니라, 단위 셀 내에 치밀한 막 형성이 가능하기 때문에 방전 공간이 넓어짐에 따라 단위 형광체의 수명 또한 향상된다.According to the present invention, in particular, the filling rate of the blue phosphor having a plate-like structure can be improved to mix the phosphor powder at 45 wt% or more, and the resulting phosphor film increases the amount of light emitted from the unit cell, thereby increasing the luminance of the entire panel. Significantly improved. In addition, when the barrier ribs are colored, the reflection of the barrier ribs can be reduced to prevent the luminance from being reduced, and a dense film can be formed in the unit cell, so that the lifetime of the unit phosphor is increased as the discharge space is increased. Is improved.

한편, 상기 폴리에틸렌 글리콜형 비이온 계면활성제, 솔비탄 에스테르, 폴리카르복실산염형 고분자 계면활성제 또는 그 혼합물의 함량은 전체 페이스트 조성물 중 3 중량% 내지 20 중량%인 것이 바람직한데, 상기 비율이 3 중량% 미만인 경우에는 페이스트 내에서 계면활성제의 효과가 나타나지 않는 문제점이 있고, 20 중량%를 초과하는 경우에는 고분자 계면활성제의 잔탄으로 인하여 발광 효율이 낮아지고, 수명에 치명적인 문제점이 있어서 바람직하지 않다.On the other hand, the content of the polyethylene glycol nonionic surfactant, sorbitan ester, polycarboxylate-type polymer surfactant or a mixture thereof is preferably 3% to 20% by weight of the total paste composition, the ratio is 3% by weight If the amount is less than%, there is a problem in that the effect of the surfactant does not appear in the paste, and if it exceeds 20% by weight, the luminous efficiency is lowered due to the xanthan of the polymer surfactant, which is not preferable because of a fatal problem.

바람직하게는, 상기 형광체 분말은 판상 형광체 분말의 비율이 40 중량% 내지 60 중량%인데, 상기 비율이 40 중량% 미만인 경우에는 발광 휘도가 낮아지는 문제점이 있고, 60 중량%를 초과하는 경우에는 격벽 셀 내의 형광체 비율이 증가하면서 방전 공간이 좁아짐에 따라 저방전 현상이 야기되는 문제점이 있어서 바람직하지 않다.Preferably, the phosphor powder has a ratio of 40% by weight to 60% by weight of the plate-shaped phosphor powder, when the ratio is less than 40% by weight, there is a problem that the emission luminance is lowered, and when the content exceeds 60% by weight, the partition wall As the proportion of the phosphor in the cell increases, the discharge space is narrowed, which causes a low discharge phenomenon, which is not preferable.

본 발명에 따른 형광체 페이스트 조성물이 상기 함량의 판상 형광체 분말을 포함하는 경우에, 그 점도는 전단 속도 30 (1/s)에서 대략 20 (Pa·s)이다.In the case where the phosphor paste composition according to the present invention comprises the above-mentioned plate-shaped phosphor powder, the viscosity is approximately 20 (Pa · s) at a shear rate of 30 (1 / s).

또한, 형광체 분말의 평균 입경은 1㎛ 내지 7㎛인 것이 바람직한데, 형광체 분말의 평균 입경이 1㎛ 미만인 경우에는 형광체를 제조하여 불순물 성분을 분리하 는 공정 및 세정 공정시에 필터링 등의 시간이 오래 걸리고, 방법이 까다로워지는 문제점이 있고, 형광체 분말의 평균 입경이 7㎛를 초과하는 경우에는 인쇄 특성이 열화된다는 문제점이 있기 때문에 바람직하지 않다.In addition, the average particle diameter of the phosphor powder is preferably 1 μm to 7 μm. However, when the average particle diameter of the phosphor powder is less than 1 μm, the time required for filtering and the like in the process of separating the impurity components by producing the phosphor and in the cleaning process It takes a long time, the method is difficult, and if the average particle diameter of the phosphor powder exceeds 7 占 퐉, it is not preferable because there is a problem of deterioration in printing characteristics.

본 발명에 따른 조성물에 있어서, 각 성분의 함량은 형광체 분말 100 중량부에 대해서, 바인더 수지는 1 내지 50 중량부, 용매는 40 내지 400 중량부인 것이 바람직하다.In the composition according to the present invention, the content of each component is preferably 1 to 50 parts by weight of the binder resin and 40 to 400 parts by weight of the solvent with respect to 100 parts by weight of the phosphor powder.

형광체 분말의 함량에 대비하여, 바인더 수지 또는 용매의 함량이 너무 크거나 작은 경우에는 초기 점도가 너무 높거나 낮게 되어, 원하는 인쇄성을 얻기 힘들게 되어 바람직하지 않다.In contrast to the content of the phosphor powder, when the content of the binder resin or the solvent is too large or small, the initial viscosity is too high or low, so that it is difficult to obtain the desired printability, which is not preferable.

본 발명에서 사용하는 형광체 분말은 진공 자외선에 의하여 여기되는 스펙트럼을 갖는 형광체라면 어느 것이든 사용가능하며, 이에 제한되는 것은 아니지만, 적색 형광체 분말로는 (Y,Gd)BO3:Eu, Y2O3:Eu, Y(P,V)O4:Eu, 및 (Y,Gd)2O3:Eu로 이루어진 군으로부터 선택된 적어도 하나 이상의 물질이, 녹색을 나타내는 형광체 분말로는 Zn2SiO4:Mn, BaAl12O19:Mn, 및 YBO3:Tb로 이루어진 군으로부터 선택된 적어도 하나 이상의 물질이, 청색을 나타내는 형광체 분말로는 BaMgAl14O24:Eu 및 SrMg(SiO2)2:Eu로 이루어진 군으로부터 선택된 적어도 하나 이상의 물질이 사용될 수 있다.The phosphor powder used in the present invention may be used as long as the phosphor having a spectrum excited by vacuum ultraviolet rays, but is not limited thereto, and the red phosphor powder may be (Y, Gd) BO 3 : Eu, Y 2 O At least one substance selected from the group consisting of 3 : Eu, Y (P, V) O 4 : Eu, and (Y, Gd) 2 O 3 : Eu is a phosphor powder in which green color is represented by Zn 2 SiO 4 : Mn , At least one substance selected from the group consisting of BaAl 12 O 19 : Mn, and YBO 3 : Tb, the phosphor powder exhibiting a blue color is selected from the group consisting of BaMgAl 14 O 24 : Eu and SrMg (SiO 2 ) 2 : Eu At least one or more materials selected may be used.

본 발명에 따른 조성물 중, 바인더 수지는 분자량 100,000 내지 5,000,000의 아크릴계 또는 비닐계 고분자 수지인 것을 특징으로 한다.In the composition according to the present invention, the binder resin is characterized in that the acrylic or vinyl polymer resin having a molecular weight of 100,000 to 5,000,000.

본 발명에서 사용가능한 아크릴계 수지로는, 이에 제한되는 것은 아니지만, 폴리메틸메타크릴레이트, 폴리메틸아크릴레이트, 폴리에틸아크릴레이트, 폴리에틸메타크릴레이트, 폴리노말프로필아크릴레이트, 폴리노말프로필메타크릴레이트, 폴리이소프로필아크릴레이트, 폴리이소프로틸 메타크릴레이트, 폴리노말부틸아크릴레이트, 폴리노말부틸메타크릴레이트, 폴리씨클로헥실아크릴레이트, 폴리씨클로헥실메타크릴레이트, 폴리라우릴아크릴레이트, 폴리라우릴메타크릴레이트, 폴리스테아릴아크릴레이트, 및 폴리스테아릴메타크릴레이트 등을 예로 들 수 있으며, 이러한 수지의 단량체들을 두개 이상 공중합하여 사용할 수도 있다.Examples of the acrylic resin usable in the present invention include, but are not limited to, polymethyl methacrylate, polymethyl acrylate, polyethyl acrylate, polyethyl methacrylate, polynormal propyl acrylate, poly normal propyl methacrylate. , Polyisopropyl acrylate, polyisopropyl methacrylate, polynormal butyl acrylate, poly normal butyl methacrylate, polycyclohexyl acrylate, polycyclohexyl methacrylate, polylauryl acrylate, polylauryl Methacrylate, polystearyl acrylate, polystearyl methacrylate, and the like. Examples thereof may be used by copolymerizing two or more monomers of such a resin.

또한, 비닐계 수지로는 폴리에틸렌, 폴리프로필렌, 폴리스티렌, 폴리비닐알콜, 폴리부틸아세테이트, 및 폴리비닐피롤리돈 등을 예로 들 수 있다.In addition, examples of the vinyl resin include polyethylene, polypropylene, polystyrene, polyvinyl alcohol, polybutyl acetate, polyvinylpyrrolidone, and the like.

또한, 상기 아크릴계 수지 및 비닐계 수지는 단독으로도 사용될 수 있지만, 경우에 따라서는 혼합하여 사용될 수도 있다.In addition, the acrylic resin and the vinyl resin may be used alone, but in some cases, may be used by mixing.

고분자 바인더 수지의 분자량은 100,000 내지 5,000,000의 값을 가지는데, 분자량이 100,000 미만인 경우에는 페이스트로 제조시에 점도가 작아서 형광체가 쉽게 침적되며, 분자량이 5,000,000을 초과하는 경우에는 페이스트의 점도가 크게 상승하여 인쇄에 적합한 유동성을 확보할 수가 없다는 문제점이 있어서 바람직하지 않다.The molecular weight of the polymer binder resin has a value of 100,000 to 5,000,000, but when the molecular weight is less than 100,000, when the paste is manufactured into a paste, the phosphor is easily deposited, and when the molecular weight exceeds 5,000,000, the viscosity of the paste increases significantly. It is not preferable because there is a problem in that fluidity suitable for printing cannot be secured.

본 발명에 따른 페이스트 조성물에 있어서, 용매는 아크릴계 수지 또는 비닐계 수지를 용해시킬 수 있는 용매라면 어느 것이든 가능하며, 예를 들어 터핀올, 부틸카비톨아세테이트, 에틸렌글리콜, 디에틸렌글리콜, 에틸에테르아세테이트, 벤 질알코올, 톨루엔, 메틸에틸케톤, 또는 그 혼합물 등의 용매를 사용할 수 있다.In the paste composition according to the present invention, the solvent may be any solvent capable of dissolving an acrylic resin or a vinyl resin, and for example, terpinol, butyl carbitol acetate, ethylene glycol, diethylene glycol, and ethyl ether. A solvent such as acetate, benzyl alcohol, toluene, methyl ethyl ketone, or a mixture thereof can be used.

본 발명에 따른 형광체 페이스트 조성물은, 형광체 분말, 바인더 수지 및 용매 이외에도, 페이스트의 유동 특성을 향상시키기 위한 Alcosperse 602-N과 같은 아크릴계 분산제, BYK 307과 같은 실리콘계 소포제, BYK 320 또는 SK-UCB사의 HS-70과 같은 평활제, Irganox 1010과 같은 산화 방지제, 및 디옥틸프탈레이트와 같은 가소제 등으로 이루어진 군으로부터 선택된 하나 이상의 첨가제를 포함할 수도 있다.The phosphor paste composition according to the present invention is, in addition to the phosphor powder, the binder resin and the solvent, an acrylic dispersant such as Alcosperse 602-N for improving the flow characteristics of the paste, a silicone antifoaming agent such as BYK 307, BYK 320 or SK-UCB Corporation HS. And one or more additives selected from the group consisting of a leveling agent such as -70, an antioxidant such as Irganox 1010, a plasticizer such as dioctylphthalate, and the like.

상기 첨가제의 함량은 형광체 페이스트 조성물 총중량에 대해서 5 중량% 이하의 함량으로 포함되는 것이 바람직한데, 첨가제의 함량이 5 중량%를 초과하는 경우에는 인쇄성의 저하, 더욱 심각하게는 잔탄 등의 문제점을 초래하기 때문에 바람직하지 않다.The content of the additive is preferably included in an amount of 5% by weight or less based on the total weight of the phosphor paste composition. When the content of the additive exceeds 5% by weight, the printability is reduced, and more seriously, xanthan is caused. It is not preferable because it is.

본 발명은 다른 구현예에서, 상기 형광체 페이스트 조성물을 이용하여 제조된 형광체층 및 상기 형광체층을 포함하는 플라즈마 디스플레이 패널을 제공한다.In another embodiment, the present invention provides a phosphor layer prepared using the phosphor paste composition and a plasma display panel including the phosphor layer.

도 1에는 본 발명에 따른 형광체층을 포함하는 플라즈마 디스플레이 패널의 구체적인 구조가 도시되어 있다.1 illustrates a specific structure of a plasma display panel including a phosphor layer according to the present invention.

도 1을 참조하면, 본 발명에 따른 플라즈마 디스플레이 패널은 전면 패널 (110) 및 배면 패널 (120)을 포함하는 구조로 되어 있다. 상기 전면 패널 (110)은 전면 기판 (111), 상기 전면 기판의 배면 (111a)에 형성된 Y전극 (112)과 X전극 (113)을 구비한 유지 전극쌍 (114)들, 상기 유지 전극쌍들을 덮는 전방 유전체층 (115), 및 상기 전방 유전체층을 덮는 보호막 (116)을 구비한다. 상기 Y전극 (112)과 X전극 (113) 각각은, ITO 등으로 형성된 투명 전극 (112b, 113b); 명암 향상을 위한 흑색 전극 (미도시) 및 도전성을 부여하는 백색 전극 (미도시)으로 구성되는 버스 전극 (112a, 113a)을 구비한다. 상기 버스 전극 (112a, 113a)들은 PDP의 좌우측에 배치된 연결 케이블과 연결된다.Referring to FIG. 1, a plasma display panel according to the present invention has a structure including a front panel 110 and a back panel 120. The front panel 110 includes a front electrode 111, sustain electrode pairs 114 including a Y electrode 112 and an X electrode 113 formed on the rear surface 111a of the front substrate, and the sustain electrode pairs. A covering front dielectric layer 115 and a protective film 116 covering the front dielectric layer. Each of the Y electrode 112 and the X electrode 113 includes: transparent electrodes 112b and 113b formed of ITO or the like; Bus electrodes 112a and 113a constituted by black electrodes (not shown) for improving contrast and white electrodes (not shown) to impart conductivity are provided. The bus electrodes 112a and 113a are connected to connection cables disposed on the left and right sides of the PDP.

상기 배면 패널 (120)은 배면 기판 (121), 배면 기판의 전면 (121a)에 상기 유지 전극쌍과 교차하도록 형성된 어드레스 전극 (122)들, 상기 어드레스 전극들을 덮는 후방 유전체층 (123), 상기 후방 유전체층 상에 형성되어 발광 셀 (126)들을 구획하는 격벽 (124)을 구비하며, 상기 어드레스 전극 (122)들은 플라즈마 디스플레이 패널의 상하측에 배치된 연결 케이블과 연결된다.The rear panel 120 includes a rear substrate 121, address electrodes 122 formed on the front surface 121a of the rear substrate to intersect the pair of storage electrodes, a rear dielectric layer 123 covering the address electrodes, and the rear dielectric layer. The barrier ribs 124 are formed on and partition the light emitting cells 126, and the address electrodes 122 are connected to connection cables disposed above and below the plasma display panel.

상기 전면 패널 (110) 및 배면 패널 (120) 사이의 발광 셀 (126) 내에는 본 발명에 따른 형광체 페이스트 조성물을 사용하여 제조된 형광체층 (125)이 배치된다.In the light emitting cell 126 between the front panel 110 and the back panel 120, a phosphor layer 125 prepared using the phosphor paste composition according to the present invention is disposed.

본 발명에 따른 플라즈마 디스플레이 패널은, 배면 기판 상에 어드레스 전극, 유전체층 및 격벽을 형성하는 단계; 상기 격벽 상에 본 발명에 따른 형광체 페이스트 조성물을 도포하고 소성하여 형광체층을 형성함으로써 배면 패널을 제조하는 단계; 전면 기판 상에 유지 전극, 유전체 및 보호층을 형성함으로써 전면 패널을 제조하는 단계; 및 상기 배면 패널 및 상기 전면 패널을 봉착하는 단계에 의해서 제조될 수 있다.According to the present invention, a plasma display panel includes: forming an address electrode, a dielectric layer, and a partition on a rear substrate; Manufacturing a back panel by applying and firing the phosphor paste composition according to the present invention on the partition to form a phosphor layer; Fabricating a front panel by forming a sustain electrode, a dielectric, and a protective layer on the front substrate; And sealing the back panel and the front panel.

일반적으로, 플라즈마 디스플레이 패널의 형성체층을 형성하는 방법에는 스크린 인쇄법, 디스펜서법, 저압 토출법, 감광성 페이스트법 또는 잉크젯법 등이 있 는데, 본 발명에 따른 플라즈마 디스플레이 패널의 제조방법에서는, 이 중에서 스크린 인쇄법, 디스펜서법 또는 저압 토출법을 사용하는 것이 바람직하다.In general, the method of forming the forming layer of the plasma display panel includes a screen printing method, a dispenser method, a low pressure discharge method, a photosensitive paste method or an inkjet method, and the like, in the method of manufacturing a plasma display panel according to the present invention, It is preferable to use the screen printing method, the dispenser method or the low pressure discharge method.

여기에서, 스크린 인쇄법이란, 비단, 금속, 화학 섬유의 천을 팽팽하게 하여 스크린으로 하고, 비화선부 (非畵線部)가 되는 부분을 UV 수지 또는 아교재로 덮어씌운 다음, 그 위에서 페이스트를 도포한 후, 스퀴즈로 페이스트를 밀어내어 인쇄하는 방법을 의미하며, 이러한 공정을 3회 반복함으로써, R, G 및 B의 형광체층을 형성하게 된다. 또한, 디스펜서법이란, 복수의 노즐을 가지는 꼭지쇠의 토출 노즐 선단으로부터 압력을 가하여 형광체 페이스트를 토출하고, 직접 격벽 사이의 홈에 페이스트를 충전하여 패턴을 형성하는 방법을 의미하며, 이러한 공정을 3회 반복함으로써, R, G 및 B의 형광체층을 형성하게 된다.Here, the screen printing method refers to a screen made of silk, metal, and chemical fiber, which is stretched to form a screen, and a portion of the non-fire line is covered with a UV resin or a glue, and then the paste is applied thereon. Then, it means a method of printing by pushing out the paste with a squeeze, by repeating this process three times, to form a phosphor layer of R, G and B. In addition, the dispenser method means a method of discharging the phosphor paste by applying pressure from the discharging nozzle tip of the clasp having a plurality of nozzles, and filling the paste directly into the grooves between the partition walls to form a pattern. By repeating once, the phosphor layers of R, G, and B are formed.

본 발명에 따른 방법에서, 상기 도포된 형광체층은 건조 장치를 통과시킴으로써 고비점의 유기 용매가 건조되며, 이와 같이 건조된 형광체층은 최종적으로 소성됨으로써, 형광체 페이스트 중의 바인더 수지 성분이 분해 제거된다.In the method according to the present invention, the coated phosphor layer is dried by passing through a drying apparatus, and the organic solvent having a high boiling point is dried, and the thus dried phosphor layer is finally baked, so that the binder resin component in the phosphor paste is decomposed and removed.

상기 소성 단계는 400℃ 내지 450℃의 온도에서 10분 내지 1시간 동안 수행되는 것이 바람직한다. 소성 온도가 상기 범위 미만인 경우에는 바인더 수지의 분재가 불충분해지므로, 잔류물에 의한 발광 휘도 저하가 발생되는 문제점이 있고, 또한 소성 온도가 상기 범위를 초과하는 경우에는 형광체가 열화되어 발광 휘도를 저하시키는 문제점이 있으므로 바람직하지 않다.The firing step is preferably performed for 10 minutes to 1 hour at a temperature of 400 ℃ to 450 ℃. When the firing temperature is less than the above range, the bonsai of the binder resin is insufficient, and thus, there is a problem of lowering the luminance of light emitted by the residue. Further, when the firing temperature exceeds the above range, the phosphor deteriorates and the emission luminance is lowered. It is not preferable because there is a problem to make.

본 발명에서는 상술한 바와 같이 400℃ 근처에서 완전 분해되는 바인더 수지를 사용하게 되므로, 소성온도를 종래의 450℃ 내지 550℃에서 400℃ 내지 450℃ 정도로 낮추는 것이 가능하며, 결과적으로, 낮은 소성 온도를 구현하는 것이 가능하여 형광체의 열화가 적어지므로, 휘도 저하도 작아지게 된다.In the present invention, since the binder resin is completely decomposed at around 400 ° C as described above, it is possible to lower the firing temperature from about 400 ° C to 450 ° C from the conventional 450 ° C to 550 ° C, resulting in a lower firing temperature. Since it is possible to implement, the deterioration of the phosphor is reduced, so that the luminance decreases.

이하, 본 발명을 실시예를 통하여 더욱 상세히 설명하나, 본 발명의 범위가 하기 실시예로 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to Examples, but the scope of the present invention is not limited to the following Examples.

실시예Example

실시예Example 1. 본 발명에 따른 형광체 페이스트 조성물의 제조 1. Preparation of the phosphor paste composition according to the present invention

벤질알코올 용매에 부틸메타크릴레이트, 메틸메타크릴레이트 단량체와 2,2'-아조비스이소부티로니트릴 (2,2'- AzobisIsoButyroNitrile, AIBN)을 첨가하여, 평균 분자량 100만 정도의 Poly(BMA-co-MMA)를 합성하였다. 여기에 터핀올 52 중량%, 벤질알콜 20 중량%, 바인더로서 에틸셀룰로오스 15 중량% 및 폴리에틸렌 글리콜형 비이온 계면활성제 13 중량%를 첨가하여 비이클을 제조하였다. 비이클 60 중량%와 분쇄된 형광체 BaMgAl14O24:Eu 40 중량%를 교반기를 이용하여 혼합한 후, 3 롤밀로 균일하게 분산시켰다. 제조된 형광체 페이스트 조성물의 점도를 이를 Rheostress기기를 이용하여 측정하였다.Butyl methacrylate, methyl methacrylate monomer and 2,2'-azobisisobutyronitrile (2,2'- AzobisIsoButyroNitrile, AIBN) were added to the benzyl alcohol solvent to obtain poly (BMA- co-MMA) was synthesized. A vehicle was prepared by adding 52 wt% terpinol, 20 wt% benzyl alcohol, 15 wt% ethylcellulose as a binder, and 13 wt% polyethylene glycol type nonionic surfactant. 60 wt% of the vehicle and 40 wt% of the pulverized phosphor BaMgAl 14 O 24 : Eu were mixed using a stirrer and then uniformly dispersed in a three roll mill. The viscosity of the prepared phosphor paste composition was measured using a Rheostress instrument.

실시예Example 2. 본 발명에 따른 형광체 페이스트 조성물의 제조 2. Preparation of the phosphor paste composition according to the present invention

폴리에틸렌 글리콜형 계면활성제 대신에 솔비탄 에스테르 13 중량%를 첨가하여 비이클을 제조하였다는 점을 제외하고는, 실시예 1과 동일한 방법에 의해서 형광체 페이스트 조성물을 제조하였다. 제조된 형광체 페이스트 조성물의 점도를 이를 Rheostress기기를 이용하여 측정하였다.A phosphor paste composition was prepared in the same manner as in Example 1, except that 13 wt% of sorbitan ester was added in place of the polyethylene glycol type surfactant. The viscosity of the prepared phosphor paste composition was measured using a Rheostress instrument.

실시예Example 3. 본 발명에 따른 형광체 페이스트 조성물의 제조 3. Preparation of the phosphor paste composition according to the present invention

폴리에틸렌 글리콜형 계면활성제 대신에 폴리카르복실산염형 고분자 계면활성제로서 13 중량%를 첨가하여 비이클을 제조하였다는 점을 제외하고는, 실시예 1과 동일한 방법에 의해서 형광체 페이스트 조성물을 제조하였다. 제조된 형광체 페이스트 조성물의 점도를 이를 Rheostress기기를 이용하여 측정하였다.A phosphor paste composition was prepared in the same manner as in Example 1, except that 13 wt% of the vehicle was prepared as a polycarboxylate type polymer surfactant instead of the polyethylene glycol type surfactant. The viscosity of the prepared phosphor paste composition was measured using a Rheostress instrument.

비교예Comparative example 1. 종래기술에 따른 형광체 페이스트 조성물의 제조 1. Preparation of phosphor paste composition according to the prior art

폴리에틸렌 글리콜형 비이온 계면활성제를 첨가하지 않았다는 점을 제외하고는, 실시예 1과 동일한 방법에 의해서 형광체 페이스트 조성물을 제조하였다. 제조된 형광체 페이스트 조성물의 점도를 이를 Rheostress기기를 이용하여 측정하였다.A phosphor paste composition was prepared in the same manner as in Example 1 except that no polyethylene glycol type nonionic surfactant was added. The viscosity of the prepared phosphor paste composition was measured using a Rheostress instrument.

상기 실시예 1 내지 3 및 비교예1의 형광체 페이스트 조성물에 대한 점도를 하기 표 1에 나타내었다.The viscosity of the phosphor paste compositions of Examples 1 to 3 and Comparative Example 1 is shown in Table 1 below.

형광체 페이스트 조성물Phosphor paste composition 점도Viscosity 실시예 1Example 1 14.314.3 실시예 2Example 2 15.715.7 실시예 3Example 3 13.513.5 비교예 1Comparative Example 1 20.320.3

표 1을 참조하면, 실시예 1 내지 3에 따른 형광체 페이스트 조성물은 동일한 형광체 분말 함량에 대해서 비교예 1에 따른 형광체 페이스트 조성물에 비해서 현저하게 낮은 점도를 가지며, 따라서 우수한 가소성을 나타냄을 알 수 있다.Referring to Table 1, it can be seen that the phosphor paste compositions according to Examples 1 to 3 have significantly lower viscosities than the phosphor paste compositions according to Comparative Example 1 for the same phosphor powder content, and thus exhibit excellent plasticity.

본 발명에 따르면, 형광막내 형광체의 충진율을 효과적으로 개선할 수 있으 며, 특히 판상의 구조를 갖는 청색 형광체의 충진율을 개선하여 형광체 분말을 45 중량% 이상으로 혼합시킬 수 있고, 결과적으로 형성된 형광체막은 단위 셀에서 발광하는 광량이 증가하여 전체 패널의 휘도가 현저히 향상된다. 또한, 격벽을 착색하여 사용하는 경우에, 격벽에서의 반사를 저감시켜 휘도가 줄어드는 것을 방지할 수 있을 뿐만 아니라, 단위 셀 내에 치밀한 막 형성이 가능하기 때문에 방전 공간이 넓어짐에 따라 단위 형광체의 수명 또한 향상된다.According to the present invention, it is possible to effectively improve the filling rate of the phosphor in the fluorescent film, in particular to improve the filling rate of the blue phosphor having a plate-like structure to mix the phosphor powder to 45% by weight or more, the resulting formed phosphor film is a unit The amount of light emitted from the cell is increased, and the luminance of the entire panel is significantly improved. In addition, when the barrier ribs are colored, the reflection of the barrier ribs can be reduced to prevent the luminance from being reduced, and a dense film can be formed in the unit cell, so that the lifetime of the unit phosphor is increased as the discharge space is increased. Is improved.

Claims (6)

형광체 분말, 바인더 수지 및 용매를 포함하는 형광체 페이스트 조성물에 있어서, 상기 용매가 폴리에틸렌 글리콜형 비이온 계면활성제, 솔비탄 에스테르, 폴리카르복실산염형 고분자 계면활성제 또는 그 혼합물을 포함하는 것을 특징으로 하는 형광체 페이스트 조성물.A phosphor paste composition comprising a phosphor powder, a binder resin, and a solvent, wherein the solvent comprises a polyethylene glycol nonionic surfactant, a sorbitan ester, a polycarboxylate type polymer surfactant, or a mixture thereof. Paste composition. 제1항에 있어서,The method of claim 1, 상기 폴리에틸렌 글리콜형 비이온 계면활성제, 솔비탄 에스테르, 폴리카르복실산염형 고분자 계면활성제 또는 그 혼합물의 함량은 전체 페이스트 조성물 중 3 중량% 내지 20 중량%인 것을 특징으로 하는 형광체 페이스트 조성물.The content of the polyethylene glycol nonionic surfactant, sorbitan ester, polycarboxylate-type polymer surfactant or a mixture thereof is 3 wt% to 20 wt% of the paste composition, characterized in that the phosphor paste composition. 제1항에 있어서,The method of claim 1, 상기 형광체 분말은 판상 형광체 분말의 비율이 40 중량% 내지 60 중량%인 것을 특징으로 하는 형광체 페이스트 조성물.The phosphor powder is a phosphor paste composition, characterized in that the ratio of the plate-shaped phosphor powder 40 to 60% by weight. 제1항에 있어서,The method of claim 1, 상기 형광체 분말의 평균 입경은 1㎛ 내지 7㎛인 것을 특징으로 하는 형광체 페이스트 조성물.An average particle diameter of the phosphor powder is 1 ㎛ to 7 ㎛ characterized in that the phosphor paste composition. 제1항 내지 제4항 중의 어느 한 항에 따른 형광체 페이스트 조성물을 이용하여 제조된 형광체층.A phosphor layer prepared using the phosphor paste composition according to any one of claims 1 to 4. 제5항에 따른 형광체층을 포함하는 플라즈마 디스플레이 패널.A plasma display panel comprising the phosphor layer according to claim 5.
KR1020060030505A 2006-04-04 2006-04-04 A phosphor paste composition, a phosphor layer prepared therefrom and a plasma displaly panel comprising the same KR20070099271A (en)