KR20060117708A - A method for manufacturing fuctional gold energy stone and a method for manufacturing panel for building using the gold energy stone - Google Patents
A method for manufacturing fuctional gold energy stone and a method for manufacturing panel for building using the gold energy stone Download PDFInfo
- Publication number
- KR20060117708A KR20060117708A KR1020050040200A KR20050040200A KR20060117708A KR 20060117708 A KR20060117708 A KR 20060117708A KR 1020050040200 A KR1020050040200 A KR 1020050040200A KR 20050040200 A KR20050040200 A KR 20050040200A KR 20060117708 A KR20060117708 A KR 20060117708A
- Authority
- KR
- South Korea
- Prior art keywords
- functional
- weight
- golden
- manufacturing
- stone
- Prior art date
Abstract
Description
도 1 은 본 발명에 따른 기능성 황금생기석의 제조방법에 관한 흐름도이다.1 is a flow chart related to a method for manufacturing a functional gold crystalline stone according to the present invention.
도 2 는 본 발명에 따른 기능성황금생기석을 포함하는 다기능성 건축내외장재의 제조방법이다.Figure 2 is a manufacturing method of a multi-functional building interior and exterior materials comprising a functional golden gilt stone according to the present invention.
본 발명은 기능성 황금생기석의 제조방법 및 기능성황금생기석을 포함하는 다기능성 건축내외장재의 제조방법에 관한 것으로, 더욱 자세히 설명하면, 음이온 및 원적외선을 방사하는 기능, 수맥으로 인하여 인체에 장해를 일으키는 것을 방지하는 기능, 전자파로 인하여 인체에 장해를 일으키는 것을 방지하는 기능, 항균 및 탈취 기능 등의 다기능성을 가지는 원료들을 배합하여 황금생기석을 제조하는 방법과 다기능성을 가지는 황금생기석을 수지, 유리섬유 및 난연성원료 등과 배합 조성하여 다기능성을 가지는 건축내외장재(판넬)를 제조하는 방법에 관한 것이다.The present invention relates to a method for manufacturing a functional golden fresh stone and a method for manufacturing a multifunctional building interior and exterior material including a functional golden fresh stone, and more specifically, to the function of radiating negative ions and far infrared rays, causing damage to the human body due to water vein. A method of manufacturing gold raw stones by combining raw materials with multi-functions such as the function of preventing, preventing damage to the human body by electromagnetic waves, and antibacterial and deodorizing functions. The present invention relates to a method for manufacturing a building interior and exterior materials (panel) having a multi-functional composition by blending with fibers and flame retardant raw materials.
산업이 발전함에 따라 제품고유의 특성은 물론 부수적인 효과를 만족시킬 수 있는 각종 기능성 제품이 제조, 판매되고 있으며 건축물의 내.외.마감재에 있어서도 특히 원적외선 방사능 및 음이온 방출능을 가지는 많은 제품들이 연구개발되고 있는 실정이다.As the industry develops, various functional products are produced and sold to satisfy the unique characteristics as well as the side effects of the product, and many products with far-infrared radiation and anion emission ability are studied in the interior, exterior, and finishing materials of buildings. It is being developed.
종래에 건축내장재 및 실내 인테리어 소재는, 주로 시멘트 콘크리트로 벽체를 구성하고, 단열재로는 스티로폼이나 폴리우레탄과 같은 유기 고분자 발포 성형 폼을 사용하고, 내부 마감재로는 석고보드나 시멘트·석고의 혼합체 등이 사용되었으며, 천장 재로는 석고보드, 바닥 재로는 유기 고분자 재료가 주로 사용되었다. 그러나, 이들 종래 내장재들은 단열성은 좋으나 인화성·화재시 유독가스의 발생 등과 같은 안전상의 문제점, 수분에 의한 강도저하 및 시간의 경과에 따른 열전도도의 저하 등 성능상의 문제점, 또한 대부분 재활용되기 어렵다는 환경상의 문제점을 안고 있었다.Conventionally, building interior materials and interior materials are mainly composed of cement concrete walls, and organic polymer foam molding foam such as styrofoam and polyurethane are used as insulation materials, and gypsum board, cement / gypsum mixture, etc. are used as interior finishing materials. It was used as a ceiling material, gypsum board and organic polymer material as a floor material. However, these conventional interior materials have good thermal insulation, but safety problems such as flammability and generation of toxic gases during fire, performance problems such as reduced strength due to moisture, and thermal conductivity over time, and most of them are difficult to recycle. I had a problem.
종래 제품들의 문제점을 해결하기 위하여 최근 들어 친환경적인 소재의 건축재가 선보이고 있다. 그러나, 최근에 소개된 친환경 건축재의 대부분은 숯, 맥반석, 황토, 옥석 등의 기능성 천연소재에 시멘트, 몰탈, 유기화합물 결합제 또는 폴리머 등을 혼합 성형한 것으로, 인화성이나 화재시의 유독가스 발생과 같은 종래기술의 문제점을 제대로 해결하지 못하고 있으며, 유기화합물 등과의 혼합으로 기능성도 극히 미미히여 실제 사용에 따른 기능성을 기대하기는 어렵다.Recently, in order to solve the problems of conventional products, building materials of environmentally friendly materials have been introduced. However, most of the recently introduced eco-friendly building materials are formed by mixing and molding cement, mortar, organic compound binders or polymers into functional natural materials such as charcoal, ganban stone, loess, and jade stone. It does not properly solve the problems of the prior art, and the functionality is also very minimal due to mixing with organic compounds, it is difficult to expect the functionality according to the actual use.
이러한 선행기술의 예로, 대한민국 공개특허 제2000-7111호는 증점액 100 중량부에 대하여 접착성 에멀젼, 에틸렌글리콜, 해포석, 규회석, 황토, 맥반석 등 을 혼합한 건축내장용 항균성 마감재 조성물을 기재하고 있으며, As an example of this prior art, Korean Patent Laid-Open Publication No. 2000-7111 discloses an antimicrobial finish composition for building interiors, which contains an adhesive emulsion, ethylene glycol, haemulite, wollastonite, loess, elvan, and the like with respect to 100 parts by weight of thickener. ,
대한민국공개특허 제2002-59855호는 골조에 단열재를 설치하고 단열재 위에 파이프를 배관한 다음 그 위에 토르마린, 맥반석, 황토, 규회석, 해포석, 접착제 등을 혼합한 마감재층을 형성한 건축물 마감재 및 이를 이용한 시공방법을 기재하고 있으며; 대한민국 실용신안등록 제298914호에서는 화강암, 맥반석, 옥분말, 일라이트 등의 혼합물을 흙, 시멘트, 응집 경화제로 성형하고 내부에 보강 철심을 구성한 패널을 기재하고 있다.Korean Laid-Open Patent No. 2002-59855 discloses a building finishing material in which a layer of finishing material is formed by installing an insulating material in a frame and piping a pipe on the insulating material, and then mixing a tourmaline, ganban stone, loess, wollastonite, calcite stone, and adhesive on it. A method is described; Korean Utility Model Registration No. 298914 describes a panel in which a mixture of granite, ganban stone, jade powder, and illite is molded with soil, cement, and cohesive hardener, and a reinforcing iron core is formed therein.
천연소재를 사용한 건축재와 관련된 선행기술로, 대한민국 공개특허 제2002-61550호는 천연 게르마늄 광석 분쇄물에 자바사이트 및 벤토나이트를 혼합한 후 성형 및 소성시킨 판재를 기술하고 있으며, 대한민국 실용신안등록 제258615호에서는 마재 직류 양면에 숯, 생석회, 황토, 생약분말 등을 시트상으로 도포하고 최종적으로 한지를 시트 표면에 부착시킨 내장재를 기술하고 있으며, 대한민국 등록실용신안 제291437호에서는 분쇄된 폐지, 톱밥, 황토, 점토, 방염제, 소금으로 구성된 항균, 항곰팡이 기능을 가진 단열재를 기술하고 있다.As a prior art related to building materials using natural materials, Korean Patent Laid-Open Publication No. 2002-61550 describes a plate formed by mixing javasite and bentonite after mixing natural germanium ore crushed product and molding and firing, and registered a utility model of Korea 258615. No. 2 describes interior materials in which charcoal, quicklime, ocher, and herbal powders are applied on both sides of direct current DC in a sheet form, and finally Hanji is attached to the surface of the sheet.In Korean Utility Model No. 291437, crushed waste paper, sawdust, It describes an antimicrobial and antifungal insulation consisting of loess, clay, flame retardant and salt.
상기와 같은 종래의 소재들은 음이온 및 원적외선 방사기능, 수맥인체장해방지기능, 전자파 인체장해방지기능, 항균, 탈취 등 다기능성이 동시에 나오는 소재가 없으며 기능 및 효능도 떨어진다. Conventional materials as described above are not anion and far-infrared radiation function, water vein human body obstacle prevention function, electromagnetic wave human body interference prevention function, antibacterial, deodorization and the same multi-functional material at the same time, the function and efficacy is also poor.
따라서 상기의 문제점을 다양한 기능성 광물질들을 배합하여 위의 기능이 효과적으로 나오도록 기능성 원료를 개발하였으며 이를 다양한 형태의 건축용, 농수산용, 공산품용으로 활용하여 제품을 생산할 수 있도록 하였다.Therefore, the above problems have been developed by combining various functional minerals to develop a functional raw material so that the above function is effectively produced, and to use it for various forms of construction, agriculture and fisheries, and industrial products to produce products.
본 발명은 기능성 황금생기석의 제조방법 및 기능성황금생기석을 포함하는 다기능성 건축내외장재의 제조방법을 제공하는 것을 목적으로 한다.It is an object of the present invention to provide a method for producing a functional golden raw stone and a method for producing a multifunctional building interior and exterior material comprising a functional golden raw stone.
본 발명은 동식물과 인간의 건강에 유익한 각종 좋은 기능들을 모두 갖추고 있는 원료 소재 개발과 이를 활용하여 종래의 기술보다 진보된 기능을 갖춘 소재를 개발하여 각종, 농수산용, 공업용 및 건축용으로 제품을 생산 보급하는데 그 목적이 있는 것으로, 인간과 동식물에 유익한 다기능성 원료 개발 및 이를 이용한 다양한 다기능성 제품 개발 생산에 관한 것이다.The present invention develops and distributes products for various, agricultural, fisheries, industrial and construction by developing materials with advanced functions than conventional technologies by utilizing raw materials having all kinds of good functions beneficial to animals and plants and human health. The purpose is to develop a multifunctional raw material beneficial to humans and animals and plants and to develop and produce various multifunctional products using the same.
상기의 목적을 달성하기 위하여, 본 발명에 따른 기능성 황금생기석의 제조방법은, 모나자이트, 전기석, 맥반석, 광물들을 각각 독립적으로 분쇄하는 단계; 상기 각각 분쇄된 광물들을 각각 분쇄된 광물들의 크기별로 분리하는 단계; 상기 분쇄된, 모나자이트를 맥반석과 서로 혼합하는 단계; 및 상기 혼합물에 유리섬유를 첨가하여 혼합하여 혼합물을 만드는 단계를 포함하고, 상기 혼합물에 있어서 모나자이트 : 상기 맥반석 : 유리섬유가 0.1 ~ 30중량% : 10 ~ 65 중량% : 0.1 ~ 40 중량% 이고, 상기 기능성 황금생기석에 분쇄된 전기석이 더 포함되고, 상기 전기석은 10 ~ 65 중량% 의 비율로 혼합되고, 상기 기능성 황금생기석에 황토가 더 포함되고, 상기 황토는 10 ~ 65 중량% 의 비율로 혼합되고, 상기 기능성 황금생기석에 질석이 더 포함되고, 상기 질석은 0.1 ~ 65 중량% 의 비율로 혼합되고, In order to achieve the above object, the manufacturing method of the functional gold crystalline stone according to the present invention, the step of crushing each independently of the monazite, tourmaline, elvan, minerals; Separating each of the crushed minerals by the size of the crushed minerals; Mixing the pulverized, monazite with elvan; And adding glass fibers to the mixture and mixing the mixture to form a mixture, wherein the monazite in the mixture is 0.1 to 30% by weight, 10 to 65% by weight, and 0.1 to 40% by weight of glass fiber. The tourmaline is further comprises a tourmaline pulverized in the functional golden giangseok, the tourmaline is mixed in a ratio of 10 to 65% by weight, the functional golden giangseok is further included ocher, the ocher is 10 to 65% by weight Mixed with, vermiculite is further included in the functional golden gilt, the vermiculite is mixed in a proportion of 0.1 to 65% by weight,
상기의 목적을 달성하기 위하여, 본 발명에 따른 기능성 황금생기석을 포함하는 다기능성 건축내외장재의 제조방법은, 기능성 황금생기석, 수지, 충진제, 유 리섬유, 토너, 기타첨가물 (이형제, 경화제, 경화지연제) 을 교반기에 넣고 배합하여 교반 반죽하여 BMC 를 만드는 단계; 상기 BMC 를 프레스에 위치시킨 후 온도 100 ~ 200℃ 및 압력 50 ± 20kg/cm²의 조건하에서 성형하는 단계; 상기 성형된 제품을 상기 프레스로부터 탈형하고 트리밍하는 단계; 및 상기 성형된 제품을 크기별로 재단하는 단계를 포함하고, 상기 BMC 를 프레스에서 성형할 경우, 상기 프레스의 하판 또는 상판에 여러가지 무늬와 색깔문양을 낼 수 있는 코팅지를 하판에 깔거나 상판에 붙여진 상태로 상기 BMC 가 성형되고, 상기 BMC 를 프레스에서 성형된 기능성황금생기석을 포함하는 다기능성 건축내외장재 패널의 한쪽면 또는 양쪽면에 염산으로 강산처리하여 표면을 거칠게 한 후 물로 세척하여 건조시킨 다음 패널에 접착제를 바르고, 여러가지 무늬와 색깔문양을 낼 수 있는 코팅지를 붙이고, 상기 교반기에 넣고 배합하는 경우 상기 기능성 황금생기석 : 수지 : 충진제 : 유리섬유 : 토너 : 기타첨가물의 재료별 각각 비율은 1 ~ 63중량% : 15 ~ 40중량% : 10 ~ 30중량% : 10 ~ 30중량% : 1.0 ~ 15중량% : 1.0 ~ 15중량% 인 것을 특징으로 한다.In order to achieve the above object, the manufacturing method of the multi-functional building interior and exterior materials comprising the functional golden raw stone according to the present invention, the functional golden raw stone, resin, filler, glass fiber, toner, other additives (release agent, hardener, Adding a curing retardant) into a stirrer and stirring to form a BMC; Placing the BMC in a press and then molding under conditions of a temperature of 100 to 200 ° C. and a pressure of 50 ± 20 kg / cm²; Demolding and trimming the molded article from the press; And cutting the molded product by size, and when the BMC is molded in a press, a coated paper capable of forming various patterns and color patterns on the lower or upper plate of the press is laid on the lower plate or attached to the upper plate. The BMC is molded, and the BMC is treated with hydrochloric acid on one or both sides of the multi-functional building interior and exterior panels including the functional golden gilts molded in a press, and then the surface is roughened, washed with water and dried. Apply the adhesive to the coated paper, which can give various patterns and colors, and put it in the stirrer. When the compound is added, the functional golden gold stone: Resin: Filler: Glass fiber: Toner: Others The ratio of each additive is 1 ~ 63% by weight: 15 to 40% by weight: 10 to 30% by weight: 10 to 30% by weight: 1.0 to 15% by weight: characterized in that 1.0 to 15% by weight.
본 발명의 특징, 장점 및 바람직한 실시예 등이 첨부된 도면을 참조하여 아래에서 상세히 설명된다.The features, advantages and preferred embodiments of the present invention will be described in detail below with reference to the accompanying drawings.
본 발명에 따른 기능성 황금생기석의 제조방법 및 이를 포함하는 다기능성 건축내외장재의 제조방법을 설명하면 다음과 같다.Referring to the manufacturing method of the functional gold fresh stone according to the present invention and the manufacturing method of the multi-functional building interior and exterior materials including the same.
도 1 은 본 발명에 따른 기능성 황금생기석의 제조방법에 관한 흐름도이다.1 is a flow chart related to a method for manufacturing a functional gold crystalline stone according to the present invention.
도 1 에 도시된 바와 같이, 먼저 본 발명에 따른 기능성 황금생기석의 제조방법을 설명한다.As shown in FIG. 1, first, a method of manufacturing a functional gold organic stone according to the present invention will be described.
우선, 기능성 황금생기석의 제조에 필요한 기능성 광물들의 선별한다. (S10)First, the functional minerals necessary for the production of the functional golden biostone are selected. (S10)
기능성 황금생기석의 제조에 필요한 광물로는 모나자이트, 맥반석, 전기석, 황토, 질석, 유리섬유를 사용한다. 각각의 광물들을 설명하면, 모나자이트 (monazite)는 단사정계(單斜晶系)에 속하는 광물로서, 굳기가 5∼5.5이고, 비중이 4.6∼5.4이고, 색깔은 황색·황갈색·적갈색, 드물게 회색·회록색, 조흔색(무색)이고, 화학성분은 (Ce, La, Y, Th)PO4 로서 세륨족 희토류원소의 인산염광물이다.The minerals required for the production of functional gold biographite include monazite, elvan, tourmaline, loess, vermiculite and glass fiber. In the description of each mineral, monazite is a monoclinic mineral, with a hardness of 5 to 5.5, specific gravity of 4.6 to 5.4, and yellow, yellowish brown, reddish brown, rarely grey. It is grayish green, streaky (colorless), and its chemical component is (Ce, La, Y, Th) PO 4 , which is a phosphate mineral of cerium group rare earth element.
맥반석은 석영반암에 속하는 약석의 화성암류 중 화강섬록반암에 속하며, 석영과 장석이 촘촘하게 섞여 있고, 색깔은 누런 백색, 연한 누런 갈색, 옅은 회색, 짙은 녹색 또는 옅은 녹색으로, 암석에 빨간 점 또는 하얀 점이 고르게 섞여 있는 모습이 보리밥과 같다고 하여 맥반석이라는 이름이 붙었다. Elvanite is one of the igneous rocks of the feldspar belonging to the quartz bedrock, and it is a fine mixture of quartz and feldspar, and the color is yellowish white, light yellowish brown, light gray, dark green or pale green, and red dots or white on the rock. The spots are evenly mixed like barley rice, so it was named Macvan Stone.
그리고, 주성분은 무수규산, 산화알루미늄이고, 산화 제 2 철 소량이 함유되고, 약석으로 알려진 것은 누런 백색을 띤 맥반석으로 예전에는 환약을 정제하는 여과제 등에 부스럼 또는 종기 등 피부질병을 치료하는 소염제로 사용하였다. 동의보감에 의하면 그 성질은 달고, 따뜻하며, 독이 없다고 한다. The main components are silicic anhydride and aluminum oxide, and a small amount of ferric oxide is contained, and the known weak stone is yellowish-white ganbanite, which used to be used as an anti-inflammatory agent to treat skin diseases such as boils or boils. Used. According to the agreement, it is sweet, warm and nonpoisonous.
맥반석의 결정구조는 1㎤ 당 3 ~ 15 만 개의 구멍으로 이루어져 있어 흡착성 이 강하고, 약 2만 5000종의 무기염류를 함유하고 있다. 중금속과 이온을 교환하는 작용을 하기 때문에 유해금속 제거제로도 사용하며, 이 암석에 열을 가하면 원적외선을 방출하는 것으로 알려져 있다. 그리고, 맥반석은 찜질방·식기·의료기 등 여러 산업 부분에서 이용되고 있다.The crystal structure of elvan is composed of 3 to 150,000 holes per cubic centimeter, which is highly adsorptive and contains about 25,000 inorganic salts. It is used as a toxic metal remover because it exchanges heavy metals and ions, and it is known to emit far infrared rays when heat is applied to this rock. Elvan has been used in various industrial sectors, such as jjimjilbang, tableware, and medical equipment.
전기석 (電氣石, tourmaline)은 육방정계(六方晶系)에 속하는 광물로서, 광물의 굳기가 7.0∼7.5 이고, 비중이 2.98 ∼ 3.20 이고, 일명 토르말린이라고도 한다. 화학성분은 철·마그네슘·알칼리금속 등과 알루미늄의 복잡한 붕규산염이다. 전기석의 결정구조는 대개 6 각 또는 9 각이고 때로는 3각 주상(柱狀)을 이루며, 주(柱)의 상하에서 결정형을 달리하는 경우도 있다. 또 상하가 편평한 능면체나 침상(針狀)·모상(毛狀)을 나타내며, 때때로 입상(粒狀)·괴상(塊狀)을 이루기도 한다. 쪼개짐은 분명하지 않고, 단구(斷口)는 평탄하지 않거나 패각상(貝殼狀)이다. 그리고, 굳기는 7.0∼7.5, 이고 유리광택 또는 수지광택이 있다. 마찰에 의해서 전기가 생기며, 가열하면 양끝이 양·음으로 대전(帶電)하기 때문에 전기석이라는 이름이 붙여졌다. 철이 많은 것을 철전기석이라 하며, 흑색을 띠며 육안으로는 불투명한 것이 많다.Tourmaline is a mineral belonging to a hexagonal system, which has a hardness of 7.0 to 7.5, a specific gravity of 2.98 to 3.20, and is also known as tourmaline. The chemicals are complex borosilicates of iron, magnesium, alkali metals and aluminum. The crystal structure of tourmaline is usually hexagonal or ninth, sometimes triangular, and sometimes different in crystalline form above and below the column. They also have flat rhombohedrons, needles, and hairs, and sometimes form granules or blocks. The cleavage is not clear, and the monocytes are not flat or shell-shaped. The hardness is 7.0 to 7.5, and there are glass gloss or resin gloss. Electricity is generated by friction, and when heated, both ends are charged positively and negatively. Many iron is called iron tourmaline, and it is black and many things are opaque to the naked eye.
전기석은 석영·백운모·장석 등과 함께 화강암질 페그마타이트 속에서 산출된다. 마그네슘이 많은 것은 고토(苦土)전기석 또는 마그네슘 전기석이라 하는데, 갈색을 띠며 반투명하다. 접촉변성암·광역변성암에서 산출된다. 알칼리금속이 많은 것을 귀전기석(貴電氣石) 또는 알칼리전기석이라 하며, 무색·홍색·청색·황색 등 여러 가지 색을 띠며 투명한 것이 많다. 그 중에서 특히 홍색인 것을 홍전 기석(루벨라이트), 남청색(藍靑色)인 것을 남전기석(인디고라이트), 녹색인 것을 녹전기석(벨데라이트 또는 브라질에메랄드)이라 하여, 아름다운 것은 보석으로 사용된다. 흔히 결정주(柱)의 양끝이나, 안쪽과 바깥쪽에서 색을 달리하는 경우가 있다. 브라질 ·미국(캘리포니아주)·남아프리카공화국 등지에서 아름다운 것이 산출되고, 화강암질 페그마타이트나 기성작용(氣成作用)에 의한 광맥 등에서 산출된다.Tourmaline is produced in granite pegmatite together with quartz, dolomite and feldspar. Magnesium is known as goto tourmaline or magnesium tourmaline, which is brown and translucent. It is calculated from contact metamorphic and wide metamorphic rocks. Many alkali metals are called precious gemstones or alkaline tourmaline, and they have many colors such as colorless, red, blue, yellow, and transparent. Among them, the red ones are called rutherite stones (rubellite), the indigo blue ones are called tourmaline (indigo light), and the green ones are called tourmaline (belderite or brazilian emerald). . Often the ends of the crystal (柱), or the color of the inner and outer are sometimes different. It is produced in Brazil, the United States (California), South Africa, etc., and is produced in granite pegmatite and veins from ready-made processes.
황토는 주로 실트 크기의 지름 0.002∼0.005mm인 입자로 이루어진 퇴적물로서, 뢰스라고도 한다. 중국 본토인 황허강[黃河] 유역에 널리 분포하는데, 그 밖에 미국의 미시시피강 유역, 유럽 중앙부 등에도 분포한다. 중국 본토의 황토는 북서부에 있는 사막으로부터 편서풍에 의하여 운반되어 퇴적된 것이며, 그 밖의 것은 빙하가 후퇴한 뒤의 퇴적물이 바람에 운반된 것이다. 황갈색을 띠고 풍화를 잘 받지 않으며, 모난 수직 벽면을 만들고 주로 석영을 함유하며 그 밖에 휘석 ·각섬석 등을 함유하여 석회질이다. 빙하 퇴적점토와 함께 스텝기후하의 체르노젬 등의 비옥한 토양의 모재가 된다. 황토는 습도를 조절하는 역할을 하고, 맥반석과 같이 원적외선 및 음이온을 발산한다.Ocher is a deposit mainly composed of particles of 0.002 to 0.005 mm diameter with silt size, also called loess. It is widely distributed in the Huanghe River basin, the mainland of China, and also in the Mississippi River basin of the United States and central Europe. The mainland China's loess was transported and deposited by the western wind from the desert in the northwest, and the other was transported by wind after the glacier retreat. It has a yellowish brown color and is not weathered well. It is made of angular vertical wall and mainly contains quartz. Together with glacial sedimentation clay, it becomes the base of fertile soil such as Chernozem under step climate. Ocher plays a role in controlling humidity and emits far infrared rays and negative ions like elvan.
유리섬유 (glass fiber) 는 용융한 유리를 섬유 모양으로 한 광물섬유로서, 그 제조방법은 녹인 유리를 기계적으로 잡아늘이는 방법, 공기나 수증기로 날리는 방법, 원심력에 의해 주위에 날려 붙이는 방법 등으로 섬유 모양을 만든다. Glass fiber is a mineral fiber made of molten glass in the form of fibers, and its manufacturing method is a method of mechanically stretching molten glass, blowing it with air or steam, blowing it around by centrifugal force, etc. Make a shape
유리섬유의 성질은 고온에 견디며, 불에 타지 않고, 흡수성이 없고, 흡습성이 적고, 화학적 내구성이 있기 때문에 부식하지 않고, 강도, 특히 인장강도가 강 하고, 신장률이 적고, 전기 절연성이 크고, 내마모성이 적고, 부서지기 쉬우며 부러지고, 비중은 나일론의 2.2배, 무명의 1.7배이고, 매트로 만든 것은 단열·방음성이 좋다. The properties of glass fiber are resistant to high temperatures, do not burn, are not absorbable, are less hygroscopic and are chemically resistant, so they do not corrode, have high strength, especially tensile strength, low elongation, high electrical insulation, and high wear resistance. It is small, brittle and broken, and its specific gravity is 2.2 times that of nylon and 1.7 times that of cotton. The material made of mat has good insulation and sound insulation.
용도는 천으로 짠 내화직물(耐火織物)이나 전기 절연재료 등의 용도로 널리 쓰이며, 건축관계 재료로서 사용되는 경우에는 보온·보냉재(保冷材), 흡음방음재, 공기여과 등에 사용된다. 이것에 사용되는 섬유의 지름은 가늘수록 여러 가지 점에서 우수하고, 인장강도도 지름이 가늘수록 강하며, 또 열전도율도 같은 비중의 것으로 비교하면 가늘수록 작아진다. 보온·흡음용으로는 5∼20μm의 것, 여과용으로는 40∼150μm의 것이 주로 사용된다. 유리섬유로 만든 건축재료에는 유리섬유판·유리섬유통·유리섬유여과기 등이 있다.It is widely used as a fireproof fabric or electric insulation material woven in cloth, and when used as a building-related material, it is used for thermal insulation, cold insulation, sound-absorbing sound-proof material, and air filtration. The diameter of the fiber used for this is excellent in various points, and the tensile strength is also stronger as the diameter is smaller, and the thermal conductivity becomes smaller as compared with the same specific gravity. The thing of 5-20 micrometers for heat insulation and a sound absorption, and the thing of 40-150 micrometers for filtration are mainly used. Building materials made of glass fibers include glass fiber plates, glass fiber barrels, and glass fiber filters.
그리고, 철근콘크리트에서의 철근의 역할처럼 수지의 성질을 강화하고, 방화성능도 향상시킨 유리섬유를 플라스틱의 보강재(補强材)로 사용한 섬유강화플라스틱(FRP:fiberglass reinforced plastics)이 개발되었으며, 사용할 수 있는 합성수지는 여러 종류가 있으나 주로 불포화 폴리에스테르 수지가 사용된다. 각 방면의 공업재료로서 널리 사용되며, 항공기·보트 등의 구조재나 파이프, 속이 빈 기둥·낚싯대 및 전기기구의 절연재로 쓰인다. In addition, fiberglass reinforced plastics (FRP) have been developed that use glass fiber as a reinforcing material for plastics, which enhances the properties of the resin and improves the fire resistance as well as the role of reinforcing concrete in reinforced concrete. There are many kinds of synthetic resins that can be used but mainly unsaturated polyester resins are used. It is widely used as an industrial material in each area, and is used for structural materials such as aircraft and boats, and insulation materials for pipes, hollow columns, fishing rods, and electric appliances.
본 발명에 따른 기능성 황금생기석의 제조에 있어서, 모나자이트는 음이온을 발생시키며, 가격이 고가이기 때문에 황금생기석의 제조에 있어서 보통 0.1 ~ 30 중량% 로 혼합된다. 그리고, 0.1 중량% 의 비율로만 함유가 되어도 본 발명의 목적을 달성하기 위한 충분한 기능을 한다.In the production of the functional gold biocides according to the present invention, the monazite generates anions, and because of the high price, it is usually mixed in the amount of 0.1 to 30% by weight in the preparation of the gold biocides. And even if it contains only 0.1 weight% of ratio, it has a sufficient function to achieve the objective of this invention.
맥반석과 황토는 습도를 조절하고, 원적외선과 음이온을 발생시킨다. 황금생기석의 제조에 대부분의 중량 % 를 차지하는 원료로 사용된다. Elvan and loess control humidity and generate far infrared rays and anions. It is used as a raw material which accounts for most weight% in the production of golden raw stones.
전기석은 모나자이트와 같이 음이온을 발생시키는 역할을 하고, 가격이 모나자이트에 비해 저렴하므로 모나자이트의 대용으로 10 내지 65 중량% 의 비율로서 사용될 수 있다. 유리섬유는 0.1 내지 40 중량% 이하의 비율로 혼합된다. Tourmaline plays a role in generating negative ions like monazite, and since the price is cheaper than monazite, it may be used as a ratio of 10 to 65% by weight as a substitute for monazite. Glass fibers are mixed in a proportion of 0.1 to 40% by weight or less.
본 발명에 따른 기능성 황금생기석의 제조에 있어서 모나자이트는 필수구성요소로서 반드시 사용되며, 전기석은 모나자이트의 대용으로 선택적으로 첨가될 수 있다. 이는 전기석이 모나자이트와 효능이 유사한데 비해 가격이 모나자이트에 비해 상대적으로 저렴하여 모나자이트의 대용품으로 사용되는 것이다.Monazite is necessarily used as an essential component in the production of the functional gold biomagnet according to the present invention, and tourmaline may be optionally added as a substitute for monazite. This is because the tourmaline has a similar effect to the monazite, but the price is relatively cheaper than the monazite, so it is used as a substitute for the monazite.
맥반석은 필수구성요소로서 10 중량% 내지 65 중량%의 비율로 혼합된다. 그리고, 황토는 필요에 따라 선택적으로 10 중량% 내지 65 중량% 이하의 비율로 혼합될 수도 있다.Elvan is an essential component and is mixed at a ratio of 10% to 65% by weight. And, the ocher may be optionally mixed in a ratio of 10 wt% to 65 wt%, if necessary.
또한, 질석이 0.1 중량% 내지 65중량% 가 혼합될 수도 있다.In addition, vermiculite may be mixed in an amount of 0.1% by weight to 65% by weight.
유리섬유는 본 발명에 따른 황금생기석의 표면을 강화하기 위한 것과 같이 일정한 수준의 경도를 유지시키는 역할을 하는 것으로 혼합비율이 40중량% 이하가 되는 조건을 유지한다.Glass fiber serves to maintain a certain level of hardness, such as to reinforce the surface of the golden fresh stone according to the present invention to maintain the condition that the mixing ratio is 40% by weight or less.
이상과 같이 본 발명에 따른 기능성 황금생기석의 제조에 필요한 기능성 광물들의 선별이 되면, 기능성 광물들을 분쇄기에 넣고 분쇄를 한다. (S20) As described above, when the selection of the functional minerals required for the production of the functional gold fresh stone according to the present invention, the functional minerals are put into a grinder and ground. (S20)
그리고, 분쇄가 된 기능성 광물들을 분쇄된 사이즈별로 분리한다. (S30) 사이즈별로 분리하는데는 예를 들어 일정한 메시(mesh) 별로 용도에 따라 분리될 수 있다. 보통 미세하게 분쇄된 기능성 광물들이 더 비싼 값에 팔린다.Then, the pulverized functional minerals are separated by the pulverized size. (S30) To be separated by size, for example, it may be separated according to a purpose by a certain mesh (mesh). Finely ground functional minerals are usually sold at higher prices.
일정한 범위의 사이즈 별로 분리된 기능성 광물들은 용도 및 출고가격에 따라 상기한 기능성 광물 배합비율의 범위내에서 혼합되고, (S40) 포장지에 넣고 (S50) 제품으로 출고한다. (S60)The functional minerals separated by the size of a certain range are mixed within the range of the functional mineral compounding ratio described above according to the use and shipping price, and put into a package (S40) and shipped as a product (S50). (S60)
기능성 광물들의 각각의 광물에 대한 배합비율은 출고되는 제품의 가격에 따라, 비싸게 출고되는 황금생기석의 경우에는 모나자이트의 비율이 높고, 저렴한 가격으로 출고되는 경우에는 맥반석 또는 황토의 혼합비율을 높이도록 한다.The proportion of functional minerals for each mineral is based on the price of the product shipped, and the ratio of monazite is high in case of expensive raw gold, and in case of low price, the mixing ratio of elvan or loess is increased. .
도 2 는 본 발명에 따른 기능성황금생기석을 포함하는 다기능성 건축내외장재의 제조방법이다.Figure 2 is a manufacturing method of a multi-functional building interior and exterior materials comprising a functional golden gilt stone according to the present invention.
도 2 에 도시된 바와 같이, 일단 기능성 황금생기석의 제조가 완료되면, 본 발명에 따른 기능성 황금생기석을 이용하여 본 발명에 따른 다기능성 건축내외장재를 제조한다.As shown in Figure 2, once the manufacturing of the functional golden raw stone is completed, using the functional golden raw stone according to the present invention to prepare a multi-functional building interior and exterior materials according to the present invention.
먼저 본 발명에 따른 다기능성 건축내외장재를 제조하기 위한 원료로는 수지, 본 발명에 따른 제조방법에 의해 제조되는 기능성 황금생기석, 충진제, 유리섬유, 토너, 기타 첨가제(이형제, 경화제, 경화지연제) 의 혼합물이 사용된다. First, as a raw material for manufacturing the multifunctional building interior and exterior materials according to the present invention, a resin, a functional golden giangseok, filler, glass fiber, toner, other additives (release agent, curing agent, curing retardant) produced by the manufacturing method according to the present invention Mixtures are used.
각각의 원료들의 혼합되는 재료별 최적의 중량% 및 (중량% 의 허용범위) 를 살펴보면, 수지 : 기능성 황금생기석 : 충진제 : 유리섬유 : 토너 : 기타 (건축내외장제의 용도에 따라 첨가제, 경화제, 경화지연제 중 어느 하나 이상)가 각각 25 (15 ~ 40) : 42 (1 ~ 63) : 15 (10 ~ 30) : 13 (10 ~ 30) : 1.5 (1 ~ 5) : 3.5 (1 ~ 5) 의 중량% 의 비율을 가지는 범위내라면 본 발명은 달성된다.Looking at the optimum weight percent and (percentage of weight percent) of each raw material, the resin: functional golden giltstone: filler: glass fiber: toner: other (additives, hardeners, At least one of the curing retardants) is 25 (15 to 40): 42 (1 to 63): 15 (10 to 30): 13 (10 to 30): 1.5 (1 to 5): 3.5 (1 to 5) The present invention is achieved as long as it is within a range having a proportion of% by weight.
각각의 원료들을 구체적으로 설명하면, 수지는 (UPE Resin) 불포화폴리에스테르 (열경화성수지: Unsaturated Polyester Resin)와 저수축제 (열가소성수지: Low shrinkage additive, Low profile additive) 의 혼합물로서 저수축제와의 혼합부피 비율은 5 : 5 ~ 9 : 1 이다. 저수축제로는 Polystyene, Polymethylmathacrylate, Polyethylene, Polyurethane, Polyvinylacetate 등이 있다.In detail, each raw material is a mixture of (UPE Resin) unsaturated polyester (Unsaturated Polyester Resin) and a low shrinkage agent (low shrinkage additive, low profile additive) and a mixing volume of the low shrinkage agent. The ratio is 5: 5-9: 1. Low-shrinkants include Polystyene, Polymethylmathacrylate, Polyethylene, Polyurethane, and Polyvinylacetate.
불포화폴리에스테르수지 (unsaturated polyester resin) 는 열경화성(熱硬化性) 플라스틱에 속하는 고분자화합물로서, 중합성이 있는 이중결합을 가진 분자량 1,000 ~ 3,000 정도의 제 1차 수지를 만들어, 이것을 스티렌과 같은 비닐단위체를 사용하여 경화시켜서 성형물(成形物)을 만든다.Unsaturated polyester resin is a high-molecular compound belonging to thermosetting plastics. It produces a primary resin having a molecular weight of 1,000 to 3,000 with a polymerizable double bond, which is a vinyl unit such as styrene. Curing is used to make a molding.
일반용 제 1 차 수지를 만드는 대표적인 예는 프로필렌글리콜 1.1, 말레산 무수물(無水物) 0.5, 프탈산무수물 0.5의 몰비(比)로 취하고 가열·축합시켜서 제 1 차 폴리에스테르로 만든다. 이것에 30% 정도 무게의 스티렌을 섞고 중합촉매를 혼합하면, 스티렌과 혼성중합하여 제1차 수지 사이에 다리결합이 생겨 경화한다. 보통 제1차 수지에 스티렌을 섞은 것이 시판되고 있는데, 실제로 사용할 때는 유리섬유로 뼈대를 만들고, 이것에 혼합수지에 중합 촉매를 섞은 것을 함침(含浸)시켜서 상온에서 경화시켜 성형물을 만든다. 200t 정도까지의 소형 선박이나 보트 등을 만드는 데도 사용되나, 플라스틱 욕조·정화조 등은 대부분 이것으로 만든다. 이 밖에 도료용·화장판용, 또한 운동용구로서 장대높이뛰기용·스키용 등이 있다. 그리고, 옷의 단추, 건축재료로서 지붕용의 플라스틱 파형판(波形板)으로도 사용된 다. 이 수지는 일반적으로 유리섬유로 강화되기 때문에 섬유강화 플라스틱(fiber reinforced plastics:FRP)이라 한다. 최근에 발달한 성형법을 사용하면 강철과 같은 강도를 가진 FRP도 만들 수 있다. 유리섬유뿐만 아니라 나일론이나 테트론 같은 섬유도 사용되며 엔지니어링 플라스틱(공업용 플라스틱)으로 쓰인다.Representative examples of making a primary resin for general use are taken as a molar ratio of propylene glycol 1.1, maleic anhydride 0.5, and phthalic anhydride 0.5, followed by heating and condensation to obtain a primary polyester. When 30% of styrene is mixed with this and a polymerization catalyst is mixed, it is mixed with styrene to form a bridge bond between the primary resins and harden. Usually, a mixture of styrene with a primary resin is commercially available. In actual use, a skeleton is made of glass fibers, and the mixture is impregnated with a mixture of a polymerization catalyst and cured at room temperature to form a molded product. It is also used to make small ships and boats up to 200t, but most plastic tubs and septic tanks are made of this. There are also paints, cosmetics, and exercise poles for skiing and skiing. It is also used as a plastic corrugated board for roofing as a button for clothes and a building material. This resin is generally called fiber reinforced plastics (FRP) because it is reinforced with glass fibers. Recent advances in molding can produce FRP with the same strength as steel. In addition to glass fibers, fibers such as nylon and tetron are also used and are used as engineering plastics.
불포화 폴리에스테르수지의 성분은 여러 가지이다. 예를 들면, 프탈산무수물 대신에 이소프탈산을 쓴 것도 있어서, 특히 내약품성이 좋은 것을 만들 수 있는데, 불에 타는 것이 결점이다. 또 디알릴프탈레이트(DAP)를 겔화(化)하기 시작할 정도로 중합시킨 것도 불포화 폴리에스테르수지로 분류하는 경우가 많다. 분말이며 이것을 그대로, 또는 DAP와 혼합하여 적층판(積層板)이나 성형물을 만든다. The components of the unsaturated polyester resin are various. For example, isophthalic acid is used instead of phthalic anhydride, so that chemical resistance is particularly good. Burning is a drawback. In addition, polymerized diallyl phthalate (DAP) to the extent that it starts to gelate is often classified as unsaturated polyester resin. It is a powder and mixed as it is or with DAP, and a laminated sheet or a molded object is formed.
불포화폴리에스테르Unsaturated polyester
저수축제Water festival
본 발명에 따른 기능성 황금생기석은 입자크기가 2㎛이하 ~ 30mm이하의 사이즈를 가지고, 음이온방사, 원적외선 방사, 항균, 항곰팡이, 탈취, 수맥인체장해 방지기능, 회전전자파(氣)의 경락순환구동력 기능, 전자파 인체 장해 방지기능, 신진 대사 촉진 기능을 가지고 있다, 기능성 황금생기석의 성분을 분석하면, 바람직하게 SiO2(70.9%), Al2O3(14.8%), Fe2O3(3.03%), CaO(1.74%), MgO(1.06%), K2O(3.27%), Na2O3(3.55%), lg.loss(1.65%): ThO2(극미량), CeO2(극미량), La2CO3(극미량), Nd2O3(극미량) 으로 구성되어 있다.The functional gold crystalline stone according to the present invention has a particle size of less than 2㎛ ~ 30mm, anion radiation, far-infrared radiation, antibacterial, antifungal, deodorizing, water vein prevention function, meridians circulation driving force of rotating electromagnetic waves Function, to prevent electromagnetic interference, and to promote metabolism. When analyzing the components of the functional golden biomagnet, preferably SiO 2 (70.9%), Al 2 O 3 (14.8%), Fe 2 O 3 (3.03% ), CaO (1.74%), MgO (1.06%), K 2 O (3.27%), Na 2 O 3 (3.55%), lg.loss (1.65%): ThO 2 (extreme), CeO 2 (extreme) , La 2 CO 3 (extreme trace), Nd 2 O 3 (extreme trace).
충진제는 난연충진제 Al2(OH)3(수산화알루미늄) or 충진제 CaCO₃(탄산칼슘) 중 어느 하나를 사용한다. Fillers are either flame retardant Al 2 (OH) 3 (aluminum hydroxide) or filler CaCO 3 (calcium carbonate).
난연충진제Flame retardant filler
유리섬유(glass fiber) 는 SiO2 50% + CaO (칼슘옥사이드) 25% + Al2O3 25% + 유기화합물인 바인더로 구성되어 있다.Glass fiber (glass fiber) is composed of a binder of 50% SiO 2 + 25% CaO (calcium oxide) + 25% Al 2 O 3 + organic compound.
유리섬유Fiberglass
토너 (Toner) 는 폴리에스테르수지 (UPR) 와 색상도료 (Color Pigment) 가 50% : 50% 로 구성된 것이다.Toner is composed of 50%: 50% of polyester resin (UPR) and color pigment (Color Pigment).
마지막으로 기타 첨가제인 이형제(Release Egent) 는 Zinc Stearate산으로 금속왁스계열이다.Finally, the other additive, release agent (Release Egent) is zinc stearate acid is a metal wax series.
이형제Release agent
* stearate: 스테아르산염, 경지산염* stearate: stearate, arborate
경화제(Initiator개시제; Catalyst) 는 Oxcide 계통화공약품이고 경화지연제 (Inhibitor개시제) 는 Qunon 계통화공약품이다.Initiator (Catalyst Initiator) is an Oxide Systemized Chemical and Inhibitor Initiator is a Qunon Systemated Chemical.
경화제Hardener
본 발명에 따른 황금생기석을 포함하는 다기능성 건축내외장재의 제조방법은, Method for producing a multi-functional building interior and exterior material comprising a golden raw stone according to the present invention,
상기한 본 발명에 따른 기능성 황금생기석을 수지와 수산화알루미늄 또는 탄산칼슘 등의 충진제, 유리섬유(glass fiber), 토너 (Toner) (수지+ Color Pigment), 기타 첨가물 (이형제 (Release Egent: Zinc Stearate산-금속왁스계열), (경화제 (Initiator 개시제; Catalyst-Oxcide 계통화공약품), 경화지연제 (Inhibitor 개시제 - Qunon 계통화공약품)중 어느 하나이상)의 혼합물에 미량의 UP(Unsaturated Polyester Resin) 칩 등을 넣고, 상기한 여러 가지 조성 배합 비율로 배합하여 교반기(Kneader)로 원료 교반 반죽 (Kneading: 원료 혼합 반죽하는 것)을 한다. (S110)The above-mentioned functional gold crystalline stone according to the present invention is a filler such as resin, aluminum hydroxide or calcium carbonate, glass fiber, toner (resin + color pigment), other additives (release agent (zinc stearate) A small amount of UP (Unsaturated Polyester Resin) chip in a mixture of acid-metal wax series, (curing agent (Initiator initiator; Catalyst-Oxcide system chemical), or curing retardant (Inhibitor initiator-Qunon system chemical) The mixture is mixed at the above-mentioned various composition ratios, and kneading is performed with a kneader (S110).
UP 칩은 본 발명에 따른 건출내외장재가 자연석의 색(자연에 있는 돌의 색깔)을 내기 위해서 사용된다.UP chip is used to produce the interior and exterior materials according to the present invention to give the color of the natural stone (the color of the stone in nature).
그리고, 상기 원료교반반죽을 하여 BMC(Bulk Moulding Compound)로 만든다. (S120)Then, the raw material stirring dough to make a BMC (Bulk Molding Compound). (S120)
이 BMC를 프레스의 하판에 놓고 프레스에 의한 고온(100~200℃), 고압( 50±20kg/cm²)으로 성형(경화반응)한다. (S130)The BMC is placed on the lower plate of the press and molded (curing reaction) at a high temperature (100 to 200 ° C.) and a high pressure (50 ± 20 kg / cm²) by the press. (S130)
이때 Coating 지를 금형에 부착하지 않고 BMC만 프레스 성형하거나 또는 하부성형판이나 상부성형판에 여러 가지 무늬와 색깔 문양을 낼 수 있는 Coating 紙(종이, 폴리에스테르, 비닐계통 등의 원료 사용한 Coating 지)를 깔거나 부착하고 BMC 를 프레스 성형할 수가 있다.At this time, do not attach the coating paper to the mold and press coating only BMC or coating 紙 (coating paper made of raw materials such as paper, polyester, and vinyl) that can give various patterns and color patterns on the lower or upper molding board. It can be laid or attached and press molded into BMC.
상기와 같이 고온 고압으로 프레스로 성형된 BMC 를 프레스로부터 탈형하고 가장자리의 흠을 제거하는 트리밍작업을 한다. 트리밍 작업후에는 상온에서 냉각을 한다. (S140)As described above, the BMC formed by the press at high temperature and high pressure is demolded from the press and trimming is performed to remove the flaw of the edge. Cool at room temperature after trimming. (S140)
냉각되어 나온 원판 성형제품은 크기별로 재단하여 1차 제품으로 사용할 수도 있고, (S150) 이 1차 제품에 금박(Gold Foil)을 접착하여 금박이 베껴지지 않도록 이를 코팅 처리한 후 2차 제품으로 활용할 수도 있다. (S160)The cooled original molded product can be cut into different sizes and used as the primary product, or (S150) is used as a secondary product after coating the gold foil to prevent the gold foil from being copied by bonding the gold foil to the primary product. It may be. (S160)
본 발명에서는 상기 BMC 를 프레스에서 성형된 기능성황금생기석을 포함하는 다기능성 건축내외장재 패널의 한쪽면 또는 양쪽면에 염산으로 강산처리하여 표면을 거칠게 한 후 물로 세척하여 건조시킨 다음, 패널에 접착제를 바르고, 여러가지 무늬와 색깔문양을 낼 수 있는 코팅지를 붙이는 것도 가능하다.In the present invention, the BMC is treated with hydrochloric acid on one or both sides of the multi-functional building interior and exterior panel including the functional golden gilt stone molded in a press, the surface is roughened, washed with water and dried, and then the adhesive is applied to the panel. It is also possible to apply coated paper to apply various patterns and colors.
본 발명에 따른 건축내외장재 패널의 실시예로서 코팅지가 붙여진 것과 금박이 붙여진 패널의 예를 설명하면 다음과 같다.As an example of the building interior and exterior panels according to the present invention will be described an example of the coated paper and the gold-plated panel as follows.
우선 코팅지가 붙여진 실시예는, 모나자이트, 맥반석 등 인체건강에 유익한 기능을 가진 기능성황금생기석을 포함하는 다기능성 건축내외장재( 다양한 두께와 크기, 모양의 건축자재 패널)에 나무무늬 또는 특별한 문양과 색깔 등 다양한 무늬와 색깔을 가진 PET; 폴리에틸렌테레프탈레이트; PolyethyleneTerephthalate(또는 PE; 폴리에틸렌; Polyethylene, LLDPE; Linear Low Density Poly Ethylene, PP; Poly Propylene, PC; Polycarbonate; 폴리카보네이트, Acryl;아크릴수지 등 합성수지)코팅지를 부착하여 건축 내외장의 장식용의 가치를 더욱 높이기 위한 것으로, 기능성황금생기석을 포함하는 다기능성건축 내외장 패널의 상부에 내마모성과 내스크래치성(표면에 긁힘을 방지하는 성질)의 성능을 발휘하는 아크릴산용(또는 우레탄 용)의 성분으로 구성된 접착성능이 좋은 첨가제를 넣은 합성수지 접착제의 접착제층; 나무무늬 또는 특별한 문양과 색깔 등 다양한 무늬와 색깔을 가진 PET;폴리에틸렌테레프탈레이트; PolyethyleneTerephthalate(또는 PE; 폴리에틸렌; Polyethylene, LLDPE; Linear Low Density Poly Ethylene, PP; Poly Propylene, PC; Polycarbonate ; 폴리카보네이트, Acryl;아크릴수지 등 합성수지)코팅지 층을 접착제층의 상부에 부착하여 형성하는 나무무늬 또는 특별한 문양과 색깔 등 다양한 무늬와 색깔을 가진 PET;폴리에틸렌테레프탈레이트; PolyethyleneTerephthalate(또는 PE; 폴리에틸렌; Polyethylene, LLDPE; Linear Low Density Poly Ethylene, PP; Poly Propylene, PC; Polycarbonate ; 폴리카보네이트, Acryl;아크릴수지 등 합성수지)코팅지층 ; 코팅지층의 상부에 코팅되며, 아크릴산으로 구성되는 보호층; 및 우레탄과 경화제로 구성되는 특수 보호층으로 구성되는 것을 특징으로 한다. First of all, the coated paper is a multi-functional building interior and exterior materials (building materials panels of various thicknesses, sizes, and shapes), including monazite, elvan, and the like. PET with various patterns and colors, etc .; Polyethylene terephthalate; Polyethylene Terephthalate (or PE; polyethylene; Polyethylene, LLDPE; Linear Low Density Poly Ethylene, PP; Poly Propylene, PC; Polycarbonate; Polycarbonate, Acryl; Acrylic resin, etc.) Adhesion performance composed of components for acrylic acid (or urethane) that exhibits abrasion resistance and scratch resistance (property to prevent scratches on the surface) on top of a multifunctional architectural interior and exterior panel including a functional golden gilded stone. Adhesive layer of a synthetic resin adhesive containing this good additive; PET with various patterns and colors, such as wood patterns or special patterns and colors; polyethylene terephthalate; Polyethylene Terephthalate (or PE; polyethylene; Polyethylene, LLDPE; Linear Low Density Poly Ethylene, PP; Poly Propylene, PC; Polycarbonate; Polycarbonate, Acryl; Acrylic resin, etc.) Or PET having various patterns and colors such as special patterns and colors; polyethylene terephthalate; Polyethylene Terephthalate (or PE; polyethylene; Polyethylene, LLDPE; Linear Low Density Poly Ethylene, PP; Poly Propylene, PC; Polycarbonate; polycarbonate, Acryl; synthetic resin such as acrylic resin) coating paper layer; A protective layer coated on top of the coated paper layer and composed of acrylic acid; And it is characterized by consisting of a special protective layer consisting of a urethane and a curing agent.
따라서, 모나자이트, 맥반석 등 인체건강에 유익한 기능을 가진 기능성황금생기석을 포함하는 다기능성 건축내외장재( 다양한 두께와 크기, 모양의 건축자재 패널)에 나무무늬 또는 특별한 문양과 색깔 등 다양한 무늬와 색깔을 가진 PET;폴리에틸렌테레프탈레이트; PolyethyleneTerephthalate(또는 PE; 폴리에틸렌; Polyethylene, LLDPE; Linear Low Density Poly Ethylene, PP; Poly Propylene, PC; Polycarbonate ; 폴리카보네이트, Acryl;아크릴수지 등 합성수지)코팅지를 부착 사용하여 코팅지에 의한 장식효과를 높일 수 있어 사람들에게 더욱 만족한 효과를 얻게 된다. 특히, 자연 상태의 나무 무늬를 코팅지에 직접 형상화 인쇄하여 뚜렷한 자연상태의 무늬를 얻을 수 있어 더욱 뚜렷한 효과를 얻을 수 있도록 한다. Therefore, various patterns and colors such as wooden patterns or special patterns and colors may be applied to multifunctional building interior and exterior materials (building materials panels of various thicknesses, sizes, and shapes), including functional golden giltstones that have beneficial functions for human health such as monazite and elvan. PET having; polyethylene terephthalate; Polyethylene Terephthalate (or PE; polyethylene; Polyethylene, LLDPE; Linear Low Density Poly Ethylene, PP; Poly Propylene, PC; Polycarbonate; Polycarbonate, Acryl; Acrylic resin, etc.) The effect is more satisfying to people. In particular, it is possible to obtain a distinctive natural pattern by printing the shape of the natural wood pattern directly on the coated paper to obtain a more distinct effect.
모나자이트, 맥반석 등 인체건강에 유익한 기능을 가진 기능성황금생기석을 포함하는 다기능성 건축내외장재패널을 벽면에 부착시키는 경우에 접착제를 이용하여 패널에 나무무늬 또는 특별한 문양과 색깔 등 다양한 무늬와 색깔을 가진 PET;폴리에틸렌테레프탈레이트; PolyethyleneTerephthalate(또는 PE; 폴리에틸렌; Polyethylene, LLDPE; Linear Low Density Poly Ethylene, PP; Poly Propylene, PC; Polycarbonate ; 폴리카보네이트, Acryl;아크릴수지 등 합성수지)코팅지를 부착을 하는데, 이러한 경우 부착되는 코팅지의 내마모성과 표면에 긁힘 현상(스크래치)를 방지하기 위하여 패널 표면를 거칠게 하여 코팅지가 패널에 잘 부착시키는 것이 매우 중요하다. 따라서 패널 표면에 적당한 온도와 시간을 경과시켜 묽은 염산으로 패널표면을 산 처리한 후 수세처리(물로 씻어 내는 것) 건조과정(말리기)을 거쳐 말린 다음, 아크릴용(또는 우레탄 용)에 접착성능이 좋은 첨가제를 넣은 합성수지 접착제를 패널표면에 바른 후 다양한 무늬와 색깔을 가진 PET;폴리에틸렌테레프탈레이트; PolyethyleneTerephthalate(또는 PE; 폴리에틸렌; Polyethylene, LLDPE; Linear Low Density Poly Ethylene, PP; Poly Propylene, PC; Polycarbonate ; 폴리카보네이트, Acryl;아크릴수지 등 합성수지) 코팅지를 감은 로울러로 패널 표면에 눌러 압착시켜 건조하면 된다. 이렇게 하면 특별한 문양과 색깔 등 다양한 무늬와 색깔을 가진 PET;폴리에틸렌테레프탈레이트; PolyethyleneTerephthalate(또는 PE; 폴리에틸렌; Polyethylene, LLDPE; Linear Low Density Poly Ethylene, PP; Poly Propylene, PC; Polycarbonate ; 폴리카보네이트, Acryl;아크릴수지 등 합성수지)코팅지를 부착한 내마모성과 내스크래치(긁힘현상방지)의 인체건강에 유익한 기능을 가진 기능성황금생기석을 포함하는 다기능성 건축내외장재패널이 완성된다. When attaching a multi-functional building interior and exterior panels containing functional golden girts that have beneficial functions to human health, such as monazite and elvan, on the wall, the panel has various patterns and colors such as wood patterns or special patterns and colors. PET; polyethylene terephthalate; Polyethylene Terephthalate (or PE; polyethylene; Polyethylene, LLDPE; Linear Low Density Poly Ethylene, PP; Poly Propylene, PC; Polycarbonate; Polycarbonate, Acryl; Acrylic resin, etc.) In order to prevent scratches (scratches) on the surface, it is very important that the surface of the panel is roughened so that the coated paper adheres well to the panel. Therefore, after proper temperature and time, the surface of the panel is acid-treated with dilute hydrochloric acid, washed with water (washed out), dried (dried), and then dried for acrylic (or urethane). PET with a variety of patterns and colors after applying synthetic adhesives with good additives to the panel surface; polyethylene terephthalate; Polyethylene Terephthalate (or PE; polyethylene; Polyethylene, LLDPE; Linear Low Density Poly Ethylene, PP; Poly Propylene, PC; Polycarbonate; polycarbonate, Acryl; acrylic resin, etc.) . This allows PET with a variety of patterns and colors, including special patterns and colors; polyethylene terephthalate; Polyethylene Terephthalate (or PE; polyethylene; Polyethylene, LLDPE; Linear Low Density Poly Ethylene, PP; Poly Propylene, PC; Polycarbonate; polycarbonate, Acryl; acrylic resin, etc.) with abrasion resistance and scratch resistance A multifunctional building interior and exterior panel is completed, which contains functional golden giltstones with functions beneficial to human health.
다른 실시예로서 금박이 붙여진 패널을 설명하면, 모나자이트, 맥반석 등 인체건강에 유익한 기능을 가진 기능성황금생기석을 포함하는 다기능성 건축내외장재(다양한 두께와 크기, 모양의 건축자재 패널)에 금박(또는 은박, 기타 합금박 및 금속박, 나무무늬 또는 특별한 문양과 색깔 등 다양한 무늬와 색깔을 가진 PET등 합성수지로 만든 코팅지 포함)을 부착하여 건축 내외장의 장식용의 가치를 더욱 높이기 위한 것으로, 기능성황금생기석을 포함하는 다기능성건축 내외장 패널의 상부에 도포되며 아크릴산으로 구성되는 접착제층; 두드려 얇게 형성되는 금박(또는 은박, 기타 합금박 및 금속박, 나무무늬 또는 특별한 문양과 색깔 등 다양한 무늬와 색깔을 가진 PET 코팅지 포함)을 접착제층의 상부에 부착하여 형성하는 금박층(또는 은박층, 기타 합금박층 및 금속박층, 나무무늬 또는 특별한 문양과 색깔 등 다양한 무늬와 색깔을 가진 PET 코팅지층 포함); 금박층의 상부에 코팅되며, 아크릴산으로 구성되는 보호층; 및 우레탄과 경화제로 구성되는 특수 보호층으로 구성되는 것을 특징으로 한다. In another embodiment, a panel coated with gold leaf is used to describe a gold foil (or a building material panel) in a multifunctional building interior and exterior material (a panel having various thicknesses, sizes, and shapes) including a functional golden gilt stone having functions beneficial to human health, such as monazite and elvan. Silver foil, other alloy foil, metal foil, wood pattern, or coated paper made of synthetic resin such as PET with various patterns and colors such as special patterns and colors) to enhance the decorative value of the interior and exterior of the building. The adhesive layer is applied to the upper portion of the multi-functional architectural interior and exterior panels including an acrylic acid; Gold foil layer (or silver foil layer) formed by attaching thin thin gold foil (or silver foil, other alloy foil and metal foil, wood pattern or PET coated paper with various patterns and colors such as special patterns and colors) on top of the adhesive layer Other alloy thin and metal thin layers, including wooden coatings or PET coated paper layers of various patterns and colors, such as special patterns and colors); A protective layer coated on top of the gold foil layer and composed of acrylic acid; And it is characterized by consisting of a special protective layer consisting of a urethane and a curing agent.
따라서, 모나자이트, 맥반석 등 인체건강에 유익한 기능을 가진 기능성황금생기석을 포함하는 다기능성 건축내외장재( 다양한 두께와 크기, 모양의 건축자재 패널)에 금박(또는 은박, 기타 합금박 및 금속박, 나무무늬 또는 특별한 문양과 색깔 등 다양한 무늬와 색깔을 가진 PET 코팅지 포함)이 부착 사용하여 금 또는 코팅지에 의한 장식효과를 높일 수 있으며, 금의 효능을 얻을 수 있어 사람들에게 더욱 유익하게 된다. 특히, 금박을 직접 형상화하여 뚜렷한 금색을 얻을 수 있어 더욱 뚜렷한 효과를 얻을 수 있도록 한다. Therefore, gold foil (or silver foil, other alloy foils and metal foil, wood pattern) on multifunctional building interior and exterior materials (building materials panels of various thicknesses, sizes and shapes), including functional golden giltstones with functions beneficial to human health, such as monazite and elvan. Or PET coated paper with various patterns and colors, such as special patterns and colors, can be used to increase the decorative effect of gold or coated paper, and the benefits of gold can be obtained to benefit people more. In particular, it is possible to obtain a distinct gold color by directly shaping the gold leaf to obtain a more distinct effect.
본 발명에 따른 다기능성 원료인 일명 기능성 황금생기석 (機能性黃金生氣石; Functional Gold Energy Stone)을 일정한 배합 비율로 섞어 각종 색깔의 기능성 건축용 자재를 생산할 수 있으며 농,수산용 동식물 사료용 및 농업용 비료, 새집증후군방지 페인트 및 시멘트 첨가제용, 화장품용 첨가제, 각종 기능성 생활용품 첨가제용, 의류 및 침구, 기능성 전자제품 첨가제용으로 응용하여 다양한 종류의 제품을 생산할 수 있다.A multifunctional raw material, also known as functional gold energy stone (functional gold energy stone) according to the present invention can be mixed in a certain mixing ratio to produce functional building materials of various colors, and for farming, fisheries animal and plant feed and agricultural fertilizer It is possible to produce various kinds of products by applying for new house syndrome prevention paint and cement additive, cosmetic additive, various functional household additive, clothing and bedding, and functional electronic additive.
본 발명에 따른 제조방법에 의해 제조된 기능성 황금생기석은 여러 가지 기능성 광물질을 배합 조성하여 음이온 (발생효능: 250~80,000 ION/cc) 및 원적외선 방사기능 (방사율: 0.85~0.932), 수맥 인체장해 방지 기능, 전자파 인체장해방지기능, 회전전자파(氣)의 경락순환구동력 기능, 신진 대사 촉진 기능, 항균, 탈취 등 다기능성이 동시에 나오는 현저한 효과가 있다. The functional gold bio-stone manufactured by the manufacturing method according to the present invention is formulated with various functional minerals to form anion (generating effect: 250 ~ 80,000 ION / cc) and far infrared radiation function (emissivity: 0.85 ~ 0.932), preventing vein human injury Function, electromagnetic wave prevention function, meridians circulatory driving force function of rotating electromagnetic wave, metabolic promoting function, antibacterial, deodorizing, etc. There is a remarkable effect coming out at the same time.
본 발명의 황금생기석의 효과를 더욱 상세히 기술하면,In more detail describing the effect of the golden raw stone of the present invention,
(1) 원적외선효과로 세포를 활성화 한다. (1) Activate the cells by far infrared effect.
- 피부 깊은 곳까지 따뜻하게 하여 혈액순환을 촉진시키며, 신진대사를 활발하게 하여 세포를 활성화 한다. -It warms deep into the skin to promote blood circulation and activates metabolism by activating cells.
- 손·발의 냉증을 및 결림·뻐근함을 해소 시키며 혈액순환 장애에 의한 질병에 탁월한 효과가 기대된다. -Relieves coldness of hands and feet, stiffness and swelling, and is expected to have an excellent effect on diseases caused by blood circulation disorder.
(2)음이온 효과로 혈액순환과 신진대사 촉진 (2) Promotes blood circulation and metabolism with negative ion effect
- 기치유력 향상, 면역기능, 신진대사를 촉진하여 자율신경의 안정, 교감신경을 억제한다. -Promotes banner potency, promotes immune function, metabolism, stabilizes autonomic nerves and suppresses sympathetic nerves.
- 운동선수, 학생, 골퍼 등에게 집중력을 향상시키며, 혈압·호흡을 안정시킨다. -Enhance concentration and improve blood pressure and breathing for athletes, students, and golfers.
- 활성산소를 억제하고 세포를 보호하며, 체내의 누적된 스트레스를 해소 한다. -It inhibits free radicals, protects cells, and relieves accumulated stress in the body.
(3) 미약파동 전류효과 (3) weak wave current effect
- 체내 혈액순환을 촉진하여 위경련, 요통, 관절통을 완화. -Promotes blood circulation in the body to relieve stomach cramps, back pain and joint pain.
(4) 회전전자파(氣)의 경락순환구동력 기능 ㆍ전자파 인체 장해 방지기능 ㆍ신진대사 촉진 기능 (4) Meridian circulation driving function of rotating electromagnetic waves ㆍ Prevents electromagnetic interference of human body ㆍ Promotes metabolism
(5) 수맥인체 장해 방지기능 (5) Preventing water vein obstacle
- 인체에 해로운 좌회전에너지를 우회전에너지로 바꿔 준다. -Turn left energy which is harmful to human body into right turn energy.
(6) 혈압·자율신경조정 (6) blood pressure and autonomic nervous system
- 체내 60%를 차지하는 수분을 활성화시키며, 경락을 자극, 체내 기관이나 장기의 원기를 회복시킨다. -Activates 60% of the body's water, stimulates meridians and restores vital organs and organs.
(7) 미용효과로 노화방지 효과 (7) Anti-aging effect by beauty effect
- 피부 세포를 자극하여 각질을 활성화하여 피부의 탄력을 유지시키고, 된 체내 수분을 알칼리화시켜 체질개선과 미용 및 노화방지효과가 기대된다. -It stimulates skin cells to activate keratin to maintain skin's elasticity, alkalinize the body's moisture and improves constitution, beauty and anti-aging effect.
(8) 그 외 효과 (8) other effects
정전기 제거효과, 미네랄방출효과, 살균효과, 온열 효과, 계면활성 효과, 표백효과, 전위효과, 운동능력 활성화 효과등이 있다. There are static elimination effect, mineral release effect, bactericidal effect, thermal effect, surfactant activity, bleaching effect, dislocation effect, exercise ability activation effect.
본 발명의 황금생기석은 한국원적외선 응용평가 연구원 시험결과 성적서에 의하면 원적외선 측정결과 방사율(5~20㎛) 92. 4% 로 매우 양호하고, 음이온 측정결과-700~1500개/cc 로 인체에 가장 유익한 음이온 수치 판정되었다.According to the test results report of the Korea Far Infrared Rays Evaluation Appraisal Institute, the golden biomagnet of the present invention is very good at 92.4% of far-infrared measurement result (5 ~ 20㎛), and is most beneficial to human body at anion measurement result of 700 ~ 1500 / cc. Anion value was determined.
또한, 아주대학교 회전전자파 측정연구팀 시험결과 성적서에 의하면, 본 발명의 황금생기석은 수맥인체 장해 방지기능이 매우 양호하고, 인체에 해로운 좌회전에너지를 우회전에너지로 매우 양호하게 바꿔 주고, 회전전자파(氣)의 경락순환구동력 기능을 매우 양호하게 하고, 기능성 황금생기석에서 발생되는 회전전자파 (氣) 가 인체에 들어가 인체에 있는 경락의 에너지 흐름을 방해하는 에너지를 외부로 몰아내고 흐름을 정상화시켜 인체의 면역활동을 및 생체활동을 활성화 시키는 작용을 매우 양호하게 지속적으로 유지하고 있고, 전자파 인체 장해 방지기능이 매우 양호하고, 핸드폰, 무전기, 가전기기 등에서 방출되는 인체에 해로운 유해 전자파 즉 좌회전 에너지(음성에너지)를 유익한 우회전에너지(양성에너지)로 바꿔주는 능력이 매우 탁월하고, 신진대사 촉진 기능이 매우 양호하다고 판정되었다.In addition, according to the test results of the Ajou University rotational electromagnetic wave measurement research team test results, the golden fresh stone of the present invention has a very good function of preventing vein human obstacle, and converts the left rotational energy, which is harmful to the human body, to the right rotational energy, and is very good. Meridian circulatory driving force of the function is very good, and the rotating electromagnetic wave generated from the functional golden fresh stone enters the human body to drive the energy that hinders the flow of the meridians in the human body to the outside and normalizes the flow of the human body's immunity. It maintains the activity of activating and activating the biological activity very well and has a very good function of preventing electromagnetic interference, and it is harmful to the human body emitted from mobile phones, walkie-talkies, home appliances, etc. Very good at converting energy into beneficial right turn energy (positive energy) It was judged to have the metabolic capability to promote very good.
이상에서, 본 발명의 구체적인 실시예들을 이용하여 본 발명의 기술적 사상을 구체적으로 설명하였으나, 이는 본 발명의 범위에서 벗어나지 않는 한도 내에서 다양한 변형이 가능함은 자명하다 하겠다. 그러므로 본 발명의 범위는 상술한 실시예에 국한되어서는 아니되며 후술하는 특허청구의 범위 및 이 특허청구의 범위와 균등한 것들에 의해 정해져야 한다.In the above, although the technical spirit of the present invention has been described in detail using specific embodiments of the present invention, it will be apparent that various modifications may be made without departing from the scope of the present invention. Therefore, the scope of the present invention should not be limited to the above-described embodiments, but should be defined by the following claims and their equivalents.
Claims (8)