KR101449345B1 - Artificial Marble - Google Patents
Artificial Marble Download PDFInfo
- Publication number
- KR101449345B1 KR101449345B1 KR1020130145984A KR20130145984A KR101449345B1 KR 101449345 B1 KR101449345 B1 KR 101449345B1 KR 1020130145984 A KR1020130145984 A KR 1020130145984A KR 20130145984 A KR20130145984 A KR 20130145984A KR 101449345 B1 KR101449345 B1 KR 101449345B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- glass fiber
- fiber reinforced
- artificial marble
- Prior art date
Abstract
Description
본 발명은 인조대리석에 관한 것으로, 좀 더 상세하게는 아크릴계의 호환성 문제를 해결하고, 기계적 강도 및 내오염성, 내스크래치성을 강화하며, 화재에 강하고 자연친화적인 인조대리석에 관한 것이다.
The present invention relates to an artificial marble, more particularly, to an artificial marble which solves the acrylic compatibility problem, enhances mechanical strength and stain resistance, scratch resistance, and is fire-resistant and natural.
일반적으로, 인조대리석은 우수한 가공성, 내후성 및 시공성을 가지고 있을 뿐만 아니라 천연대리석과 비교하여 가볍고, 비 다공질이며, 천연대리석에 뒤떨어지지 않는 우수한 색조 및 뛰어난 강도 등으로 인하여 천연대리석에 비하여 그 활용 범위가 넓다. 특히, 건축 내ㆍ외장재로 많이 사용되고 있으며, 씽크대, 상판, 세면 화장대의 상판, 은행 및 일반 매장의 접수대 등 각종 카운터의 상판, 내벽재, 각종 인테리어 조형물 등의 소재로 많이 사용되고 있다. In general, artificial marble has excellent processability, weatherability and workability, and is lighter, non-porous compared to natural marble, superior color tone that is not inferior to natural marble, and excellent strength compared to natural marble. wide. Especially, it is widely used as interior and exterior materials for construction. It is widely used as a material for various counter tops, interior wall materials, various interior sculptures such as sinks, tops, tops of washcloths, reception counter for banks and general stores.
이러한 인조대리석은 그 사용되는 베이스 레진(Base resin)에 따라 크게 아크릴계와 불포화 폴리에스테르계의 두 가지 종류로 구분된다.These artificial marbles are divided into two types, acrylic and unsaturated polyester, depending on the base resin used.
아크릴계 인조대리석은 우수한 내구성 및 내후성을 가지고 있고, 목질과 비견될 만한 우수한 가공성을 가지고 있으며, 수지 자체의 은은한 투명성과 고급스러운 질감 및 우수한 내후성 등의 장점을 가지고 있다.Acrylic artificial marble has excellent durability and weatherability, has excellent processability comparable to wood, and has merits such as the transparent transparency of the resin itself, luxurious texture and excellent weather resistance.
그리고 불포화 폴리에스테르계 인조대리석은 내후성과 내열성이 아크릴계 인조대리석보다 열악하고 열성형이 어려운 단점이 있으나, 충진제로 사용되는 수산화 알루미늄 등과 굴절율이 비슷하여 중합물의 투명도가 우수함으로써 보다 천연 대리석과 같은 자연스럽고 깊이감 있는 외관 구현이 가능하다.Unsaturated polyester artificial marble has a disadvantage in that weather resistance and heat resistance are worse than acrylic artificial marble and thermoforming is difficult, but since the refractive index is similar to that of aluminum hydroxide used as a filler, the transparency of the polymer is excellent, It is possible to realize a deep sense of appearance.
종래 수지계 인조대리석은 합성 수지에 무기 충전제와 같은 첨가제를 혼합하여 조성물을 제조하고, 이를 연속방식인 캐스팅 공법에 적용하여 제조하고 있다. 수지계 인조대리석이 주로 캐스팅 공법에 의해 제조되는 이유는 합성 수지를 주성분으로 하는 조성물의 점도를 프레스 공법의 적용이 가능한 수준으로 끌어올리는 것이 어렵기 때문이다. 예를 들어, 수지 조성물의 점도를 높이기 위하여 무기 충전제의 함량을 높일 경우, 점도 상승에 수반하여 흐름성이 매우 열악해져서 기포의 제거가 불가능하고, 성형된 제품의 강도 및 표면 품질도 매우 떨어지게 된다.Conventionally, resin-based artificial marble is prepared by mixing a synthetic resin with an additive such as an inorganic filler to prepare a composition and applying it to a continuous casting method. The reason why the resin-based artificial marble is mainly produced by the casting method is that it is difficult to raise the viscosity of a composition containing a synthetic resin as a main component to a level at which the press method can be applied. For example, when the content of the inorganic filler is increased in order to increase the viscosity of the resin composition, the flowability becomes very poor along with the viscosity increase, so that the bubbles can not be removed, and the strength and surface quality of the molded product are very low.
또한, 수지계 인조대리석은 특성상 박판으로 제조되기 어렵고, 과도한 중량으로 인하여 벽 판넬로의 이용이 제한된다. 즉, 인조대리석이 벽 판넬로 적용되는 경우 파괴 및 깨짐 현상이 쉽게 발생하고, 낮은 강도로 인하여 내오염성 및 내스크래치성이 약한 단점이 있다. 또한, 천연 대리석에 가까운 질감을 내는 데에만 치중하였을 뿐, 자연친화적 기능과는 무관하였다.
Further, the resin-based artificial marble is difficult to be manufactured as a thin plate due to its characteristics, and its use as a wall panel is limited due to its excessive weight. That is, when artificial marble is applied to a wall panel, breakage and breakage are easily occurred, and there is a disadvantage that the stain resistance and scratch resistance are weak due to low strength. In addition, we focused only on the texture of natural marble, but it was not related to nature-friendly functions.
한국등록특허: 10 - 1260148 (공고일 2013. 05. 02) Korea registered patent: 10 - 1260148 (Notification date 2013. 05. 02)
한국등록특허: 10 - 1167031 (공고일 2012. 07. 27)
Korea Registered patent: 10 - 1167031 (Notification date 07. 27, 2012)
본 발명은 종래의 문제점을 해결하기 위해 안출 된 것으로서,SUMMARY OF THE INVENTION The present invention has been made to solve the conventional problems,
본 발명의 목적은 식물섬유인 모시줄기와, 유리섬유강화석고와, 유리섬유강화시멘트를 이용하여 아크릴계의 호환성 문제를 해결하고, 기계적 강도 및 내오염성, 내스크래치성을 강화하며, 표면 질감 및 채색성을 향상시킬 뿐만 아니라 화재에 강하고, 자연친화적인 인조대리석을 제공하는 데 있다.
The object of the present invention is to solve the acrylic compatibility problem by using the stem fiber, fiberglass reinforced gypsum and fiberglass reinforced cement, which are plant fibers, to enhance the mechanical strength, stain resistance, scratch resistance, Which not only improves the properties but also is resistant to fire and is natural-friendly artificial marble.
상기와 같은 목적을 달성하기 위해 제공되는 본 발명의 일 실시 예에 따른 인조대리석은 베이스 수지, 무기충전물, 가교제, 중합개시제를 포함하는 인조대리석원료 100 중량부에 대하여 변성 모시줄기가루 0.1 내지 50 중량부, 유리섬유강화석고(GRG) 0.1 내지 20 중량부, 유리섬유강화시멘트(GRC) 0.1 내지 20 중량부를 포함한다.In order to achieve the above object, the artificial marble according to an embodiment of the present invention comprises 100 parts by weight of an artificial marble raw material containing a base resin, an inorganic filler, a crosslinking agent, and a polymerization initiator, 0.1 to 20 parts by weight of glass fiber reinforced gypsum (GRG), and 0.1 to 20 parts by weight of glass fiber reinforced cement (GRC).
여기서, 상기 변성모시줄기가루는 90 내지 110℃의 온도에서 모시줄기가루 100 중량부에 대하여 표면변성제 1 내지 2 중량부를 분사하여 제조된 것을 특징으로 한다.The modified flax seed powder is prepared by spraying 1 to 2 parts by weight of a surface modifier with respect to 100 parts by weight of foxtail flour at a temperature of 90 to 110 ° C.
그리고, 상기 인조대리석원료는 베이스 수지 100 중량부에 대하여 무기 충전물 10 내지 50 중량부, 가교제 0.1 내지 20 중량부, 중합 개시제 0.1 내지 20 중량부를 포함하는 것을 특징으로 한다.The artificial marble raw material is characterized by comprising 10 to 50 parts by weight of an inorganic filler, 0.1 to 20 parts by weight of a crosslinking agent, and 0.1 to 20 parts by weight of a polymerization initiator based on 100 parts by weight of the base resin.
그리고, 상기 유리섬유강화시멘트는 시멘트와 유리섬유가 중량비로 10:1 내지 30:1의 비율로 배합된 것을 특징으로 한다. The glass fiber reinforced cement is characterized in that cement and glass fiber are blended in a weight ratio of 10: 1 to 30: 1.
또한, 상기 유리섬유강화석고는 석고와 유리섬유가 중량비로 10:1 내지 30:1의 비율로 배합된 것을 특징으로 한다.The glass fiber reinforced gypsum is characterized in that the gypsum and the glass fiber are blended in a weight ratio of 10: 1 to 30: 1.
상기 베이스 수지는 아크릴계 수지, 에폭시계 수지, 멜라민계 수지 및 불포화 폴리에스테르계 수지로 이루어진 군으로부터 하나 이상의 것이 선택되고, 상기 무기 충전물은 탄산칼슘, 수산화 알루미늄, 실리카, 알루미나, 유산바륨 및 수산화 마그네슘으로 이루어진 군으로부터 하나 이상의 것이 선택되며, 상기 가교제는 에틸렌 글리콜 디 메타 아크릴레이트, 프로필렌 글리콜 디 메타 아크릴레이트, 글리세롤 트리 메타 아크릴레이트, 트리메틸 프로판 트리 메타 아크릴레이트 및 비스페놀 A 디 메타 아크릴레이트로 이루어진 군으로부터 하나 이상의 것이 선택되는 것을 특징으로 한다.Wherein the base resin is selected from the group consisting of an acrylic resin, an epoxy resin, a melamine resin and an unsaturated polyester resin, and the inorganic filler is selected from the group consisting of calcium carbonate, aluminum hydroxide, silica, alumina, barium sulfate and magnesium hydroxide Wherein the crosslinking agent is selected from the group consisting of ethylene glycol dimethacrylate, propylene glycol dimethacrylate, glycerol trimethacrylate, trimethylpropane trimethacrylate and bisphenol A dimethacrylate Or more is selected.
상기 인조대리석에는 베이스 수지 100 중량부에 대하여 마불칩 0.1 내지 200 중량부가 더 포함되는 것을 특징으로 한다.The artificial marble further comprises 0.1 to 200 parts by weight of a waxy chip based on 100 parts by weight of the base resin.
상기 마블칩은 베이스 수지 100 중량부에 대하여, 무기 충전물 100 내지 200 중량부, 음이온세라믹 1 내지 20 중량부, 가교제 0.1 내지 10 중량부 및 개시제 0.1 내지 10 중량부를 혼합하고 경화한 다음, 이를 0.1mm 내지 5mm 크기로 파쇄한 것을 특징으로 한다.The Marble chip is prepared by mixing and curing 100 to 200 parts by weight of an inorganic filler, 1 to 20 parts by weight of an anionic ceramic, 0.1 to 10 parts by weight of a crosslinking agent and 0.1 to 10 parts by weight of an initiator with respect to 100 parts by weight of a base resin, To 5 mm in size.
여기서, 상기 음이온 세라믹은 항균력 90%이상, 원적외선 방사율 90%이상, 음이온방출수 3,000(ion/cc) 이상의 것이 사용되는 것을 특징으로 한다.Here, the anionic ceramic is characterized in that it has an antibacterial activity of 90% or more, a far infrared ray emissivity of 90% or more, and an anion emission number of 3,000 (ion / cc) or more.
본 발명의 다른 실시 예에 따른 인조대리석은 베이스 수지 100 중량부에 대하여, 유리섬유강화석고 5 내지 150 중량부, 무기 충전물 5 내지 80 중량부, 가교제 0.1 내지 10 중량부, 중합 개시제 0.1 내지 10 중량부를 포함하는 유리섬유강화석고층; 베이스 수지 100 중량부에 대하여, 변성 모시줄기가루 5 내지 150 중량부, 무기 충전물 5 내지 80 중량부, 가교제 0.1 내지 10 중량부, 중합 개시제 0.1 내지 10 중량부를 포함하는 변성모시줄기층; 베이스 수지 100 중량부에 대하여, 유리섬유강화시멘트 5 내지 150 중량부, 무기 충전물 5 내지 80 중량부, 가교제 0.1 내지 10 중량부, 중합 개시제 0.1 내지 10 중량부를 포함하는 유리섬유강화시멘트층;을 포함하며, 상기 유리섬유강화석고층, 변성모시줄기층, 유리섬유강화시멘트층은 순서와 상관없이 다단으로 적층되어 일체로 이루어진 것을 특징으로 한다.The artificial marble according to another embodiment of the present invention comprises 5 to 150 parts by weight of glass fiber reinforced gypsum, 5 to 80 parts by weight of inorganic filler, 0.1 to 10 parts by weight of a crosslinking agent, 0.1 to 10 parts by weight of a polymerization initiator A glass fiber reinforced stone high layer including a part; A modified waxy stem layer comprising 5 to 150 parts by weight of modified stem roots powder, 5 to 80 parts by weight of an inorganic filler, 0.1 to 10 parts by weight of a crosslinking agent, and 0.1 to 10 parts by weight of a polymerization initiator, based on 100 parts by weight of the base resin. A glass fiber reinforced cement layer comprising 5 to 150 parts by weight of a glass fiber reinforced cement, 5 to 80 parts by weight of an inorganic filler, 0.1 to 10 parts by weight of a crosslinking agent and 0.1 to 10 parts by weight of a polymerization initiator, based on 100 parts by weight of the base resin And the glass fiber reinforced stone high layer, the modified ramshackle layer and the glass fiber reinforced cement layer are laminated in a multi-layered structure regardless of the order.
여기서, 상기 유리섬유강화석고층, 변성모시줄기층, 유리섬유강화시멘트층 중 선택되는 어느 하나 이상의 층에는 마불칩이 더 포함되고, 상기 마블칩은 베이스 수지 100 중량부에 대하여, 무기 충전물 100 내지 200 중량부, 음이온세라믹 1 내지 20 중량부, 가교제 0.1 내지 10 중량부 및 개시제 0.1 내지 10 중량부를 혼합하고 경화한 다음, 이를 0.1mm 내지 5mm 크기로 파쇄한 것을 특징으로 한다.
At least one layer selected from the above glass fiber-reinforced stone high layer, modified starch layer, and glass fiber reinforced cement layer further comprises a wax chip, wherein the marble chip comprises 100 to 200 parts by weight of
본 발명의 인조대리석에 따르면, 자연 친화적이고, 모시줄기 특유의 독특한 질감으로 다양하고 고급스러운 멋을 연출할 수 있어 제품의 상품성이 향상되는 효과가 있다. According to the artificial marble of the present invention, it is possible to produce diverse and luxurious fashion with a unique texture that is natural-friendly and peculiar to the stem, thereby improving the merchantability of the product.
또한, 가볍고, 시공성이 우수하여 다양한 용도로 활용될 수 있고, 기계적 강도 및 내오염성, 내스크래치성이 우수하며, 불연성이여서 화재에 강할 뿐만 아니라 표면 질감 및 채색성이 우수하고 성형이 용이하여 제품의 생산성 및 신뢰성이 향상되는 효과가 있다.
In addition, it is light, has excellent workability and can be used for various purposes, has excellent mechanical strength, stain resistance and scratch resistance, is nonflammable and is resistant to fire, has excellent surface texture and coloring property, Productivity and reliability are improved.
도 1은 본 발명의 일 실시 예에 따른 인조대리석을 개략적으로 도시한 도면.
도 2a 내지 도 2f는 본 발명의 일 실시 예에 따른 인조대리석을 제조하는 과정의 일부를 도시한 실사 이미지 사진.
도 3은 본 발명의 일 실시 예에 따른 인조대리석을 도시한 실사 이미지 사진.
도 4, 도 5는 본 발명의 일 실시 예에 따른 인조대리석이 사용되는 상태를 도시한 실사 이미지 사진.
도 6은 본 발명의 다른 실시 예에 따른 인조대리석을 개략적으로 도시한 도면.BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a schematic illustration of an artificial marble according to an embodiment of the present invention.
FIGS. 2A to 2F are photographs of actual photographs showing part of a process of manufacturing artificial marble according to an embodiment of the present invention. FIG.
3 is a photograph of an actual image showing an artificial marble according to an embodiment of the present invention.
FIG. 4 and FIG. 5 are photographs of a real image showing a state in which artificial marble is used according to an embodiment of the present invention. FIG.
6 is a schematic view of an artificial marble according to another embodiment of the present invention.
본 발명의 상기와 같은 목적, 특징 및 다른 장점들은 첨부도면을 참조하여 본 발명의 바람직한 실시 예를 상세히 설명함으로써 더욱 명백해질 것이다. 이하, 첨부된 도면을 참조하여 본 발명의 인조대리석을 상세히 설명하기로 한다. 본 명세서를 위해서, 도면에서의 동일한 참조번호들은 달리 지시하지 않는 한 동일한 구성부분을 나타낸다.These and other objects, features and other advantages of the present invention will become more apparent by describing in detail preferred embodiments of the present invention with reference to the accompanying drawings. Hereinafter, the artificial marble of the present invention will be described in detail with reference to the accompanying drawings. For purposes of this specification, like reference numerals in the drawings denote like elements unless otherwise indicated.
본 발명의 일 실시 예에 따른 인조대리석(100)은 베이스 수지, 무기충전물, 가교제, 중합개시제, 변성 모시줄기가루, 유리섬유강화석고(GRG), 유리섬유강화시멘트(GRC)를 포함한다. The
상기의 구성성분들을 포함하는 인조대리석(100)의 바람직한 실시 예는 베이스 수지, 무기충전물, 가교제, 중합개시제를 포함하는 인조대리석원료 100 중량부에 대하여 변성 모시줄기가루 0.1 내지 50 중량부, 유리섬유강화석고(GRG) 0.1 내지 20 중량부, 유리섬유강화시멘트(GRC) 0.1 내지 20 중량부를 포함한다. A preferred embodiment of the
그리고, 인조대리석 원료는 베이스 수지 100 중량부에 대하여 무기 충전물 10 내지 50 중량부, 가교제 0.1 내지 20 중량부, 중합 개시제 0.1 내지 20 중량부를 포함한다.The artificial marble raw material includes 10 to 50 parts by weight of an inorganic filler, 0.1 to 20 parts by weight of a crosslinking agent, and 0.1 to 20 parts by weight of a polymerization initiator based on 100 parts by weight of the base resin.
이하, 인조대리석의 구성성분을 상세히 설명하면 다음과 같다. Hereinafter, the components of the artificial marble will be described in detail.
베이스 수지는 아크릴계 수지, 에폭시계 수지, 멜라민계 수지 및 불포화 폴리에스테르계 수지로 이루어진 군으로부터 선택되는 하나 이상의 것을 사용한다.The base resin is at least one selected from the group consisting of an acrylic resin, an epoxy resin, a melamine resin and an unsaturated polyester resin.
여기서, 아크릴계 수지는 메틸 메타 아크릴레이트, 에틸 메타 아크릴레이트, 탄소수 1 내지 10의 메타 아크릴산 에킬 에스테르, 벤젠 메타 아크릴레이트, 글리시딜 메타 아크릴레이트로 이루어진 군으로부터 선택된 하나 이상의 단량체로 형성되는 것을 들 수 있으나, 이에 한정되는 것은 아니다.Here, the acrylic resin may be formed of one or more monomers selected from the group consisting of methyl methacrylate, ethyl methacrylate, methacrylic acid esters having 1 to 10 carbon atoms, benzene methacrylate, and glycidyl methacrylate. However, the present invention is not limited thereto.
그리고, 에폭시계 수지는 천연소재와 밀착성 등의 관점에서 이관능 또는 다관능성 에폭시 수지를 사용하는 것이 바람직하나, 이에 한정되는 것은 아니다.The epoxy resin is preferably a bifunctional or multifunctional epoxy resin from the viewpoint of adhesion with natural materials, but is not limited thereto.
이관능 또는 다관능성 에폭시 수지의 예로는 비스페놀 A형 에폭시 수지, 비스페놀 S형 에폭시 수지, 테트라 페닐 에탄 에폭시 수지 및 페놀 노볼락형 에폭시 수지로 이루어진 군으로부터 선택 하나 이상의 것을 들 수 있다. Examples of the bifunctional or multifunctional epoxy resin include at least one selected from the group consisting of bisphenol A type epoxy resin, bisphenol S type epoxy resin, tetraphenyl ethane epoxy resin and phenol novolak type epoxy resin.
그리고, 불포화 폴리에스테르계는 이 분야의 통상의 것을 사용할 수 있다. 예로는, 디카르복실산 및 다가 알코올의 축합반응으로부터 얻어지는 것을 들 수 있다. Unsaturated polyester-based resins can be used in the conventional art. Examples thereof include those obtained from the condensation reaction of a dicarboxylic acid and a polyhydric alcohol.
무기충전물은 탄산칼슘, 수산화알루미늄, 실리카, 알루미나, 유산바륨, 수산화 마그네슘과 같이 당 분야에서 통상적으로 사용되는 무기분말 중 어느 것도 사용 가능하며, 약 1 내지 100㎛의 크기를 갖는 것이 바람직하다. 특히, 무기분말 중 수산화알루미늄은 투명하고 미려한 대리석 형상의 외관을 갖는 인조대리석을 제조할 수 있다는 점에서 바람직하다. The inorganic filler may be any of inorganic powders commonly used in the art such as calcium carbonate, aluminum hydroxide, silica, alumina, barium sulfate, magnesium hydroxide, and preferably has a size of about 1 to 100 탆. Particularly, aluminum hydroxide in the inorganic powder is preferable in that it can produce artificial marble having a clear and beautiful marble-like appearance.
가교제는 다관능성 메타 아크릴레이트가 사용되며, 구체적인 예로는 에틸렌 글리콜 디 메타 아크릴레이트, 프로필렌 글리콜 디 메타 아크릴레이트, 글리세롤 트리 메타 아크릴레이트, 트리메틸 프로판 트리 메타 아크릴레이트 및 비스페놀 A 디 메타 아크릴레이트를 들 수 있다.As the crosslinking agent, polyfunctional methacrylate is used. Specific examples thereof include ethylene glycol dimethacrylate, propylene glycol dimethacrylate, glycerol trimethacrylate, trimethylpropane trimethacrylate, and bisphenol A dimethacrylate. have.
그리고, 중합 개시제는 벤조일 퍼옥사이드, 라우로일 퍼옥사이드, 부틸 하이드로 퍼옥사이드, 큐밀 하이드로 퍼옥사이드 등의 과산화물 또는 아조비스이소부틸로니트릴과 같은 아조 화합물을 사용한다.As the polymerization initiator, peroxides such as benzoyl peroxide, lauroyl peroxide, butyl hydroperoxide, cumyl hydroperoxide and the like or azo compounds such as azobisisobutyronitrile are used.
모시줄기는 모시풀에서 얻은 모시섬유의 폐기물이다. 모시섬유는 길이가 6~20cm이고, 질기기는 아마의 4배, 목화의 8배 이상을 가진다. 또한, 모시섬유는 대부분 모시의 인피섬유 부분을 방직품의 상등 섬유원료로 이용하고, 모시풀의 껍질을 벗긴 후의 모시줄기와 표피부분은 폐기물로 여겨 분사 처리된다. 이처럼 분사처리되는 폐기물은 대략 모시 한줄기의 2/3를 차지함에 따라 환경오염뿐만 아니라 극심한 자원 낭비를 초래하였다. The ramshackle is the waste of ramie fibers obtained from the ramshackle. The linen fibers are 6-20 cm long and the vagina has 4 times as much flax and 8 times more than cotton. In addition, most of the ramie fibers are used as upper textile raw materials for the textile, and the ramie stem and the epidermis after the skin is removed are treated as waste. As the wastes treated in this way occupy about two-thirds of the length of the wastes, they cause not only environmental pollution but also wasted resources.
폐기처리되는 모시줄기는 대부분 섬유질로 이루어지고, 그 섬유 가운데는 도랑형 빈강이며 파이프벽은 구멍이 많다. 또한, 가늘고 길고 질기며, 재질이 가볍고, 습기에 대한 흡인과 분산이 빠르다. 따라서, 목재를 대체할 원료로 충분한 가치가 있으며, 농산물계 자원을 활용하고 농업폐기물의 처리문제를 해결하여 농산품의 부가가치를 향상시키고, 모시원료의 광범위한 생산과 저렴한 가격으로 인하여 제품의 원가를 낮추는 데 중요한 역할을 한다.The trunks are mostly made of fibrous material. Among them, the hollow fibers are hollow. The pipe wall has many holes. In addition, it is thin, long and tough, light in material, quick in suction and dispersion with respect to moisture. Therefore, it is of great value as a substitute for timber, and it is necessary to utilize agricultural resources, improve the value added of agriculture products by solving agricultural wastes disposal problems, reduce the cost of products due to the wide production of raw materials and low prices It plays an important role.
그러나, 모시줄기가루는 식물섬유이고, 식물섬유는 강한 극성을 가지고 있어서 아크릴계와의 호환성이 떨어진다.However, flax seedling powder is plant fiber, and plant fiber has strong polarity, which makes it incompatible with acrylic resin.
따라서, 모시줄기와 아크릴계의 호환성을 해결하기 위해 변성 모시줄기가루를 제조한다.Therefore, modified starch stem powder is manufactured to solve the compatibility between the stem and acrylic.
변성 모시줄기가루는 모시줄기를 입자크기가 20 내지 100 메시(mesh)로 분쇄하고 분쇄된 모시줄기가루의 수분을 제거하여 함수량이 3%이내가 되도록 한다. 그리고, 90℃ 내지 110℃의 온도에서 모시줄기가루 100 중량부에 대하여 1 내지 2 중량부인 표면변성제를 모시줄기가루에 분사하여 제조한다. Modified stem stem powder is obtained by grinding ramshackle with a particle size of 20 to 100 mesh and removing moisture from pulverized ramshackle powder to make the water content within 3%. Then, at a temperature of 90 ° C to 110 ° C, 1 to 2 parts by weight of a surface modifier per 100 parts by weight of ramshackle flour is sprayed on the stem flour.
여기서, 상기 표면변성제는 실란 KH550 또는 티탄산염 NDZ-101 : 무수알코올 = 1: 2 내지 4의 중량비로 희석된 것이다. Here, the surface modifier is diluted with a weight ratio of silane KH550 or titanate NDZ-101: anhydrous alcohol = 1: 2 to 4.
실란 KH550은 3-아미노프로필트리에톡시실란의 화학적 명칭으로서 CAS NO : 919-30-2이고, 분자식 : NH2(CH2)3Si(OC2H5)3 이며, 우수한 접착 개선제이며 라텍스와 아미노 실리콘 오일을 생산하는 데 사용된다. 이 제품은 코팅, 접착제 및 실란트의 용도로서 당업계에서는 실란 KH550으로 칭한다.Silane KH550 is a chemical name for 3-aminopropyltriethoxysilane, CAS NO: 919-30-2, and has the molecular formula: NH2 (CH2) 3Si (OC2H5) 3. It is an excellent adhesion improving agent and produces latex and amino silicone oil . This product is referred to in the art as silane KH550 for use as coatings, adhesives and sealants.
또한, 티탄산염 표면변성제 NDZ-101은 티탄산염 기제 커플링제이며, 테트라부틸 티탄산염 중 하나의 타입으로서 이소프로필 디올레산(디옥틸인산염)티탄산염을 말한다. In addition, the titanate surface modifier NDZ-101 is a titanate-based coupling agent, and one type of tetrabutyl titanate refers to isopropyl dioleate (dioctylphosphate) titanate.
이렇게 제조된 변성 모시줄기가루는 아크릴계와의 호환성이 좋아 인조대리석에 사용될 경우, 자연친화적이고, 모시원료의 광범위한 생산과 폐모시줄기의 활용으로 고가의 대리석에 경제성을 부여할 수 있으며, 모시원료의 종합적 활용을 실현하고 농업폐기물의 처리문제를 해결하여 농산품의 부가가치를 향상시킬 수 있게 된다.The modified staphylococcus aureus powder thus produced is compatible with the acrylic system, and is thus environmentally friendly when used in artificial marble. The widespread production of waxy raw materials and the utilization of the waxy waxy stems can provide economical efficiency to expensive marble. It is possible to realize comprehensive utilization and solve the problem of disposal of agricultural wastes, thereby improving the added value of agricultural products.
유리섬유강화석고(Glassfiber reinforced gypsum. GRG)는 100% 천연 무기 광물질로서 친환경성(Environmentally friendly)이고, 불연성(Non-Flammable) 이여서 연소되지 않으며, 표현이 용이한 성형성으로 무한대의 성형이 가능하고, 표면 질감이 고풍스런 사암 느낌을 준다.Glassfiber reinforced gypsum (GRG) is an environmentally friendly, non-flammable, non-combustible, 100% natural inorganic mineral that can be molded into infinite forms with ease of expression , The surface texture gives a sense of antique sandstone.
여기서, 유리섬유강화석고(GRG)는 석고와 유리섬유가 중량비로 10:1 내지 30:1의 비율로 배합된다. 여기에, 수화반응시 감수에 의한 크랙을 방지하기 위해 감수방지 유연제를 배합하고, 유리섬유의 변형방지와 양생시 경화를 유연하게 조절하여 성형성과 강도유지를 위한 촉진재와 무기질기포제거제(소포제)를 배합하여 밀도를 증강시키고 건조 후의 강도를 강화시킬 수 있다.Here, the glass fiber reinforced gypsum (GRG) is blended with the gypsum and the glass fiber in a weight ratio of 10: 1 to 30: 1. In order to prevent cracking due to sublimation during the hydration reaction, a water softening agent is blended, and a promoter and an inorganic foam removing agent (defoamer) for moldability and strength maintenance are flexibly adjusted to prevent deformation of glass fiber and curing during curing, To increase the density and to strengthen the strength after drying.
보다 상세하게 설명하면 유리섬유강화석고는 석고 70 내지 90중량%, 유리섬유 3 내지 10중량%, 촉진재 0.1 내지 6중량%, 유연제 0.1 내지 6중량%, 무기질기포제거제(소포제) 0.1 내지 10중량%를 포함한다. More specifically, the glass fiber reinforced gypsum contains 70 to 90% by weight of gypsum, 3 to 10% by weight of glass fibers, 0.1 to 6% by weight of accelerators, 0.1 to 6% by weight of a softener, 0.1 to 10% by weight of an inorganic defoamer %.
유리섬유강화시멘트(Glassfiber reinforced cement, GRC)는 시멘트 모르타르나 콘크리트에 유리섬유를 혼합하여 강도를 높인 복합재료이다. 유리섬유강화시멘트는 수축팽창률을 낮추고, 중량을 감소시키며, 조형성과 보강성을 증대시킨다. Glassfiber reinforced cement (GRC) is a composite material reinforced by mixing glass fiber with cement mortar or concrete. Glass fiber reinforced cement lowers shrinkage expansion, reduces weight, and increases formability and reinforcement.
여기서, 유리섬유강화시멘트는 시멘트와 유리섬유가 중량비로 10:1 내지 30:1의 비율로 배합된다. 보다 상세하게 설명하면 유리섬유강화시멘트는 시멘트 70 내지 90중량%, 유리섬유 3 내지 10 중량%, 촉진재 0.1 내지 6중량%, 유연제 0.1 내지 6중량%, 무기질기포제거제(소포제) 0.1 내지 10중량%를 포함한다. Here, the glass fiber reinforced cement is blended in a ratio of 10: 1 to 30: 1 by weight of cement and glass fiber. More specifically, the glass fiber reinforced cement contains 70 to 90% by weight of cement, 3 to 10% by weight of glass fiber, 0.1 to 6% by weight of accelerator, 0.1 to 6% by weight of a softener, 0.1 to 10% by weight of an inorganic defoamer %.
이에 더하여 인조대리석에는 다양한 색상과 기능을 갖는 마블칩(200)이 첨가된다.In addition, a
마블칩(200)은 베이스 수지 100 중량부에 대하여 무기 충전물 120 내지 200 중량부, 음이온 세라믹 1 내지 20중량부, 가교제 0.1 내지 10 중량부 및 중합 개시제 0.1 내지 10 중량부를 혼합하고 경화한 다음 이를 0.1~ 5mm의 크기로 파쇄하여 제조된다. The
그리고, 마블칩(200)의 혼합비는 인조대리석원료인 베이스 수지 100 중량부를 기준으로 0.1 내지 200 중량부가 사용되며, 바람직하게는 10 내지 80 중량부가 사용되는 것이 좋다.The mixing ratio of the marble chips 200 is 0.1 to 200 parts by weight, preferably 10 to 80 parts by weight, based on 100 parts by weight of the base resin used as artificial marble raw material.
여기서, 음이온 세라믹은 항균력 90%이상, 원적외선 방사율 90%이상, 음이온방출수 3,000(ion/cc) 이상의 것이 사용된다. Here, anionic ceramics have an antibacterial power of 90% or more, a far infrared ray emissivity of 90% or more, and an ion emission number of 3,000 (ion / cc) or more.
음이온 세라믹을 포함한 마블칩(200)은 다양한 패턴을 구현하여 외관의 형태를 다양하게 표현할 수 있고, 음이온 세라믹으로부터 음이온과 원적외선을 방출되며 향균력이 우수하여 인체의 건강을 증진시키고 실내환경을 개선시킨다.The Marble chip (200) including anionic ceramic can realize various patterns to express various forms of appearance, emits negative ions and far infrared rays from anion ceramics, and has excellent antimicrobial power, thereby improving the health of the human body and improving the indoor environment.
이하에서는 실시 예를 들어 본 발명을 상세하게 설명하지만, 본 발명의 권리범위가 이에 한정되는 것은 아니다.Hereinafter, the present invention will be described in detail with reference to examples, but the scope of the present invention is not limited thereto.
[실시예1] [Example 1]
베이스 수지 100 중량부에 무기 충전물 30 중량부, 가교제 0.8 중량부, 중합 개시제 0.8 중량부를 혼합한 인조대리석원료 100 중량부에 대하여 변성모시줄기가루 50 중량부, 유리섬유강화석고 5 중량부, 유리섬유강화시멘트 5 중량부를 혼합하여 잘 교반시킨 후 연속 성형틀에 부어 50 ∼150℃의 온도에서 경화시켜 인조대리석을 제조하였다.50 parts by weight of modified starch powder, 5 parts by weight of glass fiber reinforced gypsum, 5 parts by weight of a glass fiber reinforced gypsum, 100 parts by weight of an inorganic filler, And 5 parts by weight of reinforced cement were mixed and agitated well. The mixture was then poured into a continuous forming mold and cured at a temperature of 50 to 150 DEG C to prepare artificial marble.
[실시예2] [Example 2]
베이스 수지 100 중량부에 무기 충전물 30 중량부, 가교제 0.8 중량부, 중합 개시제 0.8 중량부를 혼합한 인조대리석원료 100 중량부에 대하여 변성모시줄기가루 40 중량부, 유리섬유강화석고 10 중량부, 유리섬유강화시멘트 10 중량부를 혼합하여 잘 교반시킨 후 연속 성형틀에 부어 50 ∼150℃의 온도에서 경화시켜 인조대리석을 제조하였다.40 parts by weight of modified starch powder, 10 parts by weight of glass fiber reinforced gypsum, 10 parts by weight of a glass fiber reinforced plaster, 100 parts by weight of a glass fiber reinforced plaster, And 10 parts by weight of reinforced cement were mixed and stirred well. The mixture was poured into a continuous forming mold and cured at a temperature of 50 to 150 DEG C to prepare artificial marble.
[실시예3] [Example 3]
베이스 수지 100 중량부에 무기 충전물 30 중량부, 가교제 0.8 중량부, 중합 개시제 0.8 중량부를 혼합한 인조대리석원료 100 중량부에 대하여 변성모시줄기가루 30 중량부, 유리섬유강화석고 20 중량부, 유리섬유강화시멘트 20 중량부를 혼합하여 잘 교반시킨 후 연속 성형틀에 부어 50 ∼150℃의 온도에서 경화시켜 인조대리석을 제조하였다.30 parts by weight of modified starch powder, 20 parts by weight of glass fiber reinforced gypsum, 20 parts by weight of glass fiber reinforced gypsum, 100 parts by weight of a glass fiber reinforced plaster, And 20 parts by weight of hardened cement were mixed and agitated well. Then, the mixture was poured into a continuous casting mold and cured at a temperature of 50 to 150 DEG C to prepare artificial marble.
[비교예1] [Comparative Example 1]
베이스 수지 100 중량부에 무기 충전물 30 중량부, 가교제 0.8 중량부, 중합 개시제 0.8 중량부를 혼합한 인조대리석원료 100 중량부에 대하여 변성모시줄기가루 70 중량부를 혼합하여 잘 교반시킨 후 연속 성형틀에 부어 50 ∼150℃의 온도에서 경화시켜 인조대리석을 제조하였다.70 parts by weight of modified starch powder was mixed with 100 parts by weight of an artificial marble raw material obtained by mixing 30 parts by weight of an inorganic filler, 0.8 parts by weight of a cross-linking agent and 0.8 parts by weight of a polymerization initiator with 100 parts by weight of a base resin, And cured at a temperature of 50 to 150 DEG C to produce artificial marble.
[비교예2] [Comparative Example 2]
베이스 수지 100 중량부에 무기 충전물 30 중량부, 가교제 0.8 중량부, 중합 개시제 0.8 중량부를 혼합한 인조대리석원료 100 중량부에 대하여 유리섬유강화석고 70 중량부를 혼합하여 잘 교반시킨 후 연속 성형틀에 부어 50 ∼150℃의 온도에서 경화시켜 인조대리석을 제조하였다.70 parts by weight of glass fiber reinforced gypsum was mixed with 100 parts by weight of an artificial marble raw material obtained by mixing 30 parts by weight of an inorganic filler, 0.8 parts by weight of a cross-linking agent and 0.8 parts by weight of a polymerization initiator with 100 parts by weight of a base resin, And cured at a temperature of 50 to 150 DEG C to produce artificial marble.
[비교예3] [Comparative Example 3]
베이스 수지 100 중량부에 무기 충전물 30 중량부, 가교제 0.8 중량부, 중합 개시제 0.8 중량부를 혼합한 인조대리석원료 100 중량부에 대하여 유리섬유강화시멘트 70 중량부를 혼합하여 잘 교반시킨 후 연속 성형틀에 부어 50 ∼150℃의 온도에서 경화시켜 인조대리석을 제조하였다.70 parts by weight of a glass fiber reinforced cement was mixed with 100 parts by weight of an artificial marble raw material obtained by mixing 30 parts by weight of an inorganic filler, 0.8 parts by weight of a crosslinking agent and 0.8 parts by weight of a polymerization initiator, and the mixture was stirred well. And cured at a temperature of 50 to 150 DEG C to produce artificial marble.
[비교예4] [Comparative Example 4]
베이스 수지 100 중량부에 무기 충전물 100 중량부, 가교제 0.8 중량부, 중합 개시제 0.8 중량부를 혼합하여 잘 교반시킨 후 연속 성형틀에 부어 50 ∼150℃의 온도에서 경화시켜 인조대리석을 제조하였다.100 parts by weight of an inorganic filler, 0.8 parts by weight of a cross-linking agent and 0.8 part by weight of a polymerization initiator were mixed with 100 parts by weight of a base resin, stirred well and poured into a continuous mold to cure the mixture at a temperature of 50 to 150 DEG C to prepare artificial marble.
<시험예><Test Example>
이와 같이 제조한 인조대리석을 가로×세로×높이(또는 두께라고도 한다)를 100mm×100mm×8.0mm로 절단한 시험편을 한국건자재 시험연구원(국가공인시험연구기관)에 의뢰하여 인장강도, 휨강도, 치수안정성, 경도, 내마모성 시험을 각각 행하였으며, 그 결과는 [표 1]과 같다.The test pieces cut into 100 mm × 100 mm × 8.0 mm in width × height × height (or thickness) of the artificial marble thus manufactured were submitted to the Korea Institute of Construction Materials (National Institute of Certified Research and Development) for tensile strength, bending strength, Stability, hardness, and abrasion resistance were measured. The results are shown in [Table 1].
(%)Dimensional stability
(%)
ASTM D4060Abrasion resistance (mg)
ASTM D4060
[표 1]에서 알 수 있듯이 실시예1, 2, 3은 비교예1, 2, 3,4에 비하여 인장강도, 휨강도, 치수안정성이 우수할 뿐만 아니라 모스경도, 내마모성이 매우 우수한 것으로 나타났으며, 실시예1과 실시예2와 실시예3 중에서도 실시예3의 경우 인장강도, 모스경도, 내마모성이 우수한 것으로 나타났다. 특히, 실시예3의 경우 종래의 인조대리석인 비교예4에 비하여 내마모성, 모스경도, 치수안정성, 인장강도, 휨강도가 월등히 우수한 것으로 나타났다. As can be seen from Table 1, Examples 1, 2 and 3 exhibited excellent tensile strength, flexural strength and dimensional stability as well as excellent mos hardness and abrasion resistance in comparison with Comparative Examples 1, 2 and 3, Among Examples 1, 2 and 3, Example 3 showed excellent tensile strength, Mohs hardness and abrasion resistance. Particularly, in the case of Example 3, abrasion resistance, Mohs hardness, dimensional stability, tensile strength and flexural strength were superior to those of Comparative Example 4 which is a conventional artificial marble.
도 2는 본 발명의 다른 실시 예에 따른 인조대리석의 측면도를 나타낸 이미지 사진이다.2 is a photograph of a side view of an artificial marble according to another embodiment of the present invention.
도 3에 도시한 바와 같이 본 발명의 다른 실시 예에 따른 인조대리석(100)은 유리섬유강화석고층(110), 변성모시줄기층(120), 유리섬유강화시멘트층(130)이 순서와 상관없이 다단으로 적층되어 일체로 이루어진 것이다. As shown in FIG. 3, the
여기서, 유리섬유강화석고층(110)은 베이스 수지 100 중량부에 대하여, 유리섬유강화석고 5 내지 150 중량부, 무기 충전물 5 내지 80 중량부, 가교제 0.1 내지 10 중량부, 중합 개시제 0.1 내지 10 중량부를 포함하여 형성된다. 5 to 150 parts by weight of glass fiber reinforced gypsum, 5 to 80 parts by weight of an inorganic filler, 0.1 to 10 parts by weight of a crosslinking agent, and 0.1 to 10 parts by weight of a polymerization initiator, based on 100 parts by weight of the base resin, .
그리고, 변성모시줄기층(120)은 베이스 수지 100 중량부에 대하여, 변성 모시줄기가루 5 내지 150 중량부, 무기 충전물 5 내지 80 중량부, 가교제 0.1 내지 10 중량부, 중합 개시제 0.1 내지 10 중량부를 포함하여 형성된다. The modified
그리고, 유리섬유강화시멘트층(130)은 베이스 수지 100 중량부에 대하여, 유리섬유강화시멘트 5 내지 150 중량부, 무기 충전물 5 내지 80 중량부, 가교제 0.1 내지 10 중량부, 중합 개시제 0.1 내지 10 중량부를 포함하여 형성된다. The glass fiber reinforced
이에 더하여, 유리섬유강화석고층(110), 변성모시줄기층(120), 유리섬유강화시멘트층(130)이 선택되는 순서에 따라 다단 적층되어 일체로 이루어질 때 맨 상부에 위치하는 층에는 표면의 다양한 무늬를 구현하기 위하여 마블칩(200)이 더 포함될 수 있다. In addition, when the glass fiber-reinforced stone high-
여기서, 유리섬유강화석고, 변성모시줄기가루, 유리섬유강화시멘트, 마불칩은 일 실시 예와 동일한 설명으로 이루어진다. Here, the glass fiber-reinforced gypsum, modified starch powder, glass fiber reinforced cement, and marble chips are made the same as those in the embodiment.
이와 같이 본 발명은 식물섬유인 변성모시줄기가루가 아크릴계의 호환성 문제를 해결함으로써 자연친화적이고 가격경쟁력이 우수한 인조대리석을 제공하게 되고, 유리섬유강화석고와, 유리섬유강화시멘트를 혼합하여 기계적 강도 및 내오염성, 내스크래치성을 강화하고 표면 질감 및 채색성을 향상시키며 화재에 강한 인조대리석을 제공하게 되며, 또한, 음이온 세라믹을 포함한 마블칩을 혼합하여 외관의 형태를 다양하게 표현할 수 있고, 음이온과 원적외선을 방출하여 실내환경을 개선시킬 수 있는 인조대리석을 제공하게 된다. 또한, 가볍고 시공성이 우수한 인조대리석을 제공하게 된다. As described above, the present invention provides artificial marble which is natural-friendly and excellent in price competitiveness by solving the compatibility problem of acrylic based on vegetable fiber, modified starch stalactite powder, and is made by mixing glass fiber reinforced gypsum and glass fiber reinforced cement, It is possible to improve the surface resistance and scratch resistance, to improve the surface texture and colorability, to provide fire-resistant artificial marble, and to mix marble chips containing anion ceramics to express various forms of appearance, It is possible to provide artificial marble which can radiate far-infrared rays to improve the indoor environment. In addition, artificial marble is provided which is light and excellent in workability.
이상에서 본 발명의 바람직한 실시 예에 대하여 설명하였으나, 본 발명은 상술한 특정의 실시 예에 한정되지 아니한다. 즉, 본 발명이 속하는 기술분야에서 통상의 지식을 가지는 자라면 첨부된 특허청구범위의 사상 및 범주를 일탈함이 없이 본 발명에 대한 다수의 변경 및 수정이 가능하며, 그러한 모든 적절한 변경 및 수정은 균등물들도 본 발명의 범위에 속하는 것으로 간주 되어야 할 것이다.Although the preferred embodiments of the present invention have been described, the present invention is not limited to the specific embodiments described above. It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the appended claims, And equivalents should also be considered to be within the scope of the present invention.
100: 인조대리석 110: 유리섬유강화석고층
120: 변성모시줄기가루층 130: 유리섬유강화시멘트층
200: 마불칩100: artificial marble 110: glass fiber reinforced stone high-rise
120: Modified Stalks Stripper Layer 130: Glass Fiber Reinforced Cement Layer
200: Wanted chips
Claims (11)
상기 변성모시줄기가루는 90 내지 110℃의 온도에서 모시줄기가루 100 중량부에 대하여 표면변성제 1 내지 2 중량부를 분사하여 제조되는 것을 특징으로 하는 인조대리석.The method according to claim 1,
Wherein the modified waxy stem powder is prepared by spraying 1 to 2 parts by weight of a surface modifier with respect to 100 parts by weight of foxtail flour at a temperature of 90 to 110 캜.
상기 인조대리석원료는 베이스 수지 100 중량부에 대하여 무기 충전물 10 내지 50 중량부, 가교제 0.1 내지 20 중량부, 중합 개시제 0.1 내지 20 중량부를 포함하는 것을 특징으로 하는 인조대리석.The method according to claim 1,
Wherein the artificial marble raw material comprises 10 to 50 parts by weight of an inorganic filler, 0.1 to 20 parts by weight of a crosslinking agent, and 0.1 to 20 parts by weight of a polymerization initiator based on 100 parts by weight of the base resin.
상기 유리섬유강화시멘트는 시멘트와 유리섬유가 중량비로 10:1 내지 30:1의 비율로 배합된 것을 특징으로 하는 인조대리석.The method according to claim 1,
Wherein the glass fiber reinforced cement is blended with cement and glass fiber in a weight ratio of 10: 1 to 30: 1.
상기 유리섬유강화석고는 석고와 유리섬유가 중량비로 10:1 내지 30:1의 비율로 배합된 것을 특징으로 하는 인조대리석.The method according to claim 1,
Wherein the glass fiber reinforced gypsum is a mixture of gypsum and glass fiber in a weight ratio of 10: 1 to 30: 1.
상기 베이스 수지는 아크릴계 수지, 에폭시계 수지, 멜라민계 수지 및 불포화 폴리에스테르계 수지로 이루어진 군으로부터 하나 이상의 것이 선택되고,
상기 무기 충전물은 탄산칼슘, 수산화 알루미늄, 실리카, 알루미나, 유산바륨 및 수산화 마그네슘으로 이루어진 군으로부터 하나 이상의 것이 선택되며,
상기 가교제는 에틸렌 글리콜 디 메타 아크릴레이트, 프로필렌 글리콜 디 메타 아크릴레이트, 글리세롤 트리 메타 아크릴레이트, 트리메틸 프로판 트리 메타 아크릴레이트 및 비스페놀 A 디 메타 아크릴레이트로 이루어진 군으로부터 하나 이상의 것이 선택되는 것을 특징으로 하는 인조대리석.The method according to claim 1,
Wherein the base resin is at least one selected from the group consisting of an acrylic resin, an epoxy resin, a melamine resin and an unsaturated polyester resin,
The inorganic filler is at least one selected from the group consisting of calcium carbonate, aluminum hydroxide, silica, alumina, barium sulfate and magnesium hydroxide,
Wherein the crosslinking agent is at least one selected from the group consisting of ethylene glycol dimethacrylate, propylene glycol dimethacrylate, glycerol trimethacrylate, trimethylpropane trimethacrylate and bisphenol A dimethacrylate. marble.
상기 인조대리석에는 베이스 수지 100 중량부에 대하여 마블칩 0.1 내지 200 중량부가 더 포함되는 것을 특징으로 하는 인조대리석.The method according to claim 1,
Wherein the artificial marble further comprises 0.1 to 200 parts by weight of marble chips per 100 parts by weight of the base resin.
상기 마블칩은 베이스 수지 100 중량부에 대하여, 무기 충전물 100 내지 200 중량부, 음이온세라믹 1 내지 20 중량부, 가교제 0.1 내지 10 중량부 및 개시제 0.1 내지 10 중량부를 혼합하고 경화한 다음, 이를 0.1mm 내지 5mm 크기로 파쇄한 것을 특징으로 하는 인조대리석.8. The method of claim 7,
The Marble chip is prepared by mixing and curing 100 to 200 parts by weight of an inorganic filler, 1 to 20 parts by weight of an anionic ceramic, 0.1 to 10 parts by weight of a crosslinking agent and 0.1 to 10 parts by weight of an initiator with respect to 100 parts by weight of a base resin, To 5 mm in size.
상기 음이온 세라믹은 항균력 90%이상, 원적외선 방사율 90%이상, 음이온방출수 3,000(ion/cc) 이상의 것이 사용되는 것을 특징으로 하는 인조대리석.9. The method of claim 8,
The anionic ceramic is characterized in that an antimicrobial activity of 90% or more, a far infrared ray emissivity of 90% or more, and an ion emission number of 3,000 (ion / cc) or more is used.
베이스 수지 100 중량부에 대하여, 변성 모시줄기가루 5 내지 150 중량부, 무기 충전물 5 내지 80 중량부, 가교제 0.1 내지 10 중량부, 중합 개시제 0.1 내지 10 중량부를 포함하는 변성모시줄기층;
베이스 수지 100 중량부에 대하여, 유리섬유강화시멘트 5 내지 150 중량부, 무기 충전물 5 내지 80 중량부, 가교제 0.1 내지 10 중량부, 중합 개시제 0.1 내지 10 중량부를 포함하는 유리섬유강화시멘트층;을 포함하며,
상기 유리섬유강화석고층, 변성모시줄기층, 유리섬유강화시멘트층은 순서와 상관없이 다단으로 적층되어 일체로 이루어진 것을 포함하는 인조대리석.5 to 150 parts by weight of a glass fiber reinforced gypsum, 5 to 80 parts by weight of an inorganic filler, 0.1 to 10 parts by weight of a crosslinking agent, and 0.1 to 10 parts by weight of a polymerization initiator, based on 100 parts by weight of a base resin.
A modified waxy stem layer comprising 5 to 150 parts by weight of modified stem roots powder, 5 to 80 parts by weight of an inorganic filler, 0.1 to 10 parts by weight of a crosslinking agent, and 0.1 to 10 parts by weight of a polymerization initiator, based on 100 parts by weight of the base resin.
A glass fiber reinforced cement layer comprising 5 to 150 parts by weight of a glass fiber reinforced cement, 5 to 80 parts by weight of an inorganic filler, 0.1 to 10 parts by weight of a crosslinking agent and 0.1 to 10 parts by weight of a polymerization initiator, based on 100 parts by weight of the base resin In addition,
Wherein the glass fiber reinforced stone high layer, the modified ramshackle layer, and the glass fiber reinforced cement layer are laminated in multi-stages in any order and integrally formed.
상기 유리섬유강화석고층, 변성모시줄기층, 유리섬유강화시멘트층 중 선택되는 어느 하나 이상의 층에는 마블칩이 더 포함되고,
상기 마블칩은 베이스 수지 100 중량부에 대하여, 무기 충전물 100 내지 200 중량부, 음이온세라믹 1 내지 20 중량부, 가교제 0.1 내지 10 중량부 및 개시제 0.1 내지 10 중량부를 혼합하고 경화한 다음, 이를 0.1mm 내지 5mm 크기로 파쇄한 것을 특징으로 하는 인조대리석.11. The method of claim 10,
The at least one layer selected from the glass fiber reinforced stone high layer, the modified ramified stem layer, and the glass fiber reinforced cement layer further includes a marble chip,
The Marble chip is prepared by mixing and curing 100 to 200 parts by weight of an inorganic filler, 1 to 20 parts by weight of an anionic ceramic, 0.1 to 10 parts by weight of a crosslinking agent and 0.1 to 10 parts by weight of an initiator with respect to 100 parts by weight of a base resin, To 5 mm in size.