KR20050051534A - Method for forming of prevention of sticking - Google Patents
Method for forming of prevention of sticking Download PDFInfo
- Publication number
- KR20050051534A KR20050051534A KR1020040044846A KR20040044846A KR20050051534A KR 20050051534 A KR20050051534 A KR 20050051534A KR 1020040044846 A KR1020040044846 A KR 1020040044846A KR 20040044846 A KR20040044846 A KR 20040044846A KR 20050051534 A KR20050051534 A KR 20050051534A
- Authority
- KR
- South Korea
- Prior art keywords
- resin binder
- adhesion
- glass
- parts
- resin
- Prior art date
Abstract
본 발명은 부착방지체 형성방법에 관한 것으로, 특히 피착면에 수지바인더를 도포하고 도포된 수지바인더가 경화되기 이전에 수지바인더 상부에 유리 비드를 분사하고 경화시켜 유리 비드 돌기를 형성시키는 것을 특징으로 하는 부착방지체 형성방법에 관한 것이다.The present invention relates to a method for forming an adhesion preventing agent, in particular, by applying a resin binder on the surface to be deposited, and before the applied resin binder is cured, the glass beads are sprayed on the resin binder and cured to form a glass bead protrusion. It relates to a method for forming an anti-adhesion.
본 발명에 따라 형성된 부착방지체는 전신주, 신호등, 가로등, 교통안내표지판, 콘트롤박스 등의 노상시설물의 지주나 건축물, 구조물의 벽체와 같은 피착면에 스티커, 포스터 등 접착물의 부착을 막을 수 있고, 일단 부착되었다 하더라도 접착물을 쉽게 제거할 수 있을 뿐만 아니라, 시공이 용이하고 코팅된 피착면의 내후성, 내오염성, 내스크래치성, 내화학성, 내충격성 등의 물성을 향상시킬 수 있다.Anti-adhesion formed according to the present invention can prevent the adhesion of stickers, posters, etc. to the adhered surface, such as pillars of buildings, buildings, structures, such as telephone poles, traffic lights, street lights, traffic signs, control boxes, etc., Once attached, not only the adhesive can be easily removed, but also easy to install and improve the physical properties such as weather resistance, stain resistance, scratch resistance, chemical resistance, impact resistance of the coated surface.
Description
본 발명은 부착방지체 형성방법에 관한 것으로, 더욱 상세하게는 전신주, 신호등, 가로등, 교통안내표지판, 콘트롤박스 등의 노상시설물의 지주나 건축물, 구조물의 벽체와 같은 피착면에 스티커, 포스터 등 접착물의 부착을 막을 수 있고, 일단 부착되었다 하더라도 접착물을 쉽게 제거할 수 있을 뿐만 아니라, 시공이 용이하고 코팅된 피착면의 내후성, 내오염성, 내스크래치성, 내화학성, 내충격성 등의 물성을 향상시킬 수 있는 부착방지체 형성방법에 관한 것이다.The present invention relates to a method for forming an anti-adhesive, and more particularly, to adhere a sticker, a poster, or the like to a surface to be attached such as a pillar of a roadside facility such as a telephone pole, a traffic light, a street lamp, a traffic guide sign, a control box or a wall of a building or a structure. It can prevent the adhesion of water, and it is easy to remove the adhesive even once it is attached, and it is easy to construct and improves the physical properties such as weather resistance, pollution resistance, scratch resistance, chemical resistance, impact resistance, etc. of the coated surface. It relates to a method for forming an anti-sticking body that can be made.
일반적으로 노상에는 전신주, 가로등, 신호등, 교통안내표지판 등 많은 수의 각종 노상시설물이 설치되어 있고, 이러한 시설물은 파이프나 콘크리트 지주를 구성하고 있으며, 상기 시설물의 지주는 통행자의 안전사고를 고려하여 평평한 면으로 구성하고 있음이 일반화되어 있다.In general, a large number of roadside facilities such as telephone poles, street lights, traffic lights, traffic signboards, etc. are installed on the roads, and these facilities constitute pipes or concrete props, and the props of the facilities are flat in consideration of safety accidents of passengers. It is generalized to consist of cotton.
상기 노상시설물의 지주나 건축물 또는 구조물의 벽체에는 각종 스티커와 포스터 같은 불법광고물이 접착제, 풀 등으로 접착되어 지주나 건축물 또는 구조물의 외관을 손상시키고, 상기와 같이 접착되는 광고물이나 접착물로 인하여 거리미관이 손상되는 현상이 끊임없이 발생하며, 이에 따라 광고물이나 접착물의 제거에 막대한 예산과 인력이 투입되고 있는 실정이다.Illegal advertisements, such as stickers and posters, are glued to the pillars of buildings or structures or structures of the roadbed facilities with adhesive or glue to damage the appearance of the pillars or buildings or structures, and the advertisements or adhesives bonded as described above. Due to the phenomenon that the street beauty is damaged constantly, a huge budget and manpower is put into the removal of advertisements and adhesives.
그러나 노상시설물의 지주는 그 표면이 평평한 면이나 원주면으로 형성되어 있고, 건축물 또는 구조물의 벽체는 평면이기 때문에 스티커나 포스터와 같은 지류로 되어 있는 광고물이나 접착물의 부착이 용이하며, 따라서 이를 감시하고 방지하기가 매우 어려울 뿐만 아니라, 일단 접착이 된 후에는 스티커나 포스터와 같은 광고물이나 접착물이 평면상으로 견고하게 접착하여 있어 깨끗하게 제거되지 않아 거리미관과 시설물의 오염 및 훼손이 심각한 문제로 대두되고 있는 실정이다.However, the pillars of the roadbed are formed with flat or circumferential surfaces, and the walls of buildings or structures are flat, so it is easy to attach advertisements or adhesives made of tributaries such as stickers and posters. In addition, it is very difficult to prevent and prevent, and once adhered, advertisements and adhesives such as stickers and posters are firmly adhered to the plane and are not removed cleanly. Therefore, contamination and damage of street beauty and facilities are a serious problem. It is emerging.
이에 따라 광고물이나 접착물의 부착방지를 위해 다양한 방법이 시도되고 있으나, 광고물이나 접착물을 금지한다는 단순 경고용 문구 이외에 효과적인 방지 수단이 제시되지 못하고 있는 실정이다.Accordingly, various methods have been attempted to prevent the attachment of advertisements or adhesives, but there is no effective prevention means other than a simple warning phrase that prohibits advertisements or adhesives.
상기와 같은 종래기술의 문제점을 해결하고자, 본 발명은 전신주, 신호등, 가로등, 교통안내표지판, 콘트롤박스 등의 노상시설물의 지주나 건축물, 구조물의 벽체와 같은 피착면에 스티커, 포스터 등 접착물의 부착을 막을 수 있을 뿐만 아니라, 일단 부착되었다 하더라도 접착물을 쉽게 제거할 수 있는 부착방지체 형성방법 및 상기 방법으로 형성된 부착방지체를 제공하는 것을 목적으로 한다. In order to solve the problems of the prior art as described above, the present invention is attached to the adherends such as stickers, posters on the adhered surface, such as pillars of buildings, buildings, structures, such as telephone poles, traffic lights, street lights, traffic signs, control boxes, etc. It is an object of the present invention to provide a method for forming an antiadhesive which can easily prevent the adhesive, even once attached, and an antiadhesion formed by the above method.
본 발명의 다른 목적은 시공이 용이하고 코팅된 피착면의 내후성, 내오염성, 내스크래치성, 내화학성, 내충격성 등의 물성을 향상시킬 수 있는 부착방지체 형성방법 및 상기 방법으로 형성된 부착방지체를 제공하는 것이다.Another object of the present invention is a method for forming an antiadhesive which can be easily constructed and can improve physical properties such as weather resistance, fouling resistance, scratch resistance, chemical resistance, impact resistance, etc., and an antiadhesive formed by the above method. To provide.
상기 목적을 달성하기 위하여, 본 발명은 피착면에 수지바인더를 도포하고 도포된 수지바인더가 경화되기 이전에 수지바인더 상부에 유리 비드를 분사하고 경화시켜 유리 비드 돌기를 형성시키는 것을 특징으로 하는 부착방지체 형성방법을 제공한다.In order to achieve the above object, the present invention is coated with a resin binder on the surface to be deposited and before the applied resin binder is cured by spraying and curing the glass beads on top of the resin binder to form a glass bead projections, characterized in that It provides a method of forming a sieve.
또한 본 발명은 상기 방법에 따라 형성된 부착방지체를 제공한다.The present invention also provides an anti-stick body formed according to the above method.
이하 본 발명을 상세하게 설명한다. Hereinafter, the present invention will be described in detail.
본 발명의 부착방지체는 피착면에 수지바인더를 도포하고 도포된 수지바인더가 경화되기 이전에 수지바인더 상부에 유리 비드를 분사하고 경화시켜 수지바인더 상부에 유리 비드 돌기가 형성된 것을 특징으로 한다.The adhesion preventing member of the present invention is characterized in that the glass bead projections are formed on the resin binder by spraying and curing the glass beads on the resin binder before the resin binder is coated on the surface to be coated and the resin binder is cured.
본 발명에 사용되는 수지바인더는 부착방지체 성분 중 바인더로 작용하는 성분으로 주로 통상 외장용에 사용되는 수지를 사용할 수 있으며, 특히 아크릴계 수지, 세라믹계 수지, 또는 우레탄계 수지를 사용하는 것이 좋다.The resin binder used in the present invention is a component that acts as a binder among the adhesion preventer components, and may be mainly used for a resin, and is preferably an acrylic resin, a ceramic resin, or a urethane resin.
상기 아크릴계 수지(arcryl based resin)는 메타크릴산 또는 아크릴산 유도체를 주성분으로 하는 용제형의 아크릴 우레탄, 수성 아크릴하이드로졸, 에멀젼 무용제형 아크릴 실란, 또는 자외선 경화형 아크릴 등을 사용할 수 있다.The acrylic resin may be a solvent-type acrylic urethane, an aqueous acrylic hydrosol, an emulsion-free solvent-based acrylic silane, or an ultraviolet curable acryl based on methacrylic acid or an acrylic acid derivative.
상기 우레탄계 수지는 당업계에서 사용하는 통상의 우레탄계 수지를 사용할 수 있음은 물론이며, 일예로 히드록실 부분 및 아미노 부분에서 발견된 활성 수소 원자를 함유하는 유기 화합물 및 유기 폴리이소시아네이트로부터 제조한 일반적으로 공지된 열경화성 수지가 있다.The urethane-based resin may be used as a general urethane-based resin used in the art, of course, generally known from organic compounds and organic polyisocyanates containing active hydrogen atoms found in the hydroxyl and amino portions, for example. Thermosetting resin.
상기 세라믹계 수지는 규산에스테르, 이의 가수분해 생성물, 수분산형 실리카졸, 또는 알콜분산형 실리카졸 등을 사용할 수 있다.The ceramic resin may be a silicate ester, a hydrolysis product thereof, a water dispersion silica sol, an alcohol dispersion silica sol, or the like.
상기와 같은 수지바인더는 그 함량이 너무 낮거나 높을 경우에는 유리 비드와의 결착성과 노상시설물의 지주, 건축물이나 구조물의 벽체와 같은 피착면에 도포시 도포효율을 저하시킬 수 있을 뿐만 아니라, 강도, 물성, 기능성 등 전반적인 기능이 좋지 않게 된다는 문제점이 있다.If the resin binder is too low or too high, it may not only reduce the binding efficiency with glass beads, but also reduce the coating efficiency when applied to the surface to be adhered to, such as the pillars of roadbed facilities and the walls of buildings and structures. There is a problem that the overall function, such as physical properties, functionality is not good.
상기와 같은 수지바인더는 노상시설물의 지주, 건축물이나 구조물의 벽체와 같은 피착면에 도포하고, 상기 수지바인더가 경화되기 이전에 수지바인더의 상부에 유리 비드를 분사하고 경화시켜 부착한다.Such a resin binder is applied to the surface of the substructure of the installation, such as the wall of the building or structure, and before the resin binder is cured by spraying and curing the glass beads on top of the resin binder.
본 발명에서 사용되는 상기 유리 비드(glass bead)는 구형의 형태로 구형의 유리 비드들이 수지바인더의 상부에 유리 비드 돌기를 형성하여 피착면과 접착물간의 접촉면을 감소시키는 작용을 한다. 뿐만 아니라, 수지바인더 상부에 형성된 유리 비드 돌기들 간의 요철에 공기 또는 물이 들어올 경우 공기 또는 물이 유리 비드 상부로 퍼지면서 공기막 또는 수막이 형성되어 물체의 표면장력을 저하시키고, 이에 따라 접착물의 점착이나 부착을 방지하는 작용을 한다. The glass bead (glass bead) used in the present invention has a function of reducing the contact surface between the adhered surface and the adhesive by forming a glass bead protrusion on the top of the resin binder in the form of spherical glass beads. In addition, when air or water enters the unevenness between the glass bead protrusions formed on the resin binder, air or water is spread over the glass bead to form an air film or water film, thereby lowering the surface tension of the object. Or to prevent attachment.
상기 유리 비드는 수지바인더 상부에 분사 및 경화된 후, 수지바인더에 의하여 고정되는 동시에 수지바인더 상부로부터 돌출되어 돌기를 형성할 수 있을 정도의 형상과 입자 크기의 것을 사용할 수 있음은 물론이며, 유리, 파유리, 유리 섬유, 또는 유리 커렛 등을 분쇄하여 얻는 유리 분말을 처리하여 얻어지는 것으로, 유리 조성은 A, C, E, 내알칼리성 유리 분말 조성 등 수지바인더와 상용성이 있는 것이라면 특별히 한정되지 않는다.After the glass beads are sprayed and cured on the resin binder, the glass beads may be fixed by the resin binder and protrude from the resin binder to form protrusions. It is obtained by processing the glass powder obtained by grind | pulverizing a cullet, glass fiber, or a glass curette, etc., A glass composition will not be specifically limited if it is compatible with resin binders, such as A, C, E, and alkali-resistant glass powder composition.
상기 유리 비드는 구형, 타원형, 또는 이에 준하는 모든 형상의 유리 비드가 사용될 수 있으며, 다양한 크기가 분포된 것부터 일정한 크기만을 선별한 것까지 모두 사용할 수 있다.The glass beads may be spherical, elliptical, or glass beads of any shape equivalent thereto, and may be used, from those in which various sizes are distributed to those of only a predetermined size.
상기 유리 비드의 입경은 본 발명의 부착방지체가 형성되는 노상시설물의 지주, 건축물이나 구조물의 벽체와 같은 피착면의 재질, 용도 등에 따라서 적절히 선정하여 사용할 수 있으며, 바람직하게는 0.2 ㎛ 내지 3 ㎜인 것이 바람직하며, 더욱 바람직하게는 0.3 내지 1.5 ㎜인 것이 좋다. 또한 이들은 수 ㎛의 작은 입도와 수 ㎜의 큰 입도의 비드들의 조합에 의하여 다양한 형태 및 물성을 나타내게 할 수 있다. 그러나, 상기 유리 비드의 입경이 3 ㎜를 초과할 경우에는 피착면과 접착물의 접촉면이 증가되며, 분산성이 낮아질 수 있다는 문제점이 있다.The particle diameter of the glass beads may be appropriately selected and used according to the material, the use, and the like of the posts of the road-floor facility in which the anti-sticking body of the present invention is formed, the wall of a building or a structure, and is preferably 0.2 μm to 3 mm. It is preferable that it is preferable, More preferably, it is 0.3-1.5 mm. They can also exhibit a variety of shapes and properties by the combination of beads having a small particle size of several μm and a large particle size of several mm. However, when the particle diameter of the glass beads exceeds 3 mm, there is a problem that the contact surface and the contact surface of the adhesive is increased, the dispersibility may be lowered.
상기와 같은 유리 비드는 요구되는 부착방지성, 피착면에 따라 적절한 양을 조절하여 사용할 수 있으며, 특히 수지바인더 고형분 100 중량부에 대하여 50 내지 150 중량부로 포함되는 것이 바람직하며, 더욱 바람직하게는 70 내지 90 중량부로 포함되는 것이다. 그 함량이 50 중량부 미만일 경우에는 그 양이 너무 미미하여 접착물의 부착방지효과가 미미하다는 문제점이 있으며, 150 중량부를 초과할 경우에는 수지바인더에 비하여 상대적으로 그 함량이 많아 부착방지체가 경화된 후에 유리 비드가 탈락될 수 있다는 문제점이 있다.Glass beads as described above can be used by adjusting the appropriate amount according to the anti-adhesion, adhered surface required, and particularly preferably contained in 50 to 150 parts by weight based on 100 parts by weight of the resin binder solids, more preferably 70 To 90 parts by weight. If the content is less than 50 parts by weight, the amount is so small that the adhesion preventing effect of the adhesive is insignificant. If it exceeds 150 parts by weight, the content is relatively higher than that of the resin binder, the glass after the adhesion preventer is cured There is a problem that beads can be dropped.
상기와 같이 수지바인더가 경화되기 전 수지바인더 상부에 분사된 유리 비드는 경화되고, 도 1에 나타낸 바와 같이 피착면(1)에 도포된 수지바인더(2)에 의해 고정되어 수지바인더(2) 상부로부터 돌출된 유리 비드 돌기(3)를 형성한다.As described above, the glass beads injected onto the resin binder before curing the resin binder are cured and fixed by the resin binder 2 applied to the adhered surface 1 as shown in FIG. The glass bead projections 3 protruding from are formed.
또한 본 발명의 부착방지체 형성시 상기 수지바인더에 유리 분말(glass power)을 추가로 혼합하여 피착면에 도포할 수 있다. In addition, when forming the anti-sticking body of the present invention, the glass binder (glass power) may be further mixed with the resin binder and applied to the adhered surface.
상기 유리 분말은 열팽창계수가 수지바인더와 비슷하여 열수축, 팽창에 의한 틈이 생기지 않으며, 이로써 유리 비드와 수지바인더 간의 결합력을 향상시켜 유리 비드가 탈락되거나 이탈되지 않도록 하여 노상시설물의 지주, 건축물이나 구조물의 벽체와 같은 피착면의 표면에 포스터, 스티커 등의 광고물이나 접착물의 부착을 더욱 효과적으로 방지할 수 있다. 또한, 상기 유리 분말은 계면분리를 억제하고 외부에서 작용되는 충격을 흡수하고 전달하여 손상이 현저히 저하되는 부착방지체 조직을 형성한다.The glass powder has a thermal expansion coefficient similar to that of a resin binder, and thus does not cause gaps due to thermal contraction and expansion, thereby improving bonding strength between the glass beads and the resin binder so that the glass beads do not fall off or leave the substructure of the substructure. It is possible to more effectively prevent the attachment of advertisements and adhesives, such as posters, stickers, on the surface of the adherend such as the wall. In addition, the glass powder inhibits interfacial separation and absorbs and transmits an impact applied from the outside to form an anti-stick structure in which damage is significantly reduced.
상기 유리 분말은 다양한 입자 형상과 입자 크기의 것을 사용할 수 있으며, 유리 분말의 입자는 유리, 파유리, 유리 섬유, 또는 유리 커렛 등을 분쇄하여 얻는 것으로, 유리 조성은 A, C, E, 내알칼리성 유리 분말 조성 등 수지바인더와의 상용성이 있는 것이라면 특별히 한정되지 않으며, 특히 E-글래스 조성의 유리 분말이 각종 소재에 대한 부착성 면에서 더욱 바람직하다. The glass powder may be used in a variety of particle shapes and particle sizes, the particles of the glass powder is obtained by pulverizing glass, cullet, glass fiber, or glass curette, glass composition is A, C, E, alkali resistance It will not specifically limit, if it is compatible with resin binders, such as a glass powder composition, Especially, glass powder of an E-glass composition is more preferable at the adhesiveness with respect to various raw materials.
상기 유리 분말의 입경은 특별히 한정되는 것은 아니나, 특히 10 ㎛ 내지 1 ㎜인 것이 바람직하며, 더욱 바람직하게는 5 ㎛ 내지 1 ㎜인 것이 좋다. 상기 유리 분말의 입경이 너무 작을 경우에는 유리 비드와 수지바인더 간의 결합력 향상효과가 미미하다는 문제점이 있으며, 너무 큰 경우에는 수지바인더와 균일하게 혼합될 수 없으며, 부착방지체의 강도가 저하되거나 수축 및 팽창성이 증가할 수 있다는 문제점이 있다.Although the particle diameter of the said glass powder is not specifically limited, It is preferable that it is 10 micrometers-1 mm especially, More preferably, it is 5 micrometers-1 mm. If the particle diameter of the glass powder is too small, there is a problem that the effect of improving the bonding strength between the glass bead and the resin binder is insignificant. If the glass powder is too large, the glass powder cannot be uniformly mixed with the resin binder, and the strength of the adhesion preventing agent is reduced or shrinkage and There is a problem that the expandability can be increased.
상기 유리 분말은 상기 수지바인더 고형분 100 중량부에 대하여 20 내지 50 중량부로 포함되는 것이 바람직하다. 그 함량이 20 중량부 미만일 경우에는 유리 비드와 수지바인더 사이의 결합력 부여효과가 부족하다는 문제점이 있으며, 50 중량부를 초과할 경우에는 상대적으로 수지바인더의 함량이 감소되어 피착면에 대한 본 발명의 부착방지체의 접착성이 저하될 수 있다는 문제점이 있다.The glass powder is preferably contained in 20 to 50 parts by weight based on 100 parts by weight of the resin binder solid content. If the content is less than 20 parts by weight, there is a problem in that the effect of imparting a bonding force between the glass beads and the resin binder is insufficient, and if the content is more than 50 parts by weight, the content of the resin binder is relatively reduced, thereby adhering the present invention to the adhered surface. There is a problem that the adhesion of the preventive body may be lowered.
또한 본 발명의 부착방지체 형성시 상기 수지바인더는 필요에 따라 유리 섬유(glass fiber)를 추가로 포함할 수 있다. 상기 유리 섬유는 경화된 부착방지체의 인장력 및 내크랙성을 증가시키는 작용을 한다.In addition, the resin binder when the anti-sticking agent of the present invention is formed may further include a glass fiber (glass fiber) as needed. The glass fiber acts to increase the tensile strength and crack resistance of the cured anti-stick.
상기 유리 섬유는 E 조성의 장유리 섬유 또는 내알칼리성 조성의 섬유를 사용할 수 있으며, 구체적으로 섬유경이 10 내지 20 ㎛인 유리 섬유 또는 탄소 섬유를 균일한 스트랜드(strand) 길이로 절단한 절단 섬유(chopped fiber) 또는 평균 섬유 길이로 분쇄하여 제조한 분쇄 섬유(milled fiber)가 사용될 수 있다. 특히, 절단 섬유는 2 내지 12 ㎜ 정도의 섬유 길이로 재단된 것이 바람직하며, 분쇄 섬유는 평균 섬유길이가 100 내지 300 ㎛인 것이 바람직하다. 특히, 분쇄 섬유가 본 발명의 부착방지체의 인장력 보강 및 분산성 면을 고려할 때 바람직하며, 절단 섬유와 분쇄 섬유를 혼합하여 사용할 수도 있다.The glass fiber may be a long glass fiber of the E composition or a fiber of an alkali resistance composition, specifically, a chopped fiber cut into glass or carbon fibers having a fiber diameter of 10 to 20 ㎛ in a uniform strand length (chopped fiber) ) Or milled fibers prepared by milling to an average fiber length can be used. In particular, the chopped fibers are preferably cut to a fiber length of about 2 to 12 mm, and the pulverized fibers preferably have an average fiber length of 100 to 300 m. In particular, the pulverized fiber is preferable when considering the tensile strength reinforcement and dispersibility of the adhesion preventing body of the present invention, it is also possible to use a mixture of chopped fibers and pulverized fiber.
상기 유리 섬유는 수지바인더 고형분 100 중량부에 대하여 1 내지 100 중량부로 포함되는 것이 바람직하다. 상기 유리 섬유의 함량이 상기 범위내인 경우에는 경화된 부착방지체의 균열, 수축, 및 팽창이 발생하지 않는다는 장점이 있다.The glass fiber is preferably contained in 1 to 100 parts by weight based on 100 parts by weight of the resin binder solids. When the content of the glass fiber is within the above range, there is an advantage that cracking, shrinkage, and expansion of the hardened adhesion preventer do not occur.
또한 본 발명의 부착방지체에는 필요에 따라 통상의 충전제, 안료, 반응촉매, 증점제, 유동성조절제, 습윤제, 자외선 안정제, 또는 침강방지제 등의 첨가제를 추가로 포함할 수 있다.In addition, the anti-adhesion body of the present invention may further include additives such as conventional fillers, pigments, reaction catalysts, thickeners, flow control agents, wetting agents, UV stabilizers, or anti-settling agents.
상기와 같은 성분으로 이루어지는 본 발명의 부착방지체 형성은 광고물이나 접착물이 부착되는 전신주, 신호등, 가로등, 교통안내표지판, 콘트롤박스 등의 노상시설물의 지주나 건축물, 구조물의 벽체와 같은 다양한 피착면에 통상의 방법으로 실시하여 적용이 가능하다.Formation of the anti-sticking body of the present invention consisting of the above components is a variety of deposition such as props or buildings of the roadbed facilities, such as telephone poles, traffic lights, street lamps, traffic signs, control boxes, etc. to which advertising or adhesives are attached It is possible to apply the surface to the conventional method.
본 발명의 부착방지체 형성은 Anti-adhesion formation of the present invention
첫째, 노상시설물의 지주, 건축물이나 구조물의 벽체와 같은 피착면에 수지바인더와 필요에 따라 유리 분말, 유리 섬유, 또는 첨가제들을 혼합한 혼합물을 직접 도포하고, 상기 도포된 수지바인더를 함유하는 혼합물이 경화되기 이전에 유리 비드를 분사하여 수지바인더 상부에 유리 비드를 부착, 경화시키는 방법이 있으며,First, a resin binder and a mixture of glass powder, glass fiber, or additives are directly applied to an adhered surface such as a pillar of a substructure, a wall of a building or a structure, and a mixture containing the coated resin binder is applied. There is a method of spraying glass beads prior to curing and attaching and curing the glass beads on the resin binder.
둘째, 부직포 상에 수지바인더와 필요에 따라 유리 분말, 유리 섬유, 또는 첨가제들을 혼합한 혼합물을 직접 코팅하고, 상기 도포된 수지바인더를 함유하는 혼합물이 경화되기 이전에 유리 비드를 분사하고 수지바인더 상부에 유리 비드를 부착, 경화시킨 후, 상기 성분들이 코팅된 부직포를 노상시설물의 지주, 건축물이나 구조물의 벽체와 같은 피착면에 스티커식이나 시트타입으로 부착시키는 방법이 있다.Secondly, directly coating a resin binder and a mixture of glass powder, glass fiber, or additives as needed on the nonwoven fabric, spraying glass beads and curing the resin beads before the mixture containing the applied resin binder is cured. After attaching and curing the glass beads, there is a method of attaching a nonwoven fabric coated with the above components to a surface to be adhered to, such as a pillar of a substructure, a wall of a building or a structure, in a sticker or sheet type.
상기와 같은 부착방지체의 형성은 이미 설치된 노상시설물의 지주, 건축물이나 구조물의 벽체와 같은 피착면에 형성할 수도 있으며, 노상시설물, 건축물, 구조물 등을 제조하면서 그 표면에 직접 형성할 수도 있다.The formation of the anti-sticking agent as described above may be formed on the surface of the installation, such as the pillar of the roadbed facility, the wall of the building or structure, and may be formed directly on the surface of the road facility, building, structure, etc. while manufacturing.
상기 수지바인더와 필요에 따라 유리 분말, 유리 섬유, 또는 첨가제들을 혼합한 혼합물은 도포되는 피착면의 재질, 요구 조건, 면적 등에 따라 당업계에서 사용하는 통상의 코팅방법을 선택적으로 사용하여 피착면이나 부직포에 도포할 수 있음은 물론이며, 특히 상기 성분들이 중력외 방향으로 도포될 경우 비산될 우려가 있는 경우에는 롤러나 붓칠을 이용하여 비산을 방지하는 것이 바람직하며, 상기 성분이 비산의 우려가 없는 경우에는 스프레이 코팅을 이용하는 것이 바람직하다.The resin binder and a mixture of glass powder, glass fiber, or additives as necessary may be selectively used by using a conventional coating method used in the art according to the material, requirement, area, etc. of the surface to be coated. Of course, it can be applied to a nonwoven fabric, and in particular, if the components are likely to be scattered when applied in an outward direction of gravity, it is preferable to prevent them from scattering by using a roller or a brush, and the components may not be scattered. In this case, it is preferable to use a spray coating.
상기와 같은 방법으로 형성되는 부착방지체는 형성하고자하는 피착면의 재질이나 성능 등을 고려하여 그 두께를 조절할 수 있으며, 특히 피착면에 대하여 0.05 내지 20 ㎜의 두께로 코팅되는 것이 좋다.The anti-adhesion body formed by the above method can adjust the thickness in consideration of the material or performance of the surface to be formed to be formed, and in particular, it is preferable to be coated with a thickness of 0.05 to 20 mm with respect to the surface to be deposited.
상기와 같은 본 발명의 부착방지체 형성방법에 따르면 코팅된 전신주, 신호등, 가로등, 교통안내표지판, 콘트롤박스 등의 노상시설물의 지주나 건축물, 구조물의 벽체와 같은 피착면의 표면에 유리 비드에 의하여 형성된 돌기가 불규칙한 형태로 굴곡을 형성하여 이로 인해 노상시설물의 지주, 건축물이나 구조물의 벽체와 같은 피착면과 접착물간의 접촉면을 감소시켜 부착을 막을 수 있고, 일단 부착되었다 하더라도 접촉면을 최소화하여 쉽게 제거할 수 있다. 뿐만 아니라, 유리 비드 돌기들에 의해 형성된 요철에 먼지 등의 오염이 생길 경우 빗물이나 눈 등의 물에 의한 세척으로 쉽게 오염물이 제거될 수 있어 내오염성에 있어서도 뛰어난 효과가 있다. 또한 본 발명의 부착방지체는 용이하게 시공할 수 있으며, 피착면의 내후성, 내오염성, 내스크래치성, 내화학성, 내충격성 등의 물성을 향상시킬 수 있다는 장점이 있다.According to the method of forming the anti-sticking body of the present invention as described above by the glass beads on the surface of the surface of the installation, such as the pillars of the road facilities, such as coated telephone poles, traffic lights, street lights, traffic signs, control boxes, buildings, walls of the structure The formed protrusions form irregular shapes, which can reduce the contact surface between adherends such as struts of subsidiary facilities, walls of buildings or structures, and adhesives, preventing attachment, and once attached, minimize the contact surface and easily remove it. can do. In addition, when contamination such as dust occurs in the unevenness formed by the glass bead protrusions, contaminants can be easily removed by washing with water such as rain or snow, thereby having an excellent effect in fouling resistance. In addition, the anti-sticking body of the present invention can be easily constructed, there is an advantage that the physical properties such as weather resistance, stain resistance, scratch resistance, chemical resistance, impact resistance of the adhered surface can be improved.
이하, 본 발명의 이해를 돕기 위하여 바람직한 실시예를 제시하나, 하기 실시예는 본 발명을 예시하는 것일 뿐 본 발명의 범위가 하기 실시예에 한정되는 것은 아니다.Hereinafter, preferred examples are provided to help understanding of the present invention, but the following examples are merely to illustrate the present invention, and the scope of the present invention is not limited to the following examples.
[실시예]EXAMPLE
실시예 1Example 1
우레탄 수지 1 ㎏을 25 ㎝ × 15 ㎝의 강철과 콘크리트 위에 각각 1 ㎜의 두께로 도포하고, 상기 우레탄 수지가 경화되기 이전에 평균입도가 0.1 ㎜인 유리 비드 800 g을 분사하고 경화하여 우레탄 수지 표면에 유리 비드 돌기가 부착된 부착방지체를 형성하였다.1 kg of urethane resin was applied on the steel and concrete of 25 cm × 15 cm in thickness of 1 mm, and 800 g of glass beads with an average particle size of 0.1 mm were sprayed and cured before the urethane resin was cured. The anti-adhesion body with the glass bead protrusion was formed in.
상기와 같이 부착방지체가 형성된 강철과 콘크리트의 일면에 각각 접착제가 형성되어 있는 테이프를 부착한 결과, 각각의 강철과 콘크리트에 테이프가 붙지 않았다. 또한, 상기 부착방지체가 형성된 강철과 콘크리트를 흑연으로 오염시킨 후 물로 세척한 결과 오염부위가 쉽게 제거됨을 확인할 수 있었다.As described above, as a result of attaching a tape on which adhesive is formed on one side of the steel and concrete on which the anti-sticking agent was formed, the tape did not adhere to each steel and concrete. In addition, it was confirmed that the contamination site is easily removed as a result of contaminating the steel and concrete with the adhesion preventing member with graphite and then washing with water.
이로부터 본 발명에 따라 형성된 부착방지체는 부착방지능이 우수하고, 내오염성 또한 우수함을 확인할 수 있었다.From this, it can be confirmed that the anti-adhesion body formed according to the present invention has excellent anti-adhesion ability, and also excellent stain resistance.
실시예 2Example 2
상기 실시예 1에서 평균입도가 50 ㎛인 유리 비드를 사용한 것을 제외하고는 상기 실시예 1과 동일한 방법으로 실시하여 부착방지체를 형성하였다. Except for using glass beads having an average particle size of 50 ㎛ in Example 1 was carried out in the same manner as in Example 1 to form an adhesion preventing body.
또한, 상기와 같이 부착방지체가 형성된 강철과 콘크리트를 이용하여 상기 실시예 1과 동일한 방법으로 테이프의 접착여부를 실험한 결과, 각각의 강철과 콘크리트에 테이프가 잘 붙지 않았으며, 강한 압력을 주어 부착시켰을 경우에도 쉽게 떨어짐을 확인할 수 있었다.In addition, using the steel and concrete formed with the anti-sticking material as described above as a result of the test whether the adhesive tape in the same manner as in Example 1, the tape was not adhered well to each steel and concrete, given a strong pressure to attach Even if the fall was easy to confirm.
실시예 3Example 3
상기 실시예 1에서 우레탄 수지 1 ㎏에 평균입도가 200 메쉬이고 비중이 2.54인 유리 분말 1 ㎏을 균일하게 혼합하여 강철과 콘크리트에 각각 도포한 후, 상기 실시예 1과 동일한 방법으로 실시하여 부착방지체를 형성하고, 테이프 접착여부를 실험한 결과 상기 실시예 1과 대등한 정도의 부착방지효과를 나타내었다. In Example 1, 1 kg of urethane resin was uniformly mixed with 1 kg of glass powder having an average particle size of 200 mesh and specific gravity of 2.54, and applied to steel and concrete, respectively, followed by the same method as Example 1 to prevent adhesion. A sieve was formed and the result of the tape adhesion test showed the same degree of anti-sticking effect as in Example 1.
또한, 상기 실시예 1 및 실시예 3에서 형성한 부착방지체에 외부 압력을 가하여 유리 비드의 탈락 여부를 관찰한 결과, 유리 분말을 사용하지 않은 실시예 1과 비교하여 유리 분말을 사용한 실시예 3의 부착방지체가 더욱 우수한 유리 비드 결합력을 나타냄을 확인할 수 있었다.In addition, as a result of observing whether glass beads were dropped by applying an external pressure to the adhesion preventing agents formed in Examples 1 and 3, Example 3 using glass powder compared to Example 1 without using glass powder It could be confirmed that the anti-adhesion of showed a better glass bead binding force.
실시예 4Example 4
상기 실시예 1에서 우레탄 수지 1 ㎏에 평균섬유두께 13.5 ㎛, 평균 섬유길이 300 ㎛의 분쇄 유리 섬유 100 g을 균일하게 혼합하여 강철과 콘크리트에 각각 도포한 후, 상기 실시예 1과 동일한 방법으로 실시하여 부착방지체를 형성하고, 테이프 접착여부를 실험한 결과 상기 실시예 1과 대등한 정도의 부착방지효과를 나타내었다. In Example 1, 100 g of pulverized glass fibers having an average fiber thickness of 13.5 μm and an average fiber length of 300 μm were uniformly mixed with 1 kg of a urethane resin, and applied to steel and concrete, respectively, followed by the same method as in Example 1. To form an anti-adhesion body and test whether the tape was adhered, and showed an anti-adhesion effect equivalent to that of Example 1.
실시예 5Example 5
상기 실시예 1에서 평균입도가 200 메쉬이고 비중이 2.54인 유리 분말 1 ㎏ 및 평균섬유두께 13.5 ㎛, 평균 섬유길이 300 ㎛의 분쇄 유리 섬유 100 g을 균일하게 혼합하여 강철과 콘크리트에 각각 도포한 후, 상기 실시예 1과 동일한 방법으로 실시하여 부착방지체를 형성하고, 테이프 접착여부를 실험한 결과 상기 실시예 1과 대등한 정도의 부착방지효과를 나타내었다. In Example 1, 1 kg of glass powder having an average particle size of 200 mesh and specific gravity of 2.54 and 100 g of crushed glass fibers having an average fiber thickness of 13.5 μm and an average fiber length of 300 μm were uniformly mixed and applied to steel and concrete, respectively. In the same manner as in Example 1 to form an anti-adhesion body, and tested the adhesion of the tape showed a similar degree of anti-sticking effect to Example 1.
실시예 6Example 6
우레탄 수지 1 ㎏을 25 ㎝ × 15 ㎝의 부직포 표면에 코팅하고, 상기 우레탄 수지가 경화되기 이전에 평균입도가 1 ㎜인 유리 비드 800 g을 분사하고 경화하여 우레탄 수지 표면에 유리 비드 돌기가 부착된 부착방지체를 형성하였다. 1 kg of urethane resin was coated on the surface of a nonwoven fabric of 25 cm × 15 cm, and 800 g of glass beads having an average particle size of 1 mm were sprayed and cured before the urethane resin was cured, thereby adhering the glass bead projections to the urethane resin surface. An antiadhesion body was formed.
상기와 같이 부착방지체가 형성된 부직포를 강철과 콘크리트에 부착하여 상기 실시예 1과 동일한 방법으로 테이프 접착여부를 실험한 결과 상기 실시예 1과 대등한 정도의 부착방지효과를 나타내었다. As described above, by attaching the nonwoven fabric having the anti-sticking material to steel and concrete, and testing the adhesiveness of the tape in the same manner as in Example 1, it showed an anti-sticking effect equivalent to that of Example 1.
상기와 같은 본 발명의 부착방지체 형성방법에 따르면 코팅된 전신주, 신호등, 가로등, 교통안내표지판, 콘트롤박스 등의 노상시설물의 지주나 건축물, 구조물의 벽체와 같은 피착면의 표면에 유리 비드에 의하여 형성된 돌기가 불규칙한 형태로 굴곡을 형성하여 이로 인해 노상시설물의 지주, 건축물이나 구조물의 벽체와 같은 피착면과 접착물간의 접촉면을 감소시켜 부착을 막을 수 있고, 일단 부착되었다 하더라도 접촉면을 최소화하여 쉽게 제거할 수 있다. 뿐만 아니라, 유리 비드 돌기에 의해 형성된 굴곡에 먼지 등의 오염이 생길 경우 빗물이나 눈 등의 물에 의한 세척으로 쉽게 오염물이 제거될 수 있어 내오염성에 있어서도 뛰어난 효과가 있다. 또한 본 발명의 부착방지체는 용이하게 시공할 수 있으며, 피착면의 내후성, 내오염성, 내스크래치성, 내화학성, 내충격성 등의 물성을 향상시킬 수 있다는 효과가 있다.According to the method of forming the anti-sticking body of the present invention as described above by the glass beads on the surface of the surface of the installation, such as the pillars of the road facilities, such as coated telephone poles, traffic lights, street lights, traffic signs, control boxes, buildings, walls of the structure The formed projections form a curved shape with irregular shape, which can reduce the contact surface between adherends such as struts of substructures, walls of buildings or structures, and adhesives, and prevent them from attaching. can do. In addition, when contamination such as dust is generated in the bend formed by the glass bead protrusion, contaminants can be easily removed by washing with water such as rain or snow, and thus has excellent effects in fouling resistance. In addition, the anti-sticking agent of the present invention can be easily constructed, there is an effect that can improve the physical properties such as weather resistance, stain resistance, scratch resistance, chemical resistance, impact resistance of the adhered surface.
도 1은 본 발명에 따라 형성된 부착방지체의 단면을 나타낸 그림이다. 1 is a view showing a cross section of the anti-sticking body formed according to the present invention.
* 도면의 주요부분에 대한 부호의 설명 *Explanation of symbols on main parts of drawing
1 : 피착면1: adherend surface
2 : 수지바인더2: Resin Binder
3 : 유리 비드 돌기3: glass bead protrusion
Claims (11)