KR20050030933A - The surface repair method of concrete structure - Google Patents

The surface repair method of concrete structure Download PDF

Info

Publication number
KR20050030933A
KR20050030933A KR1020050019083A KR20050019083A KR20050030933A KR 20050030933 A KR20050030933 A KR 20050030933A KR 1020050019083 A KR1020050019083 A KR 1020050019083A KR 20050019083 A KR20050019083 A KR 20050019083A KR 20050030933 A KR20050030933 A KR 20050030933A
Authority
KR
South Korea
Prior art keywords
concrete structure
repairing
primer
impregnated resin
curing
Prior art date
Application number
KR1020050019083A
Other languages
Korean (ko)
Other versions
KR100500426B1 (en
Inventor
박호완
Original Assignee
주식회사 기해테크
박호완
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 기해테크, 박호완 filed Critical 주식회사 기해테크
Priority to KR10-2005-0019083A priority Critical patent/KR100500426B1/en
Publication of KR20050030933A publication Critical patent/KR20050030933A/en
Application granted granted Critical
Publication of KR100500426B1 publication Critical patent/KR100500426B1/en

Abstract

A method for repairing the surface of a concrete structure is provided to prevent the concrete structure from being degraded and deteriorated, and to prevent damage from sea wind, by improving adhesive force of the concrete structure and a repaired part and preventing separation of the concrete structure and a repaired part. A method for repairing the surface of a concrete structure comprises a step of flattening and cleaning the surface of the concrete structure needing repair(S1); a step of spreading and curing of a primer of very low viscosity on the concrete structure many times(S2); a step of attaching a staple fiber to the semi-cured primer layer by blowing compressed air(S3); a step of spreading impregnation resin of very low viscosity on the flocked surface of the staple fiber(S4); a step of attaching a fixing mesh(S5); a step of spreading impregnation resin and smoothing the surface(S6); and a step of forming a film layer by spreading a urethane paint on the surface where the impregnation resin is hardened and sufficiently drying the film layer(S7).

Description

콘크리트 구조물의 표면을 보수하는 방법 { the surface repair method of concrete structure }{The surface repair method of concrete structure}

본 발명은 콘크리트 구조물에서 그 표면을 보수하는 방법에 관한 것으로, 프라이머를 다수회 도포한 보수면에 나일론 단섬유를 분사하여 부착하고, 이에 함침수지를 도포하여 고정메시를 부착하며, 다시 함침수지를 도포하여 표면을 정리하는 보수 방법을 통해, 초저점도의 함침수지 및 프라이머가 기존의 콘크리트 구조물과의 괴리를 방지하여, 콘크리트 표면의 열화 및 노후화를 방지할 수 있는 것이다.The present invention relates to a method for repairing the surface of a concrete structure, by spraying nylon short fibers to the repair surface coated with a primer a plurality of times, and applied to the impregnated resin to attach a fixed mesh, and again impregnated resin Through the repair method to clean the surface by coating, the ultra-low viscosity impregnated resin and primer to prevent the deviation from the existing concrete structure, it is possible to prevent deterioration and aging of the concrete surface.

일반적으로 콘크리트의 구조물은 시간이 지남에 따라, 열화 및 노후화가 진행되고, 특히, 직접 바닷물과 접하거나, 해안과 근접한 콘크리트 구조물은, 해수, 바닷바람의 염분이 침투되어 염해가 발생하게 되므로, 이에 따른 적절한 보수가 필요한데, 통상적인 보수 방법으로는, 먼저, 보강할 콘크리트 표면의 돌출부위는 제거하고, 오목한 부위는 모르타르, 퍼티로 메워 그 표면을 평평하게 하며, 이에 프라이머를 도포하여 양생한 뒤, 폴리머 모르타르를 도포하여 그 표면을 평탄하게 하고, 일정시간 양생을 거치면 보수가 완료된다.In general, concrete structures deteriorate and age over time, and in particular, concrete structures directly in contact with sea water or close to the shore, salts of seawater and sea breeze penetrate, thereby causing salt damage. According to the conventional repair method, a conventional repair method includes, first, removing the protrusions of the concrete surface to be reinforced, and filling the concave parts with mortar and putty to flatten the surface, and applying curing to the primer. Polymer mortar is applied to smooth the surface, and after a certain period of time curing, repair is completed.

그러나 상기 보수 방법은, 콘크리트 구조물과 폴리머 모르타르의 물성이 달라서, 외력을 받거나, 외부 온도의 급격한 변화 등의 요인으로 콘크리트 구조물과 보수된 부분의 괴리가 일어나며, 이에 따라 습기가 유입되어 다시 콘크리트 구조물 내의 철근이 부식되고, 크랙이 발생 되는 문제점이 있었으며, 이를 방지하고자, 접착력을 높이기 위해, 저점도의 폴리머 모르타르를 사용하게 되면, 자체 중력으로 경화되기 전에 폴리머 모르타르가 흘러내려 균일한 도포가 어려운 문제점이 있었다.However, in the repair method, the physical structure of the concrete structure and the polymer mortar is different, the difference between the repaired portion and the concrete structure due to external forces or sudden changes in the external temperature, such that the moisture is introduced into the concrete structure again There was a problem in that the steel was corroded and cracks were generated. In order to prevent this, when a low viscosity polymer mortar is used to increase the adhesion, the polymer mortar flows out before it is cured by its own gravity, making it difficult to apply uniformly. there was.

따라서 본 발명은 상기의 문제점을 해결하고자, 콘크리트 구조물의 표면을 보수하는 방법에 있어서, 보수할 콘크리트 구조물의 표면을 정리한 뒤, 프라이머를 다수회 도포하며, 이에 나일론 단섬유를 온풍과 함께 분사하여 부착하고, 함침수지를 도포하여 피이티의 고정메시를 부착하며, 다시 함침수지의 도포로 그 표면을 정리하는 보수 방법으로, 100cps 이하의 초저점도의 프라이머 및 함침수지를 사용함에 따라, 기존 콘크리트 구조물과 보수된 부분과의 접착력을 높이고, 괴리를 방지하여, 콘크리트 구조물의 열화 및 노후화 및 염해를 방지하는데 그 목적이 있다.Therefore, the present invention to solve the above problems, in the method of repairing the surface of the concrete structure, after arranging the surface of the concrete structure to be repaired, the primer is applied a plurality of times, by spraying the nylon short fibers with warm air This is a repairing method for attaching the fixed mesh of PTI by applying impregnated resin and cleaning the surface by applying impregnated resin, and by using ultra low viscosity primer and impregnated resin of 100 cps or less, existing concrete The purpose of the present invention is to increase adhesion between the structure and the repaired part and to prevent gaps, thereby preventing deterioration, aging, and salting of the concrete structure.

본 발명은 콘크리트 구조물에서 그 표면을 보수하는 방법에 관한 것으로, 프라이머를 다수회 도포한 보수면에 나일론 단섬유를 분사하여 부착하고, 이에 함침수지를 도포하여 고정메시를 부착하며, 다시 함침수지를 도포하여 표면을 정리하는 보수 방법을 통해, 초저점도의 함침수지 및 프라이머가 기존의 콘크리트 구조물과의 괴리를 방지하여, 콘크리트 표면의 열화 및 노후화를 방지할 수 있는 것이다.The present invention relates to a method for repairing the surface of a concrete structure, by spraying nylon short fibers to the repair surface coated with a primer a plurality of times, and applied to the impregnated resin to attach a fixed mesh, and again impregnated resin Through the repair method to clean the surface by coating, the ultra-low viscosity impregnated resin and primer to prevent the deviation from the existing concrete structure, it is possible to prevent deterioration and aging of the concrete surface.

본 발명에 따른 노후화된 콘크리트 구조물의 표면 보수 방법을 도1을 참고하여 대략 설명하면, 먼저, 보수가 필요한 콘크리트 구조물(10)의 표면을 평탄하게 하는 보수면 정리 공정(S1), 상기 정리된 구조물(10)에 초저점도 프라이머(11)의 도포와 양생을 다수회 반복하여 실시하는 프라이머 반복 도포 공정(S2), 상기 프라이머(11)가 도포된 면에, 나일론 스테이플섬유, 나일론 토우와 같은 나일론 단섬유(12)를, 압축공기와 70 내지 80℃의 온풍과 함께 불어내어 부착하는 단섬유의 플로킹 공정(S3), 상기 단섬유(12)를 플로킹한 면에 초저점도의 함침수지(13)를 도포하는 함침수지 도포 공정(S4), 이에 피이티 재질로 망을 형성한 고정메시(14)를 부착하는 고정메시 부착 공정(S5), 다시 함침수지(13)를 도포하고, 표면을 매끄럽게 정리하는 함침수지 도포 및 면정리 공정(S6), 상기 함침수지(13)의 일정한 양생을 거친 후, 우레탄 페인트 등을 발라 피막층(15)을 형성하는 피막층 형성 공정(S7)으로, 콘크리트 구조물의 표면을 보수하는 방법이다.If the surface repair method of the aging concrete structure according to the present invention will be described with reference to Figure 1, first, the repair surface cleaning process (S1) to flatten the surface of the concrete structure 10 in need of repair, the arranged structure Primer repeat coating step (S2) which repeats application and curing of the ultra-low viscosity primer 11 to many times in (10), and nylon, such as nylon staple fiber and nylon tow, to the surface on which the said primer 11 was apply | coated Ultra-low viscosity impregnated resin 13 on the flocking step of the short fibers (S3) for blowing short fibers 12 together with compressed air and warm air at 70 to 80 ° C. ) Impregnated resin application process (S4) to apply, the fixed mesh attachment process (S5) to attach the fixed mesh 14 formed a mesh of Piti material, and the impregnated resin 13 is applied again, the surface smoothly Impregnation resin application and surface cleaning process S6), after undergoing a certain curing of the impregnated resin 13, a coating layer forming step (S7) to form a coating layer 15 by applying a urethane paint or the like, it is a method for repairing the surface of the concrete structure.

본 발명에 따른 콘크리트 구조물의 표면을 보수하는 공법을, 그 순서에 따라 상세히 설명하면, 먼저, 보수면 정리 공정(S1)은 노후 및 열화되어 보수가 필요한 콘크리트 구조물(10)의 표면을 평평하게 정리하되, 돌출된 부분은 치핑작업(chipping, 깎아내기)을 수행하고, 심하게 함몰된 부분이나 크랙(crack, 틈새)이 형성된 부분은 모르타르, 에폭시수지, 퍼티 등으로 메워 평평하게 하며, 평탄하게 정리된 표면은, 레이턴스(laitance), 먼지, 기름, 녹, 부식물, 수분 등을 제거하여 깨끗이 한다. The method for repairing the surface of the concrete structure according to the present invention will be described in detail according to the order. First, the repair surface cleaning process (S1) is flattened the surface of the concrete structure 10 that needs to be repaired due to deterioration and deterioration. However, the protruding part is chipped, and the heavily recessed part or the cracked part is flattened with mortar, epoxy resin, putty, and flattened. The surface is cleaned by removing latency, dust, oil, rust, corrosives, water, and the like.

다음으로, 프라이머 반복 도포 공정(S2)은, 100cps 이하의 초저점도 프라이머(11)를 선정하여, 상기 구조물(10)에 도포와 양생을 다수회 반복하는 것으로, 이는 각 도포 시, 일정시간 양생 시간을 주어 흡수와 경화가 일어나도록 하되, 처음 3 내지 4회 정도를 도포로 프라이머(11)가 더 이상 흡수되지 않으며, 다시 1 내지 2회를 더 도포함으로써, 구조물(10)의 표면에 프라이머(11)가 일정두께를 형성하게 되고, 이어서, 단섬유의 플로킹 공정(S3)은, 상기 반경화된 프라이머(11)에 나일론 단섬유(12)를 압축 공기 및 온풍과 함께 쏘아내어 부착하는 플로킹(flocking) 작업을 하되, 상기 나일론 단섬유(12)는 나일론 토우(Nylon tow), 나일론 스테이플섬유(Nylon staple fiber)이 사용되고, 상기 공급되는 온풍은 70 내지 80℃이 바람직하다.Next, the primer repeat coating step (S2), by selecting the ultra-low viscosity primer 11 of 100cps or less, repeating the coating and curing on the structure 10 a number of times, which is curing for a certain time during each application Allow time to absorb and harden, but the primer 11 is no longer absorbed by applying the first 3 to 4 times, and by applying another 1 to 2 times, the primer (on the surface of the structure 10) 11) forms a constant thickness, and then, the flocking step S3 of filament flocking is performed by flocking the short filament 12 with the compressed air and warm air to attach the semi-finished primer 11 together with compressed air and warm air. Flocking operation, the nylon short fiber 12 is used nylon tow (nylon tow), nylon staple fiber (Nylon staple fiber), the supplied warm air is preferably 70 to 80 ℃.

그리고 함침수지 도포 공정(S4)은, 상기 플로킹한 면에, 100cps 이하의 초저점도의 함침수지(13)를 도포하는 공정으로, 이에 쓰이는 함침수지(13)로는 주로 상기 점도의 에폭시 수지가 사용되며, 다음, 고정메시 부착 공정(S5)은, 피이티(PET, polyethylene terephthalate)를 망으로 형성한 고정메시(14)를 부착하는 것으로, 상기 고정메시(14)의 굵기는 30 내지 300D(데니어, denier)이고, 그 간격은 50 내지 200mesh(메시, 눈금수/inch)로 형성한다.The impregnating resin application step (S4) is a step of applying an impregnating resin (13) having an ultra low viscosity of 100 cps or less on the flocked surface, and an epoxy resin having the above viscosity is mainly used as the impregnating resin (13) used therein. Next, the fixed mesh attaching process (S5) is to attach a fixed mesh 14 formed of PET (polyethylene terephthalate) into a mesh, and the thickness of the fixed mesh 14 is 30 to 300D (denier). , denier), and the spacing is formed from 50 to 200mesh (mesh, scale number / inch).

또한, 함침수지의 도포 및 면정리 공정(S6)은, 다시 함침수지(13)를 도포하고, 그 표면을 매끄럽게 정리하는 공정으로, 함침수지(13)는 상기 함침수지 도포 공정(S4)에서 사용된 것과 같은 것을 사용하며, 표면 정리 후, 일정 시간의 양생으로 함침수지(13)를 경화하고, 마지막으로, 피막층 형성 공정(S7)은, 함침수지(13)가 경화된 표면에 우레탄 페인트 등을 칠하여 피막층(15)을 형성하는 공정이며, 이 피막층(15)이 충분히 건조되면 콘크리트 구조물의 보수가 완료된다.In addition, the impregnation resin application and surface cleaning step (S6) is a step of applying the impregnation resin 13 again and smoothing the surface thereof, and the impregnation resin 13 is used in the impregnation resin application step (S4). After the surface is cleaned, the impregnated resin 13 is cured by curing for a predetermined time. Finally, in the coating layer forming step S7, urethane paint or the like is applied to the surface of the impregnated resin 13. It is a process of coating and forming the coating layer 15, and when this coating layer 15 is fully dried, repair of a concrete structure will be completed.

따라서, 초저점도의 프라이머가 다수회 반복되어 사용됨에 따라, 프라이머가 구조물에 3 내지 5㎜의 깊이로 함침되고, 또한, 구조물의 겉면에 프라이머 층을 형성하면서, 다음으로 형성되는 단섬유 및 함침수지와의 접착이 긴밀히 이루어지므로, 후에 외력, 온도의 급격한 변화가 발생하여도, 기존의 콘크리트 구조물과 보수된 부분의 괴리가 발생하지 않는 특징이 있다. Therefore, as the primer of very low viscosity is used repeatedly, many times, the primer is impregnated to the structure to a depth of 3 to 5 mm, and also the next formed short fiber and impregnation, forming a primer layer on the outer surface of the structure. Since the adhesion to the resin is made closely, there is a feature that does not occur between the existing concrete structure and the repaired part even if a sudden change in external force and temperature occurs later.

한편, 상기 사용된 재료 및 소재에 대해 참고적으로 설명하면, 먼저, 프라이머(11)는 콘크리트 슬라브, 목재, 철재 등의 표면에 도포되어, 하층에 피막을 형성하여 표면을 정리하고, 다음으로 부착되는 피착제 대한 접착력을 강화하는 것으로, 본 발명에서는, 프라이머(11)를 충분한 반복·도포로, ㎡당 0.06 내지 0.08㎏의 프라이머(11)가 구조물(10)에 충분히 흡수되고, 그 표면에 일정두께의 프라이머(11) 층을 형성함으로써, 단섬유(12) 및 함침수지(13)가 용이하게 부착되도록 함으로써, 경화 후에도 괴리가 일어나는 것을 방지한다. Meanwhile, referring to the materials and materials used above, the primer 11 is first applied to the surface of the concrete slab, wood, steel, etc. to form a film on the lower layer to clean up the surface, and then attach it. In the present invention, 0.06 to 0.08 kg of primer 11 per m 2 is sufficiently absorbed into the structure 10 by the repetition and coating of the primer 11 by enhancing the adhesion to the adherend to be applied, and the surface is fixed to the surface. By forming a layer of primer 11 having a thickness, the short fibers 12 and the impregnated resin 13 are easily attached to each other, thereby preventing deviations even after curing.

또한, 단섬유의 플로킹 공정(S3)에 사용되는 나일론 스테이플섬유, 나일론 토우와 같은 나일론 단섬유(12)에 대해 설명하면, 이는 합성고분자 폴리 아미드(Amide, 즉, -CONH-가 많음을 의미함)계의 나일론(Nylon)을 각 스테이플섬유 및 토우로 형성한 것으로, 스테이플섬유(staple fiber)는 섬유를 일정길이로 절단한 스테이플을 가지고, 방적에 의해 연속성이 있도록 꼬임을 부여하여 만든 섬유이며, 토우(tow)는 아세테이트나 나일론과 같은 인조섬유의 필라멘트를 로프 상태의 다발로, 이들 나일론 스테이플섬유, 나일론 토우를 짧게 절단하여 사용되는데, 이외에도, 나일론 섬유의 제직 후 버려지는 폐나일론을 재활용해 쓸 수 있다. In addition, when describing the nylon staple fibers 12, such as nylon staple fibers, nylon tow used in the flocking step (S3) of the short fibers, this means that there are a lot of synthetic polymer polyamides (i.e., -CONH-). ) Nylon (Nylon) is formed of each staple fiber and tow, staple fiber (staple fiber) is a fiber made by twisting the fiber to have a staple cut to a certain length, continuity by spinning, Tow is used to cut filaments of artificial fibers such as acetate and nylon into bundles of ropes, and short cuts of these nylon staple fibers and nylon tows. Can be.

이와 같이 형성한 나일론 스테이플섬유 및 나일론 토우와 같은 나일론 단섬유(12)는, 압축공기와 함께 상기 프라이머(11)가 도포된 구조물(10)에 발사되어 부착되는 플로킹(flocking) 공정을 통해, 초저점도의 프라이머(11)의 흘러내림을 방지하고, 다음으로 도포되는 함침수지(13)의 흘러내림을 방지하는데, 이때, 70 내지 80℃의 온풍을 함께 불어 넣음으로써, 상기 프라이머(11)의 경화를 촉진하여 공기를 단축한다. Thus formed nylon staple fibers and nylon short fibers 12, such as nylon tow, through a flocking process that is fired and attached to the structure 10 to which the primer 11 is applied together with compressed air, It prevents the flow of the primer 11 of low viscosity and prevents the flow of the impregnated resin 13 to be applied next, at this time, by blowing together the warm air of 70 to 80 ℃, Accelerate hardening, shorten air.

이와 같이 본 발명은, 콘크리트 구조물의 표면을 보수하는 방법에 있어서, 보수할 콘크리트 구조물의 표면을 정리한 뒤, 프라이머를 다수회 도포하며, 이에 나일론 단섬유를 온풍과 함께 분사하여 부착하고, 함침수지를 도포하여 피이티의 고정메시를 부착하며, 다시 함침수지의 도포로 그 표면을 정리하는 보수 방법으로, 100cps 이하의 초저점도의 프라이머 및 함침수지를 사용함에 따라, 기존 콘크리트 구조물과 보수된 부분과의 접착력을 높이고, 괴리를 방지하여, 콘크리트 구조물의 열화 및 노후화 및 염해를 방지하는 효과가 있다.As described above, the present invention, in the method of repairing the surface of the concrete structure, after arranging the surface of the concrete structure to be repaired, the primer is applied a plurality of times, and the nylon short fibers are sprayed and attached together with warm air, and the impregnated resin It is a repairing method to attach the fixed mesh of FT and to clean up the surface by applying impregnated resin. As a result of using an ultra low viscosity primer and impregnated resin of 100 cps or less, the existing concrete structure and the repaired part Increasing the adhesive strength and preventing the separation, there is an effect of preventing deterioration and aging and salt of the concrete structure.

도 1은 본 발명에 따른 공정 순서도.1 is a process flow chart in accordance with the present invention.

도 2는 본 발명의 실시예에 따른 단면도.2 is a cross-sectional view according to an embodiment of the present invention.

도 3은 도2의 A부분의 확대도.3 is an enlarged view of portion A of FIG. 2;

[ 도면의 주요 부분에 따른 부호의 설명 ][Description of Symbols According to Main Parts of Drawings]

10 : 구조물 11 : 프라이머 12 : 단섬유10 structure 11 primer 12 short fiber

13 : 함침수지 14 : 고정메시 15 : 피막층13: impregnated resin 14: fixed mesh 15: coating layer

Claims (5)

보수가 필요한 콘크리트 구조물(10) 표면을 평평하고, 깨끗이 하는 보수면 정리 공정(S1), 상기 정리된 구조물(10)에 초저점도의 프라이머(11)를 도포와 양생을 다수회 반복하는 프라이머 반복 도포 공정(S2), 상기 반경화된 프라이머(11) 층에 단섬유(12)를 압축공기를 불어내어 부착하는 단섬유의 플로킹 공정(S3), 상기 표면에 초저점도의 함침수지(13)를 도포하는 함침수지 도포 공정(S4), 이에 망으로 형성된 고정메시(14)를 부착하는 고정메시 부착 공정(S5), 다시 함침수지(13)를 도포하고, 그 표면을 매끄럽게 정리하는 함침수지 도포 및 면정리 공정(S6)과, 충분한 양생을 통해 콘크리트 구조물의 표면을 보수하는 방법으로,Repair surface cleaning process (S1) to flatten and clean the surface of the concrete structure that needs to be repaired (S1), the primer repeat to repeat the application and curing of a very low viscosity primer 11 to the cleaned structure 10 a number of times Application step (S2), the flocking step (S3) of the short fiber to blow the short fibers 12 to the semi-cured primer (11) layer by blowing compressed air to attach, the ultra-low viscosity impregnated resin (13) on the surface Impregnated resin application process (S4) for applying the coating, fixed mesh attachment process (S5) for attaching the fixed mesh 14 formed by the net, and impregnated resin (13) is applied again, and impregnated resin application for smoothing the surface And a surface cleaning process (S6) and a method of repairing the surface of the concrete structure through sufficient curing, 콘크리트 표면의 노화 및 열화를 방지함을 특징으로 하는 콘크리트 구조물의 표면을 보수하는 방법.A method of repairing a surface of a concrete structure, characterized by preventing aging and deterioration of the concrete surface. 제 1항에 있어서,The method of claim 1, 상기 공정 다음으로, 페인트를 칠하여 피막층(15)을 형성하는 피막층 형성 공정(S7)이 추가됨을 특징으로 하는 콘크리트 구조물의 표면을 보수하는 방법.Next to the process, a method of repairing the surface of the concrete structure, characterized in that the coating layer forming step (S7) of painting to form the coating layer (15) is added. 제 1항 또는 제 2항에 있어서,The method according to claim 1 or 2, 상기 단섬유의 플로킹 공정(S3)에서, 70 내지 80℃의 온풍을 함께 불어넣어, 프라이머의 경화 및 양생을 촉진함을 특징으로 하는 콘크리트 구조물의 표면을 보수하는 방법.In the flocking step of the short fibers (S3), by blowing together the warm air of 70 to 80 ℃, to promote the curing and curing of the primer, characterized in that for repairing the surface of the concrete structure. 제 1항에 또는 제2항에 있어서,The method according to claim 1 or 2, 상기 단섬유(12)는, 나일론 스테이플섬유, 나일론 토우, 폐나일론 중에서 선택되어 사용됨을 특징으로 하는 콘크리트 구조물의 표면을 보수하는 방법.The short fiber (12), the method of repairing the surface of the concrete structure, characterized in that the selected from nylon staple fibers, nylon tow, waste nylon used. 제 1항에 또는 제2항에 있어서,The method according to claim 1 or 2, 상기 고정메시(14)는, 피이티(PET) 재질로, 굵기가 30 내지 300 데니어이고, 그 간격은 50 내지 200 메시로 형성함을 특징으로 하는 콘크리트 구조물의 표면을 보수하는 방법.The fixed mesh 14 is made of a PET material, the thickness is 30 to 300 denier, the spacing is a method for repairing the surface of the concrete structure, characterized in that formed by 50 to 200 mesh.
KR10-2005-0019083A 2005-03-08 2005-03-08 the surface repair method of concrete structure KR100500426B1 (en)