KR20040062200A - thin heatseal film for strengthening function of protective surface - Google Patents

thin heatseal film for strengthening function of protective surface Download PDF

Info

Publication number
KR20040062200A
KR20040062200A KR1020020088529A KR20020088529A KR20040062200A KR 20040062200 A KR20040062200 A KR 20040062200A KR 1020020088529 A KR1020020088529 A KR 1020020088529A KR 20020088529 A KR20020088529 A KR 20020088529A KR 20040062200 A KR20040062200 A KR 20040062200A
Authority
KR
South Korea
Prior art keywords
thin film
resin
functional thin
film
layer
Prior art date
Application number
KR1020020088529A
Other languages
Korean (ko)
Other versions
KR100450495B1 (en
Inventor
임승하
여상욱
Original Assignee
로얄소브린 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 로얄소브린 주식회사 filed Critical 로얄소브린 주식회사
Priority to KR10-2002-0088529A priority Critical patent/KR100450495B1/en
Priority to PCT/KR2003/002691 priority patent/WO2004058498A1/en
Priority to AU2003303341A priority patent/AU2003303341A1/en
Publication of KR20040062200A publication Critical patent/KR20040062200A/en
Application granted granted Critical
Publication of KR100450495B1 publication Critical patent/KR100450495B1/en

Abstract

PURPOSE: Provided is a thin heat seal film including a functional layer containing additives for reinforcing functions, which has improved anti-scratch property, solvent resistance, chemical resistance and water resistance of the laminated surface. CONSTITUTION: The thin laminating film for transferring a thin coating layer on a laminating sheet to a substrate to be laminated comprises: a base film(10) having releasability to be easily separated from the substrate after lamination; a functional thin film layer(20) disposed on the base film(10) and coated with a resin containing function-reinforcing additives; and an adhesive layer(30) coated with a heat sealable resin incorporated with a urethane resin and disposed on the functional thin film layer(20). After lamination, the edge of the laminated structure of the substrate is cut easily.

Description

기능성 박막 히트씰 필름{thin heatseal film for strengthening function of protective surface}Thin heatseal film for strengthening function of protective surface

본 발명은 박막 라미네이팅 필름에 관한 것으로서, 보다 상세하게는 이형성이 있는 베이스 필름 위에 수지 잉크로 코팅한 박막층을 카드, 문서 등 피착물의 표면으로 전이시키고 베이스 필름을 분리하여 수지 박막으로 피착물을 라미네이팅하는 박막 라미네이팅 필름에 관한 것이다.The present invention relates to a thin film laminating film, and more particularly, a thin film layer coated with a resin ink on a base film having releasability is transferred to a surface of an adherend such as a card or a document, and the base film is separated to laminate the adherend with a resin thin film. It relates to a thin film laminating film.

라미네이팅이란 문서, 광고물, 카드 등의 인쇄물 또는 광고물의 실사물의 내후성, 내구성 및 내광성 등의 외적 보호를 위해서 이들의 표면에 합성 수지 필름 등의 필름막을 입히는 것을 말한다.Laminating refers to coating a film film such as a synthetic resin film on the surface of the printed material such as documents, advertisements, cards, or the like for the weather protection, durability, and light resistance of real objects of the advertisements.

종래의 라미네이팅 방법으로서 폴리에칠렌, 폴리프로필렌, PVC등 폴리올레핀계 열가소성 합성 수지 필름 등으로 내용물의 보호를 위한 피착물의 양면에 융착시킨 후 일정크기로 내용물의 주연부에서 일정거리를 두고 필름을 절단하는 방법이 있다.As a conventional laminating method, there is a method of cutting a film at a predetermined distance from the periphery of the contents by fusing the both sides of the adherend for protecting the contents with a polyolefin-based thermoplastic synthetic resin film such as polyethylene, polypropylene, PVC, etc. .

그러나, 상기 합성 수지 필름은 그 두께 때문에 외관이 투박하고 합성 수지재의 소모량이 많으며, 피착물의 표면과 밀착성이 떨어져 들뜨거나 필름의 두께로 굴절되어 피착물 표면의 문자나 그림 등이 선명하게 보이지 않을 수 있고, 또한 라미네이팅이 끝난 후 피착물의 주연부에서 일정거리를 두고 일일이 재단해야 하는 단점이 있다.However, the synthetic resin film may be thin in appearance due to its thickness and consume a large amount of synthetic resin material, and may be inferior in adhesion to the surface of the adherend, or may be refracted by the thickness of the film, such that letters or pictures on the surface of the adherend may not be clearly seen. In addition, there is also a disadvantage that after a lamination is finished to cut at a certain distance from the periphery of the adherend.

또한 식품 포장 용기용 필름, 광고용 라미네이팅 필름에서와 같이 알루미늄 증착필름/폴리에칠렌수지, 폴리프로필렌필름/폴리에칠렌 수지, 폴리에스테르필름/폴리에칠렌수지/에칠비닐아세테이트수지 등과 같은 구성체로서 가공되기도 한다.It is also processed into a composition such as aluminum deposition film / polyethylene resin, polypropylene film / polyethylene resin, polyester film / polyethylene resin / ethylvinylacetate resin and the like as in food packaging container films and commercial laminating films.

이들은 내수성, 내기공성, 내구성 등의 요건을 충족시키기 위하여 수지피막 자체가 강건한 원단을 사용하기 때문에 대부분 기 성형된 필름에 티-다이 방식 또는 드라이 라미네이션 등의 압출 방식으로 핫멜트 접착제 층을 입혀 사용하므로, 원단이 저 미트론의 두께를 갖더라도 제 물성자체가 강하여, 히트씰 방식으로 라미네이팅 하고 나면 컷터 등의 도구를 이용해서 피착체 여면을 재단하지 않으면 안된다.In order to meet the requirements of water resistance, porosity, durability, etc., since the resin film itself is made of a strong fabric, most of the preformed films are coated with a hot melt adhesive layer by an extrusion method such as a tee-die method or dry lamination. Even if the fabric has a low micron thickness, the material itself is strong, and after laminating in a heat seal method, the surface of the adherend must be cut using a tool such as a cutter.

또한 합성 수지 용액으로 피착물을 로울러 코팅한 후 건조시키는 방법이 있는데, 이 방법에 사용되는 합성 수지 용액은 유기 용매에 합성 수지를 용해시킨 것이므로 피착물이 인쇄된 문자나 그림 등인 경우에는 인쇄 잉크가 유기 용매에 접촉되어 인쇄물이 번져 보일 수 있고, 유기 용매의 증발로 인체에 유해한 가스가 발생하는 등의 문제점이 있었다.In addition, there is a method of roller coating the adherend with a synthetic resin solution and then drying. The synthetic resin solution used in this method is a synthetic resin dissolved in an organic solvent. The printed matter may be smeared by contact with the organic solvent, and there may be problems such as generation of harmful gases to the human body by evaporation of the organic solvent.

한국 특허 출원 10-1998-2504호의 라미네이팅 방법은 상기한 문제점을 극복하기 위하여, 폴리에치렌을 유기 용매에 용해시킨 폴리에치렌 용액으로 이형 처리된 종이 및 합성 수지 필름 또는 이형성을 갖는 합성 수지 필름 면에 라미네이팅한 후 건조 과정을 통해 이형면상의 코팅 피막의 유기 용매를 완전히 증발시킨 라미네이팅 시트로서 인쇄된 피착물에 라미네이팅함으로써 상기 라미네이팅 시트의 폴리에치렌 코팅 피막(박막)층을 피착물 표면에 전이시키는 방법을 제안하고 있으나, 라미네이팅된 표면이 열에 약하고 방수성, 내용제성이 부족하며, 표면에 얼룩이 지거나 박막층이 부서지기 쉽고, 피착제와 박막의 접착력도 약한 결점이 있다.In order to overcome the above problems, the laminating method of Korean Patent Application No. 10-1998-2504, a paper and a synthetic resin film or a synthetic resin film surface having a mold release property with a polyethylene solution in which polyethylene was dissolved in an organic solvent. After laminating to a laminate, the organic solvent of the coating film on the heteromorphic surface is completely evaporated through lamination to the printed material as a laminating sheet, thereby transferring the polyethylene coating layer (thin film) layer of the laminating sheet to the surface of the adherend. Although the method is proposed, the laminated surface is weak in heat, lacks in water resistance and solvent resistance, and the surface is easily stained or the thin film layer is brittle, and the adhesion between the adhesive and the thin film is weak.

또한 상기 방법에 의한 박막 필름을 사용할 경우, 피착물의 주연부를 재단할 필요는 없으나 피착물의 각 주연부보다 5mm~10mm정도의 여유를 갖는 라미네이팅 시트를 사용하여야 하고, 여면의 접착층을 받는 배면지를 필요로하는 번거로움이 있다.In addition, when using the thin film according to the above method, it is not necessary to cut the periphery of the adherend, but it is necessary to use a laminating sheet having a margin of about 5 mm to 10 mm than each periphery of the adherend, and a backing paper receiving the adhesive layer of the surface is required. There is a hassle.

이에 본 발명은 상기한 바와 같은 종래의 제반 문제점을 해소하기 위하여 안출한 것으로서, 기능 강화용 첨가제를 포함하는 기능층을 포함하여 박막임에도 불구하고 라미네이팅된 표면의 내스크래치성, 내용제성, 내약품성, 내수성 등의 기능을 강화하는 박막 라미네이팅 필름을 제공하는 것을 목적으로 한다.Accordingly, the present invention has been made in order to solve the above-mentioned conventional problems, and scratches, solvent resistance, chemical resistance, and the like of the laminated surface despite the thin film including a functional layer containing a functional enhancement additive An object of the present invention is to provide a thin film laminating film that enhances functions such as water resistance.

또한 라미네이팅된 피착체 면과 박막 필름의 미피착 여면의 경계 부분이 쉽게 끊겨서 별도의 재단이 필요하지 않고, 피착체 면을 분리하기 위한 인장력만으로 용이하게 라미네이팅된 피착체와 분리되는 박막 라미네이팅 필름을 제공하는 것을 목적으로 한다.In addition, the boundary between the laminated surface and the non-deposited surface of the thin film is easily broken so that no additional cutting is required, and the thin film laminating film is easily separated from the laminated substrate simply by a tension force for separating the adherend surface. It aims to do it.

또한 핫멜트성 접착층을 포함하여 박막 라미네이팅 필름과 피착체의 접착력을 강화하고 라미네이팅 후에 표면에 공기 층이 형성되거나 얼룩이 지는 현상을 방지하는 박막 라미네이팅 필름을 제공하는 것을 목적으로 한다.In addition, an object of the present invention is to provide a thin film laminating film including a hot melt adhesive layer to strengthen the adhesion between the thin film laminating film and the adherend and to prevent an air layer from forming or staining on the surface after laminating.

도 1 은 본 발명에 따른 기능성 박막 라미네이팅 필름의 단면을 나타내는 도면이다.1 is a view showing a cross section of a functional thin film laminating film according to the present invention.

도 2 는 본 발명에 따른 기능성 박막 라미네이팅 필름의 사용 상태를 나타내는 도면이다.2 is a view showing a state of use of the functional thin film laminating film according to the present invention.

<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>

10 : 베이스 필름 20 : 기능성 박막층10: base film 20: functional thin film layer

30 : 접착층 40 : 피착물30: adhesive layer 40: adherend

50 : 피착 여면의 단재 부분50: cutting part of the deposition surface

상기와 같은 목적을 달성하기 위해서, 본 발명에 따른 기능성 박막 라미네이팅 필름은 라미네이팅 시트 위의 코팅 박막 층을 피착물 표면으로 전이하는 방식으로 피착물을 라미네이팅하는 박막 라미네이팅 필름에 있어서 라미네이팅 후 피착물과 용이하게 분리되도록 하기 위한 이형성이 있는 베이스 필름과, 상기 베이스 필름의 상층으로 기능 강화를 위한 첨가제를 포함하는 수지로 코팅된 기능성 박막 층과, 상기 기능성 박막층의 상층으로 우레탄계 수지를 첨가한 히트씰성 수지로 코팅된 접착층을 포함하여 라미네이팅 된 피착체의 가장자리가 용이하게 절단되는 것을 특징으로 한다.In order to achieve the above object, the functional thin film laminating film according to the present invention in the thin film laminating film for laminating the adherend in such a manner as to transfer the coating thin film layer on the laminating sheet to the surface of the adherend, after the lamination and easy to adhere With a base film having a releasability to be separated easily, a functional thin film layer coated with a resin containing an additive for enhancing the function to the upper layer of the base film, and a heat sealable resin to which a urethane-based resin is added to the upper layer of the functional thin film layer Including the coated adhesive layer is characterized in that the edge of the laminated adherend is easily cut.

또한 상기 목적을 달성하기 위하여 본 발명에 따른 기능성 박막 라미네이팅 필름의 접착층은 공중합 폴리에스텔 수지와 로진 변형 페놀릭 수지를 그래프트 결합시킨후 우레탄계 수지를 첨가한 히트씰성 수지 또는 초산비닐아세테이트 수지에 테키화이어로 로진을 첨가 반응시킨 후 우레탄계 수지를 첨가한 히트씰성 수지로 코팅하는 것을 특징으로 한다.In addition, in order to achieve the above object, the adhesive layer of the functional thin film laminating film according to the present invention graft-bonds a copolyester polyester resin and a rosin-modified phenolic resin and then adds urethane-based heat sealable resin or vinyl acetate resin to Tekifizer. After the addition of the rosin, the reaction is characterized by coating with a heat sealable resin to which the urethane-based resin is added.

또한 상기 목적을 달성하기 위하여 본 발명에 따른 기능성 박막 라미네이팅 필름은 내스크래치성 및 내약품성을 보강하기 위한 왁스 또는 실리콘 오일 및 열경화 촉진제의 혼합물과, 특수 보안요소를 부여하기 위한 가시 또는 비가시 형광안료/염료 또는 축광안료와, 약품변색성을 발현하기 위한 특수약제, 그밖에 펄 안료계, 전도성 재료 또는 UV 차단제등을 단독 또는 혼가하여 보호하고자 하는 피착물에 라미네이팅된 표면의 기능을 강화하는 것을 특징으로 한다.In addition, in order to achieve the above object, the functional thin film laminating film according to the present invention is a mixture of wax or silicone oil and heat curing accelerator to enhance scratch resistance and chemical resistance, and visible or invisible fluorescence to impart a special security element. Enhances the function of the surface laminated to the pigment / dye or phosphorescent pigment, and special chemicals for expressing chemical discoloration, other pearl pigments, conductive materials or UV blocking agents alone or in combination. It is done.

이하 도면을 참조하여, 본 발명에 따른 기능 강화성 박막 라미네이팅 필름에 대하여 상세히 살펴보기로 한다.With reference to the drawings, it will be described in detail with respect to the function-enhancing thin film laminating film according to the present invention.

도 1 에 도시된 바와 같이 본 발명에 따른 기능성 박막 라미네이팅 필름은 베이스 필름(10)과, 베이스 필름(10)위로 피착물 표면의 기능을 강화하기 위하여 첨가제를 혼합한 수지로 코팅된 기능성 박막층(20)이 있고, 기능성 박막층(20)위로 접착층(30)이 코팅되어 있다. 도 2 에서와 같이 접착층(30)이 라미네이팅 방법으로서 보호하고자 하는 피착물(40)에 맞닿도록 하고, 베이스 필름(10)과 함께 핫 라미네이터기를 통과시킨 후 피착물(40)을 베이스 필름(10)으로 부터 떼어내면 접착층(30) 및 기능성 박막층(20)이 깨끗하게 단재되어 피착물을 라미네이팅 할 수 있다.As shown in FIG. 1, the functional thin film laminating film according to the present invention includes a base film 10 and a functional thin film layer 20 coated with a resin mixed with additives to enhance the function of the surface of the adherend onto the base film 10. ), And the adhesive layer 30 is coated on the functional thin film layer 20. As shown in FIG. 2, the adhesive layer 30 abuts the adherend 40 to be protected as a laminating method, passes through the hot laminator together with the base film 10, and then attaches the adherent 40 to the base film 10. When it is removed from the adhesive layer 30 and the functional thin film layer 20 is cleanly cut can be laminated to the adherend.

베이스 필름(10)은 표면 소재인 1차 기능성 박막 수지의 조성에 따라 박리성을 부여하기 위하여 이형제를 처리한 종이(박리지)나 고분자 합성 수지 필름 또는 이형제를 처리하지 않은 고분자 합성 수지 필름을 사용할 수 있다. 이때 베이스 필름의 두께는 11 내지 15 미크론의 두께가 적당하다.The base film 10 may be a paper (peel release) treated with a release agent or a polymer synthetic resin film or a polymer synthetic resin film not treated with a release agent in order to provide peelability according to the composition of the primary functional thin film resin, which is a surface material. Can be. At this time, the thickness of the base film is suitable for the thickness of 11 to 15 microns.

기능성 박막층(20)은 박막층을 형성하는 수지와, 얇은 박막의 기능을 강화하기 위한 첨가제를 포함한다. 이때 기능성 박막층을 형성하는 수지의 조성은 다음의 조건을 충족시켜야 한다.The functional thin film layer 20 includes a resin forming a thin film layer and an additive for enhancing the function of the thin film. At this time, the composition of the resin forming the functional thin film layer should satisfy the following conditions.

첫째, 본 발명에 사용되는 수지는 여러 종류의 기능성 첨가제의 혼화시 이를 수용할 수 있어야 한다. 수지막 자체가 기본적으로 일정 수준의 내용제성, 내수성, 방수성 등의 특성을 갖지만, 종래 기술의 문제점으로 지적되던 라미네이팅 된 박막표면의 내열성, 방수성, 내용제성 등의 부족을 해결하기 위하여 본 발명에 따른 라미네이팅 필름은 기능 강화를 위한 첨가제를 혼화하는 것을 특징으로 하기 때문에 박막의 기재인 수지는 여러 가지 첨가제를 혼화할 때 이를 수용할 수 있어야 한다.First, the resin used in the present invention should be able to accommodate it when admixing various types of functional additives. The resin film itself basically has a certain level of solvent resistance, water resistance, water resistance, etc., but in order to solve the lack of heat resistance, water resistance, solvent resistance, etc. of the laminated thin film surface pointed out as a problem of the prior art Since the laminating film is characterized by admixing an additive for enhancing the function, the resin, which is a base material of the thin film, should be able to accommodate it when admixing various additives.

상기 사항을 충족하기 위하여, 폴리비닐 및 아크릴수지의 중합체, 우레탄수지 및 아크릴수지의 중합체 또는 폴리에스텔 및 변성 아크릴의 중합체 등을 사용할 수 있다.In order to satisfy the above matters, polymers of polyvinyl and acrylic resins, polymers of urethane resins and acrylic resins, or polymers of polyester and modified acrylics can be used.

둘째, 본 발명에 사용되는 수지는 라미네이팅 완료 후에 기능성 박막층(20)과 접착층(30)의 박리 분리가 없어야 하므로 2차 박막인 접착제 재질과의 강한 접착친화력(Bonding strength)이 요구된다. 이를 위하여 우레탄계 수지, 폴리에스텔계 수지, 비닐계 수지, 아크릴계 수지 또는 이들 혼합 수지를 중합하여 만든 중합형 고분자상의 수지, 메라민수지 또는 UV경화형 수지를 사용할 수 있다.Second, since the resin used in the present invention should not be separated from the functional thin film layer 20 and the adhesive layer 30 after the lamination is completed, a strong bonding affinity with the adhesive material, which is the secondary thin film, is required. For this purpose, a urethane-based resin, a polyester-based resin, a vinyl-based resin, an acrylic resin, or a polymerized polymer resin, a melamine resin or a UV-curable resin made by polymerizing these mixed resins can be used.

셋째, 기능성 박막층(20)과 접착층(30)이 합쳐진 상태에서도 라미네이팅 접착면과 여면의 접점에서 Z방향으로 쉽게 커팅(단재)되기 위한 조성 조건을 갖추어야 한다.Third, even when the functional thin film layer 20 and the adhesive layer 30 are combined, the composition conditions for easy cutting (cutting) in the Z direction at the contact point of the laminating adhesive surface and the surface should be provided.

그리고, 본 발명에 따른 기능성 라미네이팅 필름은 기재인 수지 외에 첨가제를 첨가하여 보호하고자 하는 피착물에 라미네이팅된 표면의 기능을 강화하는 것을 특징으로 한다. 본 발명에 사용되는 첨가제로는 내스크래치성 및 내약품성을 강화하기 위한 왁스 또는 실리콘 오일 및 열경화 촉진제의 혼합물과, 특수 보안 요소를 부여하기 위한 가시 또는 비가시 형광 안료/염료 또는 축광 안료와, 약품 변색성을 발현하기 위한 특수 약제, 그 밖에 펄 안료계, 전도성 재료 또는 UV 차단제 등을 단독 또는 혼화하여 첨가 할 수 있다.In addition, the functional laminating film according to the present invention is characterized by reinforcing the function of the laminated surface on the adherend to be protected by adding an additive in addition to the resin as the base material. Additives used in the present invention include a mixture of waxes or silicone oils and thermosetting accelerators to enhance scratch and chemical resistance, visible or invisible fluorescent pigments / dyes or photoluminescent pigments to impart special security elements, Special agents for expressing chemical discoloration, in addition to pearl pigments, conductive materials or UV blockers may be added alone or in admixture.

접착층(30)은 상기 기능성 박막층(20)위에 히트씰성 수지로 코팅하여 형성하며, 기능성 박막층(20)과 피착체(40) 사이의 접착력을 강화하고, 열 융착함으로써 라미네이팅 후에 피착물의 표면에 공기 층이 형성되거나 얼룩이 지는 현상을 방지할 수 있다.The adhesive layer 30 is formed by coating a heat sealable resin on the functional thin film layer 20, and strengthens the adhesive force between the functional thin film layer 20 and the adherend 40 and heat-bonds the air layer on the surface of the adherend after laminating. This can prevent the formation or staining phenomenon.

일반적으로 사용되는 히트씰성 핫멜트 수지는 에칠비닐아세테이트, 메칠메타크릴레이트, 저 분자량의 폴리에칠렌, 폴리에스테르, 폴리프로필렌 등으로, 티-다이 압출 또는 드라이 라미네이션 방법으로 코팅하여 접착 층을 형성한다.Commonly used heat sealable hot melt resins are ethyl vinyl acetate, methyl methacrylate, low molecular weight polyethylene, polyester, polypropylene, and the like, and are coated by a T-die extrusion or dry lamination method to form an adhesive layer.

드라이 라미네이션 방법에 의할 경우에는 테키화이어(tackifier)로 로진, 로진 유도체나 테르펜 (Terpens)중합체, 석유계 하이드로 카본 수지, 페놀릭 수지 등을 섞어서 사용하기도 한다. 에칠비닐아세테이트 수지 100에 대하여 로진 폴리에스텔 25-125, 석유계왁스 40-120을 혼합하거나, 페놀릭 수지를 네오프렌이나 니트릴에 접촉 접착제로 사용하는 것이 그 예이다. 이 경우 젖음성과 접착성이 증진되는 장점이 있다.In the case of a dry lamination method, a roche, a rosin derivative, a terpens polymer, a petroleum-based hydrocarbon resin, a phenolic resin, etc. may be used as a tackifier. For example, rosin polyester 25-125 and petroleum wax 40-120 are mixed with ethylene vinyl acetate resin 100, or phenolic resin is used as a contact adhesive to neoprene or nitrile. In this case, there is an advantage that the wettability and adhesion are enhanced.

특히 본 발명은 라미네이팅 후에 칼이나 컷터 등을 사용하지 않고, 피착체를 베이스 필름으로부터 떼어내기만 해도 쉽게 박막층이 단재되도록 하기 위하여, 접착층에 히트씰성 합성수지 이외에 우레탄 수지를 혼가한다. 상대적으로 고분자인 우레탄 수지는 히트씰성 수지의 중합 체인(chain) 사이에 약하게 분자결합하므로, 힘이 가해지면 피착체 주연부의 강한 Z 강도로 인해 쉽게 분자간 결합이 절단되므로 접착층의 X방향 인열강도를 인위적으로 낮출 수 있다.In particular, the present invention is mixed with a urethane resin in addition to the heat sealable synthetic resin in the adhesive layer in order to make the thin film layer easily cut off without using a knife or a cutter, etc. after lamination, and simply removing the adherend from the base film. Relatively high molecular weight urethane resins are weakly molecularly bonded between the polymer chains of heat sealable resins, so that the intermolecular bonds are easily broken due to the strong Z strength at the periphery of the adherend. It can be artificially lowered.

이는 열을 가하여, 원하는 문자나 패턴에만 금박 등이 코팅되도록 하는 스탬핑 호일과 기본 원리가 유사하다고 볼 수 있다. 즉, 스탬핑 호일은 알루미늄 증착 면에 히트씰성 수지를 드라이라미네이션 방식으로 코팅한 것으로, 증착된 알루미늄 입자의 X,Y 결합력이 현저히 낮기 때문에 열융착 된 접착 수지가 문자나 패턴 등의 잉크 위에 열 전사될 때, 문자나 패턴 위에만 알루미늄 증착 입자가 피착체에 부착되는 원리이다.It can be seen that the basic principle is similar to a stamping foil that heat is applied so that only gold or the like is coated on a desired letter or pattern. In other words, the stamping foil is a dry lamination method of heat-sealing resin on the aluminum deposition surface. Since the X and Y bonding strength of the deposited aluminum particles is remarkably low, the heat-bonded adhesive resin is thermally transferred onto the ink such as letters or patterns. In this case, the aluminum deposition particles are attached to the adherend only on letters or patterns.

그러나, 합성 수지계의 박막 필름상의 X 결합력을 인위적으로 낮추기 위하여, 히트씰성 수지와 대립되는 성질의 수지를 혼가하는 화학적 방법을 채택한 본 발명과는 상당한 기술적 차이가 존재한다.However, in order to artificially lower the X bonding force on the synthetic resin thin film, there is a considerable technical difference from the present invention in which the chemical method of mixing a resin having a property opposite to the heat sealable resin is adopted.

상기한 사항을 고려하면, 접착층을 형성하는 히트씰성 수지는 공중합 폴리에스텔 수지와 테키화이어로 로진 변형 페놀릭 수지를 혼가하고, 우레탄 수지를 브랜딩하여 사용하는 것이 바람직하다.In view of the above, the heat-sealing resin for forming the adhesive layer is preferably mixed with a copolyester-polyester resin and a rosin-modified phenolic resin with tekifier and branded a urethane resin.

이때, 초산 비닐 아세테이트 수지에 테키화이어로 로진계를 혼가하고, 우레탄 수지로 브랜딩하여 동일한 효과를 얻을 수 있다.At this time, the rosin system is mixed with vinyl acetate in tekifizer, and the same effect may be obtained by branding with a urethane resin.

한편 본 발명에 따른 기능성 박막 라미네이팅 필름의 제조공정을 간단하게 살펴보면 다음과 같다.Meanwhile, the manufacturing process of the functional thin film laminating film according to the present invention will be briefly described as follows.

베이스 필름 위에 마이크로 그라비아롤 코팅, 키스롤 코팅, 콤마코터 코팅, 리버스롤 코팅, 나이프 코팅 방법 등에 의하여, 기능성 박막 층을 1 내지 5 미크론의 두께로 코팅한다. 2 차 접착층은 기능성 박막층과의 접착친화성을 고려하여 적정한 용제와 희석률로 코터 적성에 맞는 점도로 조정하여 기능성 박막층 위에 4 내지 10 미크론의 두께로 코팅한다. 이때 접착층의 고른 두께 면을 위하여는 마이크로 그라비아나 콤머코터 방법에 의하는 것이 바람직하다. 특히 라미네이팅 후의 단재효과를 위하여 기능성 박막층은 3 내지 5 미크론의 두께로, 접착층은 5 내지 7 미크론의 두께가 바람직하다.The functional thin film layer is coated to a thickness of 1 to 5 microns on the base film by micro gravure roll coating, kiss roll coating, comma coater coating, reverse roll coating, knife coating method and the like. The secondary adhesive layer is coated with a thickness of 4 to 10 microns on the functional thin film layer by adjusting the viscosity to suit the coater aptitude at an appropriate solvent and dilution rate in consideration of the adhesion affinity with the functional thin film layer. At this time, for an even thickness surface of the adhesive layer is preferably by a micro gravure or comb coater method. In particular, for the effect of cutting after lamination, the functional thin film layer is preferably 3 to 5 microns thick, and the adhesive layer is preferably 5 to 7 microns thick.

이하 본 발명의 바람직한 실시예를 살펴보기로 한다.Hereinafter, a preferred embodiment of the present invention will be described.

<실시예 1><Example 1>

우레탄 수지계 85%, 아크릴수지계 5%, 미량의 첨가제(촉매제, 경화제 등)를 그래프트 중합하고, 기능 강화를 위한 첨가제를 혼가하여 만든 유성 잉크를 폴리에스텔필름위에 5 미크론의 두께로 도포하여 기능성 박막층을 형성한다. 건조된 기능성 박막층 위에 공중합 폴리에스텔 수지, 적량의 로진계 테키파이, 우레탄 수지를 혼합한 히트씰성 접착제를 7 미크론의 두께로 코팅하여 건조한다.Graft polymerization of 85% urethane resin, 5% acrylic resin, and small amounts of additives (catalysts, curing agents, etc.), and oil-based inks mixed with additives for enhancing the function to a thickness of 5 microns on the polyester film to form a functional thin film layer Form. On the dried functional thin film layer, a heat seal adhesive mixed with a copolymerized polyester resin, an appropriate amount of rosin-based tequipy, and a urethane resin is coated with a thickness of 7 microns and dried.

이때 기능 강화를 위한 첨가제로서 비가시형광 안료, 투명 유기 전도성제, 용제변색형/열변색형 변색제, 유색염료, 비가시 형광안료 및 UV차단제의 혼합물, 투명 유기전도성제 및 UV차단제의 혼합물, 실리콘 오일 및 열경화 촉진제의 혼합물중 어느 하나를 선택할 수 있다.In this case, as an additive for enhancing the function, an invisible fluorescent pigment, a transparent organic conductive agent, a solvent-chromic / thermochromic color changing agent, a color dye, a mixture of an invisible fluorescent pigment and a UV blocking agent, a mixture of a transparent organic conductive agent and a UV blocking agent, Either mixture of silicone oils and thermoset accelerators can be selected.

<실시예 2><Example 2>

우레탄 수지계 10%, 아크릴수지계 60%, 미량의 첨가제(촉매제, 경화제 등)를 그래프트 중합하고, 기능 강화를 위한 첨가제를 혼가하여 만든 유성 잉크를 폴리에스텔필름위에 5 미크론의 두께로 도포하여 기능성 박막층을 형성한다. 건조된 기능성 박막층 위에 공중합 폴리에스텔 수지, 적량의 로진계 테키파이, 우레탄 수지를 혼합한 히트씰성 접착제를 7 미크론의 두께로 코팅하여 건조한다.Graft polymerization of 10% urethane resin, 60% acrylic resin, and small amounts of additives (catalysts, curing agents, etc.) and a thin film of 5 microns on a polyester film are applied to the oil-based ink mixed with additives for enhancing the function. Form. On the dried functional thin film layer, a heat seal adhesive mixed with a copolymerized polyester resin, an appropriate amount of rosin-based tequipy, and a urethane resin is coated with a thickness of 7 microns and dried.

이때 기능 강화를 위한 첨가제로서 비가시형광 안료, 투명 유기 전도성제,용제변색형/열변색형 변색제, 유색염료, 비가시 형광안료 및 UV차단제의 혼합물, 투명 유기전도성제 및 UV차단제의 혼합물, 실리콘 오일 및 열경화 촉진제의 혼합물중 어느 하나를 선택할 수 있다.In this case, as an additive for enhancing the function, an invisible fluorescent pigment, a transparent organic conductive agent, a solvent discoloration type / thermochromic color changing agent, a color dye, a mixture of an invisible fluorescent pigment and a UV blocking agent, a mixture of a transparent organic conductive agent and a UV blocking agent, Either mixture of silicone oils and thermoset accelerators can be selected.

<실시예 3><Example 3>

우레탄 수지계 10%, 아크릴수지계 60%, 미량의 첨가제(촉매제, 경화제 등)를 그래프트 중합하고, 기능 강화를 위한 첨가제를 혼가하여 만든 유성 잉크를 폴리에스텔필름위에 5 미크론의 두께로 도포하여 기능성 박막층을 형성한다. 건조된 기능성 박막층 위에 변성 폴리에칠렌아세테이트 수지에 적량의 로진계 테키파이와 우레탄수지를 혼합한 히트씰성 접착제를 7 미크론의 두께로 코팅하여 건조한다.Graft polymerization of 10% urethane resin, 60% acrylic resin, and small amounts of additives (catalysts, curing agents, etc.) and a thin film of 5 microns on a polyester film are applied to the oil-based ink mixed with additives for enhancing the function. Form. On the dried functional thin film layer, a heat-seal adhesive mixed with a modified rosin-based tequipy and urethane resin in a modified polyethylene acetate resin is coated with a thickness of 7 microns and dried.

이때 기능 강화를 위한 첨가제로서 비가시형광 안료, 투명 유기 전도성제, 용제변색형/열변색형 변색제, 유색염료, 비가시 형광안료 및 UV차단제의 혼합물, 투명 유기전도성제 및 UV차단제의 혼합물, 실리콘 오일 및 열경화 촉진제의 혼합물중 어느 하나를 선택할 수 있다.In this case, as an additive for enhancing the function, an invisible fluorescent pigment, a transparent organic conductive agent, a solvent-chromic / thermochromic color changing agent, a color dye, a mixture of an invisible fluorescent pigment and a UV blocking agent, a mixture of a transparent organic conductive agent and a UV blocking agent, Either mixture of silicone oils and thermoset accelerators can be selected.

<실시예 4><Example 4>

폴리비닐수지계 10%, 아크릴수지계 20%, 미량의 첨가제(촉매제, 경화제 등)를 그래프트 중합하고, 기능 강화를 위한 첨가제를 혼가하여 만든 유성 잉크를 폴리에스텔필름위에 5 미크론의 두께로 도포하여 기능성 박막층을 형성한다. 건조된 기능성 박막층 위에 변성 폴리에칠렌아세테이트 수지에 적량의 페놀계 테키파이와우레탄수지를 혼합한 히트씰성 접착제를 7 미크론의 두께로 코팅하여 건조한다.Functional thin layer by graft polymerization of 10% polyvinyl resin, 20% acrylic resin, and small amount of additives (catalyst, hardener, etc.) and oil-based ink mixed with additives for enhancing function to a thickness of 5 microns on polyester film To form. On the dried functional thin film layer, a heat-seal adhesive mixed with a modified phenolic acetate resin and an appropriate amount of phenolic tekipy and urethane resin is coated with a thickness of 7 microns and dried.

이때 기능 강화를 위한 첨가제로서 비가시형광 안료, 투명 유기 전도성제, 용제변색형/열변색형 변색제, 유색염료, 비가시 형광안료 및 UV차단제의 혼합물, 투명 유기전도성제 및 UV차단제의 혼합물, 실리콘 오일 및 열경화 촉진제의 혼합물중 어느 하나를 선택할 수 있다.In this case, as an additive for enhancing the function, an invisible fluorescent pigment, a transparent organic conductive agent, a solvent-chromic / thermochromic color changing agent, a color dye, a mixture of an invisible fluorescent pigment and a UV blocking agent, a mixture of a transparent organic conductive agent and a UV blocking agent, Either mixture of silicone oils and thermoset accelerators can be selected.

<실시예 5>Example 5

폴리비닐수지계 10%, 폴리에스텔수지계 30%, 미량의 첨가제(촉매제, 경화제 등)를 그래프트 중합하고, 기능 강화를 위한 첨가제를 혼가하여 만든 유성 잉크를 폴리에스텔필름위에 5 미크론의 두께로 도포하여 기능성 박막층을 형성한다. 건조된 기능성 박막층 위에 변성 폴리에칠렌아세테이트 수지에 적량의 페놀계 테키파이와 우레탄수지를 혼합한 히트씰성 접착제를 7 미크론의 두께로 코팅하여 건조한다.Graft polymerization of 10% polyvinyl resin, 30% polyester resin, and small amounts of additives (catalyst, hardener, etc.), and oil-based ink mixed with additives for enhancing the function is applied on the polyester film to a thickness of 5 microns. A thin film layer is formed. On the dried functional thin film layer, a heat-seal adhesive mixed with an appropriate amount of a phenolic tequipy and a urethane resin in a modified polyethylene acetate resin is coated with a thickness of 7 microns and dried.

이때 기능 강화를 위한 첨가제로서 비가시형광 안료, 투명 유기 전도성제, 용제변색형/열변색형 변색제, 유색염료, 비가시 형광안료 및 UV차단제의 혼합물, 투명 유기전도성제 및 UV차단제의 혼합물, 실리콘 오일 및 열경화 촉진제의 혼합물중 어느 하나를 선택할 수 있다.In this case, as an additive for enhancing the function, an invisible fluorescent pigment, a transparent organic conductive agent, a solvent-chromic / thermochromic color changing agent, a color dye, a mixture of an invisible fluorescent pigment and a UV blocking agent, a mixture of a transparent organic conductive agent and a UV blocking agent, Either mixture of silicone oils and thermoset accelerators can be selected.

< 피막제의 조성 및 기능강화를 위한 첨가제의 실시예><Examples of Additives for Enhancing Composition and Function of Coating Agent>

기능성박막층 피막제의 조성Composition of Functional Thin Film Coating Agent 기능 강화를 위한 첨가제Additives for enhanced function 접착층피막제의 조성Composition of adhesive layer coating 우레탄수지계85%, 아크릴수지계5%85% of urethane resin systems, acrylic resin systems 5% 비가시형광안료(UV차단제)Invisible Fluorescent Pigment (UV Blocker) 공중합 폴리에스텔수지, 로진계테키파이,우레탄계수지Copolymer polyester resin, rosin-based tequipy, urethane resin 우레탄수지계10%, 아크릴수지계 60%10% of urethane resin systems, acrylic resin 60% 투명유기전도성제(UV차단제Transparent organic conductive agent (UV blocking agent 폴리비닐수지계10%, 아크릴수지계20%10% of polyvinyl resins, 20% of acrylic resins 용제변색형/열변색형변색제Solvent discoloration / thermochromic 변성폴리에칠렌아세테이트수지,페놀계테키파이,우레탄계수지Modified Polyethylene Acetate Resin, Phenolic Tequipy, Urethane Resin 폴리비닐수지계10%,폴리에스텔수지계30%10% of polyvinyl resin, 30% of polyester resin 유색염료Colored dyes

상술한 바와 같이 본 발명에 따른 기능성 박막 라미네이팅 필름은 박막임에도 불구하고, 기능강화를 위한 첨가제를 혼합함으로써 흠집이나 약품, 습기, 열, 자외선 등으로부터 피착물을 보호하는 기능을 강화하는 효과가 있다. 특히 박막체이고 접착성을 갖기 때문에 여러 겹을 중첩하여 쓸 경우 층별 보안 요소를 부여하면 더욱 견고한 보안기능을 가질 수 있는 장점이 있다.As described above, although the functional thin film laminating film according to the present invention is a thin film, there is an effect of enhancing the function of protecting the adherend from scratches, chemicals, moisture, heat, ultraviolet rays, etc. by mixing an additive for enhancing the function. In particular, since it is a thin film and has an adhesive property, it is advantageous to have a more robust security function if a layered security element is used when several layers are overlapped.

또한, 라미네이팅된 피착체 면과 박막 필름의 미피착 여면의 경계부분이 쉽게 끊겨서 별도의 재단이 필요하지 않고, 피착체면을 분리하기 위한 인장력만으로도 쉽게 라미네이팅 피착체와 분리할 수 있는 효과가 있다.In addition, the boundary between the laminated adherend surface and the non-deposition surface of the thin film is easily broken, so that no separate cutting is required, and there is an effect that can be easily separated from the laminated adherend only by a tension force for separating the adherend surface.

또한, 박막의 유연한 피막층을 가지므로, 라미네이팅 후에도 피착체의 질감과 대등하고, 피착체가 종이인 경우에는 라미네이팅 필름막도 함께 찢어질 수 있는 친환경적 효과가 있고, 일반 라미네이터기를 이용할 수 있기 때문에 작업성이 좋다.In addition, since the film has a thin flexible film layer, it is equivalent to the texture of the adherend even after laminating, and if the adherend is paper, the laminating film layer can also be torn together, and workability is good because ordinary laminators can be used. .

Claims (12)

라미네이팅 쉬트 위의 코팅 박막 층을 피착물 표면으로 전이하는 방식으로 피착물을 라미네이팅 하는 박막 라미네이팅 필름에 있어서,A thin film laminating film for laminating an adherend in such a manner as to transfer a coating thin film layer on a laminating sheet to the surface of the adherend, 라미네이팅 후 피착물과 용이하게 분리되도록 하기 위한 이형성이 있는 베이스필름과; 상기 베이스 필름의 상층으로 기능 강화를 위한 첨가제를 포함하는 수지로 코팅된 기능성 박막층과; 상기 기능성 박막층의 상층으로 우레탄계 수지를 첨가한 히트씰성 수지로 코팅된 접착층을 포함하여,A base film having releasability for easy separation from the adherend after lamination; A functional thin film layer coated with a resin including an additive for enhancing a function as an upper layer of the base film; Including an adhesive layer coated with a heat sealable resin to which a urethane-based resin is added to the upper layer of the functional thin film layer, 피착체 라미네이팅물의 가장자리가 용이하게 절단되는 것을 특징으로 하는 기능성 박막 라미네이팅 필름Functional thin film laminating film, characterized in that the edge of the adherend laminate is easily cut 제 1 항에 있어서 상기 접착층은,The method of claim 1, wherein the adhesive layer, 공중합 폴리에스텔 수지와 로진 변형 페놀릭 수지를 그래프트 결합시킨 후 우레탄계 수지를 첨가한 히트씰성 수지로 코팅되어 피착체 라미네이팅물의 가장자리가 용이하게 절단되는 것을 특징으로 하는 기능성 박막 라미네이팅 필름Functional graft laminating film characterized in that the edge of the adherend laminate is easily cut by graft bonding the copolyester polyester resin and the rosin modified phenolic resin and then coated with a heat sealable resin containing a urethane resin. 제 1 항에 있어서 상기 접착층은,The method of claim 1, wherein the adhesive layer, 초산비닐아세테이트 수지에 테키화이어로 로진을 첨가 반응시킨 후 우레탄계수지를 첨가한 히트씰성 수지로 코팅되어 피막체 라미네이팅물의 가장자리가 용이하게 절단되는 것을 특징으로 하는 기능성 박막 라미네이팅 필름Functional thin film laminating film, characterized in that the edge of the film laminate is easily cut by coating with a heat sealable resin containing urethane resin after adding rosin to vinyl acetate acetate and reacting with rosin. 제 2 내지 3 항에 있어서 상기 접착층은,The method of claim 2, wherein the adhesive layer, 우레탄계 수지를 첨가한 히트씰성 수지로 4 내지 10 미크론의 두께로 코팅된 것을 특징으로 하는 기능성 박막 라미네이팅 필름Functional thin film laminating film, which is coated with a thickness of 4 to 10 microns with a heat sealable resin to which urethane-based resin is added 제 1 항에 있어서 상기 기능성 박막층은,The method of claim 1, wherein the functional thin film layer, 기능 강화를 위한 첨가제를 포함하는 폴리비닐 및 아크릴수지의 중합체, 우레탄 및 아크릴의 그래프트 중합체 또는 변성 폴리에스텔 및 아크릴축합체 중 어느 하나의 기재를 선택하여 1 내지 5 미크론의 두께로 코팅된 것을 특징으로 하는 기능성 박막 라미네이팅 필름Characterized in that it is coated with a thickness of 1 to 5 microns by selecting a substrate of any one of polyvinyl and acrylic resins including additives for enhancing function, graft polymers of urethanes and acrylics or modified polyesters and acrylic condensates Functional thin film laminating film 제 1 항에 있어서 상기 기능성 박막층은,The method of claim 1, wherein the functional thin film layer, 내스크래치성 및 내 약품성을 강화하기 위한 왁스 또는 실리콘 오일 및 열경화 촉진제의 혼합물을 첨가제로 포함하는 수지로 코팅된 것을 특징으로 하는 기능성 박막 라미네이팅 필름Functional thin film laminating film, characterized in that it is coated with a resin containing as a additive a mixture of a wax or silicone oil and a thermosetting accelerator to enhance scratch resistance and chemical resistance 제 1 항에 있어서 상기 기능성 박막층은,The method of claim 1, wherein the functional thin film layer, 특수 보안 요소를 부여하기 위한 형광안료, 형광염료 또는 축광안료를 첨가제로 포함하는 수지로 코팅된 것을 특징으로 하는 기능성 박막 라미네이팅 필름Functional thin film laminating film, characterized in that coated with a resin containing a fluorescent pigment, fluorescent dye or photoluminescent pigment as an additive to impart a special security element 제 1 항에 있어서 상기 기능성 박막층은,The method of claim 1, wherein the functional thin film layer, 약품변색성을 발현하기 위한 특수약제 또는 펄 안료계를 첨가제로 포함하는 수지로 코팅된 것을 특징으로 하는 기능성 박막 라미네이팅 필름Functional thin film laminating film, characterized in that the coating with a resin containing a special drug or a pearl pigment-based additive to express drug discoloration 제 1 항에 있어서 상기 기능성 박막층은,The method of claim 1, wherein the functional thin film layer, 전도성을 부여하기 위한 전도성 물질을 첨가한 수지로 코팅된 것을 특징으로 하는 기능성 박막 라미네이팅 필름Functional thin film laminating film, characterized in that the coating with a resin added a conductive material for imparting conductivity 제 1 항에 있어서 상기 기능성 박막층은,The method of claim 1, wherein the functional thin film layer, UV 차단제를 첨가한 수지로 코팅된 것을 특징으로 하는 기능성 박막 라미네이팅 필름Functional thin film laminating film, which is coated with a resin added with a UV blocker 제 1 항에 있어서,The method of claim 1, 상기 기능성 박막층은 3 내지 5 미크론의 두께로 코팅되고, 상기 접착층은 5 내지 7 미크론의 두께로 코팅된 것을 특징으로 하는 기능성 박막 라미네이팅 필름The functional thin film layer is coated with a thickness of 3 to 5 microns, the adhesive layer is a functional thin film laminating film, characterized in that the coating of 5 to 7 microns thick 제 1 항에 있어서,The method of claim 1, 상기 기능성 박막층은 5 미크론의 두께로 코팅되고, 상기 접착층은 7 미크론의 두께로 코팅된 것을 특징으로 하는 기능성 박막 라미네이팅 필름The functional thin film layer is coated with a thickness of 5 microns, the adhesive layer is a functional thin film laminating film, characterized in that the coating of 7 microns thick
KR10-2002-0088529A 2002-12-31 2002-12-31 thin heatseal film for strengthening function of protective surface KR100450495B1 (en)