KR20010007776A - Manufacturing method of the special materal which rapidly repairs the cracks or/and the crushed portions between cement road and the other structure, and the construction method utilizing the material - Google Patents
Manufacturing method of the special materal which rapidly repairs the cracks or/and the crushed portions between cement road and the other structure, and the construction method utilizing the material Download PDFInfo
- Publication number
- KR20010007776A KR20010007776A KR1020000052875A KR20000052875A KR20010007776A KR 20010007776 A KR20010007776 A KR 20010007776A KR 1020000052875 A KR1020000052875 A KR 1020000052875A KR 20000052875 A KR20000052875 A KR 20000052875A KR 20010007776 A KR20010007776 A KR 20010007776A
- Authority
- KR
- South Korea
- Prior art keywords
- power
- cement
- molding
- construction
- poly
- Prior art date
Abstract
Description
- 본 발명의 목적은 품질향상과 신기술개발로 인한 시공개선의 일환으로 시멘트 도로와 구체의 균열파손을 초속으로 성형복구하는 보수재(PT POWER-TOP)의 제조방법과 이를 이용한 시공공법을 발명함에있어 일반적으로 건설현장에서 시행되어온 통상적 시공관례에 따른 기존의 보수방법과 보수재료를 개선 보완해야만 되는 문제점이 있음을 중시하고 추후 발생의 여지가 있는 시멘트 도로와 구체의 부실시공으로 인한 붕괴와 하자보수의 재발을 미연에 방지하고 또한 이로 인해 파생되는 경제적 기술적 손실과 낭비를 줄이고자 환경과 인체에 무해한 신재료, 신기술을 개발하였는바-The object of the present invention is to invent a method of manufacturing repair materials (PT POWER-TOP) for forming and repairing crack damage of cement roads and spheres at a high speed as part of construction improvements due to quality improvement and new technology development, and construction methods using the same. It is important to emphasize that there is a problem that the existing repair methods and repair materials should be improved and supplemented according to the usual construction practices that have been implemented at construction sites. We have developed new materials and new technologies that are harmless to the environment and the human body in order to prevent recurrences and reduce the economic and technical losses and wastes.
- 이는 88서울올림픽을 전후하여 고도 경제성장으로 시작된 건설의 대규모화는 지방도 및 국도의 확장건설은 물론 전국을 1일 생활권으로 묶는 고속화 도로사업으로 이어져 1960-1970년대 경부, 호남고속도로 건설이후 이미 새천년에는 전국 38여개 노선에 3200여km 고속화도로망과 99년 현재 1100만대 차량보유 분포를 고루게 갖게 되었으며 또한 시멘트 포장도로 및 구조물 건축물(도로, 교량, 터널, 아파트, 빌팅, 체육관, 풀장, 복합건물, 댐, 수조, 식수조)등의 다량건설로 이어지면서 건설호황 국면에 접어들었으나 국민적 숙원사업으로 이룩된 고도 경제성장과 이에따른 현실적인 고평가 고효율은 크다고 판단 되지만 그이면에는 언제부터인가 부실시공과 안전불감증으로 비롯된 하자 문제가 표출되어 왔으며 또한 건설 시공후 유지관리의 문제/ 보수공사의 시공시방 및 설계기준의 미흡과 보수제품의 낙후된 품질성 등으로 인한 원인으로 현존한 건축물과 구조물의 안전마져도 보장할 수 없는 심각한 지경에 이르렀으며The massive scale of construction, which began with high economic growth around the 88 Seoul Olympics, led to the expansion of local roads and national roads, as well as the high-speed road project that binds the whole nation into a one-day living zone. It has more than 3200km high-speed road network on more than 38 routes nationwide and 11 million vehicles as of 1999. It also has cement pavement and structure buildings (roads, bridges, tunnels, apartments, building, gymnasiums, pools, complex buildings, Although the construction boom began as a result of the massive construction of dams, water tanks, and drinking water tanks, etc. Defect problems have been expressed and problems of maintenance after construction / repair work Construction specifications and design criteria was reached lack of maintenance and product quality underdeveloped province, including serious majyeodo borders can not guarantee the safety of buildings and structures existing in the cause due to the
- 또한 이로 인해 발생된 삼풍참사, 성수대교붕괴, 건축물붕괴 등의 엄청난 희생을 겪어온 오늘의 현실을 직시하고 이를 사전에 예방할수 있는 대책을 마련하게 되었으며-In addition, we faced the reality of today's deaths such as the Sampoong disaster, Seongsu Bridge collapse, and the collapse of buildings, and prepared measures to prevent it.
- 기존에 시공되어 사용중이거나 현재 시공중인 시멘트 포장도로 및 구조물을 신재료, 신기술로 보수하여 구체의 견고성, 시공성, 기술성을 확보하여 붕괴의 위험과 하자의 재발을 방지할 수 있기를 기대함은 물론 환경공해로 인한 피해를 줄이기 위하여 환경과 인체에 무해한 신보수재를 개발하므로서 국민건강과 사회적 발전의 쾌적한 환경조성에도 기여하고자 시멘트도로 및 구체의 균열 파손을 초속으로 복구하는 성형재의 제조방법과 이를 이용한 시공공법을 발명하기에 이르렀으며 본 발명 이주는 파급효과가 기술적, 경제적으로 기여하는바 크리라고 확신하면서 상기와 같이 발명의 목적을 기술하는 바임-It is expected that the cement pavement and structures currently in use or under construction will be repaired with new materials and new technologies to secure the solidity, constructability, and technical properties of the concrete to prevent the risk of collapse and recurrence of defects. In order to contribute to the pleasant environment of national health and social development by developing new repair materials that are harmless to the environment and human body in order to reduce the damages caused by environmental pollution, the manufacturing method of molding materials that recovers the crack damage of cement roads and spheres at the same time and construction using them The invention has been invented, and the present invention describes the purpose of the invention as described above, convinced that the ripple effect is the technical and economic contribution.
- 본 발명은 시멘트 도로나 구체의 균열파손을 초속으로 성형복구하는 보수재(PT POWER-TOP)의 제조 방법과 이를 이용한 시공공법에 관한것으로서 상세히 설명하면 시멘트 포장도로나 구체는 기후, 온도, 습도에 따른 수축, 팽창응력의 변화와 기존구체와의 강도 부착, 탄성계수의 불균형으로 균열, 끈김, 파손 현상이 발생되므로 기술과 품질의 저하로 파생되는 하자재발의 제 문제들을 해소하기 위한 신재료, 신기술의 제조, 시공방법의 개발에 관한것임-The present invention relates to a method of manufacturing a repair material (PT POWER-TOP) for molding and repairing crack damage of cement roads or spheres at a high speed, and a construction method using the same. New materials and new technologies to solve the problems of defects caused by deterioration of technology and quality since cracks, sticking, and breakages occur due to shrinkage, change of expansion stress, adhesion to existing spheres, and unbalance of elastic modulus. Development of manufacturing and construction methods
- 시멘트 도로나 구체에 발생되는 균열파손의 주원인은 기존의 통상적인 시공관례에 따른 보수방법과 사용보수재료의 그 일반적인 내용을 검토하여보면 기존의 대다수 보수공사가 구체와의 특성, 물성에 부합되지 않는 보수재를 사용하여 왔으며 종래의 구태적 시공방법에 의존하여 축적된 기술과 기술적 검증이 미흡한 보수방법으로 시공하므로서 하자의 재발현상이 발생되었으며 보수 시공후부터 점차적으로 균열 파손등이 진행되는 것을 흔히 접할수 있는 현실이며 이로 인한 시간적, 경제적 손실은 물론 나아가 구조물 붕괴등 최악의 경우도 감수해야 했음을 알수 있기에 품질을 저하시켜 상품가치를 잃게하는 이러한 현상을 방지코자 여러 가지 수단이 강구되어 왔으나-The main causes of crack damage in cement roads and concrete spheres are that most of the existing renovation works do not meet the characteristics and properties of concrete. Rehabilitation occurred due to the lack of repairing technique and accumulated technical and technical verification depending on the old construction method, and it is common to see the crack breakdown progress gradually after repairing. It is a reality, and as a result, it has been necessary to bear the worst case such as time and economic loss as well as the collapse of the structure. Therefore, various means have been devised to prevent such a phenomenon that the quality is lowered and the product value is lost.
-그 기존의 시공방법과 내용들을 보면 보수조건과 장소, 공정에따른 변화요인을 고려하지 않은채 일반적인 시공방법으로 탄성계수가 불균형한 고강도의 에폭시나 기존의 우레탄 보수재를 사용하여 보수시공 하므로서 재하자의 우려가 있었으며 통상적인 시공관례에 따라 시멘트와 모래 에 물을 혼합하여 만든 몰탈을 파괴된 부위에 미장충진으로 마무리하는 보수방법 등이 있으나 보통의 콘크리트가 완전 양생이 되기 위해서는 실온 23°에서 재령 28일이 소요되는 문제가 있었으며 시멘트 도로의 파손이 발생했을 경우 이것을 복구하는 방법은 공사중인 도로에 차단막을 설치하여 보수시공을 해야하고 장기간 동안 차량 통행을 금지시켜 콘크리트가 완전히 양생된 뒤에 콘크리트 변형을 방지한 다음 교통을 소통시켜야 하는 불편함이 있어왔으며-The existing construction methods and contents show that the repair process is performed by using a high strength epoxy or urethane repair material with an unbalanced elastic modulus as a general construction method without considering the change factors according to the repair conditions, location, and process. There is a concern, and according to the usual construction practice, there is a repair method of finishing mortar by mixing water with cement and sand with plastering, but in order to fully cure concrete, 28 days at room temperature In case of damage to cement road, the method of repairing it is to install a barrier on the road under construction to repair and prevent the traffic for a long time to prevent the deformation of concrete after the concrete is completely cured. There have been inconveniences in communicating the next traffic
- 또한 종래의 기술로 해결할수 없는 문제점은 환경공해성 저품질의 보수자재 사용으로 인한 환경과 인체에 주는 피해/ 기후, 온도, 습도의 변화에 따른 건조수축과 골재, 모래 시멘트의 내부점착력 접착력과 발열성으로 인한 콘크리트 변형의 골재분리, 공극, 파손현상과/ 기상조건 변화와 대기가스의 화학적 반응이 콘크리트에 미치는 중성화 현상과/ 시멘트 도로나 구체에 타설되는 콘크리트 레미콘 배합의 불균형 및 시멘트 배합비율의 문제로 발생되는 균열 파손의 급진행현상/ 하절기, 동절기, 우기, 결빙기, 해빙기 시공공정과 온도변화에 따른 수축팽창균열 파손현상/ 저품질의 보수재 사용으로 인한 균열파손하자 재발현상등의 제 문제를 해결하기에는 부족함이 있어 이를 해소하기 위하여 품질개선과 신기술의 발명 개발로 종래의 기술을 개선하기 위한 수단과 방법이 강구 되어왔음-Also, the problems that cannot be solved by the conventional technology are environmental pollution and damage to the human body due to the use of low quality maintenance materials / dry shrinkage due to changes in climate, temperature and humidity, and internal adhesion of aggregate and sand cement. Aggregate segregation, voids, breakage of concrete deformation and / or neutralization of changes in weather conditions and chemical reactions of atmospheric gases on concrete and / or imbalance of concrete ready-mixed concrete mix and cement mix ratio It is not enough to solve the problems such as rapid progression of crack breakage / summer season, winter season, rainy season, ice breaker, thawing process and shrinkage expansion crack breakage caused by temperature change, and crack breakage caused by the use of low quality repair materials. In order to solve this problem, the conventional technology is improved by improving the quality and developing new technology. Came is taken a means and method for group
- 국내 등록특허 건교부 신기술지정 제 149호는 우레탄 복합마감재 및 마감 공법으로서 소정의 색상으로 조합된 에폭시 수지를 적당량 첨가하고 우레탄 수지를 혼합하여 건축물 바닥에 0.5-1.5cm로 도포하는 바닥 마감재 및 마감공법에 관한 것이며-New technology designation No. 149 of the Ministry of Registered and Registered Korea is a urethane composite finishing material and finishing method.The floor finishing material and finishing method of adding 0.5 ~ 1.5cm to the floor of the building by adding an appropriate amount of epoxy resin combined with a predetermined color and mixing urethane resin. Is about
- 국내 등록특허 건교부 신기술지정 제 59호는 비정질 실리카를 이용한 콘크리트 구체강화 수성아크릴 에폭시 폴리머로서 일반노출 및 수중열화 콘크리트를 방식보수 보강하기위한 방법으로 비정질의 실리카를 이용하며 콘크리트 내부의 철근방청과 열화된 콘크리트를 강화하는 기술이며 일반 노출열화 콘크리트에는 아크릴 폴리머몰탈과 수중 콘크리트 부위에는 수중 에폭시 몰탈과 콘크리트를 단면적의 1/10-1/5로 도포하여 보수하는 비정질 실리카를 이용한 보수공법이 공개되어 있으나-Korean Patent No. 59, New Technology Designation No. 59, is a concrete concrete-reinforced aqueous acrylic epoxy polymer using amorphous silica. It is a technique to reinforce the concrete, and the repair method using the amorphous silica that repairs by applying the acrylic polymer mortar to the exposed concrete concrete and the epoxy mortar and the concrete to 1 / 10-1 / 5 of the cross section of the underwater concrete part is disclosed.
- 이는 본 발명과는 사용목적이나 시공공법과 재료의 물성성상이 판이하게 다름을 알수 있으며 종래의 시공방법과 재료로는 시멘트 도로나 구체의 손상을 초고속으로 성형복구할수 없으며 비일비재하게 발생되는 균열, 끈김, 파손과 급진행되는 구체의 변화를 감당하기에는 아직까지는 부족한점이 많다고 판단됨-It can be seen that the purpose of use and construction method and material properties are different from the present invention. Conventional construction methods and materials can not form and repair cement roads or spheres at high speed, and cracks are infrequent. It seems that there are still many shortcomings to handle the persistence, breakage and rapid change of the sphere.
- 본 발명은 상기 문제점을 해결하고자 본출원인은 poly isocyanate (PT POWER-TOP)를 혼합하여 시멘트도로나 구체의 균열파손을 초고속으로 성형복구하는 보수재의 제조방법과 이를 이용한 시공공법을 개발 발명하게 되었으며 본재료를 이용하여 빠른시간에 초고속으로 성형복구 보수시공 하므로서 안정된 시공으로 품질 개선의 장기적인 효과와 구체의 수명을 향상시키는 시공방법을 제공하는 것으로서 본 발명이 이루고자 하는 기술적 과제임To solve the above problems, the present inventors have developed and manufactured a method of manufacturing a repairing material and a construction method using the same by mixing poly isocyanate (PT POWER-TOP) to form and repair the crack damage of cement road or sphere at high speed. It is a technical task of the present invention to provide a construction method that improves the long-term effect of quality improvement and the life of a sphere by stable construction by performing the repair and repairing of the molding at a very high speed using this material.
- 따라서 기술개선을 이루기 위하여는 첫째 과다 공사비지출로 인한 고비용 저효율/ 둘째 낙후된 시공기술의 개선/ 사용제품의 품질향상/ 재보수 하자율감소를 위한 기술 축적/ 시공후의 사후 유지 관리대책/ 등을들 수 있으며 종래 시공방법과 재료로는 당면한 하자문제와 재보수율 감소 및 경제성, 기술시공성을 기대하기는 어려움이 있어왔음에 현실적으로 이를 충족하기 위하여는 신기술 신제품 개발만이 당면한 기술적 과제임-Therefore, in order to achieve technical improvement, first, high cost and low efficiency due to excessive construction cost, second, improvement of construction technology that has fallen behind, improvement of quality of used product, accumulation of technology for reduction of defect repair rate, and post-maintenance management after construction, etc. It is difficult to expect problems with the existing construction methods and materials, reduction of repair rate, economic feasibility, and technical constructability. To satisfy this, only technical new product development is required.
- 본 발명은 상기와 같은 목적을 달성하기 위하여-The present invention to achieve the above object
isocyanate, polyol(PT POWER-TOP)을 혼합제조한 초속 성형복구재(PT POWER-TOP)몰탈을 파손된 구체에 충진 미장하여 초고속으로 보수 시공하는 방법으로서Filling and repairing super fast molding recovery material (PT POWER-TOP) mortar made of mixed isocyanate and polyol (PT POWER-TOP) at ultra high speed
- 구체 파손부위를 3-5cm 깊이로 치핑하고 치핑부위를 sand, stone(모래, 골재)/ 물(H2o)/ poly isocyanate (PT POWER-TOP)을 혼합제조한 몰탈을 파손된 구체의 치핑부위에 충진 미장하여 초속 양생으로 공사를 마무리 하는 것으로Chipping the broken spheres with a depth of 3-5cm and chipping the mortar with sand, stone (sand, aggregate) / water (H 2 o) / poly isocyanate (PT POWER-TOP) By filling the parts and finishing the work with rapid curing
- 이는 기존구체 와의 강도 부착성을 높히고 구체의 수명을 향상시키는 제조, 공법상의 기술개발 구성으로서 시멘트 도로 및 구체의 균열파손을 초속으로 성형복구하는 보수재의 제조방법과 이를 이용한 시공공법임-This is a manufacturing and construction method to improve the strength adhesion to existing spheres and improve the life of spheres. It is a manufacturing method of repairing materials for molding and repairing the crack damage of cement roads and spheres at a high speed and construction methods using the same.
- 현재까지 시공되고 있는 종래의 기술과 보수제품의 실'예'를 보면 건설 환경오염이 인체에 미치는 환경공해의 유해성 및 재료의 품질성 검증과 안전관리 대책이 부족한 보수 자재로 시공하는 관계로 기존 구체와의 물성, 성상과 부착성이 부합, 결합되지 않았으며 종래 기술과 재료의 특성상 복잡한 시공공정을 요구하므로서 공정의 단축이나 긴급을 요하는 시멘트 도로 및 구체의 보수공사에 사용이 불가 했으며 이로인한 장기간의 시공공정으로 차량 밀집 정체 현상이 발생됨으로 시간적, 경제적 손실을 가져왔기에-Actual examples of conventional technology and repair products that have been constructed so far are existing due to the construction of repair materials that lack the harmfulness of environmental pollution and the quality of materials and safety management measures. The physical properties, properties, and adhesion to the sphere were not matched and combined. Due to the complex construction process required by the prior art and the characteristics of the material, it was not possible to use it for the repair of cement roads and spheres requiring shortening or urgent processes. Due to long-term construction process, congestion of vehicles caused time and economic loss.
- 이를 개선하기 위하여 간편하게 시공할수 있는 기술과 기존 구체와의 강도, 탄성계수, 물성, 성상이 균형되고 고부착성을 갖춘 보수재료를 개발하여 기술시공 하므로서 구체의 내구성, 내용연수를 향상시키고 시공의 안전성과 환경친화의 안전성을 기대할수 있기를 바라며 이에 개발된 보수재료와 신기술로 파손된 시멘트 도로나 구체를 단 20-30분내에 빠르게 성형 복구하여 공사중 교통통제로 인한 정체 체증현상을 최소화함을 물론 파생되는 하자재발 및 이에따른 제 문제점과 기술적 경제적 손실을 줄이고자 개발된 신보수재와 기술공법을 발명하게 되었으며-In order to improve this, we develop a technology that can be easily constructed and a repair material with high adhesion and balance of strength, elastic modulus, physical properties, and properties with existing spheres. We hope to be able to expect safety and environment-friendliness, and to minimize the congestion caused by traffic control during construction by rapidly molding and repairing the damaged cement road or concrete in just 20-30 minutes. In order to reduce the recurrence of defects and related problems and technical and economic losses, we have invented new repair materials and technology.
- 본 시공공법의 유의사항은 견실한 시공을 위하여는 구체의 파손되 부위에 묻어있는 시멘트 가루, 먼지, 유분등이 기존구체와 보수재와의 부착력을 저하시켜 하자를 재발시킬 우려가 있으므로 고압에어 콤프나 와이어 브러쉬로 완전히 제거 청소하여 야하며-Caution for this construction method is that high-pressure air comp because the cement powder, dust, oil, etc. buried in the damaged part of the sphere may reduce the adhesion between the existing concrete and the repair material for the reliable construction. I have to clean it completely with a wire brush and
이후 본 발명에서 제조된 초속 성형복구 몰탈을 충진 미장하여 초고속 양생으로 시멘트 도로와 구체의 균열 파손을 성형복구하는 시공 공법을 제시하는 것임Since the present invention is to provide a construction method for molding and repairing the crack breakage of cement roads and spheres with ultra-fast curing by filling the ultra-fast molding recovery mortar prepared in the present invention.
- 본 발명에 사용되는 poly isocyanate는 초속성형복구재(PT POWER-TOP)의 제조 혼입원료로서 isocyanate(NCO)와 polyol(-OH)을 중부가 반응으로 합성하여 부재료를 혼입 개발한 수지로서 poly isocyanate(PT POWER-TOP)이라 칭하며 제조합성상의 고분자 반응과 제조성분, 성상 및 체적저항은 다음과 같음-The poly isocyanate used in the present invention is a mixed compound of isocyanate (NCO) and polyol (-OH) as a mixed raw material for the production of super fast molding recovery material (PT POWER-TOP). It is called (PT POWER-TOP) and the polymer reaction of manufacturing phase, manufacturing component, property and volume resistance are as follows.
- 고분자반응(중합반응)Polymer reaction
- 초속 성형복구재(PT POWER-TOP)의 제조첨가 원료인 poly isocyanate(POWER-TOP)의 제조성분, 성상 및 체적저항-Ingredients, properties, and volume resistance of poly isocyanate (POWER-TOP), an additive for the manufacture of high speed molding recovery materials (PT POWER-TOP)
- 초속 성형 복구재(PT POWER-TOP)의 제조성상-Manufacturing characteristics of high speed molding recovery material (PT POWER-TOP)
▷ 초속 성형복구재 (PT,POWER-TOP)의 물성,특성에 관한 시험측정결과▷ Test measurement results on the properties and properties of the ultrafast molded restoration material (PT, POWER-TOP)
- PT,POWER-TOP의 특성은 다음과 같음-The characteristics of PT, POWER-TOP are as follows.
(조제 및 측정)(Preparation and measurement)
(측정방법) 6호 Sand(모래)/ Limestonepowder(시멘트)/ H2O/ POWER-TOP=100/200/ 60/36-72wt 혼합물을 기준 몰탈 형틀 (40×40×16mm)을 사용하여 시료 제조하고 옥내에서 14일간 양생하여 인장 압축시험을 80kg/sec 속도로 구부러짐 시험은 15kg/sec 하중속도로 측정함(Measurement method) No. 6 Sand (sand) / Limestonepowder (cement) / H 2 O / POWER-TOP = 100/200/60 / 36-72wt mixture using a standard mortar mold (40 × 40 × 16mm) After curing for 14 days indoors, the bending test at 80kg / sec speed was measured at 15kg / sec load speed.
▷ 초속 성형 복구재(PT,POWER-TOP)의 유면강판과의 강도시험 측정결과▷ Measurement result of strength test with oil-plated steel sheet of super fast forming restoration material (PT, POWER-TOP)
- PT, POWER-TOP의 유면강판과의 접착시험 강도-Adhesion test strength with oil and steel plate of PT, POWER-TOP
- PT, POWER-TOP의 압축강도 시험측정결과(시간별, 배합비)-Compression strength test measurement result of PT, POWER-TOP (by time, compounding ratio)
- 상기 시험치의 압축강도는 KICM의 KSF 2451-98 / KSL 5105-97에 준한 시험결과이며 유면 강판과의 접착 시험은 시멘트/ POWER-TOP/ 백등유/ 물=100/100/100/ 15 혼합물을 1in안의 닦은 강판에 1×1in으로 도포하고 강판을 시멘트상에 중량 100g의 분강을 실어 경화시킨 다음 실온 23℃×습도 65%의 조건으로 14분간 장치 후 80kg/sec 하중 속도로 기준 측정함-The compressive strength of the test value is the test result in accordance with KSFM KSF 2451-98 / KSL 5105-97, and the adhesion test with oil-plated steel sheet is 1in of cement / POW-TOP / white kerosene / water = 100/100/100/15 mixture. 1 × 1in is applied to the polished steel sheet inside, and the steel sheet is hardened by loading a 100g weight of powder on cement, and then measured at 80kg / sec load rate after 14 minutes at 23 ℃ x 65% humidity.
▷ 환경오염 및 수질검사 용해시험결과▷ Test results for environmental pollution and water quality dissolution
- 하기 검사는 수돗물에 POWER-TOP을 환경수질 검사기준치에 따른 0.01, 0.1 및 1.0중량의 %를 혼입했을 때의 26개 수질검사 결과 중 기준치이며 시험측정 방법은 상수도(수돗물)에 POWER-TOP을 상기와 기준치로 첨가한 후 온도 20℃에서 24시간 방치후 분석용 여지 NO.5에 여과하여 측정함-The following test is the standard value among 26 water quality test results when POWER-TOP is mixed in tap water with 0.01, 0.1, and 1.0% by weight according to the environmental water quality standard.The test measurement method is POWER-TOP in tap water. After adding to the above standard value and left for 24 hours at the temperature of 20 ℃, it is measured by filtration to NO.5 for analysis.
- POWER-TOP의 혼입량에 따른 시험결과-Test result according to the mixing amount of POWER-TOP
- 수질 기준에 관한 성령 기준치-Holy Spirit Standards on Water Quality Standards
o 시험결과 잔류염소(기준치 0.7/시험결과 1ppm) 감량의 시험항목 이외에는 전부 규격치였음. 이 규격은 수돗물을 사용하는 적용장소에 보수공사에도 시공이 용이하며 건설환경으로 인한 공해와 인체에 무해한 것이 확인됨o All test values except the test item for the reduction of residual chlorine (reference value 0.7 / test result 1ppm) were standard values. This standard is easy to be used for repair work in the place where tap water is used, and it is confirmed that it is harmless to the human body due to the construction environment.
- 본 발명의 표준 시공 공정도는 다음과 같음-Standard construction process diagram of the present invention is as follows.
표준 시공시방서(균열파손 초속 성형복구 시공법/HI/repair공법) Standard construction specification (crack damage ultra-fast molding recovery construction method / HI / repair method)
※ 상기 공정표는 균열파손을 초속으로 성형 복구하는 표준 보수 시공법의 시방서임※ The above process table is the specification of standard repair construction method that repairs and breaks cracks at high speed.
실시, (예)Implementation, (example)
제 1공정 : LIMESTONE POWDER(시멘트)와 SAND(표준사)를 1:1 비율로 섞은 다음 Poly isocyanate(POWER-TOP)와 H2O(물)를 상기 혼합물 대비 10중량% 첨가 배합하며 시멘트 도로의 균열 파손을 초속으로 복구하는 성형재를 제조한 다음First step: mix LIMESTONE POWDER (cement) and SAND (standard yarn) in a 1: 1 ratio, and then add 10% by weight of poly isocyanate (POWER-TOP) and H 2 O (water) to the mixture. Produces a molding material that repairs crack breaks in seconds
제 2공정 : 구체의 균열 파손 부위를 보수조건과 시공장소에 따라 깊이 3-5cm로 절개 치핑한 뒤2nd process: Incision chipping of crack damage part of sphere to depth 3-5cm according to repair condition and factory
제 3공정 : 파손 치핑부위를 깨끗이 청소(고압에어콤프/ 와이어 브러쉬)한 다음 Poly isocyanate(POWER-TOP)를 신구접착 1회 도포하고3rd step: Clean the damaged chipping area (high pressure air comb / wire brush) and apply Poly isocyanate (POWER-TOP) once and then
제 4공정 도포 부위에 상기 1공정에서 제조한 구체의 균열 파손을 초속 복구하는 성형재(PT POWER-TOP)몰탈을 충진 미장하여 양생한다.In the fourth step, the application site is filled and cured with a molding material (PT POWER-TOP) mortar which recovers the crack breakage of the sphere prepared in the first step at a high speed.
제 5공정 미장 20-30분 후 표면을 그라인더, 센더 페이퍼로 면처리하고 시공 완료 확인하는 것으로 마무리한다.After 20-30 minutes of the 5th process plastering, the surface is finished with grinder and sender paper, and finished with the completion of construction.
이상과 같이 표준 시공시방(HI/repair 공법)을 실시 "예"로 제시하는 바이며 시공장소와 보수조건 구분에 따라 상기표준 시공시방을 기준으로 아래와 같이 시공공법을 개발함As mentioned above, the standard construction specification (HI / repair construction method) is presented as "Yes" and the construction construction method is developed as follows based on the standard construction specification according to the division of the factory and the repair condition
-시멘트도로 및 구체 줄눈부위 급속 성형복구 시공법(HI/A-repair 공법)- Rapid molding recovery construction method for cement road and concrete joint (HI / A-repair method)
모서리 파손 급속 성형복구 시공법(HI/B-repairr 공법) Corner Break Rapid Molding Repair Method (HI / B-repairr Method)
돌출 및 가라앉은 부위 급속 성형복구 시공법(HI/C-repair 공법) Rapid molding recovery construction for protruding and sinking parts (HI / C-repair method)
단차 급속 성형복구 시공법(HI/D repair 공법) Step rapid molding recovery construction method (HI / D repair method)
골재분리 몰림현상 급조성형 시공법(HI/E-repair 공법) Aggregate Separation Phenomenon Rapid Construction Method (HI / E-repair Method)
균열파손 급속 성형복구 시공법(HI/F-repair 공법) Crack damage rapid molding repair construction method (HI / F-repair method)
누수 파손부위 초속 성형복구 공극 시공법(HI/G space repair 공법) High speed molding recovery void construction method for leak damaged parts (HI / G space repair construction method)
누수 파손부위 초속 성형복구 면실 시공법(HI/H cotten yarn 공법) Ultra-fast molding recovery cotton thread construction for leak damaged parts (HI / H cotten yarn method)
을 기술개발 시공공법으로 첨부하는 바이며 상세"도"는 별지와 같음Is attached to the technology development and construction method.
- 상기 발명의 구성 및 작용에서도 기술한바와 같이 본 발명은 시공 공정의 단축과 긴급을 요하는 시공장소 및 구체의 원상회복 기능성과 내구성, 내용연수를 향상시키기 위한 보수공사에 사용되는 신 보수재와 개발된 신기술 보수공법이며 신보수재인 초속 성형복구재(PT POWER-TOP)를 제조하여 빠르게 보수 시공하는 획기적인 기술개선 고품질의 개발 공법으로서 발명의 효과가 국내의 건설업계에 기여하는바 크리라고 예상됨-As described in the configuration and operation of the present invention, the present invention is developed and developed for the new repair materials used in the repair work to improve the rehabilitation functionality, durability, and service life of the original factory and spheres that require a shortening and urgent construction process. This is a breakthrough technology improvement that manufactures and repairs super fast molding recovery material (PT POWER-TOP), which is a new technology repairing method and new repairing material. It is expected that the effect of the invention contributes to the domestic construction industry.
_ _
Claims (3)