KR102683434B1 - Room temperature curing type transparent coating agent for vehicle repair - Google Patents
Room temperature curing type transparent coating agent for vehicle repair Download PDFInfo
- Publication number
- KR102683434B1 KR102683434B1 KR1020220072634A KR20220072634A KR102683434B1 KR 102683434 B1 KR102683434 B1 KR 102683434B1 KR 1020220072634 A KR1020220072634 A KR 1020220072634A KR 20220072634 A KR20220072634 A KR 20220072634A KR 102683434 B1 KR102683434 B1 KR 102683434B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- transparent coating
- coating agent
- parts
- formula
- Prior art date
Abstract
차량 보수 작업 중에 상도 코팅제로 사용될 수 있으며, 탄소 배출량 및 VOC 함량을 감소시킬 수 있고, 상온에서 경화 특성이 우수한 투명 코팅제에 대하여 개시한다.
본 발명에 따른 투명 코팅제는 주제와 경화제를 포함하고, 상기 주제는 [화학식 1]로 표시되는 화합물을 포함하는 제1수지; [화학식 2]로 표시되는 화합물을 포함하는 제2수지; 유기 용매; 및 표면 조절용 첨가제를 포함할 수 있다.
[화학식 1]
[화학식 2]
Disclosed is a transparent coating that can be used as a top coating during vehicle maintenance work, can reduce carbon emissions and VOC content, and has excellent curing properties at room temperature.
The transparent coating agent according to the present invention includes a base material and a curing agent, and the base material includes a first resin containing a compound represented by [Chemical Formula 1]; A second resin containing a compound represented by [Formula 2]; organic solvent; and additives for surface conditioning.
[Formula 1]
[Formula 2]
Description
본 발명은 차량 보수 작업 중에 상도 코팅제로 사용될 수 있으며, 탄소 배출량 및 VOC 함량을 감소시킬 수 있고, 상온에서 경화 특성이 우수한 투명 코팅제에 관한 것이다. The present invention relates to a transparent coating agent that can be used as a top coating during vehicle maintenance work, can reduce carbon emissions and VOC content, and has excellent curing properties at room temperature.
차량 보수용으로 열경화 타입의 상도 코팅제가 사용되고 있다.A thermosetting type top coating agent is used for vehicle repairs.
상도 코팅제는 얕은 홈을 메꿔주며 도장면을 평활하게 하기 위해 사용하는 것으로, 하도 코팅 후에 최외층을 형성하는 도료이다. The top coating agent is used to fill shallow grooves and smooth the painted surface, and is a paint that forms the outermost layer after the undercoat coating.
상도 코팅제의 중요하게 요구되는 물성으로는 소재와의 부착성, 연마성, 표면 특성 및 경화성 등이 있다. Important physical properties required for top coating agents include adhesion to materials, polishing properties, surface properties, and hardenability.
종래 차량 보수에 사용되던 열경화형 상도 코팅제의 경우, 소재와의 부착성, 표면 특성 등은 우수하나, 열원을 통한 우레탄 경화방식의 제품이 주류를 이루기 때문에 열에너지 생성을 위해 따른 탄소 발생이 필연적이다. In the case of thermosetting top coatings used for conventional vehicle repair, adhesion to materials and surface properties are excellent, but since urethane curing products using a heat source are the mainstream, carbon generation is inevitable for generating heat energy.
이에 따라, 상온에서 경화 효율을 높여 열경화형 상도 코팅제의 탄소 배출량과 휘발성유기화합물(VOC)를 감소시키는 연구가 필요하다. Accordingly, research is needed to reduce carbon emissions and volatile organic compounds (VOCs) of thermosetting top coatings by increasing curing efficiency at room temperature.
본 발명의 목적은 상온에서 경화 특성이 우수한 차량 보수용 투명 코팅제를 제공하는 것이다.The purpose of the present invention is to provide a transparent coating agent for vehicle repair that has excellent curing properties at room temperature.
또한 본 발명의 목적은 탄소 배출량과 휘발성유기화합물(VOC) 발생량을 감소시킬 수 있는 차량 보수용 투명 코팅제를 제공하는 것이다. Another object of the present invention is to provide a transparent coating agent for vehicle repair that can reduce carbon emissions and volatile organic compounds (VOC) generation.
또한 본 발명의 목적은 도막의 표면 특성이 우수한 차량 보수용 투명 코팅제를 제공하는 것이다. Another object of the present invention is to provide a transparent coating agent for vehicle repair with excellent surface properties of the coating film.
또한 본 발명의 목적은 작업성이 우수한 차량 보수용 투명 코팅제를 제공하는 것이다. Another object of the present invention is to provide a transparent coating agent for vehicle repair with excellent workability.
본 발명의 목적들은 이상에서 언급한 목적으로 제한되지 않으며, 언급되지 않은 본 발명의 다른 목적 및 장점들은 하기의 설명에 의해서 이해될 수 있고, 본 발명의 실시예에 의해 보다 분명하게 이해될 것이다. 또한, 본 발명의 목적 및 장점들은 특허 청구 범위에 나타낸 수단 및 그 조합에 의해 실현될 수 있음을 쉽게 알 수 있을 것이다.The objects of the present invention are not limited to the objects mentioned above, and other objects and advantages of the present invention that are not mentioned can be understood by the following description and will be more clearly understood by the examples of the present invention. Additionally, it will be readily apparent that the objects and advantages of the present invention can be realized by the means and combinations thereof indicated in the patent claims.
본 발명에 따른 투명 코팅제는 주제와 경화제를 포함하고, 상기 주제는 [화학식 1]로 표시되는 화합물을 포함하는 제1수지; [화학식 2]로 표시되는 화합물을 포함하는 제2수지; 유기 용매; 및 표면 조절용 첨가제를 포함할 수 있다.The transparent coating agent according to the present invention includes a base material and a curing agent, and the base material includes a first resin containing a compound represented by [Chemical Formula 1]; A second resin containing a compound represented by [Formula 2]; organic solvent; and additives for surface conditioning.
[화학식 1][Formula 1]
[화학식 2][Formula 2]
상기 주제는 제1수지 100중량부에 대하여, 제2수지 7 ~ 22중량부, 유기 용매 29 ~ 57중량부 및 표면 조절용 첨가제 1.5 ~ 5중량부를 포함할 수 있다. The main agent may include 7 to 22 parts by weight of the second resin, 29 to 57 parts by weight of an organic solvent, and 1.5 to 5 parts by weight of a surface conditioning additive, based on 100 parts by weight of the first resin.
상기 유기 용매는 디메틸 카보네이트, 메틸이소부틸케톤, n-부틸 아세테이트, 프로필렌 글리콜 및 모노메틸 에테르 아세테이트 중 1종 이상을 포함할 수 있다.The organic solvent may include one or more of dimethyl carbonate, methyl isobutyl ketone, n-butyl acetate, propylene glycol, and monomethyl ether acetate.
상기 표면 조절용 첨가제는 [화학식 3]으로 표시되는 알킬 에테르 변성 폴리디메틸실록산을 포함할 수 있다.The surface control additive may include alkyl ether-modified polydimethylsiloxane represented by [Formula 3].
[화학식 3][Formula 3]
상기 경화제는 지방족 폴리이소시아네이트 및 유기 용매를 포함할 수 있다.The curing agent may include an aliphatic polyisocyanate and an organic solvent.
상기 경화제는 지방족 폴리이소시아네이트 100중량부에 대하여, 유기 용매 73 ~ 92중량부를 포함할 수 있다.The curing agent may include 73 to 92 parts by weight of an organic solvent based on 100 parts by weight of aliphatic polyisocyanate.
상기 유기 용매는 자일렌 및 n-부틸 아세테이트 중 1종 이상을 포함할 수 있다. The organic solvent may include one or more of xylene and n-butyl acetate.
상기 주제 : 경화제의 혼합비는 45 ~ 55중량% : 45 ~ 55중량%일 수 있다.Above subject: The mixing ratio of the hardener may be 45 to 55% by weight: 45 to 55% by weight.
본 발명에 따른 차량 보수용 투명 코팅제는 상온에서 경화 특성이 우수한 효과가 있다.The transparent coating agent for vehicle repair according to the present invention has excellent curing properties at room temperature.
이에 따라, 탄소 배출량과 휘발성유기화합물(VOC) 발생량을 감소시킬 수 있고, 작업성이 우수한 효과가 있다. Accordingly, carbon emissions and volatile organic compounds (VOC) generation can be reduced, and workability is excellent.
또한 차량 보수용 투명 코팅제를 이용하면, 도막의 표면 특성이 우수한 효과가 있다.In addition, using a transparent coating agent for vehicle repair has the effect of improving the surface properties of the coating film.
상술한 효과와 더불어 본 발명의 구체적인 효과는 이하 발명을 실시하기 위한 구체적인 사항을 설명하면서 함께 기술한다.In addition to the above-described effects, specific effects of the present invention are described below while explaining specific details for carrying out the invention.
전술한 목적, 특징 및 장점은 첨부된 도면을 참조하여 상세하게 후술되며, 이에 따라 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 본 발명의 기술적 사상을 용이하게 실시할 수 있을 것이다. 본 발명을 설명함에 있어서 본 발명과 관련된 공지 기술에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 상세한 설명을 생략한다. 이하, 첨부된 도면을 참조하여 본 발명에 따른 바람직한 실시예를 상세히 설명하기로 한다. 도면에서 동일한 참조부호는 동일 또는 유사한 구성요소를 가리키는 것으로 사용된다.The above-described objects, features, and advantages will be described in detail later with reference to the attached drawings, so that those skilled in the art will be able to easily implement the technical idea of the present invention. In describing the present invention, if it is determined that a detailed description of known techniques related to the present invention may unnecessarily obscure the gist of the present invention, the detailed description will be omitted. Hereinafter, preferred embodiments according to the present invention will be described in detail with reference to the attached drawings. In the drawings, identical reference numerals are used to indicate identical or similar components.
이하에서 구성요소의 "상부 (또는 하부)" 또는 구성요소의 "상 (또는 하)"에 임의의 구성이 배치된다는 것은, 임의의 구성이 상기 구성요소의 상면 (또는 하면)에 접하여 배치되는 것뿐만 아니라, 상기 구성요소와 상기 구성요소 상에 (또는 하에) 배치된 임의의 구성 사이에 다른 구성이 개재될 수 있음을 의미할 수 있다. Hereinafter, the “top (or bottom)” of a component or the arrangement of any component on the “top (or bottom)” of a component means that any component is placed in contact with the top (or bottom) of the component. Additionally, it may mean that other components may be interposed between the component and any component disposed on (or under) the component.
또한 어떤 구성요소가 다른 구성요소에 "연결", "결합" 또는 "접속"된다고 기재된 경우, 상기 구성요소들은 서로 직접적으로 연결되거나 또는 접속될 수 있지만, 각 구성요소 사이에 다른 구성요소가 "개재"되거나, 각 구성요소가 다른 구성요소를 통해 "연결", "결합" 또는 "접속"될 수도 있는 것으로 이해되어야 할 것이다. Additionally, when a component is described as being “connected,” “coupled,” or “connected” to another component, the components may be directly connected or connected to each other, but the other component is “interposed” between each component. It should be understood that “or, each component may be “connected,” “combined,” or “connected” through other components.
이하에서는, 본 발명의 몇몇 실시예에 따른 차량 보수용 상온 경화형 투명 코팅제를 설명하도록 한다.Hereinafter, a room temperature curable transparent coating agent for vehicle repair according to some embodiments of the present invention will be described.
본 발명의 차량 보수용 투명 코팅제는 상온에서 경화 특성이 우수하며, 이에 따라 열경화 타입의 투명 코팅제 대비, 탄소 배출량과 휘발성유기화합물(VOC) 발생량을 감소시킬 수 있는 효과가 있다. The transparent coating agent for vehicle repair of the present invention has excellent curing properties at room temperature, and thus has the effect of reducing carbon emissions and the amount of volatile organic compounds (VOC) generated compared to a heat-curing type transparent coating agent.
이러한 차량 보수용 투명 코팅제를 이용하는 경우, 작업성이 우수하고, 도막의 표면 특성이 우수한 효과가 있다.When using such a transparent coating agent for vehicle repair, workability is excellent and the surface properties of the coating film are excellent.
또한 전기차의 시장 점유율이 증가함에 따라 전기차의 핵심 부품인 배터리의 사용량이 증가하고 있으며, 이러한 배터리는 열을 받을수록 배터리의 효율이 감소하게 된다. 본 발명의 차량 보수용 투명 코팅제를 차량 보수 작업 시 차량의 도막 형성용으로 적용할 경우, 배터리의 효율성 유지에도 기여할 것으로 예상된다.In addition, as the market share of electric vehicles increases, the use of batteries, a key component of electric vehicles, is increasing, and as these batteries receive heat, their efficiency decreases. When the transparent coating agent for vehicle repair of the present invention is applied to form a coating film on a vehicle during vehicle repair work, it is expected to contribute to maintaining the efficiency of the battery.
본 발명에 따른 투명 코팅제는 2액형으로, 주제와 경화제를 포함하는 것이 바람직하다.The transparent coating agent according to the present invention is a two-component type and preferably contains a base material and a curing agent.
주제는 투명 코팅제를 구성하는 주요 성분으로, 상온에서 경화시킨 후에 형성되는 도막의 물리적, 화학적 특성을 결정할 수 있고, 상온에서의 경화 속도를 조절할 수 있다.The base material is the main component of the transparent coating agent, and can determine the physical and chemical properties of the coating film formed after curing at room temperature and control the curing speed at room temperature.
구체적으로, 주제는 [화학식 1]로 표시되는 화합물을 포함하는 제1수지, [화학식 2]로 표시되는 화합물을 포함하는 제2수지, 유기 용매 및 표면 조절용 첨가제를 포함할 수 있다.Specifically, the subject matter may include a first resin containing a compound represented by [Formula 1], a second resin containing a compound represented by [Formula 2], an organic solvent, and an additive for surface control.
[화학식 1][Formula 1]
[화학식 2][Formula 2]
제1수지는 상온에서 경화시킨 후 형성되는 도막의 물리적 및 화학적 특성을 결정하는 역할을 하며, [화학식 1]로 표시되는 화합물을 포함하는 폴리우레아 폴리머일 수 있다. 또한 제2수지는 상온에서의 경화 속도를 조절하는 역할을 하며, [화학식 2]로 표시되는 화합물을 포함하는 폴리우레아 폴리머일 수 있다.The first resin plays a role in determining the physical and chemical properties of the coating film formed after curing at room temperature, and may be a polyurea polymer containing a compound represented by [Formula 1]. Additionally, the second resin plays a role in controlling the curing speed at room temperature and may be a polyurea polymer containing a compound represented by [Formula 2].
유기 용매는 코팅 작업 시에 작업성을 좌우하는 요소로, 환경 규제에 부합하는 함량 및 성분을 포함하는 것이 바람직하다.The organic solvent is a factor that determines workability during coating work, and it is desirable to include content and ingredients that comply with environmental regulations.
구체적으로, 유기 용매는 디메틸 카보네이트, 메틸이소부틸케톤, n-부틸 아세테이트, 프로필렌 글리콜 및 모노메틸 에테르 아세테이트 중 1종 이상을 포함할 수 있다. Specifically, the organic solvent may include one or more of dimethyl carbonate, methyl isobutyl ketone, n-butyl acetate, propylene glycol, and monomethyl ether acetate.
표면 조절용 첨가제는 최종 도막의 우수한 평활성을 확보하기 위한 요소로, [화학식 3]으로 표시되는 알킬 에테르 변성 폴리디메틸실록산을 포함할 수 있다.The surface control additive is an element to ensure excellent smoothness of the final coating film, and may include alkyl ether-modified polydimethylsiloxane represented by [Formula 3].
하기 화학식 3에서 x는 1 ~ 100의 정수이다.In Formula 3 below, x is an integer from 1 to 100.
[화학식 3][Formula 3]
주제는 제1수지 100중량부에 대하여, 제2수지 7 ~ 22중량부, 유기 용매 29 ~ 57중량부 및 표면 조절용 첨가제 1.5 ~ 5중량부를 포함할 수 있다. The main agent may include 7 to 22 parts by weight of the second resin, 29 to 57 parts by weight of an organic solvent, and 1.5 to 5 parts by weight of a surface conditioning additive, based on 100 parts by weight of the first resin.
바람직하게, 제1수지 100중량부에 대하여, 제2수지 10 ~ 20중량부, 유기 용매 35 ~ 50중량부 및 표면 조절용 첨가제 2 ~ 4중량부를 포함할 수 있다. Preferably, based on 100 parts by weight of the first resin, it may include 10 to 20 parts by weight of the second resin, 35 to 50 parts by weight of the organic solvent, and 2 to 4 parts by weight of the surface conditioning additive.
제1수지 100중량부에 대하여, 제2수지 10 ~ 20중량부를 포함함으로써, 상온에서의 경화 속도가 빠르고 경화 특성이 우수한 효과가 있다. By including 10 to 20 parts by weight of the second resin with respect to 100 parts by weight of the first resin, the curing speed at room temperature is fast and the curing characteristics are excellent.
또한 제1수지 100중량부에 대하여, 유기 용매 29 ~ 57중량부를 포함함으로써, 코팅 작업 시 작업성이 우수한 효과가 있으며, VOC 함량을 감소시키는 효과가 있다. In addition, by including 29 to 57 parts by weight of an organic solvent per 100 parts by weight of the first resin, there is an effect of excellent workability during coating work and an effect of reducing the VOC content.
또한 제1수지 100중량부에 대하여, 표면 조절용 첨가제 1.5 ~ 5중량부를 포함함으로써, 상온 경화 후 코팅층의 표면 특성이 우수하고, 특히 평활성이 더욱 우수한 효과가 있다.In addition, by including 1.5 to 5 parts by weight of a surface control additive per 100 parts by weight of the first resin, the surface properties of the coating layer after curing at room temperature are excellent, and in particular, smoothness is excellent.
주제는 25±20℃에서 제1수지와 제2수지를 유기 용매와 함께 혼합한 후, 표면 조절용 첨가제를 투입 및 혼합하여 제조될 수 있다.The base material can be manufactured by mixing the first resin and the second resin with an organic solvent at 25 ± 20°C, then adding and mixing a surface control additive.
경화제는 지방족 폴리이소시아네이트 및 유기 용매를 포함할 수 있다.Curing agents may include aliphatic polyisocyanates and organic solvents.
지방족 폴리이소시아네이트는 “-N=C=O” 작용기를 지니는 HDI Biuret 타입의 지방족 폴리이소시아네이트이며, -N=C=O 함량은 전체 100중량% 중에서 21 ~ 24중량%이고, 지방족 폴리이소시아네이트의 중량평균분자량은 700 ~ 800일 수 있다. 이러한 지방족 폴리이소시아네이트는 화학식 4로 표시될 수 있다.Aliphatic polyisocyanate is an HDI Biuret type aliphatic polyisocyanate with a “-N=C=O” functional group. The -N=C=O content is 21 to 24% by weight out of the total 100% by weight, and the weight average of aliphatic polyisocyanate is The molecular weight may be 700 to 800. This aliphatic polyisocyanate may be represented by Chemical Formula 4.
[화학식 4][Formula 4]
유기 용매는 자일렌 및 n-부틸 아세테이트 중 1종 이상을 포함할 수 있다. The organic solvent may include one or more of xylene and n-butyl acetate.
경화제는 지방족 폴리이소시아네이트 100중량부에 대하여, 유기 용매 73 ~ 92중량부를 포함할 수 있다. 바람직하게, 지방족 폴리이소시아네이트 100중량부에 대하여, 유기 용매 80 ~ 90중량부를 포함할 수 있다The curing agent may include 73 to 92 parts by weight of an organic solvent based on 100 parts by weight of aliphatic polyisocyanate. Preferably, 80 to 90 parts by weight of organic solvent may be included based on 100 parts by weight of aliphatic polyisocyanate.
경화제가 지방족 폴리이소시아네이트 100중량부에 대하여, 유기 용매 73 ~ 92중량부를 포함함으로써, 상온에서 우수한 경화 특성을 나타낼 수 있다.By containing 73 to 92 parts by weight of an organic solvent based on 100 parts by weight of aliphatic polyisocyanate, the curing agent can exhibit excellent curing properties at room temperature.
경화제는 25±20℃에서 지방족 폴리이소이아네이트와 유기 용매를 혼합하여 제조될 수 있다.The curing agent can be prepared by mixing aliphatic polyisocyanate and an organic solvent at 25 ± 20°C.
본 발명의 차량 보수용 상온 경화형 투명 코팅제는 주제 : 경화제의 혼합비가 45 ~ 55중량% : 45 ~ 55중량%일 수 있다. 바람직하게, 주제 : 경화제의 혼합비가 50 ~ 55중량% : 45 ~ 50중량%일 수 있다.The room temperature curing transparent coating agent for vehicle repair of the present invention may have a mixing ratio of subject: hardener of 45 to 55% by weight: 45 to 55% by weight. Preferably, the mixing ratio of base material and hardener may be 50 to 55% by weight: 45 to 50% by weight.
주제와 경화제가 45 ~ 55중량% : 45 ~ 55중량%의 혼합비를 만족함으로써, 투명 코팅제가 요구하는 물성을 모두 나타내는데 유리한 이점이 있다.There is an advantage in exhibiting all the physical properties required by a transparent coating agent by satisfying the mixing ratio of 45 to 55% by weight and 45 to 55% by weight of the base material and hardener.
본 발명의 차량 보수용 상온 경화형 투명 코팅제는 25±20℃에서 주제와 경화제를 혼합하여 제조될 수 있다.The room temperature curing transparent coating agent for vehicle repair of the present invention can be manufactured by mixing the base material and the curing agent at 25 ± 20°C.
본 발명의 차량 보수용 상온 경화형 투명 코팅제는 상온인 25℃에서 경화시킨 후 지촉건조 측정을 통해 5분 이하의 지촉 건조 특성을 나타내는 효과가 있다.The room temperature curing transparent coating agent for vehicle repair of the present invention has the effect of showing touch drying characteristics of 5 minutes or less through drying to touch measurement after curing at room temperature of 25°C.
반면, 종래 투명 코팅제의 경우 60℃ 근처에서 10분 이상의 지촉 건조 특성을 나타내는 바, 본 발명의 투명 코팅제가 상온 경화 특성이 더욱 우수한 것을 보여준다.On the other hand, in the case of the conventional transparent coating agent, it exhibits touch drying characteristics for more than 10 minutes at around 60°C, showing that the transparent coating agent of the present invention has better room temperature curing characteristics.
이와 같이 차량 보수용 상온 경화형 투명 코팅제에 대하여 그 구체적인 실시예를 살펴보면 다음과 같다.Specific examples of the room temperature curing transparent coating agent for vehicle repair are as follows.
1. 차량 보수용 상온 경화형 투명 코팅제의 제조 One . Manufacture of room temperature curing transparent coating for vehicle repair
실시예 1Example 1
주제로서, 화학식 1로 표시되는 제1수지 100중량부에 대하여, 화학식 2로 표시되는 제2수지 10중량부, 유기 용매(디메틸 카보네이트와 메틸이소부틸케톤을 1:1로 혼합) 35중량부를 상온에서 혼합한 후, 화학식 3(x=5)으로 표시되는 첨가제 2중량부를 혼합하였다.As a subject, for 100 parts by weight of the first resin represented by Formula 1, 10 parts by weight of the second resin represented by Formula 2, and 35 parts by weight of an organic solvent (dimethyl carbonate and methyl isobutyl ketone mixed 1:1) at room temperature. After mixing, 2 parts by weight of the additive represented by Chemical Formula 3 (x=5) was mixed.
경화제로서, 화학식 4로 표시되는 지방족 폴리이소시아네이트 100중량부에 대하여, 유기 용매인 자일렌 80중량부를 상온에서 혼합하였다.As a curing agent, 80 parts by weight of xylene, an organic solvent, were mixed at room temperature with respect to 100 parts by weight of aliphatic polyisocyanate represented by Chemical Formula 4.
상기 주제 50중량% 및 경화제 50중량%를 상온에서 혼합하여 투명 코팅제를 제조하였다. A transparent coating agent was prepared by mixing 50% by weight of the base material and 50% by weight of the curing agent at room temperature.
실시예 2Example 2
주제에서 제2수지 20중량부를 혼합한 점을 제외하고는 실시예 1과 동일한 조건으로 투명 코팅제를 제조하였다. A transparent coating agent was prepared under the same conditions as Example 1, except that 20 parts by weight of the second resin was mixed.
실시예 3Example 3
주제에서 유기 용매 50중량부를 혼합한 점을 제외하고는 실시예 1과 동일한 조건으로 투명 코팅제를 제조하였다. A transparent coating agent was prepared under the same conditions as Example 1, except that 50 parts by weight of an organic solvent was mixed.
실시예 4Example 4
주제에서 첨가제 4중량부를 혼합한 점을 제외하고는 실시예 1과 동일한 조건으로 투명 코팅제를 제조하였다. A transparent coating agent was prepared under the same conditions as Example 1, except that 4 parts by weight of additives were mixed.
실시예 5Example 5
경화제에서 유기 용매 90중량부를 혼합한 점을 제외하고는 실시예 1과 동일한 조건으로 투명 코팅제를 제조하였다. A transparent coating agent was prepared under the same conditions as Example 1, except that 90 parts by weight of an organic solvent was mixed in the curing agent.
실시예 6Example 6
주제 550중량% 및 경화제 45중량%를 혼합한 점을 제외하고는 실시예 1과 동일한 조건으로 투명 코팅제를 제조하였다.A transparent coating agent was prepared under the same conditions as Example 1, except that 550% by weight of the base material and 45% by weight of the hardener were mixed.
실시예 7Example 7
주제에서 제2수지 5중량부를 혼합한 점을 제외하고는 실시예 1과 동일한 조건으로 투명 코팅제를 제조하였다. A transparent coating agent was prepared under the same conditions as Example 1, except that 5 parts by weight of the second resin was mixed.
실시예 8Example 8
주제에서 제2수지 30중량부를 혼합한 점을 제외하고는 실시예 1과 동일한 조건으로 투명 코팅제를 제조하였다. A transparent coating agent was prepared under the same conditions as Example 1, except that 30 parts by weight of the second resin was mixed.
실시예 9Example 9
주제에서 유기 용매 30중량부를 혼합한 점을 제외하고는 실시예 1과 동일한 조건으로 투명 코팅제를 제조하였다. A transparent coating agent was prepared under the same conditions as Example 1, except that 30 parts by weight of an organic solvent was mixed.
실시예 10Example 10
주제에서 유기 용매 55중량부를 혼합한 점을 제외하고는 실시예 1과 동일한 조건으로 투명 코팅제를 제조하였다. A transparent coating agent was prepared under the same conditions as Example 1, except that 55 parts by weight of an organic solvent was mixed.
실시예 11Example 11
주제에서 첨가제 1중량부를 혼합한 점을 제외하고는 실시예 1과 동일한 조건으로 투명 코팅제를 제조하였다. A transparent coating agent was prepared under the same conditions as Example 1, except that 1 part by weight of the additive was mixed.
실시예 12Example 12
주제에서 첨가제 5중량부를 혼합한 점을 제외하고는 실시예 1과 동일한 조건으로 투명 코팅제를 제조하였다. A transparent coating agent was prepared under the same conditions as Example 1, except that 5 parts by weight of additives were mixed.
실시예 13Example 13
경화제에서 유기 용매 75중량부를 혼합한 점을 제외하고는 실시예 1과 동일한 조건으로 투명 코팅제를 제조하였다. A transparent coating agent was prepared under the same conditions as Example 1, except that 75 parts by weight of an organic solvent was mixed in the curing agent.
실시예 14Example 14
경화제에서 유기 용매 95중량부를 혼합한 점을 제외하고는 실시예 1과 동일한 조건으로 투명 코팅제를 제조하였다. A transparent coating agent was prepared under the same conditions as Example 1, except that 95 parts by weight of an organic solvent was mixed in the curing agent.
2. 물성 평가 방법 및 그 결과2. Physical property evaluation method and results
1) TVOCs(mg/m2) : Headspace method(100℃, 1시간) 으로 측정하였으며, 2.0이하를 기준치로 하였다.1) TVOCs (mg/m 2 ): Measured using the headspace method (100℃, 1 hour), and 2.0 or less was set as the standard value.
2) 경화 시간 : KS M ISO 6721-10에 따라, 소재 표면에 롤러를 사용하여 투명 코팅제를 도포한 후, 25℃ 및 수분 40%의 조건 하에 완전히 경화되는 시간을 측정하였다.2) Curing time: In accordance with KS M ISO 6721-10, the transparent coating was applied to the surface of the material using a roller, and then the time for complete curing was measured under the conditions of 25°C and 40% moisture.
3) 경화도(%) 측정 : 소재 표면에 롤러를 사용하여 투명 코팅제를 도포한 후, 25℃ 및 수분 85%의 조건 하에 10분 동안 방치하였다. 방치하기 전 초기 무게 대비 방치 후의 무게 비율을 측정하여 경화도(%)를 도출하였다.3) Measurement of degree of cure (%): A transparent coating was applied to the surface of the material using a roller and left for 10 minutes at 25°C and 85% moisture. The degree of hardness (%) was derived by measuring the ratio of the weight after leaving compared to the initial weight before leaving.
3) 평활성 : 도막의 평활 정도를 육안으로 관찰하여, 상당히 평활하면 A, 전체 면적의 10% 이상의 요철이 있으면 B로 나타내었다.3) Smoothness: The degree of smoothness of the coating film was observed with the naked eye. If it was fairly smooth, it was indicated as A, and if it had irregularities of more than 10% of the total area, it was indicated as B.
[표 1][Table 1]
표 1의 결과를 살펴보면, 본 발명의 조성비를 모두 만족한 실시예 1 내지 6의 경우 VOC가 배출되지 않았고, 상온에서의 경화 시간이 굉장히 단축된 것을 확인할 수 있다. 또한 25℃ 및 수분 85%의 조건에서도 97% 이상의 높은 경화도를 나타내었으며, 도막의 평활성이 매우 우수하였다.Looking at the results in Table 1, it can be seen that in Examples 1 to 6, which all satisfied the composition ratio of the present invention, no VOC was emitted and the curing time at room temperature was greatly shortened. In addition, it showed a high degree of curing of over 97% even at 25°C and 85% moisture, and the smoothness of the coating film was very excellent.
반면, 본 발명의 조성비를 벗어난 실시예 7 내지 14의 경우, VOC가 약간 검출되거나, 경화 특성이 상대적으로 낮은 결과를 보였다. 또한 도막에 약간의 요철도 형성된 것을 확인할 수 있다.On the other hand, in Examples 7 to 14, which deviated from the composition ratio of the present invention, VOC was slightly detected or curing characteristics were relatively low. It can also be seen that some irregularities were formed in the paint film.
이상과 같이 본 발명에 대해서 예시한 실시예와 표를 참조로 하여 설명하였으나, 본 명세서에 개시된 실시예와 표에 의해 본 발명이 한정되는 것은 아니며, 본 발명의 기술사상의 범위 내에서 통상의 기술자에 의해 다양한 변형이 이루어질 수 있음은 자명하다. 아울러 앞서 본 발명의 실시 예를 설명하면서 본 발명의 구성에 따른 작용 효과를 명시적으로 기재하여 설명하지 않았을 지라도, 해당 구성에 의해 예측 가능한 효과 또한 인정되어야 함은 당연하다.As described above, the present invention has been described with reference to the illustrative examples and tables, but the present invention is not limited by the examples and tables disclosed in this specification, and can be understood by those skilled in the art within the scope of the technical idea of the present invention. It is obvious that various modifications can be made. In addition, although the operational effects according to the configuration of the present invention were not explicitly described and explained while explaining the embodiments of the present invention above, it is natural that the predictable effects due to the configuration should also be recognized.
Claims (8)
상기 주제는
[화학식 1]로 표시되는 화합물을 포함하는 제1수지 100중량부에 대하여,
[화학식 2]로 표시되는 화합물을 포함하는 제2수지 10 ~ 20중량부,
유기 용매 35 ~ 50중량부, 및
표면 조절용 첨가제 2 ~ 4중량부를 포함하며,
상기 경화제는 지방족 폴리이소시아네이트 100중량부에 대하여, 유기 용매 80 ~ 90중량부를 포함하는 투명 코팅제.
[화학식 1]
[화학식 2]
Contains base material and hardener,
The above topic is
With respect to 100 parts by weight of the first resin containing the compound represented by [Formula 1],
10 to 20 parts by weight of a second resin containing a compound represented by [Formula 2],
35 to 50 parts by weight of organic solvent, and
Contains 2 to 4 parts by weight of additive for surface control,
The curing agent is a transparent coating agent containing 80 to 90 parts by weight of an organic solvent based on 100 parts by weight of aliphatic polyisocyanate.
[Formula 1]
[Formula 2]
상기 유기 용매는 디메틸 카보네이트, 메틸이소부틸케톤, n-부틸 아세테이트, 프로필렌 글리콜 및 모노메틸 에테르 아세테이트 중 1종 이상을 포함하는 투명 코팅제.
According to paragraph 1,
The organic solvent is a transparent coating agent comprising one or more of dimethyl carbonate, methyl isobutyl ketone, n-butyl acetate, propylene glycol, and monomethyl ether acetate.
상기 표면 조절용 첨가제는 [화학식 3]으로 표시되는 알킬 에테르 변성 폴리디메틸실록산을 포함하는 투명 코팅제.
[화학식 3]
화학식 3에서 x는 1 ~ 100의 정수이다.
According to paragraph 1,
The surface control additive is a transparent coating agent containing alkyl ether-modified polydimethylsiloxane represented by [Formula 3].
[Formula 3]
In Formula 3, x is an integer from 1 to 100.
상기 유기 용매는 자일렌 및 n-부틸 아세테이트 중 1종 이상을 포함하는 투명 코팅제.
According to paragraph 1,
The organic solvent is a transparent coating agent containing at least one of xylene and n-butyl acetate.
상기 주제 : 경화제의 혼합비는 45 ~ 55중량% : 45 ~ 55중량%인 투명 코팅제.
According to paragraph 1,
Above subject: A transparent coating agent in which the mixing ratio of the hardener is 45 to 55% by weight: 45 to 55% by weight.