KR102619991B1 - 소화물질이 포함된 캡슐 및 이를 포함하는 난연성 조성물 - Google Patents
소화물질이 포함된 캡슐 및 이를 포함하는 난연성 조성물 Download PDFInfo
- Publication number
- KR102619991B1 KR102619991B1 KR1020180162861A KR20180162861A KR102619991B1 KR 102619991 B1 KR102619991 B1 KR 102619991B1 KR 1020180162861 A KR1020180162861 A KR 1020180162861A KR 20180162861 A KR20180162861 A KR 20180162861A KR 102619991 B1 KR102619991 B1 KR 102619991B1
- Authority
- KR
- South Korea
- Prior art keywords
- capsule
- shell
- fire
- monomer
- resin
- Prior art date
Abstract
본 발명은 연소반응을 종결시키기 위하여 산소공급을 차단하거나, 가연물을 냉각시키거나, 연소반응이 연쇄적으로 일어나게 하는 물질을 비활성화시킬 수 있는 소화물질을 쉘에 포집하여 캡슐화시켜 제조된 소화물질이 포함된 캡슐을 난연성 조성물에 포함시켜 수배전반, 전기 박스, 자동차, 변압기, 서버, 건축물, 선박 및 해양구조물 내외부 또는 단열재의 표면에 상기 조성물을 성형한 시트(sheet), 코팅(coating) 또는 필름 형태로 부착함으로써, 평상시에는 대상 구조 표면을 보호하는 역할을 하나 화재가 발생되어 소정의 온도 이상으로 주변 온도가 상승하게 되면 자동적으로 캡슐의 쉘이 온도에 의해 와해되어 소화물질이 외부로 방출됨으로써 불꽃주위의 산소를 밀어내고, 가연물을 냉각시키는 역할을 하여 초기에 화재를 진압하거나 화재가 번지는 것을 예방할 수 있는 소화물질이 포함된 캡슐 및 이를 포함하는 난연성 조성물을 제공한다.
Description
본 발명은 화재 시 소화를 시킬 수 있는 소화물질이 포함된 캡슐 및 이를 포함한 난연성 조성물에 관한 것으로, 보다 상세하게는 화재 시 가연물에 공급되는 산소를 차단하거나, 냉각을 통해 연소반응을 중단시킬 수 있는 소화물질을 포함하는 캡슐 및 이를 포함하는 난연성 조성물에 관한 것이다.
기술의 발전으로 인해 전기를 사용하는 다양한 기계들, 예를 들어 가전제품이나 공장에서 사용하는 로봇들이 다수 사용되고 있으며, 이에 동력을 제공하는 전기의 중요성이 부각되고 있다.
이러한 전기를 일반 가정까지 전달되는 과정은 예를 들어, 발전소 - 1차 변전소 - 2차 변전소 - 자가용 변전실 - 수전반 - 변압기 - 배전반 - 동별분전반 - 계량기함 - 세대 분전반을 통해 각 가정으로 전달된다.
상기 수전반(受電盤)은 말 그대로 전기를 받는 패널로서, 수전반은 변압기 이전의 패널이고, 그리고 배전반(配電盤)은 전기를 나누어 주는 패널로서, 배전반은 변압기 이후의 패널이다.
이러한 수전반 및 배전반(이하, ‘수배전반’이라 함)은 과전류나 과부하 또는 단락 등에 의하여 전기 과열로 화재 발생의 위험이 내재되어 있다.
수배전반의 화재로 인한 고장은 현대 사회에 없어서는 안 되는 전기의 공급이 끊김을 의미하며, 이로 인한 경제, 사회적 손실이 막대하다고 할 수 있다.
따라서, 이러한 수배전반의 화재 발생에 대비하여 수배전반 내에 열감지기와 연기감지기 등이 장착되고, 외부로부터 소화약제, 예를 들어, 하론(HALON)이나 이산화탄소(CO2) 등이 분사되는 분사노즐이 구비되어 있다.
수배전반은 내부의 소정 공간에 상술한 수전반 및 배전반의 내부 구성요소가 설치되고, 다수의 수배전반이 좌우로 인접되게 나열되며, 수배전반 상면에는 소화약제와 분사노즐 및 이를 연결하는 공급배관이 설치된다.
그러나, 각 수배전반 마다 소화용 설비가 구비되어 화재 발생 시에 “화재의 인식 - 소화약제의 분사” 순서로 소화절차가 이루어지기 때문에, 화재를 인식하는 센서와 소화약제를 분사하는 설비에 대한 관리비용이 상승함은 물론, 각각의 소화약제로부터 분사노즐을 연결하는 공급배관이 각각 설치되어 그 설계가 복잡하고, 화재를 인식하는 센서의 고장 시 이를 사용자가 인식하기 쉽지 않은 문제점이 있었다.
본 발명에서는, 수배전반을 포함하여 화재가 발생 할 수 있는 모든 물체의 화재 발생 시에 연소반응을 종결시키기 위하여 산소공급을 차단하거나 가연물을 냉각시키거나 연소반응이 연쇄적으로 일어나게 하는 물질을 비활성화시킬 수 있는 소화물질을 캡슐화한 뒤, 이를 포함한 난연성 조성물을 활용하여 화재 발생 시 소화물질이 내재된 캡슐의 쉘이 파괴되면서 소화물질이 외부로 방출되어 불꽃과 가연물 사이의 방벽 역할을 하여 초기에 화재를 진압할 수 있는 소화물질이 포함된 캡슐 및 이를 포함하는 난연성 조성물을 제공하고자 한다.
본 발명은 소화물질을 포함하는 코어(core); 코어를 둘러싸며, 소정의 온도 이상에서 와해되는 쉘(shell); 상기 쉘은 에틸렌계 모노머, 스티렌계 모노머, 아크릴계 모노머, 비닐계 모노머 및 니트릴계 모노머로 이루어진 군 중에서 선택된 적어도 하나 이상의 모노머를 포함하는 모노머 혼합물을 중합한 것을 특징으로 하는 소화물질을 포함하는 캡슐을 제공한다.
또한, 상기 쉘은 에틸렌 모노머 및 비닐 아세테이트 모노머 혼합물의 공중합으로 형성되는 것을 특징으로 한다.
또한, 상기 혼합물은 에틸렌은 65 내지 85 중량% 및 상기 비닐 아세테이트는 15 내지 35 중량% 인 것을 특징으로 한다.
또한, 상기 쉘은 몬모릴로나이트, 사포나이트, 헥토라이트, 바이델라이트, 스티분사이트, 논트로나이트, 질석, 할로이사이트 및 팽윤성 마이카로 이루어진 군으로부터 선택된 1종 이상의 기체 차단성 물질을 더 포함하는 것을 특징으로 한다.
또한, 상기 쉘은 아크릴로니트릴 모노머 및 스티렌 모노머 혼합물의 공중합으로 형성되는 것을 특징으로 한다.
또한, 상기 캡슐의 형태는, 구형, 타원형, 원기둥형 또는 다각기둥형인 것을 특징으로 한다.
또한, 본 발명은 코팅제 조성물; 및 소화물질이 포함된 캡슐;을 포함하고, 상기 캡슐은,소화물질을 포함하는 코어(core); 및 상기 코어를 둘러싸며, 소정의 온도 이상에서 와해되는 쉘(shell); 상기 쉘은 에틸렌계 모노머, 스티렌계 모노머, 아크릴계 모노머, 비닐계 모노머 및 니트릴계 모노머로 이루어진 군 중에서 선택된 적어도 하나 이상의 모노머를 포함하는 모노머 혼합물을 중합한 것을 특징으로 하는 소화물질을 포함하는 캡슐을 포함하는 난연성 조성물을 제공한다.
또한, 상기 코팅제 조성물은, 폴리우레아(polyurea)수지, 폴리우레탄(polyurethane)수지, 에폭시(epoxy)수지, 폴리아미드(polyamide) 수지, 폴리아크릴(polyacryl)수지, 폴리에스터(polyester)수지 및 폴리에테르(polyether)수지로 이루어진 군 중에서 적어도 하나 이상 선택된 고분자 수지에, 유기안료 및/또는 무기안료를 포함하는 충진제, 적하 방지제, 가소제, 열안정제, 산화방지제, 광안정제, 상용화제, 염료, 침강방지제 및 분산제 중 선택된 하나 이상을 더 포함하는 것을 특징으로 한다.
아울러, 상기 코팅제 조성물은,몬모릴로나이트, 사포나이트, 헥토라이트, 바이델라이트, 스티분사이트, 논트로나이트, 질석, 할로이사이트 및 팽윤성 마이카로 이루어진 군으로부터 선택된 1종 이상의 기체 차단성 물질을 더 포함하는 것을 특징으로 한다.
본 발명은 연소반응을 종결시키기 위하여 산소공급을 차단하거나, 가연물을 냉각시키거나, 연소반응이 연쇄적으로 일어나게 하는 물질을 비활성화시킬 수 있는 소화물질을 쉘에 포집하여 캡슐화시켜 제조된 소화물질이 포함된 캡슐을 난연성 조성물에 포함시켜 수배전반, 전기 박스, 자동차, 변압기, 서버, 건축물, 선박 및 해양구조물 내외부 또는 단열재의 표면에 상기 조성물을 성형한 시트(sheet), 코팅(coating) 또는 필름 형태로 부착함으로써, 평상시에는 대상 구조 표면을 보호하는 역할을 하나 화재가 발생되어 소정의 온도 이상으로 주변 온도가 상승하게 되면 자동적으로 캡슐의 쉘이 온도에 의해 와해되어 소화물질이 외부로 방출됨으로써 불꽃주위의 산소를 밀어내고, 가연물을 냉각시키는 역할을 하여 초기에 화재를 진압하거나 화재가 번지는 것을 예방할 수 있다.
뿐만 아니라, 소화물질을 캡슐화 함으로써, 조성물과 소화물질 간의 화학적 반응성을 감소시켜 안정성이 우수할 뿐만 아니라 캡슐을 포함하는 부재의 물성저하를 방지할 수 있다.
도 1은 본 발명에 따른 소화물질이 포함된 캡슐의 SEM 사진
도 2는 소화물질이 포함된 캡슐이 열에 의해 파괴된 SEM 사진
도 3은 소화물질이 포함된 캡슐을 TGA와 DSC로 분석한 그래프
도 2는 소화물질이 포함된 캡슐이 열에 의해 파괴된 SEM 사진
도 3은 소화물질이 포함된 캡슐을 TGA와 DSC로 분석한 그래프
이하 본 발명의 바람직한 실시 예를 통해 상세히 설명하기에 앞서, 본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정하여 해석되어서는 아니 되며, 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야 함을 밝혀둔다.
본 명세서 전체에서, 어떤 부분이 어떤 구성요소를 "포함" 한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것을 의미한다.
이하에서는 본 발명의 소화물질이 포함된 캡슐 및 이를 포함하는 난연성 조성물에 관하여 보다 상세히 설명하고자 한다.
먼저, 소화물질이 포함된 캡슐은, 도 1과 같이 소화물질을 포함하는 코어(core) 및 상기 코어를 둘러싸며, 소정의 온도 이상에서 와해되는 쉘(shell);을 포함할 수 있다.
상기 소화물질은, 산소공급을 차단하거나 가연물을 냉각시키거나 연소반응이 연쇄적으로 일어나게 하는 물질을 비활성화시켜 연소 반응을 종결할 수 있도록 도움을 주는 것으로서, 화재를 진압할 수 있는 물질이면 특별히 한정되지 않고 모두 사용가능하나, 바람직하게는 물, 이산화탄소, 탄산수소나트륨(sodium bicarbonate), 인산암모늄(ammonium phosphate), 브롬화삼불화메탄(bromotrifluoromethane), 브롬화염화이플루오르화메탄(bromochlorodifluoromethane, BCF), 플루오린화수소(hydrogen fluoride), 브롬화수소(hydrogen bromide), 브롬화카르보닐(carbonyl bromide), 플루오린화카르보닐(carbonyl fluoride) 및 수소불화탄소(hydrofluorocarbon, HFC) 로 이루어진 군 중에서 선택된 하나 이상을 사용할 수 있다.
상기한 소화물질 중에 수소불화탄소를 선택하여 사용할 수 있으며, 본 발명의 일 실시예로 수소불화탄소인 3M사의 노벡 1230(Novec 1230)을 사용하여 소화용 마이크로캡슐을 제조하였다.
상기 코어에는 소화물질 외에도, 유화제, 분산제, 계면활성제, 방청제, pH조정제 또는 흡습 방지제를 더 포함할 수 있으며, 이는 상기 소화물질의 산소공급을 차단하거나 가연물을 냉각시키거나 연소반응이 연쇄적으로 일어나게 하는 물질을 비활성화시켜 연소 반응을 종결할 수 있는 효과에 영향을 미치지 않을 양만큼만 적절히 조절하여 더 포함될 수 있다.
상기 코어를 둘러싸 코어의 소화물질을 보호하고, 화학적 안정성을 향상시키기 위한 쉘은 70 ~ 250 ℃ 온도에서 와해되거나 녹는 특징이 있는 합성수지면 특별히 한정되지 않고 사용 가능하며, 바람직하게는 에틸렌계 모노머, 스티렌계 모노머, 아크릴계 모노머, 비닐계 모노머 및 니트릴계 모노머로 이루어진 군 중에서 선택된 적어도 하나 이상의 모노머를 포함하는 모노머 혼합물을 중합한 것으로 더욱 바람직하게는 에틸렌 모노머 및 비닐 아세테이트 모노머 혼합물의 공중합으로 형성될 수 있다.
또한, 에틸렌 모노머 및 비닐 아세테이트 모노머의 혼합물을 공중합하여 쉘을 형성하는 경우에 에틸렌은 65 내지 85 중량% 및 비닐 아세테이트는 15 내지 35중량%의 비율로 형성될 수 있다.
또한, 쉘은 몬모릴로나이트, 사포나이트, 헥토라이트, 바이델라이트, 스티분사이트, 논트로나이트, 질석, 할로이사이트 및 팽윤성 마이카로 이루어진 군으로부터 선택된 1종 이상의 기체 차단성 물질을 더 포함할 수 있다.
기체 차단성 물질은 중합된 고분자의 내부에 분산된 층의 형태(Dispersed layer)로 형성되며, 고분자가 가지고 있는 자유 체적(free volume)의 틈을 메워 기체가 이동할 수 있는 통로(Path of Gas)를 복잡하게 함으로써, 기체의 투과를 지연 또는 저지(Retardation)하여 차단과 유사 또는 동일한 효과를 나타낸다.
본 발명에서의 기체 차단성 물질은 공지된 다양한 나노 사이즈의 클레이를 사용할 수 있으나, 바람직하게는 몬모릴로나이트(montmorillonite)를 사용할 수 있다. 몬모릴로나이트는 자연에 풍부하게 존재하여 저렴한 비용으로 사용할 수 있으며, 높은 종횡비(aspect raito)를 가지고 있다. 나노 사이즈의 몬모릴로나이트를 필러로 사용하여 쉘 내에서 분산시키면, 쉘의 자유 체적을 충실히 메꿀 수 있어 기체차단성이 향상될 수 있다.
본 발명에서 몬모릴로나이트는 900 ㎚이하의 사이즈를 가지는 나노 클레이를 사용할 수 있다.
상기 코어를 쉘에 포집하여 본 발명의 소화물질이 포함된 캡슐을 제조하는 방법은 일반적으로 어떠한 물질을 합성수지를 사용하여 폐쇄시켜 캡슐화시키는 방법이면 특별히 한정되지 않고 모두 사용할 수 있다.
일 예로, 본 발명의 소화물질이 포함된 캡슐의 제조시, 쉘을 제조하기 위한 합성수지로 AN(acrylonitrile)의 모노머를 사용하고, 소화물질, 분산제로는 PVA(Polyvinyl alcohol)을 사용한다. 계면활성제로는 SDS(Sodium dodecyl sulfate)을 사용한다. 그리고 개시제로는 AIBN(Azobisisobutylnitrile)을 사용할 수 있다.
먼저, 소화물질을 분산제로 분산시키는데, 즉 물 50㎖에 PVA(Polyvinyl alcohol) 0.1 ~ 2 g을 넣어 분산액을 제조한 뒤, 물 100 ㎖에 소화물질인 3M사의 노벡1230(Novec1230)을 20 ~ 60 ㎖ 및 SDS 0.1 ~ 0.8 g을 혼합한 후 상기 제조된 분산액에 투입하여 반응기에서 2시간 저도 교반시켜 혼합물을 제조한 후, 물 10㎖에 AN 1 ~ 30 ㎖을 넣은 쉘 용액을 분산된 혼합물에 넣은 후 약 1500 ~ 3000rpm으로 1시간 동안 추가 교반하여 소화물질이 포함된 캡슐을 제조할 수 있다.
본 발명의 소화물질이 포함된 캡슐의 형태는 도 1 또는 도 2에서 구형으로 형성된 예를 제시하였으나, 특별히 한정되지 않고 다양한 형태를 가질 수 있으며, 바람직하게는 구형, 타원형, 원기둥형, 또는 다각기둥 형태일 수 있고, 상기 캡슐의 크기는 ㎛ 단위에서부터 mm 단위까지 특별히 한정되지 않고 사용 가능하며, 바람직하게는 약 0.01 ~ 10㎛, 보다 바람직하게는 약 0.1 ~ 5㎛ 크기일 수 있다.
상기 소화물질이 포함된 캡슐은, 외기 온도가 소정의 온도 이상으로 상승하게 되면 캡슐의 쉘이 파괴되면서 쉘 내부의 코어가 외부로 방출되는 것으로서, 상기 쉘을 이루고 있는 고분자의 종류에 따라 쉘이 와해되거나 녹는 온도를 제어할 수 있으며, 쉘의 두께 및 크기를 제어함으로써, 소화물질의 방출 속도도 제어할 수 있다.
따라서, 상기 소화물질이 포함된 캡슐의 쉘을 이루고 있는 합성 수지 및 두께, 크기는 상기 캡슐이 포함되어 제조된 가 사용되는 사용양태, 사용방법, 사용환경에 따라 적절하게 조절될 수 있다.
한편, 본 발명의 다른 실시 형태는, 소화물질이 포함된 캡슐을 포함하는 난연성이 향상된 조성물로서, 바람직하게는 코팅제 조성물 및 소화물질이 포함된 캡슐을 포함할 수 있다.
상기 소화물질이 포함된 캡슐은, 위에서 구체적으로 언급하였으므로 여기서는 생략하기로 한다.
상기 코팅제 조성물은 일반적으로 코팅 대상의 구조물 표면을 보호하는 기능을 하거나 또는 시트, 필름 형태로 형성되는 모든 수지 바인더 또는 고분자 수지면 특별히 한정되지 않고 사용 가능하나, 바람직하게는 폴리우레아(polyurea)수지, 폴리우레탄(polyurethane)수지, 에폭시(epoxy)수지, 폴리아미드(polyamide) 수지, 폴리아크릴(polyacryl)수지, 폴리에스터(polyester)수지 및 폴리에테르(polyether)수지로 이루어진 군 중에서 적어도 하나 이상 선택된 것을 포함할 수 있으며, 본 발명의 소화물질이 포함된 캡슐을 포함하는 난연성이 향상된 조성물은 상기 코팅제 조성물에 소화물질이 포함된 캡슐 외 유기안료 및/또는 무기안료를 포함하는 충진제, 적하 방지제, 가소제, 열 안정제, 산화방지제, 광안정제, 상용화제, 염료, 침강방지제 및 분산제 중 선택된 하나 이상을 더 포함할 수 있다.
바람직하게는 상기 고분자 수지에 소화물질이 포함된 캡슐 외 더 포함되는 물질들은 조성물이 코팅대상이 되는 구조물 표면에 코팅되어 코팅층을 형성함으로써, 얻어질 수 있는 효과에 영향을 미치지 않을 양만큼만 적절히 조절하여 더 포함될 수 있다.
또는, 상술한 몬모릴로나이트, 사포나이트, 헥토라이트, 바이델라이트, 스티분사이트, 논트로나이트, 질석, 할로이사이트 및 팽윤성 마이카로 이루어진 군으로부터 선택된 1종 이상의 기체 차단성 물질을 더 포함할 수 있다.
또한, 상기 소화물질이 포함된 캡슐을 포함하는 난연성이 향상된 조성물에 포함되는 소화물질이 포함된 캡슐은 고분자 수지 100 중량부에 대하여 10 ~ 50 중량부 포함될 수 있으며, 10 중량부 미만으로 포함시 화재를 방지하는 충분한 효과를 얻지 못할 수 있고, 50 중량부를 초과하게 되면 코팅시 접착성이 떨어져 코팅층이 박리되는 문제가 발생될 수 있다.
일 예로, 본 발명의 소화물질이 포함된 캡슐을 포함하는 난연성이 향상된 조성물이 코팅대상이 되는 표면 즉, 기재상에 도포되어 코팅층을 형성할 수 있으며, 상기 코팅층 내 소화물질이 포함된 캡슐이 포함된다.
이로써, 상기 코팅층은 평상시에는 대상 구조 표면을 보호하는 역할을 하다가, 화재가 발생되어 소정의 온도 이상으로 주변 온도가 상승하게 되면 상기 코팅층 내부의 소화물질이 포함된 캡슐의 쉘이 와해되어 상기 소화물질이 포함된 코어가 외부로 방출됨으로써 불꽃과 가연물 사이의 방벽 역할을 하여 초기에 화재를 진압하거나 화재가 번지는 것을 예방할 수 있다.
일반적으로 시중에 널리 사용중인 난연성 조성물의 경우, 고분자 수지에 난연성 효과가 있는 물질, 유기안료 및/또는 무기안료를 포함하는 충진제, 적하 방지제, 가소제, 열안정제, 산화방지제, 광안정제, 상용화제, 염료, 침강방지제 및 분산제 등등 각종 물질이 혼합되어 제조되고, 이러한 일반적인 난연성 를 사용하여 코팅시, 난연성 효과가 있는 물질로 인하여 본래의 목적인 코팅대상인 구조 표면에 완벽히 부착되지 않아 보호효과가 떨어질 우려가 있을 뿐만 아니라, 시간이 경과함에 따라 코팅물 내 포함된 각종 물질 간의 화학 반응 또는 외부에서 유입되는 외부인자로 인하여 난연성 효과가 있는 물질의 물리적 성질이 변화하거나 기능이 저하되는 문제가 있었다.
그러나, 본 발명의 소화물질이 포함된 캡슐을 포함하는 난연성이 향상된 조성물의 경우, 연소반응을 종결시키기 위하여 산소공급을 차단하거나, 가연물을 냉각시키거나, 연소반응이 연쇄적으로 일어나게 하는 물질을 비활성화시킬 수 있는 소화물질이 합성 수지로 인하여 코팅되어 있어 외부와의 접촉이 차단되어 시간이 경과되어도 상기 소화물질의 물성이 변화되거나 활성이 저하되는 우려가 적을 뿐만 아니라, 조성물 내 포함시에도 각종 물질 간의 화학적 반응을 저감시켜 저장안정성, 화학적 안정성이 뛰어나다.
따라서, 본 발명의 소화물질이 포함된 캡슐을 포함하는 난연성이 향상된 조성물을 사용하여 코팅하여 코팅층을 형성하게 되면, 평상시에는 대상 구조 표면을 보호하는 역할을 하다가, 화재가 발생되어 소정의 온도 이상으로 주변 온도가 상승하게 되면 상기 코팅층 내부의 소화물질이 포함된 캡슐의 쉘이 와해되어 상기 소화물질이 외부로 방출됨으로써 불꽃과 가연물 사이의 방벽 역할을 하여 초기에 화재를 진압하거나 화재가 번지는 것을 예방할 수 있다.
Claims (9)
- 코팅제 조성물; 및 소화물질이 포함된 캡슐;을 포함하고,
상기 코팅제 조성물은,
폴리우레아(polyurea)수지, 폴리우레탄(polyurethane)수지, 에폭시(epoxy)수지, 폴리아미드(polyamide) 수지, 폴리아크릴(polyacryl)수지, 폴리에스터(polyester)수지 및 폴리에테르(polyether)수지로 이루어진 군 중에서 적어도 하나 이상 선택된 고분자 수지에,
유기안료 및/또는 무기안료를 포함하는 충진제, 적하 방지제, 가소제, 열안정제, 산화방지제, 광안정제, 상용화제, 염료, 침강방지제 및 분산제 중 선택된 하나 이상을 더 포함하고,
상기 코팅제 조성물은,
몬모릴로나이트, 사포나이트, 헥토라이트, 바이델라이트, 스티분사이트, 논트로나이트, 질석, 할로이사이트 및 팽윤성 마이카로 이루어진 군으로부터 선택된 1종 이상의 기체 차단성 물질을 더 포함하되,
900 ㎚이하의 사이즈를 가지는 기체 차단성 물질을 필러로 사용하여 코팅제 조성물 내에서 분산시킴으로써 코팅제 조성물의 자유 체적(free volume)의 틈을 메워 기체가 이동할 수 있는 통로(Path of Gas)를 통한 기체의 투과를 지연 또는 저지(Retardation)하고,
상기 캡슐은,
소화물질을 포함하는 코어(core); 및
코어를 둘러싸며, 소정의 온도 이상에서 와해되는 쉘(shell);을 포함하고,
상기 소화물질은 수소불화탄소(hydrofluorocarbon, HFC)를 포함하고,
상기 쉘은 에틸렌계 모노머, 스티렌계 모노머, 아크릴계 모노머, 비닐계 모노머 및 니트릴계 모노머로 이루어진 군 중에서 선택된 적어도 하나 이상의 모노머를 포함하는 모노머 혼합물을 중합하여 형성하되,
상기 쉘은 에틸렌 모노머 및 비닐 아세테이트 모노머 혼합물의 공중합으로 형성되거나 아크릴로니트릴 모노머 및 스티렌 모노머 혼합물의 공중합으로 형성되고,
상기 에틸렌 모노머 및 비닐 아세테이트 모노머 혼합물의 공중합으로 쉘이 형성될 때에는 혼합물은 에틸렌 65 내지 85 중량% 및 비닐 아세테이트 15 내지 35 중량%를 포함하고,
상기 캡슐의 형태는, 구형, 타원형, 원기둥형 또는 다각기둥형 중 하나인 것을 특징으로 하는 소화물질이 포함된 캡슐을 포함하는 난연성 조성물. - 삭제
- 삭제
- 삭제
- 삭제
- 삭제
- 삭제
- 삭제
- 삭제