KR102498314B1 - Battery package including heat insulating film - Google Patents

Battery package including heat insulating film Download PDF

Info

Publication number
KR102498314B1
KR102498314B1 KR1020150153426A KR20150153426A KR102498314B1 KR 102498314 B1 KR102498314 B1 KR 102498314B1 KR 1020150153426 A KR1020150153426 A KR 1020150153426A KR 20150153426 A KR20150153426 A KR 20150153426A KR 102498314 B1 KR102498314 B1 KR 102498314B1
Authority
KR
South Korea
Prior art keywords
battery
insulating film
batteries
battery pack
nanofiber web
Prior art date
Application number
KR1020150153426A
Other languages
Korean (ko)
Other versions
KR20160052424A (en
Inventor
노승윤
최원길
조현우
남지현
장주희
Original Assignee
주식회사 아모그린텍
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 아모그린텍 filed Critical 주식회사 아모그린텍
Publication of KR20160052424A publication Critical patent/KR20160052424A/en
Application granted granted Critical
Publication of KR102498314B1 publication Critical patent/KR102498314B1/en

Abstract

배터리 패키지가 제공된다. 본 발명의 일 실시예에 따른 배터리 패키지는 복수개의 배터리들이 내장되는 배터리 팩, 및 상기 배터리 팩 내에 배치되고 상기 배터리들을 선택적으로 구획하며 상기 배터리들 간의 열전도를 방지 또는 차단하는 단열막을 포함하여 구현된다. 이에 의하면, 배터리의 내부에서 발생되는 열 또는 외부에서 배터리에 가해지는 열의 이동을 차단하여 전자기기의 기능 및 내구성 향상시킬 수 있다. 또한, 배터리 내부 전해 물질이 누출되는 것을 방지할 수 있다.A battery package is provided. A battery package according to an embodiment of the present invention is implemented by including a battery pack in which a plurality of batteries are embedded, and an insulating film disposed in the battery pack, selectively partitioning the batteries, and preventing or blocking heat conduction between the batteries. . According to this, it is possible to improve the function and durability of the electronic device by blocking the movement of heat generated inside the battery or heat applied to the battery from the outside. In addition, leakage of the electrolyte material inside the battery can be prevented.

Description

단열막을 포함하는 배터리 패키지{Battery package including heat insulating film}Battery package including heat insulating film {Battery package including heat insulating film}

본 발명은 배터리 패키지에 관한 것으로, 더욱 상세하게는 단열막을 포함하는 배터리 패키지에 관한 것이다.The present invention relates to a battery package, and more particularly, to a battery package including an insulating film.

최근 들어 전자제품의 디지털화 및 고성능화로 인해 소형화, 박형화, 경량화, 및 고에너지 밀도를 만족할 수 있는 고용량 전원 공급 장치의 개발이 활발하다.Recently, due to digitalization and high performance of electronic products, development of high-capacity power supply devices capable of satisfying miniaturization, thinning, light weight, and high energy density has been actively pursued.

따라서, 최근에는 전술된 조건을 만족시키기 위해 고에너지 밀도 및 대용량을 갖는 리튬이온 이차전지, 리튬이온 고분자전지, 슈퍼커패시터(전기이중층 캐패시터 (Electric double layer capacitor) 및 수도 커패시터(Pseudo capacitor)) 등과 같은 전원 공급 장치가 개발되고 있다.Therefore, recently, in order to satisfy the above-mentioned conditions, lithium ion secondary batteries, lithium ion polymer batteries, and supercapacitors (electric double layer capacitors and pseudo capacitors) having high energy density and large capacity, such as Power supplies are being developed.

일반적으로, 고용량의 에너지가 필요한 전자기기에 전원을 공급하기 위해 배터리가 사용될 수 있다. 고용량의 에너지를 공급하기 위해선 복수개의 배터리가 직렬 또는 병렬로 연결된 형태의 배터리를 배터리 팩(battery pack) 내부에 수용시켜서 하나의 배터리 패키지 형태로 사용하는 것이 일반적이다.In general, a battery may be used to supply power to an electronic device requiring a high amount of energy. In order to supply high-capacity energy, it is common to accommodate a plurality of batteries connected in series or in parallel in a battery pack and use them as a single battery package.

전술된 패키지 형태의 전원공급장치가 소형화 또는 박형화된 전자기기에 적용되기 위해서는 복수의 배터리를 최대한 밀착시켜 배터리 팩 내에 수용시키게 된다. 하지만, 배터리의 내부에서 발생되는 열 또는 외부에서 배터리에 가해지는 열이 인접하는 배터리를 통해 전도되어 전자기기의 기능, 내구성을 저하시키는 문제점이 있다. 또한, 위와 같이 발생된 열은 배터리 내에 기체를 발생시키거나 전해 물질을 열팽창시켜 전해 물질 누출을 야기하는 문제점이 있다.In order to apply the above-described packaged power supply to a miniaturized or thinned electronic device, a plurality of batteries are brought into close contact with each other and accommodated in a battery pack. However, there is a problem in that heat generated inside the battery or heat applied to the battery from the outside is conducted through an adjacent battery, thereby deteriorating the function and durability of the electronic device. In addition, the heat generated as described above generates gas in the battery or thermally expands the electrolyte, causing leakage of the electrolyte.

KR 2014-0118264 AKR 2014-0118264 A KR 2014-0121205 AKR 2014-0121205 A

본 발명은 상기와 같은 점을 감안하여 안출한 것으로, 배터리의 내부에서 발생되는 열 또는 외부에서 배터리에 가해지는 열의 이동을 차단하여 전자기기의 기능 및 내구성을 향상시킬 수 있는 배터리 패키지를 제공하는 데 그 목적이 있다.The present invention has been devised in view of the above points, to provide a battery package that can improve the function and durability of electronic devices by blocking the movement of heat generated inside the battery or heat applied to the battery from the outside. It has a purpose.

또한, 본 발명은 열로 인해 배터리 내에 기체를 발생시키거나, 전해 물질이 열팽창되는 것을 방지하여 배터리 내부 전해 물질 외부로 누출되는 것을 억제할 수 있는 배터리 패키지를 제공하는 데 다른 목적이 있다.In addition, another object of the present invention is to provide a battery package capable of suppressing leakage of an electrolyte material inside a battery by preventing generation of gas in the battery due to heat or thermal expansion of the electrolyte material.

상술한 과제를 해결하기 위하여, 본 발명은 복수개의 배터리들이 내장되는 배터리 팩, 및 상기 배터리 팩 내에 배치되고 상기 배터리들을 선택적으로 구획하며 상기 배터리들 간의 열전도를 방지 또는 차단하는 단열막을 포함하는 배터리 패키지를 제공한다.In order to solve the above problems, the present invention is a battery package including a battery pack in which a plurality of batteries are embedded, and an insulating film disposed in the battery pack, selectively partitioning the batteries, and preventing or blocking heat conduction between the batteries. provides

본 발명의 일 실시예에 의하면, 상기 단열막은 상기 배터리들을 각각 구획할 수 있다.According to one embodiment of the present invention, the insulating film may partition the batteries.

또한, 상기 배터리 팩은 일면이 개구될 수 있다.Also, one surface of the battery pack may be open.

또한, 상기 배터리의 표면 및 단열막 사이에 접착제층을 더 포함할 수 있다.In addition, an adhesive layer may be further included between the surface of the battery and the insulating film.

또한, 상기 접착제층은 폴리프탈레이트, PPa(acid modified polypropylene) 또는 PEa(acid modified polyethylene) 중에서 선택된 1종 이상을 함유할 수 있다.In addition, the adhesive layer may contain at least one selected from polyphthalate, acid modified polypropylene (PPa), and acid modified polyethylene (PEa).

또한, 상기 단열막은 공기를 수용할 수 있는 다수의 미세기공이 형성된 다공성 기재 및 단열필름 중 1 종 이상을 포함할 수 있다.In addition, the insulating film may include at least one of a porous substrate having a plurality of micropores capable of accommodating air and an insulating film.

또한, 상기 다공성 기재는 섬유웹, 부직포, 직물 및 편물로 이루어진 군에서 선택된 1 종 이상의 기재를 포함하고, 상기 기재를 형성하는 섬유는 유기섬유 및 무기섬유 중 어느 하나 이상의 섬유를 포함할 수 있다.In addition, the porous substrate may include at least one substrate selected from the group consisting of a fibrous web, a nonwoven fabric, a woven fabric, and a knitted fabric, and fibers forming the substrate may include at least one of organic fibers and inorganic fibers.

또한, 상기 섬유웹은 전기방사를 통해 형성된 나노섬유웹이며, 상기 나노섬유웹을 형성하는 나노섬유는 폴리아크릴로니트릴 나노섬유, 폴리비닐리덴플루오라이드 나노섬유 및 폴리아크릴로니트릴과 폴리비닐리덴플루오라이드의 복합나노섬유 중 어느 하나 이상을 포함할 수 있다.In addition, the fiber web is a nanofiber web formed through electrospinning, and the nanofibers forming the nanofiber web are polyacrylonitrile nanofibers, polyvinylidene fluoride nanofibers, and polyacrylonitrile and polyvinylidene fluoride nanofibers. It may include any one or more of the composite nanofibers of the ride.

또한, 상기 복합나노섬유는 모노사 내에서 폴리아크릴로니트릴과 폴리비닐리덴플루오라이드가 6:4 ~ 8.5:1.5의 중량비로 혼합될 수 있다.In addition, the composite nanofibers may be mixed with polyacrylonitrile and polyvinylidene fluoride in a weight ratio of 6:4 to 8.5:1.5 in mono yarn.

또한, 상기 나노섬유웹은 평량이 2 ~ 6 g/㎡이며, 기공도가 40% 이상일 수 있다.In addition, the nanofibrous web may have a basis weight of 2 to 6 g/m 2 and a porosity of 40% or more.

한편, 본 발명의 다른 측면의 배터리 패키지는, 내부 표면 상에 단열막이 배치된 배터리 수용 홀을 적어도 하나 포함하는 배터리 팩; 및 상기 배터리 수용 홀 내에 수용되는 배터리를 포함한다.On the other hand, the battery package of another aspect of the present invention, the battery pack including at least one battery accommodating hole in which a heat insulating film is disposed on the inner surface; and a battery accommodated in the battery accommodating hole.

마지막으로, 본 발명의 또 다른 측면의 배터리 패키지는 배터리 및 단열막이 적어도 2회 교호로 배치되고, 상기 배터리 및 단열막을 패킹하는 배터리 팩을 포함한다.Finally, the battery package of another aspect of the present invention includes a battery pack in which a battery and an insulating film are alternately disposed at least twice, and the battery and the insulating film are packed.

본 발명에 의한 배터리 패키지는 배터리의 내부에서 발생되는 열 또는 외부에서 배터리에 가해지는 열의 이동을 차단하여 전자기기의 기능 및 내구성 향상시킬 수 있다. 또한, 본 발명에 의한 배터리 패키지는 열로 인해 배터리 내에 기체를 발생시키거나, 전해 물질이 열팽창되는 것을 방지하여 배터리 내부 전해 물질 외부로 누출되는 것을 억제할 수 있다.The battery package according to the present invention can improve the function and durability of an electronic device by blocking the movement of heat generated inside the battery or heat applied to the battery from the outside. In addition, the battery package according to the present invention can suppress leakage of the electrolyte material inside the battery to the outside by preventing gas generation in the battery due to heat or thermal expansion of the electrolyte material.

삭제delete

도 1은 본 발명의 일 실시예로서 복수의 배터리가 내장된 배터리 팩을 도시한 도면,
도 2는 본 발명의 다른 일 실시예로서 복수의 배터리가 내장된 배터리 팩을 도시한 도면,
그리고, 도 3은 본 발명의 또 다른 일 실시예로서 복수의 배터리가 내장된 배터리 팩을 도시한 도면이다.1 is a view showing a battery pack in which a plurality of batteries are embedded as an embodiment of the present invention;
2 is a view showing a battery pack in which a plurality of batteries are embedded as another embodiment of the present invention;
3 is a diagram showing a battery pack in which a plurality of batteries are embedded as another embodiment of the present invention.

이하, 본 발명을 보다 구체적으로 설명하기 위하여 본 발명에 따른 바람직한 실시예를 첨부된 도면을 참조하여 보다 상세하게 설명한다. 그러나, 본 발명은 여기서 설명되는 실시예에 한정되지 않고 다른 형태로 구체화될 수도 있다. 명세서 전체에 걸쳐서 동일한 참조번호들은 동일한 구성요소들을 나타낸다.Hereinafter, in order to explain the present invention in more detail, preferred embodiments according to the present invention will be described in more detail with reference to the accompanying drawings. However, the present invention is not limited to the embodiments described herein and may be embodied in other forms. Like reference numbers indicate like elements throughout the specification.

도 1 및 2를 참조하면, 본 발명의 일 실시예에 따른 배터리 패키지는 복수 개의 배터리(15)들이 내장되는 배터리 팩(10), 및 상기 배터리 팩(10) 내에 배치되고 상기 배터리(15)들을 선택적으로 구획하며 상기 배터리들(15) 간의 열전도를 방지 또는 차단하는 단열막(13)을 포함한다. 본 발명의 일 실시예에 따른 배터리 패키지는 단열막(13)을 포함함에 따라 배터리의 내부에서 발생되는 열 또는 외부에서 배터리에 가해지는 열의 이동을 차단하여 전자기기의 기능 및 내구성 향상시킬 수 있다. 또한, 열로 인해 배터리(15) 내에 기체를 발생시키거나, 전해 물질이 열팽창되는 것을 방지하여 배터리(15) 내부 전해물질이 누출되는 것을 억제할 수 있다. 1 and 2, a battery package according to an embodiment of the present invention includes a battery pack 10 in which a plurality of batteries 15 are embedded, and a battery pack 10 disposed in the battery pack 10 and storing the batteries 15. It selectively partitions and includes an insulating film 13 that prevents or blocks heat conduction between the batteries 15 . As the battery package according to an embodiment of the present invention includes the insulating film 13, the function and durability of the electronic device can be improved by blocking the movement of heat generated inside the battery or heat applied to the battery from the outside. In addition, it is possible to suppress leakage of the electrolyte inside the battery 15 by preventing generation of gas in the battery 15 due to heat or thermal expansion of the electrolyte.

상기 배터리 팩(10)은 직렬 또는 병렬로 연결된 복수개의 배터리들(15)을 내부에 수용하는 역할을 수행한다. 상기 배터리 팩(10)은 배터리들(15)을 수용할 수 있는 소정의 형태를 가질 수 있는 소재라면 제한 없이 사용이 가능하다. 일 예고, 상기 배터리 팩(10)을 형성하기 위한 소재로 절연성 수지를 사용할 수 있다. 상기 절연성 수지로 실리콘 수지, 불소 수지, 및 아크릴 수지로 이루어진 군으로부터 선택되는 적어도 하나를 사용할 수 있다.The battery pack 10 serves to accommodate a plurality of batteries 15 connected in series or parallel therein. The battery pack 10 can be used without limitation as long as the material can have a predetermined shape capable of accommodating the batteries 15 . In advance, an insulating resin may be used as a material for forming the battery pack 10 . At least one selected from the group consisting of a silicone resin, a fluororesin, and an acrylic resin may be used as the insulating resin.

상기 배터리 팩(10)은 일면이 개구될 수 있다. 이는 개구된 면을 통해 상기 배터리(15)에 전기적 접속이 가능한 다양한 단자를 연결시켜 전류를 전달 받거나 또는 외부로 전달하기 위함이다.One surface of the battery pack 10 may be open. This is to receive current or transmit it to the outside by connecting various terminals electrically connectable to the battery 15 through the open surface.

상기 배터리(15)는 일차 배터리 또는 이차 배터리일 수 있다. 일 예로, 상기 배터리(15)는 충전 및 방전이 가능한 이차 배터리가 사용될 수 있다. 이때, 상기 배터리는 원통형, 각형, 코인형 및 파우치형 중 적어도 하나의 형태를 가질 수 있다. 또한, 도 1의 배터리 패키지에서 배터리(15)를 3개 포함하는 형태로 나타냈지만, 그 개수를 한정하는 것은 아니다.The battery 15 may be a primary battery or a secondary battery. For example, the battery 15 may be a secondary battery capable of charging and discharging. In this case, the battery may have at least one shape of a cylindrical shape, a prismatic shape, a coin shape, and a pouch shape. In addition, although shown in the form of including three batteries 15 in the battery package of Figure 1, the number is not limited.

상기 배터리(15)가 2차 배터리일 경우 서로 대향 배치된 양극 조립체 및 음극 조립체, 상기 양극 조립체와 음극 조립체 사이에 배치되는 분리막으로 이루어진 전극 조립체와 전해액을 수용시킨 후, 캡 플레이트를 이용하여 상기 전극 조립체를 수용한 전지 케이스를 밀폐시킴으로써 제조될 수 있다.When the battery 15 is a secondary battery, an electrode assembly composed of a positive electrode assembly and a negative electrode assembly disposed opposite to each other and a separator disposed between the positive electrode assembly and the negative electrode assembly and an electrolyte solution are accommodated, and then the electrode is used by using a cap plate. It can be manufactured by sealing the battery case accommodating the assembly.

먼저, 양극 조립체 및 음극 조립체를 설명하면 다음과 같다.First, the positive electrode assembly and the negative electrode assembly will be described.

상기 양극 조립체 및 음극 조립체는 박형 형태를 가질 수 있는 배터리에 적합한 시트형태를 가질 수 있다.The positive electrode assembly and the negative electrode assembly may have a sheet shape suitable for a battery that may have a thin shape.

상기 양극 조립체는 양극 집전체 및 상기 양극 집전체에 도포되는 양극 활물질을 포함할 수 있고, 음극 조립체는 음극 집전체 및 상기 음극 집전체에 도포되는 음극 활물질을 포함할 수 있다.The positive electrode assembly may include a positive electrode current collector and a positive electrode active material coated on the positive electrode current collector, and the negative electrode assembly may include a negative electrode current collector and a negative electrode active material coated on the negative electrode current collector.

상기 양극 집전체 및/또는 음극 집전체는 박형의 금속 호일로 이루어질 수 있고, 일방향으로 길게 이어진 띠 형상으로 형성되며 구리, 알루미늄, 스테인리스 스틸, 니켈, 티타늄, 크롬, 망간, 철, 코발트, 아연, 몰리브덴, 텅스텐, 은, 금 및 이들의 조합에 의하여 제조되는 금속 호일로 이루어질 수 있다.The cathode current collector and/or the anode current collector may be formed of a thin metal foil, formed in a strip shape extending in one direction, and may include copper, aluminum, stainless steel, nickel, titanium, chromium, manganese, iron, cobalt, zinc, It may be made of a metal foil made of molybdenum, tungsten, silver, gold, and combinations thereof.

상기 양극 집전체 및/또는 음극 집전체는 0.5 ~ 2㎛ 두께로 형성하는 것이 바람직하다.The cathode current collector and/or the anode current collector is preferably formed to a thickness of 0.5 to 2 μm.

상기 양극 활물질은 리튬 이온을 가역적으로 인터칼레이션 및 디인터칼레이션할 수 있는 양극 활물질을 포함하며, 이러한 양극 활물질의 대표적인 예로는LiCoO2, LiNiO2, LiNiCoO2, LiMnO2, LiMn2O4, V2O5, V6O13, LiNi1 -x- yCoxMyO2(0 ≤ x ≤ 1, 0 ≤y ≤ 1, 0 ≤ x+y ≤ 1, M은 Al, Sr, Mg, La 등의 금속)와 같은 리튬-전이 금속 산화물, NCM(Lithium Nickel Cobalt Manganese)계 활물질 중 하나를 사용할 수 있고, 이들의 1종 이상의 혼합물을 사용할 수 있으나 이에 제한되지 않는다.The cathode active material includes a cathode active material capable of reversibly intercalating and deintercalating lithium ions, and representative examples of such a cathode active material include LiCoO 2 , LiNiO 2 , LiNiCoO 2 , LiMnO 2 , LiMn 2 O 4 , V 2 O 5 , V 6 O 13 , LiNi 1 -x- y Co x M y O 2 (0 ≤ x ≤ 1, 0 ≤y ≤ 1, 0 ≤ x+y ≤ 1, M is Al, Sr, Mg , a metal such as La), a lithium-transition metal oxide, NCM (Lithium Nickel Cobalt Manganese)-based active material, and a mixture of one or more of them may be used, but is not limited thereto.

음극 활물질은 리튬 이온을 인터칼레이션 및 디인터칼레이션할 수 있는 음극 활물질을 포함하며, 이러한 음극 활물질로는 결정질 또는 비정질의 탄소, 탄소 섬유, 또는 탄소 복합체의 탄소계 음극 활물질, 주석 산화물, 이들을 리튬화한 것, 리튬, 리튬합금 및 이들의 혼합물로 구성된 군에서 선택될 수 있으나, 이에 한정되지 않는다. The negative electrode active material includes a negative electrode active material capable of intercalating and deintercalating lithium ions. Examples of the negative electrode active material include crystalline or amorphous carbon, carbon fiber, or a carbon-based negative electrode active material of a carbon composite, tin oxide, and the like. It may be selected from the group consisting of lithiated ones, lithium, lithium alloys, and mixtures thereof, but is not limited thereto.

다음으로, 분리막은 전해액의 함침성을 최적화시킬 수 있는 복합 다공성 분리막을 적용할 수 있다. 상기 복합 다공성 분리막은 지지체(matrix)로서 사용되며 미세 기공을 갖는 다공성 부직포와, 다공성 부직포의 양 측면에 박막으로 적층되며, 방사 가능한 고분자 물질로 형성되어 전해액을 함침하고 있는 다공성 나노섬유 웹일 수 있다.Next, as the separator, a composite porous separator capable of optimizing the impregnation of the electrolyte may be applied. The composite porous separator is used as a support (matrix) and is a porous nonwoven fabric having micropores, laminated as a thin film on both sides of the porous nonwoven fabric, formed of a spinnable polymer material and impregnated with an electrolyte. It may be a porous nanofiber web.

마지막으로, 전해액은 분리막의 기공에 함습된 겔 상태의 겔 폴리머 전해질이 바람직하며, 기존의 액체 전해액의 누액을 개선할 수 있고, 특히 벤딩시에 가스나 누액이 발생되는 것을 방지할 수 있다.Lastly, the electrolyte solution is preferably a gel polymer electrolyte in a gel state moistened in the pores of the separator, and can improve the leakage of the existing liquid electrolyte solution, and can prevent gas or leakage from occurring especially during bending.

상기 전해액은 비수성 유기용매와 리튬염의 용질이 포함된 유기 전해액을 사용할 수 있다.The electrolyte solution may use an organic electrolyte solution containing a non-aqueous organic solvent and a solute of lithium salt.

상기 비수성 유기용매로는 카보네이트, 에스테르, 에테르 또는 케톤을 사용할 수 있다. 상기 카보네이트로는 디메틸 카보네이트(DMC), 디에틸 카보네이트(DEC), 디프로필 카보네이트(DPC), 메틸프로필 카보네이트(MPC), 에틸프로필 카보네이트(EPC), 메틸에틸 카보네이트(MEC), 에틸렌 카보네이트(EC), 프로필렌 카보네이트(PC), 부틸렌 카보네이트(BC) 등이 사용될 수 있으며, 상기 에스테르로는 부티로락톤(BL), 데카놀라이드(decanolide), 발레로락톤(valerolactone), 메발로노락톤(mevalonolactone), 카프로락톤(caprolactone), n-메틸 아세테이트, n-에틸 아세테이트, n-프로필 아세테이트 등이 사용될 수 있으며, 상기 에테르로는 디부틸 에테르 등이 사용될 수 있으며, 상기 케톤으로는 폴리메틸비닐케톤이 있으나, 본 발명은 비수성 유기용매의 종류에 한정되는 것은 아니다.As the non-aqueous organic solvent, carbonate, ester, ether or ketone may be used. Examples of the carbonate include dimethyl carbonate (DMC), diethyl carbonate (DEC), dipropyl carbonate (DPC), methylpropyl carbonate (MPC), ethylpropyl carbonate (EPC), methylethyl carbonate (MEC), and ethylene carbonate (EC) , Propylene carbonate (PC), butylene carbonate (BC), etc. may be used, and the ester includes butyrolactone (BL), decanolide, valerolactone, mevalonolactone ), caprolactone, n-methyl acetate, n-ethyl acetate, n-propyl acetate, etc. may be used, and dibutyl ether may be used as the ether, and polymethylvinyl ketone may be used as the ketone. However, the present invention is not limited to the type of non-aqueous organic solvent.

또한, 본 발명에 따른 전해액은 리튬염을 포함하며, 상기 리튬염은 전지 내에서 리튬 이온의 공급원으로 작용하여 기본적인 리튬 전지의 작동을 가능하게 하며, 그 예로는 LiPF6, LiBF4, LiSbF6, LiAsF6, LiClO4, LiCF3SO3, LiN(CF3SO2)2, LiN(C2F5SO2)2, LiAlO4, LiAlCl4, LiN(CxF2x+1SO2)(CyF2x+1SO2)(여기서, x 및 y는 유리수이다.) 및 LiSO3CF3로 이루어진 군에서 선택되는 것을 하나 이상 또는 이들의 혼합물을 포함할 수 있다.In addition, the electrolyte solution according to the present invention includes a lithium salt, and the lithium salt acts as a source of lithium ions in the battery to enable basic operation of the lithium battery, examples of which include LiPF 6 , LiBF 4 , LiSbF 6 , LiAsF 6 , LiClO 4 , LiCF 3 SO 3 , LiN(CF 3 SO 2 ) 2 , LiN(C 2 F 5 SO 2 ) 2 , LiAlO 4 , LiAlCl 4 , LiN(C x F 2x+1 SO 2 )(C y F 2x+1 SO 2 ) (where x and y are rational numbers) and LiSO 3 CF 3 may include one or more selected from the group consisting of or a mixture thereof.

다음으로, 상기 단열막(13)은 도 1과 같이 상기 배터리(15)들을 선택적으로 구획할 수 있다. 더욱 바람직하게는 상기 단열막은 상기 배터리들을 각각 구획할 수 있다. 이 경우, 상기 단열막(13)을 통해 배터리(15)들이 각각 구획된 공간 내에 수납될 수 있다. 또한, 상기 복수 개의 배터리들 중 어느 하나의 배터리에서 전해 물질이 누출됐을 때 누출된 전해 물질이 다른 배터리로 전이되는 것을 방지할 수 있다. 또한, 복수 개의 배터리들 중 어느 하나의 배터리에서 전해 물질이 누출됐을 때 해당 배터리만을 교체할 수 있어 유지 보수 비용을 절감할 수 있다.Next, the insulating film 13 may selectively partition the batteries 15 as shown in FIG. 1 . More preferably, the insulating film may partition each of the batteries. In this case, the batteries 15 may be accommodated in the space respectively partitioned through the insulating film 13 . In addition, when an electrolyte material leaks from one of the plurality of batteries, it is possible to prevent the leaked electrolyte material from being transferred to another battery. In addition, when an electrolyte leaks from any one battery among a plurality of batteries, only the corresponding battery can be replaced, thereby reducing maintenance costs.

상기 단열막(13)은 막이 외력에 의해 파손되지 않는 범위 내에서 박막으로 구현될 수 있고, 고열, 예를 들어 30℃ 이상, 바람직하게는 180℃ 이상에서 형상을 유지할 수 있는 내열성을 갖춘 공지된 단열부재인 경우 제한 없이 사용할 수 있다. 그 일 예로, 상기 단열막(13)은 공기를 수용할 수 있는 다수의 미세기공이 형성된 다공성 기재 및/또는 단열필름을 포함할 수 있다.The insulating film 13 may be implemented as a thin film within a range in which the film is not damaged by external force, and has heat resistance capable of maintaining its shape at high temperature, for example, 30 ° C. or higher, preferably 180 ° C. or higher. In the case of an insulating member, it can be used without limitation. For example, the heat insulating film 13 may include a porous substrate having a plurality of micropores capable of accommodating air and/or a heat insulating film.

상기 다공성 기재는 섬유웹, 부직포, 직물 및 편물로 이루어진 군에서 선택된 1종 이상의 기재를 포함할 수 있다. 상기 직물 및 편물은 섬유가 방향성 및/또는 규칙성을 가지고 배열된 통상의 원단을 의미한다. 또한, 상기 섬유웹 및 부직포는 섬유가 방향성을 가지지 않고 집합되어 형성된 기재를 의미하며, 상기 섬유웹은 방사와 동시에 별도의 접착공정이나 접착제의 투입 없이도 섬유간 융착에 의해 3차원 네트워크 구조를 형성하는 기재를 의미하며, 상기 부직포는 단섬유 간을 별도의 접착제나 열 등을 통해 부착시켜 제조하는 통상의 부직포를 의미한다. 상기와 같은 다공성 기재를 형성하는 섬유는 셀룰로오스계, 단백질, 폴리에스테르계(PET, PBT 등), 폴리아미드계(나일론6, 나일론66 등), 아크릴계(폴리아크릴로니트릴, 모다아크릴 등), 올레핀계(폴리프로필렌, 폴리에틸렌 등), 비닐계(폴리비닐알코올, 폴리염화비닐 등) 및 불소계(PVDF, PCTFE, PTFE 등) 등을 포함하는 공지된 유기섬유 및/또는 유리섬유, 암면섬유 등의 무기섬유일 수 있다.The porous substrate may include at least one substrate selected from the group consisting of a fiber web, a nonwoven fabric, a woven fabric, and a knitted fabric. The woven and knitted fabrics refer to conventional fabrics in which fibers are arranged in a direction and/or regularity. In addition, the fiber web and nonwoven fabric refer to substrates formed by gathering fibers without orientation, and the fiber web forms a three-dimensional network structure by fusion between fibers without a separate bonding process or adhesive at the same time as spinning. It means a base material, and the non-woven fabric refers to a conventional non-woven fabric manufactured by attaching short fibers to each other through a separate adhesive or heat. Fibers forming the porous substrate as described above are cellulose-based, protein, polyester-based (PET, PBT, etc.), polyamide-based (nylon 6, nylon 66, etc.), acrylic-based (polyacrylonitrile, modacrylic, etc.), olefin Known organic fibers including (polypropylene, polyethylene, etc.), vinyl (polyvinyl alcohol, polyvinyl chloride, etc.) and fluorine (PVDF, PCTFE, PTFE, etc.) and/or inorganic fibers such as glass fibers and rock wool fibers can be fibres.

본 발명의 일 실시예에 포함되는 단열막(13)은 섬유웹일 수 있다. 단열막으로 섬유웹을 사용할 경우 단열효과 이외에 배터리 패키지 내의 충격을 흡수할 수 있는 효과가 있다. 이는 상기 섬유웹 내에 형성된 기공이 충격이 전파되는 것을 차단함으로써 상기 배터리 내로 충격이 흡수되는 것이다.The insulating film 13 included in one embodiment of the present invention may be a fiber web. When a fiber web is used as an insulating film, there is an effect of absorbing shock in the battery package in addition to the insulating effect. This is because the pores formed in the fiber web block the propagation of the shock, so that the shock is absorbed into the battery.

일예로 상기 섬유웹은 전기방사를 통해 형성된 나노섬유웹일 수 있다. 상기 나노섬유웹을 형성하는 나노섬유는 내열성을 갖추기 위해 폴리아크릴로니트릴 나노섬유를 포함할 수 있다. 또한, 나노섬유웹을 형성하는 나노섬유 자체가 접착성을 발현하여 내구성, 기계적 강도를 향상시키기 위하여 폴리비닐리덴플루오라이드 나노섬유를 포함할 수 있다. 또는 상기 나노섬유는 폴리아크릴로니트릴과 폴리비닐리덴플루오라이드의 복합나노섬유일 수 있고, 이를 통해 내열성 및 접착성을 통한 내구성, 기계적강도를 동시에 발현시킬 수 있다. 이때, 상기 복합나노섬유는 모노사 내에서 폴리아크릴로니트릴과 폴리비닐리덴플루오라이드가 6:4 ~ 8.5:1.5의 중량비로 혼합된 복합나노섬유일 수 있다. 만일 PAN과 PVDF가 6:4 비율 미만으로 포함되는 경우 내열성이 저하되어 단열효과를 발현하는 도중에 나노섬유웹의 용융이 발생함에 따라 나노섬유웹의 기공이 현저히 감소하여 단열효과가 제대로 발현되지 않는 문제점이 있을 수 있다. 또한, 만일 PAN과 PVDF가 8.5:1.5 비율을 초과하여 포함되는 경우 기계적 강도, 내구성을 발현시키기 어려우며, PAN의 비율이 높아 전기방사시에 방사성이 현저히 떨어져 생산성이 좋지 않을 수 있고, 목적하는 수준의 기공도와 공경 등을 구현하기 어려워 충분한 단열효과를 발현하는 나노섬유웹을 제조하기 어렵다.For example, the fiber web may be a nanofiber web formed through electrospinning. The nanofibers forming the nanofiber web may include polyacrylonitrile nanofibers to have heat resistance. In addition, the nanofibers themselves forming the nanofiber web may include polyvinylidene fluoride nanofibers to improve durability and mechanical strength by expressing adhesiveness. Alternatively, the nanofibers may be composite nanofibers of polyacrylonitrile and polyvinylidene fluoride, and through this, durability and mechanical strength through heat resistance and adhesion can be simultaneously expressed. In this case, the composite nanofibers may be composite nanofibers in which polyacrylonitrile and polyvinylidene fluoride are mixed in a weight ratio of 6:4 to 8.5:1.5 in mono yarns. If PAN and PVDF are included in a ratio of less than 6:4, the heat resistance is lowered and the melting of the nanofiber web occurs while the insulation effect is expressed, so the pores of the nanofiber web are significantly reduced and the insulation effect is not properly expressed. This can be. In addition, if PAN and PVDF are included in a ratio exceeding 8.5: 1.5, it is difficult to develop mechanical strength and durability, and since the ratio of PAN is high, spinnability is significantly reduced during electrospinning, and productivity may be poor, and the desired level of It is difficult to manufacture a nanofiber web that exhibits sufficient insulation effect because it is difficult to implement porosity and pore size.

또한, 상기 단열막(13)은 평균두께 10 ㎛ ~ 50 ㎛, 바람직하게는 평균 두께 15 ㎛ ~ 40 ㎛, 더욱 바람직하게는 15 ㎛ ~ 35 ㎛로 형성시키는 것이 좋다. 이때, 단열막은 평균두께 10 ㎛ 미만이면 목적하는 수준의 단열효과를 발현시킬 수 없는 문제가 있고, 50㎛를 초과하는 것은 비경제적이며, 슬림화된 배터리 팩을 제조하는데 있어서 바람직하지 못할 수 있다.In addition, the insulating film 13 is preferably formed to have an average thickness of 10 μm to 50 μm, preferably an average thickness of 15 μm to 40 μm, and more preferably 15 μm to 35 μm. At this time, if the average thickness of the insulation film is less than 10 μm, there is a problem in that the desired level of insulation effect cannot be expressed, and if it exceeds 50 μm, it is uneconomical and may not be preferable in manufacturing a slimmed-down battery pack.

또한, 상기 나노섬유웹은 평량이 2 ~ 6 g/㎡이며, 기공도가 40% 이상일 수 있고, 보다 바람직하게는 40 ~ 80%일 수 있고, 또한, 평균공경은 300 ~ 400㎛일 수 있으며, 이를 통해 목적하는 단열효과를 더욱 더 향상되도록 발현시킬 수 있다. 만일 기공도가 80% 초과 및/또는 평균공경 400㎛ 초과하는 경우 나노섬유웹의 기계적 강도가 약해 단열막으로써의 기능을 제대로 수행할 수 없을 수 있다.In addition, the nanofibrous web has a basis weight of 2 to 6 g/m2, a porosity of 40% or more, more preferably 40 to 80%, and an average pore diameter of 300 to 400 μm, , Through this, the desired insulation effect can be expressed so as to be further improved. If the porosity exceeds 80% and/or the average pore diameter exceeds 400 μm, the mechanical strength of the nanofiber web is weak and may not function properly as a heat insulating film.

또한, 상기 단열필름은 공지된 단열필름을 사용할 수 있고, 필름 내부에 공기주머니를 구비하는 필름이거나 필름 내부에 공기를 함유하고 있지 않은 상태로 단열효과를 발현하는 공지의 단열필름인 경우 본 발명에서 특별히 구체적 종류를 한정하지 않는다. In addition, the heat insulating film may use a known heat insulating film, and in the case of a film having an air bag inside the film or a known heat insulating film that exhibits a heat insulating effect in a state in which air is not contained in the film, in the present invention It does not specifically limit a specific kind.

또한, 상기 단열막(13)은 평균두께 10 ㎛ ~ 50 ㎛, 바람직하게는 평균 두께 15 ㎛ ~ 40 ㎛, 더욱 바람직하게는 15 ㎛ ~ 35 ㎛로 형성시키는 것이 좋다. 이때, 단열막은 평균두께 10 ㎛ 미만이면 목적하는 수준의 단열효과를 발현시킬 수 없는 문제가 있고, 50㎛를 초과하는 것은 비경제적이며, 슬림화된 플렉서블 배터리를 제조하는데 있어서 바람직하지 못할 수 있다.In addition, the insulating film 13 is preferably formed to have an average thickness of 10 μm to 50 μm, preferably an average thickness of 15 μm to 40 μm, and more preferably 15 μm to 35 μm. At this time, if the average thickness of the insulation film is less than 10 μm, there is a problem in that the desired level of insulation effect cannot be expressed, and if the thickness exceeds 50 μm, it is uneconomical and may not be desirable in manufacturing a slim flexible battery.

또한, 본 발명의 일 실시에에 포함되는 단열막(13)은 제1 단열막 및 제2 단열막이 적층된 구조일 수 있고, 이때 상기 제1 단열막은 상술한 나노섬유웹일 수 있고, 제2 단열막은 부직포일 수 있다. 이때, 상기 나노섬유웹의 두께는 3 ~ 10㎛일 수 있고, 부직포의 두께는 10 ~ 40㎛일 수 있다. 이때 상기 부직포는 그 자체가 단열막의 기능을 하는 동시에 적층되는 나노섬유웹의 기계적 강도를 보완시켜 단열막의 내구성을 더욱 향상시킬 수 있도록 하는 역할을 담당할 수 있다.In addition, the heat insulating film 13 included in one embodiment of the present invention may have a structure in which a first heat insulating film and a second heat insulating film are stacked, wherein the first heat insulating film may be the above-described nanofiber web, and the second heat insulating film The membrane may be a non-woven fabric. At this time, the thickness of the nanofiber web may be 3 ~ 10㎛, the thickness of the nonwoven fabric may be 10 ~ 40㎛. At this time, the non-woven fabric itself may serve as a heat insulating film and at the same time supplement the mechanical strength of the laminated nanofiber web to further improve the durability of the heat insulating film.

한편, 상기 배터리(15)의 표면 및 단열막(13) 사이에 접착제층(미도시)을 더 포함할 수 있다. 상기 접착제층은 상기 배터리(15) 및 배터리 팩(10) 간의 접착력을 높여주는 역할을 수행한다. 동시에, 상기 접착제층은 상기 배터리(15)의 표면 손상으로 인해 전해액이 배터리로부터 누출되는 경우 상기 표면 손상부를 막아 전해액이 배터리로부터 누출되는 것을 막을 수 있다. 상기 접착제층은 실리콘, 폴리프탈레이트, 산 변성 폴리프로필렌(PPa, acid modified polypropylene), 및 산 변성 폴리에틸렌(Pea, acid modified polyethylene) 중에서 선택된 1종 이상을 포함할 수 있다. 보다 바람직하게는 산 변성 폴리프로필렌(PPa, acid modified polypropylene) 및 산 변성 폴리에틸렌(Pea, acid modified polyethylene) 중에서 선택된 1종 이상을 포함할 수 있다. 상기 산 변성 폴리프로필렌 및 산 변성 폴리에틸렌은 말레산, 아크릭산, 유기과산화물 등의 산성분을 중합체내에 0.1 ~10wt%로 포함하는 폴리프로필렌 및 폴리에틸렌일 수 있고, 만일 산성분의 함량이 상기 범위를 만족하지 못하는 경우 배터리(15)의 표면 및 단열막(13) 간의 목적하는 수준의 접착력이 발현되지 않아 층간 박리가 빈번히 발생하고 전해액이 누액되는 문제점이 있을 수 있다.Meanwhile, an adhesive layer (not shown) may be further included between the surface of the battery 15 and the insulating film 13 . The adhesive layer serves to increase adhesion between the battery 15 and the battery pack 10 . At the same time, when the electrolyte leaks from the battery due to the surface damage of the battery 15, the adhesive layer can prevent the electrolyte from leaking from the battery by blocking the surface damage. The adhesive layer may include at least one selected from silicone, polyphthalate, acid modified polypropylene (PPa), and acid modified polyethylene (Pea). More preferably, at least one selected from acid modified polypropylene (PPa) and acid modified polyethylene (Pea) may be included. The acid-modified polypropylene and acid-modified polyethylene may be polypropylene and polyethylene containing 0.1 to 10 wt% of an acid component such as maleic acid, acrylic acid, or organic peroxide in the polymer, and if the content of the acid component satisfies the above range. If this is not done, the desired level of adhesion between the surface of the battery 15 and the insulating film 13 may not be expressed, resulting in frequent separation between the layers and leakage of the electrolyte.

상기 접착제층은 드라이 라미네이트층(dry lamination layer)일 수 있다. 이 경우, 상기 배터리(15) 및 상기 배터리 팩(10) 간의 접착력을 더 강화할 수 있다.The adhesive layer may be a dry lamination layer. In this case, the adhesive force between the battery 15 and the battery pack 10 may be further strengthened.

이때, 상기 접착제층은 평균두께가 5㎛ ~ 30㎛일 수 있고, 바람직하게는 10㎛ ~ 20㎛일 수 있다. 이는, 상기 제1 접착층의 평균두께가 5㎛를 초과하면 안정적인 접착력 확보가 어려울 수 있고, 30㎛를 초과하면 박형화에 불리하다.At this time, the adhesive layer may have an average thickness of 5 μm to 30 μm, preferably 10 μm to 20 μm. If the average thickness of the first adhesive layer exceeds 5 μm, it may be difficult to secure stable adhesion, and if it exceeds 30 μm, it is disadvantageous to thinning.

본 실시예의 구성 요소 중 상술한 본 발명의 일 실시예의 구성 요소와 동일한 구성 요소에 대해서는, 상기 도 1 및 도 2의 도면 부호를 원용하고, 이에 대한 상세한 설명을 생략하기로 한다.Among the components of this embodiment, the same components as those of the above-described embodiment of the present invention are referenced by reference numerals in FIGS. 1 and 2, and detailed description thereof will be omitted.

본 발명의 다른 실시예에 따른 배터리 패키지는 도 3과 같이 내부 표면 상에 단열막(13)이 배치된 배터리 수용 홀(11)을 적어도 하나를 포함하는 배터리 팩(10), 및 상기 배터리 수용 홀(11) 내에 수용되는 배터리(15)를 포함한다. 이 경우, 상기 배터리 수용 홀(11) 내부 표면 상에 단열막(13)이 배치됨에 따라 상기 배터리 수용 홀(11) 내에 수용되는 배터리(15)로부터 발생된 열이 전도되는 것을 억제 또는 차단할 수 있다.A battery package according to another embodiment of the present invention includes a battery pack 10 including at least one battery accommodating hole 11 in which an insulating film 13 is disposed on an inner surface as shown in FIG. 3, and the battery accommodating hole and a battery 15 housed in (11). In this case, as the heat insulating film 13 is disposed on the inner surface of the battery accommodating hole 11, conduction of heat generated from the battery 15 accommodated in the battery accommodating hole 11 can be suppressed or blocked. .

이때, 전술된 실시예와 같이 상기 배터리 팩(10) 및 상기 단열막(13) 사이에 접착제층(미도시)을 더 포함할 수 있다.In this case, an adhesive layer (not shown) may be further included between the battery pack 10 and the insulating film 13 as in the above-described embodiment.

한편, 본 발명의 또 다른 실시예에 따른 배터리 패키지는 배터리 및 단열막이 적어도 2회 교호로 배치되고, 상기 배터리 및 단열막을 패킹하는 배터리 팩을 포함하는 형태이다. 이때, 상기 배터리는 도 1과 같이 육면체 형태 또는 소정의 두께를 갖는 막 형태인 것이 바람직하다. 상기 배터리 및 단열막이 서로 교호 배열됨에 따라 상기 단열막에서 서로 인접하는 배터리 간의 열전도를 억제 또는 차단한다.Meanwhile, a battery package according to another embodiment of the present invention includes a battery pack in which a battery and an insulating film are alternately disposed at least twice, and the battery and the insulating film are packed. At this time, the battery is preferably in the form of a hexahedron or a film having a predetermined thickness as shown in FIG. 1 . As the battery and the insulation film are alternately arranged with each other, the insulation film suppresses or blocks heat conduction between batteries adjacent to each other.

이하, 본 발명의 이해를 돕기 위하여 바람직한 실시예(example)를 제시한다. 다만, 하기의 실시예는 본 발명의 이해를 돕기 위한 것일 뿐, 본 발명이 하기의 실시예에 의해 한정되는 것은 아니다.Hereinafter, a preferred embodiment (example) is presented to help the understanding of the present invention. However, the following examples are only for facilitating understanding of the present invention, and the present invention is not limited by the following examples.

<실시예 1> <Example 1>

실리콘 수지를 포함하는 판을 이용하여 일면이 개구되고 육면체 형상을 갖는 배터리 팩을 제조했다.A battery pack having one surface open and having a hexahedral shape was manufactured using a plate containing a silicone resin.

다음으로, PAN(DOLAN, N-PAN, 중량평균분자량 85,000g/mol)과 PVDF(Solvary/Solef 5130)가 8:2의 중량비로 혼합된 방사용액을 전기방사하여 제조한 두께가 25㎛이고, 평량이 4.6 g/㎡이며, 기공도가 65%이고, 평균공경이 330 ㎛인 나노섬유웹 단열막을 접착제(3M, 아크릴계 접착제)를 이용하여 도 1과 같이 상기 배터리 팩 내부에 배터리 수용 공간이 세 개가 되도록 배터리 팩 내부를 구획하여 고정시켰다.Next, a thickness of 25 μm prepared by electrospinning a spinning solution in which PAN (DOLAN, N-PAN, weight average molecular weight 85,000 g / mol) and PVDF (Solvary / Solef 5130) were mixed at a weight ratio of 8: 2, The battery accommodation space inside the battery pack is three, as shown in FIG. The inside of the battery pack was partitioned and fixed so that it could open.

다음으로, 배터리를 제조하기 위해 먼저, 양극조립체 및 음극조립체를 준비했다. 양극조립체는 두께가 20㎛인 알루미늄 재질의 양극집전체에 NCM(Lithium Nickel Cobalt Manganese)계 양극활물질을 최종 두께가 120㎛이 되도록 양극집전체의 양면에 캐스팅하여 양극조립체를 제조하였다. 또한, 음극조립체는 두께가 15㎛인 구리재질의 음극집전체에 그라파이트 음극활물질을 최종 두께가 115㎛가 되도록 음극집전체의 양면에 캐스팅하여 음극조립체를 제조하였다. 이후 PET/PEN 재질의 두께 20㎛의 분리막을 준비하여, 양극조립체, 분리막 및 음극조립체를 적층시켜 전극조립체를 제조하였다. 이후, 제조된 전극조립체와 LiPF6 전해액을 수용시킨 후, 캡 플레이트를 이용하여 상기 전극 조립체를 수용한 전지 케이스를 밀폐시켜 총 3개의 배터리를 제작했다.Next, in order to manufacture a battery, first, a positive electrode assembly and a negative electrode assembly were prepared. The positive electrode assembly was prepared by casting a lithium nickel cobalt manganese (NCM)-based positive electrode active material on both sides of the positive electrode current collector to have a final thickness of 120 μm on a positive electrode current collector made of aluminum having a thickness of 20 μm. In addition, the negative electrode assembly was prepared by casting a graphite negative electrode active material on both sides of the negative electrode current collector to have a final thickness of 115 μm on a negative electrode current collector made of copper having a thickness of 15 μm. Thereafter, a separator having a thickness of 20 μm made of PET/PEN was prepared, and an electrode assembly was manufactured by laminating a positive electrode assembly, a separator, and a negative electrode assembly. Then, the manufactured electrode assembly and LiPF 6 After the electrolyte was accommodated, a battery case accommodating the electrode assembly was sealed using a cap plate to manufacture a total of three batteries.

다음으로, 앞서 제조된 배터리 팩 내 3개의 배터리 수용 공간에 각각 배터리를 수용시켰다.Next, the battery was accommodated in each of the three battery accommodating spaces in the previously manufactured battery pack.

다음으로, 상기 배터리 및 단열막 사이에 PPa 접착제를 충진한 뒤 드라이 라미네이트하여 상기 배터리 및 단열막 사이에 접착제층을 형성하여 배터리 패키지를 제조했다.Next, a PPa adhesive was filled between the battery and the insulator, and then dry laminated to form an adhesive layer between the battery and the insulator to manufacture a battery package.

<실시예 2~3><Examples 2 to 3>

실시예 1과 동일하게 실시하여 제조하되, 단열막으로 사용된 나노섬유웹의 PAN, PVDF 함량을 하기 표 2와 같이 변경하여 단열막을 제조하였고, 이를 통해 하기 표 1과 같은 배터리 패키지를 제조하였다.It was prepared in the same manner as in Example 1, but a heat insulating film was prepared by changing the PAN and PVDF contents of the nanofiber web used as the heat insulating film as shown in Table 2 below, and through this, a battery package as shown in Table 1 below was manufactured.

<실시예 4><Example 4>

실시예 1과 비교하여, 상기 단열막 형성 시, PEN 부직포 상에 상기 PAN 및 PVDF 혼합 방사 용액을 전기방사하여 부직포 및 나노섬유웹 일체형 단열막을 제조한 것을 제외하곤 동일한 조건 하에서 배터리 패키지를 제조하였다.Compared to Example 1, when forming the insulating film, a battery package was prepared under the same conditions except that the nonwoven fabric and nanofiber web integrated insulating film was prepared by electrospinning the PAN and PVDF mixed spinning solution on the PEN nonwoven fabric.

<실시예 5><Example 5>

실시예 1과 비교하여 접착제층을 형성하지 않은 것을 제외하곤 실시예 1과 동일하게 실시하여 배터리 패키지를 제조하였다.Compared to Example 1, a battery package was manufactured in the same manner as in Example 1, except that the adhesive layer was not formed.

<비교예 1><Comparative Example 1>

실시예 1과 동일하게 실시하여 제조하되, 단열막을 생략하여 배터리 패키지를 제조하여 이를 통해 하기 [표 2]와 같은 배터리 패키지를 제조하였다.It was manufactured in the same manner as in Example 1, but a battery package was manufactured by omitting the insulation film, and through this, a battery package as shown in [Table 2] was manufactured.

<실험예 1><Experimental Example 1>

실시예 1~5 및 비교예 5를 통해 제조된 배터리 패키지에서 가장 왼편에 있는 배터리를 꺼내 150 ℃의 열원에 30분 동안 접촉시킨 후 다시 배터리 팩 내에 수용시킨 후 상기 가장 왼편에 있는 배터리와 가장 인접하게 배치된 배터리의 성능변화 유무를 평가하기 위해 하기와 같은 물성을 평가하여 하기 표 2에 나타냈다.After taking out the leftmost battery from the battery package manufactured in Examples 1 to 5 and Comparative Example 5, contacting it with a heat source of 150 ° C. for 30 minutes, and then putting it back into the battery pack, the battery closest to the leftmost battery In order to evaluate the performance change of the battery arranged in such a way, the following physical properties were evaluated and shown in Table 2 below.

1. 온도 25℃, 습도 65%의 환경에서 완전방전된 배터리를 완전 충전하여 충전용량을 측정 후 다시 완전 방전시키고, 재충전하는 과정을 총 100번 실시하여 평균 충전용량을 측정하였다. 다만, 100회 실시 전 충전용량이 0mAh가 되는 경우 최초 0mAh으로 측정되었을 때까지 측정된 충전용량의 평균을 계산하였다. 이때, 충전 및 방전 조건은 하기 표 1과 같다.1. The fully discharged battery was fully charged in an environment of 25°C temperature and 65% humidity, and the charging capacity was measured, then the fully discharged and recharged process was performed a total of 100 times to measure the average charging capacity. However, when the charging capacity before 100 times was 0mAh, the average of the charging capacities measured until the first 0mAh was measured was calculated. At this time, charging and discharging conditions are shown in Table 1 below.

충전조건charging conditions Normal CurrentNormal Current 0.2C0.2C Max. CurrentMax. Current 0.5C0.5C CC-CVCC-CV 4.2V4.2V Cut-OffCut-Off 0.05C0.05C 방전조건
discharge condition
 Normal CurrentNormal Current 0.2C0.2C Max. CurrentMax. Current 0.5C0.5C Cut-off VoltageCut-off Voltage 2.8V2.8V

2. 내구성 1 2. Durability 1

배터리 패키지 내 배터리들의 단면을 광학현미경으로 관찰하여 전해액의 누액 발생 여부를 평가하였고, 평가결과 이상이 없는 경우를 ○, 누액이 발생한 경우 × 로 평가했다.Cross-sections of the batteries in the battery package were observed under an optical microscope to evaluate whether or not leakage of the electrolyte occurred. The case where there was no abnormality as a result of the evaluation was evaluated as ○, and the case where leakage occurred as ×.

3. 내구성 23. Durability 2

배터리 패키지를 지면으로부터 1m의 높이에서 낙하시키는 과정을 반복하여 배터리 팩으로부터 배터리가 분리될 때의 낙하시킨 횟수를 기록했다.The process of dropping the battery package from a height of 1 m from the ground was repeated, and the number of drops when the battery was separated from the battery pack was recorded.

Figure 112015106658028-pat00001
Figure 112015106658028-pat00001

상기 표 2를 통해 알 수 있듯이, PAN과 PVDF가 본 발명의 바람직한 범위내의 중량비로 혼합된 방사용액으로 전기방사된 나노섬유웹을 단열막으로 구비하는 실시예 1은 충전 특성이 우수함을 알 수 있다.As can be seen from Table 2, Example 1 having a nanofiber web electrospun with a spinning solution in which PAN and PVDF are mixed at a weight ratio within the preferred range of the present invention as a heat insulating film has excellent charging characteristics. .

이에 반하여 PAN이 더 많이 방사용액에 포함되어 제조된 단열막을 구비하는 실시예 2는 평균충전용량이 실시예 1에 비해 현저히 감소했는데, 이는 PAN의 전기방사성이 좋지 않아 섬유길이가 매우 짧거나 액적과 같은 상태로 섬유가 전기방사됨에 따라 제조된 나노섬유웹층의 기공도가 높게 제조되지 않고, 평균공경도 매우 작아서 단열효과가 실시예 1에 비해 현저히 저하된 결과로 해석될 수 있다. 실시예 2의 경우 내구성 평가결과 누액의 발생은 없었으며, 다만 평균충전용량의 감소로 미루어 전극조립체에 이상이 발생했을 것으로 예상할 수 있다. 또한, 배터리 팩과 배터리간의 접착력이 약화되어 낙하 이후 배터리 팩과 배터리 간의 들뜸, 이격이 발생했음을 확인할 수 있다.On the other hand, Example 2, which has an insulating film prepared by including more PAN in the spinning solution, had a significantly reduced average charge capacity compared to Example 1. As the fibers are electrospun in the same state, the porosity of the nanofiber web layer produced is not high, and the average pore diameter is also very small, which can be interpreted as a result of significantly lowering the insulation effect compared to Example 1. In the case of Example 2, there was no leakage as a result of the durability evaluation, but it can be expected that an abnormality occurred in the electrode assembly considering the decrease in the average charging capacity. In addition, it can be confirmed that the adhesive force between the battery pack and the battery is weakened, and lifting and separation between the battery pack and the battery occur after the drop.

한편, PVDF의 함량을 높인 나노섬유웹을 단열막으로 사용한 실시예 3의 경우 평균충전용량이 실시예 1 및 실시예 2보다 현저히 저하되었는데, 이는 단열막의 PVDF가 일부 용융되어 나노섬유웹의 기공을 막아 단열막의 기능을 제대로 수행하지 못한 결과로 해석할 수 있다. 다만, 실시예 3의 경우에도 누액이 발생하지 않은 것으로 미루어 보아 전극조립체에 심한 열손상에 따른 물성저하가 유발된 것으로 예상된다.On the other hand, in the case of Example 3, in which a nanofiber web with an increased PVDF content was used as an insulating film, the average charging capacity was significantly lower than that of Examples 1 and 2, which is due to partial melting of the PVDF of the insulating film to block the pores of the nanofibrous web. It can be interpreted as a result of not performing the function of the insulation film properly. However, judging from the fact that leakage did not occur even in the case of Example 3, it is expected that the electrode assembly was induced to deteriorate in physical properties due to severe thermal damage.

또한, 단열막을 구비하지 않은 비교예 1에 배터리 패키지는 평균충전용량이 30 mAh에 불과하고, 내구성 평가결과가 누액이 발생하여 내구성이 현저히 좋지 못한 것을 확인할 수 있고, 단열막이 구비되지 않은 상태로 배터리의 기능저하 및 불량이 발생한다는 것을 명확히 보여주고 있다.In addition, it can be seen that the battery package in Comparative Example 1 without an insulating film has an average charging capacity of only 30 mAh, and the durability evaluation result shows that leakage occurs and the durability is significantly poor. It clearly shows that functional degradation and defects occur.

또한, 단열막 및 배터리 사이에 접착제층을 형성한 실시예 4의 경우 다른 실시예와 비교하여 전기적 특성 및 기계적 특성이 모두 우수함을 알 수 있었다.In addition, in the case of Example 4 in which an adhesive layer was formed between the insulating film and the battery, it was found that both electrical and mechanical properties were excellent compared to other examples.

<실시예 6><Example 6>

배터리 제조 공정 없이, 실시예 1과 동일한 조건 하에서 접착제층인 PPa를 PET 기판 상에 도포하여 접착제층을 형성했다. 이후, 접착제층 상에 실시예 1과 동일한 조건으로 제조된 단열막을 부착시켰다. 이후, 상기 기판으로부터 접착제층/단열막 형태의 접착 구조물을 탈리시켰다.Without a battery manufacturing process, an adhesive layer was formed by applying PPa as an adhesive layer on a PET substrate under the same conditions as in Example 1. Thereafter, a heat insulating film prepared under the same conditions as in Example 1 was attached to the adhesive layer. Thereafter, the adhesive structure in the form of an adhesive layer/insulation film was detached from the substrate.

<실시예 7><Example 7>

상기 실시예 6과 비교하여 접착제층으로 PP를 사용한 것을 제외하곤 동일한 조건 하에서 접착 구조물을 제조했다.An adhesive structure was prepared under the same conditions as in Example 6, except that PP was used as an adhesive layer.

<실험예 2><Experimental Example 2>

접착제층에 포함된 물질에 따른 전해액 누출 시 단열막 박리 여부를 관찰했다.Whether or not the insulating film was peeled off when the electrolyte solution leaked according to the material included in the adhesive layer was observed.

자세하게는, LiPF6 전해액 60ml를 250℃까지 승온시킨 뒤, 상기 실시예 6 및 7에서 제조된 접착 구조물을 10분 동안 함침시킨 후, 접착제층 및 단열막의 박리 여부를 관찰하여 하기 표 3에 결과를 나타냈다.In detail, after raising the temperature of 60ml of LiPF 6 electrolyte to 250 ° C, impregnating the adhesive structures prepared in Examples 6 and 7 for 10 minutes, observing whether the adhesive layer and the insulating film were peeled off, the results are shown in Table 3 below. showed up

실시예 6Example 6 실시예 7Example 7 접착제층adhesive layer PPaPPa PPPP 박리여부Exfoliation ×× ○○

상기 표 3을 참조하면, 고온의 전해액에서 PP접착제층을 사용한 실시예 7의 경우 접착제층 및 단열막의 박리가 일어났으며, 실시예 6의 경우 접착제층 및 단역막의 박리가 일어나지 않았음을 확인했다.Referring to Table 3, in the case of Example 7 using the PP adhesive layer in the high-temperature electrolyte, peeling of the adhesive layer and the insulating film occurred, and in the case of Example 6, it was confirmed that the peeling of the adhesive layer and the single-layer film did not occur. .

이를 통해 접착제층으로 PPa를 사용하면 배터리 내부 열에 의해 전해액이 팽창되어 누액되더라도 접착제층으로부터 단열막이 박리되지 않고 안정적으로 결합되어 있음을 알 수 있다.Through this, it can be seen that when PPa is used as the adhesive layer, the insulating film is not separated from the adhesive layer and is stably bonded even if the electrolyte solution expands and leaks due to internal heat of the battery.

이상, 본 발명을 바람직한 실시예 및 실험예를 들어 상세하게 설명하였으나, 본 발명은 상기 실시예 및 실험예에 의해 한정되지 않고, 본 발명의 기술적 사상 및 범위 내에서 당 분야에서 통상의 지식을 가진 자에 의하여 여러 가지 변형 및 변경이 가능하다.In the above, the present invention has been described in detail with preferred embodiments and experimental examples, but the present invention is not limited by the above embodiments and experimental examples, and those skilled in the art within the technical spirit and scope of the present invention Various modifications and changes are possible by the person.

10 : 배터리 팩 11 : 배터리 수용 홀
13 : 단열막 15 : 배터리10: battery pack 11: battery accommodating hole
13: insulation film 15: battery

Claims (12)

복수 개의 배터리들이 내장되는 배터리 팩; 및
상기 배터리 팩 내에 배치되고 상기 배터리들을 선택적으로 구획하며 상기 배터리들 간의 열전도를 방지 또는 차단하는 단열막;을 포함하고,
상기 단열막은 공기를 수용할 수 있는 다수의 미세기공이 형성된 나노섬유웹을 포함하며, 상기 나노섬유웹을 형성하는 나노섬유는 모노사 내에서 폴리아크릴로니트릴과 폴리비닐리덴플루오라이드가 6:4 ~ 8.5:1.5의 중량비로 혼합된 복합나노섬유를 포함하는 배터리 패키지.A battery pack in which a plurality of batteries are built-in; and
An insulating film disposed in the battery pack, selectively partitioning the batteries, and preventing or blocking heat conduction between the batteries;
The insulating film includes a nanofiber web having a plurality of micropores capable of accommodating air, and the nanofibers forming the nanofiber web are composed of polyacrylonitrile and polyvinylidene fluoride in a ratio of 6:4 in mono yarn. A battery package containing composite nanofibers mixed in a weight ratio of ~8.5:1.5. 내부 표면 상에 단열막이 배치된 배터리 수용 홀을 적어도 하나 포함하는 배터리 팩; 및
상기 배터리 수용 홀 내에 수용되는 배터리를 포함하고,
상기 단열막은 공기를 수용할 수 있는 다수의 미세기공이 형성된 나노섬유웹을 포함하며, 상기 나노섬유웹을 형성하는 나노섬유는 모노사 내에서 폴리아크릴로니트릴과 폴리비닐리덴플루오라이드가 6:4 ~ 8.5:1.5의 중량비로 혼합된 복합나노섬유를 포함하는 배터리 패키지.a battery pack including at least one battery accommodating hole in which an insulating film is disposed on an inner surface of the battery pack; and
Including a battery accommodated in the battery accommodating hole,
The insulating film includes a nanofiber web having a plurality of micropores capable of accommodating air, and the nanofibers forming the nanofiber web are composed of polyacrylonitrile and polyvinylidene fluoride in a ratio of 6:4 in mono yarn. A battery package containing composite nanofibers mixed in a weight ratio of ~8.5:1.5. 배터리 및 단열막이 적어도 2회 교호로 배치되고, 상기 배터리 및 단열막을 패킹하는 배터리 팩을 포함하며,
상기 단열막은 공기를 수용할 수 있는 다수의 미세기공이 형성된 나노섬유웹을 포함하며, 상기 나노섬유웹을 형성하는 나노섬유는 모노사 내에서 폴리아크릴로니트릴과 폴리비닐리덴플루오라이드가 6:4 ~ 8.5:1.5의 중량비로 혼합된 복합나노섬유를 포함하는 배터리 패키지.A battery pack in which a battery and an insulator are alternately disposed at least twice and pack the battery and the insulator,
The insulating film includes a nanofiber web having a plurality of micropores capable of accommodating air, and the nanofibers forming the nanofiber web are composed of polyacrylonitrile and polyvinylidene fluoride in a ratio of 6:4 in mono yarn. A battery package containing composite nanofibers mixed in a weight ratio of ~8.5:1.5. 제1항 내지 제3항 중 어느 한 항에 있어서,
상기 배터리의 표면 및 단열막 사이에 접착제층을 더 포함하며, 상기 접착제층은 PPa(acid modified polypropylene)를 함유하는 것을 특징으로 하는 배터리 패키지.According to any one of claims 1 to 3,
The battery package further comprises an adhesive layer between the surface of the battery and the insulating film, wherein the adhesive layer contains acid modified polypropylene (PPa). 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete
KR1020150153426A 2014-10-31 2015-11-02 Battery package including heat insulating film KR102498314B1 (en)